ES2349823B1 - FABRICS FUNCTIONED WITH CARBON NANOTUBES - Google Patents

FABRICS FUNCTIONED WITH CARBON NANOTUBES Download PDF

Info

Publication number
ES2349823B1
ES2349823B1 ES201030982A ES201030982A ES2349823B1 ES 2349823 B1 ES2349823 B1 ES 2349823B1 ES 201030982 A ES201030982 A ES 201030982A ES 201030982 A ES201030982 A ES 201030982A ES 2349823 B1 ES2349823 B1 ES 2349823B1
Authority
ES
Spain
Prior art keywords
carbon nanotubes
carboxylic
stage
functionalized
amine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
ES201030982A
Other languages
Spanish (es)
Other versions
ES2349823A1 (en
Inventor
Jordi Mota Marti
Helena Esteve Nuñez
Lorenzo Bautista Perez
David Amantia
Roshan Paul
Moises Moron Soler
Meritxell De La Varga Ortiz
Marolda Brouta-Agnesa
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Marina Textil S L
MARINA TEXTIL SL
Original Assignee
Marina Textil S L
MARINA TEXTIL SL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Marina Textil S L, MARINA TEXTIL SL filed Critical Marina Textil S L
Priority to ES201030982A priority Critical patent/ES2349823B1/en
Publication of ES2349823A1 publication Critical patent/ES2349823A1/en
Application granted granted Critical
Publication of ES2349823B1 publication Critical patent/ES2349823B1/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Tejidos funcionalizados con nanotubos de carbono.#Procedimiento de preparación de un tejido funcionalizado con nanotubos de carbono y su uso en la fabricación de equipos de protección individual con propiedades antiestáticas e ignífugas resistentes a la abrasión y a los lavados.Fabrics functionalized with carbon nanotubes. # Procedure for preparing a fabric functionalized with carbon nanotubes and their use in the manufacture of personal protective equipment with anti-static and flame retardant properties resistant to abrasion and washing.

Description

Tejidos funcionalizados con nanotubos de carbono. Fabrics functionalized with carbon nanotubes.

La presente invención se refiere al procedimiento de preparación de un tejido funcionalizado con nanotubos de carbonoasícomoalostejidos directamente obtenidospordicho procedimientoyasuusoenlafabricacióndeequipos de protección individual con propiedades antiestáticase ignífugas resistentesala abrasiónya loslavados. The present invention refers to the process of preparing a fabric functionalized with carbon nanotubes as well as the fabrics directly obtained by using the procedure used in the manufacture of personal protective equipment with anti-static properties that are resistant to abrasion and washing.

Estado de la técnica State of the art

Enlaactualidad tantolas normativas vigentes comolas propias empresasexigeneldesarrollode tejidos destinados aEPI’scadavezmáscompetitivosyque ofrezcanunamejorymáselevada protecciónal trabajador contralosriesgos que puedan amenazar su salud o su seguridad en el trabajo. At present, both the regulations in force and the companies themselves are in charge of the development of tissues destined for EPI’s each time more competitive and that offer a better improvement and greater protection for workers against risks that may threaten their health or safety at work.

De especial interés son aquellos tejidos que permiten combinar más de una propiedad protectiva sin pérdida de propiedades inherentes a toda prenda textil como son la comodidad, la lavabilidad, etc. Es aquí donde se enmarca el ámbito de aplicación del proyecto.Para las aplicaciones de tejidos de protección es necesario otorgar el máximo de las propiedades combinadasparala obtenciónde productosversátilesyeficientesen situaciones rutinariaso puntuales de peligro para el trabajador. Of special interest are those fabrics that allow combining more than one protective property without loss of properties inherent to any textile garment such as comfort, washability, etc. It is here that the scope of the project is framed. For the applications of protective fabrics it is necessary to grant the maximum of the combined properties to obtain versatile and efficient products in routine or punctual situations of danger to the worker.

Se han descrito estudiosde aplicacióndelananotecnología (nanopartículas, nanosolesynanotubosde carbono) sobre tejidos de protección para incrementar las propiedades mecánicas de los mismos, sin modificar las propiedades ignífugas y antiestáticas ya existentes. De entre todas las opciones estudiadas, el recubrimiento con nanotubos de carbono, resultó incrementarmuyfavorablementela resistenciaala abrasióndelos tejidosde protección. Studies of the application of the technology (nanoparticles, nanosols and carbon tubes) on protective fabrics to increase their mechanical properties have been described, without modifying the existing flame retardant and antistatic properties. Among all the options studied, the coating with carbon nanotubes, was found to increase the resistance to abrasion of the protective fabrics.

Mediantela aplicacióndela nanotecnología se pretende conferira los tejidosde protección una mayor resistencia mecánica sin modificar sus inherentes propiedadesignífugasyantiestáticas, todo ello dirigidoatejidos para protección de agentes forestales, soldadores, etc. Además se pretenden mejorar otras propiedades como son el comportamiento a la fricción, la resistencia al envejecimiento, la solidez a la luz, etc. The application of nanotechnology is intended to confer protection fabrics with greater mechanical resistance without modifying their inherent and static static properties, all of which are aimed at protecting forest agents, welders, etc. In addition, they are intended to improve other properties such as friction behavior, aging resistance, light fastness, etc.

Por tanto, sería deseable utilizar una tecnología basada en la aplicación de nanotubos de carbono con el fin de conferir mejores propiedades mecánicasy antiestáticas a los tejidos de protección de forma que los nanotubos de carbono se adhesionarán a la superficie de la fibra estableciendo un enlace covalente entre ambos que asegure la durabilidad del tratamiento. Para que esto pueda suceder es necesario que tanto la fibra como el nanotubo posean unos grupos funcionales químicos capaces de reaccionar. Así, los tejidos son pretratados con plasma o con reactivos químicos para modificar su composición química superficial. Por otro lado, los nanotubos son sometidos a reacciones químicas para funcionalizarlos. Therefore, it would be desirable to use a technology based on the application of carbon nanotubes in order to confer better mechanical and antistatic properties to the protective fabrics so that the carbon nanotubes will adhere to the surface of the fiber by establishing a covalent bond between both that ensure the durability of the treatment. For this to happen, it is necessary that both the fiber and the nanotube have chemical functional groups capable of reacting. Thus, the tissues are pretreated with plasma or chemical reagents to modify their surface chemical composition. On the other hand, nanotubes are subjected to chemical reactions to functionalize them.

Asimismo, sería deseable evitar la aglomeración de los nanotubos una vez anclados al tejido, lo que impide que el recubrimientonoseahomogéneoyque,portanto,lapropiedad conferidatampocolosea. Likewise, it would be desirable to avoid the agglomeration of the nanotubes once anchored to the tissue, which prevents the coating from being homogenous and, therefore, the property conferred by the body.

Explicación de la invención Explanation of the invention.

Un aspecto de la invención se refiere al procedimiento para la preparación de un tejido que comprende una etapa de unión entre un tejido funcionalizado con grupos carboxílicosynanotubos de carbono funcionalizados con grupos amino. One aspect of the invention relates to the process for the preparation of a tissue comprising a step of joining between a tissue functionalized with carboxylic groups and carbonanotubes functionalized with amino groups.

Otro aspecto de la presente invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente que comprende una etapade unión entre un tejido funcionalizado con grupos carboxílicosynanotubos de carbono funcionalizados con grupos amino. Another aspect of the present invention relates to a tissue directly obtained by the process defined above comprising a step of joining between a tissue functionalized with carboxylic groups and carbon nanotubes functionalized with amino groups.

La presente invención también se refiere al uso de un tejido obtenido directamente por el procedimiento definido anteriormente que comprende una etapade unión entre un tejido funcionalizado con grupos carboxílicosynanotubos de carbono funcionalizados con grupos amino para preparar un tejido. The present invention also refers to the use of a fabric obtained directly by the process defined above comprising a step of joining between a tissue functionalized with carboxylic groups and carbon nanotubes functionalized with amino groups to prepare a tissue.

Otro aspecto de la presente invención se refiere a un tejido obtenido directamente por el procedimiento definido anteriormente que comprende una etapade unión entre un tejido funcionalizado con grupos carboxílicosynanotubos de carbono funcionalizados con grupos amino. Another aspect of the present invention relates to a fabric obtained directly by the method defined above comprising a step of joining between a tissue functionalized with carboxylic groups and carbon nanotubes functionalized with amino groups.

La presente invención también se refiere al uso de un tejido obtenido directamente por el procedimiento definido anteriormente que comprende una etapade unión entre un tejido funcionalizado con grupos carboxílicosynanotubos de carbono funcionalizados con grupos amino como equipo de protección individual. The present invention also refers to the use of a fabric obtained directly by the process defined above comprising a step of joining between a tissue functionalized with carboxylic groups and carbon nanotubes functionalized with amino groups as personal protective equipment.

En las definiciones anteriores, el término “tejido” se refiere al cuerpo obtenido en forma de lámina mediante el cruzamiento y enlace de dos series de hilos, filamentos o fibras textiles, una longitudinal y otra transversal. Hay tejidos que se han hecho con un solo hilo, que se enlaza consigo mismo, como en el caso de los géneros de punto por trama, elganchillo, etc; otros están formados por una serie de hilos, como el género de puntopor urdimbrey algunos encajes; ciertos tules, por ejemplo, se hacen con más de dos series de hilos. Por lo general, llamamos tela a toda obra hecha con telar. Si bien existen también telas no tejidas. El tejido común está compuesto por dos series de hilos, longitudinalytransversal;laserielongitudinalsellama urdimbreyla transversalsellamatrama,enlaquecada una de sus unidades recibe el nombre de pasada. Los hilos de cada serie son paralelos entre sí. Ejemplos de tejido incluyen, entre otros, telas tejidas de calada o a la plana tales como tafetán, sarga, raso o satén, de punto o tricot, telas especialesytelas no tejidas. In the previous definitions, the term "tissue" refers to the body obtained in the form of a sheet by crossing and linking two series of threads, textile fibers, one longitudinal and one transversal. There are fabrics that have been made with a single thread, which is linked to itself, as in the case of knitwear by weft, hook, etc; others are formed by a series of threads, such as the knitwear by warp and some lace; certain tulles, for example, are made with more than two series of threads. In general, we call any work made with loom cloth. While there are also nonwoven fabrics. The common fabric is composed of two series of threads, longitudinal and transverse; laserielongitudinalsellama urdimbreyla transversalalsellamatrama, in which one of its units is called a pass. The threads of each series are parallel to each other. Examples of weaving include, among others, woven or flat woven fabrics such as taffeta, twill, satin or satin, knitted or knitted, special fabrics and nonwoven fabrics.

El término “nanotubos de carbono” o “NTC” se refiere a estructuras tubulares de carbono cuyo diámetro es del orden del nanómetro. Son una forma alotrópica del carbono. Su estructura puede considerarse procedente de unaláminade grafito enrollada sobresí misma.Dependiendo del gradode enrollamiento,yla manera como se conformala lámina original,el resultado puede llevarananotubosde distinto diámetroygeometría interna. Estos tubos, conformados comosilosextremosdeun foliose uniesenpor susextremos formandoun canuto,sedenominan “nanotubos monocapa” o de pared simple. Existen, también, “nanotubos multicapas” cuya estructura se asemeja a la de una serie de tubos concéntricos, incluidos unos dentrode otrosyde diámetros crecientes desdeelcentroala periferia. The term "carbon nanotubes" or "NTC" refers to tubular carbon structures whose diameter is of the order of the nanometer. They are an allotropic form of carbon. Its structure can be considered as coming from a graphite coil wound on itself. Depending on the degree of winding, and the way in which the original sheet is formed, the result can lead to tubes of different diameter and internal geometry. These tubes, shaped as the ends of a foliose joined by their ends forming a pipe, are called "monolayer nanotubes" or single wall. There are also "multilayer nanotubes" whose structure resembles that of a series of concentric tubes, including each other and increasing diameters from the center of the periphery.

El término “agentede acoplamiento”se refierea unasustancia capazdefavorecerla unión entredos moléculaspor activacióndeunadeellas,preferiblementeuna sustanciacapazdeactivaraun electrófilotalcomounácido carboxílico para hacerlo reaccionar con un nucleófilo tal como una amina. Ejemplos de “agente de acoplamiento” incluyen entre otros, carbodiimidas tales como N,N’-diciclohexilcarbodiimida (DCC), N,N’-diisopropilcarbodiimida (DIC)y1-etil3-(3-dimetilaminopropil)carbodiimida (EDC). The term "coupling agent" refers to a substance capable of favoring the union between molecules by activation of one of them, preferably a substance capable of activating a total electrophilic carboxylic acid to make it react with a nucleol such as an amine. Examples of "coupling agent" include, among others, carbodiimides such as N, N’-dicyclohexylcarbodiimide (DCC), N, N’-diisopropylcarbodiimide (DIC) and 1-ethyl3- (3-dimethylaminopropyl) carbodiimide (EDC).

El término “detergente aniónico” o “tensioactivo aniónico” se refiere a un detergente cuya carga eléctrica presente enel grupo hidrófiloesnegativa.Hay casosde detergentes,por ejemplo ácidos carboxílicos,queabajopHno presentan carga eléctrica neta, pero que a pH más elevados son aniónicos. Estos tensioactivos se clasifican en este tipo. Los detergentes aniónicos se clasifican en: Acil-aminoácidos tales como acil-glutamatos, acil-péptidos, sarcosinatos y tauratos; ácidos carboxílicos, ésteres de ácidos carboxílicos tales como ácidos de cadena saturada, éteres de ácidos carboxílicos ésteres del ácido fosfórico, ácidos sulfónicos, acil-isotianatos, alquil aril sulfonatos, alquil sulfonatos, sulfosuccinatos, ésteres del ácido sulfúrico, alquil éter sulfatosy alquil sulfatos, preferiblemente dodecil sulfatode sodio (SDS). The term "anionic detergent" or "anionic surfactant" refers to a detergent whose electrical charge is present in the hydrophilic negative group. There are cases of detergents, for example carboxylic acids, which below do not have a net electrical charge, but which at higher pHs are anionic. These surfactants are classified in this type. Anionic detergents are classified into: Acyl amino acids such as acyl glutamates, acyl peptides, sarcosinates and taurates; carboxylic acids, esters of carboxylic acids such as saturated chain acids, ethers of carboxylic acids esters of phosphoric acid, sulfonic acids, acyl isothiates, alkyl aryl sulfonates, alkyl sulfonates, sulfosuccinates, sulfuric acid esters, alkyl ether sulfates and alkyl sulfates, preferably sodium dodecyl sulfate (SDS).

El término “sonicación” se refiere a la aplicación de energía con sonido, preferiblemente ultrasonido, para agitar partículas en una muestra. The term "sonication" refers to the application of sound energy, preferably ultrasound, to agitate particles in a sample.

