JP2001003934A - Direct acting guide sliding bearing device - Google Patents
Direct acting guide sliding bearing deviceInfo
- Publication number
- JP2001003934A JP2001003934A JP11171812A JP17181299A JP2001003934A JP 2001003934 A JP2001003934 A JP 2001003934A JP 11171812 A JP11171812 A JP 11171812A JP 17181299 A JP17181299 A JP 17181299A JP 2001003934 A JP2001003934 A JP 2001003934A
- Authority
- JP
- Japan
- Prior art keywords
- sliding
- slider
- guide rail
- bearing device
- tin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、工作機械、産業機
械、搬送装置、各種測定装置等に用いられる直動案内装
置に係わり、特に転がり軸受ではなくすべり軸受が用い
られ、軸受としての使用時に摺動面への給油を必要とし
ない小形、軽量な無潤滑の直動案内滑り軸受装置に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a linear motion guide device used for machine tools, industrial machines, transfer devices, various measuring devices, and the like. In particular, a slide bearing is used instead of a rolling bearing. The present invention relates to a small, lightweight, non-lubricated linear guide sliding bearing device that does not require oiling of a sliding surface.
【０００２】[0002]
【従来の技術及びその課題】従来のこの種の直動案内滑
り軸受装置として、例えば特開平９−２９６８２４号公
報に記載されるものが知られている。これは、外面に軸
線方向に延びる溝を有する案内レールと、案内レールの
溝に対向する溝を内面に有して軸線方向に相対滑り移動
可能に案内レールに組付けられたスライダとを備え、案
内レールとスライダとの対向した溝間に潤滑剤含有のゴ
ム又は合成樹脂からなる滑り部材を介装している。この
直動案内滑り軸受装置によれば、潤滑剤（グリース、、
パラフィン系炭化水素油、鉱油、エーテル油、エステル
油等）が、滑り部材から徐々にしみ出して、案内レール
の溝に自動的に供給されるとしている。2. Description of the Related Art As a conventional linear guide sliding bearing device of this type, for example, a device described in Japanese Patent Application Laid-Open No. 9-296824 is known. This comprises a guide rail having a groove extending in the axial direction on the outer surface, and a slider attached to the guide rail so as to be relatively slidable in the axial direction with a groove facing the groove of the guide rail on the inner surface, A sliding member made of rubber or synthetic resin containing a lubricant is interposed between the grooves facing the guide rail and the slider. According to this linear guide sliding bearing device, the lubricant (grease,
Paraffin hydrocarbon oil, mineral oil, ether oil, ester oil, etc.) gradually exudes from the sliding member and is automatically supplied to the groove of the guide rail.
【０００３】しかしながら、このような従来の直動案内
滑り軸受装置にあつては、溝に介装する滑り部材が必須
であり、スライダの軸線方向前後に滑り部材を固定する
厚肉のエンドキャップが必要になるので、構造が複雑に
なるのみならず部品点数が多くなる。更に、案内レール
やそれに対向するスライダの両側部分に滑り部材を介装
するための溝を有しており、両溝の加工が必要になると
共に、滑り部材を受け入れる大きさの溝とするために、
案内レール及びスライダに所定の肉厚も必要になる。そ
の結果、加工・組付けが面倒・複雑で、軸受装置も大
形、重量増、高コストになるという技術的課題を有して
いる。However, in such a conventional linear guide sliding bearing device, a sliding member interposed in the groove is indispensable, and a thick end cap for fixing the sliding member in the axial direction of the slider is required. Since it becomes necessary, not only the structure becomes complicated but also the number of parts increases. Furthermore, a groove for interposing a sliding member is provided on both sides of the guide rail and the slider facing the guide rail, so that both grooves need to be processed and a groove large enough to receive the sliding member. ,
The guide rail and the slider also require a predetermined thickness. As a result, there is a technical problem that machining / assembly is complicated and complicated, and the bearing device is large in size, increased in weight, and expensive.
【０００４】本発明は、このような従来の技術的課題に
鑑みてなされたものであり、部品点数が少なく、加工が
容易なため、小形、軽量、安価な無潤滑で直動案内の機
構を長期間維持できる直動案内滑り軸受装置を提供する
ことを目的としている。The present invention has been made in view of such conventional technical problems, and has a small number of parts, is easy to machine, and has a small, light-weight, inexpensive, non-lubricated linear motion guide mechanism. It is an object of the present invention to provide a linear guide sliding bearing device that can be maintained for a long time.
