JP2000052527A - Decorative material and its preparation - Google Patents

Decorative material and its preparation

Info

Publication number
JP2000052527A
JP2000052527A JP10226830A JP22683098A JP2000052527A JP 2000052527 A JP2000052527 A JP 2000052527A JP 10226830 A JP10226830 A JP 10226830A JP 22683098 A JP22683098 A JP 22683098A JP 2000052527 A JP2000052527 A JP 2000052527A
Authority
JP
Japan
Prior art keywords
layer
pattern
decorative material
synthetic resin
coating material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP10226830A
Other languages
Japanese (ja)
Inventor
Hisashi Takii
尚志 滝井
Shigenori Toda
重憲 戸田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YAMAMOTO YOGYO KAKO KK
Original Assignee
YAMAMOTO YOGYO KAKO KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YAMAMOTO YOGYO KAKO KK filed Critical YAMAMOTO YOGYO KAKO KK
Priority to JP10226830A priority Critical patent/JP2000052527A/en
Publication of JP2000052527A publication Critical patent/JP2000052527A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a plane decorative material with a pattern rich in graveness and depth and with high grade feeling and a method for preparing it. SOLUTION: This material has a metamorphic rock tone pattern consisting of the third layer 3 consisting of a synthetic resin layer prepd. by dispersing aggregate on a sheet base material, the second layer 2 which is a synthetic resin layer prepd. by dispersing aggregates covering the surface and whose surface pattern is formed of at least two kinds of the above described synthetic resin layers 2a and 2b with different color tones and the first layer 1 which is a synthetic resin layer wherein aggregates are dispersed and has a different color tone from the second layer 2 and covers discontinuously the surface of the second layer 2 to form a surface pattern and wherein at least a part of the lower part enters into the second layer 2 and wherein parts exposed on the surface of the second layers 2 (2a and 2b) and the surface of the first layer 1 are flat and form approximately the same plane.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、建築物の内外装壁
面或は床面や構築物の表面の装飾用として、重厚さ、深
みに富んだ模様、好ましくは変成岩調模様を有する装飾
材ならびにその製造方法に関する。BACKGROUND OF THE INVENTION The present invention relates to a decorative material having a heavy and deep pattern, preferably a metamorphic rock pattern, and a decorative material for decoration of an interior / exterior wall or floor of a building or a surface of the building. It relates to a manufacturing method.

【０００２】[0002]

【従来の技術】合成樹脂エマルションと大理石粉末その
他の骨材や着色硅砂あるいは有色陶磁器粉などの着色骨
材などの骨材を含む塗布材（吹付材とも言われている）
を合成繊維やガラス繊維あるいはその他の無機繊維から
なる寒冷紗や不織布その他の布帛類や適宜の固体基材上
に吹付け等適宜の方法により塗布して天然石調の模様を
施した装飾材は建築物の内外装壁面或は床面の装飾用な
ど建築物表面仕上用シートとして用いられている。（特
開平４−７６１５１号、特開平３−２７９５６１号）。
一般に吹き付けガンにより２色または３色吹きで、御影
石調の模様を発現したものなどが装飾材として知られて
いるが、表面が凹凸状のものであり、表面が平坦で、重
厚な美しい模様を有するものではない。2. Description of the Related Art Coating materials containing aggregates such as synthetic resin emulsions and marble powder and other aggregates and colored aggregates such as colored silica sand or colored ceramic powder (also called spraying materials).
Is applied to a cold gauze made of synthetic fiber, glass fiber or other inorganic fiber, a non-woven fabric or other fabrics or an appropriate solid substrate by an appropriate method such as spraying to give a natural stone-like decorative material. It is used as a sheet for finishing the surface of a building, such as for decoration of an interior / exterior wall surface or a floor surface. (JP-A-4-76151, JP-A-3-279561).
Generally, two or three colors sprayed with a spray gun and a granite-like pattern is known as a decorative material, but the surface is uneven and the surface is flat and has a heavy and beautiful pattern. Not something.

【０００３】天然に産する変成岩は、水成岩や火成岩
が、地下の深いところで熱や圧力、変成作用によって鉱
物組成や組織が変化して生成した岩石であり、大理石、
片麻岩、結晶片岩、圧砕岩（マイロナイト）、蛇紋岩な
どが知られている。大理石は、石灰岩が地殻の変動やマ
グマの熱によって変性作用を受け再結晶したもので、石
灰岩の含有成分やその変成作用の状態で種々の大理石と
なることが知られている。片麻岩は、粗粒で、鉱物組成
の異なる薄層が重なり合っている変成岩であり、熱と圧
力によって変成されたもので、花崗岩が変成されたもの
は正片麻岩と称されている。結晶片岩は、片麻岩ほど高
温にならずに、地下深くで主に高い圧力を受けてできた
変成岩であり、雲母鉱物ができることが多いと言われて
いる。そのほか圧砕岩（マイロナイト）は、地殻変動等
のせん断力による圧力変形により変成されたものであ
り、蛇紋岩は加水変成されたものであると言われてい
る。[0003] Naturally occurring metamorphic rocks are rocks formed by changing the mineral composition and texture of marine rocks and igneous rocks by heat, pressure and metamorphism deep underground.
Gneiss, crystal schist, crushed rock (mylonite), serpentine and the like are known. Marble is formed by recrystallizing limestone under the influence of the deformation of the crust and the heat of magma, and it is known that various marbles are formed depending on the components of the limestone and its metamorphic state. Gneiss is a metamorphic rock composed of coarse-grained, thin layers of different mineral composition overlapping each other. It is metamorphosed by heat and pressure. A metamorphic granite is called orthogneiss. Crystalline schist is a metamorphic rock formed under high pressure mainly underground without being as hot as gneiss, and it is said that mica minerals are often formed. In addition, crushed rock (mylonite) is metamorphosed by pressure deformation due to shearing force such as crustal deformation, and it is said that serpentine is hydromorphic.

【０００４】代表的な変成岩である大理石や蛇紋岩など
の表面を研磨して平らな平板状にすると、そこに独特の
各種模様、例えば細かい斑点状の模様とか、不定形の筋
状の模様とか、不定形の縞状の模様などが現れ、独特の
高級な風合を醸し出すので高級な建築物の装飾材などと
して使用されている。また例えば大理石のある種のもの
は、表面を研磨して平らにする事により、黄土色のベー
スにやや赤みのかかった濃色の茶色の細い不定形の筋状
模様ややや白味を帯びた細長い不定形の縞模様が入った
重厚感、高級感のある光沢のある装飾材とする事ができ
る。When the surface of a typical metamorphic rock, such as marble or serpentine, is polished into a flat plate, various unique patterns, such as fine spot-like patterns, irregular streaky patterns, etc. Because of the appearance of irregularly shaped striped patterns and the like, it has a unique high-grade feel and is used as a decorative material for high-end buildings. Also, for example, some marbles have a slightly irregular white streaky pattern of dark brown with a slightly reddish color on the ocher base by polishing and flattening the surface. It can be used as a dignified decoration material with a profound, high-grade, and glossy appearance that has a long and narrow irregular shaped stripe pattern.

【０００５】そのため、これらの表面が平らに研磨され
た平板状の変成岩からなる装飾材は、高級建築物の壁材
や床材などに用いられてきている。しかし、天然の変成
岩は高価であり、非常に重く運搬に極めてコストがかか
り、また、重いので例えば高所などでは作業がしにく
い、重くて脆いので運搬中や取り付け作業中の取り扱い
方によっては、衝撃により、例えばトラックから作業現
場に荷を降ろす際の不注意な衝撃などにより角などの一
部が欠けたりする、また、産地が限られ従って同一品種
のものを長期間に亘って安定して供給しにくい、同一色
調で揃えて建築物を装飾しようと思っても、必ずしも同
様なトーンの品質のものが大量に入手できるとは限らな
い、曲面に加工することが難しいなどの問題がある。ま
た、天然の大理石などは、表面が研磨されて非常に美し
い表面模様を有する平板状物が得られるが、炭酸カルシ
ウムが主成分であるため、酸に弱く、酸性雨などの影響
や大気中の酸成分が雨などで濡れた場合に作用するた
め、屋外では一般に用いられていないなどの問題もあ
る。[0005] For this reason, decorative materials made of flat metamorphic rocks whose surfaces are polished flat have been used as walls and floors of high-end buildings. However, natural metamorphic rocks are expensive, very heavy and extremely costly to transport, and because they are heavy, for example, it is difficult to work at high places, etc.Because they are heavy and brittle, depending on how they are handled during transportation and installation work, Due to the impact, for example, inadvertent impact when unloading the truck from the truck to the work site, some corners etc. may be chipped, and the production area is limited, so the same type of product can be stably Even if it is difficult to supply, or to decorate a building with the same color tone, it is not always possible to obtain a large quantity of similar tone quality, and it is difficult to process it into a curved surface. In addition, natural marble, etc., is polished to obtain a flat plate with a very beautiful surface pattern.However, since calcium carbonate is the main component, it is weak to acids, affected by acid rain, etc. Since the acid component acts when wet with rain or the like, it has a problem that it is not generally used outdoors.

【０００６】一方、前述した合成樹脂エマルションと大
理石粉末、硅砂、陶磁器粉あるいは着色硅砂、有色陶磁
器粉などの適宜の骨材を含む吹付材を寒冷紗や不織布そ
の他の適宜の布状シート基材上に吹付け等適宜の方法に
より塗布し、あるいは成型加工して得られる天然石風の
模様を施した装飾材は天然の岩石に比べて比較的安価で
あり、耐水・耐酸性があり、重さも軽くなり運搬コスト
の面でも有利であり同一品種のものを長期間に亘って安
定して生産でき、また、用いる合成樹脂の種類にもよる
が、最も良く用いられているアクリル系樹脂の場合など
一般に熱可塑性樹脂又はその架橋物などの場合には比較
的柔軟性があるので、適宜の岩石模様を有する平面状の
シート状物を製造しておいて、これを施工面の曲面に沿
って曲げながら曲面に施工することが可能であるし、成
型品が硬くなる合成樹脂を用いる場合には、目的の曲面
を有する基材に吹付けないし塗布する方法や、鋳型を曲
面状にしておいて成型する事なども考えられるので比較
的容易に曲面加工もできる事や、比較的軽くて施工時の
取扱が容易な事から、高所などにおいても施工作業がし
やすいなどの利点かあり、近年、建築物の内外装壁面或
は床面の装飾用など建築物表面仕上用シートなどとして
頻繁に用いられてきている。On the other hand, a spraying material containing the above-mentioned synthetic resin emulsion and a suitable aggregate such as marble powder, silica sand, porcelain powder or colored silica sand, colored porcelain powder, etc. is placed on a cold gauze, a nonwoven fabric or any other suitable cloth-like sheet base material. A decorative material with a natural stone-like pattern obtained by applying or molding by appropriate methods such as spraying is relatively inexpensive, water- and acid-resistant, and lighter in weight than natural rock. It is also advantageous in terms of transportation cost and can stably produce the same type of product over a long period of time.Although it depends on the type of synthetic resin used, it is generally used in the case of acrylic resin which is most often used. In the case of a plastic resin or a crosslinked product thereof, since it is relatively flexible, a flat sheet having an appropriate rock pattern is manufactured, and the sheet is bent while being bent along the curved surface of the construction surface. When using synthetic resin that hardens the molded product, it is necessary to spray or apply to the substrate having the target curved surface, or to mold the mold with a curved surface It is possible to perform curved surface processing relatively easily, and it is relatively light and easy to handle during construction, so there are advantages such as easy construction work even at high altitudes. It has been frequently used as a sheet for finishing the surface of a building, such as for decorating an inner or outer wall surface or a floor surface.

【０００７】[0007]

【発明が解決しようとする課題】しかし、一般にこれら
の合成による装飾材は、表面が凹凸状のものが御影石調
などの比較的天然石調の雰囲気を出す事ができるが、表
面が平らな平板状では重厚感、高級感を有するものは得
られていない。一般にこれら合成品を用いて表面を平ら
なに研磨して仕上げても、合成品と言ったイメージの比
較的単調な感じのものしか得られず、前述した重厚感、
高級感を有する表面がほぼ平らな平板状のものが得られ
ていないのが現状である。However, in general, decorative materials made of these synthetic materials can give a relatively natural stone-like atmosphere such as granite when the surface of the surface is uneven, but the flat surface is flat. However, a product having a solid feeling and a high-class feeling has not been obtained. In general, even if the surface is polished and flattened using these synthetic products, only a relatively monotonous image of the image of the synthetic product can be obtained, and the solid feeling described above,
At present, it is not possible to obtain a flat plate having a high-grade appearance and a substantially flat surface.

【０００８】本発明は従来の天然の変成岩その他の天然
石の表面研磨した平板状仕上げ品のような前述した欠点
がなく、且つ、従来の合成品ではなし得なかった、重厚
さ、深みに富んだ高級感を有し、表面がほぼ平坦な平板
状の装飾材ならびにその製造方法を提供する事を目的と
する。The present invention does not have the above-mentioned drawbacks such as the conventional polished flat surface finish of natural metamorphic rocks and other natural stones, and has a richness and depth which cannot be achieved by conventional synthetic products. It is an object of the present invention to provide a flat decorative material having a high-grade feel and a substantially flat surface, and a method for manufacturing the same.

【０００９】[0009]

【課題を解決するための手段】前記課題を解決するた
め、本発明は次ぎの様な平板状で模様を有する装飾材な
らびにその製造方法を提供する。In order to solve the above-mentioned problems, the present invention provides the following decorative material having a plate-like pattern and a method of manufacturing the same.

