JP2000207776A - Recording medium - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a high-reliability recording medium by bonding two transparent resin boards with a filmy photosetting adhesive contg. an ethylene-vinyl acetate copolymer as a main component to bond the resin boards at a good operability. SOLUTION: Two transparent resin boards 1, 2 having reflective layers 1a, 2a formed on signal bit surfaces for digital video discs of a double-side read system or two boards 1, 2 having a semitransparent layer 1b and a reflective layer 2a formed on signal bit surfaces for digital video discs of a single-side read system are mutually bonded, using an photosetting adhesive contg. an ethylene-vinyl acetate copolymer as a main component, and the ethylene-vinyl acetate copolymer to be a main component of this adhesive layer has pref. a vinyl acetate content of 10-50 wt.%, and more pref. 15-45 wt.% from the viewpoints of the reactivity in the optical setting, flexibility and durability after the photosetting.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、デジタルビデオデ
ィスク等の大容量の文字、音声、動画像といった情報を
デジタル信号により記録する記録媒体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recording medium, such as a digital video disk, for recording information such as large-capacity characters, sounds, and moving images by digital signals.

【０００２】[0002]

【従来の技術及び発明が解決しようとする課題】両面に
記録層を持つデジタルビデオディスクには、図１に示す
ようにそれぞれ片面に信号ビットを形成した２枚の透明
樹脂基板１，２の該信号ビット形成面にそれぞれ反射層
１ａ，２ａを形成し、これら反射層１ａ，２ａを互いに
対面させた状態で基板１，２を接着剤層３を介して貼り
合わせ、接合した両面読み出し方式のもの、及び、図２
に示すように、それぞれ片面に信号ビットを形成した基
板１，２において、一方の基板１の信号ビット面に半透
明層１ｂを形成すると共に、他方の基板２の信号ビット
面に反射層２ａを形成し、これら半透明層１ｂと反射層
２ａとを対面させた状態で基板１，２を接着剤層３を介
して貼り合わせ、接合した片面読み出し方式のものとが
知られている。2. Description of the Related Art As shown in FIG. 1, a digital video disk having recording layers on both sides has two transparent resin substrates 1 and 2 each having signal bits formed on one side as shown in FIG. Reflective layers 1a and 2a are formed on the signal bit forming surface, respectively. Substrates 1 and 2 are bonded via an adhesive layer 3 in a state where these reflective layers 1a and 2a face each other, and are bonded to each other. And FIG.
As shown in (1), in the substrates 1 and 2 each having signal bits formed on one surface, a translucent layer 1b is formed on the signal bit surface of one substrate 1 and the reflection layer 2a is formed on the signal bit surface of the other substrate 2. A single-sided readout type in which the substrates 1 and 2 are bonded together with the translucent layer 1b and the reflective layer 2a facing each other via an adhesive layer 3 in a state where the translucent layer 1b and the reflective layer 2a face each other is known.

【０００３】従来、上記基板１，２を接合する接着剤と
しては、ホットメルト系接着剤及び紫外線硬化性樹脂接
着剤が使用されている。しかし、これら接着剤は、下記
のような欠点があった。Conventionally, hot melt adhesives and ultraviolet curable resin adhesives have been used as adhesives for bonding the substrates 1 and 2. However, these adhesives have the following disadvantages.

【０００４】即ち、ホットメルト系接着剤は、耐候性が
劣るという問題があり、また耐熱性も劣るため、湿熱耐
久試験、冷熱サイクル耐久試験、耐熱耐久試験等の信頼
性試験において剥離やズレ等の外観異常が発生し、従っ
て、高温雰囲気、例えば車載用には使えず、用途が限定
されるという問題があった。That is, the hot-melt adhesive has a problem of poor weather resistance, and also has a poor heat resistance. Therefore, peeling and slippage in reliability tests such as a wet heat endurance test, a heat cycle endurance test, and a heat endurance test. Therefore, there is a problem in that the external appearance of the device cannot be used in a high-temperature atmosphere, for example, for use in a vehicle, and its use is limited.

【０００５】一方、紫外線硬化性樹脂接着剤は、 液状であるため、接着層の均一な厚み制御が困難であ
る。特に再生光を片面から照射して読み取る片面読み出
し方式では、円周方向の接着層厚みのミクロンオーダー
での極めて精密な制御が要求されるが、液状の紫外線硬
化性樹脂の場合は、樹脂ディスクを回転テーブルの上で
高速回転させながら液を塗布するスピンコート方式をと
るため、液が遠心力により広がる際に流紋ができ、希望
の膜厚精度が出しにくい、 硬化前の仮圧着時に接着剤が積層体の周辺からはみ出
し垂れる、 硬化後の接着層の弾性率が高く（硬く）、柔軟性に欠
け、脆いため、落とした時に割れる、 硬化膜の伸びがないため、冷熱サイクル耐久試験、耐
熱耐久試験等の信頼性試験において、透明樹脂基板の熱
膨張に接着層が耐えきれず剥離が発生する などの問題があった。On the other hand, since the ultraviolet curable resin adhesive is liquid, it is difficult to control the thickness of the adhesive layer uniformly. In particular, in the single-sided reading method in which the reproduction light is irradiated from one side to read, extremely precise control of the thickness of the adhesive layer in the circumferential direction on the order of microns is required. The spin coating method of applying liquid while rotating at high speed on a rotary table creates a ripple when the liquid spreads due to centrifugal force, making it difficult to achieve the desired film thickness accuracy. Of the adhesive layer after curing is high (hard), lacks flexibility and is brittle, cracks when dropped, and has no elongation of the cured film. In a reliability test such as a durability test, there was a problem that the adhesive layer could not withstand the thermal expansion of the transparent resin substrate and peeling occurred.

【０００６】また、ホットメルト系接着剤及び紫外線硬
化性樹脂接着剤に共通する問題として、透明樹脂基板と
の接着力が低く、耐久性の点で問題を抱えており、この
ためかかる問題のない接着剤が望まれていた。Further, as a problem common to hot melt adhesives and ultraviolet curable resin adhesives, the adhesive strength to a transparent resin substrate is low, and there is a problem in terms of durability. An adhesive was desired.

【０００７】本発明は上記要望に応えたもので、透明樹
脂基板相互を強固にしかも操作性良く接合でき、信頼性
の高い記録媒体を提供することを目的とする。SUMMARY OF THE INVENTION The present invention has been made to meet the above-mentioned demands, and has as its object to provide a highly reliable recording medium capable of firmly joining transparent resin substrates with good operability.

