JP2000177977A - Sling - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an endless sling, wherein during endless sling manufacturing, good strand handling operability is maintained, and a high strength contribution rate and excellent performance are provided. SOLUTION: In an endless sling 1 constructed in such a manner that a core portion 22 having a ring formed by winding a strand 21 made of a plurality of high strength synthetic fiber twisted or untwisted threads 20 is contained in a bag-like protective material 23, the strand 21 of the core portion 22 is made of a rough woven thread group 24 roughly woven with a horizontal thread implanting density set equal to 10 or lower, per 100 mm.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、クレーンやホイス
ト等の設備により重量物を吊り上げあるいは牽引するの
に使用される一般にエンドレススリングと呼ばれる環状
の吊り具に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an annular lifting device generally called an endless sling used for lifting or towing a heavy object by using equipment such as a crane and a hoist.

【０００２】[0002]

【従来の技術】従来エンドレススリングは、破断強力の
大きな合成繊維糸のストランドを要求される性能により
定められる回数分巻回しを行うことにより形成した無端
環状の芯材を比較的柔軟な布等の材質からなる筒状の袋
で包んで形成される。係るエンドレススリングは、細幅
織物を利用したいわゆるベルトスリングに比べて高い強
力が得やすいこと、またワイヤーロープ等の高強力を得
やすい吊り具に比べて本体が柔軟で取り扱い易く、吊り
上げる対象物に傷をつけにくい等の利点から、工場等で
重量物の玉掛け作業を行う際の吊り具として重宝されて
いる。2. Description of the Related Art Conventionally, an endless sling is formed by winding an endless annular core formed by winding a strand of synthetic fiber yarn having a large breaking strength by a number of times determined by required performance, such as a relatively soft cloth. It is formed by wrapping in a cylindrical bag made of a material. Such an endless sling is easy to obtain a high strength compared to a so-called belt sling using a narrow fabric, and the main body is flexible and easy to handle as compared to a hanging tool that easily obtains a high strength such as a wire rope, so that the object to be lifted can be used. Because of its advantages such as being less likely to be scratched, it is useful as a hanging tool for slinging heavy objects in factories and the like.

【０００３】このようなエンドレススリングを製造する
方法として、例えば、ストランドを筒状保護材の一端か
ら挿入し、他端より引き抜くことにより最初のリングを
形成した後に、これをたぐることにより保護材の中に複
数周のリングを形成する方法や予めストランドのリング
を形成したものを保護材で包み縫製または逢着する方法
がとられている。[0003] As a method of manufacturing such an endless sling, for example, a first ring is formed by inserting a strand from one end of a tubular protective material and pulling it out from the other end, and then traversing the first ring to form the protective material. A method in which a plurality of rings are formed therein, and a method in which a ring of strands is formed in advance with a protective material are sewn or sewn together.

【０００４】又、係るエンドレススリングを製造する為
の製造装置としては、例えば特公平３−５１８３６号公
報に記載されているものが知られており、その具体的な
構成は、図４のように一組のプーリ１２、１３間に回転
する支持体１１に搭載された複数個のボビン６から引き
出された糸７を撚回して糸状ストランド８とし、係るス
トランド８を使用して最初の１周分のリングを形成し、
これに後続の糸状ストランド８を接続してプーリ１２、
１３を所定回数分回転させることにより所定の周数のリ
ングを形成するといった装置が考案され販売されてい
る。As a manufacturing apparatus for manufacturing such an endless sling, for example, a manufacturing apparatus described in Japanese Patent Publication No. 3-51836 is known, and the specific configuration thereof is as shown in FIG. A thread 7 drawn from a plurality of bobbins 6 mounted on a support 11 rotating between a pair of pulleys 12 and 13 is twisted into a thread-like strand 8, and the strand 8 is used for the first round. Forming a ring of
A subsequent thread-like strand 8 is connected to the pulley 12,
An apparatus in which a ring having a predetermined number of turns is formed by rotating the ring 13 a predetermined number of times has been devised and sold.

【０００５】尚、図４中３２は、予め保護材が被覆され
ている、一部にスリット状の切り欠け部を有する中空管
であり、この中を当該ストランドが通過する様に構成さ
れている。係るエンドレススリングは上記のような方法
で製造されるが、周回させるストランドの構成が製造時
の効率と製品の性能を大きく左右する要素となる。In FIG. 4, reference numeral 32 denotes a hollow tube which is coated with a protective material in advance and has a slit-shaped notch in a part thereof. The hollow tube is configured so that the strand passes therethrough. I have. Such an endless sling is manufactured by the above-described method, and the configuration of the orbiting strand is a factor that greatly affects the efficiency at the time of manufacturing and the performance of the product.

【０００６】即ち、ストランドを単一の糸条により構成
すれば、複数本の糸条によりストランドで同等の強度の
ソフトスリングを構成した場合に比べてストランドの周
数が多くなり製造に関わる時間的な効率が悪くなる。ま
た、エンドレススリングの性能を評価する要素として、
以下の式による投入された材料原糸が持つ強力とエンド
レススリング自体の破断強力の比を強力寄与率と称し、
次式で表される特性値を使用している。That is, if the strand is constituted by a single yarn, the number of turns of the strand is increased as compared with the case where a soft sling of the same strength is constituted by the strand by a plurality of yarns, and the time required for manufacturing is reduced. Efficiency becomes worse. In addition, as an element to evaluate the performance of the endless sling,
The ratio of the strength of the input raw material yarn and the breaking strength of the endless sling itself according to the following formula is called the strength contribution rate,
The characteristic value represented by the following equation is used.

【０００７】即ち、 強力寄与率[%]=Ｆ／（ｋ×ｄ×Ｎ×Ｒ×２）×１００ ここで、 ｋ: ストランドに使用される糸の乾強度〔ｇ／ｄｅ〕 ｄ: ストランドに使用される糸の繊度〔ｄｅ〕 Ｎ: ストランドを構成する糸条の本数 Ｒ: ストランドの周回数 Ｆ: ソフトスリングの強度〔ｇ〕 つまり、上記の強力寄与率は、投入された材料の性能に
対して製品として実現される性能の効率を表すが、周数
を多くすることはこの強力寄与率を左右する要素である
ストランドの周長，テンションのばらつきといった要素
の管理を難しくするといった弊害を生じる。That is, strength contribution ratio [%] = F / (k × d × N × R × 2) × 100 where k: dry strength of yarn used for strand [g / de] d: to strand The fineness of the yarn used [de] N: The number of yarns constituting the strand R: The number of turns of the strand F: The strength of the soft sling [g] In other words, the above-mentioned strong contribution rate depends on the performance of the material input. On the other hand, it indicates the efficiency of the performance realized as a product, but increasing the number of circumferences has the adverse effect of making it difficult to manage the factors such as the circumference of the strand and the variation in tension, which are factors that influence this strong contribution ratio. .

【０００８】つまり、周回させた各ストランドの持つ強
力を効率よく利用するためには、製造時にストランドを
周回させる際のテンションを一定に保ち、各周の周長を
均一に保つことが望ましいが、これらにばらつきがある
とソフトスリングに力が加わった際に各ストランドにか
かるテンションが均一にならないため、エンドレススリ
ング全体の強度はテンションが均一にかかる場合に比べ
て低下し、相対的に前述の強力寄与率は低下することに
なる。In other words, in order to efficiently use the strength of each of the circulated strands, it is desirable to maintain a constant tension when the strands are circulated during manufacturing and to maintain the uniform perimeter of each circumstance. If there is variation, the tension applied to each strand when a force is applied to the soft sling will not be uniform, so the overall strength of the endless sling will be lower than when the tension is evenly applied, and the strength described above will be relatively high. The contribution rate will decrease.

