GB2401103A - Synthetic magnesium silicate compositions, methods and uses - Google Patents
Synthetic magnesium silicate compositions, methods and uses Download PDFInfo
- Publication number
- GB2401103A GB2401103A GB0309620A GB0309620A GB2401103A GB 2401103 A GB2401103 A GB 2401103A GB 0309620 A GB0309620 A GB 0309620A GB 0309620 A GB0309620 A GB 0309620A GB 2401103 A GB2401103 A GB 2401103A
- Authority
- GB
- United Kingdom
- Prior art keywords
- composition
- magnesium silicate
- synthetic magnesium
- formula
- hydrated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The use of a non-hydrated synthetic magnesium silicate composition of the formula: [Si8(MgaLibHc)O20(OH)4-yFy]<z->. z/nM<n+> where a is 4.95 to 6.6, b is 0 to 1.5, c is 0 to <2, a+b+c is 5 to <8, Y IS 0 TO <4,Z =12-2A-B-C, M is a cation other than Li; to form a gelled aqueous composition. a gycol degelling agent may be added to the aqueous composition. The lithium-free forms of the silicate may have longer gelling times. The counter ion M may be Na (sodium).
Description
2401 1 03 Synthetic magnesium silicate compositions, methods and uses
thereof This invention is concerned with synthetic magnesium silicate compositions, methods and uses thereof. In particular, the present invention concerns the use of synthetic magnesium silicate compositions that contain reduced amounts of lithium or are lithium-free, lithium-free synthetic magnesium silicate compositions, methods of extending the gel time of aqueous compositions comprising synthetic magnesium silicate compositions and processes for the preparation of synthetic magnesium silicate compositions.
With the name "hectorite" has been ascribed to a natural trioctahedral smectite found at Hector, California, USA. This clay is an hydrous magnesium silicate having the ideal composition Sit Mg6 O20 (OH)4 modified by having a portion of the Mg+2 and OH- ions replaced by Li+ and F- ions.
The synthesis of hydrous magnesium silicates similar to natural hectorite has been described by Granquist and Pollack in "Clays and Clay minerals" Vol. 8 (Proceedings,.
of the 8 National Conference on Clays and Clay Minerals) pages 150-169. In the process described by Granquist, gels of magnesium hydroxide and of silica are produced separately, are washed, are combined and are redispersed in water to form a suspension. Lithium hydroxide or lithium fluoride and sodium hydroxide are added to.
the suspension that is then treated hydrothermally by refluxing it with stirring until a.
product having a crystal structure similar to that of hectorite is formed.
While Granquist's product has the crystal structure similar to natural hectorite it does not have good theological properties. Measuring the gingham Yield Value of an aqueous dispersion of the substance provides a standard yardstick of theological properties of a substance. The term gingham Yield Value (also known as gingham Yield Stress, these terms being alternatives for the same property) is referred to in standard works on rheology for example in "Rheology Theory and Applications" F R Eirich (Aced. Press) Vol. 1 (1956) page 658 and "Colloidal Dispersions" L K Fisher (N.Y. Bureau of Standards) 2nd Edition 1953, pages 150-170 and "The Chemistry and Physics of Clays and other Ceramic Materials" 3rd Edition, page463, A B Searle and R W Grimshaw.
The gingham Yield Value may be determined by first obtaining a flow curve relating the shear stress to the rate of shear and then extrapolating the straight line section of the curve to the shear stress axis, the intercept being the gingham Yield Value. It can conveniently be determined on any viscometer capable of measuring a range of shear rates and shear stresses.
The product of Granquist, when in the form of a dispersion obtained using 2g silicate and lOOml tap water, gives a gingham Yield Value of only about t5 dynes per cm2.
This is a very low value, inferior to that given by natural hectorite. It also gives a low static gel strength.
Processes for the production of synthetic hydrous magnesium silicate compositions having a crystal structure similar to natural hectorite but having better theological properties than natural hectorite have been described in GB-A-1054111, GB-A tol213122 and GB-A-1432770. À A Àe::: The process described in the GB-A-1054111 involves forming a slurry by co precipitation by slowly combining with heating and agitation in an aqueous medium a constituent providing the magnesium ions with constituents providing the silicon (as À. ..
silicates), hydroxyl and sodium ions and treating the precipitate hydrothermally to. . crystalline the synthetic mineral-like clay, washing and dewatering the resulting. . crystallized product, and drying the product at a temperature up to 450 C. The concentration of the slurry is desirably such that the concentration of the product formed is from 1% to 8% by weight, preferably 4% by weight. The hydrous synthetic magnesium silicate contains fluorine and lithium. The clay-like minerals provided have the structural formula: I (Sit Mg6 x Lix.020.(0H)4 y Fy)X() x/nMn( ) in which x is between O and 6, y is from 1 up to but excluding 4, and M is a cation, preferably Na+.
