HU202166B - Water insulating composition for building industry - Google Patents
Water insulating composition for building industry Download PDFInfo
- Publication number
- HU202166B HU202166B HU872874A HU287487A HU202166B HU 202166 B HU202166 B HU 202166B HU 872874 A HU872874 A HU 872874A HU 287487 A HU287487 A HU 287487A HU 202166 B HU202166 B HU 202166B
- Authority
- HU
- Hungary
- Prior art keywords
- weight
- parts
- composition
- dispersion
- mixture
- Prior art date
Abstract
Description
A találmány szerinti vízszigetelő olyan kompozíció, mely 12-30 tömegrész cementből, 25-60 tömegrész szervetlen töltőanyagból — adott esetben —adalékanyagból és 8-10 tömegrész vízből, továbbá a 100 tömegrészhez szükséges mennyiségben vizes poliakrilát diszperzióból áll.The waterproofing composition of the present invention is comprised of 12 to 30 parts by weight of cement, 25 to 60 parts by weight of inorganic filler, optionally additive, and 8 to 10 parts by weight of water, and an aqueous dispersion of polyacrylate in 100 parts by weight.
A kompozícióra az jellemző, hogy a cementen, töltőanyagokon és — adott esetben adalékanyagon és vizen kívül 0,5-10 tömegrész 5-30 tömeg%-os, 350-800 móltömegű, alkil-akrilát oligomer vizes diszperzióját és a 100 tömegrészhez szükséges mennyiségben 5000-200.000 közötti móltömegű (1-4 szénatomos) alkil-akrilát és (4-12 szénatomos)alkil-akrilát elegyének 45-60 tömeg%-os vizes diszperzióját tartalmazza.The composition is characterized in that, in addition to cement, aggregates and, optionally, additive and water, 0.5 to 10 parts by weight of an aqueous dispersion of 5 to 30% by weight of an alkyl acrylate oligomer of 350 to 800 and 5,000 to 100 parts by weight are required. It contains from 45 to 60% by weight of an aqueous dispersion of a mixture of (C 1 -C 4) alkyl acrylate and (C 4 -C 12) alkyl acrylate having a molecular weight of from -200,000.
A leírás terjedelme: 4 oldal, ábra nélkülScope of the description: 4 pages, without figure
HU 202 166 BHU 202 166 B
-1HU 202166Β-1HU 202166Β
A találmány tárgya vízszigetelő építőipari kompozíció.The present invention relates to a waterproofing construction composition.
Műtárgyak vízszigetelésére igen gyakran olyan bevonó, illetve habarcs kompozíciókat alkalmaznak, amelyek a cementen és a töltőanyagként szolgáló porkomponenseken, valamint az egyéb adalékokon kívül polimer diszperziót is tartalmaznak.Very often, coating or mortar compositions containing a polymeric dispersion in addition to cement, filler powder and other additives are used for waterproofing artificial objects.
Ilyen kompozíciókat ismertet Kovács Géza:, Az építkezés vegyianyagai (Műszaki Könyvkiadó, Budapest, 1971.65-71,198-210.Ο.) című könyvében.Such compositions are described in Géza Kovács's, The Chemicals of Construction (Technical Publishing House, Budapest, 1971.65-71, 1988-210.Ο).
Itt olyan termékeket írnak le, amelyben a habarcs kötőanyagként cementet és polimer diszperziót együttesen alkalmaznak.Products are described herein in which cement and polymer dispersion are used together as a mortar binder.
A felhasznált polimer diszperziók között a poli(vínü-acetát)-ot, poli(vinüén-klorid)-ot, poliakszilátokat említ meg a könyv.Among the polymer dispersions used, the book mentions polyvinyl acetate, polyvinyl chloride, and polyacylates.
A 2.856.764. számú német szövetségi köztársaságbeli közrebocsátási irat olyan bevonóanyag kompozíciót ír le, mely vizes polimer, diszperzióból, cementből és adalékanyagokból áll.A 2,856,764. German Patent Application Laid-Open No. 2,900,125 describes a coating composition comprising an aqueous polymer, a dispersion, cement and additives.
