JP2001087614A - Air cleaning filter - Google Patents
Air cleaning filterInfo
- Publication number
- JP2001087614A JP2001087614A JP26878699A JP26878699A JP2001087614A JP 2001087614 A JP2001087614 A JP 2001087614A JP 26878699 A JP26878699 A JP 26878699A JP 26878699 A JP26878699 A JP 26878699A JP 2001087614 A JP2001087614 A JP 2001087614A
- Authority
- JP
- Japan
- Prior art keywords
- filter
- air
- preparation example
- electret
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、空気清浄化フィル
ターに関し、詳しくは通気性に優れた片面段ボール形状
の空気清浄化フィルターに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an air purifying filter, and more particularly to a single-sided cardboard-shaped air purifying filter having excellent air permeability.
【０００２】[0002]
【従来の技術】近年、生活環境の変化や健康志向の高ま
りなどにより、家庭や職場において空気清浄化装置の普
及が進んでいる。最近では専用の空気清浄機のみなら
ず、ルームエアコンや除湿器、加湿器などの各種空調機
器に空気清浄化機能が付与される傾向があり、実用化さ
れているものがある。2. Description of the Related Art In recent years, air purifiers have been widely used in homes and workplaces due to changes in living environment and heightened health consciousness. In recent years, not only dedicated air purifiers but also various air conditioners such as room air conditioners, dehumidifiers, and humidifiers tend to be provided with an air purifying function, and some of them have been put to practical use.
【０００３】種々の空気清浄化法の中でもフィルターを
用いるものは特殊な装置や部品を必要とせず、比較的簡
易に実施可能であるため、家庭用の空調機器などを中心
として空気清浄化フィルターが広く汎用されている。[0003] Among the various air cleaning methods, those using a filter do not require special equipment or parts and can be implemented relatively easily. Therefore, air cleaning filters are mainly used for home air conditioners and the like. It is widely used.
【０００４】空気清浄を専らとしないルームエアコン、
除湿器および加湿器などの機器においては、空気清浄化
フィルターを搭載するための空間を広く取ることが困難
な場合があり、山の高さが数ミリから十数ミリ程度のミ
ニプリーツフィルターが特に有用である。このようなミ
ニプリーツフィルターは、単板で使用した場合と比較し
て、強度が増して取り扱い性が良くなるものの、濾材面
積が増加する割には通気性が向上し難く、逆に低下する
場合もあり、改良が求められていた。[0004] Room air conditioners that do not exclusively purify air,
In equipment such as dehumidifiers and humidifiers, it may be difficult to provide a large space for installing an air purification filter, and mini-pleated filters with a mountain height of about several to several tens of millimeters are particularly suitable. Useful. Compared to the case of using a single plate, such a mini-pleated filter has increased strength and improved handleability, but it is difficult to improve the air permeability for the increase in the area of the filter medium, and conversely, when it decreases. There was a need for improvement.
【０００５】[0005]
【発明が解決しようとする課題】本発明の課題は、コン
パクトで各種装置への搭載が可能であり、適度な強度を
有して取り扱い性が良く、且つ通気性に優れた空気清浄
化フィルターを提供することである。SUMMARY OF THE INVENTION An object of the present invention is to provide an air purifying filter which is compact, can be mounted on various devices, has appropriate strength, is easy to handle, and has excellent air permeability. To provide.
【０００６】[0006]
【課題を解決するための手段】本発明者らは上記課題を
解決すべく鋭意検討の結果、下記の発明を完成するに至
った。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, have completed the following invention.
【０００７】（１）ＪＩＳ−Ｚ−１５１６に記載の「外
装用段ボール」に準拠して、空気清浄化機能を有するフ
ィルターを中しん、および通気性を有する基材をライナ
に用いて作製してなる片面段ボール形状の空気清浄化フ
ィルター。(1) In accordance with JIS-Z-1516, "corrugated cardboard for exterior", a filter having an air-cleaning function is used as a middle layer, and a base material having air permeability is produced using a liner. A single-sided cardboard-shaped air purification filter.
【０００８】（２）上記の発明（１）において、中しん
とするフィルターが少なくとも除塵性を有することを特
徴とする空気清浄化フィルター。(2) The air purifying filter according to the above invention (1), wherein the filter to be used for removing the air has at least a dust removing property.
【０００９】（３）上記の発明（１）または（２）にお
いて、中しんとするフィルターがエレクトレットを含有
することを特徴とする空気清浄化フィルター。(3) The air purifying filter according to the above invention (1) or (2), wherein the filter to be sewn contains an electret.
【００１０】[0010]
【発明の実施の形態】本発明の空気清浄化フィルター
は、空気清浄化機能を有するフィルターを中しん、およ
び通気性を有する基材をライナに用いて作製してなる片
面段ボール形状の空気清浄化フィルターであり、優れた
空気清浄化機能に加えて、高い通気性および望ましい取
り扱い性をを有するものである。BEST MODE FOR CARRYING OUT THE INVENTION The air purifying filter of the present invention is a single-sided corrugated cardboard-shaped air purifying filter prepared by using a filter having an air purifying function as a filler and a substrate having air permeability as a liner. It is a filter having high air permeability and desirable handling properties in addition to excellent air purifying function.
【００１１】本発明に係わる片面段ボールとは、ＪＩＳ
−Ｚ−１５１６に記載の「外装用段ボール」に準拠して
１枚のライナに波形状に加工した中しんを貼り合わせて
作製される。The single-sided cardboard according to the present invention is defined by JIS
It is manufactured by attaching a corrugated shin to a single liner according to the “exterior cardboard” described in -Z-1516.