El término “plasma”se refiereaungasque contiene ionesyelectrones libresyporlo tantoes capazde conducir corrientes eléctricas. Ejemplos de plasma incluyen entre otros, “plasma de vacío” o a baja presión, es un plasma no térmico en el cual la energía de los electrones es considerablemente mayor que la de los ionesymoléculas. Se combinan frecuentemente congases noblestales como helioo argón, oxígeno, hidrógeno,nitrógenoytetrafluorometano, y “plasma atmosférico” creado bajo condiciones atmosféricas caracterizado porque no necesita cámaras de vacío, preferiblemente comprende oxigeno y/o nitrógeno en diferentes proporciones. The term "plasma" refers to the fact that it contains free ions and electrons and is therefore capable of conducting electrical currents. Examples of plasma include, but are not limited to, "vacuum plasma" or at low pressure, it is a non-thermal plasma in which the energy of electrons is considerably greater than that of molecular ions. Noblestal congases such as argon helium, oxygen, hydrogen, nitrogen and fluoromethane, and "atmospheric plasma" created under atmospheric conditions are often combined, characterized in that they do not need vacuum chambers, preferably comprising oxygen and / or nitrogen in different proportions.

El término “ácido policarboxílico” se refierea un ácido carboxílico que comprende2 o más grupos carboxílicos. Ejemplos de ácido policarboxílico incluye entre otros ácido glutámico, ácido aspártico, fumárico,ácido maleico, ácido cítricoyácido succínico. The term "polycarboxylic acid" refers to a carboxylic acid comprising 2 or more carboxylic groups. Examples of polycarboxylic acid include but are not limited to glutamic acid, aspartic acid, fumaric acid, maleic acid, citric acid and succinic acid.

Una “amina” se refiere a un derivado del amoníaco por eliminación de uno de sus átomos de hidrógeno. Según se sustituyan uno, dos o tres hidrógenos, las aminas serán primarias, secundarias o terciarias, respectivamente Un compuesto que contiene un grupo amino es una amina. Ejemplos de amina incluyen entre otros metilamino, dimetilamina, dietilnamina, trietilamina, etilpropilamina, etilmetilpropilamina,sperminayetilentriamina, preferiblemente dietilndiamina. An "amine" refers to an ammonia derivative by removal of one of its hydrogen atoms. As one, two or three hydrogens are substituted, the amines will be primary, secondary or tertiary, respectively. A compound containing an amino group is an amine. Examples of amine include, among others, methylamino, dimethylamine, diethyl amine, triethylamine, ethylpropylamine, ethylmethylpropylamine, spermine and ethylenetriamine, preferably diethyl diamine.

El término “aire”se refiereala mezcladegasesque constituyela atmósfera terrestre,que permanecen alrededor delaTierraporla accióndela fuerzadegravedad.El aire está compuestoenproporciones ligeramentevariablespor sustancias tales comoel nitrógeno (78%), oxígeno (21%),vaporde agua(variable entre0y7%), ozono, dióxidode carbono, hidrógenoyalgunosgases nobles comoel criptónoel argón, es decir,1%de otras sustancias. The term “air” refers to the mixture of gases that constitute the Earth's atmosphere, which remain around the Earth by the action of the force of gravity. The air is composed of slightly variable proportions by substances such as nitrogen (78%), oxygen (21%), water vapor (variable between 0 and 7%), ozone, dioxide carbon, hydrogen and some noble gases such as krypton or argon, that is, 1% of other substances.

El término “abrasión” se refiere a la acción mecánica de rozamiento y desgaste que provoca la erosión de un material o tejido. The term "abrasion" refers to the mechanical action of friction and wear that causes erosion of a material or fabric.

El término “equipo de protección individual” (EPI) se refiere a cualquier equipo destinado a ser llevado o sujetado por el trabajador o trabajadora para que le proteja de uno o varios riesgos que puedan amenazar su seguridad o su saludenel trabajo,así como cualquier complementoo accesorio destinadoatal fin. Ejemplosde equipode protección individual incluye entre otros casco, gorro, capucha, escafandra, máscara, careta, orejeras, tapones para los oídos, visor, filtros,gafas, guantes de protección, armadura, arnés, cinturón, codera, muñequera, pantalones, rodilleras, tobilleras, botas, zuecos, ropade alta visibilidad, traje ignífugo, ropa antiestáticaychaleco salvavidas. The term "personal protective equipment" (PPE) refers to any equipment intended to be carried or held by the worker to protect him from one or more risks that could threaten his safety or his health at work, as well as any complement. accessory destined to end. Examples of personal protective equipment include, among others, a helmet, hat, hood, scuba, mask, mask, earmuffs, earplugs, visor, filters, glasses, protective gloves, armor, harness, belt, elbow, wristband, pants, knee pads, anklets, boots, clogs, high visibility clothing, fire retardant suit, antistatic clothing and life jacket.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porqueel tejido está funcionalizado con grupos carboxílicosylos nanotubosde carbono están funcionalizados con grupos amino. In another embodiment, the invention refers to the procedure defined above characterized in that the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende un agente de acoplamiento. In another embodiment, the invention relates to the process defined above characterized in that it further comprises a coupling agent.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida. In another embodiment, the invention relates to the procedure defined above characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende un catalizador, preferiblemente dimetilaminopiridina. In another embodiment, the invention relates to the process defined above characterized in that it further comprises a catalyst, preferably dimethylaminopyridine.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos. In another embodiment, the invention relates to the process defined above characterized in that it further comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentraciónde nanotubosde carbonoesde entre0,1y10gpor100mLde disolvente, preferiblementede1gpor100 mL. In another embodiment, the invention refers to the procedure defined above characterized in that the concentration of carbon nanotubes is between 0.1 and 10 g per 100 mL of solvent, preferably 1 g per 100 mL.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS). In another embodiment, the invention relates to the process defined above characterized in that it further comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS).

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentraciónde detergente aniónico esde entre0,1a5gpor100mLde disolvente, preferiblementede1gpor100 mL. In another embodiment, the invention refers to the procedure defined above characterized in that the concentration of anionic detergent is between 0.1 to 5 g per 100 ml of solvent, preferably 1 g per 100 mL.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de sonicación. In another embodiment, the invention relates to the procedure defined above characterized in that it further comprises a sonication stage.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tiempo de reaccióndela etapade sonicación esde entre5y120 minutos, preferiblemente30 minutos. In another embodiment, the invention relates to the procedure defined above characterized in that the reaction time of the sonication stage is between 5 and 120 minutes, preferably 30 minutes.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la temperatura de la etapa de sonicación es menor o igual a 60ºC, preferiblemente 40ºC. In another embodiment, the invention relates to the procedure defined above characterized in that the temperature of the sonication stage is less than or equal to 60 ° C, preferably 40 ° C.

En otra realización, la invención se refiere al procedimientodefinido anteriormente caracterizado porque la frecuenciadela etapade sonicación esde entre15y30 KHz, preferiblemente20 KHz. In another embodiment, the invention relates to the procedure defined above characterized in that the frequency of the sonication stage is between 15 and 30 KHz, preferably 20 KHz.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la potencia dela etapade sonicación esde entre entre 150a 1500W, preferiblemente 750W. In another embodiment, the invention relates to the procedure defined above characterized in that the power of the sonication stage is between 150 to 1500 W, preferably 750 W.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentraciónde agentede acoplamientoesde1 a10gpor100mLde disolución final, preferiblementede5gpor100 mL. In another embodiment, the invention refers to the procedure defined above characterized in that the concentration of coupling agent is from 1 to 10 g per 100 mL of final solution, preferably 5 g per 100 mL.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentración de catalizador es de entre 0,5 a 5 g por 100 mL de disolución final, preferiblemente de 1,6 g por 100 mL. In another embodiment, the invention relates to the procedure defined above characterized in that the catalyst concentration is between 0.5 to 5 g per 100 mL of final solution, preferably 1.6 g per 100 mL.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la metodología de formación del enlace amida es por agotamiento. In another embodiment, the invention relates to the procedure defined above characterized in that the amide bond formation methodology is by exhaustion.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tiempo de reacción esde entre1y24h, preferiblementede4h. In another embodiment, the invention relates to the procedure defined above characterized in that the reaction time is between 1 and 24 hours, preferably 4 hours.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la velocidad de rotación es de 10 a 80 revoluciones por minuto, preferiblemente de 40 revoluciones por minuto. In another embodiment, the invention relates to the procedure defined above characterized in that the rotation speed is 10 to 80 revolutions per minute, preferably 40 revolutions per minute.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el sentido de rotación se invierte cada 10 a 120 segundos, preferiblemente cada 60 segundos. In another embodiment, the invention relates to the procedure defined above characterized in that the direction of rotation is reversed every 10 to 120 seconds, preferably every 60 seconds.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la temperaturaala que se llevaa cabola etapade formación del enlace esde0 a 30ºC, preferiblementede 23ºC. In another embodiment, the invention refers to the procedure defined above characterized in that the temperature at which the bond formation stage is carried out is from 0 to 30 ° C, preferably from 23 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de secado. In another embodiment, the invention relates to the process defined above characterized in that it further comprises a drying step.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de secado se llevaa caboauna temperaturade entre85y95ºC, preferiblementea 90ºC. In another embodiment, the invention relates to the process defined above characterized in that the drying step is carried out at a temperature of between 85 and 95 ° C, preferably at 90 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de secado se llevaa cabo en un tiempode2 a5minutos, preferiblemente en5minutos. In another embodiment, the invention relates to the procedure defined above characterized in that the drying step is carried out in a time of 2 to 5 minutes, preferably in 5 minutes.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprendeunaetapadelavadoentres baños:deaguaal100%,deuna mezcladeaguaymetanolal50%yde metanol al 100%. In another embodiment, the invention refers to the procedure defined above characterized in that it also comprises a washstand between bathrooms: 100% water, a mixture of 50% methane and 100% methanol.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado por un tiempo de exposiciónde entre1 a15 minutos. In another embodiment, the invention relates to the procedure defined above characterized by an exposure time of between 1 to 15 minutes.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque comprende una segunda etapa de secado. In another embodiment, the invention relates to the process defined above characterized in that it comprises a second drying stage.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de secado se llevaa caboa una temperaturade entre85y95ºC, preferiblementea 90ºC. In another embodiment, the invention relates to the process defined above characterized in that the drying step is carried out at a temperature of between 85 and 95 ° C, preferably at 90 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de secado se llevaa cabo enun tiempode2 a5minutos, preferiblemente en5minutos. In another embodiment, the invention relates to the procedure defined above characterized in that the drying step is carried out in a time of 2 to 5 minutes, preferably in 5 minutes.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque los nanotubos de carbono son multicapa. In another embodiment, the invention relates to the procedure defined above characterized in that the carbon nanotubes are multilayer.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque los nanotubosde carbono tienen un diámetrode entre5y50 nm, preferiblementede10a20 nm. In another embodiment, the invention relates to the process defined above characterized in that the carbon nanotubes have a diameter between 5-50 nm, preferably 10-20 nm.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque los nanotubos de carbono tienen una pureza mayor del 90% en peso, preferiblemente mayor del 95%. In another embodiment, the invention relates to the process defined above characterized in that the carbon nanotubes have a purity greater than 90% by weight, preferably greater than 95%.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque los nanotubosde carbono tienen unalongitudde entre1y50 µm, preferiblemente de 20 µm. In another embodiment, the invention relates to the process defined above characterized in that the carbon nanotubes have a length between 1 and 50 µm, preferably 20 µm.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque los nanotubos de carbono tienen una concentración de carbono amorfo menor del 3%, una concentración de ceniza menor del 1% en peso, un áreade superficie especial mayorde 350m2 por gramode nanotubosde carbono,yuna conductividad térmica de mas de 2000 W/m.k. In another embodiment, the invention refers to the procedure defined above characterized in that the carbon nanotubes have an amorphous carbon concentration of less than 3%, an ash concentration of less than 1% by weight, a special surface area greater than 350m2 per gram of carbon nanotubes , and a thermal conductivity of more than 2000 W / mk

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tejido comprende: In another embodiment, the invention relates to the procedure defined above characterized in that the tissue comprises:

--
modacrílica, 45-65%, preferiblemente 55%;y modacrylic, 45-65%, preferably 55%; and

--
algodón, 35-55%, preferiblemente 45%. cotton, 35-55%, preferably 45%.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de pretratamiento del tejido para funcionalizarlo con grupos carboxílicos. In another embodiment, the invention relates to the procedure defined above characterized in that it further comprises a stage of pretreatment of the tissue to functionalize it with carboxylic groups.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el pretratamiento se lleva a cabo por plasma de vacío o atmosférico. In another embodiment, the invention relates to the procedure defined above characterized in that the pretreatment is carried out by vacuum or atmospheric plasma.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tratamiento por plasma se caracteriza por oxidarel tejido mediante tratamiento con oxígeno 100%ymezclasde nitrógeno yoxígeno. In another embodiment, the invention relates to the procedure defined above characterized in that the plasma treatment is characterized by oxidizing the tissue by treatment with 100% oxygen and mixtures of nitrogen and oxygen.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la composicióndela mezclade nitrógenoyoxígenoesdeentre0y79%de nitrógenoyde entreun21y100%deoxígeno, preferiblemente del 32%denitrógenoy68%de oxígeno. In another embodiment, the invention relates to the procedure defined above characterized in that the composition of the nitrogen mixture is oxygen between 0 and 79% nitrogen and between 21 and 100% oxygen, preferably 32% denitrogen and 68% oxygen.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tiempo de tratamiento por plasmaesde1 a30 minutos, preferiblementede10a30 minutos. In another embodiment, the invention relates to the procedure defined above characterized in that the plasma treatment time is from 1 to 30 minutes, preferably from 10 to 30 minutes.

