JP2000244137A - Fire extinguishing housing - Google Patents
Fire extinguishing housingInfo
- Publication number
- JP2000244137A JP2000244137A JP4667199A JP4667199A JP2000244137A JP 2000244137 A JP2000244137 A JP 2000244137A JP 4667199 A JP4667199 A JP 4667199A JP 4667199 A JP4667199 A JP 4667199A JP 2000244137 A JP2000244137 A JP 2000244137A
- Authority
- JP
- Japan
- Prior art keywords
- fire
- sheet
- housing
- heat
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、内部に発熱源とな
る機器及び／又は高電圧を発生する機器が収納される消
火性筐体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fire extinguisher housing in which equipment serving as a heat source and / or equipment generating a high voltage is housed.
【０００２】[0002]
【従来の技術】従来より、例えばテレビ受像機のよう
に、その筐体内部にコンデンサーのような発熱源やトラ
ンスのような高電圧部品を有する家電製品、複写機、各
種制御機器では、筐体内部に堆積した埃や塵が発端とな
って出火する恐れがある。このような事態に対処するた
めに、筐体内部の大半の部品を難燃化することによっ
て、機器自身が燃焼するのを防止してきた。しかしなが
ら、このような難燃化の手段だけでは機器からの出火を
完全に消火することができず、家電製品が火元とみられ
る火災が依然として報告されている。2. Description of the Related Art Conventionally, home appliances, copying machines, and various control devices, such as television receivers, having a heat source such as a condenser and high-voltage parts such as a transformer inside the housing have been used for housings. Dust and dust accumulated inside may start and cause a fire. In order to cope with such a situation, most of the components inside the housing are made flame-retardant, thereby preventing the device itself from burning. However, fires from equipment cannot be completely extinguished only by such means of flame retardation, and fires in which home appliances are considered to be the source of fire are still being reported.
【０００３】これに対して、特開平１０−１４５７０３
号公報には、筐体通気口に空気清浄フィルターを装備し
て筐体内部へ埃や塵が侵入するのを防止したり、特開平
８−１１７３５３号公報には、筐体内部に消火剤を内蔵
する消火装置を装備する方法が提案されている。しかし
ながら、上記いずれの方法も相当の効果は期待される
が、コストが高い装置を使用する上に、スリム化が求め
られる製品においてこれらの付帯装置のスペースを筐体
内部に確保することは困難であった。On the other hand, Japanese Patent Application Laid-Open No. 10-145703 discloses
In Japanese Patent Application Laid-Open No. H08-117353, an air purifying filter is provided in a housing air vent to prevent dust and dirt from entering the inside of the housing. A method of equipping a built-in fire extinguisher has been proposed. However, although any of the above methods is expected to have a considerable effect, it is difficult to secure a space for these auxiliary devices inside the housing in a product that requires slimness in addition to using a high-cost device. there were.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、上記
問題点に鑑み、低コストで省スペース的な部材を配置す
ることにより、機器からの出火を効果的に消火しうる消
火性筐体を提供することにある。SUMMARY OF THE INVENTION In view of the above problems, an object of the present invention is to provide a fire-extinguishing housing capable of effectively extinguishing fire from equipment by arranging low-cost and space-saving members. Is to provide.
【０００５】[0005]
【課題を解決するための手段】本発明の消火性筐体は、
内部に発熱源となる機器及び／又は高電圧を発生する機
器が収納される筐体の内面に、耐火膨張性シートが配置
されてなることを特徴とする。The fire extinguisher casing of the present invention comprises:
A fire-resistant expansion sheet is disposed on an inner surface of a housing in which a device serving as a heat source and / or a device generating a high voltage is stored.
【０００６】本発明で用いられる筐体は、内部に発熱源
となる機器及び／又は高電圧を発生する機器が収納され
るものであれば、特に制限がなく、例えば、テレビ受像
機、複写機、オーディオ機器、電子レンジ、各種制御機
器等に用いられる筐体が挙げられる。[0006] The housing used in the present invention is not particularly limited as long as it can house therein a device serving as a heat source and / or a device generating a high voltage. For example, a television receiver, a copying machine, etc. And housings used for audio equipment, microwave ovens, various control devices, and the like.
【０００７】本発明の消火性筐体を、例えばテレビ受像
機の筐体に応用する場合について、図面を参照しながら
説明する。図１（イ）はテレビ受像機の主要部のみを示
す模式断面図であり、図１（ロ）はテレビ受像機の背面
図である。図１（イ）及び（ロ）において、１はテレビ
受像機、２は筐体、３は通気口、４はＣＲＴをそれぞれ
示す。A case where the fire extinguisher casing of the present invention is applied to, for example, a casing of a television receiver will be described with reference to the drawings. FIG. 1A is a schematic sectional view showing only a main part of the television receiver, and FIG. 1B is a rear view of the television receiver. 1A and 1B, reference numeral 1 denotes a television receiver, 2 denotes a housing, 3 denotes a vent, and 4 denotes a CRT.
【０００８】本発明において、耐火膨張性シートは、テ
レビ受像機１の筐体２内面に配置される。耐火膨張性シ
ートを配置する箇所は、筐体２の内面全体が好ましく、
少なくとも、発熱源となる機器及び／又は高電圧を発生
する機器に対応する内面に配置することが好ましい。In the present invention, the fire-resistant inflatable sheet is disposed on the inner surface of the housing 2 of the television receiver 1. The place where the fire-resistant expansion sheet is arranged is preferably the entire inner surface of the housing 2.
It is preferable to arrange at least on an inner surface corresponding to a device serving as a heat source and / or a device generating a high voltage.
