JP2001084970A - Bag for thin battery - Google Patents
Bag for thin batteryInfo
- Publication number
- JP2001084970A JP2001084970A JP26035399A JP26035399A JP2001084970A JP 2001084970 A JP2001084970 A JP 2001084970A JP 26035399 A JP26035399 A JP 26035399A JP 26035399 A JP26035399 A JP 26035399A JP 2001084970 A JP2001084970 A JP 2001084970A
- Authority
- JP
- Japan
- Prior art keywords
- bag
- thin battery
- seal portion
- seal part
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、リチウムイオン二
次電池（ＬＩＢ）等の薄型電池用の発電要素を収納する
薄型電池用袋体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thin battery bag for housing a power generating element for a thin battery such as a lithium ion secondary battery (LIB).
【０００２】[0002]
【従来の技術】最近の種々の電子機器の発達に伴い、電
子機器の小型化，省スペース化のニーズが高まってお
り、これに用いる薄型電池（シート状電池）にも更なる
薄型化と可撓性が求められている。このようなニーズに
応えるものとして、ゲル状ポリマー電解質を用いたリチ
ウムイオン二次電池が実用化段階に入りつつある。2. Description of the Related Art With the recent development of various electronic devices, there is an increasing need for miniaturization and space saving of electronic devices. Flexibility is required. In order to meet such needs, a lithium ion secondary battery using a gel polymer electrolyte is entering a stage of practical use.
【０００３】この種のゲル状ポリマー電解質を用いたリ
チウムイオン二次電池の構造例を図４および図５に示
す。これらの図において、３１はアルミニウム箔からな
る正極集電体、３２はコバルト酸リチウム等のリチウム
含有複合酸化物からなる正極、３３は溶媒で可塑化され
たポリマー電解質からなる隔離材、３４は炭素材からな
る負極、３５は銅箔からなる負極集電体であり、これら
により発電要素が構成される。そして、この発電要素が
アルミニウムラミネートシートからなる袋体３６に収納
され、側縁部３６ｃをヒートシールすることにより電池
が構成されている。なお、３７は電極である。FIGS. 4 and 5 show examples of the structure of a lithium ion secondary battery using this type of gel polymer electrolyte. In these figures, 31 is a positive electrode current collector made of an aluminum foil, 32 is a positive electrode made of a lithium-containing composite oxide such as lithium cobalt oxide, 33 is a separator made of a polymer electrolyte polymerized with a solvent, and 34 is a charcoal. A negative electrode 35 made of a material is a negative electrode current collector made of copper foil, and these constitute a power generating element. The power generation element is housed in a bag 36 made of an aluminum laminate sheet, and the side edge 36c is heat-sealed to constitute a battery. In addition, reference numeral 37 denotes an electrode.
【０００４】例えば、上記アルミニウムラミネートシー
トとして、ポリエチレン層とアルミニウム箔層とポリエ
チレン層との三層ラミネート箔が用いられている（特開
平９−７６３６号）。For example, as the aluminum laminate sheet, a three-layer laminate foil of a polyethylene layer, an aluminum foil layer, and a polyethylene layer is used (Japanese Patent Laid-Open No. 9-7636).
【０００５】そして、上記薄型電池は、そのままあるい
はハードケースに収納された状態で、電子機器内部に組
み込まれる。ここで、上記薄型電池は、ハードケース内
部や電子機器内部の狭いデッドスペースに収容する際
に、収容スペースを有効に活用するために、左右両側縁
のシール部をそれぞれ内側に折り曲げることによって、
左右のシール部の幅分だけコンパクトな形状にされるこ
とが多い。[0005] The thin battery is incorporated in an electronic device as it is or in a state of being stored in a hard case. Here, when the thin battery is housed in a narrow dead space inside a hard case or an electronic device, in order to effectively utilize the housing space, the seal portions on both right and left side edges are bent inward, respectively.
In many cases, a compact shape is formed by the width of the left and right seal portions.
