GB2370278A - Well treatments using derivatized polymers - Google Patents
Well treatments using derivatized polymers Download PDFInfo
- Publication number
- GB2370278A GB2370278A GB0207779A GB0207779A GB2370278A GB 2370278 A GB2370278 A GB 2370278A GB 0207779 A GB0207779 A GB 0207779A GB 0207779 A GB0207779 A GB 0207779A GB 2370278 A GB2370278 A GB 2370278A
- Authority
- GB
- United Kingdom
- Prior art keywords
- polymer material
- polymer
- derivatized
- slurry
- guar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for treating a well comprises:<BR> ```combining a polymer material with an organic solvent to form a polymer-containing slurry;<BR> ```combining said polymer-containing slurry with a derivatizing agent, wherein said polymer material and said derivatizing agent react to form a derivatized polymer-containing slurry;<BR> ```combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form a hydrated derivatized polymer-containing treatment fluid; and<BR> ```introducing said treatment fluid into said well. The polymer may comprise guar combined with a derivatizing agent in a slurry.
Description
DERIVATTZATION OF POLYMERS AND WELL TREATMENTS USING SAME BACKGROUND OF THE INVENTION 1. Field of the Invention
This invention relates generally to derivatization of polymer materials and, more specifically, to the use of derivatized polymers in well treatments. In particular, this invention relates to the derivatization of polymers, such as polysaccharides, in liquid slurries that are subsequently introduced into a well as part of a well treatment, such as a hydraulic fracturing treatment.
2. Description of Related Art
Hydraulic fracturing of oil and gas wells is a technique routinely used to improve or stimulate the recovery of hydrocarbons, and is typically employed to stimulate wells which produce from low permeability subterranean formations. In such wells, recovery efficiency is typically limited by the flow mechanisms associated with a low permeability formation.
Hydraulic fracturing is usually accomplished by injecting a fluid, typically proppant-laden, into a producing interval at a pressure above the fracturing pressure of the subterranean formation.
This fluid induces a fracture in the reservoir and transports proppant into the fracture before leaking off into the surrounding formation. After the treatment, proppant remains in the fracture in the form of a permeable pack that serves to prop the fracture open. In this way the proppant path forms a conductive pathway for hydrocarbons to flow into the wellbore. Typically, viscous gels are employed as fracturing fluids in order to provide a medium that will adequately suspend and transport solid proppant materials, as well as to impair loss of fracture fluid to the formation during the treatment. Fracture width and geometry are determined, in part, by the viscosity of a fracturing fluid. Viscosity of most water-based fracturing fluids is typically obtained from watersoluble polymers such as guar gums, guar derivatives, and cellulose derivatives.
Further enhancement of fracturing fluid viscosity may be obtained by treating polymeric solutions with cross-linking agents, typically selected from titanium, aluminum, boron and zirconium based compounds, or mixtures thereof Most typically, boron and zirconium based
additives are employed. Boron cross-linkers are typically used with galactomannan polysaccharides such as guar gum and its derivatives, including hydroxypropyl guar ("HPG"), carboxymethyl guar ("CMG") and carboxymethylhydroxypropyl guar ("CMHPG"). Most typically, boron crosslinkers are employed with guar because it offers suitable performance at lower cost. Although gelation may be obtained by mixing zirconium-based additives with guar, the resulting gels are typically shear-sensitive and unstable. However, zirconium-based additives may be mixed with carboxymethylated guar derivatives such as CMG or CMHPG to form stable gels. Other suitable guar derivatives include alkylated carboxylated polymers such as methyl and ethyl carboxymethyl guar.
For a typical hydraulic fracturing operation derivatized polysaccharides, such as carboxymethylated guars, are usually commercially purchased from specialty polymer companies, such as Aqualon and Rhone-Poulenc. Polymers such as carboxymethylated guars
are typically formed by derivatizing the guar seed endosperm, often referred to as a"split'', which is generally semi-spherical in shape (about 1/8" (3. 2 mm) long and 1/16" (1. 6mm) in diameter) and from about 0. 5 mm3 to about 1 rom3 in volume. The relatively large size of guar splits make them favored as a polymer feedstock because they form a derivatized polymer product that is more easily isolated and purified without the need of washing with organic solvents. Derivatized products formed from fine polymer powders often require organic solvents to disperse the powders without caking. These organic solvents are typically expensive and environmentally unsound.
Guar splits are typically treated with aqueous caustic to cause swelling, and then exposed to a derivatizing agent, such as sodium chloroacetate ("SCA") in an amount necessary to provide a desired molar substitution ("M. S. ") value, which is the ratio of moles of derivative to total moles of sugar. Typical guar split derivatization yields using SCA are about 60%, with about 40% of the SCA being consumed to form undesirable byproducts such as glycolic acid.
Following derivatization, the splits are typically cooled and washed to remove excess caustic and unwanted byproducts before being dried and ground to a powder.
Among the disadvantages associated with the use of commercially purchased derivatized polysaccharides is lack of control over the M. S. value. The M. S. value affects a polymer's hydration rate, solution viscosity and salt tolerance. Properties of zirconium and
titanium crosslinked polymer gels are also affected by the polymer M. S., including gelation rate, gel strength as a function of temperature, proppant suspension, fluid loss control and controlled gel degradation. The optimum value of each such property is often achieved at different M. S. values. Therefore, the optimum M. S. value for a given fluid system typically reflects a compromise of the optimum M. S. values for each property. In the same way, the optimum M. S. value may also differ among fracturing fluids. The desired nature of the properties associated with the M. S. value varies from well treatment to well treatment based upon, among other things, individual well and formation characteristics. Therefore several commercially purchased polymers of the same class, but having different M. S. values, typically must be kept in inventory.
Another disadvantage of commercially available derivatized polysaccharides is their relatively high cost. This cost reflects the amount of post-derivatization processing required to produce derivatized polysaccharide powders Post-derivatization processing typically includes isolation, washing (such as with organic solvents), and packaging of the derivatized polysaccharide product. Furthermore, derivatization of commercial polysaccharides is typically less uniform than desirable. Although not wishing to be bound by theory, it is believed that derivatization of relatively large polysaccharide materials such as guar splits yields a particle having a large percentage of derivatized molecules concentrated near the outer surface of the particle, and a substantial percentage of underivatized molecules located in the interior of the particle. This is undesirable because a portion of the polymers having lower than desired M. S. values may exhibit poor response to crosslinking while those have excess derivatization may be overly responsive. It is believed that this situation may result in non-uniform gelation.
Recently, continuous mixing processes have been employed in the performance of hydraulic fracturing treatments. In a continuous mixing process, the polymer is carefully metered into a flowing aqueous stream enroute to the wellbore. Because precise metering is best accomplished by handling the polymer as a liquid rather than as a solid, polymer slurries are typically prepared by dispersing the polymer in an organic solvent base which contains suspending agents. Examples of typical organic solvents include hydrocarbon solvents, such as kerosene, diesel, etc. Suspending agents are typically organophilic clays and surfactants such as naphthalene sulfonate resins. Nonionic surfactants such as ethoxylated fatty alcohols are
typically added to improve wetting and hydration. During a typical well treatment employing continuous mixing, a liquid polymer slurry is measured into a flowing stream of aqueous treatment fluid, typically in a manner that allows the polymer from about one to about four minutes to hydrate before the aqueous stream enters a blender. In the blender the polymer-laden aqueous well treatment fluid may be mixed with other additives, such as cross-linking agents and other additives such as surfactants, gel stabilizers, clay control additives and proppants, before being injected into a wellbore.
SUMMARY OF THE INVENTION
According to the invention there is provided a method for forming derivatized polymer material in a slurry, comprising combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material contained m said slurry; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent ; wherein said polymer material comprises a hydratable polysaccharide, hydratable derivatized polysaccharide, or a mixture thereof ; and wherein said organic solvent based slurry comprises a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
Another aspect of the invention provides a method for treating a well, comprising: combining a polymer material with an organic solvent to form a polymer-containing slurry; combining said polymer-containing slurry with a derivatizing agent, wherein said polymer material and said derivatizing agent react to form a derivatized polymer-containing slurry ;
combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form a hydrated derivatized polymer-containing treatment fluid; and introducing said treatment fluid into said well.
A further aspect of the invention provides a method for treating a well, comprising: combining a guar material with a hydrocarbon solvent to form a slurry containing guar material; then combining said slurry containing guar material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing guar material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said guar material and said derivatizing agent; allowing said guar material and said derivatizing agent to react to form derivatized guar material contained in said slurry; then combining said slurry containing derivatized guar material with an aqueous solution to form a treatment fluid, wherein said derivatized guar material interacts with said aqueous solution to form hydrated derivatized guar contained in said treatment fluid; and then introducing said treatment fluid into said well; wherein said slurry containing guar material is combined with said basic compound or alkaline material prior to combination of said slurry containing guar material with said derivatizing agent.
A further aspect of the invention provides a method for forming derivatized polymer material in a slurry, comprising : combining an organic solvent based slurry containing polymer material with a derivatizing agent offsite, wherein said polymer material and said derivatizing agent react to form derivatized polymer material contained in said slurry offsite ; and storing said slurry containing derivatized polymer material for transportation and later onsite use.
