JP2000152854A - Mattress - Google Patents
MattressInfo
- Publication number
- JP2000152854A JP2000152854A JP25902799A JP25902799A JP2000152854A JP 2000152854 A JP2000152854 A JP 2000152854A JP 25902799 A JP25902799 A JP 25902799A JP 25902799 A JP25902799 A JP 25902799A JP 2000152854 A JP2000152854 A JP 2000152854A
- Authority
- JP
- Japan
- Prior art keywords
- mattress
- protrusions
- body pressure
- substrate
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は寝具用のマットレ
スに関する。The present invention relates to a mattress for bedding.
【０００２】[0002]
【従来の技術と発明が解決しようとする課題】従来よ
り、全体が発泡ポリウレタン等の発泡樹脂により形成さ
れたマットレスが用いられている。2. Description of the Related Art Conventionally, a mattress formed entirely of a foamed resin such as foamed polyurethane has been used.
【０００３】しかし、従来のマットレスでは、人がその
上に仰臥したときに体圧（身体にかかる圧力）が局部的
に集中して血行障害をおこし易い。そのため、身体に圧
迫感やしびれを感じて頻繁に寝返りをうつため安眠でき
なかったり、また起床後も疲労感が残ったりするという
問題がある。さらに、寝たきりの老人などのように寝返
りをうてない人の場合には、大きな体圧によって毛細血
管が破壊され、これが体組織の破壊につながり、ついに
褥瘡が生じるという問題もある。[0003] However, in a conventional mattress, when a person is lying on his / her back, body pressure (pressure applied to the body) is locally concentrated and blood circulation is likely to occur. For this reason, there is a problem in that the patient frequently feels oppression and numbness and turns over frequently, and thus cannot sleep well, or has a feeling of fatigue after getting up. Furthermore, in the case of a person who has not been turned over, such as a bedridden elderly person, there is a problem that the capillaries are destroyed by a large body pressure, which leads to the destruction of the body tissue, and finally a pressure ulcer is generated.
【０００４】これらの問題を解決するために、例えば、
本明細書で比較例１として説明されているムアツふとん
のように、マットレスの表面形状に工夫を施すことが行
われている（図７、図８参照）。このような形状の工夫
によって上記問題はかなり改善されてはいるが、まだ完
全ではなく、さらに体圧分布性能の優れたマットレスが
求められている。In order to solve these problems, for example,
As in the case of the Muatsu futon described as Comparative Example 1 in the present specification, the surface shape of the mattress is devised (see FIGS. 7 and 8). Although the above problem has been considerably improved by such a shape devising, the mattress has not been perfected yet, and a mattress having further excellent body pressure distribution performance has been demanded.
【０００５】また、上記問題を解消するために、反ぱつ
弾性率の小さい合成樹脂発泡体をマットレスの素材とし
て使用することも考えられる。しかし、このようなマッ
トレスでは、身体が沈みすぎてかえって寝心地が悪く、
寝返りもしにくいという問題がある。また、反ぱつ弾性
の小さい素材は密度が大きく、通気性が悪いという問題
もある。In order to solve the above problem, it is conceivable to use a synthetic resin foam having a low elastic modulus as a material of the mattress. However, with such a mattress, the body sinks too much and it is rather uncomfortable,
There is a problem that it is difficult to turn over. In addition, there is a problem that a material having low elasticity has a high density and poor air permeability.
【０００６】この発明は上記に鑑みてなされたものであ
り、その目的は、体圧分散性能がよく、かつ、寝心地も
よい、上記各問題が解決されたマットレスを提供するこ
とにある。[0006] The present invention has been made in view of the above, and an object of the present invention is to provide a mattress which has good body pressure dispersing performance and good sleeping comfort and which solves the above-mentioned problems.
【０００７】[0007]
【課題を解決するための手段】本願の請求項１に記載の
マットレスは、上記の課題を解決するために、全体が発
泡ポリウレタンより形成され、基板の上に多数の突部を
立設してなり、前記突部が二層構造を有し、上部側の層
が低反ぱつポリウレタンよりなるものとする。In order to solve the above problems, the mattress according to the first aspect of the present invention is formed entirely of polyurethane foam, and has a large number of protrusions erected on a substrate. The protrusion has a two-layer structure, and the upper layer is made of low-repellent polyurethane.
【０００８】請求項２に記載のマットレスは、請求項１
のものにおいて、反ぱつ弾性率が、突部の上部側の層に
おいて１３％以下であり、突部の上部側の層を除く部分
において２０〜６０％であるものとする。[0008] The mattress according to the second aspect is the first aspect.
In this case, the resilience modulus is 13% or less in the layer on the upper side of the projection and 20 to 60% in the portion excluding the layer on the upper side of the projection.
【０００９】なお、一般的に反ぱつ弾性とは、打撃した
ときに吸収されずに残留した位置エネルギーの大きさを
尺度として表される性質をいい、一定の高さから、一定
の質量の鉄丸棒などでゴム材料、合成樹脂などの試料を
打撃したときの反ぱつ高さにより評価される（ＪＩＳ
Ｂ ０１１６）。発泡ポリウレタンの反ぱつ弾性につい
ては後述する。Generally, rebound resilience refers to a property expressed as a measure of the potential energy remaining without being absorbed when struck, and from a fixed height to a fixed mass of iron. It is evaluated by the resilience height when a sample such as rubber material or synthetic resin is hit with a round bar (JIS
B 0116). The resilience of the foamed polyurethane will be described later.
【００１０】請求項３に記載のマットレスは、請求項１
または２のものにおいて、突部の頂面がほぼ平坦である
ものとする。[0010] The mattress according to the third aspect is the first aspect.
Alternatively, in the case of item 2, the top surface of the projection is substantially flat.
【００１１】請求項４に記載のマットレスは、請求項１
〜３のいずれか１項に記載のものにおいて、突部の基部
がくびれているものとする。[0011] The mattress according to the fourth aspect is the first aspect.
In any one of the above-mentioned items 3, the base of the projection is narrowed.
【００１２】［作用］請求項１に記載のマットレスの作
用はつぎのとおりである。[Operation] The operation of the mattress according to the first aspect is as follows.
【００１３】このマットレスは、多数の突部を有すると
ともに、突部の上部に反ぱつ弾性率の小さい低反ぱつポ
リウレタンからなる層が形成されており、これがマット
レスの上に仰臥した人の身体に当接するので、突部上面
が人の身体の表面の凹凸形状にやわらかくなじんで容易
に弾性変形する。すなわち、このマットレスは、突部を
形成したことと突部の上部側に低反ぱつポリウレタン層
を設けたこととの相乗効果により体圧分散性能に優れ、
このマットレスを使用した場合、局部的に大きな体圧を
受けず、身体に圧迫感が感じられない。したがって、血
行障害を起こさず、安眠ができて、疲労が残らず、さら
に、褥瘡が生じるおそれもない。This mattress has a large number of protrusions, and a layer made of a low-repellent polyurethane having a low resilience and a low elasticity is formed on the upper portion of the protrusions, and this layer is applied to the body of a person lying on the mattress. Because of the contact, the upper surface of the protrusion softly conforms to the irregular shape of the surface of the human body and easily elastically deforms. In other words, this mattress has excellent body pressure dispersion performance due to the synergistic effect of forming the protrusion and providing a low-repulsive polyurethane layer on the upper side of the protrusion,
When this mattress is used, a large body pressure is not locally received, and a feeling of oppression is not felt on the body. Therefore, it does not cause blood circulation disorder, can sleep well, does not remain tired, and there is no possibility of pressure ulcers.
【００１４】また、マットレスにおける低反ぱつポリウ
レタン層を除く部分、すなわち基板と突部の下部とは、
反ぱつ弾性率が比較的大きい素材より構成されているの
で、マットレス全体としては適度の腰があり、人の身体
が過剰に沈むことがない。Further, the portion of the mattress other than the low-repellent polyurethane layer, that is, the substrate and the lower portion of the protrusion are:
Since the mattress is made of a material having a relatively high elasticity, the mattress as a whole has a moderate waist and the human body does not sink excessively.
【００１５】そして、このように身体が過剰に沈まない
ことから、寝返りも容易である。また、人体が突部によ
り受け止められており、寝返りの際に突部が適切に横方
向に傾動して寝返りに伴う反力を吸収するので、寝返り
がいっそう容易になるという効果も得られる。Since the body does not sink excessively, turning over is easy. Further, since the human body is received by the protruding portion and the protruding portion is appropriately tilted in the lateral direction when turning over to absorb the reaction force caused by turning over, the effect of turning over is further facilitated.
【００１６】さらに、突部の上面のみが人体の表面に当
接するので、マットレスの全表面が人体に当接する場合
と比較して、通気性がよい。さらに、隣り合う突部同士
間の空間はマットレスの全体にわたって連続して空気流
通経路を構成しているので、いっそう大きな通気性が確
保される。また、前記の空間ないし空気流通経路内に滞
留した湿気をふくんだ空気は、人が寝返りをしてその体
重により突部を下方に圧縮することにより強制的に外部
に排出され、また、さらに寝返りして突部が圧縮から解
放されることにより、乾いた空気が新たに取り込まれ
る。すなわち、このマットレスは換気機能も有する。Further, since only the upper surface of the projection comes into contact with the surface of the human body, the air permeability is better than when the entire surface of the mattress comes into contact with the human body. Furthermore, since the space between the adjacent protrusions continuously forms an air circulation path over the entire mattress, greater air permeability is ensured. In addition, the air containing the moisture retained in the space or the air circulation path is forcibly discharged to the outside by a person turning over and compressing the protruding portion downward by its weight, and furthermore, When the protuberance is released from compression by turning over, dry air is newly taken in. That is, the mattress also has a ventilation function.
