JP2000182911A - Electric double-layered capacitor and manufacture thereof - Google Patents
Electric double-layered capacitor and manufacture thereofInfo
- Publication number
- JP2000182911A JP2000182911A JP35654898A JP35654898A JP2000182911A JP 2000182911 A JP2000182911 A JP 2000182911A JP 35654898 A JP35654898 A JP 35654898A JP 35654898 A JP35654898 A JP 35654898A JP 2000182911 A JP2000182911 A JP 2000182911A
- Authority
- JP
- Japan
- Prior art keywords
- case
- gas
- electric double
- atmosphere
- layer capacitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】 本発明は、電気二重層キャ
パシタおよび同キャパシタの製造方法に関する。The present invention relates to an electric double layer capacitor and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】 電気二重層キャパシタは、サイズも小
型化が可能で、かつ軽量であることに加えて、ニッケル
−カドミウム二次電池に比較して、その１回当たりの充
電容量は約８０分の１から約６０分の１と低いものの、
充放電時に化学反応を伴わないために、原理的に充放電
による劣化がなく、充電も短時間にできるという利点を
有している。充放電サイクルもほぼ半永久的であり、基
本的には特性劣化も起こさず、使用可能温度範囲も広
く、ショートしてもキャパシタそのものが破壊されるこ
とはないという二次電池にない特性を有している。従っ
て、各種電子機器のバックアップ電池として幅広く使用
されており、また、電池、蓄電池等の代替品として、例
えば、電気自動車や、点火装置用電源としてその利用が
検討されているところである。2. Description of the Related Art In addition to being small in size and light in weight, an electric double layer capacitor has a charge capacity per time of about 80 minutes as compared with a nickel-cadmium secondary battery. Although it is as low as 1 / 60th of 1
Since there is no chemical reaction during charge / discharge, there is an advantage that there is no deterioration due to charge / discharge in principle and the charge can be performed in a short time. The charge-discharge cycle is almost semi-permanent, basically there is no deterioration of characteristics, the usable temperature range is wide, and the capacitor itself is not destroyed even if it is short-circuited. ing. Therefore, it is widely used as a backup battery for various electronic devices, and its use as a power source for an electric vehicle or an ignition device, for example, as a substitute for a battery or a storage battery is being studied.
【０００３】 ところで、電気二重層キャパシタは、そ
の主要素材として炭素繊維や炭素微粉を使用しているた
めに、炭素繊維や炭素微粉の製造段階のみならず、最終
製品の電気二重層キャパシタを製造するまでの各工程
で、その表面に吸着された水分や分解により水分を生成
する官能基が炭素繊維や炭素微粉の内部に吸蔵されたま
ま最終製品である電気二重層キャパシタが製造される
と、様々な障害が発生する。勿論、電気二重層キャパシ
タの主要素材である炭素繊維や炭素微粉については、使
用前に、その表面を処理する方法が提案されており、可
成りの改善が認められている。しかし、電気二重層キャ
パシタの製造工程で吸着されるこれらの物質の除去方法
としては特別な方法がない。僅かに、電気二重層キャパ
シタの最終組立工程において水分を吸着することがない
ように、充分に乾燥した電気二重層キャパシタ用の分極
性電極を、水分を一定の量以下に制御し、かつ内部の雰
囲気をアルゴン雰囲気下に置換した組立室、即ち、グロ
ーブボックス内で組立、封止する方法が採用されている
のが現状である。By the way, since electric double layer capacitors use carbon fiber or carbon fine powder as a main material, not only the step of manufacturing carbon fiber or carbon fine powder but also the final electric double layer capacitor is manufactured. In each of the steps up to the end, the electric double layer capacitor, which is the final product, is manufactured while the functional groups that generate water by decomposition and water adsorbed on the surface are stored in the carbon fiber or carbon fine powder. Failure occurs. Of course, a method of treating the surface of carbon fiber or carbon fine powder which is a main material of the electric double layer capacitor before use has been proposed, and a considerable improvement has been recognized. However, there is no special method for removing these substances adsorbed in the manufacturing process of the electric double layer capacitor. Slightly dry polarizable electrodes for electric double layer capacitors should be controlled to a certain amount of water or less to prevent moisture from adsorbing in the final assembly process of the electric double layer capacitor, and At present, a method of assembling and sealing in an assembly room in which the atmosphere is replaced with an argon atmosphere, that is, in a glove box, is employed.
