JP2000275642A - Liquid crystal display device and its production - Google Patents
Liquid crystal display device and its productionInfo
- Publication number
- JP2000275642A JP2000275642A JP7983299A JP7983299A JP2000275642A JP 2000275642 A JP2000275642 A JP 2000275642A JP 7983299 A JP7983299 A JP 7983299A JP 7983299 A JP7983299 A JP 7983299A JP 2000275642 A JP2000275642 A JP 2000275642A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- crystal display
- substrate
- alignment film
- alignment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、電圧−透過率特性
が急峻な、マルチプレックス駆動に適した液晶表示素子
及びその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a liquid crystal display device having a steep voltage-transmittance characteristic and suitable for multiplex driving, and a method of manufacturing the same.
【０００２】[0002]
【従来の技術】液晶表示素子は薄型で軽量、かつ低消費
電力のディスプレイ素子であり、テレビやビデオなどの
画像表示装置や、モニター、ワープロ、パーソナルコン
ピュータなどのＯＡ機器に広く用いられている。2. Description of the Related Art Liquid crystal display devices are thin, lightweight, and low power consumption display devices, and are widely used in image display devices such as televisions and videos, and in OA equipment such as monitors, word processors, and personal computers.
【０００３】これらの液晶表示素子は大別してマルチプ
レックス駆動型液晶表示素子とアクティブマトリクス駆
動型液晶表示素子とに分けられる。安価なディスプレイ
として需要の多いＳＴＮ（スーパーツイステッドネマテ
ィック）型液晶表示素子はマルチプレックス駆動型液晶
表示素子に属している。[0003] These liquid crystal display elements are roughly classified into a multiplex drive type liquid crystal display element and an active matrix drive type liquid crystal display element. STN (super twisted nematic) type liquid crystal display elements, which are in great demand as inexpensive displays, belong to multiplex drive type liquid crystal display elements.
【０００４】ところで、マルチプレックス駆動において
は、オン電圧Ｖon、オフ電圧Ｖoff及び走査線本数Ｎの
間には、In the multiplex driving, the ON voltage Von, the OFF voltage Voff, and the number N of scanning lines are equal to each other.
【数１】 の関係が知られており、走査線本数を上げるため電圧−
透過率特性をより一層急峻にする試みが種々行われてき
た。その一つの典型的な例がＳＴＮ型液晶表示素子であ
り、通常液晶捻れ角は２４０度、あるいはそれ以上の２
４０度〜２７０度に設定されている。更に、用途に応じ
て１８０度〜２４０度の液晶捻れ角を有するＳＴＮ型液
晶表示素子も少なくない。(Equation 1) It is known that the voltage-
Various attempts have been made to make the transmittance characteristics even steeper. One typical example is an STN type liquid crystal display element, in which the liquid crystal twist angle is usually 240 degrees or more.
It is set to 40 degrees to 270 degrees. Further, there are many STN-type liquid crystal display elements having a liquid crystal twist angle of 180 to 240 degrees depending on the application.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、上記の
ＳＴＮ型液晶表示素子は、以下の問題が有している。However, the above STN type liquid crystal display device has the following problems.
【０００６】（１）液晶捻れ角が大きいため、低次ツイ
ストの発生を抑制するために液晶材料のカイラルピッチ
を小さくしたり、液晶プレチルト角を高くする必要があ
る。しかしながら、このようにすれば、電圧印加時のス
トライプドメインが発生しやすくなるという問題があ
る。そのため、パネル設計値に際しては、液晶プレチル
ト角の適正な範囲が存在する。通常この範囲はｄ／ｐ
（ｄ：液晶層厚、ｐ：液晶材料カイラルピッチ）範囲で
規定されるが、液晶材料や配向膜材料の種類により変化
するため、材料選択時の大きな課題となっている。(1) Since the twist angle of the liquid crystal is large, it is necessary to reduce the chiral pitch of the liquid crystal material and increase the liquid crystal pretilt angle in order to suppress the occurrence of low-order twist. However, in this case, there is a problem that a stripe domain is easily generated when a voltage is applied. Therefore, there is an appropriate range of the liquid crystal pretilt angle when designing the panel. Usually this range is d / p
(D: thickness of liquid crystal layer, p: chiral pitch of liquid crystal material). However, since it varies depending on the type of liquid crystal material or alignment film material, it is a major problem in material selection.
【０００７】（２）また、ＳＴＮ型液晶表示素子におい
ては、液晶捻れ角を大きくするため、カイラル剤の添加
量が多く、それに応じて液晶の粘度が増大し、このため
ＴＮ型液晶表示素子よりも応答が遅いという本質的問題
を有している。(2) In the STN type liquid crystal display device, the amount of the chiral agent added is large in order to increase the twist angle of the liquid crystal, and the viscosity of the liquid crystal is accordingly increased. Also have the inherent problem of slow response.
【０００８】（３）更には、ＳＴＮ型液晶表示素子は複
屈折表示モードを利用しているため、高輝度特性と高コ
ントラスト特性の両立が容易ではない、更に色付きが生
じるという課題も有している。(3) Further, since the STN-type liquid crystal display device uses a birefringent display mode, it is not easy to achieve both high luminance characteristics and high contrast characteristics, and there is a problem that coloring occurs. I have.
【０００９】本発明は、上記課題に鑑み、ＴＮ型液晶表
示素子でありながら、急峻な電圧−透過率特性を有し、
マルチプレックス駆動に適した液晶表示素子及びその製
造方法を提供することを目的とする。In view of the above problems, the present invention has a steep voltage-transmittance characteristic while being a TN type liquid crystal display element.
An object of the present invention is to provide a liquid crystal display element suitable for multiplex driving and a method for manufacturing the same.
【００１０】[0010]
【課題を解決するための手段】上記目的を達成するた
め、請求項１記載の発明は、走査信号電圧が印加される
複数のストライプ状走査電極と、走査電極上に形成され
る配向膜とを有する第１基板と、前記走査電極と交差す
るように配置され且つ画像信号電圧が印加される複数の
ストライプ状信号電極と、信号電極上に形成される配向
膜とを有する第２基板と、第１基板と第２基板との間に
封入され、且つ第１及び第２基板のうちの一方から他方
に向かって捻れ配向状態となっている液晶材料と、を含
むツイステッドネマティック型液晶表示素子であって、
前記液晶材料の前記各配向膜に対する表面アンカリング
強度が１．０×１０-4Ｊ／ｍ2以下であることを特徴と
する。According to a first aspect of the present invention, a plurality of stripe-shaped scanning electrodes to which a scanning signal voltage is applied and an alignment film formed on the scanning electrodes are provided. A second substrate comprising: a first substrate having a plurality of stripe-shaped signal electrodes disposed so as to intersect with the scanning electrodes and to which an image signal voltage is applied; and an alignment film formed on the signal electrodes. A liquid crystal material sealed between the first substrate and the second substrate and being in a twisted alignment state from one of the first and second substrates toward the other. hand,
A surface anchoring strength of the liquid crystal material with respect to each of the alignment films is 1.0 × 10 −4 J / m 2 or less.
【００１１】従来のポリイミド樹脂の配向膜を使用する
ＴＮ型液晶表示素子の場合、表面アンカリング強度は少
なくとも５×１０-4Ｊ／ｍ2〜１０-3Ｊ／ｍ2程度であ
り、これに比べると、表面アンカリング強度を１．０×
１０-4Ｊ／ｍ2以下とする本発明は、表面アンカリング
強度が弱いことになる。このようにアンカリング強度が
弱いと、電圧印加時において、基板界面近傍の液晶分子
の立ち上がりが容易となる。そのため、ＴＮ型の液晶表
示素子でありながら、急峻な電圧−透過率特性が得られ
る。この結果、ＴＮ型の液晶表示素子でありながら、マ
ルチプレックス駆動が可能となる。In the case of a conventional TN type liquid crystal display device using an alignment film of a polyimide resin, the surface anchoring strength is at least about 5 × 10 −4 J / m 2 to 10 −3 J / m 2. By comparison, the surface anchoring strength is 1.0 ×
According to the present invention of 10 −4 J / m 2 or less, the surface anchoring strength is weak. When the anchoring strength is low as described above, the liquid crystal molecules near the substrate interface easily rise when a voltage is applied. Therefore, a steep voltage-transmittance characteristic can be obtained even in the case of a TN type liquid crystal display element. As a result, multiplex driving can be performed even though the liquid crystal display element is a TN type liquid crystal display element.
【００１２】また、本発明に係る液晶表示素子は、基本
的にはＴＮ型液晶表示素子であるため、マルチプレック
ス駆動型の液晶表示素子として使用されていたＳＴＮ型
液晶表示素子の有する種々の問題を解消できることにな
る。Further, since the liquid crystal display device according to the present invention is basically a TN type liquid crystal display device, there are various problems of the STN type liquid crystal display device used as a multiplex drive type liquid crystal display device. Can be eliminated.
【００１３】尚、表面アンカリング強度を上記のように
規制するのは、少なくとも表面アンカリング強度が１．
０×１０-4Ｊ／ｍ2以下でないと、マルチプレックス駆
動に適した電圧−透過率特性の急峻性が得られないから
である。The surface anchoring strength is regulated as described above because at least the surface anchoring strength is 1.
If it is not less than 0 × 10 −4 J / m 2 , steepness of voltage-transmittance characteristics suitable for multiplex driving cannot be obtained.
