JP2001062972A - Film for facility gardening - Google Patents
Film for facility gardeningInfo
- Publication number
- JP2001062972A JP2001062972A JP24589299A JP24589299A JP2001062972A JP 2001062972 A JP2001062972 A JP 2001062972A JP 24589299 A JP24589299 A JP 24589299A JP 24589299 A JP24589299 A JP 24589299A JP 2001062972 A JP2001062972 A JP 2001062972A
- Authority
- JP
- Japan
- Prior art keywords
- film
- ethylene
- greenhouse
- layer
- tubular film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、施設園芸用フィル
ムに関する。詳しくは、施設園芸用フィルムを施設園芸
ハウスに張る(以下「展張」という)際に、予め一旦一
枚のフィルムとする(以下「開反」という)必要がな
く、展張作業性に優れた、かつ、時間が経過してもフィ
ルム折り目部の強度が低下しにくい施設園芸用フィルム
に関する。The present invention relates to a film for greenhouse horticulture. In detail, when a film for greenhouse horticulture is put on a greenhouse for greenhouse (hereinafter referred to as "extension"), it is not necessary to once make a single film (hereinafter referred to as "opening"), and it is excellent in expansion workability. Further, the present invention relates to a film for greenhouse horticulture in which the strength of the film fold is hardly reduced even after a lapse of time.
【0002】[0002]
【従来の技術】インフレーション法によって成形された
ポリオレフィン系の施設園芸用フィルムは、10m以上
の広幅品の生産が可能であり、幅継ぎの必要がなく継ぎ
部の融着不足等の問題もないため、好適に用いられてい
る。一般に、インフレーション法による多層フィルム
は、数台の加熱された押出機へ投入された熱可塑性樹脂
組成物が、各押出機のスクリューにより混練された後、
円形状のリップを有する加熱されたサーキュラーダイ内
部で各層が積層され、リップより上方に押し出される。
このようにして押し出された溶融状態の筒状フィルムを
バブルと呼ぶが、前記バブルはエアーリングを用いてバ
ブル外周よりエアーを吹き付けて冷却され、図3および
図4に示すようなダブル折りもしくはガゼット折りの筒
状フィルムとされ一対の圧着ロールにて引き取られた後
に紙管等に巻き取られる。2. Description of the Related Art A polyolefin-based horticultural film formed by an inflation method can produce a wide product of 10 m or more, does not require a width joint, and has no problems such as insufficient fusion at a joint. Are preferably used. In general, the multilayer film by the inflation method, after the thermoplastic resin composition put into several heated extruders is kneaded by the screw of each extruder,
The layers are stacked inside a heated circular die having a circular lip and extruded above the lip.
The cylindrical film in the molten state extruded in this manner is called a bubble. The bubble is cooled by blowing air from the outer periphery of the bubble using an air ring, and is double-folded or gusseted as shown in FIGS. After being formed into a folded tubular film and taken up by a pair of pressure rolls, the film is wound around a paper tube or the like.
【0003】圧着された筒状フィルムは、これを開いて
施設園芸ハウスに展張できるようにするため、図3およ
び図4に示すように折り幅片端の折り目にスリット部が
設けられた片開きフィルムとされたり、折り幅の中央部
に長手方向に沿ってスリット部が設けられた観音開きフ
ィルムとされる。前記スリット部を設ける方法には、筒
状フィルムが前記圧着ロールに引き取られた直後にスリ
ット部を設けて紙管等に巻き取る方法と、一旦巻き取ら
れた筒状フィルムの巻物から必要長さだけ繰り出す際に
スリット部を設ける方法がある。[0003] In order to open the crimped cylindrical film so that it can be spread on a greenhouse, a single-opening film provided with a slit portion at a fold at one end as shown in Figs. Or a double-opened film in which a slit portion is provided in the center of the folding width along the longitudinal direction. The method of providing the slit portion includes a method of providing a slit portion immediately after the tubular film is taken up by the pressure roll and winding it around a paper tube or the like, and a method of providing a necessary length from a wound tubular film once wound. There is a method of providing a slit portion when only feeding is performed.
【0004】インフレーション法による施設園芸用フィ
ルムは、幅が3〜8mの場合はダブル折りの状態が多い
が、幅が6mを越え更に10m以上の広幅の場合は、フ
ィルム成形後の取り扱いを簡便にするためにインフレー
ションフィルムの外面に折り込みを入れたコンパクトな
ガゼット折りの状態が一般的である。これらのダブル折
りもしくはガゼット折りされた施設園芸用フィルムは、
一旦一枚のフィルム(以下「シングル」という)とする
工程(以下「開反工程」という)を経た後に折り畳み工
程もしくは絞り工程を経て施設園芸生産者へ配送される
場合(以下「ケースA」という)とダブル折りやガゼッ
ト折りのまま折り畳み工程を経て施設園芸生産者へ配送
される場合(以下「ケースB」という)がある。[0004] In the horticultural film by the inflation method, when the width is 3 to 8 m, the state is often double-folded. When the width is more than 6 m and the width is more than 10 m, the handling after the film is formed is simplified. In general, a compact gusset-folded state in which a fold is formed on the outer surface of the blown film is used. These double-fold or gusset-folded horticultural films are:
Once the film is processed into a single film (hereinafter referred to as "single") (hereinafter referred to as "opening process") and then delivered to the greenhouse horticultural producer through a folding process or a drawing process (hereinafter referred to as "case A") ) And double folds or gusset folds and then delivered to the greenhouse horticulture producer through a folding process (hereinafter referred to as “case B”).
【0005】前記ケースAの場合、ダブル折りされたフ
ィルムをシングルとするのに2〜3人、また、開反工程
の後に縦方向に畳むのにも2〜3人の人手が必要とな
り、多くの労力と時間が費やされてきた。これらの作業
は主としてフィルム加工業者によって行われてきた。ま
た、前記ケースBの場合、すなわち、施設園芸用フィル
ムをダブル折りやガゼット折りのまま折り畳み工程を経
て施設園芸生産者へ配送される場合は、開反工程が省か
れフィルム加工業者の作業は省力化されるが、施設園芸
生産者は施設園芸用フィルムを施設園芸ハウスにへ展張
する直前にシングルとしてから展張したり、折り畳まれ
た施設園芸用フィルムを施設園芸ハウスの長手方向に解
きほぐしてから施設園芸ハウスの上に引き上げて展張し
たりしなければならず、展張作業は施設園芸生産者に多
くの労力や時間の負担をしいるものであった。これらの
展張作業については施設園芸生産者の高齢化にともなっ
て改善が強く望まれていた。In case A, two or three people are required to make the double-folded film into a single film, and two or three people are required to fold the film vertically after the opening step. Effort and time have been spent. These operations have been performed primarily by film processors. In the case B, that is, when the film for greenhouse horticulture is delivered to the greenhouse horticulture producer through the folding process while being double-folded or gusset-folded, the opening process is omitted and the work of the film processor is labor-saving. However, greenhouse horticulture producers can expand the greenhouse horticulture film as a single just before spreading it to the greenhouse, or unfold the greenhouse horticulture film in the longitudinal direction of the greenhouse, and then open the greenhouse. It had to be lifted and extended on top of a horticultural house, and the extension work put a lot of labor and time on the horticultural producers. Improvement of these extension work has been strongly desired with the aging of greenhouse horticultural producers.
【0006】一方、ポリオレフィン系の施設園芸用フィ
ルムは、農業用ポリ塩化ビニルフィルムと比較して保温
性、防曇性、強靭性および透明性などが劣っていたが、
保温性を改良するために特開昭60−104141号公
報に特定の無機質フィラーを添加する技術が、また、防
曇性や強靱性を改良するために特開昭58−90960
号公報には、多層フィルムにおいて、施設園芸ハウスに
展張した際の外層側に線状低密度ポリエチレン、中間層
にエチレン−酢酸ビニル共重合体やオレフィン−ビニル
アルコール共重合体、内層側に線状低密度ポリエチレン
やエチレン酢酸ビニル共重合体を用いた技術が開示され
ている。On the other hand, polyolefin-based horticultural films are inferior in heat retention, anti-fog properties, toughness, transparency, etc. as compared with agricultural polyvinyl chloride films.
The technique of adding a specific inorganic filler to JP-A-60-104141 for improving the heat retention, and JP-A-58-90960 for improving the antifogging property and toughness.
In the multi-layer film, a linear low-density polyethylene is formed on the outer layer side when the greenhouse is spread on a greenhouse, an ethylene-vinyl acetate copolymer or an olefin-vinyl alcohol copolymer is formed on the intermediate layer, and a linear layer is formed on the inner layer. Techniques using low-density polyethylene or ethylene-vinyl acetate copolymer are disclosed.
【0007】近年、従来のマルチサイト触媒に変わって
シングルサイト触媒を用いたエチレン−α−オレフィン
共重合体である線状低密度ポリエチレンの開発が進み、
特開平09−052332号公報や特開平08−276
542号公報にシングルサイト触媒を用いたエチレン−
α−オレフィン共重合体を使用した農業用フィルムが提
案されている。これらの農業用フィルムは、内外層にシ
ングルサイト触媒を用いたエチレン−α−オレフィン共
重合体を使用しており、強靱性は向上するが、防曇性や
防霧性の発現が十分ではなく、防曇剤や防霧剤の添加量
が多いにもかかわらず防曇性や防霧性の持続性が不十分
であった。また、これらの農業用フィルムは施設園芸ハ
ウスへの展張作業性を改善するものではなく、展張には
多くの労力や時間を要するものであった。In recent years, linear low-density polyethylene, which is an ethylene-α-olefin copolymer using a single-site catalyst instead of a conventional multi-site catalyst, has been developed.
JP-A-09-052332 and JP-A-08-276
No. 542 discloses an ethylene-single-site catalyst.
Agricultural films using α-olefin copolymers have been proposed. These agricultural films use an ethylene-α-olefin copolymer using a single-site catalyst for the inner and outer layers, and the toughness is improved, but the antifogging property and the antifogging property are not sufficiently expressed. However, despite the large amounts of antifogging agent and antifog agent added, the antifogging property and the durability of the antifogging property were insufficient. Also, these agricultural films do not improve the workability of spreading to a greenhouse, and the spreading requires much labor and time.
【0008】更に、これらの農業用フィルムを施設園芸
ハウスに展張した際に、折り目部分の強度が時間の経過
につれて低下し、強風などにより折り目部分から破れる
現象が発生することがあった。作物栽培中に施設園芸用
フィルムが破れると作物の生育が阻害されるなどの被害
が発生するため、折り目部分の強度低下に対する改善が
望まれていた。Furthermore, when these agricultural films are spread on a greenhouse, the strength of the folds decreases with the passage of time, and the folds may break from the folds due to strong winds or the like. Breakage of the horticultural film during crop cultivation may cause damage such as hindering the growth of the crop. Therefore, it has been desired to improve the strength reduction at the fold.
【0009】[0009]
【発明が解決しようとする課題】本発明の目的は、良好
な防曇性、防霧性、強靱性を有し、展張作業性に優れ、
かつ、時間の経過とともにフィルム折り目部の強度が低
下しにくい施設園芸フィルムを提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide good anti-fogging properties, anti-fog properties, toughness, excellent workability in spreading,
It is another object of the present invention to provide a greenhouse horticultural film in which the strength of the film fold hardly decreases over time.