En otra realización,lainvención serefiereal procedimiento definido anteriormente caracterizado porquelavelocidad de tratamiento por plasma es de 0,1 a 10 m/minuto, preferiblemente de 0,1 m/minuto. In another embodiment, the invention will be a real procedure defined above characterized in that the plasma treatment speed is 0.1 to 10 m / minute, preferably 0.1 m / minute.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el pretratamiento se lleva a cabo con un ácido policaroboxílico. In another embodiment, the invention relates to the procedure defined above characterized in that the pretreatment is carried out with a polycarboxylic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. In another embodiment, the invention relates to the process defined above characterized in that the polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende un catalizador, preferiblemente hipofosfito sódico. In another embodiment, the invention relates to the process defined above characterized in that it further comprises a catalyst, preferably sodium hypophosphite.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la metodología de aplicación es por agotamiento. In another embodiment, the invention refers to the procedure defined above characterized in that the application methodology is by exhaustion.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentraciónde ácido policarboxílicoesde entre0,5y2%ode entre3y6%, preferiblementedel6%. In another embodiment, the invention relates to the process defined above characterized in that the concentration of polycarboxylic acid is between 0.5 and 2% or between 3 and 6%, preferably 6%.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la concentraciónde catalizadores entre0,2y0,5%o entre2y4%, preferiblementedel4%. In another embodiment, the invention relates to the process defined above characterized in that the concentration of catalysts is between 0.2 and 0.5% or between 2 and 4%, preferably 4%.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tiempo de reacción esde1hora. In another embodiment, the invention relates to the procedure defined above characterized in that the reaction time is now.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la temperaturade reacción esde entre20y35ºC, preferiblementede 23ºC. In another embodiment, the invention relates to the procedure defined above characterized in that the reaction temperature is between 20 and 35 ° C, preferably 23 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de secado caracterizada porque: In another embodiment, the invention relates to the process defined above characterized in that it further comprises a drying step characterized in that:

--
se llevaa cabo en un tiempode entre2y5minutos, preferiblemente en5minutos;y it is carried out in a time between 2 and 5 minutes, preferably in 5 minutes; and

--
a una temperaturade entre85y95ºC, preferiblementede 90ºC. at a temperature between 85 and 95 ° C, preferably 90 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de reticulado caracterizada porque: In another embodiment, the invention refers to the procedure defined above characterized in that it further comprises a cross-linking stage characterized in that:

--
se llevaa cabo en un tiempode entre1y5minutos, preferiblementede5minutos;y it is carried out in a time between 1 and 5 minutes, preferably of 5 minutes; and

--
a una temperaturade entre120y180ºC, preferiblementede 150ºC. at a temperature between 120 and 180 ° C, preferably 150 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: In another embodiment, the invention relates to the process defined above characterized in that the functionalization stage of the carbon nanotubes functionalized with carboxylic groups comprises:

--
unaetapadetratamientodelos nanotubosde carbonoconperóxidodehidrógenoenpresenciadeácidoobase para generar nanotubosde carbono con función carboxílica;y a treatment of carbon nanotubes with hydrogen peroxide in acid presence or base to generate carbon nanotubes with carboxylic function; and

--
una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina. a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el ácido se seleccionade ácido nítrico, ácido sulfúricoymezclasde los mismos. In another embodiment, the invention relates to the process defined above characterized in that the acid is selected from nitric acid, sulfuric acid and mixtures thereof.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la proporcióndela mezclade ácido sulfúricoyácido nítrico es 1:3 respectivamente. In another embodiment, the invention relates to the procedure defined above characterized in that the ratio of the nitric acid sulfuric acid mixture is 1: 3 respectively.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el pretratamientodelos nanotuboscon ácido tienelugarenun tiempode entre1y5h, preferiblemente3h. In another embodiment, the invention relates to the procedure defined above characterized in that the pretreatment of the nanotubes with acid takes place between 1 and 5 hours, preferably 3 hours.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el pretratamiento de los nanotubos con ácido tiene lugar a una temperatura menor o igual a 40ºC, preferiblemente a 40ºC. In another embodiment, the invention relates to the process defined above characterized in that the pretreatment of the nanotubes with acid takes place at a temperature less than or equal to 40 ° C, preferably at 40 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la base se selecciona de hidróxido de amonio. In another embodiment, the invention relates to the procedure defined above characterized in that the base is selected from ammonium hydroxide.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque además comprende una etapa de secado de los nanotubos con función carboxílica. In another embodiment, the invention refers to the process defined above characterized in that it further comprises a step of drying the nanotubes with carboxylic function.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque el tiempo de secado esde6 a12h, preferiblementede12h. In another embodiment, the invention relates to the procedure defined above characterized in that the drying time is 6 to 12 hours, preferably 12 hours.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la temperaturade secado esde 100a120ºC, preferiblementede 100ºC. In another embodiment, the invention relates to the process defined above characterized in that the drying temperature is 100 to 120 ° C, preferably 100 ° C.

En otra realización,lainvención se refiereal procedimiento definido anteriormente caracterizado porquela amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se seleccionade dietilendiamina, sperminayetlilentriamina,preferiblemente dietilenediamina. In another embodiment, the invention refers to a previously defined procedure characterized in that the amine of the carbon nanotubes with carboxylic acid treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylene triamine, preferably diethylene diamine.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC). In another embodiment, the invention relates to the process defined above characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC).

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). In another embodiment, the invention relates to the process defined above characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se llevaa cabo en untiempode entre1y8h, preferiblementede4h. In another embodiment, the invention refers to the procedure defined above characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is carried out in a time between 1 and 8 hours, preferably 4 hours.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función aminasellevaacaboaunatemperaturade entre0y30ºC, preferiblementede23ºC. In another embodiment, the invention relates to the procedure defined above characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is to increase the temperature between 0 and 30 ° C, preferably 23 ° C.

En otra realización, la invención se refiere al procedimiento definido anteriormente caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una etapa de secado, preferiblemente al aire. In another embodiment, the invention refers to the procedure defined above characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a drying stage, preferably in air.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende un agente de acoplamiento. It also comprises a coupling agent.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida. It further comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende un catalizador, preferiblemente dimetilaminopiridina. It also comprises a catalyst, preferably dimethylaminopyridine.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos. It also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende un detergente anionico, preferiblemente dodecil sulfatode sodio(SDS). It also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende una etapa de sonicación. It also includes a sonication stage.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
la metodología de formación del enlace amida es por agotamiento. The methodology for forming the amide bond is due to exhaustion.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende una etapadelavado en tres baños:de aguaal 100%,de una mezclade aguaymetanolal 50% yde metanol al 100%. It also includes a stage washed in three bathrooms: 100% water, a mixture of 50% water and methane and 100% methanol.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
los nanotubos de carbono son multicapa. Carbon nanotubes are multilayer.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y -el tejido comprende: -modacrílica, 45-65%, preferiblemente 55%;y -algodón, 35-55%, preferiblemente 45%. In another embodiment, the invention refers to the procedure defined above characterized in that: -the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; and -the fabric comprises: -modacrylic, 45-65%, preferably 55%; and-cotton, 35-55 %, preferably 45%.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
además comprende una etapade pretratamiento del tejido para funcionalizarlo congrupos carboxílicos. It also includes a tissue pretreatment stage to functionalize it with carboxylic groups.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende una etapade pretratamiento del tejido para funcionalizarlo con grupos carboxílicos;y It also includes a tissue pretreatment stage to functionalize it with carboxylic groups; and

--
el pretratamiento se lleva a cabo por plasma de vacío o atmosférico. Pretreatment is carried out by vacuum or atmospheric plasma.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende una etapa de pretratamiento del tejido para funcionalizarlo con grupos carboxílicos; It also includes a tissue pretreatment stage to functionalize it with carboxylic groups;

--
el pretratamiento se llevaa cabo por plasmadevacíoo atmosférico;y the pretreatment is carried out by atmospheric plasmade evacuation; and

--
el tratamiento por plasma se caracteriza por oxidar el tejido mediante tratamiento con oxígeno 100%ymezclas de nitrógenoyoxígeno. Plasma treatment is characterized by oxidizing the tissue by treatment with 100% oxygen and nitrogen-oxygen mixtures.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende una etapade pretratamiento del tejido para funcionalizarlo congrupos carboxílicos;y It also includes a tissue pretreatment stage to functionalize it with carboxylic groups; and

--
el pretratamiento se lleva a cabo con un ácido policaroboxílico. Pretreatment is carried out with a polycarboxylic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende una etapa de pretratamiento del tejido para funcionalizarlo con grupos carboxílicos; It also includes a tissue pretreatment stage to functionalize it with carboxylic groups;

--
el pretratamiento se llevaa cabo con un ácido policaroboxílico,y pretreatment is carried out with a polycarboxylic acid, and

--
el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. The polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino;y the tissue is functionalized with carboxylic groups and carbon nanotubes are functionalized with amino groups; and

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina. a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubosde carbono con función amina;y -el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos. En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubosde carbono con función amina;y -la base se selecciona de hidróxido de amonio. a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; and - the acid is selected from nitric acid, sulfuric acid and mixtures thereof. In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of Carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function, and the base is selected from ammonium hydroxide.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubosde carbono con función amina;y a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; and

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina. The amine of the treatment stage of the carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos;y the acid is selected from nitric acid, sulfuric acid and mixtures thereof; and

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina. The amine of the treatment stage of the carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; a step of treating carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la base se seleccionade hidróxidode amonio;y the base is selected from ammonium hydroxide; and

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina. The amine of the treatment stage of the carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; a step of treating carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina;y the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine; and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; a step of treating carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos; the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina;y the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine; and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la base se selecciona de hidróxido de amonio; the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
el ácido se seleccionade ácido nítrico, ácido sulfúricoymezclasde los mismos; the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
ademáscomprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la base se selecciona de hidróxido de amonio; the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
además comprende un catalizador, preferiblemente dimetilaminopiridina; further it comprises a catalyst, preferably dimethylaminopyridine;

--
la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: The functionalization stage of carbon nanotubes functionalized with carboxylic groups comprises:

--
una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y a step of treating carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and

--
una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -ademáscomprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; -In addition it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfatode sodio(SDS); -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - furthermore it comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfatode sodio(SDS); -además comprende una etapa de sonicación; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - furthermore it comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
el ácido se seleccionade ácido nítrico, ácido sulfúricoymezclasde los mismos; the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -ademáscomprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; -In addition it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
además comprende un catalizador, preferiblemente dimetilaminopiridina; further it comprises a catalyst, preferably dimethylaminopyridine;

--
además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; it also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof;

--
además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); further comprising an anionic detergent, preferably sodium dodecyl sulfate (SDS);

--
además comprende una etapa de sonicación; It also includes a sonication stage;

--
los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate

nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; -la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanocarbon nanotubes with amine function; -the base is selected from ammonium hydroxide; -the amine of the carbon nanotubes treatment stage with carboxylic function to generate nano

tubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; Carbon tubes with amine function are selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -el ácido se seleccionade ácido nítrico, ácido sulfúricoymezclasde los mismos; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -ademáscomprende un agentede acoplamiento, caracterizadoporqueel agentede acoplamiento se seleccionade carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; -In addition it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC);y the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); and

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). The step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfatode sodio(SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - furthermore it comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC);

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP);

--
el pretratamiento se llevaa cabo con un ácido policaroboxílico,y pretreatment is carried out with a polycarboxylic acid, and

--
el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. The polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: In another embodiment, the invention relates to the procedure defined above characterized in that:

--
eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups;

--
además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; further comprising a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide;

--
además comprende un catalizador, preferiblemente dimetilaminopiridina; further it comprises a catalyst, preferably dimethylaminopyridine;

--
además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; it also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof;

--
además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); further comprising an anionic detergent, preferably sodium dodecyl sulfate (SDS);

--
además comprende una etapa de sonicación; It also includes a sonication stage;

--
los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; -la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC); -la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine; The stage of treatment of carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC); -the stage of treatment of carbon nanotubes with carboxylic function to generate carbon nanotubes

con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP); with amine function it further comprises a catalyst, preferably dimethylaminopyridine (DMAP);

--
el pretratamiento se llevaa cabo con un ácido policaroboxílico,y pretreatment is carried out with a polycarboxylic acid, and

--
el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. The polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfato de sodio (SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina; -el ácido se seleccionadeácido nítrico, ácido sulfúricoymezclasde los mismos; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - also comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a treatment stage of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; - the acid is selected from nitric acid, sulfuric acid and mixtures thereof;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC);

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP);

--
el pretratamiento se llevaa cabo con un ácido policaroboxílico,y pretreatment is carried out with a polycarboxylic acid, and

--
el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. The polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

En otra realización, la invención se refiere al procedimiento definido anteriormente anteriormente caracterizado porque: -eltejidoestá funcionalizadocongrupos carboxílicosylos nanotubosde carbonoestán funcionalizadoscongrupos amino; -además comprende un agente de acoplamiento, caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida; -además comprende un catalizador, preferiblemente dimetilaminopiridina; -además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos; -además comprende un detergente anionico, preferiblemente dodecil sulfatode sodio(SDS); -además comprende una etapa de sonicación; -los nanotubos de carbono son multicapa; -la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: -una etapa de tratamiento de los nanotubos de carbono con peróxido de hidrógeno en presencia de ácido o base para generar nanotubosde carbono con función carboxílica;y -una etapade tratamientode los nanotubosde carbono con función carboxílica con una amina paragenerar nanotubos de carbono con función amina; -la base se selecciona de hidróxido de amonio; In another embodiment, the invention relates to the procedure defined above characterized in that: the fabric is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups; - furthermore it comprises a coupling agent, characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide; - furthermore it comprises a catalyst, preferably dimethylaminopyridine; - also comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof; - furthermore it comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS); - It also includes a sonication stage; -The carbon nanotubes are multilayer; -the stage of functionalization of carbon nanotubes functionalized with carboxylic groups comprises: -a stage of treatment of carbon nanotubes with hydrogen peroxide in the presence of acid or base to generate carbon nanotubes with carboxylic function; and -a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function; -the base is selected from ammonium hydroxide;

--
la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se selecciona de dietilendiamina, sperminay etlilentriamina, preferiblemente dietilenediamina; the amine of the carbon nanotubes with carboxylic function treatment stage to generate carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylenetriamine, preferably diethylene diamine;

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC);

--
la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP); the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP);

--
el pretratamiento se llevaa cabo con un ácido policaroboxílico,y pretreatment is carried out with a polycarboxylic acid, and

--
el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. The polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.

Asimismo,la presenteinvención cubre todas las combinaciones posiblesde las realizaciones particularesypreferidas descritas aquí arriba. Also, the present invention covers all possible combinations of the particular and preferred embodiments described above.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente. In another embodiment, the invention relates to a tissue directly obtained by the procedure defined above.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizado porque se puede lavar. In another embodiment, the invention relates to a fabric directly obtained by the procedure defined above characterized in that it can be washed.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizado porqueel tejido aguantade1 a50 ciclosdelavado doméstico, preferiblementede1 a25 ciclos,yaún más preferiblementede1 a5ciclos. In another embodiment, the invention relates to a fabric directly obtained by the process defined above characterized in that the fabric endures from 1 to 50 cycles of domestic washing, preferably from 1 to 25 cycles, and even more preferably from 1 to 5 cycles.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizadoporquela temperaturadelavadoesde entre30y60ºC,preferiblementea30ºC. In another embodiment, the invention relates to a fabric directly obtained by the process defined above characterized in that the temperature of the wash is between 30 and 60 ° C, preferably at 30 ° C.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizadoporquesepuedelavarauna temperaturade entre30y60ºC,preferiblementea30ºC. In another embodiment, the invention relates to a fabric directly obtained by the method defined above characterized in that it can vary between 30 and 60 ° C, preferably at 30 ° C.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizado porque: In another embodiment, the invention relates to a tissue directly obtained by the procedure defined above characterized in that:

--
se puedelavara una temperaturade entre30y60ºC, preferiblementea 30ºC;y a temperature of between 30 and 60 ° C may be washed, preferably at 30 ° C; and

--
el tejido aguantade1 a50 ciclosdelavado doméstico, preferiblementede1 a25 ciclos,yaún máspreferiblementede1 a5ciclos. The fabric holds 1 to 50 cycles of household washing, preferably 1 to 25 cycles, and even more preferably 1 to 5 cycles.

En otra realización, la invención se refiere a un tejido directamente obtenido por el procedimiento definido anteriormente caracterizado porque presenta resistencia a la abrasión. In another embodiment, the invention relates to a fabric directly obtained by the process defined above characterized in that it exhibits resistance to abrasion.

En otra realización, la invención se refiere al uso del tejido directamente obtenido por el procedimiento definido anteriormente para equipos de protección individual. In another embodiment, the invention relates to the use of the tissue directly obtained by the procedure defined above for personal protective equipment.

En otra realización,lainvención se refiereal procedimiento seleccionadode los ejemplos1a9. In another embodiment, the invention refers to the procedure selected from examples 1-9.

