JP2000200329A - Card - Google Patents
CardInfo
- Publication number
- JP2000200329A JP2000200329A JP44299A JP44299A JP2000200329A JP 2000200329 A JP2000200329 A JP 2000200329A JP 44299 A JP44299 A JP 44299A JP 44299 A JP44299 A JP 44299A JP 2000200329 A JP2000200329 A JP 2000200329A
- Authority
- JP
- Japan
- Prior art keywords
- card
- sheet
- polycarbonate
- amorphous polyester
- heat resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えばキャッシュ
カードやクレジットカード、ＩＤカード（身分証明
書）、会員証、プリペイドカード等に用いられる情報記
録媒体に関するもので、さらに詳しくは、高温中で保存
する可能性のある車載用やコンピュータ等の家電製品内
で使用された場合でも変形せず、更には、これらが使用
後に廃棄された時により廃棄しやすいようにしたカード
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an information recording medium used for a cash card, a credit card, an ID card (identification card), a membership card, a prepaid card, and the like. The present invention relates to a card which does not deform even when used in home electric appliances such as in-vehicles and computers which may be used, and which is more easily discarded when discarded after use.
【０００２】[0002]
【従来の技術】従来から、キャッシュカード、クレジッ
トカード及びＩＤカード等の分野において、磁気記録媒
体が広く利用されており、その素材としては主にポリ塩
化ビニル（ＰＶＣ）樹脂や塩化ビニル・酢酸ビニル共重
合体が用いられており、特にポリ塩化ビニル樹脂が一般
的である。ポリ塩化ビニル樹脂は物理的な機械特性や文
字部のエンボス適性などが優れており、カード素材とし
ては申し分なく最適な素材として現在も広く用いられて
いる。2. Description of the Related Art Conventionally, magnetic recording media have been widely used in the fields of cash cards, credit cards, ID cards and the like, and are mainly made of polyvinyl chloride (PVC) resin or vinyl chloride / vinyl acetate. Copolymers are used, and polyvinyl chloride resin is particularly common. Polyvinyl chloride resin is excellent in physical mechanical properties and embossability of a character portion, and is widely used as a perfect material for card materials.
【０００３】しかし、近年、磁気記録媒体はキャッシュ
カードやクレジットカード、ＩＤカード等の分野に留ま
らず、接触式のＩＣモジュールを埋め込んだ磁気ストラ
イプ付きＩＣカードやアンテナとＩＣモジュールを組み
込んだ磁気ストライプ付き非接触ＩＣカード、又はそれ
ら全てを持ち合わせたカードなど種々ある。また、アプ
リケーションとしては、電子財布や定期券、テレホンカ
ード、免許証、車載カードなどがあげられ、このような
カードに用いる素材には、従来のカード素材以上に屈曲
性、スクラッチ強度、引っ張り強度などの強度や、保存
特性、耐熱性、耐薬品性等の耐性を含めた高い信頼性が
求められている。更に、ポリ塩化ビニル樹脂は、使用後
の廃棄において、特に焼却時の塩化水素ガスを発生させ
焼却炉を傷めて寿命を縮める等の問題を有している。ま
た、ダイオキシンとの関連性は明確にはなってはいない
ものの、この点でドイツや北欧などをはじめとする各国
で脱ＰＶＣの動きが活発になってきており、国内でも建
材分野や産業資材分野でその流れにある。In recent years, however, magnetic recording media are not limited to the fields of cash cards, credit cards, ID cards, etc., but also include magnetic cards with a magnetic stripe embedded with a contact type IC module and magnetic stripes with an antenna and an IC module. There are various types such as a non-contact IC card and a card having all of them. Applications include electronic wallets, commuter passes, telephone cards, driver's licenses, on-board cards, etc. The materials used for such cards are more flexible than conventional card materials, such as scratch strength, tensile strength, etc. There is a demand for high reliability including strength, storage characteristics, heat resistance, and chemical resistance. Further, the polyvinyl chloride resin has a problem in disposal after use, such as generation of hydrogen chloride gas particularly during incineration, damaging the incinerator and shortening its life. Also, although the relationship with dioxin has not been clarified, in this regard, countries such as Germany and Northern Europe have been actively pursuing the removal of PVC, and in the construction materials and industrial materials fields in Japan. In that flow.
