JP2000357477A - Glass molding product for display, and glass vessel - Google Patents
Glass molding product for display, and glass vesselInfo
- Publication number
- JP2000357477A JP2000357477A JP11168196A JP16819699A JP2000357477A JP 2000357477 A JP2000357477 A JP 2000357477A JP 11168196 A JP11168196 A JP 11168196A JP 16819699 A JP16819699 A JP 16819699A JP 2000357477 A JP2000357477 A JP 2000357477A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- display
- flat portion
- thickness
- glass molded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、ディスプレイ用ガ
ラス成形品及びガラス容器に関し、特に、フラット型電
子線励起ディスプレイ用ガラス成形品及びガラス容器に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a glass molded article and a glass container for a display, and more particularly to a glass molded article and a glass container for a flat type electron beam excited display.
【0002】[0002]
【従来の技術】従来、フラット型電子線励起ディスプレ
イとしては、複数の電子放出素子を配した基板(以下、
「リアプレート」という)と、蛍光体を配した基板(以
下、「フロントプレート」という)とを対向配置し、両
基板の間を減圧状態(いわゆる真空状態)として電子放
出素子から放出される電子ビームを蛍光体に照射して画
像を形成する平板状のディスプレイがあり、X線遮蔽性
が良く、さらに、実用に耐え得る機械的強度を有すると
共に軽量であることが望まれている。このフラット型電
子線励起ディスプレイは、構造上次の2つのタイプがあ
る。2. Description of the Related Art Conventionally, as a flat type electron beam excited display, a substrate (hereinafter, referred to as a substrate) on which a plurality of electron-emitting devices are arranged.
A “rear plate”) and a substrate on which a phosphor is disposed (hereinafter, referred to as a “front plate”) are disposed opposite to each other, and electrons emitted from the electron-emitting device are set in a reduced pressure state (a so-called vacuum state) between the two substrates. There is a flat panel display that forms an image by irradiating a phosphor with a beam, and it is desired that the display has good X-ray shielding properties, has a mechanical strength enough for practical use, and is lightweight. This flat type electron beam excitation display has the following two types in terms of structure.
【0003】第1のタイプは、図5に示すように、ガラ
ス製のフロントプレート31とガラス製のリアプレート
32とが複数のスペーサ33を介して対向配置され、且
つフリットガラス34により支持枠(リブ)35を介し
て封着されて減圧ガラス容器30を構成する(例えば特
開平8−190854号公報、特開平8−55589号
公報)。フロントプレート31の内面には蛍光体36が
被覆され、リアプレート32の内面には複数の電子放出
素子37が形成されている。In the first type, as shown in FIG. 5, a glass front plate 31 and a glass rear plate 32 are arranged to face each other with a plurality of spacers 33 interposed therebetween. The pressure-reduced glass container 30 is sealed via a rib 35 (for example, JP-A-8-190854 and JP-A-8-55589). A phosphor 36 is coated on the inner surface of the front plate 31, and a plurality of electron-emitting devices 37 are formed on the inner surface of the rear plate 32.
【0004】第2のタイプは、図6に示すように、矩形
の平坦部44と、平坦部44から凹形状を呈するように
折り曲げられて連なる側壁部45と、側壁部45から外
側に折り曲げられて連なるフランジ部46とを有するガ
ラス製のフロントプレート41と、ガラス製のリアプレ
ート42とがフリットガラス43により封着されて減圧
ガラス容器40を構成する(例えば特開平3−2288
40号公報、特開平5−163036号公報、及び特公
平6−43253号公報)。フロントプレート41の平
坦部44の内面には蛍光体47が被覆され、リアプレー
ト42の内面には複数の電子放出素子47が形成されて
いる。The second type is, as shown in FIG. 6, a rectangular flat portion 44, a side wall portion 45 which is bent from the flat portion 44 to form a concave shape, and a side wall portion 45 which is bent outward from the side wall portion 45. A glass front plate 41 having a continuous flange portion 46 and a glass rear plate 42 are sealed by a frit glass 43 to form a reduced-pressure glass container 40 (for example, Japanese Patent Laid-Open No. Hei 3-2288).
40, JP-A-5-163036, and JP-B-6-43253. The inner surface of the flat portion 44 of the front plate 41 is coated with a phosphor 47, and the inner surface of the rear plate 42 is formed with a plurality of electron-emitting devices 47.
【0005】[0005]
【発明が解決しようとする課題】しかしながら、上記第
1のタイプのディスプレイは、フロントプレート31、
リアプレート32、スペーサ33及びリブ35をフリッ
トガラス34等で接合する工程を必要とし、製造工程が
複雑である。また、第2のタイプのディスプレイは、減
圧ガラス容器40の耐圧強度を高めるためにフロントプ
レート41の平坦部44及びリアプレート42を厚くす
る必要があるのでディスプレイの重量が増すという問題
がある。However, the first type of display has a front plate 31,
A step of joining the rear plate 32, the spacer 33, and the rib 35 with the frit glass 34 or the like is required, and the manufacturing process is complicated. In the second type of display, the flat portion 44 of the front plate 41 and the rear plate 42 need to be thickened in order to increase the pressure resistance of the decompressed glass container 40, so that the weight of the display increases.
【0006】本発明の目的は、簡単な製造工程で製造す
ることができると共に軽量なディスプレイ用ガラス成形
品及びガラス容器を提供することにある。An object of the present invention is to provide a lightweight glass molded article for display and a glass container which can be manufactured by a simple manufacturing process and are lightweight.
【0007】[0007]
【課題を解決するための手段】上記目的を達成するため
に、請求項1記載のディスプレイ用ガラス成形品は、矩
形の平坦部と、該平坦部から凹形状を呈するように折り
曲げられて連なる側壁部と、該側壁部から外側に折り曲
げられて連なるフランジ部とを有するディスプレイ用ガ
ラス成形品において、前記ガラス成形品の平坦部の厚さ
が2〜4mmであることを特徴とする。According to a first aspect of the present invention, there is provided a molded glass article for a display, comprising: a rectangular flat portion; and a side wall which is bent from the flat portion to form a concave shape. In a glass molded product for a display having a portion and a flange portion which is bent outward from the side wall portion, the flat portion of the glass molded product has a thickness of 2 to 4 mm.
【0008】請求項1記載のディスプレイ用ガラス成形
品によれば、少ない数の構成部材でディスプレイを構成
することができるのでディスプレイの製造工程を簡単に
することができると共に、平坦部の厚さが2〜4mmで
あるのでガラス成形品を軽量化することができる。According to the glass molded article for a display according to the first aspect, the display can be constituted by a small number of components, so that the manufacturing process of the display can be simplified and the thickness of the flat portion is reduced. Since it is 2 to 4 mm, the glass molded product can be reduced in weight.