【００１０】（１）骨材が分散されてなる合成樹脂層か
ら形成されていて、表面が平らな平板状装飾材であっ
て、前記装飾材は（イ）骨材が分散されてなる合成樹脂
層であって、１種類の前記合成樹脂層からなるか、また
は、互いに色調の異なる２種類以上の前記合成樹脂層か
ら表面模様が形成されている第２の層と、（ロ）骨材が
分散されてなる合成樹脂層であって、前記第２の層と色
調が異なり、１種類または互いに色調の異なる２種類以
上の前記合成樹脂層からなり、前記第２の層の表面を不
連続的に覆っていて表面模様を形成しており、前記第２
の層の厚み方向にその下部の少なくとも一部が入り込ん
でいる第１の層とからなり、前記第２の層の表面に露出
している部分と第１の層の表面が平らでほぼ同一平面を
形成している事を特徴とする第１の層と第２の層の色調
コントラストにより模様を形成している装飾材。(1) A flat decorative material having a flat surface formed of a synthetic resin layer in which an aggregate is dispersed, wherein the decorative material is (A) a synthetic resin in which the aggregate is dispersed. A second layer comprising a single layer of the synthetic resin layer or a surface pattern formed from two or more types of the synthetic resin layers having different color tones; and (b) an aggregate. A dispersed synthetic resin layer having a different color tone from the second layer, comprising one or two or more types of the synthetic resin layers having different color tones, wherein the surface of the second layer is discontinuous. To form a surface pattern, the second
A first layer in which at least a part of a lower part of the first layer is penetrated in a thickness direction of the first layer, and a portion exposed on a surface of the second layer and a surface of the first layer are flat and almost flush with each other. A decorative material having a pattern formed by a color tone contrast between a first layer and a second layer, characterized by forming a pattern.

【００１１】（２）第１の層と第２の層から形成される
模様が、変成岩調模様である前記（１）項に記載の装飾
材。 （３）第２の層の下に骨材が分散されてなる合成樹脂層
からなる第３の層を更に有する前記（１）または（２）
項のいずれかに記載の装飾材。(2) The decorative material according to the above (1), wherein the pattern formed from the first layer and the second layer is a metamorphic rock pattern. (3) The above (1) or (2) further including a third layer made of a synthetic resin layer in which an aggregate is dispersed below the second layer.
The decorative material according to any one of the above items.

【００１２】（４）第２の層の下に更にシート状基材が
積層されている前記（１）または（２）項のいずれかに
記載の装飾材。 （５）第３の層の下に更にシート状基材が積層されてい
る前記（３）項に記載の装飾材。(4) The decorative material as described in any of (1) and (2) above, wherein a sheet-like substrate is further laminated below the second layer. (5) The decorative material according to the above (3), wherein a sheet-like substrate is further laminated below the third layer.

【００１３】（６）シート状基材が布状物である前記
（４）〜（５）項のいずれかに記載の装飾材。 （７）第１の層と第２の層との色調の差異が、色相、明
度、彩度の少なくとも１つが異なるものである前記
（１）〜（６）項のいずれかに記載の装飾材。(6) The decorative material according to any one of the above (4) to (5), wherein the sheet-like substrate is a cloth. (7) The decorative material according to any one of (1) to (6), wherein the difference in color tone between the first layer and the second layer is at least one of hue, lightness, and saturation different. .

【００１４】（８）第１の層と第２の層との色調の明度
の差異が、マンセル値で１より大きい前記（１）〜
（７）項のいずれかに記載の装飾材。 （９）凹凸反転レリーフ模様を有する鋳型に、合成樹脂
エマルションまたは溶液中に骨材が分散されてなる第２
の層を形成するための１種類の第２の塗布材を塗布する
か、または、互いに色調が異なる２種類以上の第２の塗
布材を模様状に塗布し、前記第２の塗布材を乾燥させて
形成された第２の層を前記鋳型から取り出し、第２の層
が前記鋳型に接していた側から、合成樹脂エマルション
または溶液中に骨材が分散されてなる第１の層を形成す
るための第２の層とは色調の異なる１種類または互いに
色調が異なる２種類以上の第１の塗布材を、第２の層の
凹凸の少なくとも凹部がほぼ充填されるように又は凹部
がほぼ充填され且つ第２の層の表面のほぼ全面が被覆さ
れる程度に塗布し、乾燥して第１の層を形成し、次いで
第１の層の少なくとも一部が表面に残り、かつ、第２の
層の一部が表面に現れる程度に、表面全面が平面になる
様に第１の層を形成した側から平らに研磨する工程を含
む少なくとも第１の層と第２の層とからなる色調コント
ラスト模様が表面に発現している装飾材の製造方法。(8) The difference in lightness of the color tone between the first layer and the second layer is larger than 1 in the Munsell value.
(7) The decorative material according to any one of the above. (9) A second method in which an aggregate is dispersed in a synthetic resin emulsion or a solution in a mold having an uneven relief pattern.
One kind of a second coating material for forming a layer, or two or more kinds of second coating materials having different color tones are applied in a pattern, and the second coating material is dried. The second layer thus formed is removed from the mold, and a first layer in which the aggregate is dispersed in the synthetic resin emulsion or the solution is formed from the side where the second layer was in contact with the mold. The second layer is filled with one type of first coating material having a different color tone or two or more types of different color tone from each other so that at least the concave portions of the irregularities of the second layer are substantially filled or the concave portions are substantially filled Applied to such an extent that the entire surface of the second layer is covered, and dried to form a first layer, and then at least a portion of the first layer remains on the surface and the second layer Form the first layer so that the entire surface is flat so that a part of the layer appears on the surface. At least a first layer and a manufacturing method of the second layer and the decorative material color contrast pattern is expressed on the surface consisting of including the step of flat polished by side.

【００１５】（１０）第１の層と第２の層とから形成さ
れる模様が、変成岩調模様である前記（９）項に記載の
装飾材の製造方法。 （１１）凹凸反転レリーフ模様を有する鋳型が、所望の
表面模様が描写されている写真ないしは絵を原画とし
て、デジタル光彫刻システムにより感光性合成樹脂又は
感光性ゴム状物からなる凹凸レリーフ模様を有する母型
を作成し、前記母型に鋳型形成用の合成樹脂を流し込ん
で固めて前記母型から離型させて得られた凹凸反転レリ
ーフ模様を有する鋳型である前記（９）または（１０）
項のいずれかに記載の装飾材の製造方法。(10) The method of manufacturing a decorative material according to the above (9), wherein the pattern formed from the first layer and the second layer is a metamorphic rock pattern. (11) The mold having the unevenness relief pattern has a textured relief pattern made of a photosensitive synthetic resin or a photosensitive rubber-like material by a digital optical engraving system using a photograph or a picture on which a desired surface pattern is drawn as an original image. (9) or (10), which is a mold having a concavo-convex inverted relief pattern obtained by preparing a master mold, pouring a synthetic resin for forming a mold into the master mold, solidifying the mold, and releasing the mold from the master mold.
The method for producing a decorative material according to any one of the above items.

【００１６】（１２）凹凸反転レリーフ模様を有する鋳
型に、合成樹脂エマルションまたは溶液中に骨材が分散
されてなる第２の層を形成するための１種類の第２の塗
布材を塗布するか、または、互いに色調が異なる２種類
以上の第２の塗布材を模様状に塗布し、前記第２の塗布
材を乾燥させ又は半乾燥の状態で、この上全面に更に合
成樹脂エマルションまたは溶液中に骨材が分散されてな
る第３の層を形成するための第３の塗布材を塗布する工
程を更に含む前記（９）または（１１）項のいずれかに
記載の装飾材の製造方法。(12) One type of a second coating material for forming a second layer in which an aggregate is dispersed in a synthetic resin emulsion or a solution is applied to a mold having a relief pattern with reversed irregularities. Alternatively, two or more types of second coating materials having different color tones are applied in a pattern, and the second coating material is dried or semi-dried. The method for producing a decorative material according to any one of the above (9) or (11), further comprising a step of applying a third coating material for forming a third layer in which the aggregate is dispersed.

【００１７】（１３）第２の塗布材を塗布後、その表面
が乾燥する前に、シート状基材を積層する工程を更に含
む前記（９）または（１１）項のいずれかに記載の装飾
材の製造方法。(13) The decoration according to any one of (9) and (11), further comprising a step of laminating a sheet-like substrate after the second coating material is applied and before the surface is dried. The method of manufacturing the material.

【００１８】（１４）第３の塗布材を塗布後、その表面
が乾燥する前にシート状基材を積層する工程を更に含む
前記（１２）項に記載の装飾材の製造方法。 （１５）シート状基材が布状物である前記（１３）項ま
たは（１４）項のいずれかに記載の装飾材の製造方法。(14) The method for producing a decorative material according to the above (12), further comprising a step of laminating a sheet-like substrate after the third coating material is applied and before the surface is dried. (15) The method for producing a decorative material according to any one of the above (13) or (14), wherein the sheet-like substrate is a cloth.

【００１９】（１６）第１の塗布材と第２の塗布材と
の、その乾燥後の色調の差異が、色相、明度、彩度の少
なくとも１つが異なるものである前記（９）〜（１４）
項のいずれかに記載の装飾材の製造方法。(16) The above-mentioned (9) to (14) wherein the difference in color tone between the first coating material and the second coating material after drying is at least one of hue, lightness and saturation. )
The method for producing a decorative material according to any one of the above items.

【００２０】（１７）第１の塗布材と第２の塗布材と
の、その乾燥後の色調の明度の差異が，マンセル値で１
より大きい前記（９）〜（１６）項のいずれかに記載の
装飾材の製造方法。(17) The difference in lightness of the color tone between the first coating material and the second coating material after drying is 1 in Munsell value.
The method for producing a decorative material according to any one of the above (9) to (16), which is larger.

【００２１】[0021]

【発明の実施の形態】本発明の表面に模様が現れている
平板状の装飾材を構成する一成分の合成樹脂成分は、第
１の層、第２の層及び第３の層の合成樹脂成分のいずれ
においても、通常、原料として、即ち第１の塗布材、第
２の塗布材及び第３の塗布材の合成樹脂成分の原料とし
て、合成樹脂エマルションあるいは合成樹脂溶液が用い
られ、天然石調模様を有する装飾材の製造の際に従来よ
り用いられている各種の合成樹脂エマルションや溶液を
用いることができる。有機溶剤の回収や環境問題などを
余り考慮する必要がないという点からは、合成樹脂エマ
ルションが好ましく用いられる。特に耐候性、耐アルカ
リ性、耐水性、接着性、柔軟性、耐吸水性等を満足する
合成樹脂エマルションが好ましく、具体的な例として
は、例えばアクリル系樹脂エマルション（アクリル−ス
チレン系樹脂エマルション、アクリル−ウレタン系樹脂
エマルション、アクリル−シリコン樹脂系エマルショ
ン、アクリル−弗素樹脂系エマルションも含む）、エチ
レン−酢酸ビニル樹脂などの酢酸ビニル系樹脂エマルシ
ョン、塩化ビニル系樹脂エマルション、ウレタン系樹脂
エマルション等が挙げられる。これらのいずれの樹脂も
乾燥後の樹脂マトリックスは適宜の柔軟性を有してお
り、曲面への施工も可能である。中でもアクリル系樹脂
エマルションが比較的安価な割りには、耐候性の点でよ
り優れているので建築物や構築物の内外装壁面或は床面
などの表面仕上用シートとして用いた場合など長期の耐
久性を有し好ましい。BEST MODE FOR CARRYING OUT THE INVENTION The one-component synthetic resin component constituting a flat decorative material having a pattern on its surface according to the present invention is a synthetic resin of a first layer, a second layer and a third layer. In any of the components, a synthetic resin emulsion or a synthetic resin solution is usually used as a raw material, that is, as a raw material of a synthetic resin component of the first coating material, the second coating material, and the third coating material. Various synthetic resin emulsions and solutions conventionally used in the production of decorative materials having a pattern can be used. A synthetic resin emulsion is preferably used from the viewpoint that there is no need to consider the recovery of the organic solvent, environmental problems, and the like. In particular, a synthetic resin emulsion that satisfies weather resistance, alkali resistance, water resistance, adhesiveness, flexibility, water absorption resistance, and the like is preferable. Specific examples include an acrylic resin emulsion (acryl-styrene resin emulsion, acrylic -Urethane resin emulsion, acryl-silicone resin emulsion, acryl-fluorine resin emulsion), vinyl acetate resin emulsion such as ethylene-vinyl acetate resin, vinyl chloride resin emulsion, urethane resin emulsion and the like. . In any of these resins, the resin matrix after drying has appropriate flexibility and can be applied to a curved surface. Above all, acrylic resin emulsions are relatively inexpensive, but they are more excellent in terms of weather resistance, so they can be used for long-term durability, such as when used as a surface finishing sheet for the interior and exterior walls or floors of buildings and structures. It is preferable because of its properties.

【００２２】第１の層、第２の層及び第３の層またはそ
の原料である第１の塗布材、第２の塗布材及び第３の塗
布材に配合される骨材としては、従来より天然石調模様
を有する装飾材の製造の際に用いられている各種の公知
の骨材を用いる事ができ、大理石粉や御影石粉、硅砂そ
の他の天然石粉、陶磁器粉、あるいはこれらを人工的に
着色した例えば着色焼成硅砂や有色陶磁器粉などのいわ
ゆる着色骨材と称されているものなどのような、天然石
細粒状物、陶磁器細粒状物、またはこれらの着色物の少
なくとも１種からなる骨材で代表される無機材料が好ま
しく用いられるが、これらに限定されるものではなく、
プラスチックなどの有機材料から成る骨材を用いてもよ
い。プラスチックなどの有機材料から成る骨材は、無機
材料から成る骨材に比べて若干コスト的に高くなる傾向
がある。The first layer, the second layer and the third layer or the aggregates to be mixed with the first coating material, the second coating material and the third coating material which are the raw materials thereof are conventionally known as aggregates. Various types of known aggregates used in the manufacture of decorative materials having a natural stone pattern can be used, and marble powder, granite powder, silica sand, other natural stone powder, ceramic powder, or artificially colored these For example, natural stone fine granules, ceramic fine granules, or aggregates of at least one of these colored materials, such as those called so-called colored aggregates such as colored calcined silica sand and colored ceramic powder. Representative inorganic materials are preferably used, but are not limited thereto.
An aggregate made of an organic material such as plastic may be used. Aggregates made of organic materials such as plastics tend to be slightly more costly than aggregates made of inorganic materials.