【０００９】また、この耐火膨張性シート５は、樹脂分
としてブチルゴムを使用する場合は、耐火膨張性シート
５自体が自己粘着性を有するので、特に接着剤を必要と
せずに筐体２の内面に貼着することができるが、自己粘
着性が不足する場合は通常接着剤（例えば、溶剤型ゴム
系接着剤）を使用して貼着してもよい。In the case where butyl rubber is used as the resin component, the fire-expandable sheet 5 has no self-adhesion because the fire-expandable sheet 5 itself has a self-adhesive property. However, when the self-adhesiveness is insufficient, a normal adhesive (for example, a solvent-type rubber-based adhesive) may be used.
【００１０】上記耐火膨張性シート５は、筐体２内面全
体に貼着することが好ましいが、図２に図１（イ）Ａ部
を拡大して示したように筐体２内部の上面部のみや、図
３に図１（イ）Ｂ部を拡大して示したように、通気口６
周辺に配置してもよい。The above-mentioned fire-resistant expansible sheet 5 is preferably adhered to the entire inner surface of the housing 2, but as shown in FIG. Only, as shown in FIG.
It may be arranged in the periphery.
【００１１】上面部のみに配置する場合は、耐火膨張性
シート５が落下して火元を遮断するように設計されてい
ることが好ましく、通気口６周辺に配置する場合は、そ
の位置に保持して通気口６を遮断するようになされてい
ることが好ましい。When the sheet is arranged only on the upper surface, it is preferable that the fire-resistant inflatable sheet 5 is designed to drop to block the source of fire. It is preferable that the ventilation port 6 be shut off.
【００１２】上記耐火膨張性シートは、熱可塑性樹脂及
び／又は合成ゴム、中和処理された熱膨張性黒鉛、並び
に、無機充填剤を含有する樹脂組成物（Ｉ）から形成さ
れるものが好ましい。The above-mentioned fire-resistant expansible sheet is preferably formed from a resin composition (I) containing a thermoplastic resin and / or a synthetic rubber, neutralized heat-expandable graphite, and an inorganic filler. .
【００１３】上記熱可塑性樹脂としては、特に限定され
ないが、例えば、エチレンの単独重合体、エチレンと他
のα−オレフィンとの共重合体等のポリエチレン系樹脂
が用いられる。The thermoplastic resin is not particularly limited. For example, a polyethylene resin such as a homopolymer of ethylene or a copolymer of ethylene and another α-olefin is used.
【００１４】上記ポリエチレン系樹脂としては、チーグ
ラー・ナッタ触媒、バナジウム触媒、４価の遷移金属を
含むメタロセン化合物等を重合触媒として重合されたも
のが挙げられるが、中でも、４価の遷移金属を含むメタ
ロセン化合物等を重合触媒として得られるものが好まし
い。Examples of the polyethylene resin include those obtained by polymerizing a Ziegler-Natta catalyst, a vanadium catalyst, a metallocene compound containing a tetravalent transition metal as a polymerization catalyst, and particularly containing a tetravalent transition metal. Those obtained using a metallocene compound or the like as a polymerization catalyst are preferred.
【００１５】上記メタロセン化合物に含まれる４価の遷
移金属としては、特に限定されず、例えば、チタン、ジ
ルコニウム、ハフニウム、ニッケル、パラジウム、白金
等が挙げられる。メタロセン化合物は、上記４価の遷移
金属に１つ又はそれ以上のシクロペンタジエニル環及び
その類縁体が、リガンド（配位子）として１つ又はそれ
以上存在する化合物をいう。The tetravalent transition metal contained in the metallocene compound is not particularly limited, and includes, for example, titanium, zirconium, hafnium, nickel, palladium, platinum and the like. A metallocene compound refers to a compound in which one or more cyclopentadienyl rings and their analogs are present as one or more ligands (ligands) in the tetravalent transition metal.
【００１６】上記４価の遷移金属を含むメタロセン化合
物等を重合触媒として得られるポリエチレン系樹脂の市
販品としては、例えば、ダウケミカル社製「商品名：Ｃ
ＧＣＴ」、「商品名：アフィニティー」、「商品名：エ
ンゲージ」；エクソンケミカル社製「商品名：ＥＸＴＲ
ＡＣＴ」等が挙げられる。Commercially available polyethylene resins obtained by using a metallocene compound containing a tetravalent transition metal or the like as a polymerization catalyst include, for example, "Product name: C" manufactured by Dow Chemical Company.
GCT "," Trade name: Affinity "," Trade name: Engage "; Exxon Chemical Co., Ltd." Trade name: EXTR "
ACT "and the like.
【００１７】上記熱可塑性樹脂は、単独で用いられても
よく、２種以上が併用されてもよい。熱可塑性樹脂の溶
融粘度、柔軟性、粘着性等を調節するため、２種以上を
ブレンドしたものをベース樹脂としてもよい。また、上
記熱可塑性樹脂には、耐火膨張性シートの耐火性能を阻
害しない範囲で、架橋や変性が施されてもよい。The above thermoplastic resins may be used alone or in combination of two or more. In order to adjust the melt viscosity, flexibility, tackiness and the like of the thermoplastic resin, a blend of two or more kinds may be used as the base resin. Further, the thermoplastic resin may be subjected to crosslinking or modification as long as the fire resistance of the fire-expandable sheet is not impaired.
【００１８】上記熱可塑性樹脂の架橋や変性を行なう時
期は、特に限定されず、予め架橋、変性した熱可塑性樹
脂を用いてもよく、熱可塑性樹脂に後述する無機充填剤
やリン化合物等他の成分を配合する際に同時に、又は、
熱可塑性樹脂に他の成分を配合した後で行なってもよ
い。The timing of crosslinking or modifying the thermoplastic resin is not particularly limited, and a previously crosslinked or modified thermoplastic resin may be used. At the same time as mixing the ingredients, or
It may be carried out after blending other components with the thermoplastic resin.
