JP2001018518A - Recording sheet - Google Patents
Recording sheetInfo
- Publication number
- JP2001018518A JP2001018518A JP11190202A JP19020299A JP2001018518A JP 2001018518 A JP2001018518 A JP 2001018518A JP 11190202 A JP11190202 A JP 11190202A JP 19020299 A JP19020299 A JP 19020299A JP 2001018518 A JP2001018518 A JP 2001018518A
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- ink
- recording sheet
- ink jet
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はインクジェット記録
シートに関するものであり、さらに詳しくは独特な風合
いを持ちながら十分なインクジェット印字適性を持ち、
かつ印字の際のプリンターの搬送性が良好なインクジェ
ット記録シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet, and more particularly, to a sheet having a unique feel and sufficient ink jet printing suitability.
The present invention also relates to an ink jet recording sheet having good printer transportability during printing.
【０００２】[0002]
【従来の技術】インクジェット記録方式は、種々の作動
原理によりインクの微小液滴を飛翔させて紙などの記録
シートに付着させ、画像・文字などの記録を行なうもの
であるが、高速、低騒音、多色化が容易、記録パターン
の融通性が大きい、現像−定着が不要などの特徴があ
り、漢字を含め各種図形およびカラー画像などの記録装
置として種々の用途において急速に普及している。さら
に、多色インクジェット方式により形成される画像は、
製版方式による多色印刷に比較して遜色のない記録を得
ることが可能である。また、作成部数が少なくて済む用
途においては、安価であることからフルカラー画像記録
分野にまで広く応用されつつある。2. Description of the Related Art Ink-jet recording is a method in which minute droplets of ink are made to fly and adhere to a recording sheet such as paper by various operating principles to record images and characters. It has features such as easy multi-coloring, great flexibility in recording patterns, and no need for development-fixing, and is rapidly spreading in various applications as a recording device for various figures including Chinese characters and color images. Furthermore, the image formed by the multi-color inkjet method is
It is possible to obtain a record comparable to multicolor printing by the plate making method. In addition, in applications requiring a small number of copies, it is being widely applied to the field of full-color image recording because of its low cost.
【０００３】このインクジェット記録方式で使用される
記録シートとしては、通常の印刷や筆記に使われる上質
紙やコーテッド紙を使うべく、装置やインク組成の面か
ら努力がなされてきた。しかし、装置の高速化・高精細
化あるいはフルカラー化などインクジェット記録装置の
性能の向上や用途の拡大に伴い、記録シートに対しても
より高度な特性が要求されるようになった。As recording sheets used in the ink jet recording system, efforts have been made in terms of apparatuses and ink compositions in order to use high-quality paper and coated paper used for ordinary printing and writing. However, with the improvement of the performance of ink jet recording apparatuses such as high-speed, high-definition and full-color apparatuses, and expansion of applications, more advanced characteristics are also required for recording sheets.
【０００４】即ち、当該記録シートとしては、印字ドッ
トの濃度が高く色調が明るく鮮やかであること、インク
の吸収が早く印字ドットが重なった場合においてもイン
クが流れ出したり滲んだりしないこと、印字ドットの横
方向への拡散が必要以上に大きくなく、且つ周辺が滑ら
かでぼやけないことなどの高い画像再現性が要求され
る。[0004] That is, the recording sheet has a high density of print dots, a bright and vivid color tone, quick absorption of ink, no ink bleeding or bleeding even when the print dots overlap, High image reproducibility is required such that the diffusion in the horizontal direction is not unnecessarily large and the periphery is smooth and not blurred.
【０００５】一方、デザイン、イベント、広告などの分
野では、従来から利用されている紙あるいはフィルムを
支持体にしたインクジェット記録シートに加え、布帛を
支持体としたインクジェット記録シートも、その独特の
風合い故に用いられてきている。布帛としては、織布、
編布、不織布等があるが、紙、フィルムと同様にそれ自
体はインクジェット適性をもたない。そのため、従来よ
り各種工夫がなされてきている。具体的には、水溶性高
分子を繊維表面あるいは繊維間隙に付着させた特開平０
２−０９９６７７号や布帛を構成する糸の径を限定した
特許第２８５８６５９号が挙げられる。On the other hand, in the fields of design, events, advertisements, etc., in addition to conventionally used ink jet recording sheets using paper or film as a support, ink jet recording sheets using a cloth as a support also have a unique texture. Therefore, it has been used. Woven cloth,
Although there are knitted fabrics and nonwoven fabrics, like paper and films, they themselves do not have inkjet suitability. Therefore, various devices have been conventionally devised. More specifically, Japanese Patent Application Laid-Open No. H08-214, in which a water-soluble polymer is adhered to the fiber surface or the fiber gap.
No. 2-099677 and Japanese Patent No. 285859 in which the diameter of the yarn constituting the fabric is limited.
