GB791192A - Method of manufacture of hollow metal bodies - Google Patents
Method of manufacture of hollow metal bodiesInfo
- Publication number
- GB791192A GB791192A GB11221/56A GB1122156A GB791192A GB 791192 A GB791192 A GB 791192A GB 11221/56 A GB11221/56 A GB 11221/56A GB 1122156 A GB1122156 A GB 1122156A GB 791192 A GB791192 A GB 791192A
- Authority
- GB
- United Kingdom
- Prior art keywords
- billet
- furnace
- lubricant
- die
- vitreous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
791,192. Extruding; making cupped bodies. COMPTOIR INDUSTRIEL D'ETIRAGE ET PROFILAGE DE METAUX. April 12, 1956 [May 9, 1955], No. 11221/56. Classes 83 (2) and 83 (4). A method of making a hollow metal body such as a shell, preferably having cylindrical and conical portions, comprises heating a metal billet to extrusion temperature, coating at least the external surface and lower part of the billet with a first vitreous lubricant having a low viscosity at the surface temperature of the billet, placing the billet 3, Fig. 4 (not shown), in a die 1, slightly compressing the billet in the die, Fig. 5 (not shown), placing in the centre of the upper part of the billet a small quantity of a second vitreous lubricant 6, Fig. 6, having a higher viscosity than the first lubricant, rapidly piercing the billet with a punch 2, Fig. 8, whose lower face has a recess 2e adapted to retain a certain quantity of the second vitreous lubricant, the metal of the billet being thereby forced down to the bottom of the die and also extruded upwardly along the wall of the die and punch, and ejecting the hollow body by means of an ejector 7. The billet is first heated to a temperature of about 1200‹ C. in. a coal furnace, gas or oil furnace, electric furnace or an induction furnace, the heating being effected without any special precautions to avoid oxidation. After withdrawal from the furnace the surface oxide on the billet may be removed by jets of water under pressure. The first viscous lubricant may be glass powder or enamel having a viscosity between 50 and 500 poises and is applied by depositing the powder on an asbestos sheet over which the billet rolls on its discharge from the furnace. The second viscous lubricant preferably comprises powder glass 6, Fig. 6, having a viscosity between 500 and 1000 poises and is applied through a funnel 5, Fig. 6. The extruded body may be subsequently machined. A specific example is given for the pressing of a 120 mm. calibre shell giving the dimensions of the punch and die, the dimensions of the billet, and the composition of the vitreous lubricants used. Specifications 716,933 and 731,321 are referred to.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR791192X | 1955-05-09 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB791192A true GB791192A (en) | 1958-02-26 |
Family
ID=9225311
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB11221/56A Expired GB791192A (en) | 1955-05-09 | 1956-04-12 | Method of manufacture of hollow metal bodies |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB791192A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103567249A (en) * | 2013-10-31 | 2014-02-12 | 中北大学 | Extrusion moulding combined mould of large long-cone horn cylinder member |
CN112157173A (en) * | 2020-09-22 | 2021-01-01 | 合肥明辉汽车零部件制造有限公司 | Automatic production line for axle housing thermal forming process |
-
1956
- 1956-04-12 GB GB11221/56A patent/GB791192A/en not_active Expired
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103567249A (en) * | 2013-10-31 | 2014-02-12 | 中北大学 | Extrusion moulding combined mould of large long-cone horn cylinder member |
CN103567249B (en) * | 2013-10-31 | 2015-07-22 | 中北大学 | Extrusion moulding combined mould of large long-cone horn cylinder member |
CN112157173A (en) * | 2020-09-22 | 2021-01-01 | 合肥明辉汽车零部件制造有限公司 | Automatic production line for axle housing thermal forming process |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US1720722A (en) | Slug for use in extrusion operations and method of extrusion | |
US2810478A (en) | Extrusion of hollow bodies | |
GB720948A (en) | Improvements in or relating to a method of manufacturing cathode-ray tubes comprising a hollow glass cone | |
GB836706A (en) | Improvements relating to the production of hollow metal bodies by pressing | |
GB791192A (en) | Method of manufacture of hollow metal bodies | |
US3335589A (en) | Hot working of materials | |
US2956337A (en) | Method of boring metals | |
GB1094047A (en) | A method of hot extrusion of metallic articles | |
US2755925A (en) | Extrusion of metals | |
US3350907A (en) | Method for extruding molybdenum and tungsten | |
GB1147945A (en) | Improvements in or relating to methods of hot extruding metals or alloys | |
US3182474A (en) | Hot extrusion of materials | |
US2893554A (en) | Method of extruding metals | |
US3118540A (en) | Apparatus for lubricationg of hot extruding of metal ingots | |
GB968520A (en) | Process for the extrusion of pre-sintered blanks or billets | |
GB1313370A (en) | Hot expanding of hollow metal billets | |
GB731321A (en) | Method of manufacturing hollow metal bodies by extrusion | |
US2395321A (en) | Making transparent camphor tablets | |
US3153482A (en) | Lubrication of mandrels for tube extrusion | |
GB1448277A (en) | Method of hydrostatic extrusion and a machine for carrying out the method | |
SU129467A1 (en) | Method of hot pressing low-plastic and refractory alloys | |
GB965579A (en) | Improvements in the manufacture of wall plugs | |
GB1493013A (en) | Extrusion of metals | |
JPS5522469A (en) | High temperature lubricating and extruding method of tubular body | |
GB650707A (en) | Improvements in or relating to the cold working of metals |