【００１４】また請求項２記載の発明は、請求項１記載
の液晶表示素子であって、前記配向膜がポリスチレン誘
導体から成ることを特徴とする。According to a second aspect of the present invention, there is provided the liquid crystal display device according to the first aspect, wherein the alignment film is made of a polystyrene derivative.
【００１５】上記の如くポリスチレン誘導体で配向膜を
形成した場合、ポリスチレン誘導体の側鎖としてのフェ
ニル基との相互作用により液晶分子が配向する。一方、
従来例のようにポリイミド樹脂を配向膜とする場合に
は、主鎖にある芳香環との相互作用により液晶分子が配
向する。このことは、ポリイミド樹脂から成る配向膜の
場合には、大略的に見れば、配向膜表面全体が液晶分子
の配向規制に寄与しており、一方、ポリスチレン誘導体
から成る配向膜の場合には、側鎖にあるフェニル基のみ
が液晶分子の配向規制に寄与していると見なすことがで
きる。そして、ポポリイミド主鎖（剛直性を有する骨
格）に比べて側鎖に付いているフェニル基は柔軟性を有
している。この結果、ポリスチレン誘導体で配向膜を形
成した場合、従来例の配向膜（ポリイミド膜）に比べて
アンカリング強度が弱くなると考えられる。よって、配
向膜材料としてポリスチレン誘導体を用いることによ
り、１．０×１０-4Ｊ／ｍ2以下のアンカリング強度と
することが可能となる。When the alignment film is formed from the polystyrene derivative as described above, the liquid crystal molecules are aligned by the interaction with the phenyl group as a side chain of the polystyrene derivative. on the other hand,
When a polyimide resin is used as the alignment film as in the conventional example, the liquid crystal molecules are aligned by the interaction with the aromatic ring in the main chain. This means that, in the case of an alignment film made of a polyimide resin, roughly speaking, the entire surface of the alignment film contributes to the alignment control of liquid crystal molecules, while, in the case of an alignment film made of a polystyrene derivative, It can be considered that only the phenyl group in the side chain contributes to the regulation of the alignment of the liquid crystal molecules. The phenyl group attached to the side chain has more flexibility than the main chain of the polyimide (a rigid skeleton). As a result, when the alignment film is formed of a polystyrene derivative, it is considered that the anchoring strength is lower than that of the conventional alignment film (polyimide film). Therefore, by using a polystyrene derivative as the alignment film material, it is possible to achieve an anchoring strength of 1.0 × 10 −4 J / m 2 or less.
【００１６】また請求項３記載の発明は、請求項１記載
の液晶表示素子であって、前記配向膜がポリビニルシン
ナメート誘導体から成り、且つこの配向膜は光配向法に
より配向処理がなれていることを特徴とする。According to a third aspect of the present invention, there is provided the liquid crystal display device according to the first aspect, wherein the alignment film is formed of a polyvinyl cinnamate derivative, and the alignment film has been subjected to an alignment process by a photo alignment method. It is characterized by the following.
【００１７】上記構成により、表面アンカリング強度を
弱くすることができる。これは、以下の理由によると考
えられる。即ち、ポリビニルシンナメート誘導体を配向
膜とする場合には、側鎖における官能基との相互作用に
より液晶分子が配向すると考えられる。ところが、配向
処理すべくポリビニルシンナメート誘導体に光が照射さ
れると、ポリビニルシンナメート誘導体の側鎖に、光分
解による裂断が生じる。このため、配向処理として光配
向法を用いると、ポリビニルシンナメート誘導体の液晶
分子と相互作用をなす部分の密度が、光照射前の密な状
態から疎の状態となり、この結果、表面アンカリング強
度が弱くなると考えられる。According to the above configuration, the surface anchoring strength can be reduced. This is considered for the following reason. That is, when the polyvinyl cinnamate derivative is used as the alignment film, it is considered that the liquid crystal molecules are aligned by the interaction with the functional group in the side chain. However, when the polyvinyl cinnamate derivative is irradiated with light in order to perform the alignment treatment, a side chain of the polyvinyl cinnamate derivative is broken by photolysis. Therefore, when the photo-alignment method is used as the alignment treatment, the density of the portion that interacts with the liquid crystal molecules of the polyvinyl cinnamate derivative changes from a dense state before light irradiation to a sparse state, and as a result, the surface anchoring strength is reduced. Is thought to be weaker.
【００１８】また請求項４記載の発明は、請求項１乃至
３の何れかに記載の液晶表示素子であって、液晶捻れ角
がほぼ９０度であることを特徴とする。According to a fourth aspect of the present invention, there is provided the liquid crystal display device according to any one of the first to third aspects, wherein a twist angle of the liquid crystal is substantially 90 degrees.
【００１９】上記の如く液晶捻れ角がほぼ９０度である
と、光学設計的には複屈折の影響が最も少なくなる。そ
のため、色づきの発生を最も低減することができる。When the twist angle of the liquid crystal is approximately 90 degrees as described above, the influence of birefringence is minimized in optical design. Therefore, the occurrence of coloring can be reduced most.
【００２０】また請求項５記載の発明は、請求項１記載
の液晶表示素子の製造方法であって、ＬＢ（ラングミュ
ア・ブロジェット）法を用いて、走査電極及び信号電極
の少なくとも一方の電極上に配向膜を成膜する工程を含
むことを特徴とする。According to a fifth aspect of the present invention, there is provided a method of manufacturing a liquid crystal display device according to the first aspect, wherein at least one of a scanning electrode and a signal electrode is formed using a LB (Langmuir-Blodgett) method. And a step of forming an alignment film.
【００２１】上記の如くＬＢ法により配向膜を形成する
ことにより、膜厚を格段に薄くすることができる。これ
により、表面アンカリング強度が弱くなる。従って、本
発明による方法により液晶表示素子を製造することによ
り、急峻な電圧−透過率特性を有し、マルチプレックス
駆動に適した液晶表示素子を製造することができる。By forming the alignment film by the LB method as described above, the film thickness can be significantly reduced. Thereby, the surface anchoring strength is weakened. Therefore, by manufacturing a liquid crystal display device by the method according to the present invention, a liquid crystal display device having steep voltage-transmittance characteristics and suitable for multiplex driving can be manufactured.
【００２２】また請求項６記載の発明は、請求項１記載
の液晶表示素子の製造方法であって、光配向法を用い
て、走査電極及び信号電極の少なくとも一方の電極上に
形成された配向膜を配向処理する工程を含むことを特徴
とする。According to a sixth aspect of the present invention, there is provided a method of manufacturing a liquid crystal display device according to the first aspect, wherein an alignment formed on at least one of a scanning electrode and a signal electrode by using a photo-alignment method. The method is characterized by including a step of subjecting the film to an orientation treatment.
【００２３】上記のように光配向法により得られた配向
膜はアンカリング強度が弱い。これは以下の理由によ
る。即ち、配向膜に紫外光を照射すると、配向膜を構
成する高分子に光分解による裂断が生じる。このため、
アンカリングに寄与する部分の密度が、光照射する前の
状態よりも低下した状態となる。また光配向膜の場合
には、膜の配向秩序度が、ラビング膜に比べて低い。か
かる、により、アンカリング強度が弱まるものと考
えられる。The alignment film obtained by the photo-alignment method as described above has a low anchoring strength. This is for the following reason. That is, when the alignment film is irradiated with ultraviolet light, the polymer constituting the alignment film is broken by photolysis. For this reason,
The density of the portion contributing to the anchoring is lower than that before the light irradiation. In the case of a photo-alignment film, the orientation order of the film is lower than that of a rubbing film. It is thought that the anchoring strength is weakened due to the above.
【００２４】尚、配向膜の材料としては、通常使用され
る配向膜材料の範囲内のものであれば、光配向処理によ
りアンカリング強度が１．０×１０-4Ｊ／ｍ2以下まで
弱くなることは既に知られている。従って、本発明によ
る方法により液晶表示素子を製造することにより、急峻
な電圧−透過率特性を有し、マルチプレックス駆動に適
した液晶表示素子を製造することができる。If the material of the alignment film is within the range of a commonly used alignment film material, the anchoring strength is weakened to 1.0 × 10 −4 J / m 2 or less by the optical alignment treatment. That is already known. Therefore, by manufacturing a liquid crystal display device by the method according to the present invention, a liquid crystal display device having steep voltage-transmittance characteristics and suitable for multiplex driving can be manufactured.
【００２５】[0025]
【発明の実施の形態】（実施の形態）図１は本発明の実
施の形態に係る液晶表示素子の簡略化した断面図であ
る。この液晶表示素子は、ＴＮ型液晶表示素子であっ
て、しかもマルチプレックス駆動方式の液晶表示素子で
ある。以下に、本実施の形態に係る液晶表示素子の構成
を説明する。液晶表示素子は、液晶セル２と、液晶セル
２の外側面にそれぞれ設けられた偏光板３，４とを有す
る。偏光板３，４は、クロスニコルに配置されている。
また、前記液晶セル２は、透明な第１基板５と、第１基
板５に対向して配置される透明な第２基板６と、第１基
板５の内側面に形成されている複数のストライプ状走査
電極７と、第２基板６の内側面に形成されている複数の
ストライプ状信号電極８と、走査電極７の内側面に形成
されている配向膜９と、走査電極８の内側面に形成され
ている配向膜１０と、配向膜９，１０間に封入された液
晶材料１１とから構成されている。尚、図１において、
１２はシール材であり、１３はスペーサである。(Embodiment) FIG. 1 is a simplified sectional view of a liquid crystal display device according to an embodiment of the present invention. This liquid crystal display element is a TN type liquid crystal display element and is a multiplex drive type liquid crystal display element. Hereinafter, the configuration of the liquid crystal display element according to the present embodiment will be described. The liquid crystal display element has a liquid crystal cell 2 and polarizing plates 3 and 4 provided on the outer surface of the liquid crystal cell 2, respectively. The polarizing plates 3 and 4 are arranged in crossed Nicols.
