GB750521A - Improvements in and relating to the conversion of iron to steel - Google Patents
Improvements in and relating to the conversion of iron to steelInfo
- Publication number
- GB750521A GB750521A GB29417/53A GB2941753A GB750521A GB 750521 A GB750521 A GB 750521A GB 29417/53 A GB29417/53 A GB 29417/53A GB 2941753 A GB2941753 A GB 2941753A GB 750521 A GB750521 A GB 750521A
- Authority
- GB
- United Kingdom
- Prior art keywords
- steam
- oxygen
- blast
- conversion
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
In a basic Bessemer method of converting iron into steel having a nitrogen content lower than that obtained by blowing with atmospheric air, the temperature of the blast is maintained above 225 DEG C. throughout the conversion, and for at least half the total blowing time the blowing is effected with a mixture of oxygen and steam at a temperature of 250 DEG -350 DEG C. Preferably, the ratio, by volume, of oxygen to steam in the blast is between 1 of oxygen to 1,5 of steam and 1,5 of oxygen to 1 of steam. The blast may also contain combustion gases the nitrogen content of which is such that the final blast contains less than 5 per cent nitrogen and such gases may be used for preheating the steam.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
LU750521X | 1952-10-31 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB750521A true GB750521A (en) | 1956-06-20 |
Family
ID=19733377
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB29417/53A Expired GB750521A (en) | 1952-10-31 | 1953-10-23 | Improvements in and relating to the conversion of iron to steel |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB750521A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2384849A1 (en) * | 1977-03-25 | 1978-10-20 | Hoesch Werke Ag | PROCESS FOR PREHEATING THE GASEOUS OXYGEN CARRIER DURING THE CONVERSION OF THE STEEL TO OXYGEN |
-
1953
- 1953-10-23 GB GB29417/53A patent/GB750521A/en not_active Expired
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2384849A1 (en) * | 1977-03-25 | 1978-10-20 | Hoesch Werke Ag | PROCESS FOR PREHEATING THE GASEOUS OXYGEN CARRIER DURING THE CONVERSION OF THE STEEL TO OXYGEN |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB1004006A (en) | Process and plant for the production of sponge iron | |
ES236870A1 (en) | Process for making aluminum nitride | |
FR2362789A1 (en) | PROCESS FOR SUBSEQUENT TRANSFORMATION OF COKE OVEN GAS | |
GB1457793A (en) | Method of preparing reducing gas | |
GB750521A (en) | Improvements in and relating to the conversion of iron to steel | |
ES399594A1 (en) | Process for the combustion of ammonium sulfate | |
GB713300A (en) | Improvements in or relating to the manufacture of steel | |
GB710332A (en) | Improvements in the manufacture of bessemer steel and thomas steel | |
GB777381A (en) | Improvements in and relating to the conversion of pig iron | |
GB944479A (en) | Process for refining pig iron of high phosphorus content | |
GB713246A (en) | Process for the production of a steel with fixed nitrogen content | |
GB700250A (en) | Method of manufacturing steel by blowing the molten iron | |
GB718001A (en) | Improvements in or relating to processes for the pre-treatment of raw thomas iron | |
GB583775A (en) | Improvements in the manufacture of iron and steel | |
GB815112A (en) | Improvements in or relating to blast furnaces | |
GB978759A (en) | Method of producing iron in a blast furnace | |
GB965547A (en) | Improvements in or relating to a blast furnace or a low shaft furnace | |
GB943994A (en) | Improvements in and relating to the production of cast iron | |
GB691124A (en) | Process for the production of steel having a very low nitrogen content | |
GB703427A (en) | Improvements in the manufacture of steel | |
GB758707A (en) | Process for the production of basic bessemer steel of low nitrogen content | |
GB744921A (en) | Improvements in or relating to process for making steel | |
GB703429A (en) | Improvements in the manufacture of steel | |
GB692674A (en) | Process for the recovery of sulphur values from anhydrite | |
GB796890A (en) | Controlled atmospheres for the heat treatment of steels |