【０００８】[0008]

【課題を解決するための手段及び発明の実施の形態】本
発明者らは、上記目的を達成するため、鋭意検討を行っ
た結果、２枚の透明樹脂基板を接合する接着剤として、
エチレン−酢酸ビニル共重合体を主成分とするフィルム
状の光硬化性接着剤を用いることにより、上記ホットメ
ルト系接着剤や紫外線硬化性樹脂接着剤に見られるよう
な欠点を解消し得、高信頼性の記録媒体が得られるこ
と、またかかる記録媒体を容易にかつ高精度で製造し得
ることを知見したものである。Means for Solving the Problems and Embodiments of the Invention The present inventors have conducted intensive studies to achieve the above object, and as a result, as an adhesive for joining two transparent resin substrates,
By using a film-like photo-curable adhesive containing an ethylene-vinyl acetate copolymer as a main component, it is possible to eliminate defects such as those of the above-mentioned hot-melt adhesives and ultraviolet-curable resin adhesives. It has been found that a reliable recording medium can be obtained, and that such a recording medium can be easily and accurately manufactured.

【０００９】即ち、本発明は、（１）２枚の透明樹脂基
板をエチレン−酢酸ビニル共重合体を主成分とするフィ
ルム状の光硬化性接着剤により接合してなることを特徴
とする記録媒体、（２）２枚の透明樹脂基板が、それぞ
れ反射層を有するデジタルビデオディスク用基板、又は
一方が反射層、他方が半透明層を有するデジタルビデオ
ディスク用基板である（１）記載の記録媒体、（３）光
硬化性接着剤が、エチレン−酢酸ビニル共重合体１００
重量部に対し、光増感剤を０．１〜１０重量部、シラン
カップリング剤を０．０１〜５重量部添加してなること
を特徴とする（１）又は（２）記載の記録媒体、（４）
光硬化性接着剤が、エチレン−酢酸ビニル共重合体１０
０重量部に対し、アクリロキシ基含有化合物、メタクリ
ロキシ基含有化合物及びアリル基含有化合物のうち少な
くとも１つを０．１〜５０重量部添加してなることを特
徴とする（１），（２）又は（３）記載の記録媒体、
（５）光硬化性接着剤が、エチレン−酢酸ビニル共重合
体１００重量部に対し、炭化水素樹脂を１〜２００重量
部添加してなることを特徴とする（１）乃至（４）のい
ずれか１項記載の記録媒体、（６）エチレン−酢酸ビニ
ル共重合体の酢酸ビニル含有率が１０〜５０重量％であ
ることを特徴とする（１）乃至（５）のいずれか１項記
載の記録媒体、及び、（７）フィルム状の光硬化性接着
剤の厚さが１〜１０００μｍである（１）乃至（６）の
いずれか１項記載の記録媒体を提供する。That is, according to the present invention, there is provided (1) a recording method wherein two transparent resin substrates are joined by a film-like photocurable adhesive containing ethylene-vinyl acetate copolymer as a main component. (2) The recording according to (1), wherein the two transparent resin substrates are digital video disk substrates each having a reflective layer, or one is a digital video disk substrate having a reflective layer and the other is a translucent layer. Medium, (3) the photocurable adhesive is ethylene-vinyl acetate copolymer 100
The recording medium according to (1) or (2), wherein 0.1 to 10 parts by weight of a photosensitizer and 0.01 to 5 parts by weight of a silane coupling agent are added to parts by weight. , (4)
When the photocurable adhesive is ethylene-vinyl acetate copolymer 10
(1), (2) or characterized in that 0.1 to 50 parts by weight of at least one of an acryloxy group-containing compound, a methacryloxy group-containing compound and an allyl group-containing compound is added to 0 parts by weight. (3) the recording medium described above,
(5) Any of (1) to (4), wherein the photocurable adhesive is obtained by adding 1 to 200 parts by weight of a hydrocarbon resin to 100 parts by weight of the ethylene-vinyl acetate copolymer. (6) The recording medium according to any one of (1) to (5), wherein the vinyl acetate content of the ethylene-vinyl acetate copolymer is 10 to 50% by weight. A recording medium, and (7) the recording medium according to any one of (1) to (6), wherein the thickness of the film-shaped photocurable adhesive is 1 to 1000 μm.

【００１０】本発明による２枚の透明樹脂基板との貼り
合わせに用いられる接着剤は、膜厚精度を精密に制御し
たフィルム状で提供することができるため、２枚の透明
樹脂基板との貼り合わせを容易にかつ精度良く、しかも
紫外線硬化性樹脂接着剤の場合に見られるような端部か
らの接着剤のはみ出しが一切なく貼り合わせが可能であ
る。また、２枚の透明樹脂基板との貼り合わせは、圧着
ロールや簡易プレスなどの簡便な方法で３０〜１００℃
で仮圧着した後、光により常温、１〜数十秒で硬化でき
る上、本接着剤特有の自着力によりその積層体にズレや
剥離が起き難いため、光硬化まで自由にハンドリングが
できるという特長を有している。また、本発明の記録媒
体に用いられる接着剤は、エチレン−酢酸ビニル共重合
体を主成分としているため、紫外線硬化性樹脂接着剤に
比べ、硬化後の弾性率が低く、可撓性に富むため、記録
媒体の取り扱いも容易で、誤って落としたりぶつけたり
しても、割れたり接着剥離を起こしたりすることがな
い。The adhesive used for bonding the two transparent resin substrates according to the present invention can be provided in the form of a film whose film thickness precision is precisely controlled. The bonding can be performed easily and accurately, and the bonding can be performed without any protrusion of the adhesive from the end as seen in the case of the ultraviolet curable resin adhesive. The bonding with the two transparent resin substrates is performed at 30 to 100 ° C. by a simple method such as a pressure roll or a simple press.
It can be cured by light at room temperature for 1 to several tens of seconds after light-pressing, and the laminated body is not easily displaced or peeled off due to the self-adhesive force peculiar to the adhesive. have. Further, since the adhesive used for the recording medium of the present invention contains an ethylene-vinyl acetate copolymer as a main component, the elastic modulus after curing is lower than that of the ultraviolet curable resin adhesive, and the adhesive is rich in flexibility. Therefore, handling of the recording medium is easy, and even if the recording medium is accidentally dropped or hit, the recording medium does not crack or peel off.