【０００５】[0005]
【課題を解決するための手段】本発明は、このような従
来の技術的課題に鑑みてなされたものであり、その構成
は次の通りである。請求項１の発明の構成は、内面に摺
動面４ｂ，４ｂをテーパ状に有し、無潤滑状態で良好な
摺動性能を有する錫含有アルミニウム合金摺動材で製作
されたスライダ４と、案内レール１とを備え、前記案内
レール１が、該スライダ４の摺動面４ｂ，４ｂに対応す
る被摺動面１ｂ，１ｂを両側面にテーパ状に有すると共
に、該被摺動面１ｂ，１ｂに、無潤滑状態で良好な摺動
性能を有する固体潤滑剤含有樹脂被膜１１ｂ，１１ｂを
有し、該スライダ４の摺動面４ｂ，４ｂが案内レール１
の固体潤滑剤含有樹脂被膜１１ｂ，１１ｂ上を移動する
ことを特徴とする直動案内滑り軸受装置である。請求項
２の発明の構成は、固体潤滑剤含有樹脂被膜１１ａ，１
１ｂ，１１ｂを有する案内レール１と錫含有アルミニウ
ム合金製のスライダ４とを有し、該スライダ４の摺動面
４ｂ，４ｃが該案内レール１の固体潤滑剤含有樹脂被膜
１１ａ，１１ｂ，１１ｂを摺動する直動案内滑り軸受装
置であつて、該錫含有アルミニウム合金が、重量％で、
錫６〜４０％、鉛０〜８％、珪素０〜１０％、銅０〜３
％、残部がアルミニウムからなり、該固体潤滑剤含有樹
脂被膜１１ａ，１１ｂ，１１ｂが、体積％で、ＰＴＦ
Ｅ、ＭｏＳ２、黒鉛から選ばれた１種以上を５０％以下
含有し、残部が熱硬化性樹脂によつて製作されているこ
とを特徴とする直動案内滑り軸受装置である。請求項３
の発明の構成は、内面に摺動面４ｂ，４ｂをテーパ状に
有し、かつ、内側上面に摺動上面４ｃを有し、無潤滑状
態で良好な摺動性能を有する錫含有アルミニウム合金摺
動材で製作されたスライダ４と、案内レール１とを備
え、前記案内レール１が、該スライダ４の摺動面４ｂ，
４ｂに対応する被摺動面１ｂ，１ｂを両側面にテーパ状
に有し、かつ、該スライダ４の摺動上面４ｃに対応する
被摺動上面１ａを上面に有し、該スライダ４の摺動面４
ｂ，４ｂが案内レール１の被摺動面１ｂ，１ｂに沿い、
かつ、該スライダ４の摺動上面４ｃが案内レール１の被
摺動上面１ａに沿つて移動する直動案内滑り軸受装置で
あつて、スライダ４の摺動面４ｂ及び摺動上面４ｃの少
なくとも一部に、弾力性及び潤滑性能を有した樹脂板６
又は潤滑性能を有する固体潤滑剤含有樹脂で被覆された
板状スプリング１６の少なくとも一方が、前記被摺動面
１ｂ及び被摺動上面１ａに対向させて組み込まれ、前記
樹脂板６又は板状スプリング１６が、常に予圧を与えら
れて前記案内レール１の被摺動面１ｂ，１ｂ又は被摺動
上面１ａに弾性的に接触していることを特徴とする直動
案内滑り軸受装置である。請求項４の発明の構成は、錫
含有アルミニウム合金摺動材製のスライダ４が、重量％
で、錫６〜４０％、鉛０〜８％、珪素０〜１０％、銅０
〜３％、残部がアルミニウムからなる材料によつて製作
され、潤滑性能を有した樹脂板６が、ＰＴＦＥを有し、
板状スプリング１６に被覆されている固体潤滑剤含有樹
脂が、体積％で、ＰＴＦＥ、ＭｏＳ２、黒鉛から選ばれ
た１種以上を５０％以下含有し、残部が熱硬化性樹脂か
らなることを特徴とする請求項３の直動案内滑り軸受装
置である。SUMMARY OF THE INVENTION The present invention has been made in view of such conventional technical problems, and has the following configuration. The slider according to the first aspect of the present invention has a slider 4 made of a tin-containing aluminum alloy sliding material having good sliding performance in a non-lubricated state, having sliding surfaces 4b, 4b on the inner surface in a tapered shape. And a guide rail 1. The guide rail 1 has sliding surfaces 1b, 1b corresponding to the sliding surfaces 4b, 4b of the slider 4 in a tapered shape on both side surfaces, and the sliding surfaces 1b, 1b. 1b has solid lubricant-containing resin coatings 11b, 11b having good sliding performance in a non-lubricated state, and the sliding surfaces 4b, 4b of the slider 4 are
A linear guide sliding bearing device which moves on the solid lubricant-containing resin coatings 11b, 11b. The second aspect of the present invention provides a solid lubricant-containing resin coating 11a, 1
The guide rail 1 includes a guide rail 1 having a guide rail 1b and a slider 4 made of a tin-containing aluminum alloy, and sliding surfaces 4b and 4c of the slider 4 cover the solid lubricant-containing resin coatings 11a, 11b and 11b of the guide rail 1. A sliding linear guide sliding bearing device, wherein the tin-containing aluminum alloy is, by weight%,
6-40% tin, 0-8% lead, 0-10% silicon, 0-3 copper
%, The balance being aluminum and the solid lubricant-containing resin coatings 11a, 11b, 11b are
A linear guide sliding bearing device characterized in that it contains at least 50% of at least one selected from the group consisting of E, MoS2 and graphite, and the remainder is made of a thermosetting resin. Claim 3
The present invention has a tin-containing aluminum alloy slide having good sliding performance in a non-lubricated state, having sliding surfaces 4b, 4b in a tapered shape on an inner surface and a sliding upper surface 4c on an inner upper surface. A slider 4 made of a moving material and a guide rail 1 are provided, and the guide rail 1 has a sliding surface 4b,
The slider 4 has a sliding surface 1b corresponding to the sliding surface 4b and a sliding upper surface 1a corresponding to the sliding upper surface 4c of the slider 4 on the upper surface. Moving surface 4
b, 4b are along the sliding surfaces 1b, 1b of the guide rail 1,
A linear guide sliding bearing device in which the sliding upper surface 4c of the slider 4 moves along the sliding upper surface 1a of the guide rail 1, wherein at least one of the sliding surface 4b and the sliding upper surface 4c of the slider 4 is provided. A resin plate 6 having elasticity and lubrication performance
Alternatively, at least one of the plate-like springs 16 coated with a solid lubricant-containing resin having lubricating performance is incorporated so as to face the sliding surface 1b and the sliding upper surface 1a, and the resin plate 6 or the plate-like spring is mounted. Numeral 16 is a linear guide sliding bearing device characterized in that it is always preloaded and elastically contacts the sliding surfaces 1b, 1b or the sliding upper surface 1a of the guide rail 1. According to a fourth aspect of the present invention, the slider 4 made of a tin-containing aluminum alloy sliding material has a weight percentage of
6 to 40% of tin, 0 to 8% of lead, 0 to 10% of silicon, 0 of copper
-3%, the balance being made of a material consisting of aluminum, the lubricating resin plate 6 having PTFE,
The solid lubricant-containing resin coated on the plate spring 16 contains 50% or less by volume of at least one selected from PTFE, MoS2, and graphite, and the balance is made of a thermosetting resin. The linear guide sliding bearing device according to claim 3.