The process described in GB-A-1213122 involves precipitating a synthetic magnesium silicate by combining an aqueous solution of a water soluble magnesium salt with an aqueous alkaline solution of one or more sodium compounds *n the presence of dissolved silicon compound and hydrothermally treating the precipitate under pressure to crystallise the synthetic mineral-like clay, separating the resultant solid and liquid phases, washing the resulting crystallised product, and drying the product. The concentration of the precipitate is preferably not more than 5% by weight. The hydrous magnesium silicate product contains no fluorine, optionally contains lithium and has the general formula: [Si8MgaLibH4+co24]( 22abC) M( 2-2a-b-c)+ where (i) M is a sodium, a lithium or an equivalent of an organic cation, and (ii) the value of a, b, and c is such that either a<6, b>O, c>O, b+c<2, and (a+b+c-6)<2; or a<6, b=O, c,2 and (a+c-6)<2.
The process described in GB-A- 1432770 involves the synthesis of an hydrous magnesium silicate having a crystal structure similar to that of hectorite and having the general formula: [Sis (MgaLibHc)O2o(OH)4yFy]7r.zM+ wherein a is 4.95 to 5.7, b is from 0 to 1.05, c is from 0 to <2, a+b+c is from >4 to <8, y À ....
is from O to <4, z = 12-2a-b-c, and M is Na+ or Li+. The process comprises the..
sequential steps of forming an aqueous suspension of magnesium carbonate, forming a À.- silica precipitate in the aqueous suspension magnesium carbonate, the proportions of À ., . magnesium provided by the magnesium carbonate and silica precipitated in the À ..
suspension corresponding to that of the formula of the magnesium silicate, maintaining. . the resulting mixture of magnesium carbonate and silica in the wet state and subjecting. À . it to hydrothermal treatment by heating it in an aqueous medium and in the presence of the remaining constituents of the magnesium silicate in proportions within the ranges specified in the general formula and in the presence of excess dissolved sodium or lithium compound over that required to form the cation ofthe magnesium silicate until crystal growth occurs and separating the resulting crystalline product. The crystalline material resulting from the hydrothermal treatment is then separated by filtration, washed, and dried at a temperature not exceeding 450 C. The process described in GB A1432770 is distinguished from the processes described in GB-A-1054111 and GB-A 1213122 in that, in those processes, the Mg compound and the silica are co-precipitated.
Though GB-A-1432770 discloses a general formulation for a synthetic magnesium silicate composition in which there is a possibility for the composition to be lithium free, there is no explicit disclosure in GB-A1432770, or in any other prior art, which indicates a lithium-free composition ever having been prepared.
The processes described in GB-A-1432770, GB-A-1054111 and GB-A-1213122 are generally batch processes. Continuous processes for the preparation of synthetic magnesium silicates are described in Japanese Patent Application No 06-345419 and in UK Patent Application No 0229630.9, filed 20'h December 2002.
The products of the processes described in the above prior art documents are characterized by providing dispersions having gingham Yield Values substantially in excess of any known to be given by natural hectorite dispersions. Some of these products have found widespread use, by virtue of their excellent theological properties, in many applications, including in paints and other surface coatings; cosmetic products; horticulture; shampoos; detergents; disinfectants; toothpastes; paper manufacture, for example as fillers, retention and drainage aids, and in paper coatings; and drilling muds. . ....
The products of the above batch processes are commercially available as dry white. À powders, such as the products sold by Rockwood Additives Limited, England, under the trademark "LAPONITE" and, when fully dispersed and hydrated in water, the resulting composition is colourless and transparent. À ..
As mentioned above, synthetic magnesium silicate compositions are characterized by.. . providing dispersions having gingham Yield Values substantially in excess of any known natural hectorite dispersions, and have resulted in their use, by virtue of their excellent theological properties, in various applications including in surface coatings.