【００２３】骨材の大きさは主として粒径０．０５〜
１．５ｍｍの大きさの骨材を用いることが好ましい。こ
こで粒径とは骨材が球状でない場合には、測定時に顕微
鏡などの適宜の器具で観測する場合にその観測している
骨材の粒子が見えている状態で、その粒子１つの最も大
きな径をもってその骨材粒子の粒径としている。The size of the aggregate is mainly 0.05 to
It is preferable to use an aggregate having a size of 1.5 mm. Here, when the aggregate is not spherical, when the aggregate is not spherical, the particle of the observed aggregate is visible when observing with an appropriate instrument such as a microscope at the time of measurement. The diameter is used as the diameter of the aggregate particles.

【００２４】なお、人工的に着色を施した着色骨材ある
いは特に人工的に着色を施していない素材そのままの色
の骨材などの中から適宜１種または２種以上を併用する
ことによって所望の色調や風合を調整することができ
る。It is to be noted that a desired or desired combination of two or more kinds of artificially colored aggregates or aggregates of a color that is not artificially colored can be used. The color tone and hand can be adjusted.

【００２５】骨材と合成樹脂成分の配合割合はどの様な
風合いの装飾材とするかとか、第１の塗布材と第２の塗
布材間の色調差、あるいは必要に応じて第２の塗布材と
して互いに色調の異なる２種類以上の第２の塗布材を用
いる場合にはそれらの間の色調差、又、更に必要に応じ
て第１の塗布材として互いに色調の異なる２種類以上の
塗布材を用いる場合にはそれらの間の色調差などを考慮
するなど、目的に応じて若干の相違があるが、合成樹脂
エマルションまたは溶液の割合が固形分で骨材１００重
量部に対し、５〜２０重量部程度が好ましい。The mixing ratio of the aggregate and the synthetic resin component depends on the texture of the decorative material, the color difference between the first coating material and the second coating material, or if necessary, the second coating material. When two or more kinds of second coating materials having different color tones are used as materials, the difference in color tone between them, and, if necessary, two or more kinds of coating materials having different color tones as the first coating material, if necessary When using a synthetic resin emulsion or solution is slightly different depending on the purpose, for example, considering the color tone difference between them, the solid content is 5 to 20 parts by weight per 100 parts by weight of the aggregate. It is preferably about parts by weight.

【００２６】この範囲の好ましい態様とすることによ
り、合成樹脂成分は、骨材のバインダーとしての役割も
果たすに十分な量であり、収縮やクラックの発生が生じ
る程合成樹脂成分が多すぎることもなく、しかも重厚な
風合いの発現を容易にし、且つ耐久性のある強度を有す
る装飾材が提供でき、特に変成岩調の重厚な風合いの装
飾材も容易に提供でき好ましい。By adopting a preferred embodiment within this range, the amount of the synthetic resin component is sufficient to also serve as a binder for the aggregate, and the amount of the synthetic resin component may be too large to cause shrinkage and cracks. Further, it is possible to provide a decorative material having a durable strength, which facilitates the development of a heavy texture and has a durable strength. Particularly, a decorative material having a metamorphic rock-like heavy texture can be easily provided, which is preferable.

【００２７】塗膜層の色調を調整するには各種骨材やこ
れらを人工的に着色したいわゆる着色骨材などの１種ま
たは２種以上の配合量や、添加する骨材の種類、粒度、
色を適宜選定して配合したり、着色剤を必要に応じて添
加するなどすることによって達成される。In order to adjust the color tone of the coating layer, one or more kinds of aggregates such as various aggregates and so-called colored aggregates obtained by artificially coloring these aggregates, the type of aggregate to be added, the particle size,
This can be achieved by appropriately selecting and blending colors, or adding a coloring agent as necessary.

【００２８】以下、本発明の理解を容易にするため、図
面を参照しながら本発明の変成岩調模様を有する装飾材
ならびにその製造方法について説明するが、この図面に
例示したものは、本発明の一実施の形態であって、本発
明はこれのみに限定されるものではない。Hereinafter, in order to facilitate understanding of the present invention, a decorative material having a metamorphic rock pattern and a method of manufacturing the same according to the present invention will be described with reference to the drawings. This is an embodiment, and the present invention is not limited to this.

【００２９】図１と図２は本発明の表面に模様が現れて
いる装飾材の製造方法の一実施の形態の工程を示す工程
断面図である。図１（ａ）、（ｂ）、（ｃ）、（ｄ）と
図２の（ｅ）、（ｆ）、（ｇ）、（ｈ）とは図１から続
く一連の工程であるが、１つの図に収まらないので図１
と図２に分けて描いたものである。FIGS. 1 and 2 are sectional views showing the steps of an embodiment of a method for manufacturing a decorative material having a pattern on its surface according to the present invention. 1 (a), (b), (c), (d) and (e), (f), (g), (h) of FIG. 2 are a series of steps following FIG. Figure 1 because it does not fit in one figure
And FIG. 2 separately.

【００３０】また、図３は、図２の工程（ｆ）に相当す
る別の実施の形態の工程を示す工程断面図であり、図４
はかかる工程により得られる本発明の変成岩調模様を有
する装飾材の一実施の形態の平面図である。FIG. 3 is a process sectional view showing a process of another embodiment corresponding to the process (f) of FIG.
1 is a plan view of an embodiment of a decorative material having a metamorphic rock-like pattern of the present invention obtained by such a step.

【００３１】図１（ａ）に示すように、ベニヤ板などの
適宜の平坦な基板台１０上に前述した凹凸反転レリーフ
模様を有する鋳型１１を載置する。次いで図１（ｂ）に
示すように、鋳型に合成樹脂エマルションまたは溶液中
に適宜の骨材が分散されてなる第２の層２（２ａ、２
ｂ）の原料である第２の塗布材２ａ、２ｂを塗布する。
ここでは第２の塗布材２ａ、２ｂはそれぞれ色調が互い
に異なるように調整された２種類の塗布材を使用して２
色模様を形成する例を示したが、第２の塗布材は１種類
でもよく、また更には、必要に応じて３種類以上の互い
に色調の異なる塗布材を調整して３色以上の多色模様を
形成しても良い。目的にもよるが、好ましくは２種類以
上の第２の塗布材を用いて２色以上の多色模様を形成す
るのが、重厚さ、高級感、変成岩調の風合を出すのには
好ましい。As shown in FIG. 1 (a), a mold 11 having the above-described relief inversion pattern is placed on an appropriate flat substrate table 10 such as a plywood board. Next, as shown in FIG. 1 (b), a second layer 2 (2a, 2a) in which an appropriate aggregate is dispersed in a synthetic resin emulsion or solution in a mold.
The second coating materials 2a and 2b, which are the raw material of b), are applied.
Here, as the second coating materials 2a and 2b, two types of coating materials adjusted so that the color tones are different from each other are used.
Although an example in which a color pattern is formed has been described, the second coating material may be of one type, and further, if necessary, three or more types of coating materials having mutually different color tones may be adjusted to obtain a multicolor of three or more colors. A pattern may be formed. Although it depends on the purpose, it is preferable to form a multicolored pattern of two or more colors using two or more types of second coating materials in order to obtain a heavy, high-grade, metamorphic rock texture. .

【００３２】塗布手段は特に制限するものではないが通
常は吹付けガンを用いて塗布材２ａ、２ｂを鋳型１１の
上に吹付けるか、塗布材２ａ、２ｂを鏝を用いて鋳型１
１の上に塗布するのが一般的である。通常、上記で例示
した様な２色模様を出すためには、色調の異なる２種類
の塗布材を吹付けガンで吹き付けて塗布するのが生産効
率も良く一般的に良く用いられているが、その場合に２
つの吹付けガンからそれぞれの塗布材２ａ、２ｂを吹き
付けて２色模様を形成しても良いし、吹付けガンとして
２頭ガンを用いて２色模様を形成しても良い。３種類以
上の多色模様を形成する場合にも吹付けガンを３個以上
用いるか３頭ガン以上の多頭ガンを用いれば良いことは
同様である。第２の層２を形成するための塗布材２ａ、
２ｂの合計の塗布量も特に制限するものではないが、通
常３〜３．５ｋｇ／ｍ2 程度である。The application means is not particularly limited, but usually the application materials 2a and 2b are sprayed on the mold 11 using a spray gun, or the application materials 2a and 2b are applied to the mold 1 using an iron.
It is common to apply on top of No. 1. Usually, in order to produce a two-color pattern as exemplified above, it is generally well-used to spray and apply two types of coating materials having different color tones with a spray gun. In that case 2
A two-color pattern may be formed by spraying the respective coating materials 2a and 2b from one spray gun, or a two-color pattern may be formed by using a two-head gun as the spray gun. Similarly, when three or more types of multicolor patterns are formed, three or more spray guns or three or more guns may be used. A coating material 2a for forming the second layer 2,
The total coating amount of 2b is not particularly limited, but is usually about 3 to 3.5 kg / m 2 .

【００３３】次いで図１の（ｃ）に示されるように、合
成樹脂エマルションまたは溶液中に適宜の骨材が分散さ
れてなる第３の層３を形成するための第３の塗布材３が
塗布される。第３の塗布材３を塗布する工程、即ち第３
の層を形成することは任意であり、必要に応じて採用す
ればよく、従って第３の層は存在しなくても良い。第３
の層を形成するのは、通常厚みを厚くするためであるの
で、第３の層を形成するための塗布材３の色調は任意で
ある。第３の塗布材３は、第２の塗布材２が乾燥又は半
乾燥した後塗布してもよいし、場合により、粘度が高く
両者が混ざり合う恐れが少ない場合には、第２の塗布材
２が乾燥しない内に第３の塗布材３を塗布してもよい。
塗布手段は前記第２の塗布材の塗布手段と同様の手段を
用いることができる。塗布量も特に制限するものではな
いが、通常３〜３．５ｋｇ／ｍ2程度である。Next, as shown in FIG. 1C, a third coating material 3 for forming a third layer 3 in which an appropriate aggregate is dispersed in a synthetic resin emulsion or a solution is applied. Is done. A step of applying the third coating material 3,
The formation of the third layer is optional, and may be adopted as needed. Therefore, the third layer may not be present. Third
Is usually formed to increase the thickness, and therefore, the color tone of the coating material 3 for forming the third layer is arbitrary. The third coating material 3 may be applied after the second coating material 2 has been dried or semi-dried. In some cases, when the viscosity is high and there is little possibility that the two are mixed, the second coating material 3 is used. The third coating material 3 may be applied before the second coating material 2 dries.
As the applying means, the same means as the applying means of the second applying material can be used. Although the amount of application is not particularly limited, it is usually about 3 to 3.5 kg / m 2 .

【００３４】次いで図１（ｄ）に示すように必要に応じ
て、第３の塗布材３の表面が乾燥する前に（通常塗布直
後〜塗布後３０分以内程度が好ましい。）不織布その他
のシート状基材６を積層し、必要なら鏝またはローラー
などでその上から押さえ付けて第３の塗布材層にしっか
りと積層されるようにする。そして第３の塗布材３を乾
燥させ、第３の層３とする。Next, as shown in FIG. 1 (d), if necessary, before the surface of the third coating material 3 dries (usually immediately after application to within about 30 minutes after application). The base material 6 is laminated, and if necessary, pressed down from above with a trowel or a roller or the like so as to be firmly laminated to the third coating material layer. Then, the third coating material 3 is dried to form a third layer 3.

【００３５】尚、シート状基材６は、必要に応じて設け
るものであり、設けなくても良いが、設けた方が、得ら
れる装飾材の強度の補強の点で好ましい。また、前述し
たように第３の層も必ずしも設ける必要がないことか
ら、第３の層が存在しない場合で、且つ、シート状基材
６を設ける場合には、図１（ｂ）に示したような第２の
塗布材２を塗布した段階で第２の塗布材２の表面が乾燥
する前に（通常塗布直後〜塗布後３０分以内程度が好ま
しい。）前記と同様にしてシート状基材６を積層すれば
良い。The sheet-like base material 6 is provided if necessary and need not be provided, but is preferably provided in terms of reinforcing the strength of the decorative material obtained. In addition, as described above, since the third layer does not necessarily need to be provided, when the third layer does not exist and when the sheet-like base material 6 is provided, the state shown in FIG. At the stage where the second coating material 2 is applied, before the surface of the second coating material 2 dries (generally, preferably immediately after application to within about 30 minutes after application), a sheet-like substrate is formed in the same manner as described above. 6 may be laminated.

【００３６】そして次に図２の（ｅ）に示されるよう
に、全体が乾燥した時点で鋳型を取り外し、シート状基
材６の上に第３の層３と第２の層２（２ａ、２ｂ）が形
成された、中間積層体を得る。尚、図２(ｅ)において、
２ｃは第２の層２の凹凸の凹部を指し、２ｄは凸部を指
す。以下の図面には図面が見にくくなることをさけるた
め、この記号を付与していないが、趣旨は同様である。Then, as shown in FIG. 2E, when the whole is dried, the mold is removed, and the third layer 3 and the second layer 2 (2a, An intermediate laminate in which 2b) is formed is obtained. Incidentally, in FIG.
2c indicates a concave and convex portion of the second layer 2, and 2d indicates a convex portion. This symbol is not given in the following drawings in order to avoid obscuring the drawings, but the purpose is the same.

