FI20185299A1 - Coating and coating composition - Google Patents

Coating and coating composition Download PDF

Info

Publication number
FI20185299A1
FI20185299A1 FI20185299A FI20185299A FI20185299A1 FI 20185299 A1 FI20185299 A1 FI 20185299A1 FI 20185299 A FI20185299 A FI 20185299A FI 20185299 A FI20185299 A FI 20185299A FI 20185299 A1 FI20185299 A1 FI 20185299A1
Authority
FI
Finland
Prior art keywords
coating
calcium
silicate
binder
pigment
Prior art date
Application number
FI20185299A
Other languages
Finnish (fi)
Swedish (sv)
Inventor
Sakari Saastamoinen
Sirpa Saastamoinen
Original Assignee
Keusik Oy
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Keusik Oy filed Critical Keusik Oy
Priority to FI20185299A priority Critical patent/FI20185299A1/en
Priority to PCT/FI2019/050259 priority patent/WO2019185995A1/en
Publication of FI20185299A1 publication Critical patent/FI20185299A1/en

Abstract

Den föreliggande uppfinningen avser en beläggning, som omfattar åtminstone ett utfällt poröst pigment och bindemedel. Uppfinningen avser därtill en beläggningssammansättning, som omfattar en första beläggning som omfattar åtminstone ett utfällt poröst pigment och bindemedel och en andra beläggning som omfattar ett bindemedel som ger opacitet och/eller glans samt valfritt en tredje beläggning som omfattar ett bindemedel som ger glans. Uppfinningen avser därtill användning av en sådan beläggning och beläggningssammansättning som en ersättare för titanoxid utan att försämra de optiska egenskaperna av produkten som framställs.The present invention relates to a coating comprising at least one precipitated porous pigment and binder. The invention further relates to a coating composition which comprises a first coating comprising at least one precipitated porous pigment and binder and a second coating comprising a binder which provides opacity and / or gloss and optionally a third coating comprising a binder which gives a gloss. The invention further relates to the use of such a coating and coating composition as a substitute for titanium oxide without impairing the optical properties of the product produced.

Description

Päällyste ja päällystekoostumusCoating and coating composition

Keksinnön alaFIELD OF THE INVENTION

Esillä oleva keksintö koskee päällystettä, joka käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta. Keksintö koskee 5 lisäksi päällystekoostumusta, joka käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen sekä opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen. Päällystekoostumus käsittää valinnaisesti kolmannen kiiltoa antavaa sideainetta käsittävän päällysteen. Keksintö koskee lisäksi tällaisen päällysteen ja päällystekoos10 tumuksen käyttöä titaanidioksidin korvaajana optisten ominaisuuksien heikentymättä. Edelleen keksintö koskee menetelmää päällystekoostumuksen valmistamiseksi.The present invention relates to a coating comprising at least one porous pigment and an opacity and / or gloss binder. The invention further relates to a coating composition comprising a first coating comprising at least one porous pigment and an opacity and / or gloss binder and a second coating comprising an opacity and / or gloss binder. The coating composition optionally comprises a third coating comprising a gloss binder. The invention further relates to the use of such a coating and a coating composition as a substitute for titanium dioxide without compromising the optical properties. The invention further relates to a method for preparing a coating composition.

Tekniikan taustaTechnology background

Titaanidioksidia (T1O2) käytetään yleisesti valkoisena pigmenttinä maaleissa, 15 paperin, kartongin, muovin, kumin, laminaatin ja painomusteiden täyteaineissa sekä erilaisissa päällysteissä. Tärkeimmät titaanidioksidilla saatavat ominaisuudet ovat opasiteetti, peittokyky, vaaleus, sävytettävyys ja L-arvo. T1O2 on tehokkain ja hyvin kallis optisia ominaisuuksia antava pigmentti. Titaanidioksidia on kaupallisesti saatavilla anataasi- (taitekerroin 2,55) ja rutiilikiteinä (taitekerroin 2,7). Sekä anataasi20 että rutiilikiteet ovat ei-amorfisia.Titanium dioxide (T1O2) is commonly used as a white pigment in paints, fillers for paper, board, plastic, rubber, laminate and printing inks, as well as in various coatings. The main properties obtained with titanium dioxide are opacity, opacity, brightness, tintability and L-value. T1O2 is the most effective and very expensive pigment that gives optical properties. Titanium dioxide is commercially available as anatase (refractive index 2.55) and rutile crystals (refractive index 2.7). Both anatase20 and rutile crystals are non-amorphous.

Koska T1O2 on kallista, lisätään siihen tyypillisesti nk. ekstendereitä korvaamaan osa tarvittavan titaanidioksidin määrästä. Ekstendeht ovat huomattavasti titaanidioksidia halvempia pigmenttejä tai täyteaineita, joilla titaanidioksidikiteet voidaan erottaa fyysisesti toisistaan ja saada kiteiden etäisyydet sopivammiksi valon 25 sironnalle. Ekstenderin määrä on kuitenkin pidettävä pienenä, koska TiCUm suuri taitekerroin antaa lopulta kuitenkin suurimman valonsirontakyvyn ja isommat ekstenderin määrät heikentävät valonsirontakykyä. Ekstendeht ovat optisten ominaisuuksiensa, kuten esimerkiksi opasiteetti, vaaleus, sävy, peittävyys, puolesta parhaimmillaan, kun niiden keskimääräinen partikkelikoko on noin puolen valon aallon30 pituuden luokkaa. Tyypillisesti enimmillään 25 paino-% titaanidioksidista voidaan korvata eri käyttösovelluksissa menettämättä titaanidioksidilla saatavia optisia ominaisuuksia, etenkin opasiteettia. Lisäksi titaanidioksidin valmistajat tavallisesti päällystävät titaanidioksidin 1-20 paino-% pigmentin painosta erilaisilla orgaanisilla ja/tai epäorgaanisilla kemikaalien saostus- tai polymeerituotteilla.Because T1O2 is expensive, so-called extender is typically added to replace some of the amount of titanium dioxide required. Extensions are pigments or fillers which are considerably cheaper than titanium dioxide, by means of which the titanium dioxide crystals can be physically separated and the distances of the crystals made more suitable for light scattering. However, the amount of extender must be kept small because the high refractive index of TiCUm ultimately gives the highest light scattering ability and larger amounts of extender impair the light scattering ability. Ekstendeht are the optical properties such as opacity, brightness, shade, opacity, on behalf of the best when the average particle size is about half the length of the light aallon30 class. Typically, up to 25% by weight of titanium dioxide can be replaced in various applications without losing the optical properties, especially opacity, obtained with titanium dioxide. In addition, titanium dioxide manufacturers usually coat 1-20% by weight of titanium dioxide by weight of the pigment with various organic and / or inorganic chemical precipitation or polymer products.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Titaanidioksidin osittaista korvaamista kalsiumkarbonaatilla käsitellään patenttijulkaisussa WO 2009/109705 (FP-Pigments Oy). Patenttijulkaisussa WO 2015/007954 (FP-Pigments Oy) kuvataan puolestaan koostumuksia, jotka käsittävät titaanidioksidia ja lisäaineita, joilla voidaan korvata osa mainitussa koostumuk5 sessa olevasta titaanidioksidista. Ensimmäinen lisäaine käsittää komposiittipigmentin, joka koostuu kuorenmuodostuskomponentista ja optisesta pigmentistä ja toinen lisäaine käsittää reaktiivisen polymeerin. Kuorenmuodostuskomponentti on edullisesti epäorgaaninen, veteen niukkaliukoinen yhdiste, kuten saostettu kalsiumkarbonaatti, kalsiumsulfaatti, bahumsulfaatti, magnesiumkarbonaatti, magnesiumsili10 kaatti, alumiinihydroksidi tai alumiinisilikaatti.The partial replacement of titanium dioxide with calcium carbonate is discussed in WO 2009/109705 (FP-Pigments Oy). WO 2015/007954 (FP-Pigments Oy) in turn describes compositions comprising titanium dioxide and additives which can replace part of the titanium dioxide in said composition. The first additive comprises a composite pigment consisting of a shell-forming component and an optical pigment, and the second additive comprises a reactive polymer. The shell-forming component is preferably an inorganic, sparingly water-soluble compound such as precipitated calcium carbonate, calcium sulfate, bahum sulfate, magnesium carbonate, magnesium silicate, aluminum hydroxide or aluminosilicate.

Keksinnön lyhyt kuvausBrief description of the invention

Esillä olevan keksinnön eräänä tavoitteena on saada aikaan päällyste, joka käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta. Esillä olevan keksinnön eräänä tavoitteena on saada aikaan päällyste15 koostumus, joka käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen sekä opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen. Päällystekoostumus käsittää valinnaisesti kiiltoa antavaa sideainetta käsittävän kolmannen päällysteen. Päällystekoostumuksen toinen päällyste on olennaisesti pigmenttivapaa. Päällyste20 koostumuksen kolmas päällyste on olennaisesti pigmenttivapaa.It is an object of the present invention to provide a coating comprising at least one porous pigment and an opacity and / or gloss binder. It is an object of the present invention to provide a coating composition comprising a first coating comprising at least one porous pigment and an opacity and / or gloss binder and a second coating comprising an opacity and / or gloss binder. The coating composition optionally comprises a third coating comprising a gloss binder. The second coating of the coating composition is substantially pigment-free. Coating The third coating of the composition 20 is substantially pigment free.

Keksinnön mukainen päällyste soveltuu käytettäväksi paperin, kartongin, muovin, kumin tai laminaatin täyteaineiden korvaajana. Keksinnönmukainen päällyste soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteinä sekä maaleissa, eritysesti monikerrosmaaleissa. Esillä olevan 25 keksinnön eräänä tavoitteena on vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän päällysteen käyttö opasiteettia ja/tai vaaleutta antavana pigmenttipäällysteenä. Edelleen esillä olevan keksinnön eräänä tavoitteena on vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän päällysteen käyttö titaanidioksidin korvaajana optisten omi30 naisuuksien heikentymättä.The coating according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber or laminate. The coating according to the invention is suitable for use as coatings on paper, cardboard, plastic, rubber, laminate, concrete and wood, as well as in paints, in particular multilayer paints. It is an object of the present invention to use a coating comprising at least one porous pigment and an opacity and / or gloss binder as an opacity and / or brightness pigment coating. It is a further object of the present invention to use a coating comprising at least one porous pigment and an opacity and / or gloss binder as a substitute for titanium dioxide without compromising the optical properties.

Keksinnön mukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana. Keksinnönmukainen, päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteenä sekä maaleissa, erityisesti monikerrosmaa35 leissa. Esillä olevan keksinnön eräänä tavoitteena on päällystekoostumuksen, jokaThe coating composition according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. The coating composition according to the invention is suitable for use as a coating on paper, board, plastic, rubber, laminate, concrete and wood, as well as in paints, in particular multilayer paints. It is an object of the present invention to provide a coating composition which

20185299 prh 29 -03- 2018 käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen, käyttö opasiteettia ja/tai vaaleutta antavana päällysteenä. Edelleen esillä olevan keksinnön eräänä tavoitteena on päällys5 tekoostumuksen käyttö titaanidioksidin korvaajana optisten ominaisuuksien heikentymättä. Esillä olevan keksinnön eräänä tavoitteena on myös menetelmä päällystekoostumuksen valmistamiseksi.20185299 prh 29 -03-20118 comprises the use of a first coating comprising at least one porous pigment and an opacity and / or a gloss binder and a second coating comprising an opacity and / or a gloss binder, the use of an opacity and / or a lightness coating. It is a further object of the present invention to use a coating composition as a substitute for titanium dioxide without compromising its optical properties. It is also an object of the present invention to provide a method of making a coating composition.

Keksinnön tavoitteet saavutetaan tuotteilla ja käytöillä sekä menetelmällä, joille on tunnusomaista se, mitä sanotaan itsenäisissä patenttivaatimuksissa. Kek10 sinnön edulliset suoritusmuodot kuvataan epäitsenäisissä patenttivaatimuksissa.The objects of the invention are achieved by products and uses as well as by a method which is characterized by what is stated in the independent claims. Preferred embodiments of the Kek10 invention are described in the dependent claims.

Keksinnön yksityiskohtainen kuvausDetailed description of the invention

Keksintö koskee vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävää päällystettä. Erityisesti keksintö koskee vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsit15 tävää päällystettä, jolloin huokoinen pigmentti valitaan:The invention relates to a coating comprising at least one porous pigment and an opacity and / or gloss binder. In particular, the invention relates to a coating comprising at least one porous pigment and an opacity and / or gloss binder, wherein the porous pigment is selected from:

a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaa- teista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista,a) the precipitated aluminum silicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaa- you alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, any other aluminum, magnesium, calcium and / or zinc silicate of a combination / mixture, silicas or any mixture thereof,

b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaat- tia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsiumja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta,b) the precipitated composite pigment comprising titanium dioxide and aluminum silicate, calcium silicate, magnesium silicate, carbonate alumiinimagnesiumsilikaat-, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium or / and zinc silicate combination / mixture, silica or any mixture thereof,

c) komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kalsiumkarbonaattia (MCC).c) composite pigments comprising titanium dioxide and modified calcium carbonate (MCC).

Keksinnön erään suoritusmuodon mukaan päällyste käsittää opasiteettia ja/tai kiiltoa antavaa sideainetta ja vähintään yhtä huokoista pigmenttiä, joka valitaanAccording to an embodiment of the invention, the coating comprises an opacity and / or gloss binder and at least one porous pigment selected from

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaa- teista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista, taia) the precipitated aluminum silicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaa- you alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, any other aluminum, magnesium, calcium and / or zinc silicate of a combination / mixture, silicas or any mixture thereof, or

b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaat- tia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsiumja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta.b) the precipitated composite pigment comprising titanium dioxide and aluminum silicate, calcium silicate, magnesium silicate, carbonate alumiinimagnesiumsilikaat-, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium or / and zinc silicate combination / mixture, silica or any mixture thereof.

Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumii20 nimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista.According to one embodiment of the invention, the pigment is selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium silicates, silicas or any mixtures thereof. According to one embodiment of the invention, the pigment is selected from aluminosilicates, magnesium silicates and / or alumina 20 magnesium magnesium silicates. According to an embodiment of the invention, the pigment is selected from calcium silicates, aluminosilicates and / or alumina calcium silicates. According to one embodiment of the invention, the pigment is selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium silicates, silicas or any mixtures thereof. According to an embodiment of the invention, the pigment is selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to an embodiment of the invention, the pigment is selected from calcium silicates, aluminosilicates and / or alumina calcium silicates.

Keksinnön erään suoritusmuodon mukaan huokoiset pigmentit eivät olennai30 sesti sisällä titaanidioksidia. Keksinnön erään suoritusmuodon mukaan saostetut, huokoiset pigmentit eivät sisällä titaanidioksidia, tosin sanoen saostetut, huokoiset pigmentit ovat TiO2-vapaita.According to one embodiment of the invention, the porous pigments are substantially free of titanium dioxide. According to one embodiment of the invention, the precipitated porous pigments do not contain titanium dioxide, i.e. the precipitated porous pigments are TiO2-free.

Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua pigmenttiä, joka valitaan alumiinisilikaa5According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from aluminosilicate.

20185299 prh 29 -03- 2018 teista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua pig5 menttiä, joka valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua pigmenttiä, joka valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidiok10 sidia ja vähintään yhtä saostettua pigmenttiä, joka valitaan alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua pigmenttiä, joka 15 valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua pigmenttiä, joka valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista.20185299 prh 29 -03- 2018 calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium silicates, silicas or any mixtures thereof. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from calcium silicates, aluminosilicates and / or alumina calcium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium oxides or silicon oxide silicates. According to an embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated pigment selected from calcium silicates, aluminosilicates and / or alumina calcium silicates.

Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää vähin20 tään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia korkeintaan 50 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 50 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 30 paino-% komposiittipigmentin pai25 nosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää titaanidioksidia noin 15-paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää vähintään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia noin 10-paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan kom30 posiittipigmentti sisältää titaanidioksidia noin 5-paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää vähintään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia noin 5-50 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 10-50 paino-% 35 komposiittipigmentin painosta laskettuna. Erään keksinnön suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 15-50 paino-% komposiittiAccording to one embodiment of the invention, the composite pigment contains at least one of the above-mentioned precipitated pigments and titanium dioxide in an amount of at most 50% by weight, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 50% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 30% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains titanium dioxide in an amount of about 15% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains at least one of the above-mentioned precipitated pigments and titanium dioxide in an amount of about 10% by weight, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains titanium dioxide in an amount of about 5% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises at least one of the above-mentioned precipitated pigments and titanium dioxide in an amount of about 5 to 50% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises about 10 to 50% by weight of titanium dioxide, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 15 to 50% by weight of the composite.

20185299 prh 29 -03- 2018 pigmentin painosta laskettuna Erään keksinnön suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 15-30 paino-% komposiittipigmentin painosta laskettuna.20185299 prh 29 -03-20188 by weight of pigment According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 15-30% by weight based on the weight of the composite pigment.

Keksinnön erään suoritusmuodon mukaan komposiittipigmentti ei sisällä lisä5 aineina polymeerejä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti ei sisällä kuorirakenteita.According to one embodiment of the invention, the composite pigment does not contain polymers as additional substances. According to one embodiment of the invention, the composite pigment does not contain shell structures.

Keksinnön erään suoritusmuodon mukaan saostetut pigmentit ja/tai komposiittipigmentit voivat lisäksi valinnaisesti sisältää Na-, K-, L-, SCU-, SO3-, PO4-, BO3-, B-, PO3-, NO2-, NO3-, F-, hiilihappo-, karboksyylihappo-, sinkki-, mangaani-, rauta-, 10 zirkonium-, nikkeli-, koboltti-, kromi-, barium-, rikki-, strontium-, hiili-, Cl-ja/tai muiden alkuaineiden jäämiä.According to an embodiment of the invention, the precipitated pigments and / or composite pigments may further optionally contain Na, K, L, SCU, SO3, PO4, BO3, B, PO3, NO2, NO3, F, residues of carbonic acid, carboxylic acid, zinc, manganese, iron, zirconium, nickel, cobalt, chromium, barium, sulfur, strontium, carbon, Cl and / or other elements.

Keksinnön erään suoritusmuodon mukaan saostetut pigmentit ja/tai komposiittipigmentit voivat lisäksi valinnaisesti sisältää stabilointiaineita, dispergointiaineita, pintamodifiointiaineita ja/tai muita tavanomaisia apuaineita.According to an embodiment of the invention, the precipitated pigments and / or composite pigments may additionally optionally contain stabilizers, dispersants, surface modifiers and / or other conventional auxiliaries.

Keksinnön erään suoritusmuodon mukaan huokoisella pigmentillä tarkoitetaan pigmenttiä, jonka BET-arvo on yli 15 m2/g. Keksinnön erään suoritusmuodon mukaan huokoisen pigmentin BET-arvo on yli 50 m2/g.According to one embodiment of the invention, a porous pigment means a pigment with a BET value of more than 15 m 2 / g. According to one embodiment of the invention, the porous pigment has a BET value of more than 50 m 2 / g.

Keksinnön erään suoritusmuodon mukaan huokoisen pigmentin keskimääräinen partikkelikoko on alle 100 pm, lasermittauksella määritettynä. Keksinnön erään 20 suoritusmuodon mukaan pigmentin keskimääräinen partikkelikoko on 1 - 10 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmentin keskimääräinen partikkelikoko on 1 - 2 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmentin keskimääräinen partikkelikoko on 0,2 - 0,6 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mu25 kaan komposiittipigmentin keskimääräinen partikkelikoko on alle 100 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin keskimääräinen partikkelikoko on 1 - 2 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin keskimääräinen partikkelikoko on 0,2 - 0,6 pm, lasermittauksella määritettynä. Keksinnön erään 30 suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai partikkelikokojakauma määritetään laserdiffraktiomenetelmällä. keksinnön erään suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai partikkelikokojakauma määritetään laserdiffraktiomenetelmällä käyttäen laitetta, jolla voidaan määrittää partikkelikoko 0,02 - 2000 pm alueella. Keksinnön eräänAccording to one embodiment of the invention, the average particle size of the porous pigment is less than 100, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 1 to 10, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 1 to 2, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 0.2 to 0.6, as determined by laser measurement. According to one embodiment of the invention, the composite pigment has an average particle size of less than 100, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the composite pigment is 1 to 2, as determined by laser measurement. According to one embodiment of the invention, the composite pigment has an average particle size of 0.2 to 0.6, as determined by laser measurement. According to an embodiment of the invention, the particle size and / or particle size distribution of the pigment and / or composite pigment is determined by a laser diffraction method. according to an embodiment of the invention, the particle size and / or the particle size distribution of the pigment and / or the composite pigment are determined by a laser diffraction method using an apparatus capable of determining the particle size in the range of 0.02 to 2000 μm. Of the invention

20185299 prh 29 -03- 2018 suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai partikkelikokojakauma määritetään Malvern 2000-laiteella. Keksinnön erään suoritusmuodon mukaan pigmentin huokostilavuus on tyypillisesti alueella 0,20 - 0,30 cm3/g. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin huokostilavuus on tyypillisesti alueella 0,15 - 0,20 cm3/g.20185299 prh 29 -03- 2018 According to the embodiment, the particle size and / or particle size distribution of the pigment and / or composite pigment is determined with a Malvern 2000 device. According to one embodiment of the invention, the pore volume of the pigment is typically in the range of 0.20 to 0.30 cm 3 / g. According to one embodiment of the invention, the pore volume of the composite pigment is typically in the range of 0.15 to 0.20 cm 3 / g.

Keksinnön erään suoritusmuodon mukaan saostettujen pigmenttien ilmahuokoset säilytetään kuivauksen jälkeen tyhjinä, jolloin saadaan huokosissa olevan ilman taitekertoimen (noin 1) ja pigmentin (taitekerroin 1,4-1,8) erotus hyödynnettyä valon sirontana, joka näkyy parempana opasiteettina ja vaaleutena.According to one embodiment of the invention, the air pores of the precipitated pigments are kept empty after drying, whereby the difference between the refractive index (about 1) and the pigment (refractive index 1.4-1.8) of the air in the pores can be utilized as light scattering, which appears in better opacity and brightness.

Keksinnön erään suoritusmuodon mukaan päällyste käsittää opasiteettia ja/tai kiiltoa antavaa sideainetta ja vähintään yhtä huokoista pigmenttiä, joka valitaan komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kalsiumkarbonaattia (MCC). Keksinnön erään suoritusmuodon mukaan TiCU-kalsiumkarbonaattikomposiittipigmentti valmistetaan siten, että saatetaan titaanidioksidi T1O2, kalsiumhydroksidi Ca(OH)2 ja hiilidioksidi CO2 reagoimaan keskenään ja saatu TiO2-saostettu kalsiumkarbonaatti-koostumus käsitellään hapolla kuten esimerkiksi rikkihapolla H2SO4, jolloin happo syövyttää saostetun kalsiumkarbonaatin pinnan huokoiseksi. Modifioituja kalsiumkarbonaatteja (MCC) voidaan valmistaa jauhetusta kalsiumkarbonaatista (GCC) hapoilla syövyttämällä. Marmori ja kalkkikivi ovat jauhetun kalsiumkarbonaatin (GCC) mahdollisia raaka-aineita. MCC:t toimivat hyvin mattapäällysteissä, mutta eivät kiiltävissä huokoisuuden vuoksi.According to one embodiment of the invention, the coating comprises an opacity and / or gloss binder and at least one porous pigment selected from composite pigments comprising titanium dioxide and modified calcium carbonate (MCC). According to one embodiment of the invention, the TiCU-calcium carbonate composite pigment is prepared by reacting titanium dioxide T1O2, calcium hydroxide Ca (OH) 2 and carbon dioxide CO2 and the resulting TiO2-precipitated calcium carbonate is treated with an acid such as sulfuric acid H2SO4. Modified calcium carbonates (MCC) can be prepared from powdered calcium carbonate (GCC) by acid etching. Marble and limestone are possible raw materials for ground calcium carbonate (GCC). MCCs work well on matte coatings but are not glossy due to porosity.

Keksinnönmukainen päällyste käsittää lisäksi opasiteettia ja/tai kiiltoa antavaa sideainetta, joka valitaan päällysteen käyttötarkoituksen mukaan. Keksinnön erään suoritusmuodon mukaan sideaine on opasiteettia ja kiiltoa antava sideaine. Keksinnön erään suoritusmuodon mukaan sideaine on kiiltoa antava sideaine. Keksinnön erään suoritusmuodon mukaan sideaine on opasiteettia antava sideaine. Opasiteettia antavalle sideaineelle on olennaista, että se lisää päällysteen peittokykyä. Esimerkiksi ontot ilmaa sisältävät rakenteet edustavat erästä tekniikkaa, jolla peittokyky sideaineilla saadaan aikaiseksi.The coating according to the invention further comprises an opacity and / or a gloss-providing binder selected according to the intended use of the coating. According to one embodiment of the invention, the binder is an opacity and gloss binder. According to one embodiment of the invention, the binder is a gloss-providing binder. According to one embodiment of the invention, the binder is an opacifying binder. It is essential for the opacifying binder that it increase the opacity of the coating. For example, hollow air-containing structures represent one technique for providing coverage with binders.

Keksinnönmukainen päällyste soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana sekä paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa. Erilaisia opasiteettia ja/tai kiiltoa antavia sideaineita on saatavilla kaupallisesti ja alan ammattilainen valitsee päällysteen käyttötarkoituksen mukaanThe coating according to the invention is suitable for use as a substitute for fillers in paper, cardboard, plastic, rubber and laminate, as well as in coatings for paper, cardboard, plastic, rubber, laminate, concrete and wood, as well as in paints, especially multilayer paints. Various opacifying and / or glossing binders are commercially available and will be selected by one skilled in the art according to the intended use.

20185299 prh 29 -03- 2018 soveltuvan opasiteettia ja/tai kiiltoa antavan sideaineen. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajissa. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, be5 tönin ja puun päällysteissä. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi maaleissa, erityisesti monikerrosmaaleissa. Soveltuvia sideaineita, joita käytetään yleisesti esimerkiksi maaleissa ovat mm. erilaiset akryyli-, alkydi- lateksi-ja epoksipolymeeripohjaiset yhdisteet tai polyvinyylialkoholi- sekä polyuretaanipohjaiset yhdisteet. Muita soveltuvia sideaineita ovat synteettiset tai luon10 nolliset polymeerit, jotka pohjautuvat mm. vinyyliasetaattiin, vinyylietyleeniin (VAE), polyuretaaniin, polyesteriin, melamiinihartseihin, silaaneihin, siloksaaneihin, tai öljyihin. Esimerkkeinä mm. maaleissa käytettävistä sideaineista ovat ROPAQUE™ Ultra E-polymeeh (The Dow Chemical Company) joka antaa peittokykyä (opasiteetti) ja sävyä (vaaleus), mutta ei kiiltoa ja Acronal® S 728-polymeeh (BASF Cor15 poration), joka puolestaan antaa kiiltoa.20185299 prh 29 -03- 2018 a suitable opacifier and / or gloss binder. According to one embodiment of the invention, the binder is suitable for use in substitutes for fillers in paper, board, plastic, rubber and laminate. According to one embodiment of the invention, the binder is suitable for use in coatings on paper, board, plastic, rubber, laminate, ink and wood. According to an embodiment of the invention, the binder is suitable for use in paints, in particular multilayer paints. Suitable binders which are commonly used, for example in paints, include e.g. various compounds based on acrylic, alkyd latex and epoxy polymers or compounds based on polyvinyl alcohol and polyurethane. Other suitable binders are synthetic or natural polymers based on e.g. vinyl acetate, vinyl ethylene (VAE), polyurethane, polyester, melamine resins, silanes, siloxanes, or oils. Examples include e.g. binders used in paints are ROPAQUE ™ Ultra E-polymeeh (The Dow Chemical Company) which gives opacity and hue but no gloss and Acronal® S 728 polymeeh (BASF Cor15 poration) which gives gloss.

