JP2001096902A - Ink jet recording medium, recording method and recorded article using the same - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an ink jet recording medium, by which an image having a high picture quality, a high moisture-resistance and a high light-resistance can be obtained, a recording method and a recorded article using the ink jet recording medium, in the ink jet recording medium for which a film is used as the base material. SOLUTION: In this ink jet recording medium, on one side surface of a film having air-permeability, a solvent-absorbing layer is provided. Then, on the other side surface of the film having air-permeability, an ink-receiving layer is provided. Also, an ink for ink jet is adhered to the ink-receiving layer of the ink jet recording medium, and an organic solvent in the ink for ink jet is absorbed by the solvent-absorbing layer through the film in this recording method. Also, this recorded article is recorded by sticking the ink for ink jet onto the ink jet recording medium.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、インクジェット用
記録媒体、それを用いた記録方法および記録物に関す
る。より具体的には、フィルムを基材とするインクジェ
ット用記録媒体において、高画質および高耐湿性を有す
る画像を得ることのできるインクジェット用記録媒体、
それを用いた記録方法および記録物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording medium, a recording method using the same, and a recorded matter. More specifically, in a recording medium for ink-jet based on a film, an ink-jet recording medium capable of obtaining an image having high image quality and high moisture resistance,
The present invention relates to a recording method and a recorded matter using the same.

【０００２】[0002]

【従来の技術】インクジェット記録とは、インクジェッ
ト方式により、すなわち、周知のようにインクの小滴を
飛翔させ、紙等の記録媒体に付着させて印刷を行うこと
である。この記録方式により、安価な装置で高解像度、
高品位な画像を高速かつ簡便に印刷することができるの
で、特に、カラー印刷においては、近年、写真に代わり
うる画像形成方式として技術開発が行われている。2. Description of the Related Art Ink jet recording refers to printing by jetting ink droplets and attaching the ink droplets to a recording medium such as paper, as is well known. With this recording method, high-resolution,
Since high-quality images can be printed quickly and easily, particularly in color printing, in recent years, technical development has been carried out as an image forming method that can substitute for photographs.

【０００３】インクジェット記録に使用されるインクと
しては、種々のインクが開発されているが、水、着色剤
の他に添加剤として有機溶媒を含有したものが一般的と
なっている。また、このような組成のインクを用いてイ
ンクジェット記録をするための記録媒体としては、ベー
スペーパー上に、画像を定着させるためのインク定着剤
と樹脂バインダーを含有するインク受容層を設けたもの
が知られており、昨今の画像の高画質化を達成するため
に多くのインク受容層が開発されている。これらのイン
クジェット用インク及び記録媒体等の開発により、イン
クジェット記録は単なる文章の印字記録にとどまらず、
絵などのカラー画像や写真画像を手軽に且つ高品質に印
刷できるようになるなど、その用途は拡大している。し
かも最近では、幅広い用途に応じて、記録面のみなら
ず、記録紙としても様々な機能が要求されている。[0003] Various inks have been developed as inks used for ink-jet recording, but those containing an organic solvent as an additive in addition to water and a colorant are generally used. Further, as a recording medium for ink-jet recording using an ink having such a composition, a recording medium provided with an ink fixing agent for fixing an image and an ink receiving layer containing a resin binder on a base paper. Many ink receiving layers have been developed in order to achieve high quality of recent images. With the development of these inkjet inks and recording media, inkjet recording is not limited to just printing text.
The use thereof is expanding, for example, a color image such as a picture or a photographic image can be printed easily and with high quality. In recent years, various functions have been required not only on the recording surface but also as recording paper in accordance with a wide range of applications.

【０００４】そのような記録紙として求められる機能
は、強度があること、軽量であること、平滑性が高いこ
と、高光沢面を有することなどの材質上の機能を挙げる
ことができる。これを達成する手段の一つとして、上記
ベースペーパーの代わりにフィルム上にインク受容層が
設ける手法が知られており、これにより高画質の画像が
得られるだけでなく、記録媒体全体としての材質改良が
なされた記録媒体が知られている。[0004] The functions required for such a recording paper include functions on the material such as high strength, light weight, high smoothness, and high glossy surface. As one of means for achieving this, a method in which an ink receiving layer is provided on a film instead of the base paper is known, and thus, not only can a high-quality image be obtained, but also the material of the recording medium as a whole. Improved recording media are known.

【０００５】しかしながら、インク受容層中において、
一般的なインクジェット用インク中に含まれる有機溶媒
（特に高沸点溶媒）と着色剤とが共存した状態では、光
によって着色剤の劣化が促進されやすく、また、着色剤
の記録媒体に対する定着性も前記有機溶媒により阻害さ
れすいことから、高湿度下で画像がにじみやすいという
問題があり、この現象は特に、通気性のないフィルム基
材やレジンコートされた基材を用いた場合に強く発生す
るものである。そのため、インクジェット用インクのイ
ンク滴が記録媒体上に滴下された後に、インク中の前記
有機溶媒と着色剤が速やかに分離された状態になれば、
優れた耐光性および耐水性を示すものと考えられ、これ
を目的として、前記有機溶媒を吸収する能力に優れる吸
油性材料を用いた先行技術がいくらか存在している。However, in the ink receiving layer,
In a state in which an organic solvent (especially a high boiling point solvent) contained in a general inkjet ink and a colorant coexist, the deterioration of the colorant is easily promoted by light, and the fixability of the colorant to a recording medium is also improved. Because of the inhibition caused by the organic solvent, there is a problem that images easily bleed under high humidity, and this phenomenon is particularly strong when a non-breathable film substrate or resin-coated substrate is used. Things. Therefore, after the ink droplet of the inkjet ink is dropped on the recording medium, if the organic solvent and the colorant in the ink are quickly separated,
It is believed that they exhibit excellent light and water fastness, and for this purpose, there is some prior art using oil-absorbing materials that have excellent ability to absorb the organic solvents.

【０００６】特開平９−３０９２９５号公報および特公
表１１−５０６９９１号公報には、特にフィルム基材の
みに限定しているものではないが、吸油性のある無機材
料をインク受容層中に添加することで、画像の耐光性を
向上させ、また、にじみを防ぐ試みが開示されている。
しかしながら、この手法は、インク受容層中に直接、吸
油性のある無機材料を添加するために、画像の発色濃度
が低く、高画質な画像を得ることのできる記録媒体とし
ては不十分である。[0006] JP-A-9-309295 and JP-A-11-506991 do not specifically limit the invention to a film substrate, but add an oil-absorbing inorganic material to an ink receiving layer. Thus, an attempt to improve the light fastness of an image and to prevent bleeding is disclosed.
However, this method is not sufficient as a recording medium capable of obtaining a high-quality image with a low color density of an image because an oil-absorbing inorganic material is directly added to the ink receiving layer.

【０００７】また、特開平９−２０７４２９号公報に
は、基材上に、無機物からなり、前記有機溶媒を吸収す
ることのできる溶媒吸収層を設け、その上にインク吸収
層を設ける手法が開示されている。すなわち、溶媒吸収
層とインク受容層とを分離させて設けることで、インク
中の有機溶媒と着色剤とを分離して存在させ、その結
果、優れた画質を有し、耐光性および耐水性に優れる画
像を得ることのできる記録媒体を製造しようとする試み
である。しかしながら、溶媒吸収層とインク受容層の接
着性に問題があるために、吸油性材料の添加が制限され
るだけでなく、特定のインクでないと効果が期待されな
い等の不都合があり、これらの例では、問題の本質的な
解決には至っていないのが現状である。Japanese Patent Application Laid-Open No. 9-207429 discloses a method in which a solvent absorbing layer made of an inorganic material and capable of absorbing the organic solvent is provided on a substrate, and an ink absorbing layer is provided thereon. Have been. That is, by providing the solvent absorbing layer and the ink receiving layer separately, the organic solvent and the colorant in the ink are separated and present, and as a result, it has excellent image quality, light resistance and water resistance. This is an attempt to manufacture a recording medium capable of obtaining an excellent image. However, since there is a problem in the adhesiveness between the solvent absorbing layer and the ink receiving layer, not only the addition of the oil absorbing material is limited, but there are inconveniences such that the effect is not expected unless the specific ink is used. Now, the problem has not been solved.

【０００８】[0008]

【発明が解決しようとする課題】本発明は、上記問題点
に鑑みて成されたものであり、その目的とするところ
は、フィルムを基材とするインクジェット用記録媒体に
おいて、高画質、高耐湿性および高耐光性を有する画像
を得ることのできるインクジェット用記録媒体、それを
用いた記録方法および記録物を提供することである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and an object of the present invention is to provide a recording medium for ink jet recording using a film as a base material, which has high image quality and high humidity resistance. It is an object of the present invention to provide an inkjet recording medium capable of obtaining an image having high light fastness and a recording method using the same.