【０００６】しかし、布帛の中でも不織布、特にスパン
レース不織布のようなより風合いが布に近い不織布ある
いは織り密度が低い織布では、同じ厚みのものでも腰が
なく、印字の際プリンター搬送中にシワが発生して印字
ヘッドを擦ったり、酷い場合にはヘッドと絡まってしま
ったりした。However, among non-woven fabrics, especially non-woven fabrics such as spun lace non-woven fabrics, such as spun lace non-woven fabrics, or woven fabrics having a low weaving density, are not stiff even if they have the same thickness, and are wrinkled during printing during transport of the printer. This caused the print head to be rubbed or, in severe cases, to get tangled with the print head.
【０００７】[0007]
【発明が解決しようとする課題】そこで、本発明の目的
は、独特な風合いを持ちながら十分なインクジェット印
字適性を持ち、かつ印字の際のプリンターの搬送性が良
好なインクジェット記録シートを提供することにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide an ink jet recording sheet which has sufficient ink jet printing aptitude while having a unique texture, and has good printer transportability during printing. It is in.
【０００８】[0008]
【課題を解決するための手段】本発明者らは、以上のよ
うな問題点を解決するため鋭意研究の結果、以下の発明
に至った。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, have reached the following invention.
【０００９】すなわち、支持体としての布帛にインク受
理成分を塗設あるいは含浸してなるインクジェット記録
シートにおいて、該布帛が積層構造を有する布帛である
ことを特徴とするインクジェット記録シートの発明であ
る。That is, the invention is an ink jet recording sheet in which an ink receiving component is coated or impregnated on a cloth as a support, wherein the cloth is a cloth having a laminated structure.
【００１０】さらに、支持体としての布帛が布帛と熱可
塑性樹脂層とを積層した積層構造を有することを特徴と
する上記インクジェット記録シートの発明である。Further, the invention is an ink jet recording sheet according to the invention, characterized in that the cloth as the support has a laminated structure in which the cloth and the thermoplastic resin layer are laminated.
【００１１】また、支持体としての布帛が布帛と割繊維
不織布とを積層した積層構造を有することを特徴とする
上記インクジェット記録シートの発明である。[0011] Further, the present invention is the ink jet recording sheet described above, wherein the cloth as the support has a laminated structure in which the cloth and the split-fiber non-woven fabric are laminated.
【００１２】[0012]
【発明の実施の形態】本発明のインクジェット記録シー
トは、支持体に積層構造を有する布帛を使用しているこ
とに特徴がある。本発明者らは、２種類以上の布帛なり
を単純に積層するだけでも、該記録シートの腰が強くな
り、プリンター搬送時にシワ等が発生し、印字ヘッドを
擦ったりすることがなくなることを発見した。一方、積
層構造を有さない布帛で、坪量を積層構造を有する布帛
と同等程度にしたものでは印字時のコックリングが発生
したりして、良好なプリンター適性を示すことがない。DESCRIPTION OF THE PREFERRED EMBODIMENTS The ink jet recording sheet of the present invention is characterized in that a fabric having a laminated structure is used for a support. The present inventors have found that simply laminating two or more kinds of fabrics increases the stiffness of the recording sheet, causes wrinkles and the like during transport of the printer, and eliminates rubbing of the print head. did. On the other hand, a fabric having no laminated structure and having a basis weight approximately equal to that of the fabric having the laminated structure does not exhibit good printer suitability due to occurrence of cockling at the time of printing.
【００１３】さらに、当初予想していたことではない
が、支持体としての布帛を布帛と熱可塑性樹脂層を積層
した２層積層体とすることにより印字濃度が向上するこ
とが判明した。その上、支持体としての布帛を布帛と割
繊維不織布とすることにより枚葉印字の際、重送が発生
することなく良好なプリンター搬送性を示すことが判明
した。Further, although not originally expected, it was found that the printing density was improved by using a two-layer laminate of the cloth and the thermoplastic resin layer as the support as the support. In addition, it was found that by using the cloth as the support as the cloth and the split-fiber non-woven fabric, good printer transportability was exhibited without generating double feeding during sheet-fed printing.