【０００６】[0006]
【発明が解決しようとする課題】[Problems to be solved by the invention]
【０００７】しかしながら、上記袋体３６を用いた電池
は図４に示すように、細長のアルミニウムラミネートシ
ートを長さ方向の略半分から２つ折りし、左右の側縁部
３６ｃをヒートシールしたのち、内部に発電要素を入
れ、上部開口ａをヒートシールして構成されている。そ
のため、左右両側縁のヒートシール部３６ｃを内側に折
り曲げると、ヒートシール部３６ｃの内側縁３６ｃ’が
袋体３６の外側縁となる（図６参照）。そして、左右両
側縁のヒートシール部３６ｃが内側に折り曲げられた袋
体３６の底部では、図６に示すように、袋体の底部の角
部に対応するヒートシール部の内側縁３６ｃ’の角部３
８が、直角なエッジ部となる。このエッジ部３８は、袋
体３６の内部に接しているため、ここに外的な力、例え
ば運搬時等における衝撃が加わると、亀裂や穴あきが生
じ、袋体３６の内部が露呈してしまうという欠点があ
る。また、過充電や過放電による発熱によって袋体３６
内に内圧が発生した際には、上記エッジ部３８に応力が
集中して、破袋してしまうという欠点がある。However, in the battery using the bag 36, as shown in FIG. 4, an elongated aluminum laminated sheet is folded in half from about half in the longitudinal direction, and the left and right side edges 36c are heat-sealed. A power generating element is placed inside, and the upper opening a is heat-sealed. Therefore, when the heat seal portions 36c on the left and right side edges are bent inward, the inner edge 36c 'of the heat seal portion 36c becomes the outer edge of the bag 36 (see FIG. 6). At the bottom of the bag body 36 in which the heat seal portions 36c on the left and right side edges are bent inward, as shown in FIG. 6, the corner of the inner edge 36c 'of the heat seal portion corresponding to the corner of the bottom portion of the bag body. Part 3
8 is a right-angled edge portion. Since the edge portion 38 is in contact with the inside of the bag 36, when an external force, for example, an impact during transportation or the like is applied thereto, a crack or a hole is formed, and the inside of the bag 36 is exposed. There is a disadvantage that it will. In addition, the bag 36 may be heated by overcharge or overdischarge.
When an internal pressure is generated inside, there is a disadvantage that stress concentrates on the edge portion 38 and the bag is broken.
【０００８】本発明は、このような事情に鑑みなされた
もので、袋体の左右両側縁のヒートシール部を内側に折
り曲げてコンパクトにして使用する際に、内側に折り曲
げられたヒートシール部の底部に形成されるエッジ部
に、摩擦や衝撃等が加えられても容易に破袋しない薄型
電池用袋体の提供をその目的とする。The present invention has been made in view of such circumstances, and when the heat seal portions on both right and left side edges of the bag body are bent inward to be compact and used, the heat seal portion bent inward is used. It is an object of the present invention to provide a thin battery bag that does not easily break even when friction or impact is applied to an edge formed on the bottom.
【０００９】[0009]
【課題を解決するための手段】上記の目的を達成するた
め、本発明の薄型電池用袋体は、金属層とシーラント層
とからなる略四角状のラミネートシートを略半分から２
つ折りし、かつ、両側縁をヒートシールして筒状袋体を
つくり、この筒状袋体内に薄型電池用発電要素を収容し
上部開口を密封する薄型電池用袋体であって、この袋体
の左右両側縁のシール部の底部近傍が内側に延長され延
長シール部に形成されているという構成をとる。In order to achieve the above object, a thin battery bag according to the present invention comprises a substantially square laminate sheet comprising a metal layer and a sealant layer, which is formed by a half to a half.
A thin battery bag body which is folded and heat-sealed on both side edges to form a cylindrical bag body, accommodates a thin battery power generation element in the cylindrical bag body, and seals an upper opening thereof. In this configuration, the vicinity of the bottom of the seal portion on both right and left side edges of the seal member is extended inward to form an extended seal portion.