【０００９】よって、ストランドを構成する糸条の本数
を増やし、ストランドの周数を減らすことが性能の優れ
たエンドレススリングを効率よく製造するためのポイン
トになるが、ストランドを構成する糸条の本数を増やす
ことは一方で製造時にストランドを取り扱いにくくする
ことにつながるため、取り扱い易い性状を保ったままス
トランドを形成する糸条の本数を増やすことが技術的に
重要な課題となっていた。Therefore, increasing the number of yarns constituting the strand and reducing the number of turns of the strand is a point for efficiently producing an endless sling having excellent performance. However, the number of yarns constituting the strand is On the other hand, increasing the number of strands leads to making the strands difficult to handle at the time of production. Therefore, it has been a technically important issue to increase the number of yarns forming the strands while maintaining easy-to-handle properties.

【００１０】この課題を克服するために、複数の糸条を
固定用テープにより束ねてストランドを形成する方法や
予め糸条に撚りを加えておくことにより糸状を複数本束
ねた場合の取り扱いを容易にする方法、あるいは複数の
糸条を合撚してストランドを形成するといった方法が考
案されてきたが、これらの方法はエンドレススリングの
製造の前工程における作業を繁雑にすることや、糸条に
前加工を加えるための装置を製造設備に取り付ける必要
がある等の点で問題があり、この課題を解決するための
決定的な解決策とはならなかった。[0010] In order to overcome this problem, a method of forming a strand by bundling a plurality of yarns with a fixing tape, and easily handling a bundle of a plurality of yarns by twisting the yarns in advance. Or a method of twisting a plurality of yarns to form a strand has been devised.However, these methods complicate the work in the front-end process of endless sling production, There is a problem in that a device for performing pre-processing needs to be attached to a manufacturing facility, and the solution has not been a definitive solution for solving this problem.

【００１１】又、実願昭６１−１５８７０７号に於いて
は、複数の糸条に緯方向に糸を往復させ帯状に形成する
事によりストランドを構成する方法が考案されている。
係る方法により形成されたストランドは、取扱易さの点
では相当の進歩が見られたが、ストランドの構造的な要
因からその製造にかなりの時間を要し、生産効率の点で
は従来の方法に比べて後退した技術であった。Japanese Utility Model Application No. 61-158707 has devised a method of forming a strand by reciprocating a yarn in a weft direction on a plurality of yarns to form a band.
Strands formed by such a method have made considerable progress in terms of ease of handling, but due to the structural factors of the strands, their production takes a considerable amount of time, and in terms of production efficiency, the conventional method has a disadvantage. It was a technology that receded.

【００１２】つまり、上記した従来の方法に於ける当該
緯糸の当該ストランドに対する横方向の糸の打ち込み方
法は、図６に示す様に、単純に緯糸が当該ストランドの
両端を往復するものであり、所謂シャトル織機により実
現される構造である。当該シャトル織機は一般的に製織
する速度は遅く、上記例の場合もそのストランドの製造
にかなりの時間を要し、それまでの合撚装置等を組み合
わせた製造装置に比べて製造効率の面で劣っていた。That is, the method of driving the weft into the strand in the horizontal direction in the above-described conventional method is such that the weft simply reciprocates at both ends of the strand as shown in FIG. This is a structure realized by a so-called shuttle loom. In general, the speed of weaving the shuttle loom is slow, and in the case of the above example, the production of the strand also requires a considerable amount of time. Was inferior.

【００１３】一方、織物を製造する技術として、実開昭
６３−１６７１８０号には、経糸の束を極めて緯糸密度
の低い粗い織物に織成し、この粗織糸群を使用して実際
に織物を製造する段階で当該緯糸を引き抜く事によっ
て、整経ビームを使用しないで平行な経糸を織機に供給
する様にする技術が開示されているが、スリングに関す
る内容は全く含まれていない。On the other hand, as a technique for producing a woven fabric, Japanese Utility Model Laid-Open No. 63-167180 discloses a method of weaving a bundle of warps into a coarse woven fabric having a very low weft density, and actually manufacturing the woven fabric using the group of coarse woven yarns. There is disclosed a technique in which a parallel warp is supplied to a loom without using a warping beam by pulling out the weft at a stage, but does not include any content relating to a sling.

【００１４】更に、実開昭６２−３８２８４号公報に
は、帯状織物を環状に複数回巻き重ねて環状積層体を構
成し、当該環状積層体を鞘分で被覆した後全体を逢着し
たエンドレススリングの構造が示されているが、係るエ
ンドレススリングでは、一定の方向には屈曲出来るもの
の、それ以外の方向には、容易には屈曲不可能であるた
め、使用用途が極めて限定されてしまうと言う問題があ
る。Further, Japanese Utility Model Application Laid-Open No. 62-38284 discloses an endless sling in which a band-shaped woven fabric is wound a plurality of times in an annular shape to form an annular laminated body, and the annular laminated body is covered with a sheath, and then the whole is adhered. Although such an endless sling can be bent in a certain direction, it cannot be easily bent in other directions, so that its use is extremely limited. There's a problem.

【００１５】[0015]

【発明が解決しようとする課題】本発明の目的は、上記
した従来技術が達成できなかったエンドレススリング製
造時のストランドの取り扱い性に関する問題を克服し、
且つ強力寄与率の高い性能の優れたエンドレススリング
を製造することである。SUMMARY OF THE INVENTION It is an object of the present invention to overcome the above-mentioned problems in the prior art which could not be achieved with regard to the handleability of strands during the production of endless slings.
Another object of the present invention is to produce an excellent endless sling with high performance and a high contribution ratio.

【００１６】[0016]

【課題を解決するための手段】本発明は上記した目的を
達成する為、以下に示す様な基本的な技術構成を採用す
るものである。即ち、本発明に係る第１の態様は、複数
本の高強力合成繊維の撚糸または無撚糸で構成されたス
トランドを複数回巻き上げることにより綛状のリングを
形成した芯部を、袋状の保護材に納めることにより形成
されるエンドレススリングであって、当該芯部を構成す
る当該ストランドが緯糸打込密度を１００ｍｍ当たり１
以上１０以下の粗く製編織された粗編織糸群により構成
されているエンドレススリングであり、又第２の態様と
しては、複数本の連続状合成繊維糸を当該連続状合成繊
維糸の主たる配列方向とは異なる方向に配列されている
結束糸条体により、互いに緩く結束させたストランドを
形成した後、当該ストランドを一対のローラー間に複数
回巻き回して、当該ストランドが複数本並列状に配列さ
れた芯部を形成し、次いで当該芯部を袋状の保護材で被
覆収納する様に構成されているエンドレススリングであ
る。In order to achieve the above-mentioned object, the present invention employs the following basic technical structure. That is, the first aspect according to the present invention provides a bag-shaped protection part by winding a plurality of twisted or non-twisted strands of high-strength synthetic fiber to form a skein-shaped ring. An endless sling formed by being put in a material, wherein the strands constituting the core have a weft driving density of 1 mm per 100 mm.
It is an endless sling composed of a coarsely knitted yarn group of coarsely knitted yarns of 10 or less, and as a second embodiment, a plurality of continuous synthetic fiber yarns are arranged in a main arrangement direction of the continuous synthetic fiber yarns. After forming strands loosely bound to each other by the binding yarns arranged in different directions, the strands were wound a plurality of times between a pair of rollers, and the plurality of strands were arranged in parallel. An endless sling configured to form a core, and then cover and store the core with a bag-shaped protective material.

