JP2001055242A - Bio-degradable plastic bag - Google Patents
Bio-degradable plastic bagInfo
- Publication number
- JP2001055242A JP2001055242A JP23221999A JP23221999A JP2001055242A JP 2001055242 A JP2001055242 A JP 2001055242A JP 23221999 A JP23221999 A JP 23221999A JP 23221999 A JP23221999 A JP 23221999A JP 2001055242 A JP2001055242 A JP 2001055242A
- Authority
- JP
- Japan
- Prior art keywords
- bag
- biodegradable plastic
- film
- cylindrical film
- rough
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、生分解性プラスチ
ックフイルムを素材として袋体に形成された生分解性プ
ラスチック袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a biodegradable plastic bag formed from a biodegradable plastic film as a material.
【０００２】[0002]
【従来の技術】生分解性プラスチックは、使用状態では
一般のプラスチックと同等の機能を有し、使用後に廃棄
されると、土中や海水中の微生物によって最終的に水と
二酸化炭素に分解されるプラスチックである。プラスチ
ックによる環境汚損を防止するため、このような生分解
性プラスチックを使用したゴミ袋等のプラスチック製品
が開発されている。尚、プラスチック袋は、プラスチッ
クフイルムによって形成されるもので、一般的には、原
料をインフレーション成形して筒状フイルムを形成し、
この筒状フイルムを扁平にした状態で袋体に形成され
る。この場合、扁平な筒状フイルムに底部シールを形成
しながら一定間隔毎に切断して、その切断部を口部とし
た袋体を形成し、これを所定枚数束ねて商品としたも
の、あるいは、扁平な筒状フイルムに底部シール及び切
断用のミシン目を一定間隔ごとに形成して連続袋体を形
成し、これをロール状に巻き取って商品としたもの等が
ある。2. Description of the Related Art Biodegradable plastics have the same function as ordinary plastics when used, and when they are discarded after use, they are finally decomposed into water and carbon dioxide by microorganisms in soil and seawater. Plastic. In order to prevent environmental pollution by plastics, plastic products such as garbage bags using such biodegradable plastics have been developed. Incidentally, the plastic bag is formed of a plastic film, and generally, the raw material is blown-molded to form a cylindrical film,
The tubular film is formed into a bag in a flat state. In this case, a flat cylindrical film is cut at regular intervals while forming a bottom seal, to form a bag with the cut portion as a mouth, and a predetermined number of bags are bundled into a product, or There is a product in which a bottom bag and a perforation for cutting are formed at regular intervals in a flat cylindrical film to form a continuous bag body, which is wound into a roll to obtain a product.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、このよ
うなゴミ袋等の袋体を生分解性プラスチックフイルムを
素材として形成した場合、常温下での商品の保管時に、
生分解性プラスチックの分解性によって袋体を形成する
フイルム同士が接着し、袋体を開けることができなくな
るブロッキングが生じ、袋体としての商品価値が失われ
てしまうという問題が生じている。However, when such a bag such as a garbage bag is formed from a biodegradable plastic film, it is difficult to store the product at room temperature.
The films forming the bag adhere to each other due to the degradability of the biodegradable plastic, causing blocking in which the bag cannot be opened, thereby causing a problem that the commercial value of the bag is lost.
【０００４】本発明は、このような従来の問題を解決す
るために為されたもので、生分解性プラスチックフイル
ムを素材として形成した袋体において、商品の保管時に
フイルム同士が接着するといった不具合を防止すること
ができる生分解性プラスチック袋を提供することを課題
としている。SUMMARY OF THE INVENTION The present invention has been made to solve such a conventional problem, and in a bag formed of a biodegradable plastic film as a material, there is a problem that the films adhere to each other during storage of goods. It is an object to provide a biodegradable plastic bag that can be prevented.
【０００５】[0005]
【課題を解決するための手段】上記の課題を解決するた
め、本発明（請求項１）の生分解性プラスチック袋は、
生分解性プラスチックフイルムを素材として袋体に形成
された生分解性プラスチック袋であって、袋体の内表面
が荒粗面に形成されている構成とした。In order to solve the above-mentioned problems, a biodegradable plastic bag of the present invention (claim 1) comprises:
A biodegradable plastic bag formed of a biodegradable plastic film as a raw material in a bag body, wherein the inner surface of the bag body is formed with a rough surface.
