JP2000191391A - Pyrotechnic composition and its production - Google Patents
Pyrotechnic composition and its productionInfo
- Publication number
- JP2000191391A JP2000191391A JP11295176A JP29517699A JP2000191391A JP 2000191391 A JP2000191391 A JP 2000191391A JP 11295176 A JP11295176 A JP 11295176A JP 29517699 A JP29517699 A JP 29517699A JP 2000191391 A JP2000191391 A JP 2000191391A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- nitrocellulose
- pyrotechnic composition
- composition
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は推進薬、照明剤、色
火剤、発煙剤、着火剤等に広く利用される火工品組成物
に関する。更に詳しくは、色、運動、光、煙、音等の多
くの効果を作り出すことができる火工品組成物及び火工
品組成物の製法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pyrotechnic composition widely used as a propellant, an illuminating agent, a coloring agent, a smoke generating agent, an ignition agent and the like. More particularly, it relates to a pyrotechnic composition capable of producing many effects such as color, movement, light, smoke, sound, and the like, and to a method for producing the pyrotechnic composition.
【０００２】[0002]
【従来の技術】火工品組成物は、通常、酸化剤に可燃剤
を配合して調製され、その可燃剤は酸化剤から発生する
酸素と反応して、酸化生成物を生成するとともに熱を発
生する。この熱を利用して色、運動、光、煙、音等の多
くの効果を作り出すことができる。火工品組成物の典型
的な用途はその炎色反応を利用した煙火組成物としての
利用である。例えば赤い色を出すときは焔色剤としてス
トロンチウム塩が用いられる。（以前は硝酸ストロンチ
ウムが使用されていたが、現在は安定性が高く、色も美
しいので、炭酸ストロンチウムが主に使用される。）同
様に緑色には硝酸バリウムが、黄色にはシュウ酸ナトリ
ウムや炭酸カルシウムが、青色には花緑青や酸化銅が、
紫色には炭酸ストロンチウムと酸化銅の混合物が、白色
にはアルミニウムなどが、それぞれ代表的に用いられ
る。2. Description of the Related Art A pyrotechnic composition is usually prepared by mixing a combustible agent with an oxidizing agent, and the combustible agent reacts with oxygen generated from the oxidizing agent to generate an oxidation product and generate heat. appear. This heat can be used to create many effects such as color, motion, light, smoke, sound, etc. A typical use of the pyrotechnic composition is as a fireworks composition utilizing its flame reaction. For example, when producing a red color, a strontium salt is used as a flame colorant. (Strontium nitrate was used before, but now strontium carbonate is mainly used because of its high stability and beautiful color.) Similarly, green barium nitrate, yellow sodium oxalate, Calcium carbonate, blue, flower patina and copper oxide,
A mixture of strontium carbonate and copper oxide is typically used for purple, and aluminum or the like is typically used for white.
【０００３】[0003]
【発明が解決しようとする課題】日本の打ち上げ花火
は、一般に、丸く開くいわゆる「菊花花火」であり、玉
皮の周りに星が配置され、一斉に着火され、一斉に消え
る構造となっている。この星には、掛け星と呼ばれる丸
星が用いられるが、その芯としては粟や菜種の実など丸
い雑穀や散弾などが用いられ、直接それをコンクリート
ミキサーのような造粒機に入れて、酸化剤、可燃剤、焔
色剤やのり剤からなる配合薬に水を加え、回転させなが
ら太らせ、適度な厚さに配合薬が付着して層ができた
ら、乾燥台に広げ乾燥する。よく乾燥したらまた回転釜
に入れて太らせる。必要とされる大きさになるまでこの
ような工程が繰りかえされて製造される。例えば、１０
号玉（尺玉）に使用する直径２０．５ｍｍほどの大きさ
の星は、この作業を３５回くらい繰り返され、完成まで
に最低１７日位を要す。また、花火大会で欠かせないも
のに、仕掛花火がある。仕掛花火は（枠仕掛）「ラン
ス」と「速火線」で作られる。「ランス」は、玩具花火
の「すすき」や「トーチ」のように、紙のパイプに酸化
剤、焔色剤と可燃剤の混合物を詰めたもので、紅・緑・
黄・青・紫・白（銀）の６色を呈するように焔色剤を使
用して調製される。星やランスの調製作業は、このよう
にいずれも時間のかかる作業である。特に星では、上述
したように完成まで相当の日数を要し、生産性を悪くし
ている。また、ランスでは、粉体を紙のパイプに均一に
詰めるという面倒な作業がある。Generally, Japanese fireworks are so-called "chrysanthemum fireworks" which open round and have a structure in which stars are arranged around a bark, ignited all at once, and extinguished all at once. For this star, a round star called a hanging star is used, and as its core, round cereals such as millet and rapeseed fruits and shots are used, and it is directly put into a granulator such as a concrete mixer, Water is added to the compounding agent consisting of an oxidizing agent, a flammable agent, a flame colorant and a glue, and the mixture is made thicker by rotating. When the compounding agent adheres to an appropriate thickness to form a layer, spread it on a drying stand and dry. After it dries well, put it in a rotating pot again to make it fat. These steps are repeated until the required size is obtained. For example, 10
This process is repeated about 35 times for a star with a diameter of about 20.5 mm, which is used as a No. ball (shakudama), and it takes at least 17 days to complete. Another indispensable part of a fireworks display is a fireworks display. Widow fireworks (framework) are made of "lance" and "quick-fire wire". "Lance" is a paper pipe filled with an oxidizing agent, a mixture of flame colorant and flammable agent, like the toy fireworks "Susuki" and "Torch".
