GB1159816A - Process for the Preparation of Shaped Zeolite Bodies. - Google Patents

Process for the Preparation of Shaped Zeolite Bodies.

Info

Publication number
GB1159816A
GB1159816A GB4546166A GB4546166A GB1159816A GB 1159816 A GB1159816 A GB 1159816A GB 4546166 A GB4546166 A GB 4546166A GB 4546166 A GB4546166 A GB 4546166A GB 1159816 A GB1159816 A GB 1159816A
Authority
GB
United Kingdom
Prior art keywords
bodies
hours
reaction mixture
sodium hydroxide
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB4546166A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WR Grace and Co
Original Assignee
WR Grace and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WR Grace and Co filed Critical WR Grace and Co
Publication of GB1159816A publication Critical patent/GB1159816A/en
Expired legal-status Critical Current

Abstract

1,159,816. Shaped bodies containing zeolite A. W. R. GRACE & CO. 11 Oct., 1966 [22 Oct., 1965], No. 45461/66. Heading C1A. A process for preparing shaped bodies containing zeolite A comprises the steps of (a) forming bodies, having the molar composition Na 2. O/Al 2 O 3 = 0À20-0À35, SiO 2 /Al 2 O 3 = 1À8- 2.2, and H 2 O/Al 2 O 3 = 4-8 from sodium hydroxide, water and kaolin-type clay which has been calcined at 550-850‹ C., and hardening these preformed bodies, e.g. at 25‹ C. for 24 hours; (b) forming a reaction mixture, having the overall molar composition Na 2 O/Al 2 O 3 = 1À0-1À6, SiO 2 /Al 2 O 3 = 1À8-2À2, H 2 O/Na 2 O = 12-18, from the hardened bodies, together with additional sodium hydroxide and water; (c) ageing the reaction mixture at 20-55‹ C. for 6 to 80 hours; and (d) heating the reaction mixture at 80-110‹ C., e.g. for 3-12 hours, until zeolite A is formed in the preformed bodies. The bodies are washed to remove all free sodium hydroxide, dried and heated at 400-550‹ C. The bodies may be base exchanged with potassium or calcium.
GB4546166A 1965-10-22 1966-10-11 Process for the Preparation of Shaped Zeolite Bodies. Expired GB1159816A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US50262965A 1965-10-22 1965-10-22

Publications (1)

Publication Number Publication Date
GB1159816A true GB1159816A (en) 1969-07-30

Family

ID=23998677

Family Applications (1)

Application Number Title Priority Date Filing Date
GB4546166A Expired GB1159816A (en) 1965-10-22 1966-10-11 Process for the Preparation of Shaped Zeolite Bodies.

Country Status (3)

Country Link
BE (1) BE688598A (en)
DE (1) DE1567566B2 (en)
GB (1) GB1159816A (en)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4075280A (en) * 1976-09-28 1978-02-21 J. M. Huber Corporation Preparation of improved zeolites
DE2829165A1 (en) * 1978-07-03 1980-01-17 Henkel Kgaa METHOD FOR PRODUCING ALUMOSILICATE GRANULES

Also Published As

Publication number Publication date
BE688598A (en) 1967-03-31
DE1567566A1 (en) 1970-09-10
DE1567566B2 (en) 1978-03-02

Similar Documents

Publication Publication Date Title
GB1328452A (en) Process for preparing shaped articles
SE7513029L (en) REGULATION OF THE BINDING TIME FOR MAGNESIUM OXIDE PHOSPHATE CEMENT
IT973731B (en) PROCEDURE FOR THE PRODUCTION OF PORTLAND CEMENT WITH RAPID SETTING
ZA74835B (en) A process for the production of shaped structures resistant to high temperatures
DE3882056D1 (en) APPLICABLE EPOXY COMPOSITION FOR THE PRODUCTION OF HIGH TEMPERATURE RESISTANT MOLDS.
GB1442484A (en) Process for preparing fire-resisting mouldings
GB1159816A (en) Process for the Preparation of Shaped Zeolite Bodies.
GB1123602A (en) Production of refractory bodies
BR7408941D0 (en) ADJUVANT FOR MORTAR SELF-ALISING PROCESS OF PREPARATION OF THIS ADJUVANT MORTARS CONTAINING A PART OF SUCH ADJUVANT AND COVERINGS OBTAINED FROM SUCH MORTARS
ES433533A1 (en) Granulated fertilizer composition and method for its preparation
GB1520186A (en) Production of alumina and hydraulic cement
GB1447132A (en) Production of porous shaped inorganic structures using gas- laden molecular sieve zeolites
GB1434924A (en) Cementiferous compositions
GB1304442A (en)
GB1341984A (en) Production of synthetic zeolites of faujasite structure
GB1272176A (en) Sand-lime bricks and process for making them
KR890006516A (en) Hydration method of half gypsum
GB1390257A (en) Coloured cement
GB1360872A (en) Cement clinkers and method of making same
SU490781A1 (en) Ceramic mass
SU446486A1 (en) Ceramic mass
SU476224A1 (en) Method for producing high-silicon synthetic zeolite of the faujasite type
GB996894A (en) Production of refractory objects
SU120315A1 (en) Ceramic mass for the manufacture of precision casting rods and similar products
SU460102A1 (en) Ceramic Mold Treatment Solution

Legal Events

Date Code Title Description
PS Patent sealed
PLNP Patent lapsed through nonpayment of renewal fees