【００１１】以下、本発明につき更に詳しく説明する。
本発明の記録媒体は、２枚の透明樹脂基板、例えば図
１，２に示したように、それぞれ反射層１ａ，２ａを信
号ビット面に形成した両面読み出し方式のデジタルビデ
オディスク用基板１，２相互、或いは、半透明層１ｂ及
び反射層２ａをそれぞれ信号ビット面に形成した片面読
み出し方式のデジタルビデオディスク用基板１，２相互
の接合に、エチレン−酢酸ビニル共重合体を主成分とす
る光硬化性接着剤を用いるものである。この場合、この
接着剤は、その厚みを確実に制御して高精度で基板相互
を接合し得るので、特に片面読み出し方式の基板の接合
に有効である。Hereinafter, the present invention will be described in more detail.
The recording medium of the present invention includes two transparent resin substrates, for example, double-sided reading digital video disk substrates 1 and 2 having reflection layers 1a and 2a formed on signal bit surfaces as shown in FIGS. A light containing an ethylene-vinyl acetate copolymer as a main component is bonded to the single-side read-out type digital video disk substrates 1 and 2 in which the translucent layer 1b and the reflective layer 2a are formed on the signal bit surface, respectively. A curable adhesive is used. In this case, the adhesive can bond the substrates with high accuracy by reliably controlling the thickness thereof, and is particularly effective for bonding substrates of a single-side readout method.

【００１２】ここで、記録媒体を形成する透明樹脂基板
としては、ガラス転移温度が５０℃以上の透明の有機樹
脂が好ましく、このような透明樹脂基板としては、ポリ
エチレンテレフタレート、ポリシクロヘキシレンテレフ
タレート、ポリエチレンナフタレート等のポリエステル
系樹脂、ナイロン４６、変性ナイロン６Ｔ、ナイロンＭ
ＸＤ６、ポリフタルアミド等のポリアミド系樹脂、ポリ
フェニレンスルフィド、ポリチオエーテルサルフォン等
のケトン系樹脂、ポリサルフォン、ポリエーテルサルフ
ォン等のサルフォン系樹脂の他に、ポリエーテルニトリ
ル、ポリアリレート、ポリエーテルイミド、ポリアミド
イミド、ポリカーボネート、ポリメチルメタクリレー
ト、トリアセチルセルロース、ポリスチレン、ポリビニ
ルクロライド等の有機樹脂を主成分とする透明樹脂基板
を用いることができる。特にこの中で、ポリカーボネー
ト、ポリメチルメタアクリレート、ポリビニルクロライ
ド、ポリスチレン、ポリエチレンテレフタレートが転写
性、複屈折の点で好適に用いられる。Here, as the transparent resin substrate forming the recording medium, a transparent organic resin having a glass transition temperature of 50 ° C. or higher is preferable. As such a transparent resin substrate, polyethylene terephthalate, polycyclohexylene terephthalate, polyethylene Polyester resin such as naphthalate, nylon 46, modified nylon 6T, nylon M
XD6, polyamide resins such as polyphthalamide, ketone resins such as polyphenylene sulfide and polythioether sulfone, sulfone resins such as polysulfone and polyether sulfone, as well as polyether nitrile, polyarylate, polyether imide, A transparent resin substrate mainly containing an organic resin such as polyamide imide, polycarbonate, polymethyl methacrylate, triacetyl cellulose, polystyrene, or polyvinyl chloride can be used. Particularly, among them, polycarbonate, polymethyl methacrylate, polyvinyl chloride, polystyrene, and polyethylene terephthalate are preferably used in terms of transferability and birefringence.

【００１３】一方、本発明の記録媒体に用いられる接着
剤層の主成分であるエチレン−酢酸ビニル共重合体は、
光硬化時の反応性や硬化後の可撓性、耐久性の点から酢
酸ビニル含有率が１０〜５０重量％であることが好まし
く、更に好ましくは１５〜４５重量％である。On the other hand, the ethylene-vinyl acetate copolymer, which is the main component of the adhesive layer used in the recording medium of the present invention, comprises:
The vinyl acetate content is preferably from 10 to 50% by weight, and more preferably from 15 to 45% by weight, from the viewpoint of reactivity during photocuring, flexibility after curing, and durability.

【００１４】本発明の記録媒体に用いられる接着剤層の
硬化のために添加される光増感剤は、接着剤の調製条
件、製膜温度、硬化（貼り合わせ）条件、接着剤の貯蔵
安定性等を考慮して選択されるが、ラジカル光重合開始
剤が好適に用いられる。The photosensitizer added for curing the adhesive layer used in the recording medium of the present invention includes conditions for preparing the adhesive, film forming temperature, curing (bonding) conditions, and storage stability of the adhesive. Although it is selected in consideration of the properties and the like, a radical photopolymerization initiator is preferably used.

【００１５】ラジカル光重合開始剤のうち水素引き抜き
型開始剤としては、ベンゾフェノン、オルソベンゾイル
安息香酸メチル、４−ベンゾイル−４’−メチルジフェ
ニルサルファイド、イソプロピルチオキサントン、ジエ
チルチオキサントン、エチル−４−（ジエチルアミノ）
−ベンゾエート等が用いられる。ラジカル光重合開始剤
のうち分子内開裂型開始剤としては、ベンゾインエーテ
ル、ベンジルジメチルケタールなど、α−ヒドロキシア
ルキルフェノン型として、２−ヒドロキシ−２−メチル
−１−フェニルプロパン−１−オン、１−ヒドロキシシ
クロヘキシルフェニルケトン、アルキルフェニルグリオ
キシレート、ジエトキシアセトフェノンなどが使用でき
る。更に、α−アミノアルキルフェノン型として、２−
メチル−１−［４−（メチルチオ）フェニル］−２−モ
リフォリノプロパン−１、２−ベンジル−２−ジメチル
アミノ−１−（４−モリフォリノフェニル）−ブタノン
−１などが、またアシルフォスフィンオキサイドなどが
用いられる。Among the radical photopolymerization initiators, examples of the hydrogen abstraction initiator include benzophenone, methyl orthobenzoylbenzoate, 4-benzoyl-4'-methyldiphenylsulfide, isopropylthioxanthone, diethylthioxanthone, and ethyl-4- (diethylamino).
-Benzoate and the like are used. Among radical photopolymerization initiators, examples of intramolecular cleavage initiators include benzoin ether and benzyldimethyl ketal, and α-hydroxyalkylphenones include 2-hydroxy-2-methyl-1-phenylpropan-1-one, -Hydroxycyclohexyl phenyl ketone, alkyl phenyl glyoxylate, diethoxy acetophenone and the like can be used. Furthermore, as an α-aminoalkylphenone type,
Methyl-1- [4- (methylthio) phenyl] -2-morpholinopropane-1, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butanone-1 and the like; Phosphine oxide or the like is used.