【００１９】上記熱可塑性樹脂の架橋方法については、
特に限定されず、通常行なわれている架橋方法、例え
ば、各種架橋剤、過酸化物等を使用する架橋；電子線照
射による架橋などが用いられる。Regarding the method for crosslinking the thermoplastic resin,
There is no particular limitation, and a commonly used crosslinking method, for example, crosslinking using various crosslinking agents, peroxides and the like; crosslinking by electron beam irradiation, and the like are used.
【００２０】上記合成ゴムとしては、特に制限されない
が、例えば、ブチルゴム（ＩＩＲ）が好適に用いられ
る。合成ゴムは上記熱可塑性樹脂と併用されてもよい。The synthetic rubber is not particularly limited, but, for example, butyl rubber (IIR) is preferably used. Synthetic rubber may be used in combination with the thermoplastic resin.
【００２１】上記中和処理された熱膨張性黒鉛とは、従
来公知の物質である熱膨張性黒鉛を中和処理したもので
ある。上記熱膨張性黒鉛は、天然鱗状グラファイト、熱
分解グラファイト、キッシュグラファイト等の粉末を、
濃硫酸、硝酸、セレン酸等の無機酸と、濃硝酸、過塩素
酸、過塩素酸塩、過マンガン酸塩、重クロム酸塩、過酸
化水素等の強酸化剤とで処理することにより生成するグ
ラファイト層間化合物であり、炭素の層状構造を維持し
たままの結晶化合物である。The neutralized heat-expandable graphite is obtained by neutralizing heat-expandable graphite which is a conventionally known substance. The above-mentioned heat-expandable graphite is a natural scale-like graphite, pyrolytic graphite, powder such as Kish graphite,
Produced by treating with inorganic acids such as concentrated sulfuric acid, nitric acid and selenic acid and strong oxidizing agents such as concentrated nitric acid, perchloric acid, perchlorate, permanganate, dichromate, hydrogen peroxide, etc. Is a crystalline intercalation compound that maintains the layered structure of carbon.
【００２２】上述のように酸処理して得られた熱膨張性
黒鉛は、更にアンモニア、脂肪族低級アミン、アルカリ
金属化合物、アルカリ土類金属化合物等で中和すること
により、上記中和処理された熱膨張性黒鉛が得られる。The heat-expandable graphite obtained by the acid treatment as described above is further neutralized with ammonia, an aliphatic lower amine, an alkali metal compound, an alkaline earth metal compound, etc. Heat-expandable graphite is obtained.
【００２３】上記脂肪族低級アミンとしては特に限定さ
れず、例えば、モノメチルアミン、ジメチルアミン、ト
リメチルアミン、エチルアミン、プロピルアミン、ブチ
ルアミン等が挙げられる。The aliphatic lower amine is not particularly restricted but includes, for example, monomethylamine, dimethylamine, trimethylamine, ethylamine, propylamine, butylamine and the like.
【００２４】上記アルカリ金属化合物及びアルカリ土類
金属化合物としては、特に限定されず、例えば、カリウ
ム、ナトリウム、カルシウム、バリウム、マグネシウム
等の水酸化物、酸化物、炭酸塩、硫酸塩、有機酸塩等が
挙げられる。The above-mentioned alkali metal compound and alkaline earth metal compound are not particularly restricted but include, for example, hydroxides, oxides, carbonates, sulfates and organic acid salts of potassium, sodium, calcium, barium, magnesium and the like. And the like.
【００２５】上記中和処理された熱膨張性黒鉛の市販品
としては、例えば、日本化成社製「ＣＡ−６０Ｓ」、東
ソー社製「ＧＲＥＰ−ＥＧ」等が挙げられる。Commercial products of the above-described neutralized heat-expandable graphite include, for example, "CA-60S" manufactured by Nippon Kasei Co., Ltd. and "GREP-EG" manufactured by Tosoh Corporation.
【００２６】上記中和処理された熱膨張性黒鉛の粒度
は、２０〜２００メッシュが好ましい。粒度が２００メ
ッシュより小さくなると黒鉛の膨張度が小さく、所定の
耐火断熱層が得られず、粒度が２０メッシュより大きく
なると、黒鉛の膨張度が大きいという利点はあるが、熱
可塑性樹脂及び／又は合成ゴムと混練する際に分散性が
悪くなり、物性の低下が避けられない。The particle size of the neutralized heat-expandable graphite is preferably 20 to 200 mesh. When the particle size is smaller than 200 mesh, the degree of expansion of graphite is small, and a predetermined refractory heat insulating layer cannot be obtained. When the particle size is larger than 20 mesh, there is an advantage that the degree of expansion of graphite is large, but thermoplastic resin and / or When kneaded with synthetic rubber, the dispersibility deteriorates, and a decrease in physical properties is inevitable.