It is prepared using a flame colorant so as to exhibit six colors of yellow, blue, purple and white (silver). The preparation of stars and lances is a time-consuming operation. Stars in particular take a considerable number of days to complete, as mentioned above, and are reducing productivity. In the lance, there is a troublesome work of uniformly filling powder into a paper pipe.
【０００４】[0004]
【問題を解決するための手段】本発明者らは、特に煙火
組成物として有用な火工品組成物に関して、星やランス
の製造時に必要な手間のかかる製造工程を簡便にして、
しかも従来の星やランスと同じ演出効果を有するものを
開発すべく鋭意研究を重ねた結果、特定の薬品を含有す
る火工品組成物がこれらの目的を達成するものであるこ
とを見出し、本発明を完成させるに至ったものである。Means for Solving the Problems The present inventors have simplified the complicated production steps required for the production of stars and lances, especially for pyrotechnic compositions useful as smoke compositions.
In addition, as a result of intensive research to develop those that have the same effect as conventional stars and lances, they have found that pyrotechnic compositions containing specific chemicals can achieve these objectives. The invention has been completed.
【０００５】すなわち本発明は、 （１）ニトロセルロース、酸化剤、可燃剤及び焔色剤を
主要成分として含有することを特徴とする火工品組成物 （２）ニトロセルロースとニトロセルロース以外のニト
ロ化合物を混合してゲル状組成物とし、これに酸化剤、
可燃剤及び焔色剤を混合した後、乾燥してなる火工品組
成物 （３）ゲル状組成物が、ニトロセルロース３〜４０重量
％とニトロセルロース以外のニトロ化合物９７〜６０重
量％の混合比である（２）に記載の火工品組成物 （４）ニトロセルロ−スの火工品組成物中の含有率が
０．６〜１２重量％である（１）乃至（３）のいずれか
一項に記載の火工品組成物 （５）酸化剤、可燃剤及び焔色剤の含有率がそれぞれ４
０〜６０重量％、１０〜２５重量％、１５〜５０重量で
ある（１）乃至（４）のいずれか一項に記載の火工品組
成物 （６）火工品組成物が花火の星又はランスである（１）
乃至（５）のいずれか一項に記載の火工品組成物 （７）ニトロセルロースとニトロセルロース以外のニト
ロ化合物を混合してゲル状組成物とし、これに酸化剤、
可燃剤、焔色剤を混合した後乾燥することを特徴とする
火工品組成物の製法 （８）ゲル状組成物が、ニトロセルロース３〜４０重量
％とニトロ化合物９７〜６０重量％の混合比である
（７）に記載の火工品組成物の製法 （９）ゲル状組成物が１０〜３０重量％であり、酸化
剤、可燃剤および焔色剤の合計が９０〜７０重量％であ
る（７）乃至（８）のいずれか一項に記載の火工品組成
物の製法 （１０）ニトロセルロース以外のニトロ化合物がニトロ
アルカン類である（７）乃至（９）のいずれか一項に記
載の火工品組成物の製法 （１１）ニトロアルカン類がニトロメタン、ニトロエタ
ン及びニトロプロパンからなる群から選ばれる１種又は
２種以上である（１０）に記載の火工品組成物の製法 （１２）火工品組成物が花火の星又はランスである
（７）乃至（１１）のいずれか一項に記載の火工品組成
物の製法に関する。That is, the present invention relates to a pyrotechnic composition comprising (1) nitrocellulose, an oxidizing agent, a combustible agent and a flame colorant as main components. (2) Nitrocellulose and nitro other than nitrocellulose The compound is mixed to form a gel composition, to which an oxidizing agent,
A pyrotechnic composition which is dried after mixing a combustible agent and a flame colorant. (3) A gel composition is a mixture of 3 to 40% by weight of nitrocellulose and 97 to 60% by weight of a nitro compound other than nitrocellulose. (4) The pyrotechnic composition according to (2), wherein the content of nitrocellulose in the pyrotechnic composition is 0.6 to 12% by weight. The pyrotechnic composition according to item (5), wherein the content of each of the oxidizing agent, the combustible agent and the flame colorant is 4
The pyrotechnic composition according to any one of (1) to (4), wherein the pyrotechnic composition is 0 to 60% by weight, 10 to 25% by weight, and 15 to 50% by weight. Or a lance (1)
Or the pyrotechnic composition according to any one of (5) to (7), a mixture of nitrocellulose and a nitro compound other than nitrocellulose to form a gel composition, and an oxidizing agent;
A method for producing a pyrotechnic composition comprising mixing a combustible agent and a flame colorant and then drying the mixture. (8) A gel composition comprising 3 to 40% by weight of nitrocellulose and 97 to 60% by weight of a nitro compound. (9) The gel composition is 10 to 30% by weight, and the total of the oxidizing agent, the combustible agent and the flame colorant is 90 to 70% by weight. The method for producing the pyrotechnic composition according to any one of (7) to (8). (10) The nitro compound other than nitrocellulose is a nitroalkane. (11) The method for producing a pyrotechnic composition according to (10), wherein the nitroalkane is one or more selected from the group consisting of nitromethane, nitroethane, and nitropropane. (12) The pyrotechnic composition is a fireworks star or lance Preparation regarding a certain (7) to (11) the pyrotechnic composition according to any one of.