【００１２】本発明に係わる中しんの波形状は、一般的
な正弦波または疑似正弦波の他、海波、三角波、方形
波、半円や扇形の弧がつながった波などの波形であって
も良く、特に限定されるものではないが、角の無いなめ
らかな曲線を描く形状が好ましく、高い通気性が得られ
る。これは、折り曲げた角、特に鋭利な角があると、角
の部分でフィルター濾材が厚密化して通気性が低下する
とともに、角付近ではフィルター濾材同士が接近してい
て通気できる間隔が狭いため、通気抵抗が大きくなり、
通気性が阻害される原因となるからである。The wave form of the shin according to the present invention is not only a general sine wave or a pseudo sine wave, but also a sea wave, a triangular wave, a square wave, a wave formed by connecting semicircular or fan-shaped arcs, and the like. The shape is not particularly limited, but a shape with a smooth curve with no corners is preferable, and high air permeability can be obtained. This is because if there are bent corners, especially sharp corners, the filter media becomes thicker at the corners and the air permeability decreases, and near the corners, the filter media are close to each other and the space for ventilation is narrow, so , The ventilation resistance increases,
This is because air permeability may be impaired.
【００１３】単位長さのライナに対する中しんの使用長
さ比率、すなわち段繰り率は特に限定されるものではな
いが、１．２〜２．０であることが好ましく、１．４〜
１．７であることが更に好ましい。[0013] The ratio of the length of the inner blank to the unit length of the liner, that is, the step repetition rate is not particularly limited, but is preferably 1.2 to 2.0, preferably 1.4 to 2.0.
More preferably, it is 1.7.
【００１４】本発明に係わる片面段ボールを作製する際
の接着剤は特に限定されるものではなく、澱粉系接着
剤、エチレン酢酸ビニル共重合体などのポリ酢酸ビニル
系接着剤、ポリビニルアルコール系接着剤または湿気硬
化型ウレタン系接着剤などを挙げることができる。中で
も、湿気硬化型ウレタン系接着剤は、低温で使用でき、
耐熱性が高く、耐水性に優れ、且つ各種材料との接着性
が良好であり、優位に用いられる。また、ライナまたは
中しんが熱可塑性または圧着性などの接着性を有する場
合には、所望に応じて接着剤を使用しなくても良い。The adhesive for producing the single-faced corrugated cardboard according to the present invention is not particularly limited, and is a starch-based adhesive, a polyvinyl acetate-based adhesive such as an ethylene-vinyl acetate copolymer, or a polyvinyl alcohol-based adhesive. Alternatively, a moisture-curable urethane-based adhesive can be used. Above all, moisture-curable urethane-based adhesives can be used at low temperatures,
It has high heat resistance, excellent water resistance, and good adhesion to various materials, and is used advantageously. In addition, when the liner or the middle binder has an adhesive property such as thermoplasticity or pressure bonding property, an adhesive may not be used as required.
【００１５】本発明に係わる空気清浄化機能を有するフ
ィルターとは、除塵、脱臭、有害物質除去、抗菌、防
黴、抗ウィルスなどを目的に用いられるフィルターであ
り、これらの空気清浄化機能を少なくとも一つ以上有す
るものである。The filter having an air purifying function according to the present invention is a filter used for dust removal, deodorization, removal of harmful substances, antibacterial, antifungal, antivirus, etc. It has one or more.
【００１６】本発明に係わる中しんに用いる空気清浄化
機能を有するフィルターは、除塵性を有することが好ま
しく、除塵法として濾過集塵または静電気力集塵などを
用いることができる。中でも、本発明に係わる中しんに
用いる空気清浄化機能を有するフィルターはエレクトレ
ットを含有することが好ましい。The filter having an air purifying function used for the inner lining according to the present invention preferably has a dust-removing property. As a dust-removing method, filtration dust collection, electrostatic dust collection or the like can be used. Especially, it is preferable that the filter having the air cleaning function used for the inner lining according to the present invention contains an electret.
【００１７】本発明に係わるエレクトレットとは、半永
久的に電気分極を保持し、外部に対して電気力を及ぼす
素材であって、その静電気力によって粒子を捕捉するも
のである。帯電方法としては、エレクトロエレクトレッ
ト、熱エレクトレット、ラジオエレクトレット、メカノ
エレクトレット、フォトエレクトレット、マグネットエ
レクトレットなどが挙げられるが、工業的に不織布フィ
ルターで用いられているものは、主にエレクトロエレク
トレットおよび熱エレクトレットであり、フィルター材
料としてはポリプロピレンまたはプロピレン主体の共重
合体が用いられることが多く、脂肪酸金属塩などが添加
される場合がある。The electret according to the present invention is a material that retains electric polarization semipermanently and applies an electric force to the outside, and captures particles by the electrostatic force. Examples of the charging method include an electro-electret, a heat electret, a radio-electret, a mechano-electret, a photo-electret, a magnet-electret, and the like, and those used industrially in a nonwoven fabric filter are mainly an electro-electret and a heat-electret. As a filter material, polypropylene or a propylene-based copolymer is often used, and a fatty acid metal salt or the like may be added.
【００１８】不織布をエレクトレット化すると、嵩高で
３次元空隙が存在するため、コロナ放電などによる帯電
処理では安定した帯電効果を得ることが難しい場合があ
り、コロナ放電などで帯電処理を施したフィルムを繊維
状に断裁、それを不織布化したスプリットファイバーエ
レクトレットフィルターや、メルトブロー紡糸時および
溶融紡糸時に高電圧を印加して熱エレクトレット的に繊
維を帯電させたメルトブロー不織布式エレクトレットフ
ィルターおよびスパンボンド不織布式エレクトレットフ
ィルターなどは、安定した分極電荷を得ることができ、
好ましい。なお、メルトブロー不織布式エレクトレット
フィルターなどは単体では力学的強度が小さいため、主
にプリーツ適性を付与するためのバックアップ材または
カバー材やスクリーム材などの補強材として、乾式不織
布、スパンボンドまたはネットなどを貼り合わせるなど
して使用される場合がある。When the nonwoven fabric is electretized, it is difficult to obtain a stable charging effect by charging treatment by corona discharge or the like because of the bulkiness and three-dimensional voids. A split fiber electret filter that cuts into a fibrous form and turns it into a nonwoven fabric, or a meltblown nonwoven fabric electret filter and a spunbond nonwoven fabric electret filter in which a high voltage is applied during meltblowing and melt spinning to charge the fibers as heat electret Can obtain a stable polarization charge,
preferable. In addition, since the mechanical strength of a melt blown nonwoven fabric type electret filter etc. is small by itself, a dry nonwoven fabric, spunbond or net etc. is mainly used as a backing material to give pleating suitability or a reinforcing material such as a cover material or a scream material. It is sometimes used by pasting together.