【０００６】この場合、発泡成形した生分解性プラスチ
ックフイルムを素材として用いることにより、袋体の内
表面を発泡跡凹凸により荒粗面に形成した態様（請求項
２）、袋体の内表面を掻き傷による荒粗面に形成した態
様（請求項３）、袋体の内表面を擦り傷による荒粗面に
形成した態様（請求項４）がある。In this case, the inner surface of the bag is formed as a rough surface by foaming irregularities by using a foamed biodegradable plastic film as a material (claim 2). There is a mode in which the inner surface of the bag body is formed to have a rough surface due to scratches (claim 4).
【０００７】このように、袋体の内表面を荒粗面に形成
すると、その内表面には凹凸が生じることになるため、
それだけフイルム同士の接触面積が小さくなる。従っ
て、商品の保管時に生分解性プラスチックフイルムに分
解が生じたとしても、接触面積が小さい分だけ、その接
着面積も小さくなり、袋体のブロッキングを防止するこ
とができる。As described above, if the inner surface of the bag body is formed with a rough surface, irregularities are generated on the inner surface.
The contact area between the films is reduced accordingly. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the smaller the contact area, the smaller the adhesive area, and the blocking of the bag can be prevented.
【０００８】尚、生分解性プラスチックとしては、一般
に、生物由来の天然高分子系のもの、（例えば、組成；
でん粉＋ポリビニルアルコール、主原料；とうもろこし
等の植物でん粉）、又、化石資源由来の化学合成高分子
系のもの、（例えば、組成；グリコール＋脂肪酸ジカル
ボン酸、主原料；化石資源）、これらの混合型等がある
が、本発明における生分解性プラスチックフイルムの原
料としては、上記のもの全てを含むものとする。In general, biodegradable plastics include those derived from biological polymers and natural polymers (for example, compositions;
Starch + polyvinyl alcohol, main raw material; plant starch such as corn) or chemically synthesized polymer derived from fossil resources (for example, composition; glycol + fatty acid dicarboxylic acid, main raw material; fossil resources), and mixtures thereof Although there are molds and the like, the raw materials of the biodegradable plastic film in the present invention include all of the above.
【０００９】[0009]
【実施の形態】以下、本発明の実施の形態を図面により
詳述する。図１は本発明の実施の１形態であって、生分
解性プラスチック袋を示す斜視図である。この生分解性
プラスチック袋１はゴミ袋であって、生分解性プラスチ
ックを原料としてインフレーション成形した筒状フイル
ム２を素材として袋体１０に形成されている。この場
合、原料としての生分解性プラスチックに発泡剤を添加
し、これを発泡成形させて筒状フイルム２を形成し、こ
の筒状フイルム２を扁平にした状態で、底部シール１１
を形成しながら一定間隔毎に切断して、その切断部を口
部１２とした袋体１０に形成したものである。このよう
に、原料である生分解性プラスチックに発泡剤を添加し
ているため、成形された筒状フイルム２の表面が発泡跡
凹凸により荒粗面２０に形成される。そして、この筒状
フイルム２を用いて袋体１０を形成しているため、この
袋体１０の内表面及び外表面を荒粗面２０に形成するこ
とができる。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is a perspective view showing a biodegradable plastic bag according to an embodiment of the present invention. The biodegradable plastic bag 1 is a garbage bag, and is formed in a bag body 10 by using a tubular film 2 formed by inflation molding using biodegradable plastic as a raw material. In this case, a foaming agent is added to a biodegradable plastic as a raw material, and this is foamed and formed to form a cylindrical film 2. In a state where the cylindrical film 2 is flattened, a bottom seal 11 is formed.
Is formed at regular intervals while forming the bag body 10 having the cut portion as the mouth portion 12. As described above, since the foaming agent is added to the biodegradable plastic as a raw material, the surface of the formed cylindrical film 2 is formed on the rough and rough surface 20 by the unevenness of the foaming trace. Since the bag 10 is formed using the cylindrical film 2, the inner surface and the outer surface of the bag 10 can be formed on the rough surface 20.