【０００６】[0006]
【発明の実施の形態】以下本発明を詳細に記載する。本
発明の火工品組成物に使用されるニトロセルロースとし
ては、強綿薬、弱綿薬、脆綿薬と呼ばれるどのようなタ
イプのニトロセルロースでも使用可能であり、弱綿薬に
含まれるダイナマイト用ニトロセルロースも使用可能で
ある。窒素量１１〜１２．５重量％の範囲のダイナマイ
ト用ニトロセルロースを乾燥状態で用いてもよいし、安
全のため水分を含ませてもよい。水分量は２５〜３０重
量％のものを用いるのが安全上好ましい。また、ニトロ
セルロースは、火工品組成物中に０．６〜１２重量％、
好ましくは１〜６重量％の範囲で含有される。本発明で
用いられるニトロセルロ−スは、火工品組成物中でバイ
ンダ−としての作用を有するもので、該ニトロセルロ−
スの使用は、本発明に係る製造が容易な火工品組成物を
得る上で極めて重要である。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail. As the nitrocellulose used in the pyrotechnic composition of the present invention, any type of nitrocellulose called strong cotton, weak cotton, brittle cotton can be used, and dynamite contained in the weak cotton is used. Nitrocellulose for use can also be used. Nitrocellulose for dynamite having a nitrogen content of 11 to 12.5% by weight may be used in a dry state, or may contain moisture for safety. It is preferable from the viewpoint of safety that the water content is 25 to 30% by weight. Also, nitrocellulose is contained in the pyrotechnic composition at 0.6 to 12% by weight,
Preferably, it is contained in the range of 1 to 6% by weight. The nitrocellulose used in the present invention has a function as a binder in the pyrotechnic composition.
The use of steel is very important in obtaining the easily manufactured pyrotechnic composition according to the present invention.
【０００７】本発明の火工品組成物を製造するに当たり
用いられるニトロセルロース以外のニトロ化合物として
は、ニトロセルロースと混合してゲル状組成物となるも
のが好ましく、通常、脂肪族ニトロ化合物、芳香族ニト
ロ化合物が用いられる。用いうる脂肪族ニトロ化合物の
具体例としては、ニトロメタン、ニトロエタン、ニトロ
プロパン、ニトロブタンなどのニトロアルカン類が、用
いうる芳香族ニトロ化合物の具体例としては、ニトロベ
ンゼン、ニトロトルエン、ジニトロベンゼン、ジニトロ
トルエンなどがそれぞれ挙げられ、これらは単独又は２
種以上の混合物として使用してもよい。これらのうち好
ましいものはニトロメタン、ニトロエタン、ニトロプロ
パン、ニトロブタンなどのニトロアルカン類であり、更
に好ましいものはニトロメタン、ニトロエタン、ニトロ
プロパンである。尚、ニトロセルロース以外のニトロ化
合物が常温で固体である場合は溶融状で使用するのが好
ましい。As the nitro compound other than nitrocellulose used in producing the pyrotechnic composition of the present invention, a nitro compound which is mixed with nitrocellulose to form a gel composition is preferable. Group nitro compounds are used. Specific examples of the aliphatic nitro compound that can be used include nitroalkanes such as nitromethane, nitroethane, nitropropane, and nitrobutane. Specific examples of the aromatic nitro compound that can be used include nitrobenzene, nitrotoluene, dinitrobenzene, and dinitrotoluene. Each of which may be used alone or
It may be used as a mixture of more than one species. Of these, preferred are nitroalkanes such as nitromethane, nitroethane, nitropropane and nitrobutane, and more preferred are nitromethane, nitroethane and nitropropane. When a nitro compound other than nitrocellulose is solid at room temperature, it is preferable to use it in a molten state.
【０００８】本発明の火工品組成物に用いられる酸化剤
としては、通常、中〜高温度で分解して酸素ガスを放出
する酸素に富んだイオン性固体を用いるのが好ましい。
吸湿しても中性状態で反応し、広い温度範囲で安定で、
かつ、高温では容易に分解して酸素を放出するものであ
ればいずれも使用できる。具体的には、硝酸イオン、塩
素酸イオン、過塩素酸イオン、クロム酸イオン、酸素イ
オン、重クロム酸イオン等の陰イオンを含む酸化剤が好
ましい。酸化剤の陽イオンとしては、アルカリ金属（リ
チウム、ナトリウム、カリウム）、アルカリ土類金属
（カルシウム、ストロンチウム、バリウム）およびアン
モニウムイオン等が好ましい。用いうる酸化剤の具体例
としては、硝酸アンモニウム、硝酸カリウム、硝酸ナト
リウム、硝酸バリウム、硝酸ストロンチウム、過塩素酸
アンモニウム、過塩素酸カリウム、塩素酸カリウム、塩
素酸バリウムなどが挙げられる。これらの酸化剤は単独
で又は２種以上を混合して用いることができる。As the oxidizing agent used in the pyrotechnic composition of the present invention, it is usually preferable to use an oxygen-rich ionic solid which decomposes at medium to high temperatures to release oxygen gas.
It reacts in a neutral state even when absorbing moisture, is stable over a wide temperature range,
In addition, any material that can be easily decomposed at high temperature to release oxygen can be used. Specifically, an oxidizing agent containing an anion such as a nitrate ion, a chlorate ion, a perchlorate ion, a chromate ion, an oxygen ion, and a dichromate ion is preferable. As cations of the oxidizing agent, alkali metal (lithium, sodium, potassium), alkaline earth metal (calcium, strontium, barium) and ammonium ions are preferable. Specific examples of the oxidizing agent that can be used include ammonium nitrate, potassium nitrate, sodium nitrate, barium nitrate, strontium nitrate, ammonium perchlorate, potassium perchlorate, potassium chlorate, and barium chlorate. These oxidizing agents can be used alone or in combination of two or more.
【０００９】本発明の火工品組成物に用いられる酸化剤
は、通常火工品組成物全体の３０〜７０重量％、好まし
くは４０〜６０重量％の範囲で含有されるように調製さ
れる。The oxidizing agent used in the pyrotechnic composition of the present invention is usually prepared so as to be contained in the range of 30 to 70% by weight, preferably 40 to 60% by weight of the entire pyrotechnic composition. .