【００１６】光増感剤としては、これらのうちの１種を
単独で又は２種以上を混合して用いることができ、その
添加量は、エチレン−酢酸ビニル共重合体１００重量部
に対し０．１〜１０重量部で十分である。As the photosensitizer, one of these can be used alone or in combination of two or more. The amount of the photosensitizer is 0 to 100 parts by weight of the ethylene-vinyl acetate copolymer. 0.1 to 10 parts by weight is sufficient.

【００１７】また、本発明の接着剤には、接着促進剤と
してシランカップリング剤を添加することができる。こ
のシランカップリング剤としてはビニルトリエトキシシ
ラン、ビニルトリス（β−メトキシエトキシ）シラン、
γ−メタクリロキシプロピルトリメトキシシラン、ビニ
ルトリアセトキシシラン、γ−グリシドキシプロピルト
リメトキシシラン、γ−グリシドキシプロピルトリエト
キシシラン、β−（３，４−エポキシシクロヘキシル）
エチルトリメトキシシラン、γ−クロロプロピルメトキ
シシラン、ビニルトリクロロシラン、γ−メルカプトプ
ロピルトリメトキシシラン、γ−アミノプロピルトリエ
トキシシラン、Ｎ−β（アミノエチル）−γ−アミノプ
ロピルトリメトキシシランなどがあり、これらの１種を
単独で又は２種以上を混合して用いることができる。こ
れらシランカップリング剤の添加量は、エチレン−酢酸
ビニル共重合体１００重量部に対し通常０．０１〜５重
量部で十分である。Further, a silane coupling agent can be added to the adhesive of the present invention as an adhesion promoter. Examples of the silane coupling agent include vinyltriethoxysilane, vinyltris (β-methoxyethoxy) silane,
γ-methacryloxypropyltrimethoxysilane, vinyltriacetoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, β- (3,4-epoxycyclohexyl)
Ethyltrimethoxysilane, γ-chloropropylmethoxysilane, vinyltrichlorosilane, γ-mercaptopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N-β (aminoethyl) -γ-aminopropyltrimethoxysilane, etc. These may be used alone or in combination of two or more. The addition amount of these silane coupling agents is usually 0.01 to 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer.

【００１８】更に、本発明の接着剤には、同様に接着性
を向上させる目的でエポキシ基含有化合物を添加するこ
とができる。エポキシ基含有化合物としては、トリグリ
シジルトリス（２−ヒドロキシエチル）イソシアヌレー
ト；ネオペンチルグリコールジグリシジルエーテル；
１，６−ヘキサンジオールジグリシジルエーテル；アク
リルグリシジルエーテル；２−エチルヘキシルグリシジ
ルエーテル；フェニルグリシジルエーテル；フェノール
グリシジルエーテル；ｐ−ｔ−ブチルフェニルグリシジ
ルエーテル；アジピン酸ジグリシジルエステル；ｏ−フ
タル酸ジグリシジルエステル；グリシジルメタクリレー
ト；ブチルグリシジルエーテル等が挙げられる。また、
エポキシ基を含有した分子量が数百から数千のオリゴマ
ーや重量平均分子量が数千から数十万のポリマーを添加
することによっても同様の効果が得られる。これらエポ
キシ基含有化合物の添加量はエチレン−酢酸ビニル共重
合体１００重量部に対し０．１〜２０重量部で十分で、
上記エポキシ基含有化合物の少なくとも１種を単独で又
は混合して添加することができる。Furthermore, an epoxy group-containing compound can be added to the adhesive of the present invention for the purpose of improving the adhesiveness. Examples of the epoxy group-containing compound include triglycidyl tris (2-hydroxyethyl) isocyanurate; neopentyl glycol diglycidyl ether;
1,6-hexanediol diglycidyl ether; acrylic glycidyl ether; 2-ethylhexyl glycidyl ether; phenyl glycidyl ether; phenol glycidyl ether; pt-butylphenyl glycidyl ether; adipic acid diglycidyl ester; o-phthalic acid diglycidyl ester Glycidyl methacrylate; butyl glycidyl ether and the like. Also,
Similar effects can be obtained by adding an oligomer having an epoxy group and having a molecular weight of hundreds to thousands or a polymer having a weight average molecular weight of thousands to hundreds of thousands. The addition amount of these epoxy group-containing compounds is sufficient to be 0.1 to 20 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer,
At least one of the above epoxy group-containing compounds can be added alone or in combination.

【００１９】更に、本発明の光硬化性接着剤の物性（機
械的強度、光学的特性、接着性、耐熱性、耐湿熱性、耐
候性、架橋速度）などの改良や調節のために、本発明に
おいては、アクリロキシ基、メタクリロキシ基又はアリ
ル基含有化合物を添加することができる。Further, in order to improve and adjust the physical properties (mechanical strength, optical properties, adhesiveness, heat resistance, heat and moisture resistance, weather resistance and crosslinking speed) of the photocurable adhesive of the present invention, In the above, an acryloxy group, methacryloxy group or allyl group-containing compound can be added.