【００１７】請求項２に記載のマットレスは、突部の上
部側層とそれ以外の部分の反ぱつ弾性率を特定の範囲に
限定したものであり、反ぱつ弾性率をこの範囲内にする
ことにより、上記した体圧分散性能、過剰な沈みこみ防
止等の効果が特に顕著に得られる。In the mattress according to the second aspect, the resilience of the upper layer of the projection and the other portion is limited to a specific range, and the resilience is within this range. Thereby, the above-described effects such as the body pressure dispersing performance and the prevention of excessive sinking can be obtained particularly remarkably.
【００１８】請求項３に記載のマットレスは、突部の頂
面がほぼ平坦であるので、平坦な面の全体が人体に当接
することにより、体圧分散性能がよりよくなる。また、
突部の頂面がほぼ平坦であると、寝返りをした際に突部
にかかる圧縮力がより大きくなるので、突部間に滞留し
た湿気の換気機能がより優れる。In the mattress according to the third aspect, since the top surface of the projection is substantially flat, the entire flat surface comes into contact with the human body, so that the body pressure dispersion performance is further improved. Also,
If the top surface of the projection is substantially flat, the compressive force applied to the projection when it is turned over will be greater, and the ventilation function of the moisture accumulated between the projections will be better.
【００１９】請求項４に記載のマットレスは、突部の基
部がくびれているので、突部が傾きやすく、寝返りがさ
らに容易になる。また、突部が人の体重を受けて圧縮さ
れて径が膨張しても、突部の基部においては空間部がな
お確保されるので通気性を失わない。In the mattress according to the fourth aspect, since the base of the projection is narrowed, the projection is easily inclined, and turning over is further facilitated. Further, even if the protrusion is compressed by receiving the weight of a person and expands in diameter, a space is still secured at the base of the protrusion, so that air permeability is not lost.
【００２０】[0020]
【発明の実施の形態】本発明のマットレスは、上記した
ように基板の上に多数の突部を立設してなり、各部の形
状及び寸法等は、例えば以下のように設計することがで
きるが、これに限定されるものではない。DESCRIPTION OF THE PREFERRED EMBODIMENTS The mattress of the present invention has a large number of projections erected on a substrate as described above, and the shape and dimensions of each part can be designed as follows, for example. However, the present invention is not limited to this.
【００２１】マットレスの平面形状及び幅方向と長さ方
向の寸法は、全く限定されないが、例えば従来のマット
レスと同様、幅８００〜１４５０ｍｍ、長さ１９００〜
２１００ｍｍ程度の長方形とすることができる。基板と
突部を含む全体の厚さも特に限定されるものではない
が、床（畳）用のマットレスの場合は約３０〜１００ｍ
ｍ、ベッド用の場合は約１５０〜２００ｍｍ程度が一般
的である。Although the planar shape and the width and length dimensions of the mattress are not particularly limited, for example, as in the case of a conventional mattress, the width is 800 to 1450 mm and the length is 1900 to 1900.
It can be a rectangle of about 2100 mm. The total thickness including the substrate and the protrusions is not particularly limited, but in the case of a mattress for a floor (tatami), it is about 30 to 100 m.
m, about 150-200 mm for beds.
【００２２】基板の上に立設される突部の形状は、上記
したように頂面が平坦で基部がくびれていることが好ま
しく、平面形状及び横断面形状は、製造が容易である等
の理由から正方形や長方形等の四角形が好ましい。縦断
面形状としては、上記くびれた部分がなめらかな曲線を
なしているのが好ましく、上端部付近の膨れた部分も丸
みを帯びているのが好ましい。すなわち、突部の側壁
は、断面が緩やかなＳ字を描く、なめらかな起伏面をな
していることが好ましい（図４、図５参照）。このよう
な形状をなしていることにより、突部に圧力が加わって
倒れた際に隣接する突部に引っ掛かって復元しない等の
トラブルを防ぐことができる。As for the shape of the protruding portion erected on the substrate, it is preferable that the top surface is flat and the base portion is constricted, as described above. For this reason, a quadrangle such as a square or a rectangle is preferable. As the vertical cross-sectional shape, it is preferable that the constricted portion has a smooth curve, and the bulged portion near the upper end portion is also preferably rounded. That is, it is preferable that the side wall of the projection has a smooth undulating surface with a gentle S-shaped cross section (see FIGS. 4 and 5). With such a shape, it is possible to prevent troubles such as being not restored by being caught on an adjacent projection when the projection is pressed down and falls down.
【００２３】突部の各部の寸法も特に限定されないが、
例えば、平面形状及び断面形状が正方形で基部がくびれ
たものの場合、その太さは、最大径部分で一辺の長さが
２０〜１００ｍｍ程度、くびれた部分で一辺の長さが１
５〜７０ｍｍ程度であることが好ましく、突部の高さ、
すなわち突部間の溝の深さが３０〜７０ｍｍ程度である
ことが好ましい。なお、これらの突部各部の形状及び寸
法をマットレスの部位によって変えることにより、体圧
分散性能及び使用感ともにより優れたマットレスを得る
ことができる。これについては実施例によってさらに詳
しく説明する。The dimensions of each part of the projection are not particularly limited, either.
For example, in the case where the plane shape and the cross-sectional shape are square and the base is constricted, the thickness is about 20 to 100 mm on one side at the maximum diameter part and one side on the constricted part.
It is preferably about 5 to 70 mm, the height of the projection,
That is, the depth of the groove between the protrusions is preferably about 30 to 70 mm. In addition, by changing the shape and dimensions of each of these protrusions depending on the mattress portion, it is possible to obtain a mattress with more excellent body pressure dispersion performance and usability. This will be described in more detail with reference to examples.
【００２４】上記した多数の突部は、わずかの隙間を介
して相互にほぼ隣接していることが好ましく、隙間の寸
法の好ましい範囲は突部の大きさ（太さ）にもよるが、
通常は最狭部で５〜８ｍｍ程度である。隙間の寸法が大
きすぎると突部が安定せず、一方、小さすぎると通気性
が悪くなるおそれがある。It is preferable that the plurality of protrusions are substantially adjacent to each other with a small gap therebetween. A preferable range of the size of the gap depends on the size (thickness) of the protrusion.
Usually, it is about 5 to 8 mm at the narrowest part. If the size of the gap is too large, the protrusion is not stable, while if it is too small, the air permeability may be deteriorated.
【００２５】低反ぱつポリウレタンからなる突部の上部
層は、所望の体圧分散効果を得るために厚みが１０ｍｍ
以上であることが好ましい。厚みの上限は、反ぱつ弾性
率の大きさ等にもよるので一概には言えないが、過剰な
沈み込みを防止するという観点から、おおよその目安と
しては、マットレス全体の厚みの５０％以下とする。The upper layer of the projection made of low-repellent polyurethane has a thickness of 10 mm in order to obtain a desired effect of dispersing body pressure.
It is preferable that it is above. The upper limit of the thickness cannot be said unconditionally because it depends on the magnitude of the resilience and the like, but from the viewpoint of preventing excessive sinking, as a rough guide, the upper limit is 50% or less of the entire mattress thickness. I do.
【００２６】次に、本発明のマットレスを構成する発泡
ポリウレタンとしては、従来の原料及び製法によるもの
が適宜使用できるが、以下の物性をそなえたものを用い
ることが好ましい。Next, as the foamed polyurethane constituting the mattress of the present invention, those obtained by conventional raw materials and manufacturing methods can be appropriately used, but those having the following physical properties are preferably used.
【００２７】突部の上部側の層には、上記したように体
圧分散性能向上のために低反ぱつポリウレタンを用い
る。低反ぱつポリウレタンとは、一般に反ぱつ弾性率の
比較的低い発泡ポリウレタンをいい、その具体的な反ぱ
つ弾性率は特に定められていない。本発明では２０％未
満であれば使用可能であるが、顕著な体圧分散性能を得
るためには、約１３％以下が好ましく、１０％前後が特
に好ましい。As described above, a low resilience polyurethane is used for the layer on the upper side of the projection to improve the body pressure dispersion performance. The low resilience polyurethane generally refers to a foamed polyurethane having a relatively low resilience, and the specific resilience is not particularly defined. In the present invention, if it is less than 20%, it can be used, but in order to obtain remarkable body pressure dispersion performance, it is preferably about 13% or less, particularly preferably about 10%.
【００２８】上部側層以外の部分、すなわち基板及び突
部の下部側の反ぱつ弾性率は、過剰な沈みこみ防止や寝
返りのし易さの点から約２０〜６０％が好ましく、約３
０〜４０％が特に好ましい。The rebound elastic modulus of the portion other than the upper layer, that is, the lower side of the substrate and the protrusion is preferably about 20 to 60% from the viewpoint of preventing excessive sinking and easy turning over, and is preferably about 3 to 60%.
0-40% is particularly preferred.
【００２９】発泡ポリウレタンの密度と硬さは、所望の
反ぱつ弾性率が得られるように適宜選択可能であるが、
一応の目安としては次の範囲が挙げられる。The density and hardness of the foamed polyurethane can be appropriately selected so as to obtain a desired resilience.
As a rough guide, the following ranges can be mentioned.
【００３０】すなわち、密度は、上部側の層では、４０
〜８０ｋｇ／ｍ３、基板及び突部の下部では、３０〜５
０ｋｇ／ｍ３が好ましく、硬さは、上部側の層では、３
０〜９０Ｎ、基板及び突部の下部では、１５０〜２５０
Ｎが好ましい。That is, the density is 40 in the upper layer.
８０80 kg / m 3 , 30 to 5
0 kg / m 3 is preferable, and the hardness is 3 in the upper layer.
0 to 90 N, 150 to 250 N in the lower part of the substrate and the protrusion.
N is preferred.
【００３１】なお、これら突部の形状、寸法、反ぱつ弾
性率、密度、硬さ等は、それぞれマットレスの性能を決
定する一要素であり、マットレスの性能はこれらの要素
を含む多数の要素が複雑に絡み合って決まるものであ
る。従って、いずれかの要素が上記した好ましい範囲か
ら外れていたとしても、それによって即そのマットレス
が使用に耐えないものになるというわけではなく、他の
要素とのかね合いで調整が可能な場合もある。The shape, size, resilience, density, hardness, etc. of these projections are all factors that determine the performance of the mattress, and the performance of the mattress depends on a number of factors including these factors. It is determined by complicated intertwining. Therefore, even if any element is out of the preferred range described above, this does not immediately render the mattress unusable, and in some cases can be adjusted in view of other elements. is there.