【００１０】本発明の火工品組成物で用いられる可燃剤
としては、酸化剤から発生する酸素と反応して、酸化生
成物を生成するとともに熱を発生するものを用いるのが
好ましい。この熱を利用して色、運動、光、煙、音など
の効果を作り出す。可燃剤としては、燃焼反応を起こし
うる多くの物質が使用可能であるが、熱量、発熱速度、
入手の難易性、組成物中での安定性及びガス発生量など
の要因から適宜選択される。本発明で使用しうる可燃剤
としては、大きく分けて金属元素、非金属元素および有
機化合物の３つに区分できる。As the combustible used in the pyrotechnic composition of the present invention, it is preferable to use a combustible which reacts with oxygen generated from the oxidizing agent to generate an oxidation product and generate heat. This heat is used to create color, motion, light, smoke, sound and other effects. As the combustible agent, many substances that can cause a combustion reaction can be used.
It is appropriately selected from factors such as difficulty in obtaining, stability in the composition, and the amount of gas generated. The combustible agents that can be used in the present invention can be broadly classified into three types: metal elements, nonmetal elements, and organic compounds.
【００１１】金属元素系の可燃剤としては、アルミニウ
ム、マグネシウム、マグナリウム、チタン、鉄粉および
これらの混合物を用いることができる。非金属元素系の
可燃剤としては、硫黄、ホウ素、ケイ素、リンおよびこ
れらの混合物を用いることができる。As the metal element-based combustible, aluminum, magnesium, magnalium, titanium, iron powder and a mixture thereof can be used. Sulfur, boron, silicon, phosphorus, and mixtures thereof can be used as the nonmetallic element-based combustible.
【００１２】有機化合物系の可燃剤としては、セラッ
ク、レッドガム、木炭、木粉、炭水化物、天然フェノー
ル樹脂（例えば、ビンゾール（商品名、ＢＬ助燃剤、理
化ハーキュレス（株）製））、塩化ゴム（例えば、アデ
カプレンＤ―１（商品名、旭電化工業（株）製））、フ
ェノールレジン（例えば、レジトップＰＧＡ−２４００
（商品名、群栄化学工業（株）製））、松根油ピッチお
よびこれらの混合物を用いることができる。これらの金
属元素、非金属元素および有機化合物はそれぞれ単独で
あるいは２種以上を混合したものも使用できる。Examples of organic compound-based combustibles include shellac, red gum, charcoal, wood flour, carbohydrate, natural phenolic resin (for example, Vinsol (trade name, BL burner, manufactured by Rika Hercules Co., Ltd.)), chlorinated rubber ( For example, ADECAPRENE D-1 (trade name, manufactured by Asahi Denka Kogyo Co., Ltd.)), phenolic resin (for example, REGITOP PGA-2400)
(Trade name, manufactured by Gunei Chemical Industry Co., Ltd.)), pine oil pitch and a mixture thereof. These metal elements, non-metal elements and organic compounds can be used alone or in combination of two or more.
【００１３】本発明の火工品組成物に用いられる可燃剤
の量は、上述のように多くの要因から選択されるが、火
工品組成物中に、好ましくは５〜４０重量％、より好ま
しくは１０〜２５重量％の範囲で含有されるように調製
される。The amount of combustible used in the pyrotechnic composition of the present invention is selected from a number of factors as described above, but is preferably 5 to 40% by weight, It is preferably prepared so as to be contained in the range of 10 to 25% by weight.
【００１４】本発明の火工品組成物に用いられる焔色剤
としては燃焼して炎色反応を示すあらゆる物質が使用可
能であるが、赤色には、炭酸ストロンチウム等のストロ
ンチウム塩を、緑色には硝酸バリウムなどのバリウム塩
を、青色には酸化銅、塩基性炭酸銅や硫酸銅などの銅塩
を、紫色には炭酸ストロンチウムと酸化銅を、黄色には
シュウ酸ナトリウム、クリオライトなどのナトリウム塩
を含むものを用いることが好ましい。その他、多様な物
質を調節混合する従来の調色の手法がそのまま採用でき
る。As the flame-coloring agent used in the pyrotechnic composition of the present invention, any substance which burns and shows a flame-color reaction can be used, and a red color may be a strontium salt such as strontium carbonate, and a green color may be a green color. Is barium salts such as barium nitrate, blue is copper oxide, copper salts such as basic copper carbonate and copper sulfate, purple is strontium carbonate and copper oxide, and yellow is sodium oxalate and cryolite. It is preferable to use one containing a salt. In addition, a conventional toning method of adjusting and mixing various substances can be used as it is.
【００１５】本発明の火工品組成物に用いられる焔色剤
の量は、火工品組成物中に、好ましくは５〜５０重量
％、より好ましくは１５〜５０重量％の範囲で含有され
るように調製される。硝酸バリウムなどの一部の硝酸塩
は、酸化剤の性質を持つものであるが、ここでは、焔色
剤として計算する。本発明の火工品組成物は、前記のよ
うに、酸化剤、可燃剤及び焔色剤をそれぞれ３０〜７０
重量％、５〜４０重量％、５〜５０重量％より好ましく
は４０〜６０重量％、１０〜２５重量％、１５〜５０重
量％の割合で含有される。The amount of the flame colorant used in the pyrotechnic composition of the present invention is preferably in the range of 5 to 50% by weight, more preferably 15 to 50% by weight, in the pyrotechnic composition. It is prepared as follows. Some nitrates such as barium nitrate have the property of an oxidizing agent, but are calculated here as a flame colorant. As described above, the pyrotechnic composition of the present invention contains an oxidizing agent, a combustible agent and a flame colorant in an amount of 30 to 70, respectively.
