FR2508837A1 - PROCESS FOR THE MANUFACTURE OF PLYWOOD - Google Patents
PROCESS FOR THE MANUFACTURE OF PLYWOOD Download PDFInfo
- Publication number
- FR2508837A1 FR2508837A1 FR8211514A FR8211514A FR2508837A1 FR 2508837 A1 FR2508837 A1 FR 2508837A1 FR 8211514 A FR8211514 A FR 8211514A FR 8211514 A FR8211514 A FR 8211514A FR 2508837 A1 FR2508837 A1 FR 2508837A1
- Authority
- FR
- France
- Prior art keywords
- glue
- plywood
- veneers
- hardener
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Lors de la fabrication de bois contreplaqué, il est devenu d'usage général de soumettre des placages encollés, en pile comportant plusieurs panneaux, à un pressage préalable à froid. Après le pressage à froid, les placages doivent adhérer assez fermement les uns aux autres pour que les différents panneaux puissent être acheminés, par des dispositifs d'alimentation automatiques, sans utilisation de cale en tôle, vers la presse à plateaux chauffants. During the manufacture of plywood, it has become of general use to subject glued veneers, in a pile comprising several panels, to a prior cold pressing. After cold pressing, the veneers must adhere firmly enough to each other so that the various panels can be conveyed, by automatic feeding devices, without the use of sheet metal shims, to the press with heating plates.
Ce procédé automatique permet d'économiser des frais, il assure une meilleure répartition d'humidité dans le panneau et des points défectueux, par exemple les points où se produisaient des excès de colle, peuvent être éliminés encore avant ltencollage à chaud.This automatic process saves costs, it ensures a better distribution of humidity in the panel and defective points, for example points where excess glue was produced, can be removed even before hot gluing.
La propriété des colles de conférer une certaine cohésion dès avant la prise proprement dite est appelée la résistance de collage préalable ou aptitude de collage à froid. The property of the adhesives to confer a certain cohesion even before the setting proper is called the resistance of prior bonding or aptitude for cold bonding.
Lors de ltencollage du contreplaqué avec des résines phénol-formaldéhyde (phénoplastes), le pressage préalable à froid des placages réussit eans problèmes; même après un temps de pressage préalable relativement court, on obtient une très bonne cohésion des placages. When gluing plywood with phenol-formaldehyde resins (phenoplasts), cold pressing of the veneers succeeds in these problems; even after a relatively short preliminary pressing time, very good cohesion of the veneers is obtained.
Les résines aiinoplastes (c'est-à-dire en particulier des condensats urée-formaldéhyde) présentent, de par leur nature, une aptitude au collage à froid sensiblement moins bonne que les résines phénoliques. Pour obtenir un précollage de panneaux préalablement pressés permettant leur transport, on a augmenté jusqu'a présent la viscosité du bain de colle en allongeant ce dernier de farine de blé ou en l'additionnant d'albumine du plasma en poudre ou de caséine.En dépit de ces mesures, le précollage à froid est le plus souvent d'assez médiocre qualité. C'est en particulier lors de ltencollage avec des condensats mixtes urée-mélamine et urée-mélamine-phénol que les produits dans dition ne peuvent être ajoutés en quantités suffisamment élevées étant donné qu'ils diminuent la stabilité aux in tempéries de lencollage. En effet, les bois contreplaqués encollés avec des condensats mixtes doivent être généralement résistants aux intempéries, voire à l'eau bouillante. AIinoplast resins (that is to say in particular urea-formaldehyde condensates) have, by their nature, a significantly less good ability to cold bonding than phenolic resins. To obtain a pre-bonding of previously pressed panels allowing their transport, the viscosity of the glue bath has hitherto been increased by lengthening the latter with wheat flour or by adding it with powdered plasma albumin or casein. despite these measures, cold pre-bonding is generally of rather poor quality. It is in particular when sizing with mixed urea-melamine and urea-melamine-phenol condensates that the products in the dition cannot be added in sufficiently high quantities since they reduce the temperature stability of the sizing. In fact, plywood glued with mixed condensates must generally be weatherproof, or even boiling water.
Le but essentiel de l'invention, qui se dégage de ce qui précède, consiste à améliorer la force de collage préalable à froid de condensats (mixtes) d'aminoplastes, par addition d'un produit approprié. The essential object of the invention, which emerges from the foregoing, consists in improving the strength of prior cold bonding of (mixed) condensates of aminoplasts, by addition of an appropriate product.
Or on a trouvé qu'on obtient avantageusement du bois contreplaqué par pressage préalable à froid de feuillets encollés avec des résines aminoplastes durcissables et durcissement, sous pression et à chaud, du paquet de feuillets préalablement pressé, en mélangeant à la colle une quantité secondaire d'une dispersion aqueuse de résine acrylate contenant, en liaison polymère, des groupes carboxyle libres ou neutralisés. However, it has been found that plywood is advantageously obtained by prior cold pressing of sheets glued with curable aminoplast resins and hardening, under pressure and hot, of the packet of sheets previously pressed, by mixing with the glue a secondary quantity of an aqueous dispersion of acrylate resin containing, in polymer bond, free or neutralized carboxyl groups.