Keksinnönmukainen päällyste käsittää 1-30 % sideainetta pigmentti-sideainetai komposiittipigmentti-sideainekoostumuksen painosta laskettuna. Keksinnön erään suoritusmuodon mukaan päällyste käsittää 3-10 % sideainetta pigmentti-sideaine- tai komposiittipigmentti-sideainekoostumuksen painosta laskettuna. Kek20 sinnön erään suoritusmuodon mukaan päällyste käsittää 5 % sideainetta pigmenttisideaine- tai komposiittipigmentti-sideainekoostumuksen painosta laskettuna.The coating according to the invention comprises 1-30% of a binder based on the weight of the pigment-binder or composite pigment-binder composition. According to one embodiment of the invention, the coating comprises 3-10% binder based on the weight of the pigment-binder or composite pigment-binder composition. According to one embodiment of the Kek20 invention, the coating comprises 5% binder based on the weight of the pigment binder or composite pigment binder composition.

Keksinnön erään suoritusmuodon mukaan pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine-suhde on välillä 70-99:30-1. Keksinnön erään suoritusmuodon mukaan pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine25 suhde on välillä 90-97:10-3. Keksinnön erään suoritusmuodon mukaan pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine-suhde on 95:5.According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder ratio is between 70-99: 30-1. According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder25 ratio is between 90-97: 10-3. According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder ratio is 95: 5.

Keksinnönmukainen päällyste soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana. Keksinnönmukainen päällyste soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja 30 puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa. Keksinnönmukainen päällyste soveltuu käytettäväksi opasiteettia ja vaaleutta antavana pigmenttipäällysteenä. Keksinnönmukainen päällyste soveltuu käytettäväksi titaanidioksidin korvaajana valmistettavan tuotteen optisten ominaisuuksien heikentymättä.The coating according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. The coating according to the invention is suitable for use in coatings on paper, cardboard, plastic, rubber, laminate, concrete and wood, as well as in paints, in particular multilayer paints. The coating according to the invention is suitable for use as a pigment coating which gives opacity and brightness. The coating according to the invention is suitable for use as a substitute for titanium dioxide without compromising the optical properties of the product to be manufactured.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Keksintö koskee myös päällystekoostumusta, joka käsittää vähintään yhtä saostettua huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen. Keksinnönmukainen päällystekoostumus käsittää valin5 naisesti kolmannen päällysteen, joka käsittää kiiltoa antavaa sideainetta.The invention also relates to a coating composition comprising a first coating comprising at least one precipitated porous pigment and an opacity and / or gloss binder and a second coating comprising an opacity and / or gloss binder. The coating composition of the invention optionally comprises a third coating comprising a gloss binder.

Päällystekoostumuksen toinen ja/tai kolmas päällyste ovat olennaisesti pigmenttivapaita. Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen toinen päällyste on olennaisesti pigmenttivapaa. Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen toinen päällyste on pigmenttivapaa. Keksinnön 10 erään suoritusmuodon mukaan päällystekoostumuksen kolmas päällyste on olennaisesti pigmenttivapaa. Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen kolmas päällyste on pigmenttivapaa.The second and / or third coatings of the coating composition are substantially pigment-free. According to one embodiment of the invention, the second coating of the coating composition is substantially pigment-free. According to one embodiment of the invention, the second coating of the coating composition is pigment-free. According to one embodiment of the invention 10, the third coating of the coating composition is substantially pigment-free. According to one embodiment of the invention, the third coating of the coating composition is pigment-free.

Keksinnönmukaisen päällystekoostumuksen ensimmäinen päällyste käsittää vähintään yhtä huokoista pigmenttiä, joka valitaanThe first coating of the coating composition of the invention comprises at least one porous pigment selected from

a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisili20 kaateista, mistä tahansa muusta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista,a) the precipitated aluminum silicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisili20 kaateista, any other aluminum, magnesium, calcium and / or zinc silicate of a combination / mixture of silicas or any mixture thereof,

b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaattia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsiumja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta,b) the precipitated composite pigment comprising titanium dioxide and aluminum silicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium or / and the combination of the zinc silicate / mixture, silica or any mixture thereof,

c) komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kal30 siumkarbonaattia (MCC).c) composite pigments comprising titanium dioxide and modified calcium carbonate (MCC).

Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäinen päällyste käsittää vähintään yhtä huokoista pigmenttiä, joka valitaanAccording to one embodiment of the invention, the first coating of the coating composition comprises at least one porous pigment selected from

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaa- teista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista, taia) the precipitated aluminum silicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaa- you alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, any other aluminum, magnesium, calcium and / or zinc silicate of a combination / mixture, silicas or any mixture thereof, or

b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaat- tia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsiumja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta.b) the precipitated composite pigment comprising titanium dioxide and aluminum silicate, calcium silicate, magnesium silicate, carbonate alumiinimagnesiumsilikaat-, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium or / and zinc silicate combination / mixture, silica or any mixture thereof.

Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäinen päällyste käsittää vähintään yhtä huokoista pigmenttiä, joka valitaan alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon 20 mukaan pigmentti valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alu25 miinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Keksinnön erään suoritusmuodon mukaan pigmentti valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista.According to one embodiment of the invention, the first coating of the coating composition comprises at least one porous pigment selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium silicates or any of these silicas. According to an embodiment 20 of the invention, the pigment is selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to an embodiment of the invention, the pigment is selected from calcium silicates, aluminosilicates and / or alumina calcium silicates. According to one embodiment of the invention, the pigment is selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, alumina silicates, aluminum calcium magnesium silicates, silicas or any mixtures thereof. According to an embodiment of the invention, the pigment is selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to an embodiment of the invention, the pigment is selected from calcium silicates, aluminosilicates and / or alumina calcium silicates.

Keksinnön erään suoritusmuodon mukaan huokoiset pigmentit eivät olennaisesti sisällä titaanidioksidia. Erään suoritusmuodon mukaan saostetut, huokoiset pigmentit eivät sisällä titaanidioksidia, tosin sanoen saostetut, huokoiset pigmentit ovat TiO2-vapaita.According to one embodiment of the invention, the porous pigments are substantially free of titanium dioxide. According to one embodiment, the precipitated porous pigments do not contain titanium dioxide, i.e. the precipitated porous pigments are TiO2-free.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäinen päällyste käsittää vähintään yhtä huokoista pigmenttiä, joka valitaan komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan alumiinisilikaateista, kalsiumsilikaateista, magne5 siumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaateista. Kek10 sinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan alumiinisilikaateista, kalsiumsilikaa15 teista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, piidioksideista tai mistä tahansa näiden seoksista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan alumiinisilikaateista, magnesiumsilikaateista ja/tai alumiinimagnesiumsilikaa20 teista. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia ja vähintään yhtä saostettua, huokoista pigmenttiä, joka valitaan kalsiumsilikaateista, alumiinisilikaateista ja/tai alumiinikalsiumsilikaateista.According to one embodiment of the invention, the first coating of the coating composition comprises at least one porous pigment selected from composite pigments comprising titanium dioxide and at least one precipitated porous pigment selected from aluminosilicates, aluminosilicate, aluminosilicate, magnesium silicate, aluminosilicate, aluminosilicate, aluminosilicate According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated, porous pigment selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated, porous pigment selected from calcium silicates, aluminosilicates and / or alumina calcium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated, porous pigment selected from aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminosilicate silicates, aluminosilicon magnesium, aluminosilicon magnesium According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated, porous pigment selected from aluminosilicates, magnesium silicates and / or aluminum magnesium silicates. According to one embodiment of the invention, the composite pigment comprises titanium dioxide and at least one precipitated, porous pigment selected from calcium silicates, aluminosilicates and / or alumina calcium silicates.

Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää vähintään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia korkeintaan 5025 paino-% titaanidioksidia komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 50 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 30 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan kom30 posiittipigmentti sisältää titaanidioksidia noin 15-paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää vähintään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia noin 10paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti sisältää titaanidioksidia noin 5-paino-% komposiit35 tipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää vähintään yhtä yllä mainittua saostettua pigmenttiä ja titaanidioksidia noin 5-50 paino-% komposiittipigmentin painosta laskettuna. KeksinnönAccording to one embodiment of the invention, the composite pigment contains at least one of the above-mentioned precipitated pigments and titanium dioxide at a maximum of 5025% by weight of titanium dioxide, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 50% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 30% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains about 15% by weight of titanium dioxide, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains at least one of the above-mentioned precipitated pigments and titanium dioxide in an amount of about 10% by weight, based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment contains about 5% by weight of titanium dioxide based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises at least one of the above-mentioned precipitated pigments and titanium dioxide in an amount of about 5 to 50% by weight based on the weight of the composite pigment. invention

20185299 prh 29 -03- 2018 erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 10-50 paino-% komposiittipigmentin painosta laskettuna. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti käsittää titaanidioksidia noin 15-50 paino-% komposiittipigmentin painosta laskettuna Keksinnön erään suoritusmuodon mukaan 5 komposiittipigmentti käsittää titaanidioksidia noin 15-30 paino-% komposiittipigmentin painosta laskettuna.20185299 prh 29 -03-20188 According to one embodiment, the composite pigment comprises titanium dioxide in an amount of about 10-50% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 15-50% by weight based on the weight of the composite pigment. According to one embodiment of the invention, the composite pigment comprises titanium dioxide in an amount of about 15-30% by weight based on the weight of the composite pigment.

Keksinnön erään suoritusmuodon mukaan komposiittipigmentti ei sisällä lisäaineina polymeerejä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentti ei sisällä kuorirakenteita.According to one embodiment of the invention, the composite pigment does not contain polymers as additives. According to one embodiment of the invention, the composite pigment does not contain shell structures.

Keksinnön erään suoritusmuodon mukaan saostetut, huokoiset pigmentit ja/tai komposiittipigmentit voivat lisäksi valinnaisesti sisältää Na-, K-, L-, SCU-, SO3-, PO4, BO3-, B-, PO3-, NO2-, NO3-, F-, hiilihappo-, karboksyylihappo-, sinkki-, mangaani-, rauta-, zirkonium-, nikkeli-, koboltti-, kromi-, barium-, rikki-, strontium-, hiili-, Cl-ja/tai muiden alkuaineiden jäämistä.According to an embodiment of the invention, the precipitated porous pigments and / or composite pigments may additionally optionally contain Na, K, L, SCU, SO3, PO4, BO3, B, PO3, NO2, NO3, F- , carbonic acid, carboxylic acid, zinc, manganese, iron, zirconium, nickel, cobalt, chromium, barium, sulfur, strontium, carbon, Cl and / or other elements.

Erään keksinnön suoritusmuodon mukaan saostetut, huokoiset pigmentit ja/tai komposiittipigmentit voivat lisäksi valinnaisesti sisältää stabilointiaineita, dispergointiaineita, pintamodifiointiaineita ja/tai muita tavanomaisia apuaineita.According to an embodiment of the invention, the precipitated porous pigments and / or composite pigments may additionally optionally contain stabilizers, dispersants, surface modifiers and / or other conventional auxiliaries.

Keksinnön erään suoritusmuodon mukaan huokoisella pigmentillä tarkoitetaan pigmenttiä, jonka BET-arvo on yli 15 m2/g. Keksinnön erään suoritusmuodon mu20 kaan huokoisen pigmentin BET-arvo on yli 50 m2/g.According to one embodiment of the invention, a porous pigment means a pigment with a BET value of more than 15 m 2 / g. According to one embodiment of the invention, the porous pigment has a BET value of more than 50 m 2 / g.

Keksinnön erään suoritusmuodon mukaan huokoisen pigmentin keskimääräinen partikkelikoko on alle 100 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmentin keskimääräinen partikkelikoko on 1 - 10 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmen25 tin keskimääräinen partikkelikoko on 1 - 2 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmentin keskimääräinen partikkelikoko on 0,2 - 0,6 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin keskimääräinen partikkelikoko on alle 100 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan komposiittipig30 mentin keskimääräinen partikkelikoko on 1 - 2 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin keskimääräinen partikkelikoko on 0,2 - 0,6 pm, lasermittauksella määritettynä. Keksinnön erään suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai partikkelikokojakauma määritetään laserdiffraktiomenetelmällä. keksinnön eräänAccording to one embodiment of the invention, the average particle size of the porous pigment is less than 100, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 1 to 10, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 1 to 2, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the pigment is 0.2 to 0.6, as determined by laser measurement. According to one embodiment of the invention, the average particle size of the composite pigment is less than 100, as determined by laser measurement. According to one embodiment of the invention, the composite pigment has an average particle size of 1 to 2, as determined by laser measurement. According to one embodiment of the invention, the composite pigment has an average particle size of 0.2 to 0.6, as determined by laser measurement. According to an embodiment of the invention, the particle size and / or particle size distribution of the pigment and / or the composite pigment is determined by a laser diffraction method. invention

20185299 prh 29 -03- 2018 suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai partikkelikokojakauma määritetään laserdiffraktiomenetelmällä käyttäen laitetta, jolla voidaan määrittää partikkelikoko 0,02 - 2000 pm alueella. Keksinnön erään suoritusmuodon mukaan pigmentin ja/tai komposiittipigmentin partikkelikoko ja/tai 5 partikkelikokojakauma määritetään Malvern 2000-laiteella. Keksinnön erään suoritusmuodon mukaan pigmentin huokostilavuus on tyypillisesti alueella 0,20 - 0,30 cm3/g. Keksinnön erään suoritusmuodon mukaan komposiittipigmentin huokostilavuus on tyypillisesti alueella 0,15 - 0,20 cm3/g.20185299 prh 29 -03-20188 According to the embodiment, the particle size and / or particle size distribution of the pigment and / or composite pigment is determined by a laser diffraction method using an apparatus capable of determining the particle size in the range of 0.02 to 2000 μm. According to an embodiment of the invention, the particle size and / or the particle size distribution of the pigment and / or the composite pigment are determined with a Malvern 2000 device. According to one embodiment of the invention, the pore volume of the pigment is typically in the range of 0.20 to 0.30 cm 3 / g. According to one embodiment of the invention, the pore volume of the composite pigment is typically in the range of 0.15 to 0.20 cm 3 / g.

Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäi10 nen päällyste käsittää vähintään yhtä huokoista pigmenttiä, joka valitaan komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kalsiumkarbonaattia (MCC). Keksinnön erään suoritusmuodon mukaan TiO2-kalsiumkarbonaattikomposiittipigmentti valmistetaan siten, että saatetaan titaanidioksidi T1O2, kalsiumhydroksidi Ca(OH)2ja hiilidioksidi CO2 reagoimaan keskenään ja saatu TiO2-saostettu kal15 siumkarbonaatti-koostumus käsitellään hapolla kuten esimerkiksi rikkihapolla H2SO4, jolloin happo syövyttää saostetun kalsiumkarbonaatin pinnan huokoiseksi. Modifioituja kalsiumkarbonaatteja (MCC) voidaan valmistaa jauhetusta kalsiumkarbonaatista (GCC) hapoilla syövyttämällä. Marmori ja kalkkikivi ovat jauhetun kalsiumkarbonaatin (GCC) mahdollisia raaka-aineita. MCC:t toimivat hyvin mattapääl20 lysteissä, mutta eivät kiiltävissä huokoisuuden vuoksi.According to one embodiment of the invention, the first coating of the coating composition comprises at least one porous pigment selected from composite pigments comprising titanium dioxide and modified calcium carbonate (MCC). According to one embodiment of the invention, the TiO2-calcium carbonate composite pigment is prepared by reacting titanium dioxide T1O2, calcium hydroxide Ca (OH) 2 and carbon dioxide CO2 and the resulting TiO2-precipitated calcium carbonate is treated with an acid such as sulfuric acid. Modified calcium carbonates (MCC) can be prepared from powdered calcium carbonate (GCC) by acid etching. Marble and limestone are possible raw materials for ground calcium carbonate (GCC). MCCs work well in matte coatings, but are not glossy due to porosity.

Keksinnön mukaisen päällystekoostumuksen ensimmäinen päällyste käsittää lisäksi opasiteettia ja/tai kiiltoa antavaa sideainetta, joka valitaan päällystekoostumuksen käyttötarkoituksen mukaan. Keksinnön erään suoritusmuodon mukaan ensimmäisen päällysteen sideaine on opasiteettia ja kiiltoa antava sideaine. Keksin25 nön erään suoritusmuodon mukaan ensimmäisen päällysteen sideaine on kiiltoa antava sideaine. Keksinnön erään suoritusmuodon mukaan ensimmäisen päällysteen sideaine on opasiteettia antava sideaine. Opasiteettia antavalle sideaineelle on olennaista, että se lisää päällysteen peittokykyä. Esimerkiksi ontot ilmaa sisältävät rakenteet edustavat erästä tekniikkaa, jolla peittokyky sideaineilla saadaan ai30 kaiseksi.The first coating of the coating composition of the invention further comprises an opacifying and / or glossing binder selected according to the intended use of the coating composition. According to one embodiment of the invention, the binder of the first coating is an opacity and gloss binder. According to one embodiment of the invention, the binder of the first coating is a gloss-providing binder. According to one embodiment of the invention, the binder of the first coating is an opacifying binder. It is essential for the opacifying binder that it increase the opacity of the coating. For example, hollow air-containing structures represent a technique for providing coverage with binders.

Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana sekä paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa Erilaisia sideaineita on saatavilla kaupallisesti ja alan 35 ammattilainen valitsee päällystekoostumuksen käyttötarkoituksen mukaan soveltuvan opasiteettia ja/tai kiiltoa antavan sideaineen. Keksinnön erään suoritusmuodonThe coating composition according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate, as well as in coatings for paper, board, plastic, rubber, laminate, concrete and wood, and in paints, especially multilayer paints. and / or a gloss binder. An embodiment of the invention

20185299 prh 29 -03- 2018 mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajissa. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu 5 käytettäväksi maaleissa, erityisesti monikerrosmaaleissa. Soveltuvia sideaineita, joita käytetään yleisesti maaleissa, ovat mm. erilaiset akryyli-, alkydi-, lateksi- ja epoksipolymeeripohjaiset yhdisteet. Muita soveltuvia sideaineita ovat synteettiset tai luonnolliset polymeerit, jotka pohjautuvat mm. vinyyliasetaattiin, vinyylietyleeniin (VAE), polyuretaaniin, polyesteriin, melamiinihartseihin, silaaneihin, siloksaaneihin, 10 tai öljyihin. Esimerkkeinä mm. maaleissa käytettävistä sideaineista ovat Dow:n20185299 prh 29 -03- 2018, the binder is suitable for use in substitutes for fillers in paper, board, plastic, rubber and laminate. According to one embodiment of the invention, the binder is suitable for use in coatings on paper, board, plastic, rubber, laminate, concrete and wood. According to an embodiment of the invention, the binder is suitable for use in paints, in particular multilayer paints. Suitable binders commonly used in paints include e.g. various acrylic, alkyd, latex and epoxy polymer based compounds. Other suitable binders are synthetic or natural polymers based on e.g. vinyl acetate, vinyl ethylene (VAE), polyurethane, polyester, melamine resins, silanes, siloxanes, 10 or oils. Examples include e.g. The binders used in the paints are Dow's

ROPAQUE™ Ultra E-polymeeri, joka antaa peittokykyä (opasiteetti) ja sävyä (vaaleus), mutta ei kiiltoa ja BASF:n Acronal® S 728-polymeeh, joka puolestaan antaa kiiltoa.ROPAQUE ™ Ultra E-polymer that gives opacity (opacity) and hue (brightness) but no gloss and BASF's Acronal® S 728 polymer, which in turn gives gloss.

Keksinnönmukainen päällystekoostumuksen ensimmäinen päällyste käsittää 15 1-30 % sideainetta pigmentti-sideaine- tai komposiittipigmentti-sideainekoostumuksen painosta laskettuna. Keksinnön erään suoritusmuodon mukaan ensimmäinen päällyste käsittää 3-10 % sideainetta pigmentti-sideaine- tai komposiittipigmenttisideainekoostumuksen painosta laskettuna. Keksinnön erään suoritusmuodon mukaan ensimmäinen päällyste käsittää 5 % sideainetta pigmentti-sideaine- tai kom20 posiittipigmentti-sideainekoostumuksen painosta laskettuna.The first coating of the coating composition of the invention comprises 1-30% binder based on the weight of the pigment-binder or composite pigment-binder composition. According to one embodiment of the invention, the first coating comprises 3-10% binder based on the weight of the pigment-binder or composite pigment binder composition. According to one embodiment of the invention, the first coating comprises 5% binder based on the weight of the pigment binder or composite pigment binder composition.

Keksinnön erään suoritusmuodon mukaan ensimmäisen päällysteen pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine-suhde on välillä 7099:30-1. Keksinnön erään suoritusmuodon mukaan pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine-suhde on välillä 90-97:10-3. Keksinnön erään suori25 tusmuodon mukaan pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideainesuhde on 95:5.According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder ratio of the first coating is between 7099: 30-1. According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder ratio is between 90-97: 10-3. According to one embodiment of the invention, the pigment: binder ratio and / or the composite pigment: binder ratio is 95: 5.

Keksinnönmukaisen päällystekoostumuksen toinen päällyste käsittää opasiteettia ja/tai kiiltoa antavaa sideainetta. Keksinnön erään suoritusmuodon mukaan toisen päällysteen sideaine on opasiteettia ja kiiltoa antava sideaine. Keksinnön 30 erään suoritusmuodon mukaan toisen päällysteen sideaine on opasiteettia antava sideaine. Keksinnön erään suoritusmuodon mukaan toisen päällysteen sideaine on kiiltoa antava sideaine. Sideaine valitaan päällystekoostumuksen käyttötarkoituksen mukaan. Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana sekä paperin, kar35 tongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa Erilaisia sideaineita on saatavilla kaupallisesti jaThe second coating of the coating composition of the invention comprises an opacifying and / or glossing binder. According to one embodiment of the invention, the binder of the second coating is an opacity and gloss binder. According to one embodiment of the invention 30, the binder of the second coating is an opacifying binder. According to one embodiment of the invention, the binder of the second coating is a gloss-providing binder. The binder is selected according to the intended use of the coating composition. The coating composition according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate, as well as in coatings for paper, cardboard, plastic, rubber, laminate, concrete and wood, and in paints, especially multilayer paints.

20185299 prh 29 -03- 2018 alan ammattilainen osaa valita päällystekoostumuksen käyttötarkoituksen mukaan soveltuvan sideaineen. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi 5 paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi maaleissa, erityisesti monikerrosmaaleissa. Soveltuvia ja käyttökelpoisia sideaineita ovat mm. erilaiset akryyli-, alkydi-, lateksi-ja epoksipolymeeripohjaiset yhdisteet tai polyvinyylialkoholi- ja polyuretaanipohjaiset yhdisteet. Muita soveltuvia sideaineita ovat syn10 teettiset tai luonnolliset polymeerit, jotka pohjautuvat mm. vinyyliasetaattiin, vinyylietyleeniin (VAE), polyuretaaniin, polyesteriin, melamiinihartseihin, silaaneihin, siloksaaneihin, tai öljyihin. Esimerkkeinä mm. maaleissa käytettävistä sideaineista ovat Dow:n ROPAQUE™ Ultra E-polymeeri, joka antaa peittokykyä (opasiteetti) ja sävyä (vaaleus), mutta ei kiiltoa ja BASF:n Acronal® S 728-polymeeh, joka puoles15 taan antaa kiiltoa.20185299 prh 29 -03- 2018 One skilled in the art will be able to select a suitable binder according to the intended use of the coating composition. According to one embodiment of the invention, the binder is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. According to one embodiment of the invention, the binder is suitable for use in coatings on paper, board, plastic, rubber, laminate, concrete and wood. According to an embodiment of the invention, the binder is suitable for use in paints, in particular multilayer paints. Suitable and usable binders include e.g. various compounds based on acrylic, alkyd, latex and epoxy polymers or compounds based on polyvinyl alcohol and polyurethane. Other suitable binders are synthetic or natural polymers based on e.g. vinyl acetate, vinyl ethylene (VAE), polyurethane, polyester, melamine resins, silanes, siloxanes, or oils. Examples include e.g. The binders used in the paints are Dow's ROPAQUE ™ Ultra E polymer, which gives opacity and hue but no gloss, and BASF's Acronal® S 728 polymer, which in turn gives gloss.

Keksinnönmukainen päällystekoostumus käsittää valinnaisesti kolmannen päällysteen, joka käsittää kiiltoa antavaa sideainetta. Sideaine valitaan päällystekoostumuksen käyttötarkoituksen mukaan. Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteai20 neiden korvaajana sekä paperin, kartongin, muovin, kumin, betonin, laminaatin ja puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa Erilaisia sideaineita on saatavilla kaupallisesti ja alan ammattilainen osaa valita päällystekoostumuksen käyttötarkoituksen mukaan soveltuvan sideaineen. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, ku25 min ja laminaatin täyteaineiden korvaajana. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä. Keksinnön erään suoritusmuodon mukaan sideaine soveltuu käytettäväksi maaleissa, erityisesti monikerrosmaaleissa. Soveltuvia sideaineita ovat mm. erilaiset akryyli-, alkydi-, lateksi- ja epoksipolymeeripohjaiset yh30 disteet tai polyvinyylialkoholi- sekä polyuretaanipohjaiset yhdisteet. Muita soveltuvia sideaineita ovat synteettiset tai luonnolliset polymeerit, jotka pohjautuvat mm. vinyyliasetaattiin, vinyylietyleeniin (VAE), polyuretaaniin, polyesteriin, melamiinihartseihin, silaaneihin, siloksaaneihin, tai öljyihin. Esimerkkinä mm. maaleissa käytettävistä kiiltoa antavista sideaineista on BASF:n Acronal® S 728-polymeeri.The coating composition of the invention optionally comprises a third coating comprising a gloss binder. The binder is selected according to the intended use of the coating composition. The coating composition according to the invention is suitable for use as a substitute for paper, board, plastic, rubber and laminate fillers as well as in paper, board, plastic, rubber, concrete, laminate and wood coatings and paints, especially multi-layer paints. the binder. According to one embodiment of the invention, the binder is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. According to one embodiment of the invention, the binder is suitable for use in coatings on paper, board, plastic, rubber, laminate, concrete and wood. According to an embodiment of the invention, the binder is suitable for use in paints, in particular multilayer paints. Suitable binders include e.g. various compounds based on acrylic, alkyd, latex and epoxy polymers or compounds based on polyvinyl alcohol and polyurethane. Other suitable binders are synthetic or natural polymers based on e.g. vinyl acetate, vinyl ethylene (VAE), polyurethane, polyester, melamine resins, silanes, siloxanes, or oils. As an example, e.g. gloss binders used in paints are BASF's Acronal® S 728 polymer.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäisen päällysteen sideaine on opasiteettia antava sideaine ja toisen päällysteen sideaine on kiiltoa antava sideaine. Keksinnön erään suoritusmuodon mukaan päällystekoostumuksen ensimmäisen päällysteen sideaine on opasiteettia antava sideaine 5 ja toisen päällysteen sideaine on opasiteettia antava sideaine. Keksinnön erään suoritusmuodon mukaan ensimmäisen päällysteen sideaine on opasiteetti antava sideaine, toisen päällysteen sideaine on opasiteettia antava sideaine ja kolmannen päällysteen sideaine on kiiltoa antava sideaine. Keksinnön erään suoritusmuodon mukaan ensimmäisen päällysteen sideaine on opasiteettia antava sideaine, toisen 10 päällysteen sideaine on kiiltoa antava sideaine ja kolmannen päällysteen sideaine on kiiltoa antava sideaine.According to one embodiment of the invention, the binder of the first coating of the coating composition is an opacity binder and the binder of the second coating is a gloss binder. According to one embodiment of the invention, the binder of the first coating of the coating composition is an opacifying binder 5 and the binder of the second coating is an opacifying binder. According to one embodiment of the invention, the binder of the first coating is an opacifying binder, the binder of the second coating is an opacifying binder and the binder of the third coating is a glossing binder. According to one embodiment of the invention, the binder of the first coating is an opacity binder, the binder of the second coating is a gloss binder and the binder of the third coating is a gloss binder.