【００１４】本発明において、布帛とは一般的な織布、
編布、不織布等を指し、これらを構成する繊維として
は、例えば、ポリエチレンテレフタレート、ポリブチレ
ンテレフタレート、又はこれらポリマーの変性ポリマー
等のホモポリマー及びコポリマーのようなポリエステル
系繊維、ポリプロピレン、ポリエチレン、ポリスチレ
ン、又はこれらポリマーの変性ポリマー等のホモポリマ
ー及びコポリマーのようなポリオレフィン系繊維、アク
リル繊維、モダクリル繊維等のようなポリアクリロニト
リル系繊維、ナイロン６、ナイロン６６等のようなナイ
ロン繊維、ポリビニルアルコール系繊維、ウレタン繊維
／等の有機合成繊維；又、レーヨン等の再生セルロース
繊維やコラーゲン、アルギン酸、キチン質等を溶液にし
たものを紡糸した繊維等のような再生繊維；アセテート
繊維等のような半合成繊維；麻、コットン、パルプ等の
セルロース系繊維や羊毛、絹等の蛋白質系繊維等のよう
な天然繊維；金属繊維、ガラス繊維、炭素繊維のような
無機系繊維、等の各種繊維が挙げられ、これらを単独又
は組み合わせて使用することが出来る。In the present invention, a fabric is a general woven fabric,
Knitted fabric, refers to nonwoven fabric and the like, as the fibers constituting these, for example, polyethylene-based fibers such as polyethylene terephthalate, polybutylene terephthalate, homopolymers and copolymers such as modified polymers of these polymers, polypropylene, polyethylene, polystyrene, Or polyolefin fibers such as homopolymers and copolymers such as modified polymers of these polymers, acrylic fibers, polyacrylonitrile fibers such as modacrylic fibers, nylon fibers such as nylon 6, nylon 66, etc., polyvinyl alcohol fibers, Organic synthetic fibers such as urethane fibers / etc .; regenerated cellulose fibers such as rayon or fibers spun from solutions of collagen, alginic acid, chitin, etc .; semi-synthetic fibers such as acetate fibers Fiber; natural fibers such as cellulosic fibers such as hemp, cotton, and pulp; and protein fibers such as wool and silk; and various fibers such as metal fibers, glass fibers, and inorganic fibers such as carbon fibers. These can be used alone or in combination.
【００１５】本発明で用いられる不織布は、大別して、
湿式不織布、又はステッチボンド方式、スパンボンド方
式、メルトブローン方式、サーマルボンド方式等による
乾式不織布、或いは湿式不織布又は乾式不織布を用いた
スパンレース不織布がある。The nonwoven fabric used in the present invention is roughly classified into
There is a wet nonwoven fabric, a dry nonwoven fabric by a stitch bond method, a spun bond method, a melt blown method, a thermal bond method, or the like, or a spunlace nonwoven fabric using a wet nonwoven fabric or a dry nonwoven fabric.
【００１６】本発明の支持体である積層構造を有する布
帛とは、布帛と他の基材とが積層され一体化されている
ものであればよい。布帛と積層される他の基材として
は、同一種類の布帛、異なる種類の布帛、または、紙、
合成樹脂シート、合成紙等積層し一体化が可能であるも
のであれば特に制限されない。The fabric having a laminated structure, which is the support of the present invention, may be any fabric as long as the fabric and another substrate are laminated and integrated. As the other substrate to be laminated with the fabric, the same type of fabric, different types of fabric, or paper,
There are no particular restrictions on the synthetic resin sheet, synthetic paper, etc., as long as they can be laminated and integrated.
【００１７】布帛と他の基材を積層し一体化する手段と
しては、ドライラミ、ウェットラミ、サンドラミ、熱融
着等公知の技術を用いることができる。また、布帛同士
を積層し一体化する手段としては、積層体上方から高圧
の柱状水流を噴射して行う３次元交絡法を用いることが
できる。As a means for laminating and integrating the fabric and another base material, known techniques such as dry lamination, wet lamination, sand lamination, and heat fusion can be used. Further, as a means for laminating and integrating the fabrics, a three-dimensional confounding method in which a high-pressure columnar water stream is jetted from above the laminate can be used.
【００１８】特に布帛と熱可塑性樹脂層との積層体を支
持体として用いると、インクジェット記録した際の印字
濃度が熱可塑性樹脂層以外の他の基材と貼り合わせたも
のより向上することが判明した。本発明における熱可塑
性樹脂層を形成する熱可塑性樹脂は特に制限されない
が、好ましくはポリオレフィン樹脂ラミネート層が好ま
しく用いられる。ポリオレフィン樹脂とは、例えば、以
下の物質が挙げられる。高密度ポリエチレン、低密度ポ
リエチレン、中密度ポリエチレン、直鎖状低密度ポリエ
チレン等のポリエチレン；アイソタクチック、シンジオ
タクチック、アタクチック、それらの混合物、エチレン
とのランダム共重合体又はブロック共重合体等のポリプ
ロピレン；その他ポリ−３−メチルペンテン−１、ポリ
エチレングリコールテレフタレート、ポリ塩化ビニル、
ポリ塩化ビニリデン、エバール、エチレン酢酸ビニル共
重合体等を単独或は混合して使用できる。また、熱可塑
性樹脂層を設けた直後に、他の基材を重ね合わせ一体化
し、熱可塑性樹脂層を中間層とした３層構造からなる積
層体を支持体として用いても構わない。In particular, it has been found that when a laminate of a fabric and a thermoplastic resin layer is used as a support, the print density at the time of ink-jet recording is higher than that obtained by laminating with a substrate other than the thermoplastic resin layer. did. The thermoplastic resin forming the thermoplastic resin layer in the present invention is not particularly limited, but a polyolefin resin laminate layer is preferably used. The polyolefin resin includes, for example, the following substances. Polyethylene such as high-density polyethylene, low-density polyethylene, medium-density polyethylene, and linear low-density polyethylene; isotactic, syndiotactic, atactic, mixtures thereof, random copolymers with ethylene or block copolymers, etc. Polypropylene; other poly-3-methylpentene-1, polyethylene glycol terephthalate, polyvinyl chloride,
Polyvinylidene chloride, Eval, ethylene-vinyl acetate copolymer and the like can be used alone or in combination. Immediately after the thermoplastic resin layer is provided, another substrate may be overlapped and integrated, and a laminate having a three-layer structure in which the thermoplastic resin layer is an intermediate layer may be used as the support.