Breve descripción de las figuras Brief description of the fi gures

Figura 1: Reacción de esterificación del ácido succínico con la celulosa. Figura2: MultiWall CarbónNanotubes (ARRYNANO). Figura 3: Imágenes realizadas por “Scanning Electron Microscopy” de tejidos tratados con plasma de aireyoxíFigure 1: Reaction of esterification of succinic acid with cellulose. Figure 2: MultiWall Coal Nanotubes (ARRYNANO). Figure 3: Images made by “Scanning Electron Microscopy” of tissues treated with aireyoxí plasma

geno (foto derecha)ysin tratamiento previode plasma (foto izquierda). Genus (right photo) and without plasma pretreatment (left photo).

Figura 4: Imágenes realizadas por “Scanning Electron Microscopy” de tejidos tratados con ácido succínico (al 6%). Figure 4: Images made by "Scanning Electron Microscopy" of tissues treated with succinic acid (6%).

Figura 5: Imágenes realizadas por “Scanning Electron Microscopy” de tejidos tratados con ácido succínico(al 6%) ycon1lavado domésticoa 30ºC según norma EN-ISO 6330:2001. Figure 5: Images made by “Scanning Electron Microscopy” of tissues treated with succinic acid (6%) and with domestic washing at 30ºC according to EN-ISO 6330: 2001.

Figura6: NTC, sinlavarde las muestras pretratadas con plasma oxigeno/aireytratadas posteriormente con NTC-NH2. Figure 6: NTC, without washing samples pretreated with oxygen / air plasma and subsequently treated with NTC-NH2.

Figura7:NTC,unlavado domésticodelas muestras pretratadas con plasma oxigeno/aireytratadas posteriormente con NTC-NH2. Figure 7: NTC, a domestic wash of samples pretreated with oxygen / air plasma and subsequently treated with NTC-NH2.

Figura8:NTC,cincolavadosdomésticosdelas muestras pretratadasconplasma oxigeno/aireytratadas posteriormente con NTC-NH2. Figure 8: NTC, five domestic washings of pretreated samples with oxygen / air plasm and subsequently treated with NTC-NH2.

La invención se ilustra a continuación mediante los siguientes ejemplos. The invention is illustrated below by the following examples.

Ejemplos Examples

Tipo de tejido Type of fabric

Se han realizado pruebas sobre el tejido suministrado por Marina S.L. cuyas características son las siguientes: -Composición: 55% Modacrílica/45% CO. -Densidad de urdimbre: 25 hilos/cm. -Densidad de trama: 21 pasadas/cm. -Gramaje: 122.2 gr/m2. Para el desarrollo de los tejidos funcionalizados se han definido los pre-tratamientos necesarios a realizar para Tests have been performed on the fabric supplied by Marina S.L. whose characteristics are the following: -Composition: 55% Modacrylic / 45% CO. - Warp density: 25 threads / cm. -Frame density: 21 passes / cm. -Gramaje: 122.2 gr / m2. For the development of functionalized tissues, the necessary pre-treatments to perform for

generar los grupos que serán los puntos de anclaje entre la superficie del tejidoyel recubrimiento de nanotubosde carbono a aplicar. generate the groups that will be the anchor points between the surface of the fabric and the coating of carbon nanotubes to be applied.

Ejemplo1 Example 1

Pretratamiento del tejido por plasma Plasma tissue pretreatment

Pre-tratamientos por plasma para la generación de grupos carboxílicos en la superficie del tejido para ayudar a enlazar los nanotubos funcionalizados con grupos amino. Estos tratamientos se han llevado a cabo mediante los tratamientos de plasma de vacío por oxidación de la fibra a través de tratamientos con aire/oxígeno. Plasma pre-treatments for the generation of carboxylic groups on the tissue surface to help link the functionalized nanotubes with amino groups. These treatments have been carried out by vacuum plasma treatments by oxidation of the fiber through air / oxygen treatments.

a) Tratamientos de plasmapara lageneración de grupos carboxílicos en la superficie del tejido de MOD/CO (modacrílica/algodón) mediante plasma de aire/oxígeno a) Plasma treatments for the generation of carboxylic groups on the fabric surface of MOD / CO (modacrylic / cotton) by air / oxygen plasma

Generación de grupos carboxílicos en la superficie del tejido para ayudar a enlazar los nanotubos funcionalizados. Estose conseguirá mediantelos tratamientosdeplasmadevacíopor oxidacióndela fibra mediante tratamientosde plasmade aireyde oxígeno. Generation of carboxylic groups on the tissue surface to help bind functionalized nanotubes. This will be achieved by means of treatments made of fiber vacuum oxidation by plasma air and oxygen treatments.

Se determinarálageneracióndelos grupos carboxílicos generados por lostratamientosde plasma enla superficie medianteel métodode Bircabonatode Sodio-Clorurode Sodio, unavaloración ácido-base, segúnla norma ASTMD 1926. The generation of carboxylic groups generated by plasma treatments on the surface shall be determined by the method of Sodium-Sodium Chloride Bircabonate, an acid-base titration, according to ASTMD 1926.

b) Pretratamientos con plasma de aire b) Pretreatments with air plasma

Los tratamientos con plasma de baja presión se han realizado sobre tejidos de dimensiones 10 x 10 cm utilizando unequipoTETRA30LFPC(Diener ElectronicGmbH)queposee electrodoscapacitivosqueoperanabaja frecuencia (40 kHz). Se ha utilizado un caudal constante de aire (10 sccm) con una presión inicial de 0.20 mbary una potencia de descargade 900W.Se han realizado tratamientos con plasmade baja presiónpara tiemposde tratamientode1, 5y10min,conplasmade oxígeno,deaireymezcladelosdos.Acontinuaciónse muestralatabla resumendelos tratamientos realizados. Low pressure plasma treatments have been performed on tissues of 10 x 10 cm dimensions using a TEET30LFPC (Diener ElectronicGmbH) equipment that has capacitive electrodes that operate at a low frequency (40 kHz). A constant air flow rate (10 sccm) with an initial pressure of 0.20 mb and a discharge power of 900 W has been used. Low pressure plasma treatments have been carried out for treatment times of 1.5 and 10 min, with oxygen-treated, direct and mixed-mode mixtures. The table below summarizes the treatments carried out.

c) Valoraciónde los grupos funcionalesgenerados c) Assessment of the functional groups generated

Para realizar la valoración de los grupos carboxílicos sobre los tejidos, se ha realizado una valoración indirecta. Estavaloración ácido base,seha realizado mediantela normativa ASTMD1926.Los sustratostextiles tratadoscon plasma han sido protonados con una solución de HCl, para posteriormente, desprotonarlos con la solución básica de NaCl-NaHCO3.Unavez realizadala desprotonazióndelostejidos,lavaloraciónseha realizado mediante una muestra dela solución básica (queya había perdido los protones) con una solución conocidadeHCl. To carry out the assessment of the carboxylic groups on the tissues, an indirect assessment has been carried out. This acid base evaluation has been carried out by means of the ASTMD1926 norm. The plasma-treated textile substrates have been protonated with an HCl solution, to subsequently deprotonate them with the basic solution of NaCl-NaHCO3. Once done the deprotonation of the tissues, washing has been carried out using a sample of the basic solution (which had lost the protons) with a known solution of HCl.

d) Caracterización de los tejidos d) Characterization of tissues

Acontinuación se presentan los resultadosde lasvaloraciones para las muestrasde 55%MAC/45%CO sin tratar (NT)ytratadas con plasmaa baja presión (LPP). The results of the valuations for the 55% MAC / 45% CO untreated (NT) samples and treated with low pressure plasma (LPP) are presented below.

Según los cálculos necesarios reflejados enla normativa(ver norma),el resultado esel siguiente): According to the necessary calculations reflected in the regulations (see standard), the result is as follows):

a = mililitrosde 0.01NHCl consumidos por25mL filtrados. b= mililitrosde 0.01NHClconsumidos por25mLdela solución NaCl-NaHCO3. v = peso del agua, gr. G= peso de la muestra secada, gr. c = capacidad de intercambio catiónico de la muestra en miliquivalentes por 100 gr. a = milliliters of 0.01NHCl consumed per 25mL filtered. b = milliliters of 0.01NHCl consumed per 25m of the NaCl-NaHCO3 solution. v = water weight, gr. G = weight of the dried sample, gr. c = cation exchange capacity of the sample in milliquivalents per 100 gr.

Se observa una mejora en las muestras A1, A5yOA10, pero lo más interesante es la tendencia que tiene cada tipode pretratamiento.El oxígeno consigue una formaciónde grupos carboxílicosmuy lenta,el Airea medidaque aumentamosel tratamiento disminuimosla generacióndelos grupos, mientrasqueenla mezcladegases,se observa un claro aumento de los grupos carboxílicos generados a medida que aumentamos el tiempo de tratamiento. An improvement is observed in the samples A1, A5 and OA10, but the most interesting is the tendency that each type of pretreatment has. The oxygen achieves a very slow formation of carboxylic groups, the Air as we increase the treatment we decrease the generation of the groups, while in the mixture of gases, a clear increase is observed of the carboxylic groups generated as we increase the treatment time.

Por todo ello las condiciones finales para el pre-tratamiento por plasma sobre los tejidos son: Therefore, the final conditions for plasma pre-treatment on tissues are:

• •
Mezclade OxígenoyAireen un 60%de oxígenoy un 40%de aire. Mixture of Oxygen and Air in 60% oxygen and 40% air.

• •
Tiempode tratamientode10minutosyotrode20 minutos,para comprobarquela tendenciaa aumentarla generaciónde grupos carboxílicos conel tiempode tratamiento mostrada enla tabla es cierta,yasípoder conferirle al tejido mas grupos carboxílicos. Treatment time of 10 minutes and another 20 minutes, to verify that the tendency to increase the generation of carboxylic groups with the treatment time shown in the table is true, and thus be able to confer more carboxylic groups to the tissue.

Ejemplo2 Example 2

Pretratamiento del tejido con productos químicos Tissue pretreatment with chemicals

Pre-tratamiento con productos químicos: se ha modificado la superficie de los tejidos con ácido succínico para generarenla superficietextil grupos carboxílicosyunirlos posteriormentealos nanotubosde carbono funcionalizados con grupos amino.Para ello se han utilizado dos sistemasde aplicaciónde acabados:el foulardyel agotamiento. Pre-treatment with chemical products: the surface of the tissues has been modified with succinic acid to generate it in the surface area of carboxylic groups and then merge them into carbon nanotubes functionalized with amino groups. To this end, two finishing application systems have been used: foulardy and depletion.

a) Tratamientos con ácido succínico para la generación de grupos carboxílicos en la superficie del tejido de MOD/CO (modacrílica/algodón) a) Succinic acid treatments for the generation of carboxylic groups on the fabric surface of MOD / CO (modacrylic / cotton)

Para crear los grupos carboxílicos (-COOH) en la celulosa se ha utilizado el ácido succínico (C4H6O4)con un catalizador hipofosfito de sodio (NaPH2O2). To create the carboxylic groups (-COOH) in cellulose, succinic acid (C4H6O4) was used with a hypophosphite sodium catalyst (NaPH2O2).

Enla figura1 se pueden observar los pasosdela reacción para generar grupos carboxílicos enla celulosa.Es una reacciónde esterificación. In Figure 1, the reaction steps to generate carboxylic groups in cellulose can be observed. It is an esterification reaction.

Para confirmar la reacción se ha realizado una prueba para verificar la hidrofilia del tejido. Se ha depositado una gotadeaguaenla superficieyseha comprobadoeltiempoquetardaenser absorbidaporeltejido: To confirm the reaction, a test was performed to verify the hydrophilic tissue. A drop of water has been deposited on the surface and the time taken to be absorbed by the fabric has been checked:

• Tiempo del tejido no tratado: 6,08 s. • Time of untreated tissue: 6.08 s.

• Tiempo del tejido tratado: 2,19 s. Esta diferencia de tiempo en absorber la gota significa que el tejido se ha modificado por la reacción de esterifica• Time of treated tissue: 2.19 s. This time difference in absorbing gout means that the tissue has been modified by the esterification reaction.

ción, creando grupos carboxílicos en su superficie. tion, creating carboxylic groups on its surface.

b) Característicasdeltratamientoymetodologíade aplicación b) Characteristics of the treatment and application methodology

En este caso, la metodología de aplicación ha sido por agotamiento (mediante un equipo de tintura de laboratorio In this case, the application methodology has been due to exhaustion (by means of a laboratory dyeing equipment

Ugolini), donde las características delprocesado han sido las siguientes: Ugolini), where the characteristics of the process have been the following:

• •
Relación de baño 1:20. 1:20 bath ratio.

• •
Concentraciónde ácidoyde catalizador(sehan probadodos concentraciones diferentes): 0,5%(w/w)de ácido succínicoy0.25%(w/w)de catalizador. 6% (w/w)de ácido succínicoy4%(w/w)de catalizador. Acid and catalyst concentration (different concentrations have been tested): 0.5% (w / w) of succinic acid and 0.25% (w / w) of catalyst. 6% (w / w) succinic acid and 4% (w / w) catalyst.

• •
1hde agotamiento a temperatura ambiente. 1h exhaustion at room temperature.

• •
Secado5mina 90ºC. Drying 5min 90 ° C.

• •
Reticulado5mina 150ºC. Crosslinked 5min 150 ° C.

Ejemplo3 Example 3

Funcionalización de los nanotubos de carbono Functionalization of carbon nanotubes

Lasegundafasede este tratamiento contemplala interacción entrelos tejidos tratados mediante técnicasde plasma The second phase of this treatment contemplates the interaction between tissues treated by plasma techniques

o tratamientos químicosylos nanotubosde carbonopreviamente funcionalizados. or chemical treatments and previously functionalized carbon nanotubes.

Acontinuación se detallan los procedimientos utilizados para la obtención de los nanotubos funcionalizados con grupos amino. Esta síntesis consta de dos etapas, la primera en la que se oxidan los nanotubos de carbono para conseguir funciones ácido carboxílico y la segunda, donde estas funciones se transforman en funciones amina a partir de reacciones de acoplamiento con etilenediamina, diciclohexil carbodiimida DCCy4-dimetilaminopiridina (DMAP). The procedures used to obtain the nanotubes functionalized with amino groups are detailed below. This synthesis consists of two stages, the first in which carbon nanotubes are oxidized to achieve carboxylic acid functions and the second, where these functions are transformed into amine functions from coupling reactions with ethylenediamine, dicyclohexyl carbodiimide DCCy4-dimethylaminopyridine ( DMAP)

Productode partida: MultiWall Carbón Nanotubes(ARRYNANO) (figura2). Starting product: MultiWall Carbon Nanotubes (ARRYNANO) (Figure 2).

Stock number: ARM003. Stock number: ARM003.

OD: 10-20 nm. OD: 10-20 nm.

Length: <20 µm. Length: <20 µm.

Purity: >95 wt%. Purity:> 95 wt%.

Amorphous carbón: <3%. Amorphous coal: <3%.

Ash: <1.0wt%. Ash: <1.0wt%.

Special surface area: >350 m2/g. Special surface area:> 350 m2 / g.