【００１９】本発明においても、中しんとして段成形の
適性を付与するためにこれらの補強材を用いることがで
き、このような補強材は脱臭または抗菌などの空気清浄
化機能を有しても良い。In the present invention, these reinforcing materials can also be used for imparting the suitability of step forming as a middle lining, and such reinforcing materials can have an air purifying function such as deodorization or antibacterial. good.
【００２０】本発明に係わる除塵性を有するフィルター
は、０．３μｍの粒子に対して９９．９７％以上の捕集
効率を有するＨＥＰＡフィルターや０．１μｍの粒子に
対して９９．９９９７％以上の捕集効率を有するＵＬＰ
Ａフィルターであっても良い。ＨＥＰＡフィルターは重
量比で９５％以上のガラス繊維と５％以下のバインダー
から構成されているのが通例であり、ガラス繊維はが１
〜３ｍｍ程度、平均直径が０．７μｍで太さのバラツキ
が大きい極細ガラス繊維と直径６〜１０μｍで太さが一
様、長さが５ｍｍ以上のチョップ繊維からなるものが多
いが、特にこれに限定されるものではなく、セラミック
繊維やセルロース繊維、ポリプロピレン等のポリオレフ
ィン繊維、ポリエステル繊維またはアラミド繊維などの
有機繊維からなるものであっても良い。The filter having a dust-removing property according to the present invention is a HEPA filter having a collection efficiency of 99.97% or more for 0.3 μm particles or 99.9997% or more for 0.1 μm particles. ULP with high collection efficiency
An A filter may be used. The HEPA filter is usually composed of 95% or more by weight of glass fiber and 5% or less of a binder.
Approximately 3 mm, the average diameter is 0.7 μm, and the variation in thickness is very fine glass fiber, and the diameter is 6 to 10 μm, the thickness is uniform, and the length is 5 mm or more. The material is not limited, and may be made of ceramic fibers, cellulose fibers, polyolefin fibers such as polypropylene, or organic fibers such as polyester fibers or aramid fibers.
【００２１】本発明に係わる空気清浄化機能を有するフ
ィルターに、脱臭、有害物質除去、抗菌、防黴、抗ウィ
ルスなどの機能を付与する場合には、脱臭剤や抗菌剤な
どの薬品を用いることができる。When the filter having an air purifying function according to the present invention is provided with functions such as deodorization, harmful substance removal, antibacterial, antifungal, and antiviral, chemicals such as a deodorant and an antibacterial agent are used. Can be.
【００２２】本発明に用いられる脱臭剤とは、主に悪臭
を除去する目的で用いられる薬剤であり、具体的には活
性炭、添着活性炭、活性炭素繊維、天然および合成ゼオ
ライト、ハイシリカゼオライト、シリカ、活性アルミ
ナ、活性白土、セピオライト、有機酸系化合物またはイ
オン交換樹脂などの吸着剤、鉄アスコルビン酸や鉄、コ
バルトまたはマンガン等の金属フタロシアニン誘導体な
どの酵素系脱臭剤、酸化チタンや酸化亜鉛などの光触
媒、マンガン系酸化物やペロブスカイト型触媒などの低
温酸化触媒、炭化珪素、窒化珪素、珪酸カルシウム、ア
ルミナ・シリカ系、ジルコニア系などの合成セラミクス
や麦飯石、フェルソング石などの遠赤外線セラミクス、
植物抽出成分に含まれる化合物であるカテキン、タンニ
ン、フラボノイド等を用いた消臭剤などが挙げられる。
これらの脱臭剤は必要に応じて複数のものを併用しても
良く、また、これらの脱臭剤を複合化したハイブリット
脱臭剤としても良い。The deodorizing agent used in the present invention is a chemical used mainly for the purpose of removing offensive odors. Specifically, activated carbon, impregnated activated carbon, activated carbon fiber, natural and synthetic zeolites, high silica zeolites, silica Adsorbents such as activated alumina, activated clay, sepiolite, organic acid compounds or ion exchange resins, enzymatic deodorants such as iron ascorbic acid and metal phthalocyanine derivatives such as iron, cobalt and manganese; titanium oxide and zinc oxide Photocatalysts, low-temperature oxidation catalysts such as manganese-based oxides and perovskite catalysts, synthetic ceramics such as silicon carbide, silicon nitride, calcium silicate, alumina-silica, and zirconia, and far-infrared ceramics such as maltstone and felsongite;
Deodorants using catechins, tannins, flavonoids, and the like, which are compounds contained in plant extract components, are exemplified.
If necessary, a plurality of these deodorants may be used in combination, or a hybrid deodorant obtained by combining these deodorants may be used.
【００２３】本発明に用いられる抗菌剤は、細菌、黴類
またはウイルスなどの有害微生物および病原体の除去、
殺滅、失活または繁殖抑制などの目的で用いられる薬剤
であり、具体的には、銀や亜鉛または燐酸カルシウムな
どを主成分とする無機系抗菌剤、ベンツイミダゾール
系、イソチアゾリン系、ピリチオン系、有機ヒ素系、有
機銅系、有機ヨード系、クロロヘキシジン系などの有機
系抗菌剤、キチンやキトサンなどの高分子系抗菌剤、茶
や柿などから抽出されるカテキンや孟宋竹抽出エキス、
ヒノキチオールなどの天然物由来の抗菌剤およびこれら
を複合したハイブリット抗菌剤などが挙げられる。The antibacterial agent used in the present invention can remove harmful microorganisms such as bacteria, fungi or viruses and pathogens,
It is a drug used for the purpose of killing, inactivating or suppressing reproduction, specifically, an inorganic antibacterial agent containing silver, zinc or calcium phosphate as a main component, benzimidazole, isothiazoline, pyrithione, Organic arsenic-based, organic copper-based, organic iodine-based, chlorohexidine-based organic antibacterial agents, chitin and chitosan-based polymer antibacterial agents, catechin and Meng Song bamboo extract extracted from tea and persimmon,
An antibacterial agent derived from a natural product such as hinokitiol, and a hybrid antibacterial agent obtained by combining these agents are exemplified.