【００１９】また、布帛と割繊維不織布との積層体を支
持体として用いると、Ａ４判、Ａ３判といった寸法のカ
ットシートでインクジェット印字を行う際、重なり合っ
たシートが２枚以上重なったまま搬送される重走が発生
することがなくなり、使用できるインクジェットプリン
ターの範囲が広くなる。割繊維不織布としては、連続的
なメッシュ様の形態の不織布をいい、好ましくはポリエ
チレン製割繊維不織布が用いられ得る。When a laminate of a cloth and a split-fiber non-woven fabric is used as a support, when ink-jet printing is performed on cut sheets of A4 size or A3 size, two or more overlapping sheets are conveyed while overlapping. Double running does not occur, and the range of usable inkjet printers is widened. As the split fiber non-woven fabric, a continuous mesh-like non-woven fabric is used, and preferably, a split fiber non-woven fabric made of polyethylene can be used.
【００２０】本発明のインクジェット記録シートを作製
するために積層構造を有する布帛にインク受理性を付与
する必要がある。インク受理成分を布帛に含浸或いは塗
工すればよい。その手段としては、各種ブレードコータ
ー、ロールコーター、エアーナイフコーター、バーコー
ター、ロッドブレードコーター、ショートドウェルコー
ター、コンマコーター、ダイコーター、リバースロール
コーター、キスコーター、ディップコーター、カーテン
コーター、エクストルージョンコーター、ゲートロール
コーター、グラビアコーター、マイクログラビアコータ
ー、サイズプレス、タブサイズプレスなどの塗工装置を
用いることが出来る。In order to produce the ink jet recording sheet of the present invention, it is necessary to impart ink receptivity to a fabric having a laminated structure. The cloth may be impregnated or coated with the ink receiving component. The means include various blade coaters, roll coaters, air knife coaters, bar coaters, rod blade coaters, short dwell coaters, comma coaters, die coaters, reverse roll coaters, kiss coaters, dip coaters, curtain coaters, extrusion coaters, gates Coating devices such as a roll coater, a gravure coater, a microgravure coater, a size press, and a tab size press can be used.
【００２１】本発明のインクジェット記録シートにおい
て、インク受理成分の塗工量は特に制限されることはな
いが、好ましくは５ｇ/ｍ2以上５０ｇ/ｍ2以下で、更に
好ましくは１０ｇ/ｍ2以上４０ｇ/ｍ2以下である。塗工
量が５ｇ/ｍ2より少なくなるとインク吸収能が低下しに
じみが発生する。また、塗工量が５０ｇ/ｍ2を超えると
インク受理成分の粉落ちが目立つようになり、やはり印
字品位低下をもたらす。In the ink jet recording sheet of the present invention, the coating amount of the ink receiving component is not particularly limited, but is preferably 5 g / m 2 or more and 50 g / m 2 or less, more preferably 10 g / m 2 or more. It is 40 g / m 2 or less. If the coating amount is less than 5 g / m 2 , the ink absorbing ability is reduced and bleeding occurs. On the other hand, when the coating amount exceeds 50 g / m 2 , powder dropping of the ink-receiving component becomes conspicuous, which also lowers the print quality.