【０００９】[0009]

【課題を解決するための手段】本発明者らは鋭意検討の
結果、フィルムを基材とするインクジェット用記録媒体
において、インク受容層内の有機溶媒を、効率良くイン
ク受容層外へ排出できる構成とすることで、より具体的
には、通気性のあるフィルムを利用し、インク受容層を
設ける面と反対の面に、溶媒吸収層を設けた場合に、高
画質、高耐湿性および高耐光性を有する画像が得られる
ことを見いだし、本発明を完成したものである。すなわ
ち、本発明は以下の通りである。Means for Solving the Problems As a result of intensive studies, the present inventors have found that in an ink jet recording medium using a film as a substrate, the organic solvent in the ink receiving layer can be efficiently discharged out of the ink receiving layer. More specifically, when a solvent-absorbing layer is provided on the surface opposite to the surface on which the ink receiving layer is provided using a gas-permeable film, high image quality, high moisture resistance, and high light resistance are provided. It has been found that an image having a characteristic can be obtained, and the present invention has been completed. That is, the present invention is as follows.

【００１０】本発明に係るインクジェット用記録媒体
は、透気性を有するフィルムの一方側の面に溶媒吸収層
が設けられ、該透気性を有するフィルムの他方側の面に
インク受容層が設けられたことを特徴とし（請求項
１）、これによって前記目的を達成することができる。In the ink jet recording medium according to the present invention, a solvent-absorbing layer is provided on one surface of a gas-permeable film, and an ink-receiving layer is provided on the other surface of the gas-permeable film. According to the present invention, the above object can be achieved.

【００１１】また本発明に係る上記インクジェット用記
録媒体において、 ・上記フィルムの透気度が、ＪＩＳ−Ｐ８１１７で規定
されている透気度で５０秒／１００ｃｃ以下であること
（請求項２）、 ・上記溶媒吸収層の吸油度が、ＪＩＳ−Ｋ６２２０で規
定されている吸油度で３２０ｍｌ／１００ｇ以上である
こと（請求項３）、 を特徴とする。In the ink jet recording medium according to the present invention, the air permeability of the film is 50 seconds / 100 cc or less as defined by JIS-P8117 (claim 2). The oil absorption of the solvent absorption layer is 320 ml / 100 g or more as defined by JIS-K6220 (Claim 3).

【００１２】・上記溶媒吸収層が、花弁状結晶構造を有
する珪酸カルシウムを含有すること（請求項４）、The solvent-absorbing layer contains calcium silicate having a petal-like crystal structure (claim 4);

【００１３】・上記溶媒吸収層が、溶媒吸収剤を含有
し、該溶媒吸収剤の含有割合が、該溶媒吸収層に対して
２０重量％〜１００重量％であること（請求項５）、The solvent absorbing layer contains a solvent absorbing agent, and the content of the solvent absorbing agent is 20% by weight to 100% by weight based on the solvent absorbing layer (claim 5);

【００１４】・上記インクジェット用記録媒体の透気度
が、ＪＩＳ−Ｐ８１１７で規定されている透気度で１０
０秒／１００ｃｃ以下であること（請求項６）、を特徴
とする。The air permeability of the ink jet recording medium is 10 as the air permeability defined in JIS-P8117.
0 sec / 100 cc or less (claim 6).

【００１５】また、本発明に係る記録方法は、上記イン
クジェット用記録媒体のインク受容層にインクジェット
用インクを付着させ、該インク中の有機溶媒を上記フィ
ルムを経由させて上記溶媒吸収層に吸収させることを特
徴とし（請求項７）、これによって前記目的を達成する
ことができる。Further, according to the recording method of the present invention, the ink for ink jet is attached to the ink receiving layer of the ink jet recording medium, and the organic solvent in the ink is absorbed by the solvent absorbing layer via the film. According to the present invention, the above object can be achieved.

【００１６】また、本発明に係る記録物は、上記インク
ジェット用記録媒体にインクジェット用インクを付着さ
せることで記録された記録物であり（請求項８）、これ
によって前記目的を達成することができる。Further, the recorded matter according to the present invention is a recorded matter recorded by adhering an ink-jet ink onto the above-mentioned ink-jet recording medium (claim 8), whereby the object can be achieved. .

【００１７】（作用）本発明に係るインクジェット用記
録媒体によれば、透気性を有するフィルムの一方側の面
に溶媒吸収層が設けられ、該透気性を有するフィルムの
他方側の面にインク受容層が設けられているので、着色
剤、有機溶媒を含有する一般的なインクジェット用水性
インクを用いた場合、着色剤をインク受容層内に定着さ
せるとともに、さらにインク中の有機溶媒をインク受容
層の表面から揮発させるだけでなく、フィルムを経由さ
せて溶媒吸収層に吸収させることができる。このためイ
ンク中の有機溶媒をインク受容層からほとんど除去する
ことのできるインクジェット用記録媒体となる（請求項
１）。(Function) According to the ink jet recording medium of the present invention, the solvent-absorbing layer is provided on one side of the air-permeable film, and the ink-receiving layer is provided on the other side of the air-permeable film. Since a layer is provided, when a general ink-jet ink containing a colorant and an organic solvent is used, the colorant is fixed in the ink receiving layer, and the organic solvent in the ink is further transferred to the ink receiving layer. Not only can be volatilized from the surface, but also can be absorbed by the solvent absorbing layer via a film. Therefore, an ink jet recording medium is obtained in which the organic solvent in the ink can be almost completely removed from the ink receiving layer.

【００１８】本発明に係るインクジェット用記録媒体に
よれば、上記フィルムの透気度が、ＪＩＳ−Ｐ８１１７
で規定されている透気度で５０秒／１００ｃｃ以下であ
るので、インク中の有機溶媒を、効率良くフィルムへ移
動させることができるインクジェット用記録媒体となる
（請求項２）。According to the ink jet recording medium of the present invention, the air permeability of the film is JIS-P8117.
Since the air permeability specified by the formula is 50 seconds / 100 cc or less, the ink jet recording medium can efficiently transfer the organic solvent in the ink to the film (claim 2).

【００１９】本発明に係るインクジェット用記録媒体に
よれば、溶媒吸収層の吸油度が、ＪＩＳ−Ｋ６２２０で
規定されている吸油度で３２０ｍｌ／１００ｇ以上であ
るので、インク中の有機溶媒を、溶媒吸収層に確実に吸
収させることができるインクジェット用記録媒体となる
（請求項３）。According to the ink jet recording medium of the present invention, the oil absorption of the solvent absorbing layer is 320 ml / 100 g or more as determined by JIS-K6220. An ink jet recording medium that can be reliably absorbed by the absorbing layer is obtained (claim 3).

【００２０】本発明に係るインクジェット用記録媒体に
よれば、溶媒吸収層が、非常に高い吸油度を有する花弁
状結晶構造を有する珪酸カルシウムを含有するので、イ
ンク中の有機溶媒を、溶媒吸収層に確実に吸収させるこ
とができるインクジェット用記録媒体となる（請求項
４）。According to the ink jet recording medium of the present invention, since the solvent absorbing layer contains calcium silicate having a petal-like crystal structure having a very high oil absorption, the organic solvent in the ink is removed from the solvent absorbing layer. Thus, an ink jet recording medium that can be surely absorbed is provided (claim 4).

【００２１】本発明に係るインクジェット用記録媒体に
よれば、溶媒吸収層が、溶媒吸収剤を含有し、溶媒吸収
剤の含有割合が、溶媒吸収層に対して２０重量％〜１０
０重量％であるので、インク中の有機溶媒を、溶媒吸収
層に確実に吸収させることができるインクジェット用記
録媒体となる（請求項５）。According to the ink jet recording medium of the present invention, the solvent absorbing layer contains the solvent absorbing agent, and the content of the solvent absorbing agent is from 20% by weight to 10% by weight based on the solvent absorbing layer.
Since the content is 0% by weight, the ink jet recording medium can reliably absorb the organic solvent in the ink into the solvent absorbing layer (claim 5).

【００２２】本発明に係るインクジェット用記録媒体に
よれば、上記インクジェット用記録媒体の透気度が、Ｊ
ＩＳ−Ｐ８１１７で規定されている透気度で１００秒／
１００ｃｃ以下であるので、記録媒体の厚さによらず、
インク中の有機溶媒を、フィルムを経由させて溶媒吸収
層に確実に吸収させることができるインクジェット用記
録媒体となる（請求項６）。According to the ink jet recording medium of the present invention, the air permeability of the ink jet recording medium is J
100 seconds / with air permeability specified by IS-P8117
Because it is 100 cc or less, regardless of the thickness of the recording medium,
The ink jet recording medium can reliably absorb the organic solvent in the ink into the solvent absorbing layer via the film (claim 6).

【００２３】本発明に係る記録方法によれば、上記のイ
ンクジェット用記録媒体のインク受容層に、着色剤およ
び有機溶媒を含有する一般的なインクジェット用水性イ
ンクを付着させることにより、着色剤をインク受容層内
に定着させるとともに、さらにインク中の有機溶媒をイ
ンク受容層の表面から揮発させるだけでなく、フィルム
を経由させて溶媒吸収層に吸収させることができる。こ
れにより、有機溶媒をインク受容層内からほとんど除去
できる記録方法となる（請求項７）。According to the recording method of the present invention, the colorant is added to the ink-receiving layer of the above-described ink-jet recording medium by attaching a general aqueous ink-jet ink containing a colorant and an organic solvent to the ink. As well as being fixed in the receiving layer, the organic solvent in the ink can be not only volatilized from the surface of the ink receiving layer but also absorbed by the solvent absorbing layer via a film. This provides a recording method in which the organic solvent can be almost removed from the ink receiving layer (claim 7).