【００１０】このように、袋体１０の内表面を荒粗面２
０に形成すると、その内表面には凹凸が生じることにな
るため、それだけフイルム２，２同士の接触面積が小さ
くなる。従って、商品の保管時に生分解性プラスチック
フイルムに分解が生じたとしても、接触面積が小さい分
だけ、その接着面積も小さくなり、袋体１０のブロッキ
ングを防止することができる。尚、この生分解性プラス
チック袋１では、袋体１０の外表面についても荒粗面２
０に形成されるもので、これにより生分解性プラスチッ
ク袋１を束ねたときの重なり合う生分解性プラスチック
袋１，１の外表面同士の接着を防止できる。As described above, the inner surface of the bag body 10 is
If the film is formed to have a thickness of 0, the inner surface will have irregularities, so that the contact area between the films 2 and 2 will be reduced accordingly. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the smaller the contact area, the smaller the bonding area, and the blocking of the bag 10 can be prevented. In this biodegradable plastic bag 1, the outer surface of the bag body 10 also has a rough surface 2.
This prevents the outer surfaces of the biodegradable plastic bags 1 and 1 from overlapping each other when the biodegradable plastic bags 1 are bundled.
【００１１】次に、図２〜図４は生分解性プラスチック
袋の素材となる筒状フイルムの内表面を荒粗面に形成す
るための装置の例を示す説明図である。図２の装置は、
筒状フイルム２の内表面に掻き傷３０を付けることによ
り、この筒状フイルム２の内表面を荒粗面２０に形成す
るようにしたものである。この場合、インフレーション
成形装置のリップ４０に支持棒５０を取り付け、この支
持棒５０の先端に円板５１を取り付け、この円板５１の
外周に櫛状の掻き爪５２を形成している。そして、ダイ
４１とリップ４０の間から射出される筒状フイルム２の
内表面に前記掻き爪５２を接触させることにより、筒状
フイルム２の内表面を掻き傷３０による荒粗面２０に形
成するようになっている。このようにして成形した筒状
フイルム２を素材として、袋体を形成するもので、これ
により袋体の内表面を荒粗面に形成することができる。
従って、袋体の内表面には掻き傷３０による凹凸が生じ
ることになるため、それだけフイルム同士の接触面積が
小さくなり、袋体のブロッキングを防止することができ
る。Next, FIGS. 2 to 4 are explanatory views showing an example of an apparatus for forming an inner surface of a cylindrical film, which is a raw material of a biodegradable plastic bag, into a rough surface. The device of FIG.
By scratching the inner surface of the cylindrical film 2, the inner surface of the cylindrical film 2 is formed as a rough surface 20. In this case, a support bar 50 is attached to the lip 40 of the inflation molding apparatus, a disk 51 is attached to the tip of the support bar 50, and a comb-like scraping claw 52 is formed on the outer periphery of the disk 51. Then, the scraper 52 is brought into contact with the inner surface of the cylindrical film 2 ejected from between the die 41 and the lip 40 to form the inner surface of the cylindrical film 2 on the rough surface 20 due to the scratches 30. It has become. The bag is formed by using the cylindrical film 2 thus formed as a raw material, whereby the inner surface of the bag can be formed into a rough surface.
Accordingly, the unevenness due to the scratches 30 occurs on the inner surface of the bag, so that the contact area between the films is reduced accordingly, and blocking of the bag can be prevented.
【００１２】図３の装置は、図２の装置と同様に、筒状
フイルム２の内表面に掻き傷３０を付けることにより、
この筒状フイルム２の内表面を荒粗面２０に形成するよ
うにしたものである。この場合、インフレーション成形
装置のリップ４０に支持棒５３を取り付け、この支持棒
５３の先端に全方向に向けて多数に分岐した掻き爪５４
を取り付けたものとなっている。そして、ダイ４１とリ
ップ４０の間から射出される筒状フイルム２の内表面に
前記掻き爪５４を接触させることにより、筒状フイルム
２の内表面を掻き傷３０による荒粗面２０に形成するよ
うになっている。このようにして成形した筒状フイルム
２を素材として、袋体を形成するもので、これにより袋
体の内表面を荒粗面に形成することができる。The device shown in FIG. 3 is similar to the device shown in FIG.
The inner surface of the cylindrical film 2 is formed as a rough surface 20. In this case, a support bar 53 is attached to the lip 40 of the inflation molding apparatus, and a large number of scraping claws 54 branched in all directions are attached to the tip of the support bar 53.
Is attached. Then, the inner surface of the cylindrical film 2 is formed into a rough surface 20 by the scratches 30 by bringing the scraper 54 into contact with the inner surface of the cylindrical film 2 ejected from between the die 41 and the lip 40. It has become. The bag is formed by using the cylindrical film 2 thus formed as a raw material, whereby the inner surface of the bag can be formed into a rough surface.