【００２２】本発明に用いられるインク受理成分中に
は、公知の白色顔料を１種以上用いることができる。例
えば、軽質炭酸カルシウム、重質炭酸カルシウム、カオ
リン、タルク、硫酸カルシウム、硫酸バリウム、二酸化
チタン、酸化亜鉛、硫化亜鉛、炭酸亜鉛、サチンホワイ
ト、珪酸アルミニウム、ケイソウ土、珪酸カルシウム、
珪酸マグネシウム、合成非晶質シリカ、コロイダルシリ
カ、コロイダルアルミナ、擬ベーマイト、水酸化アルミ
ニウム、アルミナ、リトポン、ゼオライト、加水ハロイ
サイト、炭酸マグネシウム、水酸化マグネシウムなどの
白色無機顔料、スチレン系プラスチックピグメント、ア
クリル系プラスチックピグメント、ポリエチレン、マイ
クロカプセル、尿素樹脂、メラミン樹脂などの有機顔料
などが挙げられる。上記の中でも、インク受理成分中に
主体成分として含有する白色顔料としては、多孔性無機
顔料が好ましく、多孔性合成非晶質シリカ、多孔性炭酸
マグネシウム、多孔性アルミナなどが挙げられ、特に細
孔容積の大きい多孔性合成非晶質シリカが好ましい。In the ink receiving component used in the present invention, one or more known white pigments can be used. For example, light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate,
White inorganic pigments such as magnesium silicate, synthetic amorphous silica, colloidal silica, colloidal alumina, pseudoboehmite, aluminum hydroxide, alumina, lithopone, zeolite, hydrohaloysite, magnesium carbonate, magnesium hydroxide, styrene-based plastic pigment, and acrylic Organic pigments such as plastic pigment, polyethylene, microcapsules, urea resin, and melamine resin. Among the above, as the white pigment contained as a main component in the ink receiving component, a porous inorganic pigment is preferable, and porous synthetic amorphous silica, porous magnesium carbonate, porous alumina, and the like, and particularly, pores Large volume porous synthetic amorphous silica is preferred.
【００２３】本発明のインク受理成分にはカチオン性染
料定着剤を含有することができる。カチオン性染料定着
剤としては２級アミン、３級アミン、４級アンモニウム
塩などが挙げられ、これらのカチオン性染料定着剤はイ
ンク受理成分中の水性インクの染料分である水溶性直接
染料や水溶性酸性染料中のスルホン酸基、カルボキシル
基、アミノ基などと不溶な塩を形成するため、インク受
理成分にて染料を捕獲し、色彩性の向上や不溶な塩の形
成により水の滴下や吸湿によるインクの流れだしや滲み
だしを抑制し耐水性が向上させることができる。The ink receiving component of the present invention can contain a cationic dye fixing agent. Examples of the cationic dye fixing agent include secondary amines, tertiary amines, and quaternary ammonium salts. These cationic dye fixing agents include a water-soluble direct dye, which is a dye component of an aqueous ink in an ink receiving component, and a water-soluble dye. To form an insoluble salt with the sulfonic acid group, carboxyl group, amino group, etc. in the acidic acid dye, the dye is captured by the ink receiving component, and water is dropped and moisture is absorbed by improving color and forming an insoluble salt. Of the ink and the bleeding of the ink can be suppressed, and the water resistance can be improved.
【００２４】また、本発明のインク受理成分で用いられ
る接着剤としては、例えば、ポリビニルアルコール、酢
酸ビニル、酸化澱粉、エーテル化澱粉、カルボキシメチ
ルセルロース、ヒドロキシエチルセルロース等のセルロ
ース誘導体、カゼイン、ゼラチン、大豆蛋白、シリル変
性ポリビニルアルコール等；スチレン−ブタジエン共重
合体、メチルメタクリレート−ブタジエン共重合体等の
共役ジエン系共重合体ラテックス；アクリル酸エステル
及びメタクリル酸エステルの重合体又は共重合体、アク
リル酸及びメタクリル酸の重合体又は共重合体等のアク
リル系重合体ラテックス；エチレン酢酸ビニル共重合体
等のビニル系重合体ラテックス；或いはこれらの各種重
合体のカルボキシル基等の官能基含有単量体による官能
基変性重合体ラテックス；メラミン樹脂、尿素樹脂等の
熱硬化合成樹脂系等の水性接着剤；ポリメチルメタクリ
レート、ポリウレタン樹脂、不飽和ポリエステル樹脂、
塩化ビニル−酢酸ビニルコポリマー、ポリビニルブチラ
ール、アルキッド樹脂等の合成樹脂系接着剤が挙げら
れ、１種以上で使用される。The adhesive used in the ink-receiving component of the present invention includes, for example, polyvinyl alcohol, vinyl acetate, oxidized starch, etherified starch, cellulose derivatives such as carboxymethylcellulose, hydroxyethylcellulose, casein, gelatin, soy protein. Conjugated diene copolymer latex such as styrene-butadiene copolymer and methyl methacrylate-butadiene copolymer; polymer or copolymer of acrylic acid ester and methacrylic acid ester; acrylic acid and methacrylic acid Acrylic polymer latex such as acid polymer or copolymer; Vinyl polymer latex such as ethylene-vinyl acetate copolymer; or functional group based on functional group-containing monomer such as carboxyl group of these various polymers Modified polymer latte Box; melamine resins, water-based adhesives of thermosetting synthetic resin such as a urea resin; polymethyl methacrylate, polyurethane resin, unsaturated polyester resin,
Synthetic resin-based adhesives such as vinyl chloride-vinyl acetate copolymer, polyvinyl butyral, and alkyd resin can be used, and one or more kinds are used.