% By weight, 5 to 40% by weight, more preferably 5 to 50% by weight, more preferably 40 to 60% by weight, 10 to 25% by weight, and 15 to 50% by weight.
【００１６】本発明の火工品組成物は、ニトロセルロー
ス、酸化剤、可燃剤、焔色剤を混合し、ニトロセルロー
ス以外のニトロ化合物を加えて、竹ベラのような簡単な
撹拌具を用いて手で混合するか、機械で混合して、プラ
スチック状の混合物とし、乾燥することにより得られ
る。The pyrotechnic composition of the present invention is obtained by mixing nitrocellulose, an oxidizing agent, a combustible, and a flame colorant, adding a nitro compound other than nitrocellulose, and using a simple stirrer such as bamboo spatula. It is obtained by mixing by hand or by mixing with a machine to form a plastic-like mixture and drying.
【００１７】本発明の火工品組成物は、上記の様にニト
ロセルロース、酸化剤、可燃剤、焔色剤及びニトロセル
ロース以外のニトロ化合物を混合し、乾燥するだけで製
造することもできるが、ニトロセルロースとニトロセル
ロース以外のニトロ化合物を混合して先ずゲル状組成物
を得、これに酸化剤、可燃剤、焔色剤を加え次いで必要
により所望の形に成形した後乾燥する方法がより好まし
い。The pyrotechnic composition of the present invention can be produced by simply mixing nitrocellulose, an oxidizing agent, a combustible, a flame colorant and a nitro compound other than nitrocellulose and drying as described above. First, a method of mixing nitrocellulose and a nitro compound other than nitrocellulose to obtain a gel-like composition, adding an oxidizing agent, a combustible agent, a flame colorant to the composition, and then, if necessary, shaping the composition into a desired shape followed by drying. preferable.
【００１８】即ち、本発明の火工品組成物は、ニトロセ
ルロースとニトロセルロース以外のニトロ化合物を容器
にとり、簡単な撹拌具を用いて手で、又は機械、例えば
ニーダーのような混合機で混合しゲル状組成物を得、こ
れに酸化剤、可燃剤、焔色剤を混合し、均一に混合する
ことによってプラスチック状の混合物を製造する。この
とき酸化剤、可燃剤、焔色剤は前もって別途混合された
ものを用いてもよいし、これらの薬剤を順次加えてもよ
い。また、攪拌、混合の機能を備えているならば、ニ−
ダ−以外の混合機も使用可能である。上記においてゲル
状組成物に対する酸化剤、可燃剤及び焔色剤の合計の混
合割合は１０〜３０重量％対９０〜７０重量％の範囲に
あるのが好ましい。That is, the pyrotechnic composition of the present invention is prepared by mixing nitrocellulose and a nitro compound other than nitrocellulose in a container and mixing them by hand using a simple stirrer or by a machine such as a mixer such as a kneader. A gel-like composition is obtained, and an oxidizing agent, a combustible agent, and a flame-coloring agent are mixed with the composition and uniformly mixed to produce a plastic-like mixture. At this time, the oxidizing agent, the combustible agent, and the flame colorant may be separately mixed in advance, or these agents may be sequentially added. Also, if it has stirring and mixing functions,
Mixers other than Darr can also be used. In the above, the total mixing ratio of the oxidizing agent, the combustible agent and the flame colorant to the gel composition is preferably in the range of 10 to 30% by weight to 90 to 70% by weight.
【００１９】上記のゲル状組成物は、通常ニトロセルロ
ース３〜４０重量％とニトロセルロース以外のニトロ化
合物９７〜６０重量％、好ましくはニトロセルロース１
５〜２５重量％とニトロセルロース以外のニトロ化合物
８５〜７５重量％の混合比で調製される。The above gel composition usually contains 3 to 40% by weight of nitrocellulose and 97 to 60% by weight of a nitro compound other than nitrocellulose, preferably 1% by weight of nitrocellulose.
It is prepared with a mixing ratio of 5 to 25% by weight and 85 to 75% by weight of a nitro compound other than nitrocellulose.
【００２０】本発明の火工品組成物は、当業者が周知の
如く、星に応用するのであれば、丸く成型し、乾燥する
ことで硬化させ、星としての十分な強度が得られる。ま
た、ランス用には、容器にダイスなどで棒状に押し出し
成型し、必要な長さに切断して、乾燥して硬化させる
か、棒状に押し出したものを乾燥、硬化してから紙など
で巻くことで製造可能である。又紙の筒にゲルを詰めて
乾燥してもよい。乾燥温度としては通常３０〜７０℃、
好ましくは５０〜６０℃である。乾燥は減圧下に行って
もよい。この乾燥工程によりニトロセルロース以外のニ
トロ化合物は気化し本発明の火工品組成物中には極めて
微量しか存在しない。本発明の製造法において、気化し
ない成分であるニトロセルロース、酸化剤、可燃剤、焔
色剤等は前記したような本発明の火工品組成物における
含有量の比で使用される。As is well known to those skilled in the art, if the pyrotechnic composition of the present invention is applied to a star, it is molded into a round shape, dried and cured to obtain sufficient strength as a star. In addition, for lances, extrude into a container using a die or the like and cut it into the required length, cut it to the required length, dry it and cure it, or extrude it into a stick and dry and cure it, then wind it with paper etc. It can be manufactured by: Alternatively, the gel may be packed in a paper cylinder and dried. The drying temperature is usually 30 to 70 ° C,
Preferably it is 50-60 degreeC. Drying may be performed under reduced pressure. By this drying step, nitro compounds other than nitrocellulose are vaporized and only a very small amount is present in the pyrotechnic composition of the present invention. In the production method of the present invention, nitrocellulose, an oxidizing agent, a flammable agent, a flame colorant and the like, which are not vaporized, are used in the ratio of the contents in the pyrotechnic composition of the present invention as described above.