【００１３】図４の装置は、筒状フイルム２の内表面に
擦り傷３１を付けることにより、この筒状フイルム２の
内表面を荒粗面２０に形成するようにしたもので、この
場合、インフレーション成形装置におけるリップ４０の
外周面に多数の小突起５５を形成したものとなってい
る。そして、ダイ４１とリップ４０の間から筒状フイル
ム２が射出される際に、筒状フイルム２の内表面が小突
起５５に擦れることで、筒状フイルム２の内表面を擦り
傷３１による荒粗面２０に形成するようになっている。
このようにして成形した筒状フイルム２を素材として、
袋体を形成するもので、これにより袋体の内表面を荒粗
面に形成することができる。尚、ダイ４１の内周面に多
数の小突起５５を形成して、同時に筒状フィルム２の外
表面を擦り傷による荒粗面に形成してもよい。この場
合、生分解性プラスチック袋を重ねたときの重なり合う
袋の外表面同士の接着を防止できる。In the apparatus shown in FIG. 4, the inner surface of the cylindrical film 2 is formed with a rough surface 20 by applying a scratch 31 to the inner surface of the cylindrical film 2. In this case, inflation is performed. A large number of small projections 55 are formed on the outer peripheral surface of the lip 40 in the molding device. When the cylindrical film 2 is ejected from between the die 41 and the lip 40, the inner surface of the cylindrical film 2 rubs against the small protrusion 55, so that the inner surface of the cylindrical film 2 is roughened by the scratches 31. It is formed on the surface 20.
Using the cylindrical film 2 thus formed as a material,
A bag is formed, whereby the inner surface of the bag can be formed with a rough surface. Incidentally, a large number of small projections 55 may be formed on the inner peripheral surface of the die 41, and the outer surface of the tubular film 2 may be simultaneously formed with a rough surface due to abrasion. In this case, it is possible to prevent the outer surfaces of the overlapping bags from being adhered to each other when the biodegradable plastic bags are stacked.
【００１４】以上、本発明の実施の形態を図面により説
明したが、具体的な構成はこれに限定されることはな
い。例えば、生分解性プラスチック袋としてはゴミ袋以
外に、スーパーマーケット等で用いられている買い物袋
やその他の包装用袋や収納袋等として形成してもよい。
又、ミシン目によって連結された連続袋体に形成しても
よい。又、生分解性プラスチック袋の素材としては、生
分解性プラスチックフイルムであればよく、筒状フイル
ムでもシート状フイルムでもよい。Although the embodiment of the present invention has been described with reference to the drawings, the specific configuration is not limited to this. For example, the biodegradable plastic bag may be formed as a shopping bag used in a supermarket or the like, or other packaging bags or storage bags, in addition to the garbage bag.
Moreover, you may form in the continuous bag body connected by the perforation. The material of the biodegradable plastic bag may be any biodegradable plastic film, and may be a cylindrical film or a sheet film.
【００１５】[0015]
【発明の効果】以上説明したように、本発明の生分解性
プラスチック袋にあっては、袋体の内表面を荒粗面に形
成したため、その内表面には凹凸が生じることになり、
それだけフイルム同士の接触面積が小さくなる。従っ
て、商品の保管時に生分解性プラスチックフイルムに分
解が生じたとしても、接触面積が小さい分だけ、その接
着面積も小さくなり、袋体のブロッキングを防止するこ
とができるという効果が得られる。As described above, in the biodegradable plastic bag of the present invention, the inner surface of the bag body is formed to be rough, so that the inner surface has irregularities.
The contact area between the films is reduced accordingly. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the smaller the contact area, the smaller the adhesive area, and the effect of preventing the blocking of the bag can be obtained.
【図１】実施の１形態であって、生分解性プラスチック
袋を示す斜視図である。FIG. 1 is a perspective view showing a biodegradable plastic bag according to an embodiment.
【図２】生分解性プラスチック袋の素材となる筒状フイ
ルムの内表面を荒粗面に形成するための装置の例を示す
説明図である。FIG. 2 is an explanatory view showing an example of an apparatus for forming a rough inner surface of a cylindrical film used as a material of a biodegradable plastic bag.
【図３】生分解性プラスチック袋の素材となる筒状フイ
ルムの内表面を荒粗面に形成するための装置の例を示す
説明図である。FIG. 3 is an explanatory view showing an example of an apparatus for forming an inner surface of a cylindrical film as a raw material of a biodegradable plastic bag into a rough surface.