【００２５】さらに、その他の添加剤として、顔料分散
剤、増粘剤、流動性改良剤、消泡剤、抑泡剤、離型剤、
発泡剤、浸透剤、着色染料、着色顔料、蛍光増白剤、紫
外線吸収剤、酸化防止剤、防腐剤、防バイ剤、耐水化
剤、湿潤紙力増強剤、乾燥紙力増強剤等をインク受理層
中に適宜配合することもできる。Further, other additives include a pigment dispersant, a thickener, a flow improver, an antifoaming agent, a foam inhibitor, a release agent,
Inks with foaming agents, penetrants, coloring dyes, coloring pigments, fluorescent whitening agents, ultraviolet absorbers, antioxidants, preservatives, anti-binders, water-proofing agents, wet strength agents, dry strength agents, etc. It can also be appropriately compounded in the receiving layer.
【００２６】本発明において、積層構造を有する布帛に
インク受理性を付与するのは、積層構造体となす前の布
帛にインク受理性を付与した後に他の基材と一体化して
もよいし、他の基材と一体化した後に積層構造を有する
布帛にインク受理性を付与してもよい。In the present invention, imparting ink receptivity to a fabric having a laminated structure may be performed by imparting ink receptivity to a fabric before forming a laminated structure, and then integrating the fabric with another substrate. After being integrated with another base material, the ink having the laminated structure may be provided with ink receptivity.
【００２７】また、インク受理性を付与した後には、マ
シンカレンダー、ＴＧカレンダー、スーパーカレンダ
ー、ソフトカレンダーなどのカレンダーを用いて平坦化
仕上げを行っても良い。After imparting ink receptivity, flattening may be performed using a calendar such as a machine calendar, a TG calendar, a super calendar, or a soft calendar.
【００２８】[0028]
【実施例】以下に、本発明の実施例をあげて説明する
が、本発明はこれらの例に限定されるものではない。ま
た、実施例、及び比較例において「部」及び「％」は、
特に明示しない限り重量部及び重量％を示す。EXAMPLES The present invention will be described below with reference to examples of the present invention, but the present invention is not limited to these examples. In Examples and Comparative Examples, “parts” and “%”
Unless indicated otherwise, parts by weight and% by weight are indicated.
【００２９】〈インク受理成分液の作製〉合成非晶質シ
リカ（Ｎｉｐｓｉｌ ＲＳ１５０：日本シリカ工業製）
１００部、酢酸ビニル−エチレン−特殊エステル系接着
剤（スミカフレックス９５１、：住友化学工業製）３０
部、カチオン性染料定着剤（スミレーズレジン１００
１：住友化学工業製）２０部を用い、これを調液し、固
形分濃度１３％としたインク受理成分液とした。<Preparation of Ink Receiving Component Liquid> Synthetic amorphous silica (Nipsil RS150: manufactured by Nippon Silica Industry)
100 parts, vinyl acetate-ethylene-special ester adhesive (Sumika Flex 951, manufactured by Sumitomo Chemical Co., Ltd.) 30
Parts, cationic dye fixing agent (SUMIREZ Resin 100
1: Sumitomo Chemical Co., Ltd.), and prepared as an ink receiving component liquid having a solid concentration of 13%.
【００３０】〈不織布の作製〉積層構造を有さない布帛
として不織布を次のようにして作製した。繊維径０．１
デニールのポリエチレンテレフタレート繊維９５部と熱
水可溶性ポリビニールアルコール繊維（２デニール、繊
維長３ｍｍ）５部からなる水性スラリーを調製し、湿式
抄紙法を用いて坪量５０ｇ/ｍ2の不織布を作製した。熱
水可溶性ポリビニールアルコール繊維は、乾燥時の熱に
より繊維としての形態を維持しなくなりバインダーとし
てポリエチレンテレフタレート繊維間に存在するように
なり、該不織布は繊維径が０．１デニールの繊維より構
成されることとなる。<Preparation of Nonwoven Fabric> A nonwoven fabric was prepared as a fabric having no laminated structure as follows. Fiber diameter 0.1
An aqueous slurry composed of 95 parts of denier polyethylene terephthalate fiber and 5 parts of hot water-soluble polyvinyl alcohol fiber (2 denier, fiber length 3 mm) was prepared, and a nonwoven fabric having a basis weight of 50 g / m 2 was prepared by a wet papermaking method. . The hot water-soluble polyvinyl alcohol fiber does not maintain its form as a fiber due to heat during drying, and exists as a binder between polyethylene terephthalate fibers, and the nonwoven fabric is composed of fibers having a fiber diameter of 0.1 denier. The Rukoto.