【０００４】 しかしながら、この方法では、組立工程
での水分吸収量を一定水準以下に制御することは可能で
あるが、各種の材料の組立前乾燥工程では完全に除去で
きずに残存している水分を電気二重層キャパシタの組立
工程に於いて完全に除去することは事実上不可能である
ことは容易に理解できるところである。ところが、この
ような状態の電気二重層キャパシタを使用すると、下記
化１However, in this method, it is possible to control the amount of water absorbed in the assembling process to a certain level or less, but it is not possible to completely remove the remaining water in the drying process before assembling various materials. It can be easily understood that it is practically impossible to completely remove the in the process of assembling the electric double layer capacitor. However, when an electric double layer capacitor in such a state is used,
【０００５】[0005]
【化１】 のような反応が起こり溶媒単独での分解反応や残存水分
が電極材料である炭素と反応して主として炭酸ガスを発
生させる。炭酸ガス以外にもメタンやエチレン等のガス
も発生することがある。このような発生ガスによって電
気二重層キャパシタのケースの内圧を上昇させて、キャ
パシタの特性の低下を引き起こすという欠点がある。Embedded image The following reaction occurs, and the decomposition reaction using the solvent alone or the remaining water reacts with carbon as the electrode material to generate mainly carbon dioxide gas. In addition to carbon dioxide gas, gases such as methane and ethylene may be generated. There is a drawback in that the generated gas increases the internal pressure of the case of the electric double layer capacitor and causes deterioration of the characteristics of the capacitor.
【０００６】[0006]
【発明が解決しようとする課題】 本発明は、上記のよ
うな従来の方法で製造された電気二重層キャパシタを使
用するときに発生する炭酸ガスを抑制することにより、
使用による特性の低下を起こさない電気二重層キャパシ
タおよびその製造方法を提供しようとするものである。DISCLOSURE OF THE INVENTION The present invention has been made by suppressing the carbon dioxide gas generated when using the electric double layer capacitor manufactured by the conventional method as described above,
An object of the present invention is to provide an electric double layer capacitor which does not cause deterioration in characteristics due to use and a method for manufacturing the same.
【０００７】[0007]
【課題を解決するための手段】 本発明者らは、上記の
課題を解決するために種々検討した結果、電気二重層キ
ャパシタの組立工程に於いて、電気二重層キャパシタの
最終封止前にケース内の雰囲気をヘリウム、アルゴン等
の不活性ガスや窒素ガス、炭酸ガス、或いは、これらの
混合物等の電気二重層キャパシタに含まれる各種部材に
悪影響を与えないガスの乾燥ガスで置換することによ
り、使用時に劣化の原因となる主として残存水分に起因
する炭酸ガス等のガスの発生を抑制することにより、使
用による特性の低下を起こさないことから、上記の課題
を解決できることを見いだして、本発明を完成させたも
のである。さらに、本発明に係る製造方法によれば、反
復使用によっても劣化を実質的に引き起こすことのない
電気二重層キャパシタが提供されることを見いだして、
本発明を完成させたものである。Means for Solving the Problems The present inventors have made various studies to solve the above-mentioned problems, and as a result, in the assembly process of the electric double layer capacitor, before the final sealing of the electric double layer capacitor, By replacing the atmosphere in the atmosphere with a dry gas of an inert gas such as helium, argon, nitrogen gas, carbon dioxide gas, or a gas that does not adversely affect various members included in the electric double layer capacitor such as a mixture thereof, By suppressing the generation of gas such as carbon dioxide gas mainly due to residual moisture which causes deterioration during use, it is possible to solve the above-described problem because the characteristics are not deteriorated by use. It has been completed. Furthermore, according to the manufacturing method of the present invention, it has been found that an electric double layer capacitor that does not substantially cause deterioration even by repeated use is provided.