Keksinnön erään suoritusmuodon mukaan ensimmäisen, toisen ja valinnaisesti kolmannen päällysteen sideaineet soveltuvat käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajina. Keksinnön erään suoritus15 muodon mukaan ensimmäisen, toisen ja valinnaisesti kolmannen päällysteen sideaineet soveltuvat käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä. Keksinnön erään suoritusmuodon mukaan ensimmäisen, toisen ja valinnaisesti kolmannen päällysteen sideaineet soveltuvat käytettäväksi maaleissa, erityisesti monikerrosmaaleissa.According to an embodiment of the invention, the binders of the first, second and optionally third coatings are suitable for use as substitutes for fillers in paper, board, plastic, rubber and laminate. According to one embodiment of the invention, the binders of the first, second and optionally third coatings are suitable for use in paper, board, plastic, rubber, laminate, concrete and wood coatings. According to an embodiment of the invention, the binders of the first, second and optionally third coatings are suitable for use in paints, in particular multilayer paints.

Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana. Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä sekä maaleissa, erityisesti monikerrosmaaleissa. Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi opasiteettia 25 ja vaaleutta antavana päällysteenä. Keksinnönmukainen päällystekoostumus soveltuu käytettäväksi titaanidioksidin korvaajana valmistettavan tuotteen optisten ominaisuuksien heikentymättä.The coating composition according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. The coating composition according to the invention is suitable for use in coatings of paper, cardboard, plastic, rubber, laminate, concrete and wood, as well as in paints, in particular multilayer paints. The coating composition of the invention is suitable for use as an opacity and brightness coating. The coating composition according to the invention is suitable for use as a substitute for titanium dioxide without compromising the optical properties of the product to be manufactured.

Optiseen tehokkuuteen eli valon sirontaan materiaalissa valon yrittäessä kulkea materiaalin läpi vaikuttavat päällystetyissä tai päällystämättömissä materiaa30 leissa seuraavat tekijät:The optical efficiency, i.e. the scattering of light in a material as light attempts to pass through the material, is affected by the following factors in coated or uncoated materials30:

- ilma-kiinteäaine -rajapinnat (ilman taitekerroin n. 1 ja tavallisesti muiden taitekertoimet 1,4 - 1,8, kuten muovien, kuitujen, kumien ja suurimman osan pigmenteistä ja täyteaineista),- air-solid interfaces (refractive index of air about 1 and usually refractive indices of others 1,4 to 1,8, such as plastics, fibers, rubbers and most pigments and fillers),

- pigmenttien etäisyydet toisistaan,- distances between pigments,

- pigmenttien sisäiset tyhjät ilmahuokoset,- empty air pores inside pigments,

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

- aineiden taitekertoimet,- refractive indices of substances,

- pigmenttien pieni keskimääräinen partikkelikoko - optimi puolet valon aallonpituudesta (näkyvä valo asettuu 400-780 nm alueelle),- small average particle size of the pigments - optimal half the wavelength of light (visible light is in the range of 400-780 nm),

- pigmenttien ja sideaineiden partikkelikokojakaumat.- particle size distributions of pigments and binders.

Kriittinen pigmenttitilavuuskonsentraatio (CPVC, Critical Pigment Volume Concentration) on varsinkin päällysteissä tärkeä mitta, joka kuvaa sitä sideaineen ja pigmenttien osuutta päällysteessä, jossa pigmentit on kokonaan päällystetty sideaineella ja pigmenttien väliset tai sisäiset huokoset ovat sideaineiden täyttämät. Tätä CPVC:tä pienemmillä arvoilla sideaineen osuus on suurempi kuin pigmentin 10 määrä päällysteessä ja päinvastoin, kun arvo on suurempi kuin CPVC. Tyypillisesti päällystekerroksen ominaisuudet, kun ylitetään CPVC, kehittyvät siten, että huokoisuus lisääntyy, korroosionkesto kasvaa, tiheys kasvaa, kiilto laskee ja hankauskesto (märkä) laskee.Critical Pigment Volume Concentration (CPVC), especially in coatings, is an important measure of the proportion of binder and pigments in a coating where the pigments are completely coated with a binder and the pores between or within the pigments are filled with binders. At values lower than this CPVC, the proportion of binder is greater than the amount of pigment 10 in the coating and vice versa when the value is higher than CPVC. Typically, the properties of the coating layer, when the CPVC is exceeded, develop such that porosity increases, corrosion resistance increases, density increases, gloss decreases, and abrasion resistance (wet) decreases.

Paperien päällysteissä ja pohjamaaleissa pigmenttiä on tavallisesti huomatta15 vasti enemmän kuin sideainetta. Kiiltävissä maaleissa puolestaan sideainetta on huomattavasti enemmän kuin pigmenttiä. Maalien kiiltoa voidaan lisätä käyttämällä ei-huokoisia, matalan BET-arvon pigmenttejä, kiiltoa antavia sideaineita ja käyttämällä öljypohjaista maalia vesipohjaisen sijaan. Paperien ja kartonkien kiiltoa voidaan lisätä kalanteroinnilla ja käyttämällä levymäisiä pigmenttejä, erityisesti kaolii20 neja.Paper coatings and primers usually contain considerably more pigment than binder. Glossy paints, on the other hand, have significantly more binder than pigment. The gloss of paints can be increased by using non-porous, low BET pigments, gloss binders and using an oil-based paint instead of a water-based one. The gloss of papers and boards can be increased by calendering and using sheet-like pigments, especially kaoli.

PVC on noin 20-40 % kiiltävillä ja puolikiiltävillä maaleilla, joiden optiset ominaisuudet saadaan T1O2 -partikkelien agglomeroitumisen estämisellä edullisesti noin 0,2 - 0,5 pm kokoisilla ekstendereillä. Vähemmän kiiltävillä sisä-ja ulkomaaleilla PVC on tyypillisesti 40 - 65 %. Matta sisämaaleilla, joiden opasiteetti ja vaaleus 25 saavat lisäystä ilmahuokosista päällysteen rakenteessa, PVC on noin 65-95 %.PVC is present in about 20-40% of glossy and semi-gloss paints, the optical properties of which are obtained by preventing agglomeration of T1O2 particles, preferably with extenders of about 0.2 to 0.5. With less glossy interior and exterior paints, PVC is typically 40 to 65%. For matt interior paints whose opacity and brightness 25 receive an increase in air pores in the coating structure, PVC is about 65-95%.

Yllättäen havaittiin, että keksinnönmukaisella päällysteellä ja päällystekoostumuksella voidaan titaanidioksidi korvata osittain (noin 1 paino-%, 1-5 paino-%, 5-15 paino-%, 10-25 paino-%, vähintään 25 paino-%, 25-50 paino-%, 50-75 paino-%) tai täysin (100 paino-%) optisia ominaisuuksia (opasiteetti ja/tai vaaleus) antavana pig30 menttinä optisten ominaisuuksien heikentymättä ja saavuttaa kiiItoarvot, joita ei tunnetuilla huokoisten pigmenttien päällystyssovellusalueilla ole saavutettu.Surprisingly, it was found that the coating and coating composition according to the invention can partially replace titanium dioxide (about 1% by weight, 1-5% by weight, 5-15% by weight, 10-25% by weight, at least 25% by weight, 25-50% by weight). -%, 50-75% by weight) or fully (100% by weight) as a pigment giving optical properties (opacity and / or brightness) without deteriorating the optical properties and achieving brightness values which have not been achieved in known porous pigment coating applications.

Edullisesti tämä saavutetaan keksinnönmukaisella päällysteellä, edullisemmin keksinnönmukaisella päällystekoostumuksella, joka käsittää vähintään yhtä saos18Preferably this is achieved with a coating according to the invention, more preferably with a coating composition according to the invention comprising at least one precipitate18

20185299 prh 29 -03- 2018 tettua huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen ja edullisimmin päällystekoostumuksella, joka käsittää vähintään yhtä saostettua huokoista pigmenttiä ja opasiteettiaja/tai kiiltoa antavaa si5 deainetta käsittävän ensimmäisen päällysteen, opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen ja kolmannen päällysteen, joka käsittää kiiltoa antavaa sideainetta. Tässä kolminkertaisessa päällysteessä, pigmentti pienen sideainemäärän kanssa muodostaa ensimmäisen päällysteen. Toinen päällyste muodostuu opasiteettia antavasta sideaineesta, joka täyttää ensimmäisen päällysteen tyhjät ti10 lat pigmenttien välissä ja osin pigmenttien huokosia. Kolmas päällyste koostuu kiiltoa antavasta sideaineesta, jolla päällystekoostumus tehdään kiiltäväksi. Pigmentin huokoset ovat päällystyksen ja kuivauksen jälkeen ilmaa täynnä, jolloin päällystettäessä opasiteettia antavaa sideainetta (ei pigmenttiä) saadaan kuivauksen jälkeen päällysterakenne, jossa pigmentit antavat optisia ominaisuuksia ja pigmenttien vä15 Iissä oleva opasiteettia antava sideaine synergistä tehokkuutta. Tämä vahvistaa kokonaisvaikutusta enemmän kuin pigmenttipäällyste tai opasiteettia antava sideaine antaisi erikseen. Tämä sopii erityisesti vähän kiiltoa vaativiin päällystesovelluksiin.20185299 prh 29 -03- 2018 with a first coating comprising a porous pigment and an opacity and / or a gloss binder and a second coating comprising an opacity and / or a gloss binder and most preferably with a coating composition comprising at least one precipitated porosity a first coating comprising a dye, a second and a third coating comprising an opacity and / or gloss binder comprising a gloss binder. In this triple coating, the pigment with a small amount of binder forms the first coating. The second coating consists of an opacifying binder that fills the voids between the pigments of the first coating and partially the pores of the pigments. The third coating consists of a gloss-providing binder with which the coating composition is made glossy. The pores of the pigment are filled with air after coating and drying, whereby coating an opacifying binder (not a pigment) gives a coating structure after drying in which the pigments impart optical properties and the opacifying binder in the pigments is synergistic. This reinforces the overall effect more than a pigment coating or opacifying binder alone would provide. This is especially suitable for low gloss coating applications.

Yllättäen havaittiin, että keksinnönmukainen päällystekoostumus, joka käsittää yhtä saostettua huokoista pigmenttiä ja opasiteettiaja/tai kiiltoa antavaa sideainetta 20 käsittävän ensimmäisen päällysteen sekä opasiteettia antavaa sideainetta käsittävän toisen päällysteen, toimii erinomaisen peittokyvyn ja vaaleuden aikaansaavana mattapäällysteenä. Tässä päällystekoostumuksessa ensimmäisen päällysteen sideaine on edullisesti opasiteettia antava sideaine. Tämän päällystekoostumuksen toisen päällysteen sideaine on edullisesti olennaisesti pigmenttivapaa.Surprisingly, it has been found that a coating composition according to the invention comprising a first coating comprising one precipitated porous pigment and an opacity and / or gloss binder 20 and a second coating comprising an opacity binder acts to provide excellent opacity and brightness. In this coating composition, the binder of the first coating is preferably an opacifying binder. The binder for the second coating of this coating composition is preferably substantially pigment-free.

Keksinnönmukainen päällyste ja/tai päällystekoostumus soveltuu käytettäväksi paperin, kartongin, muovin, kumin ja laminaatin täyteaineiden korvaajana. Tällaiset täyteainekoostumukset sisältävät pigmentin lisäksi tavanomaisia täyteainekoostumusten valmistus- ja apuaineita. Lisäksi keksinnönmukainen päällyste ja/tai päällystekoostumus soveltuu käytettäväksi päällysteenä papereilla, karton30 geilla, muoveilla, kumeilla, laminaateilla, betoneilla ja puulla. Tällaiset päällysteet sisältävät pigmentin lisäksi tavanomaisia päällystekoostumusten valmistus-ja apuaineita. Edelleen keksinnönmukainen päällyste ja/tai päällystekoostumus soveltuu käytettäväksi maaleissa. Tällaiset maalit sisältävät pigmentin lisäksi tavanomaisia maalien valmistus- ja apuaineita. Keksinnönmukaisten päällysteiden ja/tai päällys35 tekoostumusten kanssa voidaan käyttää muita pigmenttejä, Teologian säätöaineita, liimoja tai muita tarvittavia apu-ja/tai lisäaineita käyttösovelluksesta riippuen.The coating and / or coating composition according to the invention is suitable for use as a substitute for fillers in paper, board, plastic, rubber and laminate. Such filler compositions contain, in addition to the pigment, conventional excipients for the preparation and excipients of the filler compositions. In addition, the coating and / or coating composition according to the invention is suitable for use as a coating on papers, cardboard, plastics, rubbers, laminates, concretes and wood. Such coatings contain, in addition to the pigment, conventional excipients for the preparation of coating compositions and excipients. Furthermore, the coating and / or coating composition according to the invention is suitable for use in paints. In addition to the pigment, such paints contain conventional paint-making and auxiliaries. Other pigments, theological adjusters, adhesives or other necessary auxiliaries and / or additives may be used with the coatings and / or artificial compositions according to the invention, depending on the application.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Keksinnön erään keksinnön suoritusmuodon mukaan päällyste ja/tai päällystekoostumus soveltuu käytettäväksi opasiteettia ja vaaleutta antavana pigmenttipäällysteenä ja/tai päällysteenä. Keksinnön erään suoritusmuodon mukaan päällyste ja/tai päällystekoostumus soveltuu käytettäväksi titaanidioksidin korvaajana 5 optisten ominaisuuksien heikentymättä. Keksinnönmukainen päällyste ja/tai päällystekoostumus soveltuu käytettäväksi titaanidioksidin korvaajana paperin, kartongin, muovin, kumin ja laminaatin täyteaineena. Lisäksi keksinnönmukainen päällyste ja/tai päällystekoostumus soveltuu käytettäväksi titaanidioksidin korvaajana päällysteissä, joita käytetään papereilla, kartongeilla, muoveilla, kumeilla, beto10 neilla, laminaateilla ja puulla sekä pigmenttinä maaleissa.According to an embodiment of the invention, the coating and / or coating composition is suitable for use as an opacity and brightness pigment coating and / or coating. According to an embodiment of the invention, the coating and / or coating composition is suitable for use as a substitute for titanium dioxide without compromising the optical properties. The coating and / or coating composition according to the invention is suitable for use as a substitute for titanium dioxide as a filler in paper, board, plastic, rubber and laminate. In addition, the coating and / or coating composition according to the invention is suitable for use as a substitute for titanium dioxide in coatings used on papers, paperboards, plastics, rubbers, concretes, laminates and wood, and as a pigment in paints.