The liquid crystal cell 2 includes a transparent first substrate 5, a transparent second substrate 6 disposed to face the first substrate 5, and a plurality of stripes formed on an inner surface of the first substrate 5. Scan electrodes 7, a plurality of striped signal electrodes 8 formed on the inner surface of the second substrate 6, an alignment film 9 formed on the inner surface of the scan electrodes 7, It comprises an alignment film 10 formed and a liquid crystal material 11 sealed between the alignment films 9 and 10. In FIG. 1,
Reference numeral 12 denotes a sealing material, and reference numeral 13 denotes a spacer.
【００２６】前記走査電極７及び信号電極８は、例えば
ＩＴＯから成る透明電極であり、走査電極７と信号電極
８とは、直交した状態に配置されている。そして、走査
信号により走査電極７が順次選択され、これと共に信号
電極８に画像信号電圧が印加されることにより、選択さ
れた走査電極と信号電極との交点間に存在する液晶材料
１１が駆動され、こうしてマルチプレックス駆動がなさ
れる。The scanning electrode 7 and the signal electrode 8 are transparent electrodes made of, for example, ITO, and the scanning electrode 7 and the signal electrode 8 are arranged in an orthogonal state. Then, the scanning electrodes 7 are sequentially selected by the scanning signal, and the image signal voltage is applied to the signal electrode 8 at the same time, whereby the liquid crystal material 11 existing between the intersections of the selected scanning electrode and the signal electrode is driven. Thus, multiplex driving is performed.
【００２７】また前記液晶材料１１は、ネマティック液
晶であり、第１基板６から第２基板７に向かって９０°
捻れた配向状態となっている。尚、捻れ角θは、９０°
に限定さるものでなく、１２０°以下のいずれの角度で
あってもよい。但し、９０°に限定した場合、光学設計
上複屈折がでてくる要素が少なく、色付きが少ないとい
う効果を有する。The liquid crystal material 11 is a nematic liquid crystal and has a 90 ° angle from the first substrate 6 to the second substrate 7.
It is in a twisted orientation state. The twist angle θ is 90 °
However, the angle may be any angle of 120 ° or less. However, when the angle is limited to 90 °, there are few elements that cause birefringence due to optical design, and there is an effect that coloring is small.
【００２８】また液晶材料１１の配向膜に対する表面ア
ンカリング強度は、１．０×１０-4Ｊ／ｍ2以下とされ
ている。このように通常のＴＮ型液晶表示素子の表面ア
ンカリング強度（５×１０-4Ｊ／ｍ2〜１×１０-3Ｊ／
ｍ2）よりも小さい表面アンカリング強度とする点が、
本発明の主たる特徴である。このようにアンカリング強
度を弱くすることにより、僅かの電圧印加によって基板
界面近傍に存在する液晶分子が立ち上がってくる。この
ことは、ＴＮ型液晶表示素子であるにも拘わらず、γ値
が小さく、電圧−透過率特性が急峻になったことを意味
する。従って、マルチプレックス駆動を実現するが可能
となる。尚、通常のＴＮ型液晶表示素子では、強いアン
カリング強度を有しているため、電圧印加時において基
板界面近傍に存在する液晶分子は配向膜から強く束縛さ
れている。そのため、印加電圧が一定電圧（閾値電圧）
に達しても、中央部に位置する液晶分子は立ち上がり始
めるけれども、基板界面近傍に存在する液晶分子はほと
んど変化しない。そして、更に印加電圧の上昇により液
晶分子の変化が徐々に中央部から基板界面側に伝播して
いく。このような液晶分子の動きにより、通常のＴＮ型
液晶表示素子の電圧−透過率特性は緩やかなものとなっ
ている。従って、通常のＴＮ型液晶表示素子はマルチプ
レックス駆動に適していない。この点に関して、本発明
に係る液晶表示素子は、捻れ角θが通常のＴＮ型液晶表
示素子と同様の１２０°以下とされているにも拘わら
ず、急峻な電圧−透過率特性を有するため、マルチプレ
ックス駆動が可能となる。The surface anchoring strength of the liquid crystal material 11 with respect to the alignment film is set to 1.0 × 10 −4 J / m 2 or less. As described above, the surface anchoring strength (5 × 10 −4 J / m 2 to 1 × 10 −3 J / m) of the normal TN type liquid crystal display element is obtained.
The point that the surface anchoring strength is smaller than m 2 )
This is a main feature of the present invention. By weakening the anchoring strength in this manner, liquid crystal molecules existing near the substrate interface rise with a slight voltage application. This means that the γ value is small and the voltage-transmittance characteristic is sharp, despite being a TN type liquid crystal display element. Therefore, multiplex driving can be realized. Incidentally, since a normal TN type liquid crystal display element has a strong anchoring strength, liquid crystal molecules existing near the substrate interface when a voltage is applied are strongly bound by the alignment film. Therefore, the applied voltage is constant (threshold voltage)
, The liquid crystal molecules located at the center start rising, but the liquid crystal molecules existing near the substrate interface hardly change. Further, the change of the liquid crystal molecules gradually propagates from the central portion to the substrate interface due to the increase of the applied voltage. Due to such movement of the liquid crystal molecules, the voltage-transmittance characteristic of a normal TN type liquid crystal display element becomes gentle. Therefore, ordinary TN liquid crystal display elements are not suitable for multiplex driving. In this regard, the liquid crystal display element according to the present invention has a steep voltage-transmittance characteristic despite the fact that the twist angle θ is 120 ° or less, which is the same as that of a normal TN type liquid crystal display element. Multiplex drive becomes possible.
【００２９】また、本発明に係る液晶表示素子は、表面
アンカリング強度の点を除いて、基本的にはＴＮ型液晶
表示素子であるため、従来の技術の項において述べたＳ
ＴＮ型液晶表示素子の課題を全て解決することができ
る。具体的に説明すれば、通常のＴＮ型液晶表示素子と
同様の捻れ角であるので、カイラル剤の添加がＳＴＮ型
液晶表示素子に比べて少なく、そのため液晶の粘度が、
通常のＴＮ型液晶表示素子と同様である。従って、電界
応答性がよい。また、ＳＴＮ型液晶表示素子特有の液晶
材料等に関する材料選定の困難性がない。更に、複屈折
表示モードでなく、旋光性に基づく表示モードであるた
め、色づきも発生しない。Further, the liquid crystal display device according to the present invention is basically a TN type liquid crystal display device except for the surface anchoring strength.
All the problems of the TN type liquid crystal display element can be solved. More specifically, since the twist angle is the same as that of a normal TN liquid crystal display element, the addition of a chiral agent is smaller than that of an STN liquid crystal display element, and therefore, the viscosity of the liquid crystal is reduced.
This is the same as a normal TN liquid crystal display element. Therefore, the electric field response is good. Further, there is no difficulty in selecting a material for a liquid crystal material or the like peculiar to the STN type liquid crystal display element. Further, since the display mode is based on the optical rotation instead of the birefringence display mode, no coloring occurs.
【００３０】こうして、ＳＴＮ型液晶表示素子の有する
課題を解決し、しかもマルチプレックス駆動が可能な液
晶表示素子を実現することができる。尚、表面アンカリ
ング強度は、１．０×１０-4Ｊ／ｍ2以下で、１．０×
１０- 6Ｊ／ｍ2以上とするのが望ましい。なぜなら、表
面アンカリング強度が１．０×１０-6Ｊ／ｍ2よりも小
さいと、ヒステリシスが大きくなり、表示特性が劣化す
るからである。In this way, it is possible to solve the problems of the STN type liquid crystal display device and to realize a liquid crystal display device capable of multiplex driving. The surface anchoring strength is 1.0 × 10 −4 J / m 2 or less and 1.0 × 10 −4 J / m 2 or less.
10 - to the 6 J / m 2 or more. This is because if the surface anchoring strength is smaller than 1.0 × 10 −6 J / m 2 , the hysteresis increases and the display characteristics deteriorate.
【００３１】次いで、アンカリング強度を１．０×１０
-4Ｊ／ｍ2以下とする方策について説明する。具体的に
は、配向膜材料の選定、ＬＢ法により配向膜を形成
する、配向膜の配向処理として光配向処理を用いる。Next, the anchoring strength was set to 1.0 × 10
The following describes how to reduce the pressure to -4 J / m 2 or less. Specifically, selection of an alignment film material, formation of an alignment film by an LB method, and optical alignment processing are used as alignment processing of the alignment film.