【００２１】[0021]
【実施例】本発明を実施例を挙げてさらに詳しく説明す
るが、本発明がこれらの実施例のみに限定されるもので
はない。EXAMPLES The present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
【００２２】実施例１ ニトロセルロース（窒素含有率１１．９〜１２．２重量
％のダイナマイト用ニトロセルロ−ス、以下同様）４重
量部とニトロベンゼン１６重量部を混合し、ゲル状組成
物を作り、別途酸化剤である過塩素酸カリウム４６．４
重量部、可燃剤である麻炭３．６重量部、ビンゾール
（商品名、ＢＬ助燃剤、理化ハーキュレス（株）製）
６．８重量部、アデカプレンＤ―１（商品名、塩化ゴ
ム、旭電化工業（株）製）６．８重量部、レジトップＰ
ＧＡ−２４００（商品名、フェノールレジン、群栄化学
工業（株）製）２．４重量部の合計１９．６重量部及び
焔色剤である酸化銅１４重量部を混合しておき、上記の
ゲル状組成物と混合し、これを丸く成形し、５０〜６０
℃の乾燥機で乾燥し、硬化させることで本発明の火工品
組成物からなる直径２０ｍｍの打上煙火用の青星を得
た。これに着火して、従来の打上煙火用の青星と同等の
青色煙火の効果を確認した。Example 1 4 parts by weight of nitrocellulose (nitrocellulose for dynamite having a nitrogen content of 11.9 to 12.2% by weight, the same applies hereinafter) and 16 parts by weight of nitrobenzene were mixed to form a gel composition. Potassium perchlorate, which is an additional oxidizing agent, 46.4
Parts by weight, 3.6 parts by weight of combustible hemp charcoal, Vinsol (trade name, BL burner, manufactured by Rika Hercules Co., Ltd.)
6.8 parts by weight, Adecaprene D-1 (trade name, chlorinated rubber, manufactured by Asahi Denka Kogyo KK) 6.8 parts by weight, REGITOP P
A total of 19.6 parts by weight of 2.4 parts by weight of GA-2400 (trade name, phenolic resin, manufactured by Gunei Chemical Industry Co., Ltd.) and 14 parts by weight of copper oxide as a flame colorant were mixed, and the above mixture was mixed. Mix with the gel composition, shape it into a round, 50-60
After drying with a drier at a temperature of ° C. and curing, a blue star for launching smoke with a diameter of 20 mm comprising the pyrotechnic composition of the present invention was obtained. We ignited this and confirmed the effect of blue smoke which was equivalent to the blue star for conventional launch smoke.
【００２３】実施例２ ニトロセルロース４重量部とニトロメタン１６重量部を
室温で混合し、ゲル状組成物を作り、別途酸化剤である
過塩素酸カリウム４４重量部、可燃剤である麻炭３．６
重量部、ビンゾール（商品名、ＢＬ助燃剤、理化ハーキ
ュレス（株）製）６．８重量部、アデカプレンＤ―１
（商品名、塩化ゴム、旭電化工業（株）製）６．８重量
部、レジトップＰＧＡ−２４００（商品名、フェノール
レジン、群栄化学工業（株）製）２．８重量部の合計２
０重量部、及び焔色剤である炭酸ストロンチウム１６重
量部を混合しておき、上記のゲル状組成物と混合し、こ
れを丸く成形し、５０〜６０℃の乾燥機で乾燥し、硬化
させることで本発明の火工品組成物からなる直径２０ｍ
ｍの打上煙火用の赤星を得た。これに着火して、従来の
打上煙火用の赤星と同等の赤色煙火の効果を確認した。Example 2 4 parts by weight of nitrocellulose and 16 parts by weight of nitromethane were mixed at room temperature to prepare a gel composition. 44 parts by weight of potassium chlorate, an oxidizing agent, and hemp coal, a combustible agent. 6
Parts by weight, Vinsol (trade name, BL burner, manufactured by Rika Hercules Co., Ltd.) 6.8 parts by weight, Adecaprene D-1
6.8 parts by weight (trade name, chlorinated rubber, manufactured by Asahi Denka Kogyo Co., Ltd.) and 2.8 parts by weight of REGITOP PGA-2400 (trade name, phenolic resin, manufactured by Gunei Chemical Industry Co., Ltd.)
0 parts by weight and 16 parts by weight of strontium carbonate as a flame colorant are mixed, mixed with the above gel composition, formed into a round shape, dried in a dryer at 50 to 60 ° C., and cured. 20 m in diameter comprising the pyrotechnic composition of the present invention
m was obtained for the launch fire. When this was ignited, the effect of red smoke which was equivalent to that of a conventional red smoke for launching fire was confirmed.
【００２４】実施例３ ニトロセルロース３．５重量部とジニトロトルエン１４
重量部を混合し、ゲル状組成物を作り、別途酸化剤であ
る過塩素酸カリウム４０．６重量部、可燃剤である麻炭
３．２重量部、ビンゾール（商品名、ＢＬ助燃剤、理化
ハーキュレス（株）製）６．０重量部、アデカプレンＤ
―１（商品名、塩化ゴム、旭電化工業（株）製）６．０
重量部、レジトップＰＧＡ−２４００（商品名、フェノ
ールレジン、群栄化学工業（株）製）２．１重量部の合
計１７．３重量部及び焔色剤である硝酸バリウム２４．
６重量部を混合しておき、上記のゲル状組成物と混合
し、これを棒状に成形し、５０〜６０℃の乾燥機で乾燥
し、硬化させることで本発明の火工品組成物からなる緑
色のランス用薬剤を得た。これに着火して、従来の緑色
のランス用薬剤と同等の緑色煙火の効果を確認した。Example 3 3.5 parts by weight of nitrocellulose and dinitrotoluene 14
Parts by weight to form a gel composition. Separately, 40.6 parts by weight of potassium perchlorate as an oxidizing agent, 3.2 parts by weight of hemp coal as a combustible, and binsol (trade name, BL combustion aid, 6.0 parts by weight of Hercules Co., Ltd., Adecaprene D
-1 (trade name, chlorinated rubber, manufactured by Asahi Denka Kogyo KK) 6.0
2 parts by weight of Regitop PGA-2400 (trade name, phenolic resin, manufactured by Gunei Chemical Industry Co., Ltd.), and 17.3 parts by weight in total, and barium nitrate as a flame coloring agent.