【0010】[0010]
【課題を解決するための手段】本発明者らは、前記課題
解決のため鋭意検討した結果、インフレーション法によ
り成形される多層構造の筒状フィルムの内皮を施設園芸
ハウス内面側に位置する内層とし、筒状フィルムの外皮
を施設園芸ハウス外面側に位置する外層とし、かつ、内
層と外層の間に中間層を有する多層構造の施設園芸用フ
ィルムであって、前記外層を構成する組成物の主成分を
耐ブロッキング性と強靭性に優れたエチレン系樹脂と
し、更に内層を構成する組成物の主成分を破れの原因と
なるクラックなどが発生しにくく防曇剤や防霧剤を内層
表面に移行させ易いエチレン系樹脂とし、中間層を構成
する組成物の主成分を強靭性に優れるエチレン系樹脂と
する多層構造のフィルムが前記目的を達成することを見
出し、この知見に基づき本発明を完成するに至った。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to solve the above-mentioned problems, and as a result, have found that the inner skin of the multilayered tubular film formed by the inflation method is an inner layer located on the inner surface side of the greenhouse. An outer layer positioned on the outer surface side of the greenhouse, the outer shell of the tubular film is a multilayer greenhouse gardening film having an intermediate layer between the inner layer and the outer layer, and the main constituent of the composition constituting the outer layer The component is an ethylene-based resin with excellent blocking resistance and toughness.Furthermore, the main component of the composition constituting the inner layer is less likely to cause cracks, etc., which are the cause of tearing, and the anti-fog agent and anti-fog agent are transferred to the inner layer surface. It has been found that a multi-layer film using an ethylene-based resin which is easy to make and a main component of the composition constituting the intermediate layer is an ethylene-based resin having excellent toughness achieves the above-mentioned object. This has led to the completion of the present invention can.
【0011】本発明は、下記の構成を有する。 (1)インフレーション法により成形された筒状フィル
ムに長さ方向に沿ってスリット部を設け、前記スリット
部から前記筒状フィルムを開き施設園芸ハウスに展張す
る際に、前記筒状フィルムの内皮が施設園芸ハウス内面
側に位置する内層(A)であり、前記筒状フィルムの外
皮が施設園芸ハウス外面側に位置する外層(C)であ
り、かつ、内層(A)と外層(C)の間に中間層(B)
を有する多層構造の施設園芸用フィルムであって、前記
筒状フィルムの外皮である外層(C)を構成する組成物
の主成分が密度(dc1)0.88〜0.96g/cm3
のエチレン−α−オレフィン共重合体(c1)もしくは
密度(dc2)0.91〜0.93g/cm3のエチレン
単独重合体(c2)である施設園芸用フィルム。 (2)筒状フィルムの外皮である外層(C)を構成する
組成物の主成分であるエチレン−α−オレフィン共重合
体(c1)が、シングルサイト触媒を用いて重合され
た、密度(dc11)が0.88〜0.93g/cm3のエ
チレン−α−オレフィン共重合体(c11)である前記第
(1)項記載の施設園芸用フィルム。 (3)筒状フィルムの外皮である外層(C)を構成する
組成物の主成分であるエチレン−α−オレフィン共重合
体(c11)が、下記性状を有する共重合体である前記第
(2)項記載の施設園芸用フィルム。 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 (4)筒状フィルムの内皮である内層(A)を構成する
組成物の主成分が、酢酸ビニル含有量が2〜15重量%
のエチレン−酢酸ビニル共重合体である前記第(1)〜
(3)項の何れか1項記載の施設園芸用フィルム。 (5)筒状フィルムの内皮である内層(A)を構成する
組成物が、添加率X重量%と無機質フィラーのBET比
表面積Sm2/gが、1/S≦X≦100/Sの関係を
満足する無機質フィラーの1種以上をさらに添加したも
のである前記第(1)〜(4)項の何れか1項記載の施
設園芸用フィルム。 (6)中間層(B)を構成する組成物の主成分が、シン
グルサイト触媒を用いて重合された、密度(db)が
0.85〜0.93g/cm3で、かつ、下記性状を有
するエチレン−α−オレフィン重合体(b)である前記
第(1)〜(5)項の何れか1項記載の施設園芸用フィ
ルム。 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 (7)スリット部が筒状フィルムの折り幅片端の折り目
部もしくは折り幅中央部に筒状フィルムの長さ方向に沿
って1ヶ所設けられ、かつ、筒状フィルムが長手方向に
折り畳まれている前記第(1)〜(6)項の何れか1項
記載の施設園芸用フィルム。The present invention has the following configuration. (1) The tubular film formed by the inflation method is provided with a slit portion along the length direction, and when the tubular film is opened from the slit portion and spread on a greenhouse, the endothelium of the tubular film is removed. The inner layer (A) located on the inner side of the greenhouse, the outer skin of the tubular film is the outer layer (C) located on the outer side of the greenhouse, and between the inner layer (A) and the outer layer (C). In the middle layer (B)
And a main component of the composition constituting the outer layer (C), which is the outer skin of the tubular film, has a density (d c1 ) of 0.88 to 0.96 g / cm 3.
Greenhouse film is ethylene -α- olefin copolymer (c 1) or density (d c2) 0.91~0.93g / cm 3 of ethylene homopolymer (c 2). (2) An ethylene-α-olefin copolymer (c 1 ), which is a main component of the composition constituting the outer layer (C) that is the outer shell of the tubular film, is polymerized using a single-site catalyst, and has a density ( The film for greenhouse horticulture according to the above (1), wherein d c11 ) is an ethylene-α-olefin copolymer (c 11 ) having a ratio of 0.88 to 0.93 g / cm 3 . (3) The ethylene-α-olefin copolymer (c 11 ) which is a main component of the composition constituting the outer layer (C) which is the outer skin of the tubular film is a copolymer having the following properties. 2) The film for facility horticulture according to the above. a) Melt flow ratio I 10 / I 2 ≧ 5.63 b) Molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) Critical shear stress γ γ> 4 when gross melt fracture begins to occur × 10 6 dyne / cm 2 (4) The main component of the composition constituting the inner layer (A) which is the inner layer of the tubular film has a vinyl acetate content of 2 to 15% by weight.
The above-mentioned (1) to ethylene-vinyl acetate copolymers
The film for greenhouse horticulture according to any one of (3). (5) The composition of the inner layer (A), which is the inner layer of the tubular film, is such that the addition ratio X weight% and the BET specific surface area Sm 2 / g of the inorganic filler are 1 / S ≦ X ≦ 100 / S. The film for greenhouse horticulture according to any one of the above items (1) to (4), further comprising one or more inorganic fillers satisfying the following. (6) The main component of the composition constituting the intermediate layer (B) is polymerized using a single-site catalyst, has a density (d b ) of 0.85 to 0.93 g / cm 3 , and has the following properties The film for greenhouse horticulture according to any one of the above (1) to (5), which is an ethylene-α-olefin polymer (b) having the following. a) Melt flow ratio I 10 / I 2 ≧ 5.63 b) Molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) Critical shear stress γ γ> 4 when gross melt fracture begins to occur × 10 6 dyne / cm 2 (7) A slit portion is provided at one location along the length direction of the tubular film at a fold portion at one end of the folded width of the tubular film or at the center of the folded width. The film for greenhouse horticulture according to any one of the above (1) to (6), which is folded in a longitudinal direction.
【0012】[0012]
【発明の実施の形態】以下、本発明の実施の形態を説明
する。本発明の施設園芸用フィルムは、インフレーショ
ン法により成形された筒状フィルムに長さ方向に沿って
スリット部を設け、前記スリット部から前記筒状フィル
ムを開き施設園芸ハウスに展張する際に、前記筒状フィ
ルムの内皮が施設園芸ハウス内面側に位置する内層
(A)であり、前記筒状フィルムの外皮が施設園芸ハウ
ス外面側に位置する外層(C)であり、かつ、内層
(A)と外層(C)の間に中間層(B)を有する3層以
上の多層構造の施設園芸用フィルムである。なお、本発
明において組成物の「主成分」とは、組成物に50重量
%以上含まれた成分を指す。Embodiments of the present invention will be described below. The film for facility horticulture of the present invention is provided with a slit portion along the length direction in a tubular film formed by an inflation method, and when the tubular film is opened from the slit portion and expanded to a facility horticulture house, The inner layer of the tubular film is an inner layer (A) located on the inner surface side of the greenhouse, the outer skin of the tubular film is an outer layer (C) located on the outer surface of the greenhouse, and the inner layer (A). It is a film for greenhouse horticulture having a multilayer structure of three or more layers having an intermediate layer (B) between outer layers (C). In the present invention, the “main component” of the composition refers to a component contained in the composition in an amount of 50% by weight or more.
【0013】本発明の施設園芸用フィルムにおいて、筒
状フィルムの外皮である外層(C)を構成する組成物の
主成分は、エチレン−α−オレフィン共重合体(c1)
もしくは密度(dc2)0.91〜0.93g/cm3の
エチレン単独重合体(c2)である。前記エチレン−α
−オレフィン共重合体(c1)は、エチレンと炭素原子
数が3〜20のα−オレフィンとのランダム共重合体で
あり、チーグラー触媒等のマルチサイト触媒やメタロセ
ン触媒等のシングルサイト触媒を用いて重合され、その
密度(dc1)は0.88〜0.96g/cm3、好まし
くは0.89〜0.93g/cm3である。密度
(dc1)が0.88g/cm3の未満の場合にはエチレ
ン−α−オレフィン共重合体(c1)の融点が低下し太
陽光線の照射により施設園芸用フィルム同志が融着し易
くなる傾向がある。また、密度(dc1)が0.96g/
cm3を越える場合には施設園芸用フィルムの柔軟性が
低下し展張時や回収時の作業性が低下するおそれがあ
る。In the greenhouse horticulture film of the present invention, the main component of the composition constituting the outer layer (C) which is the outer skin of the tubular film is an ethylene-α-olefin copolymer (c 1 ).
Alternatively, it is an ethylene homopolymer (c 2 ) having a density (d c2 ) of 0.91 to 0.93 g / cm 3 . The ethylene-α
The olefin copolymer (c 1 ) is a random copolymer of ethylene and an α-olefin having 3 to 20 carbon atoms, using a multi-site catalyst such as a Ziegler catalyst or a single-site catalyst such as a metallocene catalyst. polymerized Te, its density (d c1) is 0.88~0.96g / cm 3, preferably 0.89~0.93g / cm 3. When the density (d c1 ) is less than 0.88 g / cm 3 , the melting point of the ethylene-α-olefin copolymer (c 1 ) is lowered and the horticultural films are easily fused together by irradiation with sunlight. Tend to be. Further, the density (d c1 ) is 0.96 g /
If it exceeds cm 3 , the flexibility of the greenhouse horticultural film may be reduced, and the workability at the time of spreading and collection may be reduced.
【0014】前記炭素原子数が3〜20のα−オレフィ
ンとしては、プロピレン、1−ブテン、1−ペンテン、1
−ヘキセン、4−メチル−1−ペンテン、1−オクテン、1
−デセン、1−ドデセン、1−テトラデセン、1−ヘキサ
デセン、1−オクタデセン、1−エイコセンなどが挙げら
れ、エチレン−α−オレフィン共重合体(c1)中のα
−オレフィン重合単位の割合は1〜45重量%、好まし
くは2〜35重量%である。The α-olefin having 3 to 20 carbon atoms includes propylene, 1-butene, 1-pentene,
-Hexene, 4-methyl-1-pentene, 1-octene, 1
-Decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1-eicosene and the like, and α in the ethylene-α-olefin copolymer (c 1 ).
The proportion of polymerized olefin units is from 1 to 45% by weight, preferably from 2 to 35% by weight;
【0015】特に、前記エチレン−α−オレフィン共重
合体(c1)が、シングルサイト触媒を用いて重合され
た、密度(dc11)が0.88〜0.93g/cm3のエ
チレン−α−オレフィン共重合体(c11)であると、強
靱性に優れ、外層(C)表面がべたつきにくい施設園芸
用フィルムにすることができる。エチレン−α−オレフ
ィン共重合体(c11)の密度(dc11)が、0.88g
/cm3未満であるとエチレン−α−オレフィン共重合
体(c11)の融点が低下し太陽光線の照射により施設園
芸用フィルム同志が融着し易くなる傾向がある。また、
密度(dc11)が0.93g/cm3のを越えると施設園
芸用フィルムの柔軟性が低下し展張時や回収時の作業性
が低下するおそれがある。In particular, the ethylene-α-olefin copolymer (c 1 ) is polymerized using a single-site catalyst and has a density (d c11 ) of 0.88 to 0.93 g / cm 3 . -If it is an olefin copolymer (c 11 ), it can be formed into a greenhouse horticultural film having excellent toughness and having a less sticky outer layer (C) surface. The density (d c11 ) of the ethylene-α-olefin copolymer (c 11 ) is 0.88 g
If it is less than / cm 3 , the melting point of the ethylene-α-olefin copolymer (c 11 ) will decrease, and the films for greenhouse horticulture will tend to fuse together by irradiation with sunlight. Also,
If the density (d c11 ) exceeds 0.93 g / cm 3 , the flexibility of the greenhouse horticultural film may decrease, and the workability at the time of spreading or collection may decrease.