【図４】生分解性プラスチック袋の素材となる筒状フイ
ルムの内表面を荒粗面に形成するための装置の例を示す
説明図である。FIG. 4 is an explanatory view showing an example of an apparatus for forming a rough inner surface of a cylindrical film used as a material of a biodegradable plastic bag.
１ 生分解性プラスチック袋 １０ 袋体 ２ 筒状フイルム（生分解性プラスチックフイルム） ２０ 荒粗面 ３０ 掻き傷 ３１ 擦り傷 DESCRIPTION OF SYMBOLS 1 Biodegradable plastic bag 10 Bag body 2 Cylindrical film (biodegradable plastic film) 20 Rough surface 30 Scratches 31 Scratches
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１２年６月１５日（２０００．６．１
５）[Submission date] June 15, 2000 (2006.1.
5)
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Correction target item name] Full text
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【書類名】 明細書[Document Name] Statement
【発明の名称】 生分解性プラスチック袋[Title of the Invention] Biodegradable plastic bag
【特許請求の範囲】[Claims]
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は、生分解性プラスチ
ックフイルムを素材として袋体に形成された生分解性プ
ラスチック袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a biodegradable plastic bag formed from a biodegradable plastic film as a material.
【０００２】[0002]
【従来の技術】生分解性プラスチックは、使用状態では
一般のプラスチックと同等の機能を有し、使用後に廃棄
されると、土中や海水中の微生物によって最終的に水と
二酸化炭素に分解されるプラスチックである。プラスチ
ックによる環境汚損を防止するため、このような生分解
性プラスチックを使用したゴミ袋等のプラスチック製品
が開発されている。尚、プラスチック袋は、プラスチッ
クフイルムによって形成されるもので、一般的には、原
料をインフレーション成形して筒状フイルムを形成し、
この筒状フイルムを扁平にした状態で袋体に形成され
る。この場合、扁平な筒状フイルムに底部シールを形成
しながら一定間隔毎に切断して、その切断部を口部とし
た袋体を形成し、これを所定枚数束ねて商品としたも
の、あるいは、扁平な筒状フイルムに底部シール及び切
断用のミシン目を一定間隔ごとに形成して連続袋体を形
成し、これをロール状に巻き取って商品としたもの等が
ある。2. Description of the Related Art Biodegradable plastics have the same function as ordinary plastics when used, and when they are discarded after use, they are finally decomposed into water and carbon dioxide by microorganisms in soil and seawater. Plastic. In order to prevent environmental pollution by plastics, plastic products such as garbage bags using such biodegradable plastics have been developed. Incidentally, the plastic bag is formed of a plastic film, and generally, the raw material is blown-molded to form a cylindrical film,
The tubular film is formed into a bag in a flat state. In this case, a flat cylindrical film is cut at regular intervals while forming a bottom seal, to form a bag with the cut portion as a mouth, and a predetermined number of bags are bundled into a product, or There is a product in which a bottom bag and a perforation for cutting are formed at regular intervals in a flat cylindrical film to form a continuous bag body, which is wound into a roll to obtain a product.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、このよ
うなゴミ袋等の袋体を生分解性プラスチックフイルムを
素材として形成した場合、常温下での商品の保管時に、
生分解性プラスチックの分解性によって袋体の内表面同
士が接着し、袋体を開けることができなくなるブロッキ
ングが生じたり、また、束ねられた袋体の外表面同士や
ロール状に巻き取られた袋体の外表面同士が接着するな
ど、袋体としての商品価値が失われてしまうという問題
が生じている。However, when such a bag such as a garbage bag is formed from a biodegradable plastic film, it is difficult to store the product at room temperature.
Depending on the degradability of the biodegradable plastic, the inner surface of the bag
Judges are bonded, or cause blocking will not be able to open the bag body, also, the outer surface each other of bundled bag body Ya
Do not bond the outer surfaces of the rolled bag.
Etc., a problem that the commercial value of the bag body is lost has occurred.
【０００４】本発明は、このような従来の問題を解決す
るために為されたもので、生分解性プラスチックフイル
ムを素材として形成した袋体において、商品の保管時に
内表面同士が接着したり、外表面同士が接着するといっ
た不具合を防止することができる生分解性プラスチック
袋を提供することを課題としている。SUMMARY OF THE INVENTION The present invention has been made to solve such a conventional problem, and a bag made of a biodegradable plastic film is used for storing a product.