6 parts by weight are mixed, mixed with the above gel composition, formed into a rod shape, dried with a drier at 50 to 60 ° C., and cured to obtain the pyrotechnic composition of the present invention. A green lance drug was obtained. When this was ignited, the effect of a green smoke fire equivalent to the conventional green lance drug was confirmed.
【００２５】実施例４ ニトロセルロース４重量部と１−ニトロプロパン１６重
量部を混合し、ゲル状組成物を作り、別途酸化剤である
過塩素酸カリウム４０重量部、可燃剤である麻炭３．６
重量部、ビンゾール（商品名、ＢＬ助燃剤、理化ハーキ
ュレス（株）製）６．８重量部、アデカプレンＤ―１
（商品名、塩化ゴム、旭電化工業（株）製）６．８重量
部、レジトップＰＧＡ−２４００（商品名、フェノール
レジン、群栄化学工業（株）製）２．８重量部の合計２
０重量部及び焔色剤である硝酸バリウム２０重量部を混
合しておき、上記のゲル状組成物と混合し、これを丸く
成形し、５０〜６０℃の乾燥機で乾燥し、硬化させるこ
とで本発明の火工品組成物からなる直径２０ｍｍの打上
煙火用の緑星を得た。これに着火して、従来の打上煙火
用の緑星と同等の緑色煙火の効果を確認した。EXAMPLE 4 4 parts by weight of nitrocellulose and 16 parts by weight of 1-nitropropane were mixed to prepare a gel composition, and 40 parts by weight of potassium perchlorate as an oxidizing agent and hemp coal 3 as a combustible agent. .6
Parts by weight, Vinsol (trade name, BL burner, manufactured by Rika Hercules Co., Ltd.) 6.8 parts by weight, Adecaprene D-1
6.8 parts by weight (trade name, chlorinated rubber, manufactured by Asahi Denka Kogyo Co., Ltd.) and 2.8 parts by weight of REGITOP PGA-2400 (trade name, phenolic resin, manufactured by Gunei Chemical Industry Co., Ltd.)
0 parts by weight and 20 parts by weight of barium nitrate, which is a flame colorant, are mixed, mixed with the above gel composition, formed into a round shape, dried in a dryer at 50 to 60 ° C., and cured. Thus, a green star for launching smoke having a diameter of 20 mm comprising the pyrotechnic composition of the present invention was obtained. We ignited this and confirmed the effect of green smoke equivalent to that of the conventional green star for launch smoke.
【００２６】実施例５ ニトロセルロース３．５重量部とニトロエタン１４重量
部を混合し、ゲル状組成物を作り、別途酸化剤である過
塩素酸カリウム５０．５重量部、可燃剤である麻炭２重
量部、ビンゾール（商品名、ＢＬ助燃剤、理化ハーキュ
レス（株）製）６．６重量部、アデカプレンＤ―１（商
品名、塩化ゴム、旭電化工業（株）製）６．６重量部、
レジトップＰＧＡ−２４００（商品名、フェノールレジ
ン、群栄化学工業（株）製）２．１重量部の合計１７．
３重量部及び焔色剤である蓚酸ナトリウム１４．７重量
部を混合しておき、上記のゲル状組成物と混合し、これ
を丸く成形し、５０〜６０℃の乾燥機で乾燥し、硬化さ
せることで本発明の火工品組成物からなる直径２０ｍｍ
の打上煙火用の黄星を得た。これに着火して、従来の打
上煙火用の黄星と同等の黄色煙火の効果を確認した。Example 5 3.5 parts by weight of nitrocellulose and 14 parts by weight of nitroethane were mixed to form a gel composition, and 50.5 parts by weight of potassium perchlorate as an oxidizing agent and hemp coal as a combustible agent 2 parts by weight, vinsol (trade name, BL burner, Rika Hercules Co., Ltd.) 6.6 parts by weight, Adecaprene D-1 (trade name, chlorinated rubber, Asahi Denka Kogyo KK) 6.6 parts by weight ,
17. Regitop PGA-2400 (trade name, phenolic resin, manufactured by Gunei Chemical Industry Co., Ltd.)
3 parts by weight and 14.7 parts by weight of sodium oxalate as a flame colorant are mixed, mixed with the above gel composition, formed into a round shape, dried in a dryer at 50 to 60 ° C., and cured. The pyrotechnic composition of the present invention is made to have a diameter of 20 mm.
A yellow star was obtained for the launching fire. We ignited this and confirmed the effect of yellow smoke equivalent to that of the conventional launch star.
【００２７】実施例６〜９ 実施例１と同様な方法で下記する組成比の火工品組成物
を（星）得た。（実施例６、実施例７）又、実施例３と
同様な方法で下記する組成比の火工品組成物（ランス）
を得た。（実施例８、実施例９）表において数値の単位
は部である。Examples 6 to 9 Pyrotechnic compositions having the following composition ratio (star) were obtained in the same manner as in Example 1. (Examples 6 and 7) A pyrotechnic composition (lance) having the following composition ratio in the same manner as in Example 3
I got (Examples 8 and 9) In the table, the unit of the numerical value is part.