【０００４】一般的な磁気カードの製造方法は、白色の
塩化ビニル（ＰＶＣ）基材にオフセット印刷、グラビア
印刷、スクリーン印刷等公知の印刷方法で印刷を施し、
その両面に透明性の高いＰＶＣシートを積層した後、磁
気テープを転写し、加熱プレス機で熱融着を行い、ＰＶ
Ｃ基材積層品と磁気テープを一体化させ、所定サイズの
金型で打ち抜いてカード形状にする。熱転写タイプの磁
気テープは転写後にはカード表面より浮き出て段差を生
じているが、加熱プレス機での熱融着によって埋め込ま
れ、カード表面と面一になる。A general method of manufacturing a magnetic card is to print on a white vinyl chloride (PVC) substrate by a known printing method such as offset printing, gravure printing, or screen printing.
After laminating a highly transparent PVC sheet on both sides, the magnetic tape is transferred, and heat fusion is performed with a heating press machine.
The C base laminate and the magnetic tape are integrated and punched out with a mold of a predetermined size to form a card shape. After the transfer, the magnetic tape of the thermal transfer type protrudes from the surface of the card after the transfer and has a step.
【０００５】ちなみに、カード表面の状態は、ＪＩＳＸ
６３０１４．２．６項で以下のように決められている。
「磁気ストライプの周囲それぞれから、６．３５ｍｍの
領域には磁気ストライプに対する情報の正常な書き込み
又は磁気ストライプに記録された情報の正常な読み取り
を損なう恐れのある表面不連続部を設けないこと。更
に、II型においてはカードの下端から２４ｍｍ以上の範
囲で０．０５ｍｍ以上のとつ部を設けないこと。・・
・」[0005] Incidentally, the state of the card surface is JISX
It is determined as follows in 630142.6.
"A region of 6.35 mm from the periphery of the magnetic stripe is not provided with a surface discontinuity that may impair normal writing of information on the magnetic stripe or normal reading of information recorded on the magnetic stripe. In the case of type II, do not provide a shank of 0.05 mm or more within a range of 24 mm or more from the bottom of the card.-
・ "
【０００６】磁気カードにおける磁気テープの役割は、
個人の持っている固有データを記録し、使用時に固有デ
ータの読み取りや書き込みをすることである。従って、
もし、この磁気テープがカード表面と面一になっていな
いと、カード携帯時や、リーダ／ライターによる繰り返
し使用で、磁気テープのエッジ部が破損、または欠損
し、磁気テープの持つ役割をしない使用不可能な磁気カ
ードとなってしまう恐れがある。The role of a magnetic tape in a magnetic card is
It is to record the unique data possessed by the individual, and to read and write the unique data at the time of use. Therefore,
If the magnetic tape is not flush with the surface of the card, the edge of the magnetic tape will be damaged or lost when the card is carried or when it is repeatedly used by a reader / writer. There is a risk that the card will become an impossible magnetic card.
【０００７】一般カード素材として用いられているポリ
塩化ビニル樹脂の物性の欠点として耐熱性の低いことが
あげられる。一般的にポリ塩化ビニル樹脂は約６０℃で
軟化し、変形するため、高温域でのアプリケーション、
例えば家電用、車載用などには適さないと考えられる。
更に、廃棄時の問題や脱ＰＶＣ活動の流れがあるため、
ポリ塩化ビニル樹脂の使用は問題になる。A disadvantage of the physical properties of polyvinyl chloride resin used as a general card material is that heat resistance is low. In general, polyvinyl chloride resin softens and deforms at about 60 ° C.
For example, it is considered unsuitable for home appliances, vehicles and the like.
Furthermore, due to disposal issues and the flow of PVC removal activities,
The use of polyvinyl chloride resin is problematic.