Thermal conductivity: ∼2000 W/m·k Thermal conductivity: ∼2000 W / m · k

a) Nanotubos de carbono con función carboxílica (MWCNT-COOH) a) Carbon nanotubes with carboxylic function (MWCNT-COOH)

10gde nanotubosde carbono multi capa (MWCNT) se tratan conuna mezclade ácido sulfúrico,H2SO4 del 98% (150mL)yácido nítrico, HNO3 65%(50mL) (1:3) durante3horas en un bañode ultrasonidosalatemperaturade 40ºC.La suspensiónde nanotubosde carbono funcionalizados se añadea 400mLde agua destiladayse filtraa través de una membrana de policarbonato con un tamaño de poro de1 µm. Los nanotubos de carbono se lavan con agua destilada hasta obtener unpH neutrode las aguas residualesyse secan durante12h a100ºC. 10g of multi-layer carbon nanotubes (MWCNT) are treated with a mixture of sulfuric acid, H2SO4 of 98% (150mL) and nitric acid, HNO3 65% (50mL) (1: 3) for 3 hours in an ultrasonic bath at a temperature of 40 ° C. The suspension of functionalized nanotubes of carbon is added 400mL of distilled water is filtered through a polycarbonate membrane with a pore size of 1 µm. The carbon nanotubes are washed with distilled water until a neutral wastewater is obtained and dried for 12 hours at 100 ° C.

b) Nanotubos de carbono con función amina (MWCNT-NH2) b) Carbon nanotubes with amine function (MWCNT-NH2)

6.5 g de MWNT-COOH se añaden a una solución de etilenediamina (200 mL) con diciclohexil carbodiimida, DCC(255mg,1.23mmol)y4-dimetilaminopiridina,DMAP(150mg,1.23mmol).La mezclaseagitaenunbañode ultrasonidos durante4horasa temperatura ambienteyse filtraa travésde un filtrode papel,lavando con metanol(3x 100 mL). Posteriormente los MWCNT-NH2 se secan al aire. 6.5 g of MWNT-COOH are added to a solution of ethylenediamine (200 mL) with dicyclohexyl carbodiimide, DCC (255mg, 1.23mmol) and 4-dimethylaminopyridine, DMAP (150mg, 1.23mmol). The mixture is stirred in an ultrasound bath for 4 hours at room temperature and a fi lter through a filter. paper, washing with methanol (3x 100 mL). Subsequently the MWCNT-NH2 is air dried.

Cabe destacar que finalmente sólo se han empleado los nanotubos de carbono funcionalizados con grupos amino, ya que la generación de grupos amino en la superficie textil para anclar nanotubos funcionalizados con grupos carboxílicos, no ha ofrecido resultados positivos (no se ha generado la cantidad de grupos suficiente sobre la superficie textil). Por tanto,el estudioseha centradoenla generaciónde grupos carboxílicosenla superficietextil,funcionalizandolos naonotubos de carbono con grupos amino. It should be noted that finally only carbon nanotubes functionalized with amino groups have been used, since the generation of amino groups on the textile surface to anchor nanotubes functionalized with carboxylic groups has not offered positive results (the number of groups has not been generated enough on the textile surface). Therefore, the study has focused on the generation of carboxylic groups on the surface textile, functionalizing the carbon naonotubes with amino groups.

Ejemplo4 Example 4

Reacciones de formación de enlace peptídico Peptide bond formation reactions

Una vez preparados los nanotubos de carbono funcionalizados con el grupo amino (MWCNT-NH2)se hizo interaccionar conlos tejidosde MarinaTextilS.L.,55% MOD/45%CO) utilizandoel procedimientoquese detallaa continuación: Once the carbon nanotubes functionalized with the amino group (MWCNT-NH2) were prepared, the tissues of MarinaTextil S.L., 55% MOD / 45% CO) were interacted using the procedure detailed below:

Primera reacción entre losgrupos -COOHdela celulosayel DCC (dicyclohexylcarbodiimide) (esquema1): First reaction between the groups -COOHdela cellulosayel DCC (dicyclohexylcarbodiimide) (scheme1):

Esquema1 Scheme1

Segunda reacción (esquema2)entreel producto estable anterioryel DMAP (dimethylaminopyridine), produciendo un compuesto derivado de la urea: Second reaction (scheme2) between the previous stable product and DMAP (dimethylaminopyridine), producing a urea-derived compound:

Esquema2 Scheme2

Una última reacción (esquema3)se produce entreel producto anteriorylos nanotubosde carbono funcionalizados NTC-NH2. Esta reacción genera el enlace peptídico de abajoy con el DMAP, que actúa como un catalizador para la reacción. A final reaction (scheme3) occurs between the previous product and the NTC-NH2 functionalized carbon nanotubes. This reaction generates the peptide bond below and with the DMAP, which acts as a catalyst for the reaction.

Esquema3 Scheme3

c) Investigaciónydesarrollodelmétodode aplicaciónde los nanotubosde carbono c) Research and development of the method of application of carbon nanotubes

El procedimiento seguido para eltratamiento de los tejidos con nanotubos de carbono ha sido el siguiente: The procedure followed for the treatment of tissues with carbon nanotubes has been as follows:

Se ha preparado una solución principal: A main solution has been prepared:

◦ ◦
Relación de baño 1:20 total, Total 1:20 bath ratio,

◦ ◦
1g/100 mL de NTC-NH2. 1g / 100 mL of NTC-NH2.

◦ ◦
1g/100 mL de detergente SDS. 1g / 100 mL of SDS detergent.

Se sónica la solución durante 30min en hielo para que no sobrepase los 40ºC con los siguientes parámetros de máquina: The solution is sonicated for 30min on ice so that it does not exceed 40ºC with the following machine parameters:

◦ ◦
Frecuencia de 20 kHz. 20 kHz frequency

◦ ◦
Potenciade 750Whasta obtener una transferenciade 850.000 Joule. Power of 750W until you get a transfer of 850,000 Joule.

Se pesan los vasos para determinar la pérdida de NTC al centrifugar la muestra. Seguidamente se centrifuga la muestra a 2400 rpm durante 10 minutos. The vessels are weighed to determine the loss of NTC upon centrifuging the sample. The sample is then centrifuged at 2400 rpm for 10 minutes.

Acontinuación se decanta la solución dejando el precipitado al fondo. Se dejan secar los NTC precipitados para un posterior pesadoysaberla concentraciónexacta aplicada. Then the solution is decanted leaving the precipitate at the bottom. The precipitated NTCs are allowed to dry for later weighing and the exact concentration applied.

Se enfría una solución preparada en función a la relación de baño total de CH3OH (metanol). A solution prepared is cooled according to the total bath ratio of CH3OH (methanol).

Se preparan5g/100 mLDCC (dicyclohexylcarbodiimidey1,6 g/100 mL DMAP (dimethylaminopyridine)y se añaden al metanol. 5g / 100 mLDCC (dicyclohexylcarbodiimidey1.6 g / 100 mL DMAP (dimethylaminopyridine) are prepared and added to methanol.

Unavez esta solución está preparada, se añadeel tejido, se mezclay se deja en reposodurante15 minutos. Once this solution is prepared, the tissue is added, mixed and left to stand for 15 minutes.

A continuación se juntan las solucionesde metanolylade NTCy finalmente se agotala mezclaenel equipo Ugolini, según las características de procesado que se citan a continuación, The NTC methanolylade solutions are then combined and the Ugolini equipment is finally depleted, according to the processing characteristics mentioned below,

◦ ◦
Tiempo:4h. Time: 4h

◦ ◦
Velocidad de rotación: 40 rpm. Rotation speed: 40 rpm.

◦ ◦
Inversión del sentido cada 60 s. Reversal of the direction every 60 s.

◦ ◦
Temperatura ambiente. Room temperature.

Una vez los tejidos están tratados con los nanotubos de carbono, se secan durante durante 5min a 90ºC. Seguidamente se lavan siguiendo los siguientes baños: agua/agua-metanol/metanol. Once the tissues are treated with the carbon nanotubes, they are dried for 5min at 90 ° C. They are then washed following the following baths: water / water-methanol / methanol.

Finalmente las muestras tratadas se secana 90ºC durante5minutos. Finally the treated samples are dried 90 ° C for 5 minutes.

Ejemplo5 Example 5

CaracterizaciónyOptimizaciónde los NuevosTextiles Desarrollados Characterization and Optimization of the New Textiles Developed

Resultados SEM SEM Results

Tejido (55% mod/45% co) con pre-tratamiento por plasma aire/oxígeno Fabric (55% mod / 45% co) with pre-treatment by air / oxygen plasma

La siguiente figura (Figura3) muestrael tejido sinpre-tratamiento por plasmayel tejido pre-tratado con aire/oxí-geno.Taly como puede observarse,el pre-tratamiento por plasma genera una mayor adhesiónde los nanotubosde carbonoquedando todala superficietextil recubiertade forma uniforme.Elrecubrimiento noparece distinguirlos dos tiposde fibras presentes enel tejido (algodónymodacrílica), sinembargo las fibrasde algodón tienen una mayor cantidad de recubrimiento debido a su estructura química natural que les confiere en su superficie grupos carboxílicos The following figure (Figure 3) shows the tissue without pre-treatment by plasma and the fabric pre-treated with air / oxygen.As may be observed, the pre-treatment by plasma generates a greater adhesion of the carbon nanotubes, leaving all the uniformly coated textile surface.The coating does not appear distinguish between the two types of fibers present in the fabric (cotton and acrylic), however the cotton fibers have a greater amount of coating due to their natural chemical structure that confers on their surface carboxylic groups

o aminos reactivos. or reactive aminos.

La diferencia con los experimentos realizados previamente sobre el mismo tipo de tejido (modacrílica/algodón), estáenlos tratamientospreviosdeplasmaAire/Oxígenoyenla preparacióndela suspensiónde nanotubosde carbono utilizadaenel recubrimiento.Enlosexperimentos anteriores,el análisisde microscopíaporSEM nos mostrabauna clara agregación de los nanotubos de carbono sobre las fibras. The difference with the experiments previously carried out on the same type of fabric (modacrylic / cotton), are in the previous treatments of the Air / Oxygen plasma in the preparation of the suspension of carbon nanotubes used in the coating. In the previous experiments, the microscopy analysis by SEM showed us a clear aggregation of the carbon nanotubes on the fibers.

Sin embargo, en esta nueva estrategia, el uso de potentes ultrasonidos para la homogenización de la solución de nanotubos de carbono, nos ha permitido reducir esta agregación. Además, para optimizar la obtención de enlaces covalentes entre las fibrasy los nanotubos de carbono, se incrementó la concentración (x10) del agente acoplante (DCC)yel catalizador (DMAP).Los resultados obtenidosporSEM demostraronel caráctercovalentedel enlacetipo amida entrela superficiede las fibrasylos nanotubosde carbono. However, in this new strategy, the use of powerful ultrasound for the homogenization of the carbon nanotube solution has allowed us to reduce this aggregation. Furthermore, in order to optimize the obtaining of covalent bonds between the fi bers and the carbon nanotubes, the concentration (x10) of the coupling agent (DCC) and the catalyst (DMAP) was increased. The results obtained by SEM demonstrated the covalent character of the amide type bond between the surface of the fi nanity and carbon nanotubes.

Tejido (55% mod/45% co) con pre-tratamiento con ácido succínico Fabric (55% mod / 45% co) with pre-treatment with succinic acid

Como se puede observar en la figura4el pre-tratamiento con ácido succínico también permite que los nanotubos de carbono se adhieran a la fibra. As can be seen in Figure 4, pre-treatment with succinic acid also allows carbon nanotubes to adhere to the fiber.

En este caso se puede observar como algunos nanotubos sobresalen de la fibray como otros forman parte del recubrimiento que queda adherido a las fibras. Asimismo se observa como en este caso, el recubrimiento no genera una capa muyespesa. Este hecho podría implicar un mayor efecto de los nanotubos de carbono al no quedar demasiado recubiertos (que talvez tapenyreduzcanla acciónde los nanotubosde carbono). In this case it can be seen how some nanotubes protrude from the fi ber and others form part of the coating that is adhered to the fibers. It is also observed how in this case, the coating does not generate a very thick layer. This fact could imply a greater effect of carbon nanotubes by not being too coated (which may cover and reduce the action of carbon nanotubes).

Una vez realizado un ciclo de lavado doméstico, se continúan apreciando nanotubos de carbono en la superficie textil aunque los nanotubosque sobresalíande las fibras, parecen haberse roto (figura5). Once a domestic washing cycle has been carried out, carbon nanotubes continue to be seen on the textile surface, although the nanotubes that protrude from the fibers appear to have broken (Figure 5).

En general, al comparar las imágenes de los tejidos no tratadosylas de los tratados, se observa un cambio en la textura de las fibras indicando el recubrimiento de nanotubos de carbono. Antes del tratamiento, las fibras parecen lisasydespués tienen unamayor rugosidad generadaporlosNTCenla superficiedelas mismas. In general, when comparing the images of the untreated tissues and the treated ones, a change in the texture of the fibers is observed indicating the coating of carbon nanotubes. Before treatment, the fibers appear smooth and then have a greater roughness generated by the NTCs on the surfaces themselves.

Ejemplo6 Example 6

Resistencia a la Abrasión Abrasion resistance

Para determinar si el recubrimiento de nanotubos de carbono mejora las propiedades mecánicas de los tejidos, se realizan ensayos de resistencia a la abrasión según la norma UNE-EN ISO 12947-2 mediante el equipo Nu-Martindale Abrasión and PillingTester. To determine whether the coating of carbon nanotubes improves the mechanical properties of the fabrics, abrasion resistance tests are carried out according to UNE-EN ISO 12947-2 by means of the Nu-Martindale Abrasion and PillingTester equipment.

Acontinuación se muestran los resultadosde resistenciaala abrasiónhastala roturade3hilosde cada unade las probetas: The results of resistance to abrasion to breakage of 3 strands of each of the specimens are shown below:

Talycomopuedeobservarseenlatabla,engeneral,la resistenciaala abrasióndelostejidos pre-tratadosconácido succínico seguido del tratamiento con nanotubos de carbono, es inferior que la del tejido original, reduciéndose más en aquellas probetasquehansido sometidasa5ciclosdelavadoaexcepcióndeltejidoquehasidopre-tratadocon un 0.5% de ácido succínico. Estos resultados pueden conducir a concluir que el uso de ácido reduce las propiedades mecánicas de la fibra, dado que cuanto mayor es la concentración de ácido, menor es el número de ciclos que resiste eltextil.Para comprobarsiel responsablede esta reducciónde resistencia esel ácidoono,se realizaun ensayode abrasión sobre una probeta textil pre-tratada con la concentración de ácido que mejores resultados ha ofrecido(un 0.5% de ácido succínico). Esta probeta resiste 14.000 ciclos hasta la rotura de3 hilos, resultados similares al dela probeta original (la no tratada). Por este motivo, se puede concluir que para los tejidos pre-tratados con ácido, la reducción de la resistencia a la abrasión se debe al recubrimiento de los nanotubos de carbono, que generan una capa sobrelas fibras responsabledevariaryaumentarla rugosidaddelas fibras, hechoporel cual,la fricciónes mayory, por tanto,la resistenciadecarbono puede generar una mayor fricciónypor tanto una reduccióndela abrasión. In general, the resistance to abrasion of pre-treated fabrics with succinic acid followed by treatment with carbon nanotubes can be observed in general, being lower than that of the original tissue, being reduced more in those specimens that have been subjected to 5 cycles of the tissue that have been pre-treated with 0.5% acid. These results may lead to the conclusion that the use of acid reduces the mechanical properties of the fiber, since the higher the concentration of acid, the lower the number of cycles that the textile resists. To verify the responsibility for this reduction in resistance is acid, a Abrasion test on a pre-treated textile specimen with the acid concentration that has offered the best results (0.5% succinic acid). This test tube withstands 14,000 cycles until the break of 3 wires, results similar to the original test tube (the untreated one). For this reason, it can be concluded that for the pre-treated tissues with acid, the reduction in abrasion resistance is due to the coating of the carbon nanotubes, which generate a layer on the fibers responsible for varying and increasing the roughness of the fibers, made of which, friction Mayory, therefore, carbon resistance can generate greater friction and both reduce abrasion.