【００２８】 薬剤 実施例 ６ ７ ８ ９ ○ニトロセルロ−ス 1.2 10.0 6.8 3.5 ○ニトロセルロ−ス以外のニトロ化合物 ニトロメタン 15.8 ニトロエタン 16.5 ニトロプロパン 11.7 ジニトロトルエン 15.5 ○酸化剤 過塩素酸カリウム 25.0 40.0 45.0 42.0 過塩素酸アンモニウム 25.0 ○可燃剤 麻炭 2.3 1.6 3.0 2.1 ＢＬ助燃剤 6.0 5.0 7.6 6.5 塩化ゴム 8.0 5.0 7.0 6.5 フェノ−ルレジン 1.6 0.9 2.5 1.5 ○焔色剤 炭酸ストロンチウム 11.0 16.4 シュウ酸ナトリウム 21.4 酸化銅 11.0 硝酸バリウム 15.1 ○煙火の色 緑 紫 紅 黄 Drug Example 6 7 8 9 ○ Nitrocellulose 1.2 10.0 6.8 3.5 ○ Nitro compound other than nitrocellulose Nitromethane 15.8 Nitroethane 16.5 Nitropropane 11.7 Dinitrotoluene 15.5 ○ Oxidizing agent Potassium perchlorate 25.0 40.0 45.0 42.0 Perchloric acid Ammonium 25.0 ○ Flammable agent Hemp coal 2.3 1.6 3.0 2.1 BL combustion aid 6.0 5.0 7.6 6.5 Chloride rubber 8.0 5.0 7.0 6.5 Phenol resin 1.6 0.9 2.5 1.5 ○ Flame colorant Strontium carbonate 11.0 16.4 Sodium oxalate 21.4 Copper oxide 11.0 Barium nitrate 15.1 ○ Smoke color green purple red yellow
【０００２９】[00029]
【発明の効果】製造が容易で、煙火組成物としての効果
を有する火工品組成物が得られた。According to the present invention, a pyrotechnic composition which is easy to produce and has an effect as a smoke composition is obtained.
Claims (12)
色剤を主要成分として含有することを特徴とする火工品
組成物1. A pyrotechnic composition comprising nitrocellulose, an oxidizing agent, a combustible agent and a flame colorant as main components.
のニトロ化合物を混合してゲル状組成物とし、これに酸
化剤、可燃剤及び焔色剤を混合した後、乾燥してなる火
工品組成物2. A pyrotechnic composition comprising a mixture of nitrocellulose and a nitro compound other than nitrocellulose to form a gel composition, an oxidizing agent, a combustible agent and a flame colorant, followed by drying.
０重量％とニトロセルロース以外のニトロ化合物９７〜
６０重量％の混合比である請求項２に記載の火工品組成
物3. A gel composition comprising nitrocellulose 3-4.
0% by weight and nitro compounds other than nitrocellulose 97 ~
3. The pyrotechnic composition according to claim 2, wherein the mixing ratio is 60% by weight.
率が０．６〜１２重量％である請求項１乃至３のいずれ
か一項に記載の火工品組成物4. The pyrotechnic composition according to claim 1, wherein the content of nitrocellulose in the processed product composition is 0.6 to 12% by weight.
ぞれ４０〜６０重量％、１０〜２５重量％、１５〜５０
重量である請求項１乃至４のいずれか一項に記載の火工
品組成物5. An oxidizing agent, a combustible agent and a flame colorant content of 40 to 60% by weight, 10 to 25% by weight, and 15 to 50%, respectively.
The pyrotechnic composition according to any one of claims 1 to 4, which is a weight.
請求項１乃至５のいずれか一項に記載の火工品組成物6. The pyrotechnic composition according to claim 1, wherein the pyrotechnic composition is a fireworks star or a lance.
のニトロ化合物を混合してゲル状組成物とし、これに酸
化剤、可燃剤、焔色剤を混合した後乾燥することを特徴
とする火工品組成物の製法7. A pyrotechnic composition comprising mixing a nitrocellulose and a nitro compound other than nitrocellulose to form a gel composition, mixing an oxidizing agent, a combustible agent, and a flame colorant, followed by drying. Manufacturing method
０重量％とニトロ化合物９７〜６０重量％の混合比であ
る請求項７に記載の火工品組成物の製法8. A gel composition comprising nitrocellulose 3-4.
The method for producing a pyrotechnic composition according to claim 7, wherein the mixing ratio is 0% by weight and 97 to 60% by weight of the nitro compound.
酸化剤、可燃剤および焔色剤の合計が９０〜７０重量％
である請求項７乃至８のいずれか一項に記載の火工品組
成物の製法9. The composition according to claim 1, wherein the gel composition comprises 10 to 30% by weight.
The total amount of the oxidizing agent, the combustible agent and the flame colorant is 90 to 70% by weight.
The method for producing a pyrotechnic composition according to any one of claims 7 to 8, wherein
ニトロアルカン類である請求項７乃至９のいずれか一項
に記載の火工品組成物の製法10. The method for producing a pyrotechnic composition according to claim 7, wherein the nitro compound other than nitrocellulose is a nitroalkane.
ロエタン及びニトロプロパンからなる群から選ばれる１
種又は２種以上である請求項１０に記載の火工品組成物
の製法11. The nitroalkane is selected from the group consisting of nitromethane, nitroethane and nitropropane.
11. The method for producing a pyrotechnic composition according to claim 10, wherein the composition is at least one species.
る請求項７乃至１１のいずれか一項に記載の火工品組成
物の製法12. The method for producing a pyrotechnic composition according to claim 7, wherein the pyrotechnic composition is a fireworks star or a lance.