【００３７】次に図２の（ｆ）に示されるように、第２
の層２が形成されている側（第２の層２が鋳型に接して
いた側）から合成樹脂エマルションまたは溶液中に骨材
が分散されてなる第１の層１を形成するための第１の塗
布材１をその全面に塗布する。勿論第２の層の凹部も第
１の塗布材１で充填される。塗布量は第２の層２がほぼ
覆い隠される程度の量でよい。場合によっては図３の
（ｆ’）で示されるように第２の層２の凹部２ｃがほぼ
充填されるように凹部２ｃの部分のみに第１の塗布材１
を塗布し、第２の層２の凸部２ｄが一部覆われていない
程度でもよい。そして第１の塗布材１を乾燥後、第１の
層１の少なくとも一部が表面に残り、かつ、第２の層２
模表面に現れる程度に、表面全面が平面になる様に第１
の層を形成した側から研磨する。この図２（ｆ）ないし
図３の（ｆ’）では研磨して現れる表面の水平面を点線
７（矢印Ａ−Ａ’ライン）で示した（これを研磨面７ま
で平らに研磨すると言うこともある。）。Next, as shown in FIG.
From the side where the second layer 2 is formed (the side where the second layer 2 was in contact with the mold) to form the first layer 1 in which the aggregate is dispersed in a synthetic resin emulsion or solution. Is applied to the entire surface. Of course, the concave portion of the second layer is also filled with the first coating material 1. The amount of application may be such that the second layer 2 is almost covered. In some cases, as shown in FIG. 3 (f ′), the first coating material 1 is applied only to the concave portion 2c so that the concave portion 2c of the second layer 2 is almost filled.
Is applied, and the protrusion 2d of the second layer 2 may not be partially covered. After drying the first coating material 1, at least a part of the first layer 1 remains on the surface and the second layer 2
First so that the entire surface is flat to the extent that it appears on the surface
Is polished from the side where the layer is formed. In FIG. 2F to FIG. 3F ′, the horizontal surface of the surface appearing after polishing is indicated by a dotted line 7 (arrow AA ′ line). is there.).

【００３８】こうして研磨面７まで平らに研磨して得ら
れた、本発明の平板状の装飾材を図２の（ｇ）に示し
た。これを上から見た平面図で示した変成岩調模様、特
に蛇紋岩調模様を有する装飾材の一態様例が図４であ
る。FIG. 2 (g) shows the flat decorative material of the present invention obtained by flattening the polishing surface 7 in this manner. FIG. 4 shows an example of a decorative material having a metamorphic rock-like pattern, particularly a serpentine-like pattern, shown in a plan view as viewed from above.

【００３９】そして、必要に応じて図２の（ｈ）に示す
ように、この上に乾燥後透明となる合成樹脂エマルショ
ンまたは溶液を薄く塗布しトップコート層４を形成して
もよい。トップコート層４を形成させるかどうかは任意
であり、一般に表面を研磨した場合には、研磨の程度や
手法にもよるが、樹脂層が研磨されて、表面の荒さによ
り、光が乱反射するため、全体の色調がやや白っぽくな
ることがあり、これを抑える色調としたり、より光沢を
持たせたい場合には、トップコート４の層を設ける事が
好ましい。If necessary, as shown in FIG. 2H, a top coat layer 4 may be formed by applying a thin synthetic resin emulsion or solution which becomes transparent after drying. The formation of the top coat layer 4 is optional. Generally, when the surface is polished, the resin layer is polished and the light is irregularly reflected due to the roughness of the surface, though depending on the degree and method of polishing. In some cases, the overall color tone may become slightly whitish, and if it is desired to provide a color tone that suppresses this or to impart more gloss, it is preferable to provide a layer of the top coat 4.

【００４０】トップコート層に用いられる乾燥後透明な
樹脂層を形成し得る合成樹脂エマルションまたは溶液と
しては、前述した塗布材用の合成樹脂エマルションまた
は溶液成分として例示したと同様な合成樹脂エマルショ
ンまたは溶液を用いることができる。トップコート層
は、装飾材に表面光沢を付与したい場合とか、耐候性、
耐水性、防汚性などの性質を更に付与するために用いら
れるが、すべての種類の表面仕上用装飾材に施されるこ
とが必須のものではなく、余り表面光沢を出したくない
装飾材に仕上げる場合には使用されないか、艶消し剤を
添加したトップコート剤が用いられる。The synthetic resin emulsion or solution used for the top coat layer which can form a transparent resin layer after drying includes the same synthetic resin emulsion or solution as exemplified above as the synthetic resin emulsion or solution component for the coating material. Can be used. The top coat layer can be used to add surface gloss to decorative materials, weather resistance,
It is used to further impart properties such as water resistance and antifouling properties, but it is not essential that it be applied to all types of decorative materials for surface finishing, and to decorative materials that do not want to give too much surface gloss It is not used for finishing, or a top coat agent to which a matting agent is added is used.

【００４１】かかる工程により第１の層１の模様と第２
の層の２ａ、２ｂの２色模様不定形模様が表面に発現し
ている変成岩調模様を有する装飾材が得られる。尚、図
４に示した本発明の装飾材の模様は、蛇紋岩調の模様の
ものを示したが、何らこれのみに限定されるものではな
い。本発明の装飾材の模様としては、変成岩調模様が重
厚で高級感があり特に好ましく、また、本発明において
は特にかかる変成岩調模様の装飾材を比較的容易に製造
し得ると言う利点があるが、この様な不定形模様だけで
なく、他の模様、例えば花柄摸様とか唐草模様などその
他の任意の定形模様なども必要に応じて容易に作成可能
である。この場合でも重厚感、高級感を有する装飾材が
得られる。According to this process, the pattern of the first layer 1 and the second layer
A decorative material having a metamorphic rock-like pattern in which the two-color pattern irregular-shaped pattern 2a, 2b of the layer is developed on the surface is obtained. The pattern of the decorative material of the present invention shown in FIG. 4 has a serpentine pattern, but is not limited to this. As the pattern of the decorative material of the present invention, a metamorphic rock-like pattern is heavy and has a high-class feeling, which is particularly preferable. In the present invention, there is an advantage that the decorative material of the metamorphic rock-like pattern can be relatively easily produced. However, in addition to such an irregular pattern, other patterns such as a flower pattern or an arabesque pattern can be easily created as required. Even in this case, a decorative material having a solid feeling and a luxury feeling can be obtained.

【００４２】本発明において色調の異なる２種以上の第
２の塗布材を用いる場合において、その乾燥後の色調に
差が生じるようにするには、各塗布材の着色材や骨材の
配合を調整する。目的とする色調差によって異なるが、
色調差は例えば、塗布材の乾燥後の色相、明度、彩度の
少なくとも１つが異なるように調整することによって達
成される。そして、好ましくは塗布材の乾燥後の明度の
差異の範囲が，マンセル値で０．５〜４とするか（この
場合、彩度の差異はマンセル値で０でもよい。）、彩度
の差異の範囲が，マンセル値で１〜５の範囲にするか
（この場合、明度の差異はマンセル値で０でもよ
い。）、その両者を満足させる範囲にするか、更にこの
両者の範囲を満足し色相を異ならせる範囲の色調差とす
ると、特に変成岩により類似した重厚性、深みを有する
装飾材を作成する場合に有利であり好ましい。尚、塗布
材の色調差を乾燥後の色調で比べるのは、乾燥前で色調
を整えておけば通常の場合十分であるが、一部のものに
は乾燥前と乾燥後で色調が若干異なってくるものもある
ので、乾燥後の色調で比べることが好ましいためであ
る。もし、表面に現れるいずれか少なくとも１つの層中
に斑点状模様に肉眼ではっきり認識できる程度の骨材
や、色彩の異なる比較的小さな斑点状模様が存在する場
合には、通常色調の相違は斑点状模様部分を除いたベー
スとなる部分の色調で比較する。また、もし第１の層の
形成に用いる第１の塗布材として、２種以上の色調の異
なる塗布材を用いる場合も同様である。When two or more kinds of second coating materials having different color tones are used in the present invention, in order to cause a difference in the color tone after drying, the coloring material and the aggregate of each coating material must be mixed. adjust. It depends on the target color tone difference,
The color tone difference is achieved, for example, by adjusting at least one of the hue, lightness, and saturation of the applied material after drying. Preferably, the range of the difference in brightness after drying of the coating material is 0.5 to 4 in Munsell value (in this case, the difference in saturation may be 0 in Munsell value) or the difference in saturation. Is a range of 1 to 5 in Munsell value (in this case, the difference in brightness may be 0 in Munsell value), a range that satisfies both of them, or a range that satisfies both ranges. A color tone difference in a range in which the hue is different is advantageous and preferable particularly when a decorative material having a similar depth and depth to metamorphic rocks is produced. In addition, it is usually sufficient to compare the color tone difference of the coating material with the color tone after drying if the color tone is adjusted before drying, but in some cases the color tone is slightly different before and after drying. This is because it is preferable to compare the color tone after drying, since some of the color tone may come. If at least one of the layers that appear on the surface contains a spotted pattern with aggregates that are clearly recognizable to the naked eye or a relatively small spotted pattern with a different color, the difference in color tone is usually a spotted pattern. The comparison is made based on the color tone of the base part excluding the pattern part. The same applies to the case where two or more kinds of coating materials having different color tones are used as the first coating material used for forming the first layer.

【００４３】尚、マンセル値は、色彩学などの各種書籍
に掲載されていて、著名であるので説明は省略する。例
えぱ「マンセル ブック オブ カラー、 ネーバリン
グヒューズ 版」（米国メリーランド州ボルチモアのマ
ンセル カラー カンパニー インコーポレーテッド発
行）（MUNSELL BOOK OF COLOR, NEIGHBORING HUESEDIT
ION, MUNSELL COLOR COMPANY, Inc. BALTIMORE ・ MAR
YLAND U.S.A.）などに掲載されている。Incidentally, the Munsell value is published in various books such as chromatics and is well-known, and therefore its description is omitted. For example, "Munsell Book of Color, a Neighboring Fuse Edition" (published by Mansell Color Company, Inc. of Baltimore, Maryland, USA) (MUNSELL BOOK OF COLOR, NEIGHBORING HUESEDIT
ION, MUNSELL COLOR COMPANY, Inc. BALTIMORE ・ MAR
YLAND USA).

【００４４】尚、２種類以上の第２の塗布材の相互間の
色調は余り色調差が極端に大きく異ならない方が重厚な
落ち着いた感じの装飾材が得られ好ましい。一方、第１
の層は第２の層と比べてその模様がある程度目立つよう
に第１の層の周辺に存在する第２の層の色調とはやや大
き目に異なる方が好ましく、特に明度の点で、乾燥後の
明度の差異が、マンセル値で１より大きいことが好まし
い。マンセル値で１より大きい明度の差があれば、第１
の層が第２の層と比べて明度が高い組合わせのものでも
良いし、第１の層が第２の層と比べて明度が低い組合わ
せのものでも良い。以上は好ましい色調の差について説
明したが、必ずしもこれに限られるものではなく、色相
で差をつけても良いし、彩度で差をつけても良いが、こ
のうちでは明度と色相のファクターが色調の差異を顕著
にする要因としては大きな比重を占めると言える。実際
には明度と色相と彩度の３つのファクターが組み合わさ
れて顕著な色調の差を実現することが多い。It is preferable that the color tone between two or more kinds of the second coating materials does not significantly differ so much as to obtain a thick and calm decorative material. Meanwhile, the first
It is preferable that the color of the second layer is slightly different from the color tone of the second layer existing around the first layer so that the pattern is more noticeable than the second layer. Is preferably greater than 1 in Munsell value. If there is a brightness difference greater than 1 in the Munsell value, the first
May be a combination having a higher brightness than the second layer, or a combination of the first layer having a lower brightness than the second layer. The preferred color difference has been described above. However, the present invention is not necessarily limited to this. A difference may be given by hue or a difference may be given by saturation. It can be said that the factor that makes the difference in color tone remarkable occupies a large proportion. In practice, three factors of lightness, hue, and saturation are often combined to realize a remarkable difference in tone.

【００４５】また、必要に応じて装飾材全体の厚みを厚
くするために用いられる第３の層については、前述した
ようにその色調はほとんど考慮する必要はなく、各塗布
材の回収物の混合物などを用いることも差し支えない。As described above, the color tone of the third layer used to increase the thickness of the entire decorative material, if necessary, does not need to be considered. It is also acceptable to use such a method.

【００４６】各塗布材には、更に必要に応じて充填材、
造膜助剤、増粘剤、消泡剤、ｐＨ調整剤などを加えた
り、粘度を調整するために水などや適宜の溶剤などを加
えてもよい。Each coating material may further include a filler, if necessary.
A film forming aid, a thickener, a defoaming agent, a pH adjuster, and the like may be added, and water or an appropriate solvent may be added to adjust the viscosity.

【００４７】例えば、充填材としては炭酸カルシウムな
ど、増粘剤としては例えばメチルセルロース系のもの
（たとえば“ハイメトローズ９０ＳＨ−３００００”、
信越化学（株）社製）、造膜助剤としては例えばブチル
カルビトールアセテートなど、消泡剤としては例えば
“ノプコサントＮＸＺ”（サンノプコサン（株）社製）
など、ｐＨ調整剤としては濃アンモニア水などが好適に
用いられるが、これらのみに限定されるものではない。For example, as a filler, calcium carbonate or the like, and as a thickener, for example, a methylcellulose-based one (for example, “Hymetrose 90SH-30000”,
Shin-Etsu Chemical Co., Ltd.), as a film-forming aid, for example, butyl carbitol acetate, and as a defoaming agent, for example, "Nopcosanto NXZ" (manufactured by San Nopcosan Co., Ltd.)
For example, concentrated ammonia water or the like is preferably used as the pH adjuster, but is not limited thereto.

【００４８】本発明の装飾材に於てはその裏側にシート
状基材が積層されていることが装飾材の強度をより大き
くでき、従って取扱がより容易な装飾材を提供できる点
からも好ましいが、かかるシート状基材としては、布状
のシート基材が特に好ましく、具体的には、例えば合成
繊維や無機繊維からなる織物や不織布、たとえばより具
体的には、アクリル繊維やポリエステル繊維からなる寒
冷紗や不織布、ガラス繊維織物、グラスウール不織布、
合成紙などの布帛類が好ましい。吸水性のない又は吸水
性の小さい布帛類が好ましいのは、吸水性の大きいもの
は水分により膨張し、乾燥時に収縮しやすい傾向があ
り、乾燥後の製品が反ったりして変形する恐れがある
が、吸水性のない又は吸水性の小さい布状物を用いた場
合にはこの様な問題が生じないので好ましい。In the decorative material of the present invention, it is preferable that a sheet-like base material is laminated on the back side, since the strength of the decorative material can be increased, and a decorative material which can be easily handled can be provided. However, as such a sheet-like substrate, a cloth-like sheet substrate is particularly preferable, and specifically, for example, a woven or nonwoven fabric made of synthetic fibers or inorganic fibers, for example, more specifically, an acrylic fiber or a polyester fiber Cold gauze and nonwoven fabric, glass fiber woven fabric, glass wool nonwoven fabric,
Fabrics such as synthetic paper are preferred. Non-absorbent or low-absorbent fabrics are preferred because those with high water absorption tend to expand due to moisture and tend to shrink during drying, and the product after drying may warp and deform. However, when a cloth material having no or low water absorption is used, such a problem does not occur, which is preferable.