【００２４】本発明に係る記録物によれば、上記のイン
クジェット用記録媒体に、着色剤および有機溶媒を含有
する一般的なインクジェット用水性インクを付着させる
ことにより、着色剤がインク受容層に定着されるととも
に有機溶媒がほとんど除去された記録物となる（請求項
８）。According to the recorded matter of the present invention, a general aqueous ink jet ink containing a colorant and an organic solvent is adhered to the above-mentioned ink jet recording medium, whereby the colorant is fixed to the ink receiving layer. Thus, a recorded matter from which the organic solvent is almost completely removed is obtained (claim 8).

【００２５】[0025]

【発明の実施の形態】本発明に係る実施の形態のインク
ジェット用記録媒体は、透気性を有するフィルムの一方
側の面に溶媒吸収層が設けられ、該透気性を有するフィ
ルムの他方側の面にインク受容層が設けられた構成とな
っている。BEST MODE FOR CARRYING OUT THE INVENTION An ink jet recording medium according to an embodiment of the present invention has a solvent-absorbing layer provided on one surface of a gas-permeable film, and the other surface of the gas-permeable film. Is provided with an ink receiving layer.

【００２６】［透気性を有するフィルム］先ず、本発明
に係るインクジェット用記録媒体に用いられる透気性を
有するフィルムについて詳述する。通常、インクジェッ
ト用水性インクには、主成分である水および着色剤以外
に、添加剤として有機溶媒が添加される。この有機溶媒
は、インクジェットに適したインク粘度とするために添
加され、メタノール、エタノール、ｎ−プロピルアルコ
ール、ｉｓｏ−プロピルアルコール等の低沸点溶媒およ
びジエチレングリコール、ポリエチレングリコール、ポ
リプロピレングリコール、エチレングリコール、グリセ
リン等の高沸点溶媒が用いられる。よって、本発明に係
るインクジェット用記録媒体のベースシートに使用され
るフィルムとしては、インクジェット記録後、インクの
成分として用いられる上記の有機溶媒をインク受容層か
ら吸い込み、この有機溶剤を溶媒吸収層に吸収させるこ
とができるものであれば、いずれのものも選択できる。[Air-permeable film] First, the air-permeable film used for the ink jet recording medium according to the present invention will be described in detail. Usually, an organic solvent is added to the aqueous inkjet ink as an additive in addition to water and a colorant as main components. This organic solvent is added in order to make the ink viscosity suitable for inkjet, and low-boiling solvents such as methanol, ethanol, n-propyl alcohol, and iso-propyl alcohol, and diethylene glycol, polyethylene glycol, polypropylene glycol, ethylene glycol, glycerin, etc. Is used. Therefore, as the film used for the base sheet of the inkjet recording medium according to the present invention, after inkjet recording, the organic solvent used as a component of the ink is sucked from the ink receiving layer, and the organic solvent is absorbed into the solvent absorbing layer. Any substance can be selected as long as it can be absorbed.

【００２７】このような作用を有するフィルムは、例え
ば特公平６−６７６０３号公報、特公平８−２２６０９
号公報および特許第２８７６６８３号公報を参考に作製
することができる。すなわち主成分としては、超高分子
量ポリオレフィンを挙げることができ、好ましくは超高
分子量ポリエチレン、超高分子量ポリプロピレンおよび
それらの混合物である。このような超高分子量ポリオレ
フィンは、例えばハイモント、ユー・エス・エー社（Ｈ
ｉｍｏｎｔ，Ｕ．Ｓ．Ａ，Ｉｎｃ．）製の超高分子量ポ
リエチレン、ハイモント（Ｈｉｍｏｎｔ）１９００など
が上市されており好適に用いることができる。このよう
な超高分子量ポリオレフィンは、フィルムの全乾燥重量
に基づいて１０重量％〜６０重量％の範囲にあることが
好ましい。Films having such an action are described, for example, in Japanese Patent Publication No. 6-67603 and Japanese Patent Publication No. 8-226609.
And Japanese Patent No. 2,876,683. That is, as the main component, an ultrahigh molecular weight polyolefin can be mentioned, and ultrahigh molecular weight polyethylene, ultrahigh molecular weight polypropylene and a mixture thereof are preferable. Such ultrahigh molecular weight polyolefins are available, for example, from Himont, USA
immont, U.S.A. S. A, Inc. ), Himont 1900, etc. are commercially available and can be suitably used. Such ultrahigh molecular weight polyolefins are preferably in the range of 10% to 60% by weight based on the total dry weight of the film.

【００２８】またそれ以外に熱可塑性の有機高分子を所
望のフィルム物性に影響を与えない範囲で任意の成分と
して用いることができる。このような熱可塑性の有機高
分子としては、低密度ポリエチレン、高密度ポリエチレ
ン、ポリ（テトラフルオロ）エチレン、ポリプロピレ
ン、エチレンおよびプロピレンのコポリマー、エチレン
およびアクリル酸のコポリマー、エチレンおよびアクリ
ル酸のコポリマーが挙げられるがこれに限定されるもの
ではない。これらの熱可塑性の有機高分子はフィルムの
全乾燥重量に対して５重量％〜３０重量％の範囲にある
ことが好ましい。In addition, a thermoplastic organic polymer can be used as an optional component as long as it does not affect desired film properties. Such thermoplastic organic polymers include low density polyethylene, high density polyethylene, poly (tetrafluoro) ethylene, polypropylene, copolymers of ethylene and propylene, copolymers of ethylene and acrylic acid, copolymers of ethylene and acrylic acid. However, the present invention is not limited to this. These thermoplastic organic polymers are preferably in the range of 5% to 30% by weight based on the total dry weight of the film.

【００２９】さらに必須の添加剤として、水不溶性珪質
充填剤が添加される。このような珪質充填剤としては、
シリカ、マイカ、モンモリロナイト、カオリナイト、ア
スベスト、タルク、珪藻土、ひる石、天然または合成ゼ
オライト、セメント、カルシウムシリケート、アルミニ
ウムシリケート、ナトリウムアルミニウムシリケート、
アルミニウムポリシルケート、アルミナシリカゲルおよ
びガラス粒子が挙げられ、形状は好ましくは微細粒状で
ある。シリカの中では沈降シリカ、シリカゲルまたはヒ
ュームドシリカが最も好ましい。また、後に詳述する花
弁状結晶構造を有する珪酸カルシウムを好適に用いるこ
ともできる。このような水不溶性珪質充填剤は、フィル
ムの全乾燥重量に基づいて２０重量％〜７０重量％の範
囲にあることが好ましい。Further, as an essential additive, a water-insoluble siliceous filler is added. Such siliceous fillers include:
Silica, mica, montmorillonite, kaolinite, asbestos, talc, diatomaceous earth, vermiculite, natural or synthetic zeolites, cement, calcium silicate, aluminum silicate, sodium aluminum silicate,
Examples include aluminum polysilicate, alumina silica gel and glass particles, the shape preferably being finely divided. Among silicas, precipitated silica, silica gel or fumed silica is most preferred. Further, calcium silicate having a petal-like crystal structure described in detail later can also be suitably used. Such water-insoluble siliceous fillers preferably range from 20% to 70% by weight based on the total dry weight of the film.

【００３０】上記珪質添加剤の他にも、水不溶性非珪質
充填剤を用いることができ、そのような例としてはカー
ボンブラック、活性炭、グラファイト、酸化チタン、酸
化鉄、酸化銅、酸化亜鉛、酸化アンチモン、ジルコニ
ア、マグネシア、アルミナ、二硫化モリブデン、硫化亜
鉛、硫化バリウム、硫酸ストロンチウム、炭酸カルシウ
ム、炭酸マグネシウム、水酸化マグネシウムなどが挙げ
られ、形状は好ましくは微細粒状である。このような水
不溶性非珪質充填剤は、フィルムの全乾燥重量に基づい
て２０重量％以下の範囲にあることが好ましい。In addition to the above siliceous additives, water-insoluble non-siliceous fillers can be used, such as carbon black, activated carbon, graphite, titanium oxide, iron oxide, copper oxide, zinc oxide. , Antimony oxide, zirconia, magnesia, alumina, molybdenum disulfide, zinc sulfide, barium sulfide, strontium sulfate, calcium carbonate, magnesium carbonate, magnesium hydroxide and the like, and the shape is preferably finely granular. Such a water-insoluble non-silica filler is preferably in the range of 20% by weight or less based on the total dry weight of the film.

【００３１】その他にも離型剤および水等の添加剤をフ
ィルムの乾燥重量に対して５重量％より少ない量で存在
させることができる。さらに酸化防止剤、紫外線吸収
剤、難然剤、強化用繊維、染料、顔料等を、用途に応じ
て用いることができ、フィルムの全乾燥重量に対して１
５重量％より少ない量で存在させることができる。In addition, additives such as release agents and water can be present in an amount of less than 5% by weight based on the dry weight of the film. Further, antioxidants, ultraviolet absorbers, repellents, reinforcing fibers, dyes, pigments and the like can be used depending on the application, and 1 to the total dry weight of the film.
It can be present in an amount less than 5% by weight.