【００３２】［配向膜材料の選定］配向膜材料として
は、ポリスチレン誘導体、ポリビニルシンナメート誘導
体を用いる。ポリスチレン誘導体としては、例えば、ポ
リスチレン、ｐ−フェニルポリスチレン、ｐ−メトキシ
ポリスチレン、ｐ−フルオロポリスチレン等が挙げられ
る。また、ポリビニルシンナメート誘導体としては、例
えばポリビニルシンナメート、ポリビニルｐ−メトキシ
シンナメート、ポリビニルｐ−フルオロシンナメート等
が挙げられる。[Selection of Alignment Film Material] As the alignment film material, a polystyrene derivative or a polyvinyl cinnamate derivative is used. Examples of the polystyrene derivative include polystyrene, p-phenyl polystyrene, p-methoxy polystyrene, p-fluoro polystyrene, and the like. Examples of the polyvinyl cinnamate derivative include polyvinyl cinnamate, polyvinyl p-methoxy cinnamate, polyvinyl p-fluoro cinnamate, and the like.
【００３３】ポリスチレン誘導体を配向膜材料とする場
合には、膜形成としてはスピンコート法による塗布によ
ればよく、又、配向処理としてはラビング処理を用いれ
ばよい。但し、膜形成としてＬＢ法を用いてもよく、ま
た、配向処理としては光配向法を用いてもよい。このよ
うにすれば、アンカリング強度をより一層弱くすること
ができる。When a polystyrene derivative is used as the alignment film material, the film may be formed by spin coating, and the rubbing may be used as the alignment treatment. However, the LB method may be used for film formation, and the photo-alignment method may be used for the alignment treatment. In this case, the anchoring strength can be further reduced.
【００３４】また、ポリビニルシンナメート誘導体を配
向膜とする場合には、膜形成としてはＬＢ法を用いる
か、または配向処理として光配向法を用いる。スピンコ
ート法等の通常の膜形成法を用いたり、ラビングによる
配向処理を用いたりすると、アンカリング強度を弱める
ことができないからである。When a polyvinyl cinnamate derivative is used as the alignment film, the LB method is used for forming the film, or the photo-alignment method is used for the alignment treatment. This is because the anchoring strength cannot be reduced by using a normal film forming method such as a spin coating method or by using an alignment treatment by rubbing.
【００３５】尚、後述するように通常使用される配向膜
材料の範囲内では、ＬＢ法を用いるとアンカリング強度
が１．０×１０-4Ｊ／ｍ2程度まで弱くなることが知ら
れている。かかる観点からすれば、ポリビニルシンナメ
ート誘導体以外の材料を配向膜材料として用いてもよ
い。しかし、特にポリビニルシンナメート誘導体を配向
膜材料とし、且つ光配向法を用いた場合には、光配向処
理の際に側鎖の裂断によるアンカリング強度の弱まりと
共に、光感応性基を有するため架橋構造が生じる。この
ため、ポリビニルシンナメート誘導体を配向膜材料とし
且つ配向膜の配向処理に光配向法を用いると、アンカリ
ング強度が弱いことに加えて、安定な配向状態を有する
液晶表示素子が得られる。As will be described later, it is known that the anchoring strength is reduced to about 1.0 × 10 −4 J / m 2 when the LB method is used within the range of the commonly used alignment film material. I have. From this viewpoint, a material other than the polyvinyl cinnamate derivative may be used as the alignment film material. However, in particular, when a polyvinyl cinnamate derivative is used as the alignment film material and the photo-alignment method is used, the photo-alignment treatment has a light-sensitive group together with weakened anchoring strength due to side chain breakage during the photo-alignment treatment. A crosslinked structure results. Therefore, when a polyvinyl cinnamate derivative is used as an alignment film material and the optical alignment method is used for the alignment treatment of the alignment film, a liquid crystal display element having a stable alignment state in addition to a low anchoring strength can be obtained.
【００３６】尚、ポリビニルシンナメート誘導体と同様
に光感応性基を有するアゾベンゼン誘導体を配向膜材料
として用いてもよい。It is to be noted that an azobenzene derivative having a light-sensitive group may be used as the alignment film material similarly to the polyvinyl cinnamate derivative.
【００３７】［ＬＢ法による配向膜の形成］ＬＢ法によ
り配向膜を形成することにより膜厚を格段に薄くするこ
とができ、これにより表面アンカリング強度が弱くな
る。従って、配向膜材料としては、通常使用される配向
膜材料の範囲内のものを用いることができる。尚、単分
子膜の累積層数は、膜の安定性を考慮すれば３０程度以
内とするのが望ましい。[Formation of Alignment Film by LB Method] By forming an alignment film by the LB method, the film thickness can be made much thinner, whereby the surface anchoring strength becomes weak. Therefore, as the alignment film material, a material within the range of a commonly used alignment film material can be used. It is desirable that the cumulative number of monomolecular films be within about 30 in consideration of the stability of the film.
【００３８】［光配向法による配向膜の配向処理］配向
膜の材料としては、通常使用される配向膜材料の範囲内
のものであれば、光配向処理によりアンカリング強度が
１．０×１０-4Ｊ／ｍ2以下まで弱くなることが、既に
知られている。従って、光配向法により配向膜の配向処
理を行う場合には、配向膜材料としては上記のポリスチ
レン誘導体、ポリビニルシンナメート誘導体等に限ら
ず、従来例において使用されていたポリイミド樹脂等で
あってもよい。[Orientation treatment of alignment film by photo-alignment method] If the material of the alignment film is within the range of a commonly used alignment film material, the anchoring strength by photo-alignment treatment is 1.0 × 10 5 It is already known that it becomes weak to -4 J / m 2 or less. Therefore, when performing the alignment treatment of the alignment film by a photo-alignment method, the alignment film material is not limited to the above polystyrene derivatives, polyvinyl cinnamate derivatives and the like, but may be polyimide resins and the like used in conventional examples. Good.
【００３９】尚、配向膜材料の選定、ＬＢ法による
配向膜の形成、光配向法による膜の配向処理は、各々
単独で用いてもよく、また、〜を適宜組み合わせる
ようにしてもよい。更に、配向膜９，１０の全てについ
て、上記〜を適用してもよく、また配向膜９と配向
膜１０の何れか一方のみに、上記〜を適用してもよ
い。例えば、配向膜９のみを光配向法により配向処理
し、配向膜１０はラビングにより配向処理するようにし
てもよい。勿論このような場合であても、配向膜９，１
０のいずれにおいても、表面アンカリング強度は、１．
０×１０-4Ｊ／ｍ 2以下に設定する必要がある。The material for the alignment film is selected by the LB method.
The formation of the alignment film and the alignment treatment of the film by the photo alignment method
They may be used alone, or may be appropriately combined with
You may do so. Further, all of the alignment films 9 and 10 are
Above may be applied, and the alignment film 9 and the alignment
The above-mentioned may be applied to only one of the films 10.
No. For example, only the alignment film 9 is subjected to an alignment process by a photo alignment method.
The alignment film 10 is subjected to an alignment process by rubbing.
You may. Of course, even in such a case, the alignment films 9, 1
0, the surface anchoring strength was 1.
0x10-FourJ / m TwoIt is necessary to set below.
【００４０】また、本発明に係る液晶表示素子の製造方
法は、上記〜の点を除いて、通常のＴＮ型液晶表示
素子の製造方法と同様である。The method of manufacturing a liquid crystal display device according to the present invention is the same as the method of manufacturing a normal TN type liquid crystal display device, except for the above points.
【００４１】（その他の事項）上記の例では、捻れ角θ
が１２０°以下のＴＮ型液晶表示素子について説明した
けれども、捻れ角θが１８０°〜３００°のＳＴＮ型液
晶表示素子についても、上記の配向膜材料の選定、
ＬＢ法による配向膜の形成、光配向法による膜の配向
処理を適宜選択してアンカリング強度を弱めるようにし
てもよい。このようにすれば、ＳＴＮ型液晶表示素子で
ありながら、逆ツイストドメイン及び電圧印加時におけ
るストライプドメインの発生を防止することができる。(Other Matters) In the above example, the twist angle θ
Has been described for a TN type liquid crystal display device having a twist angle of 180 ° to 300 °.
The anchoring strength may be reduced by appropriately selecting the formation of the alignment film by the LB method and the alignment treatment of the film by the photo-alignment method. With this configuration, it is possible to prevent the occurrence of a reverse twist domain and a stripe domain when a voltage is applied, even though the device is an STN type liquid crystal display device.
【００４２】[0042]
【実施例】以下，本発明を実施例に基づいて更に詳細に
説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in more detail with reference to embodiments.
【００４３】尚、以下の実施例において、表面アンカリ
ング強度は飽和閾値法（Ａ．Ｓｕｇｉｍｕｒａ，Ｔ．Ｍ
ｉｙａｍｏｔｏ，Ｍ．Ｔｓｕｊｉ ａｎｄ Ｍ．Ｋｕｚ
ｅ，Ａｐｐｌ．Ｐｈｙｓ．Ｌｅｔｔ．，Ｖｏｌ．７２，
ｐ３２９（１９９８）参照）により測定した。In the following examples, the surface anchoring strength was determined by the saturation threshold method (A. Sugimura, TM).
iyamoto, M .; Tsuji and M.S. Kuz
e, Appl. Phys. Lett. , Vol. 72,
p329 (1998)).
