IE56821B1 - Balloon and manufacture thereof - Google Patents
Balloon and manufacture thereofInfo
- Publication number
- IE56821B1 IE56821B1 IE1390/90A IE139090A IE56821B1 IE 56821 B1 IE56821 B1 IE 56821B1 IE 1390/90 A IE1390/90 A IE 1390/90A IE 139090 A IE139090 A IE 139090A IE 56821 B1 IE56821 B1 IE 56821B1
- Authority
- IE
- Ireland
- Prior art keywords
- balloon
- tubing
- molecular weight
- high molecular
- psi
- Prior art date
Description
Background
Xn Nonoperative Dilatation of Coronary10 Artery Stenosis - Percutaneous Transluminal Coronary
Angioplasty, The New England Journal of Medicine,
Vol. 301, No. 2, pages 61-68, July 12, 1979, Gruntzig ef al. disclose an improved technique for the use of a dilating catheter to relieve arterial stenosis. Accord15 ing fo Gruntzig et al. the technique of transluminal angioplasty for the treatment of atherosclerotic obstruction of the femoral artery was first introduced in 1964 by Doffer and Judkins.
Balloon catheters are not limited in their use to the relief of arterial stenosis but have been found useful in many medical applications involving not only insertion into blood vessels but also involving insertion into a variety of body cavities.
Although medical procedures using balloon catheters are still in the exploratory stage, particularly in the United States, considerable art is already available on the use of balloon catheters and their fabrication. Representative of such art are United States Patents 4,093,484; 4,154,244; and 4,254,774,
US-&-4 254 774 discloses a single-lumen, one piece catheter approximately 1mm (0.04 inch) in diameter with an integral balloon at its end having a wall thickness of 0ol3mm (0.005 inch) or less, sufficiently smell to.be retractable by suction into the catheter and to be extensible at a desired site by fluid pressure. The balloon may have a calibrated restricted leak aperture.
The balloon portion of the catheter is made by heating a portion of the catheter tubing, stretching the tubing lengthwise, and applying fluid pressure to the tubing*
The apparatus for forming the balloon includes a spring-loaded clamp to hold the tubing at one end, a capstan to hold the tubing at the other end, a heating coil wrapped around th© tubing near the clamped end thereof and mounted with the clamp, and a mechanism for controlling the pressure and volume of the pressurizing gas entering the lumen of the tube in accordance with the retractile movement of the spring-loaded clamp*
Balloons cen be made from a variety of known materials which ere generally of the thermoplastic polymeric type* included among the known materials disclosed in the aforesaid Patents are ethylenebutylene- styrene block copolymers admixed with low molecular weight polystyrene and, optionally, polypropylene, and similar compositions
J employing butadiene or isoprene in place of the ethylene and butylene; poly(vinyl chloride); polyurethanes; copolyesters; thermoplastic rubbers; siliconepolycarbonate copolymers; and ethylene-vinyl acetate copolymers;
It Is an object of this invention to provide * balloons which exhibit physical properties, for example, toughness, flexibility and tensile strength, superior to those exhibited by balloons known in the d arte A further object is to provide balloons which, because of their superior physical properties, have thinner wall thicknesses than commonly used balloons.
Another object is to provide such balloons vtfiich, because of their flexibility and thin walls, are more readily collapsible and more easily transportable in the body. It is also an object of the invention to provide such balloons which exhibit very little elongation or creep radially, collectively referred to herein as radial expansion, when inflated to the pressure necessary to perform the desired medical procedure, A further object is to provide such balloons which, if they burst under pressure, burst in the axial direction to give an axial rupture, thus ensuring atraumatic removal, it being well known that a balloon which bursts in a circumferential direction may provide fragments which either are removable only with difficulty or are not removable at all nonsurgically, A further object is to provide such balloons which, because of their superior physical properties, can be used in medical procedures with a greater probability of success. Another object is to provide such balloons which, because of their superior physical properties, can be used in medical procedures under conditions not currently achievable using commonly available balloons.
Still another object is to provide a process for fabricating such balloonse These and other objects will become apparent from the following discussion of the invention*
BRIEF DESCRIPTION OF THE DRAWINGS 5 FIG, 1 lu an elevation, in section, showing f only tlie back half of the mold, balloon, tubing and attendant hardware of an apparatus which can be used to form the balloon of the invention from drawn 1 polymeric tubing«,
FXG* 2 shows the radial expansion (%) and burst pressure (psi) of three balloons of the invention (C, D and E) as compared to the radial expansion (%) and burst pressure (psi) of two balloons of the art (A and 3)»
DETAILED DESCRIPTION OF THE INVENTION
The invention resides in an improved balloon having an unusual combination of physical properties and which is especially useful in medical dilatation procedures. The invention also resides in a process for fabricating such balloons, and in a dilatation balloon catheter comprising such an improved balloon.