【０００６】[0006]
【発明の実施の形態】以下、本発明の第１実施の形態に
ついて図１〜図３を参照して説明する。図中において符
号１は金属又は合成樹脂製の案内レールであり、案内レ
ール１は、断面が台形をなす長尺部材であり、上面が形
成する被摺動上面１ａの左右の両側面がテーパ状をなし
てそれぞれ被摺動面１ｂを形成している。なお、一対の
被摺動面１ｂは、被摺動上面１ａから底面に向けて、次
第に間隔が小さくなつている。３は、案内レール１の被
摺動上面１ａから底面にまで貫通させて形成したボルト
用孔であり、案内レール１を図外の基盤に固定するため
に使用される。この案内レール１を跨いで、スライダ４
が摺動自在に組付けられる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a first embodiment of the present invention will be described with reference to FIGS. In the drawing, reference numeral 1 denotes a guide rail made of metal or synthetic resin. The guide rail 1 is a long member having a trapezoidal cross section, and the left and right sides of a sliding upper surface 1a formed by an upper surface are tapered. To form the sliding surface 1b. The distance between the pair of sliding surfaces 1b gradually decreases from the sliding upper surface 1a to the bottom surface. Reference numeral 3 denotes a bolt hole formed by penetrating from the sliding upper surface 1a to the bottom surface of the guide rail 1, and is used for fixing the guide rail 1 to a base (not shown). The slider 4 is straddled over the guide rail 1.
Are slidably assembled.
【０００７】スライダ４は、アルミニウム合金摺動材に
て一体に製作され、図３に示すように台形凹部４ａを有
し、台形凹部４ａを区画する左右の両内面がテーパ状を
なしてそれぞれ摺動面４ｂを形成している。台形凹部４
ａを区画する内側上面は、摺動上面４ｃを形成してい
る。スライダ４の台形凹部４ａは、図２に示すように案
内レール１の上部と適合する形状を有しており、従つ
て、一対の摺動面４ｂが案内レール１の左右の被摺動面
１ｂと適合し、摺動上面４ｃが案内レール１の被摺動上
面１ａと適合している。スライダ４の外側上面に形成し
たねじ穴５は、案内レール１に沿つて往復移動させたい
テーブル等の移動部材を取り付けるためのものである。
アルミニウム合金摺動材は、軽量、かつ、無潤滑状態で
良好な摺動性能を有している。なお、スライダ４は、後
述するように錫を含有するアルミニウム合金摺動材にて
製作することが、摺動抵抗を低減させる上で望ましい。
このスライダ４は、案内レール１の端部から差し入れ
て、摺動自在に組付けられる。The slider 4 is integrally formed of an aluminum alloy sliding material and has a trapezoidal concave portion 4a as shown in FIG. 3, and both left and right inner surfaces of the trapezoidal concave portion 4a are tapered to slide. The moving surface 4b is formed. Trapezoidal recess 4
The inner upper surface that defines “a” forms a sliding upper surface 4c. The trapezoidal concave portion 4a of the slider 4 has a shape compatible with the upper part of the guide rail 1 as shown in FIG. 2, so that a pair of sliding surfaces 4b are formed on the left and right sliding surfaces 1b of the guide rail 1. And the sliding upper surface 4c matches the sliding upper surface 1a of the guide rail 1. A screw hole 5 formed on the outer upper surface of the slider 4 is for attaching a moving member such as a table to be reciprocated along the guide rail 1.
The aluminum alloy sliding material is lightweight and has good sliding performance in a non-lubricated state. The slider 4 is desirably made of a tin-containing aluminum alloy sliding material as described later in order to reduce sliding resistance.
The slider 4 is inserted from the end of the guide rail 1 and slidably assembled.
【０００８】ここで、スライダ４を、重量％で、錫６〜
４０％、鉛０〜８％、珪素０〜１０％、銅０〜３％、残
部がアルミニウムからなる錫含有アルミニウム合金によ
つて製作すれば、無潤滑状態で良好な摺動性能を与える
ことができる。錫及び鉛は、無潤滑状態での潤滑性を良
好にする機能があり、上記の添加量未満では潤滑性が乏
しくなり、反対に上記の添加量を超えるとスライダ４の
剛性が低くなり、実用的でなくなるため、上記の範囲が
好ましい。珪素や銅は、更にスライダ４に耐摩耗性と強
度を必要とする場合に添加する。上記の添加量を超える
とアルミニウム合金中の析出珪素サイズが粗大になつた
り、アルミニウム合金の硬さが過大になるので、摺動相
手面を損耗させるので好ましくなく上記の範囲とする。[0008] Here, the slider 4 is made up of tin 6 to
If it is made of a tin-containing aluminum alloy consisting of 40%, lead 0-8%, silicon 0-10%, copper 0-3% and the balance being aluminum, good sliding performance can be given in a non-lubricated state. it can. Tin and lead have the function of improving the lubricity in a non-lubricated state. If the amount is less than the above, the lubricity becomes poor. The above range is preferable because it is not appropriate. Silicon or copper is added when the slider 4 needs wear resistance and strength. If the amount exceeds the above range, the size of the precipitated silicon in the aluminum alloy becomes coarse or the hardness of the aluminum alloy becomes excessive.