【００２７】上記無機充填剤としては特に限定されず、
例えば、アルミナ、酸化亜鉛、酸化チタン、酸化カルシ
ウム、酸化マグネシウム、酸化鉄、酸化錫、酸化アンチ
モン、フェライト類等の金属酸化物；水酸化カルシウ
ム、水酸化マグネシウム、水酸化アルミニウム、ハイド
ロタルサイト等の含水無機物；塩基性炭酸マグネシウ
ム、炭酸カルシウム、炭酸マグネシウム、炭酸亜鉛、炭
酸ストロンチウム、炭酸バリウム等の金属炭酸塩；硫酸
カルシウム、石膏繊維、ケイ酸カルシウム等のカルシウ
ム塩；シリカ、珪藻土、ドーソナイト、硫酸バリウム、
タルク、クレー、マイカ、モンモリロナイト、ベントナ
イト、活性白土、セピオライト、イモゴライト、セリサ
イト、ガラス繊維、ガラスビーズ、シリカ系バルン、窒
化アルミニウム、窒化ホウ素、窒化けい素、カーボンブ
ラック、グラファイト、炭素繊維、炭素バルン、木炭粉
末、各種金属粉、チタン酸カリウム、硫酸マグネシウム
「ＭＯＳ」（商品名）、チタン酸ジルコン酸鉛、アルミ
ニウムボレート、硫化モリブデン、炭化ケイ素、ステン
レス繊維、ホウ酸亜鉛、各種磁性粉、スラグ繊維、フラ
イアッシュ、脱水汚泥等が挙げられる。これらは単独で
用いられてもよく、２種以上が併用されてもよい。The inorganic filler is not particularly limited.
For example, metal oxides such as alumina, zinc oxide, titanium oxide, calcium oxide, magnesium oxide, iron oxide, tin oxide, antimony oxide, and ferrites; calcium hydroxide, magnesium hydroxide, aluminum hydroxide, hydrotalcite, and the like. Hydrous inorganic substances; Basic magnesium carbonate, calcium carbonate, magnesium carbonate, zinc carbonate, strontium carbonate, barium carbonate and other metal carbonates; calcium salts such as calcium sulfate, gypsum fiber and calcium silicate; silica, diatomaceous earth, dawsonite, barium sulfate ,
Talc, clay, mica, montmorillonite, bentonite, activated clay, sepiolite, imogolite, sericite, glass fiber, glass beads, silica-based balun, aluminum nitride, boron nitride, silicon nitride, carbon black, graphite, carbon fiber, carbon balun , Charcoal powder, various metal powders, potassium titanate, magnesium sulfate "MOS" (trade name), lead zirconate titanate, aluminum borate, molybdenum sulfide, silicon carbide, stainless steel fiber, zinc borate, various magnetic powders, slag fiber , Fly ash, dehydrated sludge and the like. These may be used alone or in combination of two or more.
【００２８】上記無機充填剤としては、特に含水無機物
と金属炭酸塩との併用が好ましい。上記含水無機物及び
金属炭酸塩は、骨材的な働きをすることから、残渣強度
の向上や熱容量の増大に寄与すると考えられる。As the inorganic filler, a combination of a water-containing inorganic substance and a metal carbonate is particularly preferable. Since the above-mentioned hydrated inorganic substance and metal carbonate function as an aggregate, it is considered that they contribute to the improvement of residue strength and the increase of heat capacity.
【００２９】さらに、上記含水無機物は、加熱時の脱水
反応によって生成した水のために吸熱が起こり、温度上
昇が低減されて高い耐熱性が得られる点、及び、加熱残
渣として酸化物が残存し、これが骨材となって働くこと
で残渣強度が向上する点で特に好ましい。中でも、水酸
化マグネシウムと水酸化アルミニウムは、脱水効果を発
揮する温度領域が異なるため、併用すると脱水効果を発
揮する温度領域が広がり、より効果的な温度上昇抑制効
果が得られることから、併用することが好ましい。Further, the above-mentioned hydrated inorganic substance is endothermic due to water generated by a dehydration reaction during heating, and the temperature rise is reduced so that high heat resistance is obtained. Also, an oxide remains as a heating residue. This is particularly preferable in that it works as an aggregate to improve the residue strength. Among them, magnesium hydroxide and aluminum hydroxide are different in the temperature range in which the dehydrating effect is exerted, so that when used in combination, the temperature range in which the dehydrating effect is exerted expands, and a more effective temperature rise suppression effect is obtained, so that they are used together. Is preferred.
【００３０】上記無機充填剤の粒径としては、０．５〜
１００μｍが好ましく、より好ましくは１〜５０μｍで
ある。また、粒径の大きいものと粒径の小さいものとを
組み合わせて使用することによって、より高充填化でき
るので好ましい。The inorganic filler has a particle size of 0.5 to
It is preferably 100 μm, more preferably 1 to 50 μm. In addition, it is preferable to use a combination of a material having a large particle size and a material having a small particle size, since a higher filling can be achieved.
【００３１】上記含水無機物の市販品としては、例え
ば、水酸化アルミニウムとして、粒径１μｍの「Ｈ−４
２Ｍ」（昭和電工社製）、粒径１８μｍの「Ｈ−３１」
（昭和電工社製）が挙げられる。As a commercially available product of the above-mentioned hydrous inorganic material, for example, aluminum hydroxide “H-4” having a particle size of 1 μm is used.
2M "(manufactured by Showa Denko KK)," H-31 "with a particle size of 18 µm
(Manufactured by Showa Denko KK).
【００３２】上記炭酸カルシウムの市販品としては、例
えば、粒径１．８μｍの「ホワイトンＳＢ赤」（白石カ
ルシウム社製）、粒径８μｍの「ＢＦ３００」（白石カ
ルシウム社製）等が挙げられる。Examples of commercially available calcium carbonate include "Whiteton SB Red" having a particle size of 1.8 μm (manufactured by Shiraishi Calcium Co., Ltd.) and "BF300" having a particle size of 8 μm (manufactured by Shiraishi Calcium Co., Ltd.). .