【0009】請求項2記載のディスプレイ用ガラス成形
品は、請求項1記載のディスプレイ用ガラス成形品にお
いて、前記ガラス成形品を構成するガラスのX線吸収係
数が40〜110cm-1であることを特徴とする。The glass molded article for a display according to claim 2 is the glass molded article for a display according to claim 1, wherein the glass constituting the glass molded article has an X-ray absorption coefficient of 40 to 110 cm -1. Features.
【0010】請求項2記載のディスプレイ用ガラス成形
品によれば、ガラスのX線吸収係数が40〜110cm
-1であるので、当該ガラス成形品を電子線励起型ディス
プレイに適用したときにディスプレイの外部へのX線の
漏洩量を抑制することができる。According to the glass molded article for a display according to the second aspect, the glass has an X-ray absorption coefficient of 40 to 110 cm.
Since it is -1 , the amount of X-rays leaking out of the display can be suppressed when the glass molded article is applied to an electron beam excited display.
【0011】請求項3記載のディスプレイ用ガラス成形
品は、請求項2記載のディスプレイ用ガラス成形品にお
いて、前記平坦部の厚さが2.5〜4mmであることを
特徴とする。According to a third aspect of the present invention, there is provided a molded glass article for a display according to the second aspect, wherein the flat portion has a thickness of 2.5 to 4 mm.
【0012】請求項3記載のディスプレイ用ガラス成形
品によれば、平坦部の厚さが2.5〜4mmのように比
較的厚いときにはガラスのX線吸収係数を40〜110
cm -1のように小さく設定して該X線吸収係数を増加さ
せる組成成分の量を低減させることによりガラス成形品
の重量増加を抑制することができ、同時に当該ガラス成
形品を電子線励起型ディスプレイに適用したときにおけ
るディスプレイの外部へのX線の漏洩量を抑制すること
ができる。A glass molding for a display according to claim 3.
According to the product, the flat part has a thickness of 2.5 to 4 mm.
When the thickness is relatively thick, the X-ray absorption coefficient of the glass is 40 to 110.
cm -1To increase the X-ray absorption coefficient.
Glass molded products by reducing the amount of constituent components
Increase in the weight of the glass
When the shape is applied to an electron beam excited display
The amount of X-ray leakage outside the display
Can be.
【0013】請求項4記載のディスプレイ用ガラス成形
品は、請求項2記載のディスプレイ用ガラス成形品にお
いて、前記ガラス成形品を構成するガラスのX線吸収係
数が70〜150cm-1であることを特徴とする。According to a fourth aspect of the present invention, there is provided a glass molded article for a display according to the second aspect, wherein the glass constituting the glass molded article has an X-ray absorption coefficient of 70 to 150 cm -1. Features.
【0014】請求項4記載のディスプレイ用ガラス成形
品によれば、当該ガラス成形品を電子線励起型ディスプ
レイに適用したときにディスプレイの外部へのX線の漏
洩量を確実に抑制することができる。According to the glass molded article for a display according to the fourth aspect, when the glass molded article is applied to an electron beam excitation type display, the amount of X-ray leakage to the outside of the display can be reliably suppressed. .
【0015】請求項5記載のディスプレイ用ガラス成形
品は、請求項4記載のディスプレイ用ガラス成形品にお
いて、前記平坦部の厚さが2〜2.5mmであることを
特徴とする。According to a fifth aspect of the present invention, there is provided a molded glass article for a display according to the fourth aspect, wherein the flat portion has a thickness of 2 to 2.5 mm.
【0016】請求項5記載のディスプレイ用ガラス成形
品によれば、平坦部の厚さが2〜2.5mmのように比
較的薄いときにはガラスのX線吸収係数を70〜150
cm -1のように大きく設定して該X線吸収係数を増加さ
せる組成成分の量を増加させることにより、ガラス成形
品を電子線励起型ディスプレイに適用したときにおける
ディスプレイの外部へのX線の漏洩量の増加を抑制する
ことができる。A glass molding for a display according to claim 5.
According to the product, the flat part has a thickness of 2 to 2.5 mm.
When the glass is relatively thin, the X-ray absorption coefficient of the glass is 70-150.
cm -1To increase the X-ray absorption coefficient.
Glass molding by increasing the amount of
When the product is applied to an electron beam excited display
Suppresses the increase in the amount of X-ray leakage outside the display
be able to.
【0017】請求項6記載のディスプレイ用ガラス成形
品は、請求項1乃至5のいずれか1項に記載のディスプ
レイ用ガラス成形品において、前記側壁部の高さが1〜
5mmであることを特徴とする。According to a sixth aspect of the present invention, there is provided a glass molded article for a display according to any one of the first to fifth aspects, wherein the height of the side wall portion is 1 to 5.
It is characterized by being 5 mm.
【0018】請求項6記載のディスプレイ用ガラス成形
品によれば、側壁部の高さが1〜5mmであるので、ガ
ラス成形品をフラット型電子線励起ディスプレイに容易
に適用させることができる。According to the glass molded article for display according to the sixth aspect, since the height of the side wall is 1 to 5 mm, the glass molded article can be easily applied to a flat type electron beam excited display.
【0019】請求項7記載のディスプレイ用ガラス成形
品は、請求項1乃至6のいずれか1項に記載のディスプ
レイ用ガラス成形品において、前記フランジ部の長さが
1〜20mmであることを特徴とする。According to a seventh aspect of the present invention, there is provided a glass molded article for a display according to any one of the first to sixth aspects, wherein the length of the flange portion is 1 to 20 mm. And
【0020】請求項7記載のディスプレイ用ガラス成形
品によれば、フランジ部の長さが1〜20mmであるの
で、ディスプレイを形成すべくフランジ部をリアプレー
トにフリットガラス、レーザ等で接合する際に封着性を
向上させることができる。According to the seventh aspect of the present invention, since the length of the flange portion is 1 to 20 mm, the flange portion is joined to the rear plate by frit glass, laser or the like to form a display. In addition, the sealing property can be improved.
【0021】請求項8記載のディスプレイ用ガラス成形
品は、請求項1乃至7のいずれか1項に記載のディスプ
レイ用ガラス成形品において、前記ガラス成形品を構成
するガラスの比抵抗が、室温において1.0×1012Ω
・cm以上であることを特徴とする。The glass molded article for a display according to claim 8 is the glass molded article for a display according to any one of claims 1 to 7, wherein the glass constituting the glass molded article has a specific resistance at room temperature. 1.0 × 10 12 Ω
・ Cm or more.
【0022】請求項8記載のディスプレイ用ガラス成形
品によれば、ガラスの比抵抗が、室温において1.0×
1012Ω・cm以上であるので、ガラス成形品の電気絶
縁性を向上させることができる。According to the glass molded product for a display of the present invention, the specific resistance of the glass at room temperature is 1.0 ×.
Since it is 10 12 Ω · cm or more, the electrical insulation of the glass molded product can be improved.
【0023】請求項9記載のディスプレイ用ガラス成形
品は、請求項1乃至8のいずれか1項に記載のディスプ
レイ用ガラス成形品において、表面層のナトリウムイオ
ンとカリウムイオンに置換したことを特徴とする。According to a ninth aspect of the present invention, there is provided a glass molded article for a display according to any one of the first to eighth aspects, wherein sodium ions and potassium ions in the surface layer are substituted. I do.
【0024】請求項9記載のディスプレイ用ガラス成形
品によれば、ガラス成形品の表面層を圧縮歪層にしてガ
ラス成形品の機械的強度を向上させることができると共
に、該表面層を電子ビームの照射に対して着色しにくい
組成とすることができる。According to the glass molded product for a display according to the ninth aspect, the surface layer of the glass molded product can be made a compression strain layer to improve the mechanical strength of the glass molded product, and the surface layer can be formed by an electron beam. Can be made to be a composition that is difficult to be colored by the irradiation of.
【0025】請求項10記載のディスプレイ用ガラス成
形品は、請求項1乃至9のいずれか1項に記載のディス
プレイ用ガラス成形品において、フラット型電子線励起
ディスプレイに使用されることを特徴とする。According to a tenth aspect of the present invention, there is provided the glass molded article for a display according to any one of the first to ninth aspects, which is used for a flat type electron beam excited display. .
【0026】請求項10記載のディスプレイ用ガラス成
形品によれば、フラット型電子線励起ディスプレイに適
したガラス成形品を提供することができる。According to the glass molded product for a display according to the tenth aspect, a glass molded product suitable for a flat type electron beam excited display can be provided.
【0027】上記目的を達成するために、請求項11記
載のディスプレイ用ガラス容器は、請求項1乃至10の
いずれか1項に記載のガラス成形品を備えることを特徴
とする。In order to achieve the above object, a glass container for a display according to the present invention is provided with the glass molded product according to any one of the first to tenth aspects.
【0028】請求項11記載のディスプレイ用ガラス容
器によれば、請求項1乃至10のいずれか1項に記載し
たディスプレイ用ガラス成形品を備えるので、上述した
と同様の効果を奏するガラス容器を提供することができ
る。According to the glass container for a display according to the eleventh aspect, since the molded glass product for a display according to any one of the first to tenth aspects is provided, a glass container having the same effects as described above is provided. can do.
【0029】[0029]
【発明の実施の形態】本発明者は、上記目的を達成すべ
く鋭意検討を行った結果、矩形の平坦部と、平坦部から
凹形状を呈するように折り曲げられて連なる側壁部と、
側壁部から外側に折り曲げられて連なるフランジ部とを
有するディスプレイ用ガラス成形品において、ガラス成
形品の平坦部の厚さが2〜4mmであるときは、ガラス
成形品を軽量化することができること、平坦部の厚さが
2.5〜4mmのように比較的厚いときにはガラスのX
線吸収係数を40〜110cm-1のように小さく設定し
て該X線吸収係数を増加させる組成成分の量を低減させ
ることによりガラス成形品の重量増加を抑制することが
でき、同時に当該ガラス成形品を電子線励起型ディスプ
レイに適用したときにおけるディスプレイの外部へのX
線の漏洩量を抑制することができること、及び平坦部の
厚さが2〜2.5mmのように比較的薄いときにはガラ
スのX線吸収係数を70〜150cm-1のように大きく
設定して該X線吸収係数を増加させる組成成分の量を増
加させることにより、当該ガラス成形品を電子線励起型
ディスプレイに適用したときにおけるディスプレイの外
部へのX線の漏洩量の増加を抑制することができること
を見い出した。本発明は、上記知見に基づいてなされた
ものである。DETAILED DESCRIPTION OF THE INVENTION As a result of intensive studies to achieve the above object, the present inventor has found that a rectangular flat portion, and a side wall portion which is bent from the flat portion to form a concave shape,
In a glass molded product for a display having a flange portion that is bent outward from the side wall portion, when the thickness of the flat portion of the glass molded product is 2 to 4 mm, the glass molded product can be reduced in weight, When the thickness of the flat portion is relatively thick such as 2.5 to 4 mm, X
By setting the linear absorption coefficient as small as 40 to 110 cm -1 to reduce the amount of the composition component that increases the X-ray absorption coefficient, it is possible to suppress an increase in the weight of the glass molded product, and at the same time, the glass molding To the outside of the display when the product is applied to an electron beam excited display
When the flat portion has a relatively small thickness such as 2 to 2.5 mm, the X-ray absorption coefficient of the glass is set to a large value such as 70 to 150 cm -1 to suppress the amount of leakage of the line. By increasing the amount of the composition component that increases the X-ray absorption coefficient, it is possible to suppress an increase in the amount of leakage of X-rays to the outside of the display when the glass molded article is applied to an electron beam excited display. I found The present invention has been made based on the above findings.
【0030】以下、上記知見について具体的に説明す
る。Hereinafter, the above findings will be specifically described.
【0031】本発明に係るガラス成形品は、その主要組
成が、重量%で表して、SiO255〜74%、Al2O
31〜15%、B2O30〜11%、MgO1〜5%、C
aO2〜10%、BaO及びSrO合計量0〜29%、
Na2O3〜14%、K2O0〜8%であり、その他、清
澄剤としてAS2O3、SO3、SnO2等を含有する。The glass molded article according to the present invention has a main composition represented by wt% of 55 to 74% of SiO 2 and Al 2 O
3 1~15%, B 2 O 3 0~11%, MgO1~5%, C
aO2-10%, total amount of BaO and SrO 0-29%,
Na 2 O3~14%, a K 2 O0~8%, others contain AS 2 O 3, SO 3, SnO 2 or the like as a fining agent.
【0032】SiO2が55重量%より少ないとガラス
の化学的耐久性が劣化し、74重量%を越えるとガラス
の溶解成形性が困難になる。Al2O3が1重量%より少
ないとガラスの化学的耐久性が劣化し、15重量%を越
えるとガラスの溶解時の粘度が高くなり溶解しにくくな
る。B2O3が11重量%を越えるとガラス成型時の粘度
の制御が困難になる。MgOが1重量%より少ないとガ
ラス成型時の粘度の制御が困難になり、5重量%を越え
ると成型時のガラス粘度が大きくなり板状に成形するの
が困難になる。CaOが2重量%より少ないとガラス成
型時の粘度の制御が困難になり、10重量%を越えると
成型時のガラス粘度が大きくなり板状に成形するのが困
難になる。BaO及びSrOがそれらの合計量で29重
量%を越えるとガラス溶融時にガラスを失透させ易くな
る。Na2Oが3重量%より少ないとガラスの粘度が高
くなり、14重量%を越えるとガラスの化学的耐久性が
劣化する。K2Oが8重量%を越えるとガラスの化学的
耐久性が劣化する。When the content of SiO 2 is less than 55% by weight, the chemical durability of the glass deteriorates, and when the content exceeds 74% by weight, the melt formability of the glass becomes difficult. If the content of Al 2 O 3 is less than 1% by weight, the chemical durability of the glass deteriorates, and if it exceeds 15% by weight, the viscosity of the glass at the time of melting becomes high and the glass is hardly melted. If B 2 O 3 exceeds 11% by weight, it becomes difficult to control the viscosity during glass molding. If the content of MgO is less than 1% by weight, it is difficult to control the viscosity at the time of molding the glass. If the content exceeds 5% by weight, the viscosity of the glass at the time of molding becomes large and it becomes difficult to form a plate. If the content of CaO is less than 2% by weight, it is difficult to control the viscosity at the time of molding the glass. If the content exceeds 10% by weight, the viscosity of the glass at the time of molding becomes large and it becomes difficult to form a plate. When the total amount of BaO and SrO exceeds 29% by weight, the glass tends to be devitrified when the glass is melted. If the content of Na 2 O is less than 3% by weight, the viscosity of the glass increases, and if it exceeds 14% by weight, the chemical durability of the glass deteriorates. If K 2 O exceeds 8% by weight, the chemical durability of the glass deteriorates.
【0033】ところで、ガラスのX線遮蔽性能は、ガラ
ス中の電子密度に依存しており、より具体的には、ガラ
ス組成成分の中で、SrO、BaO又はPbOのような
重金属酸化物の含有量に関係し、これらの成分の合計量
が増加すると大きくなる。他方、ガラスの比重はとりわ
けガラス組成中のSrO、BaO又はPbOのような重
金属酸化物の含有量に大きく依存する。Incidentally, the X-ray shielding performance of glass depends on the electron density in the glass, and more specifically, the content of heavy metal oxides such as SrO, BaO or PbO among the glass composition components. In relation to the amount, it increases as the total amount of these components increases. On the other hand, the specific gravity of the glass depends largely on the content of heavy metal oxides such as SrO, BaO or PbO in the glass composition.
【0034】これらの関係を示す例を表1に示す。Table 1 shows an example showing these relationships.
【0035】[0035]
【表1】 [Table 1]
【0036】表1は、種々のガラス材料(試料A〜G)
について、BaO及びSrOの合計量と比重との関係、
BaO及びSrOの合計量とX線吸収係数との関係を示
す。表1において、ガラスのX線吸収係数(cm-1)と
しては電子線加速電圧が10keVのときの値を示す。
これは、フラット型電子線励起ディスプレイの電子線加
速電圧は通常数keV〜10keV程度であることを考
慮したものである。Table 1 shows various glass materials (samples A to G).
About the relationship between the total amount of BaO and SrO and the specific gravity,
The relationship between the total amount of BaO and SrO and the X-ray absorption coefficient is shown. In Table 1, the X-ray absorption coefficient (cm -1 ) of the glass is a value when the electron beam acceleration voltage is 10 keV.
This takes into account that the electron beam acceleration voltage of a flat type electron beam excitation display is usually about several keV to 10 keV.
【0037】図1は、SrO及びBaOの合計量とガラ
スの比重との関係を示すグラフであり、図2は、SrO
及びBaOの合計量とガラスのX線吸収係数との関係を
示すグラフである。FIG. 1 is a graph showing the relationship between the total amount of SrO and BaO and the specific gravity of glass, and FIG.
3 is a graph showing the relationship between the total amount of BaO and BaO and the X-ray absorption coefficient of glass.
【0038】図1及び図2から、ガラスのX線遮蔽性能
(X線吸収係数(cm-1))を大きくするにはBaO及
びSrOの合計量を増加させる必要があり(図2)、こ
のBaO及びSrOの合計量が増加すると自ずとガラス
の比重が増加する(図1)ことが分かる。From FIGS. 1 and 2, it is necessary to increase the total amount of BaO and SrO to increase the X-ray shielding performance (X-ray absorption coefficient (cm -1 )) of the glass (FIG. 2). It can be seen that the specific gravity of the glass naturally increases as the total amount of BaO and SrO increases (FIG. 1).
【0039】本発明のガラス成形品として、フラット型
電子線励起ディスプレイの(とりわけ、FED)電子加
速電圧が数kv〜10kv程度であることを考慮して、
ガラス成形品の軽量化と、X線遮蔽性能に関する安全性
及びガラス成形品の耐圧強度とから好ましい態様が存在
することを見い出した。As the glass molded article of the present invention, considering that the electron acceleration voltage (especially FED) of the flat type electron beam excited display is about several kv to 10 kv,
It has been found that there is a preferable embodiment from the viewpoint of reducing the weight of the glass molded product, the safety with respect to the X-ray shielding performance, and the pressure resistance of the glass molded product.
【0040】即ち、ガラス成形品の表示面積が比較的小
さい場合は、ガラス成形品の耐圧強度を確保するための
ガラス成形品の厚さは薄くてよいが、X線遮蔽性能を維
持するためにX線吸収係数が大きいガラスを用いるのが
好ましい。一方、ガラス成形品の表示面積が比較的大き
い場合は、ガラス成形品の耐圧強度を確保するためにガ
ラス成形品の厚さを厚くする必要があり、ガラスのX線
遮蔽性能はそれほど大きくなくてもよく、むしろ小さい
比重のガラスを用いるのが好ましい。That is, when the display area of the glass molded product is relatively small, the thickness of the glass molded product for securing the pressure resistance of the glass molded product may be small, but it is necessary to maintain the X-ray shielding performance. It is preferable to use glass having a large X-ray absorption coefficient. On the other hand, when the display area of the glass molded product is relatively large, it is necessary to increase the thickness of the glass molded product in order to secure the pressure resistance of the glass molded product, and the X-ray shielding performance of the glass is not so large. It is preferable to use glass having a lower specific gravity.
【0041】本発明のガラス成形品においては、X線吸
収係数が40cm-1以上のガラスを用いるのが画像表示
時に必要なX線遮蔽性能を確保する上で好ましい。In the glass molded article of the present invention, it is preferable to use glass having an X-ray absorption coefficient of 40 cm -1 or more from the viewpoint of securing X-ray shielding performance required for displaying an image.
【0042】ガラス成形品のX線遮蔽性能と耐圧強度に
ついて実用的な性能を具備するためには、ガラス成形品
の厚さが2.5〜4mmの場合、X線吸収係数が40〜
110cm-1のガラスでガラス成形品を構成するのが好
ましい。このガラス成形品は、比較的小さい大型の画像
表示に適している。ガラス成形品の厚さが2.5〜4m
mのように比較的厚いときにはガラスのX線吸収係数を
40〜110cm-1のように小さく設定して該X線吸収
係数を増加させる組成成分(SrO、BaO又はPbO
のような重金属酸化物)の量を低減させることによりガ
ラス成形品の重量増加を抑制することができ、同時に当
該ガラス成形品を電子線励起型ディスプレイに適用した
ときにおけるディスプレイの外部へのX線の漏洩量を抑
制することができる。ガラス成形品の厚さが2.5〜4
mmのときに、X線吸収係数が40cm-1より小さいと
ガラスのX線遮蔽性能が許容範囲を下回り、一方、X線
吸収係数が110cm-1を越えるとX線吸収係数を増加
させる組成成分(SrO、BaO又はPbOのような重
金属酸化物)の合計含有量が増加してガラス成形品の重
量が許容範囲を越える。In order for the glass molded article to have practical performance in terms of X-ray shielding performance and pressure resistance, when the thickness of the glass molded article is 2.5 to 4 mm, the X-ray absorption coefficient is 40 to 40 mm.
Preferably, the glass molded article is made of 110 cm -1 glass. This glass molded product is suitable for displaying relatively small and large images. 2.5-4m thick glass molded product
When the composition is relatively thick such as m, the X-ray absorption coefficient of the glass is set as small as 40 to 110 cm -1 to increase the X-ray absorption coefficient (SrO, BaO or PbO).
By reducing the amount of heavy metal oxides), it is possible to suppress an increase in the weight of the glass molded article, and at the same time, to apply X-rays to the outside of the display when the glass molded article is applied to an electron beam excitation type display. Can be suppressed. The thickness of the glass molded product is 2.5-4
When the X-ray absorption coefficient is smaller than 40 cm -1 , the X-ray shielding performance of the glass falls below an allowable range. On the other hand, when the X-ray absorption coefficient exceeds 110 cm -1 , a composition component that increases the X-ray absorption coefficient The total content of (heavy metal oxides such as SrO, BaO or PbO) increases and the weight of the glass molded product exceeds the allowable range.
【0043】一方、ガラス成形品の厚さが2〜2.5m
mの場合、X線吸収係数が70〜150cm-1のガラス
でガラス成形品10を構成するのが好ましい。このガラ
ス成形品は、比較的小さい小型の画像表示に適してい
る。ガラス成形品の厚さが2〜2.5mmのように比較
的薄いときにはガラスのX線吸収係数を70〜150c
m-1のように大きく設定して該X線吸収係数を増加させ
る組成成分(SrO、BaO又はPbOのような重金属
酸化物)の量を増加させることにより、当該ガラス成形
品を電子線励起型ディスプレイに適用したときにおける
ディスプレイの外部へのX線の漏洩量の増加を抑制する
ことができる。ガラス成形品の厚さが2〜2.5mmの
ときに、X線吸収係数が70cm-1より小さいとガラス
のX線遮蔽性能が許容範囲を下回り、一方、X線吸収係
数が150cm-1を越えると、X線吸収係数を増加させ
る組成成分(SrO、BaO又はPbOのような重金属
酸化物)の合計含有量が増加してガラス成形品の重量が
許容範囲を越える。On the other hand, the thickness of the glass molded product is 2 to 2.5 m
In the case of m, it is preferable that the glass molded article 10 is made of glass having an X-ray absorption coefficient of 70 to 150 cm -1 . This glass molded article is suitable for displaying relatively small and small images. When the thickness of the glass molded product is relatively thin such as 2 to 2.5 mm, the X-ray absorption coefficient of the glass is 70 to 150 c.
By increasing the amount of a composition component (a heavy metal oxide such as SrO, BaO, or PbO) that increases the X-ray absorption coefficient by setting a large value such as m −1, the glass molded product is converted to an electron beam excitation type. When applied to a display, an increase in the amount of leakage of X-rays to the outside of the display can be suppressed. When the thickness of the glass molded product is 2 to 2.5 mm, if the X-ray absorption coefficient is smaller than 70 cm -1 , the X-ray shielding performance of the glass falls below an allowable range, while the X-ray absorption coefficient becomes 150 cm -1 . If it exceeds, the total content of the components (heavy metal oxides such as SrO, BaO or PbO) which increases the X-ray absorption coefficient increases, and the weight of the glass molded product exceeds the allowable range.
【0044】上記知見において、SrO及びBaOの合
計量に基づいてガラスの比重及びX線吸収係数を評価し
たが、SrO又はBaOを他の重金属酸化物に代えても
よく、他の重金属酸化物を加えてもよい。In the above findings, the specific gravity and the X-ray absorption coefficient of the glass were evaluated based on the total amount of SrO and BaO. However, SrO or BaO may be replaced with another heavy metal oxide. May be added.
【0045】以下、本発明の実施の形態に係るディスプ
レイ用ガラス成形品の構成を図3を参照して説明する。
図3は、本発明の実施の形態に係るディスプレイ用ガラ
ス成形品(以下、「フロントプレート」と云う)の断面
図である。Hereinafter, the structure of a glass molded product for a display according to an embodiment of the present invention will be described with reference to FIG.
FIG. 3 is a cross-sectional view of a molded glass article for a display (hereinafter, referred to as a “front plate”) according to an embodiment of the present invention.
【0046】図3において、フロントプレート10は、
矩形の平坦部11と、平坦部11から凹形状を呈するよ
うに折り曲げられて連なる側壁部(以下、「リブ」と云
う)12と、及びリブ12から外側に折り曲げられて連
なるフランジ部13とを有する。平坦部11は厚さが2
〜4mmであり、好ましくは、2〜3mmである。平坦
部11の厚さは、画像表示面の対角長を6インチ程度の
実用的な大きさとするためには、その画像表示面の耐圧
強度を確保する観点から2mm以上とするのが好まし
い。また、装置の軽量化を図る上で4mm以下とするの
が好ましい。In FIG. 3, the front plate 10 is
A rectangular flat portion 11, a side wall portion (hereinafter, referred to as a “rib”) 12 that is bent and formed to have a concave shape from the flat portion 11, and a flange portion 13 that is bent outward from the rib 12 and continuous. Have. The flat part 11 has a thickness of 2
44 mm, preferably 2-3 mm. The thickness of the flat portion 11 is preferably 2 mm or more from the viewpoint of securing the pressure resistance of the image display surface in order to make the diagonal length of the image display surface a practical size of about 6 inches. Further, in order to reduce the weight of the apparatus, it is preferable that the thickness be 4 mm or less.
【0047】リブ12の高さは、ディスプレイ固有の必
要高さとするが、1〜5mmが好ましい。5mmを越え
ると、ディスプレイ構成時に同時に使用される後述のス
ペーサの強度を低下させる等の問題があり、フロントプ
レートをディスプレイ用として用いるのが困難になる。The height of the rib 12 is set to a required height unique to the display, but is preferably 1 to 5 mm. If it exceeds 5 mm, there is a problem that the strength of spacers, which will be described later, which are used at the same time when the display is constructed, is reduced, and it becomes difficult to use the front plate for the display.