【００４９】また、布状シート基材が好ましいのは、柔
軟な装飾材の場合にはその柔軟性を阻害しないことや、
布は通気性があるため鋳型で本発明の装飾材を成型し乾
燥させる場合に、水分や溶剤などを鋳型の存在しない
側、すなわち裏側から容易に蒸発させることができるか
らである。また布帛類以外の基材としては、本発明の様
な鋳型による成型でなく、基材の上に第３の塗布材を適
宜の形状で塗布し乾燥し又は乾燥せずに、第２の塗布材
を塗布し乾燥し、ついで第１の塗布材を塗布し乾燥する
方法などの様に表側から乾燥する方法を採用する場合に
は、例えばコンクリートパネル押出成形セメント板、石
膏ボード、硅カル板（硅酸カルシウム板）、アルミニウ
ムシートや亜鉛引鋼板その他の金属板、金属金網、エキ
スパンドメタル、ゴムシート、合成樹脂シートなどを用
いてもよい。また、これらのシートでも穴開きのものを
用いれば、鋳型を用いる本発明方法にも適用可能であ
る。Further, the cloth-like sheet substrate is preferable because, in the case of a soft decorative material, it does not impair the flexibility.
This is because, since the cloth has air permeability, when the decorative material of the present invention is molded with a mold and dried, moisture and a solvent can be easily evaporated from the side where no mold is present, that is, from the back side. As a substrate other than fabrics, a third coating material is applied in an appropriate shape on a substrate and dried or not dried. When a method of applying and drying a material from the front side, such as a method of applying and drying a first coating material and then drying the same, is used, for example, a concrete panel extruded cement board, a gypsum board, a silica board ( A calcium silicate plate), an aluminum sheet, a zinc-plated steel plate or another metal plate, a metal wire mesh, an expanded metal, a rubber sheet, a synthetic resin sheet, or the like may be used. If these sheets are perforated, they can be applied to the method of the present invention using a mold.

【００５０】本発明方法の如く裏側にシート状基材を積
層する場合には、前述したように通常、第２の塗布材ま
たは第３の塗布材を塗布後、その表面が乾燥する前にシ
ート状基材を積層し、必要に応じて積層後その上を例え
ば適宜のローラーなどで押さえてから乾燥させる方法を
採用してもよい。In the case of laminating a sheet-like base material on the back side as in the method of the present invention, as described above, usually, after the second coating material or the third coating material is applied, the sheet is dried before the surface is dried. It is also possible to adopt a method in which the base materials are laminated, and if necessary, after lamination, the surface is pressed with, for example, a suitable roller and then dried.

【００５１】本発明の装飾材の製造方法を実施する際に
使用する凹凸反転レリーフ模様を有する鋳型としては、
特に限定するものではないがシリコンゴムの鋳型やポリ
エステルフィルムまたはその発泡体シート、ポリオレフ
ィンフィルムまたはその発泡体シートなどの適宜のプラ
スチックフィルムまたはシート（発泡体シートを含む）
からなる鋳型が好適に用いられる。As a mold having a concave-convex inversion relief pattern used in carrying out the method for manufacturing a decorative material of the present invention,
Although not particularly limited, an appropriate plastic film or sheet (including a foam sheet) such as a silicone rubber mold, a polyester film or its foam sheet, a polyolefin film or its foam sheet, etc.
Is preferably used.

【００５２】また、好ましい鋳型の製法としては、所望
の表面模様が描写されている写真ないしは絵を原画とし
て、デジタル光彫刻システムにより感光性合成樹脂又は
感光性ゴム状物からなる凹凸レリーフ模様を有する母型
を作成し、前記母型に鋳型形成用の合成樹脂を流し込ん
で固めて前記母型から離型させて得られた凹凸反転レリ
ーフ模様を有する鋳型である。かかるデジタル光彫刻シ
ステムにおいては、所望の表面模様が描写されている平
面状の凹凸のない写真ないしは絵を原画として、スキャ
ナーなどでコンピューターに読み取り、それにどの部分
をどの程度の深さに彫るか指令を与え、光の強弱などを
コントロールし、ポジ型またはネガ型の感光性合成樹脂
又は感光性ゴム状物のシートに前記コントロールされた
光を照射し、ポジ型またはネガ型に応じて光で硬化され
た溶剤に不溶になった部分を残し、光の照射のされなか
った部分や照射の少ない部分をその程度に応じて溶剤で
溶かし出したり、あるいはその逆の原理を応用して、光
が照射されずに溶剤に不溶のままの部分を残し、光が照
射されて溶剤に溶解性となった部分をその程度に応じて
溶剤で溶かし出すなどの手法により、凹凸レリーフ模様
を有する母型を作成し、母型からその反転凹凸レリーフ
模様を有する鋳型を通常の方法で作成する方法が、きわ
めて安易で且つ、凹凸の深さをある程度自由にコントロ
ールでき、好ましい鋳型が得られるので好ましい。特に
変成岩調などの複雑な模様の鋳型も極めて簡単に得るこ
とが出来好ましい。かかるデジタル光彫刻システムは、
上市されており、例えば“ニッペ デジタル光彫刻シス
テム”(日本ペイント株式会社)などが利用可能である。Further, as a preferable method for producing a mold, a concave or convex relief pattern made of a photosensitive synthetic resin or a photosensitive rubber-like material is formed by a digital optical engraving system using a photograph or a picture on which a desired surface pattern is drawn as an original image. A mold having a concave-convex inversion relief pattern obtained by forming a master mold, pouring a synthetic resin for forming a mold into the master mold, solidifying the mold, and releasing the mold from the master mold. In such a digital optical engraving system, a photo or picture without a flat uneven surface on which a desired surface pattern is drawn is read as an original image by a computer using a scanner or the like, and a command is issued as to which part is to be carved to what depth. To control the intensity of light and the like, irradiate the above-mentioned controlled light to a positive or negative type photosensitive synthetic resin or photosensitive rubber-like sheet, and cure with light according to the positive or negative type. Depending on the degree of exposure, light can be dissolved out of the unirradiated or light-irradiated parts, or vice versa. The part that remains insoluble in the solvent is left unremoved, and the part that has become soluble in the solvent when irradiated with light is dissolved with a solvent according to its degree. A method in which a matrix having a pattern is formed, and a mold having an inverted concave-convex relief pattern is formed from the matrix by a usual method is extremely easy, and the depth of the concave-convex can be controlled to some extent freely, and a preferable mold is obtained. Is preferred. Particularly, a mold having a complicated pattern such as metamorphic rock tone can be obtained very easily, which is preferable. Such digital optical engraving systems are:
It is on the market, and for example, "Nippe Digital Optical Engraving System" (Nippon Paint Co., Ltd.) can be used.

【００５３】乾燥後透明となる合成樹脂エマルションま
たは溶液を薄く塗布しトップコート層を形成するのに用
いられる合成樹脂エマルションまたは溶液としては、前
記塗布材の合成樹脂エマルションまたは溶液と同様の合
成樹脂エマルションまたは溶液が使用でき、このうちで
もアクリル系樹脂エマルションが一般的に好ましく用い
られ、特にアクリル−シリコン樹脂系エマルション、ア
クリル−弗素樹脂系エマルション等が耐候性、耐水性、
防汚性に特に優れており好ましい。The synthetic resin emulsion or solution used to form a top coat layer by applying a thin synthetic resin emulsion or solution that becomes transparent after drying is the same as the synthetic resin emulsion or solution of the coating material. Or a solution can be used, and among them, acrylic resin emulsions are generally preferably used. In particular, acrylic-silicone resin-based emulsions, acrylic-fluorine resin-based emulsions and the like are weather-resistant, water-resistant,
It is particularly excellent in antifouling property and is preferable.

【００５４】以上、本発明の装飾材は天然の変成岩やそ
の他の天然石の平板状物に比べて軽いし、天然の変成岩
やその他の天然石の平板状物の様に脆くないので作業中
に落したり、運搬中の不注意などによる多少の衝撃が加
わっても欠けたりする恐れが少なく、取り扱いが容易で
あり、高所などでの作業もやりやすくなる。又、天然の
大理石など酸性雨などの酸に弱い変成岩では使用できな
い屋外用としても用いることができる。As described above, the decorative material of the present invention is lighter than natural metamorphic rocks and other natural stone slabs, and is not brittle like natural metamorphic rocks and other natural slabs, so that it can be dropped during work. There is little risk of chipping even if a slight impact is applied due to carelessness during transportation, etc., and handling is easy, and work at high places and the like is easy. It can also be used for outdoor use that cannot be used with metamorphic rocks that are sensitive to acids such as acid rain such as natural marble.

【００５５】そして従来の合成品ではなし得なかった、
重厚さ、深みに富んだ高級感を有する表面に模様が形成
された装飾材を得ることができる。特に本発明は天然の
変成岩の平板状物と同等な重厚さ、深みに富んだ高級感
を有する変成岩調模様を有する装飾材も容易に得る事が
出来、このような高級感のある表面が平らな平板状装飾
材の製造に好適である。And it could not be done with conventional synthetic products,
It is possible to obtain a decorative material in which a pattern is formed on a surface having a high-class feeling rich in depth and depth. In particular, according to the present invention, it is possible to easily obtain a decorative material having a metamorphic rock-like pattern having a thickness equivalent to that of a flat plate of a natural metamorphic rock and a rich sense of quality, and such a high-grade surface is flat. It is suitable for producing a flat flat decorative material.

【００５６】従って本発明の装飾材は、建築物や構築物
の表面、例えば、建築物内外装壁面や床面、支柱の表
面、塀の表面、宅地造成の法面、建築物用擁壁、高架道
路や橋梁などの壁面や脚柱の外装、横断歩道橋の外壁、
トンネルなどの出入口などの表面仕上げ用の装飾材とし
て、好適に用いられる。Accordingly, the decorative material of the present invention can be used for the surface of a building or a building, for example, the interior and exterior walls and floors, the surface of a column, the surface of a fence, the slope of a residential land, the retaining wall for a building, an elevated surface. Exterior of walls and pillars such as roads and bridges, outer walls of pedestrian crossings,
It is suitably used as a decorative material for surface finishing such as entrances and exits of tunnels.

【００５７】[0057]

【実施例】以下、より具体的な実施例を挙げて更に本発
明を説明するが、本発明はこの実施例のもののみに限定
されるものではない。EXAMPLES Hereinafter, the present invention will be further described with reference to more specific examples, but the present invention is not limited to only these examples.

【００５８】実施例１ 巾９３０ｍｍ、長さ６３０ｍｍの大きさの天然の蛇紋岩
の表面写真から、前述のデジタル光彫刻システム“ニッ
ペ デジタル光彫刻システム”（日本ペイント株式会
社）を利用して感光性ゴム状物より凹凸レリーフ模様を
有する母型を作成し、前記母型面に、型取り用シリコン
ゴム（信越化学工業（株）製の“信越シリコンＫＥ−１
４１４”）を用いて型取りした後、シリコンゴムを母型
から剥離した。シリコンゴムの使用量は１Ｋｇ／０．７
５ｍ2 であった。Example 1 Photosensitivity was obtained from a photograph of the surface of a natural serpentine having a width of 930 mm and a length of 630 mm using the above-mentioned digital optical engraving system "Nippe Digital Optical Engraving System" (Nippon Paint Co., Ltd.). A matrix having an uneven relief pattern was formed from a rubber-like material, and a silicone rubber for molding (Shin-Etsu Silicon KE-1 manufactured by Shin-Etsu Chemical Co., Ltd.) was formed on the matrix.
414 "), and the silicone rubber was peeled off from the matrix. The amount of the silicone rubber used was 1 kg / 0.7.
It was 5 m 2 .

【００５９】以上の様に作製したシリコンゴムの凹凸反
転レリーフ型シートの周囲の４辺を断裁して、９３０mm
×６３０mmの大きさに加工して鋳型を作成した。鋳型を
基板台（ベニヤ板５．５mm厚 ９２０×６２０mm）の上
に、凹凸反転レリーフ模様が形成されている面を上にし
て置く。The four sides around the relief-type sheet of silicon rubber produced as described above are cut out to 930 mm.
A mold was prepared by processing to a size of × 630 mm. The mold is placed on a substrate table (5.5 mm thick, 920 × 620 mm plywood) with the surface on which the uneven relief pattern is formed facing up.

【００６０】次いで第２の層を形成するための第２の塗
布材として、第２の塗布材ａとｂとを用意した。 第２の塗布材ａ ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：変成岩骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
６５００ｇと、変成岩骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２０００ｇ、 ［着色骨材］：ベージュ系着色焼成硅砂［新東陶料
（株）製“２０Ｙ２０５”（粒子サイズ８号 ：粒径
０．１８〜０．２５ｍｍ）］５００ｇと、イエロー系着
色焼成硅砂［新東陶料（株）製“６７ イエロー”（粒
子サイズ６号と７号の混合：粒径０．３０〜０．３５ｍ
ｍ）］３００ｇと、オレンジ系着色焼成硅砂［新東陶料
（株）製“Ｎｏ．８ バフ”（粒子サイズ８号 ：粒径
０．１８〜０．２５ｍｍ）］７００ｇ、 とから調整された第２の塗布材ａ（調合乾燥後の色が比
較的鮮明なベージュ系の色、マンセル値が１０ＹＲ ８
／４、ここで１０ＹＲは色相を表す記号で赤色よりの黄
色を示している。８／４の８は明度を示す記号で、数値
が大きい方が明るい色であることを示している。４は彩
度を示す記号で、数値が大きい方が鮮やかな色であるこ
とを示している。） 第２の塗布材ｂ ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：天然石骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
６５００ｇと、天然石骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２０００ｇ、 ［着色骨材］：ベージュ系着色焼成硅砂［新東陶料
（株）製“２０Ｙ２０５”（粒子サイズ８号 ：粒径
０．１８〜０．２５ｍｍ）］２００ｇと、イエロー系着
色焼成硅砂［新東陶料（株）製“６７ イエロー”（粒
子サイズ６号と７号の混合：粒径０．３０〜０．３５ｍ
ｍ）］４００ｇと、オレンジ系着色焼成硅砂［新東陶料
（株）製“Ｎｏ．８ バフ”（粒子サイズ８号 ：粒径
０．１８〜０．２５ｍｍ）］９００ｇ、 とから調整された第２の塗布材ｂ（調合乾燥後の色がや
や混濁したベージュ系の色、マンセル値が１０ＹＲ ８
／３）を、塗布器具として吹付ガン（２頭ガン：各ノズ
ルの口径８mm）を用いて塗布量が約３ｋｇ／ｍ2 となる
様に前記鋳型に吹付けて、その直後にスポンジローラー
にて塗布材を押さえつけて２色からなる第２の塗布材層
２（２ａ、２ｂ）を形成し、気温１６℃、湿度７５％で
６時間自然乾燥した。Next, second coating materials a and b were prepared as second coating materials for forming the second layer. Second coating material a [Synthetic resin emulsion]: Acrylic resin emulsion (“Polytron E-300” manufactured by Asahi Kasei Corporation) 3
000 g, [Aggregate]: metamorphic rock aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
6500 g and metamorphic rock aggregate (cold rock) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle size 0.075 to 0.1)
5g)] 2000g, [colored aggregate]: beige-colored calcined silica sand [Shinto Ceramics Co., Ltd. "20Y205" (particle size 8: particle size 0.18 to 0.25mm)] 500g, and yellow color Colored calcined silica sand [Shinto Toilei Co., Ltd. "67 Yellow" (Particle size No. 6 and No. 7: particle size 0.30 to 0.35 m
m)] and 300 g of orange-colored calcined silica sand [“No. 8 buff” manufactured by Shinto Tohoku Co., Ltd. (particle size: 8: particle size 0.18 to 0.25 mm)] 700 g. Second coating material a (beige color having a relatively clear color after preparation and drying, Munsell value is 10 YR 8
/ 4, where 10YR is a symbol representing hue, indicating yellow over red. 8 of 8/4 is a symbol indicating lightness, and the larger the numerical value, the brighter the color. 4 is a symbol indicating the saturation, and the larger the numerical value, the brighter the color. ) Second coating material b [Synthetic resin emulsion]: Acrylic resin emulsion (“Polytron E-300” manufactured by Asahi Kasei Kogyo Co., Ltd.) 3
000 g, [Aggregate]: natural stone aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
6500 g, natural stone aggregate (cold water stone) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle diameter 0.075 to 0.1)
5 gm)] 2000 g, [colored aggregate]: beige-colored calcined silica sand [Shinto Ceramics Co., Ltd. “20Y205” (particle size 8: particle size 0.18 to 0.25 mm)] 200 g, and yellow color Colored calcined silica sand [Shinto Toilei Co., Ltd. "67 Yellow" (Particle size No. 6 and No. 7: particle size 0.30 to 0.35 m
m)] and 400 g of orange-colored calcined silica sand [“No. 8 buff” manufactured by Shinto Tohoku Co., Ltd. (particle size: 8: particle size: 0.18 to 0.25 mm)], and 900 g. Second coating material b (beige color in which the color after preparation and drying is slightly turbid, Munsell value is 10 YR 8
/ 3) was sprayed onto the mold using a spray gun (two-headed gun: 8 mm in diameter of each nozzle) as an applicator so that the application amount was about 3 kg / m 2, and immediately thereafter, with a sponge roller. The coating material was pressed down to form a second coating material layer 2 (2a, 2b) of two colors, which was naturally dried at a temperature of 16 ° C. and a humidity of 75% for 6 hours.

【００６１】次いで第３の層を形成するための第３の塗
布材として、第２の塗布材と同じものを、塗布器具とし
てタイルガン（吹付ガン）口径８mmを用いて塗布量が約
３ｋｇ／ｍ2 となる様に前記第２の塗布材層が形成され
ている上に吹付けて、第３の塗布材層を形成し、塗布後
すぐにポリエステル繊維の不織布を積層しローラーで押
さえ付けた。その後温度４５℃の乾燥室で８時間放置し
て乾燥し、乾燥後鋳型を取り外した。こうすることによ
り、表面側が第２の塗布材層２の２ａからなる比較的鮮
明なベージュ系の色を呈している部分と２ｂからなるや
や混濁したベージュ系の色を呈している部分で、これら
の塗布材層２ａと２ｂの明度のマンセル値の差が０で、
彩度のマンセル値の差が１の表面が凹凸模様の中間積層
体を得た。Next, as the third coating material for forming the third layer, the same coating material as that of the second coating material was applied, and the application amount was about 3 kg / m 2 using a tile gun (spray gun) having a diameter of 8 mm as an application tool. wherein the 2 become as by blowing on the second coating material layer is formed, the third to form a coating material layer was pressed by a nonwoven fabric was laminated rollers immediately polyester fibers after application. Then, it was left to dry in a drying room at a temperature of 45 ° C. for 8 hours, and after drying, the mold was removed. By doing so, the surface portion of the second coating material layer 2 having a relatively clear beige color composed of 2a and the portion composed of 2b exhibiting a slightly turbid beige color, The difference between the Munsell values of the lightness of the coating material layers 2a and 2b is 0,
An intermediate laminate having a surface having a concavo-convex pattern with a difference in the Munsell value of saturation of 1 was obtained.

【００６２】この中間積層体の第２の塗布材層が塗布さ
れている側から下記の組成の第１の塗布材をノズル口径
６ｍｍの吹付ガンを用いて第２の塗布材層の全面に表面
全体がほぼ同じ高さ（レベル）になる様に塗布し、温度
４５℃の乾燥室で８時間放置して乾燥した。 第１の塗布材 ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：天然石骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
７５００ｇと、天然石骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２５００ｇ、 とから調整された第１の塗布材（調合乾燥後の色が白
色、マンセル値がＮ−９．０）。A first coating material having the following composition was applied to the entire surface of the second coating material layer from the side where the second coating material layer was coated, using a spray gun having a nozzle diameter of 6 mm. The coating was applied so that the whole was almost the same height (level), and was left to dry in a drying room at a temperature of 45 ° C. for 8 hours. First coating material [Synthetic resin emulsion]: Acrylic resin emulsion (“Polytron E-300” manufactured by Asahi Kasei Kogyo Co., Ltd.) 3
000 g, [Aggregate]: natural stone aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
7500 g and natural stone aggregate (cold water stone) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle diameter 0.075 to 0.1)
5 mm)] 2500 g, the first coating material (the color after blending and drying is white, and the Munsell value is N-9.0).

【００６３】得られた図２の（ｆ）に相当する段階の状
態の積層物の表面から、点線ライン７（矢印Ａ−Ａ’ラ
イン）で例示した様に、図２の（ｇ）の段階で例示した
様な第１の層が部分的に表面に残り、かつ、第２の層２
（２ａと２ｂ）とが表面に現れる程度に、表面全面が平
面になる様に第１の層を形成した側から平らに研磨し、
第１の層１と第２の層２（２ａと２ｂ）とからなり、第
１の層１が白色で目立った不定形模様が表面に発現して
いる図５に示した様な平板状蛇紋岩調模様でありながら
ベージュ色をベースに有する装飾材を得た。As shown by the dotted line 7 (arrow AA ′ line) from the surface of the obtained laminate at the stage corresponding to FIG. 2F, the stage of FIG. The first layer as exemplified in (1) partially remains on the surface and the second layer 2
(2a and 2b) is polished flat from the side where the first layer is formed so that the entire surface is flat, to the extent that (2a and 2b) appear on the surface.
A plate-like serpentine pattern as shown in FIG. 5 in which a first layer 1 is composed of a first layer 1 and a second layer 2 (2a and 2b), and the first layer 1 has a white and conspicuous irregular pattern on its surface. A decorative material having a rock-like pattern but having a beige base was obtained.

【００６４】実施例２ 実施例１で用いたと同様の凹凸レリーフ模様が形成され
ている鋳型を用意し、この鋳型を基板台（ベニヤ板５．
５mm厚 ９２０×６２０mm）の上に、鋳型の凹凸レリー
フ模様が形成されている面を上にして置く。Example 2 A mold having a relief pattern similar to that used in Example 1 was prepared, and this mold was mounted on a substrate table (Veneer board 5.
The mold is placed on a 5 mm thick 920 × 620 mm) with the surface on which the relief pattern of the mold is formed facing up.

【００６５】次いで第２の層を形成するための第２の塗
布材として、第２の塗布材ａとｂとを用意した。 第２の塗布材ａ ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：天然石骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
６５００ｇと、天然石骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２０００ｇ、 ［着色骨材］：グリーン系着色焼成硅砂［新東陶料
（株）製“Ｎｏ．８グリーン”（粒子サイズ８号 ：粒
径０．１８〜０．２５ｍｍ）］１５００ｇ、とから調整
された第２の塗布材ａ（調合乾燥後の色がグリーン系の
色、マンセル値が７．５Ｇ ６／２） 第２の塗布材ｂ ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：天然石骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
４１００ｇと、天然石骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２０００ｇ、 ［着色骨材］：ブラック系着色焼成硅砂［新東陶料
（株）製“２０Ｎ−１”（粒子サイズ８号：粒径０．１
８〜０．２５ｍｍ）］３９００ｇと、 とから調整された第２の塗布材ｂ（調合乾燥後の色が黒
色、マンセル値がＮ−４．０）を、塗布器具として吹付
ガン（２頭ガン：各ノズルの口径８mm）を用いて塗布量
が約３Ｋｇ／ｍ2 となる様に前記鋳型に吹付けて２色か
らなる第２の塗布材層２（２ａ、２ｂ）を形成し、気温
１６℃、湿度７５％で６時間自然乾燥した。Next, the second coating materials a and b were prepared as the second coating material for forming the second layer. Second coating material a [Synthetic resin emulsion]: Acrylic resin emulsion (“Polytron E-300” manufactured by Asahi Kasei Corporation) 3
000 g, [Aggregate]: natural stone aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
6500 g, natural stone aggregate (cold water stone) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle diameter 0.075 to 0.1)
5 mm)] 2000 g; [Colored aggregate]: green colored calcined silica sand [Shinto Ceramics Co., Ltd. “No. 8 Green” (particle size 8: particle size 0.18 to 0.25 mm)] 1500 g; (A color after preparation and drying is a green color, and a Munsell value is 7.5G 6/2). A second coating material b [synthetic resin emulsion]: an acrylic resin emulsion ( "Polytron E-300" manufactured by Asahi Kasei Corporation) 3
000 g, [Aggregate]: natural stone aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
4100 g and natural stone aggregate (cold water stone) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle diameter 0.075 to 0.1)
5 mm)] 2000 g, [colored aggregate]: black-colored calcined silica sand [“20N-1” manufactured by Shinto Tohzo Co., Ltd. (particle size 8: particle size 0.1)
8 to 0.25 mm)] as a spraying gun (two-head gun) as a coating tool using the second coating material b (the color after blending and drying is black, the Munsell value is N-4.0) adjusted to 3900 g. A second coating material layer 2 (2a, 2b) of two colors is formed by spraying the mold using the nozzle with a diameter of 8 mm so that the coating amount is about 3 kg / m 2. It air-dried for 6 hours at 75 degreeC and 75% of humidity.

【００６６】次いで第３の層を形成するための第３の塗
布材として、第２の塗布材と同じものを、塗布器具とし
てタイルガン（吹付ガン）口径８mmを用いて塗布量が約
３ｋｇ／ｍ2 となる様に前記第２の塗布材層が形成され
ている上に吹付けて、第３の塗布材層を形成し、塗布後
すぐにポリエステル繊維の不織布を積層しローラーで押
さえ付けた。その後温度４５℃の乾燥室で８時間放置し
て乾燥し、乾燥後鋳型を取り外した。こうすることによ
り、表面側が第２の塗布材層２の２ａからなるグリーン
系の色を呈している部分と２ｂからなる黒系の色を呈し
ている部分で、これらの塗布材層２ａと２ｂの明度のマ
ンセル値の差が２で、彩度のマンセル値の差が２の表面
が凹凸模様の中間積層体を得た。Next, as the third coating material for forming the third layer, the same material as the second coating material was applied, and the application amount was about 3 kg / m 2 using a tile gun (spray gun) having a diameter of 8 mm as an application tool. wherein the 2 become as by blowing on the second coating material layer is formed, the third to form a coating material layer was pressed by a nonwoven fabric was laminated rollers immediately polyester fibers after application. Then, it was left to dry in a drying room at a temperature of 45 ° C. for 8 hours, and after drying, the mold was removed. In this manner, the surface of the second coating material layer 2 has a green-colored portion composed of 2a and a portion of the second coating material layer 2 having a black color composed of 2b. The difference in the Munsell value of the brightness was 2 and the difference in the Munsell value of the saturation was 2 to obtain an intermediate laminate having an uneven pattern on the surface.