The present invention has been completed.
【０００８】[0008]
【発明の実施の形態】 本発明の第１の側面は、電気二
重層キャパシタの組立工程において、電気二重層キャパ
シタ用の各部品を電気二重層キャパシタ用のケ−ス内に
収納し、これに電解液を加た後、該ケースの一端に設け
られた送気孔から乾燥ガスを吹き込み、ケース内の雰囲
気を乾燥ガスで置換することを特徴とする電気二重層キ
ャパシタの製造方法に関する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A first aspect of the present invention is that, in a process of assembling an electric double layer capacitor, each component for the electric double layer capacitor is housed in a case for the electric double layer capacitor. The present invention relates to a method for manufacturing an electric double layer capacitor, characterized in that after an electrolyte is added, a dry gas is blown from an air supply hole provided at one end of the case to replace an atmosphere in the case with the dry gas.
【０００９】 ケース内の雰囲気を乾燥ガスで置換する
ことにより、電気二重層キャパシタの使用時に、主とし
て残存水分と炭素原子が反応することにより発生する炭
酸ガスを抑制することができる。また、送気孔から乾燥
ガスを吹き込むと共に、ケースの別の一端に設けられた
排気孔からケース内の雰囲気に含まれる空気を強制排気
してケース内を乾燥ガスで置換することによりケース内
の雰囲気を効率よく置換することもできる。なお、使用
する乾燥ガスとしては、ヘリウム、アルゴン等の不活性
ガスや窒素ガス、炭酸ガス、或いは、これらの混合物等
の電気二重層キャパシタに含まれる各種部材に悪影響を
与えないガスを乾燥させたものが好適に使用される。中
でも、炭酸ガスが好ましい。By replacing the atmosphere in the case with the dry gas, it is possible to suppress carbon dioxide gas generated mainly by a reaction between residual moisture and carbon atoms when the electric double layer capacitor is used. In addition, the dry gas is blown from the air supply hole, and the air contained in the case is forcibly exhausted from the exhaust hole provided at another end of the case to replace the inside of the case with the dry gas. Can be efficiently replaced. In addition, as a drying gas to be used, an inert gas such as helium or argon, a nitrogen gas, a carbon dioxide gas, or a gas that does not adversely affect various members included in the electric double layer capacitor, such as a mixture thereof, was dried. Are preferably used. Among them, carbon dioxide is preferable.
【００１０】 本発明に係る製造方法において使用する
電気二重層キャパシタ用の部品としては、分極性電極、
セパレータ、集電電極等の通常電気二重層キャパシタ用
部品として使用されるものであれば、特に制限なく使用
可能である。即ち、本発明においては、分極性電極は、
所定の容量密度と耐電圧性を充足する限り、その製造方
法の如何に拘わらず使用できる。係る分極性電極の製造
方法は当業者の間においては公知である。しかしなが
ら、できるだけ、水分を吸収しないような条件で製造さ
れたものが好ましいことは、ことの性質上明らかであろ
う。セパレータとしては、やはり公知のものが使用で
き、例えば、ポリオレフィン系樹脂製の微孔性フィル
ム、不織布等のセルーロース系多孔質材料などが使用で
きる。[0010] Components for the electric double layer capacitor used in the manufacturing method according to the present invention include a polarizable electrode,
Any material that is normally used as a component for an electric double layer capacitor, such as a separator and a collecting electrode, can be used without any particular limitation. That is, in the present invention, the polarizable electrode is
It can be used irrespective of its manufacturing method as long as it satisfies predetermined capacity density and withstand voltage. A method for producing such a polarizable electrode is known to those skilled in the art. However, it will be clear from the nature of the matter that it is preferred to be manufactured under conditions that do not absorb moisture as much as possible. Known separators can also be used as the separator, and for example, a cellulosic porous material such as a microporous film made of a polyolefin resin or a nonwoven fabric can be used.