【００２４】本発明に用いられる抗菌剤はハイブリット
抗菌剤の中でも上記した有機系抗菌剤の抗菌性金属塩で
あることが好ましく、中でもメルカプトピリジン−Ｎ−
オキシド化合物の銀塩、銅塩または亜鉛塩を主成分とす
ることが特に好ましい。この抗菌剤は、主に該金属塩に
由来する細菌類に対する抗菌性および主にメルカプトピ
リジン−Ｎ−オキシド化合物に由来する黴類に対する防
黴性を併せ持つため広範囲な細菌、黴類などの有害微生
物に対して有効な抗菌防黴作用が得られ、さらに高速度
且つ大容量で有効期間が長く、非常に優れた抗菌防黴性
を付与することが可能である。従って、本発明に係わる
抗菌剤として特に有用である。The antibacterial agent used in the present invention is preferably the above-mentioned antibacterial metal salt of the organic antibacterial agent among the hybrid antibacterial agents, and in particular, mercaptopyridine-N-
It is particularly preferable to use a silver salt, a copper salt or a zinc salt of an oxide compound as a main component. Since this antibacterial agent has both antibacterial properties against bacteria derived from the metal salt and fungicidal properties against fungi derived mainly from mercaptopyridine-N-oxide compound, it has a wide range of harmful microorganisms such as bacteria and molds. An effective antibacterial and fungicidal action can be obtained, and a high speed, a large capacity, a long effective period, and very excellent antibacterial and fungicidal properties can be imparted. Therefore, it is particularly useful as an antibacterial agent according to the present invention.
【００２５】また、メルカプトピリジン−Ｎ−オキシド
化合物の金属塩に加えて、ベンゾイミダゾール化合物、
イソチアゾロン化合物、ベンゾチアゾール化合物もしく
はベンゾチアゾロン化合物の銀塩、銅塩または亜鉛塩を
併用することが更に好ましく、一層広範囲な細菌類およ
び黴類に対して有効な抗菌防黴作用が得られる。Further, in addition to a metal salt of a mercaptopyridine-N-oxide compound, a benzimidazole compound,
It is more preferable to use a silver salt, a copper salt or a zinc salt of an isothiazolone compound, a benzothiazole compound or a benzothiazolone compound in combination, and an effective antibacterial and fungicidal action can be obtained against a wider range of bacteria and fungi.
【００２６】メルカプトピリジン−Ｎ−オキシド化合物
の銀塩、銅塩または亜鉛塩を主成分とする抗菌剤は、一
般に、メルカプトピリジン−Ｎ−オキシドのナトリウム
塩をイオン交換処理した水に溶かした水溶液と硝酸銀、
硝酸銅、硝酸亜鉛またはこれら金属塩の混合物をイオン
交換処理した水に溶かした水溶液を撹拌混合することに
よって調製される。生成した塩は水に不溶または難溶で
あるため固形物として析出するが、高い抗菌防黴性を得
るためには、上記の２つの水溶液の混合過程において充
分な撹拌を行って生成する金属塩を微粒子に分散するこ
とが好ましい。An antibacterial agent containing a silver salt, a copper salt or a zinc salt of a mercaptopyridine-N-oxide compound as a main component is generally an aqueous solution in which a sodium salt of mercaptopyridine-N-oxide is dissolved in ion-exchanged water. silver nitrate,
It is prepared by stirring and mixing an aqueous solution obtained by dissolving copper nitrate, zinc nitrate or a mixture of these metal salts in ion-exchanged water. The generated salt is insoluble or hardly soluble in water and precipitates as a solid. However, in order to obtain high antibacterial and antifungal properties, the metal salt formed by performing sufficient stirring in the mixing process of the above two aqueous solutions is used. Is preferably dispersed in fine particles.
【００２７】本発明に係わる通気性を有する基材は、ラ
イナとして用いられるものであり、その通気度は特に限
定されるものではないが、ＪＩＳ−Ｂ−９９０８に準じ
て面風速５．３ｃｍ／秒で測定した圧力損失が２Ｐａ以
下であることが好ましく、０．５Ｐａ以下であることが
更に好ましく、０．１Ｐａ以下であることが殊更に好ま
しい。The air-permeable base material according to the present invention is used as a liner, and the air permeability thereof is not particularly limited, but the surface wind velocity is 5.3 cm / cm in accordance with JIS-B-9908. The pressure loss measured in seconds is preferably 2 Pa or less, more preferably 0.5 Pa or less, and even more preferably 0.1 Pa or less.
【００２８】本発明に係わるライナとして用いられる通
気性を有する基材は、上記に挙げた空気清浄化機能を有
するフィルターと同じように、脱臭、抗菌または除塵な
どの空気清浄化機能を有しても良い。The air-permeable base material used as the liner according to the present invention has an air purifying function such as deodorization, antibacterial or dust removal, similarly to the above-mentioned filters having an air purifying function. Is also good.
【００２９】本発明に係わる空気清浄化機能を有するフ
ィルター、または、通気性を有する基材の材質は、特に
限定されるものではなく、各種の紙、不織布、織布、編
布、ネット、フェルト、ウレタンフォームなどの発泡体
および樹脂フィルムや金属箔などが挙げられ、シートの
通気性が乏しい場合には穴開け加工などを施して通気性
を向上させることができる。中でも、適度な通気性を有
し、且つ中しんとしては段成形が可能な素材として不織
布が好ましい。The material of the filter having an air purifying function or the air-permeable base material according to the present invention is not particularly limited, and various papers, nonwoven fabrics, woven fabrics, knitted fabrics, nets, felts, etc. And foams such as urethane foam, resin films and metal foils. When the sheet has poor air permeability, it can be perforated to improve the air permeability. Above all, a nonwoven fabric is preferable as a material having appropriate air permeability and capable of being formed in a stepped manner as a middle sash.
