DE967716C - Process for the production of plates or molded bodies from malleable synthetic wood compounds - Google Patents
Process for the production of plates or molded bodies from malleable synthetic wood compoundsInfo
- Publication number
- DE967716C DE967716C DEB27449A DEB0027449A DE967716C DE 967716 C DE967716 C DE 967716C DE B27449 A DEB27449 A DE B27449A DE B0027449 A DEB0027449 A DE B0027449A DE 967716 C DE967716 C DE 967716C
- Authority
- DE
- Germany
- Prior art keywords
- production
- plates
- water
- synthetic wood
- molded bodies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Herstellung von Platten oder Formkörpern aus formbaren Kunstholzmassen Nach Patent 96604I werden gegebenenfalls in bekannter Weise mit organischen Säuren vorhydrolysierte zerkleinerte Holzabfälle zusammen mit mineralischen Füllstoffen, zumindest Kreide und Gips unter Rühren bzw. Vermengen in eine homogene Mischung aus wäßrigen Kaseinsuspensionen, sowie Alkalien bzw. Erdalkalien und/oder alkalisch wirkenden Salzen bzw. Alkalisilikaten und aus bekannten konservieren den, fäulnis- und zersetzungshindernden Mitteln, gegebenenfalls bedarfsweise bekannten feuerhemmenden, insektiziden, fungiziden Mitteln bzw. Schädlingsbekämpfungsmitteln, sowie gegebenenfalls bekannten Verdickungsmitteln, Wachsen bzw. wachsähnlichen Stoffen und Farbstoffen, eingebracht und die entstehende, gut durchgeknetete teigige Masse ohne Druck und Wärmezufuhr geformt, die Erzeugnisse vorgetrocknet und bei erhöhten Temperaturen, vorzugsweise von 70 bis go0, in einer Atmosphäre größtmöglicher Feuchtigkeit fertiggetrocknet.Process for the production of sheets or moldings from moldable Synthetic wood compounds according to patent 96604I are optionally used in a known manner organic acids pre-hydrolyzed shredded wood waste together with mineral ones Fillers, at least chalk and plaster of paris with stirring or mixing into a homogeneous one Mixture of aqueous casein suspensions, as well as alkalis or alkaline earths and / or alkaline salts or alkali silicates and from known preservatives, putrefaction and decomposition inhibitors, if necessary known fire retardant, insecticidal, fungicidal agents or pesticides, and, if appropriate, known thickeners, waxes or wax-like substances and dyes, introduced and the resulting, well-kneaded doughy mass Shaped without pressure or heat, the products are pre-dried and at increased Temperatures, preferably from 70 to go0, in an atmosphere of the greatest possible humidity completely dried.
Gegenstand der Erfindung ist die Regulierung der Schrumpfung bei der Herstellung von Platten oder Formkörpern nach diesem Verfahren. The subject of the invention is the regulation of the shrinkage the production of panels or moldings according to this process.
Es ist bekannt, daß aus Eiweiß stoffen bestehende Bindemittel, insbesondere Kaseinleime, eine große Kontraktionsfähigkeit besitzen und bei der Verwendung als Bindemittel zur Herstellung von Kunstholz od.dgl. Massen Schrumpfungen des Ma- terials bis zu 35 O/o bewirken. Diese Eigenschaft der Kaseinleime prädestiniert diese zur Erzielung außerordentlich fester und hochbeanspruchbarer Leimverbindungen. Jedoch sind in vielen Fällen die durch die starke Zusammenziehung bzw. durch Schrumpfungen hervorgerufenen Erscheinungen unerwünscht, so beispielsweise beim Bau von Segelflugzeugen u. a. It is known that binders made of protein, in particular Casein glues, possessing great contractility and when used as a Binder for the production of synthetic wood or the like. Mass shrinkage of the terials effect up to 35 o / o. This property of casein glues makes them ideal for Achievement of extremely strong and highly stressable glue connections. However are in many cases those caused by strong contraction or shrinkage caused phenomena undesirable, for example in the construction of gliders i.a.
Es wurde nun gefunden, daß die Schrumpfung bei der Anwendung von eiweißhaltigen Bindemitteln bei dem eingangs aufgeführten Verfahren in der Weise geregelt werden kann, daß bei der Zusammenmischung der verschiedenen Werkstoffmassen wasserlösliche Polymerisationsprodukte vorzugsweise des Vinylalkohols zugesetzt werden. It has now been found that the shrinkage when using protein-containing binders in the process listed at the beginning in the manner it can be regulated that when the various materials are mixed together water-soluble polymerization products are preferably added to the vinyl alcohol will.
Der gewünschte Schrumpfungsgrad läßt sich durch die jeweils zugesetzten Mengen an wasserlöslichen Polymerisationsprodukten einstellen.The desired degree of shrinkage can be determined by the added Adjust the amounts of water-soluble polymerisation products.
Es hat sich fernerhin gezeigt, daß es besonders vorteilhaft ist, wenn den Polymerisationsprodukten noch Weichmacher, wie beispielsweise Dibutylphthalat od. dgl. andere, zugemischt werden. It has also been shown that it is particularly advantageous if the polymerization products also contain plasticizers such as dibutyl phthalate or the like. Others are added.