Keksinnönmukaisella päällysteellä ja/tai päällystekoostumuksella voidaan korvata noin 1 -100 paino-% titaanidioksidista ilman, että valmistettavan materiaalin ja/tai tuotteen optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällystekoostumuksella voidaan kor15 vata 5 -100 paino-%, 10-100 paino-%, 15-100 paino-% titaanidioksidista ilman, että optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällystekoostumuksella voidaan korvata 25 -100 paino-% titaanidioksidista ilman, että optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällyste20 koostumuksella voidaan korvata 50 -100 paino-% titaanidioksidista ilman, että optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällystekoostumuksella voidaan korvata 75 -100 paino% titaanidioksidista ilman, että optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällystekoostumuk25 sella voidaan korvata noin 25 paino-%, noin 50 paino-%, noin 75 paino-%, noin 100 paino-% titaanidioksidista ilman, että optisissa ominaisuuksissa havaitaan heikentymistä. Erään keksinnön suoritusmuodon mukaan päällysteellä ja/tai päällystekoostumuksella voidaan korvata 100 paino-% titaanidioksidista optisten ominaisuuksien heikentymättä.The coating and / or coating composition according to the invention can replace about 1 to 100% by weight of titanium dioxide without any deterioration in the optical properties of the material and / or product to be produced. According to one embodiment of the invention, the coating and / or the coating composition can replace 5 to 100% by weight, 10 to 100% by weight, 15 to 100% by weight of titanium dioxide without any deterioration in the optical properties. According to one embodiment of the invention, the coating and / or the coating composition can replace 25 to 100% by weight of titanium dioxide without any deterioration in the optical properties. According to one embodiment of the invention, the coating and / or the coating composition 20 can replace 50-100% by weight of titanium dioxide without any deterioration in the optical properties. According to one embodiment of the invention, the coating and / or coating composition can replace 75-100% by weight of titanium dioxide without any deterioration in the optical properties. According to one embodiment of the invention, the coating and / or coating composition can replace about 25% by weight, about 50% by weight, about 75% by weight, about 100% by weight of titanium dioxide without any deterioration in optical properties. According to one embodiment of the invention, the coating and / or the coating composition can replace 100% by weight of titanium dioxide without deteriorating the optical properties.

Koska keksinnönmukaisella päällysteellä tai päällystekoostumuksella voidaan titaanidioksidi korvata täysin tai osittain, saavutetaan sillä huomattava raaka-ainekustannusten lasku. Keksinnönmukaisella päällysteellä tai päällystekoostumuksella saavutetaan edullisemmin vastaava sirontakyky kuin titaanidioksidia käytettäessä. Keksinnönmukaista päällystettä tai päällystekoostumusta käytettäessä voidaan val35 mistettavia materiaaleja ohentaa ja/tai keventää saavutettavan sirontakyvyn (vaaleus ja opasiteetti) heikentymättä titaanidioksidin käyttöön verrattuna. Näin ollen,Since the coating or coating composition according to the invention can completely or partially replace titanium dioxide, it achieves a considerable reduction in raw material costs. The coating or coating composition according to the invention more preferably achieves a similar scattering ability than when titanium dioxide is used. When using the coating or coating composition according to the invention, the materials to be produced can be thinned and / or lightened without compromising the scattering ability (brightness and opacity) achieved compared to the use of titanium dioxide. Hence,

20185299 prh 29 -03- 2018 paperin tai kartongin neliöpainon laskeminen mahdollistuu, päällystekerrosten lukumäärää voidaan pienentää, useista päällystekerroksista voidaan poistaa päällystekerroksia tarpeettomina tai voidaan ohentaa käytettyjä päällystekerroksia, maalia tai laminaattia peittokyvyn ja/tai vaaleuden ja opasiteetin heikentymättä. Näistä toi5 mista kustakin seuraa, että materiaalikustannukset laskevat, tuottavuus parantuu ja ympäristö säästyy.20185299 prh 29 -03- 2018 the basis weight of paper or board can be calculated, the number of coating layers can be reduced, coating layers can be removed from several coating layers as unnecessary or used coating layers, paint or laminate can be thinned without opacity and / or opacity and / or opacity. Each of these measures results in lower material costs, improved productivity and environmental savings.

Keksintö koskee myös menetelmää päällystekoostumuksen, joka käsittää vähintään yhtä huokoista pigmenttiä ja sideainetta käsittävän ensimmäisen päällys10 teen ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen sekä valinnaisesti kiiltoa antavaa sideainetta käsittävän kolmannen päällysteen valmistamiseksi, joka menetelmä käsittää seuraavat vaiheet:The invention also relates to a process for preparing a coating composition comprising a first coating comprising at least one porous pigment and a binder and a second coating comprising an opacity and / or a gloss binder and optionally a third coating comprising a gloss binder, the process comprising the steps of:

a) saatetaan pigmentti ja sideaine tai komposiittipigmentti ja sideaine kosketuksiin toistensa kanssa ensimmäisen päällysteen aikaansaamiseksi,a) contacting the pigment and the binder or the composite pigment and the binder to form a first coating;

b) valinnaisesti kuivataan ensimmäinen päällyste,b) optionally drying the first coating,

c) lisätään toinen opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävä päällyste,c) adding a second coating comprising an opacity and / or gloss binder,

d) valinnaisesti kuivataan saatu päällystekoostumus,d) optionally drying the resulting coating composition,

e) valinnaisesti lisätään kolmas kiiltoa antavaa sideainetta käsittävä päällyste,e) optionally adding a third coating comprising a gloss binder,

f) valinnaisesti kuivataan saatu päällystekoostumus.f) optionally drying the resulting coating composition.

Keksinnön erään suoritusmuodon mukaan menetelmä käsittää seuraavat vaiheet:According to an embodiment of the invention, the method comprises the following steps:

a) saatetaan pigmentti ja sideaine tai komposiittipigmentti ja sideaine kosketuksiin toistensa kanssa ensimmäisen päällysteen aikaansaamiseksi,a) contacting the pigment and the binder or the composite pigment and the binder to form a first coating;

b) kuivataan ensimmäinen päällyste,b) drying the first coating,

c) lisätään toinen opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävä päällyste,c) adding a second coating comprising an opacity and / or gloss binder,

d) kuivataan saatu päällystekoostumus,d) drying the obtained coating composition,

e) lisätään kolmas kiiltoa antavaa sideainetta käsittävä päällyste,e) adding a third coating comprising a gloss binder,

f) kuivataan saatu päällystekoostumus.f) drying the resulting coating composition.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Menetelmän kuivausvaiheet voidaan suorittaa millä tahansa alan ammattilaisen tiedossa ja/tai käytössä olevalla soveltuvalla menetelmällä.The drying steps of the process can be performed by any suitable method known and / or used by a person skilled in the art.

Menetelmä soveltuu yllä yksityiskohtaisesti kuvattujen päällystekoostumusten valmistamiseen.The method is suitable for preparing the coating compositions described in detail above.

Seuraavat esimerkit kuvaavat keksinnön suorittamista, mutta eivät rajaa keksintöä ainoastaan kuvattuihin sovelluksiin.The following examples illustrate the practice of the invention, but do not limit the invention to the described applications only.

EsimerkiteXAMPLES

Materiaalitmaterials

Alla olevissa esimerkeissä on käytetty sideaineina ROPAQUE™ Ultra E-latek10 siä (The Dow Chemical Company, Dow) ja Acronal® S 728-lateksia (BASF Corporation).In the examples below, ROPAQUE® Ultra E-latex (The Dow Chemical Company, Dow) and Acronal® S 728 latex (BASF Corporation) have been used as binders.

ROPAQUE™ Ultra E-lateksi (Dow) antaa peittokykyä (opasiteettia) ja sävyä (vaaleutta), mutta ei kiiltoa. ROPAQUE™ Ultra E-polymeeh on emulsiopolymeeri, joka on pallomainen ja sisältä ontto. Keskusta on täynnä päällysteen liuotinta, kun15 nes kuivaukseen jälkeen liuotin haihtuu ja ontto keskusta on ilman täyttämä tai ilmatäytteinen jo ennen kuivatusta. Keskimääräinen partikkelikoko on noin 0,4 pm. ROPAQUE™ Ultra E ei muodosta yhtenäistä filmiä kuivauksen jälkeen toisin kuin useimmat lateksit. Sitä käytetään tyypillisesti ekstenderinä TiO2-partikkelien agglomeroitumisen estämiseen.ROPAQUE ™ Ultra E-latex (Dow) gives opacity (opacity) and hue (brightness) but no shine. ROPAQUE ™ Ultra E-polymeeh is an emulsion polymer that is spherical and hollow inside. The center is filled with the coating solvent when the solvent evaporates after drying and the hollow center is filled with air or air before drying. The average particle size is about 0.4 μm. ROPAQUE ™ Ultra E does not form a uniform film after drying unlike most latexes. It is typically used as an extender to prevent agglomeration of TiO2 particles.

Acronal® S 728-lateksi (BASF) antaa kiiltoa, mutta ei opasiteettia ja sävyä. Acronal® S 728-polymeeh on styreeniakrylaattikopolymeehn vesipohjainen dispersio, jota käytetään sideaineena.Acronal® S 728 latex (BASF) gives shine but no opacity and shade. Acronal® S 728 polymeeh is an aqueous dispersion of styrene acrylate copolymer used as a binder.

ROPAQUE™ Ultra E-lateksista käytetään nimitystä ”Dow” ja Acronal® S 728lateksista nimitystä ”Basf” esimerkeissä 1-3.ROPAQUE ™ Ultra E latex is referred to as “Dow” and Acronal® S 728 latex is referred to as “Basf” in Examples 1-3.

Esimerkeissä 1-3 käytetään pigmenttinä natriumalumiinimagnesiumsilikaattipigmenttiä (KEU1), joka on valmistettu suomalaisessa patenttihakemuksessa 20176090 kuvatulla valmistusmenetelmällä. Esimerkeissä 1-3 käytetään komposiittipigmenttinä nathumalumiinimagnesiumtitaanidioksidisilikaattipigmenttiä (KEU2), joka on valmistettu suomalaisessa patenttihakemuksessa 20176092 kuvatulla val30 mistusmenetelmällä.Examples 1-3 use sodium aluminum magnesium silicate pigment (KEU1) as a pigment, which has been prepared by the production method described in Finnish patent application 20176090. Examples 1-3 use nathumaluminum magnesium titanium dioxide silicate pigment (KEU2) as a composite pigment, which has been prepared by the preparation method described in Finnish patent application 20176092.

Taulukossa 1 kuvatuissa päällystyspastoissa on 5 % lateksia (Dow tai Basf) vedessä. Tämän vesilietteen pH pidettiin lipeälisäyksillä yli pH-arvon 8,3 ja lisäämällä paksuntajaa (Sterocoll FS, BASF) dispersion viskositeetti säädettiin arvoon 800 - 850 cp (Brookfield, 100 rpm, spindeli 4).The coating pastes described in Table 1 contain 5% latex (Dow or Basf) in water. The pH of this aqueous slurry was maintained by addition of lye above pH 8.3 and the viscosity of the dispersion was adjusted to 800-850 cp (Brookfield, 100 rpm, spindle 4) by adding a thickener (Sterocoll FS, BASF).

Tuloksista nähdään, että Dow-lateksi antaa opasiteettia ja sävyä (vaaleus), mutta ei kiiltoa. Basf-lateksi antaa kiiltoa, mutta ei anna opasiteettia eikä sävyä (vaaleus).The results show that Dow latex gives opacity and hue (brightness) but no shine. Basf latex gives shine but does not give opacity or hue (brightness).

Taulukko 1.Table 1.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto-60°, % Gloss-60 °,% 5 5 ei mitään nothing Dow Dow 71,6 71.6 61,5 61.5 2,7 2.7 5 5 ei mitään nothing Basf Basf 5,1 5.1 4,9 4.9 86,7 86.7

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Esimerkki 1Example 1

Esimerkissä verrattiin pigmenttejä KEU1 ja KEU2 sisältäviä keksinnön mukaisia päällysteitä rutiili-titaanidioksidiin (SR5 liete, Venator) T1O2, kontrolli koepiste. Jäljempänä tämä on merkitty T1O2, kontrolli koepisteeksi. Yllä valmistetuista KEU1ja KEU2-pigmenttidispersioista valmistettiin päällystepasta, jossa oli 5 % kuivaa pigmenttiä vedessä ja kuivasta pigmentin määrästä laskettuna 5 % lateksia (Dow). Tä15 män vesilietteen pH pidettiin lipeälisäyksillä yli pH 8,3:n ja paksuntajaa lisättiin (Sterocoll FS, BASF), kunnes dispersion viskositeetti 800-850 cp (Brookfield, 100 rpm, spindeli 4) oli saavutettu.The example compared the coatings of the invention containing the pigments KEU1 and KEU2 with rutile titanium dioxide (SR5 slurry, Venator) T1O2, control test point. Hereinafter, this is labeled T1O2, control as a test point. From the KEU1 and KEU2 pigment dispersions prepared above, a coating paste was prepared with 5% dry pigment in water and 5% latex (Dow) based on the dry amount of pigment. The pH of this aqueous slurry was maintained by pH additions above pH 8.3 and a thickener (Sterocoll FS, BASF) was added until a dispersion viscosity of 800-850 cp (Brookfield, 100 rpm, spindle 4) was reached.