【００３０】不織布は、ポリアミド系繊維、ポリエステ
ル系繊維、ポリアルキレンパラオキシベンゾエート系繊
維、ポリウレタン系繊維、ポリビニルアルコール系繊
維、ポリ塩化ビニリデン系繊維、ポリ塩化ビニル系繊
維、ポリアクリロニトリル系繊維、ポリオレフィン系繊
維、フェノール系繊維などの合成繊維、ガラス繊維、金
属繊維、アルミナ繊維、炭素繊維、活性炭素繊維などの
無機繊維、木材パルプ、竹パルプ、麻パルプ、ケナフパ
ルプ、藁パルプ、バガスパルプ、コットンリンターパル
プ、木綿、羊毛、絹などの天然繊維、古紙再生パルプ、
レーヨン等の再生セルロース繊維やコラーゲン等のタン
パク質、アルギン酸、キチン、キトサン、澱粉などの多
糖類等を原料とした再生繊維など、あるいはこれらの繊
維に親水性や難燃性などの機能を付与した繊維などを単
独または組み合わせて使用し、各種方法によって製造し
たものである。The non-woven fabric is made of polyamide fiber, polyester fiber, polyalkylene paraoxybenzoate fiber, polyurethane fiber, polyvinyl alcohol fiber, polyvinylidene chloride fiber, polyvinyl chloride fiber, polyacrylonitrile fiber, polyolefin fiber. , Phenolic fiber, synthetic fiber, glass fiber, metal fiber, alumina fiber, inorganic fiber such as carbon fiber, activated carbon fiber, wood pulp, bamboo pulp, hemp pulp, kenaf pulp, straw pulp, bagasse pulp, cotton linter pulp, cotton , Wool, silk and other natural fibers, recycled pulp,
Regenerated cellulose fibers such as rayon, proteins such as collagen, and regenerated fibers made from polysaccharides such as alginic acid, chitin, chitosan, and starch, and fibers obtained by imparting functions such as hydrophilicity and flame retardancy to these fibers. These are used alone or in combination and manufactured by various methods.
【００３１】不織布の製造方法については特に制限はな
く、目的・用途に応じて、乾式法、湿式抄造法、メルト
ブローン法、スパンボンド法、フラッシュ紡糸法、エア
レイド法などで得られたウェブを水流交絡法、ニードル
パンチ法、ステッチボンド法などの物理的方法、サーマ
ルボンド法などの熱による接着方法、レジンボンドなど
の接着剤による接着方法で強度を発現させる方法を適宜
組み合わせて製造することができる。The method for producing the nonwoven fabric is not particularly limited, and the web obtained by a dry method, a wet papermaking method, a melt blown method, a spunbond method, a flash spinning method, an air laid method or the like is subjected to hydroentanglement according to the purpose and application. It can be produced by appropriately combining a physical method such as a method such as a needle punching method and a stitch bonding method, a bonding method using heat such as a thermal bonding method, and a bonding method using an adhesive such as a resin bond.
【００３２】本発明の空気清浄化フィルターは、片面段
ボールの幅方向の剛度は高いが、流れ方向には比較的柔
らかい場合があるため、取り扱い性を改良するために適
宜補強を施しても良く、補強法としてライナなどへの補
強ネットの取り付け、およびライナまたは側面などへの
帯状フィルムの取り付けなどが挙げられる。The air purifying filter of the present invention has a high rigidity in the width direction of the single-faced corrugated cardboard, but may be relatively soft in the flow direction. Therefore, the air purifying filter may be appropriately reinforced in order to improve handleability. Examples of the reinforcing method include attaching a reinforcing net to a liner or the like, attaching a belt-like film to the liner or a side surface, and the like.
【００３３】本発明の空気清浄化フィルターは、本発明
の趣旨を逸脱しない限りにおいて、更に防虫、殺虫、害
虫忌避、芳香、除湿、調湿、水分透過、油吸着などの各
種機能を有しても良い。The air purifying filter of the present invention further has various functions such as insect repellent, insecticidal, pest repellent, aroma, dehumidification, humidity control, moisture permeation, oil absorption, etc., without departing from the spirit of the present invention. Is also good.
【００３４】本発明の空気清浄化フィルターの具体例と
して、中しんがエレクトレットフィルターおよびライナ
が粗塵ネットからなる除塵フィルター、中しんが油吸着
フィルターおよびライナがエレクトレットフィルターか
らなる耐油性除塵フィルター、中しんがエレクトレット
フィルターおよびライナが脱臭フィルターからなる除塵
・脱臭フィルター、中しんがエレクトレットフィルター
およびライナが抗菌フィルターからなる除塵・抗菌フィ
ルター、中しんがエレクトレットフィルターと脱臭フィ
ルターを積層してなる複層フィルターおよびライナが抗
菌フィルターからなる除塵・脱臭・抗菌フィルター、中
しんがエレクトレットフィルターと抗菌フィルターを積
層してなる複層フィルターおよびライナが活性炭ネット
からなる除塵・脱臭・抗菌フィルター、中しんがＨＥＰ
Ａフィルターおよびライナが光触媒フィルターからなる
高性能除塵・光触媒フィルター、中しんが光触媒フィル
ターおよびライナがエレクトレットフィルターからなる
光触媒・除塵フィルター、および、中しんが酸性・中性
ガス吸着フィルターおよびライナが塩基性ガス吸着フィ
ルターからなる複合脱臭フィルターなどが挙げられる。As a specific example of the air purifying filter of the present invention, a dust removing filter in which a medium iron electret filter and a liner are formed of a coarse dust net, an oil-resistant dust removing filter in which a medium iron absorbing oil filter and a liner are an electret filter, and a medium. A dust removing / deodorizing filter in which the iron electret filter and the liner are composed of a deodorizing filter, a dust removing / antibacterial filter in which the medium electret filter and the liner are composed of an antibacterial filter, a multilayer filter comprising a laminated sheet electrified filter and a deodorizing filter, and Dust removal / deodorization / antibacterial filter with liner made of antibacterial filter, multi-layer filter consisting of laminated inner electret filter and antibacterial filter, and dust removal / desorption made of liner made of activated carbon net Antibacterial filter, medium-Shin is HEP
A-filter and liner are high-performance dust-removal / photocatalyst filters consisting of photocatalyst filters, medium-catalyst photocatalyst filters and liners consist of electret filters, and medium-acid / neutral gas adsorption filters and liners are basic. Examples include a composite deodorizing filter including a gas adsorption filter.