【００３１】実施例１ 布帛としての予備操作で作製した不織布の一方の面に同
じく予備操作で作製したインク受理成分液をコンマコー
ターを用いて乾燥後の塗工量３０ｇ/ｍ2となるように塗
布し、乾燥してインク受理性を付与された不織布を作製
した。つぎに、インク受理性を付与された不織布のイン
ク受理成分液が塗布された面の反対面と他の基材として
予備操作で作製した不織布の一方の面が向かい合うよう
にしてドライラミネート法により両者を一体化して、本
発明のインクジェット記録シートを得た。Example 1 A nonwoven fabric prepared by a preliminary operation as a cloth was coated on one side with an ink receiving component liquid prepared by the same preliminary operation using a comma coater so as to have a coating amount of 30 g / m 2 after drying. It was applied and dried to produce a nonwoven fabric provided with ink receptivity. Next, the non-woven fabric provided with the ink-receiving property was subjected to a dry lamination method such that the opposite surface of the surface on which the ink receiving component liquid was applied and one surface of the non-woven fabric prepared by the preliminary operation as another substrate faced each other. Were integrated to obtain an ink jet recording sheet of the present invention.
【００３２】実施例２ 他の基材を坪量４０ｇ/ｍ2の上質紙に変更した以外は実
施例１と同様にして本発明のインクジェット記録シート
を得た。Example 2 An ink jet recording sheet of the present invention was obtained in the same manner as in Example 1 except that the other base material was changed to high quality paper having a basis weight of 40 g / m 2 .
【００３３】実施例３ 布帛としての予備操作で作製した不織布の一方の面に低
密度ポリエチレンを溶融押し出しダイを用いて、厚さが
１０μｍになるようにラミネートした。ラミネートされ
た該不織布のラミネート面と反対面に予備操作で作製し
たインク受理成分液をコンマコーターを用いて乾燥後の
塗工量３０ｇ/ｍ2となるように塗布し、乾燥して本発明
のインクジェット記録シートを得た。Example 3 A low-density polyethylene was laminated on one surface of a nonwoven fabric prepared by a preliminary operation as a fabric to a thickness of 10 μm using a melt extrusion die. The ink-receiving component liquid prepared by the preliminary operation is applied to the opposite side of the laminated nonwoven fabric from the laminating surface using a comma coater so as to have a coating amount of 30 g / m 2 after drying, and then dried and dried. An ink jet recording sheet was obtained.
【００３４】実施例４ 他の基材を厚さ７０μｍの割繊維不織布（日石ワリフＳ
Ｓ、日石プラスト（株））製に変更し、積層構造体の作
製方法を熱融着に変更した以外は実施例１と同様にして
本発明のインクジェット記録シートを得た。Example 4 A 70-μm-thick split-fiber nonwoven fabric (Nisseki Warif S
S, an ink jet recording sheet of the present invention was obtained in the same manner as in Example 1 except that the method was changed to Nisseki Plast Co., Ltd., and the method of manufacturing the laminated structure was changed to heat fusion.
【００３５】実施例５ 予備操作で作製した積層構造を有さない布帛としての不
織布の表裏共に水圧１００kg/cm2、速度２０ｍ／分で交
絡処理を行い、１２０℃で乾燥し、３次元交絡してなる
スパンレース不織布を得た。該スパンレース不織布に実
施例１と同様にしてインク受理性を付与した後、実施例
４と同様にして割繊維不織布との積層構造体とした。Example 5 Entangling treatment was performed at a water pressure of 100 kg / cm 2 at a speed of 20 m / min on both sides of a nonwoven fabric as a non-laminated fabric prepared by a preliminary operation, dried at 120 ° C., and three-dimensionally entangled. The resulting spunlace nonwoven fabric was obtained. After imparting ink receptivity to the spunlaced nonwoven fabric in the same manner as in Example 1, a laminated structure with a split-fiber nonwoven fabric was formed in the same manner as in Example 4.
【００３６】比較例１ 実施例１で作製したインク受理性を付与された積層構造
を有さない布帛としての不織布を比較例のインクジェッ
ト記録シートとした。Comparative Example 1 The non-woven fabric as the fabric having no ink-accepting laminated structure and prepared in Example 1 was used as an ink jet recording sheet of Comparative Example.
【００３７】比較例２ 不織布の坪量を１００ｇ/ｍ2として予備操作と同様に作
製した不織布を使用した以外は比較例１と同様にしてイ
ンクジェット記録シートを作製した。Comparative Example 2 An ink jet recording sheet was produced in the same manner as in Comparative Example 1 except that the nonwoven fabric was prepared in the same manner as in the preliminary operation, except that the basis weight of the nonwoven fabric was 100 g / m 2 .
【００３８】〈試験方法〉 １）プリンター適性 実施例及び比較例で作製したインクジェット記録シート
をＡ２判に断裁後、大型インクジェットプリンター
（（株）ミマキエンジニアリング製 ＪＶ２−１３０）
で適当な画像を全面に渡り印字する。印字を１０枚のサ
ンプルについて行い、印字ヘッドとの擦れ等障害が発生
した枚数を結果とした。<Test Method> 1) Suitability for Printer After cutting the ink jet recording sheets prepared in Examples and Comparative Examples to A2 size, a large ink jet printer (JV2-130 manufactured by Mimaki Engineering Co., Ltd.)