【０００９】そして、案内レール１の被摺動上面１ａ及
び左右の被摺動面１ｂには、無潤滑状態で良好な摺動性
能を有する固体潤滑剤含有樹脂被膜１１ａ，１１ｂが施
されている。案内レール１に固体潤滑剤含有樹脂１１
ａ，１１ｂを被覆する方法としては、有機溶剤で所望の
固体潤滑剤と添加物を含有させたエポキシ系、ポリアミ
ド・イミド系などの熱硬化性樹脂溶液をスプレー塗布や
浸漬によつて案内レール１に被覆させた後、１５０〜３
５０℃の温度中で１０〜６０分間焼成する方法が好適で
ある。固体潤滑剤としては、ＰＴＦＥ（ポリテトラフル
オロエチレン）、ＭｏＳ２（輝水鉛鉱）、黒鉛等が好適
である。The sliding upper surface 1a and the left and right sliding surfaces 1b of the guide rail 1 are provided with solid lubricant-containing resin films 11a and 11b having good sliding performance in a non-lubricated state. . Solid lubricant-containing resin 11 on guide rail 1
As a method of coating a and 11b, the guide rail 1 is spray-coated or dipped with a thermosetting resin solution such as an epoxy-based or polyamide-imide-based resin containing a desired solid lubricant and an additive in an organic solvent. After coating, 150 ~ 3
A method of baking at a temperature of 50 ° C. for 10 to 60 minutes is preferable. As the solid lubricant, PTFE (polytetrafluoroethylene), MoS2 (molybdenite), graphite and the like are preferable.
【００１０】案内レール１に被覆する固体潤滑剤含有樹
脂を、体積％で、ＰＴＦＥ、ＭｏＳ２、黒鉛から選ばれ
た１種以上の固体潤滑剤を５０％以下含有し、残部が熱
硬化性樹脂とすることで、無潤滑状態でも良好な潤滑性
を与えることができる。ＰＴＦＥ、ＭｏＳ２、黒鉛は、
樹脂被膜に混入させることにより、無潤滑状態での摩擦
力を小さくすることができ、良好な潤滑性を付与するた
めに添加する。これらの固体潤滑剤の添加量が体積％で
５０％を超えると樹脂被膜全体としての結合が弱くな
り、耐摩耗性（耐久性）が極端に低下し、実用的でなく
なるため、上記範囲とする。従つて、固体潤滑剤の添加
量は、本装置の用途によつて、上記範囲内で適宜調整さ
れる。つまり、耐摩耗性（耐久性）よりも低摩擦性を優
先する場合には固体潤滑剤の添加量を上記範囲内で多く
し、その反対に低摩擦性よりは耐摩耗性（耐久性）を優
先する場合には固体潤滑剤の添加量を最小限にする。ま
た、固体潤滑剤含有樹脂被膜１１ａ，１１ｂ，１１ｂに
すれば、液状潤滑剤とは異なり、補給の必要がないのみ
ならず、しみ出た液状潤滑剤によつて付近を汚損する恐
れがない。The resin containing the solid lubricant for coating the guide rail 1 contains, by volume%, at least 50% or less of one or more solid lubricants selected from PTFE, MoS2, and graphite, with the balance being a thermosetting resin. By doing so, good lubricity can be provided even in a non-lubricated state. PTFE, MoS2, graphite
By mixing in the resin film, the frictional force in a non-lubricated state can be reduced, and it is added to impart good lubricity. If the addition amount of these solid lubricants exceeds 50% by volume, the bonding of the entire resin film becomes weak, the wear resistance (durability) is extremely lowered, and it becomes impractical. . Therefore, the amount of the solid lubricant to be added is appropriately adjusted within the above range depending on the use of the present apparatus. In other words, when low friction is prioritized over wear resistance (durability), the amount of the solid lubricant added is increased within the above range, and conversely, wear resistance (durability) is improved over low friction. When priority is given, the amount of the solid lubricant to be added is minimized. In addition, unlike the liquid lubricant, the solid lubricant-containing resin coatings 11a, 11b, 11b not only do not need to be replenished, but also do not cause contamination of the vicinity due to the exuded liquid lubricant.
【００１１】このように、案内レール１の被摺動上面１
ａ及び左右の被摺動面１ｂ，１ｂには、無潤滑状態で良
好な摺動性能を有する固体潤滑剤含有樹脂被膜１１ａ，
１１ｂを形成させてあり、かつ、摺動相手材であるスラ
イダ４は、それ自体でも無潤滑状態で良好な摺動性能を
有するアルミニウム合金摺動材にて製作されている。こ
のため、それらを組み合わせた本発明に係る直動案内滑
り軸受装置によれば、案内レール１の被摺動上面１ａの
被膜１１ａ上をスライダ４の摺動上面４ｃが円滑に摺動
し、案内レール１の両被摺動面１ｂ，１ｂの被膜１１ｂ
をスライダ４の両摺動面４ｂ，４ｂが円滑に摺動する。Thus, the sliding upper surface 1 of the guide rail 1
a and the left and right sliding surfaces 1b, 1b are solid lubricant-containing resin coatings 11a, which have good sliding performance in a non-lubricated state.
The slider 4 on which 11b is formed and which is a sliding partner is made of an aluminum alloy sliding material which itself has good sliding performance in a non-lubricated state. For this reason, according to the linear guide sliding bearing device according to the present invention in which they are combined, the sliding upper surface 4c of the slider 4 smoothly slides on the coating 11a of the sliding upper surface 1a of the guide rail 1, and Coating 11b on both sliding surfaces 1b, 1b of rail 1
The sliding surfaces 4b of the slider 4 slide smoothly.
【００１２】台形凹部４ａを有するスライダ４と、台形
凹部４ａに適合する形状の案内レール１との組合せから
なる直動案内滑り軸受装置にすれば、従来例に比して構
造を簡素して軽量化することが可能であり、かつ、小さ
な摩擦力で滑らかに長時間往復移動させることができ
る。A linear guide sliding bearing device comprising a combination of a slider 4 having a trapezoidal recess 4a and a guide rail 1 having a shape adapted to the trapezoidal recess 4a has a simpler structure and lighter weight than the conventional example. It is possible to smoothly reciprocate for a long time with a small frictional force.