【００４４】また、以下の実施例における電圧−透過率
特性図での縦軸の光透過率は、それぞれの偏光軸が平行
に配置された２枚の偏光板の光透過率を１とした時の光
透過率を表している。Further, the light transmittance on the vertical axis in the voltage-transmittance characteristic diagram in the following examples is obtained when the light transmittance of two polarizing plates whose respective polarization axes are arranged in parallel is set to 1. Represents the light transmittance.
【００４５】（実施例１）上記実施の形態に係る液晶表
示素子を以下の方法で作製した。先ず、走査電極７が形
成されたガラスから成る第１基板５上に、出光スチロー
ルＨＦ−１１（出光（株）ポリスチレンペレットの商品
名）を溶かしたメチルエチルケトン溶液をスピンコート
法にて塗布し、この塗布された第１基板５を恒温槽中
で、１００度、１時間乾燥させる。その後、レーヨン製
ラビング布を用いて図２に示すａ１方向にラビング処理
を施した。信号電極８が形成されたガラスから成る第２
基板６についても、上記と同様に出光スチロールＨＦ−
１１（出光（株）ポリスチレンペレットの商品名）を溶
かしたメチルエチルケトン溶液をスピンコート法にて塗
布し、恒温槽中１００度、１時間乾燥させ、その後、レ
ーヨン製ラビング布を用いて図２に示すａ２方向にラビ
ング処理を施した。次いで、第１基板５と第２基板６と
を、スペーサ１３（積水ファインケミカル（株）製）、
及びシール材１２（商品名：ストラクトボンド３５２Ａ
（三井東圧化学（株）製）を用いて基板間隔が５．０μ
ｍとなるように貼り合わせ、液晶セル２を作製した。Example 1 The liquid crystal display device according to the above embodiment was manufactured by the following method. First, a methyl ethyl ketone solution in which Idemitsu Styrol HF-11 (trade name of polystyrene pellets of Idemitsu Co., Ltd.) is applied by spin coating onto a first substrate 5 made of glass on which the scanning electrode 7 is formed. The applied first substrate 5 is dried in a thermostat at 100 degrees for 1 hour. Thereafter, a rubbing treatment was performed in the a1 direction shown in FIG. 2 using a rubbing cloth made of rayon. A second electrode made of glass on which the signal electrode 8 is formed;
As for the substrate 6, the light emitting styrol HF-
11 (a trade name of polystyrene pellets of Idemitsu Co., Ltd.) was applied by a spin coating method, dried in a thermostat at 100 ° C. for 1 hour, and then shown in FIG. 2 using a rubbing cloth made of rayon. Rubbing was performed in the a2 direction. Next, the first substrate 5 and the second substrate 6 are separated by a spacer 13 (manufactured by Sekisui Fine Chemical Co., Ltd.),
And sealing material 12 (trade name: Structbond 352A)
(Mitsui Toatsu Chemical Co., Ltd.) and the substrate spacing is 5.0 μm.
m to obtain a liquid crystal cell 2.
【００４６】次に、カイラル材料としてコレステリルノ
ナノエートを添加してカイラルピッチが４０μｍになる
ように調製したメルク社製液晶ＺＬＩ−４７９２（ＮＩ
点（ネマティック・アイソトロピック転移温度）＝９１
度、Δｎ＝０．０９４）を、真空注入法にて液晶セル２
に注入した。Next, cholesteryl nonanoate as a chiral material was added to adjust the chiral pitch to 40 μm, and the liquid crystal ZLI-4792 (NI
Point (nematic-isotropic transition temperature) = 91
Degree, Δn = 0.094) by the vacuum injection method.
Was injected.
【００４７】その後、偏光板３の偏光軸方向ｂ１と偏光
板４の偏光軸方向ｂ２が、図２に示す状態となるよう
に、偏光板３と偏光板４とを液晶セル２に貼り合わせて
本実施例の液晶表示素子Ａを作成した。Thereafter, the polarizing plate 3 and the polarizing plate 4 are bonded to the liquid crystal cell 2 such that the polarizing axis direction b1 of the polarizing plate 3 and the polarizing axis direction b2 of the polarizing plate 4 are in the state shown in FIG. A liquid crystal display element A of this example was produced.
【００４８】次に、定法に従い、液晶表示素子Ａの電圧
−透過率特性を３０Ｈｚ矩形波の電圧を印加して測定し
た。結果を図３に示す。Next, a voltage-transmittance characteristic of the liquid crystal display element A was measured by applying a 30 Hz rectangular wave voltage according to a conventional method. The results are shown in FIG.
【００４９】ここで、電圧−透過率特性の急峻を示すγ
値をＶ５０／Ｖ９０で定義すると、図３からγ＝１．０
３となる。一方、通常のＴＮ型液晶表示素子では、γ＝
１．２５程度である。従って、本液晶表示素子ＡがＴＮ
型液晶表示素子であるにも拘わらず、急峻な特性を有す
ることが分かる。Here, γ indicating a steep voltage-transmittance characteristic
When the value is defined as V50 / V90, γ = 1.0 from FIG.
It becomes 3. On the other hand, in a normal TN type liquid crystal display element, γ =
It is about 1.25. Therefore, the present liquid crystal display element A is TN
It can be seen that the device has steep characteristics in spite of being a type liquid crystal display device.
【００５０】本実施例１で得られたγ値では走査線本数
３００本（デュアルスキャン方式では６００本）の表示
が可能であり、その実用的価値は極めて大きい。With the γ value obtained in the first embodiment, it is possible to display 300 scanning lines (600 lines in the dual scan system), and its practical value is extremely large.
【００５１】また、液晶表示素子Ａについて、３０Ｈｚ
矩形波の電圧を１．１Ｖから１．４Ｖへ、および１．４
Ｖから１．１Ｖへ電圧値を変化させ、そのときの応答時
間を測定した。その結果、応答時間（立ち上がり時間と
立ち下がり時間との総和）は１５０ミリ秒であった。ま
た、このときのコントラスト比は９５：１であった。For the liquid crystal display element A, 30 Hz
Square wave voltage from 1.1V to 1.4V and 1.4
The voltage value was changed from V to 1.1 V, and the response time at that time was measured. As a result, the response time (sum of the rise time and the fall time) was 150 milliseconds. The contrast ratio at this time was 95: 1.
【００５２】以上より明らかなように、本実施例の液晶
表示素子Ａによればマルチプレックス駆動でありなが
ら、高コントラスト、高速応答可能な液晶表示素子を提
供することが可能であり、その実用的価値は極めて大き
い。As is clear from the above, according to the liquid crystal display element A of the present embodiment, it is possible to provide a liquid crystal display element capable of high contrast and high speed response while performing multiplex driving. The value is extremely large.
【００５３】次に、本実施例に用いた液晶材料のポリス
チレン配向膜に対する表面アンカリングエネルギ強度を
測定する目的でホモジニアス配向セルを作製し、室温で
の表面アンカリングエネルギ強度を測定したところ、
２．３×１０-5［Ｊ／ｍ2］の値が得られた。Next, a homogeneous alignment cell was prepared for the purpose of measuring the surface anchoring energy intensity of the liquid crystal material used in this example with respect to the polystyrene alignment film, and the surface anchoring energy intensity at room temperature was measured.
A value of 2.3 × 10 −5 [J / m 2 ] was obtained.
【００５４】本実施例においては液晶の捻れ角を９０度
としたが、これにより本発明を何ら限定するものではな
い。In this embodiment, the twist angle of the liquid crystal is set to 90 degrees, but this does not limit the present invention in any way.
【００５５】また、視角依存性の改善や色相の改善等を
目的として、位相補償板を設けても良いことは言うまで
もない。Needless to say, a phase compensating plate may be provided for the purpose of improving the viewing angle dependency and the hue.
【００５６】（比較例１）配向膜材料としてポリイミド
（日産化学工業製配向膜塗料ＲＮ−７４７）を使用し、
スピンコート法により製膜後、１８０℃、１時間の硬化
処理を行うこと以外は実施例１と同様にしてＴＮ型液晶
表示素子Ｒ１を作製した。(Comparative Example 1) Polyimide (Nissan Chemical Industries alignment film paint RN-747) was used as an alignment film material.
After forming a film by spin coating, a TN liquid crystal display element R1 was produced in the same manner as in Example 1 except that a curing treatment was performed at 180 ° C. for 1 hour.
【００５７】次に、定法に従い、液晶表示素子Ｒ１の電
圧−透過率特性を３０Ｈｚ矩形波の電圧を印加しながら
測定した。結果を図４に示す。この図４から液晶表示素
子Ｒ１のγ値を求めると、γ＝１．２５であった。この
値では走査線本数６０本〜１００本程度の表示しかする
ことが出来ない。Next, the voltage-transmittance characteristic of the liquid crystal display element R1 was measured while applying a 30 Hz rectangular wave voltage according to a standard method. FIG. 4 shows the results. When the γ value of the liquid crystal display element R1 was determined from FIG. 4, γ = 1.25. With this value, it is possible to display only about 60 to 100 scanning lines.
【００５８】従って、ポリイミド配向膜を使用する従来
のＴＮ型液晶表示素子は、マルチプレックス駆動に適し
ておらず、ポリスチレン配向膜を使用する実施例１がマ
ルチプレックス駆動に適していることが認められる。Therefore, it is recognized that the conventional TN type liquid crystal display device using the polyimide alignment film is not suitable for multiplex driving, and that the embodiment 1 using the polystyrene alignment film is suitable for multiplex driving. .