To print an appropriate image over the entire surface. Printing was performed on ten samples, and the number of sheets having troubles such as rubbing with the print head was determined.
【００３９】２）印字濃度 実施例及び比較例で作製した記録シートをＡ４判に断裁
した後、インクジェットプリンター（（株）ミマキエン
ジニアリング製 ＪＶ２−１３０）でブラック、シア
ン、マゼンタ、イエローの各色１００％のベタ印字を行
う。マクベスＲＤ９１９で印字部の濃度を測定した。値
は大きい方が印字濃度が高く印字性が良好であることを
示す。2) Print Density The recording sheets prepared in Examples and Comparative Examples were cut to A4 size, and then 100% each of black, cyan, magenta, and yellow was printed by an inkjet printer (JV2-130, manufactured by Mimaki Engineering Co., Ltd.). Perform solid printing. The density of the printed area was measured by Macbeth RD919. Larger values indicate higher print density and better printability.
【００４０】３）プリンター搬送性 実施例及び比較例で作製した記録シートをＡ４判に断裁
した後、インクジェットプリンター（エプソン製 ＰＭ
−７５０Ｃ）で２０枚を１セットとして５セット連続印
字を行う。重走等の搬送トラブル発生率をトラブル数と
印字回数から算出する。トラブル発生率が低いほどプリ
ンター搬送性は良好である。3) Printer transportability The recording sheets prepared in the examples and comparative examples were cut into A4 size papers, and then ink-jet printers (PM manufactured by Epson).
At −750 C), five sets of continuous printing are performed with 20 sheets as one set. The transport trouble occurrence rate such as heavy running is calculated from the number of troubles and the number of times of printing. The lower the trouble rate, the better the printer transportability.
【００４１】[0041]
【表１】 [Table 1]
【００４２】評価：表１から明らかなように、本発明の
インクジェット記録シートはプリンターで搬送時にたる
み等が発生することなく印字ヘッドと擦ることなく良好
なプリンター適性を有している（実施例１〜５）。さら
に、実施例３のように不織布と積層する他の基材を熱可
塑性樹脂層にすると明らかに印字濃度が向上している。
また、実施例４，５のように他の基材を割繊維不織布に
することにより枚葉シートでの搬送性が向上しプリンタ
ーの搬送トラブルが全く発生しないことがわかる。しか
し、比較例のように、積層構造とする前の不織布をその
まま支持体とした比較例１、あるいは腰を増すため不織
布の坪量を増やした比較例２では、特にプリンター適
性、プリンター搬送性に劣ることがわかる。Evaluation: As is evident from Table 1, the ink jet recording sheet of the present invention has good printer suitability without causing sagging or the like when transported by a printer and rubbing against a print head (Example 1). ~ 5). Further, when the other substrate laminated with the nonwoven fabric as in Example 3 is made of a thermoplastic resin layer, the print density is clearly improved.
Further, it can be seen that the transferability of a single sheet is improved by using a split-fiber nonwoven fabric as another substrate as in Examples 4 and 5, and no transfer trouble occurs in the printer. However, in Comparative Example 1 in which the nonwoven fabric before the laminated structure was used as a support as in the comparative example, or in Comparative Example 2 in which the basis weight of the nonwoven fabric was increased in order to increase the stiffness, the printer suitability and printer transportability were particularly reduced. It turns out that it is inferior.
【００４３】[0043]
【発明の効果】本発明のインクジェット記録シートは、
優れたプリンター適性を有しているため、特に大判での
印刷の際印字ヘッドとの擦れが発生することなく良好な
画像を得ることができる上、枚葉としても連続印字が可
能で、幅広く多くのプリンターで使用でき有用である。The ink jet recording sheet of the present invention is
Because of its excellent printer suitability, it is possible to obtain good images without rubbing with the print head especially when printing in large format, and it is also possible to print continuously as single sheet, It can be used with other printers and is useful.
Claims (3)
塗設あるいは含浸してなるインクジェット記録シートに
おいて、該布帛が積層構造を有する布帛であることを特
徴とするインクジェット記録シート。1. An ink jet recording sheet obtained by coating or impregnating an ink receiving component on a cloth as a support, wherein the cloth is a cloth having a laminated structure.
脂層とを積層した積層構造を有することを特徴とする請
求項１記載のインクジェット記録シート。2. The ink jet recording sheet according to claim 1, wherein the cloth as the support has a laminated structure in which the cloth and the thermoplastic resin layer are laminated.
布とを積層した積層構造を有することを特徴とする請求
項１記載のインクジェット記録シート。3. The ink jet recording sheet according to claim 1, wherein the cloth as the support has a laminated structure in which the cloth and the split-fiber non-woven fabric are laminated.