【００１１】 集電電極としては、やはり電気二重層キ
ャパシタに使用されている公知の材質のもの、例えば、
純度が９９．８％以上のいわゆる純アルミエッチド箔が
使用できる。誘電加熱操作完了後に添加される電解液と
しては、公知のもの、例えば、炭酸プロピレン、γ−ブ
チロラクトン、アセトニトリル、ジメチルホルムアミド
等の溶媒に第４級アンモニウム塩、ホスフォニウム塩等
の溶質を溶解して調製したものが使用される。収納用の
ケースとしては、金属製のもの、例えば、ステンレス製
のものやアルミニウム製のものや樹脂に金属箔を積層し
た構造を有するラミネートフィルムが使用される。The current collecting electrode is made of a known material also used for an electric double layer capacitor, for example,
A so-called pure aluminum etched foil having a purity of 99.8% or more can be used. As the electrolytic solution added after the completion of the dielectric heating operation, known electrolytes, for example, prepared by dissolving a solute such as a quaternary ammonium salt or a phosphonium salt in a solvent such as propylene carbonate, γ-butyrolactone, acetonitrile, or dimethylformamide. Is used. As the storage case, a metal case, for example, a stainless steel case, an aluminum case, or a laminate film having a structure in which a metal foil is laminated on a resin is used.
【００１２】 本発明に係る電気二重層キャパシタの製
造方法において、使用する乾燥ガスは、充分に乾燥させ
たガスを使用することが好ましい。使用する乾燥ガスの
由来は特には問題とはならず、通常市販されているもの
が好適に使用される。In the method for manufacturing an electric double layer capacitor according to the present invention, it is preferable to use a sufficiently dried gas as a drying gas. The origin of the dry gas to be used does not matter in particular, and those commercially available are preferably used.
【００１３】 ケース内の雰囲気を乾燥ガスで置換する
に際しては、置換用の乾燥ガスを強制的に送り込めるよ
うにすることが好ましい。置換用の乾燥ガスを送り込む
に際しては、送気孔を収納用ケースに設けておくことが
好ましい。特に、強制送気用のポンプ、即ち、送気ポン
プにつながれた送気ホースが容易に着脱できる送気ホー
ス装着用部材が該ケースから突出して形成されているこ
とが好ましい。さらに好ましくは、この突出して形成さ
れている送気ホース装着用部材、換言すれば、送気孔が
熱可塑性樹脂製であれば、ケース内の雰囲気の置換操作
の終了と同時に、該送気用部材を加熱し溶融することに
より、容易に封止することができる。所望により、送気
ポンプとして吸排気兼用ポンプを使用し送気孔からケ−
ス内部の空気を排気して後、次いで、ポンプを給気モー
ドに切り替え、乾燥ガスを供給して内部雰囲気を乾燥ガ
スに置換してもよい。また、場合によっては、置換操作
を効率よく行うために、排気孔を設けてもよいが、この
排気孔も同一の材料で構成されていることが好ましい。
同一の材料で構成されておれば、ケース内の雰囲気の置
換操作の終了と同時に、該排気孔を送気孔と共に加熱し
溶融することにより、容易に封止することができるから
である。When replacing the atmosphere in the case with a dry gas, it is preferable that the dry gas for replacement can be forcibly fed. When sending the replacement dry gas, it is preferable to provide an air supply hole in the storage case. In particular, it is preferable that a pump for forced air supply, that is, an air supply hose mounting member from which the air supply hose connected to the air supply pump can be easily attached and detached is formed to protrude from the case. More preferably, if the protruding air supply hose mounting member, in other words, if the air supply hole is made of a thermoplastic resin, the air supply member is replaced with the air supply member at the same time as the end of the atmosphere replacement operation in the case. Can be easily sealed by heating and melting. If desired, use a pump for both intake and exhaust as the air supply pump, and
After exhausting the air inside the gas, the pump may be switched to the air supply mode, and the drying gas may be supplied to replace the internal atmosphere with the drying gas. In some cases, an exhaust hole may be provided in order to perform the replacement operation efficiently, but it is preferable that the exhaust hole is also made of the same material.