【0016】エチレン−α−オレフィン共重合体
(c11)を重合するために用いられるシングルサイト触
媒としては、チタン、ジルコニウム、ハフニウム、バナ
ジウムなどの元素の周期表第IV又はV族遷移金属のメタ
ロセン化合物と、有機アルミニウム化合物及び/又はイ
オン性化合物の組合せが用いられる。The single-site catalyst used for polymerizing the ethylene-α-olefin copolymer (c 11 ) includes a metallocene of a transition metal of Group IV or V of the Periodic Table of elements such as titanium, zirconium, hafnium and vanadium. A combination of a compound and an organoaluminum compound and / or an ionic compound is used.
【0017】前記メタロセン化合物としては、少なくと
も一個のシクロペンタジエニル基、置換シクロペンタジ
エニル基、ヒドロカルビル珪素などによって架橋された
もの、さらにシクロペンタジエニル基が酸素、窒素、燐
原子に架橋されたものを配位子とする公知のメタロセン
化合物をいずれも使用できる。The metallocene compound may be a compound obtained by crosslinking at least one cyclopentadienyl group, a substituted cyclopentadienyl group, hydrocarbyl silicon, or the like, and a compound obtained by crosslinking a cyclopentadienyl group to oxygen, nitrogen, and phosphorus atoms. Any known metallocene compound having a compound as a ligand can be used.
【0018】これらのメタロセン化合物の具体例として
は、ジメチルシリル(2、4−ジメチルシクロペンタジエ
ニル)(3'、5'−ジメチルシクロペンタジエニル)ジルコ
ニウムジクロライド、ジメチルシリル(2、4−ジメチル
シクロペンタジエニル)(3'、5'−ジメチルシクロペンタ
ジエニル)ハフニウムジクロライドなどのケイ素架橋型
メタロセン化合物、エチレンビスインデニルジルコニウ
ムジクロライド、エチレンビスインデニルハフニウムジ
クロライド、エチレンビス(メチルインデニル)ジルコニ
ウムジクロライド、エチレンビス(メチルインデニル)ハ
フニウムジクロライドなどのインデニル系架橋型メタロ
セン化合物を挙げることができる。Specific examples of these metallocene compounds include dimethylsilyl (2,4-dimethylcyclopentadienyl) (3 ', 5'-dimethylcyclopentadienyl) zirconium dichloride, dimethylsilyl (2,4-dimethyl Silicon-bridged metallocene compounds such as (cyclopentadienyl) (3 ′, 5′-dimethylcyclopentadienyl) hafnium dichloride, ethylenebisindenyl zirconium dichloride, ethylenebisindenylhafnium dichloride, ethylenebis (methylindenyl) zirconium Examples include indenyl crosslinked metallocene compounds such as dichloride and ethylenebis (methylindenyl) hafnium dichloride.
【0019】メタロセン化合物との組合せで用いられる
有機アルミニウム化合物としては、一般式−(Al
(R)O)n−で示される直鎖状、あるいは環状重合体
(Rは炭素数1〜10の炭化水素基であり、一部ハロゲ
ン原子及び/又はRO基で置換されたものも含む。nは重合
度であり、5以上、好ましくは10以上である)であ
り、具体例としてRがそれぞれメチル、エチル、イソブ
チル基である、メチルアルモキサン、エチルアルモキサ
ン、イソブチルエチルアルモキサンなどが挙げられる。The organoaluminum compound used in combination with the metallocene compound is represented by the general formula-(Al
(R) O) n- a linear or cyclic polymer (R is a hydrocarbon group having 1 to 10 carbon atoms, including those partially substituted with a halogen atom and / or an RO group. n is the degree of polymerization and is 5 or more, preferably 10 or more), and specific examples include methylalumoxane, ethylalumoxane, and isobutylethylalumoxane, wherein R is each a methyl, ethyl, or isobutyl group. Can be
【0020】さらに、その他の有機アルミニウム化合物
としては、トリアルキルアルミニウム、ジアルキルハロ
ゲノアルミニウム、セスキアルキルハロゲノアルミニウ
ム、アルケニルアルミニウム、ジアルキルハイドロアル
ミニウム、セスキアルキルハイドロアルミニウムなどが
挙げられる。Further, other organic aluminum compounds include trialkylaluminum, dialkylhalogenoaluminum, sesquialkylhalogenoaluminum, alkenylaluminum, dialkylhydroaluminum, sesquialkylhydroaluminum and the like.
【0021】イオン性化合物としては、一般式 [Q]m+ [Y]m- (mは1以上の整数) で示されるものであり、式中のQはイオン性化合物のカ
チオン成分であり、カルボニウムイオン、トロピリウム
カチオン、アンモニウムカチオン、オキソニウムカチオ
ン、スルホニウムカチオン、ホスホニウムカチオン等が
挙げられる。また、Yはイオン性化合物のアニオン成分
であり、メタロセン化合物と反応して安定なアニオンと
なる成分であって、有機硼素化合物アニオン、有機アル
ミニウム化合物アニオン、有機ガリウム化合物アニオ
ン、有機燐化合物アニオン、有機砒素化合物アニオン、
有機アンチモン化合物アニオン等が挙げられる。The ionic compound is represented by the general formula [Q] m + [Y] m- (m is an integer of 1 or more), wherein Q is a cation component of the ionic compound, And a cationium ion, a tropylium cation, an ammonium cation, an oxonium cation, a sulfonium cation, and a phosphonium cation. Y is an anionic component of an ionic compound, which is a component that reacts with a metallocene compound to form a stable anion, and includes an organic boron compound anion, an organic aluminum compound anion, an organic gallium compound anion, an organic phosphorus compound anion, and an organic compound. Arsenic compound anions,
Organic antimony compound anions and the like.
【0022】シングルサイト系触媒を用いて行うエチレ
ンとα−オレフィンの共重合方法としては公知の重合方
法が用いられ、気相重合法、スラリー重合法、溶液重合
法などが挙げられる。As a method for copolymerizing ethylene and an α-olefin using a single-site catalyst, a known polymerization method is used, and examples thereof include a gas phase polymerization method, a slurry polymerization method, and a solution polymerization method.
【0023】シングルサイト触媒により重合されたエチ
レン−α−オレフィン共重合体は従来のチーグラーナッ
タ触媒のようなマルチサイト触媒のものと比較して、分
子量分布が狭く、α−オレフィンの高含有量のものも均
一に重合され、ラメラ間のタイ分子が多い等の特徴があ
ることから、低分子量成分が少なく耐ブロッキング性に
優れ、透明性、耐衝撃性、強靱性に優れた特性を有す
る。The ethylene-α-olefin copolymer polymerized by the single-site catalyst has a narrower molecular weight distribution and a higher α-olefin content than that of a multi-site catalyst such as a conventional Ziegler-Natta catalyst. Since they are also polymerized uniformly and have many tie molecules between lamellae, they have low molecular weight components, are excellent in blocking resistance, and are excellent in transparency, impact resistance, and toughness.
【0024】シングルサイト触媒を用いて重合されたエ
チレン−α−オレフィン共重合体(c11)は、重量平均
分子量(Mw)と数平均分子量(Mn)の比であるQ値
(Mw/Mn)が1.5〜3.5である。また、190
℃、2.16kgfの荷重条件におけるメルトフローレ
ート(以下、MFRという)は0.2〜20/10分で
あり、示差走査熱量測定法(DSC)による融解ピーク
は2つ以上であっても構わない。The ethylene-α-olefin copolymer (c 11 ) polymerized using a single-site catalyst has a Q value (Mw / Mn) which is a ratio of a weight average molecular weight (Mw) to a number average molecular weight (Mn). Is 1.5 to 3.5. Also, 190
The melt flow rate (hereinafter, referred to as MFR) under a load condition of 2.16 kgf at 0.2 ° C. is 0.2 to 20/10 minutes, and the number of melting peaks by differential scanning calorimetry (DSC) may be two or more. Absent.
【0025】また、エチレン−α−オレフィン共重合体
(c11)が、下記性状を有するエチレン−α−オレフィ
ン共重合体(c12)であると、インフレーション法によ
り多層構造の筒状フィルムを成形する際に、押出機のモ
ーターに加わる負荷を軽減し、比較的低い押出温度でも
表面平滑性に優れたフィルムを得ることができる。 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 中でも、メルトフロー比I10/I2は、好ましくは5.
63〜50、より好ましくは7〜30、更に好ましくは
8〜20であり、分子量分布Mw/Mnは好ましくは
1.5〜2.5であり、更に好ましくは1.7〜2.3
である。また、臨界せん断応力γは、好ましく4×10
6〜10×106dyne/cm2である。Further, when the ethylene-α-olefin copolymer (c 11 ) is the ethylene-α-olefin copolymer (c 12 ) having the following properties, a cylindrical film having a multilayer structure is formed by an inflation method. In doing so, the load applied to the motor of the extruder can be reduced, and a film having excellent surface smoothness can be obtained even at a relatively low extrusion temperature. a) Melt flow ratio I 10 / I 2 ≧ 5.63 b) Molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) Critical shear stress γ γ> 4 when gross melt fracture begins to occur Even at 10 6 dyne / cm 2 , the melt flow ratio I 10 / I 2 is preferably 5.
63 to 50, more preferably 7 to 30, still more preferably 8 to 20, and the molecular weight distribution Mw / Mn is preferably 1.5 to 2.5, more preferably 1.7 to 2.3.
It is. The critical shear stress γ is preferably 4 × 10
It is 6 to 10 × 10 6 dyne / cm 2 .
【0026】ここで、メルトフロー比I10/I2、分子
量分布Mw/Mnおよびグロスメルトフラクチャーが起
こり始める時の臨界せん断応力γは、特開平6−306
121号公報に記載されているように、メルトフロー比
は、ASTM D−1238に基づいて、190℃10
kgの荷重条件で測定されるメルトインデックスI10と
190℃2.16kgの荷重条件で測定されるメルトイ
ンデックスI2の比で表される。臨界せん断応力はガス
・イクストルージョン・レオメーター(GER)により
測定され、グロスメルトフラクチャーが起こり始める時
の臨界せん断応力は、不安定な流れ条件下で規則的もし
くは不規則的な歪みとして捉えられ、GERによって押
出される押出物の表面荒さ及び形状の変化に基づいて測
定される。Here, the melt flow ratio I 10 / I 2 , the molecular weight distribution Mw / Mn and the critical shear stress γ at which gross melt fracture begins to occur are described in JP-A-6-306.
As described in JP-A-121, the melt flow ratio is 190 ° C. 10 based on ASTM D-1238.
expressed as the ratio of the melt index I 2 measured at a load condition of the melt index I 10 and 190 ° C. 2.16 kg as measured at a load condition of kg. Critical shear stress is measured by a gas extrusion rheometer (GER), and the critical shear stress at which gross melt fracture begins to occur is considered as a regular or irregular strain under unstable flow conditions. , GER, based on the change in surface roughness and shape of the extrudate extruded.