The process comprises, at a temperature within the range extending from the second order transition temperature to the first order transition temperature, preferably at a temperature of S4-99°C, more preferably 86-96eC, drawing a polymeric, preferably a polyethylene terephthalate (PET) homopolyester, tubing, having a finite length (Lp and an internal diameter (ID) which is preferably about oneMialf the outer diameter (OD), to a length (l>2) which is preferably 3 to 6 L^, and thereafter expanding the drawn tubing of internal diameter IDi and outer diameter ODx by expanding means to an internal diameter (ID2) which is preferably 6 to 8 ID and an outer diameter
I (OD^) which is preferably about 3 to about 4 OD, followed by cooling the drawn and expanded tubing to less than its second order transition temperature, the balloon thus formed having a burst pressure, that is, the internal pressure at which the balloon bursts, of at least 200 psi (1.4 MPa) and a radial expansion beyond nominal inflated diameter of less than 55 at 200 psi (1.4 MPa), the preferred PET homopolyester, after conversion to tubing and balloon, having an intrinsic viscosity of 0.8 to 1.1. Such preferred tubing can be commonly formed by conventional extrusion techniques from PET homopolyester resin having an intrinsic viscosity of 1.0 to 1.3 and a density of 1.35 to 1.45.
The balloon prepared by the process of this invention exhibits an unusual combination of film properties, such as toughness, flexibility and tensile strength.
For example, the balloon of the invention exhibits a burst pressure of at least 200 psi (1.4 MPa), preferably at least 400 psi (2.8 MPa), more preferably at least 500 psi (3.4 MPa) at ambient temperature (20°C) . Moreover, the balloon of the invention exhibits a radial expansion beyond nominal inflated diameter of less than 55 when at a pressure of 200 psi (1.4 MPa) and less than 105 when at a pressure of 400 psi (2.8
MPa). PIG. 2 herein depicts burst pressure vs. radial expansion for two balloons (A and B) commonly available commercially and comprised of poly(vinyl chloride) and for three balloons (C, D and E) of the invention and comprised of PET homopolyester. Balloons A and C have nominal outer diameters of 3.7 mm; balloons B and □,
.0 mm; and E, 6.0 mm. The wall thicknesses of A through
E were, respectively, about 0.028, 0.038, 0.028, 0.038, and 0.045 mm. Radial stress data for the balloons of the invention were calculated from the well known was membrane equation,and the ultimate elongation/measured on flat film samples which were similarly biaxially oriented. Similar calculations were made for the poly (vinyl chloride) balloons except that published data were used for ultimate elongation. Xt can be seen that the burst pressures for the balloons of the invention are, respectively, 3*2, 3.4 «and 3.5 times those for the balloons of the art. Regarding the burst pressure and radial expansion data reported M herein, radial expansion is determined frost the point af which the balloon is pressurized so as to be free
J of wrinkles, that is, after being inflated from its collapsed position* to its nominal inflated diameter; a gas pressure of 75-100 psi (0.3-0.7 ») is required fo reach this first expanded position with the PET homopolyester balloon of this invention. Xn general, a balloon of higher strength can be produced from the polymeric tubing by operating af high stretch ratios, that is, af the upper ends of the draw and expansion ratios. The balloon thus produced exhibits lower elongation, which is reflected in lower expansion values at a given inflation pressure, vis-a-vis a balloon produced under lower stretch conditions.
Intrinsic viscosity is determined herein by means of ANSX/ASTM D 2857-70 and density, by ASTM D 1505* Burst pressure is determined by a simple laboratory procedure whereby one end of the polymeric balloon is sealed off and a pressurised gas is introduced incrementally into the other end. The inflation pressure af which the balloon bursts af about 20°C (ambient temperature) is referred to herein as the burst pressure.
The process by which the balloon is prepared can be carried out in a conventional manner with conventional equipment using a specialized polymer as the material of fabrication. For example, the tubing of appropriate dimensions and of high molecular weight polymer is first drawn at a suitable temperature
J from a length Χ,χ to a length Lo. The drawn tubing is then expanded in a confining apparatus such as depicted in FIG. 1 which is a part of this specification. As shown therein one end of the tubing can be filled with a fluid under pressure during the expansion step of the process. The mold has a cavity of dimensions commensurate with the desired size of the balloon to be produced. The open end of the tubing is equipped with a suitable fitting so that a pressurized fluid can be introduced info the tubing. Any suitable fluid can be used fo pressurize for inflation of drawn tubing, for example, a gas, such as nitrogen.
Xf the tubing extends beyond the mold, such as shown in FIG. 1, use of a restraining means is preferred fo
I5 maintain the dimensions of the tubing in the region outside the mold while pressure is being applied to the inside wall of the tubing. The restraining means can be of any material which is nondeformable under the tubing expansion conditions. After the drawn tubing is positioned in the mold, heat is applied to raise the tubing temperature. Similar temperatures can be used for both the drawing and expanding steps.
A suitable temperature is the range extending from the second order transition temperature fo the first order transition temperature of the polymer from which the tubing has been fabricated. For the PET homopolymer demonstrated herein, the preferred temperature is 84-99°C, more preferably 86-96®C. Although PET homopolymer is the only polymer demonstrated herein, it is to be understood that any high molecular weight polymer that can be extruded info tubing and then drawn and expanded in general accordance with the aforesaid process is operable, for example, a PET copolyester or even a nonpolyester polymer, provided the resultant balloon exhibits the desired film properties, such as toughness.
Xf the balloon flexibility and tensile strength* is to be used in medical procedures involving contact with tissue, the polymeric material of construction should be tissue compatible.
xt is critical to the invention that the intrinsic viscosity, a measure of the molecular weight of the polymer, be high. When the polymer is a homopolyester or copolyester PET resin, special, but * well known, techniques may be employed to increase the molecular weight to the necessary level. The most commonly available PET homopolyester generally has an intrinsic viscosity of about 0.5 to 0.6, well below the requisite 1.0 to 1*3.
Xt win be understood by one skilled in the 15 art that some adjustment in the draw and expansion ratios and the draw and expansion temperatures, as well as the intrinsic viscosity (molecular weight) and density, may be necessary to accommodate the difference in basic physical properties between the PET homopolyester exemplified herein and anv other polymer used to fabricate the balloon*
One skilled in the art also will understand that, although the tubing drawing step is performed prior to the tubing expansion step, the latter can be performed immediately after the drawing of the tubing, or it can be performed at a later time. Moreover, although the drawing of the tubing can be performed using any suitable drawing means, it conveniently can be effected in the apparatus depicted in FIG. 1 so that the drawn tubing is already in place to perform the expansion. Because of the recovery characteristic of shaped polymeric structures v/hich are drawn by the procedures used herein, it may be necessary to maintain axial tension on the drawn tubing during the expansion step. Consistent with all I the above and readily understandable to one skilled in the art, the drawing and expansion steps can be performed at the same or at different temperatures e
The desired temperature can be achieved by any suitable heat generating meanse Xn actual experiments carried out herein with respect to the use of FET homopolyester, hot water was employed. Drawing of the tubing herein V was achieved by using the weight of the mold.
A dilatation balloon catheter comprising the i* balloon of the invention can be fabricated by means of conventional techniques, and such a catheter can be used in accordance with accepted medical procedures.
Following is a description of a representative example of the invention. References to FIG. 1 in this example are for purpose of describing the cylinder dimensions A, B, C and D, since the embodiment of this example is only partially reflected in the figure, as will be obvious from the description. Tubing (1.5 mm CD x 0.75 mm ID) is inserted into a mold having a cavity shaped in the form of a cylinder, similar fo that shown in FIG. 1, with ends which taper to smaller diameter cylinders slightly larger than the tubing OD. The diameter D of the cavity is about 5 mm and its length A > B 4- C, about 15 mm. The tubing is pinched off af the lower end of the mold, and weights are attached to the mold to produce the required axial drawing (about 3X). The total weight of mold and weights is about 150 g. The weight of the assembly (mold, tubing and weights) is supported by the tubing which is fixed af its upper end by insertion info a tubing fitting. The assembly is inserted into a liquid medium at 87eC and allowed to heat for about 1 minute.
During that time axial orientation occurs because of the weight of the assembly in the heated liquid supported by the tubing. About 200 psi (1.4 MPa) of gas b
pressure is applied to the tubing, which radially orients the tubing (about 3.33X) in the mold cavity. This pressurization step lasts about two minutes, during which there is some additional axial draw. The assembly is cooled by immersion into a cold liquid, the pressure is released and the finished balloon is removed from the mold.
The process oi' this example was used to produce balloons having wall thicknesses of about 0.028 0.045 mm and burst strengths of 480-525 psi (3.3-3.6 MPa) t as showing in FIGo 2. The failure mode (on bursting) of such balloons is an elliptically shaped hole having its major axis substantially along the axial direction.
An alternate fabrication method and one more suitable for mass production would utilise a stationary mold having internal flow passages for hot and cold fluids. The tubing would be axially oriented to predetermined ratios by a stepper motor rather than by means of an attached weight. During the radial expansion phase, additional axial drawing may be required.
Claims (17)
1. High molecular weight, biaxially oriented, flexible polymeric balloon, the tensile strength of the wall of said balloon being at least 218*66 MPa (31,7X4 psi). 5
2. Balloon of Claim 1 having a burst pressure of at least 1.4 MPa (200 psi).
3. High molecular weight, high tensile strength, biaxially oriented, flexible polymeric balloon having a burst pressure of at least 1.
4. MPa (200 psi). 10 4. Balloon of any one of Claims 1 to 3 wherein the polymer is a polyethylene terephthalate homopolyester having an intrinsic viscosity of 0*8 to 1.1.
5. Balloon of any one of claims l to 4 having a wall thickness of 0.028 to 0.045 am. 15
6. Dilatation balloon catheter comprising the balloon of any one of claims 1 to 5.
7. Process for forming a high molecular weight, high tensile strength, biaxially oriented, flexible polymeric balloon according to Claim 1 or Claim 3, the process 20 comprising, at a temperature within the range extending from the second order transition temperature to the first order transition temperature, drawing a polymeric tubing having a finite length (L 1 ), an infernal diameter (ID) and an outer diameter (OD) to a length (L 2 ), and thereafter expanding the 25 drawn tubing of infernal diameter (ID X ) and outer diameter (0D x ) by expanding means to an infernal diameter (ID 2 ) and an outer diameter (OD 2 ) whereby the ratio (XD 2 )/(ID) is substantially greater than the ratio (OD 2 )/(OD), followed by cooling the drawn and expanded tubing to less than its 30 second order transition temperature.
8. process of claim 7 (when referred to Claim 1) wherein the balloon thus formed has a burst pressure of at least 1.4 MPa (200 psi).
9. Process of Claim 7 or claim 8 wherein the expanding 35 means is pressurized fluid applied to the inside of the tubing.
10. Process of claim 9 wherein the pressurized fluid is a pressurized gas.
11. Process of any one of Claims 7 to 10 wherein the polymeric tubing is formed hy extrusion of polyethylene terephthalate homopolyester resin having an intrinsic viscosity of 1.0 to 1.3 and a density of 1.35 to 1.45. 5
12. Process of any one of Claims 7 to 11 wherein the j tubing drawing temperature is different from the tubing expanding temperature.
13. Process of any one of Claims 7 to 12 wherein the ratio 9 (ID 2 )/(ID) to (OD 3 )/(OD) is in the range 1.5 to 2.57. 10
14. Dilatation balloon catheter comprising the balloon produced by the process of any one of Claims 7 to 13.
15. High molecular weight, biaxially oriented, flexible polymeric balloon, the tensile strength of the wall of said balloon being at least 218.66 MPa (31,714 psi), obtainable 15 by drawing and radially expanding high molecular weight biaxially orientable polymeric tubing of internal diameter (ID) and outer diameter (OD) to an internal diameter (ID 2 ) and outer diameter (OD 2 ) whereby the ratio (XD 2 )/(ID) is substantially greater than the ratio (OD 2 )/(OD). 20 16. High molecular weight, high tensile strength, biaxially oriented, flexible polymeric balloon having a burst pressure of at least 1.4 MPa (200 psi) obtainable by drawing and radially expanding high molecular weight biaxially orientable polymeric tubing of internal diameter 25 (ID) and outer diameter (OD) to an internal diameter (ID 2 ) and outer diameter (0D 2 ) whereby the ratio (ID 2 )/(ID) is substantially greater than the ratio (OD 2 )/(OD). -1217. A high molecular weight flexible polymeric balloon substantially as hereinbefore described with reference to the drawings.
16. 18. A process substantially as hereinbefore described with reference to the drawings.
17. 19. A dilation balloon catheter substantially as hereinbefore described with reference to the drawings.