【００３３】上記樹脂組成物（Ｉ）における中和処理さ
れた熱膨張性黒鉛の配合量は、熱可塑性樹脂及び／又は
合成ゴム１００重量部に対して１０〜３００重量部が好
ましい。配合量が１０重量部未満では十分な耐火性を有
する耐火膨張性シートが得られず、３００重量部を超え
ると耐火膨張性シートの機械的物性が低下する。The amount of the neutralized thermally expandable graphite in the resin composition (I) is preferably 10 to 300 parts by weight based on 100 parts by weight of the thermoplastic resin and / or synthetic rubber. If the amount is less than 10 parts by weight, a fire-resistant expansion sheet having sufficient fire resistance cannot be obtained, and if it exceeds 300 parts by weight, the mechanical properties of the fire-resistant expansion sheet deteriorate.
【００３４】上記樹脂組成物（Ｉ）における無機充填剤
の配合量は、熱可塑性樹脂及び／又は合成ゴム１００重
量部に対して５０〜５００重量部が好ましい。配合量
が、５０重量部未満では十分な耐火性を有する耐火膨張
性シートが得られず、５００重量部を超えると耐火膨張
性シートの機械的物性が低下する。The amount of the inorganic filler in the resin composition (I) is preferably 50 to 500 parts by weight based on 100 parts by weight of the thermoplastic resin and / or synthetic rubber. If the amount is less than 50 parts by weight, a fire-resistant expansion sheet having sufficient fire resistance cannot be obtained, and if it exceeds 500 parts by weight, the mechanical properties of the fire-resistant expansion sheet deteriorate.
【００３５】上記耐火膨張性シートは、熱可塑性樹脂及
び／又は合成ゴム、リン化合物、中和処理された熱膨張
性黒鉛、並びに、無機充填剤を含有する樹脂組成物（I
I）から形成されるものであってもよい。The above-mentioned fire-expandable sheet is a resin composition (I) containing a thermoplastic resin and / or a synthetic rubber, a phosphorus compound, neutralized heat-expandable graphite, and an inorganic filler.
It may be formed from I).
【００３６】上記熱可塑性樹脂、合成ゴム、中和処理さ
れた熱膨張性黒鉛及び無機充填剤としては、上記樹脂組
成物（Ｉ）と同様のものが用いられる。上記樹脂組成物
（II）は樹脂組成物（Ｉ）にリン化合物を加えているの
で、燃焼残渣の強度が向上するため、通気口を塞いで酸
素を遮断する上で有利である。The same thermoplastic resin, synthetic rubber, neutralized heat-expandable graphite and inorganic filler as those used in the resin composition (I) are used. Since the resin composition (II) contains a phosphorus compound in the resin composition (I), the strength of the combustion residue is improved, which is advantageous in blocking oxygen by closing the ventilation port.
【００３７】上記リン化合物としては特に限定されず、
例えば、赤リン；トリフェニルホスフェート、トリクレ
ジルホスフェート、トリキシレニルホスフェート、クレ
ジルジフェニルホスフェート、キシレニルジフェニルホ
スフェート等の各種リン酸エステル；リン酸ナトリウ
ム、リン酸カリウム、リン酸マグネシウム等のリン酸金
属塩；ポリリン酸アンモニウム類；下記一般式（１）で
表される化合物等が挙げられる。これらのうち、耐火性
の観点から、赤リン、ポリリン酸アンモニウム類、及
び、下記一般式（１）で表される化合物が好ましく、性
能、安全性、コスト等の点において、ポリリン酸アンモ
ニウム類がより好ましい。The phosphorus compound is not particularly limited.
For example, red phosphorus; various phosphates such as triphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, cresyl diphenyl phosphate, xylendiphenyl phosphate; phosphorus such as sodium phosphate, potassium phosphate, and magnesium phosphate Acid metal salts; ammonium polyphosphates; and compounds represented by the following general formula (1). Among these, from the viewpoint of fire resistance, red phosphorus, ammonium polyphosphates, and compounds represented by the following general formula (1) are preferable. In terms of performance, safety, cost, and the like, ammonium polyphosphates are preferable. More preferred.
【００３８】[0038]
【化１】 Embedded image
【００３９】式中、Ｒ1 、Ｒ3 は、水素、炭素数１〜１
６の直鎖状若しくは分岐状のアルキル基、又は、炭素数
６〜１６のアリール基を表す。Ｒ2 は、水酸基、炭素数
１〜１６の直鎖状若しくは分岐状のアルキル基、炭素数
１〜１６の直鎖状若しくは分岐状のアルコキシル基、炭
素数６〜１６のアリール基、又は、炭素数６〜１６のア
リールオキシ基を表す。In the formula, R 1 and R 3 are hydrogen, C 1 -C 1
6 represents a linear or branched alkyl group or an aryl group having 6 to 16 carbon atoms. R 2 is a hydroxyl group, a linear or branched alkyl group having 1 to 16 carbon atoms, a linear or branched alkoxyl group having 1 to 16 carbon atoms, an aryl group having 6 to 16 carbon atoms, Represents an aryloxy group represented by Formulas 6 to 16.
【００４０】上記赤リンは、少量の添加で難燃効果が向
上する。上記赤リンとしては、市販の赤リンを用いるこ
とができるが、耐湿性、混練時に自然発火しない等の安
全性の点から、赤リン粒子の表面を樹脂でコーティング
したもの等が好適に用いられる。The flame retardant effect is improved by adding a small amount of the above-mentioned red phosphorus. As the red phosphorus, commercially available red phosphorus can be used, but from the viewpoint of moisture resistance, safety such as not spontaneously igniting during kneading, those obtained by coating the surface of red phosphorus particles with a resin are preferably used. .