【００３２】[0032]
【実施例】以下、実施例により本発明をさらに具体的に
説明するが、本発明はこれに限定されるものではない。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
【００３３】図１〜６はこの発明の一実施例にかかるマ
ットレスを示す。FIGS. 1 to 6 show a mattress according to an embodiment of the present invention.
【００３４】これらの図においては、マットレスの全体
を符号１０で示している。マットレス１０は発泡ポリウ
レタンより形成され、基板１２とその上に立設された多
数の突部１４よりなる。なお、符号１４は突部を全般的
に示し、以下に記載する形状の異なる種々の突部につい
ては、１４ａ，１４ｂ……などの符号によりそれぞれ別
個に示す。In these figures, the entire mattress is indicated by reference numeral 10. The mattress 10 is formed of foamed polyurethane, and includes a substrate 12 and a number of protrusions 14 erected thereon. Reference numeral 14 generally indicates a protrusion, and various protrusions having different shapes described below are separately denoted by reference numerals such as 14a, 14b.
【００３５】マットレス１０はその長手方向において、
３つの部分１０ａ，１０ｂ，１０ｃに区分されている。
これら３つの部分はマットレスの長手方向における長さ
がほぼ等しい。これら３部分は別体に形成してふとんカ
バーに収納することにより一体のふとんとなしてもよ
く、あるいは３部分を連続した形態に形成してもよい。The mattress 10 has, in its longitudinal direction,
It is divided into three parts 10a, 10b, 10c.
These three portions are approximately equal in length in the longitudinal direction of the mattress. These three parts may be formed separately and housed in a futon cover to form an integral futon, or the three parts may be formed in a continuous form.
【００３６】各部分１０ａ，１０ｂ，１０ｃにおける突
部の形状や大きさの概略を次に述べる。ただし、部分１
０ａと部分１０ｃとは、突部も含めて同一寸法及び形状
に形成されているので、ここでは部分１０ａについて説
明する（図１〜図４参照）。The outline of the shape and size of the projection in each of the portions 10a, 10b and 10c will be described below. However, part 1
Since 0a and the portion 10c are formed to have the same size and shape including the protrusion, the portion 10a will be described here (see FIGS. 1 to 4).
【００３７】部分１０ａの四周を除く中央部に位置する
突部１４ａは平面で見て正方形をなしている。これに対
し、マットレスの長手方向に延びる両側部において位置
する突部１４ｂはマットレスの幅方向に細長く形成され
ている。また、マットレス１０の幅方向に延びる両側端
部に位置する突部１４ｃはマットレスの長手方向に細長
く形成されている。そして、部分１０ａの４つの隅角部
に位置する突部１４ｄは平面で見てほぼ正方形をなして
おり、中央部に位置する突部１４ａより大きい。The projection 14a, which is located at the center of the portion 10a except for the four circumferences, has a square shape in plan view. On the other hand, the protrusions 14b located on both sides extending in the longitudinal direction of the mattress are formed to be elongated in the width direction of the mattress. Further, the protrusions 14c located at both end portions extending in the width direction of the mattress 10 are formed to be elongated in the longitudinal direction of the mattress. The projections 14d located at the four corners of the portion 10a are substantially square in plan view, and are larger than the projections 14a located at the center.
【００３８】また、マットレス１０の中央部１０ｂにお
いては、四周を除く中央部に位置する突部１４Ａは平面
で見て正方形をなしている。これに対し、マットレスの
長手方向に延びる両側部において位置する突部１４Ｂは
マットレスの幅方向にやや細長く形成されている。ま
た、マットレス１０の幅方向に延びる両側端部に位置す
る突部１４Ｃはマットレスの長手方向に細長く形成され
ている。そして、中央部１０ｂの４つの隅角部に位置す
る突部１４Ｄは長手方向に細長く形成されている（図
１，２）。Further, in the central portion 10b of the mattress 10, the protrusion 14A located at the central portion except for four circumferences has a square shape when viewed on a plane. On the other hand, the protrusions 14B located on both sides extending in the longitudinal direction of the mattress are formed slightly elongated in the width direction of the mattress. Further, the protrusions 14C located at both side ends of the mattress 10 extending in the width direction are formed to be elongated in the longitudinal direction of the mattress. The projections 14D located at the four corners of the central portion 10b are formed to be elongated in the longitudinal direction (FIGS. 1 and 2).
【００３９】このようなマットレス１０は、基板１２の
厚みと突部１４の厚みの和を厚みとして有する矩形の発
泡体から、隣接する突部間にある空所（カット部）１６
を切除することにより得られる。The mattress 10 is made of a rectangular foam having a thickness equal to the sum of the thickness of the substrate 12 and the thickness of the projections 14, and a space (cut portion) 16 between adjacent projections.
Is obtained by excision.
【００４０】このようにして、多数の突部１４はマット
レス１０の長手方向および幅方向において直線上に整列
している。部分１０ａについていえば、隣接する各２つ
の突部１４ａ，１４ａ；１４ａ，１４ｂ；１４ａ，１４
ｃ；１４ｂ，１４ｄまたは１４ｃ，１４ｄの間にあるカ
ット部１６はマットレスの下方側において円弧状に広が
っている。すなわち、各突部１４ａ，１４ｂ，１４ｃ，
１４ｄはその基部において湾曲状に括れている。このよ
うな突部の態様は、部分１０ｂ，１０ｃにおいても同様
である。In this way, the large number of protrusions 14 are linearly aligned in the longitudinal direction and the width direction of the mattress 10. As for the portion 10a, two adjacent protrusions 14a, 14a; 14a, 14b; 14a, 14
c; 14b, 14d or the cut portion 16 between 14c, 14d extends in an arc shape below the mattress. That is, each projection 14a, 14b, 14c,
14d is curved at its base. Such an aspect of the protrusion is the same in the portions 10b and 10c.
【００４１】突部１４の形状及び大きさを上記のように
することにより、極めて優れた体圧分散効果を得ること
ができ、またマット周辺部の突部の安定性の点でも優れ
る。しかし、突部１４の形状等は上記のものに限られる
わけではなく、例えば、すべての突部が平面で見てほぼ
正方形であってもよい。また、マットレスの長手方向お
よび幅方向に並列する突部の数にも限定がない。By setting the shape and size of the protrusions 14 as described above, an extremely excellent body pressure dispersion effect can be obtained, and the stability of the protrusions around the mat is also excellent. However, the shape and the like of the protrusions 14 are not limited to those described above. For example, all the protrusions may be substantially square when viewed in a plane. In addition, there is no limitation on the number of protrusions arranged in the longitudinal direction and the width direction of the mattress.
【００４２】マットレス１０の基板１２と、突部１４
ａ，１４ｂ，１４ｃ，１４ｄ；１４Ａ，１４Ｂ，１４
Ｃ，１４Ｄの下部側１７とは反ぱつ弾性が比較的大きい
発泡ポリウレタンよりなり、各突部の上部側１８は反ぱ
つ弾性が比較的小さい発泡ポリウレタン（低反ぱつポリ
ウレタン）よりなっている（図３〜５参照）。表１に、
基板１２及び突部下部１７と、突部上部１８の素材の一
例を示す。The substrate 12 of the mattress 10 and the projections 14
a, 14b, 14c, 14d; 14A, 14B, 14
The lower side 17 of C and 14D is made of foamed polyurethane having a relatively large resilient elasticity, and the upper side 18 of each projection is made of foamed polyurethane having a relatively low resilient elasticity (low-repellent polyurethane) (FIG. 8). 3-5). In Table 1,
An example of the material of the substrate 12, the lower part 17 of the protrusion, and the upper part 18 of the protrusion is shown.
【００４３】[0043]
【表１】 [Table 1]
【００４４】表１において「密度」の「上」の項に記載
の数値は試験片の上面から３ｍｍの個所における密度を
表し、「下」の項に記載の数値は試験片の下面から３ｍ
ｍの個所の密度を表す。表１における「硬さ」について
も同様である。In Table 1, the value described in the "upper" section of "density" represents the density at a location 3 mm from the upper surface of the test piece, and the value described in the "lower" section is 3 m from the lower surface of the test piece.
It represents the density at the point m. The same applies to “hardness” in Table 1.
【００４５】表１に記載の各物性の定義ないし測定方法
はつぎのとおりである（詳細は、ＪＩＳ Ｋ ６４００
を参照）。The definition or measurement method of each physical property shown in Table 1 is as follows (for details, see JIS K 6400).
See).
【００４６】［密度］一辺３００ｍｍの正方形で厚さ５
０ｍｍの試験片の体積と重量を測定し、次式により算出
する。[Density] A square having a side of 300 mm and a thickness of 5
The volume and weight of a test piece of 0 mm are measured and calculated by the following equation.
【００４７】[0047]
【数１】 (Equation 1)
【００４８】［硬さ］一辺３００ｍｍの正方形で厚さが
５０ｍｍの試験片を平らに置き、２００ｍｍの円形加圧
板を試験片の上面にのせて、前荷重を０．５ｋｇにした
時の厚さを測定し、これをはじめの厚さとする。次に円
形加圧板を１０ｍｍ／ｓｅｃ以下の速度で、はじめの厚
さの７５％の距離押し込んだのち、ただちに荷重を除
き、再び、ただちに円形加圧板を１０ｍｍ／ｓｅｃ以下
の速度ではじめの厚さの２５％の距離押し込み、静止後
２０秒のときの荷重を読む。[Hardness] A test piece having a square shape of 300 mm on a side and a thickness of 50 mm was placed flat, and a 200 mm circular pressure plate was placed on the upper surface of the test piece, and the thickness when a pre-load of 0.5 kg was applied. Is measured, and this is defined as the initial thickness. Next, after pressing the circular pressure plate at a speed of 10 mm / sec or less at a distance of 75% of the initial thickness, immediately remove the load, and immediately again press the circular pressure plate at a speed of 10 mm / sec or less at the initial thickness. Read the load at 20 seconds after resting.
【００４９】［反ぱつ弾性］試験片を試験器の水平な台
上に置き、鋼球を試験片上４６０ｍｍの距離から自由落
下させ、その時の最高反ぱつ距離を測定する。試験片は
３個の試験片か又は１個の試験片の３個所について、そ
れぞれ３回以上行ない、それぞれの個所の最高反ぱつ距
離を記録する。反ぱつ弾性率は次式により算出する。[Rebound Elasticity] A test piece is placed on a horizontal table of a tester, and a steel ball is freely dropped from a distance of 460 mm on the test piece, and the maximum repulsion distance at that time is measured. The test piece is performed at least three times for each of three test pieces or three places of one test piece, and the maximum repulsion distance of each place is recorded. The resilient modulus is calculated by the following equation.
【００５０】[0050]
【数２】 (Equation 2)
【００５１】［圧縮残留歪］一辺が５０ｍｍの正方形で
厚さ４０ｍｍの試験片を温度７０℃±１℃の恒温槽中で
連続２２時間加熱条件下で５０％圧縮固定し、取り出し
たのち３０分放置後、その厚さを測定する。なお、試験
片の数は３個とし、厚さをダイヤルゲージ式測厚器で測
定しておく。圧縮残留歪は次式により算出する。[Compression Residual Strain] A test piece having a square shape of 50 mm on a side and a thickness of 40 mm was fixed in a constant temperature bath at a temperature of 70 ° C. ± 1 ° C. under a heating condition of 50% continuously for 22 hours, taken out, and taken out for 30 minutes. After standing, the thickness is measured. The number of test pieces is three, and the thickness is measured by a dial gauge type thickness measuring device. The compression residual strain is calculated by the following equation.
【００５２】[0052]
【数３】 (Equation 3)
【００５３】［繰返し圧縮残留歪］一辺１５０ｍｍの正
方形で厚さ５０ｍｍの試験片を予め厚みをダイヤルゲー
ジ式側厚器で測定した後、平行平面板の間にはさみ、６
０±１回／ｍｉｎの速さで厚さの５０％を連続８０，０
００回繰返し圧縮したのち試験片を取り出し、３０分後
の厚さを測定する。繰返し圧縮残留歪は次式により算出
する。[Repeated Compressive Residual Strain] A test piece of 150 mm square with a thickness of 50 mm was measured in advance with a dial gauge side thickness instrument, and then sandwiched between parallel flat plates.
50% of the thickness at a speed of 0 ± 1 times / min.
After being repeatedly compressed 00 times, the test piece is taken out, and the thickness after 30 minutes is measured. The cyclic compression residual strain is calculated by the following equation.
【００５４】[0054]
【数４】 (Equation 4)
【００５５】［引張り強さ及び伸び］１０ｍｍの厚さの
試験片でダンベル状試験片を作り、試験片の平行部分の
中央に４０ｍｍの間隔をもって標線をつけ、平行部分の
３ケ所以上について厚さを測定し、それらの最小値を求
める。測定に当ってはゆがみが出ないようにチャックで
充分締めつけ、これを５００±２５ｍｍ／ｍｉｎの速さ
で引張り、切断時の荷重及び標線間距離を求める。引張
り強さ及び伸びは次式により算出する。[Tensile strength and elongation] A dumbbell-shaped test piece was prepared from a test piece having a thickness of 10 mm, and marked lines were provided at intervals of 40 mm at the center of the parallel portion of the test piece, and the thickness was measured at three or more parallel portions. And measure their minimum values. In the measurement, the plate is sufficiently fastened with a chuck so as not to distort, and is pulled at a speed of 500 ± 25 mm / min, and the load at the time of cutting and the distance between marked lines are obtained. Tensile strength and elongation are calculated by the following equations.
【００５６】[0056]
【数５】 (Equation 5)
【００５７】［引裂き強さ］この試験は引張り強さ、伸
びに類し、試験片の引裂に要する荷重を求める。１０ｍ
ｍの厚さの試験片を採り、平行部分の３ケ所以上につい
て厚さを測定し、それらの最少値を求める。測定に当っ
ては試験片がはずれないようにチャックで充分締めつ
け、これを５００±２５ｍｍ／ｍｉｎの速さで引裂き、
切断時の荷重を求める。引裂き強さを次式により算出す
る。[Tear Strength] In this test, a load required for tearing a test piece is determined in a manner similar to tensile strength and elongation. 10m
A test piece having a thickness of m is taken, the thickness is measured at three or more parallel portions, and their minimum values are determined. In the measurement, the test piece was sufficiently fastened with a chuck so as not to come off, and this was torn at a speed of 500 ± 25 mm / min.
Find the load at cutting. The tear strength is calculated by the following equation.
【００５８】[0058]
【数６】 (Equation 6)
【００５９】以下においては、表１の素材により形成さ
れた図１〜６に示す実施例を「実施例１」又は「快圧」
と称する。In the following, the examples shown in FIGS. 1 to 6 formed from the materials shown in Table 1 are referred to as "Example 1" or "free pressure".
Called.
【００６０】実施例１のマットレスの形状と寸法は、つ
ぎのとおりである。The shape and dimensions of the mattress of the first embodiment are as follows.
【００６１】マットレス１０の全体の幅は９１０ｍｍ、
長さは２０００ｍｍ、厚さ７０ｍｍである。The overall width of the mattress 10 is 910 mm,
The length is 2000 mm and the thickness is 70 mm.
【００６２】マットレスの長手方向の両端側の部分１０
ａ，１０ｃは、同形・同寸法であり、その長さ（マット
レスの長手方向の寸法）は６６７ｍｍである。Parts 10 at both ends in the longitudinal direction of the mattress
a and 10c have the same shape and the same size, and the length (dimension in the longitudinal direction of the mattress) is 667 mm.
【００６３】各部分１０ａ，１０ｃにおいて、突部は、
マットレスの幅方向に２１個、マットレスの長手方向に
１５個が設けられている。In each of the portions 10a and 10c, the protrusion is
21 mattresses are provided in the width direction of the mattress, and 15 mattresses are provided in the longitudinal direction of the mattress.
【００６４】各部分１０ａ，１０ｃにおいて、突部は、
寸法の異なる数種類のものが設けらている。すなわち、
部分１０ａ，１０ｃの周縁部においては、寸法が比較的
大きい突部１４ｂ，１４ｃ，１４ｄが額縁状に並んでお
り、その内部には寸法が比較的小さく互いに同一寸法の
突部１４ａが縦横に並んでいる。In each of the portions 10a and 10c, the protrusion is
Several types with different dimensions are provided. That is,
At the periphery of the portions 10a, 10c, projections 14b, 14c, 14d having relatively large dimensions are arranged in a frame shape, and projections 14a having relatively small dimensions are arranged vertically and horizontally within the frame. In.
【００６５】額縁状に並ぶ突部１４ｂ，１４ｃ，１４ｄ
のうち、突部１４ｄはマットレス１０の部分１０ａ，１
０ｃの４つの隅角部に設けられており、その形状はほぼ
正方形である。また、突部１４ｂは、マットレスの幅方
向に細長い形状であり、部分１０ａ，１０ｃの長手方向
に延びる両側部において、隅角部にある２つの突部１４
ｄ，１４ｄの間において１３個配されている。さらに、
突部１４ｃは、マットレスの長手方向に細長い形状であ
り、部分１０ａ，１０ｃの幅方向に延びる両側部におい
て、隅角部にある２つの突部１４ｄ，１４ｄの間におい
て１９個配されている。また、突部１４ａは正方形であ
り、マットレスの幅方向に１９個、長手方向に１３個が
配されている。各突部１４ａ，１４ｂ，１４ｃ，１４ｄ
の寸法は表２に記載のとおりである。なお、各突部の寸
法は図４のｍ，ｎに示すように膨みの最大径である。The projections 14b, 14c, 14d arranged in a frame shape
Of them, the protrusion 14d is the portion 10a, 1 of the mattress 10.
0c are provided at the four corners, and the shape is substantially square. Further, the protrusions 14b are elongated in the width direction of the mattress, and two protrusions 14 at corners are provided on both sides extending in the longitudinal direction of the portions 10a and 10c.
Thirteen are arranged between d and 14d. further,
The protrusions 14c are elongated in the longitudinal direction of the mattress, and are provided on both sides extending in the width direction of the portions 10a, 10c, between the two protrusions 14d, 14d at the corners. Also, the protrusions 14a are square, and 19 are arranged in the width direction of the mattress and 13 are arranged in the longitudinal direction. Each projection 14a, 14b, 14c, 14d
Are as shown in Table 2. The dimension of each protrusion is the maximum diameter of the bulge as shown by m and n in FIG.
【００６６】[0066]
【表２】 [Table 2]
【００６７】なお、突部１４ａのくびれ部（図４におい
てｏで示す個所）はマットレスの長手方向、幅方向とも
２５ｍｍである。また、カット部１６の底部からマット
レスの底面までの距離（ｑ）は３０ｍｍであり、したが
って、カット部１６の深さｒはさらに、４０ｍｍであ
る。隣接する突部間の間隔ｓ（突部の最大径の個所同士
の間隔）はマットレスの長手方向、幅方向とも６ｍｍで
ある。また、全体の厚みｈは７０ｍｍ、突部の上部１８
の厚みｈ１は１５ｍｍ、残りの厚みｈ２は５５ｍｍであ
る。The constricted portion of the projection 14a (the position indicated by "o" in FIG. 4) is 25 mm in both the longitudinal and width directions of the mattress. The distance (q) from the bottom of the cut portion 16 to the bottom surface of the mattress is 30 mm, and the depth r of the cut portion 16 is further 40 mm. The distance s between the adjacent protrusions (the distance between the protrusions having the maximum diameter) is 6 mm in both the longitudinal direction and the width direction of the mattress. Also, the overall thickness h is 70 mm,
Thickness h 1 is 15 mm, the remaining thickness h 2 is 55 mm.
【００６８】マットレスの長手方向の中央部分１０ｂに
ついては、長さ（マットレスの長手方向の寸法）は６６
６ｍｍである。The length (dimension in the longitudinal direction of the mattress) of the central portion 10b in the longitudinal direction of the mattress is 66.
6 mm.
【００６９】部分１０ｂにおいて、突部は、マットレス
の幅方向に１４個、マットレスの長手方向に１０個が設
けられている。In the portion 10b, 14 protrusions are provided in the width direction of the mattress, and 10 protrusions are provided in the longitudinal direction of the mattress.
【００７０】部分１０ｂにおいても、突部は、寸法の異
なる数種類のものが設けらている。すなわち、部分１０
ｂの周縁部においては、寸法が比較的大きい突部１４
Ｂ，１４Ｃ，１４Ｄが額縁状に並んでおり、その内部に
は寸法が比較的小さく互いに同一寸法の突部１４Ａが並
んでいる。Also in the portion 10b, several types of protrusions having different dimensions are provided. That is, part 10
In the periphery of b, the protrusion 14 having a relatively large dimension
B, 14C, and 14D are arranged in a frame shape, and the projections 14A having relatively small dimensions are arranged in the inside thereof.
【００７１】額縁状に並ぶ突部１４Ｂ，１４Ｃ，１４Ｄ
のうち、突部１４Ｄは部分１０ｂの４つの隅角部に設け
られており、マットレスの長手方向に細長い。また、突
部１４Ｂは、マットレスの幅方向にやや細長い形状であ
り、部分１０ｂの長手方向に伸びる両側部において、隅
角部にある２つの突部１４Ｄ，１４Ｄの間において８個
配されている。さらに、突部１４Ｃは、マットレスの長
手方向に細長い形状であり、部分１０ｂの幅方向に延び
る両側部において、隅角部にある２つの突部１４Ｄ，１
４Ｄの間において１２個配されている。また、突部１４
Ａは正方形であり、マットレスの幅方向に１２個、長手
方向に８個が配されている。各突部１４Ａ，１４Ｂ，１
４Ｃ，１４Ｄの寸法は表３に記載のとおりである。な
お、この場合も、各突部の寸法は図５のＭ，Ｎに示すよ
うに膨みの最大径を示している。The projections 14B, 14C, 14D arranged in a frame shape
Of these, the protrusions 14D are provided at four corners of the portion 10b, and are elongated in the longitudinal direction of the mattress. The protrusions 14B are slightly elongated in the width direction of the mattress, and eight protrusions 14B are provided between the two protrusions 14D at the corners on both sides extending in the longitudinal direction of the portion 10b. . Further, the protrusions 14C are elongated in the longitudinal direction of the mattress, and two protrusions 14D, 1 at corners are provided on both sides extending in the width direction of the portion 10b.
Twelve are arranged between 4D. Also, the protrusion 14
A is a square, and 12 are arranged in the width direction of the mattress and 8 are arranged in the longitudinal direction. Each protrusion 14A, 14B, 1
The dimensions of 4C and 14D are as shown in Table 3. In this case as well, the dimensions of each protrusion indicate the maximum diameter of the bulge as shown by M and N in FIG.
【００７２】[0072]
【表３】 [Table 3]
【００７３】なお、突部１４Ａのくびれ部（図５におい
てＯで示す個所）の径はマットレスの長手方向、幅方向
とも４５ｍｍである。また、カット部１６の底部からマ
ットレスの底面までの距離（Ｑ）は２０ｍｍであり、し
たがって、カット部１６の深さＲは５０ｍｍである。さ
らに、隣接する突部間の間隔Ｓはマットレスの長手方
向、幅方向とも６ｍｍである。また、全体の厚みＨは７
０ｍｍ、突部の上部１８の厚みＨ１は１５ｍｍ、残りの
厚みＨ２は５５ｍｍである。The diameter of the constricted portion (the portion indicated by O in FIG. 5) of the projection 14A is 45 mm in both the longitudinal direction and the width direction of the mattress. The distance (Q) from the bottom of the cut portion 16 to the bottom surface of the mattress is 20 mm, and therefore, the depth R of the cut portion 16 is 50 mm. Further, the interval S between adjacent protrusions is 6 mm in both the longitudinal direction and the width direction of the mattress. The total thickness H is 7
0 mm, the thickness H 1 of the upper 18 of the projection is 15 mm, the remaining thickness H 2 is 55 mm.
【００７４】比較例１としては、ムアツふとん（略称ム
アツ）と称されるマットレスを用いた。なお、「ムアツ
ふとん」は登録商標である。As Comparative Example 1, a mattress called Muatsu Futon (abbreviated as Muatsu) was used. “Muatsu Futon” is a registered trademark.
【００７５】比較例１のマットレスを図７と図８とに示
す。このマットレスは全体が発泡ポリウレタンよりな
り、全体の寸法が幅９１０ｍｍ、長さ１９５０ｍｍ、厚
さ８０ｍｍ（図８のＴ）であり、また、山の高さは３
５．０ｍｍ（図８のｔ）である。図８に示すように、山
の一つの列（第一列）に隣接する山の他の列（第２列）
においては、第１列の隣り合う２つの山の間に第２列の
山が位置している。このマットレスの物性を表４に示
す。The mattress of Comparative Example 1 is shown in FIGS. This mattress is entirely made of foamed polyurethane, has overall dimensions of 910 mm in width, 1950 mm in length, and 80 mm in thickness (T in FIG. 8), and has a peak height of 3 mm.
It is 5.0 mm (t in FIG. 8). As shown in FIG. 8, another row (second row) adjacent to one row (first row) of the mountains
In, the second row of peaks is located between two adjacent peaks of the first row. Table 4 shows the physical properties of the mattress.
【００７６】[0076]
【表４】 [Table 4]
【００７７】比較例２としては、固綿ふとん（略称固
綿）と称されるマットレスを用いた。As Comparative Example 2, a mattress called firm cotton futon (abbreviated to firm cotton) was used.
【００７８】比較例２のマットレスは、全体が凹凸のな
い板状に形成され、幅１０００ｍｍ、長さ２０５０ｍ
ｍ、厚さ１００ｍｍである。ポリエステル１００％から
なる中芯の全面（６面）を、ウール５０％とポリエステ
ル５０％とからなる巻綿により囲繞してなる。中芯、巻
綿ともに重量は２ｋｇである。中芯の物性は表５のとお
りである。The mattress of Comparative Example 2 was entirely formed in a plate shape without unevenness, and was 1000 mm wide and 2050 m long.
m, thickness 100 mm. The entire surface (six surfaces) of the core made of 100% polyester is surrounded by a cotton wool made of 50% wool and 50% polyester. Both the core and the wrapping cotton weigh 2 kg. Table 5 shows the physical properties of the core.
【００７９】[0079]
【表５】 [Table 5]
【００８０】上記実施例１及び比較例１，２のマットレ
スを用いて体圧分散性能の評価を行った。The body pressure dispersion performance was evaluated using the mattresses of Example 1 and Comparative Examples 1 and 2.
【００８１】試験の環境温度は２４℃、湿度は６０％Ｒ
Ｈとした。The environmental temperature of the test was 24 ° C. and the humidity was 60% R.
H.
【００８２】被験者は表６に示す４名である。The subjects were the four subjects shown in Table 6.
【００８３】[0083]
【表６】 [Table 6]
【００８４】なお、表６に記載のＢＭＩ値は「ＢＯＤＹ
ＭＡＳＳ ＩＮＤＥＸ」の略称であり、肥満度ないし
体格を表す指数の一つである。ＢＭＩ値は国際的に広く
普及しており、体の中に占める脂肪量との相関関係が高
いことから、日本肥満学会も推薦している。The BMI values shown in Table 6 are “BODY
It is an abbreviation for "MASS INDEX," and is one of the indices indicating the degree of obesity or physique. Since the BMI value is widely spread internationally and has a high correlation with the amount of fat occupying in the body, the Japanese Society of Obesity also recommends it.
【００８５】ＢＭＩ値は、体重（ｋｇ）を身長（ｍ）の
２乗で割って算出し、２０未満が「やせぎみ」、２０以
上２４未満が「正常体重」、２４以上２６．５未満が
「やや肥満」、２６．５以上が「肥満」とされている。The BMI value is calculated by dividing the body weight (kg) by the square of the height (m). The BMI value is less than 20 as "Yasagimi", 20 or more and less than 24 as "normal weight", and 24 or more and less than 26.5 as "normal weight". "Slightly obese" and 26.5 or more are considered "obese".
【００８６】試験には、株式会社ニッタ製のタクタイル
センサシート「ＢＩＧＭＡＴ２０００」と測定システム
「ＶＩＲＴＵＡＬ」を用いた。このセンサシートは幅４
４０ｍｍ、長さ９６０ｍｍであり、行方向に延びる電極
と列方向に延びる電極とが交叉しており、各交叉部分に
おいて圧力を検知する。各交叉部分の面積は１．０１６
ｃｍ２であり、これを１ポイントとする。以下の記述に
おいて面積を表す数値に単位が付されていないものはポ
イント数を表している。上記したところから分かるよう
に１ポイントは１ｃｍ２にほぼ等しい。For the test, a tactile sensor sheet “BIGMAT2000” manufactured by Nitta Corporation and a measurement system “VIRTUAL” were used. This sensor sheet has a width of 4
The electrodes are 40 mm long and 960 mm long. The electrodes extending in the row direction and the electrodes extending in the column direction intersect, and pressure is detected at each intersection. The area of each intersection is 1.016
cm 2, which is defined as one point. In the following description, those with no unit attached to the numerical value representing the area represent the number of points. As can be seen from the above, one point is approximately equal to 1 cm 2 .
【００８７】実施例１及び比較例１，２のマットレスの
上面の中心部にセンサシートを設置し、その上にシーツ
を敷いた。より詳細には、マットレスの長手方向の一端
（例えば部分１０ａの自由端）から他端（１０ｃ）の側
へ３５０ｍｍの幅を余してセンサシートをマットレスの
幅方向の中央部に敷いた。このとき、前記の３５０ｍｍ
の幅の箇所には枕をおいた。A sensor sheet was placed at the center of the upper surface of the mattress of Example 1 and Comparative Examples 1 and 2, and sheets were laid thereon. More specifically, the sensor sheet was laid at the center in the width direction of the mattress from the one end in the longitudinal direction of the mattress (for example, the free end of the portion 10a) to the side of the other end (10c) with a width of 350 mm. At this time, the above 350 mm
A pillow was placed in the area of the width.
【００８８】枕は図９に示す形状と寸法のものを用い
た。枕の材質は表１に示された、マットレスの基板と突
部下部において用いる素材と同じである。The pillow used had the shape and dimensions shown in FIG. The material of the pillow is the same as the material used for the mattress substrate and the lower part of the protrusion shown in Table 1.
【００８９】シーツの上に、パジャマに着替えた被験者
を肩から大腿部までがセンサシート上に載るように仰臥
させた。センサシートの特性を考慮して、２分後に記録
を開始し、およそ１秒間隔で６回データを収録した。各
被験者につき各試料（実施例１と比較例１，２のマット
レス）ごとに同様の試験を行なった。The subject, who changed into pajamas, was placed on the sheet so that the shoulder to thigh rested on the sensor sheet. In consideration of the characteristics of the sensor sheet, recording was started two minutes later, and data was recorded six times at approximately one-second intervals. The same test was performed for each sample (mattress of Example 1 and Comparative Examples 1 and 2) for each subject.
【００９０】このようにして被験者の背面の体圧分布状
況を測定した。データの解析には３回目に収録したデー
タを用いた。以下の記述及び図面において示すデータは
４人の平均値である。In this manner, the distribution of body pressure on the back of the subject was measured. The data collected for the third time was used for data analysis. The data shown in the following description and drawings are average values of four persons.
【００９１】実施例１について行った試験の結果を図１
０〜１２の体圧分布図に示す。FIG. 1 shows the results of the test performed on Example 1.
It is shown in the body pressure distribution chart of 0-12.
【００９２】図１０において、Ａ部分は背面上部、Ｂ部
分は背面下部、Ｃ部分は腰部を示す。In FIG. 10, the portion A indicates the upper rear portion, the portion B indicates the lower rear portion, and the portion C indicates the waist.
【００９３】図１０〜１２において、評点１〜１４を与
えた領域のそれぞれの圧力を図１０の右側において示し
ている。評点１〜１４は数値が大きいほど圧力が高いこ
とを表している。従って、数値の大きい評点が与えられ
た領域が狭く、数値の小さい評点が与えられた領域が広
い方が体圧がよく分散されていることを示す。すなわ
ち、人の体重をより広い面積で受け止めて圧力を分散さ
せるものが体圧分散性能がよいといえる。図によれば、
臀部に最も大きな圧力がかかっている。In FIGS. 10 to 12, the pressures in the areas where the scores 1 to 14 are given are shown on the right side of FIG. The scores 1 to 14 indicate that the larger the numerical value, the higher the pressure. Therefore, the smaller the area given a score with a large numerical value, and the wider the area given a score with a small numerical value, the better the body pressure is dispersed. In other words, it can be said that a device that receives a person's weight in a wider area and disperses the pressure has good body pressure dispersion performance. According to the figure,
The greatest pressure on the buttocks.
【００９４】比較例１，２についても、図１０と同様の
体圧分布図を作成した（添付を省略する）。For Comparative Examples 1 and 2, body pressure distribution charts similar to those shown in FIG. 10 were created (not shown).
【００９５】実施例１と比較例１，２とを数値的に比較
するために、前者については図１０に示すデータを、ま
た後者については不図示の体圧分布図に表われたデータ
をそれぞれ処理して図１３に示すグラフと表とを作成し
た。To numerically compare Example 1 with Comparative Examples 1 and 2, the data shown in FIG. 10 was used for the former, and the data shown in a body pressure distribution chart (not shown) was used for the latter. This was processed to create the graph and table shown in FIG.
【００９６】すなわち、実施例１につき、図１０〜１２
に示す評点１〜１４の領域につき１０ｍｍＨｇごとに面
積を集計し、グラフと表に示した。比較例１，２につい
ても同様にした。That is, FIGS.
The area was totaled for each area of 10 mmHg for the areas of the scores 1 to 14 shown in Table 1 and shown in the graph and table. The same applies to Comparative Examples 1 and 2.
【００９７】より具体的には、実施例１につき、図１０
〜１２の評点１の領域と評点２の領域（「０−１０ｍｍ
Ｈｇ」に相当）の面積（ポイント）を集計して、図１３
の下部の表においての文字を付した横枠の該当箇所に
「８９１．０」と記入した。比較例１，２についても、
それぞれの体圧分布図（不図示）から同様に面積を集計
して、その数値をの数字を付した横枠の該当箇所に記
入した。すなわち、ムアツでは「９９１．３」、固綿で
は「９７０．３」と記入した。以下同様にして、１０ｍ
ｍＨｇごとに面積を集計して、横枠〜の該当箇所に
記入した。以上から明らかなように、〜の数字は、
図１０〜１２に示す評点の場合と同様に、数値が小さい
ものが圧力が小さいことを示している。More specifically, FIG.
The area of the score 1 and the area of the score 2 of １２12 (“0-10 mm
Hg "), the area (points) of FIG.
"891.0" was written in the corresponding part of the horizontal frame with the letters in the table below "." Also for Comparative Examples 1 and 2,
The area was similarly tabulated from each body pressure distribution map (not shown), and the numerical value was entered in the corresponding part of the horizontal frame with the number. That is, "991.3" was entered for Muatsu and "970.3" for solid cotton. Similarly, 10 m
The area was tabulated for each mHg and entered in the corresponding places from the horizontal frame. As is clear from the above, the numbers of ~
As in the case of the scores shown in FIGS. 10 to 12, a smaller numerical value indicates a smaller pressure.
【００９８】図１３の上部においては、以上のような面
積を表す数値を棒グラフに表している。棒グラフの各バ
ーは上下方向に複数の部分に区分されており、各部分の
高さが〜の横枠に記載された数値を表している。各
バーの各部分であって、〜の横枠に記載された数値
を表した各部分には、該当する〜の数字を記入し
た。ただし、各バーにおける〜に対応する部分は、
グラフ上におけるその面積が小さすぎるので、〜の
数字の記入を省略した。In the upper part of FIG. 13, the numerical values representing the areas as described above are shown in a bar graph. Each bar of the bar graph is divided into a plurality of portions in the vertical direction, and the height of each portion represents a numerical value described in a horizontal frame of ~. In each part of each bar, which represents the numerical value described in the horizontal frame of 〜, the corresponding numeral of 〜 is entered. However, the part corresponding to ~ in each bar is
Since the area on the graph was too small, the entry of the numbers of ~ was omitted.
【００９９】折線グラフは平均体圧を示しており、右側
の縦軸には、この折線グラフのために圧力を５ｍｍＨｇ
間隔目盛で取った。The line graph shows the average body pressure, and the vertical axis on the right shows the pressure of 5 mmHg for this line graph.
Taken on an interval scale.
【０１００】体圧分布については、低い圧力の部分（横
枠の番号の数値の小さいもの）が広いものが好ましい
が、図１３に示すように、実施例１（快圧）が比較例
１，２（ムアツ、固綿）に比して、棒グラフのうち〜
の部分が大きい。したがって、まず、マットレス全体
の体圧分散性能について見た場合、この発明は比較例に
比して優れていることが明らかである。Regarding the body pressure distribution, it is preferable that the low pressure portion (the one with a small numerical value in the horizontal frame) is wide, but as shown in FIG. 2 (Muatsu, solid cotton)
Part is big. Therefore, when first looking at the body pressure dispersion performance of the entire mattress, it is clear that the present invention is superior to the comparative example.
【０１０１】ところで、マットレスの体圧分散性能につ
いて特に重要なことは、マットレスのうち高い圧力がか
かる部分における分散性能である。すなわち、高い圧力
がかかると血行が阻害されて寝返りをせざるを得ず、眠
りが浅くなり、また寝たきり老人などの場合には褥瘡が
発生するので、高い圧力がかかる部分においてこそ、で
きるだけ分散性能をよくして、局部的な圧力の集中をさ
けることが重要である。What is particularly important for the body pressure dispersing performance of the mattress is the dispersing performance of a portion of the mattress to which a high pressure is applied. In other words, when high pressure is applied, blood circulation is obstructed and it is necessary to turn over, sleep becomes shallow, and in the case of bedridden elderly people, pressure ulcers occur. It is important to improve the pressure and avoid local pressure concentration.
【０１０２】一般的に、褥瘡防止の観点からは、基準を
３２ｍｍＨｇとして、それ以上は褥瘡が発生する「高い
値」であるとしている。これは、毛細血管が直接圧力を
受けたとき、３２ｍｍＨｇ以上で不可逆的な変化をして
人体の組織を壊すとされているからである（例えば、三
田勝己、赤滝久美、伊東晋彦、篠田剛、石田義人、吉田
誠「新合繊マットレス物理的特性と褥予防効果」総合リ
ハ２２巻１０号、８５８、１９９４）。In general, from the viewpoint of pressure ulcer prevention, the criterion is set to 32 mmHg, and above that, the pressure ulcer is considered to be “high value”. This is because capillaries are supposed to undergo irreversible changes above 32 mmHg and destroy human tissues when subjected to direct pressure (eg, Katsumi Mita, Kumi Akataki, Masahiko Ito, Tsuyoshi Shinoda , Yoshito Ishida, Makoto Yoshida, "Synthetic Fiber Mattress Physical Properties and Preventive Effect on Puerper", General Rehabilitation Vol. 22, No. 10, 858, 1994).
【０１０３】そこで、高い圧力がかかる部分における分
散性能を見るために、３２ｍｍＨｇ以上の圧力が測定さ
れた総面積を集計したものが図１４である。なお、体圧
の分散傾向は、背肩甲骨付近と臀部を高い圧力として現
れる傾向が大きいため、便宜的に、測定した人体面を上
半身部分と下半身部分とに２分割し、上半身部分をさら
に２分割して、合計３部位すなわち背上部Ａ、背下部
Ｂ、腰部Ｃ（図１０参照）に分けて分析した。FIG. 14 shows the total area where the pressure of 32 mmHg or more was measured in order to check the dispersion performance in the portion where a high pressure is applied. Since the tendency of body pressure to disperse tends to appear as high pressure near the back scapula and the buttocks, for convenience, the measured human body surface is divided into an upper body part and a lower body part, and the upper body part is further divided into two parts. It was divided into three parts, that is, the upper back A, the lower back B, and the waist C (see FIG. 10) and analyzed.
【０１０４】これによれば、実施例１（快圧）は、３２
ｍｍＨｇ以上の高い圧力がかかる部分の面積が、比較例
１（ムアツ）と比較例２（固綿）にくらべて小さく、こ
のことから、本発明は特に高い圧力がかかる領域におい
て体圧分散性能が優れていることが分かる。According to this, Example 1 (free pressure) is 32
The area of a portion to which a high pressure of not less than mmHg is applied is smaller than that of Comparative Example 1 (Muatsu) and Comparative Example 2 (solid cotton). It turns out that it is excellent.
【０１０５】このように、この発明のマットレスは、全
体的にも体圧分散性能がよく、また、特に問題となる高
い圧力のかかる領域においても体圧分散性能が優れてい
ると言える。As described above, it can be said that the mattress of the present invention has good body pressure dispersing performance as a whole and also has excellent body pressure dispersing performance even in a region where a high pressure, which is particularly problematic, is applied.
【０１０６】この発明の効果をより明らかにするため
に、さらに実施例２及び３、比較例３〜６として、次に
示す各マットレスを用いて同様の体圧分布性能の評価を
行った。In order to further clarify the effect of the present invention, the same body pressure distribution performance was evaluated as in Examples 2 and 3 and Comparative Examples 3 to 6 using the following mattresses.
【０１０７】実施例２：突部の上部側の層を反ぱつ弾性
率が２％のポリウレタンで形成した以外は、実施例１と
同じ形状・寸法・素材で構成したマットレス。Example 2: A mattress made of the same shape, dimensions and material as in Example 1 except that the upper layer of the protrusion was made of polyurethane having a resilience of 2%.
【０１０８】実施例３：基板及び突部の下部側を反ぱつ
弾性率が６０％のポリウレタンで形成した以外は、実施
例１と同じ形状・寸法・素材で構成したマットレス。Example 3 A mattress made of the same shape, dimensions and material as in Example 1 except that the substrate and the lower side of the protrusion were formed of polyurethane having a resilience of 60%.
【０１０９】比較例３：実施例１の基板と突部の高さの
総計を高さとして有する矩形に形成され（すなわちカッ
ト部を有しない）、全体を実施例１のマットレスの突部
の上部側の素材（低反ぱつポリウレタン、表１参照）の
みにより構成したマットレス。Comparative Example 3: A rectangular shape having the sum of the height of the substrate and the protrusions of Example 1 as a height (that is, having no cut portion), and the entire upper part of the protrusions of the mattress of Example 1 Mattress composed only of the side material (low-repellent polyurethane, see Table 1).
【０１１０】比較例４：実施例１の基板と突部の高さの
総計を高さとして有する矩形に形成され、全体を実施例
１のマットレスの基板及び突部の下部側の素材のみによ
り構成したマットレス。Comparative Example 4 The substrate of Example 1 was formed in a rectangular shape having the total height of the protrusions as heights, and the whole was composed only of the mattress substrate of Example 1 and the material on the lower side of the protrusions. Mattress.
【０１１１】比較例５：実施例１の基板と突部の高さの
総計を高さとして有する矩形に形成され、その上層部
（厚さ１５ｍｍ）は実施例１のマットレスの突部の上部
側の素材により構成し、その下部層は実施例１のマット
レスの突部の下部側の素材により構成したマットレス。Comparative Example 5: The substrate of Example 1 was formed into a rectangle having the total height of the protrusions as the height, and the upper layer (thickness: 15 mm) was on the upper side of the protrusion of the mattress of Example 1. A mattress whose lower layer is made of a material below the protrusions of the mattress of Example 1.
【０１１２】比較例６：マットレス全体を実施例１のマ
ットレスの突部の下部側の素材により構成した以外は、
実施例１と同じ形状・寸法で構成したマットレス。Comparative Example 6: Except that the entire mattress was made of the material below the protrusion of the mattress of Example 1,
A mattress having the same shape and dimensions as in the first embodiment.
【０１１３】なお、比較例３〜５のマットレスの寸法
は、幅９１０ｍｍ、長さ２０００ｍｍ、厚さ７０ｍｍで
ある。The dimensions of the mattresses of Comparative Examples 3 to 5 are 910 mm in width, 2000 mm in length, and 70 mm in thickness.
【０１１４】比較例３についての試験結果を図１５〜１
７に、比較例４についての試験結果を図１８〜２０に示
し、また、これらの図に表れたデータについて図１３と
図１４の場合と同じ処理をして、それぞれ、図２１と図
２２を得た。The test results for Comparative Example 3 are shown in FIGS.
7 shows the test results of Comparative Example 4 in FIGS. 18 to 20, and the same processing as in FIGS. 13 and 14 is performed on the data shown in these figures, and FIG. 21 and FIG. Obtained.
【０１１５】これによると、突部がなく全体が矩形に形
成されたマットレスの場合、反ぱつ弾性の小さい素材を
全体的に使用したものが反ぱつ弾性が比較的大きい素材
を全体的に使用したものに比して、全体的に見て体圧の
分散がよく、また、腰部においても高い圧力（３２ｍｍ
Ｈｇ以上）が分散されていることが分かる。According to this, in the case of a mattress having a rectangular shape without protrusions, a material having a relatively low resilience is generally used instead of a material having a relatively low resilience. The body pressure distribution is better as a whole, and the higher pressure (32 mm
Hg or more) is dispersed.
【０１１６】比較例５の試験結果を図２３〜２５に示
す。また、比較例５を実施例１（図１０〜１２）と比較
するために、図１３と図１４の場合と同じ処理をして、
それぞれ、図２６と図２７を得た。The test results of Comparative Example 5 are shown in FIGS. In order to compare Comparative Example 5 with Example 1 (FIGS. 10 to 12), the same processing as in FIGS. 13 and 14 was performed.
26 and 27 are obtained, respectively.
【０１１７】これによると、本発明のように反ぱつ弾性
が比較的大きい素材と比較的小さい素材との二層構造で
あり、かつ突部を有する（カット部を有する）ものが、
比較例５のように二層構造ではあっても突部を有しない
ものに比して、マットレス全体で見ても（図２６）、ま
た高い圧力がかかる部分においても（図２７）、体圧分
散性能に優れていることが分かる。According to this, the two-layer structure of the material having relatively high resilience and the material having relatively small resilience as in the present invention, and having a projection (having a cut portion),
Compared to a double-layered structure having no protrusions as in Comparative Example 5, the mattress can be seen in the entire mattress (FIG. 26) and in a portion where high pressure is applied (FIG. 27). It can be seen that the dispersion performance is excellent.
【０１１８】マットレスの体圧分散性能について特に重
要なのは、上記したように高い圧力がかかる部分におけ
る分散性能であるので、さらに実施例２，３及び比較例
６についても同様の試験を行い、圧力３２ｍｍＨｇ以上
の部分の面積を求めた。Since the dispersion performance of the mattress, which is particularly important for the body pressure dispersion performance as described above, is the dispersion performance in the portion where a high pressure is applied, the same test was further performed on Examples 2, 3 and Comparative Example 6 to obtain a pressure of 32 mmHg. The area of the above parts was determined.
【０１１９】以上により得られた実施例１〜３及び比較
例３〜６の圧力３２ｍｍＨｇ以上の部分の面積を下表７
に示す。Table 7 below shows the areas of the parts having a pressure of 32 mmHg or more in Examples 1 to 3 and Comparative Examples 3 to 6 obtained as described above.
Shown in
【０１２０】ところで反ぱつ弾性率の低い素材を用いた
場合、一般に体圧分散性能は優れるが、それと引き替え
に沈みこみ感が大きくなりすぎ、寝返りも困難になる傾
向がある。By the way, when a material having a low elastic modulus is used, the body pressure dispersing performance is generally excellent, but in exchange for this, the feeling of sinking becomes too large, and it tends to be difficult to turn over.
【０１２１】そこで、反ぱつ弾性率及び突部形成の有無
と使用感との関係を調べるために、上記実施例１〜３、
比較例３〜６の各マットレスに被験者Ａ〜Ｄを仰臥さ
せ、仰臥した際の沈みこみ感と寝返りのし易さを次の基
準に従って申告させ、それぞれの平均値を求めた。少数
以下は四捨五入した。結果を表７に併せ示す。Therefore, in order to investigate the relationship between the resilience and the presence or absence of the formation of the projections and the feeling of use, the above Examples 1 to 3,
The subjects A to D were supine on each of the mattresses of Comparative Examples 3 to 6, and the feeling of sinking and ease of turning over when lying down were reported according to the following criteria, and the average value of each was determined. Less than a few are rounded. The results are shown in Table 7.
【０１２２】沈みこみ感 ５…適度である、３…やや大きすぎる、１…大きすぎ
る。Sinking feeling 5: moderate, 3: slightly too large, 1 ... too large.
【０１２３】寝返りのし易さ ５…良い、４…やや良い、３…普通、２…やや悪い、１
…悪い。Ease of turning over 5 ... Good, 4 ... Somewhat good, 3 ... Normal, 2 ... Somewhat bad, 1
…bad.
【０１２４】[0124]
【表７】 [Table 7]
【０１２５】表７に示された結果から分かるように、基
板の上に突部を立設した構成にするとともに、突部の上
部側と、突部の上部を除くその余の部分を反ぱつ弾性率
を所定の範囲内にすることにより、体圧分散性能向上と
沈み込み感や寝返りのし易さとのバランスのとれた、理
想的なマットレスを得ることが可能となる。As can be seen from the results shown in Table 7, the structure was such that the protrusions were erected on the substrate, and the upper side of the protrusions and the remaining portion excluding the upper portions of the protrusions were repeated. By setting the elastic modulus within a predetermined range, it is possible to obtain an ideal mattress that balances the improvement of the body pressure dispersion performance with the feeling of sinking and the ease of turning over.
【０１２６】[0126]
【発明の効果】請求項１に記載のマットレスは体圧分散
性能に優れており、使用者の身体に局部的に大きな圧力
を与えない。したがって、身体に圧迫感ないし刺激感を
感じず、安眠ができて、睡眠時の疲労がない。さらに、
血行障害を起こさないので、長期間寝たきりの使用者に
も褥瘡を生じにくい。The mattress according to the first aspect is excellent in the body pressure dispersing performance and does not locally apply a large pressure to the user's body. Therefore, the body does not feel a feeling of pressure or irritation, can sleep well, and does not have fatigue during sleep. further,
Since it does not cause blood circulation disorders, it is difficult for bedridden users to develop pressure sores for a long time.
【０１２７】また、使用者の身体が過剰に沈むことがな
く、寝返りも容易であるので、寝心地がよい。Further, since the body of the user does not sink excessively and the user can easily turn over, the sleeping comfort is good.
【０１２８】さらに、通気性がよく、湿気も外部に排出
しやすい。Further, the air permeability is good, and the moisture is easily discharged to the outside.
【０１２９】請求項２に記載のマットレスは体圧分散性
能と寝心地のバランスが特によい。The mattress according to the second aspect has a particularly good balance between body pressure dispersion performance and comfort.
【０１３０】請求項３に記載のマットレスは、体圧分散
性能と換気機能が特に優れる。[0130] The mattress according to the third aspect is particularly excellent in body pressure dispersion performance and ventilation function.
【０１３１】請求項４に記載のマットレスは、突部が傾
きやすく、これにより寝返りがさらに容易になる。ま
た、突部が人の重量により拡径しても、その基部におい
ては空間部が確保されており通気性を失わない。[0131] In the mattress according to the fourth aspect, the protruding portion is easily inclined, which makes it easier to turn over. Further, even if the diameter of the protrusion is increased by the weight of a person, a space is secured at the base of the protrusion, so that air permeability is not lost.
【図１】この発明のマットレスの一実施例を示す一部を
省略した斜視図。FIG. 1 is a partially omitted perspective view showing an embodiment of a mattress of the present invention.
【図２】図１のマットレスの一部を省略した平面図。FIG. 2 is a plan view of the mattress of FIG. 1 with a part thereof omitted;
【図３】図１のマットレスの隅角部の拡大斜視図。FIG. 3 is an enlarged perspective view of a corner of the mattress of FIG. 1;
【図４】図３のＩＶ−ＩＶ線断面図。FIG. 4 is a sectional view taken along line IV-IV in FIG. 3;
【図５】図２のＶ−Ｖ線断面図。FIG. 5 is a sectional view taken along line VV of FIG. 2;
【図６】図１のマットレスの上に人が仰臥した状態を示
す側面図。FIG. 6 is a side view showing a state where a person is lying on the mattress of FIG. 1;
【図７】比較例１のマットレス（ムアツ）を示す斜視
図。FIG. 7 is a perspective view showing a mattress (Muatsu) of Comparative Example 1.
【図８】図７のマットレスの一部の側面図。FIG. 8 is a side view of a part of the mattress of FIG. 7;
【図９】体圧分散性能の試験の際に用いた枕の斜視図。FIG. 9 is a perspective view of a pillow used in a test of body pressure dispersion performance.
【図１０】本発明の実施例１のマットレスにつき行った
体圧分散性能試験の結果を示す体圧分布図。FIG. 10 is a body pressure distribution diagram showing the results of a body pressure dispersion performance test performed on the mattress of Example 1 of the present invention.
【図１１】図８の半部であって背部を示す拡大図。FIG. 11 is an enlarged view showing a half part and a back part of FIG. 8;
【図１２】図８の半部であって腰部を示す拡大図。FIG. 12 is an enlarged view of a half part of FIG. 8 showing a waist.
【図１３】本発明の実施例１と比較例１，２のマットレ
スの体圧分散性能を比較したグラフ。FIG. 13 is a graph comparing the body pressure dispersion performance of the mattresses of Example 1 of the present invention and Comparative Examples 1 and 2.
【図１４】本発明の実施例１と比較例１，２のマットレ
スの体圧分散性能を高い圧力がかかる部分について比較
したグラフ。FIG. 14 is a graph comparing the body pressure dispersion performance of the mattresses of Example 1 of the present invention and Comparative Examples 1 and 2 with respect to a portion to which high pressure is applied.
【図１５】比較例３のマットレスにつき行った体圧分散
性能試験の結果を示す図１０〜１２と同様の体圧分布
図。FIG. 15 is a body pressure distribution diagram similar to FIGS. 10 to 12 showing the results of a body pressure dispersion performance test performed on the mattress of Comparative Example 3.
【図１６】図１５の半部であって背部を示す図１１と同
様の拡大図。FIG. 16 is an enlarged view similar to FIG. 11 showing a half part and a back part of FIG. 15;
【図１７】図１５の半部であって腰部を示す図１２と同
様の拡大図。FIG. 17 is an enlarged view similar to FIG. 12, showing the waist, which is a half part of FIG. 15;
【図１８】比較例４のマットレスにつき行った体圧分散
性能試験の結果を示す図１０と同様の体圧分布図。FIG. 18 is a body pressure distribution diagram similar to FIG. 10 showing the results of a body pressure dispersion performance test performed on the mattress of Comparative Example 4.
【図１９】図１８の半部であって背部を示す図１１と同
様の拡大図。FIG. 19 is an enlarged view similar to FIG. 11, showing a half part and a back part of FIG. 18;
【図２０】図１８の半部であって腰部を示す図１２と同
様の拡大図。FIG. 20 is an enlarged view similar to FIG. 12, showing the waist, which is a half part of FIG. 18;
【図２１】比較例３と比較例４のマットレスの体圧分散
性能を比較した図１３と同様のグラフ。FIG. 21 is a graph similar to FIG. 13 comparing the body pressure dispersion performance of the mattresses of Comparative Example 3 and Comparative Example 4.
【図２２】比較例３と４のマットレスの体圧分散性能を
高い圧力がかかる部分について比較した図１３と同様の
グラフ。FIG. 22 is a graph similar to FIG. 13 in which the body pressure dispersion performance of the mattresses of Comparative Examples 3 and 4 is compared for a portion where a high pressure is applied.
【図２３】比較例５のマットレスにつき行った体圧分散
性能試験の結果を示す図１０と同様の体圧分布図。FIG. 23 is a body pressure distribution diagram similar to FIG. 10 showing the results of a body pressure dispersion performance test performed on the mattress of Comparative Example 5.
【図２４】図２３の半部であって背部を示す図１１と同
様の拡大図。FIG. 24 is an enlarged view similar to FIG. 11, showing a half part and a back part of FIG. 23;
【図２５】図２３の半部であって腰部を示す図１２と同
様の拡大図。FIG. 25 is an enlarged view similar to FIG. 12, showing a waist, which is a half part of FIG. 23;
【図２６】本発明の実施例１と比較例５のマットレスの
体圧分散性能を比較した図１３と同様のグラフ。FIG. 26 is a graph similar to FIG. 13 comparing the body pressure dispersion performance of the mattresses of Example 1 of the present invention and Comparative Example 5.
【図２７】実施例１と比較例５のマットレスの体圧分散
性能を高い圧力がかかる部分について比較した図１３と
同様のグラフ。FIG. 27 is a graph similar to FIG. 13 in which the body pressure dispersion performance of the mattresses of Example 1 and Comparative Example 5 is compared for a portion to which high pressure is applied.
１０…マットレス １２… 基板 １４，１４ａ，１４ｂ，１４ｃ，１４ｄ，１４Ａ，１４
Ｂ，１４Ｃ，１４Ｄ…突部 １７…突部の下部側 １８…突部の上部側10 Mattress 12 Substrate 14, 14a, 14b, 14c, 14d, 14A, 14
B, 14C, 14D: Projecting portion 17: Lower side of projecting portion 18: Upper side of projecting portion
Claims (4)
板の上に多数の突部を立設してなるマットレスであっ
て、前記突部が二層構造を有し、上部側の層が低反ぱつ
ポリウレタンよりなることを特徴とするマットレス。1. A mattress which is formed entirely of foamed polyurethane and has a large number of protrusions erected on a substrate, wherein the protrusions have a two-layer structure, and an upper layer has a low resistance. Mattress characterized by being made of polyurethane.
３％以下であり、突部の上部側の層を除く部分の反ぱつ
弾性率が２０〜６０％であることを特徴とする、請求項
１に記載のマットレス。2. A resilient modulus of the upper layer of the projection is 1
2. The mattress according to claim 1, wherein the mattress is 3% or less, and a portion excluding a layer on an upper side of the protrusion has a resilience of 20 to 60%.
徴とする、請求項１または２に記載のマットレス。3. The mattress according to claim 1, wherein a top surface of the projection is substantially flat.
とする、請求項１〜３のいずれか１項に記載のマットレ
ス。4. The mattress according to claim 1, wherein a base of the projection is narrowed.