【００６７】この中間積層体の第２の塗布材層が塗布さ
れている側から下記の組成の第１の塗布材をノズル口径
６ｍｍの吹付ガンを用いて第２の塗布材層の全面に表面
全体がほぼ同じ高さ（レベル）になる様に塗布し、温度
４５℃の乾燥室で８時間放置して乾燥した。 第１の塗布材 ［合成樹脂エマルション］：アクリル樹脂系エマルショ
ン（旭化成工業（株）製“ポリトロンＥ−３００”）３
０００ｇ、 ［骨材］：天然石骨材（寒水石）［（株）同和カルファ
イン製“ＫＤ−１”（粒径０．３５〜０．５５ｍｍ）］
８０００ｇと、天然石骨材（寒水石）［（株）同和カル
ファイン製“ＫＤ−１００”（粒径０．０７５〜０．１
５ｍｍ）］２０００ｇ、 とから調整された第１の塗布材（調合乾燥後の色が白
色、マンセル値がＮ−９．０）。The first coating material having the following composition was applied to the entire surface of the second coating material layer from the side of the intermediate laminate on which the second coating material layer was coated using a spray gun having a nozzle diameter of 6 mm. The coating was applied so that the whole was almost the same height (level), and was left to dry in a drying room at a temperature of 45 ° C. for 8 hours. First coating material [Synthetic resin emulsion]: Acrylic resin emulsion (“Polytron E-300” manufactured by Asahi Kasei Kogyo Co., Ltd.) 3
000 g, [Aggregate]: natural stone aggregate (cold water stone) [“KD-1” (particle size: 0.35 to 0.55 mm) manufactured by Dowa Calfine Co., Ltd.]
8000 g, natural stone aggregate (cold water stone) [“KD-100” manufactured by Dowa Calfine Co., Ltd. (particle size: 0.075 to 0.1)
5 mm)] 2000 g, the first coating material (color after blending and drying is white, Munsell value is N-9.0).

【００６８】得られた図２の（ｆ）に相当する段階の状
態の積層物の表面から、点線ライン７（矢印Ａ−Ａ‘ラ
イン）で例示した様に、図２の（ｇ）の段階で例示した
様な第１の層が部分的に表面に残り、かつ、第２の層２
（２ａと２ｂ）とが表面に現れる程度に、表面全面が平
面になる様に第１の層を形成した側から平らに研磨し、
更に研磨した面側から図２（ｈ）で示したようにトップ
コートとして乾燥すると透明になるアクリル−シリコー
ン系樹脂エマルション塗料を口径１ｍｍの塗料ガンを用
いて２回塗布により０．２〜０．３ｋｇ／ｍ2 となるよ
うに均一に塗布して仕上た。As shown by the dotted line 7 (arrow AA ′ line) from the surface of the obtained laminate at the stage corresponding to FIG. 2F, the stage of FIG. The first layer as exemplified in (1) partially remains on the surface and the second layer 2
(2a and 2b) is polished flat from the side where the first layer is formed so that the entire surface is flat, to the extent that (2a and 2b) appear on the surface.
Further, as shown in FIG. 2 (h), an acryl-silicone resin emulsion paint which becomes transparent when dried as a top coat from the polished surface side is applied twice using a paint gun having a diameter of 1 mm to 0.2 to 0. The composition was uniformly applied so as to be 3 kg / m 2 and finished.

【００６９】得られた装飾材は第１の層１と第２の層２
（２ａと２ｂ）とからなり、第１の層１が白色で目立っ
た不定形模様が表面に発現している図４に示した様な平
板状蛇紋岩調模様を有する装飾材であり、かつ表面が光
沢のある高級感のある蛇紋岩調の平板状装飾材であっ
た。The obtained decorative material comprises a first layer 1 and a second layer 2
(2a and 2b), wherein the first layer 1 is a decorative material having a plate-like serpentine-like pattern as shown in FIG. It was a serpentine-like flat decorative material with a glossy surface.

【００７０】[0070]

【発明の効果】（１）本発明の装飾材は、軽量で取扱が
容易であり、運搬中や作業中のちょっとした衝撃により
欠けたりする欠点が改良され、酸性雨などによる酸性環
境に対して耐久性があり、かつ重厚さ、深みに富んだ高
級感を有する模様を有する表面が平面の平板状の装飾材
を提供できる。(1) The decorative material of the present invention is lightweight and easy to handle, has an improved defect that it is chipped by a slight impact during transportation or work, and is durable in an acidic environment such as acid rain. It is possible to provide a flat plate-shaped decorative material having a flat surface having a pattern having a high quality feeling rich in thickness and depth.

【００７１】（２）また、前記（２）項に記載したよう
に、第１の層と第２の層から形成される模様が、変成岩
調模様である本発明の好ましい態様とすることにより、
天然の変成岩の平板状物と同等の、重厚さ、深みを有
し、高級感のある変成岩調模様を有する平板状の装飾材
を提供できる。(2) As described in the above item (2), the pattern formed from the first layer and the second layer is a metamorphic rock-like pattern according to a preferred embodiment of the present invention.
It is possible to provide a flat decorative material having a thickness and depth equivalent to that of a natural metamorphic rock plate and a high-grade metamorphic rock-like pattern.

【００７２】（３）また、前記（３）項に記載したよう
に、第２の層の下に骨材が分散されてなる合成樹脂層か
らなる第３の層を更に有する本発明の好ましい態様とす
ることにより、前記効果を損なわずに厚みの厚い平板状
の装飾材を提供できる。(3) As described in the above (3), a preferred embodiment of the present invention further comprising a third layer made of a synthetic resin layer in which an aggregate is dispersed below the second layer. By doing so, it is possible to provide a thick flat decorative material without impairing the effect.

【００７３】（４）また、前記（４）項に記載したよう
に、第２の層の下に更にシート状基材が積層されている
本発明の好ましい態様とすることにより、シート状基材
により補強されたより強度の改善された平板状の装飾材
を提供できる。(4) As described in the above (4), in a preferred embodiment of the present invention in which a sheet-like substrate is further laminated under the second layer, the sheet-like substrate The present invention can provide a flat decorative material reinforced by the above and having improved strength.

【００７４】（５）また、前記（５）項に記載したよう
に、第３の層の下に更にシート状基材が積層されている
本発明の好ましい態様とすることにより、厚みを厚くで
き、また、シート状基材により補強されたより強度の改
善された平板状の装飾材を提供できる。(5) As described in the above item (5), the thickness can be increased by adopting a preferred embodiment of the present invention in which a sheet-like substrate is further laminated under the third layer. Further, a flat decorative material reinforced with a sheet-like base material and having improved strength can be provided.

【００７５】（６）また、前記（６）項に記載したよう
に、シート状基材が布状物である本発明の好ましい態様
とすることにより、シート状基材が布状物であることに
より、軽さを保ち、又、柔軟性を阻害せず曲面にも施工
可能で、より強度の改善された平板状の装飾材を提供で
きる。(6) As described in the above item (6), by adopting a preferred embodiment of the present invention in which the sheet-like substrate is a cloth-like material, the sheet-like substrate is a cloth-like material. Accordingly, it is possible to provide a flat decorative material which is light in weight, can be applied to a curved surface without impairing flexibility, and has improved strength.

【００７６】（７）また、前記（７）項に記載したよう
に、第１の層と第２の層との色調の差異が、色相、明
度、彩度の少なくとも１つが異なるものである本発明の
好ましい態様とすることにより、より重厚さ、深みに富
んだ高級感を有する平板状の装飾材を提供できる。(7) As described in the above (7), the difference in the color tone between the first layer and the second layer is at least one of hue, lightness and saturation different from each other. By adopting a preferred embodiment of the present invention, it is possible to provide a flat-shaped decorative material having a richer and deeper sense of quality.

【００７７】（８）また、前記（８）項に記載したよう
に、第１の層と第２の層との色調の明度の差異が、マン
セル値で１より大きい本発明の好ましい態様とすること
により、第１の層による模様が引き立ち、重厚さ、深み
に富んだ、より高級感を有する平板状の装飾材を提供で
きる。(8) Further, as described in the above item (8), a preferable embodiment of the present invention is that the difference in lightness of the color tone between the first layer and the second layer is larger than 1 in Munsell value. Thereby, the pattern by the first layer is prominent, and it is possible to provide a flat-shaped decorative material which is rich in thickness and depth and has a higher quality.

【００７８】（９）また、前記（９）項に記載したよう
に、本発明の装飾材の製造方法によれば、軽量で取扱が
容易であり、運搬中や作業中のちょっとした衝撃により
欠けたりする欠点が改良され、酸性雨などによる酸性環
境に対して耐久性があり、しかも重厚さ、深みに富んだ
高級感のある模様を有する平板状の装飾材を容易に製造
し得る。(9) As described in the above item (9), according to the method for manufacturing a decorative material of the present invention, the decorative material is lightweight and easy to handle, and may be chipped by a slight impact during transportation or work. This makes it possible to easily produce a flat decorative material having durability, which is durable against an acidic environment caused by acid rain, etc., and which has a rich, deep, high-grade pattern.

【００７９】（１０）また、前記（１０）項に記載した
ように、第１の層と第２の層とから形成される模様が、
変成岩調模様である本発明の好ましい態様とすることに
より、天然の変成岩の平板状物と同等の、重厚さ、深み
を有し、高級感のある変成岩調模様を有する平板状の装
飾材を容易に製造できる。(10) As described in the above (10), the pattern formed from the first layer and the second layer is:
By adopting the preferred embodiment of the present invention which is a metamorphic rock pattern, a flat decorative material having a metamorphic rock-like pattern having the same thickness, depth and high quality as a natural metamorphic rock plate can be easily obtained. Can be manufactured.

【００８０】（１１）また、前記（１１）項に記載した
ように、凹凸反転レリーフ模様を有する鋳型が、所望の
表面模様が描写されている写真ないしは絵を原画とし
て、デジタル光彫刻システムにより感光性合成樹脂又は
感光性ゴム状物からなる凹凸レリーフ模様を有する母型
を作成し、前記母型に鋳型形成用の合成樹脂を流し込ん
で固めて前記母型から離型させて得られた凹凸反転レリ
ーフ模様を有する鋳型である本発明の好ましい態様とす
ることにより、所望の表面模様が描写されている平面状
の凹凸のない写真ないしは絵を原画とするのみで、その
原画でイメージされる表面模様に近い模様を有する平板
状の装飾材を容易に製造し得る鋳型を容易に作成でき、
従って所望の模様の高級感のある平板状の装飾材を容易
に製造し得る。(11) Further, as described in the above item (11), a mold having a concave-convex inverted relief pattern is exposed to light by a digital optical engraving system using a photograph or a picture on which a desired surface pattern is drawn as an original. A matrix having a relief pattern made of a conductive synthetic resin or a photosensitive rubber-like material is formed, and the synthetic resin for forming a mold is poured into the matrix, solidified, and released from the matrix to form a concavo-convex inversion. By adopting a preferred embodiment of the present invention, which is a mold having a relief pattern, only a photograph or a picture without a planar unevenness on which a desired surface pattern is drawn is used as an original image, and the surface pattern imaged by the original image is used. Can easily create a mold that can easily produce a flat decorative material having a pattern close to,
Therefore, it is possible to easily produce a high-quality flat decorative material having a desired pattern.

【００８１】（１２）また、前記（１２）項に記載した
ように、凹凸反転レリーフ模様を有する鋳型に、合成樹
脂エマルションまたは溶液中に骨材が分散されてなる第
２の層を形成するための１種類の第２の塗布材を塗布す
るか、または、互いに色調が異なる２種類以上の第２の
塗布材を模様状に塗布し、前記第２の塗布材を乾燥させ
又は半乾燥の状態で、この上全面に更に合成樹脂エマル
ションまたは溶液中に骨材が分散されてなる第３の層を
形成するための第３の塗布材を塗布する工程を更に含む
本発明の好ましい態様とすることにより、本発明の前記
効果を損なわずに厚みの厚い平板状の装飾材を容易に製
造できる。(12) As described in the above item (12), a method for forming a second layer in which an aggregate is dispersed in a synthetic resin emulsion or a solution in a mold having a relief inversion pattern. Is applied, or two or more kinds of second coating materials having different color tones are applied in a pattern, and the second coating material is dried or semi-dried. In a preferred embodiment of the present invention, the method further includes a step of applying a third coating material for forming a third layer in which the aggregate is dispersed in the synthetic resin emulsion or the solution over the entire upper surface. Thereby, a thick plate-shaped decorative material can be easily manufactured without impairing the effect of the present invention.

【００８２】（１３）また、前記（１３）項に記載した
ように、第２の塗布材を塗布後、その表面が乾燥する前
に、シート状基材を積層する工程を更に含む本発明の好
ましい態様とすることにより、シート状基材により補強
されたより強度の改善された平板状の装飾材を容易に製
造できる。(13) As described in the above item (13), the present invention further comprises a step of laminating a sheet-like substrate after the second coating material is applied and before the surface is dried. By adopting a preferred embodiment, a flat decorative material having improved strength reinforced by the sheet-like base material can be easily manufactured.

【００８３】（１４）また、前記（１４）項に記載した
ように、第３の塗布材を塗布後、その表面が乾燥する前
にシート状基材を積層する工程を更に含む本発明の好ま
しい態様とすることにより、厚みを厚くでき、また、シ
ート状基材により補強されたより強度の改善された平板
状の装飾材を容易に製造できる。(14) As described in the above (14), the present invention preferably further comprises a step of laminating a sheet-like substrate after the third coating material is applied and before the surface is dried. By adopting the embodiment, the thickness can be increased, and a flat decorative material with improved strength reinforced by the sheet-like base material can be easily manufactured.

【００８４】（１５）また、前記（１５）項に記載した
ように、シート状基材が布状物である本発明の好ましい
態様とすることにより、シート状基材が布状物であるこ
とにより、軽さを保ち、又、柔軟性を阻害せず曲面にも
施工可能で、より強度の改善された平板状の装飾材を容
易に製造し得る。(15) As described in the above item (15), by adopting a preferred embodiment of the present invention in which the sheet-like substrate is a cloth-like material, the sheet-like substrate is a cloth-like material. Thereby, it is possible to easily manufacture a flat decorative material which is light in weight, can be applied to a curved surface without impairing flexibility, and has improved strength.