Opasiteettimittarilla (Rhopoint Novoshade Duo+) määritettiin 5 g/m2 päällysteen opasiteetti ja sävy sekä kiiltomittarilla (Rhopoint Novogloss Trio) kiilto. Pääl20 lyste levitettiin sauvapäällysmenetelmän (RK101 Control Coater) standardisauvalla (K Bar) muovikalvolle (Leneta 1 mm, clear polyester sheets). Päällysteet kuivattiin 60°C:ssa ilmavirrassa.The opacity meter (Rhopoint Novoshade Duo +) was used to determine the opacity and shade of the 5 g / m2 coating and the gloss meter (Rhopoint Novogloss Trio) was used to determine the gloss. The top 20 lyste was applied with a rod coating method (RK101 Control Coater) standard rod (K Bar) to a plastic film (Leneta 1 mm, clear polyester sheets). The coatings were dried at 60 ° C in a stream of air.

Taulukko 2.Table 2.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto-60°, % Gloss-60 °,% 5 5 TiO2, kontrolliTiO 2 , control Dow Dow 71,3 71.3 61,7 61.7 8,2 8.2 5 5 KEU1 KEU1 Dow Dow 71,7 71.7 62,3 62.3 2,2 2.2 5 5 KEU2 KEU2 Dow Dow 82,7 82.7 71,3 71.3 2,2 2.2

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

TiO2:a paremmat peittokyky- (opasiteetti) ja vaaleusarvot (sävy) saadaan molemmilla KEU-pigmenteillä.Opacity (opacity) and brightness (hue) values better than TiO 2 are obtained with both KEU pigments.

Esimerkki 2Example 2

Esimerkissä on osoitettu, että keksinnönmukaisella päällystekoostumuksella päällystämällä saavutetaan synergistä etua pigmenttejä KEU1 ja KEU2 sisältävien keksinnön mukaisten ensimmäisten päällysteiden ja toisena päällysteenä käytetyn sideaineen Dow-lateksin välillä, mikä nostaa opasiteetin ja sävyn aivan uudelle ta10 solle varsinkin KEU2-pigmenttiä käytettäessä. Kiiltoa ei edelleenkään saavuteta johtuen käytetystä Dow-lateksista, joka ei anna kiiltoa vaan opasiteettia ja sävyä.In the example, it has been shown that coating with the coating composition according to the invention achieves a synergistic advantage between the first coatings according to the invention containing KEU1 and KEU2 and the Dow latex of the binder used as the second coating, which raises the opacity and tone to a completely new TA Gloss is still not achieved due to the Dow latex used, which does not give gloss but opacity and hue.

Ensimmäinen päällystys on tehty KEU-pigmenteillä vastaavalla päällystyspastalla kuin on kuvattu esimerkissä 1. Toinen päällystys on valmistettu kuten esimerkissä 1 mutta ilman pigmenttiä pelkällä Dow-lateksilla, joka valmistettiin Matehaalit15 kappaleessa kuvatusti. Keksinnönmukaista päällystyskoostumusta käytettäessä on edullista, että KEU-pigmenttien huokoset saadaan tyhjäksi vedestä välillä kuivaamalla, jolloin Dow-lateksi täyttää huokoset pigmenttien väleistä ja osittain pigmenttien rakenteessa toisen päällystyksen ja kuivauksen jälkeen.The first coating was made with KEU pigments with a coating coating similar to that described in Example 1. The second coating was prepared as in Example 1 but without pigment with Dow latex alone, prepared as described in Matehaalit15. When using the coating composition according to the invention, it is preferred that the pores of the KEU pigments are emptied of water by occasional drying, whereby the Dow latex fills the pores between the pigments and partly in the pigment structure after the second coating and drying.

TiO2, kontrolli koepisteessä päällystepasta on valmistettu kuten esimerkissä 1. 20 Tällä päällystepastalla on ensin muovikalvo päällystetty 5 g/m2 määrällä ja kuivattu. Tämän jälkeen on vielä päällystetty ja kuivattu 2 g/m2 oleva päällyste, jotta sama määrä kuivaa päällystettä olisi Taulukossa 3 kaikissa koepisteissä.TiO2, control at the test point, the coating paste is prepared as in Example 1. 20 This coating paste is first coated with a plastic film at a rate of 5 g / m 2 and dried. The coating is then coated and dried at 2 g / m 2 so that the same amount of dry coating is present in Table 3 at all test points.

Taulukko 3.Table 3.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto60°, % Gloss 60 °,% 5 5 TiO2, kontrolliTiO 2 , control Dow Dow 2 2 TiO2 TiO 2 Dow Dow 72,8 72.8 60,8 60.8 5,3 5.3 5 5 T1O2, kontrolli T1O2, control Dow Dow 2 2 ei pigmenttiä no pigment Dow Dow 76,8 76.8 59,2 59.2 6,1 6.1 5 5 KEU1 KEU1 Dow Dow 2 2 ei pigmenttiä no pigment Dow Dow 78,5 78.5 63,1 63.1 2,6 2.6 5 5 KEU2 KEU2 Dow Dow 2 2 ei pigmenttiä no pigment Dow Dow 87,3 87.3 73,8 73.8 2,5 2.5

Esimerkki 3Example 3

Taulukon 4 tuloksista nähdään, että kun päällystetään kerran TiCU-päällyste5 pastalla, jonka kuivapainosta on puolet pigmenttiä ja puolet lateksia (Basf), saavutetaan tyydyttävä opasiteetti-, sävy-ja kiiltotaso. Pigmenttien KEU1 ja KEU:2 opasiteetti-ja sävyarvot vastaavasti laskevat niistä lukemista, jotka on esitetty edellisissä esimerkeissä. Tämä johtuu siitä, että huokoisten KEU-pigmenttien huokoset ovat täyttyneet Basf-lateksilla, jonka taitekerroin on noin 1,4 -1,5 ja siten suurempi kuin 10 ilman. Kiilto-ominaisuudet ovat myös huonommat kuin T1O2, kontrolli koepisteessä.It can be seen from the results in Table 4 that once a TiCU coating5 is coated with a paste having half pigment and half latex (Basf) in dry weight, a satisfactory level of opacity, hue and gloss is achieved. The opacity and hue values of the pigments KEU1 and KEU: 2, respectively, decrease from those readings given in the previous examples. This is because the pores of the porous KEU pigments are filled with Basf latex having a refractive index of about 1.4 to 1.5 and thus greater than 10 without. Gloss properties are also inferior to T1O2, control at the test point.

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Taulukko 4.Table 4.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Pigmentti: sideaine, % Pigment: binder,% Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto-60°, % Gloss-60 °,% 5 5 TiO2, kontrolliTiO 2 , control Basf Basf 50:50 50:50 67,3 67.3 56,8 56.8 13,2 13.2 5 5 KEU1 KEU1 Basf Basf 50:50 50:50 18,2 18.2 13,8 13.8 5,4 5.4 5 5 KEU2 KEU2 Basf Basf 50:50 50:50 50,6 50.6 41,9 41.9 2,9 2.9

Taulukon 5 tuloksista nähdään, keksinnönmukaisella päällystyskoostumuksella saatuja arvoja, kun päällystepastat on valmistettu samalla tavoin kuin Esimerkissä 1. 5 g/m2 päällystys ensimmäisellä kerralla pastalla, jossa pigmenttiä 95 % ja 5 Dow-lateksia 5 % pigmentin painosta ja kuivaus. Toisella päällystyskerralla 5 g/m2 päällyste Basf-lateksilla, joka antaa kiiltoa. KEU2-pigmentillä saavutetaan sama taso ominaisuuksissa kuin Taulukossa 4 T1O2, kontrolli koepisteessä, tosin paksummalla kokonaispäällystemäärällä.The results of Table 5 show the values obtained with the coating composition according to the invention when the coating pastes were prepared in the same way as in Example 1. 5 g / m 2 coating for the first time with 95% pigment and 5 Dow latex 5% by weight of pigment and drying. With a second coat of 5 g / m 2 coating with Basf latex, which gives a shine. The KEU2 pigment achieves the same level of properties as in Table 4 T1O2, control at the test point, albeit with a thicker total amount of coating.

Taulukko 5.Table 5.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto60°, % Gloss 60 °,% 5 5 KEU1 KEU1 Dow Dow 5 5 ei pigmenttiä no pigment Basf Basf 61,3 61.3 52,6 52.6 12,3 12.3 5 5 KEU2 KEU2 Dow Dow 5 5 ei pigmenttiä no pigment Basf Basf 67,7 67.7 60,3 60.3 13,5 13.5

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Taulukossa 6 esitetään tulokset, kun muovikalvo on päällystetty keksinnönmukaisella päällystyskoostumuksella, jossa on kolme päällystettä. Päällystyskertojen välillä on tehty kuivaus 60°C ilmalla. Ensimmäinen päällystys ja kuivaus ovat samat kuin Esimerkissä 1. Tämän päällysteen päälle on vedetty toisena päällysteenä 2 15 g/m2 oleva Dow-päällyste ilman pigmenttejä (valmistettu Matehaalit-kappaleessa kuvatusti) ja kuivattu. Kolmantena päällysteenä on vedetty tämän päälle 5 g/m2 oleva Basf-päällyste (valmistettu Matehaalit-kappaleessa kuvatusti) ja kuivattu. Näin saavutetaan molemmilla KEU-pigmenteillä samaa tasoa olevat opasiteettisävy-ja kiiltoarvot kuin T1O2, kontrolli koepisteessä.Table 6 shows the results when the plastic film is coated with a coating composition of the invention having three coatings. Drying with 60 ° C air has been done between coats. The first coating and drying are the same as in Example 1. A Dow coating without pigments (prepared as described in the Materials) is applied to this coating as a second coating 2 of 15 g / m 2 and dried. As a third coating, a 5 g / m 2 Basf coating (prepared as described in the Materials section) has been applied and dried. In this way, both KEU pigments achieve the same level of opacity tint and gloss values as T1O2, control at the test point.

Taulukko 6.Table 6.

Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Päällystemäärä, g/m2 Amount of coating, g / m 2 Pigmentti Pigment Sideaine binder Opasiteetti, % Opacity,% Sävy, % Shade,% Kiilto- 60°, % Gloss- 60, % 5 5 TiO2, kontrolli TiO2, control Dow Dow 2 2 ei mi- tään not what a Dow Dow 5 5 ei mi- tään not what a Basf Basf 76,4 76.4 58,5 58.5 14,3 14.3 5 5 KEU1 KEU1 Dow Dow 2 2 ei mi- tään not what a Dow Dow 5 5 ei mi- tään not what a Basf Basf 77,6 77.6 64,2 64.2 15,7 15.7 5 5 KEU2 KEU2 Dow Dow 2 2 ei mi- tään not what a Dow Dow 5 5 ei mi- tään not what a Basf Basf 80,9 80.9 67,2 67.2 13,9 13.9

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

20185299 prh 29 -03- 201820185299 prh 29 -03- 2018

Claims (18)