【００１７】[0017]

【発明の実施の形態】本発明は、前述したエンドレスス
リングの製造時において複数の糸条を引き揃えて製造装
置に供給するという状況と、繊維編織物の製造時におい
て行われる経糸を引き揃えて織機に供給するという状況
との共通点に着目し、細幅編織物の分野において利用さ
れている編織機に平行に引き揃えた糸を供給するための
技術を応用することによって開発されたものであり、具
体的には、実開昭６３−１６７１８０号公報に記載され
ている様な、方法を利用して経糸の束、つまり本発明に
於ける当該複数本の連続合成繊維糸条を、緯糸と称され
る当該連続状合成繊維糸の主たる配列方向とは異なる方
向に配列されている粗緯糸群、換言すれば結束糸条によ
り、互いに緩く結束させる事によって、極めて緯糸密度
の低い粗い編織物状の糸条である粗編織糸群、或いは結
束糸条体に編織成し、この粗編織糸群若しくは結束糸条
体を直接ストランドとして使用するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a situation in which a plurality of yarns are aligned and supplied to a manufacturing apparatus during the production of the endless sling, and a warp performed in the production of a fiber knitted fabric is aligned. Focusing on the commonalities with the situation of supplying to looms, it was developed by applying technology for supplying parallel aligned yarns to looms used in the field of narrow knitting and weaving. Specifically, a bundle of warp yarns, that is, the plurality of continuous synthetic fiber yarns according to the present invention is formed into a weft yarn by using a method as described in Japanese Utility Model Application Laid-Open No. 63-167180. Coarse weft group, which is arranged in a direction different from the main arrangement direction of the continuous synthetic fiber yarns referred to as the continuous synthetic fiber yarns, in other words, by binding loosely to each other with binding yarns, a coarse knitted fabric having an extremely low weft density. Yarn in which coarse knitting yarn groups, or woven knitting the binding yarn body is for use as a direct strand crude knitting yarn group or bundling yarn body.

【００１８】この結束糸条体を事前に編成、織成技術に
よって形成しておくことにより、本数の多い経糸の取り
扱いが非常に簡便になり従来の技術では不可欠であった
整経ビーム等を利用した経糸の引き揃えといった作業は
全く必要がなくなったのである。即ち、本発明はエンド
レススリングの製造時におけるストランドの取り扱い性
を高めるという課題が、芯部及びストランド製造時にお
ける経糸の取り扱い性を高める事により可能となったも
のである。By forming the binding yarns in advance by knitting and weaving techniques, handling of a large number of warp yarns becomes very simple, and a warping beam or the like which is indispensable in the conventional technique is used. This eliminates the need for such operations as the alignment of warps. That is, the object of the present invention is to improve the handleability of the strand during the production of the endless sling by increasing the handleability of the warp during the production of the core and the strand.

【００１９】更に、本発明に於ける好ましい具体例とし
ては、従来の方法に於ける様に、緯糸つまり結束糸をシ
ャトル織機を使用するものではなく、ニードル編織機を
使用して製造するものである。つまり、本発明に於ける
上記具体例に於いては、当該ストランドに打ち込まれる
横方向の糸は、単に当該ストランドの両端を往復するの
ではなく、図７に示す様に、当該ストランドの一端に於
てステッチ状のループを形成するものである。Further, as a preferred embodiment of the present invention, as in the conventional method, the weft yarn, that is, the binding yarn, is manufactured not by using the shuttle loom, but by using the needle knitting machine. is there. That is, in the above specific example of the present invention, the horizontal yarn driven into the strand does not simply reciprocate at both ends of the strand, but as shown in FIG. This forms a stitch-like loop.

【００２０】係る構造とニードル編織機そのものの機構
的な相違によって、従来のシャトル織機によるストラン
ドの製造に比べて、遙に高速でストランドを製造する事
が可能となる。即ち、本発明に於いては当該エンドレス
スリングの製造時に於けるストランドの取扱性を高め、
且つ製造効率を低下させないと言う課題を編物或いは織
物製造時に於て製造効率を損ねずに経糸の取扱性を高め
ると言う共通の要求として捉え、エンドレススリングの
ストランドを粗織糸群で構成するものである。Due to such a structure and the mechanical difference between the needle loom itself, it is possible to manufacture the strand at a much higher speed than that of the conventional shuttle loom. That is, in the present invention, the handleability of the strand during the production of the endless sling is improved,
In addition, the problem that the production efficiency is not reduced is regarded as a common requirement that the handling efficiency of the warp is improved without impairing the production efficiency at the time of producing a knitted or woven fabric, and the endless sling strand is constituted by a group of coarse woven yarns. is there.

【００２１】本発明においてストランドを構成する結束
糸条体の構成や本来の使用方法は前述の公知例に開示さ
れているため省略するが、比較的簡便な設備で多数の原
糸を束ねた結束糸条体を高速で製造することができる。
また、製造した結束糸条体をその仕様毎に予め容器に保
管することにより、製造するエンドレススリングの仕様
に合わせたストランドの選択幅も広がり、それに伴うス
トランドの交換も手早く実施することが可能である。In the present invention, the structure of the binding yarns constituting the strands and the original method of use are disclosed in the above-mentioned known examples, so they will be omitted, but the binding of a number of raw yarns with relatively simple equipment is omitted. The thread can be manufactured at high speed.
In addition, by storing the manufactured binding yarns in a container in advance for each specification, the selection range of the strands according to the specifications of the endless sling to be manufactured is expanded, and the accompanying strand exchange can be carried out quickly. is there.

【００２２】よって、本発明は従来技術を使用したエン
ドレススリングの製造に比較して、ストランドの準備，
接続，装置への装填といった取り扱い性は飛躍的に向上
した。また、本発明の構成を採用すれば、粗編織糸群或
いは結束糸条体の製造は従来よりある細幅編織物用織機
或いは編機を利用した製造装置で製造することができ、
さらにエンドレススリングの製造装置にストランドを供
給するための付属装置として必要となるのは結束糸条体
を収容した容器の設置のみであり、従来の技術において
必要とされた糸を設置するためのクリールスタンドや、
糸の合撚等を目的とした付属装置は一切必要とせず、製
造装置面においても大幅な合理化が実現した。Thus, the present invention provides a method for preparing strands,
Handling properties such as connection and loading into equipment have been dramatically improved. In addition, if the configuration of the present invention is adopted, the production of a group of coarse knitting yarns or binding yarns can be performed using a conventional manufacturing apparatus utilizing a conventional narrow-width knitting or weaving machine,
Further, only an installation of a container accommodating a bundled filament is required as an auxiliary device for supplying a strand to an endless sling manufacturing apparatus, and a creel for installing a yarn required in the conventional technology is required. Stands,
There is no need for any additional equipment for twisting yarns, etc., and the production equipment has been greatly streamlined.

【００２３】また、本発明の技術によれば製造時のスト
ランドの周長、テンションを従来技術に比べて均一に管
理できるため、後述の実施例においても明らかなように
従来技術で製造したエンドレススリングに比較して強力
寄与率の高い、性能の優れた製品を製造可能となった。Further, according to the technique of the present invention, the circumference and the tension of the strand at the time of manufacture can be managed more uniformly than in the prior art, so that the endless sling manufactured by the prior art can be clearly understood from the embodiments described later. As a result, it is possible to manufacture a product having a high contribution ratio and excellent performance.