【００３２】以下に透気性を有するフィルムの好適な作
製方法を示す。 （工程１）上記主成分の超高分子量ポリオレフィン、上
記の水不溶性珪質充填剤、任意に用いられる上記の水不
溶性非珪質充填剤、熱可塑性の有機高分子および添加剤
に、さらに必須成分である水不溶性珪質充填剤を添加
し、ミキサーで混合する。A preferred method of producing a film having air permeability will be described below. (Step 1) In addition to the ultra-high molecular weight polyolefin of the main component, the water-insoluble siliceous filler described above, the water-insoluble non-silica filler optionally used, the thermoplastic organic polymer and additives, further essential components Is added and mixed with a mixer.

【００３３】（工程２）次に、上記工程により得られた
混合物に加工可塑剤を添加・混合し、この混合流動体を
スクリュー押出機の加熱バレルに導入後、シート押し出
しダイから混合流動体を押し出すことでシートを得る。
このような加工可塑剤は、室温で液体であり、パラフィ
ン系石油、ナフテン系石油、芳香油などの加工油が用い
られる。具体的には、シェルフレックス（Ｓｈｅｌｌｆ
ｌｅｘ）４１２およびシェルフレックス（Ｓｈｅｌｌｆ
ｌｅｘ）３７１（シェルオイル社（ＳｈｅｌｌＯｉｌ
Ｃｏ．）の商品名）が好ましく用いられる。加工可塑剤
の添加量は、上記工程１で作製された混合物の５重量％
〜３０重量％の範囲にあることが好ましい。(Step 2) Next, a processing plasticizer is added and mixed to the mixture obtained in the above step, and the mixed fluid is introduced into a heating barrel of a screw extruder, and then the mixed fluid is discharged from a sheet extrusion die. The sheet is obtained by extruding.
Such processing plasticizers are liquid at room temperature, and processing oils such as paraffinic petroleum, naphthenic petroleum, and aromatic oils are used. Specifically, Shellflex (Shellf
lex) 412 and Shellflex
lex) 371 (Shell Oil)
Co. ) Is preferably used. The amount of the processing plasticizer added was 5% by weight of the mixture prepared in Step 1 above.
It is preferably in the range of 〜30% by weight.

【００３４】（工程３）引き続き、シート内の加工可塑
剤を除去するために、加工可塑剤には良溶媒であり、他
のシート内の成分には貧溶媒である有機抽出液を用いて
シートから加工可塑剤を抽出する。このような有機抽出
液としては、１，１，２−トリクロロエチレン、パーク
ロロエチレン、１，２−ジクロロエタン、１，１，１−
トリクロロエタン、１，１，２−トリクロロエタン、メ
チレンクロライドおよびクロロホルムなどの塩素系有機
溶媒、イソプロピルアルコール、ジエチルエーテル並び
にアセトンなどが挙げられる。(Step 3) Subsequently, in order to remove the processing plasticizer in the sheet, an organic extract, which is a good solvent for the processing plasticizer and a poor solvent for the components in the other sheets, is used. Extract the processing plasticizer from Such organic extracts include 1,1,2-trichloroethylene, perchlorethylene, 1,2-dichloroethane, 1,1,1-
Chlorinated organic solvents such as trichloroethane, 1,1,2-trichloroethane, methylene chloride and chloroform, isopropyl alcohol, diethyl ether, acetone and the like.

【００３５】（工程４）最後に、加工可塑剤が除去され
たシートを蒸気または水で洗浄し、乾燥機で乾燥させる
ことによりフィルムが得られる。このようにして得られ
たフィルムに、通常行われる一軸延伸、二軸延伸のよう
な延伸処理を施して、所望な特性・特質にすることも望
ましい。最終的なフィルムの厚さは、上記（２）におけ
るシートの厚さを調整することにより、また延伸を行う
時にはその延伸比、延伸温度等の延伸条件を調整するこ
とにより、５０μｍ〜２５０μｍの範囲とするのが好ま
しい。(Step 4) Finally, the sheet from which the processing plasticizer has been removed is washed with steam or water, and dried with a dryer to obtain a film. It is also desirable that the film obtained in this manner is subjected to a stretching treatment such as uniaxial stretching or biaxial stretching that is usually performed to obtain desired properties and characteristics. The final thickness of the film is in the range of 50 μm to 250 μm by adjusting the thickness of the sheet in the above (2) and adjusting the stretching conditions such as the stretching ratio and the stretching temperature when stretching is performed. It is preferred that

【００３６】以上、例えば上記のような方法により、微
細な気孔を数多く有し、透気性を有するフィルムを作製
することができる。所望の材質特性および透気性に応じ
て、上記配合成分の種類、配合比およびフィルムの厚さ
が上記範囲内で適宜選択され、必要に応じて延伸処理が
施される。しかしながら、透気性が少な過ぎると、イン
ク受容層にインクジェット用インクを付着させた場合、
インク中の有機溶媒をフィルムを経由させて溶媒吸収層
に吸収させることが困難となる。そのためフィルムの透
気度はＪＩＳ−Ｐ８１１７で規定されている透気度で、
５０秒／１００ｃｃ以下であることが好ましい。As described above, for example, a film having many fine pores and having air permeability can be produced by the above-described method. Depending on the desired material properties and air permeability, the type, mixing ratio, and film thickness of the above components are appropriately selected within the above ranges, and a stretching treatment is performed as necessary. However, if the air permeability is too small, when the ink for ink jet is attached to the ink receiving layer,
It becomes difficult to absorb the organic solvent in the ink through the film and into the solvent absorbing layer. Therefore, the air permeability of the film is the air permeability specified in JIS-P8117,
It is preferably 50 seconds / 100 cc or less.

【００３７】また、上記の好ましい透気度を有するフィ
ルムとして、テズリン（ピーピージー・インダストリー
ズ・インコーポレイテッドの登録商標）等が上市されて
おり、材質特性が所望のものであれば、本発明に係る記
録媒体のベースシートとして、これらをそのまま用いる
こともできる。なお、本明細書における透気度とは、フ
ィルムに対して、その厚み方向に空気が通過できる度合
い示すものであり、具体的な数値は、ＪＩＳ−Ｐ８１１
７に準じた測定によるものである。Tezulin (registered trademark of PPG Industries, Inc.) or the like is marketed as a film having the above-mentioned preferable air permeability, and if the material characteristics are desired, the recording according to the present invention is carried out. These can be used as they are as the base sheet of the medium. The air permeability in the present specification indicates the degree to which air can pass through the film in the thickness direction, and specific numerical values are based on JIS-P811.
7 based on the measurement.

【００３８】［溶媒吸収層］次に、本発明に係る溶媒吸
収層について説明する。溶媒吸収層は、溶媒吸収剤を主
成分とし、必要に応じて、後述するようなバインダー、
着色顔料を含有することができる。本発明に用いられる
最も好ましい溶媒吸収剤としては、花弁状結晶構造（ジ
ャイロライト型結晶構造ともいう）を有する珪酸カルシ
ウムを挙げることができ、特開平１−１５３５６２号公
報、特開昭５４−９３６９８号公報、特開昭５５−３２
７５３号公報等に記載された製法により得ることができ
る。しかしながら、花弁状結晶構造を有する珪酸カルシ
ウムに限定されるものではなく、シリカゲル、ゼオライ
ト、タルク、カオリン等の同様な性質が示される親油性
無機物質を用いても良い。上記例示した無機物質の粉体
は、必要に応じて、適当なバインダーと混合され、イン
ク受容層とは逆の裏面に塗工されて用いられる。また、
上記無機物質のみに限らず、有機物質単独、もしくは無
機物質と有機物質との混合物を用いることもでき、この
ような有機物質としては、特開平３−２２１５８２号公
報、特開平５−９２１１号公報、特開平５−９２４３号
公報、特開平５−１７５３７号公報、特開平５−１１７
３３５号公報、特開平５−１１２５２４６号公報、特開
平７−１３３３８３号公報、特開平８−７１４１６号公
報などに示される公知の有機物質を用いることができ
る。上記有機物質としては、主にアクリル系、スチレン
系、ノルボルネン系、オレフィン系樹脂を用いることが
でき、これらから成る樹脂によって撥水処理したセルロ
ース系繊維から成るパルプや、前記パルプと、ポリエチ
レン，ポリプロピレンなどの合成繊維または粉砕状物質
（上記例示した無機物質を含む）とを混合させたものな
どを用いても良い。[Solvent Absorbing Layer] Next, the solvent absorbing layer according to the present invention will be described. The solvent absorbing layer contains a solvent absorbing agent as a main component and, if necessary, a binder as described below,
Color pigments can be included. As the most preferred solvent absorbent used in the present invention, calcium silicate having a petal-like crystal structure (also referred to as a gyrolite-type crystal structure) can be mentioned, for example, JP-A-1-153562 and JP-A-54-93698. No., JP-A-55-32
No. 753, and the like. However, the present invention is not limited to calcium silicate having a petal-like crystal structure, and a lipophilic inorganic substance having similar properties such as silica gel, zeolite, talc, and kaolin may be used. The powder of the inorganic substance exemplified above is mixed with an appropriate binder, if necessary, and is used after being coated on the back surface opposite to the ink receiving layer. Also,
Not only the above-mentioned inorganic substance, but also an organic substance alone or a mixture of an inorganic substance and an organic substance can be used. Examples of such an organic substance include JP-A-3-221852 and JP-A-5-9221. JP-A-5-9243, JP-A-5-17537, JP-A-5-117
Known organic substances described in JP-A-335, JP-A-5-112246, JP-A-7-133383, JP-A-8-71416 and the like can be used. As the organic substance, acrylic, styrene, norbornene, and olefin resins can be mainly used, and pulp made of cellulose fiber water-repellent with a resin made of these resins, pulp, polyethylene, polypropylene For example, a mixture of synthetic fibers or a pulverized substance (including the inorganic substances exemplified above) may be used.