【００１３】更に、本発明に係る直動案内滑り軸受装置
は、案内レール１及びスライダ４に加工や組付けが複雑
・困難な溝を形成する必要がないのみならず、特にスラ
イダ４の構造が簡素であり、低コストかつ故障し難く耐
久性及び信頼性が共に向上する。Further, in the linear guide sliding bearing device according to the present invention, not only is it not necessary to form grooves which are complicated and difficult to process and assemble in the guide rail 1 and the slider 4, and in particular, the structure of the slider 4 is reduced. It is simple, low-cost, hard to break down, and improves both durability and reliability.
【００１４】図４，図５は、本発明の第２実施の形態を
示し、第１実施の形態と実質的に同一機能部分には同一
符号を付してそれらの説明は省略する。本実施の形態に
あつては、スライダ４に弾力性及び潤滑性を有する樹脂
板６を設けた点において、第１実施の形態と異なつてい
る。FIGS. 4 and 5 show a second embodiment of the present invention, in which substantially the same functional parts as those in the first embodiment are denoted by the same reference numerals, and their description is omitted. This embodiment is different from the first embodiment in that the slider 4 is provided with a resin plate 6 having elasticity and lubricity.
【００１５】図４，図５に示す樹脂板６は、スライダ４
の内側上面の摺動上面４ｃに固定され、その下面が案内
レール１の被摺動上面１ａに弾性的に接触している。従
つて、スライダ４の摺動上面４ｃは、案内レール１の被
摺動上面１ａと非接触状態にある。なお、案内レール１
の固体潤滑剤含有樹脂被膜１１ａ，１１ｂは、省略して
ある。この潤滑性能を有する樹脂板６は、ＰＴＦＥシー
トによつて形成するのが好適であり、ＰＴＦＥシートに
弾力性を与える予圧手段としては、摺動面となるＰＴＦ
Ｅを薄鋼板にコーティングし、ＰＴＦＥの支持体となる
薄鋼板に板ばね性を付与するのが好ましい。The resin plate 6 shown in FIGS.
The upper surface is fixed to a sliding upper surface 4c on the inner upper surface, and the lower surface thereof is in elastic contact with the sliding upper surface 1a of the guide rail 1. Therefore, the sliding upper surface 4c of the slider 4 is not in contact with the sliding upper surface 1a of the guide rail 1. In addition, guide rail 1
The solid lubricant-containing resin films 11a and 11b are omitted. The resin plate 6 having the lubricating performance is preferably formed of a PTFE sheet. As a preload means for giving elasticity to the PTFE sheet, PTFE serving as a sliding surface is used.
It is preferable that E is coated on a thin steel plate to impart a leaf spring property to the thin steel plate serving as a support of PTFE.
【００１６】この樹脂板６を備えるスライダ４によれ
ば、樹脂板６のＰＴＦＥ等の摺動面が案内レール１の被
摺動上面１ａを摺動し、樹脂板６の弾力性によつて上昇
傾向にあるスライダ４の左右の摺動面４ｂ，４ｂが案内
レール１の左右の被摺動面１ｂ，１ｂを摺動するように
なる。なお、樹脂板６をスライダ４の左右の摺動面４
ｂ，４ｂの一方に設けても、左右の摺動面４ｂ，４ｂの
他方が案内レール１の被摺動面１ｂ，１ｂを摺動し、摺
動上面４ｃが案内レール１の被摺動上面１ａを摺動する
ので、ほぼ同様の作用を得ることができる。According to the slider 4 having the resin plate 6, the sliding surface of the resin plate 6 such as PTFE slides on the slidable upper surface 1 a of the guide rail 1 and rises due to the elasticity of the resin plate 6. The left and right sliding surfaces 4b, 4b of the slider 4 tend to slide on the left and right sliding surfaces 1b, 1b of the guide rail 1. Note that the resin plate 6 is connected to the left and right sliding surfaces 4 of the slider 4.
b, 4b, the other of the left and right sliding surfaces 4b, 4b slides on the sliding surfaces 1b, 1b of the guide rail 1, and the sliding upper surface 4c is the sliding upper surface of the guide rail 1. Since the sliding member 1a slides, substantially the same operation can be obtained.
【００１７】図６は、樹脂板６に代えて潤滑性能を有す
る固体潤滑剤含有樹脂を被覆させた板状スプリング１６
を設けた構造例を示す。板状スプリング１６の摺動面に
被覆する固体潤滑剤含有樹脂の組成及び被覆手段は、前
述の案内レール１の被膜１１ａ，１１ｂに用いた固体潤
滑剤含有樹脂と同様でよい。固体潤滑剤含有樹脂を被覆
した板状スプリング１６は、上記樹脂板６と同様に取り
付ける。つまり、板状スプリング１６をスライダ４の内
側上面に固定させ、その下面を案内レール１の被摺動上
面１ａに弾性的に接触させる。FIG. 6 shows a plate-like spring 16 coated with a solid lubricant-containing resin having lubricating performance instead of the resin plate 6.
2 shows an example of a structure provided with. The composition and coating means of the solid lubricant-containing resin for coating the sliding surface of the plate spring 16 may be the same as the solid lubricant-containing resin used for the coatings 11a and 11b of the guide rail 1 described above. The plate spring 16 coated with the solid lubricant-containing resin is attached in the same manner as the resin plate 6. That is, the plate-shaped spring 16 is fixed to the inner upper surface of the slider 4, and the lower surface thereof is brought into elastic contact with the slidable upper surface 1 a of the guide rail 1.
