JP2000167272A - Cotton wadding product rich in warmth retaining property - Google Patents

Abstract

PROBLEM TO BE SOLVED: To use the object of covering cotton wadding, for which the slices of fibers plating cotton with silver (silver plating fibers) are mixed with cloth as a cotton wadding product and to enable use sanitary and improved in warmth retaining property by weaving silver plating fibers into at least one part of cloth. SOLUTION: When producing the cotton wadding product to be applied to bedding or warmth retaining clothing, the cotton wadding mixed with the slices of silver plating fibers into the cotton is covered with the cloth and the object woven with the silver plating fibers into at least one part is used as the cloth. As cotton to be used, pure cotton or synthetic fiber cotton can be used but it is preferable to use comparatively light pure cotton rich in warmth retaining property. Besides, it is preferable the silver plating fibers are contained in 2 to 20 wt.%, especially, about 5 to 15 wt.% in the cotton wadding and the average fiber length of silver plating fiber slices contained in the cotton wadding is made into 1 to 8 cm, especially, about 2 to 6 cm. Thus, the warmth retaining, antibacterial and antistatic properties of the cotton wadding product are improved.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は、銀メッキした繊維を混
入してなる詰綿製品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cotton filling product mixed with silver-plated fiber.

【０００２】[0002]

【従来の技術】寝具や保温性衣料に詰綿製品を使用する
ことは広く知られているが、通常の詰綿製品は、洗濯し
難く非衛生的である、また、十分な保温性を得るために
は重く、非常の嵩張ったものとなる等の欠点があった。BACKGROUND OF THE INVENTION The use of cotton products in bedding and warm clothing is widely known, but ordinary cotton products are difficult to wash, are unsanitary, and have sufficient heat retention. For this reason, it has a drawback that it is heavy and very bulky.

【０００３】他方、表面に銀メッキした合成繊維は、抗
菌性に優れることが知られているが、磨耗係数が高く、
合糸、引揃え、ボビン巻、コーン巻、撚糸、整経等の準
備工程が非常に困難であり、特に１５デニールや３０デ
ニールの如き、細デニールのものは、単糸切れを起こし
易く、製織性及び製編性が悪く、従って、衣料分野等に
実用性あるものとは考えられなかった。[0003] On the other hand, synthetic fibers silver-plated on the surface are known to have excellent antibacterial properties, but have a high abrasion coefficient,
It is very difficult to prepare yarn, yarn, bobbin winding, cone winding, twisting, warping, etc., and especially fine deniers such as 15 denier and 30 denier are liable to break single yarns and weave. The properties and knitting properties were poor, and therefore, it was not considered to be practical in the field of clothing.

【０００４】[0004]

【発明が解決しようとする課題】本発明は、詰綿製品と
このような銀メッキした繊維を組み合わせることによっ
て、従来になく、衛生的で、軽量にして保温性ある詰綿
製品を提供することを課題とする。SUMMARY OF THE INVENTION It is an object of the present invention to provide an unconventional, sanitary, lightweight and heat-retaining cotton product by combining the cotton product with such silver-plated fibers. As an issue.

【０００５】[0005]

【課題を解決するための手段】本発明では、詰綿製品を
綿に銀メッキした繊維（以下、銀メッキ繊維と述べる）
の裁断物を混入した詰綿を、布帛で覆ってなるものと
し、しかも該布帛の少なくと一部に銀メッキした繊維を
織り込むことにより、上記課題を解決した。SUMMARY OF THE INVENTION In the present invention, a cotton-filled product is a fiber obtained by silver-plating cotton (hereinafter referred to as a silver-plated fiber).
The above-mentioned problem has been solved by making the wadding mixed with the above-mentioned cut material covered with a cloth, and weaving silver-plated fibers into at least a part of the cloth.

【０００６】本発明において綿としては、木綿綿、合繊
綿など使用することができるが、比較的軽量にして保温
性に富む真綿を使用するのが好ましい。[0006] In the present invention, cotton cotton, synthetic cotton, and the like can be used as the cotton, but it is preferable to use relatively light weight cotton which is rich in heat retention.

【０００７】また、銀メッキ繊維は、詰綿に２〜２０重
量％、特に５〜１５重量％程度含まれるのが好ましく、
詰綿に含まれる銀メッキ繊維裁断物の平均繊維長は１〜
８cm、特に２〜６cm程度であるのがよい。The silver-plated fiber preferably contains about 2 to 20% by weight, especially about 5 to 15% by weight, of the filling.
The average fiber length of the silver-plated fiber cut material contained in the cotton wadding is 1 to
It is preferably 8 cm, especially about 2 to 6 cm.