【００３９】このような溶媒吸収剤は、溶媒吸収層の全
乾燥重量に基づいて、２０重量％〜１００重量％の範囲
にあることが好ましく、また、溶媒吸収層の吸油度は、
ＪＩＳ−Ｋ６２２０で規定されている吸油度で３２０ｍ
ｌ／１００ｇ以上であることが好ましい。（溶媒吸収剤
が２０重量％より少ないと、また、溶媒吸収層の吸油度
が３２０ｍｌ／１００ｇより少ないと、インク中の有機
溶媒を溶媒吸収層に吸収させにくくなる。）Such a solvent absorbent is preferably in the range of 20% by weight to 100% by weight based on the total dry weight of the solvent absorbent layer.
320 m in oil absorption specified by JIS-K6220
It is preferably at least 1/100 g. (If the solvent absorbent is less than 20% by weight, and if the oil absorption of the solvent absorbent layer is less than 320 ml / 100g, it becomes difficult to absorb the organic solvent in the ink into the solvent absorbent layer.)

【００４０】溶媒吸収層の形成方法は、溶媒吸収性を示
す上記材料を乾燥重量比で２０重量部以上含む水溶液ス
ラリーを製造し、これを定法に従って、バーコーター、
エアナイフコーター、ブレードコーター、グラビアコー
ター等を用いて裏面に塗工し、乾燥することによって形
成され、特に塗工方法や乾燥方法によって制限されるも
のではない。The solvent absorbing layer can be formed by preparing an aqueous slurry containing at least 20 parts by weight of the above-mentioned material exhibiting solvent absorbency in a dry weight ratio, and subjecting it to a bar coater,
It is formed by coating the back surface using an air knife coater, blade coater, gravure coater or the like and drying the coating, and is not particularly limited by a coating method or a drying method.

【００４１】［インク受容層］次に本発明に係るインク
ジェット用記録媒体のインク受容層について説明する。
インク受容層は、カラー画像や写真画像などを高品質に
再現するために、本発明に係るインクジェット用記録媒
体の必須の構成要素であり、従来公知のものをいずれも
使用することができる。すなわち、インク受容層には、
インク吸収顔料、インク定着剤およびバインダーが含有
されるのが好ましく、更に必要に応じて、染料固着剤
（耐水化剤）、蛍光増白剤、界面活性剤、消泡剤、ｐＨ
調整剤、防黴剤、紫外線吸収剤および酸化防止剤等の各
種添加剤が含有される。[Ink receiving layer] Next, the ink receiving layer of the ink jet recording medium according to the present invention will be described.
The ink receiving layer is an essential component of the ink jet recording medium according to the present invention in order to reproduce a color image or a photographic image with high quality, and any conventionally known one can be used. That is, in the ink receiving layer,
The ink preferably contains an ink-absorbing pigment, an ink fixing agent, and a binder. If necessary, a dye fixing agent (waterproofing agent), a fluorescent whitening agent, a surfactant, a defoaming agent, pH
Various additives such as a regulator, a fungicide, an ultraviolet absorber and an antioxidant are contained.

【００４２】インク吸収顔料としては、公知の白色顔料
を１種以上用いることができる。例えば、軽質炭酸カル
シウム、重質炭酸カルシウム、炭酸マグネシウム、カオ
リン、タルク、硫酸カルシウム、硫酸バリウム、二酸化
チタン、酸化亜鉛、硫化亜鉛、炭酸亜鉛、チタンホワイ
ト、珪酸アルミニウム、ケイソウ土、珪酸カルシウム、
珪酸マグネシウム、合成非晶質シリカ、コロイダルシリ
カ、アルミナ、コロイダルアルミナ、擬ベーマイト、水
酸化アルミニウム、リトポン、ゼオライト、加水ハロイ
サイト、水酸化マグネシウム等の白色無機顔料、スチレ
ン系プラスチックピグメント、アクリル系プラスチック
ピグメント、ポリエチレン、メラミン樹脂、尿素樹脂等
の有機顔料などが挙げられる。As the ink absorbing pigment, one or more known white pigments can be used. For example, light calcium carbonate, heavy calcium carbonate, magnesium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, titanium white, aluminum silicate, diatomaceous earth, calcium silicate,
White inorganic pigments such as magnesium silicate, synthetic amorphous silica, colloidal silica, alumina, colloidal alumina, pseudoboehmite, aluminum hydroxide, lithopone, zeolite, hydrohaloysite, magnesium hydroxide, styrene-based plastic pigment, acrylic-based plastic pigment, Organic pigments such as polyethylene, melamine resin, and urea resin are exemplified.

【００４３】インク定着剤としては、特にカチオン性化
合物が好ましく、１級〜３級アミンあるいは４級アンモ
ニウム塩基を有する低分子化合物、それらの基を有する
オリゴマー、またはそれらの基を有するポリマーが挙げ
られる。具体的には、ジアリルジメチルアンモニウムク
ロライドポリマー，ジアリルジメチルアンモニウムクロ
ライド−二酸化イオウコポリマー，ジアリルジメチルア
ンモニウムクロライド−アクリルアミドコポリマーなど
のジアリルメチルアンモニウム塩ポリマー、ジアリルア
ミン塩酸塩−二酸化イオウコポリマー、ジアリルメチル
アミン塩酸塩コポリマー、ポリアリルアミン、ポリエチ
レンイミン、ポリエチレンイミン４級アンモニウム塩化
合物、（メタ）アクリル酸アルキルアンモニウム塩ポリ
マー、（メタ）アクリルアミドアルキルアンモニウム塩
ポリマー、４級アンモニウム塩を含むアイオネン等を挙
げることができる。これらのインク定着剤の含有量は、
インク受容層の全乾燥重量に対して１重量％〜３０重量
％が好ましく、より好ましくは５重量％〜１０重量％の
範囲である。As the ink fixing agent, a cationic compound is particularly preferable, and a low molecular compound having a primary to tertiary amine or a quaternary ammonium base, an oligomer having such a group, or a polymer having such a group can be mentioned. . Specifically, diallyldimethylammonium chloride polymer, diallyldimethylammonium salt polymer such as diallyldimethylammonium chloride-sulfur dioxide copolymer, diallyldimethylammonium chloride-acrylamide copolymer, diallylamine hydrochloride-sulfur dioxide copolymer, diallylmethylamine hydrochloride copolymer, Examples thereof include polyallylamine, polyethyleneimine, polyethyleneimine quaternary ammonium salt compound, (meth) acrylic acid alkylammonium salt polymer, (meth) acrylamidoalkylammonium salt polymer, and ionene containing quaternary ammonium salt. The content of these ink fixing agents is
It is preferably 1% by weight to 30% by weight, more preferably 5% by weight to 10% by weight, based on the total dry weight of the ink receiving layer.

【００４４】バインダーとしては、酸化澱粉、エーテル
化澱粉、リン酸エステル化澱粉等の澱粉誘導体；カルボ
キシメチルセルロース、ヒドロキシエチルセルロース等
のセルロース誘導体；カゼイン、ゼラチン、大豆蛋白、
ポリビニルアルコール又はその誘導体；ポリビニルピロ
リドン、無水マレイン酸樹脂、スチレン−ブタジエン共
重合体、メチルメタクリレート−ブタジエン共重合体等
の共役ジエン系共重合体ラテックス；アクリル酸エステ
ル及びメタクリル酸エステルの重合体又は共重合体等の
アクリル系重合体などのアクリル系重合体ラテックス；
エチレン酢酸ビニル共重合体等のビニル系重合体ラテッ
クス；あるいはこれら各種重合体のカルボキシ基等の官
能基含有単量体による官能基変性重合体ラテックス；メ
ラミン樹脂、尿素樹脂等の熱硬化性樹脂などの水性接着
剤；ポリメチルメタクリレート等のアクリル酸エステ
ル；メタクリル酸エステルの重合体又は共重合体；ポリ
ウレタン樹脂、不飽和ポリエステル樹脂、塩化ビニル酢
酸ビニルコポリマー、ポリビニルブチラール、アルキッ
ド樹脂等の合成樹脂系接着剤などを挙げることができ
る。これらのバインダーの含有量は、インク受容層の全
乾燥重量に対して１０重量％〜６０重量％が好ましく、
より好ましくは３０重量％〜５０重量％の範囲である。Examples of the binder include starch derivatives such as oxidized starch, etherified starch, and phosphated starch; cellulose derivatives such as carboxymethyl cellulose and hydroxyethyl cellulose; casein, gelatin, soy protein,
Polyvinyl alcohol or a derivative thereof; polyvinyl pyrrolidone, a maleic anhydride resin, a conjugated diene-based copolymer latex such as a styrene-butadiene copolymer, a methyl methacrylate-butadiene copolymer; a polymer or a copolymer of an acrylate ester and a methacrylate ester An acrylic polymer latex such as an acrylic polymer such as a polymer;
Vinyl-based polymer latex such as ethylene-vinyl acetate copolymer; or functional group-modified polymer latex with a monomer containing a functional group such as carboxy group of these various polymers; Thermosetting resin such as melamine resin and urea resin Water-based adhesives; acrylic esters such as polymethyl methacrylate; polymers or copolymers of methacrylic esters; synthetic resin-based adhesives such as polyurethane resins, unsaturated polyester resins, vinyl chloride vinyl acetate copolymers, polyvinyl butyral, and alkyd resins Agents and the like. The content of these binders is preferably from 10% by weight to 60% by weight based on the total dry weight of the ink receiving layer.
More preferably, it is in the range of 30% by weight to 50% by weight.