A polimer diszperzió minősége befolyásolja a kompozíció rugalmasságát. így sztirol-butadién polimer alkalmazása esetén ridegebb, akrilgyanta alkalmazása esetén rugalmasabb bevonatot nyernek.The quality of the polymer dispersion affects the elasticity of the composition. Thus, the use of a styrene-butadiene polymer gives them a rigid coating and a more flexible coating when using an acrylic resin.
Útburkolóanyagként olyan akrilát diszperziót, cementet és bitumenemulziót tartalmazó kompozíciót ismertet a 2.809.446. sz. német szövetségi köztársaságbeli leírás, amely jó rugalmassággal rendelkezik.A composition comprising an acrylate dispersion, cement and bitumen emulsion as a paving material is disclosed in U.S. Patent No. 2,809,446. s. description in the Federal Republic of Germany, which has good flexibility.
Az 56.106.970. és 56.55.441. sz. nem vizsgált japán közrebocsátási iratok vízzáró, hézagoló kompozícióként cementet, etílén-vinü-acetát kopolimert és adalékokat tartalmazó kompozíciót ismertet.No. 56,106,970. and 56.55.441. s. Japanese Unpublished Japanese Patent Laid-Open Papers discloses a composition comprising cement, ethylene-vinyl acetate copolymer and additives as a watertight sealing composition.
A 2.524.228. számú és a 3.327.167. számú német szövetségi köztársaságbeli közrebocsátási iratok habarcs, illetve beton kompozíciókat írnak le, amelyek cementből és poliakrilát vagy butadién-sztlrol diszperzióból állnak.A 2.524.228. No. 3,327,167 and No. 3,327,167. German Patent Application Laid-Open No. 4,102,125 describes mortar or concrete compositions consisting of cement and a dispersion of polyacrylate or butadiene-styrene.
Az ismert kompozíciók hátránya az, hogy sok esetben vízszigetelő képességük, vízzáróságuk, illetve tapadószilárdságuk nem kielégítő.A disadvantage of the known compositions is that in many cases their waterproofing, waterproofing and adhesive strength are not satisfactory.
Célul tűztük ki egy olyan építőipari célra alkalmazható kompozíció kidolgozását, amely az ismerteknél jobb vízszigetelő, vízzáró tulajdonsággal rendelkezik, és a száraz vagy nedves felülethez, így pl. a beton vagy tégla felülethez jobban tapad, valamint nagyobb rugalmassággal rendelkezik, mint az ismert kompozíciók.It is an object of the present invention to provide a composition suitable for use in the construction industry, which has a better waterproofing, waterproofing properties and is suitable for dry or wet surfaces, e.g. it adheres better to concrete or brick surfaces and has greater elasticity than known compositions.
Ezt a célt úgy érjük el, hogy a kompozícióban a cement és az ismert töltő- és adalékanyagokon kívül olyan polimer kötőanyagot keverünk, amely egy (1 4 szénatomszámú) alkil-akrüát és egy (4-12 szénatomos) alkü-akrilát elegyének vizes diszperziója, ahol a fenti polimerek egymás közötti tömegaránya — szárazanyagtartalomra számítva — 1:9 és 5:5 közötti.This object is achieved by mixing in the composition, in addition to cement and known fillers and additives, a polymeric binder which is an aqueous dispersion of a mixture of (C 1 -C 4) alkyl acrylate and a (C 4 -C 12) alkyl acrylate. wherein the weight ratio of the above polymers is between 1: 9 and 5: 5 on a dry weight basis.
Ugyanis az alkü-akrilát-észter polimerek ilyen tömegarányú elegyének alkalmazásával érhető el a legjobb vízszigetelő, tapadószüárdságot és rugalmasságot mutató kompozíció.In fact, the use of such a weight ratio of alkyl acrylate ester polymers provides the best waterproofing composition with good adhesion and elasticity.
A találmány szerinti kompozícióban a polimerek móltömege: 5000 és 200.000 közötti.In the composition of the invention, the molecular weight of the polymers is between 5,000 and 200,000.