【００１０】すなわち、本発明の薄型電池用袋体は、左
右両側縁のシール部の底部近傍が内側に延長され延長シ
ール部に形成されているため、左右両側縁のヒートシー
ル部を内側に折り曲げてコンパクトにして使用する際
に、内側に折り曲げられたヒートシール部の底部のエッ
ジ部は、直接、袋体の内部に接しないで延長シール部を
介して接することとなる。したがって、エッジ部に亀裂
等が生じても、延長シール部の存在により、その亀裂が
袋体の内部まで及ばなくなる。また、上記延長シール部
によりエッジ部自体の強度も向上することから、多少の
衝撃では亀裂等は生じなくなる。That is, in the thin battery bag according to the present invention, since the vicinity of the bottom of the seal portion on both left and right edges is extended inward and formed as an extended seal portion, the heat seal portions on both right and left edges are bent inward. When used in a compact form, the bottom edge portion of the heat seal portion bent inward is not in direct contact with the inside of the bag body but is in contact with the heat seal portion via the extension seal portion. Therefore, even if a crack or the like occurs in the edge portion, the crack does not reach the inside of the bag due to the presence of the extension seal portion. In addition, since the strength of the edge portion itself is also improved by the extension seal portion, a crack or the like does not occur with a slight impact.
【００１１】また、上記延長シール部が、袋体の側縁シ
ール部を底辺とする略三角形に形成されていると、薄型
電池用発電要素が発熱等して薄型電池用袋体の内圧が異
常に大きくなっても、それに耐えられるようになる。特
に、上記略三角形の上辺がアール状に形成されている
と、角部がないため圧力が均等にかかり圧力集中個所を
生じないことから、より大きな圧力に耐えうるようにな
る。Further, if the extension seal portion is formed in a substantially triangular shape with the side edge seal portion of the bag as the base, the internal pressure of the thin battery bag is abnormal due to heat generation of the thin battery power generating element. Even if it gets bigger, it can withstand it. In particular, when the upper side of the above-mentioned substantially triangular shape is formed in a round shape, since there is no corner, the pressure is evenly applied and no pressure concentration portion occurs, so that it is possible to withstand a larger pressure.
【００１２】つぎに、本発明を詳しく説明する。Next, the present invention will be described in detail.
【００１３】本発明の薄型電池用袋体は、例えば、１枚
の略四角状のシートで形成され、上記シートを略半分か
ら２つ折りにし、かつ両側縁をヒートシールして筒状に
し、その内部に発電要素を収納し、上部開口をヒートシ
ールすることにより電池を構成するようになっている。The thin battery bag of the present invention is formed of, for example, one substantially square sheet, and the above sheet is folded substantially from half to two, and both side edges are heat-sealed to form a cylinder. A battery is configured by housing a power generation element therein and heat sealing the upper opening.
【００１４】上記薄型電池用袋体は、金属層とシーラン
ト層とからなる略四角状のラミネート材で構成されてお
り、上記金属層の材料としては、圧延，電解等により得
られる、アルミニウム，アルミニウム合金，銅，銅合
金，鉄，ステンレス，チタン，チタン合金等からなる金
属箔が用いられている。そして、その厚みは５〜１００
μｍの範囲に設定されることが好ましい。上記厚みが５
μｍを下回ると、金属箔層にピンホール等が発生し易く
なり、ラミネート材のガスバリア性や遮水性が低下し、
１００μｍを上回ると、薄型電池用袋体の薄型化や可撓
性に不利となるからである。The thin battery bag is made of a substantially square laminate material comprising a metal layer and a sealant layer. The metal layer may be made of aluminum, aluminum, or the like obtained by rolling, electrolysis, or the like. Metal foils made of alloys, copper, copper alloys, iron, stainless steel, titanium, titanium alloys and the like are used. And the thickness is 5-100
It is preferable that the distance be set in the range of μm. The thickness is 5
When the thickness is less than μm, pinholes and the like easily occur in the metal foil layer, and the gas barrier property and the water shielding property of the laminate material are reduced,
If the thickness exceeds 100 μm, it is disadvantageous for thinning and flexibility of the thin battery bag.