【0048】フランジ部13の長さは、フリットガラ
ス、レーザ等によりフロントプレートをリアプレートに
接合する際に、封着性を維持できるような長さである必
要があり、1〜20mmであるのが好ましい。フランジ
部13の長さが、1mm未満では封着性を確保すること
ができず、20mmを越えると画像表示面の周辺部まで
画像表示することができなくなる。The length of the flange portion 13 must be such that the sealing property can be maintained when the front plate is joined to the rear plate by frit glass, laser, or the like, and is 1 to 20 mm. Is preferred. If the length of the flange portion 13 is less than 1 mm, the sealing property cannot be ensured, and if it exceeds 20 mm, the image cannot be displayed up to the peripheral portion of the image display surface.
【0049】また、ガラスの比抵抗は、フロントプレー
トの電気絶縁性の確保の観点から室温において1.0×
1012Ω・cm以上であるのが好ましい。The specific resistance of the glass is 1.0 × at room temperature from the viewpoint of securing the electrical insulation of the front plate.
It is preferably at least 10 12 Ω · cm.
【0050】このようなフロントプレート10は公知の
加熱曲げ加工法によって作製する(例えば特公平6−4
9581号公報)。即ち、後述する組成の原料バッチを
約1450℃で溶解した後公知のロールアウト法で板ガ
ラスに成形し、その板ガラスを研磨加工により所定厚さ
に整えると共に所定寸法に切断した後、切断された板ガ
ラスを凸成形型上に載置し、その外周部を中央部分より
も高温に加熱して凸成形型上に自重で変形させ、その後
凹成形型で板ガラスをプレスすることにより所定深さの
フランジ付きガラス成形品を成形するものである。Such a front plate 10 is manufactured by a known heating bending method (for example, Japanese Patent Publication No. 6-4).
No. 9581). That is, after a raw material batch having a composition described below is melted at about 1450 ° C., it is formed into a sheet glass by a known roll-out method, and the sheet glass is polished to a predetermined thickness and cut to a predetermined size. Is placed on the convex mold, the outer periphery is heated to a higher temperature than the central part, deformed by its own weight on the convex mold, and then the sheet glass is pressed with the concave mold to form a flange with a predetermined depth. This is for forming a glass molded product.
【0051】次いで、上記フランジ付きガラス成形品を
約460℃の硝酸カリウム溶液中に3時間浸漬すること
により、表面から約4〜30μmの深さの層でナトリウ
ムイオンからカリウムイオンへのイオン交換を行う。こ
れにより、ガラス成形品の表面層を圧縮歪層にしてガラ
ス成形品の機械的強度を向上させることができると共
に、該表面層を電子ビームの照射に対して着色しにくい
組成とすることができる。Next, the glass molded article with a flange is immersed in a potassium nitrate solution at about 460 ° C. for 3 hours to perform ion exchange from sodium ions to potassium ions in a layer having a depth of about 4 to 30 μm from the surface. . This makes it possible to improve the mechanical strength of the glass molded article by using the surface layer of the glass molded article as a compression strain layer and to make the surface layer a composition that is not easily colored by electron beam irradiation. .
【0052】上記フロントプレート10は、電子線励起
ディスプレイ(FED)、プラズマディスプレイパネル
(PDP)、バックライト式液晶ディスプレイに使用す
ることができる。以下の説明では、フロントプレート1
0を電子線励起型ディスプレイに使用した場合について
述べる。The front plate 10 can be used for an electron beam excited display (FED), a plasma display panel (PDP), and a backlight type liquid crystal display. In the following description, the front plate 1
A case where 0 is used for an electron beam excited display will be described.
【0053】上記フロントプレート10を用いて作製さ
れたディスプレイを図4を参照して説明する。図4は、
本発明の実施の形態に係るディスプレイ用ガラス容器の
断面図である。A display manufactured using the front plate 10 will be described with reference to FIG. FIG.
It is sectional drawing of the glass container for displays which concerns on embodiment of this invention.
【0054】図4に示すように、フロントプレート10
は、リアプレート14と複数のスペーサ15を介して対
向配置され、且つフリットガラス16によってフランジ
部13がリアプレート15に封着されて耐圧ガラス容器
20を構成する。フリットガラス16によるフランジ部
13の封着は、フリットガラス16に代えてレーザ光に
よる封着であってもよい。As shown in FIG. 4, the front plate 10
Is arranged to face the rear plate 14 with a plurality of spacers 15 interposed therebetween, and the flange portion 13 is sealed to the rear plate 15 by the frit glass 16 to form the pressure-resistant glass container 20. The sealing of the flange portion 13 by the frit glass 16 may be performed by laser light instead of the frit glass 16.
【0055】スペーサ15はリブ12と同じ高さを有
し、平坦部11の間隔をその全面に亘って均等に保持す
る。また、スペーサ15の材質は、ガラス、セラミック
ス等が好ましい。このスペーサは、平坦部11の画像が
形成される面に接するが、画面の表示の均一性を確保す
るために、平坦部11において画像が表示されない部
分、具体的には、配線電極部分やRGB画素の継ぎ目の
ブラックマトリックス等の部分に配置する。スペーサ1
5の幅は、これらの幅より小さいことが必要であり、具
体的には0.3mm以下である。The spacers 15 have the same height as the ribs 12, and maintain the spacing of the flat portions 11 uniformly over the entire surface. Further, the material of the spacer 15 is preferably glass, ceramic, or the like. The spacer is in contact with the surface of the flat portion 11 on which an image is formed. However, in order to ensure uniform display of the screen, a portion where the image is not displayed in the flat portion 11, specifically, a wiring electrode portion or RGB. It is arranged in a portion such as a black matrix at the joint of pixels. Spacer 1
The width of 5 needs to be smaller than these widths, specifically 0.3 mm or less.
【0056】さらに、フロントプレート10の平坦部1
1の内面には蛍光体17が被覆され、リアプレート14
の内面には複数の電子放出素子18が形成されている。
このような減圧ガラス容器20の内部は減圧ガラス容器
20に設けられた図示しない通気管を介して内部が真空
に排気される。Further, the flat portion 1 of the front plate 10
1 is coated with a phosphor 17 and the rear plate 14
Are formed with a plurality of electron-emitting devices 18 on the inner surface thereof.
The inside of the reduced pressure glass container 20 is evacuated to a vacuum via a not-shown ventilation pipe provided in the reduced pressure glass container 20.