Kísérleteink során azt találtuk, hogy a kompozíció vízzáróképessége és tapadószüárdsága tovább növelhető, ha a porkomponenseket a fenti polimer diszperzióval való elegyítés előtt (1-4 szénatomszámú) alkü-akrilát, előnyösen etíl-akrílát, oligomer vizes oldatával előkezeljük, és csak ezután elegyítjük a 45-60 tömeg% szárazanyagtartalmú polimer diszperzióval.In our experiments, it has been found that the waterproofing and adhesive strength of the composition can be further increased by pre-treating the powder components with an aqueous solution of an alkyl acrylate (C1-C4), preferably ethyl acrylate, prior to mixing with the above polymeric dispersion. With a solids polymer dispersion of -60% by weight.
Az oligomer móltömege 350-800 közötti és 1030 tömeg% szárazanyagtartalmú diszperzió formájában alkalmazzuk.The oligomer has a molecular weight of from 350 to 800 and has a dry weight dispersion of 1030% by weight.
A poranyagok és az adott esetben adagolt víz tömegére számítva 0,5-10 tömeg% alkü-akrilát oligomer 5-30 tömeg%-os vizes diszperziót és 30-50 tömeg% 45-60 tömeg%-os vizes alkü-akrilát elegyet alkalmazunk.The weight of the powder materials and of the water optionally added is in the range of 0.5 to 10% by weight of an aqueous acrylate oligomer, 5 to 30% by weight of an aqueous dispersion and 30 to 50% by weight of a 45 to 60% by weight of aqueous alkyl acrylate.
A kompozíció előállításánál úgy járunk el, hogy a cementet, töltőanyaggal, előnyösen homokkal és mészkőliszttel elegyítjük.The composition is prepared by mixing the cement with a filler, preferably sand and limestone.
Az elegyet homogenizáljuk és hozzákeverjük adott esetben az adalékanyagokat.The mixture is homogenized and optionally mixed with additives.
A porelegy és adott esetben adagolt víz tömegére számítva 0,5-10 tömeg%-nyi mennyiségben 5-30 tömeg%-os vizes diszperzió formájában oligomert adunk. Aporelegyet 5-10 percig keverjük az oligomer diszperzióval és csak ezután adjuk hozzá az alkü-akrüát elegy vizes diszperzióját, mellyel további 10-15 percig keverjük az előkezelt porelegyet.An oligomer in the form of an aqueous dispersion of from 5 to 30% by weight is added in an amount of 0.5 to 10% by weight based on the weight of the powder mixture and optionally water. The apor mixture is stirred for 5-10 minutes with the oligomer dispersion and only then is the aqueous dispersion of the alkyl acrylate added, with which the pre-treated powder mixture is stirred for an additional 10-15 minutes.
A porkomponenseknek az oligomerrel történő előkezelése elősegíti a poranyagok tökéletesebb diszpergálását az alkü-akrilát elegy vizes diszperziójában.Pre-treatment of the powder components with the oligomer facilitates a more perfect dispersion of the powder materials in the aqueous dispersion of the alkyl acrylate mixture.
Ezáltal egy homogénebb, tökéletesebben összeépült szílikát-polimer rendszert tudunk előállítani, mely megszilárdulás után kiváló vízszigetelő, vízzáró tulajdonsággal és megnövelt tapadással, rugalmassággal rendelkezik.This allows us to produce a more homogeneous silicate polymer system, which, after solidification, has excellent waterproofing, waterproofing properties and increased adhesion and flexibility.
A találmány tárgya vízszigetelő építőipari kompozíció, mely 12-30 tömegrész cementből, 25-60 __ tömegrész szervetlen töltőanyagból — adott esetben adalékanyagból és 8-10 tömegrész vízből —, továbbá a 100 tömegrészhez szükséges mennyiségben vizes poliakrüát diszperzióból áll.The present invention relates to a waterproofing construction composition comprising 12 to 30 parts by weight of cement, 25 to 60 parts by weight of inorganic filler, optionally an additive, and 8 to 10 parts by weight of water, and 100 parts by weight of an aqueous polyacrylic dispersion.
A kompozíciót az jellemzi, hogy a cementen, töltőanyagokon és — adott esetben adalékanyagon és vizen — kívül 0,5-10 tömegrész 5-30 tömeg%-os 350-800 móltömegű, alkü-akrilát oligomer vizes diszperzióját és a 100 tömegrészhez szükséges mennyiségben 5000-200.000 közötti móltömegű (1-4 szénatomos) alkil-akrilát és (4-12 szénatomos)alkü-akrüát elegyének 45-60 tömeg%-os vizes diszperzióját tartalmazza.The composition is characterized in that, apart from cement, aggregates and optionally additive and water, 0.5 to 10 parts by weight of an aqueous dispersion of 5 to 30% by weight of a 350 to 800 molar alkyl acrylate oligomer and 5,000 to 100 parts by weight are required. It contains from 45 to 60% by weight of an aqueous dispersion of a mixture of (C 1 -C 4) alkyl acrylate and (C 4 -C 12) alkyl acrylate having a molecular weight of -200,000.
A polimer diszperzió elegyben az (1-4 szénatomos)alkil-akrilát és a (4-12 szénatomos)alkü-akrilát egymás közötti tömegaránya 1:9 és 5:5 közötti.The weight ratio of C 1 -C 4 alkyl acrylate to C 4 -C 12 alkyl acrylate in the polymer dispersion mixture is between 1: 9 and 5: 5.
Töltőanyagként bármely ismert, természetes vagy mesterséges szemcsés anyag alkalmazható, például barit, kaolin, kréta, kvarcliszt, kőzetőrlemények, homok és hasonlók.The filler may be any known natural or artificial particulate material, such as barite, kaolin, chalk, quartz flour, rock fragments, sand and the like.
Adalékanyagként olyan komponenseket alkalmazunk, melyek a találmány szerinti keverék kezelhetőségét, tárolhatóságát javítják. Ilyenek például a sűrítők, melyek a viszkozitást növelik: például poliakrílsavas sók, poliakrilamidok, CMC-származékok stb.: emulgeátorok például poli(vinü-alkohol), felületaktív és hasonlók; permeabilitást gátló szerek, például mikroszilikátok; színezőanyagok: például ásványi festékek, vízoldható festékek; lágyítók:As an additive, components are used which improve the handling and storage stability of the mixture according to the invention. Examples include thickeners which increase the viscosity: for example polyacrylic acid salts, polyacrylamides, CMC derivatives, etc.: emulsifiers such as polyvinyl alcohol, surfactant and the like; permeability inhibitors, such as microsilicates; coloring agents such as mineral paints, water-soluble paints; softeners:
-2HU 202166 Β például vinil-izobutíl-éter; tapadásjavítók: például alkidgyanták, uretán-alkidgyanta diszperziók és hasonló szerek.-20H 202166 Β for example vinyl isobutyl ether; adhesives such as alkyd resins, urethane alkyd resin dispersions and the like.
A találmány szerinti kompozíciót úgy állítjuk elő, hogy a cementből, töltőanyagból és az adalékanyagokból álló porelegyhez hozzáadjuk az alkilakrilát oligomer vizes diszperzióját, kívánt esetben a vizet, és homogenizáljuk az elegyet.The composition of the invention is prepared by adding an aqueous dispersion of an alkyl acrylate oligomer, optionally water, to the powder mixture of cement, filler and additives, and homogenizing the mixture.
Ezután hozzáadjuk az alkil-akrilát polimer elegy vizes diszperzióját.An aqueous dispersion of the alkyl acrylate polymer mixture is then added.
Ez a diszperziót előnyösen etil-akrilát polimer ésThis dispersion is preferably ethyl acrylate polymer and
2-dietil-hexil-akrilát polimer 2:8 tömegarányú keverékét tartalmazza.It contains a 2: 8 weight ratio of 2-diethylhexyl acrylate polymer.
Az alkalmazás során a találmány szerinti homogenizált kompozíciót felvisszük a szigetelendő felületre, amely előnyösen beton vagy tégla.In use, the homogenized composition of the invention is applied to the surface to be insulated, which is preferably concrete or brick.
Adott esetben a felvitt kompozíció két vagy több rétege közé a felületen elhelyezünk egy üveg- vagy műszál hálót vagy - szövetet és erre rávisszük a találmány szerinti kompozícióból egy további réteget.Optionally, a glass or synthetic fiber web or fabric is placed on the surface between two or more layers of the applied composition and an additional layer of the composition of the invention is applied thereto.
A találmány szerinti készítmény a következő területeken alkalmazható:The composition of the invention can be used in the following areas:
- víztároló medencék, víztornyok szigetelése,- insulation of water reservoirs, water towers,
- mozgó-, csatlakozó hézagok vízzáró lezárása,- watertight closure of moving joints,
- terasz- és erkélyszigetelések,- terrace and balcony insulation,
- hídszerkezetek szigetelése,- insulation of bridge structures,
- pincék utólagos szigetelése.- retrofitting of cellars.
A találmány szerinti kompozíciót rendszerint a helyszínen keverjük össze és a kompozíciót az öszszekeveréstől számított 30 percen belül fel kell használnunk.The composition of the invention is usually mixed on site and the composition should be used within 30 minutes of mixing.
A találmány szerinti kompozíció előnyei a következők:Advantages of the composition according to the invention are as follows:
- Bármilyen anyagú, de előnyösen tégla vagy beton műtárgy vízszigetelő bevonására, mozgó hézagok áthidalására alkalmas.- Suitable for waterproofing coatings of brick or concrete structures of any material, bridging moving gaps.
- Száraz és nedves felületre egyaránt felhordható.- Can be applied on both dry and wet surfaces.
- Kitűnő vízszigetelő-, vízzáró tulajdonsággal és megnövelt tapadószilárdsággal rendelkező, rugalmas bevonatot képez.- Provides a flexible coating with excellent waterproofing, waterproofing properties and increased adhesive strength.
- A megszilárdult keverék a betonkorróziónak ellenáll.- The solidified mixture is resistant to concrete corrosion.
A találmány szerinti kompozíciót és annak előállítási eljárását az alábbi példákkal mutatjuk be.The following examples illustrate the composition of the invention and the process for its preparation.
1. példa tömegrész F 350 pc-20 cementet (MSZ 4720 szerinti) 20 tömegrész „00”-s (MSZ 08.1366 szerinti) mészkőlisztet és 20 tömegrész mosással agyagmentesített és szárított fehérvárcsurgói homokot összekeverünk betonkeverőben.Example 1 Parts of F 350 pc-20 cement (according to MSZ 4720) 20 parts of "00" (according to MSZ 08.1366) limestone flour and 20 parts by washing of de-scaled and dried whitecoat sand in a concrete mixer.
Hozzáadunk 2 tömegrész mikroszilikát port.Add 2 parts by weight of microsilicate powder.
A homogén por elegyhez hozzáadunk 2 tömegrész mennyiségű, 300-as átlagmóltömegű etü-akri4 lát oligomer 20 tömeg%-os vizes diszperzióját.To the homogeneous powder mixture was added 2 parts by weight of a 20% aqueous dispersion of ethyl acrylate oligomer of average molecular weight 300.
Az elegyet homogenizáljuk, majd hozzáadunk 36 tömegrész 60 tömeg% szárazanyagtartalmú olyan poliakrilát diszperziót, amely 20 tömeg% 20.000 móltömegű poli(etil-akrüát) és 80 tömeg% 60.000 móltömegű poli(2-dietil-hexil-akrilát) vizes diszperzióból áll. Az elegy viszkozitása: 1000 m Pás.The mixture is homogenized and 36 parts by weight of a 60% by weight dry solids polyacrylate dispersion consisting of 20% by weight of an aqueous dispersion of 20,000 molar polyethyl acrylate and 80% by weight of 60,000 molar poly (2-diethylhexyl acrylate) are added. Viscosity of the mixture: 1000 m Pás.
A keverő tartalmát 10 percig homogenizáljuk, majd 20 percen belül portalanított, sima, nedves betonfelületre visszük fel. A felvitt rétegvastagsága: 2 mm.The contents of the mixer were homogenized for 10 minutes and then applied within 20 minutes to a dust-free, smooth, wet concrete surface. Coating thickness: 2 mm.
2. példaExample 2
Mindenben az 1. példa szerint járunk el, de a 20 tömegrész mészkőliszt helyett csak 10 tömegrésznyit alkalmazunk, és a porelegyhez még 3 tömegrész karboximetil-cellulóz 10 tömeg%-os vizes diszperzióját is hozzákeverjük.All were carried out as in Example 1, except that instead of 20 parts by weight of limestone flour, only 10 parts by weight were used and an additional 3 parts by weight of a 10% by weight aqueous dispersion of carboxymethylcellulose were added.
Az alkalmazott 50 tömeg%-os vizes akrilát diszperzió elegy (etil-akrilát és hexil-akrilát polimer 1:1 tömegarányú elegye) mennyisége 44 tömegrész.The amount of the 50% by weight aqueous acrylate dispersion mixture (1: 1 by weight mixture of ethyl acrylate and hexyl acrylate polymer) is 44 parts by weight.
A szigetelést úgy végezzük, hogy az előkészített (portalanított) nedves betonfelületre a szigetelő kompozícióból 1,5 mm vastag réteget felviszünk, majd 15 óra múlva a rétegre üvegszövetet fektetünk és erre újabb 1,5 mm vastag réteget viszünk fel a kompozícióból.The insulation is carried out by applying a 1.5 mm thick layer of the insulating composition to the prepared (dusted) wet concrete surface, then, after 15 hours, laying a layer of fiberglass onto the layer and applying an additional 1.5 mm layer of the composition.
3. példaExample 3
Az 1. példa szerint állítunk elő szigetelő kompozíciót, amelynek összetétele 25 tömegrész cement (1. példa szerinti minőségű) 10 tömegrész mészkőliszt 20 tömegrész homok.Example 1 is an insulating composition comprising 25 parts by weight of cement (grade 1) with 10 parts by weight of limestone flour and 20 parts by weight of sand.
A homogenizált porelegyhez 5 tömegrész 800 átlagmóltömegű poli(etil-akrilát) oligomer 10 tömeg%-os diszperzióját és 5 tömegrész vizet adunk.To the homogenized powder mixture were added 5 parts by weight of a 10% dispersion of polyethyl acrylate oligomer having an average molecular weight of 800 and 5 parts by weight of water.
Az elegyet 10 percig homogenizáljuk, majd hozzáadunk 35 tömegrész 2. példa szerinti etil-akrilát és hexil-akrilát polimer elegyet.The mixture was homogenized for 10 minutes and then 35 parts by weight of a mixture of ethyl acrylate and hexyl acrylate polymer of Example 2 were added.
A szigetelést azl. példában leírtak szerint végezzük.The insulation is provided by azl. Example 4a.
4. (összehasonlító) példaExample 4 (Comparative)
Mindenben az 1. példa szerint járunk el, de a porelegyhez nem adunk oligomer diszperziót.All proceed as in Example 1, but no oligomeric dispersion is added to the powder mixture.
Ennek mennyisége helyett a homok mennyiségét növeljük 2 tömegrésszel.Instead, the amount of sand is increased by 2 parts by weight.
Az etil-akrilát polimer és 2-dietil-hexil-akrilát polimer elegye helyett 36 tömegrész 60 tömeg%-os 20.000 móltömegű poli(etil-akrilát)-ot alkalmazunk.Instead of a mixture of ethyl acrylate polymer and 2-diethylhexyl acrylate polymer, 36 parts by weight of 60% polyethyl acrylate (20,000 molar weight) are used.
Mérjük az 1. példa szerinti és a kontroll kompozícióból készült bevonat tulajdonságait.The coating properties of Example 1 and the control composition were measured.
A vizsgálati eredmények az alábbiak:The test results are as follows:
-3HU 202166Β-3HU 202166Β
A vizsgálatból kitűnik, hogy a találmány szerinti bevonat rugalmasabb, jobb a felülethez való tapadása, vízzárósága jobb, vízfelvétele kisebb.The test shows that the coating according to the invention is more elastic, has better adhesion to the surface, has better water tightness and less water uptake.
Claims (2)