Por otro lado, para el caso de los tejidos pre-tratados por plasma, la resistencia a la abrasión mejora respecto la muestra original.Taly comoseha observadoenlas imágenesdeSEM,quedaun recubrimiento uniformesobretoda la superficie textil, dejando más libres los nanotubos de carbono a diferencia del recubrimiento que se forma sobre las fibras conel usode ácido.El principalinconveniente del uso del plasma esla baja solideza loslavados que tienenlos tejidos tratados. On the other hand, in the case of pre-treated plasma tissues, the abrasion resistance improves with respect to the original sample. As it has been observed in the SEM images, there is a uniform coating on all the textile surface, leaving carbon nanotubes more unlike the coating. It is formed on the fi bers with the use of acid. The main drawback of the use of plasma is the low solidity of the washings that have treated tissues.

Ejemplo7 Example7

Carácter Antiestático Antistatic Character

Dado que el tejido objeto de estudio posee propiedades antiestáticas, es necesario que tras este tratamiento, estas propiedades no se alteren. Además, el uso de nanotubos de carbono puede contribuir a mejorar las propiedades antiestáticas ya que una de las principales características de los nanotubos de carbono es el poder conductivo que poseen. Por todo esto,ha sidonecesarioevaluar esta propiedad.Para ellosseha aplicadola siguiente norma: EN-1149-3:04. Carácter antiestático. Resistencia eléctrica: medida de las propiedades electroestáticas. Since the tissue under study has antistatic properties, it is necessary that after this treatment, these properties are not altered. In addition, the use of carbon nanotubes can help improve antistatic properties since one of the main characteristics of carbon nanotubes is the conductive power they possess. For all this, it is necessary to evaluate this property. The following standard has been applied to them: EN-1149-3: 04. Antistatic character Electrical resistance: measurement of electrostatic properties.

Este ensayo seha realizado en los tejidos tratados con nanotubosde carbonoypre-tratados con succínico, antesy despuésde1cicloy5ciclosdelavado domésticoa 30ºC. Las muestras pre-tratadas por plasma noseevalúanyaque se ha comprobado mediante SEM, que tras un único ciclo de lavado, la mayor parte de los nanotubos de carbono se pierde. This test has been performed on tissues treated with carbon nanotubes and pre-treated with succinic, before and after the cycle and 5 cycles of domestic washing at 30 ° C. The samples pre-treated by plasma noseevaluanyaque has been verified by SEM, that after a single wash cycle, most of the carbon nanotubes are lost.

La siguiente tabla muestra los resultados de resistencia eléctrica de los tejidos tratadosy no tratados, es decir, la dificultad u oposición que presentan los textiles al paso de corriente eléctrica: The following table shows the electrical resistance results of treated and untreated tissues, that is, the difficulty or opposition that textiles present to the passage of electric current:

Según la norma la material cumple si la resistencia es ≤ 2,5 x 109 Ω According to the standard, the material complies if the resistance is ≤ 2.5 x 109 Ω

Como ya se ha comentado, el tejido tratado ya posee propiedades antiestáticas, con lo que tras el tratamiento con nanotubos de carbono, esta propiedad no debería verse reducida. No obstante, para todos los pre-tratamientos con ácido la resistencia eléctrica se reduce; a excepción del tejido pre-tratado con una concentración de ácido succínico más baja (0.5%). Esto puede deberse principalmente, al espeso recubrimiento que genera una mayor concentración de ácido. Este espesor, tapa los nanotubos de carbono, reduciendo así elefecto conductivo que pueden conferir. Por este motivo, con una menorconcentraciónde ácido, se llegan inclusoa mejorar las propiedadesde resistencia eléctricadel tejido. As already mentioned, the treated tissue already has antistatic properties, so after treatment with carbon nanotubes, this property should not be reduced. However, for all acid pre-treatments the electrical resistance is reduced; with the exception of pre-treated tissue with a lower succinic acid concentration (0.5%). This may be mainly due to the thick coating that generates a higher concentration of acid. This thickness covers the carbon nanotubes, thus reducing the conductive effect they can confer. For this reason, with a lower concentration of acid, the electrical resistance properties of the tissue are even improved.

Ejemplo8 Example8

Carácter Ignífugo Flame Retardant Character

Del mismo modo que el recubrimiento no debe afectar las propiedades antiestáticas, tampoco debe reducir el carácter ignífugoque poseeel tejido.Por este motivosehaevaluadoel carácter ignífugosegúnla norma UNE-EN ISO 15025:03. Ensayo de propagación limitada de la llama. In the same way that the coating should not affect the antistatic properties, it should also not reduce the fire retardant character that the fabric possesses.This is why the fire retardant character has been evaluated according to the UNE-EN ISO 15025: 03 standard. Limited flame spread test.

En ninguna de las muestras se han formado agujeros ni ha habido goteos de restos inflamados. Por otro lado, se considera que las probetas cumplen la norma si el tiempo de postcombustiónyel tiempo de postincandescencia es inferiora2 segundos.Enel casode las muestras original,la que contiene un 0.5%deácido succínico sinlavary la que contiene un 0.5%de ácido succínico tras5 ciclosdelavado,apesarde ser probetas en las queel tiempode postincandescencia es superiora2 segundos (concretamente son6 segundos), se considera que estos resultados son aceptables ya que los puntos de incandescencia no avanzan. Por tanto, de todas las muestras tratadas, las únicas que no cumplenla normayque, consecuentemente, reducenla propiedad ignífuga inicial del tejido no tratado,sonlas dos probetas pre-tratadas con ácido succínicoyrecubiertas con nanotubosde carbono tras haber sido sometidasa5ciclos de lavado. El resto de tratamientos mantienen las propiedades ignífugas iniciales deltejido original. No holes have been formed in any of the samples and there have been no drips of fl ammated remains. On the other hand, the test specimens are considered to comply with the standard if the post-combustion time and the post-glow time is less than 2 seconds. In the case of the original samples, the one containing 0.5% sinlavac succinic acid and the one containing 0.5% succinic acid after 5 washing cycles , despite being test pieces in which the post-glow time is longer than 2 seconds (specifically 6 seconds), these results are considered acceptable since the glow points do not advance. Therefore, of all the treated samples, the only ones that do not comply with the standard and, consequently, reduce the initial fire retardant property of the untreated tissue, are the two pre-treated specimens with succinic acid and coated with carbon nanotubes after having been subjected to 5 wash cycles. The rest of treatments maintain the initial flame retardant properties of the original fabric.

El pre-tratamiento por plasma, tal y como se ha visto en los resultados de SEM, genera un recubrimiento de nanotubosde carbono uniformeyhomogéneoentodala superficietextilymejoradola resistenciamecánicadeltejido. Por tanto, se puede concluir que este tipo de sistema es viable industrialmente ya que hay empresas que poseen equipos de plasma industriales. Además, el posterior tratamiento para el recubrimiento con nanotubos de carbono se realiza por agotamiento, método que requiere de tecnología textil habitualy frecuente en cualquier empresade acabados. Graciasaeste tratamientosepuedenmejorarlas propiedades mecánicasdeltejidode MarinaTextil.Elpretratamiento con ácido succínico mediante agotamiento no genera rigidez ni reducción de la resistencia a la abrasión deltextil.La estructura moleculardel ácido succínico ofrece mejores resultadosde uniónentrelosNTCyeltextil así comouna mayorflexibilidaddel tejido. Además,la técnicadel agotamiento permite obtenerun recubrimientode menor espesor sobrela superficietextil, conloquelos resultadosde resistenciaala abrasión sonmás positivosylos valores de resistencia eléctrica se mantienen incluso llegando a mejorarlos, además de mantener el carácter ignífugo delostejidostrasla aplicación.Estetipodetratamientoofrecebuena solidezaloslavados.Otrohechopositivodeeste tipode aplicaciónesla maquinaria necesariapararealizarelpre-tratamientodeltextilyel posterior recubrimiento. En ambos casos se utiliza maquinaria de agotamiento, hecho que simplificaría el procedimiento a seguir, ya que se utilizaría el mismo equipo durante todo el proceso.A nivel de viabilidad industrial, la tecnología del agotamiento es una técnica habitual en la industria textil, así como los productos necesarios para llevar a cabo el pre-tratamiento textil. Por lo que respecta a los nanotubos de carbono, deberían obtenerse a través de empresas que sean capaces de proveer estos nanotubos funcionalizados con los grupos necesarios (en este caso grupos amino). Por tanto, el método de aplicaciónyobtencióndeestostextiles,es viable industrialmente. Plasma pretreatment, as seen in the SEM results, generates a uniform and homogeneous carbon nanotube coating on the textural surface and improves the mechanical resistance of the fabric. Therefore, it can be concluded that this type of system is industrially viable since there are companies that own industrial plasma equipment. In addition, the subsequent treatment for coating with carbon nanotubes is carried out by exhaustion, a method that requires regular and frequent textile technology in any finishing company. Thanks to this treatment, the mechanical properties of the MarinaTextile fabric can be improved. The pretreatment with succinic acid by depletion does not generate stiffness or reduction of the abrasion resistance of the textile. The molecular structure of the succinic acid offers better bonding results between NTC and the textile as well as a greater flexibility of the tissue. In addition, the exhaustion technique allows to obtain a thinner coating on the textile surface, with the results of abrasion resistance being more positive and the electrical resistance values are maintained even improving them, in addition to maintaining the flame retardant nature of the fabrics after application. This type of treatment offers good welding. covering. In both cases, depletion machinery is used, a fact that would simplify the procedure to be followed, since the same equipment would be used throughout the process. At the level of industrial viability, depletion technology is a common technique in the textile industry, as well as the products necessary to carry out the textile pre-treatment. As regards carbon nanotubes, they should be obtained through companies that are able to provide these functionalized nanotubes with the necessary groups (in this case amino groups). Therefore, the method of application and collection of these textures is industrially viable.

Ejemplo9 Example 9

Resultadosdelas muestraspretratadas con plasmaoxigeno/aireytratadas posteriormente con NTC-NH2 a) Tratamiento Pretratamiento de la muestra con plasma: Results of samples pretreated with plasma oxygen / air and subsequently treated with NTC-NH2 a) Treatment Pretreatment of the sample with plasma:

b) Aplicación de NTC Primera solución:Tratamiento con ultrasonidos para dispersar los NTC. b) NTC application First solution: Ultrasound treatment to disperse the NTC.

Segunda solución: Activación de los grupos funcionales de la celulosa para enlazar los NTC, posteriormente al juntarlasdos solucionesy aplicarloenel tejidopor agotamiento. Second solution: Activation of the functional groups of the cellulose to bind the NTCs, later to join the two solutions and apply it to the tissue by exhaustion.

c) Resistencia eléctrica: (UNEEN 1149-5:2008) (Rsuperf. ≤ 2,5·109) c) Electrical resistance: (UNEEN 1149-5: 2008) (Rsuperf. ≤ 2.5 · 109)

d) Resistencia a la abrasión: (UNE-EN ISO 12947-2) d) Abrasion resistance: (UNE-EN ISO 12947-2)

e) Imágenes SEM de las muestras e) SEM images of the samples

Trasverlosdiferentesresultados:resistenciaeléctrica, resistenciaala abrasiónylas imágenesSEM,sehallegado ala conclusiónde queel tratamiento plasma-NTCha mejorado las propiedades mecánicasyeléctricas del tejido. After seeing the different results: electrical resistance, resistance to abrasion and SEM images, it has been concluded that plasma-NTC treatment has improved the mechanical and electrical properties of the tissue.

Tambiénsehan realizado unoycinco ciclosdelavadosdelas muestraspara asegurarla adhesióndeNTC,según norma UNE-EN ISO 6330:2001 a 30ºC.Sehaverificadolabuena adhesiónde NTC, porlo tanto significa queel pretratamiento con plasma a generado los grupos -COOH previstos para que los NTC-NH2 se adhieran al reaccionar. One and five cycles of the sample samples have also been carried out to ensure the adhesion of NTC, according to UNE-EN ISO 6330: 2001 at 30 ° C. It has been verified that good adhesion of NTC, therefore it means that the pretreatment with plasma has generated the -COOH groups provided for the NTC-NH2 to adhere when reacting.

Claims (73)