【００３５】[0035]
【実施例】以下、実施例により更に本発明を詳細に説明
するが、本発明はその主旨を越えない限り、これらに限
定されるものではない。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto unless it exceeds the gist of the invention.
【００３６】調製例１ 脱臭剤として燐酸添着活性炭８０重量％と、バインダー
として市販のスチレン−アクリル共重合樹脂エマルジョ
ン２０重量％とを混合攪拌して塗液を調製し、調製例１
の脱臭剤塗液Ａとした。Preparation Example 1 A coating liquid was prepared by mixing and stirring 80% by weight of activated carbon impregnated with phosphoric acid as a deodorant and 20% by weight of a commercially available styrene-acrylic copolymer resin emulsion as a binder.
The deodorant coating liquid A was used.
【００３７】調製例２ 調製例１において、燐酸添着活性炭に代えてハイシリカ
ゼオライトとする以外は全て調製例１と同一の方法で塗
液を調製し、調製例２の脱臭剤塗液Ｂとした。Preparation Example 2 A coating liquid was prepared in the same manner as in Preparation Example 1 except that high-silica zeolite was used in place of the phosphoric acid-impregnated activated carbon in Preparation Example 1, and a deodorant coating liquid B of Preparation Example 2 was obtained. .
【００３８】調製例３ 硝酸銀をイオン交換水に溶解した水溶液を高速回転式ア
ジテーターで撹拌しながら等モル相当量の２−メルカプ
トピリジン−Ｎ−オキシドナトリウム液を添加し、銀／
２−メルカプトピリジン−Ｎ−オキシドの微粒子分散液
を調製し、次いでこの抗菌剤に接着剤として等量のスチ
レンアクリルエマルジョンを加えて撹拌、混合し、これ
を調製例３の抗菌剤塗液とした。Preparation Example 3 An aqueous solution in which silver nitrate was dissolved in ion-exchanged water was stirred with a high-speed agitator, and an equimolar equivalent of 2-mercaptopyridine-N-oxide sodium solution was added.
A fine particle dispersion of 2-mercaptopyridine-N-oxide was prepared, and then an equivalent amount of styrene acrylic emulsion was added as an adhesive to this antibacterial agent, followed by stirring and mixing. This was used as an antibacterial agent coating liquid of Preparation Example 3. .
【００３９】調製例４ ポリエステル繊維およびレーヨン繊維を主体繊維とし、
アクリル系接着剤でレジンボンドしてなる坪量４５ｇ／
ｍ2の市販の乾式不織布に、調製例１の脱臭剤塗液Ａを
３５ｇ／ｍ2含浸塗布して乾燥し、これを調製例４の脱
臭フィルターとした。Preparation Example 4 Polyester fiber and rayon fiber were used as main fibers,
45g / basis weight resin-bonded with acrylic adhesive
The deodorant coating solution A of Preparation Example 1 was impregnated and applied to 35 g / m 2 of a commercially available dry nonwoven fabric of m 2 and dried to obtain a deodorizing filter of Preparation Example 4.
【００４０】調製例５ 調製例４において、調製例１の脱臭剤塗液Ａに代えて調
製例２の脱臭剤塗液Ｂとする以外は全て調製例４と同一
の方法で脱臭フィルターを作製し、これを調製例５の脱
臭フィルターとした。Preparation Example 5 A deodorizing filter was prepared in the same manner as in Preparation Example 4 except that the deodorant coating liquid B of Preparation Example 2 was used instead of the deodorant coating liquid A of Preparation Example 1. This was used as a deodorizing filter of Preparation Example 5.
【００４１】調製例６ 調製例４において、調製例１の脱臭剤塗液Ａを３５ｇ／
ｍ2に代えて調製例３の抗菌剤塗液を１ｇ／ｍ2とする以
外は全て調製例４と同一の方法で抗菌フィルターを作製
し、これを調製例６の抗菌フィルターとした。Preparation Example 6 In Preparation Example 4, 35 g of the deodorant coating solution A of Preparation Example 1 was used.
An antibacterial filter was prepared in the same manner as in Preparation Example 4 except that the coating solution of the antibacterial agent of Preparation Example 3 was changed to 1 g / m 2 instead of m 2 .
【００４２】調製例７ 調製例５の脱臭フィルターの片面上に熱可塑性樹脂とし
てエチレン酢酸ビニル共重合樹脂１５ｇ／ｍ2 を散布
し、散布側から表面温度１５０℃の赤外線ヒーターを当
てて加熱し、次いで熱可塑性樹脂が可塑化した後に加熱
を止め、速やかに脱臭フィルターの熱可塑性樹脂散布側
に市販のエレクトレットフィルター３０ＥＰ（三菱製紙
（株）製）を重ね合わせて２本の回転ロール間に挟んで
加圧、接着により積層し、これを調製例７の複層フィル
ターとした。Preparation Example 7 On one side of the deodorizing filter of Preparation Example 5, 15 g / m 2 of ethylene vinyl acetate copolymer resin was sprayed as a thermoplastic resin, and heated by applying an infrared heater having a surface temperature of 150 ° C. from the spraying side. Next, after the thermoplastic resin is plasticized, the heating is stopped, and a commercially available electret filter 30EP (manufactured by Mitsubishi Paper Mills) is immediately superimposed on the thermoplastic resin spraying side of the deodorizing filter and sandwiched between two rotating rolls. The layers were laminated by pressure and adhesion, and this was used as a multilayer filter of Preparation Example 7.
