JP2000051411A - Fiber-reinforced plastic shaft for golf club - Google Patents
Fiber-reinforced plastic shaft for golf clubInfo
- Publication number
- JP2000051411A JP2000051411A JP10230797A JP23079798A JP2000051411A JP 2000051411 A JP2000051411 A JP 2000051411A JP 10230797 A JP10230797 A JP 10230797A JP 23079798 A JP23079798 A JP 23079798A JP 2000051411 A JP2000051411 A JP 2000051411A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- golf club
- fiber
- reinforced plastic
- club shaft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、繊維強化プラスチ
ック製ゴルフクラブ用シャフトに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fiber reinforced plastic golf club shaft.
【０００２】[0002]
【従来の技術】ゴルフクラブ用シャフトは、一方向に引
き揃えた補強繊維に樹脂を含浸させてなるいわゆる一方
向性プリプレグシートを、テーパー付きの芯金に巻き付
けて積層し、これを硬化させて得られるところの繊維強
化プラスチック製シャフトが、その比剛性及び比強度が
高いこと、又設計の自由さがあることから広く用いられ
ている。2. Description of the Related Art A golf club shaft is formed by winding a so-called unidirectional prepreg sheet obtained by impregnating a resin into a reinforcing fiber aligned in one direction and winding it around a tapered core metal, and curing this. The obtained fiber reinforced plastic shaft is widely used because of its high specific rigidity and specific strength and freedom of design.
【０００３】そして、上記の繊維強化プラスチック製ゴ
ルフクラブ用シャフトは、多くの場合、その内側から外
側に向かって積層されているアングル層とストレート層
との２層構造になっている。[0003] In many cases, the fiber reinforced plastic golf club shaft has a two-layer structure of an angle layer and a straight layer laminated from the inside to the outside.
【０００４】アングル層は、一方向に引き揃えた補強繊
維がシャフトの長手方向に対して±（３０〜７０°）に
配向している繊維強化プラスチック層であり、通常、シ
ャフトの長手方向に対して＋θ°に配向する補強繊維に
よるプリプレグシートと、同じくシャフトの長手方向に
対して−θ°に配向する補強繊維によるプリプレグシー
トとを貼り合わせた積層プリプレグシートによって成形
されている。The angle layer is a fiber reinforced plastic layer in which reinforcing fibers aligned in one direction are oriented at ± (30 to 70 °) with respect to the longitudinal direction of the shaft. The prepreg sheet is formed by laminating a prepreg sheet made of reinforcing fibers oriented at + θ ° and a prepreg sheet made of reinforcing fibers oriented at −θ ° with respect to the longitudinal direction of the shaft.
【０００５】又、ストレート層は、補強繊維がシャフト
の長手方向に対して−２０〜＋２０°に配向している繊
維強化プラスチック層からなる。[0005] The straight layer comprises a fiber reinforced plastic layer in which the reinforcing fibers are oriented at -20 to +20 with respect to the longitudinal direction of the shaft.
【０００６】そして、上記のアングル層とストレート層
とを具備する繊維強化プラスチック製ゴルフクラブ用シ
ャフトにあっては、アングル層が捻り強度を向上させ、
又ストレート層が曲げ強度を向上させる作用を果たして
いる。In the fiber reinforced plastic golf club shaft having the angle layer and the straight layer, the angle layer improves the torsional strength,
In addition, the straight layer has a function of improving the bending strength.
【０００７】なお、ゴルフクラブ用シャフトの長手方向
に対する補強繊維の配向角度を、単に補強繊維の配向角
という。The orientation angle of the reinforcing fibers with respect to the longitudinal direction of the golf club shaft is simply referred to as the orientation angle of the reinforcing fibers.
【０００８】ところで近年のゴルフクラブ用シャフトに
おいては、ゴルフボールの打撃の際のヘッドスピードの
向上、シャフトの長尺化、ヘッドの大型化等に伴なっ
て、スイートスポットエリアの拡大を目的として、シャ
フトの軽量化が一段と進められてきた。By the way, in recent golf club shafts, with the aim of improving the head speed when hitting a golf ball, increasing the length of the shaft, and increasing the size of the head, the sweet spot area is enlarged. Shaft weight reduction has been further advanced.
【０００９】これに対して従来の繊維強化プラスチック
製ゴルフクラブ用シャフトにあっては、厚みが０．１２
０〜０．２００ｍｍ程度のプリプレグシートによってア
ングル層を成形しているために、軽量シャフトにする場
合にはアングル層の層数を少なくしなければならなく、
設計の自由度が小さかった。On the other hand, the conventional fiber reinforced plastic golf club shaft has a thickness of 0.12.
Because the angle layer is formed by a prepreg sheet of about 0 to 0.200 mm, the number of angle layers must be reduced when making a lightweight shaft.
The degree of freedom in design was small.
【００１０】又、ゴルフクラブ用シャフトの軽量化を図
るために単にストレート層やアングル層の層数を減らす
と、シャフトの曲げ剛性、曲げ強力、捻り剛性、捻り強
力、及び潰し強力等が低減するという問題が発生する。Further, if the number of straight layers and angle layers is simply reduced in order to reduce the weight of the golf club shaft, the bending rigidity, bending strength, torsional rigidity, torsional strength, crushing strength, etc. of the shaft are reduced. The problem occurs.