【００４５】インク受容層の形成は、上記のバインダー
を適当な溶媒に溶解又は分散させ、これにインク定着剤
を添加し、必要に応じて上記各種の添加剤を添加して得
た塗工液を、ロールコーティング法、スプレーコーティ
ング法、ロッドバーコーティング法、エアナイフコーテ
ィング法等のコーティング法等の公知のコーティング方
法で、上述した透気度を有するフィルムに塗工し、乾燥
させることによりなされる。インクジェット用記録媒体
全体の透気度が１００秒／１００ｃｃ以下となるように
層形成のための塗工量は調整される。塗工後の乾燥は、
一般的な乾燥機を用いて行なうことができ、一般的には
１００〜１５０℃の範囲で行なわれる。The ink receiving layer is formed by dissolving or dispersing the above binder in an appropriate solvent, adding an ink fixing agent thereto, and, if necessary, adding the various additives described above. Is applied to a film having the above-mentioned air permeability by a known coating method such as a roll coating method, a spray coating method, a rod bar coating method, an air knife coating method or the like, and dried. The coating amount for forming a layer is adjusted so that the air permeability of the entire inkjet recording medium is 100 seconds / 100 cc or less. Drying after coating,
It can be performed using a general dryer, and is generally performed in a range of 100 to 150 ° C.

【００４６】なお、本発明に係る記録方法および記録物
において使用するインクは、基本的に、水、着色剤およ
び有機溶媒を含有する公知のインクジェット用インクを
制限なく用いることができる。As the ink used in the recording method and recorded matter according to the present invention, basically, a known inkjet ink containing water, a colorant and an organic solvent can be used without limitation.

【００４７】以上、詳述した構成を有するインクジェッ
ト用記録媒体のインク受容層に、インクジェット方式に
より、着色剤および有機溶媒を含有する一般的なインク
ジェット用インクを付着させることにより、インク中の
有機溶媒をフィルムを経由させて上記溶媒吸収層に吸収
させ、有機溶媒をインク受容層内からほとんど除去でき
る記録方法とすることができる。The general ink-jet ink containing a colorant and an organic solvent is adhered to the ink-receiving layer of the ink-jet recording medium having the above-described structure by an ink-jet method, so that the organic solvent in the ink is removed. Can be absorbed by the solvent absorbing layer through a film, and the organic solvent can be almost completely removed from the ink receiving layer.

【００４８】また、このインクジェット用記録媒体にイ
ンクジェット用水性インクを付着させるので、着色剤が
インク受容層に付着されるとともに、インク受容層内に
おいて有機溶媒がほとんど除去された記録物とすること
ができる。Further, since the aqueous ink for ink jet is adhered to the recording medium for ink jet, a colorant is adhered to the ink receiving layer, and the organic solvent is almost completely removed from the ink receiving layer. it can.

【００４９】[0049]

【実施例】次に、本発明の実施例と比較例を共に挙げ、
本発明を具体的に説明するが、本発明は、以下の実施例
によって限定されるものではない。Next, both examples of the present invention and comparative examples will be described.
The present invention will be specifically described, but the present invention is not limited by the following examples.

【００５０】（実施例１で用いる記録媒体）以下のイン
ク受容層成分を、総固形分濃度として１５重量％の水溶
液となるように混合・調整し、透気度４５秒／１００ｃ
ｃのフィルム（厚さ：１６０μｍ）上に混合水溶液を塗
工し、乾燥機（ダバイエスペック株式会社製、ＰＨ−２
０１型オーブン）を用いて、１３０℃で２分間乾燥させ
た。その結果、インク受容層の塗布量は、２５ｇ／ｍ²
となった。(Recording Medium Used in Example 1) The following ink receiving layer components were mixed and adjusted so as to be an aqueous solution having a total solid content of 15% by weight, and the air permeability was 45 seconds / 100 c.
c. A film (thickness: 160 μm) was coated with the mixed aqueous solution, and a dryer (manufactured by Davai Spec Co., Ltd., PH-2)
(Type 01 oven) at 130 ° C. for 2 minutes. As a result, the coating amount of the ink receiving layer was 25 g / m ^2.
It became.

【００５１】 ・インク吸収顔料：シリカゲル Ｐ７８Ｄ（水澤化学工業株式会社の商品名） ６５重量％ ・インク定着剤：ジアリルジメチルアンモニウムクロライド−二酸化イオウコポ リマー ＰＡＳ−Ａ（日東紡績株式の商品名） １０重量％ ・バインダー：ポリビニルアルコール ＣＭ３１８（重合度１８００）（クラレ 株式会社の商品名） ２５重量％Ink absorbing pigment: Silica gel P78D (trade name of Mizusawa Chemical Industry Co., Ltd.) 65% by weight Ink fixing agent: diallyl dimethyl ammonium chloride-sulfur dioxide polymer PAS-A (trade name of Nitto Boseki Co., Ltd.) 10% by weight -Binder: polyvinyl alcohol CM318 (degree of polymerization 1800) (trade name of Kuraray Co., Ltd.) 25% by weight

【００５２】以下に、用いたフィルムの作製工程の成分
および配合比を、上述した工程毎に示す。 （工程１） ・超高分子量ポリエチレン：ハイモント１９００（ハイモント、ユー・エス・エ ー社の商品名） ４０重量％ ・熱可塑性の有機高分子：Ｌ−ＬＤＰＥペレット（三菱化学株式会社の商品名） １０重量％ ・シリカゲル：ミズカソーブＳ−０（水澤化学工業株式会社の商品名） ４０重量％ ・二酸化チタン：ＪＡ−１（テイカ株式会社の商品名） １０重量％ （工程２）工程１の混合物に対し５重量％の加工可塑剤
であるシェルフレックス（Ｓｈｅｌｌｆｌｅｘ）４１２
（シェルオイル社の商品名）を用いた。 （工程３）有機抽出液としては１，１，２−トリクロロ
エチレンを用いた。In the following, the components and the compounding ratios of the steps for producing the used film are shown for each of the above-mentioned steps. (Step 1)-Ultra high molecular weight polyethylene: Himont 1900 (trade name of Himont, USA) 40% by weight-Thermoplastic organic polymer: L-LDPE pellet (trade name of Mitsubishi Chemical Corporation) 10% by weight ・ Silica gel: Mizukasorb S-0 (trade name of Mizusawa Chemical Industry Co., Ltd.) 40% by weight ・ Titanium dioxide: JA-1 (trade name of Teica Co., Ltd.) 10% by weight (Step 2) To the mixture of Step 1 Shellflex 412, 5% by weight of the processing plasticizer
(Trade name of Shell Oil) was used. (Step 3) 1,1,2-Trichloroethylene was used as the organic extract.

【００５３】このようにして得た、透気性を有するフィ
ルム上にインク受容層が設けられた媒体のインク受容層
と反対側の面に、以下の溶媒吸収層成分となるように混
合・調整した総固形分濃度として２０重量％の水溶液を
塗布した。引き続き、乾燥機（ダバイエスペック株式会
社製、ＰＨ−２０１型オーブン）を用いて、１３０℃で
２分間乾燥させることで、溶媒吸収層の塗布量を８ｇ／
ｍ²とし、実施例１で用いる記録媒体を作製した。The medium having the ink-receiving layer provided on the air-permeable film thus obtained was mixed and adjusted so that the following solvent-absorbing layer components were formed on the surface opposite to the ink-receiving layer. An aqueous solution having a total solid content of 20% by weight was applied. Subsequently, it was dried at 130 ° C. for 2 minutes using a drier (manufactured by Davai Spec Co., Ltd., PH-201 type oven), so that the coating amount of the solvent absorbing layer was 8 g /.
m ^2, and the recording medium used in Example 1 was produced.

【００５４】 ・溶媒吸収層剤：フローライトＲ（株式会社トクヤマの商品名） ８０重量％ （吸油度４００〜５００ｍｌ／１００ｇ（ＪＩＳ−Ｋ６２２０）） ・アクリル樹脂：ボンロンＳ４１９（三井化学株式会社の商品名 ２０重量％Solvent absorbing layer agent: FLORITE R (trade name of Tokuyama Corporation) 80% by weight (oil absorption 400 to 500 ml / 100 g (JIS-K6220)) Acrylic resin: Bonron S419 (a product of Mitsui Chemicals, Inc.) 20% by weight

【００５５】（比較例１で用いる記録媒体）フィルム作
製方法の工程１の成分を下記組成に代える以外は実施例
１と同様の操作を行い、実質的に透気性を有さない（透
気度１００００秒以上／１００ｃｃの）フィルムを作製
した（厚さ：１６０μｍ）。このフィルム上へのインク
受容層および溶媒吸収層の塗工は実施例１と全く同様で
ある。なお記録媒体全体の透気度も、ＪＩＳ−Ｐ８１１
７に準じた測定の結果、１００００秒以上／１００ｃｃ
であった。(Recording Medium Used in Comparative Example 1) The same operation as in Example 1 was carried out except that the components in step 1 of the film production method were changed to the following compositions, and the film had substantially no air permeability (air permeability) A film (of 10,000 seconds or more / 100 cc) was prepared (thickness: 160 μm). The coating of the ink receiving layer and the solvent absorbing layer on this film is exactly the same as in Example 1. The air permeability of the entire recording medium is also JIS-P811
As a result of measurement according to 7, 10,000 seconds or more / 100 cc
Met.