【００２０】この目的に供せられる化合物としては、ア
クリル酸或いはメタアクリル酸誘導体、例えばそのエス
テルやアミドが最も一般的である。この場合、エステル
残基としては、メチル、エチル、ドデシル、ステアリ
ル、ラウリルのようなアルキル基の他に、シクロヘキシ
ル基、テトラヒドロフルフリル基、アミノエチル基、２
−ヒドロエチル基、３−ヒドロキシプロピル基、３−ク
ロロ−２−ヒドロキシプロピル基などが挙げられる。ま
た、アクリル酸又はメタクリル酸とエチレングリコー
ル、トリエチレングリコール、ポリエチレングリコー
ル、グリセリン、トリメチロールプロパン、ペンタエリ
スリトール等の多官能アルコールとのエステルも同様に
用いられる。アミドとしては、アクリルアミドが代表的
である。また、アリル基含有化合物としては、トリアリ
ルシアヌレート、トリアリルイソシアヌレート、フタル
酸ジアリル、イソフタル酸ジアリル、マレイン酸ジアリ
ル等が挙げられ、これらの１種又は２種以上の混合物
が、エチレン−酢酸ビニル共重合体１００重量部に対し
０．１〜５０重量部、好ましくは０．５〜２０重量部添
加して用いられる。０．１重量部未満であると耐熱性、
機械的強度向上という改良効果を低下させることがあ
り、５０重量部を超えると接着剤の調製時の作業性や製
膜性を低下させることがある。As the compound used for this purpose, acrylic acid or methacrylic acid derivatives, for example, esters and amides thereof are most common. In this case, as an ester residue, in addition to an alkyl group such as methyl, ethyl, dodecyl, stearyl, lauryl, a cyclohexyl group, a tetrahydrofurfuryl group, an aminoethyl group,
-Hydroethyl group, 3-hydroxypropyl group, 3-chloro-2-hydroxypropyl group and the like. Esters of acrylic acid or methacrylic acid with polyfunctional alcohols such as ethylene glycol, triethylene glycol, polyethylene glycol, glycerin, trimethylolpropane, and pentaerythritol are also used. A typical amide is acrylamide. Examples of the allyl group-containing compound include triallyl cyanurate, triallyl isocyanurate, diallyl phthalate, diallyl isophthalate, diallyl maleate, and the like. One or a mixture of two or more thereof is ethylene-acetic acid. It is used in an amount of 0.1 to 50 parts by weight, preferably 0.5 to 20 parts by weight, based on 100 parts by weight of the vinyl copolymer. Heat resistance is less than 0.1 parts by weight,
The effect of improving the mechanical strength may be reduced, and if it exceeds 50 parts by weight, the workability and the film forming property at the time of preparing the adhesive may be reduced.

【００２１】なおまた、本発明の接着剤には、加工性や
貼り合わせ等の加工性向上の目的で炭化水素樹脂を添加
することができる。この場合、添加される炭化水素樹脂
は天然樹脂系、合成樹脂系のいずれでも差支えない。天
然樹脂系ではロジン、ロジン誘導体、テルペン系樹脂が
好適に用いられる。ロジンではガム系樹脂、トール油系
樹脂、ウッド系樹脂を用いることができる。ロジン誘導
体としてはロジンをそれぞれ水素化、不均一化、重合、
エステル化、金属塩化したものを用いることができる。
テルペン系樹脂ではα−ピネン、β−ピネンなどのテル
ペン系樹脂のほか、テルペンフェノール樹脂を用いるこ
とができる。また、その他の天然樹脂としてダンマル、
コーバル、シェラックを用いても差支えない。一方、合
成樹脂系では石油系樹脂、フェノール系樹脂、キシレン
系樹脂が好適に用いられる。石油系樹脂では脂肪族系石
油樹脂、芳香族系石油樹脂、脂環族系石油樹脂、共重合
系石油樹脂、水素化石油樹脂、純モノマー系石油樹脂、
クマロンインデン樹脂を用いることができる。フェノー
ル系樹脂ではアルキルフェノール樹脂、変性フェノール
樹脂を用いることができる。キシレン系樹脂ではキシレ
ン樹脂、変性キシレン樹脂を用いることができる。Further, a hydrocarbon resin can be added to the adhesive of the present invention for the purpose of improving processability and processability such as bonding. In this case, the hydrocarbon resin to be added may be either a natural resin or a synthetic resin. Rosin, rosin derivatives, and terpene resins are preferably used in the natural resin system. For rosin, gum-based resins, tall oil-based resins, and wood-based resins can be used. As rosin derivatives, rosin is hydrogenated, heterogenized, polymerized,
Esterified or metal salted ones can be used.
As the terpene-based resin, terpene-based resins such as α-pinene and β-pinene, as well as terpene phenol resins can be used. Also, Dammar as other natural resin,
Coral and shellac can be used. On the other hand, in the case of synthetic resins, petroleum resins, phenol resins, and xylene resins are preferably used. Petroleum resins include aliphatic petroleum resins, aromatic petroleum resins, alicyclic petroleum resins, copolymerized petroleum resins, hydrogenated petroleum resins, pure monomer petroleum resins,
Coumarone indene resin can be used. As the phenolic resin, an alkylphenol resin and a modified phenol resin can be used. As the xylene-based resin, a xylene resin or a modified xylene resin can be used.

【００２２】上記炭化水素樹脂の添加量は適宜選択され
るが、エチレン−酢酸ビニル共重合体１００重量部に対
して１〜２００重量部が好ましく、より好ましくは５〜
１５０重量部である。The amount of the hydrocarbon resin to be added is appropriately selected, but is preferably 1 to 200 parts by weight, more preferably 5 to 200 parts by weight, per 100 parts by weight of the ethylene-vinyl acetate copolymer.
It is 150 parts by weight.

【００２３】以上の添加剤の他、本発明の光硬化性接着
剤は紫外線吸収剤、老化防止剤、染料、加工助剤等を少
量含んでいてもよい。また、場合によってはシリカゲ
ル、炭酸カルシウム、シリコン共重合体の微粒子等の添
加剤を少量含んでもよい。In addition to the above additives, the photocurable adhesive of the present invention may contain a small amount of an ultraviolet absorber, an antioxidant, a dye, a processing aid and the like. In some cases, additives such as silica gel, calcium carbonate, silicon copolymer fine particles and the like may be contained in a small amount.

【００２４】本発明の光硬化性接着剤は、エチレン−酢
酸ビニル共重合体と上述の添加剤とを均一に混合し、押
出機、ロール等で混練した後、カレンダー、ロール、Ｔ
ダイ押出、インフレーション等の製膜法により所定の形
状に製膜して用いることができる。より好ましい本発明
の光硬化性接着剤の製膜方法は、各構成成分を良溶媒に
均一に混合溶解し、この溶液をシリコーンやフッ素樹脂
を精密にコートしたセパレーターにフローコート法、ロ
ールコート法、グラビアロール法、マイヤバー法、リッ
プダイコート法等により塗工し、溶媒を乾燥することに
より製膜する方法である。The photocurable adhesive of the present invention is prepared by uniformly mixing an ethylene-vinyl acetate copolymer and the above-mentioned additives, kneading the mixture with an extruder, a roll, or the like, and then calendering, rolling, and molding the mixture.
The film can be formed into a predetermined shape by a film forming method such as die extrusion or inflation and used. A more preferred method of forming a photocurable adhesive of the present invention is to uniformly mix and dissolve each component in a good solvent, and apply this solution to a separator precisely coated with silicone or a fluororesin by flow coating or roll coating. A gravure roll method, a Myrbar method, a lip die coating method, and the like, and a solvent is dried to form a film.

