GB899098A - Vulcanisable silicone rubber-forming compositions - Google Patents
Vulcanisable silicone rubber-forming compositionsInfo
- Publication number
- GB899098A GB899098A GB31302/59A GB3130259A GB899098A GB 899098 A GB899098 A GB 899098A GB 31302/59 A GB31302/59 A GB 31302/59A GB 3130259 A GB3130259 A GB 3130259A GB 899098 A GB899098 A GB 899098A
- Authority
- GB
- United Kingdom
- Prior art keywords
- absorbed
- silicate
- aluminium
- oil
- cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Natural or synthetic aluminium silicates, e.g. natural and synthetic zeolites (the latter being described and claimed in Specification 773,233), permutite, heulandite, natrolite, thomsonite, analcime, kaolinite, montmorillonite, bentonite, floridine, commercial clays and bleaching earths, having absorbed therein a cross-linking agent and/or a non-peroxidic curing catalyst for silicone rubbers (see Group IV(a)), may be coated with a hydrophobic material, e.g. a triorganosilyl- or hydroxy-terminated-silicone oil, paraffin oil or a softener. In Example (5) particles of "Linde's Molecular Sieve" containing absorbed therein hexaethoxydisiloxane and dibutyl tin dilaurate, were coated with a silicone oil. In Example (3) sandblasted and degreased sheet iron and masonry were coated by spraying with a composition comprising a liquid hydroxy-terminated dimethylpolysiloxane, quartz meal and a synthetic zeolite having absorbed therein tetraethyl silicate and dibutyl tin dilaurate and hydrophobed with a coating of a dimethylsilicone oil, and the coatings were cured to rubbers at room temperature by atmospheric humidity (which drives the curing system out of the zeolite).ALSO:A silicone rubber-forming composition consists essentially of (1) an organopolysiloxane of the general formula XO(R2SiO)nX, wherein X is H or an alkyl radical, each R is an alkyl, alkenyl, aryl or halo-alkyl or halo-aryl radical and n has an average value of at least 50, (2) a filler, (3) a cross-linking agent, (4) a nonperoxidic curing catalyst, and (5) a porous aluminium silicate having absorbed therein (3) and/or (4). Ingredients specified are:-fillerssilicas, C blacks, quartz meal, asbestos meal, titania, the oxides of Zn, Fe and Mg, CaCO3, glass frit, cork powder and sawdust; cross-linking agentsethyl ortho- and polysilicates, hexabutoxy disiloxane, methyltriethoxysilane, phenyltripropoxysilane, phenylsilane-triol, triethoxysilane, tetra- and hexa-ethoxydisiloxanes, methyldibutoxysilane, tetramethylcyclotetrasiloxane, tetrabutyl titanate, polymeric butyl titanate, aluminium isopropylate, boric acid triallyl ester and butyl metaborate; catalysts-stearic, trifluoracetic and perchloric acids, dibutylamine, piperidine, tetramethylammonium hydroxide, lead octoate, tin ricinoleate, cobalt hexoate, aluminium acetyl acetonate, zirconium acetoacetate, dibutyl tin dilaurate and dioctyl tin dimaleate; aluminium silicatesnatural and synthetic zeolites (as described and claimed in Specification 773,233), permutite, heulandite, natrolite, thomsonite, analcime, kaolinite, montmorillonite, bentonite, floridine, commercial clays and bleaching earths. The silicate itself may act as a filler. The compositions can be stored at room temperature and vulcanized simply by expelling the absorbed cross-linking agent and/or catalyst from the silicate, e.g. by heating to at least 50 DEG C. or by using polar liquids, e.g. water, alcohols or nitriles, which will effect vulcanization at room temperature. The silicate containing (3) and/or (4) may be provided with a hydrophobic coating, e.g. a siloxane oil, paraffin oil or a softener. Examples are given.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DEW24088A DE1127586B (en) | 1958-09-12 | 1958-09-12 | Process for making organopolysiloxane elastomers from linear organopolysiloxanes |
Publications (1)
Publication Number | Publication Date |
---|---|
GB899098A true GB899098A (en) | 1962-06-20 |
Family
ID=7597753
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB31302/59A Expired GB899098A (en) | 1958-09-12 | 1959-09-14 | Vulcanisable silicone rubber-forming compositions |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE1127586B (en) |
GB (1) | GB899098A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2144442A (en) * | 1983-08-08 | 1985-03-06 | Gen Electric | Room temperature vulcanizable organopolysiloxane compositions |
US6669835B1 (en) | 1997-02-18 | 2003-12-30 | Atofina Chemicals, Inc. | Aqueous dispersions of polymerizable reactants and a water incompatible catalyst sorbed on an inorganic particulate carrier |
CN102827470A (en) * | 2011-06-16 | 2012-12-19 | 信越化学工业株式会社 | Room temperature curing fluorinated polyol serial-containing rubber composition and cured substance thereof |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4103650B1 (en) | 2020-02-10 | 2023-08-02 | Wacker Chemie AG | Silicone rubber compositions and their vulcanizates for use in potable water applications |
CN115504726B (en) * | 2022-09-20 | 2023-09-08 | 安徽理工大学 | Preparation method of slow-release hydrophobic microcapsule and hydrophobic concrete |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE550105A (en) * |
-
1958
- 1958-09-12 DE DEW24088A patent/DE1127586B/en active Pending
-
1959
- 1959-09-14 GB GB31302/59A patent/GB899098A/en not_active Expired
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2144442A (en) * | 1983-08-08 | 1985-03-06 | Gen Electric | Room temperature vulcanizable organopolysiloxane compositions |
US6669835B1 (en) | 1997-02-18 | 2003-12-30 | Atofina Chemicals, Inc. | Aqueous dispersions of polymerizable reactants and a water incompatible catalyst sorbed on an inorganic particulate carrier |
US7138044B2 (en) | 1997-02-18 | 2006-11-21 | Arkema Inc. | Aqueous dispersions of polymerizable reactants and a water incompatible catalyst sorbed on an inorganic particulate carrier and polymers produced thereby |
CN102827470A (en) * | 2011-06-16 | 2012-12-19 | 信越化学工业株式会社 | Room temperature curing fluorinated polyol serial-containing rubber composition and cured substance thereof |
CN102827470B (en) * | 2011-06-16 | 2016-08-03 | 信越化学工业株式会社 | Room temp solidified fluorochemical polyether based rubber composition and solidfied material thereof |
Also Published As
Publication number | Publication date |
---|---|
DE1127586B (en) | 1962-04-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US3070559A (en) | Silicone rubber stocks | |
US3065194A (en) | Method of preparing silicone rubber compositions | |
US3294739A (en) | Method of making one component room temperature curing siloxane rubbers | |
US3334062A (en) | Process for rendering inorganic powders hydrophobic | |
CA1037186A (en) | Transparent storage-stable polysiloxanes which crosslink under atmospheric conditions | |
JP4088764B2 (en) | Room temperature curable organopolysiloxane composition | |
EP0316591B1 (en) | One-component conposition curable at room temperature while eliminating an oxime | |
EP0347049A3 (en) | Improved primer compositions | |
CA1330678C (en) | Room temperature-curable organopolysiloxane composition | |
US4131589A (en) | Low temperature transmission room temperature vulcanizable silicone compositions | |
US3109013A (en) | Acyloxysilcarbosiloxanes and their uses | |
GB899098A (en) | Vulcanisable silicone rubber-forming compositions | |
US3137670A (en) | Silicone elastomers heat-stabilized with heavy metal oxides | |
US3796686A (en) | Organopolysiloxane compositions convertible into elastomers at room temperature | |
DE2117027A1 (en) | Transparent silicone rubber that can be vulcanized under ambient conditions | |
US3619256A (en) | Silicone rubber coated substrates and a method for bonding silicone rubber thereto | |
US5302648A (en) | Dealcoholization-type room temperature vulcanizing silicone rubber composition | |
US3772240A (en) | Silicone elastomers containing boric acid | |
DE3864622D1 (en) | TIN CATALYST PREPARED FROM BETA-DICARBONYL COMPOUND AND A TIN SALT AND ITS APPLICATION IN ELASTOMERIC SILOXANE COMPOSITIONS. | |
GB1590815A (en) | Low water vapour transmission rate silicone composition | |
US3705120A (en) | Room temperature vulcanizing composition | |
US4077937A (en) | Curable organopolysiloxane compositions | |
US4877828A (en) | Self-bonding silicone caulking compositions | |
GB2249552A (en) | Curable siloxane sealant | |
KR950008580A (en) | Accelerator system for crosslinking of polymers cured upon exposure to moisture in the air |