GB565520A - Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compound - Google Patents
Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compoundInfo
- Publication number
- GB565520A GB565520A GB649943A GB649943A GB565520A GB 565520 A GB565520 A GB 565520A GB 649943 A GB649943 A GB 649943A GB 649943 A GB649943 A GB 649943A GB 565520 A GB565520 A GB 565520A
- Authority
- GB
- United Kingdom
- Prior art keywords
- sintering
- powders
- cobalt
- nickel
- final sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
In the manufacture of articles from powdered material, which may be wholly or in part of metal, a number of sections are separately formed and joined to form the article required by applying to the abutting surfaces a boundary material having a lower melting point than the final sintering temperature of the body. The parts may be formed by pressing unsintered powders or may be cut and ground from presintered bars. The boundary material may be applied in the form of powder, foil, or by plating or sputtering &c. Bodies of large dimensions or complicated shape may be made from carbides of tungsten, molybdenum, titanium or tantalum bonded with cobalt, nickel or iron &c., and in these cases the boundary material is the same as the bond so that the final sintering yields a substantially homogeneously bonded body. Porous bodies made from powders by sintering without bonding material are united by copper, nickel, silver, cobalt, tin, or their alloys with each other or with cadmium and zinc; the sintering material diffusing into the pores. Non-metallic powders, such as ceramics, embedded in a bond of copper &c., as above, may be united to metal parts produced as described. The sections may be arranged to have different characteristics, such as hardness, specific gravity, or brittleness. The final sintering may take place in a mould of refractory material such as graphite.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB649943A GB565520A (en) | 1943-04-22 | 1943-04-22 | Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compound |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB649943A GB565520A (en) | 1943-04-22 | 1943-04-22 | Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compound |
Publications (1)
Publication Number | Publication Date |
---|---|
GB565520A true GB565520A (en) | 1944-11-14 |
Family
ID=9815613
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB649943A Expired GB565520A (en) | 1943-04-22 | 1943-04-22 | Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compound |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB565520A (en) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2717225A (en) * | 1948-08-30 | 1955-09-06 | Williams Albert Etheridge | Sintered refractory mass |
US2725265A (en) * | 1951-11-26 | 1955-11-29 | Thompson Prod Inc | Valve stem guides |
US2753858A (en) * | 1952-05-27 | 1956-07-10 | Thompson Prod Inc | Valve seat insert ring |
US2753859A (en) * | 1952-03-07 | 1956-07-10 | Thompson Prod Inc | Valve seat insert |
EP0075648A1 (en) * | 1981-09-25 | 1983-04-06 | Osaka Diamond Industrial Company, Ltd. | A method for producing a rotary dresser |
GB2135627A (en) * | 1983-01-21 | 1984-09-05 | Shahai Gulian | Improvements in or relating to the manufacture of Tandoori ovens |
EP0211643A1 (en) * | 1985-08-02 | 1987-02-25 | Ceracon, Inc. | Powder metal consolidation of multiple preforms |
EP0630713A1 (en) * | 1993-06-25 | 1994-12-28 | Saar-Hartmetall Und Werkzeuge Gmbh | Composite body made from materials having different thermal and mechanical properties |
EP1158061A1 (en) * | 2000-05-26 | 2001-11-28 | Technodop Ltd. (Société de Droit Irlandais) | Production of a solid material in parallelepipedal or cylindrical shape, laminated, sintered, cut-up and thermally treated |
-
1943
- 1943-04-22 GB GB649943A patent/GB565520A/en not_active Expired
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2717225A (en) * | 1948-08-30 | 1955-09-06 | Williams Albert Etheridge | Sintered refractory mass |
US2725265A (en) * | 1951-11-26 | 1955-11-29 | Thompson Prod Inc | Valve stem guides |
US2753859A (en) * | 1952-03-07 | 1956-07-10 | Thompson Prod Inc | Valve seat insert |
US2753858A (en) * | 1952-05-27 | 1956-07-10 | Thompson Prod Inc | Valve seat insert ring |
EP0075648A1 (en) * | 1981-09-25 | 1983-04-06 | Osaka Diamond Industrial Company, Ltd. | A method for producing a rotary dresser |
GB2135627A (en) * | 1983-01-21 | 1984-09-05 | Shahai Gulian | Improvements in or relating to the manufacture of Tandoori ovens |
EP0211643A1 (en) * | 1985-08-02 | 1987-02-25 | Ceracon, Inc. | Powder metal consolidation of multiple preforms |
EP0630713A1 (en) * | 1993-06-25 | 1994-12-28 | Saar-Hartmetall Und Werkzeuge Gmbh | Composite body made from materials having different thermal and mechanical properties |
EP1158061A1 (en) * | 2000-05-26 | 2001-11-28 | Technodop Ltd. (Société de Droit Irlandais) | Production of a solid material in parallelepipedal or cylindrical shape, laminated, sintered, cut-up and thermally treated |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US3684463A (en) | Jewelry products | |
GB565520A (en) | Improvements in the production of bodies formed of or comprising metal powder or powdered metallic compound | |
GB1440196A (en) | Method of producing a specified solder layer thickness in the production of semiconductor components | |
RU2011110729A (en) | DRILL BIT AND OTHER PRODUCTS CONTAINING CEMENT CARBIDE | |
US2671955A (en) | Composite metal-ceramic body and method of making the same | |
ES351215A1 (en) | Method for making a metal bonded diamond abrasive tool | |
GB1374033A (en) | Method of manufacturing a sintered body from powdered material | |
US2313070A (en) | Metal composition | |
US3672881A (en) | Method of making powder composites | |
WO2014018235A8 (en) | Composite sintered powder metal articles | |
US4280841A (en) | Method for manufacturing a mechanical seal ring | |
US2331584A (en) | Method of making composite articles | |
US2679683A (en) | Porous metal element | |
US3087814A (en) | Friction element | |
KR850004121A (en) | Composite bearing material and its manufacturing method | |
US2600995A (en) | Tungsten alloy | |
US2126737A (en) | Manufacture of articles from powdered materials | |
GB1117668A (en) | Improvements in and relating to the production of composite metallic billets by powder metallurgy | |
GB1399669A (en) | Method of consolidating metallic powder | |
US2162701A (en) | Manufacture of articles from powdered metals | |
GB772435A (en) | Improvements in or relating to sintered metallic bodies and their manufacture | |
CN108495730B (en) | Material obtained by compression and densification of metal powders | |
US3294530A (en) | Flash sintering | |
RU2582867C1 (en) | Method of producing copper-titanium current-conducting element | |
ES397356A1 (en) | Composite product including magnetic material and method of production thereof |