REIVINDICACIONES
1. one.
Un procedimiento para la preparación de un tejido que comprende una etapa de formación de un enlace amida entre un tejidoynanotubosde carbono. A process for the preparation of a tissue comprising a step of forming an amide bond between a tissue and carbon tubes.
2. 2.
Procedimiento según la reivindicación1 caracterizado porque el tejido está funcionalizado con grupos carboxílicosylos nanotubosde carbono están funcionalizados con grupos amino. Method according to claim 1 characterized in that the tissue is functionalized with carboxylic groups and the carbon nanotubes are functionalized with amino groups.
3. 3.
Procedimiento según cualquiera de las reivindicaciones 1 o 2 caracterizado porque además comprende un agente de acoplamiento. Method according to any one of claims 1 or 2, characterized in that it further comprises a coupling agent.
4. Four.
Procedimiento según la reivindicación 3 caracterizado porque el agente de acoplamiento se selecciona de carbodiimida, preferiblemente diciclohexilcarbodiimida. Method according to claim 3 characterized in that the coupling agent is selected from carbodiimide, preferably dicyclohexylcarbodiimide.
5. 5.
Procedimiento según cualquiera de las reivindicaciones 1 a 4 caracterizado porque además comprende un catalizador, preferiblemente dimetilaminopiridina. Process according to any one of claims 1 to 4 characterized in that it further comprises a catalyst, preferably dimethylaminopyridine.
6. 6.
Procedimiento según cualquiera de las reivindicaciones 1 a 5 caracterizado porque además comprende un disolvente seleccionado de agua, metanol, dimetilformamida o mezclas de los mismos. Process according to any one of claims 1 to 5 characterized in that it further comprises a solvent selected from water, methanol, dimethylformamide or mixtures thereof.
7. 7.
Procedimientosegún cualquieradelasreivindicaciones1 a6 caracterizado porque la concentración de nanotubosde carbono esde entre0,1y10gpor 100mLde disolvente, preferiblementede1gpor 100 mL. Procedure according to any one of claims 1 to 6 characterized in that the concentration of carbon nanotubes is between 0.1 and 10 g per 100 mL of solvent, preferably 1 g per 100 mL.
8. 8.
Procedimiento según cualquiera de las reivindicaciones 1 a 7 caracterizado porque además comprende un detergente aniónico, preferiblemente dodecil sulfato de sodio (SDS). Process according to any one of claims 1 to 7, characterized in that it further comprises an anionic detergent, preferably sodium dodecyl sulfate (SDS).
9. 9.
Procedimiento según la reivindicación8 caracterizado porque la concentración de detergente aniónico es de entre0,1a5gpor100mLdedisolvente, preferiblementede1gpor100mL. Method according to claim 8, characterized in that the concentration of anionic detergent is between 0.1 to 5 g per 100 ml solvent, preferably 1 g per 100 ml.
10. 10.
Procedimiento según cualquierade las reivindicaciones1 a9 caracterizado porque además comprende una etapa de sonicación. Method according to any one of claims 1 to 9 characterized in that it further comprises a sonication stage.
11. eleven.
Procedimiento según la reivindicación 10 caracterizado porque el tiempo de reacción de la etapa de sonicación esde entre5y120 minutos,preferiblemente30 minutos. Method according to claim 10 characterized in that the reaction time of the sonication stage is between 5 and 120 minutes, preferably 30 minutes.
12. 12.
Procedimiento según cualquiera de las reivindicaciones 10 u 11 caracterizado porque la temperatura de la etapa de sonicación es menor o igual a 60ºC, preferiblemente 40ºC. Method according to any of claims 10 or 11 characterized in that the temperature of the sonication stage is less than or equal to 60 ° C, preferably 40 ° C.
13. 13.
Procedimientosegún cualquieradelasreivindicaciones10a12 caracterizado porque la frecuencia de la etapa de sonicación esde entre15y30 KHz, preferiblemente20 KHz. Procedure according to any of claims 10 to 12 characterized in that the frequency of the sonication stage is between 15 and 30 KHz, preferably 20 KHz.
14. 14.
Procedimiento según cualquiera de las reivindicaciones 10 a 13 caracterizado porque la potencia de la etapa de sonicación esde entre entre 150a 1500W, preferiblemente 750W. Method according to any of claims 10 to 13 characterized in that the power of the sonication stage is between 150 to 1500W, preferably 750W.
15. fifteen.
Procedimientosegún cualquieradelasreivindicaciones1a14 caracterizado porque la concentración de agente de acoplamientoesde1 a10gpor100mLde disolución final, preferiblementede5gpor100mL. Procedure according to any of claims 1 to 14 characterized in that the concentration of coupling agent is 1 to 10 g per 100 mL of final solution, preferably 5 g per 100 mL.
16. 16.
Procedimiento según cualquiera de las reivindicaciones 1 a 15 caracterizado porque la concentración de catalizadoresde entre0,5a5gpor100mLde disolución final, preferiblementede1,6gpor100mL. Process according to any one of claims 1 to 15 characterized in that the concentration of catalysts between 0.5 to 5 g per 100 ml of final solution, preferably 1.6 g per 100 ml.
17. 17.
Procedimientosegún cualquieradelasreivindicaciones1a16 caracterizado porque la metodología de formación del enlace amida es por agotamiento. Procedure according to any of claims 1 to 16 characterized in that the amide bond formation methodology is by depletion.
18. 18.
Procedimiento según la reivindicación 17 caracterizado porqueel tiempode reacción esde entre1y24h, preferiblemente de4h. Method according to claim 17 characterized in that the reaction time is between 1 and 24 hours, preferably 4 hours.
19. 19.
Procedimientosegún cualquieradelasreivindicaciones17o18 caracterizado porquelavelocidadde rotación es de 10 a 80 revoluciones por minuto, preferiblemente de 40 revoluciones por minuto. Procedure according to any one of claims 17 or 18 characterized in that the rotational speed is 10 to 80 revolutions per minute, preferably 40 revolutions per minute.
20. twenty.
Procedimiento según la reivindicación 19 caracterizado porque el sentido de rotación se invierte cada 10 a 120 segundos, preferiblemente cada 60 segundos. Method according to claim 19 characterized in that the direction of rotation is reversed every 10 to 120 seconds, preferably every 60 seconds.
21. twenty-one.
Procedimiento según cualquiera de las reivindicaciones 17 a 20 caracterizado porque la temperatura a la que se llevaa cabola etapadeformación del enlace esde0a 30ºC, preferiblementede23ºC. Process according to any of claims 17 to 20, characterized in that the temperature at which the bond deformation stage is carried out is from 0 ° C to 30 ° C, preferably from 23 ° C.
22. 22
Procedimiento según cualquiera de las reivindicaciones 17 a 21 caracterizado porque además comprende una etapa de secado. Method according to any of claims 17 to 21, characterized in that it further comprises a drying step.
23. 2. 3.
Procedimiento según la reivindicación 22 caracterizado porque la etapa de secado se lleva a cabo a una temperaturade entre85y95ºC, preferiblementea 90ºC. Method according to claim 22, characterized in that the drying step is carried out at a temperature of between 85 and 95 ° C, preferably at 90 ° C.
24. 24.
Procedimiento según cualquiera de las reivindicaciones 22 o 23 caracterizado porque la etapa de secado se llevaa cabo en un tiempode2a5minutos, preferiblemente en5minutos. Method according to any of claims 22 or 23, characterized in that the drying step is carried out in a time of 2 to 5 minutes, preferably in 5 minutes.
25. 25.
Procedimiento según cualquiera de las reivindicaciones 22 a 25 caracterizado porque además comprende una etapadelavado en tres baños:de aguaal 100%,de una mezclade aguaymetanolal 50%yde metanolal 100%. Method according to any of claims 22 to 25, characterized in that it also comprises a three-wash stage: 100% water, a mixture of 50% water and methane and 100% methalal.
26. Procedimiento según la reivindicación 25 caracterizado por un tiempodeexposiciónde entre1a15 minutos. 26. Method according to claim 25 characterized by an exposure time of between 15 and 15 minutes.
27. 27.
Procedimientosegún cualquieradelasreivindicaciones26o27 caracterizado porque comprende una segunda etapa de secado. Procedure according to any of claims 26 or 27 characterized in that it comprises a second drying stage.
28. 28.
Procedimiento según la reivindicación 27 caracterizado porque la etapa de secado se lleva a cabo a una temperaturade entre85y95ºC, preferiblementea 90ºC. Process according to claim 27, characterized in that the drying step is carried out at a temperature of between 85 and 95 ° C, preferably at 90 ° C.
29. 29.
Procedimiento según cualquiera de las reivindicaciones 27 o 28 caracterizado porque la etapa de secado se llevaa cabo en un tiempode2a5minutos, preferiblemente en5minutos. Method according to any of claims 27 or 28 characterized in that the drying step is carried out in a time of 2 to 5 minutes, preferably in 5 minutes.
30. 30
Procedimientosegún cualquieradelasreivindicaciones1a29 caracterizado porque los nanotubos de carbono son multicapa. Procedure according to any one of claims 1 to 29 characterized in that the carbon nanotubes are multilayer.
31. 31.
Procedimiento según la reivindicación 30 caracterizado porque los nanotubos de carbono tienen un diámetro de entre5y50 nm, preferiblementede10a20 nm. Method according to claim 30 characterized in that the carbon nanotubes have a diameter between 5-50 nm, preferably 10-20 nm.
32. 32
Procedimientosegún cualquieradelasreivindicaciones30a31 caracterizado porque los nanotubos de carbono tienen una pureza mayor del90% en peso, preferiblemente mayor del 95%. Method according to any of claims 30 to 31 characterized in that the carbon nanotubes have a purity greater than 90% by weight, preferably greater than 95%.
33. 33.
Procedimientosegún cualquieradelasreivindicaciones30a32 caracterizado porque los nanotubos de carbono tienen una longitudde entre1y50 µm, preferiblemente de 20 µm. Method according to any one of claims 30 to 32 characterized in that the carbon nanotubes have a length between 1 and 50 µm, preferably 20 µm.
34. 3. 4.
Procedimientosegún cualquieradelasreivindicaciones30a33 caracterizado porque los nanotubos de carbono tienen una concentración de carbono amorfo menor del 3%, una concentración de ceniza menor del 1% en peso, un áreade superficie especial mayorde 350m2 por gramode nanotubosde carbono,yunaconductividad térmicade mas de 2000 W/m.k. Procedure according to any of claims 30 to 33 characterized in that the carbon nanotubes have an amorphous carbon concentration of less than 3%, an ash concentration of less than 1% by weight, a special surface area greater than 350m2 per gram of carbon nanotubes, and a thermal conductivity of more than 2000 W / m.k.
35. Procedimiento según cualquierade las reivindicaciones1 a34 caracterizado porque el tejido comprende: 35. Method according to any one of claims 1 to 34 characterized in that the fabric comprises:
• •
modacrílica, 45-65%, preferiblemente 55%;y modacrylic, 45-65%, preferably 55%; and
• •
algodón, 35-55%, preferiblemente 45%. cotton, 35-55%, preferably 45%.
36. 36.
Procedimientosegún cualquieradelasreivindicaciones1 a35 caracterizado porque además comprende una etapa de pretratamiento del tejido para funcionalizarlo con grupos carboxílicos. Method according to any of claims 1 to 35 characterized in that it also comprises a stage of pretreatment of the tissue to functionalize it with carboxylic groups.
37. 37.
Procedimiento según la reivindicación 36 caracterizado porqueel pretratamientosellevaa caboporplasma de vacío o atmosférico. Method according to claim 36 characterized in that the pretreatments ensure vacuum or atmospheric caboporplasm.
38. 38.
Procedimiento según la reivindicación 37 caracterizado porque el tratamiento por plasma se caracteriza por oxidarel tejido mediante tratamiento con oxígeno 100%ymezclasde nitrógenoyoxígeno. Method according to claim 37 characterized in that the plasma treatment is characterized by oxidizing the tissue by treatment with 100% oxygen and nitrogen-oxygen mixtures.
39. 39.
Procedimiento según la reivindicación 38 caracterizado porque la composición de la mezcla de nitrógenoy oxígeno esde entre0y79%de nitrógenoyde entre un21y100%de oxígeno, preferiblemente del 32%de nitrógeno y68% de oxígeno. Process according to claim 38, characterized in that the composition of the mixture of nitrogen and oxygen is between 0 and 79% nitrogen and between 21 and 100% oxygen, preferably 32% nitrogen and 68% oxygen.
40. 40
Procedimientosegúncualquieradelasreivindicaciones37a39 caracterizado porque el tiempo de tratamiento por plasma esde1a30 minutos, preferiblementede10a30 minutos. Procedure according to any of the claims 37 to 39 characterized in that the plasma treatment time is from 30 to 30 minutes, preferably from 10 to 30 minutes.
41. 41.
Procedimiento según cualquiera de las reivindicaciones 37 a 40 caracterizado porque la velocidad de tratamiento por plasma es de 0,1 a 10 m/minuto, preferiblemente de 0,1 m/minuto. Method according to any of claims 37 to 40, characterized in that the plasma treatment rate is 0.1 to 10 m / minute, preferably 0.1 m / minute.
42. 42
Procedimiento según la reivindicación 36 caracterizado porque el pretratamiento se lleva a cabo con un ácido policaroboxílico. Method according to claim 36 characterized in that the pretreatment is carried out with a polycarboxylic acid.
43. 43
Procedimiento según loa reivindicación 42 caracterizado porque el ácido policarboxílico se selecciona de ácido succínico o ácido cítrico, preferiblemente ácido succínico. Process according to claim 42 characterized in that the polycarboxylic acid is selected from succinic acid or citric acid, preferably succinic acid.
44. 44.
Procedimiento según cualquiera de las reivindicaciones 42 o 43 caracterizado porque además comprende un catalizador, preferiblemente hipofosfito sódico. Method according to any of claims 42 or 43 characterized in that it further comprises a catalyst, preferably sodium hypophosphite.
45. Four. Five.
Procedimiento según cualquiera de las reivindicaciones 42 a 44 caracterizado porque la metodología de aplicación es por agotamiento. Method according to any of claims 42 to 44 characterized in that the application methodology is by exhaustion.
46. 46.
Procedimiento según cualquiera de las reivindicaciones 42 a 45 caracterizado porque la concentración de ácido policarboxílicoesde entre0,5y2%ode entre3y6%, preferiblementedel6%. Method according to any of claims 42 to 45, characterized in that the concentration of polycarboxylic acid is between 0.5 and 2% or between 3 and 6%, preferably 6%.
47. 47
Procedimiento según cualquiera de las reivindicaciones 42 a 46 caracterizado porque la concentración de de catalizadores entre0,2y0,5%o entre2y4%, preferiblementedel4%. Method according to any of claims 42 to 46, characterized in that the concentration of catalysts is between 0.2 and 0.5% or between 2 and 4%, preferably 4%.
48. 48.
Procedimiento según cualquiera de las reivindicaciones 42 a 47 caracterizado porque el tiempo de reacción esde1hora. Method according to any of claims 42 to 47 characterized in that the reaction time is 1 hour.
49. 49.
Procedimiento según cualquiera de las reivindicaciones 42 a 48 caracterizado porque la temperatura de reacción esde entre20y35ºC, preferiblementede 23ºC. Process according to any of claims 42 to 48 characterized in that the reaction temperature is between 20 and 35 ° C, preferably 23 ° C.
50. fifty.
Procedimiento según cualquiera de las reivindicación 42 a 49 caracterizado porque además comprende una etapa de secado caracterizada porque: Method according to any of claims 42 to 49 characterized in that it further comprises a drying stage characterized in that:
-se llevaa cabo en un tiempode entre2y5minutos, preferiblemente en5minutos;y -a una temperaturade entre85y95ºC, preferiblementede 90ºC. - it is carried out in a time between 2 and 5 minutes, preferably in 5 minutes; and -at a temperature between 85 and 95 ° C, preferably 90 ° C.
51. 51.
Procedimiento según cualquiera de las reivindicaciones 42 a 50 caracterizado porque además comprende una etapa de reticulado caracterizada porque: Method according to any of claims 42 to 50 characterized in that it further comprises a cross-linking stage characterized in that:
-se llevaa cabo en un tiempode entre1y5minutos, preferiblementede5minutos;y -a una temperaturade entre120y180ºC, preferiblementede 150ºC. - it is carried out in a time between 1 and 5 minutes, preferably of 5 minutes; and -at a temperature between 120 and 180 ° C, preferably 150 ° C.