【００４１】上記ポリリン酸アンモニウム類としては、
特に限定されず、例えば、ポリリン酸アンモニウム、メ
ラミン変性ポリリン酸アンモニウム等が挙げられるが、
難燃性、安全性、コスト等の点からポリリン酸アンモニ
ウムが好適に用いられる。市販品としては、例えば、ヘ
キスト社製「ＡＰ４２２」、「ＡＰ４６２」；住友化学
社製「スミセーフＰ」；チッソ社製「テラージュＣ６
０」、「テラージュＣ７０」、「テラージュＣ８０」等
が挙げられる。The above ammonium polyphosphates include:
Not particularly limited, for example, ammonium polyphosphate, melamine-modified ammonium polyphosphate and the like,
Ammonium polyphosphate is preferably used in terms of flame retardancy, safety, cost and the like. Commercially available products include, for example, "AP422" and "AP462" manufactured by Hoechst; "Sumisafe P" manufactured by Sumitomo Chemical; "Terage C6" manufactured by Chisso.
0, "" Terage C70, "" Terage C80, "and the like.
【００４２】上記一般式（１）で表される化合物として
は特に限定されず、例えば、メチルホスホン酸、メチル
ホスホン酸ジメチル、メチルホスホン酸ジエチル、エチ
ルホスホン酸、プロピルホスホン酸、ブチルホスホン
酸、２−メチルプロピルホスホン酸、ｔ−ブチルホスホ
ン酸、２，３−ジメチル−ブチルホスホン酸、オクチル
ホスホン酸、フェニルホスホン酸、ジオクチルフェニル
ホスホネート、ジメチルホスフィン酸、メチルエチルホ
スフィン酸、メチルプロピルホスフィン酸、ジエチルホ
スフィン酸、ジオクチルホスフィン酸、フェニルホスフ
ィン酸、ジエチルフェニルホスフィン酸、ジフェニルホ
スフィン酸、ビス（４−メトキシフェニル）ホスフィン
酸等が挙げられる。中でも、ｔ−ブチルホスホン酸は、
高価ではあるが、高難燃性の点において好ましい。The compound represented by the above general formula (1) is not particularly restricted but includes, for example, methylphosphonic acid, dimethyl methylphosphonate, diethyl methylphosphonate, ethylphosphonic acid, propylphosphonic acid, butylphosphonic acid, 2-methylpropyl Phosphonic acid, t-butylphosphonic acid, 2,3-dimethyl-butylphosphonic acid, octylphosphonic acid, phenylphosphonic acid, dioctylphenylphosphonate, dimethylphosphinic acid, methylethylphosphinic acid, methylpropylphosphinic acid, diethylphosphinic acid, dioctyl Examples include phosphinic acid, phenylphosphinic acid, diethylphenylphosphinic acid, diphenylphosphinic acid, and bis (4-methoxyphenyl) phosphinic acid. Among them, t-butylphosphonic acid is
Although expensive, it is preferable in terms of high flame retardancy.
【００４３】上記これらのリン化合物は、単独で用いら
れてもよく、２種以上が併用されてもよい。These phosphorus compounds may be used alone or in combination of two or more.
【００４４】また、上記金属炭酸塩は、上記リン化合物
としてポリリン酸アンモニウムを使用した場合、ポリリ
ン酸アンモニウムとの反応で膨張を促進すると考えられ
る。また、有効な骨材として働き、燃焼後に形状保持性
の高い残渣を形成する。When ammonium polyphosphate is used as the phosphorus compound, the metal carbonate is considered to promote expansion by a reaction with ammonium polyphosphate. In addition, it acts as an effective aggregate and forms a residue having high shape retention after burning.
【００４５】上記樹脂組成物（II）におけるリン化合物
と中和処理された熱膨張性黒鉛との配合量（両者の合計
量）は、上記熱可塑性樹脂及び／又は合成ゴム１００重
量部に対して２０〜５００重量部が好ましい。リン化合
物と中和処理された熱膨張性黒鉛の合計量が、２０重量
部より少なくなると十分な熱膨張性が得られず、５００
重量部を超えると均一な分散が困難となるため、均一な
厚みに施工することが難しくなり、施工方法が限定され
る。The amount of the phosphorus compound and the neutralized heat-expandable graphite in the resin composition (II) (the total amount of both) is based on 100 parts by weight of the thermoplastic resin and / or synthetic rubber. 20 to 500 parts by weight are preferred. If the total amount of the phosphorus compound and the neutralized thermally expandable graphite is less than 20 parts by weight, sufficient thermal expandability cannot be obtained, and 500
When the amount exceeds the weight part, uniform dispersion becomes difficult, so that it is difficult to construct a uniform thickness, and the construction method is limited.
【００４６】また、中和処理された熱膨張性黒鉛とリン
化合物との重量比（熱膨張性黒鉛／リン化合物）は、
０．０１〜９が好ましい。熱膨張性黒鉛の比率が多くな
ると、燃焼時に膨張した黒鉛が飛散して十分な耐火断熱
層が形成されず、リン化合物の比率が多くなると、十分
な耐火断熱層が形成されなくなるため、十分な断熱性が
得られない。The weight ratio of the neutralized heat-expandable graphite to the phosphorus compound (heat-expandable graphite / phosphorus compound) is as follows:
0.01 to 9 is preferred. If the ratio of the heat-expandable graphite increases, the expanded graphite during combustion scatters and a sufficient refractory heat-insulating layer is not formed.If the ratio of the phosphorus compound increases, a sufficient refractory heat-insulating layer is not formed. Heat insulation cannot be obtained.
【００４７】上記樹脂組成物（II）における無機充填剤
の配合量は、上記樹脂組成物（Ｉ）と同様な理由によ
り、熱可塑性樹脂及び／又は合成ゴム１００重量部に対
して５０〜５００重量部が好ましい。The amount of the inorganic filler in the resin composition (II) is 50 to 500 parts by weight based on 100 parts by weight of the thermoplastic resin and / or synthetic rubber for the same reason as in the resin composition (I). Parts are preferred.