【００５９】（比較例２）比較例２としてＳＴＮ型液晶
表示素子Ｒ２を以下の方法で作製した。尚、以下の方法
は一般的製造方法である。先ず、透明電極を有する２枚
のガラス基板上にポリイミド（ＪＳＲ製配向膜塗料ＡＬ
−５５１７）をスピンコート法にて塗布し、恒温槽中１
８０度、１時間硬化させる。その後、レーヨン製ラビン
グ布を用いて、一方のガラス基板（第１基板５に対応）
に図５に示すａ３方向にラビング処理を施し、他方のガ
ラス基板（第２基板６に対応）に図５に示すａ４方向に
ラビング処理を施す。そして、上記２枚のガラス基板
を、積水ファインケミカル（株）製スペーサ及びストラ
クトボンド３５２Ａ（三井東圧化学（株）製シール樹脂
の商品名）を用いて基板間隔が７．３μｍとなるように
貼り合わせ、液晶セル（液晶セル２に対応）を作成し
た。(Comparative Example 2) As Comparative Example 2, an STN type liquid crystal display element R2 was manufactured by the following method. The following method is a general production method. First, a polyimide (alignment film paint AL manufactured by JSR) was placed on two glass substrates having transparent electrodes.
-5517) by spin coating, and then
Cure at 80 degrees for 1 hour. Then, using a rubbing cloth made of rayon, one glass substrate (corresponding to the first substrate 5)
Is subjected to a rubbing process in the a3 direction shown in FIG. 5, and the other glass substrate (corresponding to the second substrate 6) is subjected to a rubbing process in the a4 direction shown in FIG. Then, the two glass substrates are attached using a spacer and Stract Bond 352A (trade name of seal resin manufactured by Mitsui Toatsu Chemicals, Inc.) so that the substrate interval becomes 7.3 μm using Sekisui Fine Chemical Co., Ltd. Together, a liquid crystal cell (corresponding to liquid crystal cell 2) was created.
【００６０】次に、カイラル材料としてコレステリルノ
ナノエートを添加してカイラルピッチが１０μｍになる
ように調製したメルク社製液晶ＺＬＩ−２２９３（ＮＩ
点＝８５度、Δｎ＝０．１３０）を、真空注入法にて液
晶セルに注入した。Next, a liquid crystal ZLI-2293 (NI, manufactured by Merck & Co., Ltd.) prepared by adding cholesteryl nonanoate as a chiral material to adjust the chiral pitch to 10 μm.
(Point = 85 degrees, Δn = 0.130) was injected into the liquid crystal cell by a vacuum injection method.
【００６１】その後、偏光板（偏光板３に対応）の吸収
軸方向ｃ１と偏光板（偏光板４に対応）の吸収軸方向ｃ
２が、図５に示す状態となるように、偏光板（偏光板３
に対応）と偏光板（偏光板４に対応）とを上記液晶セル
に貼り合わせ、液晶表示素子Ｒ２を作製した。尚、図５
中の数字は角度を表している。Thereafter, the absorption axis direction c1 of the polarizing plate (corresponding to the polarizing plate 3) and the absorption axis direction c of the polarizing plate (corresponding to the polarizing plate 4) are set.
2 is in a state shown in FIG.
And a polarizing plate (corresponding to the polarizing plate 4) were adhered to the liquid crystal cell to produce a liquid crystal display element R2. FIG.
The numbers inside represent angles.
【００６２】次に、定法に従い液晶表示素子Ｒ２の電圧
−透過率特性を３０Ｈｚ矩形波の電圧を印加しながら測
定した。結果を図６に示す。Next, the voltage-transmittance characteristic of the liquid crystal display element R2 was measured while applying a rectangular wave voltage of 30 Hz according to a standard method. FIG. 6 shows the results.
【００６３】また、液晶表示素子Ｒ２について、３０Ｈ
ｚ矩形波の電圧を１．８Ｖから２．２Ｖへ、及び２．２
Ｖから１．８Ｖへ電圧値を変化させ、そのときの応答時
間を測定した。その結果、応答時間（立ち上がり時間と
立ち下がり時間との総和）は２８０ミリ秒であった。ま
た、このときのコントラスト比は１５：１となった。Further, for the liquid crystal display element R2, 30H
The voltage of the z square wave was changed from 1.8V to 2.2V, and 2.2
The voltage value was changed from V to 1.8 V, and the response time at that time was measured. As a result, the response time (total of the rise time and the fall time) was 280 milliseconds. The contrast ratio at this time was 15: 1.
【００６４】よって、液晶表示素子Ａと液晶表示素子Ｒ
２とは、急峻な電圧−透過率特性を有する点おいては共
通するが、液晶表示素子Ａは液晶表示素子Ｒ２に比べて
応答性及びコントラスト比が格段向上していることが認
められる。Therefore, the liquid crystal display elements A and R
2 is common in that it has a steep voltage-transmittance characteristic, but it can be recognized that the liquid crystal display element A has much improved responsiveness and contrast ratio as compared with the liquid crystal display element R2.
【００６５】（実施例２）この実施例２に係る液晶表示
素子Ｂは、配向膜を光配向法を用いて配向処理したこと
を特徴とするものである。液晶表示素子Ｂを以下の方法
で作製した。先ず、走査電極７が形成されたガラスから
成る第１基板５上に、ポリビニルシンナメートの２ｗ
ｔ．％溶液（モノクロロベンゼンとジクロロメタンの
１：１混合溶液中に希釈）をスピンコート法にて塗布
し、この塗布された第１基板５を恒温槽中で、１００
度、１時間乾燥させる。その後、図７に示すように、参
照符号３０の方向に偏光した紫外線３１を照射する紫外
線照射装置（図示せず）を第１基板５上に配置し、波長
３６５ｎｍの偏光紫外線光３１を３０分間照射した。こ
のときの紫外線照射方向θは９０度であり、照射光強度
は１ｍＷ／ｃｍ2であった。更に、照射角度θ＝４５度
で、同様の偏光紫外線を３分間照射した。このように２
段階照射するのは、以下の理由による。即ち、照射角度
θ＝９０度の照射により配向膜分子鎖を一方向に並ばせ
る。次いで、照射角度θ＝４５度の照射により、配向膜
分子の分布状態を、同一方向に傾斜した液晶分子の配向
が得られるような分布状態へ変化させるためである。紫
外線３１の偏光方向３０が図７に示す方向であれば、液
晶分子は図７の左右方向に並び、しかも左端が基板から
離れる状態に配向することになる。(Embodiment 2) The liquid crystal display element B according to Embodiment 2 is characterized in that an alignment film is subjected to an alignment treatment using a photo-alignment method. The liquid crystal display element B was manufactured by the following method. First, 2 w of polyvinyl cinnamate is placed on a first substrate 5 made of glass on which the scanning electrodes 7 are formed.
t. % Solution (diluted in a 1: 1 mixed solution of monochlorobenzene and dichloromethane) is applied by spin coating, and the applied first substrate 5 is placed in a thermostat at 100%.
Dry for 1 hour. Thereafter, as shown in FIG. 7, an ultraviolet irradiation device (not shown) for irradiating ultraviolet light 31 polarized in the direction of reference numeral 30 is arranged on the first substrate 5, and polarized ultraviolet light 31 having a wavelength of 365 nm is applied for 30 minutes. Irradiated. At this time, the ultraviolet irradiation direction θ was 90 degrees, and the irradiation light intensity was 1 mW / cm 2 . Further, the same polarized ultraviolet light was irradiated for 3 minutes at an irradiation angle θ = 45 degrees. Thus 2
The step irradiation is performed for the following reason. That is, the molecular chains of the alignment film are aligned in one direction by the irradiation at the irradiation angle θ = 90 degrees. Then, by the irradiation at the irradiation angle θ = 45 degrees, the distribution state of the alignment film molecules is changed to a distribution state in which the alignment of the liquid crystal molecules inclined in the same direction can be obtained. If the polarization direction 30 of the ultraviolet light 31 is the direction shown in FIG. 7, the liquid crystal molecules are aligned in the left-right direction in FIG. 7, and the left end is oriented away from the substrate.
【００６６】第２基板６についても、上記と同様に配向
膜材料としてポリビニルシンナメートを使用し、且つ光
配向法により配向膜の配向処理を行った。次いで、第１
基板５と第２基板６とを、スペーサ１３（積水ファイン
ケミカル（株）製）、及びシール材１２（商品名：スト
ラクトボンド３５２Ａ（三井東圧化学（株）製）を用い
て基板間隔が５．０μｍとなるように貼り合わせ、液晶
セル２を作製した。As for the second substrate 6, polyvinyl cinnamate was used as the alignment film material and the alignment processing of the alignment film was performed by the optical alignment method in the same manner as described above. Then the first
The substrate 5 and the second substrate 6 are separated by a spacer 13 using a spacer 13 (manufactured by Sekisui Fine Chemical Co., Ltd.) and a sealing material 12 (trade name: Stract Bond 352A (manufactured by Mitsui Toatsu Chemicals, Inc.)). The liquid crystal cell 2 was manufactured by bonding together to a thickness of 0 μm.