It is an object of the present invention to provide a biodegradable plastic bag that can prevent inconveniences such as inner surfaces being bonded to each other and outer surfaces being bonded to each other .
【０００５】[0005]
【課題を解決するための手段】上記の課題を解決するた
め、本発明（請求項１）の生分解性プラスチック袋は、
発泡成形した生分解性プラスチックフイルムが素材とし
て用いられ、袋体の内表面及び外表面が全面にわたって
発泡跡凹凸による荒粗面に形成されている構成とした。In order to solve the above-mentioned problems, a biodegradable plastic bag of the present invention (claim 1) comprises:
Biodegradable plastic films and foam molding is used as the material, inner and outer surfaces of the bag body is configured to be formed on by that OH DEAR surface <br/> foam remains uneven over the entire surface.
【０００６】又、本発明（請求項２）の生分解性プラス
チック袋は、インフレーション成形装置におけるダイと
リップの間から筒状フイルムを射出する際に、リップの
外周面及びダイの内周面に形成した多数の小突起に擦れ
ることで、筒状フイルムの表裏両面に擦り傷を形成した
生分解性プラスチックフイルムが素材として用いられ、
袋体の内表面及び外表面が全面にわたって擦り傷による
荒粗面に形成されている構成とした。Further, the biodegradable plastic bag of the present invention (claim 2) is provided with a die in an inflation molding apparatus.
When ejecting the tubular film from between the lips,
Rubbing many small protrusions formed on the outer peripheral surface and the inner peripheral surface of the die
Scratches on both sides of the tubular film
Biodegradable plastic film is used as a material,
The inner and outer surfaces of the bag are scratched over the entire surface
It was configured to be formed on a rough surface .
【０００７】このように、袋体の表面（内表面及び外表
面）を荒粗面に形成すると、その表面には凹凸が生じる
ことになる。従って、商品の保管時に生分解性プラスチ
ックフイルムに分解が生じたとしても、荒粗面の凹凸に
よって接触面積が小さい分だけ、その接着面積も小さく
なり、内表面同士の接着による袋体のブロッキングを防
止することができるし、束ねられた袋体やロール状に巻
き取られた袋体の外表面同士の接着を防止することがで
きる。As described above, the surface of the bag (the inner surface and the outer surface)
When forming the surface) to OH DEAR surface, so that unevenness occurs on the surface thereof. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the adhesion area is reduced by the small contact area due to the unevenness of the rough surface , and the blocking of the bag body due to the adhesion between the inner surfaces is prevented. Can be prevented and rolled into a bundled bag or roll
This prevents the outer surfaces of the removed bag from bonding to each other.
I can .
【０００８】尚、生分解性プラスチックとしては、一般
に、生物由来の天然高分子系のもの、（例えば、組成；
でん粉＋ポリビニルアルコール、主原料；とうもろこし
等の植物でん粉）、又、化石資源由来の化学合成高分子
系のもの、（例えば、組成；グリコール＋脂肪酸ジカル
ボン酸、主原料；化石資源）、これらの混合型等がある
が、本発明における生分解性プラスチックフイルムの原
料としては、上記のもの全てを含むものとする。In general, biodegradable plastics include those derived from biological polymers and natural polymers (for example, compositions;
Starch + polyvinyl alcohol, main raw material; plant starch such as corn) or chemically synthesized polymer derived from fossil resources (for example, composition; glycol + fatty acid dicarboxylic acid, main raw material; fossil resources), and mixtures thereof Although there are molds and the like, the raw materials of the biodegradable plastic film in the present invention include all of the above.
【０００９】[0009]
【発明の実施の形態】以下、本発明の実施の形態を図面
により詳述する。図１は本発明の実施の１形態であっ
て、生分解性プラスチック袋を示す斜視図である。この
生分解性プラスチック袋１はゴミ袋であって、生分解性
プラスチックを原料としてインフレーション成形した筒
状フイルム２を素材として袋体１０に形成されている。
この場合、原料としての生分解性プラスチックに発泡剤
を添加し、これを発泡成形させて筒状フイルム２を形成
し、この筒状フイルム２を扁平にした状態で、底部シー
ル１１を形成しながら一定間隔毎に切断して、その切断
部を口部１２とした袋体１０に形成したものである。こ
のように、原料である生分解性プラスチックに発泡剤を
添加しているため、成形された筒状フイルム２の表裏両
面が発泡跡凹凸により荒粗面２０に形成される。そし
て、この筒状フイルム２を用いて袋体１０を形成してい
るため、この袋体１０の内表面及び外表面を全面的に荒
粗面２０に形成することができる。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, described in detail with reference to the accompanying drawings of embodiments of the present invention. FIG. 1 is a perspective view showing a biodegradable plastic bag according to an embodiment of the present invention. The biodegradable plastic bag 1 is a garbage bag, and is formed in a bag body 10 by using a tubular film 2 formed by inflation molding using biodegradable plastic as a raw material.