【0027】インフレーション法により筒状フィルムを
成形するために、エチレン−α−オレフィン共重合体
(c1)を押出機で溶融・混練する際に、押出機のモー
ター負荷の上昇、混練による自己発熱または溶融樹脂押
出時の筒状フィルムの表面荒れなどが発生する場合があ
る。特に、シングルサイト触媒を用いて重合されたエチ
レン−α−オレフィン共重合体(c11)は均一な分子量
となりやすく、分子量分布が狭くなるため、これらの加
工時の課題が発生しやすい傾向がある。これらの加工時
の課題を解決するために筒状フィルムの外皮である外層
(C)を構成する組成物に低密度ポリエチレンを添加し
たり、押出温度を高めに設定する等の方法が取られてい
るが、強靭性の低下や熱劣化の発生につながるため好ま
しい方法ではない。When the ethylene-α-olefin copolymer (c 1 ) is melted and kneaded with an extruder in order to form a cylindrical film by the inflation method, the motor load of the extruder is increased, and self-heating is caused by kneading. Alternatively, the surface of the cylindrical film may be roughened during the extrusion of the molten resin. In particular, the ethylene-α-olefin copolymer (c 11 ) polymerized using a single-site catalyst tends to have a uniform molecular weight and a narrow molecular weight distribution, and thus tends to cause problems during processing. . In order to solve these problems at the time of processing, methods such as adding low-density polyethylene to the composition constituting the outer layer (C), which is the outer skin of the tubular film, and setting the extrusion temperature higher are taken. However, this is not a preferred method because it leads to a decrease in toughness and the occurrence of thermal degradation.
【0028】また、筒状フィルムを成形する際のエチレ
ン−α−オレフィン共重合体(c1)の自己発熱または
設定温度上昇は、筒状フィルムの外皮のみならず筒状フ
ィルムの内皮の温度をも上昇させるため、筒状フィルム
内皮同志が密着(ブロッキング)し、スリット部から開
きにくくなる傾向がある。前記加工時の課題は、エチレ
ン−α−オレフィン共重合体(c11)としてエチレン−
α−オレフィン共重合体(c12)を用いることにより強
靭性の低下や熱劣化の発生なしに解消される。In addition, the self-heating of the ethylene-α-olefin copolymer (c 1 ) or the rise in the set temperature at the time of forming the cylindrical film may be caused by not only the temperature of the inner skin of the cylindrical film but also the temperature of the inner skin of the cylindrical film. , The inner surfaces of the tubular film tend to adhere to each other (block), making it difficult for the inner surface to open from the slit. The problem at the time of the processing is that the ethylene-α-olefin copolymer (c 11 )
The use of the α-olefin copolymer (c 12 ) eliminates the problem without lowering the toughness or causing thermal deterioration.
【0029】前記エチレン−α−オレフィン共重合体
(c12)は、特開平6−306121号公報に記載され
ているような拘束幾何触媒(constrained geometry cata
lyst)を用いて重合することができるが、市販品を用い
てもよい。市販品としては、ダウケミカル日本(株)発
売のアフィニティ PF1140、PL1880、FM
1570(何れも商品名)やエリート5100、5400
(何れも商品名)を例示することができる。The ethylene-α-olefin copolymer (c 12 ) is prepared by using a constrained geometry catalyst as described in JP-A-6-306121.
lyst), but commercially available products may be used. Commercially available products include Affinity PF1140, PL1880, FM sold by Dow Chemical Japan Co., Ltd.
1570 (both trade names) and Elite 5100, 5400
(All are trade names).
【0030】本発明の施設園芸用フィルムにおいて、筒
状フィルムの外皮である外層(C)を構成する組成物の
主成分として用いられるエチレン単独重合体(c2)
は、密度(dc2)が0.91〜0.93g/cm3であ
る。エチレン単独重合体は公知の高圧法ラジカル法や前
記シングルサイト触媒を用いて重合されたものが用いら
れる。エチレン単独重合体(c2)の密度(dc2)が
0.91g/cm3未満であるとエチレン単独重合体
(c2)の融点が低下し太陽光線の照射により施設園芸
用フィルム同志が融着し易くなる傾向がある。また、密
度(dc2)が0.93g/cm3を越えると施設園芸用
フィルムの柔軟性が低下し展張時や回収時の作業性が低
下するおそれがある。In the greenhouse horticulture film of the present invention, ethylene homopolymer (c 2 ) used as a main component of the composition constituting the outer layer (C), which is the outer skin of the tubular film
Has a density (d c2 ) of 0.91 to 0.93 g / cm 3 . As the ethylene homopolymer, a polymer obtained by polymerization using a known high-pressure radical method or the single-site catalyst is used. Ethylene homopolymer (c 2) a density (d c2) is 0.91 g / cm 3 less than a is ethylene homopolymer (c 2) horticulture film each other by irradiation melting point is lowered sunlight of fusion It tends to be easy to wear. On the other hand, if the density (d c2 ) exceeds 0.93 g / cm 3 , the flexibility of the greenhouse horticultural film may decrease, and the workability at the time of spreading or collection may decrease.
【0031】なお、筒状フィルムの外皮である外層
(C)を構成する組成物には、前記エチレン−α−オレ
フィン共重合体、エチレン単独重合体、更に異種のエチ
レン−α−オレフィンや異種のエチレン単独重合体を2
種以上を併用してもよい。The composition constituting the outer layer (C), which is the outer skin of the cylindrical film, includes the above-mentioned ethylene-α-olefin copolymer, ethylene homopolymer, different ethylene-α-olefin and different ethylene-α-olefin. 2 ethylene homopolymers
More than one species may be used in combination.
【0032】本発明の施設園芸用フィルムにおいて、筒
状フィルムの内皮である内層(A)を構成する組成物の
主成分としては、公知の高密度ポリエチレン、低密度ポ
リエチレン、線状低密度ポリエチレン等のポリエチレン
系樹脂をはじめとして、ポリプロピレン樹脂、ポリエス
テル樹脂、ポリアミド樹脂などの熱可塑性樹脂が挙げら
れるが、中でも、筒状フィルムの外層(C)を構成する
組成物の主成分であるエチレン−α−オレフィン共重合
体もしくはエチレン単独重合体と共押出によりインフレ
ーション成形ができ、かつ、得られる施設園芸用フィル
ムの防曇性などの性能が良好であるため、酢酸ビニル含
有量が2〜15重量%であるエチレン−酢酸ビニル共重
合体(a)が好適に用いられる。前記エチレン−酢酸ビ
ニル共重合体(a)中の酢酸ビニル含有量が2重量%未
満であると、得られる施設園芸用フィルムの防曇性特に
低温時の発現効果が得られにくく、防曇持続性も低下す
る傾向がある。また、前記酢酸ビニル含有量が15重量
%を越える場合には、フィルム同志が密着したり、屋外
に放置した際に太陽光線により蓄熱し、フィルム同志が
融着するおそれがある。In the greenhouse horticultural film of the present invention, the main component of the composition constituting the inner layer (A) which is the inner layer of the tubular film is a known high-density polyethylene, low-density polyethylene, linear low-density polyethylene, or the like. And thermoplastic resins such as polypropylene resin, polyester resin, and polyamide resin. Among them, ethylene-α-, which is a main component of the composition constituting the outer layer (C) of the tubular film, is exemplified. Inflation molding can be performed by co-extrusion with an olefin copolymer or an ethylene homopolymer, and the resulting facility horticultural film has good performance such as anti-fogging property. Therefore, the vinyl acetate content is 2 to 15% by weight. Certain ethylene-vinyl acetate copolymer (a) is preferably used. When the vinyl acetate content in the ethylene-vinyl acetate copolymer (a) is less than 2% by weight, it is difficult to obtain the antifogging property of the obtained greenhouse horticultural film, especially at low temperatures, and to maintain the antifogging property. Also tends to decrease. If the vinyl acetate content exceeds 15% by weight, the films may adhere to each other or may be stored by the sun rays when left outdoors, and the films may fuse together.
【0033】エチレン−酢酸ビニル共重合体(a)は、
エチレンと酢酸ビニルを公知の高圧ラジカル重合プロセ
スにより反応させて製造され、そのMFRは0.1〜1
0好ましくは0.5〜5g/10分のものが使用され
る。MFRが小さすぎるとフィルムの成形性、特に押出
加工性、高速延伸性が悪くなる。MFRが大きすぎると
フィルムの成形性、特にインフレーション成形における
バブルの安定性が低下するおそれがある。The ethylene-vinyl acetate copolymer (a) is
It is produced by reacting ethylene and vinyl acetate by a known high-pressure radical polymerization process, and has an MFR of 0.1 to 1
0, preferably 0.5 to 5 g / 10 min. If the MFR is too small, the moldability of the film, particularly the extrudability and high-speed stretchability, deteriorate. If the MFR is too large, the moldability of the film, particularly the stability of bubbles in inflation molding, may be reduced.
【0034】また、筒状フィルムの内皮を構成する組成
物の主成分として前記エチレン−酢酸ビニル共重合体
(a)を用いることにより、筒状フィルムの外皮を構成
する組成物としてエチレン−α−オレフィン共重合体や
エチレン単独重合体を用いる場合に、時間の経過に伴っ
て発生する筒状フィルム折り目部分の強度低下を防止す
ることができる。従って、本発明の施設園芸用フィルム
においては、筒状フィルムの内皮である内層(A)を構
成する組成物の主成分としてエチレン−酢酸ビニル共重
合体(a)を用いるのが好ましく、筒状フィルムの外皮
である外層(C)を構成する組成物の主成分としてエチ
レン−α−オレフィン共重合体(c1)もしくはエチレ
ン単独重合体(c2)、好ましくはエチレン−α−オレ
フィン共重合体(c11)、さらに好ましくはエチレン−
α−オレフィン共重合体(c12)が用いられる。Further, by using the ethylene-vinyl acetate copolymer (a) as a main component of the composition constituting the inner skin of the tubular film, ethylene-α- In the case of using an olefin copolymer or an ethylene homopolymer, it is possible to prevent a decrease in the strength of the folded portion of the tubular film which occurs with the passage of time. Therefore, in the film for greenhouse horticulture of the present invention, it is preferable to use the ethylene-vinyl acetate copolymer (a) as a main component of the composition constituting the inner layer (A) which is the inner skin of the tubular film. Ethylene-α-olefin copolymer (c 1 ) or ethylene homopolymer (c 2 ), preferably ethylene-α-olefin copolymer, as the main component of the composition constituting the outer layer (C) which is the outer skin of the film (C 11 ), more preferably ethylene-
α-olefin copolymer (c 12 ) is used.
【0035】本発明の施設園芸用フィルムにおいては、
筒状フィルムの内皮である内層(A)を構成する組成物
の主成分としてエチレン−酢酸ビニル共重合体(a)
を、筒状フィルムの外皮である外層(C)を構成する組
成物の主成分としてエチレン−α−オレフィン共重合体
(c12)が用いることにより、筒状フィルム内皮同志の
ブロッキングが少なく、開反性がよくて展張性に優れ、
施設園芸ハウスへの展張後の時間の経過に伴う折り目強
度低下が著しく改善された施設園芸フィルムを得ること
ができる。また、成形時のモーター負荷の上昇も少なく
筒状フィルム表面の肌荒れもない。In the greenhouse horticulture film of the present invention,
Ethylene-vinyl acetate copolymer (a) as a main component of the composition constituting the inner layer (A) which is the inner layer of the tubular film
By using an ethylene-α-olefin copolymer (c 12 ) as a main component of the composition constituting the outer layer (C) which is the outer skin of the tubular film, the blocking of the tubular film endothelium is reduced, and It has good reactivity and excellent extensibility,
It is possible to obtain a greenhouse horticultural film in which the decrease in the fold strength with time after the spread to the greenhouse is remarkably improved. Also, there is no increase in motor load during molding and there is no rough surface on the surface of the tubular film.