【０００８】そこで、ポリエチレン樹脂、ポリプロピレ
ン樹脂、ポリエステル樹脂、ポリカーボネート樹脂、ポ
リアクリル樹脂等のハロゲンを含まない熱可塑性樹脂を
用いて、カード化する考えがある。これらの樹脂を単体
で用いて、ポリ塩化ビニル樹脂同様にカード化すること
は可能であるが、カードとしての物性において、ポリ塩
化ビニル樹脂に劣り、工夫が必要となってくる。[0008] Therefore, there is a plan to make a card using a halogen-free thermoplastic resin such as a polyethylene resin, a polypropylene resin, a polyester resin, a polycarbonate resin, and a polyacryl resin. These resins can be used alone to form a card in the same manner as a polyvinyl chloride resin, but the physical properties of the card are inferior to those of the polyvinyl chloride resin and require some contrivance.
【０００９】[0009]
【発明が解決しようとする課題】本発明は以上のような
問題点に着目してなされたもので、カード用基材として
ポリ塩化ビニル樹脂の代わりに、非晶性のポリエチレン
テレフタレート樹脂基材の両面に高耐熱性のポリカーボ
ネート樹脂を積層した後、磁気記録層を積層したことに
より、耐熱性の高い、使用後焼却された際に塩化水素の
問題やダイオキシンの問題がなく、廃棄処理を考慮した
カードを提案するものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems. Instead of a polyvinyl chloride resin as a card base, an amorphous polyethylene terephthalate resin base is used. After laminating a high heat-resistant polycarbonate resin on both sides, and by laminating the magnetic recording layer, there is no problem of hydrogen chloride or dioxin when incinerated after use with high heat resistance, considering disposal processing Suggest a card.
【００１０】[0010]
【課題を解決するための手段】本発明に於いて上記課題
を達成するために、まず請求項１の発明では、非晶性ポ
リエステルシート層の両面に、高耐熱性を有するポリカ
ーボネートシート層を積層した基材上に、磁気記録層な
どの情報を記録する層を積層することで、高耐熱性を有
することを特徴とするものである。In order to achieve the above object, the present invention firstly comprises laminating a polycarbonate sheet layer having high heat resistance on both sides of an amorphous polyester sheet layer. It is characterized by having high heat resistance by laminating a layer for recording information such as a magnetic recording layer on the base material thus formed.
【００１１】また、請求項２の発明では、上記非晶性ポ
リエステルシート層とポリカーボネートシート層を積層
した基材上に、磁気記録層やＩＣモジュール等の情報を
記録する機能を持たせたことを特徴とするものである。Further, in the invention of claim 2, a function of recording information such as a magnetic recording layer and an IC module is provided on the substrate on which the amorphous polyester sheet layer and the polycarbonate sheet layer are laminated. It is a feature.
【００１２】また、請求項３の発明では、上記非晶性ポ
リエステルシートはテレフタル酸と、シクロヘキサンジ
メタノール及びエチレングリコールとの共重合体、又は
その共重合体とポリカーボネートとのポリマーアロイで
あることを特徴とするものである。Further, in the invention of claim 3, it is preferable that the amorphous polyester sheet is a copolymer of terephthalic acid and cyclohexanedimethanol and ethylene glycol, or a polymer alloy of the copolymer and polycarbonate. It is a feature.
【００１３】請求項４の発明では、上記非晶性ポリエス
テルシートは、ガラス転移温度が８０度以上であること
を特徴とするものである。ガラス転移温度が８０度以下
の場合には、カードの耐熱性が低下してしまい好ましく
ない。According to a fourth aspect of the present invention, the amorphous polyester sheet has a glass transition temperature of 80 ° C. or higher. If the glass transition temperature is 80 ° C. or lower, the heat resistance of the card is undesirably reduced.
【００１４】請求項５の発明では、上記ポリカーボネー
トシートは、ビスフェノールＡを主成分とし、結晶化度
が３０％以下で、ガラス転移温度が１４０度以上である
ことを特徴とするものである。結晶化度が３０％より高
くなると、屈曲性などのカード適性が低下し、ガラス転
移温度が１４０度以下の場合には、カードの耐熱性が低
下してしまい好ましくない。According to a fifth aspect of the present invention, the polycarbonate sheet contains bisphenol A as a main component, has a crystallinity of 30% or less, and a glass transition temperature of 140 ° C. or more. If the crystallinity is higher than 30%, the suitability of the card, such as flexibility, is reduced. If the glass transition temperature is 140 ° C. or lower, the heat resistance of the card is lowered, which is not preferable.