【００２５】なお、製膜に際してはブロッキング防止、
基材（透明樹脂基板）との圧着時の脱気を容易にするた
め、エンボス加工を施してもよい。エンボス加工の方法
としては公知の手法が採用でき、例えばエンボスロール
での型付け等がある。また、溶液塗工法の場合、離型性
を有するエンボスフィルム（紙）上に塗工することによ
り、そのエンボスを転写することができる。このエンボ
スの平均粗さ（Ｒａ）は５０μｍ以下、より好ましくは
０．０１〜５０μｍ、更に好ましくは０．１〜２０μｍ
の凸凹を形成することが好ましく、これによりデバイス
との接着面において空気が抜け易く、デバイス表面の複
雑な凸凹を埋めることが可能である。０．０１μｍより
小さいと脱気不良を起こし易く、また５０μｍより大き
いと仮圧着時に凸凹が残ってしまうこともある。When forming a film, blocking is prevented.
Embossing may be performed to facilitate degassing during pressure bonding with the base material (transparent resin substrate). As a method of embossing, a known method can be adopted, and for example, there is embossing roll molding or the like. In the case of the solution coating method, the emboss can be transferred by applying the composition on an embossed film (paper) having a releasing property. The average roughness (Ra) of the emboss is 50 μm or less, more preferably 0.01 to 50 μm, and still more preferably 0.1 to 20 μm.
It is preferable to form irregularities, whereby air can easily escape from the bonding surface with the device, and complicated irregularities on the device surface can be filled. If it is smaller than 0.01 μm, poor degassing tends to occur, and if it is larger than 50 μm, irregularities may remain during temporary press bonding.

【００２６】また、接着剤の厚さは１〜１０００μｍ、
特に５〜５００μｍとすることが好ましい。１μｍより
薄いと封止性が劣り、透明樹脂基板の凸凹を埋め切れな
い場合が生じる。一方、１０００μｍより厚いと記録媒
体の厚みが増し、記録媒体の収納、アッセンブリー等に
問題が生じるおそれがあり、更に光線透過に影響を与え
るおそれもある。The thickness of the adhesive is 1 to 1000 μm,
In particular, the thickness is preferably 5 to 500 μm. When the thickness is less than 1 μm, the sealing property is poor, and there are cases where the unevenness of the transparent resin substrate cannot be completely filled. On the other hand, if the thickness is more than 1000 μm, the thickness of the recording medium increases, which may cause problems in storage of the recording medium, assembly, and the like, and may further affect light transmission.

【００２７】本発明の光硬化性接着剤を硬化する場合
は、光源として紫外〜可視領域に発光する多くのものが
採用でき、例えば超高圧、高圧、低圧水銀灯、ケミカル
ランプ、キセノンランプ、ハロゲンランプ、マーキュリ
ーハロゲンランプ、カーボンアーク灯、白熱灯、レーザ
ー光等が挙げられる。照射時間は、ランプの種類、光源
の強さによって一概には決められないが、数十秒〜数十
分程度である。When the photocurable adhesive of the present invention is cured, many light sources that emit light in the ultraviolet to visible region can be used as the light source. For example, ultrahigh pressure, high pressure, low pressure mercury lamps, chemical lamps, xenon lamps, halogen lamps , A mercury halogen lamp, a carbon arc lamp, an incandescent lamp, a laser beam and the like. The irradiation time cannot be determined unconditionally depending on the type of lamp and the intensity of the light source, but is about several tens of seconds to several tens of minutes.

【００２８】また、硬化促進のために、予め積層体を３
０〜８０℃に加温し、これに紫外線を照射してもよい。In order to accelerate curing, the laminate is
It may be heated to 0 to 80 ° C. and irradiated with ultraviolet rays.

【００２９】本発明における記録媒体の製造方法を以下
に例示するが、必ずしもこれらの方法に限定されるもの
ではなく、本発明の目的を達成し得る方法であればいず
れの方法を用いてもよい。The method for producing a recording medium according to the present invention is described below, but is not necessarily limited to these methods, and any method may be used as long as the object of the present invention can be achieved. .

【００３０】まず、異なる信号面を転写した金属板（ス
タンパ）にそれぞれ前記透明樹脂の溶融物を流し込み固
める。一層目の透明樹脂基板には、金属膜或いは誘電体
膜からなる半透明層を形成し、二層目の透明樹脂基板に
は金属膜からなる反射層を形成する。この２枚の透明樹
脂基板の信号面を対向させ、予めセパレーターの上に形
成させた、前記光硬化性接着剤フィルムを片側の透明樹
脂基板の信号面側に転写し、セパレーターを剥がす。こ
れにもう一枚の透明樹脂基板をかぶせ、加圧ロール、加
圧プレス、真空袋、真空ラミネーター等で仮圧着する。
仮圧着と同時に３０〜１００℃程度の熱を加え、効率を
上げることもできる。仮圧着を行った積層体を取り出
し、まとめて大型或いは連続の光（ＵＶ）照射装置を通
して光硬化させる。この時、硬化促進のために３０〜８
０℃に熱を加えてもよい。本発明の記録媒体に用いられ
る光硬化性接着剤フィルムは、加熱時の溶融粘度が５０
００ｃｐｓ以上であるため、液状の紫外線硬化性樹脂の
ように硬化時に積層体の端部より接着剤がはみ出し垂れ
ることが全くなく、また予め所定の厚みに精度良くセパ
レーター上に形成させることができるため、記録信号の
読み出し時のエラーのない記録媒体を提供することが可
能である。First, a melt of the transparent resin is poured into a metal plate (stamper) onto which different signal surfaces have been transferred, and solidified. A translucent layer made of a metal film or a dielectric film is formed on the first transparent resin substrate, and a reflection layer made of a metal film is formed on the second transparent resin substrate. The signal surfaces of the two transparent resin substrates are opposed to each other, the photocurable adhesive film previously formed on the separator is transferred to the signal surface side of one transparent resin substrate, and the separator is peeled off. This is covered with another transparent resin substrate, and temporarily pressure-bonded with a pressure roll, a pressure press, a vacuum bag, a vacuum laminator, or the like.
Efficiency can also be increased by applying heat of about 30 to 100 ° C. at the same time as the temporary pressing. The preliminarily pressed laminate is taken out and collectively light cured through a large or continuous light (UV) irradiation device. At this time, 30 to 8 to accelerate the curing
Heat may be applied to 0 ° C. The photocurable adhesive film used in the recording medium of the present invention has a melt viscosity of 50 when heated.
Since it is not less than 00 cps, the adhesive does not protrude from the end of the laminate at the time of curing like a liquid ultraviolet curable resin, and it can be formed on the separator with a predetermined thickness with high precision. In addition, it is possible to provide a recording medium free from errors when reading a recording signal.