【００１５】また、上記シーラント層の材料としては、
ポリプロピレン，ポリエチレン，ポリエステル，ポリア
クリロニトリル，エチレン酢酸ビニルコポリマー（ＥＶ
Ａ），ポリビニルアルコール（ＰＶＡ），変性ポリプロ
ピレン，変性ポリエチレン，ポリ酢酸ビニル，ポリビニ
ルアセテート等が用いられる。特に、ガスバリア性およ
び耐薬品性の面からポリプロピレン，ポリエチレンが好
ましい。そして、その厚みは５〜１０００μｍの範囲に
設定されることが好ましい。上記厚みが５μｍを下回る
と、電極シール部の気密性（シーラントの埋まり性）お
よび電極と金属層との絶縁性が低下し、１０００μｍを
上回ると、薄型電池用袋体の薄型化に不利となるからで
ある。The material of the sealant layer is as follows:
Polypropylene, polyethylene, polyester, polyacrylonitrile, ethylene vinyl acetate copolymer (EV
A), polyvinyl alcohol (PVA), modified polypropylene, modified polyethylene, polyvinyl acetate, polyvinyl acetate and the like are used. Particularly, polypropylene and polyethylene are preferable from the viewpoint of gas barrier properties and chemical resistance. The thickness is preferably set in the range of 5 to 1000 μm. When the thickness is less than 5 μm, the airtightness (embedding property of the sealant) of the electrode seal portion and the insulation between the electrode and the metal layer are reduced, and when the thickness is more than 1000 μm, it is disadvantageous for thinning the thin battery bag. Because.
【００１６】そして、上記ラミネート材は、金属層とシ
ーラント層の積層体であれば特に限定されない。例え
ば、特開平９−７６３６号公報では、アルミニウム箔の
表面および裏面にポリエチレン層を設けた三層ラミネー
ト箔が用いられている。The laminate is not particularly limited as long as it is a laminate of a metal layer and a sealant layer. For example, in JP-A-9-7636, a three-layer laminate foil in which a polyethylene layer is provided on the front and back surfaces of an aluminum foil is used.
【００１７】[0017]
【発明の実施の形態】つぎに、本発明の実施の形態を図
面にもとづいて詳しく説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, embodiments of the present invention will be described in detail with reference to the drawings.
【００１８】図１は、本発明の薄型電池用袋体の一実施
の形態を示すための要部拡大図である。この薄型電池用
袋体１は、図４のものと同様、１枚の細長形アルミニウ
ムラミネートシート材（例えば３層構造で、アルミニウ
ム箔の両面にポリエチレン層が形成されている）を略半
分から２つ折りにし、その部分を底部とし、左右両側縁
をヒートシールして全体を筒状にし、その内部に発電要
素〔例えば、４０ｍｍ×８０ｍｍ×２ｍｍ（厚み）のサ
イズ〕を収容し、上部開口をヒートシールして電池を構
成している。注目すべきは、図１のように、側縁シール
部３の底部近傍が内側に延長され延長シール部３ａに形
成され、上記延長シール部３ａが、袋体の側縁シール部
３を底辺とする略三角形に形成され、かつ、その上辺３
ｂがアール状に形成されていることである。３ｂ’は側
縁シール部３の内側縁である。それ以外の部分は図４と
同じであるから、図示および説明を省略する。FIG. 1 is an enlarged view of a main portion showing an embodiment of a thin battery bag according to the present invention. As in the case of FIG. 4, the thin battery bag 1 is made of a single elongated aluminum laminated sheet material (for example, having a three-layer structure in which polyethylene layers are formed on both sides of an aluminum foil) from about half to two. Fold it, make that part the bottom, heat seal the left and right side edges and make the whole cylindrical, house the power generation element [for example, 40 mm x 80 mm x 2 mm (thickness) size] inside, heat the top opening The battery is sealed. It should be noted that, as shown in FIG. 1, the vicinity of the bottom of the side edge seal portion 3 is extended inward to form an extension seal portion 3a, and the extension seal portion 3a defines the side edge seal portion 3 of the bag body as a base. Is formed in a substantially triangular shape, and its upper side 3
b is formed in a round shape. 3b 'is an inner edge of the side edge seal portion 3. The other parts are the same as those in FIG. 4, and illustration and description are omitted.