【００１５】請求項６の発明では、上記非晶性ポリエス
テルシート及びポリカーボネートシートは各々押し出し
法によりシート化したことを特徴とするものである。According to a sixth aspect of the present invention, the amorphous polyester sheet and the polycarbonate sheet are each formed into a sheet by an extrusion method.
【００１６】[0016]
【発明の実施の形態】以下、本発明の実施の形態を説明
する。本発明のカードの構成の一例を図１に示す。本発
明における非晶性ポリエステル樹脂（１）は、ポリエチ
レンテレフタレート、又はポリエチレンテレフタレート
とポリカードネートとのポリマーアロイである。ポリエ
チレンテレフタレートはエチレングリコールとシクロヘ
キサンジメタノールをテレフタル酸と共重合させて製造
する。また、エチレングリコールとシクロヘキサンジメ
タノールの配合比を変えることで、結晶性及びガラス転
移温度を制御することが可能になる。本発明におけるポ
リカーボネート（２、３）は、ビスフェノールＡを主成
分とし、結晶化度が３０％以下でで、ガラス転移温度が
１４０度以上のものである。Embodiments of the present invention will be described below. FIG. 1 shows an example of the configuration of the card of the present invention. The amorphous polyester resin (1) in the present invention is polyethylene terephthalate or a polymer alloy of polyethylene terephthalate and polycardate. Polyethylene terephthalate is produced by copolymerizing ethylene glycol and cyclohexane dimethanol with terephthalic acid. Further, by changing the mixing ratio of ethylene glycol and cyclohexanedimethanol, it becomes possible to control the crystallinity and the glass transition temperature. The polycarbonate (2, 3) in the present invention has bisphenol A as a main component, a crystallinity of 30% or less, and a glass transition temperature of 140 ° C or more.
【００１７】本発明におけるポリエステルシート、ポリ
エステル及びポリカーボネートのアロイシート、及びポ
リカーボネートシートのシート化は、全て押し出し法に
より、シート化する。次に、本発明におけるカード素材
を用いたカード製造方法には、加熱プレス機による溶融
ラミネート方式がある。溶融ラミネート方式は、印刷さ
れた基材の両面に透明な保護シートを積層するが、その
際両面の保護シートの種類は異なっていてもよい。溶融
ラミネート方式は一回り大きい鏡面板で挟み込み、その
後加熱溶融プレスによりカード素材を一体化する方法で
ある。In the present invention, the polyester sheet, the alloy sheet of polyester and polycarbonate, and the polycarbonate sheet are all formed by extrusion. Next, as a card manufacturing method using a card material in the present invention, there is a melt lamination method using a heating press machine. In the melt lamination method, a transparent protective sheet is laminated on both sides of a printed base material, and at that time, the types of the protective sheets on both sides may be different. The melt lamination method is a method in which a card material is sandwiched between mirror plates that are one size larger, and then the card material is integrated by a hot melt press.
【００１８】この時に用いる鏡面板は、ニッケル−クロ
ムメッキした銅板、表面を研磨したステンレス板、表面
を研磨したアルミ板などを用いることができる。また、
基材への印刷は、紙やプラスチックフィルムの場合と同
じ方法、すなわち、オフセット印刷法、スクリーン印刷
法、グラビア印刷法等の公知の印刷法で文字或いは絵柄
を印刷することができる。As the mirror plate used at this time, a nickel-chromium-plated copper plate, a stainless plate having a polished surface, an aluminum plate having a polished surface, or the like can be used. Also,
The printing on the base material can be performed by the same method as that of paper or plastic film, that is, characters or pictures can be printed by a known printing method such as an offset printing method, a screen printing method, and a gravure printing method.