【００１１】更に、ゴルフクラブ用シャフトの曲げ剛性
や捻り剛性を低減させることなく軽量化を図る手段とし
て、ストレート層及び／又はアングル層の層数を減らす
と同時に、これらの層を構成する補強繊維として弾性率
のより高い補強繊維を使用する方法があるが、かかる手
段において、従来から使用されている厚さ０．１２０〜
０．２００ｍｍ程度のプリプレグシートを適用すると、
シャフトの周方向の層数が不均一になり、周方向に厚み
ムラを有するシャフトになってしまう。Further, as means for reducing the weight without reducing the bending rigidity and torsional rigidity of the golf club shaft, the number of straight layers and / or angle layers is reduced, and at the same time, the reinforcing fibers constituting these layers are reduced. There is a method of using a reinforcing fiber having a higher modulus of elasticity, but in such a means, a thickness of 0.120 to
When a prepreg sheet of about 0.200 mm is applied,
The number of layers in the circumferential direction of the shaft becomes non-uniform, resulting in a shaft having thickness unevenness in the circumferential direction.
【００１２】更に又、実開昭６２−３３８７２号公報に
は、繊維強化プラスチック製ゴルフクラブ用シャフトの
捻り剛性や捻り強力を改善する手段として、アングル層
とストレート層との外に、その最外層にさらにアングル
層を設ける方法が開示されている。しかしながら、この
方法によって得られた繊維強化プラスチック製ゴルフク
ラブ用シャフトは、捻り剛性や捻り強力の保持のために
最外層に形成したアングル層が、研磨等の仕上げ加工に
よって失われることがあり、安定した品質の繊維強化プ
ラスチック製ゴルフクラブ用シャフトにすることができ
ない。Further, Japanese Utility Model Laid-Open Publication No. Sho 62-33872 discloses a means for improving the torsional rigidity and torsional strength of a fiber reinforced plastic golf club shaft, in addition to the angle layer and the straight layer, and the outermost layer. Discloses a method of further providing an angle layer. However, the fiber reinforced plastic golf club shaft obtained by this method has a problem that the angle layer formed on the outermost layer for maintaining the torsional rigidity and the torsional strength may be lost due to finishing processing such as polishing. Quality golf club shafts made of fiber reinforced plastics.
【００１３】しかるに、アングル層を成形するためのプ
リプレグシートの厚みを０．０２０〜０．０９５ｍｍに
すると、シャフト全体の重量やその外径にも大きな影響
を与えることなくアングル層の層数を変更することがで
き、これによって従来のゴルフクラブ用シャフトの曲げ
剛性や捻り剛性等を維持したまま軽量化を図ることが可
能であり、これによってシャフト設計の自由度を向上さ
せることができる。However, when the thickness of the prepreg sheet for forming the angle layer is set to 0.020 to 0.095 mm, the number of the angle layers can be changed without greatly affecting the weight of the entire shaft and its outer diameter. As a result, it is possible to reduce the weight while maintaining the bending rigidity and the torsional rigidity of the conventional golf club shaft, thereby improving the degree of freedom in designing the shaft.
【００１４】又、上記のように薄いプリプレグシートに
よってアングル層を成形することにより、周方向の厚み
にバラツキの少ない安定した品質のゴルフクラブ用シャ
フトにすることができる。Further, by forming the angle layer from the thin prepreg sheet as described above, it is possible to obtain a stable golf club shaft having a small variation in circumferential thickness.
【００１５】[0015]
【発明が解決しようとする課題】従って本発明の課題
は、シャフト全体の重量を従来の繊維強化プラスチック
製ゴルフクラブ用シャフトと同等にしたままで、捻り強
力を従来の繊維強化プラスチック製ゴルフクラブ用シャ
フトよりも高いものにしたり、或いは捻り強力を従来の
繊維強化プラスチック製ゴルフクラブ用シャフトと同等
にしたままで、シャフト全体の重量を従来の繊維強化プ
ラスチック製ゴルフクラブ用シャフトよりも小さいもの
にしたりすることができ、設計の自由度が高く、しかも
安定した品質の繊維強化プラスチック製ゴルフクラブ用
シャフトを提供することにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a golf club made of a conventional fiber reinforced plastic with a high torsional strength while keeping the weight of the entire shaft equal to that of a conventional fiber reinforced plastic golf club shaft. Make the overall weight of the shaft lower than that of a conventional fiber-reinforced plastic golf club shaft, while keeping it higher than the shaft, or keeping the torsional strength equal to that of the conventional fiber-reinforced plastic golf club shaft. An object of the present invention is to provide a fiber reinforced plastic golf club shaft having a high degree of freedom in design and a stable quality.
【００１６】[0016]
【課題を解決するための手段】上記の課題は、下記の通
りの構成による本発明の繊維強化プラスチック製ゴルフ
クラブ用シャフトにすることによって解決することがで
きる。すなわち本発明は、複数の繊維強化プラスチック
層を積層させてなるゴルフクラブ用シャフトであって、
アングル層とストレート層とを具備し、しかも前記アン
グル層が厚さ０．０２０〜０．０９５ｍｍのプリプレグ
シートによって成形されており、かつゴルフクラブ用シ
ャフト全体の重量が３０〜５５ｇである繊維強化プラス
チック製ゴルフクラブ用シャフトからなる。The above objects can be attained by providing a fiber reinforced plastic golf club shaft according to the present invention having the following structure. That is, the present invention is a golf club shaft formed by laminating a plurality of fiber-reinforced plastic layers,
A fiber reinforced plastic comprising an angle layer and a straight layer, wherein the angle layer is formed of a prepreg sheet having a thickness of 0.020 to 0.095 mm, and the total weight of the golf club shaft is 30 to 55 g. Golf club shaft.