【００５６】 （工程１） ・超高分子量ポリエチレン：ハイモント１９００（ハイモント、ユー・エス・エ ー社の商品名） ５０重量％ ・熱可塑性の有機高分子：Ｌ−ＬＤＰＥペレット（三菱化学株式会社の商品名） ４０重量％ ・シリカゲル：ミズカソーブＳ−０（水澤化学工業株式会社の商品名） １０重量％(Step 1) Ultra-high molecular weight polyethylene: 50% by weight of Himont 1900 (trade name of Himont, USA) Thermoplastic organic polymer: L-LDPE pellet (Mitsubishi Chemical Corporation) Silica gel: Mizukasorb S-0 (trade name of Mizusawa Chemical Industry Co., Ltd.) 10% by weight

【００５７】（比較例２で用いる記録媒体）溶媒吸収層
を設けなかった以外は、実施例１と同様の操作により、
比較例２で用いる記録媒体を得た。この記録媒体全体の
透気度は、ＪＩＳ−Ｐ８１１７に準じた測定の結果、７
５秒／１００ｃｃであった。(Recording Medium Used in Comparative Example 2) The same operation as in Example 1 was performed except that the solvent absorbing layer was not provided.
A recording medium used in Comparative Example 2 was obtained. As a result of measurement according to JIS-P8117, the air permeability of the entire recording medium was 7
It was 5 seconds / 100 cc.

【００５８】（１）画像の鮮明性試験 また、上記実施例及び比較例で得られた記録媒体（サン
プル）を用いて、セイコーエプソン製のインクジェット
プリンタＰＭ−７７０Ｃにより印刷を行ない、高精細カ
ラーデジタル標準画像データ（ＩＳＯ／ＪＩＳ−ＳＣＩ
Ｄ）の画像名称ポートレート（サンプル番号１、画像の
識別番号Ｎ１）を印刷し、画像の鮮明性を目視により下
記のように評価した。 鮮やかに画像が再現されている：Ａ 画像が不鮮明である ：Ｂ(1) Image sharpness test Further, using the recording media (samples) obtained in the above Examples and Comparative Examples, printing was performed by an inkjet printer PM-770C manufactured by Seiko Epson, and a high-definition color digital Standard image data (ISO / JIS-SCI
The image name portrait (sample number 1, image identification number N1) of D) was printed, and the sharpness of the image was visually evaluated as follows. The image is reproduced vividly: A The image is unclear: B

【００５９】（２）画像の耐光性試験 上記（１）で得られた画像を用い、キセノンフェードメ
ーター（ＣＩ３５Ａ）を用いて、１００時間の加速試験
を行った。試験前後のポートレート画像の背景（グレー
色）とブルー色の色差ΔＥを、ＪＩＳ−Ｚ８７３０で規
定された方法に基づき測定し、下記のように評価した。 色差が５未満 ：Ａ 色差が５〜１０ ：Ｂ 色差が１０を超える：Ｃ(2) Light fastness test of image Using the image obtained in the above (1), an acceleration test for 100 hours was performed using a xenon fade meter (CI35A). The color difference ΔE between the background (gray color) of the portrait image before and after the test and the blue color was measured based on the method specified in JIS-Z8730, and evaluated as follows. Color difference is less than 5: A Color difference is 5 to 10: B Color difference is more than 10: C

【００６０】（３）画像の耐湿性試験 画像の耐湿性は、上記実施例及び比較例で得られた記録
媒体（サンプル）を用いて、セイコーエプソン製のイン
クジェットプリンタＰＭ−７７０Ｃにより、図１に示す
ような、０．５ｍｍスペースの十字白抜きのべたをパタ
ーンとし、このパターンがＫＣＭＹＲＧＢ各色において
隣接するように並んだパッチの印刷を行い、乾燥させ
た。得られた記録物を、４０℃、８５％湿度で７２時間
の条件下で、曝し、十字白抜き部分の幅の狭まり程度を
観察し、下記のように評価した。 ０．５ｍｍスペースが確認でき、滲まなかった ：Ａ ０．４５ｍｍ以上のスペースとなった ：Ｂ ０．４５ｍｍ未満のスペースとなった ：Ｃ 以上の画像の鮮明性試験、耐光性試験および耐湿性試験
の試験結果を表１に示す。(3) Moisture Resistance Test of Image The moisture resistance of the image was measured using the recording medium (sample) obtained in the above Examples and Comparative Examples by an inkjet printer PM-770C manufactured by Seiko Epson as shown in FIG. As shown in the figure, a solid pattern of a white cross in a 0.5 mm space was used as a pattern, and a patch in which the pattern was adjacent to each other in KCMYRGB was printed and dried. The obtained recorded matter was exposed under the condition of 40 ° C. and 85% humidity for 72 hours, and the degree of narrowing of the white cross portion was observed and evaluated as follows. A space of 0.5 mm was confirmed and did not bleed: A became a space of 0.45 mm or more: B became a space of less than 0.45 mm: C The sharpness test, light resistance test, and moisture resistance test of an image of not less than C Table 1 shows the test results.

【００６１】[0061]

【表１】 [Table 1]

【００６２】本発明に係る記録媒体（実施例１）を用い
た場合は、鮮明性試験における画像は、鮮やかに再現さ
れ、耐光性も良好であった。さらに画像の耐湿性が良
く、隣接するパッチ間での“にじみ”や白地への“滲み
出し”は確認されなかった。比較例１および比較例２の
記録媒体を用いた場合は、鮮明性試験における画像は、
鮮やかに再現されたものの、十分な耐光性を得ることは
できなかった。また、隣接するパッチ間での“にじみ”
や白地への“滲み出し”も確認され、画像の耐湿性にも
不具合が生じた。When the recording medium according to the present invention (Example 1) was used, the image in the sharpness test was reproduced vividly and the light resistance was good. Furthermore, the image had good moisture resistance, and no "bleeding" between adjacent patches or "bleeding out" to a white background was observed. When the recording media of Comparative Example 1 and Comparative Example 2 were used, the image in the sharpness test was
Although reproduced vividly, sufficient lightfastness could not be obtained. Also, "bleeding" between adjacent patches
Also, "bleeding out" to a white background was confirmed, and a problem occurred in the moisture resistance of the image.

【００６３】[0063]

【発明の効果】本発明に係るインクジェット用記録媒体
によれば、透気性を有するフィルムの一方側の面に溶媒
吸収層が設けられ、該透気性を有するフィルムの他方側
の面にインク受容層が設けられているので、着色剤、有
機溶媒を含有する一般的なインクジェット用水性インク
を用いた場合、インク中の有機溶媒がインク受容層から
ほとんど除去される。その結果、着色剤がインク受容層
に定着することにより高画質な画像が得られるだけでな
く、有機溶媒が高湿度下で水分を吸収し着色剤を再溶解
することがないので、高湿度下でも画像の滲みが生じ
ず、また、光による着色剤の劣化も起こりにくいものと
なった。よって、フィルムをベースシートとするインク
ジェット用記録媒体において、高画質、高耐湿性および
高耐光性を有する画像を得ることのできるインクジェッ
ト用記録媒体を提供することができた（請求項１）。According to the ink jet recording medium of the present invention, the solvent-absorbing layer is provided on one surface of the air-permeable film, and the ink-receiving layer is provided on the other surface of the air-permeable film. Is provided, the organic solvent in the ink is almost completely removed from the ink receiving layer when a general aqueous inkjet ink containing a colorant and an organic solvent is used. As a result, not only can a high-quality image be obtained by fixing the colorant to the ink receiving layer, but also the organic solvent does not absorb water under high humidity and does not redissolve the colorant, so that under high humidity, However, no bleeding of the image occurred and the colorant hardly deteriorated by light. Accordingly, an inkjet recording medium capable of obtaining an image having high image quality, high moisture resistance, and high light resistance in an inkjet recording medium using a film as a base sheet can be provided (claim 1).

【００６４】本発明のインクジェット用記録媒体によれ
ば、上記フィルムの透気度が、ＪＩＳ−Ｐ８１１７で規
定されている透気度で５０秒／１００ｃｃ以下であり、
インク中の有機溶媒を、効率良くフィルムへ移動させる
ことができ、画像の滲み、および光による着色剤の劣化
をより確実に抑制できるので、特に高耐湿性および高耐
光性を有する画像を得ることのできるインクジェット用
記録媒体を提供することができた（請求項２）。According to the ink jet recording medium of the present invention, the air permeability of the film is 50 seconds / 100 cc or less in air permeability specified in JIS-P8117,
The organic solvent in the ink can be efficiently transferred to the film, and blurring of the image and deterioration of the colorant due to light can be more reliably suppressed, so that an image having particularly high moisture resistance and high light resistance is obtained. Thus, it was possible to provide an ink jet recording medium capable of performing the following (claim 2).