【００１９】溶融ラミネート後はカード素材を鏡面板か
ら剥がし、片刃またはオスーメスの金型による打ち抜き
でカード形状に打ち抜く。カードには、磁気記録層を設
けることもでき、カードの片面あるいは両面に、従来か
ら用いられている熱転写タイプの磁気テープを転写した
り、或いは、基材に直接磁気記録層を印刷する方法が用
いられる。通常、カード形状になった後は、エンボッサ
ーにより浮き文字をエンボスし、その文字の上に熱転写
箔によりティッピングして色付けしたり、磁気記録層に
磁気情報をエンコードしたり、場合によっては顔写真や
バーコード等を転写しカードを仕上げる。そして、文
字、絵柄印刷層の摩耗等の耐性を向上させる目的で保護
層を設ける事もできる。After the melt lamination, the card material is peeled off from the mirror surface plate, and the card material is punched into a card shape by punching with a single-edged or male-female mold. The card can be provided with a magnetic recording layer, and a method of transferring a conventionally used thermal transfer type magnetic tape to one or both sides of the card, or printing the magnetic recording layer directly on the base material is used. Used. Normally, after the card is formed, the embosser embosses the floating characters and then colors the characters by tipping them with a thermal transfer foil, encodes the magnetic information on the magnetic recording layer, and, in some cases, Transfer the barcode etc. to finish the card. Then, a protective layer can be provided for the purpose of improving the resistance of the character or picture printing layer to wear or the like.
【００２０】[0020]
【実施例】次に、本発明の実施例により、本発明を具体
的に説明する。 〈実施例１〉厚み５４０μｍの非晶性ポリエステルであ
る白色ＰＥＴＧシート（５）（三菱樹脂（株）製、ＰＥ
ＴＧ）に、オフセット印刷法により、絵柄印刷層（１
０）を膜厚１μｍで設け、更に磁気テープ（８）を転写
した厚み１００μｍの透明ＰＣシート（６）（帝人化成
（株）製、パンライト）と、裏面に文字（９）を印刷し
たシート（７）を両面に重ねた後、表面を平滑にしたス
テンレス板で挟み込み、１２０℃で２０分間圧着熱融着
させて冷却固化させた後カード形状に打ち抜いて図２に
示すような断面構造の実施例１のカードを作製した。Next, the present invention will be described in detail with reference to examples of the present invention. <Example 1> White PETG sheet (5) which is an amorphous polyester having a thickness of 540 µm (manufactured by Mitsubishi Plastics, Inc., PE
TG) on the pattern printing layer (1) by the offset printing method.
0) having a thickness of 1 μm, and a 100 μm-thick transparent PC sheet (6) (Panlite, manufactured by Teijin Chemicals Ltd.) onto which a magnetic tape (8) was transferred, and a sheet having characters (9) printed on the back surface After (7) was placed on both sides, it was sandwiched between stainless steel plates whose surfaces were smoothed, pressed and fused at 120 ° C. for 20 minutes, cooled and solidified, and then punched into a card shape to obtain a cross-sectional structure as shown in FIG. The card of Example 1 was produced.
【００２１】〈比較例１〉厚み１００μｍの透明ＰＣシ
ート（帝人化成（株）製、パンライト）の代わりに厚み
１００μｍの透明ＰＶＣシート（三菱樹脂（株）製、ビ
ニホイル）を用いた以外は実施例１と同様である比較例
１のカードを作製した。<Comparative Example 1> A 100 μm thick transparent PVC sheet (manufactured by Mitsubishi Plastics, Inc., vinyl foil) was used in place of a 100 μm thick transparent PC sheet (manufactured by Teijin Chemicals Ltd., Panlite). A card of Comparative Example 1 similar to that of Example 1 was produced.
【００２２】〈実施例２〉スクリーン印刷法により絵柄
印刷層（１４）を膜厚３μｍで設けた、厚み５００μｍ
の非晶性ポリエステルのＰＥＴＧ／ＰＣのアロイシート
（１１）（三菱樹脂（株）製）と磁気テープ（１５）を
転写した厚み１２０μmの透明ＰＣシート（１２）（東
洋プラスチック精工（株）製、ＰＣ）と裏面に文字（１
６）を印刷したシート（１３）を両面に重ねた後、表面
を平滑にしたステンレス板で挟み込み、１３０℃で２０
分間圧着熱融着させて冷却固化させた後カード形状に打
ち抜いて図３に示すような断面構造のカードを作製し
た。Example 2 A pattern printing layer (14) was provided with a film thickness of 3 μm by a screen printing method.
An amorphous polyester PETG / PC alloy sheet (11) (manufactured by Mitsubishi Plastics, Inc.) and a 120 μm-thick transparent PC sheet (12) onto which a magnetic tape (15) was transferred (manufactured by Toyo Plastic Seiko Co., Ltd. PC) and letters (1
After the sheet (13) on which 6) is printed is placed on both sides, the sheet (13) is sandwiched between stainless steel plates having smooth surfaces,
After being heat-bonded for 1 minute and cooled and solidified, it was punched into a card shape to produce a card having a sectional structure as shown in FIG.