【００１７】上記の構成を備えてなる本発明の繊維強化
プラスチック製ゴルフクラブ用シャフトにおいては、ア
ングル層を成形するためのプリプレグシートの補強繊維
の繊維目付が２０〜９５ｇ／ｍ2 であることが好まし
い。In the fiber reinforced plastic golf club shaft according to the present invention having the above-described structure, the basis weight of the reinforcing fibers of the prepreg sheet for forming the angle layer may be 20 to 95 g / m 2. preferable.
【００１８】[0018]
【発明の実施の形態】以下に、本発明の繊維強化プラス
チック製ゴルフクラブ用シャフトの望ましい実施の形態
を説明する。本発明の複数の繊維強化プラスチック層を
積層させてなるゴルフクラブ用シャフトは、アングル層
とストレート層とを具備しており、しかも前記アングル
層が厚さ０．０２０〜０．０９５ｍｍのプリプレグシー
トによって成形されているものであり、かつゴルフクラ
ブ用シャフト全体の重量が３０〜５５ｇの範囲にある繊
維強化プラスチック製ゴルフクラブ用シャフトからな
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the fiber reinforced plastic golf club shaft of the present invention will be described below. The golf club shaft formed by laminating a plurality of fiber-reinforced plastic layers of the present invention includes an angle layer and a straight layer, and the angle layer is formed of a prepreg sheet having a thickness of 0.020 to 0.095 mm. The golf club shaft is made of a fiber reinforced plastic golf club shaft and has a total weight of 30 to 55 g.
【００１９】上記のように、本発明の繊維強化プラスチ
ック製ゴルフクラブ用シャフトは、アングル層からなる
繊維強化プラスチック層とストレート層からなる繊維強
化プラスチック層とを具備していることが必要である
が、これらの各繊維強化プラスチック層以外に、先端部
の補強や径合わせ等の目的で、他の繊維強化プラスチッ
ク層を設けてあってもよいことは勿論である。As described above, the fiber reinforced plastic golf club shaft of the present invention needs to have the fiber reinforced plastic layer composed of the angle layer and the fiber reinforced plastic layer composed of the straight layer. Of course, other than these fiber reinforced plastic layers, other fiber reinforced plastic layers may be provided for the purpose of reinforcing the tip portion or adjusting the diameter.
【００２０】上記の構成を具備してなる本発明の繊維強
化プラスチック製ゴルフクラブ用シャフトにおいて、繊
維強化プラスチック層を形成するための補強繊維は特に
限定されるものではなく、通常の繊維強化プラスチック
層の補強繊維として用いられる繊維を使用し得るが、特
にパラ系芳香族ポリアミドや高強度ポリエチレン等の有
機系補強繊維、炭素繊維、ガラス繊維、ボロン繊維、炭
化ケイ素繊維、アルミナ繊維、チラノ繊維等の無機系繊
維や金属系繊維が好適であり、さらにこれらの繊維を２
種類以上組み合わせて用いることも可能である。In the fiber reinforced plastic golf club shaft of the present invention having the above-mentioned structure, the reinforcing fibers for forming the fiber reinforced plastic layer are not particularly limited. Fibers used as reinforcing fibers can be used, especially organic reinforcing fibers such as para-aromatic polyamide and high-strength polyethylene, carbon fibers, glass fibers, boron fibers, silicon carbide fibers, alumina fibers, and Tyranno fibers. Inorganic fibers and metal fibers are preferred, and these fibers are
It is also possible to use more than one kind in combination.
【００２１】又、上記の繊維強化プラスチック層を形成
するためのマトリックス樹脂も特に限定されるものでは
なく、通常の繊維強化プラスチック層のマトリックス樹
脂として用いられている各種の樹脂を使用し得るが、特
にエポキシ樹脂、不飽和ポリエステル樹脂、ビニルエス
テル樹脂、ポリイミド樹脂、ポリビスマレイミド樹脂等
の熱硬化性樹脂が一般的であり、又熱可塑性樹脂であっ
てもよいことは勿論である。The matrix resin for forming the above-mentioned fiber reinforced plastic layer is not particularly limited, and various resins used as a matrix resin for a normal fiber reinforced plastic layer can be used. Particularly, a thermosetting resin such as an epoxy resin, an unsaturated polyester resin, a vinyl ester resin, a polyimide resin, and a polybismaleimide resin is generally used. Of course, a thermoplastic resin may be used.
【００２２】更に上記の繊維強化プラスチック層は、一
方向に引き揃えてある補強繊維にマトリックス樹脂を含
浸させたプリプレグシートによって成形してなるものが
一般的であり、このときに使用するプリプレグシートの
樹脂含浸率は特に限定されるものではない。Further, the above-mentioned fiber-reinforced plastic layer is generally formed by molding a prepreg sheet in which a matrix resin is impregnated with reinforcing fibers aligned in one direction, and a prepreg sheet used at this time. The resin impregnation rate is not particularly limited.