【０００８】かかる本発明では、詰綿に、単独でも比較
的保温性に富んだ真綿等に、抗菌性や保温性に富み、通
電性をも有する銀メッキ繊維を混入して使用するため、
後の実施例に示すように、軽く、保温性、抗菌性、静電
防止性のいずれにも優れた布団やキルティング衣料等を
得ることができるのである。[0008] In the present invention, since the silver-coated fiber which is rich in antibacterial property and heat retaining property and also has electric conductivity is mixed and used in the cotton wool, silk cotton and the like which are relatively rich in heat retaining property alone.
As will be shown in the examples below, it is possible to obtain a futon or quilted garment which is light and excellent in all of heat retention, antibacterial properties and antistatic properties.

【０００９】しかも、本発明の製品は、詰綿を覆う布帛
にも銀メッキ繊維を使用するため、その効果はより著し
いものとなる。この銀メッキ繊維を使用した布帛は、製
品の少なくとも片面に存在するようにするのがよく、例
えば、その製品により覆われる被保温体に接する側、即
ち、衣料や掛布団の裏地等の布帛を、銀メッキ繊維を含
むものとすることにより、それを着用した者は、より効
果的に、保温性や抗菌性、静電防止性などの効果を得る
ことができるものとなる。[0009] In addition, since the product of the present invention uses silver-plated fibers also in the cloth covering the wadding, the effect is more remarkable. The fabric using the silver-plated fiber is preferably present on at least one side of the product, for example, the side in contact with the insulated body covered by the product, that is, the fabric such as clothing or lining of a comforter, By including the silver-plated fiber, a person wearing the fiber can more effectively obtain effects such as heat retention, antibacterial properties, and antistatic properties.

【００１０】なお、銀メッキ繊維は、布帛の面積当たり
２〜２０％、特に５〜１５％程度の範囲で織り込まれる
のよい。The silver-plated fibers are preferably woven in a range of 2 to 20%, particularly 5 to 15% per area of the fabric.

【００１１】本発明で使用する銀メッキ繊維は、合成繊
維に銀メッキしたものを使用するのが好ましく、詰綿に
含まれるものは、その混綿性等の点から、１００デニー
ル以下、特に３０デニール前後であるのが効果的である
が、布帛に使用される銀メッキ繊維の太さは、それ以上
であってもよい。The silver-plated fiber used in the present invention is preferably a synthetic fiber obtained by plating silver on a synthetic fiber, and the fiber contained in the filling is preferably 100 denier or less, particularly 30 denier, in view of the cotton mixing property. It is effective that the thickness is before and after, but the thickness of the silver-plated fiber used for the fabric may be larger.

【００１２】[0012]

【発明の実施の形態】次に、本発明を実施例に従って更
に詳しく説明する。 実施例１ 真綿１００重量部に、ナイロン繊維に銀メッキした糸
（３０デニールで、銀含有量は１５重量％である）の裁
断物（長さ３cm）１０重量部を均一に混入したものを詰
綿とし、掛布団を製造した。掛布団は、表地及び裏地共
に絹織物からなるものとしたが、特に裏地は、絹織物
（羽二重）の地緯糸に、ナイロン繊維に銀メッキした糸
（３０デニールで、銀含有量は１５重量％である）を裏
地面積の１０％となるように使用した。このようにして
得た掛布団は、厚さ３０mm、重さ２kgという薄く軽量な
ものであっても、それ一枚で、厚手の羽毛掛布団と同等
の保温性があり、しかも、抗菌性や静電防止効果をも有
するため、不当に身体にまとわりつくことなく、常に爽
やかに使用できるものであった。Next, the present invention will be described in more detail with reference to examples. Example 1 100 parts by weight of cotton was mixed with 10 parts by weight of a cut (length 3 cm) of a thread (30 denier, silver content: 15% by weight) silver-coated nylon fiber was uniformly mixed. Made of cotton and quilt was manufactured. The quilt was made of silk fabric for both the outer fabric and the lining. In particular, the lining was made of a silk woven fabric (Habuta), a nylon-coated silver-coated yarn (30 denier, and a silver content of 15 wt. % Was used to make up 10% of the lining area. Even if the comforter obtained in this way is thin and lightweight, having a thickness of 30 mm and weighing 2 kg, one piece of the comforter has the same heat insulation as a thick down comforter, and has antibacterial and electrostatic properties. Since it also has a preventive effect, it can always be used freshly without clinging to the body unduly.

【００１３】実施例２ 実施例１と同様の詰綿を使用してキルティングのジャケ
ットを製造した。このジャケットは表地にナイロン防水
布を使用し、裏地にレーヨン地を使用したが、該レーヨ
ン地は、緯糸に、ナイロン繊維に銀メッキした糸（３０
デニールで、銀含有量は１５重量％である）を、裏地面
積の８％となるように均等に織り込んでなる平織物とし
た。このようにして得たジャケットは、軽量でありなが
ら、非常に保温性に富むものであった。Example 2 A quilted jacket was manufactured using the same wadding as in Example 1. This jacket uses nylon waterproof fabric for the outer material and rayon fabric for the lining. The rayon fabric has a weft and a nylon-plated thread (30%).
(Denier, silver content is 15% by weight) to obtain a plain woven fabric which is uniformly woven so as to make up 8% of the lining area. The jacket obtained in this way was very lightweight and very heat-retaining.

【００１４】[0014]

【発明の効果】本発明では、真綿等に銀メッキ繊維を混
入して使用するため、従来になく軽量にして保温性に富
んだ掛布団や防寒衣料等の詰綿製品を得ることができ
る。この詰綿製品は、抗菌性や静電防止性にも富み、し
かも、直接身体に触れる側の布帛にも銀メッキ繊維が存
在するため、表地に静電気を発生しやすい合成繊維の加
工布等を使用しても、帯電性を気にすることなく、常に
清潔な状態で着用でき、しかも着用者の血行を良好にす
る効果もある。また、銀繊維の含有量が増加すると電磁
波シールド効果もある。According to the present invention, since silk-plated fiber is mixed with silver-plated fiber for use, it is possible to obtain a lightweight and highly heat-insulating comforter such as a comforter or a winter clothing, which has not been obtained conventionally. This cotton-filled product is also rich in antibacterial and antistatic properties, and since there is silver-plated fiber in the fabric that directly touches the body, it is necessary to use synthetic fabric processed cloth that easily generates static electricity on the outer material. Even if it is used, it can always be worn in a clean state without worrying about the chargeability, and has the effect of improving the blood circulation of the wearer. Further, when the content of the silver fiber increases, there is also an electromagnetic wave shielding effect.

Claims (6)

【特許請求の範囲】[Claims] 【請求項１】 綿に銀メッキした繊維の裁断物を混入し
た詰綿を、布帛で覆ってなるものであり、該布帛の少な
くと一部に銀メッキした繊維が織り込まれていることを
特徴とする保温性に富んだ詰綿製品。1. A cotton-filled cotton mixed with a cut material of silver-plated fiber, which is covered with a cloth, wherein at least a part of the cloth is woven with silver-plated fibers. Cotton filling product with rich heat retention. 【請求項２】 前記綿が真綿であることを特徴とする請
求項１の詰綿製品。2. A cotton filling according to claim 1, wherein said cotton is cotton. 【請求項３】 前記詰綿が銀メッキした繊維を２〜２０
重量％含むことを特徴とする請求項１又は２の詰綿製
品。3. The method according to claim 2, wherein the filling comprises silver-plated fibers of 2 to 20%.
3. The cotton filling product according to claim 1, wherein the cotton product contains 0.1% by weight. 【請求項４】 前記詰綿に含まれる銀メッキした繊維の
裁断物が平均１〜８cmの繊維長を有するものであること
を特徴とする請求項１〜３いずれか１項の詰綿製品。4. The cotton-filled product according to claim 1, wherein the cut material of the silver-plated fiber contained in said cotton has an average fiber length of 1 to 8 cm. 【請求項５】 前記製品の少なくとも片面の布帛に、銀
メッキした繊維が、該布帛の面積当たり２〜２０％の範
囲で織り込まれていることを特徴とする請求項１〜４い
ずれか１項の詰綿製品。5. The product according to claim 1, wherein silver-plated fibers are woven into the fabric on at least one side of the product in a range of 2 to 20% per area of the fabric. Cotton products. 【請求項６】 前記銀メッキした繊維が合成繊維に銀メ
ッキしたものであることを特徴とする請求項１〜５いず
れか１項の詰綿製品。6. The cotton-filled product according to claim 1, wherein the silver-plated fibers are silver-plated synthetic fibers.