【００３１】[0031]

【実施例】以下、実施例及び比較例を示し、本発明を具
体的に説明するが、本発明は下記の実施例に制限される
ものではない。EXAMPLES The present invention will be described below in detail with reference to Examples and Comparative Examples, but the present invention is not limited to the following Examples.

【００３２】〔実施例、比較例〕表１に示す配合Ｎｏ．
Ａ〜Ｃの各成分をエチレン−酢酸ビニル共重合体１００
重量部に対し所定量を秤量し、これを４０℃のトルエン
中で均一に混合溶解し、溶質濃度２０％のトルエン溶液
を調製した。この溶液をシリコン離型処理したポリエス
テル製エンボス付（Ｒａ＝１．５μｍ）セパレーター上
にリバースロールコーターを用いて塗布し、ドライ厚み
で４０±１μｍの膜厚精度を有する光硬化性接着剤フィ
ルムを作製した。[Examples and Comparative Examples]
Each component of A to C is an ethylene-vinyl acetate copolymer 100
A predetermined amount was weighed to the parts by weight, and this was uniformly mixed and dissolved in toluene at 40 ° C. to prepare a toluene solution having a solute concentration of 20%. This solution is applied to a polyester release-treated polyester embossed (Ra = 1.5 μm) separator using a reverse roll coater, and a photocurable adhesive film having a dry thickness of 40 ± 1 μm is obtained. Produced.

【００３３】２枚のポリカーボネート製透明樹脂基板の
それぞれ片面に予め信号面を転写し、それぞれの信号面
側に誘電体材料及びアルミニウムの反射層を設けた厚み
０．６ｍｍの透明樹脂基板を準備した。１枚目の透明樹
脂基板の信号面側に上記光硬化性接着剤フィルムを転写
し、セパレーターを剥がした。この光硬化性接着剤フィ
ルム面側に、もう１枚の透明樹脂基板の信号面側を対向
させ重ね合わせた。この積層体を５０℃に設定した熱プ
レスを用い、１ｋｇｆ／ｃｍ²の圧力を１０分間かけて
仮圧着を行った。次に、プレスから取り出した積層体
を、４ｋＷの高圧水銀ランプの下で１分間照射し、光硬
化性接着剤フィルムの硬化を完了し、本発明の記録媒体
を得た。A signal surface was previously transferred to one surface of each of the two polycarbonate transparent resin substrates, and a 0.6 mm thick transparent resin substrate provided with a dielectric material and an aluminum reflective layer on each signal surface side was prepared. . The photocurable adhesive film was transferred to the signal side of the first transparent resin substrate, and the separator was peeled off. Another transparent resin substrate was superposed on the photocurable adhesive film surface with the signal surface side facing the photocurable adhesive film surface. Using a hot press set at 50 ° C., the laminated body was subjected to temporary pressure bonding at a pressure of 1 kgf / cm ² for 10 minutes. Next, the laminate taken out of the press was irradiated for 1 minute under a high-pressure mercury lamp of 4 kW to complete the curing of the photocurable adhesive film, thereby obtaining a recording medium of the present invention.

【００３４】硬化後の記録媒体の板厚偏差は、いずれも
±３．５μｍ以下という極めて精度の高い、即ち記録さ
れた信号の再生には申し分のない板厚偏差であることが
確認できた。It was confirmed that the thickness deviation of the cured recording medium was extremely high, that is, ± 3.5 μm or less, that is, the thickness deviation was satisfactory for reproducing recorded signals.

【００３５】これに対し、比較例として、市販の光硬化
性接着剤（商品名フォトボンド：サンライズサンセイ
（株）製）を用い、目標膜厚４０μｍでスピンコートに
より製膜したが、４ｋＷの高圧水銀ランプを１分間照射
後の板厚偏差を測定すると、±８．５μｍと板厚精度の
点で劣っていた。On the other hand, as a comparative example, a commercially available photocurable adhesive (trade name: Photobond: manufactured by Sunrise Sansei Co., Ltd.) was used to form a film with a target film thickness of 40 μm by spin coating. When the thickness deviation after irradiation with a mercury lamp for 1 minute was measured, it was inferior in thickness accuracy to ± 8.5 μm.

【００３６】更に実施例及び比較例の各記録媒体の信頼
性試験を実施した。その結果を表２に示す。信頼性試験
の評価項目としては、耐熱耐久性（８５℃×１０００時
間）、湿熱耐久性（６０℃、９０％ＲＨ×１０００時
間）、冷熱サイクル耐久試験（−３０℃×６時間→７０
℃×６時間の５０サイクル）の３種類について実施し
た。判定基準としては、試験終了後、接着剥離や反り、
ズレ等の外観変化の有無を目視により観察した。Further, a reliability test was performed on each recording medium of the examples and comparative examples. Table 2 shows the results. Evaluation items of the reliability test include heat resistance (85 ° C. × 1000 hours), wet heat resistance (60 ° C., 90% RH × 1000 hours), and heat cycle resistance test (−30 ° C. × 6 hours → 70).
(50 cycles of 6 ° C. × 6 hours). As a criterion, after the end of the test,
The presence or absence of a change in appearance such as displacement was visually observed.

【００３７】[0037]

【表１】 [Table 1]

【００３８】[0038]

【表２】 [Table 2]

【００３９】各配合Ａ〜Ｃにおいて、エチレン−酢酸ビ
ニル共重合体として上記（１）〜（４）のものを用いた
いずれの本発明による記録媒体も、上記各信頼性試験で
異常が認められず、信頼性に優れた記録媒体が得られる
ことが確認された。In each of the formulations A to C, any of the recording media according to the present invention using the above-mentioned (1) to (4) as the ethylene-vinyl acetate copolymer showed abnormalities in the above reliability tests. It was confirmed that a recording medium having excellent reliability was obtained.