【００６７】次に、カイラル材料としてコレステリルノ
ナノエートを添加してカイラルピッチが４０μｍになる
ように調製したメルク社製液晶ＺＬＩ−４７９２（ＮＩ
点＝９１度、Δｎ＝０．０９４）を、真空注入法にて液
晶セル２に注入した。Next, cholesteryl nonanoate as a chiral material was added to adjust the liquid crystal ZLI-4792 (NI
(Point = 91 degrees, Δn = 0.094) was injected into the liquid crystal cell 2 by a vacuum injection method.
【００６８】その後、偏光板３の偏光軸方向ｂ１と偏光
板４の偏光軸方向ｂ２が、図８に示す状態となるよう
に、偏光板３と偏光板４とを液晶セル２に貼り合わせて
本実施例の液晶表示素子Ｂを作成した。尚、図８におい
て、ｄ１は第１基板５界面近傍の液晶の配向方向を示
し、ｄ２は第２基板６界面近傍の液晶の配向方向を示し
ている。また、配向方向ｄ１，ｄ２の矢印は、矢印の方
向に向かって液晶分子が基板から離れるように配向して
いることを表している。Then, the polarizing plate 3 and the polarizing plate 4 are bonded to the liquid crystal cell 2 such that the polarizing axis direction b1 of the polarizing plate 3 and the polarizing axis direction b2 of the polarizing plate 4 are in the state shown in FIG. A liquid crystal display element B of this example was produced. In FIG. 8, d1 indicates the alignment direction of the liquid crystal near the interface of the first substrate 5, and d2 indicates the alignment direction of the liquid crystal near the interface of the second substrate 6. The arrows in the alignment directions d1 and d2 indicate that the liquid crystal molecules are oriented so as to move away from the substrate in the direction of the arrows.
【００６９】次に、定法に従い、本実施例の液晶表示素
子Ｂの電圧−透過率特性を３０Ｈｚ矩形波の電圧を印加
しながら測定した。結果を図９に示す。この図９よりγ
値を求めると、γ＝１．０４であった。このようにし
て、ＴＮ型液晶表示素子であるにも拘わらず急峻な電圧
−透過率特性を有する液晶表示素子Ｂが得られた。Next, the voltage-transmittance characteristic of the liquid crystal display element B of this example was measured according to a conventional method while applying a voltage of a 30 Hz rectangular wave. FIG. 9 shows the results. From FIG. 9, γ
The calculated value was γ = 1.04. Thus, a liquid crystal display element B having a steep voltage-transmittance characteristic was obtained despite being a TN type liquid crystal display element.
【００７０】また、実施例１と同様の手法にて液晶材料
のポリビニルシンナメート配向膜に対する表面アンカリ
ング強度を測定したところ、１．６×１０-5［Ｊ／
ｍ2］の値が得られた。When the surface anchoring strength of the liquid crystal material to the polyvinyl cinnamate alignment film was measured in the same manner as in Example 1, 1.6 × 10 −5 [J /
m 2 ] was obtained.
【００７１】尚、実施例１に比べて表面アンカリング強
度が小さいにも拘わらず、γ値が小さくならないのは、
プレチルト角が小さいことによるものと思われる。The reason why the γ value does not decrease in spite of the lower surface anchoring strength as compared with the first embodiment is that
This is probably due to the small pretilt angle.
【００７２】（実施例３）この実施例３に係る液晶表示
素子Ｃは、配向膜をＬＢ法により作製したものであるこ
とを特徴とする。走査電極７が形成されたガラスから成
る第１基板５上に、（化１）で示されるポリイミド分子
をＬＢ法にて１５層累積し、恒温槽中１００度、１時間
乾燥させる。こうして、第１基板５に配向膜９を形成し
た。信号電極８が形成されたガラスから成る第２基板６
についても、上記と同様の方法で配向膜１０を形成し
た。次いで、第１基板５と第２基板６とを、スペーサ１
３（積水ファインケミカル（株）製）、及びシール材１
２（商品名：ストラクトボンド３５２Ａ（三井東圧化学
（株）製）を用いて基板間隔が５．０μｍとなるように
貼り合わせ、液晶セル２を作製した。(Embodiment 3) The liquid crystal display element C according to Embodiment 3 is characterized in that an alignment film is manufactured by the LB method. On the first substrate 5 made of glass on which the scanning electrodes 7 are formed, 15 layers of polyimide molecules represented by the following formula (1) are accumulated by the LB method, and dried in a thermostat at 100 ° C. for 1 hour. Thus, the alignment film 9 was formed on the first substrate 5. Second substrate 6 made of glass on which signal electrodes 8 are formed
The alignment film 10 was formed in the same manner as described above. Next, the first substrate 5 and the second substrate 6 are
3 (manufactured by Sekisui Fine Chemical Co., Ltd.) and sealing material 1
2 (trade name: Struct Bond 352A (manufactured by Mitsui Toatsu Chemicals, Inc.)) so that the distance between the substrates was 5.0 μm, thereby producing a liquid crystal cell 2.
【化１】 Embedded image
【００７３】次に、カイラル材料としてコレステリルノ
ナノエートを添加してカイラルピッチが４０μｍになる
ように調製したメルク社製液晶ＺＬＩ−４７９２（ＮＩ
点（ネマティック・アイソトロピック転移温度）＝９１
度、Δｎ＝０．０９４）を、真空注入法にて液晶セル２
に注入した。Next, cholesteryl nonanoate was added as a chiral material, and a liquid crystal ZLI-4792 (NI, manufactured by Merck & Co., Ltd.) was prepared to have a chiral pitch of 40 μm.
Point (nematic-isotropic transition temperature) = 91
Degree, Δn = 0.094) by the vacuum injection method.
Was injected.
【００７４】その後、偏光板３の偏光軸方向ｂ１と偏光
板４の偏光軸方向ｂ２が、図１０に示す状態となるよう
に、偏光板３と偏光板４とを液晶セル２に貼り合わせて
本実施例の液晶表示素子Ｃを作成した。尚、図１０にお
いて、ｅ１は第１基板５の引き上げ方向、従って第１基
板５界面近傍の液晶の配向方向を示し、ｅ２は第２基板
６の引き上げ方向、従って第２基板６界面近傍の液晶の
配向方向を示している。また、引き上げ方向ｅ１，ｅ２
の矢印は、基板の引き上げ方向を表している。Then, the polarizing plate 3 and the polarizing plate 4 are bonded to the liquid crystal cell 2 so that the polarizing axis direction b1 of the polarizing plate 3 and the polarizing axis direction b2 of the polarizing plate 4 are in the state shown in FIG. A liquid crystal display element C of this example was produced. In FIG. 10, e1 indicates the pulling direction of the first substrate 5, that is, the orientation direction of the liquid crystal near the interface of the first substrate 5, and e2 indicates the pulling direction of the second substrate 6, and therefore, the liquid crystal near the interface of the second substrate 6. Are shown. Further, the lifting directions e1 and e2
Arrows indicate the direction in which the substrate is pulled up.
【００７５】次に、定法に従い、本発明の液晶表示素子
Ｃの電圧−透過率特性を３０Ｈｚ矩形波の電圧を印加し
ながら測定した。結果を図１１に示す。この図１１より
γ値を求めると、γ＝１．０６であった。このようにし
て、ＴＮ型液晶表示素子であるにも拘わらず急峻な電圧
−透過率特性を有する液晶表示素子Ｃが得られた。Next, the voltage-transmittance characteristic of the liquid crystal display element C of the present invention was measured while applying a 30 Hz rectangular wave voltage according to a conventional method. The results are shown in FIG. The γ value obtained from FIG. 11 was γ = 1.06. Thus, a liquid crystal display element C having steep voltage-transmittance characteristics was obtained despite being a TN type liquid crystal display element.
【００７６】また、実施例１と同様の手法にて液晶材料
のポリイミドＬＢ膜に対する表面アンカリングエネルギ
を測定したところ、３．３×１０-6［Ｊ／ｍ2］の値が
得られた。When the surface anchoring energy of the liquid crystal material for the polyimide LB film was measured in the same manner as in Example 1, a value of 3.3 × 10 −6 [J / m 2 ] was obtained.
【００７７】（実施例４）配向膜のラビング強度が異な
ること以外、実施例１と同様にして液晶表示素子Ｄ、
Ｅ、Ｆ、Ｇを作製し、そのγ値を測定した。表面アンカ
リング強度の測定値と併せて表１に示す。Example 4 A liquid crystal display element D was prepared in the same manner as in Example 1 except that the rubbing strength of the alignment film was different.
E, F, and G were prepared, and their γ values were measured. The results are shown in Table 1 together with the measured values of the surface anchoring strength.
【表１】 [Table 1]
【００７８】表１より明らかなように、表面アンカリン
グ強度が１．０×１０-4Ｊ／ｍ2以下の液晶表示素子
Ｄ，Ｅ，Ｆは高い急峻性を示しているが、表面アンカリ
ング強度が１．０×１０-4Ｊ／ｍ2以上の液晶表示素子
Ｇは急峻性が悪い。このことから、表面アンカリング強
度を１．０×１０-4Ｊ／ｍ2以下とすることにより、急
峻な電圧−透過率特性を有し、マルチプレックス駆動に
適した液晶表示素子が得られることが認められる。As is clear from Table 1, the liquid crystal display devices D, E, and F having a surface anchoring strength of 1.0 × 10 −4 J / m 2 or less show high steepness, but have a high surface anchoring. The liquid crystal display element G having an intensity of 1.0 × 10 −4 J / m 2 or more has poor steepness. From this, it can be seen that by setting the surface anchoring strength to 1.0 × 10 −4 J / m 2 or less, a liquid crystal display element having steep voltage-transmittance characteristics and suitable for multiplex driving can be obtained. Is recognized.
