FR2772624A1 - Skateboard, snowboard or ski manufacture - Google Patents

Abstract

The procedure consists of applying layers of glass fibre or carbon fibre (2) to a supporting layer or core (1) of polycarbonate, using a resin adhesive to hold them together. The polycarbonate can be in different forms e.g. in sheet or honeycomb form or with a filler of glass fibres or glass fibres and resin. It can be in a single layer or in two layers on either side of glass fibre or carbon fibre layers.

Description

La présente invention concerne une nouvelle conception dans la fabrication de planche à roulettes, surf des neiges, ski, et monoski; elle correspond à la stratification de fibre de verre (ou fibre de carbone) sur un support en polycarbonate, destinée à améliorer les performances de la planche. The present invention relates to a new design in the manufacture of skateboards, snowboarding, skiing, and monoskiing; it corresponds to the stratification of fiberglass (or carbon fiber) on a polycarbonate support, intended to improve the performance of the board.

Les planches traditionnelles possèdent déjà des qualités intéressantes telles qu'une nervosité efficace, un poids diminué. Cependant, elles restent fragiles à l'impact ainsi qu'au vieillissement. De plus une planche classique, très couramment fabriquée avec un noyau bois, n'est pas étanche à l'infiltration d' eau et de neige. Traditional boards already have interesting qualities such as effective nervousness, reduced weight. However, they remain fragile at impact as well as at aging. In addition, a conventional board, very commonly made with a wooden core, is not waterproof against the infiltration of water and snow.

Le dispositif selon l'invention permet d'apporter à une planche une étanchéité et une solidité incomparable de nos jours. Il permet également d' améliorer le phénomène de nervosité d'une planche et d'en diminuer son poids. Il comporte en effet selon une première caractéristique, un support en polycarbonate. L'invention consiste à disposer des couches de fibre de verre (ou de fibre de carbone) sur le support en polycarbonate. La liaison des deux matières est assurée par une résine étudiée pour garantir l'accroche entre polycarbonate et fibre de verre. Selon des modes particuliers de réalisation, le polycarbonate existe sous différentes formes industrielles:
- Le polycarbonate en plaques est plus particulièrement adapté à la fabrication de planche à roulettes car il est indestructible à l'impact.The device according to the invention makes it possible to provide a board with a seal and an incomparable solidity these days. It also improves the nervousness of a board and reduces its weight. According to a first characteristic, it indeed comprises a polycarbonate support. The invention consists in placing layers of glass fiber (or carbon fiber) on the polycarbonate support. The connection of the two materials is ensured by a resin studied to guarantee the bond between polycarbonate and fiberglass. According to particular embodiments, polycarbonate exists in different industrial forms:
- Polycarbonate sheets are more particularly suitable for making skateboards because they are indestructible on impact.

- Le nid d'abeille en polycarbonate est plus adapté à la fabrication de surf des neiges, monoski, ou ski, car on prime la légèreté. - The polycarbonate honeycomb is more suitable for making snowboard, monoski, or ski, because lightness is more important.

- Le polycarbonate chargé fibre de verre permet une accroche maximun entre fibre de verre et polycarbonate chargé fibre de verre, ainsi la délamination est inexistance. - The glass fiber loaded polycarbonate allows maximum grip between glass fiber and glass fiber loaded polycarbonate, so delamination is non-existent.

Observons que, quelque soit sa forme industrielle, le polycarbonate reste indestructible à l'impact, très nerveux, totalement étanche à l'infiltration d'eau et de neige. La fibre de verre peut être dirigée suivant des orientations multiples, et combinée suivant des grammages différents, afin d'améliorer la nervosité et les torsions multidirectionnelles de la planche. Let us observe that, whatever its industrial form, polycarbonate remains indestructible on impact, very nervous, completely waterproof against the infiltration of water and snow. The fiberglass can be directed according to multiple orientations, and combined according to different grammages, in order to improve the nervousness and the multidirectional twists of the board.

Il est à souligner qu'une planche fabriquée grâce à un support polycarbonate stratifié requiert les mêmes techniques de fabrication qu'une planche conçue traditionnellement. It should be noted that a board manufactured using a laminated polycarbonate support requires the same manufacturing techniques as a board traditionally designed.

Toutes les techniques de fabrication existantes dans le domaine de la stratification d'un support classique pour fabriquer un surf des neiges, planche à roulettes, ski, monoski, sont alors utilisables. All the existing manufacturing techniques in the field of the stratification of a conventional support for manufacturing a snowboard, skateboard, ski, monoski, can then be used.