【００１９】上記側縁シール部３は、通常１０ｍｍ幅に
形成される。そして、上記側縁シール部３の底部近傍か
ら略三角形状に内側に延長された延長シール部３ａは、
上記側縁シール部３を底辺とする略三角形としてとらえ
たときに、その高さｈが、上記側縁シール部３のシール
幅１０ｍｍに対し、２〜１０ｍｍの範囲に設定されるの
が好ましく、より好ましくは２〜７ｍｍの範囲である
（図１参照）。これは、図３に示す他の実施の形態のも
のの、延長シール部１３ａの形状のときも同様である。
すなわち、２ｍｍ未満であると内部の角部２の保護効果
があらわれにくい傾向があり、１０ｍｍを超えると内容
積が小さくなるため袋体として支障をきたす傾向がある
からである。The side edge seal portion 3 is usually formed with a width of 10 mm. The extended seal portion 3a extended inward in a substantially triangular shape from the vicinity of the bottom of the side edge seal portion 3 includes:
When the side edge seal portion 3 is taken as a substantially triangular shape having a bottom side, the height h is preferably set in a range of 2 to 10 mm with respect to the seal width 10 mm of the side edge seal portion 3, More preferably, it is in the range of 2 to 7 mm (see FIG. 1). This is the same as in the case of the other embodiment shown in FIG.
That is, if it is less than 2 mm, the protective effect of the inner corner portion 2 tends to be hard to appear, and if it exceeds 10 mm, the inner volume tends to be small, which tends to hinder the bag.
【００２０】図２は、上記薄型電池用袋体の側縁シール
部３を内側に折り曲げた状態を示している。この状態に
すると、側縁シール部３の内側縁３ｂ’が袋体１の外側
縁となる。このとき、底部近傍に形成されるエッジ部３
ｃは、延長シール部３ａの存在により、直接、袋体１の
内部に接することなく延長シール部３ａを介して接する
こととなる。したがって、エッジ部３ｃに亀裂等が生じ
ても、延長シール部３ａの存在により、その亀裂が袋体
１の内部まで及ばなくなる。また、上記延長シール部３
ａによりエッジ部３ｃ自体の強度も向上することから、
多少の衝撃では亀裂は生じなくなる。なお、本発明の薄
型電池用袋体において、それ以外の構成は、先に述べた
ように、図４および図５に示す従来例と同様である。FIG. 2 shows a state in which the side edge seal portion 3 of the thin battery bag is bent inward. In this state, the inner edge 3 b ′ of the side edge seal portion 3 becomes the outer edge of the bag 1. At this time, the edge portion 3 formed near the bottom portion
Due to the presence of the extension seal portion 3c, the contact c does not come into direct contact with the inside of the bag body 1 but contacts through the extension seal portion 3a. Therefore, even if a crack or the like occurs in the edge portion 3c, the crack does not reach the inside of the bag body 1 due to the presence of the extension seal portion 3a. In addition, the extension seal portion 3
a also improves the strength of the edge portion 3c itself,
Cracks do not occur with a slight impact. The remaining structure of the thin battery bag of the present invention is the same as that of the conventional example shown in FIGS. 4 and 5 as described above.