【００６５】本発明のインクジェット用記録媒体によれ
ば、溶媒吸収層の吸油度が、ＪＩＳ−Ｋ６２２０で規定
されている吸油度で３２０ｍｌ／１００ｇ以上であり、
インク中の有機溶媒を、溶媒吸収層に確実に吸収させる
ことができるので、特に高耐湿性および高耐光性を有す
る画像を得ることのできるインクジェット用記録媒体を
提供することができた（請求項３）。According to the ink jet recording medium of the present invention, the solvent absorption layer has an oil absorption of 320 ml / 100 g or more as defined by JIS-K6220.
Since the organic solvent in the ink can be surely absorbed by the solvent absorbing layer, it was possible to provide an inkjet recording medium capable of obtaining an image having particularly high moisture resistance and high light resistance. 3).

【００６６】本発明に係るインクジェット用記録媒体に
よれば、溶媒吸収層が、非常に高い吸油度を有する花弁
状結晶構造を有する珪酸カルシウムを含有し、インク中
の有機溶媒を、溶媒吸収層に確実に吸収させることがで
きるので、特に高耐湿性および高耐光性を有する画像を
得ることのできるインクジェット用記録媒体を提供する
ことができた（請求項４）。According to the ink jet recording medium of the present invention, the solvent absorbing layer contains calcium silicate having a petal-like crystal structure having a very high oil absorption, and the organic solvent in the ink is added to the solvent absorbing layer. Since it is possible to reliably absorb the ink, it was possible to provide an ink jet recording medium capable of obtaining an image having particularly high moisture resistance and high light resistance (claim 4).

【００６７】本発明に係るインクジェット用記録媒体に
よれば、溶媒吸収層が、溶媒吸収剤を含有し、溶媒吸収
剤の含有割合が、溶媒吸収層に対して２０重量％〜１０
０重量％であり、インク中の有機溶媒を、溶媒吸収層に
確実に吸収させることができるので、特に高耐湿性およ
び高耐光性を有する画像を得ることのできるインクジェ
ット用記録媒体を提供することができた（請求項５）。According to the ink jet recording medium of the present invention, the solvent absorbing layer contains the solvent absorbing agent, and the content of the solvent absorbing agent is from 20% by weight to 10% by weight based on the solvent absorbing layer.
0% by weight, and the organic solvent in the ink can be surely absorbed by the solvent absorbing layer, so that an ink jet recording medium capable of obtaining an image having particularly high moisture resistance and high light resistance is provided. (Claim 5).

【００６８】本発明に係るインクジェット用記録媒体に
よれば、上記インクジェット用記録媒体の透気度が、Ｊ
ＩＳ−Ｐ８１１７で規定されている透気度で１００秒／
１００ｃｃ以下であるので、記録媒体の厚さによらず、
インク中の有機溶媒を、フィルムを経由させて溶媒吸収
層に確実に吸収させることができるインクジェット用記
録媒体を提供することができた（請求項６）。According to the ink jet recording medium of the present invention, the air permeability of the ink jet recording medium is J
100 seconds / with air permeability specified by IS-P8117
Because it is 100 cc or less, regardless of the thickness of the recording medium,
It was possible to provide an inkjet recording medium capable of reliably absorbing the organic solvent in the ink into the solvent absorbing layer via the film (claim 6).

【００６９】本発明に係る記録方法によれば、上記のイ
ンクジェット用記録媒体のインク受容層に、着色剤およ
び有機溶媒を含有する一般的なインクジェット用水性イ
ンクを付着させることにより、着色剤をインク受容層内
に定着させるとともに、さらにインク中の有機溶媒をイ
ンク受容層の表面から揮発させるだけでなく、フィルム
を経由させて溶媒吸収層に吸収させることにより、有機
溶媒をインク受容層内からほとんど除去できるので、高
画質、高耐湿性および高耐光性を有する画像を得ること
のできるインクジェット用記録媒体の記録方法を提供す
ることができた（請求項７）。According to the recording method of the present invention, the colorant is added to the ink-receiving layer of the above-described ink-jet recording medium by attaching a general aqueous ink-jet ink containing a colorant and an organic solvent. In addition to fixing the organic solvent in the receiving layer, the organic solvent in the ink is not only volatilized from the surface of the ink receiving layer, but also absorbed into the solvent absorbing layer via a film, so that the organic solvent is almost completely removed from the ink receiving layer. Since it can be removed, it was possible to provide a recording method for an inkjet recording medium capable of obtaining an image having high image quality, high moisture resistance and high light resistance (claim 7).

【００７０】本発明に係る記録物によれば、上記のイン
クジェット用記録媒体に、着色剤および有機溶媒を含有
する一般的なインクジェット用水性インクを付着させる
ことで、着色剤がインク受容層に定着されるとともに有
機溶媒がほとんど除去されるので、高画質、高耐湿性お
よび高耐光性の画像を有する記録物を提供することがで
きた（請求項８）。According to the recorded matter of the present invention, the colorant is fixed to the ink receiving layer by adhering a general aqueous ink jet ink containing a colorant and an organic solvent to the above-mentioned ink jet recording medium. In addition, the organic solvent was almost completely removed, so that a recorded matter having an image with high image quality, high moisture resistance and high light resistance could be provided (claim 8).

【図面の簡単な説明】[Brief description of the drawings]

【図１】画像の耐湿性を測定するための、０．５ｍｍス
ペースの十字白抜きのベタ印刷を表す図である。FIG. 1 is a diagram illustrating a solid print with a white cross in a 0.5 mm space for measuring the moisture resistance of an image.

Claims (8)

【特許請求の範囲】[Claims] 【請求項１】 透気性を有するフィルムの一方側の面に
溶媒吸収層が設けられ、該透気性を有するフィルムの他
方側の面にインク受容層が設けられたことを特徴とする
インクジェット用記録媒体。1. An ink jet recording apparatus comprising: a solvent-absorbing layer provided on one surface of a gas-permeable film; and an ink-receiving layer provided on the other surface of the gas-permeable film. Medium. 【請求項２】 上記フィルムの透気度が、ＪＩＳ−Ｐ８
１１７で規定されている透気度で５０秒／１００ｃｃ以
下であることを特徴とする請求項１に記載のインクジェ
ット用記録媒体。2. The air permeability of the film is JIS-P8.
2. The ink jet recording medium according to claim 1, wherein the air permeability specified in 117 is 50 seconds / 100 cc or less. 【請求項３】 上記溶媒吸収層の吸油度が、ＪＩＳ−Ｋ
６２２０で規定されている吸油度で３２０ｍｌ／１００
ｇ以上であることを特徴とする請求項１または２に記載
のインクジェット用記録媒体。3. The method according to claim 1, wherein the solvent absorption layer has an oil absorption degree of JIS-K.
320ml / 100 at oil absorption specified in 6220
3. The recording medium for ink jet according to claim 1, wherein the recording medium is not less than g. 【請求項４】 上記溶媒吸収層が、花弁状結晶構造を有
する珪酸カルシウムを含有することを特徴とする請求項
１〜３のいずれかに記載のインクジェット用記録媒体。4. The ink jet recording medium according to claim 1, wherein said solvent absorbing layer contains calcium silicate having a petal-like crystal structure. 【請求項５】 上記溶媒吸収層が、溶媒吸収剤を含有
し、該溶媒吸収剤の含有割合が、該溶媒吸収層に対して
２０重量％〜１００重量％であることを特徴とする請求
項１〜４のいずれかに記載のインクジェット用記録媒
体。5. The solvent absorbing layer according to claim 1, wherein the solvent absorbing layer contains a solvent absorbing agent, and the content of the solvent absorbing agent is 20% by weight to 100% by weight based on the solvent absorbing layer. 5. The recording medium for inkjet according to any one of 1 to 4. 【請求項６】 請求項１〜５のいずれかに記載のインク
ジェット用記録媒体の透気度が、ＪＩＳ−Ｐ８１１７で
規定されている透気度で１００秒／１００ｃｃ以下であ
ることを特徴とするインクジェット用記録媒体。6. The air permeability of the ink jet recording medium according to any one of claims 1 to 5, which is 100 seconds / 100 cc or less in terms of air permeability specified in JIS-P8117. Recording media for inkjet. 【請求項７】 請求項１〜６のいずれかに記載のインク
ジェット用記録媒体のインク受容層にインクジェット用
インクを付着させ、該インクジェット用インク中の有機
溶媒を上記フィルムを経由させて上記溶媒吸収層に吸収
させることを特徴とする記録方法。7. An ink jet ink is attached to the ink receiving layer of the ink jet recording medium according to claim 1, and an organic solvent in the ink jet ink is passed through the film to absorb the solvent. A recording method characterized in that the layer is absorbed by a layer. 【請求項８】 請求項１〜６のいずれかに記載のインク
ジェット用記録媒体にインクジェット用インクを付着さ
せることで記録された記録物。8. A recorded matter recorded by attaching an ink-jet ink to the ink-jet recording medium according to claim 1.