【００２４】[0024]

【実施例】以下に、本発明に係るエンドレススリングの
一具体例の構成を図面を参照しながら詳細に説明する。
即ち、図１は、本発明に係るエンドレススリング１の一
具体例の構成を示す斜視図であり、図中、複数本の高強
力合成繊維の撚糸または無撚糸２０で構成されたストラ
ンド２１を複数回巻き上げることにより綛状のリングを
形成した芯部２２を、袋状の保護材２３に納めることに
より形成されるエンドレススリング１であって、当該芯
部２２を構成する当該ストランド２１が緯糸打込密度を
１００ｍｍ当たり１以上１０以下の粗く製編織された粗
編織糸群２４により構成されているエンドレススリング
１が示されている。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective view of an endless sling according to the present invention.
That is, FIG. 1 is a perspective view showing a configuration of one specific example of the endless sling 1 according to the present invention. In the drawing, a plurality of strands 21 composed of a plurality of twisted or non-twisted yarns 20 of high-strength synthetic fibers are used. An endless sling 1 formed by placing a core 22 formed into a skein-shaped ring by winding it up into a bag-shaped protective material 23, wherein the strands 21 constituting the core 22 are driven by weft driving. An endless sling 1 composed of a coarsely woven coarsely woven yarn group 24 having a density of 1 to 10 per 100 mm is shown.

【００２５】又、図１から明らかな様に、本発明に係る
当該芯部２２を構成する当該ストランド２１のそれぞれ
は、当該ストランド２１を構成する当該複数本の連続状
合成繊維糸２０が、当該連続状合成繊維糸２０の主たる
配列方向とは異な方向に配列されている粗編織緯糸２４
が、当該ストランド２１を互いに緩く結束する結束糸条
体として機能している。As is apparent from FIG. 1, each of the strands 21 constituting the core portion 22 according to the present invention is formed by the plurality of continuous synthetic fiber yarns 20 constituting the strand 21. Coarse woven weft yarns 24 arranged in a direction different from the main arrangement direction of continuous synthetic fiber yarns 20
Function as a binding thread that loosely binds the strands 21 to each other.

【００２６】又、本発明に於ける当該粗編織糸群である
結束糸条２４は、例えば、図７に示す様な、ニードル式
織機或いは編機を使用して緯入れされた、当該ストラン
ドの一端に於てステッチ状のループを形成するものであ
る事が好ましい。当該芯部２２を構成するストランド２
１に於ける該複数本の連続状合成繊維糸２０のそれぞれ
は、撚糸または無撚糸である事が望ましい。The binding yarn 24 as the group of coarse knitting yarns according to the present invention is, for example, one end of the strand inserted into a weft using a needle type loom or a knitting machine as shown in FIG. It is preferable to form a stitch-like loop in the above. Strand 2 constituting core part 22
Each of the plurality of continuous synthetic fiber yarns 20 in 1 is preferably a twisted or non-twisted yarn.

【００２７】又、本発明に於ける当該芯部２２を構成す
るストランド２１の該複数本の連続状合成繊維糸２０
は、当該粗織緯糸換言するならば結束糸条体２４により
所定の間隔で、緩い状態で結束されているものである。
本発明に於ける一具体例に於いては、当該粗編織緯糸２
４は、当該複数本の連続状合成繊維糸群２０に対して編
織物の緯糸として機能するものであり、従って当該スト
ランド２１は、粗織糸２４によって所定の結束糸条体を
形成しているものである。In the present invention, the plurality of continuous synthetic fiber yarns 20 of the strands 21 constituting the core portion 22 are provided.
Are loosely bound at predetermined intervals by the binding yarns 24 in other words.
In one specific example of the present invention, the coarse knitted weft 2
4 functions as a weft of a knitted woven fabric with respect to the plurality of continuous synthetic fiber yarn groups 20. Therefore, the strand 21 forms a predetermined binding yarn by the coarse woven yarn 24. It is.

【００２８】本発明に於ける当該ストランド２１に於け
る当該粗編織緯糸である当該結束糸条体２４は、当該複
数本の連続状合成繊維糸群２０に対して、例えば、１０
０ｍｍ当たり１以上１０以下の緯糸打ち込み密度で配置
されている事が望ましい。つまり、本発明に於いては、
当該ストランド２１を構成する当該複数本の連続状合成
繊維糸２０と当該粗編織緯糸である結束糸条体２４と
は、比較的緯糸密度の低い、又は粗い編物或いは織物状
構造を呈するものである事が望ましいが、本発明は係る
構成に限定されるものではなく、当該結束糸条体２４
が、単に当該複数本の連続状合成繊維糸群２０を緩くそ
の外周に巻きついている状態のものであっても良い。The binding yarn 24, which is the coarse knitting weft in the strand 21 of the present invention, is, for example, 10 times smaller than the plurality of continuous synthetic fiber yarn groups 20.
It is desirable that the yarns are arranged at a weft driving density of 1 to 10 per 0 mm. That is, in the present invention,
The plurality of continuous synthetic fiber yarns 20 constituting the strand 21 and the binding yarns 24 that are the coarse knitting wefts have a relatively low weft density or exhibit a coarse knitted or woven structure. It is desirable that the present invention is not limited to such a configuration.
However, the plurality of continuous synthetic fiber yarn groups 20 may be simply loosely wound around the outer periphery thereof.

【００２９】つまり、図６及び図７に示す様に、本発明
に係るエンドレスリングを構成する個々のストランド２
１の構成は、例えば、複数本の連続状合成繊維糸２０か
らなる撚糸または無撚糸で構成されたストランドが複数
本互いに並列状態に配列され、且つ無端状のリングを形
成すると共に、当該ストランド２１のそれぞれは、当該
ストランド２１を構成する当該複数本の連続状合成繊維
糸２０が、当該連続状合成繊維糸の主たる配列方向とは
異なる方向に配列されている結束糸条体２４により、互
いに緩く結束されているものである。That is, as shown in FIGS. 6 and 7, the individual strands 2 constituting the endless ring according to the present invention are formed.
The first configuration is, for example, that a plurality of strands composed of a plurality of continuous synthetic fiber yarns 20 made of twisted or non-twisted yarns are arranged in parallel with each other, form an endless ring, and Are loosened mutually by the binding yarns 24 in which the plurality of continuous synthetic fiber yarns 20 constituting the strand 21 are arranged in a direction different from the main arrangement direction of the continuous synthetic fiber yarns. They are united.

【００３０】より具体的には、図６に於いては、当該複
数本の連続状合成繊維糸２０が、緯糸２４によって粗く
製織された状態で互いに緩く結束されているものであ
り、従って当該緯糸２４は、当該連続状合成繊維糸の主
たる配列方向、つまり図に於ける縦方向に対して所定の
角度（９０度を含む）を持って交差している。係る角度
は、当該緯糸２４の打ち込み密度によって任意に変更可
能である。More specifically, in FIG. 6, the plurality of continuous synthetic fiber yarns 20 are loosely bound to each other in a state where they are coarsely woven by the weft yarns 24. Numeral 24 intersects at a predetermined angle (including 90 degrees) with respect to the main arrangement direction of the continuous synthetic fiber yarns, that is, the longitudinal direction in the figure. Such an angle can be arbitrarily changed according to the driving density of the weft yarn 24.