In this case, a foaming agent is added to the biodegradable plastic as a raw material, and this is foamed and formed to form a tubular film 2, and while the tubular film 2 is flattened, the bottom seal 11 is formed. It is cut at regular intervals and formed on the bag body 10 with the cut portion as the mouth portion 12. As described above, since the foaming agent is added to the biodegradable plastic as the raw material, the front and back sides of the formed cylindrical film 2 are formed.
The surface is formed on the rough and rough surface 20 by the irregularities of the foaming trace. Since the bag 10 is formed using the cylindrical film 2, the inner surface and the outer surface of the bag 10 can be entirely formed into the rough surface 20.
【００１０】このように、袋体１０の内表面及び外表面
を荒粗面２０に形成すると、その表面には凹凸が生じる
ことになる。従って、商品の保管時に生分解性プラスチ
ックフイルムに分解が生じたとしても、荒粗面の凹凸に
よって接触面積が小さい分だけ、その接着面積も小さく
なり、内表面同士の接着による袋体１０のブロッキング
を防止することができるし、束ねられて重なり合う袋体
１０やロール状に巻き取られて重なり合う袋体１０の外
表面同士の接着を防止することができる。 When the inner surface and the outer surface of the bag body 10 are formed on the rough surface 20 as described above, the surface has irregularities. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the adhesion area is reduced by the small contact area due to the unevenness of the rough surface , and the bag body 10 is blocked by the adhesion between the inner surfaces. Can be prevented and the bags are bundled and overlapped
Outside the bag 10 which is wound up in a roll shape or overlapped
Adhesion between the surfaces can be prevented.
【００１１】次に、図２は生分解性プラスチック袋の素
材となる筒状フイルムの表裏両面を荒粗面に形成するた
めの装置の例を示す説明図である。この装置は、筒状フ
イルム２の表裏両面に擦り傷３１を付けることにより、
この筒状フイルム２の表裏両面を荒粗面２０に形成する
ようにしたものである。この場合、インフレーション成
形装置におけるリップ４０の外周面に多数の小突起５５
を形成すると共に、ダイ４１の内周面に多数の小突起
（図示せず）を形成したものとなっている。 Next, FIG. 2 is an explanatory view showing an example of an apparatus for forming both the front and back surfaces of a cylindrical film as a raw material of a biodegradable plastic bag with rough surfaces. This device forms scratches 31 on both the front and back surfaces of the cylindrical film 2,
The front and back surfaces of the cylindrical film 2 are formed on the rough surface 20. In this case, a large number of small projections 55 are formed on the outer peripheral surface of the lip 40 in the inflation molding apparatus.
And a large number of small protrusions are formed on the inner peripheral surface of the die 41.
(Not shown) .
【００１２】 そして、ダイ４１とリップ４０の間から筒
状フイルム２が射出される際に、筒状フイルム２の表裏
両面がそれぞれ小突起に擦れることで、筒状フイルム２
の表裏両面を擦り傷３１による荒粗面２０に形成するよ
うになっている。このようにして成形した筒状フイルム
２を素材として袋体を形成するもので、これにより袋体
の内表面及び外表面を全面的に荒粗面に形成することが
できる。 When the cylindrical film 2 is ejected from between the die 41 and the lip 40, the front and back surfaces of the cylindrical film 2 rub against the small projections, respectively.
Are formed on the rough surface 20 due to the abrasion 31. The bag is formed using the cylindrical film 2 formed as described above as a raw material, whereby the inner surface and the outer surface of the bag can be entirely roughened.
【００１３】従って、内表面同士の接着による袋体のブ[0013] Therefore, the bag of the bag is adhered by the adhesion of the inner surfaces.
ロッキングを防止することができるし、束ねられて重なLocking can be prevented and bundled and heavy
り合う袋体やロール状に巻き取られて重なり合う袋体のOf overlapping bags or overlapping bags that are wound in rolls
外表面同士の接着を防止することができる。Adhesion between the outer surfaces can be prevented.
【００１４】以上、本発明の実施の形態を図面により説
明したが、具体的な構成はこれに限定されることはな
い。例えば、生分解性プラスチック袋としてはゴミ袋以
外に、スーパーマーケット等で用いられている買い物袋
やその他の包装用袋や収納袋等として形成してもよい。
又、ミシン目によって連結された連続袋体に形成して
もよい。又、生分解性プラスチック袋の素材としては、
生分解性プラスチックフイルムであればよく、筒状フイ
ルムでもシート状フイルムでもよい。Although the embodiment of the present invention has been described with reference to the drawings, the specific configuration is not limited to this. For example, the biodegradable plastic bag may be formed as a shopping bag used in a supermarket or the like, or other packaging bags or storage bags, in addition to the garbage bag.
Moreover, you may form in the continuous bag body connected by the perforation. Also, as a material for biodegradable plastic bags,
Any biodegradable plastic film may be used, and may be a cylindrical film or a sheet film.
【００１５】[0015]
【発明の効果】以上説明したように、本発明の生分解性
プラスチック袋にあっては、袋体の内表面及び外表面を
全面的に荒粗面に形成したため、その表面には凹凸が生
じることになる。従って、商品の保管時に生分解性プラ
スチックフイルムに分解が生じたとしても、接触面積が
小さい分だけ、その接着面積も小さくなり、内表面同士
の接着による袋体のブロッキングを防止することができ
るし、束ねられて重なり合う袋体やロール状に巻き取ら
れて重なり合う袋体の外表面同士の接着を防止すること
ができるという効果が得られる。As described above, in the biodegradable plastic bag of the present invention, since the inner surface and the outer surface of the bag are entirely formed as rough surfaces, irregularities are generated on the surface. Will be. Therefore, even if the biodegradable plastic film is decomposed during storage of the product, the smaller the contact area, the smaller the adhesive area, and the smaller the inner surface.
Can prevent blocking of the bag due to adhesion of
Rolls, rolled up into overlapping bags or rolls
To prevent the outer surfaces of overlapping bags from sticking together
Is obtained.
【図面の簡単な説明】[Brief description of the drawings]
【図１】実施の１形態であって、生分解性プラスチック
袋を示す斜視図である。FIG. 1 is a perspective view showing a biodegradable plastic bag according to an embodiment.
【図２】生分解性プラスチック袋の素材となる筒状フイ
ルムの表裏両面を荒粗面に形成するための装置の例を示
す説明図である。 Fig. 2 Cylindrical fiber used as a material for biodegradable plastic bags
An example of an apparatus for forming rough surfaces on both front and back
FIG.
【符号の説明】 １ 生分解性プラスチック袋 １０ 袋体 ２ 筒状フイルム（生分解性プラスチックフイルム） ２０ 荒粗面 ３１ 擦り傷[Description of Signs] 1 Biodegradable plastic bag 10 Bag body 2 Cylindrical film (biodegradable plastic film) 20 Rough surface 31 Scratches
【手続補正２】[Procedure amendment 2]
【補正対象書類名】図面[Document name to be amended] Drawing
【補正対象項目名】全図[Correction target item name] All figures
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【図１】 FIG.
【図２】 FIG. 2
Claims (4)
して袋体に形成された生分解性プラスチック袋であっ
て、 袋体の内表面が荒粗面に形成されていることを特徴とし
た生分解性プラスチック袋。1. A biodegradable plastic bag formed in a bag using a biodegradable plastic film as a raw material, wherein the inner surface of the bag is formed with a rough surface. Plastic bag.
ルムを素材として用いることにより、袋体の内表面を発
泡跡凹凸により荒粗面に形成した請求項１記載の生分解
性プラスチック袋。2. The biodegradable plastic bag according to claim 1, wherein the foamed biodegradable plastic film is used as a raw material, and the inner surface of the bag body is formed to have a rough and rough surface by foaming irregularities.
成した請求項１記載の生分解性プラスチック袋。3. The biodegradable plastic bag according to claim 1, wherein the inner surface of the bag is formed with a rough surface due to a scratch.
成した請求項１記載の生分解性プラスチック袋。4. The biodegradable plastic bag according to claim 1, wherein the inner surface of the bag is formed with a rough surface due to abrasion.