【0057】本実施の形態によれば、平坦部11の厚さ
が2〜4mmであるので、フロントプレート10を軽量
化することができ、平坦部11の厚さが2.5〜4mm
のように比較的厚いときにはガラスのX線吸収係数を4
0〜110cm-1のように小さく設定して該X線吸収係
数を増加させる組成成分の量を低減させることによりフ
ロントプレート10の重量増加を抑制することができ、
同時に当該フロントプレート11を電子線励起型ディス
プレイに適用したときにおけるディスプレイの外部への
X線の漏洩量を抑制することができ、且つ平坦部11の
厚さが2〜2.5mmのように比較的薄いときにはガラ
スのX線吸収係数を70〜150cm-1のように大きく
設定して該X線吸収係数を増加させる組成成分の量を増
加させることにより、当該フロントプレート10を電子
線励起型ディスプレイに適用したときにおけるディスプ
レイの外部へのX線の漏洩量の増加を抑制することがで
きる。According to the present embodiment, since the thickness of the flat portion 11 is 2 to 4 mm, the weight of the front plate 10 can be reduced, and the thickness of the flat portion 11 is 2.5 to 4 mm.
When the glass is relatively thick, as in
An increase in the weight of the front plate 10 can be suppressed by reducing the amount of the composition component that increases the X-ray absorption coefficient by setting it as small as 0 to 110 cm −1 ,
At the same time, when the front plate 11 is applied to an electron-beam-excited display, the amount of X-ray leakage to the outside of the display can be suppressed, and the thickness of the flat portion 11 can be reduced to 2 to 2.5 mm. When the front plate 10 is very thin, the X-ray absorption coefficient of the glass is set to a large value such as 70 to 150 cm -1 to increase the amount of a composition component that increases the X-ray absorption coefficient. In this case, it is possible to suppress an increase in the amount of leakage of X-rays to the outside of the display when the present invention is applied.
【0058】[0058]
【発明の効果】以上詳細に説明したように、請求項1記
載のディスプレイ用ガラス成形品によれば、少ない数の
構成部材でディスプレイを構成することができるのでデ
ィスプレイの製造工程を簡単にすることができると共
に、平坦部の厚さが2〜4mmであるのでガラス成形品
を軽量化することができる。As described above in detail, according to the glass molded article for a display according to the first aspect, the display can be constituted by a small number of components, so that the manufacturing process of the display is simplified. In addition, since the thickness of the flat portion is 2 to 4 mm, the weight of the glass molded product can be reduced.
【0059】請求項2記載のディスプレイ用ガラス成形
品によれば、ガラスのX線吸収係数が40〜110cm
-1であるので、当該ガラス成形品を電子線励起型ディス
プレイに適用したときにディスプレイの外部へのX線の
漏洩量を抑制することができる。According to the glass molded article for a display according to the second aspect, the glass has an X-ray absorption coefficient of 40 to 110 cm.
Since it is -1 , the amount of X-rays leaking out of the display can be suppressed when the glass molded article is applied to an electron beam excited display.
【0060】請求項3記載のディスプレイ用ガラス成形
品によれば、平坦部の厚さが2.5〜4mmのように比
較的厚いときにはガラスのX線吸収係数を40〜110
cm -1のように小さく設定して該X線吸収係数を増加さ
せる組成の量を低減させることによりフロントプレート
の重量増加を抑制することができ、同時に当該ガラス成
形品を電子線励起型ディスプレイに適用したときにおけ
るディスプレイの外部へのX線の漏洩量を抑制すること
ができる。Glass molding for display according to claim 3
According to the product, the flat part has a thickness of 2.5 to 4 mm.
When the thickness is relatively thick, the X-ray absorption coefficient of the glass is 40 to 110.
cm -1To increase the X-ray absorption coefficient.
Reduce the amount of composition
Increase in the weight of the glass
When the shape is applied to an electron beam excited display
The amount of X-ray leakage outside the display
Can be.
【0061】請求項4記載のディスプレイ用ガラス成形
品によれば、当該ガラス成形品を電子線励起型ディスプ
レイに適用したときにディスプレイの外部へのX線の漏
洩量を確実に抑制することができる。According to the glass molded article for a display according to the fourth aspect, when the glass molded article is applied to an electron beam excitation type display, the amount of X-ray leakage to the outside of the display can be reliably suppressed. .
【0062】請求項5記載のディスプレイ用ガラス成形
品によれば、平坦部の厚さが2〜2.5mmのように比
較的薄いときにはガラスのX線吸収係数を70〜150
cm -1のように大きく設定して該X線吸収係数を増加さ
せる組成の量を増加させることにより、当該プレートを
電子線励起型ディスプレイに適用したときにおけるディ
スプレイの外部へのX線の漏洩量の増加を抑制すること
ができる。Glass molding for display according to claim 5
According to the product, the flat part has a thickness of 2 to 2.5 mm.
When the glass is relatively thin, the X-ray absorption coefficient of the glass is 70-150.
cm -1To increase the X-ray absorption coefficient.
By increasing the amount of the composition
When applied to electron-beam excited displays,
To suppress an increase in the amount of X-ray leakage outside the spray
Can be.
【0063】請求項6記載のディスプレイ用ガラス成形
品によれば、側壁部の高さが1〜5mmであるので、ガ
ラス成形品をフラット型電子線励起ディスプレイに適用
させることができる。According to the glass molded article for display according to the sixth aspect, since the height of the side wall is 1 to 5 mm, the glass molded article can be applied to a flat type electron beam excited display.
【0064】請求項7記載のディスプレイ用ガラス成形
品によれば、フランジ部の長さが1〜20mmであるの
で、ディスプレイを形成すべくフランジ部をリアプレー
トにフリットガラス、レーザ等で接合する際に封着性を
向上させることができる。According to the glass molded product for a display according to the present invention, since the length of the flange portion is 1 to 20 mm, the flange portion is bonded to the rear plate by frit glass, laser or the like in order to form a display. In addition, the sealing property can be improved.
【0065】請求項8記載のディスプレイ用ガラス成形
品によれば、ガラスの比抵抗が、室温において1.0×
1012Ω・cm以上であるので、ガラス成形品の電気絶
縁性を向上させることができる。According to the glass molded article for a display according to the eighth aspect, the specific resistance of the glass is 1.0 × at room temperature.
Since it is 10 12 Ω · cm or more, the electrical insulation of the glass molded product can be improved.
【0066】請求項9記載のディスプレイ用ガラス成形
品によれば、ガラス成形品の表面層を圧縮歪層にしてガ
ラス成形品の機械的強度を向上させることができると共
に、該表面層を電子ビームの照射に対して着色しにくい
組成とすることができる。According to the glass molded article for a display according to the ninth aspect, the surface layer of the glass molded article can be made a compression strain layer to improve the mechanical strength of the glass molded article, and the surface layer can be formed by an electron beam. Can be made to be a composition that is difficult to be colored by the irradiation of.