If the same material is used, the exhaust hole is heated and melted together with the air supply hole at the same time as the completion of the replacement operation of the atmosphere in the case, so that the case can be easily sealed.
【００１４】 本発明の第２の側面である、本発明に係
る電気二重層キャパシタの製造方法により製造された電
気二重層キャパシタは、特に乾燥ガスとして炭酸ガスを
使用した場合には、二重層キャパシタ内の雰囲気が炭酸
ガスにより置換されているので、万が一残存水分がケー
ス内に存在していても雰囲気の炭酸ガス分圧が高いので
炭酸ガスの発生が抑制されるため、１０，０００サイク
ル繰り返し充放電を繰り返しても、静電容量の低下は５
％以下で、内部抵抗の増加は１０％以下であり、顕著な
性能の劣化は認められないという優れた特性を有してい
る。The electric double layer capacitor manufactured by the method for manufacturing an electric double layer capacitor according to the second aspect of the present invention is a double layer capacitor particularly when carbon dioxide is used as a drying gas. Since the atmosphere in the chamber is replaced by carbon dioxide, even if residual moisture is present in the case, the generation of carbon dioxide is suppressed because the carbon dioxide partial pressure of the atmosphere is high. Even if the discharge is repeated, the decrease in capacitance is 5
% Or less, the increase in internal resistance is 10% or less, and it has excellent characteristics that no remarkable deterioration in performance is observed.
【００１５】[0015]
【実施例】 次に、本発明を実施例を用いてさらに詳し
く説明するが、本発明はこれらの実施例に限られるもの
ではない。なお、以下に示す方法より本発明に係る電気
二重層キャパシタの静電容量の低下、および内部抵抗の
増加を測定した。EXAMPLES Next, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples. In addition, a decrease in the capacitance and an increase in the internal resistance of the electric double layer capacitor according to the present invention were measured by the following methods.
【００１６】（静電容量の低下の測定法）被検サンプル
を定格電圧で２０分以上充電した後、所定の定電流で放
電させる。放電開始直後の電圧降下した時点ｔ1での電
圧Ｖ1から放電終止電圧Ｖ2に至るまでの時間ｔ2までの
放電電力の積分値(Measurement Method of Capacitance Reduction) A test sample is charged at a rated voltage for 20 minutes or more, and then discharged at a predetermined constant current. Integrated value of discharging power from voltages V 1 at time t 1 which is the voltage drop immediately after discharge start up time t 2 until reaching the discharge termination voltage V 2
【００１７】[0017]
【数１】 (Equation 1)
【００１８】[0018]
【数２】 により求める。(Equation 2) Ask by
【００１９】（内部抵抗の増加の測定法）被検サンプル
を定格電圧で２０分以上充電した後、所定の定電流で放
電させる。放電開始直後の電圧降下量（Ｖ0−Ｖ1）と放
電電流Ｉから内部抵抗値Ｒを下式 Ｒ＝（Ｖ0−Ｖ1）／Ｉ により求める。(Measurement method of increase in internal resistance) A test sample is charged at a rated voltage for 20 minutes or more, and then discharged at a predetermined constant current. From the voltage drop (V 0 -V 1 ) immediately after the start of discharge and the discharge current I, the internal resistance value R is determined by the following equation: R = (V 0 -V 1 ) / I.