Comme dans la stratification d'un support classique (donnant une planche traditionnelle), il est possible de placer un cadre en carbone (poutre centrale + pourtour extérieur) afin d'améliorer la nervosité de la planche.  As in the stratification of a traditional support (giving a traditional board), it is possible to place a carbon frame (central beam + outer periphery) in order to improve the nervousness of the board.

Les dessins annexés illustrent l'invention
La figure 1 représente, en coupe, le dispositif de l'invention.The accompanying drawings illustrate the invention
Figure 1 shows, in section, the device of the invention.

La figure 2 représente, en coupe, une première variante de ce dispositif.Figure 2 shows, in section, a first variant of this device.

La figure 3 représente, en coupe, une seconde variante de ce dispositif.Figure 3 shows, in section, a second variant of this device.

La figure 4 représente, en coupe, une troisième variante de ce dispositif.Figure 4 shows, in section, a third variant of this device.

En référence à ces dessins, le dispositif comporte un support en polycarbonate. On a disposé des couches de fibre de verre (ou fibre de carbone) imbibées d'une résine (2)sur le support en polycarbonate (1) faisant office de noyau dans ce cas de figure. C'est donc dans ce cas une conception sandwich. La liaison est assurée par une résine conçue pour garantir l'adhérence entre polycarbonate et fibre de verre. With reference to these drawings, the device comprises a polycarbonate support. Layers of glass fiber (or carbon fiber) impregnated with a resin (2) were placed on the polycarbonate support (1) acting as a core in this case. It is therefore in this case a sandwich design. The connection is ensured by a resin designed to guarantee the adhesion between polycarbonate and fiberglass.

Selon une variante illustrée dans la figure 2, le noyau polycarbonate peut être remplacé par un noyau polycarbonate chargé fibre de verre (3) pour renforcer encore la liaison entre les deux matières : polycarbonate chargé fibre de verre et fibre de verre + résine (2). On utilise ici aussi une technique de fabrication sandwich. According to a variant illustrated in FIG. 2, the polycarbonate core can be replaced by a polycarbonate core loaded with fiberglass (3) to further strengthen the connection between the two materials: polycarbonate loaded with fiberglass and fiberglass + resin (2) . A sandwich manufacturing technique is also used here.

Selon une variante illustrée dans la figure 3, on assemble deux plaques de polycarbonate (1) (chargé fibre de verre ou non) grâce à une liaison assurée par une stratification d'une composition identique aux figures 1 et 2 (fibre de verre + résine) (2). Cet aspect de fabrication peut faciliter les finitions d'une planche, car le poiycarbonate (en plaque principalement dans ce cas) a l'aspect d'une vitre (lisse, transparent). According to a variant illustrated in FIG. 3, two polycarbonate plates (1) are assembled (fiberglass loaded or not) by virtue of a connection provided by a stratification of a composition identical to FIGS. 1 and 2 (fiberglass + resin ) (2). This manufacturing aspect can facilitate the finishing of a board, because the poiycarbonate (mainly in the plate in this case) has the appearance of glass (smooth, transparent).

Selon une variante illustrée dans la figure 4, le noyau (4) est en nid d'abeille de polycarbonate. On réalise un sandwich stratifié de fibre de verre (2). Le nid d'abeille est un procédé récent dans l'industrialisation, sa forme géométrique est désormais réputée comme la plus efficace à la résistance à la compression. Observons les caractéristiques propres au nid d'abeille seul (efficacité de la forme géométrique) et au polycarbonate seul (efficacité de la matière):
- POLYCARBONATE
* Forte résistance à la compression
* Très nerveux
* Incassable
* Etanche -NID D'ABEILLE (MATIERE QUELCONQUE)
* Forte résistance à la compression
* Légèreté
A savoir que pour le nid d'abeille de polycarbonate, tous les paramètres cités ci-dessus sont conservés. Cette variante donne une planche toujours très nerveuse, très légère, incassable à l'impact et étanche à l'infiltration d'eau et de neige. Elle est adaptée à la fabrication de surf des neiges, ski et monoski.According to a variant illustrated in Figure 4, the core (4) is made of polycarbonate honeycomb. A laminated fiberglass sandwich (2) is produced. Honeycomb is a recent process in industrialization, its geometric shape is now known as the most effective in compressive strength. Let us observe the characteristics specific to the honeycomb alone (efficiency of the geometric shape) and to polycarbonate alone (efficiency of the material):
- POLYCARBONATE
* Strong compressive strength
* Very nervous
* Unbreakable
* Waterproof - HONEYCOMB (ANY MATERIAL)
* Strong compressive strength
* Lightness
Note that for the polycarbonate honeycomb, all the parameters mentioned above are kept. This variant gives a board that is always very nervous, very light, unbreakable on impact and waterproof against the infiltration of water and snow. It is suitable for the manufacture of snowboard, ski and monoski.