【００１８】この板状スプリング１６を備えるスライダ
４によれば、板状スプリング１６の固体潤滑剤含有樹脂
からなる摺動面が案内レール１の被摺動上面１ａを摺動
し、板状スプリング１６の弾力性によつて上昇傾向にあ
るスライダ４の左右の摺動面４ｂ，４ｂが案内レール１
の左右の被摺動面１ｂ，１ｂを摺動するようになる。な
お、板状スプリング１６をスライダ４の左右の摺動面４
ｂ，４ｂの一方に設けても、左右の摺動面４ｂ，４ｂの
他方が案内レール１の被摺動面１ｂ，１ｂを摺動し、摺
動上面４ｃが案内レール１の被摺動上面１ａを摺動す
る。従つて、上記樹脂板６とほぼ同様の作用を得ること
ができる。According to the slider 4 having the plate spring 16, the sliding surface of the plate spring 16 made of a resin containing a solid lubricant slides on the sliding upper surface 1 a of the guide rail 1. The right and left sliding surfaces 4b, 4b of the slider 4 which tend to rise due to the elasticity of the
Slide on the left and right sliding surfaces 1b, 1b. Note that the plate-like spring 16 is connected to the left and right sliding surfaces 4 of the slider 4.
b, 4b, the other of the left and right sliding surfaces 4b, 4b slides on the sliding surfaces 1b, 1b of the guide rail 1, and the sliding upper surface 4c is the sliding upper surface of the guide rail 1. Slide 1a. Therefore, substantially the same operation as that of the resin plate 6 can be obtained.
【００１９】なお、樹脂板６又は板状スプリング１６の
軸線方向の端部の固定手段としては、樹脂板６及び板状
スプリング１６の摺動面より凹んだビス止めでよいが、
スライダ４の軸線方向の前後箇所に樹脂板６又は板状ス
プリング１６の板厚より薄い段差を設けて弾性的に係止
させることも可能である。The means for fixing the axial end of the resin plate 6 or the plate spring 16 may be a screw stop recessed from the sliding surface of the resin plate 6 and the plate spring 16.
It is also possible to provide a step that is thinner than the thickness of the resin plate 6 or the plate-shaped spring 16 at the front and rear positions in the axial direction of the slider 4 to elastically lock the slider.
【００２０】図４〜図６に示す第２実施の形態に係る直
動案内滑り軸受装置の最大の利点は、樹脂板６又は板状
スプリング１６が、常に予圧を与えられて案内レール１
の被摺動上面１ａに弾性的に接触することにより、樹脂
板６又は板状スプリング１６が組み込まれていない摺動
面、つまりスライダ４の左右の摺動面４ｂ，４ｂを、案
内レール１の被摺動面１ｂ，１ｂに弾性的に密着させる
ところにある。これにより、長期間使用する場合、摺動
条件が比較的過酷な場合、案内レール１及びスライダ４
の摺動摩擦面の摩耗が進行した場合等においても、予圧
により自己調整機能が作用し、案内レール１とスライダ
４との間に余分なガタが生じることを防止でき、長期
間、安定した往復移動機能が維持できる。The greatest advantage of the linear guide sliding bearing device according to the second embodiment shown in FIGS. 4 to 6 is that the resin plate 6 or the plate spring 16 is always given a preload and the guide rail 1
The sliding surface on which the resin plate 6 or the plate spring 16 is not built, that is, the left and right sliding surfaces 4b, 4b of the slider 4 It is in a position to be elastically adhered to the sliding surfaces 1b, 1b. Thus, when used for a long time, when the sliding conditions are relatively severe, the guide rail 1 and the slider 4
Even when wear of the sliding friction surface progresses, the self-adjustment function works by the preload, and it is possible to prevent the occurrence of extra play between the guide rail 1 and the slider 4 and to achieve stable reciprocating movement for a long period of time. Function can be maintained.
【００２１】また、本実施の形態の場合、案内レール１
の固体潤滑剤含有樹脂被覆１１ａ，１１ｂを省略するこ
とができ、その場合は予圧手段である樹脂板６又は板状
スプリング１６の部品が増える分がコスト増になつて
も、装置全体としてのコストがそれ程高くならない利点
がある。In the case of this embodiment, the guide rail 1
The solid lubricant-containing resin coatings 11a and 11b can be omitted. In this case, even if the cost increases because the number of components of the resin plate 6 or the plate spring 16 as the preload means increases, the cost of the entire apparatus increases. Has the advantage of not being too high.
【００２２】ところで、図１〜図５に示すスライダ４
は、左右の摺動面４ｂ及び内側上面の摺動上面４ｃが一
体成形されているが、図６に示すように、右側の摺動面
４ｂ及び内側上面の摺動上面４ｃが形成されたスライダ
部材４Ａと、左側の摺動面４ｂが形成されたスライダ部
材４Ｂとを、それぞれ精度良く仕上げ加工した後にねじ
８止めなどの締結手段で一体化させ、スライダ４を構成
させることもできる。By the way, the slider 4 shown in FIGS.
The left and right sliding surfaces 4b and the inner upper sliding surface 4c are integrally formed. As shown in FIG. 6, the slider has the right sliding surface 4b and the inner upper sliding surface 4c. The slider 4 can also be configured by finishing the member 4A and the slider member 4B on which the left sliding surface 4b is formed with high precision and then integrating them with a fastening means such as a screw 8 or the like.