【0036】本発明においては、筒状フィルムの内皮で
ある内層(A)を構成する組成物には、フィルム同志の
ブロッキングを防止するため、1種以上の無機質フィラ
ーが添加され、その添加率X(重量%)と無機質フィラ
ーのBET比表面積S(m2/g)が、1/S≦X≦1
00/Sの関係を満足することが望ましい。なお、BE
T比表面積はJIS Z 8830に従って測定され
る。添加率Xが1/Sより少ない場合は、フィルム同志
がブロッキングし易くなり、また、添加率Xが100/
Sより大きい場合は、透明性や機械的強度が低下する。In the present invention, one or more inorganic fillers are added to the composition constituting the inner layer (A), which is the inner skin of the tubular film, in order to prevent blocking between the films. (% By weight) and the BET specific surface area S (m 2 / g) of the inorganic filler are 1 / S ≦ X ≦ 1
It is desirable to satisfy the relationship of 00 / S. In addition, BE
The T specific surface area is measured according to JIS Z 8830. When the addition rate X is less than 1 / S, the films are likely to be blocked easily, and the addition rate X is 100 / S.
If it is larger than S, the transparency and the mechanical strength decrease.
【0037】前記無機質フィラーとしては、酸化珪素、
珪酸マグネシウム、珪酸アルミニウム、珪酸カルシウム
等の珪酸化合物、アルミノ珪酸カルシウム、アルミノ珪
酸ナトリウム、アルミノ珪酸カリウム等のアルミノ珪酸
化合物、アルミナ、アルミン酸ナトリウム、アルミン酸
カリウム、アルミン酸カルシウム等のアルミン酸化合
物、炭酸カルシウム、下記1式で示されるハイドロタル
サイト類や下記2式や3式で示されるリチウム・アルミ
ニウム複合水酸化物塩等の群から選ばれる1種以上の無
機フィラーが挙げられる。As the inorganic filler, silicon oxide,
Silicate compounds such as magnesium silicate, aluminum silicate and calcium silicate; aluminosilicate compounds such as calcium aluminosilicate, sodium aluminosilicate and potassium aluminosilicate; aluminate compounds such as alumina, sodium aluminate, potassium aluminate and calcium aluminate; Examples of the inorganic filler include calcium, hydrotalcites represented by the following formula (1), and lithium-aluminum composite hydroxide salts represented by the following formulas (2) and (3).
【0038】[0038]
【化1】 [Al2Li(OH)6]2(An-)・mH2O −式1 (式中、mは3以下の数を示す。)Embedded image [Al 2 Li (OH) 6 ] 2 (A n− ) · mH 2 O—Formula 1 (where m represents a number of 3 or less)
【0039】[0039]
【化2】 [Al2(Li(1-x)・M2+ x)(OH)6]2 ・(SiyO2y+1 2-)1+x・mH2O −式2 (式中、M2+は2価の金属、mは0≦m<5の範囲にあ
る数、xは0≦x<1の範囲にある数、yは2≦y≦4
の範囲にある数を示す。)Embedded image [Al 2 (Li (1-x) · M 2+ x ) (OH) 6 ] 2 · (Si y O 2y + 1 2 ) 1 + x · mH 2 O-Formula 2 , M 2+ is a divalent metal, m is a number in the range of 0 ≦ m <5, x is a number in the range of 0 ≦ x <1, y is 2 ≦ y ≦ 4
Indicates a number in the range. )
【0040】[0040]
【化3】 M2+ 1-xAlx(OH)2(An-)x/2・mH2O −式3 (式中、M2+はMg2+、Ca2+、およびZn2+の中から
選ばれた少なくとも1種の2価金属イオンを示し、An-
はn価のアニオン、xおよびmは次の条件、0<x<
0.5、0≦m≦2を満足する。) Embedded image M 2 + 1 -x Al x (OH) 2 (A n− ) x / 2 .mH 2 O-Formula 3 (where M 2+ is Mg 2+ , Ca 2+ , and Zn 2 + represents at least one divalent metal ion selected from among, a n-
Is an n-valent anion, x and m are the following conditions, 0 <x <
0.5, 0 ≦ m ≦ 2. )
【0041】前記無機質フィラーは、必要に応じて筒状
フィルムの内皮である内層(A)だけでなく他の層を構
成する組成物にも添加することができる。その場合、前
記無機質フィラーの群から選ばれた1種を単独で添加し
ても、2種以上を併用してもよい。The inorganic filler can be added, if necessary, not only to the inner layer (A), which is the inner layer of the tubular film, but also to the composition constituting other layers. In that case, one kind selected from the group of the inorganic fillers may be added alone, or two or more kinds may be used in combination.
【0042】本発明の施設園芸用フィルムにおいて、筒
状フィルムの中間層(B)を構成する組成物の主成分と
しては、公知の高密度ポリエチレン、低密度ポリエチレ
ン、線状低密度ポリエチレン等のポリエチレン系樹脂を
はじめとして、ポリプロピレン樹脂、ポリエステル樹
脂、ポリアミド樹脂などの熱可塑性樹脂が挙げられる
が、中でも、得られる施設園芸用フィルムの強靱性や表
面平滑性、押出機モーター負荷の上昇を防ぎ押出温度を
低く抑えるフィルムの成形性の観点から、シングルサイ
ト触媒を用いて重合された、密度(db)が0.85〜
0.93g/cm3で、 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 であるエチレン−α−オレフィン共重合体(b)が好適
に用いられる。なお、エチレン−α−オレフィン共重合
体(b)はエチレン−α−オレフィン共重合体(c12)
と同一であってもよい。In the greenhouse horticulture film of the present invention, the main component of the composition constituting the intermediate layer (B) of the tubular film is a known high-density polyethylene, low-density polyethylene, or linear low-density polyethylene. Thermoplastic resins such as polypropylene resin, polyester resin, and polyamide resin, among others, can be cited. Among them, the toughness and surface smoothness of the resulting greenhouse horticultural film, the increase in the motor load of the extruder, and the extrusion temperature In view of the moldability of the film, the density (d b ) polymerized using a single-site catalyst is 0.85 to 0.85.
0.93 g / cm 3 , a) melt flow ratio I 10 / I 2 ≧ 5.63 b) molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) when gross melt fracture begins to occur The ethylene-α-olefin copolymer (b) having a critical shear stress γγ> 4 × 10 6 dyne / cm 2 is preferably used. The ethylene-α-olefin copolymer (b) is an ethylene-α-olefin copolymer (c 12 )
May be the same as
【0043】本発明の施設園芸用フィルムにおいては、
筒状フィルムの外層(C)、内層(A)および中間層
(B)を構成する組成物に、必要に応じて、柔軟性を向
上させるためにシングルサイト触媒や公知のマルチサイ
ト触媒で重合されたエチレン−ジエン弾性共重合体、エ
チレンープロピレン弾性共重合体やスチレン−ブタジエ
ン系弾性共重合体等の弾性共重合体を添加することがで
き、更に、通常の施設園芸用フィルムに用いられている
公知の、無機質もしくは有機質の保温剤、防曇剤、ヒン
ダードアミン系耐候剤、紫外線吸収剤、防霧剤(フッ素
系界面活性剤)、帯電防止剤、滑剤、アンチブロッキン
グ剤、酸化防止剤、熱安定剤、抗菌剤、色素・着色剤な
どを添加することができる。また、筒状フィルムの内面
に、コーンスターチや馬鈴薯等の澱粉を付着させ、フィ
ルム同志のブロッキングを更に緩和させることができ
る。In the film for greenhouse horticulture of the present invention,
The composition constituting the outer layer (C), the inner layer (A) and the intermediate layer (B) of the tubular film is polymerized with a single-site catalyst or a known multi-site catalyst to improve flexibility, if necessary. Elastic copolymers such as ethylene-diene elastic copolymers, ethylene-propylene elastic copolymers and styrene-butadiene-based elastic copolymers can be added, and further used in ordinary greenhouse horticultural films. Known inorganic or organic warming agents, anti-fogging agents, hindered amine weathering agents, ultraviolet absorbers, anti-fog agents (fluorinated surfactants), antistatic agents, lubricants, anti-blocking agents, antioxidants, heat Stabilizers, antibacterial agents, dyes / colorants, and the like can be added. Further, starch such as corn starch or potato can be adhered to the inner surface of the tubular film to further reduce blocking between the films.
【0044】本発明の施設園芸用フィルムの厚みは、使
用する場所や耐用年数等により異なるが、一般的に0.
05〜0.3mm程度のものが好適に用いられる。内層
の厚みと外層の厚みは特に限定されるものではないが、
全層厚みの5〜50%の範囲が好適に用いられる。な
お、本発明の施設園芸用フィルムの中間層は、1層から
構成されていても、2層以上から構成されていてもよ
い。また、本発明の施設園芸用フィルムは、透明でも、
梨地でも、半梨地であってもいずれでも良く、施設園芸
用のハウスやトンネル等の被覆用以外のマルチング用、
袋掛け用等の用途に使用することもできる。The thickness of the greenhouse horticultural film of the present invention varies depending on the place where the film is used and the service life thereof.
Those having a thickness of about 05 to 0.3 mm are preferably used. Although the thickness of the inner layer and the thickness of the outer layer are not particularly limited,
A range of 5 to 50% of the total layer thickness is preferably used. In addition, the intermediate | middle layer of the film for greenhouse horticulture of this invention may be comprised from one layer, and may be comprised from two or more layers. The film for greenhouse horticulture of the present invention is transparent,
For pears and semi-pears, it may be any, and for mulching other than covering such as greenhouses and tunnels for facility horticulture,
It can also be used for applications such as bagging.
【0045】本発明の施設園芸用フィルムは、インフレ
ーション法により成形された筒状フィルムに長さ方向に
沿ってスリット部を設け、前記スリット部から前記筒状
フィルムを開き施設園芸ハウスに展張する際に、前記筒
状フィルムの内皮が施設園芸ハウス内面側に位置する内
層(A)であり、前記筒状フィルムの外皮が施設園芸ハ
ウス外面側に位置する外層(C)であり、かつ、内層
(A)と外層(C)の間に中間層(B)を有する多層構
造の施設園芸用フィルムであるが、スリット部が筒状フ
ィルムの折り幅片端の折り目部もしくは折り幅中央部に
筒状フィルムに長さ方向に沿って1ヶ所設けられ、か
つ、筒状フィルムが長手方向に折り畳まれたフィルムで
あると、予め開反を行なわなくとも、施設園芸ハウスへ
の展張作業を容易に行なうことができる。すなわち、前
記施設園芸用フィルムは、ダブル折りやガゼット折りの
まま施設園芸生産者へ配送され、容易に施設園芸ハウス
へ展張される。In the facility horticulture film of the present invention, a slit portion is provided along a length direction in a tubular film formed by an inflation method, and the tubular film is opened from the slit portion to be extended to a facility horticulture house. The inner skin of the tubular film is an inner layer (A) located on the inner surface side of the greenhouse, the outer skin of the tubular film is an outer layer (C) located on the outer surface of the greenhouse, and the inner layer ( A multi-layered horticultural film having an intermediate layer (B) between the outer layer (A) and the outer layer (C), and the slit portion is formed at the fold portion at one end of the fold width of the cylindrical film or at the center of the fold width. If it is provided at one place along the length direction and the tubular film is a film folded in the longitudinal direction, it can be easily spread to the greenhouse without the need to open it in advance. Ukoto can. That is, the film for greenhouse horticulture is delivered to the greenhouse horticulture producer in a double fold or gusset fold, and is easily spread to the greenhouse horticulture house.
【0046】以下に、本発明の施設園芸用フィルムを施
設園芸ハウスに展張する方法を例示する。前記ダブル折
りやガゼット折りされた施設園芸用フィルムには、折り
幅片端の折り目部に開口用のスリット部が設けられた片
開きフィルムタイプと折り幅の中央部に長手方向に沿っ
て開き口が設けられた観音開きフィルムタイプがあり、
各々のタイプにより本発明の施設園芸用フィルムの施設
園芸ハウスへの展張方法は異なる。Hereinafter, a method for spreading the film for greenhouse horticulture of the present invention in a greenhouse horticulture will be described. The double-fold or gusset-folded horticultural film has a single-opening film type in which a slit portion for opening is provided at a fold portion at one end of a folding width and an opening along a longitudinal direction at a central portion of the folding width. There is a double door film type provided,
The extension method of the facility horticulture film of the present invention to the facility horticulture house differs depending on each type.