A titre d'exemple non limitatif, on utilisera pour la stratification d'une planche (pour un seul côté du noyau ou support) :
3 couches de fibre de verre en unidirectionnel
Grammage par couche: 350 g/m2
3 couches de fibre de verre pour la finition en bidirectionnel
Grammage couche de finition 1 300 g/m2
Grammage couche de finition 2 : 220 g/m2 Grammage couche de finition 3 3:110 g/m2
On obtient 62% en unidirectionnel et 38% en bidirectionnel.By way of nonlimiting example, we will use for the stratification of a board (for only one side of the core or support):
3 layers of fiberglass in unidirectional
Weight per layer: 350 g / m2
3 layers of fiberglass for bidirectional finishing
Top coat weight 1,300 g / m2
Weight of top coat 2: 220 g / m2 Weight of top coat 3 3: 110 g / m2
We obtain 62% in unidirectional and 38% in bidirectional.

La nervosité importante ainsi que la raideur sont très efficaces pour une planche à roulettes. Elle est indestrutible à l'impact et étanche à l'infiltration d'eau et de neige.  The high nervousness as well as the stiffness are very effective for a skateboard. It is indestructible on impact and waterproof against water and snow infiltration.

Claims (3)

1/ La présente invention concerne une nouvelle conception dans la fabrication de planche à roulettes, surf des neiges, ski, monoski. Le dispositif, selon l'invention, permet d'apporter à une planche une étanchéité et une solidité inégalables. Elle permet également d'améliorer le phénomène de nervosité mais aussi de diminuer le poids d'une planche. Ce dispositif est caractérisé par la disposition des couches de fibre de verre (ou fibre de carbone) (2) sur un support en polycarbonate (1). La liaison est assurée par une résine (3) conçue pour adhérer au polycarbonate et à la fibre de verre. 1 / The present invention relates to a new design in the manufacture of skateboards, snowboards, ski, monoski. The device according to the invention makes it possible to provide a board with unequaled tightness and solidity. It also improves the nervousness phenomenon but also reduces the weight of a board. This device is characterized by the arrangement of the layers of glass fiber (or carbon fiber) (2) on a polycarbonate support (1). The connection is ensured by a resin (3) designed to adhere to polycarbonate and to fiberglass. REVENDICATION CLAIM 2/ Dispositif selon la revendication 1/ caractérisé par le fait que le polycarbonate existe sous différentes formes industrielles adaptées à la conception de surf des neiges, planche à roulettes, ski, monoski. 2 / Device according to claim 1 / characterized in that the polycarbonate exists in different industrial forms suitable for the design of snowboarding, skateboarding, skiing, monoskiing. ski, monoski (fabrication idéale : planche à roulettes car le polycarbonate en plaques est indestructible à l'impact de par sa forte densité). ski, monoski (ideal manufacture: skateboard because polycarbonate in plates is indestructible on impact due to its high density). Le polycarbonate en plaques est indestructible à l'impact. On peut l'utiliser dans la fabrication d'un surf des neiges, planche à roulettes, Polycarbonate sheets are indestructible on impact. It can be used in the manufacture of a snowboard, skateboard, Le nid d'abeille en polycarbonate est également utilisable en tant que noyau ou support dans la fabrication de sùrf des neiges, planche à roulettes, ski, monoski. The polycarbonate honeycomb can also be used as a core or support in the manufacture of snow sifr, skateboard, ski, monoski. Le polycarbonate chargé fibre de verre permet une accroche maximale lors de la liaison entre le polycarbonate chargé fibre de verre et la fibre de verre. Ainsi la délamination est inexistante. The glass fiber filled polycarbonate allows maximum grip when bonding between the glass fiber filled polycarbonate and the glass fiber. Thus delamination is non-existent. 3/ Dispositif selon la revendication 1/ ou la revendicationi2/ caractérisé par le fait que le polycarbonate peut faire office de noyau (stratification sandwich), ou Il peut être disposé deux plaques de polycarbonate, de part et d'autre de couches de fibre de verre (ou fibre de carbone).  3 / Device according to claim 1 / or claimi2 / characterized in that the polycarbonate can act as a core (sandwich lamination), or It can be arranged two polycarbonate plates, on either side of fiber layers glass (or carbon fiber).