【００２３】〈比較例２〉厚み５００μｍのＰＥＴＧ／
ＰＣのアロイシート（三菱樹脂（株）製）（１１）の代
わりに、ＡＢＳシート（旭化成工業（株）製、スタイラ
ック）を使用した以外は実施例２と同様である比較例２
のカードを作製した。Comparative Example 2 PETG / 500 μm thick
Comparative Example 2 which is the same as Example 2 except that an ABS sheet (Styrac, manufactured by Asahi Kasei Kogyo Co., Ltd.) was used instead of the alloy sheet of PC (manufactured by Mitsubishi Plastics, Inc.) (11).
Was made.
【００２４】かかる比較例１，及び２のカードはカード
に要求される耐光性、耐薬品性などは実施例１、２と同
様であったが、１００℃のオーブン中では実施例１、２
のものは何ら変化はないが、比較例１、２のものは変形
が激しく、磁気カードとしては使用に耐えうるものでな
かった。The cards of Comparative Examples 1 and 2 were the same as those of Examples 1 and 2 in terms of light resistance and chemical resistance required for the cards, but were cured in a 100 ° C. oven.
Although there was no change in the magnetic card, those in Comparative Examples 1 and 2 were severely deformed, and were not usable as a magnetic card.
【００２５】以上のように比較例１、２のカードは基材
自体に耐熱性を有していないため、高温となる室内等で
使用する場合は変形が著しく使用に耐えないという問題
点を有している。更に、使用済み後、廃棄時に焼却処理
した場合、塩化ビニル樹脂を用いているため、塩化水素
ガスが発生し炉を痛めるという廃棄性に優れないという
問題を有していた。これに対して実施例１、２、の磁気
カードは、耐熱性に優れており、例えば真夏の車内にど
んな形で置かれても変形はせず、また、塩化ビニル樹脂
を用いていないため、用済み後焼却したとしても極めて
廃棄性に優れたカードといえることができる。As described above, the cards of Comparative Examples 1 and 2 do not have heat resistance on the base material itself, and therefore have a problem that when used in a room or the like where the temperature is high, the card is significantly deformed and cannot be used. are doing. Further, when incinerated at the time of disposal after use, the use of a vinyl chloride resin has the problem that hydrogen chloride gas is generated and the furnace is damaged, which is not excellent in disposability. On the other hand, the magnetic cards of Examples 1 and 2 are excellent in heat resistance. For example, they are not deformed even if they are placed in a car in the middle of summer, and they do not use vinyl chloride resin. Even if it is incinerated after being used, it can be said that the card is extremely excellent in disposability.
【００２６】[0026]
【発明の効果】本発明は以上の構成であるから、下記に
示す如き効果がある。即ち、本発明に係わるカードによ
れば、カード用素材としてポリ塩化ビニル樹脂の代わり
に、ポリエステルである非晶性ポリエチレンテレフタレ
ート、又は非晶性ポリエチレンテレフタレート及びポリ
カーボネートとのポリマーアロイの基材の両面に高耐熱
性のポリカーボネートを積層した後、磁気記録層を積層
したことにより、耐熱性の高いカードを製造することが
可能となる。また、使用後焼却された際に塩化水素の問
題やダイオキシンの問題がない、廃棄処理を考慮したカ
ードとなる。As described above, the present invention has the following effects. That is, according to the card of the present invention, instead of polyvinyl chloride resin as the card material, amorphous polyethylene terephthalate which is polyester, or amorphous polyethylene terephthalate and amorphous polyethylene terephthalate and both sides of a polymer alloy substrate with polycarbonate. By laminating the magnetic recording layer after laminating the polycarbonate having high heat resistance, it becomes possible to manufacture a card having high heat resistance. In addition, there is no problem of hydrogen chloride or dioxin when incinerated after use, and the card is considered for disposal.
【図１】本発明の一実施例のカードの断面を示す説明図
である。FIG. 1 is an explanatory diagram showing a cross section of a card according to an embodiment of the present invention.