Par quantité secondaire dans le sens de l'invention, on entend par exemple, une quantité efficace de 0,5 à 10 * en poids (extrait sec de la dispersion rapporté à l'extrait sec de la colle). By secondary quantity in the sense of the invention is meant, for example, an effective amount of 0.5 to 10 * by weight (dry extract of the dispersion relative to the dry extract of the adhesive).
Comme dispersions aqueuses de résines acrylates utilisables dans le procédé selon l'invention, c-mportant des groupes carboxyle libres, c'est-à-dire non estérifiés mais éventuellement neutralisés (sous forme de sel), on citera, par exemple, des copolymères ester (méth)acrylique-acide (méth)acrylique contenant généralement - rapporté à la somme molaire des unités monomères - jusqu'à 70 * (moles) d'unités acide (méth)acrylique ou de quantités équivalentes d'acide maléique.Outre l'acide (méth)acrylique ou l'acide maléique, ils contiennent le plus souvent, principalement ou exclusivement, des esters de l'acide (méth)acrylique à 1 - 6 atomes de carbone dans le reste alcool, de préférence 1 ou 2, et éventuellement des quantités secondaires d'autres composés polymérisables à insaturation oléfinique, tels que styrène ou composés vinyliques, dans chaque cas sous forme d'unités en liaison polymère. As aqueous dispersions of acrylate resins which can be used in the process according to the invention, having free carboxyl groups, that is to say not esterified but optionally neutralized (in the form of a salt), mention may be made, for example, of copolymers (meth) acrylic ester (meth) acrylic acid generally containing - based on the molar sum of the monomer units - up to 70 * (moles) of (meth) acrylic acid units or equivalent amounts of maleic acid. '(meth) acrylic acid or maleic acid, they most often contain, mainly or exclusively, esters of (meth) acrylic acid with 1 - 6 carbon atoms in the alcohol residue, preferably 1 or 2, and optionally secondary quantities of other polymerizable olefinically unsaturated compounds, such as styrene or vinyl compounds, in each case in the form of polymer bonded units.
Le cas échéant, ces dispersions de résines acrylates peuvent autre additionnées d'émulsifiants anioniques, par exemple de carboxylates ou de sulfonates. Where appropriate, these dispersions of acrylate resins can be supplemented with other anionic emulsifiers, for example carboxylates or sulfonates.
Les dites dispersions, qui sont généralement exemptes de plastifiants et de solvants, se trouvent certes dans le commerce, mais n'ont jusqu'à présent pas été ajoutées aux colles de résines aminoplastes. Said dispersions, which are generally free of plasticizers and solvents, are certainly on the market, but have not hitherto been added to glues of aminoplast resins.
Quant à l'opération d'addition, on notera que le pH du bain de colle est abaissé à environ 3,5 à 6,0, par addition d'un acide faible, libre, en tant que durcisseur, donc par exemple d'un acide carboxylique ou d'un mélange d'acides carboxyliques, et que la dispersion n'est ajoutée qu'ensuite. As for the addition operation, it will be noted that the pH of the adhesive bath is lowered to approximately 3.5 to 6.0, by addition of a weak, free acid, as a hardener, therefore for example a carboxylic acid or a mixture of carboxylic acids, and the dispersion is added only afterwards.
Lorsque la valeur du pH de la colle est trop élevée, supérieure à pH 6, le polymère initialement insoluble dans liteau gonfle si fortement qu'on constate une trop forte augmentation de la viscosité. C'est pourquoi l'utilisation de durcisseurs ammoniacaux (ou latents) n'est pas recommandée. When the pH value of the adhesive is too high, greater than pH 6, the initially insoluble polymer in the strip swells so strongly that there is a too strong increase in viscosity. This is why the use of ammoniacal (or latent) hardeners is not recommended.
La dispersion utilisée dans les exemples suivants est une dispersion aqueuse à environ 25 ffi d'un copolymère, à parties molaires environ égales, d'ester acrylique et d'acide (méth)acrylique. The dispersion used in the following examples is an aqueous dispersion at approximately 25 ffi of a copolymer, with approximately equal molar parts, of acrylic ester and (meth) acrylic acid.
Les quantités indiquées dans les exemples suivants (concernant colle, durcisseurs, charges et dispersions de polymère) sont des parties en poids. The quantities indicated in the following examples (relating to glue, hardeners, fillers and polymer dispersions) are parts by weight.