A further aspect of the invention provides a method for forming derivatized polymer material, comprising: combining a polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material;
then combining said polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent ; and allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material; wherein said polymer material is combined with said basic compound or alkaline material prior to combination of said polymer material with said derivatizing agent; and wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, or a mixture thereof
A further aspect of the invention provides a method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material contained in said slurry ; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said organic solvent based slurry comprises a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
A further aspect of the invention provides a method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and
allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material contained in said slurry ; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said derivatizing agent comprises at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof ; and wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, or a mixture thereof
A further aspect of the invention provides a method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to react to form derivatized polymer material contained in said slurry; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said organic solvent based slurry containing polymer material further comprises a viscosifier and dispersant.
A further aspect of the invention provides a method for forming a hydrated derivatized polymer-containing fluid, comprising: combining a polymer material with an organic solvent to form a polymer-containing slurry ; combining said polymer-containing slurry with a derivatizing agent, wherein said polymer material and said derivatizing agent react to form a derivatized polymer-containing slurry ; and combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form said hydrated derivatized polymer-containing treatment fluid.
In one respect, this invention is both a method for forming derivatized polymer material in a slurry and, in another respect, is the derivatized polymer material contained in a slurry and produced by this method. This method includes the steps of combining a hydrocarbon-based slurry containing polymer material with a derivatizing agent under conditions such that the polymer material and the derivatizing agent react to form derivatized polymer material contained in the slurry. In one embodiment of this method, the hydrocarbon based slurry may include a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof, and the polymer material may include a water soluble substantially high molecular weight polyhydric polymer such as a hydratable polysaccharide, hydratable derivatized polysaccharide, or a mixture thereof Specific types of polymers that may be employed include at least one of guar, derivatized guar, derivatized cellulose, starch, polyvinyl alcohol, or a mixture thereof In one typical embodiment, the polymer material includes guar particles having a size of between about 60 mesh and about 400 mesh. In the practice of one embodiment of this method, the derivatizing agent may include at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof In another embodiment of this method, the derivatizing agent may include at least one of alkali metal haloacetate, haloacetic acid, or a mixture thereof Specific examples of derivatizing agents include at least one of sodium chloroacetate, sodium bromoacetate, chloroacetic acid, bromoacetic acid, propylene oxide, or a mixture thereof ; and, more typically, at least one of sodium chloroacetate, chloroacetic acid or a mixture thereof In one typical embodiment of this method, the polymer material includes guar; the derivatizing agent includes sodium chloroacetate, chloroacetic acid, or a mixture thereof ; and the derivatized polymer material includes carboxymethyl guar. In the practice of this method, the hydrocarbon based slurry containing polymer material typically includes a viscosifier and dispersant and, most typically, the viscosifier includes organophilic clay and the dispersant includes an ethoxylated alcohol. A further embodiment of this method includes the step of combining the slurry containing polymer material with a basic compound or alkaline material prior to the step of combining the slurry containing polymer material with the derivatizing agent; and also includes the step of combining the slurry containing derivatized polymer material with an acidic agent or compound after the step of combining the slurry containing polymer material with the derivatizing agent.
In another respect, this invention is a method for treating a well, including the steps of combining a polymer material with a hydrocarbon solvent to form a polymer-containing slurry; combining the polymer-containing slurry with a derivatizing agent under conditions such that the
polymer material and the derivatizing agent react to form a derivatized polymer-containing slurry ; combining the derivatized polymer-containing slurry with an aqueous solution under conditions such that the polymer material reacts with the aqueous solution to form a hydrated derivatized polymer-containing treatment fluid; and introducing the treatment fluid into the well
In one embodiment of this method, the polymer material typically includes a water soluble high molecular weight polyhydric polymer having a molecular weight of greater than about 100, 000.
In another embodiment of this method, the polymer material typically includes a hydratable polysaccharide, hydratable derivatized polysaccharide, or a mixture thereof In one embodiment, specific examples of suitable polymers include, but are not limited to, at least one of guar, derivatized guar, derivatized cellulose, starch, polyvinyl alcohol, or a mixture thereof In another embodiment, specific examples of suitable polymers include, but are not limited to, at least one of guar, hydroxypropyl guar, hydroxyethyl cellulose, or a mixture thereof In yet another embodiment, the polymer material may include guar particles having a size of between about 100 mesh and about 325 mesh. In one embodiment, examples of suitable derivatizing agents include, but are not limited to, at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof In another embodiment, examples of suitable derivatizing agents include, but are not limited to, at least one of alkali metal haloacetate, haloacetic acid, or a mixture thereof Specific examples of suitable derivatizing agents include, but are not limited to, at least one of sodium chloroacetate, sodium bromoacetate, chloroacetic acid, bromoacetic acid, propylene oxide, or a mixture thereof Typically employed derivatizing agents include at least one of sodium chloroacetate, chloroacetic acid or a mixture thereof In one typical embodiment of this method, the polymer material may include guar; the derivatizing agent may include sodium chloroacetate, chloroacetic acid, or a mixture thereof ; and the derivatized polymer material may include carboxymethyl guar. In another typical embodiment of this method, the step of combining a polymer material with a hydrocarbon solvent to form a polymer-containing slurry includes dispersing from about 15% to about 50% powdered guar by weight of polymer to weight of final polymer slurry ("BWOS"or w/w) in the hydrocarbon solvent, and the step of combining the polymer-containing slurry with a derivatizing agent includes adding between about 4% and about 25% by weight chloroacetate by weight of polymer to the polymer-containing slurry. Another typical embodiment of the method includes the step of combining a viscosifier and a dispersant with the hydrocarbon solvent prior to the step of combining a polymer material with the hydrocarbon solvent to form a polymercontaining slurry, and most typically the viscosifier includes organophilic clay and the dispersant includes an ethoxylated alcohol. In another typical embodiment of the method, the well
penetrates a subterranean formation and the step of introducing includes the step of injecting a contents of the hydrated derivatized polymer-containing treatment fluid into the subterranean formation at a pressure above a fracturing pressure of the subterranean formation. Another typical embodiment of the method includes the step of combining the hydrated derivatized polymer-containing treatment fluid with a crosslinking agent under conditions such that the crosslinking agent and the derivatized polymer material react to form crosslinked derivatized polymer material contained in the treatment fluid. Another typical embodiment of the method includes the steps of combining the polymer-containing slurry with a basic compound or alkaline material prior to the step of combining the polymer-containing slurry with the derivatizing agent; and combining the derivatized polymer-containing slurry with an acidic agent or compound prior to the step of introducing; most typically in this embodiment, the polymer material includes
polymer particles having a size of between about 38 pm and about 600 sum, and the method further includes the steps of combining the polymer material with a hydrocarbon solvent to form the polymer-containing slurry prior to the step of combining the polymer-containing slurry with a basic compound or alkaline material; combining the derivatized polymer-containing slurry with an aqueous solution to form a treatment fluid after the step of exposing the derivatized polymer to the acid; and the step of introducing includes the step of introducing the treatment fluid into the well. Furthermore, in this embodiment, the organic solvent is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof In another typical embodiment, the step of combining the derivatized polymer-containing slurry with an aqueous solution occurs within a process stream in a continuous mixing process, and the step of introducing includes the step of introducing the process stream into the well immediately after the steps of combining the derivatized polymer-containing slurry with an aqueous solution.
In another respect, this invention is a method for treating a well, including the steps of combining a guar material with an hydrocarbon solvent to form a slurry containing guar material; combining the slurry containing guar material with a basic compound or alkaline material ; combining the slurry containing guar material with a derivatizing agent under conditions such that the guar material and the derivatizing agent react to form derivatized guar material contained in the slurry; combining the slurry containing derivatized guar material with an aqueous solution to form a treatment fluid under conditions such that the derivatized guar material reacts with the aqueous solution to form hydrated derivatized guar contained in the treatment fluid; and introducing the treatment fluid into the well. In this method the derivatizing agent typically includes sodium chroroacetate, chloroacetic acid, or a mixture thereof In one
typical embodiment of this method, the derivatizing agent includes sodium chloroacetate, chloroacetic acid, or a mixture thereof ; wherein the derivatized guar material includes carboxymethyl guar; and the method further includes the step of heating the slurry containing guar material to a temperature of between about 20 C and about 90 C prior to the reaction between the guar material and the derivatizing agent. In another typical embodiment, the well penetrates a subterranean formation and the step of introducing includes the step of injecting the treatment fluid into the subterranean formation at a pressure above a fracturing pressure of the subterranean formation. In yet still another embodiment, the method further includes the step of combining a contents of the treatment fluid containing hydrated derivatized guar with a crosslinking agent under conditions such that the crosslinking agent and the hydrated derivatized guar react to form crosslinked hydrated derivatized guar. In yet still another embodiment, the step of combining the slurry containing guar material with a derivatizing agent includes the step of combining a selected amount of the derivatizing agent with the slurry containing guar material to produce a derivatized guar material having a desired degree of substitution value, and even more typically, the amount of the derivatizing agent is selected to produce a derivatized guar material having a degree of substitution value of between about 0.05 and about 0.25.
DETAILED DESCRIPTION OF THE SPECIFIC EMBODIMENTS
Using embodiments of the disclosed method polymer materials may be derivatized to form derivatized polymer materials. These derivatized polymer materials include those typically used as rheological modifiers in well treatment fluids, especially fracturing fluids, used for treating oil and gas wells. As used herein, "well treatment fluid"means any fluid suitable for introduction into a wellbore during drilling, completion, workover, remedial or other well operations including, but not limited to, stimulation fluids (such as acid-containing fluids, condensate treatment fluids, scale removal or inhibitor fluids, asphaltene inhibitor or removal fluids, fracturing fluids with or without proppant, oxidizer-containing fluids, etc.), drilling fluids and muds, blocking gels, gravel pack fluids, frac pack fluids, clear fluids, foamed fluids, packer fluids, etc. Advantageously, embodiments of the disclosed method may be used to derivatize polymers in a continuous mixing process at a wellsite. Unexpectedly, this method results in a derivatized product which offers improved performance and stability, but at a lower cost than commercially-purchased derivatized polymers.
In the practice of the disclosed method, polymers that may be derivatized include, but are not limited to, substantially high molecular weight water soluble polymers containing alcohol
functional groups. Examples include, but are not limited to, substantially high molecular weight water soluble polyhydric alcohol polymers such as hydratable polysaccharide polymers, polyvinyl alcohol polymers and copolymers thereof As used herein"high molecular weight polymer" means a polymer typically having a molecular weight greater than about 100,000, and more typically greater than about 500,000. Suitable hydratable polysaccharide polymers include, but are not limited to, polygalactomannans, polyglucomannans, galactomannan gums, guars, guars, cellulose materials, starches, xanthans, and similar materials, as well as derivatives thereof.
Suitable polygalactomannans include, but are not limited to, those polysaccharides composed primarily of galactose and mannose units. Among other sources, polygalactomannans are typically found in endosperm of leguminous seeds, such as guar, locust bean, honey locust, flame tree, and cassia occidentialis. Specific examples of suitable polysaccharide polymers include, but are not limited to, guar gum, locust bean gum, xanthan gum, caraya gum, carrageenan, agar and the like, as well as derivatives thereof Additional information on hydratable polymers may be found, for example, in U. S. Patent No. 5,247, 995, which is incorporated by reference herein.
Furthermore, in the practice of the disclosed method polymer powders are typically used for derivatizing.
In the practice of the disclosed method, typical polygalactomannans include guar gum and locust bean gum. Guar gum is composed primarily of a polygalactomannan which is essentially a straight-chain mannan with single-membered galactose branches. The ratio of galactose to mannose in the guar polymer is typically 1: 2. In guar, mannose units are typically linked in a 1, 4 ss-glycositic linkage with galactose units attached by means of a 1,6 linkage on alternate mannose units. Typically, fracturing fluid quality guar gum has a molecular weight of about 2,000, 000. Locust bean gum is a similar polygalactomannan gum, having a ratio of galactose to mannose of 1: 4. Typical commercial sources of guar gum and locust bean gum include Rhone Poulenc and Aqualon. Most typically, fracturing fluid quality guar or locust bean gums available from these suppliers is employed.
It will be understood with benefit of the present disclosure that in addition to those polymers described above, the disclosed method may be practiced with any other polymer materials suitable for derivatization. For example, derivatized polymers may be used as a starting material and further derivatized using the disclosed method. Specific examples include derivatization of hydroxyethyl cellulose or hydroxypropyl guar to carboxymethylhydroxyethyl cellulose or carboxymethylhydroxypropyl guar, respectively. Synthetic polyhydric polymers such as polyvinyl alcohol may also be derivatized by using the disclosed method to make, for example, carboxymethyl polyvinyl alcohol.
In the practice of the disclosed method, any derivatizing agent suitable for derivatizing polymers such as polysaccharides may be employed. Suitable derivatizing agents include, but are not limited to, alkylene oxides, haloacetates and haloalkylquatemary ammonium halides such as chloroethyl trimethylammonium chloride, or mixtures thereof Typically, agents capable of derivatizing polygalactomannans are employed. For example, hydroxyalkylgalactomannan gums may be made by reacting galactomannan gums with an alkylene oxide having two or more carbon atoms. In this case, reactive hydroxyl groups on the galactomannan molecules react with alkylene oxides to produce a hydroxyalkylether of the gum in a manner as described, for example, in U. S. Patent No. 3,483, 121 ; U. S. Patent No. 3,723, 408; U. S. Patent No. 5,128, 462;
U. S. Patent No. 5,233, 032; U. S. Patent No. 4,137, 400; and U. S. Patent No. 4,094, 795; which are incorporated herein by reference. Typically, alkylene oxides having from 2 to 8 carbon atoms are employed. Other typical derivatizing agents include those agents suitable for producing alkylethers, carboxyalkylethers, hydroxyalkylether-carboxyalkylethers mixed derivatives, other mixed derivatives (such as mixed hydrophobic hydrophilic derivatives), and
N, N-dialkylaIkylcrylamide derivatives (such as N, N-dialkymethacrylamide) of polygalactomannans as described in the above-listed references.
Derivatized polysaccharide polymers which are typically produced according to the disclosed method include, but are not limited to, derivatized guars, guar gum derivatives, starches and polyvinyl alcohol and cellulose derivatives. Specific examples include, but are not limited to, carboxymethyl guar (sodium carboxymethyl guar), hydroxypropyl guar, carboxymethylhydroxypropyl guar, carboxymethyl cellulose, carboxymethylhydroxyethyl cellulose, hydroxyethyl cellulose, carboxymethyl starch, carboxymethyl polyvinyl alcohol, etc.
Most typically in the practice of the disclosed method, derivatized guar materials are produced.
Typical guar derivatizing agents include, but are not limited to, alkylene oxides, haloacetic acids such as chloroacetic acid ("CAA") and alkali metal haloacetates including, but not limited to, sodium chloroacetate ("SCA") and its analogs, such as sodium bromoacetate ("SBA"). When used as derivatizing agents, alkylene oxides produce hydroxyalkyl guar derivatives, while acetate-based derivatizing agents produce carboxymethylated guar derivatives.
Most typically in the practice of the disclosed method, propylene oxide is used to produce hydroxypropyl guar. Chloroacetic acid and sodium bromoacetate are typically used to produce carboxymethyl guar. Carboxymethylhydroxypropyl guar (CMHPG) may also be produced by sequentially using propylene oxide and chloroacetic acid. For long term storage of a slurry, haloacetic acids are typically used due to excessive water contamination which may occur with slurries using the alkali metal haloacetate process.
In the practice of the disclosed method, liquid polymer slurries are typically utilized to form derivatized polymers. As used herein"slurry"includes those mixtures in which a polymer is dispersed in a substantially inert solvent such as a hydrocarbon based liquid. Typically, such slurries are comprised of solid polymer material dispersed in an organic solvent. Acceptable organic solvents include any organic liquid suitable for forming a polymer slurry. Typical examples include diesel, kerosene, refined aliphatic oils such as Exxon's"ESCAID 110", and/or mixtures thereof Other examples of suitable organic solvents include, but are not limited to, alcohols (such as t-butanol and isopropanol), alkanes having greater than about 5 carbon atoms (such as heptane and hexane), etc.
Although not necessary, a typical organic solvent slurry base also includes one or more suspending agents such as organophilic clays (like, for example,"CLAYTONE) IMG-400," (commercially available from Southern Clay) and/or surfactants (like, for example, napthalene sulfonate resins. Nonionic surfactants such as ethoxylated nonylphenols or ethoxylated fatty alcohols may also be added to improve wetting and hydration.
Suitable polymers for use in the practice of the disclosed method include polymers such as those materials discussed above, as well as any other polymer materials that may be used to form an organic slurry for derivatizing polysaccharides. Acceptable forms of polymers include any solid form suitable for forming a slurry in an organic solvent for derivatizing polymers.
Specific examples include, but are not limited to, relatively large polymer particles such as seed endosperms and relatively small polymer particles such as powders. Most typically powders are used, especially those powders offering the highest surface area without being subject to agglomeration during the process. Typically, powders having a size of between about 600 um
and about 38 um, more typically between about 250 um and about 45 um, are used in order to obtain more uniform derivatization.
In the practice of the disclosed method, guar powders are typically employed. Among these are any guar powders suitable for derivatizing. Typically, powdered guar having a size of between about 60 mesh and about 400 mesh, more typically between about 100 and about 325 mesh, is employed. Advantageously, the ratio of particle surface area to number of polymer
molecules in such powdered guars is typically much higher than the particle surface area to polymer molecule ratio of guar split particles. This higher ratio tends to provide greater surface area exposed for derivatization and typically yields more uniform and random substitution of the derivatizing agent. Most typically, a fracturing fluid grade guar powder known as"GUAR X0694-17-1"and available from Aqualon (Hercules, Inc. ) is used. Most typically in the practice of the disclosed method, a polymer slurry is 100-325 mesh powdered guar dispersed in a diesel hydrocarbon solvent in a concentration of between about 15% and about 50% BWOS, and most typically between about 25% and about 45% BWOS. As used herein,"BWOS"refers to the weight of a component by weight of the final slurry.
Using the disclosed method, and with benefit of this disclosure, a polymer slurry may be formed using any suitable method known to those of skill in the art and may be prepared onsite or offsite. For example, one or more viscosifiers or suspending additives may be first added to a hydrocarbon solvent to suspend polymer particles and, in another embodiment, after viscosifier or suspending agent/s are added, surfactants may be added followed by polymer particles.
Although any amount and/or type of viscosifier suitable for achieving desired slurry dispersal may be employed, in one typical embodiment an organophilic clay is added to a hydrocarbon solvent at concentrations of typically from about 0.2% to about 1.0% BWOS by weight of hydrocarbon solvent. In other embodiments, greater or lesser amounts are possible. A specific example of a typical organophilic clay is CLAYTONE IMG-400, available from Southern
Clay Products of Gonzalez, Texas.
In one typical embodiment, after adding viscosifier a dispersant, such as a surfactant for dispersing and/or wetting may be added, followed by polymer particles. Typical dispersants include, but are not limited to, surfactants such as ethoxylated nonylphenols and/or ethoxylated fatty alcohols. However, any surfactant or mixture of surfactants suitable for acting as a dispersant and/or water wetting polymer particles in a hydrocarbon solvent may be employed.
Typically, such surfactants are liquid and nonionic, although solid surfactants may also help fulfill this role. Examples of suitable surfactants include, but are not limited to, alcohol ether sulfates, liquid ethoxylated alcohols, nonylphenol ethoxylates, mixtures thereof : etc. In one typical embodiment, a liquid ethoxylated alcohol surfactant may optionally be employed. In this regard, a most typical liquid ethoxylated alcohol is an ethoxylated tridecyl alcohol known as "ICONOL TDA-6"and available from BASF. Examples of typical solid surfactant compositions include, but are not limited to, solid alpha olefin sulfonate, alcohol ethoxylates, alcohol ether sulfates, betaines, sulfosuccinate esters, alkyl sulfates, alkyl aryl sulfonate, and mixtures thereof
Other suitable ethoxylated alcohol wetting surfactants include, but are not limited to, "L610-3"available from Huntsman,"L12-3"available from Huntsman,"SYNPERONIC 13/5"available from ICI,"SYNPERONIC 13/8"available from ICI. Suitable secondary alcohol ethoxylates include, but are not limited to"TERGITOL 15-S-9"available from UNION CARBIDE and"TERGITOL 15-S-5"available from UNION CARBIDE. Other suitable surfactants include, but are not limited to polyethylene glycol diester of oelic acid, "400- DO"available from RP; ethox sorbitan monooleate,"PSMO-20"available from RP; and ethox castor oil,"EL-620"available from RP.
When used, a surfactant is typically employed in an amount of from about 0.1% to about 2% BWOS, more typically from about 0.25% to about 1% BWOS, and most typically about 0.5% BWOS.
In the practice of the disclosed method, a polymer slurry may comprise, among other things, any combination of polymer particles, viscosifiers, and/or surfactants. Furthermore, in any given polymer slurry, each of the above-mentioned components (when employed) are typically present in a polymer slurry in the amounts or concentrations mentioned above. Other additives may also be present including, but not limited to, alcohols and similar solvents that do not substantially react with derivatizing agent. In this regard, alcohol solvents are most typically tertiary alcohols and water content is typically minimized. For example, in one most typical embodiment for a D. S. value of about 0.17, a polymer slurry when combined with a derivatizing agent typically includes about 29% polysaccharide (most typically guar gum) by weight per weight of final slurry ("BWOS"), about 0. 6% clay suspending agent (most typically CLAYTONE IMG-400 organophilic clay) BWOS, about 0.3% dispersing surfactant (most typically ICONOL TDA-6 liquid ethoxylated alcohol) BWOS, about 50.9% hydrocarbon solvent (most typically No. 2 diesel hydrocarbon solvent), about 7. 2% alcohol solvent (most typically tbutanol) BWOS, 8.2% of 50% aqueous caustic BWOS, and about 3.8% derivatizing agent (typically chloracetate or chloroacetic acid) BWOS.
When derivatization is performed as part of a wellsite operation, a slurry may be prepared offsite and transported to the well location, or alternatively may be prepared onsite.
Onsite preparation of a polymer slurry is typically performed by mixing in substantially the same sequence and fashion as that offsite. Advantageously, when used either as part of a continuous mixing or batch process for well treatment operations, washing of the polysaccharide derivative product is unnecessary.
In the practice of the disclosed method, derivatization of polymers, regardless of type, is typically performed as a batch process. After derivatization is substantially completed, the mixing of the fracturing fluid components, for example, at a well site, may be prepared either by batch or continuous mix methods. Derivatization is typically accomplished by the reaction of a derivatizing agent with polymer material contained in a slurry. Typically this reaction is performed in a substantially inert or substantially carbon dioxide-free and substantially nonoxidizing (e. g., oxygen free) atmosphere to prevent polymer oxidation and/or degradation, and in the presence of a basic compound or alkaline agent to swell the polymer particles and activate the derivatizing sites on the polymer by, for example, forming alkoxide (the anion of an alcohol).
A stoichiometric excess of basic compound or alkaline agent based on the weight of derivatizing agent is typically employed to ensure activation of derivatization sites following neutralization of acid content (such as hydrochloric acid) resulting from reaction. In this regard a stoichiometric excess of greater than about 100%, more typically greater than about 125%, and most typically greater than or equal to about 150% based on the weight of derivatizing agent, of basic compound or alkaline agent required to activate polymer derivatization sites is typically employed.
Acceptable basic compounds and alkaline agents include, among other things, any agent suitable for swelling the polymer particles, forming alkoxides and which does not react substantially with a derivatizing agent. Examples of suitable basic compounds and alkaline agents include, but are not limited to, inorganic and organic derivatives such as alkali metal and alkaline earth metal hydroxides, quaternary ammonium hydroxides, alkoxide, organic acid salts, and the like. Illustrative of specific basic compounds are sodium hydroxide, potassium hydroxide, calcium hydroxide, barium hydroxide, sodium carbonate, potassium acetate, sodium methoxide, tetramethylammonium hydroxide, and the like, caustic (sodium hydroxide), or mixtures thereof Typically, caustic (NaOH), a mixture of caustic and potassium hydroxide, or potassium hydroxide is employed. Most typically, caustic is employed. In this regard, caustic amount (expressed as 100% active caustic) typically ranges between about 4 and about 25% (based on the weight of polymer) and typically depends on the degree of substitution desired.
As used herein degree of substitution ("D. S. ") means number of hydroxyl groups on each pyrannoside sugar occupied by the derivative. One typical formulation uses about 4. 5% caustic by weight of polymer to achieve an intended D. S. of about 0.05, another typical formulation uses about 22.6% caustic by weight of polymer to achieve an intended D. S. of about 0.25. In a most typical embodiment, a D. S. of about 0.17 is achieved. This is so because a byproduct of
the reaction is hydrochloric acid, and the higher the D. S., the greater amount of HCI is produced. Table 1 gives example embodiments based on derivatizing one sugar (MW=162).
TABLEt
D. S. Sodium Chloro-Sodium Chloro-100% 50% Chloro-acetic Chloro-acetic Caustic Caustic Caustic acetate Acid acetate Acid (Moles) (%) (%) (Moles) (Moles) (%) (%) 0. 05 5. 4x 10-4 5. 14x10-6. 0 4. 8 1. 132x10-3 4. 5 9. 0 0.17 1. 75x10-3 1. 75xlO"'20. 4 16. 5 3. 848x 10-3 15. 4 30. 8 0.25 2. 57xi3 2. 57x10-3 30'0 24. 3 5. 66x10-3 22. 6 45. 3 An inert atmosphere may be provided by degassing with nitrogen, helium, argon, or any other gas that does not substantially inhibit or interfere with the derivatizing reaction.
Alternatively, derivatization may be carried out in the absence of a gaseous atmosphere. The purpose of degassing is to remove diatomic oxygen molecules from the system. Oxygen under alkaline conditions can dramatically degrade polysaccharides. Therefore, any method capable of displacing or otherwise removing oxygen molecules from a reaction mixture, such as by using a vacuum may be employed.
In a most typical embodiment, a polymer slurry including dispersed guar powder is exposed to low volumes of caustic (typically in the form of commercially available 50% aqueous sodium hydroxide) prior to derivatization. Typically, as previously mentioned caustic (expressed as 100% active (dry) caustic) is employed in an amount from about 4% to about 25% by weight of polymer, and most typically from about 12% to about 18% by weight of polymer, although any other amount suitable for catalyzing a derivation may be employed.
Derivatization is accomplished by combining a slurry containing polymer particles or combined with a derivatizing agent under conditions such that the polymer and derivatizing agent react to form a derivatized polymer. As used herein, the term"combining"includes any method suitable for admixing, exposing, contacting, or otherwise causing two or more materials, compounds, or components to come together in a manner sufficient to cause at least partial reaction and/or at least partial mixing to occur between the components. Examples of suitable methods of combining include, but are not limited to, adding one component to another component or vice versa, simultaneously adding together streams or batches of one or more components, and adding components sequentially. In the case of treating a polymer slurry with a derivatizing agent, such suitable combining methods include, but are not limited to, adding derivatizing agent to polymer slurry, adding polymer slurry to derivatizing agent, simultaneously mixing streams of polymer slurry and derivatizing agent, and any combination thereof In conjunction with these methods of combining, derivatization is typically accomplished using batch mix processes.
In embodiments of the disclosed method employing guar particles, a derivatization agent is typically at least one of sodium chloroacetate ("SCA"), sodium bromoacetate ("SBA"), or chloroacetic acid, bromoacetic acid, or mixtures thereof Typically, such a derivatizing agent is added to a guar powder slurry in any amount suitable for achieving the desired D. S. under reaction conditions. Typically a derivatizing agent is added in an amount of between about 4% and about 25% based on weight of polymer, most typically between about 12% and about 17% based on weight of polymer. In this regard, a derivatizing agent may be added to a polymer slurry in any suitable manner known to the art, for example as a dry powder or solution. Most typically derivatizating is added as an about 40% solution in either water or alcohol (such as methanol, ethanol, propanol, butanol, or mixtures thereof).
Prior to or following addition of a derivatizing agent/s, a polymer slurry may be heated to a temperature appropriate for obtaining sufficient and timely derivatization of the polymer material using the particular derivatizing agent/s. For example, when derivatizing a guar powder slurry using SCA, the slurry is typically heated to a temperature of between about 20 C and about 90oC, most typically between about 50 C and about 70OC. Advantageously, when SBA is used as a derivatizing agent, a relatively low reaction temperature of typically between about
20 C and about 70oC, more typically between about 20 C and 50 C is employed. Thus, depending on the ambient temperature, no heating may be needed.
In the case of the derivatization of guar powders using SCA or SBA a reaction time of between about 1 hr. and about 6 hr. , more typically between about 2 hr. and about 5 hr. , and most typically about 3 hr. , is provided to allow complete derivatization. Heating times and temperatures will vary according to particular combinations of polymer particles and derivatizing agents, and may be determined and adjusted for other polymer materials and/or derivatizing agents with benefit of this disclosure and using techniques known to those of skill in the art.
During derivatization, process control parameters that may affect the degree and success of derivatization reactions include stochiometry, reaction time, temperature control, and maintenance of an inert atmosphere during the derivatization reaction. With benefit of this disclosure, adjustment of temperature, reaction time, and stochiometry may be made using techniques known to those of skill in the art to produce the desired derivatized product.
Typically, a derivatization reaction may be controlled to provide better yields by reducing temperature, controlling stochiometry and extending reaction time. For example, the required amount or concentration of a derivatization agent relative to concentration of polymer material that is required to obtain a desired degree of molar substitution may be determined and adjusted.
As a specific example for derivatizing 29% BWOS guar gum in a hydrocarbon-based slurry, the concentration of a chloroacetic acid derivatization agent is typically about 16.5% (based on guar gum) and the slurry is typically heated to about 60 C for about 3 h to produce a carboxymethyl guar having a D. S. of about 0.17. In this way, the disclosed method allows the characteristics of a polymer to be customized at the wellsite to fit particular criteria. For most applications, polymers with D. S. of about 0.10 to about 0.17 appear to function well as fracturing fluids, although the disclosed method may be used to make polymers having D. S. values up to or exceeding about 0.25. In contrast, most commercial processes are capable of making polymers with D. S. values of up to about 0.15.
Although not required in the practice of the disclosed method, a derivatized polymer slurry may be treated with relatively small volumes of an acidic agent or compound to consume any excess alkaline material remaining from the derivatization step, for example, to allow or facilitate polymer hydration. When such neutralization is desired, any acidic agent or compound suitable for neutralizing a polymer slurry may be employed. For example, typical neutralizing acids include, but are not limited to, fumaric acid, formic acid, sodium diacetate, sulfamic acid, acetic acid, glacial acetic acid, hydrochloric acid, mixtures thereof, etc. Most typically acetic acid is utilized. Alternatively, a buffered aqueous solution may be employed to achieve a hydrated polymer solution having a desired pH, for example a pH in the range described below.
In this regard, one buffered solution typically employs sodium bicarbonate and fumaric acid.
In one embodiment,"neutralization"is achieved by adding sufficient acidic agent to adjust the pH of a hydrated polymer solution to be from about 4 to about 10, more typically from about 6 to about 8.5. After heating and derivatization, a slurry may be cooled prior to neutralization if desired. Cooling may be desirable, for example, before neutralizing the excess caustic with an acid such as hydrochloric acid, fumaric acid, glacial acetic acid or acetic acid. In such cases, neutralizing at reaction temperatures may cause polymer degradation. In the case of a derivatized guar slurry, the sluny is typically cooled to a post derivatization temperature of between about 20 C and about 30oC.
When used onsite to produce derivatized polymers for well treatments, a polysaccharide is typically derivatized in bulk using batch methods prior to introduction into a wellbore as part of a batch or continuous mix well treatment. In this regard, polymer powder may be dispersed in an organic solvent, derivatized and stored onsite prior to the time the well treatment is introduced into the wellbore. Derivatization is typically performed offsite, though onsite batch derivatization is also possible. When derivatized offsite, a derivatized slurry may be typically transported, trucked, to the wellsites.
When a combination of polymer, derivatizing agent and ambient temperature dictates heating for the derivatization process, with benefit of this disclosure any suitable method known to those of skill in the art for heating a well treatment fluid may be employed. For example, a polymer slurry or precursor to a polymer slurry may be circulated through a conventional heater treated to obtain the necessary temperature. Typically, a substantially inert or substantially nonoxidizing atmosphere is provided by maintenance of a nitrogen gas blanket in process vessels. A polymer slurry may be derivatized in any vessel suitable for containing and supporting the derivatization reaction including, but not limited to, frac tanks, reactor vessels, etc. Most typically, a reactor or modified vessel, such as those known in the art to be suitable for mixing hydrocarbon-based polymer slurries is employed. Most typically, degassing is accomplished by submerging a tube under the slurry surface and sparging with inert gas while stirring. Any given amount of derivatized slurry may be produced in a given batch treatment, though typically a batch is only as large as required for a given well treatment. For example, a large fracturing treatment may use up to about 1,000, 000 gallons (3785 m3) of polymer solution and typically requires about 10,000 gallons (37.9 m3) of slurry. However, most fracture treatments require about 1,000-2, 000 gallons (3.8-7. 6 m3) of slurry.
Following derivatization, a derivatized polymer slurry may be stored for later use. With benefit of this disclosure and using methods and materials known to those of skill in the art, a stored or pre-derivatized polymer slurry may be combined with an aqueous solution or treatment fluid and other components (such as one or more crosslinkers, proppants, breakers, clay protection agents, etc.), including those as previously described herein prior to introduction into a wellbore. Typical clay protection agents include, but are not limited to, aqueous solutions of
tetramethlammonium chloride, potassium chloride, etc. Examples of typical crosslinking agents include, but are not limited to, those described in U. S. Patent No. 4,514, 309 and U. S. Patent
No. 5,247, 995, which are incorporated herein by reference.
As used herein, "introduced into a wellbore"includes pumping, injecting, pouring, releasing, displacing, spotting, circulating or otherwise placing a material within a well or wellbore using any suitable method known in the art. Typically, crosslinking agents are added to a hydrated polymer solution, ie., after combination with aqueous treatment fluid. An aqueous treatment fluid may be heated if desired, as described above by circulation through a conventional heater treated, or by any other suitable means. It will be understood with benefit of the present disclosure that a polymer slurry may be formed and/or introduced into a well in other ways. For example, the polymer in the slurry may be solvated in an alcohol (methanol) based solvent.
As described above, use of the disclosed method to derivatize polymers advantageously results in a substitution reaction which may produce derivatized polymers typically having more uniform derivatization than commercially available derivatized polymers. Furthermore, when used to derivatize polymers for well treating purposes, the disclosed method typically does not require post derivatization processing, such as isolation, washing, purification (such as by washing with organic solvents) andior packaging of the polymer, thereby reducing costs.
Finally, the disclosed method allows production of customized polymer compositions by allowing the manipulation of the D. S. value, and thus allows the characteristics of a polymer to be customized, for example, to fit particular wellbore or downhole criteria. In one most typical embodiment, a derivatized polymer of the disclosed method has a D. S. value of between about 0.05 and about 0.25, and more typically between about 0.10 and about 0.17, although values outside these ranges are possible. In this regard, concentration of alkaline agent (such as caustic) and derivatizing agent employed to achieve a derivatized polymer is related to desired
D. S. value and polymer concentration in a given slurry and, with benefit of this disclosure, may be determined by those of skill in the art. Most typically, such a derivatized polymer is a derivatized guar material.
Although use of the disclosed method for derivatizing polymers for use in hydraulic fracturing treatments has been described above, it will be understood with benefit of the present disclosure that the disclosed method may also be employed to produce derivatized polymers for use in other types of well operations and treatments. Examples include any treatment or
operation that may benefit from the use of derivatized polymer materials including, but not limited to, drill-in, drilling, completion, cementing, stimulation, workover and remedial operations. Specific examples of treatment fluids include drilling muds and lost circulation compositions, drill in fluids, gravel pack fluids, frac pack fluids, gel cleanout fluids, blocking gels, gelled acid fluids or other similar treatments employing gels, foamed fluids, etc.
EXAMPLES
The following examples are illustrative and should not be construed as limiting the scope of the invention or the claims thereof
Example 1-Derivatization of Guar 120.0 g of fracturing fluid quality guar ("GW-4"available from Rhone Poulenc) was added to 210.0 g of"ESCAID 110", a refined aliphatic oil available from Exxon. The resulting slurry was rapidly stirred in a resin kettle while degassing with N2 for about 20 min
Then, 19.0 g of 40% aqueous caustic was added dropwise over a time period of about ten minutes. The slurry was continuously degassed for about thirty minutes to allow maximum particle swelling to occur. After swelling, 52.33 g of aqueous sodium chloroacetate was added dropwise over a time period of about fifteen minutes. After about 90% of the sodium chloroacetate had been added, the slurry was heated to 85 C for two hours and then cooled.
The solids in the slurry were then isolated by vacuum filtration, washed twice with 80% aqueous methanol, and dried. A 0.48% by weight of solution of this derivatized polymer was prepared in deionized water and was found to have a Fanny 35 (RIB I cup and bob geometry) viscosity of 38 centipoise ("cp"), and a D. S. value of 0. 14.
Example 2-Crosslinking and Evaluation of Rheological Properties
The polymer derivatized in Example I was evaluated for its rheological performance as the gelant in a fracturing fluid. The fluid was prepared by hydrating 1.80 g of polymer in IL of water. After mixing for about 30 min, I ml of a 50% aqueous tetramethylammonium chloride solution was added, followed by 1.2 g sodium thiosulfate. The pH of the solution was increased by adding 0.5 ml of 46% aqueous KOH. Lastly, 0.7 ml of a zirconium lactate crosslinking agent (5.3% ZrO2) was added under conditions of excessive shear (using a Waring Blender) for thirty seconds. The resulting product was a viscous semi-solid gel.
To test the resulting gel, 45 g of gel was placed into a Fann "50C"cup (RCBI cup and bob geometry) and the cup positioned back onto the Fann"50C"viscometer. The sample was pressured to about 100 psi (6.9 bar) with N2 and was pre-conditioned by shearing at 105 sec-l for 60 sec. Afterward, a rate sweep, using 105, 84,63 and 42 sec'*, was made and repeated every 30 min. The shear rate and corresponding stresses were used to determine the
Power Law indices, n'and K. This procedure is described in American Petroleum Institute publication RP-39, Recommended Practice Standard Procedure for the Evaluation of Hydraulic
Fracturing Fluids. The Power Law indices were then used to calculate the fluid viscosities at 105, 85 and 42 sec-l as shown in Table 2. After the initial rate sweep, the fluid was heated to 22SOP (107OC) for the duration of the test. The interim rate between sweeps was 105 sec-l. The data reported in Table 2 suggests satisfactory stability and performance at this temperature was achieved with a relatively low polymer concentration. More specifically, this example shows that a polymer derivatized using the disclosed method may be used to produce viscous gels suitable for hydraulic fracturing processes.
Example 3--Crosslinking and Evaluation of Rheological Properties at Low pH
The polymer derivatized in Example 1 was evaluated for its rheological performance as the gelant in a low pH fracturing fluid. The fluid was prepared by hydrating 1.80 g of polymer in
IL of water. After mixing for about 30 min, 1 ml of a 50% aqueous tetramethylammonium chloride solution was added and the pH of the solution was reduced to 4.5 with 0.5 ml of glacial acetic acid. Lastly, 0.5 ml of a zirconium lactate crosslinking agent (5.3% ZrO2) was added with excessive shear for thirty seconds. The product formed was a semi-solid gel.
To test the resulting gel, 45 g of gel was placed into a Fann "50C"cup (and the cup positioned back onto the Fann"50C"viscometer). The test method described in Example 2 was repeated except that the test temperature was 150OF (66OC). As shown in Table 3, the derivatized polymer exhibited satisfactory stability and performance at relatively low polymer concentrations. More specifically, this example shows that a guar polymer derivatized under relatively low pH conditions, may be used to form gels that are applicable for fracturing fluids.
In this regard, underivatized guar gum generally does not crosslink in low pH environments and the viscosity is very unstable while heating.
Example 4--Derivatization of Guar at Ambient Temperature In this example, the sodium chloroacetate used in Example I was replaced with sodium bromoacetate. This substitution allowed the derivatization reaction to proceed at ambient temperature.
The derivatization process began by adding 120.0 g of fracturing fluid quality guar ("GW-4"from Rhone Poulenc) to 210.0 g of"ESCAID (TM) (from Exxon). The dispersion was degassed with N2 and stirred in a 500 ml resin kettle for about 90 min. Afterward, 14.34 g of 50% aqueous caustic solution was added dropwise over about 12 min. After an additional 10 min to allow swelling, a solution composed of 33.02 g bromoacetic acid, 40.0 g deionized water and 20.03 g of 50% aqueous caustic was mixed to form a solution having a final pH of
6. 60. The temperature of this solution was 28OC. This solution was added dropwise to the slurry, which had a temperature of 24OC. The interaction of the swollen particles with the sodium bromoacetate was exothermic and generated temperatures up to 32OC. The addition took about 15 min followed by an additional three hours of stirring while degassing. The temperature gradually declined to an ambient temperature of 21 C. The slurry solids were isolated by vacuum filtration, washed twice with 80% aqueous methanol and dried. A polymer solution of 0.48% by weight of solution of the resulting derivatized polymer in deionized water had a Fann 35 (RIB1) viscosity of 36 cp and a D. S. value of 0.08.
The results of this example indicate that polysaccharides may be derivatized at ambient conditions utilizing sodium bromoacetate.
Example 5-Derivatization of Guar using Chloroacetic Acid
The derivatization process began by adding 2.50 g of organophillic clay to 210 g of #2 diesel in a 500 mi resin kettle. The mixture was stirred with a magnetic stirrer. After 5 min., 1.09 g of an ethoxylated fatty alcohol was added and stirred for an additional 10 min. followed by the addition of 120 g of guar gum supplied as"GW-4"by Rhone Poulenc. The resulting amber slurry was degassed with N2 by means of a sparge tube. The slurry was then treated with the rapid addition of 34. 04 g of 50% (wt. ) aqueous sodium hydroxide. After stirring for an hour with a lightening stirrer, a solution of 15.7 g of 99% + chloroacetic acid (Aldrich) dissolved in 20 g of t-Butanol was added dropwise over 40 min. The slurry was stirred at ambient temperature for another two hours, followed by heating to 90OC for three hours. The resulting dark brown slurry was cooled and neutralized with 10.7 g of 15% (wt. ) hydrochloric acid. The
polymer was isolated by vacuum filtration and washed five times in 90% aqueous methanol, filtered and dried. A solution of 0. 48% by weight of solution of the resulting derivatized polymer in deionized water had a Fann(TM) 50 (R1B1) viscosity of 41 cp and a D. S. value of 0.17.
The results of this example show that, using the disclosed method, chloroacetic acid is an effective agent for derivatizing guar.
TABLE 2-Data for Example 1
Temperature : 150OF (66OC) Instrument: Fann 50C with RIB5 cup and bob geometry
Additives: 1.0 gallon (0.004 m3) per thousand gallons (4 m3) ("gpt") 50% aqueous tetramethyl ammonium chloride, 15 pounds (6.8 kg) per thousand pounds (453.6 kg) ("ppt") polymer from Example 1 (13.5 centapoises (cps) ), acetic acid (pH=4.5) and 0.5 gpt zirconium lactate crosslinker, pH: 4.67, 4.77 ; Rate: 105 S. l Target pH range: From about 4.5 to about 5
Breaker: None
TIME TEMP n' K Viscosity Viscosity Viscosity (min.) (OF ( C)) (dyne/cm2) (at 105 s-10 (at 85 s-1) (at 42 s-1) 4 78 (26). 318 35. 2168 147 170 275 34 151 (66) 63 11. 4042 204 no 286 64 147 (64) .693 9.4724 227 242 301 94148 (64). 643 11. 5438219236304 124 148 (64). 671 9. 8142 212 228 287 151 148 (64) .654 10. 197204219280 180 148 (64) .69 8.2749 196 209 260 210 148 (64) . 67 8. 6764 187 200 253 240 148 (64). 685 7. 7673 179 192 239 270 148 (64). 808 4. 3174 177 184 211 300 148 (64). 787 4. 527 168 176 204 330 148 (64). 73 5. 6446 161 170 206 360 148 (64). 699 6. 3509 156 167 206 390 148 (64) . 674 6. 8788 151 162 203 420 148 (640 .703 5.8489 147 156 193 450 148 (64). 722 5. 2208 143 152 185 480148 (64). 74 4. 6623 139 147 176
Table 2-Continued
TIME TEMP n'K Viscosity Viscosity Viscosity (min.) ( F ( C)) (dyne/cm2) (at 105 s-1) (at 85 s-1) (at 42 s-1) 510 148 (64) .768 4.015 136 143 169 540 148 (64). 739 4. 4826 133 141 169 570 149 (65). 739 4. 355 129 137 164 600 148 (64). 855 2. 5534 130 134 149 630 149 (65). 753 3. 9082 124 130 155 660 148 (64). 702 4. 8114 120 128 158 690 149 (65). 754 3. 7422 119 125 149 720 149 (65). 803 2. 9517 118 123 141 750 149 (65). 793 3. 0058 115 120 139 780 149 (65). 78 3. 1581 113 119 139 810 149 (65). 795 2. 8888 111 116 134 840 149 (65). 754 3. 4307 109 115 137 870 149 (65). 751 3. 3645 106 ho 133 900 149 (65). 813 2. 5348 106 110 126 930 149 (65). 731 3. 5882 103 109 131 960149 (65). 746 3. 3135 102107128 1049 94 (34) .655 8.5715 172 185 236 TABLE 3 : Data for Example 2
Temperature: 225 F (107OC) Instrument : Fann 50C with RIB5 cup and bob geometry.
Additives: 1.0 gpt 50% aqueous tetramethyl ammonium chloride, 15 ppt polymer made in
Example 1 (13.5 cps), 10 ppt sodium thiosulfate, 0.5 gpt 46% aqueous KOH and 0.7 gpt zirconium lactate crosslinker, pH : 11.40, 10.50 ; Interim Rate : 105 s-1 Target pH range: From about 10 to about 11.5
Breaker: None
TIME TEMP n' K Viscosity Viscosity Viscosity (min.) ( F ( C)) (dyne/cm2) (at 105 s-1) (at 85 s-1) (at 42 s-1) 4 98 (37). 545 70. 5602 849 935 1288 34 229 (109). 552 19. 4097 241 265 364 64 230 (110). 518 17. 1433 182 201 283 94 229 (109). 508 15. 7621 160 177 251 124 229 (109). 511 14. 1648 145 161 228 154 229 (109). 533 11. 9797 136 150 209 171 228 (109) . 518 12. 2489 130 144 202 201 226 (108). 547 10. 1492 123 136 187 231 226 (108) .528 10.3501 115 127 177 261 226 (108) .536 9.2335 107 118 163 291 226 (108). 575 7. 1387 99 108 146 320 226 (108). 546 7. 5314 91 100 138 350 226 (108). 532 7. 5052 85 94 131 380 226 (108). 549 6. 4993 80 88 120 410 226 (108). 568 5. 5464 74 81 110 440 226 (108). 599 4. 5835 71 77 102 470 226 (108). 597 4. 4039 67 73 98 500 226 (108). 572 4. 6816 64 70 95 530226 (108). 575 4. 3245606588
Table 3-Continued
TIME TEMP n'K Viscosity Viscosity Viscosity (min. ) (OF (OC)) (dyne/cm2) (at 105 s-l) (at 85 s-l) (at 42s') 560 226 (108) . 563 4. 3485 57 62 85 590 226 (108). 562 4. 161 54 59 81 620 226 (108). 556 4 0532515677 650 226 (108). 535 4. 1969 48 53 74 680 226 (108). 589 3. 124 46 50 67 710 226 (108). 604 2. 7953 44 48 64 740 226 (108). 605 2. 6328 42 46 60 770 226 (108). 604 2. 5281 40 44 58 800 226 (108). 631 2. 1571 39 42 54 830 226 (108). 595 2. 3723 36 39 52 860 226 (108). 572 2. 5344 35 38 51 890 225 (107). 691 1. 4129 34 36 45 920 99 (37). 627 3. 8742 68 74 96 Example 6-Rheological Evaluation of Polymer Prepared in
Example 5 and Comparison to Underivatized Starting Polymer
The polymer prepared in Example 5 was evaluated for its rheological performance as a gelant in low pH fracturing fluids. The performance data is presented in Table 4. For comparison, the rheological performance of the underivatized, starting guar gum is presented in
Table 5. Both fluids were prepared by hydrating 3.0 g of polymer in IL of water. After mixing for about 30 min, 1 ml of 50% aqueous tetramethylammonium chloride solution was added and the pH of the solution was reduced to 5.13 (for the derivatized guar) and to 5.23 (for the guar gum) with glacial acetic acid. Lastly, 0.5 ml of zirconium lactate crosslinking solution (5.3% ZrO2) was added with excessive shear for about 30 sec. The product formed a thin polymer solution.
The rheological performance of the resulting gel was evaluated by placing 45 g of gel on the Fann 50C. The test conditions and analysis methods were identical to those described in
Example 2. Data for the derivatized polymer is presented in Table 4 and data for the underivatized polymer in Table 5. As shown, the derivatized polymer generates viscosity values
that are applicable or suitable for most fracturing treatment applications. The underivatized polymer performance, in comparison, is significantly inferior. The current trend in the industry is for target viscosity to exceed 200 cp at 42 s-l for the fluid to adequately suspend proppant. This data also suggests that the disclosed method of derivatization is applicable to produced polymers suited for fracturing fluids.
Table 4-Data for Derivatized Polymer of Example 6
Temperature : 150 F (66OC) Additives : 1 gpt 50% aqueous tetramethylammonium chloride solution, 25 ppt polymer from example 5, glacial acetic acid (pH : 5.13) and 0.5 gpt zirconium lactate crosslinker
Time Temp N'K'Viscosity Viscosity Viscosity (min) (OF ( C)) (dyne/cm2) (cp) 105s-l (cp) 85 5-1 (cp) 42 s-1 5 78 (26) 0. 575 3. 354 46 51 69 35 158 (70) 0. 255 92. 885 290 339 574 65 150 (66) 0. 308 76. 416 305 353 575 94 148 (64) 0. 307 78. 427 312 361 588 124 150 (66) 0. 33 71. 535 316 365 585 153 150 (66) 0. 315 77. 692 321 370 600 183 151 (66) 0. 333 72. 938 327 377 603 213 101 (38) 0. 371 72. 380 388 443 690 243 86 (30) 0. 375 74. 828 408 466 724 Table 5-Data for Underivatized Polymer of Example 6
Temperature: 150 F (66OC) Additives: 1 gpt 50% aqueous tetramethylammonium chloride solution, 25 ppt guar
gum (Aqualon, glacial acetic acid (pH : 5. 23) and 0. 5 gpt zirconium lactate crosslinker.
Time Temp N'K'Viscosity Viscosity Viscosity Time Temp N' K' Viscosity Viscosity Viscosity (min) ( F ( C)) (dyne/cm2) (cp) 105 s-1 (cp) 85 s-1 (cp) 42 s-1 5 78 (26) 0.53 3.328 37 41 57 35 160 (71) 0. 686 3. 215 75 80 99 64 150 (66) 0. 816 1. 702 72 75 86 94 146 (63) 0.821 1.574 68 71 81 124 102 (39) 0.69 3.954 93 100 124
Claims (57)
1. A method for treating a well, comprising : combining a polymer material with an organic solvent to form a polymer-containing slurry ; combining said polymer-containing slurry with a derivatizing agent, wherein said polymer material and said derivatizing agent react to form a derivatized polymer containing slurry ; combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form a hydrated derivatized polymer-containing treatment fluid; and introducing said treatment fluid into said well.
2. The method of claim 1, wherein said method comprises: combining said polymer material with said organic solvent to form said polymer containing slurry ; then combining said polymer-containing slurry with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said polymer-containing slurry with said derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; allowing said polymer material and said derivatizing agent to react to form a derivatized polymer-containing slurry ;
combining said derivatized polymer-containing slurry with said aqueous solution, wherein said polymer material interacts with said aqueous solution to form said hydrated derivatized polymer-containing treatment fluid ; and introducing said treatment fluid into said well; wherein said polymer-containing slurry is combined with said basic compound or alkaline material prior to combination of said polymer-containing slurry with said derivatizing agent.
3. The method of claim 1, wherein said polymer material comprises a water soluble high molecular weight polyhydric polymer having a molecular weight of greater than about 100,000.
4. The method of claim 1, wherein said polymer material comprises a hydratable polysaccharide, hydratable derivatized polysaccharide, or a mixture thereof
5. The method of claim 1, wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, polyvinyl alcohol, or a mixture thereof
6. The method of claim 1, wherein said polymer material comprises at least one of guar, hydroxypropyl guar, hydroxyethyl cellulose, or a mixture thereof
7. The method of claim 1, wherein said polymer material comprises guar particles having a size of between about 100 mesh and about 325 mesh.
8. The method of claim 1, wherein said derivatizing agent comprises at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof
9. The method of claim 1, wherein said derivatizing agent comprises at least one of alkali metal haloacetate, haloacetic acid, or a mixture thereof
10. The method of claim 1, wherein said derivatizing agent comprises at least one of sodium chloroacetate, sodium bromoacetate, chloroacetic acid, bromoacetic acid, propylene oxide, or a mixture thereof
11. The method of claim 1, wherein said derivatizing agent comprises at least one of sodium chloroacetate, chloroacetic acid or a mixture thereof /
12. The method of claim 1, wherein said polymer material comprises guar ; wherein said derivatizing agent comprises sodium chloroacetate, chloroacetic acid, or a mixture thereof ; and wherein said derivatized polymer material comprises carboxymethyl guar.
13. The method of claim 1, wherein said combining a polymer material with an organic solvent to form a polymer-containing slurry comprises dispersing from about 15% to about 50% powdered guar by weight of polymer to weight of final polymer slurry in said hydrocarbon solvent, and wherein said step of combining said polymer-containing slurry with a derivatizing agent comprises adding between 6% and about 30% by weight chloroacetate by weight of polymer to said polymer-containing slurry.
14. The method of claim 1, further comprising combining a viscosifier and a dispersant with said organic solvent prior to combining a polymer material with said organic solvent to form a polymer-containing slurry.
15. The method of claim 14, wherein said viscosifier comprises organophilic clay and said dispersant comprises an ethoxylated alcohol.
16. The method of claim 1, wherein said well penetrates a subterranean formation and wherein said introducing comprises injecting a contents of said hydrated derivatized polymercontaining treatment fluid into said subterranean formation at a pressure above a fracturing pressure of said subterranean formation.
17. The method of claim 1, further comprising combining said hydrated derivatized polymercontaining treatment fluid with a crosslinking agent, wherein said crosslinking agent and said derivatized polymer material react to form crosslinked derivatized polymer material contained in said treatment fluid.
18. The method of claim 1, further comprising:
combining said polymer-containing slurry with a basic compound or alkaline material prior to combining said polymer-containing slurry with said derivatizing agent ; and combining said derivatized polymer-containing slurry with an acidic agent or compound prior to said introducing.
19. The method of claim 18, wherein said polymer material comprises polymer particles having a size of between about 38 um and about 600 um, and further comprising the steps of : combining said derivatized polymer-containing slurry with an aqueous solution to form a treatment fluid after exposing said derivatized polymer to said acid ; and wherein said step of introducing comprises injecting said treatment fluid into said subterranean formation at a pressure above a fracturing pressure of said subterranean formation.
20. The method of claim 18, wherein said organic solvent comprises a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
21. The method of claim 1, wherein said combining said derivatized polymer-containing slurry with an aqueous solution occurs within a process stream in a continuous mixing process, and wherein said introducing includes the step of introducing said process stream into said well immediately after said steps of combining said derivatized polymer-containing slurry with an aqueous solution.
22. The method of claim 1, wherein said polymer-containing slurry is combined with said derivatizing agent onsite.
23. The method of claim 1, wherein said method comprises combining a selected amount of said derivatizing agent with said polymer-containing slurry to produce a derivatized polymer material having a desired degree of substitution value to fit particular wellbore or downhole criteria.
24. The method of claim 1, wherein said first two combining steps occur offsite, and further comprising storing said slurry containing derivatized guar material for transportation and later onsite use.
25. A method for treating a well, comprising: combining a guar material with a hydrocarbon solvent to form a slurry containing guar material; then combining said slurry containing guar material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing guar material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said guar material and said derivatizing agent; allowing said guar material and said derivatizing agent to react to form derivatized guar material contained in said slurry; then combining said slurry containing derivatized guar material with an aqueous solution to form a treatment fluid, wherein said derivatized guar material interacts with said aqueous solution to form hydrated derivatized guar contained in said treatment fluid; and then introducing said treatment fluid into said well; wherein said slurry containing guar material is combined with said basic compound or alkaline material prior to combination of said slurry containing guar material with said derivatizing agent.
26. The method of claim 25, wherein said derivatizing agent comprises sodium chroroacetate, chloroacetic acid, or a mixture thereof
27. The method of claim 25, wherein said derivatizing agent comprises sodium chloroacetate, chloroacetic acid, or a mixture thereof wherein said derivatized guar material comprises carboxymethyl guar ; and further comprising heating said slurry containing guar material to a temperature of between about 20 C and about 90 C prior to said reaction between said guar material and said derivatizing agent.
28. The method of claim 25, wherein said well penetrates a subterranean formation and wherein said introducing comprises injecting said treatment fluid into said subterranean formation at a pressure above a fracturing pressure of said subterranean formation.
29. The method of claim 25, further comprising combining a contents of said treatment fluid containing hydrated derivatized guar with a crosslinking agent, wherein said crosslinking agent and said hydrated derivatized guar react to form crosslinked hydrated derivatized guar.
30. The method of claim 25, wherein said combining said slurry containing guar material with a derivatizing agent includes combining a selected amount of said derivatizing agent with said slurry containing guar material to produce a derivatized guar material having a desired degree of substitution value to fit particular wellbore or downhole criteria.
31, The method of claim 30, wherein said amount of said derivatizing agent is selected to produce a derivatized guar material having a degree of substitution value of between about 0.05 and about 0.25.
32. The method of claim 25, wherein said slurry containing guar material is combined with said derivatizing agent onsite.
33. The method of claim 27, wherein said hydrocarbon solvent comprises at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
34. The method of claim 25, wherein said first three combining steps and said allowing step occur offsite, and further comprising storing said slurry containing derivatized polymer material for transportation and later onsite use.
35. A method for treating a well substantially as herein described with reference to the examples.
36. A method for forming a hydrated derivatized polymer-containing fluid, comprising: combining a polymer material with an organic solvent to form a polymer-containing slurry ; combining said polymer-containing slurry with a derivatizing agent, wherein said polymer material and said derivatizing agent react to form a derivatized polymer containing slurry; and combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form said hydrated derivatized polymer-containing treatment fluid.
37. A method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a derivatizing agent offsite, wherein said polymer material and said derivatizing agent react to form derivatized polymer material contained in said slurry offsite ; and
- storing said slurry containing derivatized polymer material for transportation and later onsite use.
38. The method of claim 37, wherein said method comprises: combining said organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material;
then combining said slurry containing polymer material with said derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to react to form said derivatized polymer material contained in said slurry ; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said first two combining steps and said allowing step occur offsite.
39. The method of claim 37, further comprising: transporting said slurry containing derivatized polymer material to a wellsite ; combining said slurry containing derivatized polymer material with an aqueous solution, wherein said derivatized polymer material interacts with said aqueous solution to form a hydrated derivatized polymer-containing treatment fluid; and introducing said treatment fluid into said well.
40. A method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material ; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and
allowing said polymer material and said derivatizing agent to at least partially react with. no heating to form derivatized polymer material contained in said slurry ; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material
with said derivatizing agent ; wherein said polymer material comprises a hydratable polysaccharide, hydratable derivatized polysaccharide, or a mixture thereof ; and wherein said organic solvent based slurry comprises a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
41. The method of claim 40, wherein said method further comprises combining said derivatized polymer-containing slurry with an aqueous solution, wherein said polymer material interacts with said aqueous solution to form a hydrated derivatized polymer-containing treatment fluid ; and introducing said treatment fluid into a well.
42. The method of c ! ait 40, wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, or a mixture thereof
43. The method of claim 40, wherein said derivatizing agent is combined with said organic solvent in an amount of from 6% to about 30% by weight of said polymer material; and wherein said polymer material comprises guar particles having a size of between about 60 mesh and about 400 mesh.
44. The method of claim 40, wherein said derivatizing agent comprises at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof
45. The method of claim 40, wherein said derivatizing agent comprises at least one of alkali metal haloacetate, haloacetic acid, or a mixture thereof
.
46. The method of claim 40, wherein said derivatizing agent comprises at least one of sodium chloroacetate, sodium bromoacetate, chloroacetic acid, bromoacetic acid, propylene oxide, or a mixture thereof
47. The method of claim 40, wherein said derivatizing agent comprises at least one of sodium chloroacetate, chloroacetic acid or a mixture thereof
48. The method of claim 40, wherein said polymer material comprises guar, wherein said derivatizing agent comprises sodium chloroacetate, chloroacetic acid, or a mixture thereof, and wherein said derivatized polymer material comprises carboxymethyl guar.
49. The method of claim 40, wherein said organic solvent based slurry containing polymer material comprises a viscosifier and dispersant.
50. The method of claim 49, wherein said viscosifier comprises organophilic clay and said dispersant comprises an ethoxylated alcohol.
51. The method of claim 40, further comprising combining said slurry containing derivatized polymer material with an acidic agent or compound after combining said slurry containing polymer material with said derivatizing agent.
52. The derivatized polymer material contained in a slurry and produced by the method of claim 40.
53. A method for forming derivatized polymer material, comprising: combining a polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and
allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material ; wherein said polymer material is combined with said basic compound or alkaline material prior to combination of said polymer material with said derivatizing agent; and wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, or a mixture thereof
54. A method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material contained in said slurry; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said organic solvent based slurry comprises a hydrocarbon solvent that is at least one of diesel, kerosene, refined aliphatic oil, or a mixture thereof
55. The method of claim 54, wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, polyvinyl alcohol, or a mixture thereof
56. A method for forming derivatized polymer material in a slurry, comprising:
combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to at least partially react with no heating to form derivatized polymer material contained in said slurry ; wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said derivatizing agent comprises at least one of alkylene oxide, alkali metal haloacetate, haloacetic acid, or a mixture thereof ; and wherein said polymer material comprises at least one of guar, derivatized guar, derivatized cellulose, starch, or a mixture thereof
57. A method for forming derivatized polymer material in a slurry, comprising: combining an organic solvent based slurry containing polymer material with a basic compound or alkaline material at ambient temperature to activate derivatizing sites on the polymer material; then combining said slurry containing polymer material with a derivatizing agent at ambient temperature to cause at least partial mixing to occur between said polymer material and said derivatizing agent; and allowing said polymer material and said derivatizing agent to react to form derivatized polymer material contained in said slurry;
- 3wherein said slurry containing polymer material is combined with said basic compound or alkaline material prior to combination of said slurry containing polymer material with said derivatizing agent; and wherein said organic solvent based slurry containing polymer material further comprises a viscosifier and dispersant.