【００４０】[0040]

【発明の効果】本発明の記録媒体は、板厚精度に優れ、
信号の再生精度が高く、更に各種耐久性に優れたもの
で、高信頼性を有し、しかも容易に高精度に製造するこ
とができる。The recording medium of the present invention has excellent plate thickness accuracy,
It has high signal reproduction accuracy and various durability, has high reliability, and can be easily manufactured with high accuracy.

【図面の簡単な説明】[Brief description of the drawings]

【図１】両面読み出し方式デジタルビデオディスクの一
例を示す概略断面図である。FIG. 1 is a schematic cross-sectional view showing an example of a digital video disk of a double-sided reading system.

【図２】片面読み出し方式デジタルビデオディスクの一
例を示す概略断面図である。FIG. 2 is a schematic sectional view showing an example of a single-side read digital video disc.

【符号の説明】[Explanation of symbols]

１ 透明樹脂基板 １ａ 反射層 １ｂ 半透明層 ２ 透明樹脂基板 ２ａ 反射層 ３ 接着剤層 DESCRIPTION OF SYMBOLS 1 Transparent resin substrate 1a Reflective layer 1b Translucent layer 2 Transparent resin substrate 2a Reflective layer 3 Adhesive layer

フロントページの続き (51)Int.Cl.⁷ 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｊ 123/08 Ｃ０９Ｊ 123/08 131/04 131/04 Ｓ (72)発明者 稲宮 隆人 東京都小平市小川東町３−１−１ 株式会 社ブリヂストン技術センター内 (72)発明者 森村 泰大 東京都小平市小川東町３−１−１ 株式会 社ブリヂストン技術センター内 Ｆターム(参考） 4F100 AH06G AK01A AK01B AK02G AK68G AS00G BA02 CA30G CB04 GB90 JD04 JJ03 JL00 JN01A JN01B JN02A JN02B JN06A JN06B YY00G 4J040 BA192 BA202 DA051 DK012 DN032 DN072 EB032 EB082 EL012 FA062 FA092 FA102 FA142 FA152 FA172 FA282 HB13 HB19 HD19 HD27 HD32 HD35 HD36 HD37 JA09 JB08 KA13 KA26 LA06 LA10 MA10 MB05 NA17 NA21 5D029 RA30 RA33 RA38 RA45 RA46Continued on the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat II (Reference) C09J 123/08 C09J 123/08 131/04 131/04 S (72) Inventor Takato Inamiya 3 Ogawa Higashicho, Kodaira-shi, Tokyo -1-1 Inside Bridgestone Technology Center (72) Inventor Yasuhiro Morimura 3-1-1 Ogawa-Higashicho, Kodaira-shi, Tokyo F-term (reference) 4F100 AH06G AK01A AK01B AK02G AK68G AS00G BA02 CA30G CB04 GB90 JD04 JJ03 JL00 JN01A JN01B JN02A JN02B JN06A JN06B YY00G 4J040 BA192 BA202 DA051 DK012 DN032 DN072 EB032 EB082 EL012 FA062 FA092 FA102 FA142 FA152 FA172 FA282 HB13 HDB13 HD19 HD19 HD19 RA33 RA38 RA45 RA46

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 ２枚の透明樹脂基板をエチレン−酢酸ビ
ニル共重合体を主成分とするフィルム状の光硬化性接着
剤により接合してなることを特徴とする記録媒体。1. A recording medium comprising two transparent resin substrates joined by a film-like photocurable adhesive containing an ethylene-vinyl acetate copolymer as a main component. 【請求項２】 ２枚の透明樹脂基板が、それぞれ反射層
を有するデジタルビデオディスク用基板、又は一方が反
射層、他方が半透明層を有するデジタルビデオディスク
用基板である請求項１記載の記録媒体。2. The recording according to claim 1, wherein the two transparent resin substrates are digital video disk substrates each having a reflective layer, or one is a digital video disk substrate having a reflective layer and the other is a translucent layer. Medium. 【請求項３】 光硬化性接着剤が、エチレン−酢酸ビニ
ル共重合体１００重量部に対し、光増感剤を０．１〜１
０重量部、シランカップリング剤を０．０１〜５重量部
添加してなることを特徴とする請求項１又は２記載の記
録媒体。3. A photocurable adhesive comprising a photosensitizer in an amount of 0.1 to 1 with respect to 100 parts by weight of an ethylene-vinyl acetate copolymer.
3. The recording medium according to claim 1, wherein 0 parts by weight and 0.01 to 5 parts by weight of a silane coupling agent are added. 【請求項４】 光硬化性接着剤が、エチレン−酢酸ビニ
ル共重合体１００重量部に対し、アクリロキシ基含有化
合物、メタクリロキシ基含有化合物及びアリル基含有化
合物のうち少なくとも１つを０．１〜５０重量部添加し
てなることを特徴とする請求項１，２又は３記載の記録
媒体。4. A photocurable adhesive comprising at least one of an acryloxy group-containing compound, a methacryloxy group-containing compound and an allyl group-containing compound in an amount of 0.1 to 50 parts by weight per 100 parts by weight of an ethylene-vinyl acetate copolymer. 4. The recording medium according to claim 1, wherein the recording medium is added in parts by weight. 【請求項５】 光硬化性接着剤が、エチレン−酢酸ビニ
ル共重合体１００重量部に対し、炭化水素樹脂を１〜２
００重量部添加してなることを特徴とする請求項１乃至
４のいずれか１項記載の記録媒体。5. A photocurable adhesive comprising a hydrocarbon resin in an amount of from 1 to 2 parts by weight based on 100 parts by weight of an ethylene-vinyl acetate copolymer.
The recording medium according to any one of claims 1 to 4, wherein the recording medium is added by 00 parts by weight. 【請求項６】 エチレン−酢酸ビニル共重合体の酢酸ビ
ニル含有率が１０〜５０重量％であることを特徴とする
請求項１乃至５のいずれか１項記載の記録媒体。6. The recording medium according to claim 1, wherein the ethylene-vinyl acetate copolymer has a vinyl acetate content of 10 to 50% by weight. 【請求項７】 フィルム状の光硬化性接着剤の厚さが１
〜１０００μｍである請求項１乃至６のいずれか１項記
載の記録媒体。7. A film-like photocurable adhesive having a thickness of 1
The recording medium according to any one of claims 1 to 6, wherein the thickness is from 1000 to 1000 µm.