【0047】片開きフィルムタイプの場合、長手方向に
折り畳まれた施設園芸用フィルムを、施設園芸ハウスの
張設部1(図1)の妻面2(図1)に対して折り目(図
1)がスリット部4(図1)よりも遠方であって、妻面
1に対してスリット部4が平行となるようにハウス張設
部1の妻面2の下方に設置し、前記施設園芸用フィルム
の裁断部5(図1)より、ハウス張設部1へ繰り出しな
がら張設する。In the case of the single-opening film type, the greenhouse horticultural film folded in the longitudinal direction is folded (FIG. 1) with respect to the end surface 2 (FIG. 1) of the stretched portion 1 (FIG. 1) of the greenhouse. Is located farther than the slit portion 4 (FIG. 1), and is installed below the wife surface 2 of the house extending portion 1 so that the slit portion 4 is parallel to the wife surface 1. From the cutting portion 5 (FIG. 1) of the house while being extended to the house extending portion 1.
【0048】観音開きフィルムタイプの場合、長手方向
に折り畳まれた施設園芸用フィルムを、スリット部4
(図2)が施設園芸ハウス張設部1(図2)の妻面2
(図2)を向き、施設園芸ハウス張設部1の妻面2に対
して裁断部5(図2)が平行となるようにハウス張設部
1の妻面2の下方に設置し、前記施設園芸用フィルムの
裁断部5より、ハウス張設部1へ繰り出しながら張設す
る。In the case of the double-opening film type, the facility gardening film folded in the longitudinal direction is inserted into the slit portion 4.
(Fig. 2) is the wife's face 2 of the facility horticulture house extension part 1 (Fig. 2).
(FIG. 2), the cutting section 5 (FIG. 2) is installed below the wife surface 2 of the house stretching section 1 so that the cutting section 5 (FIG. 2) is parallel to the wife surface 2 of the facility horticulture house stretching section 1. The film is stretched out from the cutting section 5 of the greenhouse horticultural film to the house stretching section 1.
【0049】前記片開きタイプと観音開きタイプの何れ
の施設園芸用フィルムの展張方法においても、施設園芸
用ハウスと施設園芸用フィルムの摩擦を低減するため
に、また、施設園芸用ハウスの突起物により施設園芸用
フィルムに破れが生じないようにするために、妻面上部
に回転治具等を設置して、施設園芸用フィルムの破れ防
止を行なうことができる。また、本発明の施設園芸用フ
ィルムの展張作業性を更に向上させる目的から、必要に
応じ筒状フィルムが長手方向に折り畳まれる前にスリッ
ト部よりエアーを注入、圧着することができる。In any of the above-described one-side opening type and two-way opening type horticultural film expanding methods, in order to reduce friction between the horticultural horticulture house and the horticultural horticultural film, and by using the protrusions of the horticultural horticultural house. In order to prevent the facility horticultural film from being torn, a rotating jig or the like may be installed on the upper part of the wife's face to prevent the facility horticultural film from being torn. In addition, for the purpose of further improving the spreadability of the film for greenhouse horticulture of the present invention, air can be injected from the slit portion and pressed before the cylindrical film is folded in the longitudinal direction, if necessary.
【0050】[0050]
【実施例】以下、実施例および比較例によって本発明を
具体的に説明するが、本発明はこれらにより限定される
ものではない。The present invention will be described below in more detail with reference to examples and comparative examples, but the present invention is not limited to these examples.
【0051】実施例および比較例において用いられた熱
可塑性樹脂を以下に示す。 エリート 5400 ダウケミカルジャパン(株)製 ・シンク゛ルサイト触媒系エチレン-α-オレフィン共重合体樹脂(S-LLDPE) ・MFR;1.0g/10min.、密度;0.916g/cm3 アフィニティ PF1140 ダウケミカルジャパン
(株)製 ・シンク゛ルサイト触媒系エチレン-α-オレフィン共重合体樹脂(S-LLDPE) ・MFR;1.6g/10min.、密度;0.895g/cm3 ユメリット 1520F 宇部興産(株)製 ・シンク゛ルサイト触媒系エチレン-α-オレフィン共重合体樹脂(S-LLDPE) ・MFR;2.0g/10min.、密度;0.913g/cm3 ユメリット 0540F 宇部興産(株)製 ・シンク゛ルサイト触媒系エチレン-α-オレフィン共重合体樹脂(S-LLDPE) ・MFR;4.0g/10min.、密度;0.904g/cm3 NUC3270 日本ユニカー(株)製 ・エチレン酢酸ヒ゛ニル共重合体樹脂(酢酸ヒ゛ニル含有量7.5%)(EV
A) ・MFR;2.3g/10min.、密度;0.925g/cm3 ウルトラセン 630 東ソー(株)製 ・エチレン酢酸ヒ゛ニル共重合体樹脂(酢酸ヒ゛ニル含有量15%)(EVA) ・MFR;1.5g/10min.、密度;0.936g/cm3 ニポロン−L FR151A 東ソー(株)製 ・マルチサイト触媒系エチレン-α-オレフィン共重合体樹脂(M-LLDPE) ・MFR;0.9g/10min.、密度;0.924g/cm3 NUC8505 日本ユニカー(株)製 ・高圧法低密度ホ゜リエチレン(LDPE) ・MFR0.8g/10min.、密度0.923g/cm3 The thermoplastic resins used in the examples and comparative examples are shown below. Elite 5400 manufactured by Dow Chemical Japan Co., Ltd. ・ Think Persite catalyst-based ethylene-α-olefin copolymer resin (S-LLDPE) ・ MFR: 1.0 g / 10 min., Density: 0.916 g / cm 3 affinity PF1140 Dow Chemical Japan (・ Think Persite catalyst ethylene-α-olefin copolymer resin (S-LLDPE) ・ MFR: 1.6g / 10min., Density: 0.895g / cm 3 Yumerit 1520F Ube Industries, Ltd. ・ Think Persite catalyst -Based ethylene-α-olefin copolymer resin (S-LLDPE) ・ MFR: 2.0g / 10min., Density: 0.913g / cm 3 Yumerit 0540F manufactured by Ube Industries, Ltd. ・ Think Persite catalyst-based ethylene-α-olefin copolymer Polymer resin (S-LLDPE)-MFR: 4.0 g / 10 min., Density: 0.904 g / cm 3 NUC3270 manufactured by Nippon Unicar Co., Ltd.-Ethylene divinyl acetate copolymer resin (7.5% divinyl acetate content) (EV
A) · MFR: 2.3 g / 10 min., Density: 0.925 g / cm 3 Ultracene 630 manufactured by Tosoh Corporation · Ethylene divinyl acetate copolymer resin (vinyl acetate content 15%) (EVA) · MFR: 1.5 g 0.936 g / cm 3 Nipolon-L FR151A manufactured by Tosoh Corporation ・ Multi-site catalytic ethylene-α-olefin copolymer resin (M-LLDPE) ・ MFR: 0.9 g / 10 min., Density; 0.924g / cm 3 NUC8505 Nippon Unicar Co., Ltd. ・ High pressure method low density polyethylene (LDPE) ・ MFR 0.8g / 10min., Density 0.923g / cm 3
【0052】上記熱可塑性樹脂のそれぞれの特性は、下
記条件にて測定を実施した。 a)MFR;JIS K 7210に従って190℃、
2.16kgfの条件で測定した。 b)密度;JIS K 7112に従って測定した。The characteristics of each of the above thermoplastic resins were measured under the following conditions. a) MFR; 190 ° C. according to JIS K 7210,
It was measured under the condition of 2.16 kgf. b) Density: measured according to JIS K7112.
【0053】実施例および比較例における筒状フィルム
の評価方法は次の通りである。 1)成形試験;サーキュラーダイリップクリアランスが
2.0mmであるサーキュラーダイを備え、50mmφ
押出機3台を有する3種3層インフレーションフィルム
製膜試験機を用い、押出温度(サーキュラーダイリップ
温度)160、170、180、190℃にて、厚さ
0.1mm(厚さ比、内層:中間層:外層=1:3:
1)、成形幅0.6mの3層構造の筒状フィルムを成形
して製膜性を評価し、得られた筒状フィルムのブロッキ
ング性を評価した。なお、筒状フィルムの折り幅片端の
折り目部に開反のためのスリット部を設けた。 1−1)製膜性;各押出温度で成形されたフィルム表面
を観察し、下記評価基準に従い評価を実施した。 ○:メルトフラクチャーがなく良好な状態。 △:若干メルトフラクチャーが認められる状態。 ×:メルトフラクチャーが継続して認められ、実用に耐
えない状態。The evaluation method of the cylindrical film in the examples and comparative examples is as follows. 1) Molding test; equipped with a circular die having a circular die lip clearance of 2.0 mm and a diameter of 50 mm
0.1 mm thickness (thickness ratio, inner layer: middle) at an extrusion temperature (circular die lip temperature) of 160, 170, 180 and 190 ° C. using a three-type three-layer blown film forming tester having three extruders. Layer: outer layer = 1: 3:
1) A cylindrical film having a three-layer structure with a width of 0.6 m was molded, the film forming property was evaluated, and the blocking property of the obtained cylindrical film was evaluated. In addition, a slit part for opening was formed in the fold part of one end of the folding width of the cylindrical film. 1-1) Film-forming property: The surface of the film formed at each extrusion temperature was observed and evaluated according to the following evaluation criteria. :: good state without melt fracture. Δ: Slight melt fracture is observed. X: A state in which melt fracture is continuously observed and is not practical.
【0054】1−2)耐ブロッキング性;各押出温度で
成形され紙管にダブル巻きされた圧着状態の筒状フィル
ムをスリット部から手で開反して密着(ブロッキング)
性を下記評価基準に従い評価した。 ○:フィルム同士の密着が全くない状態。 △:フィルム同士の密着が見られるが、容易に剥離する
ことができる状態。 ×:フィルム同士の密着が激しく、剥離するのに難があ
り、無理に剥離させようとすると、破れが発生する状
態。1-2) Blocking resistance: A press-bonded cylindrical film formed at each extrusion temperature and double-wound around a paper tube is opened by hand from the slit portion and adhered (blocking).
The property was evaluated according to the following evaluation criteria. :: No adhesion between films. Δ: A state in which adhesion between the films is observed, but the films can be easily peeled. ×: A state in which the films are strongly adhered to each other and have difficulty in peeling, and when the film is forcibly peeled, tearing occurs.
【0055】2)引張特性の変化;上記成形試験の最適
押出温度で成形された厚さ0.1mm、成形幅0.6m
の3層構造の筒状フィルムを開反して間口5mのアーチ
パイプハウスに1年間(98年4月〜99年4月)展張し
た後、折り目部強度と折り目部以外の引張強さと伸びを
測定し、展張前と比較して、時間の経過に伴う折り目部
強度の変化を評価した。引張強さと伸びの測定は、JI
S K 7127に従い筒状フィルムの横方向(TD)
について行なった。折り目部の測定は、折り目が引張方
向に対して垂直で、試験片標線間の中央になるようにし
て実施した。2) Change in tensile properties; thickness 0.1 mm, molding width 0.6 m molded at the optimal extrusion temperature in the molding test.
After opening the three-layered tubular film in the arch pipe house with a width of 5 m for one year (April 1998 to April 1999), the fold strength and the tensile strength and elongation other than the fold part were measured. The change in the strength of the fold portion over time was evaluated as compared with that before stretching. For measurement of tensile strength and elongation, refer to JI
Lateral direction (TD) of tubular film according to S K 7127
It was performed about. The measurement of the fold was performed so that the fold was perpendicular to the tensile direction and was located at the center between the test piece reference lines.
【0056】3)低温防曇性;傾斜10度、直径3イン
チの天窓を有するウォーターバスを使用し、該ウォータ
ーバスの天窓にフィルムサンプルを固定し、環境温度2
3℃、水温45℃の条件下で12日間放置後、環境温度
5℃、水温15℃の条件下で2日間放置し、サンプルの
ウォーターバス側表面の防曇性を5段階基準にて目視判
定し、低温防曇性を評価した。5段階の数字が大きい
程、低温防曇性に優れる。 <低温防曇性 評価基準> 評価5:水滴の付着がなく均一な水膜を形成。 評価4:水滴の付着が15%未満である。 評価3:水滴の付着が40%未満である。 評価2:水滴の付着が65%未満である。 評価1:水滴の付着が65%以上である。3) Low-temperature anti-fog property: Using a water bath having a skylight of 10 degrees in inclination and 3 inches in diameter, fixing a film sample to the skylight of the water bath, and setting an environmental temperature of 2
After leaving for 12 days under the condition of 3 ° C. and water temperature of 45 ° C., it was left for 2 days under the condition of environmental temperature of 5 ° C. and water temperature of 15 ° C., and the antifogging property of the water bath side surface of the sample was visually judged based on five levels. Then, the low-temperature antifogging property was evaluated. The larger the five-stage number, the better the low-temperature antifogging property. <Evaluation criteria for low-temperature antifogging property> Evaluation 5: A uniform water film was formed without adhesion of water droplets. Evaluation 4: Adhesion of water droplets is less than 15%. Evaluation 3: Adhesion of water droplets is less than 40%. Evaluation 2: Adhesion of water droplets is less than 65%. Evaluation 1: Adhesion of water droplets is 65% or more.
【0057】7)防曇持続性;傾斜10度、直径3イン
チの天窓を有するウォーターバスを使用し、該ウォータ
ーバスの天窓にフィルムサンプルを固定し、環境温度2
3℃、水温45℃の条件下で昼夜放置し、防曇性が維持
された期間を目視評価した。日数が長い程、防曇持続性
が良いことを示す。7) Antifogging persistence: Using a water bath having a 10-degree tilted, 3-inch diameter skylight, fixing a film sample to the skylight of the water bath, and setting the environmental temperature to 2
It was left standing day and night under the conditions of 3 ° C. and a water temperature of 45 ° C., and the period during which the antifogging property was maintained was visually evaluated. The longer the number of days, the better the antifogging durability.
【0058】実施例1〜8、比較例1〜6 各3構造筒状フィルムの配合例と評価結果を表1〜2に
示す。なお、表中の実施例の内層A、中間層B、外層C
は、それぞれ3層に積層された筒状フィルムの内皮、中
間層、外皮を指し、比較例の内層A、中間層B、外層C
は、それぞれ3層に積層された筒状フィルムの外皮、中
間層、内皮を指す。また、引張特性の変化の押出温度は
成形試験における最適押出温度である。Examples 1 to 8 and Comparative Examples 1 to 6 Tables 1 and 2 show the composition examples and evaluation results of the three-structure tubular films. Note that the inner layer A, the intermediate layer B, and the outer layer C of the examples in the table are shown.
Indicates an inner layer, an intermediate layer, and an outer layer of a cylindrical film laminated in three layers, respectively, and an inner layer A, an intermediate layer B, and an outer layer C of a comparative example.
Indicates an outer skin, an intermediate layer, and an inner skin of a cylindrical film laminated in three layers. The extrusion temperature at which the tensile properties change is the optimum extrusion temperature in the molding test.
【0059】なお、表1〜2の配合例に記載のDHT4
A−2は、BET比表面積13m2/gを有するMg−
Al複合水酸化物塩(協和化学工業(株)製)であり、
フジレインLS(A)は、BET比表面積11m2/g
を有するLi−Al−Mg−Siは複合水酸化物塩(富
士化学工業(株)製)であり、サイシリア310は、B
ET比表面積300m2/gを有する二酸化ケイ素(富
士シシリア(株)製)である。また、防曇剤は、ジグリ
セリンモノステアレート:ジエタノールステアリルアミ
ンジステアレート:ジエタノールアミン=2:7:1
(重量比)の混合物である。DHT4 described in the formulation examples of Tables 1 and 2
A-2 is Mg- having a BET specific surface area of 13 m 2 / g.
Al composite hydroxide salt (manufactured by Kyowa Chemical Industry Co., Ltd.)
Fujirain LS (A) has a BET specific surface area of 11 m 2 / g.
Is a composite hydroxide salt (manufactured by Fuji Chemical Industry Co., Ltd.),
Silicon dioxide having an ET specific surface area of 300 m 2 / g (manufactured by Fuji Sicilia Corporation). The antifogging agent is diglycerin monostearate: diethanol stearylamine distearate: diethanolamine = 2: 7: 1.
(Weight ratio).
【0060】表1〜2に記載された以外の添加剤とし
て、内層Aを構成する組成物に、ヒンダードアミン系耐
候剤0.5重量%、紫外線吸収剤0.05重量%、フェ
ノール系安定剤0.1重量%、リン系安定剤0.1重量%を、
中間層Bを構成する組成物には、ヒンダードアミン系耐
候剤0.5重量%、紫外線吸収剤0.05重量%、フッ
素系界面活性剤0.2重量%、フェノール系安定剤0.1重量
%、リン系安定剤0.1重量%を、外層Cを構成する組成
物には、ヒンダードアミン系耐候剤0.5重量%、紫外
線吸収剤0.05重量%、フッ素系界面活性剤0.2重量
%、フェノール系安定剤0.1重量%、リン系安定剤0.1重
量%を添加した。As additives other than those described in Tables 1 and 2, 0.5% by weight of a hindered amine-based weathering agent, 0.05% by weight of an ultraviolet absorber, and 0.1% of a phenolic stabilizer were added to the composition constituting the inner layer A. % By weight, 0.1% by weight of phosphorus-based stabilizer
The composition constituting the intermediate layer B contains 0.5% by weight of a hindered amine-based weathering agent, 0.05% by weight of an ultraviolet absorber, 0.2% by weight of a fluorine-based surfactant, 0.1% by weight of a phenol-based stabilizer, and 0.1% by weight of a phosphorus-based stabilizer. 0.1% by weight of the agent, 0.5% by weight of a hindered amine-based weathering agent, 0.05% by weight of an ultraviolet absorber, 0.2% by weight of a fluorine-based surfactant, 0.1% by weight of a phenol-based stabilizer %, And 0.1% by weight of a phosphorus-based stabilizer.
【0061】実施例1〜8と比較例1〜6を比較する
と、筒状フィルムの内皮をハウス外面側の外層とした場
合より、前記内皮をハウス内面側の内層とした場合の方
が時間の経過に伴う折り目部の強度低下が少なく、更
に、前記内皮であるハウス内面側の内層を構成する組成
物の主成分をエチレン−酢酸ビニル共重合体とすること
により折り目部の強度低下が更に改善された。また、前
記内皮であるハウス内面側の内層を構成する組成物の主
成分をエチレン酢酸ビニル共重合体とし、筒状フィルム
の外皮であるハウス外面側の外層を構成する組成物の主
成分をエチレン−α−オレフィン共重合体とした場合に
フィルム同志のブロッキングが課題となったが、シング
ルサイト触媒を用いて重合された特定のエチレン−α−
オレフィン共重合体を使用することにより低温でのフィ
ルム成形が可能となり、フィルム同志のブロッキングも
解消され、口開き性および開反加工性の良好な施設園芸
用フィルムを得ることができた。When Examples 1 to 8 and Comparative Examples 1 to 6 are compared, it takes more time when the inner skin of the tubular film is used as the inner layer on the inner surface side of the house than when the inner skin is used as the outer layer on the outer surface side of the house. The decrease in the strength of the fold portion with the passage of time is small, and the decrease in the strength of the fold portion is further improved by using an ethylene-vinyl acetate copolymer as a main component of the composition constituting the inner layer of the inner surface of the house as the inner skin. Was done. Further, the main component of the composition constituting the inner layer of the inner surface of the house as the inner skin is an ethylene vinyl acetate copolymer, and the main component of the composition constituting the outer layer of the outer surface of the house which is the outer skin of the tubular film is ethylene. When the α-olefin copolymer was used, blocking between films became a problem, but specific ethylene-α-polymerized using a single-site catalyst was used.
By using an olefin copolymer, film forming at low temperature became possible, blocking between films was eliminated, and a film for greenhouse horticulture with good openability and openability was obtained.
【0062】実施例9 90mmφ押出機3台を有する3種3層インフレーショ
ンフィルムの生産用大型機を用い、実施例1と同様な配
合で押出温度170℃にて厚さ0.1mm、成形幅4m
の3層構造のフィルムを成形し、折り幅片端の折り目部
にスリット部が設けられた片開きフィルムとし、紙管に
巻き取り施設園芸用フィルムとした。この、施設園芸用
フィルムを紙管から長さ50mを繰り出して、ダブル折
りの状態で長手方向に折り畳み、施設園芸ハウスを有す
る圃場へ搬送した。次に、間口4mで長さ40mの施設
園芸ハウス張設部1(図1)の妻面2(図1)に対して
折り目3(図1)がスリット部4(図1)よりも遠方で
あって、妻面2に対してスリット部4が平行となるよう
に施設園芸ハウス張設部1の妻面2の下方に設置し、施
設園芸用フィルムの裁断部5(図1)より、施設園芸ハ
ウスの天面である張設部へ繰り出しながら展張した。こ
の際、施設園芸用フィルム裁断部の幅方向両端部を1名
ずつ保持しながら、地面上を移動することにより展張す
ることができた。Example 9 Using a large-sized three-layer, three-layer blown film production machine having three 90 mmφ extruders, the same composition as in Example 1 at an extrusion temperature of 170 ° C., a thickness of 0.1 mm and a molding width of 4 m.
Was formed into a single-opening film in which a slit portion was provided at a fold portion at one end of a folding width, and was wound around a paper tube to obtain a film for facility horticulture. The film for facility horticulture was fed out from a paper tube by 50 m in length, folded in the longitudinal direction in a double fold state, and transported to a field having a facility horticulture house. Next, the crease 3 (FIG. 1) is farther than the slit portion 4 (FIG. 1) with respect to the wife surface 2 (FIG. 1) of the facility horticulture house extension 1 (FIG. 1) having a width of 4 m and a length of 40 m. Then, it is installed below the wife surface 2 of the facility horticulture house extension part 1 so that the slit portion 4 is parallel to the wife surface 2, and the facility horticulture film is cut from the cutting portion 5 (FIG. 1). We extended it to the top of the horticultural house while stretching it out. At this time, the film could be spread by moving on the ground while holding both ends in the width direction of the film cutting portion for greenhouse horticulture one by one.
【0063】比較例7 90mmφ押出機3台を有する3種3層インフレーショ
ンフィルムの生産用大型機を用い、比較例1と同様な配
合で成形温度170℃にて厚さ0.1mm、成形幅4m
の3層構造のフィルムを成形し、折り幅片端の折り目が
スリットされ開き口が設けられた片開きフィルムとし、
紙管に巻き取り施設園芸用フィルムとした。この、施設
園芸用フィルムを紙管から長さ50mを繰り出して、ダ
ブル折りの状態で長手方向に折り畳み、施設園芸用ハウ
スを有する圃場へ搬送した。次に、間口4mで長さ40
mの施設園芸ハウスの長手方向の地面へ繰り出した後
に、ダブル折りの状態から一枚物(シングル)の状態とし
ながら、ハウス天面へ繰り出しながら展張した。この際
に、施設園芸ハウスの天面に2名が登って作業する必要
があった。COMPARATIVE EXAMPLE 7 Using a large-sized three-layer, three-layer blown film production machine having three 90 mmφ extruders, the same composition as in Comparative Example 1 was used at a molding temperature of 170 ° C., a thickness of 0.1 mm, and a molding width of 4 m.
A three-layered film is formed, and a fold at one end of the folding width is slit to form a single-opening film provided with an opening,
The film was wound into a paper tube and used as a facility horticulture film. The film for facility horticulture was drawn out from a paper tube by 50 m in length, folded in the longitudinal direction in a double fold state, and transported to a field having a house for facility horticulture. Next, at the frontage 4m, length 40
After extending to the ground in the longitudinal direction of the m horticulture house, it was unfolded from the double-folded state to a single (single) state and extended to the top of the house. At this time, it was necessary for two people to climb and work on the top of the greenhouse.
【0064】本発明の実施例9と従来技術の比較例7を
比較すると、実施例9では施設園芸用ハウスの長手方向
に繰り出す作業がなく、折り畳まれた施設園芸用フィル
ムをを直接展張に供することが可能でありこれまでの展
張作業を簡素化できる。また、施設園芸ハウスの天面に
登る必要がないことから安全であり、地面に居ながらに
して展張できることから突風等の緊急時の対応が取りや
すい等のメリットが認めらる。Comparing the ninth embodiment of the present invention with the comparative example 7 of the prior art, in the ninth embodiment, there is no work of feeding out the greenhouse for facility horticulture in the longitudinal direction, and the folded greenhouse horticulture film is directly extended. It is possible to simplify the existing expansion work. In addition, it is safe because it is not necessary to climb the top of the greenhouse, and it can be deployed while staying on the ground.
【0065】[0065]
【表1】 [Table 1]
【0066】[0066]
【表2】 [Table 2]
【0067】[0067]
【発明の効果】本発明の施設園芸用フィルムは、ダブル
折りやガゼット折りされた施設園芸用フィルムを特定の
構成とすることにより時間の経過に伴う折り目部分の強
度低下を防止することが可能となり、また、特定の展張
方法とすることにより展張作業性及び安全性が向上する
ことから、施設園芸ハウスの被覆資材およびその展張方
法として好適に用いることができる。The greenhouse horticultural film of the present invention can prevent the strength of the fold portion from decreasing with the lapse of time by using a double fold or gusset-folded greenhouse horticultural film with a specific configuration. Moreover, since the spreading workability and safety are improved by adopting a specific spreading method, it can be suitably used as a covering material for a facility gardening house and its spreading method.
【図1】図1は、片開きの施設園芸用フィルムの施設園
芸ハウスへの展張方法を示す。BRIEF DESCRIPTION OF DRAWINGS FIG. 1 shows a method of spreading a single-opening facility horticulture film to a facility horticulture house.
【図2】図2は、観音開きの施設園芸用フィルムの施設
園芸ハウスへの展張方法を示す。FIG. 2 shows a method of extending a double-opening horticulture film to a horticulture house.
【図3】図3は、片開きのダブル折り施設園芸用フィル
ムを示す。FIG. 3 shows a single-folding double-fold facility horticultural film.
【図4】図4は、観音開きのガゼット折り施設園芸用フ
ィルムを示す。FIG. 4 shows a double-folded gusset-folded horticultural film.
【図5】図5は、本発明に関わる施設園芸用フィルムの
断面図の一例である。FIG. 5 is an example of a cross-sectional view of a facility horticulture film according to the present invention.
1・・・・・・施設園芸用フィルムの施設園芸ハウスへの張設
部。 2・・・・・・施設園芸ハウスの妻面。 3・・・・・・施設園芸用フィルムの折り目部。 4・・・・・・施設園芸用フィルムのスリット部。 5・・・・・・施設園芸用フィルムの裁断部。 6・・・・・・筒状フィルムの外皮であってハウス外面側の外
層。 7・・・・・・筒状フィルムの内皮と外皮の間に位置する中間
層。 8・・・・・・筒状フィルムの内皮であってハウス内面側の内
層。1 ... The section where the film for greenhouse horticulture is installed on the greenhouse for greenhouse. 2. The wife of the greenhouse. 3. The fold of the film for greenhouse horticulture. 4 Slit part of film for greenhouse horticulture. 5 ... Cutting part of film for greenhouse horticulture. 6 ... An outer layer on the outer surface side of the house, which is the outer skin of the tubular film. 7 ... An intermediate layer located between the inner skin and the outer skin of the tubular film. 8 An inner layer on the inner surface side of the house, which is the inner skin of the tubular film.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) C08K 3/00 C08K 3/00 4J028 C08L 23/06 C08L 23/06 23/08 23/08 // C08F 4/645 C08F 4/645 C08J 5/18 CES C08J 5/18 CES Fターム(参考) 2B024 DA07 DB01 DB08 2B029 EB04 EC02 EC09 EC19 RA01 RA03 4F071 AA15 AA15X AA20X AA21X AA28X AA82X AB18 AB19 AB21 AB26 AE11 AF14 AF53 AF56 AH01 BA01 BB06 BB09 BC01 BC07 4F100 AA01B AK04A AK04B AK22B AK62A AK62C AK68B AL01B BA03 BA06 BA10A BA10B BA16 CA23B GB01 JA06A JA06C JA07A JA07C JA13A JA13C JK01 JK03A JK03C JL05 JL07 JL08A JL08C YY00A YY00B YY00C 4J002 BB03W BB03X BB05W BB06X BB12X BB15W CF00X CL00X DE146 DE186 DE236 DE286 DJ006 DJ016 FD016 FD176 GA01 GF00 4J028 AA01A AB00A AB01A AC02A AC23A BA00A BA01B BB00A BB01B BC15B BC16B BC18B BC24B BC25B CA42C CB65C CB81C CB86C CB94C EB02 EB03 EB04 EB05 EB07 EB08 EB09 EB10 EC02 FA02 FA03 FA04 GA06 GA08 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification code FI Theme coat ゛ (Reference) C08K 3/00 C08K 3/00 4J028 C08L 23/06 C08L 23/06 23/08 23/08 // C08F 4 / 645 C08F 4/645 C08J 5/18 CES C08J 5/18 CES F term (reference) 2B024 DA07 DB01 DB08 2B029 EB04 EC02 EC09 EC19 RA01 RA03 4F071 AA15 AA15X AA20X AA21X AA28X AA82X AB18 AB19 AB21 AF26 BB09 BC01 BC07 4F100 AA01B AK04A AK04B AK22B AK62A AK62C AK68B AL01B BA03 BA06 BA10A BA10B BA16 CA23B GB01 JA06A JA06C JA07A JA07C JA13A JA13C JK01 JK03A JK03C JL05 JL07 JL08A JL08C YY00A YY00B YY00C 4J002 BB03W BB03X BB05W BB06X BB12X BB15W CF00X CL00X DE146 DE186 DE236 DE286 DJ006 DJ016 FD016 FD176 GA01 GF00 4J028 AA01A AB00A AB01A AC02A AC23A BA00A BA01B BB00A BB0 1B BC15B BC16B BC18B BC24B BC25B CA42C CB65C CB81C CB86C CB94C EB02 EB03 EB04 EB05 EB07 EB08 EB09 EB10 EC02 FA02 FA03 FA04 GA06 GA08
Claims (7)
フィルムに長さ方向に沿ってスリット部を設け、前記ス
リット部から前記筒状フィルムを開き施設園芸ハウスに
展張する際に、前記筒状フィルムの内皮が施設園芸ハウ
ス内面側に位置する内層(A)であり、前記筒状フィル
ムの外皮が施設園芸ハウス外面側に位置する外層(C)
であり、かつ、内層(A)と外層(C)の間に中間層
(B)を有する多層構造の施設園芸用フィルムであっ
て、前記筒状フィルムの外皮である外層(C)を構成す
る組成物の主成分が密度(dc1)0.88〜0.96g
/cm3のエチレン−α−オレフィン共重合体(c1)も
しくは密度(dc2)0.91〜0.93g/cm3のエ
チレン単独重合体(c2)である施設園芸用フィルム。1. A tubular film formed by an inflation method is provided with a slit portion along a length direction, and when the tubular film is opened from the slit portion and spread on a facility gardening house, the tubular film is formed. The inner layer is the inner layer (A) located on the inner surface side of the greenhouse, and the outer layer of the tubular film is the outer layer (C) located on the outer surface of the greenhouse.
And a multi-layered horticultural film having an intermediate layer (B) between the inner layer (A) and the outer layer (C), which constitutes the outer layer (C) which is the outer skin of the tubular film. The main component of the composition has a density (d c1 ) of 0.88 to 0.96 g.
/ Cm 3 of ethylene -α- olefin copolymer (c 1) or density (d c2) horticulture film is 0.91~0.93G / cm 3 of ethylene homopolymer (c 2).
成する組成物の主成分であるエチレン−α−オレフィン
共重合体(c1)が、シングルサイト触媒を用いて重合
された、密度(dc11)が0.88〜0.93g/cm3
のエチレン−α−オレフィン共重合体(c11)である請
求項1記載の施設園芸用フィルム。2. An ethylene-α-olefin copolymer (c 1 ) which is a main component of a composition constituting an outer layer (C) which is an outer shell of a cylindrical film is polymerized using a single-site catalyst. Density (d c11 ) of 0.88 to 0.93 g / cm 3
The greenhouse horticultural film according to claim 1, which is an ethylene-α-olefin copolymer (c 11 ).
成する組成物の主成分であるエチレン−α−オレフィン
共重合体(c11)が、下記性状を有する共重合体である
請求項2記載の施設園芸用フィルム。 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 3. The ethylene-α-olefin copolymer (c 11 ) which is a main component of the composition constituting the outer layer (C) which is the outer skin of the tubular film is a copolymer having the following properties. Item 7. The film for facility horticulture according to Item 2. a) Melt flow ratio I 10 / I 2 ≧ 5.63 b) Molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) Critical shear stress γ γ> 4 when gross melt fracture begins to occur × 10 6 dyne / cm 2
成する組成物の主成分が、酢酸ビニル含有量が2〜15
重量%のエチレン−酢酸ビニル共重合体である請求項1
〜3の何れか1項記載の施設園芸用フィルム。4. The composition for forming the inner layer (A), which is the inner layer of the tubular film, has a vinyl acetate content of 2 to 15%.
2. An ethylene-vinyl acetate copolymer of 1% by weight.
4. The film for greenhouse horticulture according to any one of items 3 to 3.
成する組成物が、添加率X重量%と無機質フィラーのB
ET比表面積Sm2/gが、1/S≦X≦100/Sの
関係を満足する無機質フィラーの1種以上をさらに添加
したものである請求項1〜4の何れか1項記載の施設園
芸用フィルム。5. The composition constituting the inner layer (A), which is the inner layer of the tubular film, comprises X weight% of additive and B of inorganic filler.
The facility horticulture according to any one of claims 1 to 4, wherein the ET specific surface area Sm 2 / g further includes one or more inorganic fillers satisfying a relationship of 1 / S ≦ X ≦ 100 / S. For film.
が、シングルサイト触媒を用いて重合された、密度(d
b)が0.85〜0.93g/cm3で、かつ、下記性状
を有するエチレン−α−オレフィン重合体(b)である
請求項1〜5の何れか1項記載の施設園芸用フィルム。 a)メルトフロー比I10/I2≧5.63 b)分子量分布Mw/Mn≦(I10/I2)−4.63 c)グロスメルトフラクチャーが起こり始める時の臨界
せん断応力γ γ>4×106dyne/cm2 6. The density (d) in which the main component of the composition constituting the intermediate layer (B) is polymerized using a single-site catalyst.
In b) is 0.85~0.93g / cm 3, and horticulture film of an ethylene -α- olefin polymer (b) is according to any one of claims 1 to 5 having the following properties. a) Melt flow ratio I 10 / I 2 ≧ 5.63 b) Molecular weight distribution Mw / Mn ≦ (I 10 / I 2 ) −4.63 c) Critical shear stress γ γ> 4 when gross melt fracture begins to occur × 10 6 dyne / cm 2
折り目部もしくは折り幅中央部に筒状フィルムの長さ方
向に沿って1ヶ所設けられ、かつ、筒状フィルムが長手
方向に折り畳まれている請求項1〜6の何れかに記載の
施設園芸用フィルム。7. A slit portion is provided at one position along a longitudinal direction of the tubular film at a fold portion or a central portion of the folded width at one end of the tubular film, and the tubular film is folded in the longitudinal direction. The film for greenhouse horticulture according to any one of claims 1 to 6, wherein