GB1261432A - Production of ceramic components from stabilised zirconium dioxide - Google Patents

Production of ceramic components from stabilised zirconium dioxide

Info

Publication number
GB1261432A
GB1261432A GB08337/69A GB1833769A GB1261432A GB 1261432 A GB1261432 A GB 1261432A GB 08337/69 A GB08337/69 A GB 08337/69A GB 1833769 A GB1833769 A GB 1833769A GB 1261432 A GB1261432 A GB 1261432A
Authority
GB
United Kingdom
Prior art keywords
cao
per cent
zro
sio
mgo
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB08337/69A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Evonik Operations GmbH
Original Assignee
Degussa GmbH
Deutsche Gold und Silber Scheideanstalt
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Degussa GmbH, Deutsche Gold und Silber Scheideanstalt filed Critical Degussa GmbH
Publication of GB1261432A publication Critical patent/GB1261432A/en
Expired legal-status Critical Current

Abstract

1,261,432. Stabilized zirconia. DEUTSCHE GOLD - UND SILBER - SCHEIDEANSTALT. 10 April, 1969 [27 April, 1968], No. 18337/69. Heading C1J. Stabilized zirconium dioxide is made by heating at 1100-1300‹ C. a mixture of equimolecular amounts of ZrO 2 and CaO with Al 2 O 3 and/or iron oxide and/or SiO 2 and optionally MgO and excess CaO, mixing the intermediate product with more ZrO 2 to reduce its alkaline earth metal content to 10-30 mol. per cent, moulding and sintering at 1600- 1900‹ C. The amount of Al 2 O 3 and/or iron oxide and/or SiO 2 used is at least that necessary to combine any CaO or MgO not combined with the ZrO 2 . The intermediate product contains 0À2 to 20 wt. per cent Al 2 O 3 and/or iron oxide and/or SiO 2 , 0À05-8 wt. per cent MgO and 21-33 wt. per cent CaO and is fine-grained, friable and readily crushed and passed through a 35Á screen. An aqueous solution of a cellulose ether is used as a moulding aid. Instead of oxides, compounds, e.g. carbonates, which are thermally decomposed to the oxides can be used.
GB08337/69A 1968-04-27 1969-04-10 Production of ceramic components from stabilised zirconium dioxide Expired GB1261432A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE1771273A DE1771273C3 (en) 1968-04-27 1968-04-27 Process for the production of ceramic parts from stabilized zirconium oxide

Publications (1)

Publication Number Publication Date
GB1261432A true GB1261432A (en) 1972-01-26

Family

ID=5700807

Family Applications (1)

Application Number Title Priority Date Filing Date
GB08337/69A Expired GB1261432A (en) 1968-04-27 1969-04-10 Production of ceramic components from stabilised zirconium dioxide

Country Status (3)

Country Link
DE (1) DE1771273C3 (en)
FR (1) FR2007089A1 (en)
GB (1) GB1261432A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0114655A1 (en) * 1983-01-21 1984-08-01 Feldmühle Aktiengesellschaft Piston ring for an internal-combustion engine

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2714558A1 (en) * 1977-04-01 1978-10-12 Bosch Gmbh Robert SINTER-ACTIVE, HIGH-STRENGTH ZIRCONIA CERAMICS
DE2810134A1 (en) * 1978-03-09 1979-09-20 Bosch Gmbh Robert ZIRCONIUM OXIDE CERAMICS WITH A FINE-GRAY AND THERMALLY STABLE STRUCTURE AND HIGH THERMAL SHOCK RESISTANCE, MOLDED BODIES MANUFACTURED FROM THEM, METHOD FOR MANUFACTURING THE MOLDED BODIES AND THEIR USE
DE2858801C2 (en) * 1978-03-09 1991-08-01 Robert Bosch Gmbh, 7000 Stuttgart, De Zirconia ceramic for use as solid electrolyte
FR2633611B1 (en) * 1988-07-01 1991-05-10 Vesuvius France Sa MATERIAL FOR COVERING OF A CASTING MEMBER
US5151201A (en) * 1988-07-01 1992-09-29 Vesuvius Crucible Company Prevention of erosion and alumina build-up in casting elements
DE4116732A1 (en) * 1991-05-23 1992-11-26 Abb Patent Gmbh METHOD FOR PRODUCING POROESIC CERAMIC PARTS
DE102012003483B3 (en) 2012-02-21 2013-02-21 Technische Universität Bergakademie Freiberg Thermal shock and corrosion resistant ceramic based on calcium zirconate and process for its preparation

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0114655A1 (en) * 1983-01-21 1984-08-01 Feldmühle Aktiengesellschaft Piston ring for an internal-combustion engine

Also Published As

Publication number Publication date
DE1771273B2 (en) 1976-05-06
DE1771273C3 (en) 1978-10-05
FR2007089A1 (en) 1970-01-02
DE1771273A1 (en) 1972-01-05

Similar Documents

Publication Publication Date Title
GB1416730A (en) Method of cementing a ceramic liner in a metal tube
GB1261432A (en) Production of ceramic components from stabilised zirconium dioxide
GB1236905A (en) Improvements in or relating to the manufacture of glass
GB1373634A (en) Preparation of ammonium and potassium zirconium carbonates
FR2223328A1 (en)
GB1281112A (en) A method of preparing catalysts
ES435063A1 (en) Refractory compositions
GB1387468A (en) Basic refractory shapes
GB1176297A (en) Laser Glass Compositions
GB1178825A (en) Improvements in or relating to Dielectric Ceramic Materials
GB1340276A (en) Process for decomposing metallic oxide materials
SU414234A1 (en)
GB1225966A (en)
GB1194515A (en) Aluminous Cement
SU327793A1 (en) METHOD FOR PREPARATION OF MIXED SOLUTION OF TITANIUM CHLORIDES AND ZIRCONIUM
GB1358352A (en) Inorganic antimony-containing compositions
GB1349527A (en) Silica-containing bonding materials
ES390406A1 (en) Zirconium pigments
GB1214361A (en) Improvements in pigments
GB1436586A (en) Ceramic dielectric bodies
ES345803A1 (en) Production of phosphate fertilizers
GB1137576A (en) Improvements in yttrium orthovanadate phosphor
SU77972A1 (en) Method of making ceramic products based on titanium dioxide
GB1296860A (en)
GB1344650A (en) Heat-shock resistant heat-fused refractory products having mgo as a main component