Exemple 1 colle de résine d'urée, à 65 * 100,0 100,0 farine de blé 30,0 30,0 durcisseur A)++ durcisseur B)++ 10,0 dispersion de polymère - 5,0 viscosité après avoir laissé reposer
10 mn à 2O0C [mPa.s 13300 6250 2 quantité de colle appliquée par m
simple face [gj 180 180 temps de séjour après application
de la colle [mn 1 15 15 durée de pressage à froid sous
0,5 mm de pression [mn] 10 10 % de joints ouverts (valeur moyenne
de 3 panneaux 3 x 2,5 mm,
placage déroulé de hêtre) après
séjour de 5 mn à découvert 20 14 )+ Une résine appropriée se trouve à l'état liquide dans
le commerce, par exemple sous le nom de Colle de
Kaurit 285.Example 1 urea resin adhesive, at 65 * 100.0 100.0 wheat flour 30.0 30.0 hardener A) ++ hardener B) ++ 10.0 polymer dispersion - 5.0 viscosity after let sit
10 min at 2O0C [mPa.s 13300 6250 2 quantity of glue applied per m
single sided [gj 180 180 dwell time after application
glue [min 1 15 15 cold pressing time under
0.5 mm pressure [min] 10 10% open joints (average value
3 x 3 x 2.5 mm panels,
beech veneer) after
5-minute stay in the open 20 14) + A suitable resin is in the liquid state in
trade, for example under the name of Colle de
Kaurit 285.
)++ Le durcisseur A est une solution aqueuse à 16 % d'un
mélange technique d'acides dicarboxyliques en C3 à C5.) ++ Hardener A is a 16% aqueous solution of
technical mixture of C3 to C5 dicarboxylic acids.
Le durcisseur B est une solution aqueuse à 15 % de
chlorure d ammonium.Hardener B is a 15% aqueous solution of
ammonium chloride.
En diminuant la dose de durcisseur A, on obtient une plus forte viscosité et une meilleure aptitude de collage à froid. Normalement, la qualité de collage obtenue (cf. tableau ci-dessus) devrait cependant être satisfaisante. By reducing the dose of hardener A, a higher viscosity and a better cold bonding ability are obtained. Normally, the quality of bonding obtained (see table above) should however be satisfactory.
Exemple 2
Condensat mixte à base de résine de mélamine (à 63 %)+ 100,0 100,0 100,0
Infusil)++ 12,0 12,0 12,0
Vavanite)++ 10,0 10,0 10,0 farine de blé 2,0 2,0 2,0 durcisseur A 4,0 4,0 4,0
Dispersion comme à l'exemple 1 2,5 5,0 viscosité après avoir laissé reposer
10 mn à 20 C [mPa.s] 4400 7600 3900 quantité de colle appliquée par m
simple face g] 180 180 180 temps de séjour après application
de la colle Lmn] 15 15 15 durée de pressage à froid sous
0,5 mm de pression [mn] 10 10 10 * de joints ouverts (valeur
moyenne de 3 panneaux 3 x 2,5 mm,
placage déroulé de hêtre) apres
séjour de 5 mn à découvert 13 7 20 )+ Une colle de résine appropriée se trouve à l'état
liquide dans le commerce sous le nom de Colle
Kauramine 541.Example 2
Mixed condensate based on melamine resin (at 63%) + 100.0 100.0 100.0
Infusil) ++ 12.0 12.0 12.0
Vavanite) ++ 10.0 10.0 10.0 wheat flour 2.0 2.0 2.0 hardener A 4.0 4.0 4.0
Dispersion as in Example 1 2.5 5.0 viscosity after leaving to stand
10 min at 20 C [mPa.s] 4400 7600 3900 quantity of glue applied per m
single sided g] 180 180 180 dwell time after application
glue Lmn] 15 15 15 cold pressing time under
0.5 mm pressure [min] 10 10 10 * of open joints (value
average of 3 panels 3 x 2.5 mm,
beech veneer) after
5-minute stay uncovered 13 7 20) + An appropriate resin adhesive is present
commercially available under the name of Glue
Kauramine 541.
)++ Charges de type commercial.) ++ Commercial type charges.
Avec le condensat mélamine-urée-phénol-formal utilisé dans l'exemple 2 ci-dessus, l'effet de la dispersion est nettement plus fort qu'avec la résine urée-formaldéhyde utilisée dans exemple 1. En ajoutant, par exemple, dans
2 la préparation/ci-dessus, seulement 2 parties en poids de durcisseur A à la place de 4 parties en poids, il s'établit un pH de 6,4; dès un temps de repos de 15 minutes, le bain de colle devient trop visqueux pour pouvoir être travaillé. L'effet de l'aptitude au collage à froid désiré peut donc être adapté exactement aux exigences en réglant la valeur du pH par addition de quantités variables de durcisseur.With the melamine-urea-phenol-formal condensate used in Example 2 above, the effect of the dispersion is clearly stronger than with the urea-formaldehyde resin used in Example 1. By adding, for example, in
2 the preparation / above, only 2 parts by weight of hardener A instead of 4 parts by weight, a pH of 6.4 is established; from a rest time of 15 minutes, the adhesive bath becomes too viscous to be able to be worked. The effect of the desired cold bonding ability can therefore be adapted exactly to the requirements by adjusting the pH value by adding variable amounts of hardener.
L'adjonction de la dispersion selon l'invention ntin- flue ni sur la résistance à l'eau bouillante ni sur la résistance aux essais alternés. The addition of the dispersion according to the invention does not affect either the resistance to boiling water or the resistance to alternating tests.
Claims (1)