【００３１】又、図７に於いては、当該複数本の連続状
合成繊維糸２０が、ループ状に互いに結合された緯糸２
４によって粗く製織された状態で互いに緩く結束されて
いるものであり、従って当該緯糸２４は、当該連続状合
成繊維糸の主たる配列方向、つまり図に於ける縦方向に
対して所定の角度（９０度を含む）を持って交差してい
る。In FIG. 7, a plurality of continuous synthetic fiber yarns 20 are connected to each other in a weft 2
4 and loosely bound to each other in a coarsely woven state. Therefore, the weft yarns 24 are arranged at a predetermined angle (90 degrees) to the main arrangement direction of the continuous synthetic fiber yarns, that is, the longitudinal direction in the figure. (Including degrees).

【００３２】係る角度も、当該緯糸２４の打ち込み密度
によって任意に変更可能である。要は、エンドレススリ
ングを製造する工程に於て、当該ストランド２１の製造
工程からその供給工程、更には芯部の形成工程及び保護
材２３の被覆工程の一連の工程を通して、当該複数本の
連続状合成繊維糸２０の配列が極度の乱れない様に維持
する事が可能で且つ当該ストランドがソフトに維持され
る様な構成であれば特に限定されるものではない。The angle can be arbitrarily changed according to the density of the weft yarn 24. In short, in the process of manufacturing the endless sling, the continuous process of the plurality of strands 21 is performed through a series of processes from a process of manufacturing the strand 21 to a process of supplying the strand 21, a process of forming the core portion, and a process of coating the protective material 23. There is no particular limitation as long as the arrangement of the synthetic fiber yarns 20 can be maintained so as not to be extremely disturbed, and the strands are softly maintained.

【００３３】該袋状の保護材２３は袋状に製編織された
編物或いは織物により構成されていても良く、又袋状に
形成された合成樹脂等のチューブにより構成されていて
も良い。更には、当該袋状の保護材は予め袋状に縫製さ
れた編織物あるいは袋状に逢着されたシートにより構成
されているもので有っても良く、又、該袋状の保護材が
袋状に形成された組紐により構成されているもので有っ
ても良い。The bag-shaped protective member 23 may be made of a knitted or woven fabric knitted or woven in a bag shape, or may be made of a tube made of a synthetic resin or the like formed in a bag shape. Further, the bag-shaped protective material may be formed of a knitted fabric sewn in a bag shape in advance or a sheet adhered in a bag shape. It may be constituted by a braid formed in a shape.

【００３４】本発明に於いては、当該エンドレススリン
グ１の芯部２２は、前記した様な公知技術によって、当
該粗編織緯糸群２４により結束せしめられた連続状合成
繊維糸群２０を直接若しくは適宜の収納手段に一旦収納
した後、図５に示す様な、基本的には、図４に示される
エンドレススリング製造装置と略同様の構成を有するエ
ンドレススリング製造装置３０に供給される。In the present invention, the core portion 22 of the endless sling 1 is directly or appropriately connected to the continuous synthetic fiber yarn group 20 tied by the coarse knitting weft group 24 by the known technique as described above. After once stored in the storage means, it is supplied to an endless sling manufacturing apparatus 30 having substantially the same configuration as the endless sling manufacturing apparatus shown in FIG. 4, basically as shown in FIG.

【００３５】即ち、当該ストランド２１が、ストランド
供給手段３１から一対のローラ１２、１３の一方のロー
ラ１２に供給され、その後当該ストランド２１が、一対
のローラ１２、１３の双方に複数回ループ状に巻き上げ
られる。その間、当該ストランド２１は、当該一対のロ
ーラ１２、１３間に設けられている一部に切り欠け部が
形成された中空管３２の中を通過する事になる。That is, the strand 21 is supplied from the strand supply means 31 to one roller 12 of the pair of rollers 12, 13, and then the strand 21 is looped around the pair of rollers 12, 13 a plurality of times. Can be wound up. During that time, the strand 21 passes through a hollow tube 32 provided with a cutout in a part provided between the pair of rollers 12 and 13.

【００３６】当該中空管３２の外周部には、予め形成さ
れた袋状の保護材２３が、収縮状態で搭載されている。
当該ストランド２１が当該一対のローラ１２、１３間で
所定の回数の巻き回しが完了した後、図３に示す様に、
当該ストランド２１の両端部２７を当該ループ状に巻き
上げられた本体部の一部に適宜の固定手段を使用して固
着させる事によって、芯部２２の形成が完了する。On the outer peripheral portion of the hollow tube 32, a bag-shaped protective material 23 formed in advance is mounted in a contracted state.
After the strand 21 has been wound a predetermined number of times between the pair of rollers 12 and 13, as shown in FIG.
By fixing both ends 27 of the strand 21 to a part of the main body part wound up in a loop shape using an appropriate fixing means, the formation of the core part 22 is completed.

【００３７】その後当該芯部２２を当該一対のローラ１
２、１３間から取外し、既に嵌合されている当該保護材
２３を延展して、当該芯部２２全体を当該保護材２３で
被覆するように処理が行われる。つまり、本発明に係る
エンドレススリングの製造方法としては、例えば、複数
本の連続状合成繊維糸を当該連続状合成繊維糸の主たる
配列方向とは異なる方向に配列されている粗織緯糸換言
すれば本発明で言う結束糸条体２４により、互いに緩く
結束させたストランドを形成した後、当該ストランドを
一対のローラー間に複数回巻き回して、当該ストランド
が複数本並列状に配列された芯部を形成し、次いで当該
芯部を袋状の保護材で被覆収納する様に構成されたエン
ドレススリングの製造方法である。Thereafter, the core 22 is connected to the pair of rollers 1.
The processing is performed such that the protection member 23 which has been removed from between the points 2 and 13 is extended, and the entire core 22 is covered with the protection member 23. In other words, the method for producing an endless sling according to the present invention includes, for example, a coarse weft in which a plurality of continuous synthetic fiber yarns are arranged in a direction different from the main arrangement direction of the continuous synthetic fiber yarns. After forming the strand loosely bound to each other by the binding thread 24 referred to in the present invention, the strand is wound a plurality of times between a pair of rollers to form a core in which a plurality of the strands are arranged in parallel. This is a method for producing an endless sling configured to form and then cover the core with a bag-shaped protective material.

【００３８】本発明に係る当該エンドレススリング１の
外観は、例えば、図２（Ａ）に示す様に、全体が当該保
護材２３で被覆されたループ状の形状を有しているもの
であっても良く、又図２（Ｂ）に示す様に、一旦図２
（Ａ）に示す様な形状のループを製造した後、当該本体
部の中央部分を適宜の固定部材２５で収束し、その両端
部にループ状の耳部２６を形成したもので有ってもよ
い。The external appearance of the endless sling 1 according to the present invention is, for example, as shown in FIG. As shown in FIG. 2 (B),
After a loop having a shape as shown in FIG. 1A is manufactured, the central portion of the main body is converged by an appropriate fixing member 25, and loop-shaped ears 26 are formed at both ends. Good.

【００３９】以下に本発明に係るエンドレススリングの
具体例の詳細を以下に説明する。本発明は、エンドレス
スリングを構成するストランドに粗織緯糸或いは結束糸
条体を使用することを前提として、粗織緯糸或いは結束
糸条体の仕様がエンドレススリングの性能に及ぼす影響
を検討した。この結果、以下に示すように粗織緯糸或い
は結束糸条体を構成する糸の本数及び緯糸の打込密度が
大きな要素であるとの知見を得たものである。The details of a specific example of the endless sling according to the present invention will be described below. The present invention examined the effect of the specifications of the coarse weft or the binding yarn on the performance of the endless sling on the premise that the coarse weft or the binding yarn is used for the strands constituting the endless sling. As a result, it has been found that the number of yarns constituting the coarse woven weft or the binding yarn and the driving density of the weft are large factors as described below.

【００４０】つまり、同等の強度のエンドレススリング
を得るための製造時の効率から考えた場合、粗織緯糸或
いは結束糸条体を構成する糸の本数を多くした方が、ス
トランドの周回数が減少するため構成本数をより多くし
た方が有利と考えられる。但し、単純に構成本数を多く
した場合、粗織緯糸或いは結束糸条体そのものの体積が
大きくなり取り扱い性が低下することや、製造時にスト
ランドにかかる条件を管理することが難しくなるといっ
た弊害も予測される。In other words, from the point of view of efficiency at the time of manufacturing to obtain an endless sling having the same strength, the larger the number of yarns constituting the coarse woven weft or the binding yarn, the smaller the number of turns of the strand. Therefore, it is considered advantageous to increase the number of components. However, if the number of components is simply increased, the adverse effects such as an increase in the volume of the coarse weft or the binding yarn itself and a decrease in handleability, and difficulty in managing the conditions of the strand during production are also predicted. Is done.

【００４１】この点を把握するために、粗編織緯糸或い
は結束糸条体を構成する原糸として高強度ポリエステル
繊維１２６０デニール１０８フィラメントの糸を使用
し、構成本数と製造時の周回数をそれぞれ変更して製造
したエンドレススリングの強度を測定した。その結果を
表１に示すが、係る結果から、周回数が同等の場合に
は、当該粗編織緯糸或いは結束糸条体を構成する原糸本
数を２０本とした方が６０本としたものに比べ、優れた
強力寄与率を示す傾向にある。In order to grasp this point, high-strength polyester fiber 1260 denier 108 filament yarn was used as the raw yarn constituting the coarse knitting weft or the binding yarn, and the number of components and the number of turns during production were changed respectively. The strength of the endless sling manufactured as described above was measured. The results are shown in Table 1. From the results, when the number of turns is equal, the number of raw yarns constituting the coarse knitted woven weft or the binding yarn is set to 20 and the number of the original yarns is set to 60. In comparison, they tend to show excellent strength contribution rates.

【００４２】また、測定時の強力のばらつきも前者の方
が少ないため、エンドレススリングの物性の均一性にお
いても構成本数を少なくした方が好ましいという考察さ
れる。これは、構成本数が多くなることにより、エンド
レススリングの製造時においてストランドにかかる外的
変化（例えばテンションの変動といった）に影響される
原糸の本数が相対的に多くなり、結果的に強力寄与率の
低下やばらつきの増大といった傾向の原因となると推察
できる。Also, since the variation in the strength at the time of measurement is smaller in the former case, it is considered that it is preferable to reduce the number of components in the uniformity of the physical properties of the endless sling. This is because, as the number of constituent yarns increases, the number of yarns affected by external changes (for example, fluctuations in tension) applied to the strands during the production of the endless sling relatively increases, and as a result, a strong contribution is made. It can be inferred that it causes a tendency such as a decrease in rate or an increase in variation.

【００４３】また、緯糸の打込密度が変化すると、粗編
織緯糸或いは結束糸条体を構成する原糸が互いに拘束さ
れる程度が変化するため、エンドレススリングの物性に
影響を及ぼすことが予測される。この点を確認するた
め、次に前述の試験と同様に高強度ポリエステル繊維１
２６０デニール１０８フィラメントの糸を２０本使用
し、緯糸打込密度を０．５８ｐｉｃ／３０ｍｍ及び３．
００ｐｉｃ／３０ｍｍの２種類で製編織した粗編織緯糸
或いは結束糸条体をストランドとして使用し、ストラン
ドの周回数を変えて製造したエンドレススリングの強度
を測定した。Also, when the driving density of the weft changes, the degree to which the raw yarns constituting the coarsely woven weft or the binding yarns are bound to each other changes, which is expected to affect the physical properties of the endless sling. You. In order to confirm this point, the high strength polyester fiber 1
Using 20 yarns of 260 denier and 108 filaments, the weft driving density was 0.58 pic / 30 mm and 3.
The strength of an endless sling manufactured by changing the number of rounds of the strand was measured using a coarsely woven weft or a binding yarn that was knitted and woven at 00 pic / 30 mm.

【００４４】表２に示す結果から、緯糸打込密度０．５
８ｐｉｃ／３０ｍｍの粗織緯糸或いは結束糸条体をスト
ランドに使用したエンドレススリングの方が、３．００
ｐｉｃ／３０ｍｍの粗編織緯糸或いは結束糸条体を使用
したものに比べ周回数に関わらず全般に高い強度を示す
傾向にある。また、強度のばらつきも前者の方が小さい
ため、粗編織緯糸或いは結束糸条体の緯糸の打込密度が
小さい方がエンドレススリングの性能面から有利である
と判断できる。From the results shown in Table 2, weft driving density of 0.5
An endless sling using a 8 pic / 30 mm coarse weft or a binding yarn as a strand is 3.00.
pic / 30 mm tend to exhibit higher strength as a whole, irrespective of the number of turns, as compared with those using a coarse knitting weft or a binding yarn. In addition, since the variation in strength is smaller in the former, it can be determined that a smaller driving density of the coarse knitting weft or the weft of the binding yarn is advantageous from the viewpoint of endless sling performance.

【００４５】これは、緯糸打込密度を大きくすると、粗
編織緯糸或いは結束糸条体を構成する原糸がお互いの動
きを拘束することになるため、ストランドにかかる外的
変化に対する影響が大きくなり、結果的に強力寄与率の
低下やばらつきの増大といった傾向の原因となると推察
できる。以上の検討から、ストランドを構成する粗編織
緯糸或いは結束糸条体の仕様のみから考えた場合、粗編
織緯糸或いは結束糸条体の原糸本数を少なく、緯糸打込
密度を低く抑えた方が有利であると考えられる。This is because if the weft driving density is increased, the raw yarns constituting the coarse knitting weft or the binding yarn restrict the movement of each other, so that the influence on the external change applied to the strand increases. As a result, it can be inferred that this causes a tendency such as a decrease in the strong contribution ratio or an increase in variation. From the above examination, when considering only the specifications of the coarse knitting weft or the binding yarns constituting the strands, it is better to reduce the number of raw yarns of the coarse knitting wefts or the binding yarns and keep the weft driving density low. Considered to be advantageous.

【００４６】一方、エンドレススリングの製造時の条件
としては、ストランドを複数回巻き付ける場合の各周の
周長のばらつきが抑えることがエンドレススリングの性
能を確保する上で重要な要素となる。この点を確認する
ため、前述の試験と同様に高強度ポリエステル繊維１２
６０デニール１０８フィラメントの糸を使用し、ストラ
ンドを複数回巻き付けてエンドレススリングを製造した
場合の各周のリング長のばらつきとエンドレススリング
の強度を、粗編織緯糸或いは結束糸条体の原糸構成本数
とストランドの周回数及び設定リング長を変えて測定し
た。On the other hand, as a condition at the time of manufacturing the endless sling, it is an important factor in securing the performance of the endless sling that the variation in the circumferential length of each circumference when the strand is wound plural times is suppressed. In order to confirm this point, the high-strength polyester fiber 12
When the endless sling is manufactured by winding a strand a plurality of times using a yarn of 60 denier and 108 filaments, the variation of the ring length of each circumference and the strength of the endless sling are determined by the number of raw yarns constituting a coarse knitting weft or a binding yarn. And the number of turns of the strand and the set ring length were changed.

【００４７】表３に示す結果から、リング長のばらつき
と周回数の関係を見ると、周回数が少ない方がリング長
のばらつきが小さくなっている。これは周回数が多くな
るほど、各周のストランドが互いに空間的に干渉するこ
とによる影響が大きくなることや、周回数を多くするほ
ど製造装置上のリングを縮めようとする方向に働く応力
が大きくなることなどが原因と考えられる。From the results shown in Table 3, looking at the relationship between the variation of the ring length and the number of rotations, the smaller the number of rotations, the smaller the variation of the ring length. This is because as the number of turns increases, the influence of the spatial interference of the strands of each circumference increases, and as the number of turns increases, the stress acting in the direction to shrink the ring on the manufacturing equipment increases. Is considered to be the cause.

【００４８】また、同程度の周回数で比較した場合は、
粗編織緯糸或いは結束糸条体の原糸構成本数が少ない方
がリング長のばらつきは小さくなる。これは本数が多い
方が粗編織緯糸或いは結束糸条体の体積が大きくなるた
め、前述の周回数を多くした時と同様な原因によるもの
と考える。このように、エンドレススリングの仕様面か
ら見るとストランドの周回数が小さい方がリング長のば
らつきは小さくなるが、本願発明者はこれまで述べた一
連の実験における経験から、製造装置側の要件としてス
トランドの巻き付け時において、ストランドにかかるテ
ンションの変動を極力抑えることがリング長のばらつき
を抑えることに効果があることを見いだした。Also, when compared at the same number of laps,
The smaller the number of raw yarns constituting the coarse knitting weft or the binding yarn, the smaller the variation in ring length. This is considered to be due to the same reason as that when the number of turns described above was increased, because the larger the number, the larger the volume of the coarsely woven weft or the binding yarn. Thus, from the point of view of the specification of the endless sling, the smaller the number of turns of the strand, the smaller the variation of the ring length. It has been found that suppressing the fluctuation of the tension applied to the strand as much as possible during the winding of the strand is effective in suppressing the variation in the ring length.

【００４９】そこで我々は市販のプーリ型の製造装置の
ストランドの引き込み側にテンションの変動を吸収する
ためのテンション機構３３を設け、リング長のばらつき
を抑えるための工夫を施した。一方、リング長のばらつ
きと強力寄与率の関係を見ると、全体としてはリング長
のばらつきが小さくなるほど強力寄与率が大きくなる傾
向が見られる。但し、表３の（１）と（２）でこの関係
が逆転しているが、これはリング長のばらつきという要
素による強力寄与率への支配が８０％の前後の値までし
か及ばないということが予測される。Therefore, we have provided a tension mechanism 33 for absorbing fluctuations in tension on the pull-in side of the strand of a commercially available pulley-type manufacturing apparatus, and have devised to suppress variations in ring length. On the other hand, when looking at the relationship between the variation in the ring length and the strong contribution ratio, the tendency that the strong contribution ratio increases as the variation in the ring length decreases as a whole is seen. However, this relationship is reversed in Tables (1) and (2), which means that the influence on the strong contribution rate due to the ring length variation extends only to values around 80%. Is predicted.

【００５０】即ち、この実験の条件においては表３の
（２）のデータにおけるリング長のばらつきσ＝１．７
２以下にばらつきを抑えても強力寄与率は上がらないも
のと考えられ、これ以上の強力寄与率を求める場合には
さらに細かい条件の検討が必要になると予測する。以上
の検討から、ストランドの巻き付け時にリング長のばら
つきσを１．７程度に抑えることが好ましいと判断で
き、同一の条件で巻き付けを行った場合には周回数が少
ない方がばらつきを抑える面では有利に働くといえる。That is, under the conditions of this experiment, the variation σ of the ring length in the data of (2) in Table 3 was 1.7.
Even if the variation is suppressed to 2 or less, it is considered that the strong contribution ratio does not increase, and it is predicted that more detailed examination of the conditions is necessary when obtaining a stronger contribution ratio. From the above examination, it can be determined that it is preferable to suppress the variation σ of the ring length at the time of winding the strand to about 1.7, and when the winding is performed under the same conditions, the smaller the number of rotations is, the smaller the variation is. It works well.

【００５１】但し、周回数を極端に少なくするとストラ
ンド同士で摩擦力が働きにくくなるため、エンドレスス
リングにテンションが加えられてリングを広げる方向に
力が加わった場合にリングが自己形状を保つことができ
ずにスリップしてしまうといった現象が起きる。これに
ついては、これまで述べてきた実験の中での予備的な経
験によると、周回数が２０を下回った場合は比較的この
ような現象が発生する可能性が高いと考える。However, if the number of turns is extremely reduced, the frictional force between the strands becomes difficult to work. Therefore, when tension is applied to the endless sling and a force is applied in the direction of expanding the ring, the ring may maintain its own shape. A phenomenon such as slipping without being able to occur occurs. According to preliminary experiences in the experiments described above, it is considered that such a phenomenon is relatively likely to occur when the number of turns is less than 20.

【００５２】つまり、強力寄与率を高くするためにはス
トランドの周回数を低く設定する方が好ましいが、スト
ランドがリング形状を保つための下限が存在することが
わかった。以上の検討から考えると、粗編織緯糸或いは
結束糸条体の仕様のみについて考えた場合は、緯糸の打
込密度を小さくし、構成する原糸の本数を減らした方が
好ましいが、同等の強度を有するエンドレススリングの
製造するための条件を考えた場合、原糸の構成本数を減
らすことはこの粗編織緯糸或いは結束糸条体を使用した
ストランドの周回数を増加させることにつながり、結果
的に強力寄与率を低下させることになる。That is, in order to increase the strength contribution ratio, it is preferable to set the number of turns of the strand to be low, but it has been found that there is a lower limit for maintaining the ring shape of the strand. Considering the above considerations, when considering only the specifications of the coarse knitting weft or the binding yarn, it is preferable to reduce the driving density of the weft and reduce the number of constituent yarns, but the same strength Considering the conditions for producing an endless sling having the following, reducing the number of constituent yarns leads to an increase in the number of turns of the strand using the coarse knitting weft or the binding yarn, and consequently It will reduce the strong contribution.

【００５３】よって、粗編織緯糸或いは結束糸条体を構
成する原糸本数、ストランドの周回数、強力寄与率は相
関関係を持っており、エンドレススリングの目標とする
強度によって設計上の検討が必要な内容である。Therefore, the number of raw yarns, the number of turns of the strands, and the strong contribution ratio of the coarsely woven weft or the binding yarn have a correlation, and a design study is required depending on the target strength of the endless sling. Content.

【００５４】[0054]

【発明の効果】以上に述べたような知見を考慮して、表
４に示すように従来技術により既に商品化されているエ
ンドレススリングの強度を目標として具体的な仕様を設
定した製品を本発明の技術により製造し、既存製品との
比較を行った。本発明による製品はこれまで述べた実験
と同様に高強度ポリエステル繊維１２６０デニール１０
８フィラメントの糸を30本で構成した粗編織緯糸或いは
結束糸条体を使用している。In consideration of the above-described knowledge, the present invention is directed to a product which has already been commercialized according to the prior art and has specific specifications set with the aim of the strength of the endless sling as shown in Table 4 according to the present invention. It was manufactured using the technology described above and compared with existing products. The product according to the present invention has a high strength polyester fiber of 1260 denier 10
A coarsely woven weft or a bundled yarn composed of 30 8-filament yarns is used.

【００５５】表４の強力寄与率は使用されている原糸の
デニールあたりの強度を９．０ｇ／デニールで計算した
が、これを見ると全ての設定において本発明による製品
の方が既存商品より優れた強力寄与率を示している。ま
た、両者ともに設定強度が大きくなるに従って強力寄与
率も低下する傾向にあるものの、両者の差そのものは拡
大する傾向にあり、強度の大きな製品の方が本発明によ
る優位性が発揮されやすいことが明らかになった。The strength contribution ratio in Table 4 was calculated by calculating the strength per denier of the used yarn at 9.0 g / denier. It can be seen from the table that the product according to the present invention was more effective than the existing product in all settings. It shows an excellent strength contribution. In addition, although the strength contribution ratio tends to decrease as the set strength increases, the difference between the two tends to increase, and a product having a higher strength tends to exert superiority according to the present invention. It was revealed.

【００５６】[0056]

【表１】 [Table 1]

【００５７】[0057]

【表２】 [Table 2]

【００５８】[0058]

【表３】 [Table 3]

【００５９】[0059]

【表４】 [Table 4]

【図面の簡単な説明】[Brief description of the drawings]

【図１】図１は、本発明に係るエンドレススリングの構
成の要部を示す斜視図である。FIG. 1 is a perspective view showing a main part of a configuration of an endless sling according to the present invention.

【図２】図２（Ａ）及び図２（Ｂ）は、本発明に係るエ
ンドレススリングの形態の一例を示す図である。FIGS. 2A and 2B are diagrams showing an example of an endless sling according to the present invention. FIG.

【図３】図３は、本発明にエンドレススリングで使用さ
れる芯部の形態を示す図である。FIG. 3 is a view showing a form of a core used in an endless sling according to the present invention.

【図４】図４は、従来に於けるエンドレススリングの製
造装置の例を示す図である。FIG. 4 is a diagram showing an example of a conventional endless sling manufacturing apparatus.

【図５】図５は、本発明に係るエンドレススリングの製
造装置の例を示す図である。FIG. 5 is a diagram showing an example of an endless sling manufacturing apparatus according to the present invention.

【図６】図６は、従来に於ける粗編織緯糸の緯打ち込に
形態の一例を示す図である。FIG. 6 is a view showing an example of a conventional mode of weft driving of a coarse knitting weft yarn.

【図７】図７は、本発明に於ける粗編織緯糸の緯打ち込
に形態の一例を示す図である。FIG. 7 is a view showing an example of a mode of weft driving of a coarse knitting weft in the present invention.

【符号の説明】[Explanation of symbols]

１…エンドレススリング ６…ボビン ７…糸 ８…ストランド １１…支持体 １２、１３…ローラ ２０…エンドレススリング ２１…ストランド ２２…芯部 ２３…保護材 ２４…粗織緯糸或いは結束糸条体 ２５…固定部材 ２６…耳部 ３０…エンドレススリング製造装置 ３１…供給手段 ３２…中空管 ３３…テンション機構 DESCRIPTION OF SYMBOLS 1 ... Endless sling 6 ... Bobbin 7 ... Yarn 8 ... Strand 11 ... Support body 12, 13 ... Roller 20 ... Endless sling 21 ... Strand 22 ... Core part 23 ... Protective material 24 ... Coarse weft or binding thread 25 ... Fixed Member 26: Ear part 30: Endless sling manufacturing apparatus 31: Supply means 32: Hollow tube 33: Tension mechanism

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 複数本の高強力合成繊維の撚糸または無
撚糸で構成されたストランドを複数回巻き上げることに
より綛状のリングを形成した芯部を、袋状の保護材に納
めることにより形成されるエンドレススリングであっ
て、当該芯部を構成する当該ストランドが緯糸打込密度
を１００ｍｍ当たり１以上１０以下の粗く製編織された
粗編織糸群により構成されている事を特徴とするエンド
レススリング。1. A core formed by winding a plurality of twisted or non-twisted strands of high-strength synthetic fiber a plurality of times into a skein-shaped ring, and placing the core in a bag-shaped protective material. An endless sling, wherein the strands constituting the core portion are constituted by a group of coarsely woven coarsely woven yarns having a weft driving density of 1 to 10 per 100 mm. 【請求項２】 当該袋状の保護材が袋状に製編織された
編物或いは織物により構成されている事を特徴とする請
求項１記載のエンドレススリング。2. The endless sling according to claim 1, wherein the bag-shaped protective material is made of a knitted or woven fabric woven in a bag shape. 【請求項３】 当該袋状の保護材が袋状に形成された合
成樹脂等のチューブにより構成されている事を特徴とす
る請求項１記載のエンドレススリング。3. The endless sling according to claim 1, wherein the bag-shaped protective material is formed of a tube made of a synthetic resin or the like formed in a bag shape. 【請求項４】 当該袋状の保護材が袋状に縫製された編
織物あるいは袋状に逢着されたシートにより構成されて
いる事を特徴とする請求項１記載のエンドレススリン
グ。4. The endless sling according to claim 1, wherein the bag-shaped protective material is constituted by a knitted fabric sewn in a bag shape or a sheet adhered in a bag shape. 【請求項５】 当該袋状の保護材が袋状に形成された組
紐により構成されている事を特徴とする請求項１記載の
エンドレススリング。5. The endless sling according to claim 1, wherein the bag-shaped protective material is constituted by a braid formed in a bag shape. 【請求項６】 複数本の連続状合成繊維糸からなる撚糸
または無撚糸で構成されたストランドが複数本互いに並
列状態に配列され、且つ無端状のリングを形成する芯部
と、当該芯部を被覆収納する袋状の保護材とで構成され
ているエンドレススリングであって、当該芯部を構成す
る当該ストランドのそれぞれは、当該ストランドを構成
する当該複数本の連続状合成繊維糸が、当該連続状合成
繊維糸の主たる配列方向とは異なる方向に配列されてい
る結束糸条体により、互いに緩く結束されている事を特
徴とするエンドレススリング。6. A core part in which a plurality of strands composed of a continuous yarn or a non-twist yarn composed of continuous synthetic fiber yarns are arranged in parallel with each other and form an endless ring; An endless sling comprising a bag-shaped protective material for covering and storing, wherein each of the strands constituting the core is formed by the plurality of continuous synthetic fiber yarns constituting the strand. An endless sling characterized by being loosely bound to each other by binding yarns arranged in a direction different from the main arrangement direction of the synthetic fiber yarns. 【請求項７】 当該エンドレススリングの芯部は、当該
結束糸条体により結束せしめられた連続状合成繊維糸群
からなるストランドの本体部を複数回ループ状に巻き上
げて構成すると同時に、当該ストランドの両端部を当該
ループ状に巻き上げられた本体部の一部に固着させてい
る事を特徴とする請求項１又は６に記載のエンドレスス
リング。7. The core of the endless sling is formed by winding a main body of a strand composed of a group of continuous synthetic fiber yarns bound together by the binding yarns into a loop a plurality of times, and at the same time, at both ends of the strand. The endless sling according to claim 1, wherein a part is fixed to a part of the main body part wound up in a loop shape.