PatenttivaatimuksetThe claims 1. Päällyste, joka käsittää vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta, jolloin vähintään yksi huokoinen pigmentti valitaan:A coating comprising at least one porous pigment and an opacity and / or gloss binder, wherein the at least one porous pigment is selected from: a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaa5 teista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiini- kalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, 10 kalsium- ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista,a) precipitated aluminosilicates, calcium silicates, you magnesiumsilikaa5, aluminum magnesium silicate, alumiinikalsiumsilikaateista, aluminum, calcium magnesium silicate, zinc silicate, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, any other aluminum, magnesium, calcium, 10 and / or the combination of the zinc silicate / mixture, silicas or any mixture thereof, b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaattia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sink-(b) precipitated composite pigments comprising titanium dioxide and aluminosilicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, aluminum calcium silicate, aluminum calcium magnesium silicate, zinc 15 kisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta, tai15 silicate, aluminum zinc silicate, calcium zinc silicate, calcium magnesium silicate, aluminum calcium zinc silicate, aluminum calcium magnesium zinc silicate, aluminum magnesium zinc silicate, any other of these aluminum, magnesium, calcium and / or silicon 20 c) komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kalsiumkarbonaattia (MCC).C) composite pigments comprising titanium dioxide and modified calcium carbonate (MCC). 2. Patenttivaatimuksen 1 mukainen päällyste, jolloin vähintään yksi huokoinen pigmentti valitaan:The coating of claim 1, wherein the at least one porous pigment is selected from: a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaa25 teista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, 30 kalsium- ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista, taia) precipitated aluminosilicates, calcium silicates, you magnesiumsilikaa25, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, any other aluminum, magnesium, 30 calcium and / or zinc silicate of a combination / mixture, silicas or any mixture thereof, or 20185299 prh 29 -03- 201820185299 prh 29 -03- 2018 b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsilikaattia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagne-(b) precipitated composite pigments comprising titanium dioxide and aluminosilicate, calcium silicate, magnesium silicate, aluminum magnesium silicate, aluminum calcium silicate, aluminum calcium magnesium silicate, zinc silicate, aluminum zinc silicate, 5 siumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmää/seosta, piidioksidia tai mitä tahansa näiden seosta.5 silicon silicate, aluminum calcium zinc silicate, aluminum calcium magnesium zinc silicate, aluminum magnesium zinc silicate, any other combination / mixture of aluminum, magnesium, calcium and / or zinc silicate, silica or any mixture thereof. 3. Patenttivaatimuksen 1 tai 2 mukainen päällyste, jolloin komposiittipigmentti sisäl10 tää noin 5-50 paino-%, noin 10-50 paino-%, noin 15-50 paino-% tai noin 15-30 paino-% titaanidioksidia komposiittipigmentin painosta laskettuna.The coating of claim 1 or 2, wherein the composite pigment comprises about 5-50% by weight, about 10-50% by weight, about 15-50% by weight, or about 15-30% by weight of titanium dioxide based on the weight of the composite pigment. 4. Patenttivaatimuksen 3 mukainen päällyste, jolloin komposiittipigmentti sisältää noin 50 paino-%, noin 30 paino-%, noin 15-paino-%, noin 10-paino-%, noin 5-paino% titaanidioksidia komposiittipigmentin painosta laskettuna.The coating of claim 3, wherein the composite pigment contains about 50% by weight, about 30% by weight, about 15% by weight, about 10% by weight, about 5% by weight of titanium dioxide based on the weight of the composite pigment. 15 5. Minkä tahansa patenttivaatimuksen 1-4 mukainen päällyste, jolloin pigmentti:sideaine-suhde ja/tai komposiittipigmentti:sideaine-suhde on välillä 70-99:30-1.The coating according to any one of claims 1 to 4, wherein the pigment: binder ratio and / or the composite pigment: binder ratio is between 70 and 99: 30-1. 6. Minkä tahansa patenttivaatimuksen 1-5 mukainen päällyste, jolloin sideaine valitaan sideaineista, jotka soveltuvat käytettäviksi paperin, kartongin, muovin, kumin, laminaatin, betonin ja puun päällysteissä sekä maaleissa, erityisesti monikerros-Coating according to any one of claims 1 to 5, wherein the binder is selected from binders suitable for use in paper, board, plastic, rubber, laminate, concrete and wood coatings and paints, in particular multilayer coatings. 20 maaleissa.20 goals. 7. Päällystekoostumus, joka käsittää7. A coating composition comprising - vähintään yhtä huokoista pigmenttiä ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän ensimmäisen päällysteen, ja- a first coating comprising at least one porous pigment and an opacity and / or gloss binder, and - opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen, ja- a second coating comprising an opacifying and / or glossing binder, and 25 - valinnaisesti kiiltoa antavaa sideainetta käsittävän kolmannen päällysteen, jolloin ensimmäisen päällysteen vähintään yksi huokoinen pigmentti valitaan:25 - optionally a third coating comprising a gloss binder, wherein at least one porous pigment of the first coating is selected: a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista,(a) precipitated aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicates, aluminum calcium silicates, aluminum calcium magnesium silicates, zinc silicates, aluminum zinc silicates, 30 kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumiinimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, 30 of calcium zinc silicates, calcium magnesium silicates, aluminum calcium zinc silicates, aluminum calcium magnesium zinc silicates, aluminum magnesium zinc silicates, any other aluminum, magnesium, 20185299 prh 29 -03- 2018 kalsium- ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista,20185299 prh 29 -03- 2018 a combination / mixture of calcium and / or zinc silicate, silicas or any mixture thereof, b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsi-(b) precipitated composite pigments comprising titanium dioxide and aluminosilicate, calcium silicate, magnesium silicate, aluminum magnesium 5 likaattia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmää/seosta, piidiok10 sidia tai mitä tahansa näiden seosta, tai5 silicate, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium and / or zinc silicate combination / mixture piidiok10 hydroxide, or any mixture thereof, or c) komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja modifioitua kalsiumkarbonaattia (MCC).c) composite pigments comprising titanium dioxide and modified calcium carbonate (MCC). 8. Patenttivaatimuksen 7 mukainen päällystekoostumus, jolloin vähintään yksi huokoinen pigmentti valitaan:The coating composition of claim 7, wherein the at least one porous pigment is selected from: 15 a) saostetuista alumiinisilikaateista, kalsiumsilikaateista, magnesiumsilikaateista, alumiinimagnesiumsilikaateista, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, sinkkisilikaateista, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, kalsiummagnesiumsilikaateista, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumii20 nimagnesiumsinkkisilikaateista, mistä tahansa muusta alumiini-, magnesium-, kalsium- ja/tai sinkkisilikaatin yhdistelmästä/seoksesta, piidioksideista tai mistä tahansa näiden seoksista, tai15a) precipitated aluminosilicates, calcium silicates, magnesium silicates, aluminum magnesium silicate, alumiinikalsiumsilikaateista, alumiinikalsiummagnesiumsilikaateista, zinc, alumiinisinkkisilikaateista, kalsiumsinkkisilikaateista, calcium magnesium silicate, alumiinikalsiumsinkkisilikaateista, alumiinikalsiummagnesiumsinkkisilikaateista, alumii20 nimagnesiumsinkkisilikaateista, any other aluminum, magnesium, calcium and / or zinc silicate of a combination / mixture, silicas or any mixture thereof, or b) saostetuista komposiittipigmenteistä, jotka käsittävät titaanidioksidia ja alumiinisilikaattia, kalsiumsilikaattia, magnesiumsilikaattia, alumiinimagnesiumsi25 likaattia, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, sinkkisilikaattia, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, kalsiummagnesiumsilikaattia, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, mitä tahansa muuta alumiini-, magnesium-, kalsium-ja/tai sinkkisilikaatin yhdistelmää/seosta, piidiok30 sidia tai mitä tahansa näiden seosta.b) the precipitated composite pigment comprising titanium dioxide and aluminum silicate, calcium silicate, magnesium silicate, alumiinimagnesiumsi25 silicate, alumiinikalsiumsilikaattia, alumiinikalsiummagnesiumsilikaattia, zinc silicate, alumiinisinkkisilikaattia, kalsiumsinkkisilikaattia, calcium magnesium silicate, alumiinikalsiumsinkkisilikaattia, alumiinikalsiummagnesiumsinkkisilikaattia, alumiinimagnesiumsinkkisilikaattia, any of the other aluminum, magnesium, calcium, and / or zinc silicate combination / mixture, silica or any mixture thereof. 9. Patenttivaatimuksen 7 tai patenttivaatimuksen 8 mukainen päällystekoostumus, jolloin komposiittipigmentti sisältää noin 5-50 paino-%, noin 10-50 paino-%, noin 1550 paino-% tai noin 15-30 paino-% titaanidioksidia komposiittipigmentin painosta laskettuna.The coating composition of claim 7 or claim 8, wherein the composite pigment comprises about 5-50% by weight, about 10-50% by weight, about 1550% by weight, or about 15-30% by weight of titanium dioxide based on the weight of the composite pigment. 20185299 prh 29 -03- 201820185299 prh 29 -03- 2018 10. Patenttivaatimuksen 9 mukainen päällystekoostumus, jolloin komposiittipigmentti sisältää noin 50 paino-%, noin 30 paino-%, noin 15-paino-%, noin 10-paino%, noin 5-paino-% titaanidioksidia komposiittipigmentin painosta laskettuna.The coating composition of claim 9, wherein the composite pigment contains about 50% by weight, about 30% by weight, about 15% by weight, about 10% by weight, about 5% by weight of titanium dioxide based on the weight of the composite pigment. 11. Minkä tahansa patenttivaatimuksen 7-10 mukainen päällystekoostumus, jolloin 5 ensimmäisen päällysteen pigmentti:sideaine-suhde ja/tai komposiittipigmentti:side- aine-suhde on välillä 70-99:30-1.The coating composition according to any one of claims 7 to 10, wherein the pigment: binder ratio and / or the composite pigment: binder ratio of the first coating is between 70 and 99: 30-1. 12. Minkä tahansa patenttivaatimuksen 7-11 mukainen päällystekoostumus, jolloin ensimmäisen päällysteen sideaine valitaan opasiteettia ja/tai kiiltoa antavista sideaineista, jotka soveltuvat käytettäviksi paperin, kartongin, muovin, kumin, betonin,A coating composition according to any one of claims 7 to 11, wherein the binder of the first coating is selected from opacity and / or gloss binders suitable for use in paper, board, plastic, rubber, concrete, 10 laminaatin tai puun päällysteissä tai maaleissa, erityisesti monikerrosmaaleissa.10 in laminate or wood coatings or paints, especially multi-layer paints. 13. Minkä tahansa patenttivaatimuksen 7-12 mukainen päällystekoostumus, jolloin toisen päällysteen sideaine valitaan opasiteettia ja/tai kiiltoa antavista sideaineista, jotka soveltuvat käytettäviksi paperin, kartongin, muovin, kumin, laminaatin, betonin tai puun päällysteissä tai maaleissa, erityisesti monikerrosmaaleissa.Coating composition according to any one of claims 7 to 12, wherein the binder for the second coating is selected from opacity and / or gloss binders suitable for use in coatings or paints of paper, board, plastic, rubber, laminate, concrete or wood, in particular multilayer paints. 15 14. Minkä tahansa patenttivaatimuksen 7-13 mukainen päällystekoostumus, jolloin kolmannen päällysteen sideaine valitaan kiiltoa antavista sideaineista, jotka soveltuvat käytettäviksi paperin, kartongin, muovin, kumin, laminaatin, betonin tai puun päällysteissä tai maaleissa, erityisesti monikerrosmaaleissa.Coating composition according to any one of claims 7 to 13, wherein the binder of the third coating is selected from gloss-providing binders suitable for use in coatings or paints of paper, board, plastic, rubber, laminate, concrete or wood, in particular multilayer paints. 15. Minkä tahansa patenttivaatimuksen 7 -14 mukainen päällystekoostumus, jolloin 20 toinen ja/tai kolmas päällyste on olennaisesti pigmenttivapaa.The coating composition according to any one of claims 7 to 14, wherein the second and / or third coating is substantially pigment-free. 16. Minkä tahansa patenttivaatimuksen 1 - 6 mukainen päällyste tai minkä tahansa patenttivaatimuksen 7-15 mukainen päällystekoostumus, jolloin päällysteen tai ensimmäisen päällysteen sideaine on opasiteettia antava sideaine.The coating of any one of claims 1 to 6, or the coating composition of any one of claims 7 to 15, wherein the binder of the coating or the first coating is an opacifying binder. 17. Minkä tahansa patenttivaatimuksen 1- 6 tai 16 mukaisen päällysteen tai minkä 25 tahansa patenttivaatimuksen 7-16 mukaisen päällystekoostumuksen käyttö paperin, kartongin, muovin, kumin tai laminaatin täyteaineiden korvaajana, tai paperin, kartongin, muovin, kumin, laminaatin, betonin tai puun päällysteissä tai maaleissa, erityisesti monikerrosmaaleissa.Use of a coating according to any one of claims 1 to 6 or 16 or a coating composition according to any one of claims 7 to 16 as a substitute for fillers in paper, board, plastic, rubber or laminate, or in coatings for paper, board, plastic, rubber, laminate, concrete or wood or in paints, especially multilayer paints. 18. Minkä tahansa patenttivaatimuksen 1-6 tai 16 mukaisen päällysteen tai minkä 30 tahansa patenttivaatimuksen 7-16 mukaisen päällystekoostumuksen käyttö titaanidioksidin korvaajana paperin, kartongin, muovin, kumin tai laminaatin täyteaineiden Use of a coating according to any one of claims 1 to 6 or 16 or a coating composition according to any one of claims 7 to 16 as a substitute for titanium dioxide for fillers in paper, board, plastic, rubber or laminate 20185299 prh 29 -03- 2018 korvaajana, tai paperin, kartongin, muovin, kumin, laminaatin, betonin tai puun päällysteissä tai maaleissa, erityisesti monikerrosmaaleissa.20185299 prh 29 -03- 2018 as a substitute, or in coatings or paints of paper, cardboard, plastic, rubber, laminate, concrete or wood, especially in multi-layer paints. 19. Patenttivaatimuksen 18 mukainen käyttö, jolloin päällysteellä tai päällystekoostumuksella korvataan 25-100 paino-%, 50-100 paino-%, 75-100 paino-% tai 100Use according to claim 18, wherein the coating or coating composition replaces 25-100% by weight, 50-100% by weight, 75-100% by weight or 100% by weight. 5 paino-% titaanidioksidista.5% by weight of titanium dioxide. 20. Menetelmä päällystekoostumuksen, joka käsittää vähintään yhtä huokoista pigmenttiä ja sideainetta käsittävän ensimmäisen päällysteen ja opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävän toisen päällysteen sekä valinnaisesti kiiltoa antavaa sideainetta käsittävän kolmannen päällysteen valmistamiseksi, joka mene-A method of making a coating composition comprising a first coating comprising at least one porous pigment and a binder and a second coating comprising an opacity and / or a gloss-providing binder, and optionally a third coating comprising a gloss-binding binder, the method comprising: 10 telmä käsittää seuraavat vaiheet:The system comprises the following steps: a) saatetaan pigmentti ja sideaine tai komposiittipigmentti ja sideaine kosketuksiin toistensa kanssa ensimmäisen päällysteen aikaansaamiseksi,a) contacting the pigment and the binder or the composite pigment and the binder to form a first coating; b) valinnaisesti kuivataan ensimmäinen päällyste,b) optionally drying the first coating, c) lisätään toinen opasiteettia ja/tai kiiltoa antavaa sideainetta käsittävä päällyste,c) adding a second coating comprising an opacity and / or gloss binder, 15 d) valinnaisesti kuivataan saatu päällystekoostumus,15 d) optionally drying the resulting coating composition, e) valinnaisesti lisätään kolmas kiiltoa antavaa sideainetta käsittävä päällyste,e) optionally adding a third coating comprising a gloss binder, f) valinnaisesti kuivataan saatu päällystekoostumus.f) optionally drying the resulting coating composition. 21. Patenttivaatimuksen 20 mukainen menetelmä, jolloin päällystekoostumus on minkä tahansa patenttivaatimuksen 7-16 mukainen.The method of claim 20, wherein the coating composition is according to any one of claims 7 to 16.
FI20185299A 2018-03-29 2018-03-29 Coating and coating composition FI20185299A1 (en)