【００８５】（１６）また、前記（１６）項に記載した
ように、第１の塗布材と第２の塗布材との、その乾燥後
の色調の差異が、色相、明度、彩度の少なくとも１つが
異なるものである本発明の好ましい態様とすることによ
り、より重厚さ、深みに富んだ高級感を有する平板状の
装飾材を容易に製造し得る。(16) Further, as described in the above (16), the difference in the color tone between the first coating material and the second coating material after drying is at least one of hue, lightness, and saturation. By adopting the preferred embodiment of the present invention in which one is different, it is possible to easily produce a flat-plate-shaped decorative material having a thicker and deeper sense of quality.

【００８６】（１７）また、前記（１７）項に記載した
ように、第１の塗布材と第２の塗布材との、その乾燥後
の色調の明度の差異が，マンセル値で１より大きい本発
明の好ましい態様とすることにより、第１の層による模
様が引き立ち、重厚さ、深みに富んだ、より高級感を有
する平板状の装飾材を容易に製造し得る。(17) As described in the above item (17), the difference in the lightness of the color tone between the first coating material and the second coating material after drying is greater than 1 in Munsell value. By adopting a preferred embodiment of the present invention, the pattern formed by the first layer is prominent, and a thick, deep, high-grade, flat-plate-shaped decorative material can be easily manufactured.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の装飾材の製造方法の一実施の形態の工
程の一部を示す工程断面図である。FIG. 1 is a process cross-sectional view showing a part of a process of an embodiment of a method for manufacturing a decorative material of the present invention.

【図２】本発明の装飾材の製造方法の一実施の形態の工
程の前記図１に示した工程の続きの工程示す工程断面図
である。FIG. 2 is a cross-sectional view showing a step that follows the step shown in FIG. 1 in the step of the embodiment of the method for manufacturing a decorative material according to the present invention.

【図３】図２の工程（ｆ）に相当する別の実施の形態の
工程を示す工程断面図である。FIG. 3 is a process cross-sectional view showing a process of another embodiment corresponding to the process (f) of FIG. 2;

【図４】本発明の一実施の形態の変成岩調模様を有する
装飾材の平面図である。FIG. 4 is a plan view of a decorative material having a metamorphic rock pattern according to one embodiment of the present invention.

【符号の説明】[Explanation of symbols]

１ 第１の層（第１の塗布材） ２、２ａ、２ｂ 第２の層（第２の塗布材） ２ｃ 第２の層２の凹凸の凹部 ２ｄ 第２の層２の凹凸の凸部 ３ 第３の層（第３の塗布材） ４ トップコート層 ６ シート状基材 ７ 研磨面 １０ 基板台 １１ 鋳型 DESCRIPTION OF SYMBOLS 1 1st layer (1st coating material) 2, 2a, 2b 2nd layer (2nd coating material) 2c Concavo-convex concave part of 2nd layer 2d 2d Concave convex part of 2nd layer 2 3 Third layer (third coating material) 4 Top coat layer 6 Sheet base material 7 Polished surface 10 Substrate stand 11 Mold

フロントページの続き Ｆターム(参考） 2E110 AA57 AB04 AB05 AB22 AB23 BA05 BB38 EA09 GA07W GA23Z GA32X GA33X GA42X GA43Z GB02X GB06X GB13Z GB14Z GB16X GB17X GB23X GB28Z GB32X GB42W GB42X GB44X GB52X GB55X GB63X 4D075 AC11 AC43 AE03 CB16 DA06 DB12 DC02 EA05 EA13 EB03 EB22 EC13 4F100 AJ01C AK01A AK01B AK25 AT00D BA03 BA04 BA07 BA10A BA10D BA41A BA41B BA41C BA44 CA13 CA13H CA24A CA24C CA24H DE01 DG11D EA061 EC052 EG00 EG002 EH313 EH46 EH462 EJ31 EJ39 GB07 HB04 HB11 HB21 HB26 HB40 JK01 JK12 JL02 JL03 JL05 JL10B JM01A Continued on the front page F-term (reference) 2E110 AA57 AB04 AB05 AB22 AB23 BA05 BB38 EA09 GA07W GA23Z GA32X GA33X GA42X GA43Z GB02X GB06X GB13Z GB14Z GB16X GB17X GB23X GB28Z GB32X GB42W GB42X GB44X GB52X GB55X AC03EB03 DA033 EB22 EC13 4F100 AJ01C AK01A AK01B AK25 AT00D BA03 BA04 BA07 BA10A BA10D BA41A BA41B BA41C BA44 CA13 CA13H CA24A CA24C CA24H DE01 DG11D EA061 J0505 EG00 EG002 EH313 EH46 E0511 J03H01 EB31B01 J02H

Claims (17)

【特許請求の範囲】[Claims] 【請求項１】 骨材が分散されてなる合成樹脂層から形
成されていて、表面が平らな平板状装飾材であって、前
記装飾材は（イ）骨材が分散されてなる合成樹脂層であ
って、１種類の前記合成樹脂層からなるか、または、互
いに色調の異なる２種類以上の前記合成樹脂層から２色
以上の表面模様が形成されている第２の層と、（ロ）骨
材が分散されてなる合成樹脂層であって、前記第２の層
と色調が異なり、１種類または互いに色調の異なる２種
類以上の前記合成樹脂層からなり、前記第２の層の表面
を不連続的に覆っていて表面模様を形成しており、前記
第２の層の厚み方向にその下部の少なくとも一部が入り
込んでいる第１の層とからなり、前記第２の層の表面に
露出している部分と第１の層の表面が平らでほぼ同一平
面を形成している事を特徴とする第１の層と第２の層の
色調コントラストにより模様を形成している装飾材。1. A flat decorative material having a flat surface and made of a synthetic resin layer in which an aggregate is dispersed, wherein the decorative material is (a) a synthetic resin layer in which the aggregate is dispersed. A second layer made of one kind of the synthetic resin layer, or a surface pattern of two or more colors formed from two or more kinds of the synthetic resin layers having different color tones; A synthetic resin layer in which aggregates are dispersed, wherein the second layer has a different color tone from the second layer, and is composed of one or more types of the synthetic resin layers having different color tones; It comprises a first layer that is discontinuously covered to form a surface pattern, and at least a part of a lower part of the second layer penetrates in a thickness direction of the second layer. The exposed part and the surface of the first layer are flat and almost coplanar. A decorative material, wherein a pattern is formed by a color tone contrast between a first layer and a second layer. 【請求項２】 第１の層と第２の層から形成される模様
が、変成岩調模様である請求項１に記載の装飾材。2. The decorative material according to claim 1, wherein the pattern formed from the first layer and the second layer is a metamorphic rock pattern. 【請求項３】 第２の層の下に骨材が分散されてなる合
成樹脂層からなる第３の層を更に有する請求項１または
２のいずれかに記載の装飾材。3. The decorative material according to claim 1, further comprising a third layer made of a synthetic resin layer in which an aggregate is dispersed below the second layer. 【請求項４】 第２の層の下に更にシート状基材が積層
されている請求項１または２のいずれかに記載の装飾
材。4. The decorative material according to claim 1, wherein a sheet-like base material is further laminated below the second layer. 【請求項５】 第３の層の下に更にシート状基材が積層
されている請求項３に記載の装飾材。5. The decorative material according to claim 3, wherein a sheet-like base material is further laminated below the third layer. 【請求項６】 シート状基材が布状物である請求項４ま
たは５のいずれかに記載の装飾材。6. The decorative material according to claim 4, wherein the sheet-like substrate is a cloth. 【請求項７】 第１の層と第２の層との色調の差異が、
色相、明度、彩度の少なくとも１つが異なるものである
請求項１〜６のいずれかに記載の装飾材。7. The difference in color tone between the first layer and the second layer is as follows:
The decorative material according to any one of claims 1 to 6, wherein at least one of hue, lightness, and saturation is different. 【請求項８】 第１の層と第２の層との色調の明度の差
異が、マンセル値で１より大きい請求項１〜７のいずれ
かに記載の装飾材。8. The decorative material according to claim 1, wherein a difference in lightness of the color tone between the first layer and the second layer is greater than 1 in Munsell value. 【請求項９】 凹凸反転レリーフ模様を有する鋳型に、
合成樹脂エマルションまたは溶液中に骨材が分散されて
なる第２の層を形成するための１種類の第２の塗布材を
塗布するか、または、互いに色調が異なる２種類以上の
第２の塗布材を模様状に塗布し、前記第２の塗布材を乾
燥させて形成された第２の層を前記鋳型から取り出し、
第２の層が前記鋳型に接していた側から、合成樹脂エマ
ルションまたは溶液中に骨材が分散されてなる第１の層
を形成するための第２の層とは色調の異なる１種類また
は互いに色調が異なる２種類以上の第１の塗布材を、第
２の層の凹凸の少なくとも凹部がほぼ充填されるように
又は凹部がほぼ充填され且つ第２の層の表面のほぼ全面
が被覆される程度に塗布し、乾燥して第１の層を形成
し、次いで第１の層の少なくとも一部が表面に残り、か
つ、第２の層の一部が表面に現れる程度に、表面全面が
平面になる様に第１の層を形成した側から平らに研磨す
る工程を含む少なくとも第１の層と第２の層とからなる
色調コントラスト模様が表面に発現している装飾材の製
造方法。9. A mold having a concave-convex inverted relief pattern,
One kind of a second coating material for forming a second layer in which an aggregate is dispersed in a synthetic resin emulsion or a solution is applied, or two or more kinds of second coating materials having different color tones from each other The material is applied in a pattern, and the second layer formed by drying the second applied material is removed from the mold,
From the side where the second layer is in contact with the mold, one or more kinds of different color tones from the second layer for forming the first layer in which the aggregate is dispersed in the synthetic resin emulsion or the solution. Two or more types of first coating materials having different color tones are filled so that at least the concave portions of the irregularities of the second layer are almost filled, or the concave portions are almost filled, and almost the entire surface of the second layer is covered. And then dried to form a first layer, and then the entire surface is flat to the extent that at least a portion of the first layer remains on the surface and a portion of the second layer appears on the surface. A method for producing a decorative material having a color tone contrast pattern composed of at least a first layer and a second layer on the surface, the method including a step of polishing the surface flat from the side on which the first layer is formed. 【請求項１０】 第１の層と第２の層とから形成される
模様が、変成岩調模様である請求項９に記載の装飾材の
製造方法。10. The method for manufacturing a decorative material according to claim 9, wherein the pattern formed from the first layer and the second layer is a metamorphic rock pattern. 【請求項１１】 凹凸反転レリーフ模様を有する鋳型
が、所望の表面模様が描写されている写真ないしは絵を
原画として、デジタル光彫刻システムにより感光性合成
樹脂又は感光性ゴム状物からなる凹凸レリーフ模様を有
する母型を作成し、前記母型に鋳型形成用の合成樹脂を
流し込んで固めて前記母型から離型させて得られた凹凸
反転レリーフ模様を有する鋳型である請求項９または１
０のいずれかに記載の装飾材の製造方法。11. A relief pattern comprising a photosensitive synthetic resin or a photosensitive rubber-like material by a digital optical engraving system, wherein a mold having a relief reverse pattern is formed from a photograph or a picture on which a desired surface pattern is drawn as an original image. A mold having a concavo-convex reversal relief pattern obtained by preparing a matrix having the following, casting a synthetic resin for forming a mold into the matrix, solidifying the resin, and releasing the mold from the matrix.
0. The method for producing a decorative material according to any one of the above items. 【請求項１２】 凹凸反転レリーフ模様を有する鋳型
に、合成樹脂エマルションまたは溶液中に骨材が分散さ
れてなる第２の層を形成するための１種類の第２の塗布
材を塗布するか、または、互いに色調が異なる２種類以
上の第２の塗布材を模様状に塗布し、前記第２の塗布材
を乾燥させ又は半乾燥の状態で、この上全面に更に合成
樹脂エマルションまたは溶液中に骨材が分散されてなる
第３の層を形成するための第３の塗布材を塗布する工程
を更に含む請求項９〜１１のいずれかに記載の装飾材の
製造方法。12. A type of second coating material for forming a second layer in which an aggregate is dispersed in a synthetic resin emulsion or a solution is applied to a mold having a concave-convex inverted relief pattern, Alternatively, two or more kinds of second coating materials having different color tones are applied in a pattern, and the second coating material is dried or semi-dried, and further over the entire upper surface thereof in a synthetic resin emulsion or solution. The method for producing a decorative material according to claim 9, further comprising a step of applying a third coating material for forming a third layer in which the aggregate is dispersed. 【請求項１３】 第２の塗布材を塗布後、その表面が乾
燥する前に、シート状基材を積層する工程を更に含む請
求項９〜１１のいずれかに記載の装飾材の製造方法。13. The method for producing a decorative material according to claim 9, further comprising a step of laminating a sheet-like substrate after the second coating material is applied and before the surface is dried. 【請求項１４】 第３の塗布材を塗布後、その表面が乾
燥する前にシート状基材を積層する工程を更に含む請求
項１２に記載の装飾材の製造方法。14. The method for manufacturing a decorative material according to claim 12, further comprising a step of laminating a sheet-like substrate after the third coating material is applied and before the surface is dried. 【請求項１５】 シート状基材が布状物である請求項１
３または１４のいずれかに記載の装飾材の製造方法。15. The sheet-like base material is a cloth-like material.
15. The method for producing a decorative material according to any one of items 3 and 14. 【請求項１６】 第１の塗布材と第２の塗布材との、そ
の乾燥後の色調の差異が、色相、明度、彩度の少なくと
も１つが異なるものである請求項９〜１５のいずれかに
記載の装飾材の製造方法。16. The method according to claim 9, wherein a difference in color tone between the first coating material and the second coating material after drying is at least one of hue, lightness, and saturation. 3. The method for producing a decorative material according to item 1. 【請求項１７】 第１の塗布材と第２の塗布材との、そ
の乾燥後の色調の明度の差異が，マンセル値で１より大
きい請求項９〜１６のいずれかに記載の装飾材の製造方
法。17. The decorative material according to claim 9, wherein a difference in lightness of a color tone between the first coating material and the second coating material after drying is greater than 1 in Munsell value. Production method.
JP10226830A 1998-08-11 1998-08-11 Decorative material and its preparation Pending JP2000052527A (en)