【００２３】上記のストレート層の厚みは特に限定され
るものではないが、アングル層とストレート層とによる
通常の２層構造の繊維強化プラスチック製ゴルフクラブ
用シャフトにおけるストレート層の厚み程度でよく、普
通は０．２〜０．４ｍｍ程度である。The thickness of the straight layer is not particularly limited, but may be about the thickness of the straight layer in a fiber reinforced plastic golf club shaft having a normal two-layer structure including an angle layer and a straight layer. Is about 0.2 to 0.4 mm.
【００２４】アングル層は、厚さ０．０２０〜０．０９
５ｍｍのプリプレグシートによって成形されるが、該プ
リプレグシートとしては、補強繊維の繊維目付が２０〜
９５ｇ／ｍ2 の極薄プリプレグシート、例えば三菱レイ
ヨン株式会社製のプリプレグＨＲＸ３５０Ｃ０５０Ｓ
（繊維目付５８ｇ／ｍ2 、樹脂含有率２４．７重量％、
厚み０．０４７ｍｍ）や、同じくＨＲＸ３５０Ｃ１００
Ｓ（繊維目付９２ｇ／ｍ2 、樹脂含有率２５．２重量
％、厚み０．０７６ｍｍ）を適用することができる。The angle layer has a thickness of 0.020 to 0.09.
The prepreg sheet is formed from a 5 mm prepreg sheet.
95 g / m 2 ultra-thin prepreg sheet, for example, prepreg HRX350C050S manufactured by Mitsubishi Rayon Co., Ltd.
(Fiber weight 58 g / m 2 , resin content 24.7% by weight,
0.047mm in thickness) or HRX350C100
S (92 g / m 2 in fiber weight, resin content 25.2% by weight, thickness 0.076 mm) can be applied.
【００２５】このアングル層を成形するためのプリプレ
グシートの厚さが０．０２０ｍｍ未満になると、プリプ
レグシートが薄くなり過ぎて、巻き付け作業が困難にな
る。又、アングル層を成形するためのプリプレグシート
として厚さ０．０９５ｍｍを超えるものを使用すると、
アングル層の積層数を少なくしなければならなくなるた
めに、結果としてゴルフクラブ用シャフトの曲げ強力、
捻り剛性、捻り強力、及び潰し強力が低減してしまう。If the thickness of the prepreg sheet for forming the angle layer is less than 0.020 mm, the prepreg sheet becomes too thin, and the winding operation becomes difficult. Also, when using a prepreg sheet having a thickness of more than 0.095 mm as a prepreg sheet for forming an angle layer,
As the number of angle layers must be reduced, the bending strength of the golf club shaft becomes
The torsional stiffness, torsional strength, and crush strength are reduced.
【００２６】[0026]
【実施例】以下、本発明の繊維強化プラスチック製ゴル
フクラブシャフトの具体的な構成を実施例に基づいてよ
り詳しく説明し、併せて該実施例品のゴルフクラブシャ
フトの諸物性を、比較例品のゴルフクラブシャフトの諸
物性と比較して説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The specific structure of the fiber reinforced plastic golf club shaft of the present invention will be described in more detail below with reference to examples, and various physical properties of the golf club shaft of the example product will be compared with those of a comparative example product. This will be described in comparison with various physical properties of the golf club shaft.
【００２７】なお、実施例及び比較例で使用した各プリ
プレグシートは、炭素繊維を一方向に引き揃えた炭素繊
維シートに樹脂を含浸させてなるものであり、下記の表
１〜表２に示す通りのものである。The prepreg sheets used in the examples and comparative examples are obtained by impregnating a resin into a carbon fiber sheet in which carbon fibers are aligned in one direction, and are shown in Tables 1 and 2 below. It's the street.
【００２８】[0028]
【表１】 [Table 1]
【００２９】[0029]
【表２】 [Table 2]
【００３０】実施例１ 表１〜表２の所定欄に示す三菱レイヨン株式会社製の市
販のプリプレグシート（Ａ）〜（Ｆ）をそれぞれ裁断
し、細径端部外径５．２５ｍｍ、太径端部外径１８．８
０ｍｍ、長さ１２００ｍｍのテーパー付きの芯金の外周
に、下記の（１）〜（６）に説明する手順により、補強
繊維の配向角が９０°の９０°補強層用の巻き付け層、
アングル層用の巻き付け層、先端部補強層用の巻き付け
層、第１ストレート層用の巻き付け層、第２ストレート
層用の巻き付け層、及び細径部径調整層用の巻き付け層
を順次形成した。Example 1 Commercially available prepreg sheets (A) to (F) manufactured by Mitsubishi Rayon Co., Ltd., shown in predetermined columns of Tables 1 and 2, were cut into small-diameter end portions having an outer diameter of 5.25 mm and a large diameter. End outer diameter 18.8
A winding layer for a 90 ° reinforcing layer in which the orientation angle of the reinforcing fibers is 90 ° on the outer periphery of a tapered core metal having a length of 0 mm and a length of 1200 mm by the procedure described in the following (1) to (6):
A winding layer for an angle layer, a winding layer for a tip reinforcing layer, a winding layer for a first straight layer, a winding layer for a second straight layer, and a winding layer for a small diameter portion diameter adjusting layer were sequentially formed.