【００２３】[0023]
【発明の効果】以上の説明によつて理解されるように、
本発明に係る直動案内滑り軸受装置によれば、次の効果
を奏することができる。請求項１の発明によれば、スラ
イダは、無潤滑状態で良好な摺動性能を有する錫含有ア
ルミニウム合金摺動材で製作され、摺動面をテーパ状に
有する構造であるため、構造が簡素である。また、案内
レールは、被摺動面をテーパ状に有すると共に、被摺動
面に、無潤滑状態で良好な摺動性能を有する固体潤滑剤
含有樹脂被膜を有する構造であるため、構造が簡素であ
る。その結果、部品点数が少なく、加工・組付けが容易
なため、小形、軽量、安価な無潤滑で直動案内の機構を
維持できる。加えて、案内レールのテーパ状の固体潤滑
剤含有樹脂被膜上をスライダのテーパ状の摺動面が移動
するため、変形し難い固体接触状態で精密な移動が可能
になる。As will be understood from the above description,
According to the linear guide sliding bearing device of the present invention, the following effects can be obtained. According to the invention of claim 1, the slider is made of a tin-containing aluminum alloy sliding material having good sliding performance in a non-lubricated state, and has a structure in which the sliding surface is tapered, so that the structure is simple. It is. In addition, the guide rail has a structure in which the sliding surface has a tapered shape, and the sliding surface has a solid lubricant-containing resin film having good sliding performance in a non-lubricated state. It is. As a result, since the number of parts is small and machining / assembly is easy, a small-sized, light-weight, inexpensive, lubrication-free linear motion guide mechanism can be maintained. In addition, since the tapered sliding surface of the slider moves on the tapered solid lubricant-containing resin film of the guide rail, precise movement is possible in a solid contact state that is hardly deformed.
【００２４】請求項２の発明によれば、所定成分の固体
潤滑剤含有樹脂被膜を有する案内レールと所定成分の錫
含有アルミニウム合金製のスライダとを有し、スライダ
の摺動面が案内レールの固体潤滑剤含有樹脂被膜上を摺
動するため、スライダの円滑な移動が可能になると共
に、変形し難い固体接触状態で精密な移動が可能にな
る。According to the second aspect of the present invention, there is provided a guide rail having a resin lubricant-containing resin film of a predetermined component and a slider made of a tin-containing aluminum alloy of a predetermined component, and a sliding surface of the slider is formed of the guide rail. Since the slider slides on the solid lubricant-containing resin film, the slider can be moved smoothly, and the slider can be precisely moved in a solid contact state that is hardly deformed.
【００２５】請求項３の発明によれば、スライダに組み
込んだ樹脂板及び固体潤滑剤含有樹脂で被覆された板状
スプリングの少なくとも一方が、案内レールの被摺動面
及び被摺動上面のいずれかに弾性的に接触している。そ
の結果、小形、軽量、安価、かつ、無潤滑で直動案内す
る機構の品質を長時間、安定して維持できる。According to the third aspect of the present invention, at least one of the resin plate incorporated in the slider and the plate-like spring coated with the solid lubricant-containing resin is provided on any one of the sliding surface and the sliding upper surface of the guide rail. Crab elastically contacts. As a result, the quality of the small, lightweight, inexpensive, lubrication-free linear motion guide mechanism can be stably maintained for a long time.
【図１】 本発明の第１実施の形態に係る直動案内滑り
軸受装置を示す斜視図。FIG. 1 is a perspective view showing a linear guide sliding bearing device according to a first embodiment of the present invention.
【図２】 同じく直動案内滑り軸受装置を示す図。FIG. 2 is a diagram showing a linear motion guide sliding bearing device.
【図３】 同じくスライダを示す図。FIG. 3 is a diagram showing a slider.
【図４】 本発明の第２実施の形態に係る直動案内滑り
軸受装置を示す斜視図。FIG. 4 is a perspective view showing a linear motion guide sliding bearing device according to a second embodiment of the present invention.
【図５】 図４のＶ−Ｖ線断面図。FIG. 5 is a sectional view taken along line VV of FIG. 4;
【図６】 直動案内滑り軸受装置の他の構造例を示す図
５と同様の断面図。FIG. 6 is a sectional view similar to FIG. 5, showing another example of the structure of the linear motion guide sliding bearing device.
１：案内レール、１ａ：被摺動上面、１ｂ：被摺動面、
４：スライダ、４ａ：台形凹部、４ｂ：摺動面、４ｃ：
摺動上面（摺動面）、６：樹脂板、１１ａ，１１ｂ：固
体潤滑剤含有樹脂被膜、１６：板状スプリング。1: Guide rail, 1a: Sliding upper surface, 1b: Sliding surface,
4: slider, 4a: trapezoidal recess, 4b: sliding surface, 4c:
Sliding upper surface (sliding surface), 6: resin plate, 11a, 11b: solid lubricant-containing resin coating, 16: plate spring.
Claims (4)
に有し、無潤滑状態で良好な摺動性能を有する錫含有ア
ルミニウム合金摺動材で製作されたスライダ（４）と、
案内レール（１）とを備え、前記案内レール（１）が、
該スライダ（４）の摺動面（４ｂ，４ｂ）に対応する被
摺動面（１ｂ，１ｂ）を両側面にテーパ状に有すると共
に、該被摺動面（１ｂ，１ｂ）に、無潤滑状態で良好な
摺動性能を有する固体潤滑剤含有樹脂被膜（１１ｂ，１
１ｂ）を有し、該スライダ（４）の摺動面（４ｂ，４
ｂ）が案内レール（１）の固体潤滑剤含有樹脂被膜（１
１ｂ，１１ｂ）上を移動することを特徴とする直動案内
滑り軸受装置。1. A slider (4) made of a tin-containing aluminum alloy sliding material having a tapered sliding surface (4b, 4b) on its inner surface and having good sliding performance in a non-lubricated state;
A guide rail (1), wherein the guide rail (1) is
Sliding surfaces (1b, 1b) corresponding to the sliding surfaces (4b, 4b) of the slider (4) are tapered on both side surfaces, and the sliding surfaces (1b, 1b) are lubricated without lubrication. Solid lubricant-containing resin coating (11b, 1
1b), and the sliding surface (4b, 4b) of the slider (4).
b) is the solid lubricant-containing resin coating (1) of the guide rail (1).