【００４８】上記樹脂組成物にブチルゴムが用いられる
場合は、必要に応じて、ポリブテン等の液状成分、石油
樹脂等の粘着付与剤が添加されてもよい。When butyl rubber is used in the resin composition, a liquid component such as polybutene and a tackifier such as petroleum resin may be added as necessary.
【００４９】上記樹脂組成物から耐火膨張性シートを得
るには、例えば、押出成形、カレンダー成形、熱プレス
成形等、通常のシートの成形方法が使用可能である。In order to obtain a fire-resistant expansion sheet from the above resin composition, a usual sheet forming method such as extrusion molding, calender molding, hot press molding and the like can be used.
【００５０】上記耐火膨張性シートとしては、例えば、
筐体内部の上面部に樹脂組成物（Ｉ）から形成されるも
のを使用し、それ以外の筐体内面には樹脂組成物（II）
から形成されるものを使用するように、樹脂組成物
（Ｉ）及び（II）からなる耐火膨張性シートを組み合わ
せて使用してもよい。Examples of the fire-resistant expansion sheet include:
A resin composition (I) is used for the upper surface inside the housing, and the resin composition (II) is used for the other inner surfaces of the housing.
May be used in combination with a fire-resistant expansive sheet composed of the resin compositions (I) and (II).
【００５１】（作用）本発明の消火性筐体は、筐体内部
に堆積した塵や埃が発端となって出火しても、筐体の内
面に配置された耐火膨張性シートが熱膨張することによ
って、発熱源となる機器及び／又は高電圧を発生する機
器を被覆して、酸素の供給を遮断することにより消火す
ることができる。また、筐体の通気口周辺に配置された
耐火膨張性シートが熱膨張することによって通気口を塞
ぎ、酸素の供給を遮断することにより消火することがで
きる。また、筐体内面の上面部に耐火膨張性シートを配
置する態様では、耐火膨張性シートが火元の上に落下し
て消火することができる。(Function) In the fire extinguisher casing of the present invention, even if dust or dust accumulated inside the casing becomes a starting point and a fire occurs, the fire-resistant expansible sheet disposed on the inner surface of the casing thermally expands. This makes it possible to extinguish a fire by covering a device that is a heat source and / or a device that generates a high voltage and shutting off supply of oxygen. In addition, the fire-resistant expansion sheet disposed around the ventilation port of the housing thermally expands to close the ventilation port, and the fire can be extinguished by shutting off the supply of oxygen. Further, in a mode in which the fire-resistant expansion sheet is disposed on the upper surface of the inner surface of the housing, the fire-resistant expansion sheet can fall on the fire source and extinguish the fire.
【００５２】[0052]
【発明の実施の形態】以下に実施例を掲げて本発明を更
に詳しく説明する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail with reference to the following examples.
【００５３】（実施例１）図１に示したテレビ受像機筐
体の内面全体に耐火膨張性シートを貼着した消火性筐体
を使用した。ブチルゴム４０重量部、ポリブテン５０重
量部、水添石油樹脂１０重量部、ポリリン酸アンモニウ
ム１００重量部、中和処理された熱膨張性黒鉛３０重量
部、水酸化アルミニウム５０重量部、及び、炭酸カルシ
ウム１００重量部を含有する混合物を、２軸押出機によ
り混練、押出成形して、厚み２ｍｍの耐火膨張性シート
を得た。得られた耐火膨張性シートを所定の形状に切断
して、通気口に相当する部分には打抜き機により所定の
形状に打抜いて貼着した。上記耐火膨張性シートは自己
粘着性を有しており、特に筐体内面に貼着するために接
着剤等を必要としなかった。(Example 1) A fire extinguisher housing was used in which a fire-resistant expansive sheet was adhered to the entire inner surface of the television receiver housing shown in FIG. 40 parts by weight of butyl rubber, 50 parts by weight of polybutene, 10 parts by weight of hydrogenated petroleum resin, 100 parts by weight of ammonium polyphosphate, 30 parts by weight of neutralized thermally expandable graphite, 50 parts by weight of aluminum hydroxide, and 100 parts by weight of calcium carbonate The mixture containing parts by weight was kneaded and extruded with a twin-screw extruder to obtain a fire-resistant expansible sheet having a thickness of 2 mm. The obtained fire-resistant intumescent sheet was cut into a predetermined shape, and a portion corresponding to a vent was punched into a predetermined shape by a punching machine and attached. The fire-resistant intumescent sheet has self-adhesiveness, and does not require an adhesive or the like particularly for sticking to the inner surface of the housing.
【００５４】上記で得られた消火性筐体は、内部から出
火した火炎によって耐火膨張性シートが熱膨張して形成
された断熱層によって筐体内面が被覆されると共に、通
気口が断熱層により閉塞されて外部への火炎の噴出を防
止されたため、最終的に筐体内部が酸欠状態になり消火
された。In the fire extinguishing case obtained above, the inner surface of the case is covered with a heat insulating layer formed by the thermal expansion of the fire-resistant expandable sheet by the flame ignited from the inside, and the ventilation hole is formed by the heat insulating layer. Since the flame was prevented from escaping to the outside due to the blockage, the inside of the housing eventually became oxygen-deficient and the fire was extinguished.