The free flowing white powder takes no more than an hour at ambient temperatures from it being dispersed under shear in water at a level from 1% by wt to hydrate sufficiently to form a highly viscous, thixotropic gel. The time required to form the gel can be reduced by using increased temperatures and by using higher shearing conditions.
It is known, for example from an inspection of the www.laponite.com website, that at concentrations of above 2% by wt synthetic magnesium silicate in tap water, highly thixotropic gels are formed(substantially less than one hour e.g a 5% by wt aqueous composition may gel in 5 minutes), which can make it difficult to incorporate other raw materials into the formulation. Accordingly, if the concentration of synthetic magnesium silicate to be used is above 2% by wt. the use of a degelling agent, such as tetrasodium pyrophosphate or a low molecular weight polyethylene glycol, is often recommended.
Whilst the onset of gelling can be delayed by the presence of a degelling agent, some applications of the end formulation, such as coatings for some metals, do not permit the presence of condensed phosphates. Further, it may be more convenient in a manufacturing process not to have to rely upon the presence of a degelling agent.
It is an object of the present invention to delay the onset of gelling in aqueous formulations comprising synthetic magnesium silicate compositions. It is another object to provide synthetic magnesium silicate compositions which demonstrate delayed gelling properties. It is another object of the present invention to reduce or eliminate the amount of degelling agent e.g. phosphate used in an aqueous synthetic magnesium. ..
silicate compositions. Preferably, the delay in gelling will occur without having any..
detrimental effects on the final properties of the gelled composition. À: :e
In accordance with a first aspect of the present invention, there is provided the use of a À non-hydrated synthetic magnesium silicate compostion of Formula I below: .. *, I.- À ..', Formula l [Sia (MgaLibHc)020(0H)4 yFy]Z- %Mn+ whereinais4.95to6.6,bis from Oto 1.5, cishromOto<2,a+b+cistromSto<8,yis from O to <4, z = 12-2a-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 in a method for the preparation of an aqueous composition comprising said synthetic magnesium silicate composition in a hydrated form, which method comprises adding under mLxing conditions said non-hydrated synthetic magnesium silicate composition to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate.
In another aspect, the present invention provides the use of a nonhydrated synthetic magnesium silicate composition of Formula I below: Formula I [Sis (MgaLibH')020(0H)4yFy]Z.7/nM wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from 5 to <8, y is from O to <4, z = 12-2a-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95in a method for the preparation of a gelled aqueous composition comprising said synthetic magnesium silicate composition in a hydrated form, which method comprises adding under mixing conditions said non l O hydrated synthetic magnesium silicate composition to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate, for delaying gelling of said gelled aqueous composition.
In another aspect, the present invention provides a method of reducing or eliminating the amount of degelling agent used in the preparation of an aqueous composition comprising a synthetic magnesium silicate composition in hydrated form, which method if comprises adding under mixing conditions a non-hydrated synthetic magnesium silicate..
composition of Formula 1: Formula I..
[Sit (MgaLibHC)o2o(oH)4-yFy]Z-.Z/nMn À.
wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from 5 to <8, y is, . from O to <4, z = 12-2a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate.
In another aspect, there is provided an aqueous composition comprising an aqueous fluid and a synthetic magnesium silicate composition of Formula l: Formula I [Sit (MgaLibHc)020(0H)4yFy]Z.z/nMn wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from 5 to <8, y is from O to <4, z = 1 2-2a-b-c, M is a cation which is other than Li and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 Preferably, the synthetic magnesium silicate composition used in the preset invention is completely free of Li. Such a composition preferably has the composition of Formula II below: Formula II [Six (MgHc)02o(0H)4 yFy]7.7/nMn+ whereinais4.95to6.6,cisfromOto<2,a+ eisbrom5to<8,yisbromOto<4,z= 12 2a-c, M is a cation which is other than Li, and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 In accordance with another aspect ofthe present invention there is provided a synthetic magnesium silicate composition of Formula II below: Formula 11 [Six (MgaHc)o2o(oH)4yFyz-%Mn+ wherein a is 4.95 to 6.6, c is from O to <2, a+c is from 5 to <8, y is from O to <4, z= 12 2a-c, M is a cation which is other than Li, and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 In the synthetic magnesium silicate compositions of Formula I and Formula 2: a) the Si:Mg ratio is prefereably from 8:5.8 to 8:5.3, more preferably from 8:5.68 to 8:5.42; b) the M+ cation is preferably Ma+, c) y is preferably from O to 3.
It has been found that by reducing or eliminating the amount of Li in the synthetic magnesium silicate composition and employing a specific Si:Mg ratio, the time within which the composition gels once it has been added to water or other aqueous fluid is extended. For example, it can be demonstrated that an aqueous composition formed by the addition to water under conventional mixing conditions at room temperature of a synthetic magnesium silicate composition of Formula II in an amount of 5 wt % may take well over an hour before it forms a highly viscous, gelled composition. Further, once the composition has gelled, its theological properties are substantially similar to the aqueous gels formed from hydrating conventional highcontent lithium magnesium silicate compositions. This finding is very surprising and, at present, cannot be explained by the inventors.
The ability to delay gelling without loss of final gel properties offers significant advantages over the conventional compositions. For example, it enables the preparation of aqueous compositions comprising higher amounts of synthetic magnesium silicate compositions than would normally be possible with conventional lithium containing magnesium silicates. Further, aqueous compositions can be prepared which contain reduced or no degelling agents e.g. phosphate free coatings may now be available for use in the metal finishing industry.
The compositions of Formula I may be prepared by the processes detailed in GB-A 1054111, GB-A-tol213122, GB-A-1432770, Japanese Patent Application No 06 345419 and UK Patent Application No 0229630.9, which are incorporated herein by reference. 1 The compositions of Formula II may be prepared by a similar procedure as detailed in GB-A-1054111, GB-A-tol213122, GB-A1432770, Japanese Patent Application No 06-345419 and UK Patent Application No 0229630.9, except that all Li- containing.
compounds are absent. Accordingly, in another aspect, the present invention provides a..
method of preparing a synthetic magnesium silicate composition of Formula II, having a À À crystal structure similar to natural hectorite, wherein the process comprises the steps of...
a) forming a precursor slurry by mixing and reacting together water, magnesium À sulphate, sodium carbonate and sodium silicate, b) subjecting said precursor slurry to a hydrothermal reaction at a temperature offrom 210 to 400 C, and c) washing and À À À À filtering to remove water soluble salts formed in the preparation of the precursor slurry. À . . .: 25; The composition of Formula II retains substantially similar theological properties to the products formed in GB-A-1054111, GB-A- 1213122 and GB-A-1432770. The compositions may be supplied as dry white powders or as moist solids or in dispersions.
Accordingly, the compositions may be used in the same type of applications as the prior art products. For example, the compositions may be used in paints; cosmetic products; horticulture; shampoos; detergents; disinfectants, toothpastes; paper manufacture, for example as fillers, retention and drainage aids, and in paper coatings; and drilling muds.
The Li-free compositions of Formula II, may additionally be useful in applications in which the product is intended to be consumed, such as in food and medicinal applications.
In yet another aspect, the present invention provides a method of extending the gelling time of an aqueous composition comprising a synthetic magnesium silicate composition in hydrated form and a degelling agent, such as a glycol or a phosphate, which method comprises adding under mixing conditions a non-hydrated synthetic magnesium silicate having a structure similar to natural hectorite, preferably as made by any of the processes claimed in GB-A-1432770, GB-A-1054111, GB-A-1213122, Japanese Patent Application No 06-345419 and in UK Patent Application No 0229630.9 (filed 20th December 2002), to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate, characterized in that the aqueous fluid into which said non-hydrated composition is added comprises at least 80% by weight, preferably 100 % by weight, of the degelling agent used in the aqueous composition. In one particular embodiment, the degelling agent is a glycol, which is preferably selected from one or more of ethylene glycol, propylene glycol, polyethylene glycol and polypropylene glycol. Preferably, the nonhydrated synthetic magnesium silicate.
composition is of Formula I: . Formula I [Sit (MgaLibH:)020(0H)4 yFy]Z-.Z/nM À . wherein a is 4.95 to 6.6, b is from O to l.5, c is from O to <2, a+b+c is from S to <8, y is: . À.
from O to <4, z = 12-2a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to X:4.95. More preferably, the synthetic À À À magnesium silicate composition is of Formula II below: À . . .: Formula II [Sig (MgaHc)o2o(oH)4-yFy]z- %Mn+ whereinais4.95to6.6,cisbromOto<2,a+ cisfromSto<8,yistromOto<4,z= 12 2a-c, M is a cation which is other than Li, and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95.
The following examples illustrate aspects of the invention, but are not in any way intended to limit the scope the invention.
Various synthetic magnesium silicate compositions were prepared by the procedure detailed in Examples 1 and 2 below from the amounts of raw materials, as indicated in
Table 1:
Example 1 - Preparation of precursor slurry (bulk preparation) A measured quantity of magnesium sulphate and water (sufficient to dissolve the measured quantity of magnesium carbonate) is placed in a flask fitted with a stirrer, a heating mantle and a refluxing condenser. The mixture was brought to a temperature of at least 60 C under reflux while stirring efficiently.
From a separate vessel a measured quantity of sodium carbonate solution is added slowly to the reaction vessel containing the magnesium sulphate solution. The addition is made over a period of up to one hour, while the reaction mixture is kept at 60 C or greater and stirred efficiently throughout.
From a separate vessel a measured quantity of sodium silicate solution is added slowly to the reaction vessel containing the magnesium sulphate and sodium carbonate.
solution. The addition is made over a period of up to one hour, while the reaction.
mixture is kept at 60 C or greater and stirred efficiently throughout. À..
The mixture is then boiled under reflux, with efficient stirring, for about 2 hours. À Example 2 - Hydrothermal treatment (bulk preparation) The precursor slurry obtained in each of Example 1 was fed into a reactor having an internal temperature of 200 C and pressure of 16 barg. The slurry now undergoes a hydrothermal reaction. The material is retained in the reactor for up to 18 hours, before it is ejected from the reactor into a bath where magnesium silicate crystal so formed are wash and filtered to remove soluble salts.
After being drying at 1 05 C and milled to particle size of no greater than 250 microns, the rheology properties of the powders so produced were evaluated. The results of the evaluation are also presented in Table 1.
From Table 1, it is evident that compositions comprising reduced or no lithium develop gelling properties more slowly than the conventional composition Laponite RD.
Laponite RD is a synthetic magnesium silicate of the typical formula [Sis(Mgs sLio 3Ho 2)020(0H)4] 5 o sNa+, available from Rockwood Additives Limited, England.
Viscosity was measured at 25 C using a number 4 Ford viscosity cup. The unit of measurement for this method is 'seconds'. À À À À. À À . À À. À:. :. À... À.. À À À .
- -
3 _ u, _ _ a _ a _ iS
_ _ _ _ _ _ _ _ _ _ _ _ L _ _
O _ O _ O _ O _ O _ O _ O _ N O
a. , ' : :.
_ _ _ -- _ _ _ _:: _ X. _ 0,0 _ _ _ vm0 _ iO,, _ o.0 O,, _ _ _ __s -i-( :...
_ C_ _ _ _c _ = _ C S = cn V q eq & w 5' _ _ n n- v- g l? 1: MEL e r. _ A _ _ _ _ D V _ W. 5= v _ -- _ 2 Q 2 _ _ of...
o X it, _ e 3 _ _ _ Y À.-..
e c _ ___ n! BE: BE an 1' S r LL L Ll
Claims (16)
- - Is - Claims 1. The use of a non-hydrated synthetic magnesium silicatecomposition of Formula I below: Formula I [Six (MgaLibHc)o2o(oH)4-yFyz-%Mn+ wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, ab+c is from 5 to <8, y is from O to <4, z = 12-2a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 in a method for the preparation of an aqueous composition comprising said synthetic magnesium silicate composition in a hydrated form, which method comprises adding under mixing conditions said non-hydrated synthetic magnesium silicate composition to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate.
- 2. The use of a non-hydrated synthetic magnesium silicate composition of Formula.I below: . Formula I [Sit (MgaLibHc)020(0H)4yFy]Z Z/nMn À À wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from 5 to <8, y is.. . from O to <4, z = 12-2a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 À À in a method for the preparation of a gelled aqueous composition comprising said À À À synthetic magnesium silicate composition in a hydrated form, which method comprises adding under mixing conditions said non-hydrated synthetic magnesium silicate composition to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate, for delaying gelling of said gelled aqueous composition.
- 3. A method of reducing or eliminating the amount of degelling agent used in the preparation of an aqueous composition comprising a synthetic magnesium silicate composition in hydrated form, which method comprises adding under mixing conditions a non-hydrated synthetic magnesium silicate composition of Formula I: Formula I [Sib (MgaLibHc)o2o(oH)4-yFy]z-.%Mn+ whereinais4.95to6.6,bistromOto 1.5, cisfromOto<2,a+b+cistrom5to<8,yis Dom O to <4, z = 12-2a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95 to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate.
- 4. An aqueous composition comprising an aqueous fluid and a synthetic magnesium silicate composition of Formula 1: Formula I [Sit (MgaLibHc)020(0H)4 yFy] .%M wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from S to <8, y is from O to <4, z = 122a-b-c, M is a cation which is other than Li, and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95
- 5. The use of claim 1 or claim 2, method of claim 3 or composition of claim 4, wherein the synthetic magnesium silicate composition is free of Li. ....
- 6. The use of claim 1 or claim 2, method of claim 3 or composition of claim 4, À À wherein the non-hydrated synthetic magnesium silicate composition is of Formula II.. . below: ....Formula II À [Six (MgaHc)o2o(oH)4yFy] . /nM À. À: wherein a is 4.95 to 6.6, c is from O to <2, a+c is from 5 to <8, y is from O to <4, z = 12 2a-c, M is a cation which is other than Li, and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95.
- 7. The use, method, or composition as claimed in any one of the preceding claims, wherein the aqueous composition comprises a degelling agent. I
- 8. The use, method or composition of claim 7, wherein the degelling agent is a glycol, preferably ethylene glycol, propylene glycol or a low molecular weight polyglycol.
- 9. A synthetic magnesium silicate composition of Formula II below: Formula II [Sis (MgaNc)020(0H)4 yFy]Z-.zlnMn+ wherein a is 4.95 to 6.6, c is from O to <2, a+c is from S to <8, y is from O to <4, z = 12 2a-c, M is a cation which is other than Lit and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95
- 10. A method of extending the gelling time of an aqueous composition comprising a synthetic magnesium silicate composition in hydrated form and degelling agent, preferably a glycol, which method comprises adding under mixing conditions a non hydrated synthetic magnesium silicate having a structure similar to natural hectorite, preferably as made by any ofthe processes claimed in GB-A-1432770, GB-A-1054111, GB-A-1213122, Japanese Patent Application No 06-345419 and in UK Patent Application No 0229630.9 (filed 20'h December 2002), to an aqueous fluid and allowing said non-hydrated synthetic magnesium silicate composition to hydrate, characterized in that the aqueous fluid into which said non-hydrated composition is added comprises at. . least 80% by weight, preferably 100 % by weight, of the degelling agent used in the.aqueous composition.
- 11. The method of claim 1 O. wherein the degelling agent is a glycol, preferably a., À glycol selected from one or more of ethylene glycol, propylene glycol, polyethylene....glycol and polypropylene glycol. . . eel-
- 12. The method of claim 11 or claim 12, wherein the non-hydrated synthetic magnesium silicate composition is of Formula I: Formula I [sib (MgaLibHC)o2o(oH)4-yFy]Z- zlnMn wherein a is 4.95 to 6.6, b is from O to 1.5, c is from O to <2, a+b+c is from 5 to <8, y is from O to <4, z = 12-2a-b-c, M is a cation which is other than Lit and n is the valency of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95.
- 13. The method of claim 12, wherein the synthetic magnesium silicate composition is of Formula II below: Formula II LSis (Mg8)O20(0H)4 yFy]z%M wherein a is 4.95 to 6.6, c is from 0 to <2, a+c is from 5 to <8, y is from 0 to <4, z = 12 2a-c, M is a cation which is other than Li, and n is the valancy of M, wherein the ratio of Si:Mg is from 8:6.6 to 8:4.95.
- 14. The use, method, or composition as claimed in any one ofthe preceding claims, wherein the Si:Mg ratio in the synthetic magnesium silicate composition is from 8:5.8 to 8:5.3, preferably from 8:5.68 to 8:5.42.
- 15. The use, method, or composition as claimed in any one of the preceding claims, wherein the Mt cation in the synthetic magnesium silicate composition is Ma+
- 16. The use, method, or composition as claimed in any one of the preceding claims, wherein y in the synthetic magnesium silicate composition is from 0 to 3. À. Àe a me a :'e. . . Àe À- Àe e.