【００２１】図３は、本発明の薄型電池用袋体の他の実
施の形態を示す要部拡大図である。この実施の形態が、
図１に示される実施の形態と違う点は、延長シール部１
３ａの上辺１３ｂが直線状になっている点である。この
場合であっても、図２のように、側縁シール部１３を内
側に折り曲げた態様をとるとき、底部近傍に形成される
エッジ部は、直接、袋体の内部に接することなく延長シ
ール部１３ａを介して接することとなる。FIG. 3 is an enlarged view of a main part showing another embodiment of the thin battery bag of the present invention. This embodiment is
The difference from the embodiment shown in FIG.
The point is that the upper side 13b of 3a is linear. Even in this case, as shown in FIG. 2, when the side edge seal portion 13 is bent inward, the edge portion formed near the bottom portion does not directly contact the inside of the bag body without extending the seal. The contact is made via the portion 13a.
【００２２】なお、上記実施の形態では、シート材をヒ
ートシールすることのみで袋体に形成しているが、シー
ル性を向上させるために、接着剤を併用してもよい。こ
の場合、接着剤には、変性ポリオレフィン，ウレタン
系，エポキシ系，ＥＥＡ系，シランカップリング剤等が
用いられる。In the above embodiment, the bag is formed only by heat-sealing the sheet material, but an adhesive may be used in combination to improve the sealing property. In this case, a modified polyolefin, urethane-based, epoxy-based, EEA-based, silane coupling agent, or the like is used as the adhesive.
【００２３】本発明の薄型電池用袋体は、例えば、つぎ
のようにして製造される。まず、略四角状に裁断された
上記シート材を用意し、このシートを略半分から上下に
２つ折りにする。そして、２つ折りされたものの両側縁
をヒートシールして筒状袋体をつくる。この際、両側縁
をヒートシールするための上下一対の金型は長板状金型
とし、延長シール部に対応するように端部が延長シール
部の形状だけ大きくなったものを使用する。そして、こ
の筒状袋体内に薄型電池用発電要素を収容し、上記薄型
電池用発電要素から延出された正極リード線と負極リー
ド線が袋体の外に出るよう挟んだ状態で、上部開口をヒ
ートシールにより密封することにより薄型電池が形成さ
れる。The thin battery bag of the present invention is manufactured, for example, as follows. First, the above-mentioned sheet material cut into a substantially square shape is prepared, and this sheet is folded in two from approximately half up and down. Then, both sides of the folded part are heat-sealed to form a cylindrical bag. At this time, a pair of upper and lower molds for heat-sealing the both side edges are long plate-shaped molds, and the ones whose ends are enlarged by the shape of the extension seal portion so as to correspond to the extension seal portion are used. Then, the thin battery power generating element is accommodated in the tubular bag body, and the upper opening is formed in a state where the positive electrode lead and the negative electrode lead extended from the thin battery power generating element are sandwiched so as to come out of the bag. Is sealed by heat sealing to form a thin battery.
【００２４】[0024]
【発明の効果】以上のように、本発明の薄型電池用袋体
は、両側縁のシール部の底部近傍が内側に延長され延長
シール部に形成されている。すなわち、上記の構成をと
ることによって、左右両側縁のヒートシール部を内側に
折り曲げてコンパクトにして使用する際に、内側に折り
曲げられたヒートシール部の底部のエッジ部は、直接、
袋体の内部に接しないで延長シール部を介して接するこ
ととなる。したがって、エッジ部に亀裂等が生じても、
延長シール部の存在により、その亀裂が袋体の内部まで
及ばなくなるという効果を奏する。また、上記延長シー
ル部によりエッジ部自体の強度も向上することから、多
少の衝撃では亀裂は生じなくなるという効果を奏する。
また、上記延長シール部が、袋体の側縁シール部を底辺
とする略三角形に形成されていると、薄型電池用発電要
素が発熱等して薄型電池用袋体の内圧が異常に大きくな
っても、それに耐えられるようになる。特に、上記略三
角形の上辺がアール状に形成されていると、角部がない
ため圧力が均等にかかり、圧力集中個所を生じないこと
から、より大きな圧力に耐えうるようになるという効果
を奏する。As described above, the thin battery bag of the present invention is formed in the extended seal portion with the vicinity of the bottom of the seal portion on both side edges being extended inward. That is, by adopting the above configuration, when the heat seal portions on the left and right side edges are bent inward and used compactly, the bottom edge portion of the heat seal portion bent inward is directly
It does not come into contact with the inside of the bag, but comes in contact with the bag via the extension seal portion. Therefore, even if cracks occur at the edge,
Due to the presence of the extension seal portion, there is an effect that the crack does not reach the inside of the bag body. Further, since the strength of the edge portion itself is also improved by the extension seal portion, there is an effect that a crack is not generated by a slight impact.