【図２】本発明の実施例１のカードの断面を示す説明図
である。FIG. 2 is an explanatory diagram showing a cross section of the card according to the first embodiment of the present invention.
【図３】本発明の実施例２のカードの断面を示す説明図
である。FIG. 3 is an explanatory diagram illustrating a cross section of a card according to a second embodiment of the present invention.
１、５・・・・非晶性ＰＥＴシート ２、３、６、７、１２、１３・・・・ポリカーボネートシー
ト ８、１５・・・・磁気記録層 ９、１６・・・・文字印刷層 １０、１４・・・・絵柄印刷層 １１・・・・非晶性ＰＥＴ／ＰＣポリマーアロイシート1, 5,... Amorphous PET sheet 2, 3, 6, 7, 12, 13,... Polycarbonate sheet 8, 15,... Magnetic recording layer 9, 16,. , 14 .... Pattern printing layer 11 ... Amorphous PET / PC polymer alloy sheet
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ｂ２９Ｃ 47/00 Ｂ２９Ｃ 47/00 Ｂ２９Ｋ 67:00 Ｆターム(参考） 2C005 HA10 HA21 HB01 HB04 HB09 JA01 JA08 JA15 JA26 JB02 KA15 LA03 LA11 LA18 LA20 LA22 LA25 LA29 4F100 AK41A AK41J AK45B AK45C AT00A BA03 BA06 BA10B BA10C EH17 GB41 GB71 HB00 JA12A JJ03 JJ03B JJ03C JL05 4F207 AA24C AA28C AG03 AH37 KA01 KA17 KW41 4F213 AA24C AA28C AG03 AH37 WA06 WA14 WA52 WA54 WA58 WB01 WB22 WK01 5B035 AA07 BA05 BB09 CA01 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) // B29C 47/00 B29C 47/00 B29K 67:00 F term (Reference) 2C005 HA10 HA21 HB01 HB04 HB09 JA01 JA08 JA15 JA26 JB02 KA15 LA03 LA11 LA18 LA20 LA22 LA25 LA29 4F100 AK41A AK41J AK45B AK45C AT00A BA03 BA06 BA10B BA10C EH17 GB41 GB71 HB00 JA12A JJ03 JJ03B JJ03C JL05 4F207 AA24C AA28KA14A37A37A14A37C14A37A14K37 WK01 5B035 AA07 BA05 BB09 CA01
Claims (6)
耐熱性を有するポリカーボネートシート層を積層するこ
とにより、高耐熱性を持たせたことを特徴とするカー
ド。A card having high heat resistance by laminating polycarbonate sheet layers having high heat resistance on both sides of an amorphous polyester sheet layer.
ーボネートシート層を積層した基材上に、磁気記録層や
ＩＣモジュール等の情報を記録する機能を持たせたこと
を特徴とする請求項１記載のカード。2. The apparatus according to claim 1, wherein a function of recording information such as a magnetic recording layer and an IC module is provided on the substrate on which the amorphous polyester sheet layer and the polycarbonate sheet layer are laminated. Card.
タル酸と、シクロヘキサンジメタノール及びエチレング
リコールとの共重合体、又はその共重合体とポリカーボ
ネートとのポリマーアロイであることを特徴とする請求
項１記載のカード。3. The amorphous polyester sheet is a copolymer of terephthalic acid and cyclohexanedimethanol and ethylene glycol, or a polymer alloy of the copolymer and polycarbonate. The stated card.
転移温度が８０度以上であることを特徴とする請求項１
記載のカード。4. The amorphous polyester sheet according to claim 1, wherein the glass transition temperature is 80 ° C. or higher.
The stated card.
ノールＡを主成分とし、結晶化度が３０％以下で、ガラ
ス転移温度が１４０℃以上であることを特徴とする請求
項１記載のカード。5. The card according to claim 1, wherein the polycarbonate sheet contains bisphenol A as a main component, has a crystallinity of 30% or less, and has a glass transition temperature of 140 ° C. or more.
ーボネートシートは各々押し出し法によりシート化した
ことを特徴とする請求項１記載のカード。6. The card according to claim 1, wherein said amorphous polyester sheet and said polycarbonate sheet are each formed by extrusion.