【0067】請求項10記載のディスプレイ用ガラス成
形品によれば、フラット型電子励起ディスプレイに適し
たガラス成形品を提供することができる。According to the glass molded article for a display according to the tenth aspect, a glass molded article suitable for a flat type electronically excited display can be provided.
【0068】請求項11記載のディスプレイ用ガラス容
器によれば、請求項1乃至10のいずれか1項に記載し
たディスプレイ用ガラス成形品を備えるので、上述した
と同様の効果を奏するガラス容器を提供することができ
る。According to the glass container for a display according to the eleventh aspect, since the molded glass product for a display according to any one of the first to tenth aspects is provided, a glass container having the same effects as described above is provided. can do.
【図面の簡単な説明】[Brief description of the drawings]
【図1】SrO及びBaOの合計量とガラスの比重との
関係を示すグラフである。FIG. 1 is a graph showing the relationship between the total amount of SrO and BaO and the specific gravity of glass.
【図2】SrO及びBaOの合計量とガラスのX線吸収
係数との関係を示すグラフである。FIG. 2 is a graph showing the relationship between the total amount of SrO and BaO and the X-ray absorption coefficient of glass.
【図3】本発明の実施の形態に係るディスプレイ用ガラ
ス成形品の断面図である。FIG. 3 is a cross-sectional view of a molded glass article for a display according to an embodiment of the present invention.
【図4】本発明の実施の形態に係るディスプレイ用ガラ
ス容器の断面図である。FIG. 4 is a cross-sectional view of the display glass container according to the embodiment of the present invention.
【図5】従来のフラット型電子線励起ディスプレイの断
面図である。FIG. 5 is a cross-sectional view of a conventional flat electron beam excitation display.
【図6】従来の別のフラット型電子線励起ディスプレイ
の断面図である。FIG. 6 is a cross-sectional view of another conventional flat electron beam excited display.
10 フロントプレート 11 平坦部 12 側壁部 13 フランジ部 14 リアプレート 15 スペーサ 16 フリットガラス 17 蛍光体 18 電子線放出素子 20 減圧容器 DESCRIPTION OF SYMBOLS 10 Front plate 11 Flat part 12 Side wall part 13 Flange part 14 Rear plate 15 Spacer 16 Frit glass 17 Phosphor 18 Electron beam emitting element 20 Pressure reducing container
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 4G062 AA03 BB01 DA06 DA07 DB03 DB04 DC01 DC02 DC03 DC04 DD01 DE01 DE02 DE03 DF01 EA01 EA02 EB03 EB04 EC01 EC02 EC03 ED03 EE03 EF01 EF02 EF03 EF04 EG01 EG02 EG03 EG04 FA01 FB01 FC01 FC02 FC03 FD01 FE02 FF01 FG01 FH01 FJ01 FK01 FL01 GA01 GB02 GC01 GD01 GE01 HH01 HH03 HH05 HH07 HH09 HH11 HH13 HH15 HH17 HH20 JJ01 JJ03 JJ04 JJ05 JJ07 JJ10 KK01 KK03 KK05 KK07 KK10 MM12 MM25 MM27 NN14 NN26 NN33 5C032 AA01 BB02 BB03 5C094 AA15 AA43 BA21 DA05 FB02 FB15 JA08 JA11 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4G062 AA03 BB01 DA06 DA07 DB03 DB04 DC01 DC02 DC03 DC04 DD01 DE01 DE02 DE03 DF01 EA01 EA02 EB03 EB04 EC01 EC02 EC03 ED03 EE03 EF01 EF02 EF03 EF04 EG01 FC04 FC03 FC01 FC03 FC04 FD01 FE02 FF01 FG01 FH01 FJ01 FK01 FL01 GA01 GB02 GC01 GD01 GE01 HH01 HH03 HH05 HH07 HH09 HH11 HH13 HH15 HH17 HH20 JJ01 JJ03 JJ04 NN05 JJ07 JJ10 KK01 KK15 NN12 NN03 NN05 NN2 FB15 JA08 JA11
Claims (11)
呈するように折り曲げられて連なる側壁部と、該側壁部
から外側に折り曲げられて連なるフランジ部とを有する
ディスプレイ用ガラス成形品において、前記ガラス成形
品の平坦部の厚さが2〜4mmであることを特徴とする
ディスプレイ用ガラス成形品。1. A glass molded product for a display, comprising: a rectangular flat portion; a side wall portion which is bent to have a concave shape from the flat portion and is continuous; and a flange portion which is bent outward from the side wall portion and is continuous. A glass molded article for a display, wherein the flat part of the glass molded article has a thickness of 2 to 4 mm.
線吸収係数が40〜110cm-1であることを特徴とす
る請求項1に記載のディスプレイ用ガラス成形品。2. X of glass constituting said glass molded product
The glass molded article for a display according to claim 1 , wherein the linear absorption coefficient is 40 to 110 cm- 1 .
ることを特徴とする請求項2記載のディスプレイ用ガラ
ス成形品。3. The molded glass article for a display according to claim 2, wherein the thickness of the flat portion is 2.5 to 4 mm.
線吸収係数が70〜150cm-1であることを特徴とす
る請求項1に記載のディスプレイ用ガラス成形品。4. The X of the glass constituting the glass molded product
The glass molded article for a display according to claim 1 , wherein the linear absorption coefficient is 70 to 150 cm- 1 .
ることを特徴とする請求項4記載のディスプレイ用ガラ
ス成形品。5. The molded glass article for a display according to claim 4, wherein the flat portion has a thickness of 2 to 2.5 mm.
とを特徴とする請求項1乃至5のいずれか1項に記載の
ディスプレイ用ガラス成形品。6. The glass molded product for a display according to claim 1, wherein the height of the side wall portion is 1 to 5 mm.
あることを特徴とする請求項1乃至6のいずれか1項に
記載のディスプレイ用ガラス成形品。7. The molded glass article for a display according to claim 1, wherein the length of the flange portion is 1 to 20 mm.
抵抗が、室温において1.0×1012Ω・cm以上であ
ることを特徴とする請求項1乃至7のいずれか1項に記
載のディスプレイ用ガラス成形品。8. The method according to claim 1, wherein the glass constituting the molded glass article has a specific resistance of 1.0 × 10 12 Ω · cm or more at room temperature. Glass molding for display.
イオンをカリウムイオンに置換したことを特徴とする請
求項1乃至8のいずれか1項に記載のディスプレイ用ガ
ラス成形品。9. The molded glass article for display according to claim 1, wherein sodium ions in the surface layer of the flat portion are replaced with potassium ions.
使用されることを特徴とする請求項1乃至9のいずれか
1項に記載のディスプレイ用ガラス成形品。10. The molded glass article for display according to claim 1, which is used for a flat type electron beam excited display.
載のディスプレイ用ガラス成形品を備えるディスプレイ
用ガラス容器。A glass container for a display, comprising the glass molded product for a display according to any one of claims 1 to 10.