Im folgenden wird der Gegenstand der Erfindung an Hand zweier Ausführungsbeispiele näher erläutert. In the following, the subject matter of the invention is based on two exemplary embodiments explained in more detail.
Beispiel I 250 g einer Polyvinylacetatemulsion, die 500/0 Polyvinylacetat Festsubstanz enthält, wird mit 200 g Wasser vermischt. Dieser Mischung werden 50 g Dibutylphthalat, in 250 g Wasser eingerührt, zugesetzt. Diese Mischung wird stehengelassen und erst etwa 24 Stunden nach dem Ansetzen verwandt. Example I 250 g of a polyvinyl acetate emulsion containing 500/0 polyvinyl acetate Contains solid substance, is mixed with 200 g of water. This mix will be 50 g of dibutyl phthalate, stirred into 250 g of water, added. This mixture is left to stand and used only about 24 hours after preparation.
1 kg Kasein wird in 41 Wasser angeschwemmt und mehrere Stunden stehengelassen. In diese Anschwemmung werden dann 300 g Kalkhydrat in 2 1 Wasser unter gutem Rühren eingebracht. 1 kg of casein is washed up in water and left to stand for several hours. 300 g of hydrated lime in 2 l of water are then poured into this alluvial layer with thorough stirring brought in.
Die wenigstens 24 Stunden alte Polyvinylacetatmischung wird in die Kaseinauschwemmung eingerührt, anschließend mengt man in dieses Gemisch unter stetiger Zugabe Holzabfälle, bis eine teigige Masse entsteht, die dann in der in den vorgenannten Patenten beschriebenen Weise weiterverarbeitet wird. The polyvinyl acetate mixture, which is at least 24 hours old, is added to the Casein flooding stirred in, then mixed into this mixture with constant Adding wood waste until a doughy mass is formed, which is then used in the aforementioned Patents described manner is further processed.
Beispiel 2 Die Kaseinaufschwemmung wird in gleicher Weise, wie im Beispiel I angegeben, hergestellt. Example 2 The casein suspension is made in the same way as in Example I indicated, produced.
Dieser Anschwemmung wird eine etwa I Tag alte Emulsion zugesetzt, die in folgender Weise erhalten wurde: 250 g einer Polyvinylacetatemulsion, die aus 53 0/o Polyvinylacetat, 35 0/o Wasser und I2°/e Weichmacher, z. B. Dibutylphthalat, besteht, werden mit 375 bis 500 ccm Wasser verdünnt, so daß eine milchige Flüssigkeit entsteht. An emulsion about 1 day old is added to this alluvium, which was obtained in the following manner: 250 g of a polyvinyl acetate emulsion, the from 53% polyvinyl acetate, 35% water and 12% plasticizer, e.g. B. dibutyl phthalate, are diluted with 375 to 500 cc of water, so that a milky liquid arises.
Nach Zusammenmischung der Kaseinaufschwemmung mit der Polyvinylacetatemulsion werden in diese 14 bis I81 vorhydrolysierte, zerfaserte Holzabfälle eingebracht, denen verschiedene Zuschläge zugesetzt sind. Zweckmäßigerweise wird eine gute und innige Mischung mit Hilfe eines mechanischen Mischers erzielt. After mixing the casein suspension with the polyvinyl acetate emulsion pre-hydrolyzed, shredded wood waste is introduced into these 14 to I81, to which various supplements are added. Appropriately, a good and intimate mixing achieved with the aid of a mechanical mixer.
Die Masse wird anschließend ohne Anwendung von Druck und Wärme in gewünschter Weise geformt. The mass is then in without the application of pressure and heat shaped as desired.
Beispiel 3 500 g Kasein, 500 g Sojamehl und 200 g Kaolin werden in 3 1 kaltem Wasser eingeweicht. Example 3 500 g casein, 500 g soy flour and 200 g kaolin are used in 3 1 soaked in cold water.
In diese Aufschwemmung werden I50 g einer wäßrigen 15 e/0 Ammoniak enthaltenden Lösung und 50 g Calziumcarbonat eingebracht und das Ganze auf etwa 700 erwärmt. 150 g of an aqueous 15 e / 0 ammonia are added to this suspension containing solution and 50 g of calcium carbonate introduced and the whole to about 700 heated.
500 g Polyvinylacetat, 25 g technischer Polyvinylalkohol in 1 1 Wasser und 100 g Weichmacher in 1/2 1 Wasser werden zusammengemischt und der ersten Mischung zugesetzt. Die Einbringung von zerkleinerten Holzabfällen oder anderen Stoffen erfolgt anschließend in bekannter Weise. 500 g of polyvinyl acetate, 25 g of technical grade polyvinyl alcohol in 1 l of water and 100 g plasticizer in 1/2 1 water are mixed together and the first mixture added. The introduction of shredded wood waste or other substances takes place then in a known manner.
Claims (2)