【００２０】（実施例）水蒸気賦活活性炭を使用して製
造した２００ｐｐｍの水分を残存水分として含んだ分極
性電極と、真空乾燥により充分に乾燥させたセパレー
タ、および集電電極を使用し、常法に従いポリプロピレ
ン製の送気孔と排気孔を取り付けたケース内に収納し、
次いで、電解液を添加した後、図１に模式的に示した装
置を用い、前記排気孔からケース内の雰囲気内に含まれ
る空気を排気させながら、前記送気孔から乾燥ガスとし
て乾燥炭酸ガスを強制的に送り込み、ケース内の雰囲気
を乾燥炭酸ガスにより置換し、残存水分を実質的に零と
した。この置換操作には、５分必要とした。置換操作終
了後ポリプロピレン製の送気孔と排気孔とを加熱、溶融
してふさぐと共に、ケースを常法に従い封止した。この
ものを用いて充放電を１０，０００サイクル繰り返した
が静電容量の低下は５％以内で、内部抵抗の増加は１０
％以内であり顕著な特性劣化は認められなかった。(Example) A polarizable electrode containing 200 ppm of water as residual water produced by using steam activated carbon, a separator sufficiently dried by vacuum drying, and a current collecting electrode were used in a conventional manner. In a case fitted with a polypropylene air vent and exhaust vent according to
Then, after adding the electrolytic solution, using a device schematically shown in FIG. 1, while exhausting air contained in the atmosphere in the case from the exhaust hole, dry carbon dioxide gas as a dry gas from the air supply hole. The atmosphere in the case was replaced with dry carbon dioxide gas to reduce the residual moisture to substantially zero. This replacement operation required 5 minutes. After the replacement operation, the air supply and exhaust holes made of polypropylene were heated, melted and closed, and the case was sealed in a conventional manner. The charge / discharge cycle was repeated 10,000 times using this device. The decrease in capacitance was within 5%, and the increase in internal resistance was 10%.
% Or less, and no remarkable property deterioration was observed.
【００２１】（比較例）ケース内の雰囲気を炭酸ガスで
置換する操作を行わなかった以外は、実施例と同様にし
て電気二重層キャパシタを製造した。得られた電気二重
層キャパシタは１０，０００サイクルの充放電を繰り返
したところ、静電容量の低下は１５％で、内部抵抗の増
加は２５％であり、特性の著しい著しい低下が認められ
た。Comparative Example An electric double layer capacitor was manufactured in the same manner as in the example, except that the operation of replacing the atmosphere in the case with carbon dioxide was not performed. When the obtained electric double layer capacitor was repeatedly charged and discharged for 10,000 cycles, the decrease in capacitance was 15% and the increase in internal resistance was 25%, and a remarkable remarkable decrease in characteristics was observed.
【００２２】[0022]
【発明の効果】 電気二重層キャパシタの組立工程に於
いて電気二重層キャパシタ用の各種部品をケースに収納
し、電解液を加え、電気二重層キャパシタを封止する前
にケース内の雰囲気を特定のガス、特に乾燥炭酸ガスで
置換することによりケース内に水分が残存しないように
して、使用時に劣化の原因となる残存水分と炭素原子等
との反応により発生する主として炭酸ガスからなるガス
の発生を抑制することにより長時間使用しても実質的に
劣化のない電気二重層キャパシタが得られる。また、収
納用のケ−スに設けた送気孔と排気孔を置換作業の終了
と同時に、加熱、溶融することにより、容易に封止する
ことができるという効果が得られる。[Effects of the Invention] In the assembly process of an electric double layer capacitor, various parts for the electric double layer capacitor are stored in a case, an electrolyte is added, and the atmosphere in the case is specified before the electric double layer capacitor is sealed. Of gas, especially of carbon dioxide, generated by the reaction of residual water with carbon atoms, etc., which causes deterioration during use by replacing the gas with dry gas, especially dry carbon dioxide , An electric double layer capacitor that does not substantially deteriorate even when used for a long time can be obtained. In addition, an effect is obtained that the air supply and exhaust holes provided in the housing case are heated and melted at the same time as the completion of the replacement operation, whereby the sealing can be easily performed.