【００５５】（実施例２）実施例１と同様の耐火膨張性
シートを、図１に示した筐体内面の通気口周辺のみに貼
着することによって、消火性筐体を作製した。得られた
消火性筐体は、内部から出火した火炎によって耐火膨張
性シートが熱膨張して形成された断熱層によって、通気
口が閉塞されて外部への火炎の噴出を防止されたため、
最終的に筐体内部が酸欠状態になり消火された。(Example 2) A fire-extinguishing case was produced by sticking the same fire-resistant intumescent sheet as in Example 1 only around the vent on the inner surface of the case shown in FIG. The resulting fire-extinguishing casing has a heat-insulating layer formed by the thermal expansion of the fire-resistant expansion sheet due to the flame ignited from the inside, so that the ventilation holes are blocked and the emission of the flame to the outside is prevented,
Eventually, the inside of the case became oxygen-deficient and the fire was extinguished.
【００５６】（実施例３）図１に示したテレビ受像機筐
体内面の上面部にのみ耐火膨張性シートを貼着した消火
性筐体を使用した。ブチルゴム４０重量部、ポリブテン
５０重量部、水添石油樹脂１０重量部、中和処理された
熱膨張性黒鉛３０重量部、水酸化アルミニウム５０重量
部、及び、炭酸カルシウム１００重量部の混合物を、２
軸押出機により混練、押出成形して、厚み２ｍｍの耐火
膨張性シートを得た。得られた耐火膨張性シートを所定
の形状に切断して貼着した。上記耐火膨張性シートは、
自己粘着性を有しており、特に接着剤等の使用は必要と
しなかった。(Example 3) A fire extinguisher housing was used in which a fire-resistant expansion sheet was adhered only to the upper surface of the inner surface of the television receiver housing shown in FIG. A mixture of 40 parts by weight of butyl rubber, 50 parts by weight of polybutene, 10 parts by weight of hydrogenated petroleum resin, 30 parts by weight of neutralized thermally expandable graphite, 50 parts by weight of aluminum hydroxide, and 100 parts by weight of calcium carbonate was mixed with 2 parts by weight.
The mixture was kneaded and extruded by a screw extruder to obtain a fire-resistant expansion sheet having a thickness of 2 mm. The obtained fire-resistant expansion sheet was cut into a predetermined shape and attached. The fire resistant expansion sheet,
It has self-adhesive properties and did not require the use of an adhesive or the like.
【００５７】上記で得られた消火性筐体は、内部から出
火した火炎によって耐火膨張性シートが熱膨張して形成
された断熱層が火元に落下して遮蔽し、火元部を酸欠状
態にして消火した。In the fire-extinguishing casing obtained above, the heat-expandable sheet is thermally expanded by the flame ignited from the inside, and the heat-insulating layer formed by the fire-extinguishing sheet falls to the source of fire and is shielded. The fire was extinguished in the condition.
【００５８】[0058]
【発明の効果】本発明の消火性筐体は、上述の構成であ
り、筐体の内面に耐火膨張性シートを配置することによ
って、特にスペースをとることもなく、機器からの出火
を効果的に消火する。The fire extinguisher casing of the present invention has the above-described structure, and by arranging a fire-resistant expansive sheet on the inner surface of the casing, it is possible to effectively prevent fire from the equipment without taking up any particular space. Extinguish a fire.
【図１】図１（イ）はテレビ受像機の主要部を示す模式
断面図であり、図１（ロ）はテレビ受像機の背面図であ
る。FIG. 1A is a schematic sectional view showing a main part of a television receiver, and FIG. 1B is a rear view of the television receiver.
【図２】図１（イ）Ａ部を拡大して示す模式断面図であ
る。FIG. 2 is an enlarged schematic cross-sectional view of a portion A in FIG.
【図３】図１（イ）Ｂ部を拡大して示す模式断面図であ
る。FIG. 3 is an enlarged schematic cross-sectional view showing a portion B in FIG.
１ テレビ受像機 ２ 筐体 ３ 通気口 ４ ＣＲＴ ５ 耐火膨張性シート REFERENCE SIGNS LIST 1 television receiver 2 housing 3 vent 4 CRT 5 fire-resistant inflatable sheet
Claims (5)
圧を発生する機器が収納される筐体の内面に、耐火膨張
性シートが配置されてなることを特徴とする消火性筐
体。1. A fire-extinguishing housing, wherein a fire-resistant expansion sheet is disposed on an inner surface of a housing in which a device serving as a heat source and / or a device generating a high voltage is stored.
膨張性シートが配置されてなることを特徴とする請求項
１記載の消火性筐体。2. The fire extinguisher casing according to claim 1, wherein a fire-resistant inflatable sheet is disposed at least around the ventilation hole on the inner surface of the casing.
配置されてなることを特徴とする請求項１記載の消火性
筐体。3. The fire extinguisher casing according to claim 1, wherein a fire-resistant expansion sheet is disposed on an upper surface of the inner surface of the casing.
／又は合成ゴム、中和処理された熱膨張性黒鉛、並び
に、無機充填剤を含有する樹脂組成物（Ｉ）からなるこ
とを特徴とする請求項１〜３のいずれか１項に記載の消
火性筐体。4. A fire-resistant expansible sheet comprising a resin composition (I) containing a thermoplastic resin and / or synthetic rubber, neutralized heat-expandable graphite, and an inorganic filler. The fire extinguisher casing according to any one of claims 1 to 3.
／又は合成ゴム、リン化合物、中和処理された熱膨張性
黒鉛、並びに、無機充填剤を含有する樹脂組成物（II）
からなることを特徴とする請求項１〜３のいずれか１項
に記載の消火性筐体。5. A resin composition (II) in which the fire-resistant expansible sheet contains a thermoplastic resin and / or a synthetic rubber, a phosphorus compound, neutralized heat-expandable graphite, and an inorganic filler.
The fire extinguisher casing according to any one of claims 1 to 3, comprising: