JP2000122548A - Tacky adhesive label with peelable base material and its production - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a tacky adhesive for sticking which prevents the color development caused by penetration of an organic solvent at the time of production of a slip for sticking using thermosensitive recording paper having a color development layer as a base material and is wide in a range of resin selection at the time of formation of a peelable layer and an intermediate layer, etc., and its production method. SOLUTION: A solvent impermeable layer 3 is previously formed adjacently to the color development layer of a base material sheet 2, by which the color development of the dyes in the color development layer is prevented. A sheet which makes the organic solvent hardly permeable is rolled in together when the base material sheet is rolled during the course of production, by which the color development of the color development layer is prevented.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、基材が１枚のシー
トからなる１パートの貼付用伝票に適した粘着ラベルに
関するものである。特に本発明の粘着ラベルは、基材が
染料を含む発色層を有しているために製造途中で種々の
コーティングの際に溶剤により発色層が発色するのを、
溶剤が浸透しない層で遮断して防止している。又、本発
明はそのような粘着ラベルの製造途中において、コーテ
ィング直後に巻き取ると、塗膜中の溶剤が発色層の発色
を引き起こす恐れがあるのを、溶剤が浸透しにくいシー
トと共に巻き取ることにより防止しつつ行なう製造法に
関するものである。本発明の粘着ラベルは、集荷業者、
運送業者、もしくは配達業者等の貨物の輸送の際や、通
信販売業者が顧客の注文に応じて、取扱い商品を発送す
る際等に、商品や商品を集めて収納する通箱等に貼って
使用するのに、特に適したものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive label suitable for a one-part pasting slip in which a base material is composed of one sheet. In particular, the pressure-sensitive adhesive label of the present invention, since the substrate has a coloring layer containing a dye, because the coloring layer is colored by a solvent during various coatings during production,
It is blocked and prevented by a layer that does not penetrate the solvent. In addition, the present invention relates to the fact that, if such a pressure-sensitive adhesive label is wound up immediately after coating during the production thereof, the solvent in the coating film may cause coloring of the coloring layer. And a manufacturing method performed while preventing the above. The adhesive label of the present invention is a collector,
Used when transporting cargo such as a carrier or a delivery company, or when mail-order dealers ship products handled according to customer orders, etc. It is particularly suitable for

【０００２】[0002]

【従来の技術】商品が多くの経路を流通したり、貨物が
多くの輸送拠点を経由して輸送されたり、あるいは素材
が多種類の加工機により加工されるような場合には、情
報の管理が非常に重要である。流通の各経路、輸送の各
拠点、あるいは加工の各工程等において、そこに流れて
いる物品に特有な諸事項に関する情報を把握し、それら
の情報に基づいて、輸送条件や輸送経路を適切に選択し
たり、素材や仕様に基づいて、加工条件を選択する等の
処置、判断を行なう必要があるからである。また、流通
・輸送の各拠点や加工の各工程では、それらの場所にお
いて、新たに発生する情報を追加入力する必要もある
し、その段階での情報を記録しておく必要があり、内容
を記載した粘着ラベルのコピーを保管する必要がある。2. Description of the Related Art Information management is used when goods are distributed through many routes, cargo is transported through many transportation bases, or when materials are processed by various types of processing machines. Is very important. In each route of distribution, each base of transportation, each process of processing, etc., grasp information about various items specific to the goods flowing there, and based on that information, appropriately adjust the transportation conditions and transportation routes. This is because it is necessary to perform measures and determinations, such as selection, processing conditions, etc., based on materials and specifications. In addition, at each distribution / transportation base and each processing step, it is necessary to additionally input newly generated information at those locations, and it is necessary to record information at that stage, and It is necessary to keep a copy of the self-adhesive label described.

【０００３】このため、従来は複数枚の伝票を重ねて帳
合いする事により１組の貼付用伝票（粘着ラベルでもあ
る）を作成し、最初に所定事項を記入して物品に貼り付
け、上記したような各拠点や加工の職場毎に、必要の都
度、追加記入したり、表側から１枚ずつめくって分離
し、保管する等の作業を行なっていた。[0003] For this reason, conventionally, a set of sticking slips (which is also an adhesive label) is created by stacking a plurality of slips and registering them, firstly, filling in predetermined items and sticking them to the article. At each of the sites and processing workplaces described above, additional work was performed as needed, and work was performed such as turning over one sheet from the front side, separating and storing it.

【０００４】しかし、多数枚の用紙が重ねられた伝票
は、厚みがあるため、伝票の保管時にも使用時にも不便
である上、多くは片側のみが綴じられている構造である
ため、輸送中にめくれたり、破損する事もあり、更に、
流通ルートや輸送ルートが単純なときは、用紙の一部が
不要となる等の無駄もあった。また、最近は、伝票に付
けられたバーコードを読み取ることにより、伝票に記載
された内容に頼らなくても情報の把握が可能なシステム
が出現しており、そのような場合には、流通・輸送ルー
ト、加工工程等が複雑であっても、多数枚の伝票を要し
ないことも出てきた。これとは別に、手書きによる記入
を中止し、ノンインパクトプリンターによる一括印字を
行ないたいとの要請もあり、この意味でも、多数枚の伝
票が片側のみが綴じられてる構造の従来品は扱いにくか
った。However, a slip on which a large number of sheets are stacked is thick, which is inconvenient at the time of storing and using the slip, and is often transported because it has a structure in which only one side is bound. It may be turned up or damaged,
When the distribution route and the transportation route are simple, there is a waste that a part of the paper becomes unnecessary. Recently, a system has emerged that can read information from a barcode attached to a slip without having to rely on the contents of the slip. In some cases, even if the transportation route and processing steps are complicated, a large number of slips are not required. Apart from this, there was also a request to stop handwritten entry and perform batch printing with a non-impact printer, and in this sense, conventional products with a structure in which a large number of slips are bound only on one side were difficult to handle. .

【０００５】これらの状況を踏まえて、発明者は先に、
１枚の基材を、２つの部分に分離可能に作成し、一方を
配達先の住所・氏名等を印字して物品に貼るための荷札
の部分とし、他方を配達先で受取印を押印して貰うため
の通称、「判取り」の部分としたものを提案した。この
ものを使用するときは、まず、シート全体を物品に貼り
付けて配達し、配達先において認め印を押して貰った
「判取り」の部分を分離して持ち帰るものである（特開
平９−３２７９８５号）。[0005] In view of these circumstances, the inventor has first
One base material is made to be separable into two parts, one of which is used as a part of a tag for printing the address and name of the delivery destination and pasting it to the article, and the other is stamped with a receiving stamp at the destination. He proposed what was known as the "judgment" part. When this product is used, the entire sheet is first attached to an article for delivery, and the "judgment" portion which has been stamped at the delivery destination is separated and brought back (Japanese Patent Laid-Open No. 9-327985). ).

【０００６】この配送伝票は、従来の欠点をすべて解消
するものではあるが、ただ、製品の特性上、また、製造
上、次のような問題点がある。現在、この種の伝票には
感熱プリンターを使用して印字する事が多く、伝票用紙
としては、染料を含む発色層を塗布した感熱記録紙が使
用されている。感熱プリンターを使用すると、インキ、
インキリボン、あるいはトナーのような発色のための色
材を準備しておく必要がなく、装置が単純化でき、メン
テナンスの点でも有利であるが、感熱記録紙を貼付用伝
票用として使用する際には、剥離性層、中間層、及び粘
着剤層の形成や、場合によっては印刷等の加工を施す必
要があるため、特に、剥離性層、及び中間層を形成する
際に、コーティング用の組成物やインキ組成物の中の有
機溶剤が発色層に浸透し、染料を発色させる欠点があ
り、あるいは、製造時には発色しなくても経時的に発色
し、印字の視認性を低下させるものである。そこで、現
在は、水に溶解又は分散する樹脂に限って使用し、発色
を防止しているが、水に溶解又は分散する樹脂は、種類
が限られるため、使用用途に応じて、性質の異なるもの
を使い分けることができない。また、水に溶解又は分散
した樹脂を使用し、有機溶剤を含まない組成物を調整し
て使用すると、水の蒸発潜熱が大きいために乾燥機の熱
容量を大きくする必要があり、また、乾燥時間の短縮を
図って温度を上げると、発色の恐れがある。Although this delivery slip eliminates all of the conventional disadvantages, it has the following problems in terms of the characteristics of the product and the manufacturing. At present, this type of slip is often printed using a thermal printer, and as the slip sheet, a thermosensitive recording paper coated with a coloring layer containing a dye is used. When using a thermal printer, ink,
There is no need to prepare color materials for color development such as ink ribbons or toner, which simplifies the equipment and is advantageous in terms of maintenance.However, when using thermal recording paper for pasting slips In order to form a peelable layer, an intermediate layer, and an adhesive layer, and in some cases, it is necessary to perform processing such as printing. The organic solvent in the composition or ink composition penetrates into the color-forming layer and has the disadvantage of coloring the dye, or it develops color over time without producing color at the time of manufacture, and reduces the visibility of printing. is there. Therefore, at present, it is used only for resins that dissolve or disperse in water to prevent color development.However, resins that dissolve or disperse in water are limited in type, and have different properties depending on the intended use. You can't use different things. In addition, when a resin dissolved or dispersed in water is used and a composition containing no organic solvent is adjusted and used, it is necessary to increase the heat capacity of the dryer because the latent heat of evaporation of water is large, and the drying time If the temperature is increased to shorten the color, there is a risk of color development.

【０００７】[0007]

【発明が解決しようとする課題】本発明においては、上
記のように、発色層を持つ感熱記録紙を基材として貼付
用伝票を製造する際に、有機溶剤の浸透により起こる発
色を防止し、剥離性層、及び中間層等を形成する際の樹
脂選択の範囲の広い、貼付用の粘着ラベルとその製造法
を提供する事を課題としている。In the present invention, as described above, when producing a sticking slip using a heat-sensitive recording paper having a color-forming layer as a base material, the color formation caused by the penetration of an organic solvent is prevented. An object of the present invention is to provide an adhesive label for sticking and a method for producing the same, which have a wide range of resin selections when forming a peelable layer and an intermediate layer.

【０００８】[0008]

【課題を解決するための手段】本発明においては、有機
溶剤が透過しない層を発色層に隣接して形成しておくこ
とにより、以降の各層の形成時に、有機溶剤を含む組成
物が塗布されても、組成物中の有機溶剤が浸透するのを
防止し、発色層中の染料の発色が起きないようにするこ
とができた。また、本発明においては、製造途中で加工
の都度、巻き取ると、十分乾燥していない塗膜内部の有
機溶剤が、シートが巻かれることにより、溶剤が残存し
ている層が発色層に触れるのを、有機溶剤を透過しにく
いシートを共に巻き込むことにより解消することができ
た。In the present invention, by forming a layer through which an organic solvent does not permeate adjacent to a color forming layer, a composition containing an organic solvent is applied during the subsequent formation of each layer. Even so, it was possible to prevent the organic solvent in the composition from penetrating and prevent the coloring of the dye in the coloring layer from occurring. Further, in the present invention, the organic solvent inside the coating film that has not been sufficiently dried is wound up each time processing is performed during the manufacturing process, and the layer in which the solvent remains touches the coloring layer by winding the sheet. This problem could be solved by wrapping together a sheet that hardly permeates the organic solvent.

【０００９】請求項１の発明は、表側から基材シート、
剥離性層、中間層、及び粘着剤層と、必要に応じ、剥離
性シートが記載順に積層されており、前記基材シートが
溶剤透過性のシート上に染料を含む発色層を積層したも
のであり、前記基材シートと中間層との間に溶剤不透過
層を積層してある事を特徴とする、基材が剥離可能な粘
着ラベルに関するものである。[0009] The invention according to claim 1 is a substrate sheet from the front side,
A peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer, and, if necessary, a peelable sheet is laminated in the order described, and the base sheet is formed by laminating a coloring layer containing a dye on a solvent-permeable sheet. The present invention relates to an adhesive label from which a substrate can be peeled off, wherein a solvent impermeable layer is laminated between the substrate sheet and the intermediate layer.

【００１０】請求項２の発明は、表側から基材シート、
剥離性層、中間層、及び粘着剤層と、必要に応じ、剥離
性シートが記載順に積層されており、前記基材シートが
溶剤透過性のシート上に染料を含む発色層を積層したも
のであり、前記発色層の上には、溶剤不透過層を積層し
てある事を特徴とする、基材が剥離可能な粘着ラベルに
関するものである。[0010] The invention of claim 2 provides a base material sheet from the front side,
A peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer, and, if necessary, a peelable sheet is laminated in the order described, and the base sheet is formed by laminating a coloring layer containing a dye on a solvent-permeable sheet. The present invention relates to a pressure-sensitive adhesive label from which a substrate can be peeled off, wherein a solvent-impermeable layer is laminated on the color-forming layer.

【００１１】請求項３の発明は、表側から基材シート、
剥離性層、中間層、及び粘着剤層と、必要に応じ、剥離
性シートが記載順に積層されており、前記基材シートが
溶剤透過性のシート上に染料を含む発色層を積層したも
のであり、前記基材シートと中間層との間、及び前記発
色層上の２箇所に、溶剤不透過性の層を積層してある事
を特徴とする、基材が剥離可能な粘着ラベルに関するも
のである。[0011] The invention according to claim 3 is that the substrate sheet from the front side,
A peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer, and, if necessary, a peelable sheet is laminated in the order described, and the base sheet is formed by laminating a coloring layer containing a dye on a solvent-permeable sheet. A pressure-sensitive adhesive label from which a substrate can be peeled off, wherein a solvent-impermeable layer is laminated between the substrate sheet and the intermediate layer and at two places on the color-forming layer. It is.

【００１２】請求項４の発明は、基材シートに、剥離性
層、中間層、及び粘着剤層と、必要に応じ、剥離性シー
トを積層する各工程を順次行なうに当たり、前記基材シ
ートとしては溶剤透過性のシート上に染料を含む発色層
を積層したものを用い、前記基材シートに、前記剥離性
層、及び前記中間層を順次形成した後、前記発色層に接
するように、溶剤透過性の少ないシートを重ねて一旦巻
き取り、又は折り重ね、その後、再び巻き出して以降の
工程を行なう事を特徴とする、基材が剥離可能な粘着ラ
ベルの製造法に関するものである。[0012] The invention of claim 4 is a method for laminating a peelable layer, an intermediate layer and an adhesive layer on a base sheet and, if necessary, successively laminating the peelable sheet. Using a laminate of a coloring layer containing a dye on a solvent permeable sheet, forming the release layer and the intermediate layer on the base sheet in order, and then contacting the coloring layer with a solvent. The present invention relates to a method for producing a pressure-sensitive adhesive label from which a substrate can be peeled, characterized by stacking and temporarily winding or folding a sheet having low permeability, and then unwinding the sheet and performing the subsequent steps.

【００１３】[0013]

【発明の実施の形態】BEST MODE FOR CARRYING OUT THE INVENTION

【００１４】図１は本発明の一実施例の粘着ラベルの断
面図であり、上側から、基材シート２、溶剤不透過層
３、剥離性層４、中間層５、粘着剤層６、及び剥離性シ
ート７が順に積層されたものである。ここで基材シート
は、紙等の浸透性の素材からなるシートの上面に染料を
含む発色層を形成してあるものであり、この実施例で
は、そのような基材シートに隣接する、真下に当たる位
置に、実質上、有機溶剤が透過しない、溶剤不透過層を
形成してある。このような構成とする事により、基材シ
ート２に溶剤不透過層を形成した以降は、剥離性層、中
間層等を形成する際に、それらを形成する際に使用する
組成物中の有機溶剤の浸透を防止する。FIG. 1 is a cross-sectional view of an adhesive label according to an embodiment of the present invention. From the upper side, a base sheet 2, a solvent impermeable layer 3, a peelable layer 4, an intermediate layer 5, an adhesive layer 6, and The peelable sheets 7 are sequentially laminated. Here, the base sheet is formed by forming a coloring layer containing a dye on the upper surface of a sheet made of a permeable material such as paper. A solvent-impermeable layer, which is substantially impermeable to organic solvents, is formed at a position corresponding to. With such a configuration, after forming the solvent-impermeable layer on the base sheet 2, when forming the releasable layer, the intermediate layer, and the like, the organic material in the composition used for forming them is used. Prevents solvent penetration.

【００１５】図２は、別の実施例の粘着ラベルの断面図
であり、上側から、基材シート２、剥離性層４、溶剤不
透過層３、中間層５、粘着剤層６、及び剥離性シート７
が順に積層されたものであって、図１に示したものと比
較すると、溶剤不透過層３と剥離性層４の順が入れ替わ
っている。このようにすると、中間層５以降の形成に際
して、有機溶剤の影響を回避することができる。剥離性
層４の形成は、基材シート２との密着強度を向上させる
目的で、剥離性層形成用樹脂組成物として紫外線硬化型
のような電離放射線硬化型のものを使用する場合があ
り、紫外線硬化型のものを使用するときは、有機溶剤に
よる影響はごく少ないので、そのような場合にはこの図
２に示す構造のものでもよい。FIG. 2 is a cross-sectional view of another embodiment of the pressure-sensitive adhesive label, from the top, a base sheet 2, a release layer 4, a solvent-impermeable layer 3, an intermediate layer 5, a pressure-sensitive adhesive layer 6, and a release layer. Sheet 7
Are sequentially laminated, and the order of the solvent impermeable layer 3 and the peelable layer 4 is switched as compared with that shown in FIG. In this way, the influence of the organic solvent can be avoided when forming the intermediate layer 5 and thereafter. The release layer 4 may be formed by using an ionizing radiation-curable resin such as an ultraviolet-curable resin composition as a resin composition for forming a peelable layer in order to improve the adhesive strength with the base sheet 2. When an ultraviolet-curing type is used, the influence of the organic solvent is very small. In such a case, the structure shown in FIG. 2 may be used.

【００１６】図３は、基材シートの上側に溶剤不透過層
３を形成したもので、直接、下側からの有機溶剤の浸透
を阻止する事はできないが、粘着ラベル１を、製造途中
で重ねる際には、例えば剥離性層３と中間層４を形成し
た段階で、一旦、巻き取ったり、折り重ねて保管する際
には、塗布から時間的に間もない塗膜が直接、発色層に
接触して染料が発色するのが防止できる。なお、この図
３に示す構造の場合で、一旦巻き取って、時間的にあま
り間を置かずに、次の工程に進む場合には、層３は有機
溶剤を透過しないものでなくても、透過しにくいもので
あれば、使用しうる。FIG. 3 shows a case in which a solvent impermeable layer 3 is formed on the upper side of a base sheet, and it is impossible to directly prevent the permeation of an organic solvent from the lower side. At the time of stacking, for example, once the releasable layer 3 and the intermediate layer 4 are formed, when the film is once wound up or folded and stored, the coating film that has been shortly after application is directly applied to the coloring layer. And the dye can be prevented from developing color when contacted. In the case of the structure shown in FIG. 3, when the film is wound up once and then proceeded to the next step without leaving much time, even if the layer 3 does not transmit the organic solvent, Any material that is difficult to transmit can be used.

【００１７】図４に示すものは、基材シート２の上側と
下側の両方に溶剤不透過層３、３を形成したもので、図
１を引用して説明した実施例と図３を引用して説明した
実施例の両方の要素を兼ね備えているため、効果に関し
ても両者の効果を併せ持つものである。FIG. 4 shows a structure in which solvent-impermeable layers 3, 3 are formed on both the upper and lower sides of the base material sheet 2. The embodiment described with reference to FIG. 1 and FIG. Since both of the elements of the embodiment described above are provided, the effects of the present invention are also obtained.

【００１８】図５に示すものは、基材シート２の上側と
剥離性層４の下側の２ヵ所に溶剤不透過層３、３を形成
したもので、図２を引用して説明した実施例と図３を引
用して説明した実施例の両方の要素を兼ね備えているた
め、効果に関しても両者の効果を併せ持つものである。FIG. 5 shows a structure in which solvent-impermeable layers 3 and 3 are formed at two places above the base sheet 2 and below the release layer 4, respectively. Since both elements of the example and the embodiment described with reference to FIG. 3 are provided, the effects are both obtained.

【００１９】図６に示すのは、図３を引用して説明した
ものに似ており、例えば剥離性層３と中間層４を形成し
た段階の中間製品８をそのまま巻き取ったり、折り重ね
て保管する際には、塗布から時間的に間もない塗膜が直
接、発色層に接触して染料が発色する事が避けられない
ので、単独のシート状の溶剤不透過層３を間に入れて重
ねるか、又は、中間製品８もシート状の溶剤不透過層３
も連続状のものである場合には、共に巻き取るかジグザ
グ折りのような重ね折りとすることによって、中間製品
８とシート状の溶剤不透過層３が交互に重なり合った状
態となる。この状態のものは、再び、巻き出すことによ
り以降の工程を行なうことができる。この方法は、粘着
ラベル１の構造中に溶剤不透過層３を有していない場合
にも有効であるが、図１、及び図２に示したような溶剤
不透過層３を有している場合にも有効である。なお、一
旦、このように溶剤不透過層３と交互に重ねて保管し、
あまり時間を置かずに巻き出して次の工程に進む場合に
は、図６中の層３は、有機溶剤の不透過の程度が幾分低
いものでも支障がない事もある。FIG. 6 is similar to that described with reference to FIG. 3. For example, the intermediate product 8 at the stage where the releasable layer 3 and the intermediate layer 4 are formed is wound up or folded as it is. When storing, it is unavoidable that the coating film, which has just been applied for a short time, comes into direct contact with the coloring layer and the dye develops color. Or the intermediate product 8 is also a sheet-like solvent-impermeable layer 3
Is also continuous, the intermediate product 8 and the sheet-like solvent-impermeable layer 3 are alternately overlapped with each other by winding them together or by folding them in a zigzag manner. In this state, the subsequent steps can be performed by unwinding again. This method is effective even when the solvent-impermeable layer 3 is not provided in the structure of the pressure-sensitive adhesive label 1, but has the solvent-impermeable layer 3 as shown in FIGS. 1 and 2. It is also effective in cases. In addition, once it is stored alternately with the solvent impermeable layer 3 as described above,
When unwinding and proceeding to the next step without leaving much time, the layer 3 in FIG. 6 may have no problem even if the degree of impermeability of the organic solvent is somewhat low.

【００２０】基材シート２の役目は色々であるが、例え
ば、物品に貼付けられた際に、配達先に関する情報が印
字された荷札としての機能を持つ事であり、あるいは、
物品の分類、仕分けのためのラベルとしての役目を持つ
事もある。基材シート２の表側には、これらの役目の場
合であれば、依頼日、配達先の住所・氏名、発送元の住
所・氏名、内容物等の情報を印字又は手書きするための
記入欄や項目等が予めオフセット印刷等の印刷方式によ
り印刷されており、ラベル毎にバーコードや一連番号を
印刷して１つの案件毎の固有の番号を付けておけば、バ
ーコードリーダーにより読み取って、詳しい情報を照会
したり、取り扱った事を記録することもできる。荷札以
外の用途の場合には、貼る目的にもよるが、日付、大分
類・中分類・小分類などの分類の記号の欄、その後の取
扱い（単価の割引や無償提供、セット販売、景品として
の使用等、）を記入する記入欄が予め印刷されている。The role of the base sheet 2 is various. For example, when the base sheet 2 is attached to an article, it has a function as a tag on which information on a delivery destination is printed.
It may also serve as a label for classifying and sorting goods. On the front side of the base sheet 2, in the case of these roles, an entry column for printing or handwriting information such as a request date, an address and name of a delivery destination, an address and name of a shipping source, contents, etc. Items are printed in advance by a printing method such as offset printing. If a bar code or a serial number is printed for each label and a unique number is assigned to each case, it can be read by a bar code reader and read in detail. You can also refer to information and record what you have done. In the case of applications other than tags, depending on the purpose of pasting, depending on the purpose of pasting, date, symbol column of classification such as major classification, middle classification, small classification, etc., and subsequent handling (discount of unit price, free provision, set sale, premium , Etc.) is pre-printed.

【００２１】基材シート２は又、配達先に届けられた際
に、予め剥離しておくか、受取りの確認のための押印を
受けた後に剥離して、配達業者や取り扱った人が回収す
る部分とする事もできる。このように、受取り確認のた
めの押印をして貰う場合は、「判取り」と通称される。
「判取り」としても使用するときは、基材シート２の表
側には、受取印を押す押印欄を設けておく事が望まし
い。The base sheet 2 is also peeled off when it is delivered to the delivery destination, or is peeled off after receiving a seal for confirming receipt, and is collected by a delivery company or a person who has handled it. It can also be a part. In this manner, the case where the seal is received for confirmation of receipt is generally called "judgment".
When it is used also as a “reading”, it is desirable to provide an imprint column for pressing a receiving stamp on the front side of the base sheet 2.

【００２２】基材シート２は、本発明の粘着ラベルの本
体を構成するもので、配送伝票等として使用する場合に
は、上質紙等の紙が使われる事が普通だが、感熱紙、感
圧紙等の機能を持った機能紙を使用用途によって使い分
けるとよい。本発明においては、基材シート２は、溶剤
透過性のある基材、例えば紙に、ロイコ染料と酸性顕色
剤の２成分系等の、染料前駆体を含む発色層が塗布ない
し積層されたものを使用する。このような発色層中の染
料前駆体は溶剤の存在により顕色剤と接触して反応し、
発色する性質を持っている。印字や手書き、押印等の様
々な情報記録の手法が適用されるので、これらの手法が
適用されたときに文字が滲んだり、弾かれたりする事の
無いよう、基材シート２の素材としては、印字適性、筆
記適性、または捺印適性を備えたものを選んで使用する
とよい。印刷した項目や欄を見えやすくする意味で、基
材シート２としては下地隠蔽性があるものが好ましく、
色彩は特に問わないものの、使いやすさから言えば、白
色か、他の色であっても淡色で、明度の高いものが好ま
しい。The base sheet 2 constitutes the main body of the pressure-sensitive adhesive label of the present invention. When used as a delivery slip or the like, paper such as high-quality paper is usually used. It is preferable to use functional paper having functions such as the above depending on the intended use. In the present invention, the base sheet 2 is formed by coating or laminating a color-forming layer containing a dye precursor, such as a two-component leuco dye and an acidic developer, on a solvent-permeable base material, for example, paper. Use things. The dye precursor in such a color forming layer reacts by contacting with the color developer due to the presence of the solvent,
It has the property of coloring. Since various information recording methods such as printing, handwriting, and stamping are applied, as a material of the base sheet 2, characters are not blurred or flicked when these methods are applied. It is preferable to select a material having printability, writing suitability, or sealability. In order to make printed items and columns easy to see, it is preferable that the base sheet 2 has a base concealing property,
The color is not particularly limited, but in terms of ease of use, it is preferable that the color be white or other colors that are light and have high brightness.

【００２３】基材シート２には、基材シート２の一部を
分離するため、ミシン目等を形成してもよい。ミシン目
等とは、ミシン目のほか、ハーフカット、又は筋押し等
も含むものとする。ミシン目等を形成する位置、形成す
る箇所の数、ミシン目等によって区画する形状は任意で
ある。また、ミシン目等を形成する際の深さは、基材シ
ート２を確実に分離する意味で、基材シート２を貫通し
て、少なくとも剥離性層４に到達する深さである事が望
ましい。A perforation or the like may be formed on the base sheet 2 in order to separate a part of the base sheet 2. Perforations and the like include not only perforations but also half cuts or creasing. The positions where the perforations and the like are formed, the number of locations to be formed, and the shape defined by the perforations and the like are arbitrary. Further, it is desirable that the depth at which the perforations and the like are formed is a depth that penetrates the base sheet 2 and reaches at least the peelable layer 4 in order to surely separate the base sheet 2. .

【００２４】溶剤不透過層３は、一般的なコーティング
用樹脂組成物中に溶剤として含まれるトルエン、キシレ
ン等の芳香族炭化水素、メチルエチルケトン、メチルイ
ソブチルケトン等のケトン類等、比較的極性の低い有機
溶剤に溶解しない樹脂を選んで作成した樹脂組成物を使
用して形成する。例えば、ポリアクリルアミド、ポリア
クリル酸、ポリアクリロニトリル、ポリアミド、ポリビ
ニルアセタール、ポリビニルピロリドン等の有機高分子
化合物、シリコーン樹脂等を含浸したグラシン紙、熱硬
化性や電離放射線硬化性の樹脂が硬化したもの、金属
箔、ポリエステル樹脂フィルム等がある。これらは、直
接、基材シート２に、あるいは基材シート２に形成され
た剥離性層４に直接塗布して形成するか、あるいは、一
旦、別の一時的キャリヤの上に塗布し、乾燥させて乾燥
して皮膜を得てから、その皮膜のみを接着剤を介して貼
る等の方法が採れる。The solvent-impermeable layer 3 has a relatively low polarity, such as aromatic hydrocarbons such as toluene and xylene and ketones such as methyl ethyl ketone and methyl isobutyl ketone which are contained as solvents in a general coating resin composition. It is formed using a resin composition prepared by selecting a resin that does not dissolve in an organic solvent. For example, polyacrylamide, polyacrylic acid, polyacrylonitrile, polyamide, polyvinyl acetal, organic polymer compounds such as polyvinylpyrrolidone, glassine paper impregnated with silicone resin, etc., thermosetting or ionizing radiation curable resin cured, There are metal foil, polyester resin film and the like. These are formed by directly applying to the base sheet 2 or to the peelable layer 4 formed on the base sheet 2 or by applying the coating once on another temporary carrier and drying. After drying to obtain a film, a method such as attaching only the film via an adhesive can be employed.

【００２５】中間層５は、基材シート２の裏側の面に粘
着剤層６を設けるのに先立ち、基材シートの裏側の表面
を調整する意味で設けられると同時に、基材シート２と
中間層５との間に設けられた剥離性層４との間の剥離
性、言い換えれば、必要な程度の弱い接着力を安定に維
持するための役割を持ち、なおかつ、場合によっては、
印刷層（図示せず）を形成する際の印刷対象としての役
割も持っている。また、中間層５は、基材シート２を剥
離性層４ごと剥離した後に、粘着剤層６が露出してベタ
付くのを防止する役割も持っている。The intermediate layer 5 is provided to adjust the back surface of the base sheet 2 prior to providing the pressure-sensitive adhesive layer 6 on the back surface of the base sheet 2, and at the same time, the intermediate layer 5 Has a role to stably maintain the releasability between the releasable layer 4 and the releasable layer 4 provided between the layer 5 and, in other words, a necessary weak adhesive force, and in some cases,
It also has a role as a printing target when forming a printing layer (not shown). The intermediate layer 5 also has a role of preventing the pressure-sensitive adhesive layer 6 from being exposed and sticking after the base sheet 2 is peeled off together with the peelable layer 4.

【００２６】実際の中間層５は、合成樹脂等のコーティ
ングないし印刷による層である。中間層４の形成に使用
される合成樹脂としては、ポリエステル樹脂、ポリウレ
タン樹脂等のウレタン系樹脂、アクリル系樹脂、酢酸ビ
ニル共重合樹脂、又はポリビニルアルコール樹脂等の熱
可塑性樹脂。ＮＲ、ＳＢＲ等の天然ゴム又は合成ゴム、
ＰＶＡ−ＬＡ（ポリビニルアルコール−長鎖アルキルイ
ソシアネート付加物）又はエポキシ等の熱硬化性樹脂等
が挙げられ、これらは単独もしくは混合して使用し、あ
るいはさらに、必要に応じ、硬化剤、架橋剤、顔料など
の添加されたものを使用する。The actual intermediate layer 5 is a layer formed by coating or printing a synthetic resin or the like. The synthetic resin used for forming the intermediate layer 4 is a urethane-based resin such as a polyester resin or a polyurethane resin, an acrylic resin, a vinyl acetate copolymer resin, or a thermoplastic resin such as a polyvinyl alcohol resin. NR, natural rubber such as SBR or synthetic rubber,
Thermosetting resins such as PVA-LA (polyvinyl alcohol-long chain alkyl isocyanate adduct) or epoxy, etc., may be used alone or in combination, or, if necessary, a curing agent, a crosslinking agent, A pigment or the like is used.

【００２７】印刷層（図示せず）は、基材シート２によ
り隠蔽されているが、基材シート２を剥離性層４と共に
剥離してしまうと、中間層５が最上層になり、中間層５
は、大抵、樹脂を主成分として構成されるために、透明
である。従って、中間層５の下層に印刷層を積層すると
上から見る事ができる。基材シートを剥がした後に必要
となる情報は、伝票の役割が済んだ後に必要な事項であ
って、例えば、各伝票に共通な問い合わせ先、内容物に
関する注意、輸送会社や発送元の会社の配達先への謝辞
等がある。印刷層の印刷は、印刷したのとは反対の側か
ら見るので、左右が逆になった逆像の印刷用版を使用し
て印刷する必要がある。The printing layer (not shown) is concealed by the base sheet 2, but when the base sheet 2 is peeled off together with the release layer 4, the intermediate layer 5 becomes the uppermost layer, 5
Is usually composed mainly of resin, and is therefore transparent. Therefore, when a printing layer is laminated below the intermediate layer 5, it can be seen from above. The information required after peeling the base sheet is necessary after the role of the voucher has been completed.For example, common inquiries for each voucher, precautions regarding contents, transportation company and shipping company There is an acknowledgment to the delivery destination. Since the printing of the printing layer is viewed from the side opposite to the side on which the printing was performed, it is necessary to print using a reversed image printing plate in which the left and right are reversed.

【００２８】剥離性層４及び必要に応じ形成する印刷層
５は、好ましくは、電離放射線硬化性樹脂組成物を使用
して塗布又は印刷により適用され、適用後に電離放射線
の照射を受けて硬化させられる。電離放射線硬化性樹脂
組成物としては、分子中に重合性不飽和結合または、エ
ポキシ基を有するプレポリマー、オリゴマー、及び／又
はモノマーを適宜に混合したものである。電離放射線と
は、電磁波又は荷電粒子線のうち分子を重合又は架橋し
得るエネルギー量子を有するものを指し、通常は、紫外
線又は電子線を用いる。The releasable layer 4 and the optional printed layer 5 are preferably applied by coating or printing using an ionizing radiation-curable resin composition, and after application, cured by irradiation with ionizing radiation. Can be The ionizing radiation-curable resin composition is obtained by appropriately mixing a prepolymer, an oligomer, and / or a monomer having a polymerizable unsaturated bond or an epoxy group in a molecule. Ionizing radiation refers to electromagnetic waves or charged particle beams having energy quanta that can polymerize or crosslink molecules, and usually use ultraviolet rays or electron beams.

【００２９】電離放射線硬化性樹脂組成物中のプレポリ
マー、オリゴマーの例としては、不飽和ジカルボン酸と
多価アルコールの縮合物等の不飽和ポリエステル類、ポ
リエステルメタクリレート、ポリエーテルメタクリレー
ト、ポリオールメタクリレート、メラミンメタクリレー
ト等のメタクリレート類、ポリエステルアクリレート、
エポキシアクリレート、ウレタンアクリレート、ポリエ
ーテルアクリレート、ポリオールアクリレート、メラミ
ンアクリレート等のアクリレート、カチオン重合型エポ
キシ化合物が挙げられる。Examples of prepolymers and oligomers in the ionizing radiation-curable resin composition include unsaturated polyesters such as condensates of unsaturated dicarboxylic acids and polyhydric alcohols, polyester methacrylates, polyether methacrylates, polyol methacrylates, melamines. Methacrylates such as methacrylate, polyester acrylate,
Examples include acrylates such as epoxy acrylate, urethane acrylate, polyether acrylate, polyol acrylate, and melamine acrylate, and cationic polymerization type epoxy compounds.

【００３０】電離放射線硬化性樹脂組成物中のモノマー
の例としては、スチレン、α−メチルスチレン等のスチ
レン系モノマー、アクリル酸メチル、アクリル酸−２−
エチルヘキシル、アクリル酸メトキシエチル、アクリル
酸ブトキシエチル、アクリル酸ブチル、アクリル酸メト
キシブチル、アクリル酸フェニル等のアクリル酸エステ
ル類、メタクリル酸メチル、メタクリル酸エチル、メタ
クリル酸プロピル、メタクリル酸メトキシエチル、メタ
クリル酸エトキシメチル、メタクリル酸フェニル、メタ
クリル酸ラウリル等のメタクリル酸エステル類、アクリ
ル酸−２−（Ｎ，Ｎ−ジエチルアミノ）エチル、アクリ
ル酸−２−（Ｎ，Ｎ−ジメチルアミノ）エチル、アクリ
ル酸−２−（Ｎ，Ｎ−ジベンジルアミノ）メチル、アク
リル酸−２−（Ｎ，Ｎ−ジエチルアミノ）プロピル等の
不飽和置換の置換アミノアルコールエステル類、アクリ
ルアミド、メタクリルアミド等の不飽和カルボン酸アミ
ド、エチレングリコールジアクリレート、プロピレング
リコールジアクリレート、ネオペンチルグリコールジア
クリレート、１，６−ヘキサンジオールジアクリレー
ト、トリエチレングリコールジアクリレート等の化合
物、ジプロピレングリコールジアクリレート、エチレン
グリコールジアクリレート、プロピレングリコールジメ
タクリレート、ジエチレングリコールジメタクリレート
等の多官能性化合物、及び／又は分子中に２個以上のチ
オール基を有するポリチオール化合物、例えばトリメチ
ロールプロパントリチオグリコレート、トリメチロール
プロパントリチオプロピレート、ペンタエリスリトール
テトラチオグリコレート等が挙げられる。Examples of the monomer in the ionizing radiation-curable resin composition include styrene monomers such as styrene and α-methylstyrene, methyl acrylate, and acrylic acid-2-
Acrylic esters such as ethylhexyl, methoxyethyl acrylate, butoxyethyl acrylate, butyl acrylate, methoxybutyl acrylate, phenyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, methoxyethyl methacrylate, methacrylic acid Methacrylic esters such as ethoxymethyl, phenyl methacrylate and lauryl methacrylate; 2- (N, N-diethylamino) ethyl acrylate; 2- (N, N-dimethylamino) ethyl acrylate; -2 acrylic acid -(N, N-dibenzylamino) methyl, unsaturated substituted substituted alcoholic esters such as 2- (N, N-diethylamino) propyl acrylate, unsaturated carboxylic acid amides such as acrylamide and methacrylamide, ethylene Guri Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, 1,6-hexanediol diacrylate, triethylene glycol diacrylate, and other compounds, dipropylene glycol diacrylate, ethylene glycol diacrylate, propylene glycol dimethacrylate, diethylene glycol Polyfunctional compounds such as dimethacrylate and / or polythiol compounds having two or more thiol groups in the molecule, such as trimethylolpropane trithioglycolate, trimethylolpropane trithiopropylate, pentaerythritol tetrathioglycolate, etc. Is mentioned.

【００３１】通常、電離放射線硬化性樹脂組成物中のモ
ノマーとしては、以上の化合物を必要に応じて１種若し
くは２種以上を混合して用いるが、電離放射線硬化性樹
脂組成物に通常の塗布適性を与えるために、前記のプレ
ポリマー又はオリゴマーを５重量％以上、前記モノマー
及び／又はポリチオール化合物を９５重量％以下とする
のが好ましい。Usually, as the monomer in the ionizing radiation-curable resin composition, one or a mixture of two or more of the above compounds is used as necessary. In order to provide suitability, it is preferable that the content of the prepolymer or oligomer is 5% by weight or more and the content of the monomer and / or polythiol compound is 95% by weight or less.

【００３２】電離放射線硬化性樹脂組成物を塗布し、硬
化させたときのフレキシビリティーが要求されるとき
は、モノマー量を減らすか、官能基の数が１又は２のア
クリレートモノマーを使用するとよい。電離放射線硬化
性樹脂組成物を塗布し、硬化させたときの耐摩耗性、耐
熱性、耐溶剤性が要求されるときは、官能基の数が３つ
以上のアクリレートモノマーを使う等、電離放射線硬化
性樹脂組成物の設計が可能である。ここで、官能基が１
のものとして、２−ヒドロキシアクリレート、２−ヘキ
シルアクリレート、フェノキシエチルアクリレートが挙
げられる。官能基が２のものとして、エチレングリコー
ルジアクリレート、１，６−ヘキサンジオールジアクリ
レートが挙げられる。官能基が３以上のものとして、ト
リメチロールプロパントリアクリレート、ペンタエリス
リトールトリアクリレート、ペンタエリスリトールテト
ラアクリレート、ジペンタエリスリトールヘキサアクレ
リート等が挙げられる。When flexibility is required when the ionizing radiation-curable resin composition is applied and cured, the amount of the monomer may be reduced or an acrylate monomer having one or two functional groups may be used. . When abrasion resistance, heat resistance, and solvent resistance when applying and curing an ionizing radiation-curable resin composition are required, use ionizing radiation such as using an acrylate monomer having three or more functional groups. It is possible to design a curable resin composition. Here, the functional group is 1
Examples thereof include 2-hydroxyacrylate, 2-hexyl acrylate, and phenoxyethyl acrylate. Examples of those having two functional groups include ethylene glycol diacrylate and 1,6-hexanediol diacrylate. Examples of the compound having three or more functional groups include trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, and dipentaerythritol hexaacrylate.

【００３３】電離放射線硬化性樹脂組成物を塗布し、硬
化させたときのフレキシビリティーや表面硬度等の物性
を調整するため、電離放射線硬化性樹脂組成物に、電離
放射線照射では硬化しない樹脂を添加することもでき
る。具体的な樹脂の例としては次のものがある。ポリウ
レタン樹脂、セルロース樹脂、ポリビニルブチラール樹
脂、ポリエステル樹脂、アクリル樹脂、ポリ塩化ビニル
樹脂、ポリ酢酸ビニル等の熱可塑性樹脂である。中で
も、ポリウレタン樹脂、セルロース樹脂、ポリビニルブ
チラール樹脂等の添加がフレキシビリティーの向上の点
で好ましい。In order to adjust physical properties such as flexibility and surface hardness when the ionizing radiation-curable resin composition is applied and cured, a resin which is not cured by ionizing radiation irradiation is added to the ionizing radiation-curable resin composition. It can also be added. Examples of specific resins include the following. Thermoplastic resins such as polyurethane resin, cellulose resin, polyvinyl butyral resin, polyester resin, acrylic resin, polyvinyl chloride resin, and polyvinyl acetate. Above all, addition of a polyurethane resin, a cellulose resin, a polyvinyl butyral resin or the like is preferable from the viewpoint of improving flexibility.

【００３４】電離放射線硬化性樹脂組成物の塗布後の硬
化が紫外線照射により行われるときは、光重合開始剤や
光重合促進剤を添加する。光重合開始剤としては、ラジ
カル重合性不飽和基を有する樹脂系の場合は、アセトフ
ェノン類、ベンゾフェノン類、チオキサントン類、ベン
ゾイン、ベンゾインメチルエーテル等を単独又は混合し
て用いる。また、カチオン重合性官能基を有する樹脂系
の場合は、光重合開始剤として、芳香族ジアゾニウム
塩、芳香族スルホニウム塩、芳香族ヨードニウム塩、メ
タセロン化合物、ベンゾインスルホン酸エステル等を単
独又は混合物として用いる。光重合開始剤の添加量は、
電離放射線硬化性樹脂組成物１００重量部に対し、０．
１〜１０重量部である。When the ionizing radiation-curable resin composition is cured by ultraviolet irradiation after application, a photopolymerization initiator or a photopolymerization accelerator is added. As the photopolymerization initiator, in the case of a resin system having a radically polymerizable unsaturated group, acetophenones, benzophenones, thioxanthones, benzoin, benzoin methyl ether or the like is used alone or as a mixture. In the case of a resin system having a cationically polymerizable functional group, an aromatic diazonium salt, an aromatic sulfonium salt, an aromatic iodonium salt, a metaceron compound, a benzoin sulfonic acid ester, or the like is used alone or as a mixture as a photopolymerization initiator. . The addition amount of the photopolymerization initiator,
0.1 parts by weight based on 100 parts by weight of the ionizing radiation-curable resin composition.
It is 1 to 10 parts by weight.

【００３５】粘着剤層６は、粘着ラベル１を物品に貼る
ためのもので、中間層５に直接、あるいは、印刷層があ
るときは、印刷層を介して中間層５と接着している。具
体的な粘着剤層６の素材は、一般的な（メタ）アクリル
酸エステル系、もしくは酢酸ビニル樹脂などの合成樹
脂、又はＳＢＲなどのゴム系のものである。粘着剤層６
は一回限りの使用のためのものと、接着・剥離が何回も
可能としたものがある。後者は、粘着ラベルを数回貼っ
たり剥がしたりする用途に合わせたもので、例えば、最
初は、個々の注文に応じて物品に粘着ラベルを貼り、次
に、同じ輸送経路や同じ配達先のものを集め、１個又は
数個の荷姿に改めて包装し直すような場合に、一旦貼っ
たラベルを剥がし、他に貼り直す必要があるからであ
る。The pressure-sensitive adhesive layer 6 is for attaching the pressure-sensitive adhesive label 1 to an article, and is adhered to the intermediate layer 5 directly on the intermediate layer 5 or, if there is a print layer, via the print layer. A specific material of the pressure-sensitive adhesive layer 6 is a general (meth) acrylate ester-based material, a synthetic resin such as a vinyl acetate resin, or a rubber-based material such as SBR. Adhesive layer 6
Some are for one-time use, while others are capable of bonding and peeling many times. The latter is tailored for applications where the adhesive label is to be applied and peeled several times, for example, first applying the adhesive label to the goods according to the individual order, then to the same transport route or the same destination This is because when collecting and repacking one or several packages, it is necessary to peel off the label once applied and reapply it to another.

【００３６】剥離性シート７は、粘着剤層６に積層され
ていて、ラベルを物品に貼るまでの間、粘着剤層６を保
護し、かつ、粘着剤層６が不用意に他の物品に貼りつく
のを防止するものである。剥離性シート７としては、ポ
リエチレンのような接着性の低いポリオレフィン系等の
プラスチックフィルムや、紙の表面にシリコーン樹脂や
ワックスをコーティングして剥離性層を設けたシートを
選択して使用さればよいが、剥離性シートの粘着剤層に
積層するのとは反対側に印刷する場合は、印刷適性をも
考慮して選択する。The peelable sheet 7 is laminated on the pressure-sensitive adhesive layer 6 to protect the pressure-sensitive adhesive layer 6 until the label is attached to the article, and the pressure-sensitive adhesive layer 6 is inadvertently applied to another article. This is to prevent sticking. As the releasable sheet 7, a plastic film such as a polyethylene having low adhesiveness such as polyethylene or a sheet having a releasable layer provided by coating a silicone resin or wax on the surface of paper may be used. However, when printing is performed on the side of the peelable sheet opposite to the side where it is laminated on the pressure-sensitive adhesive layer, it is selected in consideration of printability.

【００３７】以上に説明した本発明の粘着ラベルは、基
材シート２の表皺に印字し、剥離性シート７を剥がして
物品に貼り付け、粘着ラベルの役割が概ね終わった時点
で基材シート２を剥離性層４と共に剥離して回収するも
のである。The pressure-sensitive adhesive label of the present invention described above is printed on the surface wrinkles of the substrate sheet 2, the peelable sheet 7 is peeled off and attached to an article. 2 is peeled and collected together with the peelable layer 4.

【００３８】[0038]

【発明の効果】請求項１の発明によれば、基材シートと
中間層との間に溶剤不透過層を積層してあるため、中間
層以降の層を形成する際の、層形成用樹脂組成物中の有
機溶剤の影響による発色層の発色が防止でき、従って、
中間層以降の層を形成する際に水溶性や水分散性の樹脂
を使用しなければならない制約がない。According to the first aspect of the present invention, since the solvent impermeable layer is laminated between the base sheet and the intermediate layer, the resin for forming the layer when forming the layers after the intermediate layer is formed. The coloring of the coloring layer due to the influence of the organic solvent in the composition can be prevented, and therefore,
There is no restriction that a water-soluble or water-dispersible resin must be used when forming a layer after the intermediate layer.

【００３９】請求項２の発明によれば、基材シートの発
色層の上に溶剤不透過層を積層してあるため、生産途中
において、折り重ねたり、巻き取ったりしたときに、直
前に形成して層中の有機溶剤が発色層に触れることを避
けることができ、発色の防止ができる。According to the second aspect of the present invention, since the solvent-impermeable layer is laminated on the coloring layer of the base sheet, it is formed immediately before folding or winding up during production. As a result, the organic solvent in the layer can be prevented from touching the color forming layer, and the color formation can be prevented.

【００４０】請求項３の発明によれば、基材シートと中
間層との間、及び前記発色層上の２箇所に、溶剤不透過
層を積層してあるため、請求項１の発明の効果と、請求
項２の発明の効果が併せて発揮される。According to the third aspect of the present invention, the solvent impermeable layer is laminated between the base sheet and the intermediate layer and at two places on the color forming layer. And the effect of the invention of claim 2 is also exhibited.

【００４１】請求項４の発明によれば、粘着ラベルの製
造の際に、中間層を形成した、製造の途中の段階で、溶
剤透過性の少ないシートを重ねて巻き取るか、又は折り
重ねるため、直前に形成して層中の有機溶剤が発色層に
触れることを避けることができ、発色の防止ができる。According to the fourth aspect of the present invention, in the production of the pressure-sensitive adhesive label, the intermediate layer is formed, and in the middle of the production, the sheets having low solvent permeability are rolled up or rolled up or folded. In addition, it is possible to prevent the organic solvent in the layer formed immediately before from touching the color-forming layer, thereby preventing color formation.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の粘着ラベルの模式的な断面図である。FIG. 1 is a schematic sectional view of the pressure-sensitive adhesive label of the present invention.

【図２】本発明の粘着ラベルの模式的な断面図である。FIG. 2 is a schematic sectional view of the pressure-sensitive adhesive label of the present invention.

【図３】本発明の粘着ラベルの模式的な断面図である。FIG. 3 is a schematic sectional view of the pressure-sensitive adhesive label of the present invention.

【図４】本発明の粘着ラベルの模式的な断面図である。FIG. 4 is a schematic sectional view of the pressure-sensitive adhesive label of the present invention.

【図５】本発明の粘着ラベルの模式的な断面図である。FIG. 5 is a schematic sectional view of the pressure-sensitive adhesive label of the present invention.

【図６】本発明の粘着ラベルの製造法を示す図である。FIG. 6 is a diagram showing a method for producing the pressure-sensitive adhesive label of the present invention.

【符号の説明】[Explanation of symbols]

１ 粘着ラベル ２ 基材シート ３ 溶剤不透過層 ４ 剥離性層 ５ 中間層 ６ 粘着剤層 ７ 剥離性シート DESCRIPTION OF SYMBOLS 1 Adhesive label 2 Base sheet 3 Solvent impermeable layer 4 Releasable layer 5 Intermediate layer 6 Adhesive layer 7 Releasable sheet

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 表側から基材シート、剥離性層、中間
層、及び粘着剤層と、必要に応じ、剥離性シートが記載
順に積層されており、前記基材シートが溶剤透過性のシ
ート上に染料を含む発色層を積層したものであり、前記
基材シートと中間層との間に溶剤不透過層を積層してあ
る事を特徴とする、基材が剥離可能な粘着ラベル。1. A substrate sheet, a releasable layer, an intermediate layer, and an adhesive layer, and a releasable sheet, if necessary, are laminated in this order from the front side, and the substrate sheet is formed on a solvent-permeable sheet. A pressure-sensitive adhesive label, wherein a solvent-impermeable layer is laminated between the substrate sheet and the intermediate layer, wherein the substrate is peelable. 【請求項２】 表側から基材シート、剥離性層、中間
層、及び粘着剤層と、必要に応じ、剥離性シートが記載
順に積層されており、前記基材シートが溶剤透過性のシ
ート上に染料を含む発色層を積層したものであり、前記
発色層の上には、溶剤不透過層を積層してある事を特徴
とする、基材が剥離可能な粘着ラベル。2. A substrate sheet, a peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer, and if necessary, a peelable sheet are laminated in the stated order from the front side, and the substrate sheet is formed on a solvent-permeable sheet. A pressure-sensitive adhesive label from which a substrate is peelable, wherein a color-forming layer containing a dye is laminated on the color-forming layer, and a solvent-impermeable layer is laminated on the color-forming layer. 【請求項３】 表側から基材シート、剥離性層、中間
層、及び粘着剤層と、必要に応じ、剥離性シートが記載
順に積層されており、前記基材シートが溶剤透過性のシ
ート上に染料を含む発色層を積層したものであり、前記
基材シートと中間層との間、及び前記発色層上の２箇所
に、溶剤不透過層を積層してある事を特徴とする、基材
が剥離可能な粘着ラベル。3. A substrate sheet, a peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer, and if necessary, a peelable sheet are laminated in this order from the front side, and the base sheet is formed on a solvent-permeable sheet. Wherein a solvent-impermeable layer is laminated between the base sheet and the intermediate layer and at two places on the color developing layer. Adhesive label that can be peeled off 【請求項４】 基材シートに、剥離性層、中間層、及び
粘着剤層と、必要に応じ、剥離性シートを積層する各工
程を順次行なうに当たり、前記基材シートとしては溶剤
透過性のシート上に染料を含む発色層を積層したものを
用い、前記基材シートに、前記剥離性層、及び前記中間
層を順次形成した後、前記発色層に接するように、溶剤
透過性の少ないシートを重ねて一旦巻き取り、又は折り
重ね、その後、再び巻き出して以降の工程を行なう事を
特徴とする、基材が剥離可能な粘着ラベルの製造法。4. When sequentially performing each step of laminating a peelable layer, an intermediate layer, and a pressure-sensitive adhesive layer on a base sheet and, if necessary, a peelable sheet, the base sheet has a solvent-permeable property. Using a laminate of a coloring layer containing a dye on a sheet, and forming the release layer, and the intermediate layer on the base sheet in order, and then contacting the coloring layer, a sheet having a low solvent permeability. A method for producing a pressure-sensitive adhesive label from which a substrate can be peeled off, characterized in that: