GB2047721A - Coating composition - Google Patents
Coating composition Download PDFInfo
- Publication number
- GB2047721A GB2047721A GB8012249A GB8012249A GB2047721A GB 2047721 A GB2047721 A GB 2047721A GB 8012249 A GB8012249 A GB 8012249A GB 8012249 A GB8012249 A GB 8012249A GB 2047721 A GB2047721 A GB 2047721A
- Authority
- GB
- United Kingdom
- Prior art keywords
- weight
- percent
- trade mark
- melamine
- silane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
An aqueous coating composition is based on a mixture of melamine- formaldehyde resin, a colloidal silica and a mono-organo trialkoxy- or trialkoxyalkoxy- silane in a solvent system consisting of water and a water- miscible organic solvent and including a curing agent. When cured the coating composition forms an abrasion- resistant coating material for solid substrates.
Description
SPECIFICATION
Coating composition
This invention relates to a coating composition and, in particular, to an aqueous coating composition suitable for coating substrates to renderthe substrates abrasion-resistant. Even though the primary objective is to obtain a coating which is extremely difficult to abrade, it is often the case that one has to balance other factors against such an objective in order to obtain a coating which is commercially acceptable. For example, abrasion-resistant coatings are available which give the ultimate in abrasionresistance but they are expensive and quite often do not exhibit good adhesion on solid substrates. There are other coatings, however, that have excellent adhesion on solid substrates but these lack good abrasion resistance. Other coatings lack flexibility but are economical.
Generally, the coatings available today enjoy limited commercial success because they are economical but do not have all of the properties needed for good abrasion-resistance coatings.
Generally good abrasion resistant coatings have been described in U.S. Patent No. 3,986,997 which consist of an aqueous solution of a colloidal silica and a hydrolyzable alkyl silane. These coatings are excellent coatings but tend to be somewhat expensive. On the other hand, there are less expensive coatings based on urethanes but they do not have good abrasion-resistant properties.
Melamines have been known for some time, mostly as crosslinking additives for urethane polymers and other organic polymers. Just recently, the melamines have been used in larger proportions in polymeric mixtures. For example, in French Patent No. 2,194,734, alkyd resins (caster oil-modified), methacrylate/ vinyltoluene copolymers with hexakis-(methoxymethyl)melamine were used as coatings to give improved surfaces.
Melamines have also been mixed with alkoxysilanes and cured onto substrates as coatings as shown in
German Patent Publication No. 2,436,191. The coatings were claimed to have good resistance to chemicals and abrasion. The melamine is claimed also to give increased adhesion compared to the same coatings without the melamine. Similar coatings were prepared using mixtures of siloxanes and alkylated melamine-formaldehyde polymers.
Several coatings have been prepared which contain, in addition to the melamine, silicates which are prepared utilizing several different starting materials, for example, tetraalkoxysilanes shown in Japanese
Patent Publication No.80175/1973; silicic acid as shown in Swiss Patent No.545,835; ethylsilicate as shown in Japanese Patent Publication No. 41431/1974; and silica sols as shown in Japanese Patent Publication No.
58732/1977.
None of these references, however, describe the type of coating one would expect by including both colloidal silica and a hydrolyzable silane in a curable melamine resin. The present invention is based on such a combination.
We have discovered an economical, abrasion resistant coating that gives good adhesion to most solid substrates. The coating comprises melamine-formaldehyde resins, colloidal silica and hydrolyzable alkylsilanes, which results in better abrasion resistance with concurrent adhesion to solid substrates than those melarnine coatings containing either the colloidal silaca of the hydrolyzable alkylsilane by themselves.
Thus, the present invention provides an aqueous coating composition consisting of (A) 10-95 percent by weight, based on the weight of components (A), (B) and (C) of a melamine
formaldehyde resin; (B) 5-90 percent by weight, based on the weight of components (A), (B) and (C) of a colloidal silica; (C) 0.5-10 percent by weight, based on the weight of (B) and (C) of a silane having the general formula:RSi (OR')3 wherein R is selected from methyl, ethyl, vinyl, gamma-chloropropyl, gamma
methacryloxypropyl, gamma-gylcidoxypropyl and mercaptopropyl; R' is an alkyl group having 1-4
carbon atoms or an alkoxy-alkyl radical wherein the alkyl group has 1 or 2 carbon atoms; (D) 50-90 weight percent, based on the weight of (A), (B), (C) and (D) of water and a water miscible organic
solvent selected from lower aliphatic alcohols, ketones, esters, glycols, glycol ethers and glycol esters
wherein 1-70 weight percent of (D) is water and, (E) 1-10 percent, based on the weight of (A) of a curing agent.
According to the invention, component (A) is a melamine-formaldehyde resin common to those skilled in the art. Such resins are well known in the chemical arts and do not need elaborate discussion herein. Those resins preferred to this invention are those having the general formula:
wherein R1 and R2 are selected from hydrogen, -CH2OH, -CH2OR" wherein R" is an alkyl group of 1-4 carbon atoms. R1 and R2 may each be selected independently from the above groups and R1 and R2 may be the same or different. Such commercial melamine res: Fq are, for example, a series of resins manufactured by the
American Cyanamid Company, Wayne, New Jersey, U.S.A., and sold underthetradename Cymel (Trade
Mark).
Component (A) is utilized at 10-95 percent by weight based on the weight of components (A), (B) and (C) in the composition. Preferred amounts are from 40 to 60 percent by weight.
The second component of the composition according to the invention, component (B) is a colloidai silica.
These colloidal silicas have particle sizes in the range of 1-100 mu and can be either acidic or basic. These colloidal silicas are commercially available and specific examples of such commercial colloidal silicas are those sold under the tradenames Ludox (Trade mark) AS-40, Nalcoag (Trade Mark) 1030 and Nalcoag (Trade
Mark) 1034A.
The colloidal silica is present in the invention composition from 5-90 weight percent of the total solids in the composition. The preferred amount if from 30-70 weight percent.
Component (C) is a silane. Silanes useful in this invention have the general formula RSi(OR')3 wherein R and R' are as previously defined. Specific examples where R' is an alkoxyalkyl radical are -CH2OCH3, -CH2CH2OCH3, -CH2OCH2CH3, -CH2OCH2CH2CH3 and -CH2OCH2CH2CH2CH3.
The silanes of component (C) are present in the composition from 0.5-10 percent by weight based on the weight of (B) and (C) in the composition. The preferred amount of silane present in the composition is 2 to 6 weight percent.
Component (D) of the inventive composition is water and a water miscible organic solvent selected from lower aliphatic alcohols, ketones, esters, glycols, glycol ethers and glycol esters. By "lower" we mean organic aliphatic alcohols having 1-4 carbon atoms. Examples of useful ketones are acetone, methyl ethyl ketone and methyl iso-butyl ketone. Examples of useful esters are ethyl acetate and methyl acetate. By the use of the term "glycols", we mean organic polymeric materials that have been prepared from alkylene oxides and which have molecular weights sufficiently low to be liquids at room temperature. Specific examples of glycols useful in this invention are ethylene glycol and diethylene glycol.
Glycol ethers are those solvents composed of low molecular weight polymeric materials described as glycols, above, which have ether end caps. Examples of materials useful in this invention are ethylene glycol monomethyl ether and ethylene glycol monoethyl ether.
Glycol esters are similar to glycol ethers but instead of ether end caps, they have ester end caps. An example of such a solvent is 2-hydroxy ethyl acetate.
Component (D) is used in this invention from 50-90 weight percent based on the weight of (A), (B), (C) and (D) components in the invention. Preferred amounts for this invention are from 50 to 70 weight percent.
The proportion of water in the aqueous compositions is dependent on the water-miscible solvents used, the type of melamine resin used and the type of silanes. Generally, the water can be present from 1-70 weight percent of the non-solids present in the composition. Thus, the water-miscible solvents present in the non-solids portion of the composition should be from 39-99 weight percent. Preferably, the non-solids portion of the composition should contain less than 50 weight percent water.
Another component of this invention, component (E), is a curing agent for the melamine.
In some cases where an acidic colloidal silica sol is used as the starting material, there is enough residual acid to give the final composition cureability. Generally, however, additional curing agents are required, especially if the end application requires accelerated cure. The usual curing agents for curing melamineformaldehyde resins can be used in this invention. Such curing agents are for examplep-toluenesulphonic acid; inorganic mineral acids such as hydrochloric acid; organic acids such as acetic acid; amine salts (e.g., NH4CI) and metal salts (e.g. Al(NO3)3).
Generally, 1-10 weight percent of curing agent is required in this invention, based on the amount of melamine resin used (melamine solids). Greater amounts can be used but serve no useful purpose and are uneconomical. Examples of commercially available curing agents are
Catalyst 4040 (Trade Mark) p-toluene sul- 40% in isoprop
phonic acid panol
Cycat (Trade Mark) 296-9 Alkyl phos- 50% in iso
phoric acid butanol
Cycat (Trade Mark)600 liquid org- 70% in iso
anicacid propanol
All are available from American Cyanamid Company, Industrial Chemicals Division, Resins Department.
The total solids in the composition according to the invention ranges from 10-50 weight percent based on the total composition. Preferred for most applications is a range of 20-35 weight percent for best results.
Generally, the manner in which the components are mixed together is not critical because the cure to achieve the final coating is not spontaneous, that is, the coatings have to be heated to cure them.
Thus, a preferred method is to add the desired silane i.e., component (C) to a given quantity of component (B) while stirring. In order thoroughly to hydrolyze the silane and make the mixture of components (B) and (C) homogeneous, the mixture is generally stirred for a few minutes to a few hours. Generally, the mixture is homogeneous in 1 hour or less. Then a second solution is prepared which contains the melamine resin dissolved by simple mixing in the desired water miscible solvents. Finally, the two solutions are mixed together with enough mixing to homogenize them, the curing agent is stirred in and homogenized.
The coating is then coated on a substrate using conventional means appropriate to the particular substrate. For example, one can use dip coating, flow coating, spin coating or a spraying technique.
The coatings are then cured by heating them to elevated temperatures. Generally, the time and temperature of cure are dependent on the ultimate composition according to the invention. Especially important are the type of melamine resins used and the type of catalysts used. Generally, the coatings can be cured, to give good properties, at temperatures ranging from 75 to 200 C. Most preferred are temperatures ranging from 90 to 1 1 5"C. The time of cure is dependent upon the temperature utilized. Generally, from 2 to 24 hours is sufficient for good cure. Preferred are 8 to 16 hours for optimum performance of the coating.
Generally, primers can be used on the substrates to enhance the adhesion of the coatings. The priming is not generally needed with the composition according to the invention but under certain circumstances, it may be required.
Other optional components may be added to the inventive composition in order to enhance other needed properties. For example, ultraviolet stabilizers are often required on some transparent plastic applications and any ultraviolet stabilizer which is compatible with the composition is acceptable. Other materials such as pigments, fillers and dyes may also be added to the composition.
The following examples and samples are included to further illustrate the invention. Whenever used herein, the abbreviations Ph, Me, Et, Vi and Bu mean phenyl, methyl, ethyl, vinyl and butyl respectively.
The abrasion resistance was determined according to ASTM Method D1044-76. The instrument was the
Tabor Abraser. A 500 gram test load was used with CS-1 OF abrasive wheels and the test panels containing the coatings were subjected to 500 revolutions on the abraser turntable. The percent change in haze which is the criterion for determining the abrasion-resistance of the coating is determined by measuring the difference in haze of the unabrased and abrased coatings. Haze is defined as that percentage of transmitted light which in passing through the specimen deviates from the incident beam by forward scattering. In this method, only light flux which deviates more than 2.5 degrees on the average is considered to be haze. The A haze on the coatings was determined by ASTM Method D1003-61. A Hunter Haze Meter, Gardner Laboratory,
Inc. was used.The A haze was calculated by measuring the amount of diffused light, dividing by the amount of transmitted light and multiplying by one hundred.
Adhesion was measured by the Crosshatch Adhesion Test wherein a 1 inch square portion of the cured coating was scored to give a 1/8 inch grid. Adhesive tape (No. 600 adhesive sold by the 3M Company, St.
Paul, Minnesota, U.S.A.) was pressed onto the grid and removed quickly. The adhesion of any portion of the grid coat is reported in percent adhesion.
Silanes
Ill (CH30)3Si(CH2)3SH
IV (CH30)3SiCH3
V (CH30)3Si(CH2)3CI
VI (CH30)3SiCH=CH2
VII (CH30)3Si(CH2)3SCH2CH(CH2H)2
VIII (CH3O)3Si(CH2)2SCH2COOH
Melamine Resins
All information on Cymel (Trade Mark) resins used in this invention can be found in a publication entitled "Resinews", American Cyanamid Co., May, 1977. Uformite MM83 is a product manufactured by the
Reichhold Chemical Company. Uformite MM83 is a melamine-Formaldehyde resin, 78-82% non volatiles in isopropanol/isobutanol.
Example 1
Two dispersions were prepared:
Dispersion A: Silane 1(2.4 grams) was added slowly with stirring to a colloidal silica which was about 34% SiO2, 20 mu particle size and had a pH of 3.2 which had been placed in a 250 ml. glass beaker. The dispersion was stirred for one hour after all the silane had been added. The dispersion was homogeneous.
Dispersion B: Cymel (Trade Mark) 303 was dissolved, with stirring, in a solvent solution consisting of 2:1 weight ratio of isopropanol and n-butanol to give a 25 weight percent solids dispersion.
The coating composition consisted of mixing 14:7 grams of Dispersion A and 20 grams of Dispersion B and an additional 5.7 grams of a 2:1 weight ratio of isopropanol/n-butanol. After thorough mixing, 0.13 grams of para-toluene sulfonic acid (Catalyst 4040 Trade Mark) was added and the mixing continued until the whole composition was homogeneous. This material was designated la. Similar compositions were prepared in essentially the same manner as set forth above except that the type of silane and the quantity were changed. These examples are set forth on Table I with the results from abrasion testing.The compositions in Example 1 were cured at 110"C for 16 hours after being coated onto 10.2 cm x 10.2 cm x 0.64 cm. polycarbonate panels by a flow coating technique which consisted of puddling the solution on the panel, spreading the solution to the edges and draining the excess by standing the panel on end. The polycarbonate paneling (Lexan (Trade Mark)) was manufactured by General Electric Co., Pittsfield,
Massachusetts.
Example 2
In this example, Uformite MM83 was substituted for the Cymel (Trade Mark) resin in Example 1. Therefore for purposes of this example, Dispersion B was prepared by mixing 62.5 grams of Uformite MM83, 50 grams of n-butanol and 87.5 grams of isopropanol. This change in solvent weight was due to the fact that MM83 is supplied as approximately 80% solids in isopropanol/isobutanol. These compositions were coated onto polycarbonate panels as was done in Example 1 and cured for 16 hours at 1 100C. The results can be found in
Table
Example 3
The samples of this example were prepared as in Example 1 (b) except the melamine resin was Cymel
(Trade Mark) 370. The curing agent was Cycat (Trade Mark) 296-9 and the cure was 110 C for 16 hours. The
results can be found in Table I.
Example 4
This example was carried out as shown in Example 3 except the melamine resin was Cymel (Trade Mark) 325. The results can be found in Table I.
Example 5
This was the same as Example 1 except the resin was Cymel (Trade Mark) 385 and the curing agent was
Cycat (Trade Mark) 296-9. The results can be found on Table I.
Example 6
Dispersions were prepared essentially as in Example 1 (b) except that the ratio of melamine solids (using
Cymel (Trade Mark)303) to the silica/silane solids was varied from 100:0 to 10:90. The total solids was
maintained at 25 percent in a 2:1 weight ratio of isopropanol/n-butanol solvents. Catalyst 4040 (Trade Mark),
was added at 1% based on the melamine resin weight. The dispersions were coated on polycarbonate panels
and cured 16 hours at 1 10"C. The panels were abraded and the results are shown in Table II.
TABLE II
% A Haze on Samples, Example 6
Sample Melamine/SiO2 % A Haze
6a 50:50 5.0
6b 70:30 8.6
6c 90.10 12.4
6d 100:0 18.2
Example 7
Example 1 (b) was repeated except that the solvents and solvent combinations were changed as shown in
Table Ill.
Example 8
This example was carried out to determine if the method of formulation was critical. Uformite MM83 was
the melamine resin and the silane was silane II.
Method:
I The silane and melamine (25% in 2:1 IPA/BuOH, weight basis) were added simultaneously to the
silica.
II The silica/silane were mixed together and then homogenized. The melamine was added to the
silica/silane after the silica/silane was aged for one hour.
Ill The silica and melamine were mixed and aged one hour. The silane was then added.
In each method, the melamine/silica ratio was 50:50 and total solids was 25% in 2:1 IPA/BuOH weight ratio.
Catalyst 4040 (Trade Mark) was added at 1% of the melamine weight. The materials were flow coated on polycarbonate panels and cured for 16 hours at 110"C. The results are shown on Table IV.
Examle 9
This example shows the effect of the concentration of curing agent versus film abrasion resistance. The results are in Table V.
This material was prepared as in Example 2(b) except that the solvent was a 50/50 weight percent mixture of isopropanol/butylcellosolve. The catalyst was Cycat (Trade Mark) 296-9 and was added at 0-10% of the melamine weight.
Also in this example, the effect of different curing agents was tested using Catalyst 4040 (Trade Mark) and
Cycat (Trade Mark) 600 which were added at 2 weight percent based on the melamine present. The samples were cured at 110 C for 16 hours after flow coating on polycarbonate panels.
Example 10
The effect of varying silane content on film hardness was studied. The resin used was MM83 and the catalyst was Catalyst 4040 (Trade Mark). The preparation of the examples was carried out as in 1 (b) except that the total solids was 34% in butyl cellosolve. The catalyst was added at 1% of the melamine resin weight.
Polycarbonate sheets, Lexan (Trade Mark), were flow coated and cured overnight at 110 C. The results are given in Table VI.
TABLE VI
Type of
Sample % silane Silane % A Haze
a 0 None 9.6
b 2.49 VI 8.2
c 5.00 VI 2.6
d 7.49 VI 6.6
e 9.99 VI 8.2
f o None 9.3
g 2.47 Ill 7.0
h 5.03 III 6.4
7.49 Ill 5.0
10.01 III 7.4
Example 11
The curing conditions of the various combinations of silanes and a melamine resin were studied. The
melamine was used in a 50:50 ratio with the colloidal silica and the silanes were added at 5 weight percent of the colloidal silica present. Catalyst 4040 (Trade Mark) was added to each sample at 1 weight percent based
on the melamine resin present. The solutions were coated on polycarbonate sheet, Lexan (Trade Mark), by a flowcoat method. The results are on Table VII.
TABLE VII
Cure Time/ Type
Sample Temp. Silane A Haze
a 16 hr. Ill 3.9
b 16 hr. Ill 4.2 c 8 hr. III 4.9
d 4hr. Ill 4.3
e 2 hr. Ill 11.9
f 16 hr. I 3.8
g 16 hr. 4.0 h 8hr. I 5.4
4hr. I 7.4
2hr. I 11.1
Example 12
This experiment shows the effect of varying the type of melamine resin. The samples were prepared
essentially as in Example 11. The samples were cured at 110 C. for 16 hours after coating on polycarbonate
Lexan (Trade Mark) sheets. The catalyst was indicated in the table below and was used at 1% based on the melamine resin present. The melamine/colloidal silica ratio was 50:50 and 5% of the silane based on the amount of colloidal silicas was used.
Type
Sample Melamine Silane % %AHaze a Cymel (Trade Mark) 303 (') IV 6.1 b Cymel (Trade Mark) 385 (2) IV 4.0 c Cymel (Trade Mark) 370 (2) IV 4.2 d Cymel (Trade Mark) 325 (2) IV 3.4 1)Catalyst 4040 (2)Cywat 296-9
Example 13
This example was carried out to show that the source of silica for the composition according to the invention is critical. Experiments were carried out in which the silica was colloidal silica obtained according to the specification herein. Another silica was obtained by hydrolyzing ethylorthosilicate: ethylsilicate, (EtO)4Si, where EtO is ethoxy, was hydrolyzed using 100 grams of (EtO)4Si, 70 grams of isopropyl alcohol and 30 grams of 0.65 N HCI wherein the three were mixed together and stirred until homogeneous.One-half of this hydrolyzate was used fresh and the other one-half was aged for one month. The solids content of these solutions was 14.5%. These materials were designated 1 a and 1 b respectively. A second material was prepared from a material manufactured by the Nalco Chemical Co., Chicago, Illinois, U.S.A., and sold under the tradename Nalcoag (Trade Mark) 1034A (34% SiO2 in water) by simple dilution with alcohol to 14.5% solids. This material was designated II (See below). A third material was prepared from Nalcoag (Trade
Mark) 1129 by diluting to 14.5% solids. This material was designated Ill (see below).
42.6 grams Nalcoag (Trade Mark) 1034A 48.3 grams Nalcoag
(Trade Mark) 1129 32.0 grams Isopropyl alcohol 14.7 grams Isopropyl
alcohol 25.4 grams ethanol 37.0 grams ethanol
Note that Nalcoag (Trade Mark) 1129 is 30% SiO2 in a 60:40 mixture of isopropanol and water.
Cymel (Trade Mark) 303 was dissolved in butyl cellosolve at 25% solids.
Using the above solutions, several samples were prepared, coated on polycarbonate panels, cured at 11 0 C for 16 hours, and evaluated to show the difference in the source of "SiO2". The catalyst was Catalyst 4040 (Trade Mark) and was used in 0.6 grams in each sample. The results are shown in Table VIII.
Note that samples g and h fall within the scope of this invention and samples a-f do not. It can be observed that the compositions according to the invention give superior results compared to the prior art.
Example 14
The materials of this invention were compared with U.S. Patent 3,935,345 for abrasion resistance of cured coatings. Since the concept of adding larger quantities of melamine resins (other than crosslinker quantities) to siloxanes has been shown in the above patent, it follows that these materials should be compared to the materials of the instant invention to show the advantages of including colloidal silica in the coating formulation.
The materials were prepared following Example 1 of the U.S. Patent No. 3,935,346. The materials were coated and cured according to the patent and then evaluated by the abrasion test described in this specification. All A haze readings on the patented compositions were between 20 and 25 as compared to samples g and h in Example 13 above.
Example 15
In this example, the effect of varying the ratio of melamine resin to silica content was evaluated. The silane used in all cases was CH3Si(OCH3)3 and was used at 5% of the silane/silica solids. Two solutions were prepared:
Solution A was Cymel (Trade Mark) 303 diluted to 25% solids resin with 1:1 weight ratio of isopropanol/2-butoxyethanol.
Solution B was 95 parts (solids) of the colloidal silica of Example 1 and 5 parts of CH3Si(OCH3)3.
After mixing, samples 2 through 6 were diluted to 25% total solids with 1:1 isopropanol/2-butoxyethanol.
All solutions were catalyzed with Cycat (Trade Mark) 600 at 2% of the melamine solids weight. The solutions were well mixed and filtered through a 1.2 micron filter. Each. sample was flow coated on two separate polycarbonate panels measuring 0.32 cm x 10.2 cm x 10.2 cm. that had been cleaned with hexane and butanol and which had been heated for one hour at 1200C and cooled before coating. After coating, the panels were air dried and then heated 16 hours at 1 OO"C. The following table shows the results of adhesion and abrasion resistance testing.
Sample No. % adhesion % A haze
1 100 18.7
2 100 10.9
3 100 7.1
4 > 90 4.4
5 25 7.0
6 (1) (1) (1) the coating was flaky and could be rubbed off the panel.
Example 16
Solutions were prepared similarly as in Example 1 except the type of silane used in Solution A was either
VI or VII. The colloidal silica was the same as was used in Example 1. Cymel (Trade Mark) 303 was the melamine resin, the solvents were isopropanol and butyl-cellosolve and catalyst was Catalyst 4040 (Trade
Mark). The quantities of each are shown in the following table and the isopropanol/butylcellosolve was a 50/59 weight ratio mixture. Panels of polycarbonate 0.32 cm. x 10.2 cm. x 10.2 cm. were flow coated after being cleaned and treated similar to the panels in Example 15. The panels were flow coated and then air dried and then cured 16 hours at 1000C. Samples 2,4,6,8 are duplicate panels of 1,3,5 and 7 respectively.
TABLE I
Abrasion Resistance
Control was uncoated polycarbonate sheet
Example Silane %# Haze
Control --- 25.0 1a I 3.1 1b II 4.5 1c III 5.0 1d IV 4.7 le V 1f VI 1.6 1g VII 6.0 1h VIII 4.1 2a 1 3.0 2b 11 2.9 2c III 2.3 2d IV 3.2 2e V 6.2 2f VI 2.6 3a 1 6.3 3b 11 3.0 3c III 3d IV 4.8 3e V 3f VI 4a 4b II 4c III 4d IV 2.2 4e V 4f VI 5a I 4.0 5b II --5c III --5d IV 5.0 5e V --5f VI --
TABLE Ill
Results of Abrasion Resistance Testing, Example 7
(IPA is isopropanol and BuOH is n-butanol)
Solvents/
Sample Melamine ratios Silane 7a Cymel (Trade Mark) 303 IPA/BuOH 2:1 11 7b " butyclcellosolve II 7c " Butylcellosolve/lPA II
1::1
Sample %#Haze %Adhesion
7a 7.4 100
7b 6.8 100
7c 4.5 95
TABLE IV
Sample Silane Method Melamine %Adhesion %AHaze 8a II 1 Uformite MM83 100 5.4 8b 11 2 " 100 7.3 Sc 11 3 " 100 7.0
TABLE V
Sample Curing Agent % % A Haze
a Catalyst 4040 0 10.4
(Trade Mark)
b " 1 6.8
c " 3 7.3
d " 5 2.9
e " 5 3.6
f " 7.5 4.9
g " 10 4.3
h " 2 6.7
Cycat (Trade 2 5.0
Mark) 600
Catalyst 4040 2 6.0
(Trade Mark)
k Cycat (Trade 2 4.7
Mark) 600
TABLE VIII
Sample Grams IA grams IB grams II grams lil a 20 --b --- 20 c --- --- 20 d --- --- --- 20 e 20 --- --- --f --- 20 9 20 h --- --- -- 20
grams Silane III
Sample Cymel 303 grams % A Haze a 12.2 0 Coating Flaked off b 12.2 0 c 12.2 0 15.7 d 12.2 0 6.8 e 12.2 0.3 Coating Flaked off f 12.2 0.3 g 12.2 0.3 1.4 h 12.2 0.3 2.7
Ratio
Sample No. melamine resin/ Grams Sol. A Grams Sol. B silica 1 100/0 16 2 90/10 18 1.4 3 70/30 28 8.4 4 50/50 20 14.1 5 30/70 12 19.7 6 20/80 8 22.5
gms gms gms/lPA gms
Sample No. Silica Cymel 303 Butylcellosolve Catalyst 4040 1 14.7 21 5,8 .1 2 14.7 21 5.8 .1 3 14.7 21 5.8 .1 4 14.7 21 5.8 .1 5 14.8 21 5.8 .1 6 14.8 21 5.8 .1 7 14.7 16.7 8.5 .1 8 --- --
gms gms gms
Sample No. Silane IV Silane VIII 1 --- --- .35 2 --- --- .35 3 0.5 --4 0.5 5 --- --- 0.6 6 --- 7 --- 1.75 8 ---
Claims (5)
1. An aqueous coating composition comprising: (A) 10-95 percent by weight, based on the weight of components (A), (B), and (C) of a melamine
formaldehyde resin; (B) 5-90 percent by weight, based on the weight of components (A), (B) and (C) of a colloidal silica; (C) 0.5-10 percent by weight, based on the weight of (B) and (C) of a silane having the general formula::
RSi(OR')3
wherein R is selected from methyl, ethyl, vinyl, gamma-chloropropyl, gamma-methacryloxypropyl,
gamma-glycidoxypropyl and mercaptopropyl;
R' is an alkyl group having 1-4 carbon atoms or an alkoxyalkyl radical wherein the alkyl group has 1 or 2
carbon atoms; (D) 50-90 weight percent, based on the weight of (A), (B), (C) and (D) of water and a water-miscible organic
solvent selected from lower aliphatic alcohols, ketones, esters, glycols, glycol ethers and glycol esters
wherein 1-70 weight percent of (D) is water and, (E) 1-10 percent, based on the weight of (A) of a curing agent.
2. An aqueous coating composition as claimed in claim 1, wherein (A) is present at 40 to 60 percent by weight; (B) is present at 30 to 70 weight percent; (C) is present at 2 to 6 weight percent; (D) is present at 50 to 70 weight percent and contains 50 weight percent water and, (E) is present at 1 to 10 weight percent.
3. An aqueous coating composition as claimed in claim 1, substantially as herein described with reference to any of the specific Examples.
4. A solid article coating with an aqueous coating composition as claimed in any of claims 1 to 3.
5. An article as claimed in claim 4 wherein the coating has been cured.