Further, when the extended seal portion is formed in a substantially triangular shape with the side edge seal portion of the bag as a bottom, the internal pressure of the thin battery bag becomes abnormally large due to heat generation of the thin battery power generating element or the like. But you can withstand it. In particular, when the upper side of the above-mentioned substantially triangular shape is formed in a round shape, the pressure is evenly applied because there are no corners, and there is no pressure concentration point, so that it is possible to endure a larger pressure. .
【図１】本発明の一実施の形態の薄型電池用袋体を示す
要部拡大図である。FIG. 1 is an enlarged view of a main part showing a thin battery bag according to an embodiment of the present invention.
【図２】図１に示す本発明の薄型電池用袋体の、側縁シ
ール部を折り曲げた態様を示す要部拡大図である。FIG. 2 is an enlarged view of a main part of the thin battery bag of the present invention shown in FIG. 1 in which a side edge seal portion is bent.
【図３】本発明の他の実施の形態の薄型電池用袋体を示
す要部拡大図である。FIG. 3 is an enlarged view of a main part showing a thin battery bag according to another embodiment of the present invention.
【図４】従来のリチウムイオン二次電池を示す斜視図で
ある。FIG. 4 is a perspective view showing a conventional lithium ion secondary battery.
【図５】図４のＡ−Ａ’断面図である。FIG. 5 is a sectional view taken along line A-A ′ of FIG. 4;
【図６】図４に示す従来の薄型電池用袋体の、側縁シー
ル部を折り曲げた態様を示す要部拡大図である。FIG. 6 is an enlarged view of a main part of the conventional thin battery bag shown in FIG. 4, in which a side edge seal portion is bent.
１ 薄型電池用袋体 ３ 側縁シール部 ３ａ 延長シール部 DESCRIPTION OF SYMBOLS 1 Thin battery bag 3 Side edge seal part 3a Extension seal part
Claims (3)
状のラミネートシートを略半分から２つ折りし、かつ、
両側縁をヒートシールして筒状袋体をつくり、この筒状
袋体内に薄型電池用発電要素を収容し上部開口を密封す
る薄型電池用袋体であって、この袋体の左右両側縁のシ
ール部の底部近傍が内側に延長され延長シール部に形成
されていることを特徴とする薄型電池用袋体。1. A substantially square laminate sheet comprising a metal layer and a sealant layer is folded from about half to two, and
A thin battery bag body which heat seals both side edges to form a cylindrical bag body, accommodates a thin battery power generating element in the cylindrical bag body, and seals an upper opening, and has left and right side edges of the bag body. A thin battery bag, wherein a portion near the bottom of the seal portion is extended inward to form an extended seal portion.
部を底辺とする略三角形に形成されている請求項１記載
の薄型電池用袋体。2. The thin battery bag according to claim 1, wherein the extension seal portion is formed in a substantially triangular shape with the side edge seal portion of the bag body as a base.
れている請求項１または２記載の薄型電池用袋体。3. The thin battery bag according to claim 1, wherein an upper side of the substantially triangular shape is formed in a round shape.