【００７９】（実施例５）この実施例５は、捻れ角を大
きくしたＳＴＮ型液晶表示素子において、表面アンカリ
ング強度を１．０×１０-4Ｊ／ｍ2以下としたことを特
徴とする。液晶捻れ角と捻れ方向が異なること以外、実
施例４の液晶表示素子Ｆと同一条件で液晶表示素子Ｈを
作製した。このときの偏光板貼合角度の設定を図１２に
示す。尚、図１２において、ａ５は第１基板５のラビン
グ方向、ａ６は第２基板６のラビング方向、ｂ３は偏光
板３の偏光軸方向、ｂ４は偏光板４の偏光軸方向を示し
ている。また、図１２において、数字は角度を表してい
る。(Embodiment 5) This embodiment 5 is characterized in that the surface anchoring strength of the STN type liquid crystal display element having a large twist angle is 1.0 × 10 −4 J / m 2 or less. . A liquid crystal display element H was manufactured under the same conditions as the liquid crystal display element F of Example 4 except that the liquid crystal twist angle and the twist direction were different. FIG. 12 shows the setting of the polarizing plate bonding angle at this time. In FIG. 12, a5 indicates the rubbing direction of the first substrate 5, a6 indicates the rubbing direction of the second substrate 6, b3 indicates the polarization axis direction of the polarizing plate 3, and b4 indicates the polarization axis direction of the polarizing plate 4. In FIG. 12, the numerals represent angles.
【００８０】本液晶表示素子Ｈは、逆ツイストドメイン
及び電圧印加時におけるストライプドメインの発生が認
められず、優れた配向性能が確認された。これは、本液
晶表示素子に用いられる配向膜の表面アンカリング強度
が小さいため、液晶分子に対する束縛が小さいためと推
定される。In the present liquid crystal display element H, generation of a reverse twist domain and stripe domain upon application of a voltage was not recognized, and excellent alignment performance was confirmed. This is presumed to be because the surface anchoring strength of the alignment film used in the present liquid crystal display element is small, and the constraint on the liquid crystal molecules is small.
【００８１】[0081]
【発明の効果】以上のように本発明によれば、ＴＮ型液
晶表示素子であるにも拘わらず、急峻な電圧−透過率特
性を有し、マルチプレックス駆動が可能な液晶表示素子
を実現することができる。As described above, according to the present invention, a liquid crystal display device having a steep voltage-transmittance characteristic and capable of multiplex driving, despite being a TN type liquid crystal display device, is realized. be able to.
【００８２】また、捻れ角がＳＴＮ型液晶表示素子より
も小さいため、ｄ／ｐマージンが広く（即ち、液晶材料
及び配向膜材料の選択範囲が広く）、高速・高コントラ
ストな液晶表示素子を実現することができる。Further, since the twist angle is smaller than that of the STN type liquid crystal display device, a d / p margin is wide (that is, the selection range of the liquid crystal material and the alignment film material is wide), and a high speed and high contrast liquid crystal display device is realized. can do.
【図１】本発明の実施の形態に係る液晶表示素子の構成
を簡略化した断面図である。FIG. 1 is a simplified cross-sectional view of a configuration of a liquid crystal display device according to an embodiment of the present invention.
【図２】本発明の実施例１に係る液晶表示素子の各光学
要素の配置状態を示す図である。FIG. 2 is a diagram illustrating an arrangement state of each optical element of the liquid crystal display element according to the first embodiment of the present invention.
【図３】本発明の実施例１に係る液晶表示素子の電圧−
透過率特性を示す図である。FIG. 3 is a graph showing a voltage-
FIG. 3 is a diagram illustrating transmittance characteristics.
【図４】比較例１における液晶表示素子の電圧−透過率
特性を示す図である。FIG. 4 is a diagram showing voltage-transmittance characteristics of a liquid crystal display element in Comparative Example 1.
【図５】比較例２における各光学要素の配置状態を示す
図である。FIG. 5 is a diagram showing an arrangement state of each optical element in Comparative Example 2.
【図６】比較例２における液晶表示素子の電圧−透過率
特性を示す図である。FIG. 6 is a diagram showing voltage-transmittance characteristics of a liquid crystal display element in Comparative Example 2.
【図７】本発明の実施例２における偏光紫外線の照射方
法を説明するための図である。FIG. 7 is a diagram for explaining a method of irradiating polarized ultraviolet light in Example 2 of the present invention.
【図８】本発明の実施例２における各光学要素の配置状
態を示す図である。FIG. 8 is a diagram showing an arrangement state of each optical element in Embodiment 2 of the present invention.
【図９】本発明の実施例２における液晶表示素子の電圧
−透過率特性を示す図である。FIG. 9 is a diagram showing a voltage-transmittance characteristic of the liquid crystal display element in Example 2 of the present invention.
【図１０】本発明の実施例３における各光学要素の配置
状態を示す図である。FIG. 10 is a diagram showing an arrangement state of each optical element in Embodiment 3 of the present invention.
【図１１】本発明の実施例３における液晶表示素子の電
圧−透過率特性を示す図である。FIG. 11 is a view showing a voltage-transmittance characteristic of a liquid crystal display element in Example 3 of the present invention.
【図１２】本発明の実施例５における各光学要素の配置
状態を示す図である。FIG. 12 is a diagram showing an arrangement state of each optical element in Embodiment 5 of the present invention.
２：液晶セル ３，４： 偏光板 ５：第１基板 ６：第２基板 ７：走査電極 ８：信号電極 ９，１０：配向膜 １１：液晶材料 ａ１〜ａ６：基板のラビング方向 ｂ１〜ｂ４：偏光板の偏光軸方向 ｃ１〜ｃ２：偏光板の吸収軸方向 ｄ１，ｄ２：基板表面での液晶配向方向 ｅ１，ｅ２：基板引き上げ方向 2: liquid crystal cells 3, 4: polarizing plate 5: first substrate 6: second substrate 7: scanning electrode 8: signal electrode 9, 10: alignment film 11: liquid crystal material a1 to a6: rubbing direction of substrate b1 to b4: Polarization axis direction of polarizing plate c1 to c2: Absorption axis direction of polarizing plate d1, d2: Liquid crystal alignment direction on substrate surface e1, e2: Substrate lifting direction
Claims (6)
イプ状走査電極と、走査電極上に形成される配向膜とを
有する第１基板と、 前記走査電極と交差するように配置され且つ画像信号電
圧が印加される複数のストライプ状信号電極と、信号電
極上に形成される配向膜とを有する第２基板と、 第１基板と第２基板との間に封入され、且つ第１及び第
２基板のうちの一方から他方に向かって捻れ配向状態と
なっている液晶材料と、を含むツイステッドネマティッ
ク型液晶表示素子であって、 前記液晶材料の前記各配向膜に対する表面アンカリング
強度が１．０×１０-4Ｊ／ｍ2以下であることを特徴と
する液晶表示素子。A first substrate having a plurality of stripe-shaped scanning electrodes to which a scanning signal voltage is applied, an alignment film formed on the scanning electrodes, and an image signal arranged to intersect the scanning electrodes. A second substrate having a plurality of striped signal electrodes to which a voltage is applied, and an alignment film formed on the signal electrodes; a first substrate and a second substrate sealed between the first substrate and the second substrate; A twisted nematic liquid crystal display device comprising: a liquid crystal material in a twisted alignment state from one of the substrates toward the other; wherein the surface anchoring strength of the liquid crystal material with respect to each of the alignment films is 1.0. the liquid crystal display element characterized by × is 10 -4 J / m 2 or less.
ることを特徴とする請求項１記載の液晶表示素子。2. The liquid crystal display device according to claim 1, wherein said alignment film is made of a polystyrene derivative.
導体から成り、且つこの配向膜は光配向法により配向処
理がなれていることを特徴とする請求項１記載の液晶表
示素子。3. The liquid crystal display device according to claim 1, wherein the alignment film is made of a polyvinyl cinnamate derivative, and the alignment film has been subjected to an alignment process by a photo alignment method.
徴とする請求項１乃至３の何れかに記載の液晶表示素
子。4. The liquid crystal display device according to claim 1, wherein a twist angle of the liquid crystal is approximately 90 degrees.
であって、 ＬＢ（ラングミュア・ブロジェット）法を用いて、走査
電極及び信号電極の少なくとも一方の電極上に配向膜を
成膜する工程を含むことを特徴とする液晶表示素子の製
造方法。5. The method for manufacturing a liquid crystal display element according to claim 1, wherein an alignment film is formed on at least one of the scanning electrode and the signal electrode using an LB (Langmuir-Blodgett) method. A method for manufacturing a liquid crystal display element, comprising the steps of:
であって、 光配向法を用いて、走査電極及び信号電極の少なくとも
一方の電極上に形成された配向膜を配向処理する工程を
含むことを特徴とする液晶表示素子の製造方法。6. The method for manufacturing a liquid crystal display device according to claim 1, wherein the step of aligning an alignment film formed on at least one of the scanning electrode and the signal electrode by using a photo alignment method. A method for manufacturing a liquid crystal display element, comprising: