GB2403684A - Plastic injection moulding with a rotating insert member - Google Patents

Abstract

A method for making hollow rib structures for trim components and panels (50 figure 3) using gas assisted injection moulding. Plastic material is first injected into a mould cavity 303 and then further packed into the mould cavity. A gas is injected into the packed plastic, and a rotatable insert 300 with a recess 304 located in the mould cavity is rotated to increase the volume of the mould cavity. Gas is then introduced into the rib members (54 figure 3) displacing a portion of the molten plastic material into the recess created by the rotatable insert, thereby forming hollow channels or openings in the plastic material. The completed article is allowed to cool and solidify in the mould where the gas is then vented from the hollow portion of the plastic article. A further embodiment relates to an injection moulding system comprising a mould cavity, a plastic injector and a rotatable insert having a recess.

Description

PLASTIC INJECTION MOLDING WITH

ROTATING INSERT MEMBERS

The present invention relates to plastic injection molding and more particularly to plastic injection molding using gas assist and the formation of hollow rib members on plastic injection molded parts.

In the plastic injection molding art, the usual challenges facing the product designer include designing an article having the requisite strength for the product application and satisfactory surface finish, as well as avoiding excessive weight, surface distortions, and increased cycle time. For flat or thin products, it is typical to include one or more rib members in the design to provide relative strength and structure for the molded article. The rib members are typically thicker than the molded article which increases the weight, material usage, and cycle time of the article, and often induces sink marks and other surface defects due to a thermal gradients in the area of the thickened section.

It is known in the plastic molding art to use pressurized gas, such as nitrogen, in conjunction with plastic injection molding of articles. Pressurized gas serves several purposes. The gas allows the article or rib structure to have hollow interior portions which result in savings in weight and material, thereby reducing costs. The pressurized gas also applies an outward pressure to force the plastic against the mold surfaces while the article solidifies. This helps provide a better surface on the molded article and also reduces or eliminates sink marks and other surface defects. The use of pressurized gas also reduces the cycle time as the gas is introduced and/or migrates to the most fluent inner volume of the plastic and replaces the plastic in those areas which would otherwise require an extended cooling cycle. The pressure of the gas pushing the plastic against the mold surfaces further increases the cooling effect of the mold on the part, thus solidifying the part in a faster manner and reducing the overall cycle time.

Where the rib members or other portions of the article in which the gas is being introduced are elongated, it is often difficult to provide a satisfactory molded article. For example, if the pressure of the gas is too great as it enters the mold cavity, there is a risk that it may rupture or blow out the plastic within the mold cavity, i.e. the gas is not contained within the plastic. Also, it is often difficult to have the gas migrate along the full length of an elongated, thicker plastic section, thus creating a product which has an uneven thickness and cooling cycle.

One manner which has been developed in order to overcome some of the above-mentioned problems is shown in U.S. Patent No. 5,098,637. In that process, a secondary cavity (alk/a "spillover" cavity) is provided at one end of the molded part or elongated rib member in order to collect and contain the more fluent plastic material which is forced out of the article or rib member by the pressurized gas.

Another system is shown in U.S. Patent No. 5,885,518.

An object of the present invention is to provide an improved method of gas assisted injection molding. It is another object of the present invention to provide an improved method and system for injection molding plastic parts with structural i rib members.

It is a still further object of the present invention to provide a method and system for gas assist injection molding which eliminates the need for spillover cavities and the subsequent capture and regrinding of excess plastic material from a mold cavity. It is an additional object of the present invention to provide a moveable insert in a mold cavity and allow packing of the plastic material in the; mold for better dimensional and surface effects. i According to the present invention there is therefore provided a method, and system, for making an injection molded plastic article as defined in the t accompanying claims.

In accordance with the objects of the present invention, in an embodiment one or more movable insert members are provided in the mold cavity. The insert members are particularly located in portions of elongated rib members in which pressurized gas is to be introduced in order to provide hollow portions in them. The insert members can be held in place by spring or other biasing members or mechanisms which are adapted to be overcome by the force of the plastic and pressurized gas when the gas is introduced into the rib members.

A full-shot of plastic material is first injected into the mold cavity. The I plastic material is then packed in the mold by additional pressure and/or plastic injection from the molding machine. Thereafter, pressurized gas is introduced into at least one of the rib members. As the gas channel is formed in the rib member(s) and the fluent plastic material in the center of the rib member(s) is pushed along the rib member(s) and out the opposite end(s), the spring or biasing force on the insert member(s) in one embodiment of the invention is overcome. As the insert member(s) retracts, the plastic material fills the entire article defining mold cavity.

The displaced plastic material flows into the area formerly occupied by the insert member(s), creating an additional rib or part of the molded article.

Once the entire article is formed, the plastic is allowed to cool and solidify.

The injected gas pressure is then relieved (vented or exhausted) from the formed i article and the article is ejected or removed from the mold.

In one preferred embodiment, the insert member is held in its initial position by spring tension, pressurized cylinders, damping mechanisms, or the like. These tensioning or biasing mechanisms provide a sufficient biasing force to resist the level of force caused by pressure in the mold from the initial injection of the plastic material. This maintains the nominal wall thickness of the article being molded throughout the full extent of the mold with the exception of the thicker section of I the rib members. Once the cavity is full, pressurized gas is introduced at the end of the rib members opposite the insert members. The force of the gas pressure and the t resin forced from the rib members overcomes the biasing force of the insert members.

In order to withstand the additional packing pressure applied to the plastic material in the mold, the insert members are fixed or locked into position by use of a releasable locking mechanism. The locking mechanism can be a pneumatic, hydraulic, or electrical mechanism, or can utilize a controllable fluid which can be solidified by application of an electric current. The insert member can then be released for movement when the gas is injected by the use of various devices, such as position sensors, cavity pressure sensors, timers, or the like, or the deactivation of the electric current. The release or deactivation of the locking mechanism can be based or triggered in a number of different ways, such as by attainment of certain pressures in the mold, process timing sequences, linear movement of the injection screw, etc. In another embodiment, the insert member is rotatable and has a recess or groove therein. Once the plastic packing step is completed, the insert member is rotated so that the recess or groove opens up into the mold cavity. The injection of the gas displaces a portion of the still-fluent plastic into the recess or groove, thereby forming the complete article.

the above objects and other objects, features, and advantages of the present invention are readily apparent from the following detailed description of the preferred embodiments for carrying out the invention when taken in accordance with accompanying drawings, in which:.

FIGURE 1 is a schematic diagram of a typical plastic injection molding system; FIGURE 2 is a schematic diagram of an article being molded in a conventional gas assisted plastic injection molded system; FIGURE 3 is a perspective view of a molded part or article according to an embodiment of the present invention; FIGURE 4 is a cross-section of a structural rib member on a part made in accordance with an embodiment of the present invention, the cross-section being taken along lines 4-4 in Figure 3 and in the direction of the arrows; FIGURE 5 is a cross-sectional view of a mold utilizing an embodiment of the present invention.

FIGURE 6 is a partial cross-sectional view showing an insert member in accordance with an embodiment of the present invention; FIGURE 7 is another view of an insert member in accordance with the present invention, the view being taken in the direction of the arrows 7-7 in Figure 6.; FIGURE 8 is another view of the insert member and mechanism as shown in Figure 7, with the insert member being displaced in response to the introduction of gas in a rib member; FIGURE 9 is a flow diagram indicating the basic steps involved in the practice of the method of an embodiment of the present invention; FIGURE 10 is a schematic diagram depicting a locking mechanism for an insert member; FIGURES 11 illustrates an alternate mechanism and system for locking an insert member in place; FIGURE 12 is a flow diagram of an alternate embodiment of the invention; FIGURES 13 and 14 illustrate an alternate type of insert mechanism for use with an embodiment of the present invention; FIGURE 15 illustrates another embodiment of an alternate insert member; and FIGURE 1 6A- 1 6F schematically depict a molding process utilizing an embodiment of the present invention.

The present invention is particularly suitable for producing hollow rib structures for structural reinforcement of decorative or non-decorative trim components and panels using gas-assist plastic injection molding.

As shown in Figure 1, a conventional plastic injection molding system 20 is shown. The system 20 includes an injection molding machine 22, a mold 24, and a source of gas 26 for the gas assisted injection molding. As is well known in the injection molding field, injection molding machine 22 has a hopper 28 in which plastic pellets are added to the machine. The injection molding machine includes a mechanism t'or melting the plastic material and a screw-type ram (not shown) in the body of the machine. 'I'he molten plastic material is injected through a nozzle 30 into the mold 24.

Mold 24 includes two mold halves 24A and 24B. 'I'he two mold halves are connected to platens 32 and 34 which separate and come together as one or more is moved on the injection molding machine.

The gas used in injection molding is typically an inert gas, such as nitrogen, and is supplied from a storage canister or system (not shown) to a gas injection controller 26. The controller 26 regulates the flow of gas through a conduit 36 or the like into the mold 24.

It is to be understood that the present invention can be used with any plastic injection molding machine 22, any gas assist controller 26, and virtually any type of mold 24. In this regard, a schematic drawing of a representative mold 24 is shown in Figure 2.

An article forming cavity 40 is provided between the two mold halves 24A and 24B. The plastic material 42 is injected through the machine nozzle 30, and through a bushing 44 into the mold cavity 40. After all or a substantial portion of the plastic material 42 is injected into the mold cavity 40, gas from the controller 26 is introduced into the mold cavity. The gas forces the plastic material into all portions and into all surfaces of the mold cavity 40 and provides a hollow interior 46.

Once the plastic material 42 has cooled and solidified in the mold, the gas is vented, and the mold is then opened in order to allow the part to be removed. In this regard, there are many mechanism systems known for relieving the gas pressure in the mold, i.e. venting or exhausting the gas from the mold, and any conventional system and method can be utilized. For example, gas can be vented back through the conduit 36 to the controller, or the nozzle 30 can be backed off from the bushing 44 creating a "sprue break." Also, plastic formed articles are typically assisted in being removed from the mold by one or more ejector pins (not shown).

As indicated, the present invention is particularly suitable for producing plastic injection molded trim components and panels having rib members. A representative article of this type is shown in Figure 3 and identified generally by the reference numeral 50. As shown, the article 50 has a relatively thin thickness 52 relative to its width and length and has a plurality of rib members 54 on one surface (typically the back or non-visible surface). The outer surface 50A of the article 50 is the surface which is exposed to view when the part is used or installed in its appropriate environment. The article 50 could be, for example, a computer housing, a panel for a door or other article of a vehicle, or the like. Rib members 54 are provided on the opposite side 50B and are hidden from view during normal use of the article 50. Although four rib members 54 are shown on the article 50, any number of rib members may be utilized. The rib members in particular provide structural support for the panel-type article 50.

Since the rib members 54 are typically thicker in dimension than the width or thickness of the article 50, gas assist injection molding techniques and procedures are typically utilized in order to hollow out the rib members. This reduces the thickness of the rib members, thereby saving material cost, reducing cycle times, and minimizing or eliminating surface defects, such as sink marks, on i the viewed surface 50A.

The term "gas" used herein means any gas body gaseous during normal temperature and pressure, such as nitrogen, carbon dioxide and air. Preferably, the gas is an inert material, such as nitrogen or carbon dioxide. The gas can be provided from any conventional source, such as a storage tank, bottled gas, or the like. It is also possible in accordance with the present invention to utilize another fluid, such as water, in place of the gas. These other fluid systems are known in the art and do not need to be discussed in more detail here.

A rib member 54 is shown in cross-section in Figure 4. The article 50 has a certain thickness 52 which requires a certain cooling and cycle time. In order to provide requisite structural support, the rib member 54 typically has thicker portions, such as 54A. In order to lighten the weight of the rib member 54 and reduce its thickness, a channel 56 is provided in the rib member by the introduction of the pressurized gas or other fluid.

Although the injection molding system is shown utilizing a single bushing member 44 positioned between the nozzle 30 of the injection molding machine 22 and the mold 24, it is understood that any conventional injection molding system could be utilized in transporting the molten plastic material from the nozzle 30 to the mold cavity 40. For example, a hot runner system with one or more manifolds and a plurality of bushings could be utilized. Other systems and mechanisms known in the art could also be utilized.

A representative molding system in which the present invention is utilized is shown in Figure 5. Further details of this embodiment are shown in Figures 6-8.

The basic steps in this embodiment of the invention are set forth in Figure 9.

The present invention can be used with all types of plastic materials, particularly thermoplastic materials, which generally may be injection molded.

These materials can be, for example, low or high density polyethylene, polyurethane, polypropylene, polystyrene, acrylonitrile butadiene styrene (ADS) resin, SAN resin, polyvinyl chloride, polymethyl methacrylate, and the like.

Materials such as polycarbonate, polyester, acetyl, polyacetyl and nylon also may be used, as well as ethylene copolymers such as ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, and the like. Furthermore, any of these resins may contain fillers, such as glass fiber, powdered glass, calcium carbonate, calcium sulfate, talc, mica, and the like.

In accordance with the present invention, molten plastic material is injected from a machine nozzle 30 to a bushing 44 and into a mold cavity 60 in a mold 62.

The two mold halves 62A and 62B are adapted to separate along part line 64 in order to allow the formed plastic article to be removed. A gas regulated by gas controller 26 is introduced through conduits 36 into ends 66A of rib members 66 on the plastic article 68, which is formed in the mold cavity 60. Movable or displaceable insert members 70 are provided in the mold cavity 60, and are positioned such that they are situated at the opposite ends 66B of the rib members 66. Pressurized gas is introduced into the rib members 66 and forms channels 72 essentially through the centers of the cross-sections and throughout their lengths.

Prior to injection of the gas, the plastic material in the mold is packed by the introduction of more plastic material, and at a higher pressure. This insures excellent surface quality for the molded article or product. Also, once the plastic packing is completed, a shut off valve (not shown) in the nozzle closes off the plastic supply prior to the injection of the gas. This prevents plastic material from being forced or pushed back into the barrel of the injection molding machine. : The gas is injected into the resin in the mold at a pressure higher than the plastic injection pressure and typically at a much higher pressure. For example, the initial plastic injection fill pressure could be 100-200 psi, which will normally increase to 500-1000 psi or higher when the plastic injection is completed. 'the gas injection could be 1000- 1500 psi (if, for example, the plastic material was polypropylene) and 3000-7000 psi (if, for example, engineering grade resins were used). In general, the pressure of the gas should be sufficient to provide a commercially acceptable surface and finish on the plastic part. When the plastic is packed in the mold cavity, the pressure is raised several times over the initial injection pressure and additional plastic material is packed into the mold cavity.

The pressure of the gas is typically higher than the plastic packing pressure.

The insert members 70 are held in position in the mold cavity by a biasing or tensioning mechanism 80. In this regard, as shown in Figures 7 and 8, the insert member 70 is typically elongated in shape and thus a number of biasing mechanisms 80 are provided along its length. A biasing force is provided by the biasing mechanism 80 such as by one or more coil spring members 82 as shown in Figures 6-8. The spring members 82 provide a biasing force against the insert member 70 sufficient to oppose the force of the plastic material 68 when it is injected into the mold cavity 60. The biasing force or spring tension holding the insert member in place preferably should be sufficient to resist a force of 150-200 psi (10.4-13.8 bars).

It is to be understood that any type of biasing, tension, or force-type member or mechanism can be used to hold the insert members in place. For example, gas or air charge cylinders can be utilized in place of the coil spring members 82, or a conventional dampening mechanism could be utilized. The biasing member has to provide a sufficient force or load on the insert member to resist the level of force caused by pressure in the mold cavity during the injection of the plastic material.

This maintains the nominal wall thickness of the article 68 to the end of the flow length with the exception of the thicker section of the rib member 66. : As shown in Figures 7 and 8, the introduction of pressurized gas through the rib member 66 forms channel 72 in the rib member and forces plastic material against the insert member forcing it to move downwardly in the direction of the arrow 84 in Figure 8. The additional space formed in the mold cavity by the movement of the insert member is filled with molten plastic forced from the rib member. The additional plastic forms an additional rib member 90 adjacent the end of the now hollow rib member 66. Additional rib members of this type are shown in Figure 3 and identified by the reference numeral 90'. The additional rib members 90' are positioned at the end of the rib members 54 and can provide additional support and structural stability to the article 50. Depending on the amount of displaced plastic material and the gas injection pressure, it is also possible to provide a gas channel - and thus a hollow structure - through a portion of the new rib member 90.

Although the invention is primarily directed to the formation of structural rib members on plastic injection molded articles, such as trim components and panels, it is also possible to use the present invention to produce or provide portions of articles necessary to allow appropriate molding. For example, it is often necessary to provide molded portions of an article in order to prevent undercuts and the like and thus to assist in the production of molds which can be opened and closed more easily and allow the parts to be removed and ejected.

The thickness of the additional rib member 90 should not be greater than the maximum thickness of any other part of the molded article (for minimum cycle times). Preferably, the rib member 90 has a maximum thickness which is at least 10% less than the maximum thickness of the article. Also, depending on the strength of the rib members 90 needed for the particular application and molded part, the rib members can be increased in width. In order to insure that size and thickness of the added portion or rib member 90 remain within predetermined limits, a stop member (not shown) can be utilized to limit the travel of the insert member 70.

Although the portion formed on the molded article by the displacement of the insert member is referred to herein as a rib member, it is to be understood that the portion can have the shape and size to add virtually any structure to the article, such as, for example, a boss, a snap fit member, etc. The portion can also be used to add additional strength to the article.

The size, shape and volume of the insert member and resultant added portion formed on the article should be predetermined, so that all ejected plastic material from the rib member can be accommodated. Similarly, the size of the added portion should be sufficient to accommodate for volumetric differences in the plastic material from the shot-to-shot (i.e. from cycle to cycle). The biasing mechanism 80 allows for such volumetric differences.

As an alternate embodiment, it is also possible to introduce the gas into the rib member 66 at a location inbetween the ends 66A and 66B. In such an embodiment, it is also possible to position insert members and form additional article portions at both ends of a rib member.

The basic steps in the process in accordance with the present invention are set forth in the flow diagram in Figure 9. The basic method is referred to generally by reference numeral 100. As a first step, the plastic material is injected into the mold cavity in the mold. This is referred to by the reference numeral 110 in Figure 9. this first step is completed after the precise mold cavity size and shape is selected the mold cavity is machined in the mold, the appropriate resin distribution system, bushing, and manifold mechanism is selected and provided, the requisite size of the injection molding machine is selected, the particular type of plastic or resin material for the article or part is selected and provided, and the appropriate processing parameters, such as time, pressures, temperatures, and cycle times are determined. All of these matters are within the ordinary skill in the art. These same conventional preliminary steps and procedures are preferably followed with respect to all of the methods and process set forth herein.

The molten plastic resin material is injected into the mold cavity by the injection molding machine until the article cavity is full of plastic material. In this manner, a "full shot" of plastic material is injected into the mold cavity. In order to provide better aesthetics on the final product and insure that all of the dimensions and surface details are obtained, the injected plastic material is then packed in the mold. The pressure of the plastic injection is increased and additional plastic material is forced into the mold cavity. This pressure can be held for a certain length of time, such as 10-15 seconds, in order to form a solidified outer shell on the product. This is shown in Box 1 12 in Figure 9.

In this regard, in order to prevent the insert member from being dislodged or moving during the additional pressure or packing procedure, the insert members are held or locked into position by the use of an external locking mechanism 92 which can he a wedge, pin, or the like 94 (see Figures 5-6 and 10). The wedge 94 is situated in the mold to be moved into position preventing movement of the insert member 70. The wedge 94 is activated by a activation system 96, such as a pneumatic, hydraulic, electric, or mechanical mechanism or system and set and locked into position or released by the use of various devices, such as position sensors, cavity pressure sensors, timers, and the like (not shown).

After the mold cavity is full of packed molten plastic resin material, the gas is injected into one or more of the rib members. This is shown by Box 120 in Figure 9. The gas is preferably injected at one end of the rib members opposite the insert members and at a predetermined time and pressure. The pressure of the gas can be higher than the pressure used to pack the plastic in the mold.

In order to prevent any of the plastic material from being forced back into the nozzle or injection molding machine during gas injection, a shutoff valve should be provided at, or adjacent to, the nozzle and closed upon the completion of the packing procedure.

During the gas injection procedure, the molten plastic material is displaced from the core or interior of the rib members creating an increase in pressure on the insert member or members. This pressure overcomes the biasing force caused by the spring mechanisms or the like, forcing the insert members away from their rest positions and retracting to increase the available volume of the cavity. This is shown in Box 130 in Figure 9. The displaced plastic material from the rib members will flow into the voids formed by the displacement of the insert members. The range of movement of the insert member is preferably predetermined in order to provide an additional part or portion on the article of a certain size, shape, and length. At the end of movement of the insert member, the pressures equalize on the insert member, allowing the external gas pressure to provide packing pressure to the molded part throughout the rib members.

If desired, once the insert members are displaced and the voids are filled with the plastic material, an additional packing procedure can be provided by the introduction of a higher pressurized gas. This is shown as an alternative in Box 132 in Figure 9.

Once the mold cavity is filled with plastic material and the gas assist process is completed, the plastic article is allowed to cool and solidify in the mold. This is shown in Box 140 in Figure 9. Thereafter, the gas is vented or exhausted from the rib members as shown in Box lSO. the venting of the gas from the rib members can be accomplished in any standard manner known to persons of ordinary skill in the art. For example, one method allows the gas to vent back through the end of the rib members where the gas is initially introduced. The gas pressure can also be relieved in a stepped manner over time, or simply allowed to decay.

For the final step, the mold is opened and the formed plastic part or article is removed (or ejected) from the mold cavity. This is shown in Box 160 in Figure 9.

Thereafter, the mold is closed and the process is repeated.

lO In an alternate process, all or a portion of the gas can be injected into the plastic material after the initial plastic injection (Step 110)and prior to the plastic packing procedure (Step 112). This would allow more of the gas to be introduced into the plastic material in the mold cavity. The shut off valve in the nozzle also could be actuated prior to the gas injection step in order to prevent plastic from being forced back into the injection molding machine. The valve then could be reopened in order to pack additional plastic material into the mold cavity.

Thereafter, the shut-off valve could be closed again if the gas injection is restarted.

Movement of the insert members may provide a sufficient pressure drop to obviate the need to shut-off the plastic flow again. Also, a process procedure of backing off the clamping pressure by, for example, opening the mold a few thousands of an inch for a few milliseconds, and then closing it again - after or together with movement of the insert members could be utilized. This would allow the plastic material to flow into the void caused by displacement of the insert members and form hollow portions filled with gas in the ribs.

A flow diagram schematically illustrating this alternate process is set forth in Figure 12. The process is designated generally by the reference numeral 200. At Step 210, the plastic material is injected into the mold cavity. Then, in Step 220, all or a portion of the gas is injected into the plastic material in the mold cavity.

Thereafter, in Step 230, the plastic material in the mold is packed by the addition of additional plastic material at a higher pressure. This insures that the plastic material entirely fills out the mold cavity and is pressed tightly against all of the surfaces of the mold cavity. -D Then, if all of the gas had not been injected earlier, the remaining amount of pressurized gas is injected into the plastic material in the mold cavity. This is shown in Step 240. Also, after the plastic packing Step 230, the shut-off valve in the nozzle is closed in order to prevent plastic material from being pushed back into the barrel of the injection molding machine.

The insert member or members are moved or displaced forming voids in the mold cavity and creating additional volume(s) for the plastic material. This is shown in Step 250. A portion or portions of the still-molten plastic material is displaced or flows into the void volumes, as shown in Step 260. It is also possible at this point to open and close the mold as described above. This is shown in alternate Step 265. As the plastic material flows or is forced into the void areas, the o injected gas forms hollow portions in the plastic material, particularly along the rib members.

Once the plastic article is fully formed, it is allowed to cool and solidify (Step 270). Once the gas is vented (Step 280) or the gas pressure is otherwise relieved in some manner, the mold is opened and the molded plastic article is removed or ejected from the mold cavity (step 290).

I he rib members in which the gas is to be introduced should be designed to prevent the gas from escaping from the rib structure into the nominal wall thickness of the article. Also, the insert members should be dimensioned such that the increase in volume in the mold cavity is proportional to the volume of plastic material which is displaced by the injection of gas into the rib members. Persons skilled in the art have sufficient knowledge to accomplish these tasks.

With the present invention, the mold cavity is increased in available volume at a predetermined point in the plastic injection molding process in order to allow the molten plastic resin from the interior of the rib members to be displaced by the introduction of the gas. The present invention does not require a secondary cavity external to the mold cavity for displacement of the plastic resin material. The insert members compensate for the volumetric variation due to resin viscosity variation inherent in injection molding processes.

Also, with the present invention, volumes of plastic material from a secondary cavity do not have to be recycled or reground. This eliminates an additional processing step which results from other known processes.

An alternate mechanism for locking the insert members in place is shown in Figure 11 and identified generally by the reference numeral 170. The insert member 70' is biased by spring members 82' and connected by rod member 172 to a piston member 174. The piston member 174 is positioned in a chamber or container 176 which is filled with a controllable fluid 178. Controllable fluids are materials that respond to an applied electric or magnetic field with a change in theological behavior. Typically, this change is manifested when the fluids are sheared by the development of a yield stress that is more or less proportional to the magnitude of the applied field. These materials are commonly referred to as electrorheological (FR) or magnetorheological (MR) fluids.

Conventional devices that utilize controllable fluids are typically classified as having either fixed poles (valve mode) or relatively moveable poles (direct-shear mode). Valve mode devices can include servovalves, dampers and shock absorbers, while direct-sheer mode devices can include clutches, brakes, chucking and locking devices. The response time of the fluid damping in these devices can be on the order of 60milliseconds as the field is changed.

With the embodiment and system shown in Figure 11, coils 180 are connected to electric current source 182. When the source 182 is activated, the current through coils 180 causes the fluid 178 to harden, thereby preventing the piston member 174 from moving. This, in turn, holds or locks the insert member 70' in place. Activation of the electric current source 182 can be caused in any manner, such as being triggered by a pressure sensor 184 positioned in the mold cavity 186. A control system or mechanism 188, which preferably is a microprocessor, is set or programmed to lock up the insert member when a certain pressure is reached in the mold cavity which would otherwise displace the insert member.

The locking of the insert member could also be triggered by measurement of the movement of the screw ram in the injection molding machine, by certain timing considerations, or any other manner known in the art. For example, a linear transducer could be utilized which measures the axial movement of the screw ram and be connected to a microprocessor system.

An alternate insert member 300 is shown in Figures 13 and 14. In this embodiment of the invention, the insert member is not biased or displacable, but instead is rotatable. The insert member 300 is preferably an elongated cylinder which is positioned in one surface 302 of a mold cavity 303. The insert member 300 has an elongated recess or groove 304 which is used to form or extend a rib member on the plastic article formed in the mold cavity. The rotation (movement) of the insert member 300 is operated by a motor 306 (with appropriate gearing, etc. which is not shown) which in turn is activated by a control system or mechanism 308. The insert member 300 is also supported by and rotatable in bearing members (not shown) preferably positioned adjacent the ends of the insert member.

When the rotatable insert member 300 is in the position shown in Figures 13 and 14, a portion of its external surface 310 forms a portion of a surface of the mold cavity. However, when the motor 306 is activated and rotates the insert member in the direction shown by arrow 312, the recess or groove 304 becomes opened into the mold cavity 303. When the insert member is in the latter position, the plastic material displaced when the gas is injected moves into and fills the groove 304'.

An alternate embodiment of rotating insert member 320 is shown in Figure 15. The insert member is positioned in a mold 322 as part of an insert mechanism and insert system 323. The mold 322 has two halves 322A and 322B in which a mold cavity 324 is provided. The mold cavity 324 is filled with molten plastic material 326 as shown.

The insert member 320 rotates around its central axis 328 in the directions of rotation shown by the double-headed arrow 330. The amount of rotation can be in the range of 30 -180 , but preferably is from 60 - 90 . In Figure 15, the degree of rotation is 90 .

Two grooves 332 and 334 are provided in member 320. The grooves are elongated in the axial direction of the insert member (in the manner shown in Figure 13). Groove 332 has a moveable piston member 336 which is operated by a solenoid 338. The top surface 336A of the piston member 336 is roughened, such as by serrations or saw-tooth ridges as shown. When the groove 332 is positioned so that it is in communication with the mold cavity 324, the serrated surface 336A is substantially flush or level with the lower surface 324A of the mold cavity.

Following the injection of plastic material 326 into the mold cavity, the insert member 320 is rotated in order to expose open groove 334 to the mold cavity (as shown in Figure 15). The groove member 334 has the shape of a rib member and is used to form part of a rib member 335 on the molded plastic article.

In order to rotate the insert member 320 from one position to the other, the solenoid 338 is actuated and the piston member 336 is lowered in groove 322 to the position shown in Figure 15. This prevents the serrated surface 336A from interfering with the edge of the opening 340 in the surface 324A of the mold cavity, or from smoothing out the serrations 342 formed in the bottom surface of the plastic material 326 in the mold cavity. The serrations 342 formed in the plastic material can provide improved bonding or adhesion of the plastic material which flows, or is displaced, into the groove 334. (It is also possible to utilize this process without any serrations or roughened surfaces on the piston member 336.) Also, to prevent distorting or damaging of the serrated surface 342 and/or to allow the insert member 320 to rotate freely between the two positions, it is possible to lower or alter surface 344 on the insert member surface between the two grooves 332 and 334. Such a surface 344A is shown in broken lines in Figure 15.

The operation of the insert member during the gas-assisted plastic injection molding process is the same as that described above, especially with reference to Figures 13 and 14. The inventive process forms a hollow section 350 in the rib member 335.

Another schematic illustration of the inventive process and in particularly wherein the rotating insert members described above with respect to Figures 13-14 and 15 could be utilized, is shown in Figures 16A-16F. The process is designated generally by the reference numeral 400. Figure 16A shows the first step in the process in which the mold cavity 402 is filled with plastic material 404. The plastic material is supplied to the mold cavity by a conventional melt delivery system, such as a sprue, hot runner, cold runner, etc., all generally designated by reference numeral 406. A rotating insert member 410 is positioned below one section of the mold cavity and article. In Figure 16B, the mold cavity is packed with additional plastic material forcing the plastic material 404 into every area and against every surface of the mold cavity 404.

Figure 16C shows the position of the insert member 410 after it is rotated opening up open groove 412 to the mold cavity 404. This rotation preferably takes place prior to gate freeze or seal and creates a low pressure area under the part for plastic material 404A to flow into. The plastic material will flow partially into the groove 412 under conventional pressures and form a part of the rib member 404B.

This is shown in Figure 16D.

Pressurized gas 415 is then injected into the plastic material 404A and 404B in the groove 412. The gas is injected through inlet 418. Since the rib member has the greatest thickness of plastic material in the mold cavity, and thus contains the hottest and most fluent molten plastic material, the gas will move into that area.

This is shown in Figure 16E. The gas pressure will push out or displace the plastic material into the remaining open area in the groove, as shown in Figure 16F. This fonms the completed rib members with a hollow section 415 along its length. The rib member has a substantially uniform wall thickness throughout its length.

Although the present invention has been described above with reference to Connation of hollow rib structures and trim components of panels, it is to be understood that the present invention can be used in any gas- assisted injection molding process or system.

While the invention has been described in connection with one or more embodiments, it is to be understood that the specific mechanisms, processes and procedures which have been described are merely illustrative of the principles of the invention, numerous modifications may be made to the methods and apparatus described without departing from the scope of the invention as defined by the appended claims.

Claims (16)

1. A method for making an injection molded plastic article with at least one hollow portion, said method comprising the steps of: injecting a quantity of a plastic material into a mold cavity, the quantity of plastic material sufficient to completely fill the mold cavity; packing said plastic material in said mold cavity; injecting a fluid material into said packed plastic material in said mold cavity; increasing the volume of said mold cavity by rotating an insert member with a groove therein; displacing by said fluid material at least a portion of said plastic material into said groove and thereby creating a hollow portion in said plastic material forming said article; allowing the completed plastic article to cool and solidify in the mold cavity; exhausting said fluid material from the hollow portion of the plastic article; and removing the plastic material from the mold cavity.

2. The method as described in claim 1 wherein said fluid material is a gas.

3. The method as described in claim 1 or 2 wherein said plastic article has at least one rib member and said hollow portion is in said rib member.

4. The method as described in any preceding claims wherein said quantity of plastic material is injected at a first pressure and said plastic material is packed in said mold cavity at a second pressure greater than said first pressure.

5. The method as described in claim 4 wherein said fluid material is injected into said packed plastic material at a third pressure.

6. The method as described in claim 5 wherein said third pressure is greater than said second pressure.

7. A method for making an injection molded plastic article having a hollow rib member, said method comprising the steps of: injecting a full shot of plastic material into a mold cavity at a first pressure, said mold cavity having a first portion forming said rib member on the completed plastic article and said mold cavity having a rotatable insert member in said first portion, said rotating member having a recess therein; packing said plastic material in said mold cavity at a second pressure greater than said first pressure; rotating said insert member in order to position said recess in communication with said mold cavity; injecting a gas into the plastic material in said first portion and displacing a portion of plastic material into said recess; and allowing said plastic material to solidify.

8. The method as described in claim 7 further comprising exhausting said gas from said plastic material and removing said completed plastic article from said mold cavity.

9. An injection molding system comprising a mold defining a mold cavity, a plastic injector for injecting plastic material into the mold cavity, a fluid injector for injecting fluid material in the mold cavity and any plastic material

-

therein, and a rotatable insert member having a recess defined therein arranged such that when the insert member is rotate the recess opens up into the mold cavity.

10. A system as claimed in claim 9 in which the insert member is fixed in position by use of a releasable locking mechanism.

11. A system as claimed in claim 9 or 10 in which the insert member comprises an elongate cylinder which is positioned in one surface of the mold cavity.

12. A system as claimed in any one of claims 9 to 1 1 in which the insert member is rotated by a motor.

13. A system as claimed in any one of claims 9 to 12 in which recess in the insert member comprises an elongate groove.

14. A system as claimed in claim 13 in which the elongate groove is used to form a rib of a molded article.

15. A method for making injection molded plastic articles substantially as hereinbefore described with reference to and/or as shown in accompanying figures 3 to 16F.

16. A system for making injection molded plastic articles substantially as hereinbefore described with reference to and/or as shown in accompanying figures 3 to 1 6F.