【図１】 本発明に係る製造方法に使用する装置の概要
図である。FIG. 1 is a schematic view of an apparatus used for a manufacturing method according to the present invention.
【符号の説明】 １…電気二重層キャパシタ、２…送気孔、３…印加通電
用回路、４…送気用ポンプ、５…送気用ホース。[Description of Signs] 1 ... Electric double layer capacitor, 2 ... Air supply hole, 3 ... Applying current supply circuit, 4 ... Air supply pump, 5 ... Air supply hose.
Claims (9)
層し、この積層体をケース内に収納し、電解液を加えた
後、ケース内に乾燥ガスを吹き込み、ケース内の雰囲気
を乾燥ガスで置換することを特徴とする電気二重層キャ
パシタの製造方法。1. A polarizing electrode, a separator, and a current collecting electrode are laminated, the laminated body is housed in a case, an electrolyte is added, and then a dry gas is blown into the case, and an atmosphere in the case is dried gas. A method for manufacturing an electric double layer capacitor.
燥ガスを吹き込み、ケース内の雰囲気を乾燥ガスで置換
することを特徴とする請求項１に記載の製造方法。2. The method according to claim 1, wherein a dry gas is blown from an air supply hole provided at one end of the case, and the atmosphere in the case is replaced with the dry gas.
した後、同送気孔から乾燥ガスを吹き込みケース内の雰
囲気を乾燥ガスで置換することを特徴とする請求項２に
記載の製造方法。3. The manufacturing method according to claim 2, wherein after the air in the case is sucked and exhausted from the air supply hole, a dry gas is blown from the air supply hole to replace the atmosphere in the case with the dry gas. .
ケースの別の一端に設けられた排気孔からケース内の雰
囲気に含まれる空気を強制排気してケース内を乾燥ガス
で置換することを特徴とする請求項１または２に記載の
製造方法。4. Dry gas is blown from an air supply hole,
3. The method according to claim 1, wherein air contained in the atmosphere in the case is forcibly exhausted from an exhaust hole provided at another end of the case to replace the inside of the case with a dry gas.
きる熱可塑性樹脂により形成されていることを特徴とす
る請求項２〜４のいずれか１項に記載の製造方法。5. The method according to claim 2, wherein at least the air holes are formed of a thermoplastic resin that can be sealed by heating.
特徴とする請求項１〜５のいずれか１項に記載の製造方
法。6. The method according to claim 1, wherein the dry gas is a dry carbon dioxide gas.
よび電解液と、これら材料を収納したケースとからな
り、ケース内の雰囲気が乾燥ガスにより置換されてお
り、かつ、請求項１〜６のいずれか１項に記載の方法に
より製造されたことを特徴とする電気二重層キャパシ
タ。7. A polarizing electrode, a separator, a collecting electrode, and an electrolytic solution, and a case containing these materials, wherein the atmosphere in the case is replaced by a dry gas, and An electric double-layer capacitor manufactured by the method according to any one of claims 1 to 3.
特徴とする請求項７に記載の電気二重層キャパシタ。8. The electric double layer capacitor according to claim 7, wherein the dry gas is a dry carbon dioxide gas.
止できる熱可塑性樹脂により形成されている該送気孔お
よび該排気孔が加熱により封止されていることを特徴と
する請求項８に記載の電気二重層キャパシタ。9. The air supply hole and the exhaust hole formed of a thermoplastic resin which can be sealed by heating provided in the case are sealed by heating. Electric double layer capacitor.