1b, 11b) A linear guide sliding bearing device characterized by moving on the sliding surface.
ｂ，１１ｂ）を有する案内レール（１）と錫含有アルミ
ニウム合金製のスライダ（４）とを有し、該スライダ
（４）の摺動面（４ｂ，４ｃ）が該案内レール（１）の
固体潤滑剤含有樹脂被膜（１１ａ，１１ｂ，１１ｂ）を
摺動する直動案内滑り軸受装置であつて、該錫含有アル
ミニウム合金が、重量％で、錫６〜４０％、鉛０〜８
％、珪素０〜１０％、銅０〜３％、残部がアルミニウム
からなり、該固体潤滑剤含有樹脂被膜（１１ａ，１１
ｂ，１１ｂ）が、体積％で、ＰＴＦＥ、ＭｏＳ２、黒鉛
から選ばれた１種以上を５０％以下含有し、残部が熱硬
化性樹脂によつて製作されていることを特徴とする直動
案内滑り軸受装置。2. A solid lubricant-containing resin film (11a, 11a).
b, 11b) and a slider (4) made of a tin-containing aluminum alloy, and the sliding surface (4b, 4c) of the slider (4) is a solid of the guide rail (1). A linear guide sliding bearing device for sliding a lubricant-containing resin film (11a, 11b, 11b), wherein the tin-containing aluminum alloy is 6 to 40% tin and 0 to 8 lead by weight%.
%, Silicon 0 to 10%, copper 0 to 3%, and the balance being aluminum, and the solid lubricant-containing resin film (11a, 11
(b, 11b) contains 50% or less in volume% of at least one selected from PTFE, MoS2, and graphite, and the remainder is made of a thermosetting resin. Sliding bearing device.
に有し、かつ、内側上面に摺動上面（４ｃ）を有し、無
潤滑状態で良好な摺動性能を有する錫含有アルミニウム
合金摺動材で製作されたスライダ（４）と、案内レール
（１）とを備え、前記案内レール（１）が、該スライダ
（４）の摺動面（４ｂ，４ｂ）に対応する被摺動面（１
ｂ，１ｂ）を両側面にテーパ状に有し、かつ、該スライ
ダ（４）の摺動上面（４ｃ）に対応する被摺動上面（１
ａ）を上面に有し、該スライダ（４）の摺動面（４ｂ，
４ｂ）が案内レール（１）の被摺動面（１ｂ，１ｂ）に
沿い、かつ、該スライダ（４）の摺動上面（４ｃ）が案
内レール（１）の被摺動上面（１ａ）に沿つて移動する
直動案内滑り軸受装置であつて、スライダ（４）の摺動
面（４ｂ）及び摺動上面（４ｃ）の少なくとも一部に、
弾力性及び潤滑性能を有した樹脂板（６）又は潤滑性能
を有する固体潤滑剤含有樹脂で被覆された板状スプリン
グ（１６）の少なくとも一方が、前記被摺動面（１ｂ）
及び被摺動上面（１ａ）に対向させて組み込まれ、前記
樹脂板（６）又は板状スプリング（１６）が、常に予圧
を与えられて前記案内レール（１）の被摺動面（１ｂ，
１ｂ）又は被摺動上面（１ａ）に弾性的に接触している
ことを特徴とする直動案内滑り軸受装置。3. A tin-containing material having a tapered sliding surface (4b, 4b) on the inner surface and a sliding upper surface (4c) on the inner upper surface, and having good sliding performance in a non-lubricated state. A slider (4) made of an aluminum alloy sliding material and a guide rail (1) are provided, and the guide rail (1) is provided on a surface corresponding to a sliding surface (4b, 4b) of the slider (4). Sliding surface (1
b, 1b) are tapered on both side surfaces, and the sliding upper surface (1) corresponding to the sliding upper surface (4c) of the slider (4).
a) on the upper surface, and the sliding surface (4b,
4b) is along the sliding surface (1b, 1b) of the guide rail (1), and the sliding upper surface (4c) of the slider (4) is on the sliding upper surface (1a) of the guide rail (1). A linear guide sliding bearing device that moves along at least a part of a sliding surface (4b) and a sliding upper surface (4c) of a slider (4).
At least one of a resin plate (6) having elasticity and lubrication performance or a plate-like spring (16) coated with a solid lubricant-containing resin having lubrication performance is provided on the sliding surface (1b).
And the resin plate (6) or the plate-like spring (16) is always pre-loaded to be slid on the sliding surface (1b, 1b) of the guide rail (1).
1b) or a linear guide sliding bearing device characterized by being elastically in contact with the sliding upper surface (1a).
イダ（４）が、重量％で、錫６〜４０％、鉛０〜８％、
珪素０〜１０％、銅０〜３％、残部がアルミニウムから
なる材料によつて製作され、潤滑性能を有した樹脂板
（６）が、ＰＴＦＥを有し、板状スプリング（１６）に
被覆されている固体潤滑剤含有樹脂が、体積％で、ＰＴ
ＦＥ、ＭｏＳ２、黒鉛から選ばれた１種以上を５０％以
下含有し、残部が熱硬化性樹脂からなることを特徴とす
る請求項３の直動案内滑り軸受装置。4. A slider (4) made of a tin-containing aluminum alloy sliding material comprising, by weight%, 6 to 40% tin, 0 to 8% lead,
A resin plate (6) made of a material consisting of silicon 0 to 10%, copper 0 to 3% and the balance being aluminum and having lubricating performance is coated with a plate-like spring (16) having PTFE. Solid lubricant-containing resin is PT
4. The linear guide sliding bearing device according to claim 3, wherein 50% or less of at least one selected from FE, MoS2, and graphite is contained, and the balance is made of a thermosetting resin.