52. 52
Procedimiento según cualquierade las reivindicaciones1 a51 caracterizado porque la etapa de funcionalización de los nanotubos de carbono funcionalizados con grupos carboxílicos comprende: Method according to any one of claims 1 to 51 characterized in that the step of functionalization of the carbon nanotubes functionalized with carboxylic groups comprises:
--
unaetapadetratamientodelos nanotubosde carbonoconperóxidodehidrógenoenpresenciadeácidoobase para generar nanotubosde carbono con función carboxílica;y a treatment of carbon nanotubes with hydrogen peroxide in acid presence or base to generate carbon nanotubes with carboxylic function; and
--
una etapa de tratamiento de los nanotubos de carbono con función carboxílica con una amina para generar nanotubos de carbono con función amina. a stage of treatment of carbon nanotubes with carboxylic function with an amine to generate carbon nanotubes with amine function.
53. 53.
Procedimiento según la reivindicación 52 caracterizado porque el ácido se selecciona de ácido nítrico, ácido sulfúricoymezclasde losmismos. Method according to claim 52 characterized in that the acid is selected from nitric acid, sulfuric acid and mixtures thereof.
54. 54
Procedimiento según la reivindicación 53 caracterizado porque la proporción de la mezcla de ácido sulfúrico yácido nítrico es 1:3 respectivamente. Process according to claim 53, characterized in that the ratio of the nitric acid sulfuric acid mixture is 1: 3 respectively.
55. 55.
Procedimiento según cualquiera de las reivindicaciones 52 a 54 caracterizado porqueelpretratamientode los nanotubos con ácido tienelugarenun tiempode entre1y5h, preferiblemente3h. Method according to any of claims 52 to 54 characterized in that the pretreatment of the nanotubes with acid takes place between 1 and 5 hours, preferably 3 hours.
56. 56.
Procedimiento según cualquiera de las reivindicaciones 52 a 55 caracterizado porqueelpretratamientode los nanotubos con ácido tiene lugar a una temperatura menor o igual a 40ºC, preferiblemente a 40ºC. Process according to any of claims 52 to 55 characterized in that the pretreatment of the nanotubes with acid takes place at a temperature less than or equal to 40 ° C, preferably at 40 ° C.
57. Procedimiento según la reivindicación 52 caracterizado porque la base se selecciona de hidróxido de amonio. 57. Method according to claim 52 characterized in that the base is selected from ammonium hydroxide.
58. 58.
Procedimiento según cualquiera de las reivindicaciones 52 a 57 caracterizado porque además comprende una etapa de secado de los nanotubos con función carboxílica. Method according to any one of claims 52 to 57, characterized in that it further comprises a step of drying the nanotubes with carboxylic function.
59. 59.
Procedimiento según la reivindicación 58 caracterizado porqueel tiempode secadoesde6a12h, preferiblemente de 12 h. Method according to claim 58 characterized in that the drying time is from 6 to 12 h, preferably 12 h.
60. 60
Procedimientosegúncualquieradelasreivindicaciones58o59 caracterizado porque la temperatura de secado es de 100 a 120ºC, preferiblemente de 100ºC. Procedure according to any of claims 58 or 59 characterized in that the drying temperature is 100 to 120 ° C, preferably 100 ° C.
61. 61.
Procedimiento según cualquiera de las reivindicaciones 52 a 60 caracterizado porque la amina de la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se seleccionade dietilendiamina, sperminayetlilentriamina, preferiblemente dietilendiamina. Method according to any one of claims 52 to 60, characterized in that the amine of the carbon nanotubes with carboxylic acid treatment stage for generating carbon nanotubes with amine function is selected from diethylene diamine, spermine and ethylene triamine, preferably diethylene diamine.
62. 62
Procedimiento según la reivindicación 61 caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una carbodiimida, preferiblemente diciclohexilcarbodiimida (DCC). Method according to claim 61, characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a carbodiimide, preferably dicyclohexylcarbodiimide (DCC).
63. 63.
Procedimiento según cualquiera de las reivindicaciones 61 o 62 caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende un catalizador, preferiblemente dimetilaminopiridina (DMAP). Method according to any of claims 61 or 62, characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a catalyst, preferably dimethylaminopyridine (DMAP).
64. 64.
Procedimiento según cualquiera de las reivindicaciones 61 a 63 caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se lleva a cabo en un tiempode entre1y8h, preferiblementede4h. Method according to any of claims 61 to 63, characterized in that the step of treating the carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is carried out in a time between 1 and 8 hours, preferably 4 hours.
65. 65
Procedimiento según cualquiera de las 61 a 64 caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina se lleva a cabo a una temperaturade entre0y30ºC, preferiblementede 23ºC. Method according to any of 61 to 64 characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function is carried out at a temperature of between 0 and 30 ° C, preferably of 23 ° C.
66. 66.
Procedimiento según cualquiera de las reivindicaciones 61 a 65 caracterizado porque la etapa de tratamiento de los nanotubos de carbono con función carboxílica para generar nanotubos de carbono con función amina además comprende una etapa de secado, preferiblemente al aire. Method according to any one of claims 61 to 65, characterized in that the step of treating carbon nanotubes with carboxylic function to generate carbon nanotubes with amine function further comprises a drying stage, preferably in air.
67.Un tejido directamente obtenido porel procedimientode cualquierade las reivindicaciones1a 66. 67. A tissue directly obtained by the process of any of claims 1 to 66. 68.Tejido segúnla reivindicación67 caracterizado porque se puede lavar. 68. Fabric according to claim 67 characterized in that it can be washed. 69.Tejido segúnla reivindicación68 caracterizado porqueel tejidoaguantade1a50 ciclosdelavado doméstico, preferiblementede1a25 ciclos,yaún más preferiblementede1 a5ciclos. 69. Fabric according to claim 68, characterized in that the fabric is maintained at 150 cycles of domestic washing, preferably from 25 cycles, and even more preferably from 1 to 5 cycles. 70.Tejido según cualquierade las reivindicaciones67a69 caracterizado porque la temperatura de lavado es de entre30y60ºC, preferiblementea 30ºC. 70. Fabric according to any one of claims 67 to 69 characterized in that the washing temperature is between 30 and 60 ° C, preferably at 30 ° C. 71.Tejidosegún cualquieradelasreivindicaciones67a70 caracterizado porque presenta resistenciaala abrasión. 71.Weave according to any of the claims 67 to 70 characterized in that it exhibits resistance to abrasion. 72. Uso de un tejido según cualquiera de las reivindicaciones 67 a 71 para equipos de protección individual. 72. Use of a fabric according to any of claims 67 to 71 for personal protective equipment. OFICINA ESPAÑOLA DE PATENTES Y MARCAS SPANISH OFFICE OF THE PATENTS AND BRAND N.º solicitud:201030982 Application no .: 201030982 ESPAÑA SPAIN Fecha de presentación de la solicitud: 25.06.2010 Date of submission of the application: 06.25.2010 Fecha de prioridad: 00-00-0000 Priority Date: 00-00-0000 INFORME SOBRE EL ESTADO DE LA TECNICA REPORT ON THE STATE OF THE TECHNIQUE 51 Int. Cl. : Ver Hoja Adicional 51 Int. Cl.: See Additional Sheet DOCUMENTOS RELEVANTES RELEVANT DOCUMENTS
Categoría Category
Documentos citados Reivindicaciones afectadas Documents cited Claims Affected
X X
CN 101085863 (SHANGHAI YANGZE NANOMETER NEW MATERIALCO LTD.) 05.07.2007 (resumen) World Patents Index[bases de datos en línea]. Derwent publications,Ltd. [recuperado el 02.01.11]. Recuperado de: Questel. Nº de acceso 2008-K47214[63]. 1,67-72 CN 101085863 (SHANGHAI YANGZE NANOMETER NEW MATERIALCO LTD.) 05.07.2007 (summary) World Patents Index [online databases]. Derwent publications, Ltd. [retrieved on 02.01.11]. Recovered from: Questel. Accession No. 2008-K47214 [63]. 1.67-72
A TO
PANHUIS, M. et al “Conducting textiles fron single-walled carbon nanotubes”. Synthetic Metals, 2007, Volumen 157, páginas 358-362. Ver resumen; página 359, Experimental. 1-72 PANHUIS, M. et al. “Conducting textiles fron single-walled carbon nanotubes”. Synthetic Metals, 2007, Volume 157, pages 358-362. See summary; page 359, Experimental. 1-72
A TO
WO 2006/086344 A2 (DOUGLAS, J. S) 17.08.2006, página 1, líneas 9-15; página 3, líneas 21-32. 1-72 WO 2006/086344 A2 (DOUGLAS, J. S) 08.17.2006, page 1, lines 9-15; page 3, lines 21-32. 1-72
A TO
US 2006/0062944 (SLADE, S.H. et al.) 23.03.2006, reivindicaciones 1-8. 1-72 US 2006/0062944 (SLADE, S.H. et al.) 23.03.2006, claims 1-8. 1-72
A TO
LAACHACHI, A. et al. “A chemical method of graft carbon nanotubes onto a carbon fiber”. Material Letters, 2008, Volumen 62, páginas 394-397. Ver resumen; páginas 394 y 395, Experimental. 1-72 LAACHACHI, A. et al. "A chemical method of graft carbon nanotubes onto a carbon fiber." Material Letters, 2008, Volume 62, pages 394-397. See summary; pages 394 and 395, Experimental. 1-72
Categoría de los documentos citados X: de particular relevancia Y: de particular relevancia combinado con otro/s de la misma categoría A: refleja el estado de la técnica O: referido a divulgación no escrita P: publicado entre la fecha de prioridad y la de presentación de la solicitud E: documento anterior, pero publicado después de la fecha de presentación de la solicitud Category of the documents cited X: of particular relevance Y: of particular relevance combined with other / s of the same category A: reflects the state of the art O: refers to unwritten disclosure P: published between the priority date and the date of priority submission of the application E: previous document, but published after the date of submission of the application
El presente informe ha sido realizado • para todas las reivindicaciones □ para las reivindicaciones nº: TODAS This report has been prepared • for all claims □ for claims no: ALL
Fecha de realización del informe 10.11.2010 Date of realization of the report 10.11.2010
Examinador N. Martín Laso Página 1/4 Examiner N. Martín Laso Page 1/4
INFORME DEL ESTADO DE LA TÉCNICA REPORT OF THE STATE OF THE TECHNIQUE Nº de solicitud:201030982 Application number: 201030982 CLASIFICACIÓN OBJETO DE LA SOLICITUD D06M11/74(2006.01) CLASSIFICATION OBJECT OF THE APPLICATION D06M11 / 74 (2006.01) H01B1/24(2006.01) C08K7/00(2006.01) Documentación mínima buscada (sistema de clasificación seguido de los símbolos de clasificación) H01B1 / 24 (2006.01) C08K7 / 00 (2006.01) Minimum documentation sought (classification system followed by classification symbols) D06M, H01B, C08K D06M, H01B, C08K Bases de datos electrónicas consultadas durante la búsqueda (nombre de la base de datos y, si es posible, términos de búsqueda utilizados) INVENES, EPODOC, WPI, XPESP, NPL, CAS. Electronic databases consulted during the search (name of the database and, if possible, terms of search used) INVENES, EPODOC, WPI, XPESP, NPL, CAS. Informe del Estado de la Técnica Página 2/4 State of the Art Report Page 2/4 OPINIÓN ESCRITA  WRITTEN OPINION Nº de solicitud:201030982 Application number: 201030982 Fecha de Realización de la Opinión Escrita: Date of Written Opinion: Declaración Statement
Novedad (Art. 6.1 LP 11/1986) Novelty (Art. 6.1 LP 11/1986)
Reivindicaciones Reivindicaciones 2-66 1, 67-72 SI NO Claims Claims 2-66 1, 67-72 IF NOT
Actividad inventiva (Art. 8.1 LP11/1986) Inventive activity (Art. 8.1 LP11 / 1986)
Reivindicaciones Reivindicaciones 2-66 1, 67-72 SI NO Claims Claims 2-66 1, 67-72 IF NOT
Se considera que la solicitud cumple con el requisito de aplicación industrial. Este requisito fue evaluado durante la fase de examen formal y técnico de la solicitud (Artículo 31.2 Ley 11/1986). The application is considered to comply with the industrial application requirement. This requirement was evaluated during the formal and technical examination phase of the application (Article 31.2 Law 11/1986). Base de la Opinión.-  Opinion Base.- La presente opinión se ha realizado sobre la base de la solicitud de patente tal y como se publica. This opinion has been made on the basis of the patent application as published. Informe del Estado de la Técnica Página 3/4 State of the Art Report Page 3/4 OPINIÓN ESCRITA  WRITTEN OPINION Nº de solicitud:201030982 Application number: 201030982 1. Documentos considerados.-1. Documents considered.- A continuación se relacionan los documentos pertenecientes al estado de la técnica tomados en consideración para la realización de esta opinión. The documents belonging to the state of the art taken into consideration for the realization of this opinion are listed below.
Documento Document
Número Publicación o Identificación Fecha Publicación Publication or Identification Number publication date
D01 D01
CN 101085863 A 05.07.2007 CN 101085863 A 05.07.2007
2. Declaración motivada según los artículos 29.6 y 29.7 del Reglamento de ejecución de la Ley 11/1986, de 20 de marzo, de Patentes sobre la novedad y la actividad inventiva; citas y explicaciones en apoyo de esta declaración 2. Statement motivated according to articles 29.6 and 29.7 of the Regulations for the execution of Law 11/1986, of March 20, on Patents on novelty and inventive activity; quotes and explanations in support of this statement La solicitud se refiere a un procedimiento para la preparación de un tejido que comprende la formación de enlaces amida entre el tejido y nanotubos de carbono previamente funcionalizados. Se refiere igualmente al tejido obtenido por dicho procedimiento y al uso de dicho tejido en equipos de protección individual. The application refers to a process for the preparation of a tissue comprising the formation of amide bonds between the tissue and previously functionalized carbon nanotubes. It also refers to the fabric obtained by said procedure and the use of said fabric in personal protective equipment. Novedad (Art 6.1 LP 11/1986): New (Art 6.1 LP 11/1986): El documento D01 divulga un tejido textil de nylon que incorpora nanotubos de carbono unidos mediante un enlace amida. El material se prepara mediante reacción de los grupos amina libres de la poliamida con los grupos carboxílicos con los que han sido funcionalizados los nanotubos de carbono. El tejido de poliamida es resistente al uso y posee cierta resistencia al fuego, mejorándose la conductividad y las propiedades antiestáticas de dicho tejido al incorporar los nanotubos de carbono (resumen). Document D01 discloses a nylon textile fabric incorporating carbon nanotubes bonded by an amide bond. The material is prepared by reacting the free amine groups of the polyamide with the carboxylic groups with which the carbon nanotubes have been functionalized. The polyamide fabric is resistant to use and has some resistance to fire, improving the conductivity and antistatic properties of said fabric by incorporating carbon nanotubes (summary). Por lo tanto, la invención tal y como ha sido definida en las reivindicaciones 1 y 67-72 de la solicitud, carece de novedad a la vista del documento D01 (Art 6.1 LP 11/1986). Therefore, the invention, as defined in claims 1 and 67-72 of the application, is not new in view of document D01 (Art 6.1 LP 11/1986). Sin embargo, parece claro a partir de la descripción, que la contribución de la invención al estado de la técnica radica en la unión tipo amida entre los nanotubos de carbono funcionalizados con un grupo amina y un tejido funcionalizado con un grupo carboxílico, no habiéndose encontrado en el estado de la técnica documentos que divulguen o dirijan al experto en la materia hacia dicha invención. However, it seems clear from the description that the contribution of the invention to the state of the art lies in the amide type bond between the carbon nanotubes functionalized with an amine group and a tissue functionalized with a carboxylic group, not having been found in the state of the art documents that disseminate or direct the person skilled in the art towards said invention. En consecuencia, la invención definida en las reivindicaciones 2-66 es nueva y posee actividad inventiva (Art. 6.1 y 8.1 LP 11 /1986). Consequently, the invention defined in claims 2-66 is new and has inventive activity (Art. 6.1 and 8.1 LP 11/1986). Informe del Estado de la Técnica Página 4/4 State of the Art Report Page 4/4
ES201030982A 2010-06-25 2010-06-25 FABRICS FUNCTIONED WITH CARBON NANOTUBES Expired - Fee Related ES2349823B1 (en)