【００３１】（１）プリプレグシートシート（Ｄ）を、
繊維方向が芯金の径方向中心線に対して９０°となるよ
うにして芯金に巻き付けたときに、細径端部から太径端
部に亙って１層となって巻き付かるような概台形に裁断
し、これを芯金上に巻き付け、補強繊維の配向角が９０
°の９０°補強層用の巻き付けを行なった。(1) The prepreg sheet (D) is
When the fiber is wound around the core so that the fiber direction is at 90 ° to the center line in the radial direction of the core, it is wound as a single layer from the small diameter end to the large diameter end. Cut into a roughly trapezoidal shape, wound around a cored bar, and the orientation angle of the reinforcing fibers was 90%.
The winding for the 90 ° reinforcement layer was performed.
【００３２】（２）プリプレグシート（Ａ）を、繊維方
向が芯金の径方向中心線に対して＋４５°となるように
して、（１）にて形成した９０°補強層用の巻き付け層
の上に巻き付けたときに、細径端部において２．１層、
その後はなだらかに増加して太径側端部において２．６
層となって巻き付かるように裁断し、又同じくプリプレ
グシート（Ａ）を、繊維方向が芯金の径方向中心線に対
して−４５°となるようにして、同じく（１）にて形成
した９０°補強層用の巻き付け層の上に巻き付けたとき
に、細径端部において２．１層、その後はなだらかに増
加して太径側端部において２．６層となって巻き付かる
ように裁断した。(2) The prepreg sheet (A) is formed so that the fiber direction is + 45 ° with respect to the radial centerline of the cored bar, and the wrapping layer for the 90 ° reinforcing layer formed in (1) is formed. When wound up, 2.1 layers at the narrow end,
After that, it gradually increased to 2.6 at the larger diameter end.
The prepreg sheet (A) is cut in such a manner as to be wound as a layer, and the prepreg sheet (A) is formed in the same manner as in (1), so that the fiber direction is at -45 ° with respect to the radial center line of the core metal. When wound on the wound layer for the 90 ° reinforcing layer, the layer is wound at 2.1 layers at the small-diameter end, and thereafter gradually increased to 2.6 layers at the large-diameter end. Was cut as follows.
【００３３】続いて、上記の２枚のプリプレグシートを
その繊維方向が互いに直交するようにして貼り合わせた
後、この貼り合わせプリプレグシートを、（１）にて形
成した９０°補強層用の巻き付け層の上に巻き付け、ア
ングル層用の巻き付けを行なった。Subsequently, the two prepreg sheets are bonded together so that their fiber directions are orthogonal to each other, and the bonded prepreg sheets are wound around the 90 ° reinforcing layer formed in (1). Winding on the layer, winding for the angle layer was performed.
【００３４】（３）プリプレグシート（Ｅ）を、繊維方
向が芯金の径方向中心線に対して０°となるようにし
て、（２）にて形成したアングル層用の巻き付け層の上
に巻き付けたときに、細径端部〜該細径端部から２５０
ｍｍの位置迄に亙って２層となって巻き付かるような概
台形に裁断し、（２）にて形成したアングル層用の巻き
付け層の上に巻き付け、先端部補強層用の巻き付けを行
なった。(3) Place the prepreg sheet (E) on the wrapping layer for the angle layer formed in (2) so that the fiber direction is at 0 ° to the radial center line of the cored bar. When wound, 250 mm from the small diameter end to the small diameter end.
mm, cut into an approximately trapezoidal shape that can be wound in two layers, wound on the angle layer winding layer formed in (2), and wound for the front end reinforcing layer. Done.
【００３５】（４）プリプレグシート（Ｂ）を、繊維方
向が芯金の径方向中心線に対して０°となるようにし
て、（３）にて形成した先端部補強層用の巻き付け層の
上と（２）にて形成したアングル層用の巻き付け層の上
とに亙って巻き付けたときに、細径端部〜太径端部の全
長に亙って１層となって巻き付かるような概台形に裁断
し、これを（３）工程に続いて巻き付け、第１ストレー
ト層用の巻き付けを行なった。(4) The prepreg sheet (B) is formed so that the fiber direction is 0 ° with respect to the radial center line of the cored bar, and the wrapping layer for the front end reinforcing layer formed in (3) is formed. When it is wound over the upper part and on the winding layer for the angle layer formed in (2), it is wound as one layer over the entire length from the small diameter end to the large diameter end. This was cut into a substantially trapezoidal shape, and this was wound following the step (3), and was wound for the first straight layer.
【００３６】（５）プリプレグシート（Ｃ）を、繊維方
向が芯金の径方向中心線に対して０°となるようにし
て、第１ストレート層用の巻き付け層の上に巻き付けた
ときに、細径端部〜太径端部の全長に亙って１層となっ
て巻き付かるような概台形に裁断し、（４）にて形成し
た第１ストレート層用の巻き付け層の上に巻き付け、第
２ストレート層用の巻き付けを行なった。(5) When the prepreg sheet (C) is wound on the winding layer for the first straight layer so that the fiber direction is 0 ° with respect to the radial center line of the cored bar, It is cut into a substantially trapezoidal shape that can be wound as one layer over the entire length from the small diameter end to the large diameter end, and wound on the winding layer for the first straight layer formed in (4). Then, winding for the second straight layer was performed.