【００４３】実施例１ 調製例４の脱臭フィルターをライナ、および調製例５の
脱臭フィルターを中しんに用いて、ＪＩＳ−Ｚ−１５１
６に記載の「外装用段ボール」に準拠して、Ａ段に相当
する片面段ボールを作製し、これを実施例１の空気清浄
化フィルターとした。Example 1 Using the deodorizing filter of Preparation Example 4 as a liner and the deodorizing filter of Preparation Example 5 as a middle lining, JIS-Z-151 was used.
A single-sided corrugated cardboard corresponding to the A-stage was prepared according to the “corrugated cardboard for exterior” described in No. 6, and this was used as the air cleaning filter of Example 1.
【００４４】実施例２ 調製例４の脱臭フィルターをライナ、および市販のＰＰ
製補強ネット付きエレクトレットフィルター３０ＥＰＮ
（三菱製紙（株）製）を中しんに用いて、ＪＩＳ−Ｚ−
１５１６に記載の「外装用段ボール」に準拠して、Ａ段
に相当する片面段ボールを作製し、これを実施例２の空
気清浄化フィルターとした。Example 2 The deodorizing filter of Preparation Example 4 was replaced with a liner and commercially available PP.
Filter 30EPN with reinforced net
(Manufactured by Mitsubishi Paper Mills) as a JIS-Z-
A single-sided corrugated cardboard corresponding to the A-stage was produced in accordance with “Exterior Corrugated Cardboard” described in No. 1516, and this was used as the air cleaning filter of Example 2.
【００４５】実施例３ 調製例６の抗菌フィルターをライナ、および調製例７の
複層フィルターを中しんに用いて、ＪＩＳ−Ｚ−１５１
６に記載の「外装用段ボール」に準拠して、Ａ段に相当
する片面段ボールを作製し、これを実施例３の空気清浄
化フィルターとした。Example 3 Using the antibacterial filter of Preparation Example 6 as a liner and the multilayer filter of Preparation Example 7 as a middle layer, JIS-Z-151 was used.
A single-sided corrugated cardboard corresponding to the A-stage was prepared according to the “exterior cardboard” described in No. 6, and this was used as the air purification filter of Example 3.
【００４６】比較例１ 調製例５の脱臭フィルターをピッチ５ｍｍ、山高さ５ｍ
ｍのプリーツ状に加工し、その片面に調製例４の脱臭フ
ィルターを貼り合わせてミニプリーツフィルターを作製
し、これを比較例１の空気清浄化フィルターとした。Comparative Example 1 The deodorizing filter of Preparation Example 5 was prepared with a pitch of 5 mm and a peak height of 5 m.
m was pleated, and the deodorizing filter of Preparation Example 4 was adhered to one surface of the pleated filter to produce a mini-pleated filter, which was used as an air cleaning filter of Comparative Example 1.
【００４７】比較例２ 市販のＰＰ製補強ネット付きエレクトレットフィルター
３０ＥＰＮ（三菱製紙（株）製）をピッチ５ｍｍ、山高
さ５ｍｍのプリーツ状に加工し、その片面に調製例４の
脱臭フィルターを貼り合わせてミニプリーツフィルター
を作製し、これを比較例２の空気清浄化フィルターとし
た。Comparative Example 2 A commercially available electret filter 30 EPN with a reinforcing net made of PP (manufactured by Mitsubishi Paper Mills) was processed into a pleated shape having a pitch of 5 mm and a height of 5 mm, and the deodorizing filter of Preparation Example 4 was bonded to one surface thereof. Thus, a mini-pleated filter was prepared, and this was used as an air purification filter of Comparative Example 2.
【００４８】比較例３ 調製例７の複層フィルターをピッチ５ｍｍ、山高さ５ｍ
ｍのプリーツ状に加工し、その片面に調製例６の抗菌フ
ィルターを貼り合わせてミニプリーツフィルターを作製
し、これを比較例３の空気清浄化フィルターとした。Comparative Example 3 The multilayer filter of Preparation Example 7 was prepared with a pitch of 5 mm and a peak height of 5 m.
m was pleated, and the antibacterial filter of Preparation Example 6 was adhered to one surface of the pleated filter to produce a mini-pleated filter, which was used as an air purification filter of Comparative Example 3.
【００４９】比較例４ 調製例５の脱臭フィルターと調製例４の脱臭フィルター
とを積層して単板のフィルターを作製し、これを比較例
４の空気清浄化フィルターとした。Comparative Example 4 The deodorizing filter of Preparation Example 5 and the deodorizing filter of Preparation Example 4 were laminated to produce a single-plate filter, which was used as the air cleaning filter of Comparative Example 4.
【００５０】比較例５ 市販のＰＰ製補強ネット付きエレクトレットフィルター
３０ＥＰＮ（三菱製紙（株）製）と調製例４の脱臭フィ
ルターとを積層して単板のフィルターを作製し、これを
比較例５の空気清浄化フィルターとした。Comparative Example 5 A commercially available single-plate filter was prepared by laminating a commercially available electret filter 30EPN with a reinforcing net made of PP (manufactured by Mitsubishi Paper Mills) and the deodorizing filter of Preparation Example 4. An air purification filter was used.
【００５１】比較例６ 調製例７の複層フィルターと調製例６の抗菌フィルター
とを積層して単板のフィルターを作製し、これを比較例
６の空気清浄化フィルターとした。Comparative Example 6 A multilayer filter was prepared by laminating the multilayer filter of Preparation Example 7 and the antibacterial filter of Preparation Example 6, and was used as an air purification filter of Comparative Example 6.
【００５２】以上、実施例および比較例で得られた空気
清浄化フィルターの特性を以下の方法により評価した。The characteristics of the air cleaning filters obtained in Examples and Comparative Examples were evaluated by the following methods.
【００５３】［除塵性試験］ＪＩＳ−Ｂ−９９０８に準
拠して、粒子として０．３〜０．５μｍの大気塵を用い
て風速１ｍ／秒における実施例および比較例の空気清浄
化フィルターの粒子捕集率（％）を測定した。[Dust Removal Test] According to JIS-B-9908, particles of the air cleaning filters of Examples and Comparative Examples at an air velocity of 1 m / sec using 0.3 to 0.5 μm air dust as particles. The collection rate (%) was measured.
【００５４】［通気性試験］ＪＩＳ−Ｂ−９９０８に準
拠して、風速１ｍ／秒における実施例および比較例の空
気清浄化フィルターの圧力損失（Ｐａ）を測定した。圧
力損失の値が小さい方が通気性が優れることを表す。[Air permeability test] The pressure loss (Pa) of the air cleaning filters of the examples and comparative examples at a wind speed of 1 m / sec was measured in accordance with JIS-B-9908. The smaller the value of the pressure loss, the better the air permeability.
【００５５】［脱臭性試験］実施例および比較例の空気
清浄化フィルターを市販の家庭用エアコン（商品名霧ケ
峰、三菱電機（株）製）の室内機の吸気部に取り付けて
送風運転し、ＪＥＭ−１４６７−１９９５に準拠してタ
バコを用いた脱臭性能試験を行い、耐久性の総合耐久本
数を求めた。[Deodorizing Test] The air purifying filters of Examples and Comparative Examples were attached to the air intake section of an indoor unit of a commercially available home air conditioner (trade name: Kirigamine, manufactured by Mitsubishi Electric Corporation), and a blow operation was performed. A deodorizing performance test using tobacco was performed in accordance with -1467-1995, and the total number of pieces of durability was determined.
【００５６】［取扱性試験］Ａ４判の大きさに断裁した
実施例および比較例の空気清浄化フィルター各２枚を角
形２号の紙製封筒に入れる作業を５人の測定者が行い、
作業時の空気清浄化フィルターの取扱性を評価した。取
扱性は、良いを５、やや良いを４、普通を３、やや悪い
を２、悪いを１と判定し、測定者５人の平均値を求め
た。[Handling test] Five measurers performed the work of putting each of the two air cleaning filters of the example and the comparative example cut into A4 size paper into a square No. 2 paper envelope.
The workability of the air cleaning filter during operation was evaluated. The handling was determined to be 5 for good, 4 for fair, 3 for normal, 2 for poor, and 1 for bad, and the average value of 5 measurers was obtained.
【００５７】上記の方法により試験を行い、その性能を
評価した結果を表１に記載する。Tests were conducted according to the above method, and the results of evaluation of the performance are shown in Table 1.
【００５８】[0058]
【表１】 [Table 1]
【００５９】表１の結果から、本発明の空気清浄化フィ
ルターは、構成要素が同じであるミニプリーツフィルタ
ーと比較して、圧力損失が低くて通気性に優れ、除塵性
が高い傾向にある、また、構成要素が同じである単板の
フィルターと比較して、通気性に優れ、取扱性が良好
で、除塵性または脱臭性が高いことが分かる。From the results shown in Table 1, the air purifying filter of the present invention has a lower pressure loss, a higher air permeability and a higher dust-removing property than the mini-pleated filter having the same components. Further, it can be seen that, compared to a single-plate filter having the same constituent elements, the filter has excellent air permeability, good handleability, and high dust removal or deodorization.
【００６０】[0060]
【発明の効果】本発明の空気清浄化フィルターは、通気
性に優れ、薄型でコンパクトであり、適度な強度を有し
て取り扱い性が良く、且つ除塵性や脱臭性などの空気清
浄化機能が高く、空気清浄機やエアコン等の空調機など
に搭載されるフィルターとして特に有用なものである。The air purifying filter of the present invention has excellent air permeability, is thin and compact, has appropriate strength, is easy to handle, and has an air purifying function such as dust removal and deodorization. It is high and is particularly useful as a filter mounted on an air purifier or an air conditioner such as an air conditioner.
【００６１】また、このような空気清浄化フィルター
は、特殊な折り加工機すなわちプリーツマシンを必要と
せず、段ボール製造機すなわちコルゲータを用いて比較
的簡易に加工すること可能であり、量産性が非常に高い
ことも特長の一つである。Further, such an air purifying filter does not require a special folding machine, ie, a pleating machine, can be processed relatively easily using a corrugated cardboard manufacturing machine, ie, a corrugator, and has high productivity. Is one of the features.
【図１】本発明の空気清浄化フィルターの一実施例を示
す斜視図である。FIG. 1 is a perspective view showing one embodiment of an air cleaning filter of the present invention.
１ 中しん ２ ライナ 1 Nakashin 2 Liner
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4C080 AA03 BB02 BB05 CC01 HH05 JJ03 KK08 MM03 MM04 MM05 MM06 MM14 QQ03 4D058 JA13 JB50 QA05 TA02 TA03 TA07 TA08 4H011 AA02 AA03 AA04 BA06 BB09 BB18 BC19 DA07 DD07 DH16 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4C080 AA03 BB02 BB05 CC01 HH05 JJ03 KK08 MM03 MM04 MM05 MM06 MM14 QQ03 4D058 JA13 JB50 QA05 TA02 TA03 TA07 TA08 4H011 AA02 AA03 AA04 BA06 BB09 BB07 BC19 DA
Claims (3)
段ボール」に準拠して、空気清浄化機能を有するフィル
ターを中しん、および通気性を有する基材をライナに用
いて作製してなる片面段ボール形状の空気清浄化フィル
ター。1. In accordance with JIS-Z-1516, "corrugated cardboard for exterior", a filter having an air-cleaning function is used as a lining, and a substrate having air permeability is used as a liner. One side corrugated cardboard air cleaning filter.
塵性を有することを特徴とする請求項１記載の空気清浄
化フィルター。2. The air purifying filter according to claim 1, wherein the filter to be lumped has at least a dust removing property.
トを含有することを特徴とする請求項１または２記載の
空気清浄化フィルター。3. The air purifying filter according to claim 1, wherein the hollow filter contains an electret.