【００３７】（６）プリプレグシート（Ｆ）を、繊維方
向が直角を挟む２辺のうちの１辺と同方向であって、か
つ該直角を挟む辺の長さが１００ｍｍ×１００ｍｍの直
角３角形に裁断し、これを繊維方向が芯金の径方向中心
線に対して０°となるようにして、細径端部において最
も多重にして巻き付け、その後は徐々に巻き付けが無く
なるようにして、（５）にて形成した第２ストレート層
用の巻き付け層の上に巻き付け、細径部径調整層用の巻
き付けを行なった。(6) The prepreg sheet (F) is a right-angled triangle having a fiber direction in the same direction as one of two sides sandwiching the right angle and a length of the side sandwiching the right angle being 100 mm × 100 mm. This is wound so that the fiber direction is 0 ° with respect to the radial center line of the cored bar, and the winding is multiplexed most at the small diameter end, and thereafter the winding is gradually eliminated, Winding was performed on the winding layer for the second straight layer formed in 5), and winding for the small diameter portion diameter adjusting layer was performed.
【００３８】続いてその最外層に、幅２０ｍｍ、厚さ３
０μｍのポリプロピレンテープを２ｍｍピッチで巻き付
けた後、１４５℃の硬化炉で２４０分間の加熱硬化を行
ない、更に芯金の除去、ラッピングテープの除去、及び
外周面の研磨を順次行なった。Subsequently, the outermost layer has a width of 20 mm and a thickness of 3 mm.
After winding a 0 μm polypropylene tape at a pitch of 2 mm, the resultant was heated and cured in a curing oven at 145 ° C. for 240 minutes, and the core metal, the wrapping tape were removed, and the outer peripheral surface was sequentially polished.
【００３９】しかる後に、細径端部側及び太径端部側の
それぞれから１０ｍｍをトリミングカットし、重量５０
ｇ、長さ１１９５ｍｍ、細径端部の外径８．５ｍｍ、太
径端部の外径２０．０ｍｍのゴルフクラブシャフトを得
た。Thereafter, 10 mm was trimmed from each of the small-diameter end portion and the large-diameter end portion to obtain a weight of 50 mm.
g, a golf club shaft having a length of 1195 mm, an outer diameter of 8.5 mm at the narrow end, and an outer diameter of 20.0 mm at the thick end.
【００４０】上記の実施例品のゴルフクラブシャフトの
諸物性を、下記の通りの方法によって測定した。その結
果を、細径端部のアングル層の厚み（ｍｍ）と共に表３
に示す。The physical properties of the golf club shafts of the above examples were measured by the following methods. Table 3 shows the results together with the thickness (mm) of the angle layer at the small-diameter end.
Shown in
【００４１】曲げ剛性（ｍｍ） ゴルフクラブ用シャフトの太径端部を固定し、細径端部
から１０ｍｍの位置に１Ｋｇの荷重をかけたときのたわ
み量（ｍｍ）を測定した。Flexural rigidity (mm) The large diameter end of the golf club shaft was fixed, and the amount of deflection (mm) when a load of 1 kg was applied to a position 10 mm from the small diameter end was measured.
【００４２】曲げ強力（Ｋｇｆ） ゴルフクラブ用シャフトのＴ点（細径端部から９０ｍｍ
の位置）、Ａ点（同１７５ｍｍの位置）、Ｂ点（同５２
５ｍｍの位置）、及びＣ点（太径端部から１７５ｍｍの
位置）の各位置を中心にして、Ｔ点ではスパン１５０ｍ
ｍ、それ以外の位置ではスパン３００ｍｍで、３点曲げ
試験を行ない、その強力（Ｋｇｆ）を測定た。なお、圧
子は７５ｍｍＲ、支持は１２．５ｍｍＲとした。Flexural Strength (Kgf) Point T of golf club shaft (90 mm from small diameter end)
A) (point 175 mm), point B (52 mm)
5 mm) and C (175 mm from the end of the large diameter) at the center, 150 m span at T
m, and at other positions, a three-point bending test was performed with a span of 300 mm, and the strength (Kgf) was measured. The indenter was 75 mmR, and the support was 12.5 mmR.
【００４３】潰し強力（Ｋｇ／１０ｍｍ） 万能圧縮試験機を用いて、ゴルフクラブ用シャフトの太
径端部からａ点（１０ｍｍの位置）、ｂ点（同１００ｍ
ｍの位置）、ｃ点（同２００ｍｍの位置）、及びｄ点
（同３００ｍｍの位置）の各位置を中心にして、長さ約
１０ｍｍの試験片を切り出し、該試験片についての圧縮
試験を行ない、その強力（Ｋｇ／１０ｍｍ）を測定し
た。Crushing strength (Kg / 10 mm) Using a universal compression tester, point a (position 10 mm) and point b (point 100 m) from the large diameter end of the golf club shaft.
A test piece having a length of about 10 mm is cut out around each of the positions of point m (point m), point c (position 200 mm), and point d (position 300 mm), and a compression test is performed on the test piece. And its strength (Kg / 10 mm) was measured.
【００４４】捻り強力（Ｋｇｆ・ｍ・度） 有限会社メカトロニクスエンジニアリング製の「５ＫＮ
ユニバーサルテスタ」を用いて、ゴルフクラブ用シャ
フトの細径端部を固定すると共に、太径端部にトルクを
かけてゆき、ゴルフクラブ用シャフトが捻り破壊を生じ
たときのトルク（Ｋｇｆ・ｍ・度）を以って、捻り強力
とした。Torsion strength (Kgf · m · degree) “5KN” manufactured by Mechatronics Engineering Co., Ltd.
Using a “universal tester”, the small-diameter end of the golf club shaft is fixed, and torque is applied to the large-diameter end, so that the torque (Kgf · m · Degree) to give a strong twist.
【００４５】比較例１ 表１〜表２の所定欄に示す三菱レイヨン株式会社製の市
販のプリプレグシート（Ａ）〜（Ｇ）をそれぞれ裁断
し、細径端部外径５．２５ｍｍ、太径端部外径１８．８
０ｍｍ、長さ１２００ｍｍのテーパー付きの芯金の外周
に、下記の（１）〜（６）に説明する手順により、補強
繊維の配向角が９０°の９０°補強層用の巻き付け層、
アングル層用の巻き付け層、先端部補強層用の巻き付け
層、第１ストレート層用の巻き付け層、第２ストレート
層用の巻き付け層、及び細径部径調整層用の巻き付け層
を順次形成した。COMPARATIVE EXAMPLE 1 Commercially available prepreg sheets (A) to (G) manufactured by Mitsubishi Rayon Co., Ltd. shown in predetermined columns of Tables 1 and 2 were cut, and the small-diameter end portion outer diameter was 5.25 mm and the large diameter was large. End outer diameter 18.8
A winding layer for a 90 ° reinforcing layer in which the orientation angle of the reinforcing fibers is 90 ° on the outer periphery of a tapered core metal having a length of 0 mm and a length of 1200 mm by the procedure described in the following (1) to (6):
A winding layer for an angle layer, a winding layer for a tip reinforcing layer, a winding layer for a first straight layer, a winding layer for a second straight layer, and a winding layer for a small diameter portion diameter adjusting layer were sequentially formed.
【００４６】（１）実施例１の（１）と同様にして、９
０゜補強層用の巻き付け層を形成した。(1) In the same manner as (1) of the first embodiment,
A winding layer for a 0 ° reinforcing layer was formed.
【００４７】（２）プリプレグシート（Ｇ）を、繊維方
向が芯金の径方向中心線に対して＋４５°となるように
して、（１）にて形成した９０°補強層用の巻き付け層
の上に巻き付けたときに、細径端部において１．１層、
その後はなだらかに増加して太径側端部において１．５
層となって巻き付かるように裁断し、又同じくプリプレ
グシート（Ａ）を、繊維方向が芯金の径方向中心線に対
して−４５°となるようにして、同じく（１）にて形成
した９０°補強層用の巻き付け層の上に巻き付けたとき
に、細径端部において１．１層、その後はなだらかに増
加して太径側端部において１．５層となって巻き付かる
ように裁断した。(2) The prepreg sheet (G) is formed so that the fiber direction is + 45 ° with respect to the radial center line of the cored bar, and the wrapping layer for the 90 ° reinforcing layer formed in (1) is formed. When wound up, 1.1 layers at the small diameter end,
After that, it gradually increased to 1.5 at the end on the large diameter side.
The prepreg sheet (A) is cut in such a manner as to be wound as a layer, and the prepreg sheet (A) is formed in the same manner as in (1), so that the fiber direction is at -45 ° with respect to the radial center line of the core metal. When wound on the wound layer for the 90 ° reinforcing layer, the layer is wound at 1.1 layers at the small-diameter end and then gradually increased to 1.5 layers at the large-diameter end. Was cut as follows.
【００４８】続いて、上記の２枚のプリプレグシートを
その繊維方向が互いに直交するようにして貼り合わせた
後、この貼り合わせプリプレグシートを、（１）にて形
成した９０°補強層用の巻き付け層の上に巻き付け、ア
ングル層用の巻き付けを行なった。Subsequently, after bonding the two prepreg sheets so that their fiber directions are orthogonal to each other, the bonded prepreg sheets are wound around the 90 ° reinforcing layer formed in (1). Winding on the layer, winding for the angle layer was performed.
【００４９】（３）実施例１の（３）と同様にして、先
端部補強層用の巻き付け層を形成した。(3) In the same manner as in (3) of Example 1, a wrapping layer for a tip reinforcing layer was formed.
【００５０】（４）実施例１の（４）と同様にして、第
１ストレート層用の巻き付け層を形成した。(4) A winding layer for the first straight layer was formed in the same manner as (4) of Example 1.
【００５１】（５）実施例１の（５）と同様にして、第
２ストレート層用の巻き付け層を形成した。(5) In the same manner as (5) of Example 1, a winding layer for the second straight layer was formed.
【００５２】（６）実施例１の（６）と同様にして、細
径部径調整層用の巻き付け層を形成した。(6) In the same manner as in (6) of Example 1, a winding layer for a small diameter portion diameter adjusting layer was formed.
【００５３】以下、実施例１の対応する工程と同様にし
て、加熱硬化、及び後処理を施し、重量５０ｇ、長さ１
１９５ｍｍ、細径端部の外径８．５ｍｍ、太径端部の外
径２０ｍｍの比較のためのゴルフクラブ用シャフトを得
た。この比較例品のゴルフクラブシャフトの諸物性を、
細径端部のアングル層の厚み（ｍｍ）と共に表３に示
す。Thereafter, heat curing and post-treatment were carried out in the same manner as in the corresponding steps of Example 1, and the weight was 50 g and the length was 1
A golf club shaft for comparison with 195 mm, an outer diameter of 8.5 mm at the small diameter end, and 20 mm at the large diameter end was obtained. Various physical properties of the golf club shaft of this comparative example product,
Table 3 shows the thickness (mm) of the angle layer at the small diameter end.
【００５４】[0054]
【表３】 [Table 3]
【００５５】[0055]
【発明の効果】本発明の繊維強化プラスチック製ゴルフ
クラブ用シャフトは、アングル層を成形するためのプリ
プレグシートの厚みを０．０２０〜０．０９５ｍｍにし
たことにより、従来の繊維強化プラスチック製ゴルフク
ラブ用シャフトに比較して、該ゴルフクラブ用シャフト
全体の重量やその外径に大きな影響を与えることなくア
ングル層の積層数を増加させることができるものであ
る。According to the shaft for a golf club made of a fiber-reinforced plastic of the present invention, the thickness of the prepreg sheet for forming the angle layer is set to 0.020 to 0.095 mm so that the conventional golf club made of a fiber-reinforced plastic can be obtained. Compared with the golf club shaft, the number of the angled layers can be increased without greatly affecting the weight and the outer diameter of the entire golf club shaft.
【００５６】これによって、ゴルフクラブ用シャフト全
体の重量が従来の繊維強化プラスチック製ゴルフクラブ
用シャフトと同等であって、しかも捻り強力が従来の繊
維強化プラスチック製ゴルフクラブ用シャフトよりも高
いゴルフクラブ用シャフトにしたり、或いは捻り強力が
従来の繊維強化プラスチック製ゴルフクラブ用シャフト
と同等であって、しかもゴルフクラブ用シャフト全体の
重量が従来の繊維強化プラスチック製ゴルフクラブ用シ
ャフトよりも軽いゴルフクラブ用シャフトにしたりする
ことができ、設計の自由度が向上する。Thus, the weight of the entire golf club shaft is equal to that of the conventional fiber reinforced plastic golf club shaft, and the torsional strength is higher than that of the conventional fiber reinforced plastic golf club shaft. A golf club shaft having a shaft or torsion strength equivalent to that of a conventional fiber reinforced plastic golf club shaft, and having a lighter overall weight than the conventional fiber reinforced plastic golf club shaft. And the degree of freedom in design is improved.
【００５７】又、上記のように、薄いプリプレグシート
を使用したことにより、周方向の厚みにバラツキの少な
い安定した品質の繊維強化プラスチック製ゴルフクラブ
用シャフトにすることができる。Further, by using the thin prepreg sheet as described above, a golf club shaft made of a fiber-reinforced plastic having a stable quality with a small variation in circumferential thickness can be obtained.
【００５８】これによって、本発明の繊維強化プラスチ
ック製ゴルフクラブ用シャフトによれば、軽量であっ
て、しかも捻り強力が従来の繊維強化プラスチック製ゴ
ルフクラブ用シャフトと同等或いはそれ以上であり、か
つ安定した品質の繊維強化プラスチック製ゴルフクラブ
用シャフトになる。Thus, according to the fiber reinforced plastic golf club shaft of the present invention, the golf club shaft is lightweight, has a torsional strength equal to or higher than that of the conventional fiber reinforced plastic golf club shaft, and is stable. A golf club shaft made of fiber reinforced plastic having a high quality.
フロントページの続き (72)発明者 滝口 郁朗 愛知県豊橋市牛川通四丁目１番地の２ 三 菱レイヨン株式会社豊橋事業所内 Ｆターム(参考） 2C002 AA05 CS03 MM02 Continuation of the front page (72) Inventor Ikuro Takiguchi 4-1-1 Ushikawa-dori, Toyohashi-shi, Aichi F-term (reference) 2C002 AA05 CS03 MM02
Claims (2)
せてなるゴルフクラブ用シャフトであって、アングル層
とストレート層とを具備し、しかも前記アングル層が厚
さ０．０２０〜０．０９５ｍｍのプリプレグシートによ
って成形されており、かつゴルフクラブ用シャフト全体
の重量が３０〜５５ｇであることを特徴とする繊維強化
プラスチック製ゴルフクラブ用シャフト。1. A golf club shaft comprising a plurality of fiber reinforced plastic layers laminated, the prepreg having an angle layer and a straight layer, wherein the angle layer has a thickness of 0.020 to 0.095 mm. A golf club shaft made of a fiber-reinforced plastic, which is formed of a sheet and has a total weight of the golf club shaft of 30 to 55 g.
の補強繊維の繊維目付が２０〜９５ｇ／ｍ2 であること
を特徴とする請求項１に記載の繊維強化プラスチック製
ゴルフクラブ用シャフト。2. The fiber reinforced plastic golf club shaft according to claim 1, wherein the basis weight of the reinforcing fibers of the prepreg sheet for forming the angle layer is 20 to 95 g / m 2 .