Verfahren zur Herstellung von Fensterkitt Zur Herstellung von Fensterkitt
und ähnlichen Massen wurden bisher trocknende oder halbtrocknende Öle verwendet,
mit denen man Schlämmkreide oder andere feingemahlene Mineralbestandteile innig
vermischte. Auch ölfreie Kittmassen, die wie Leinölkitte steinhart werden, sind
bereits vorgeschlagen worden. In vielen Fällen ist es jedoch unerwünscht, wenn der
Kitt steinhart wird, da die Entfernung alter Kittreste in diesem Fall bei Reparaturen
usw. erhebliche Schwierigkeiten verursacht. Aus diesem Grunde und wegen des Mangels
an Leinöl und Firnis hat man nach Stoffen gesucht, mit deren Hilfe man Kitte von
besseren Eigenschaften herstellen kann.Process for the manufacture of window putty For the manufacture of window putty
and similar masses, drying or semi-drying oils have been used so far,
with which you can get whitewashed chalk or other finely ground mineral components intimately
mingled. Oil-free putty compounds, which are rock-hard like linseed oil putty, are also
has already been proposed. In many cases, however, it is undesirable if the
Putty becomes rock-hard, as old putty residues are removed in this case during repairs
etc. causes considerable trouble. For this reason and because of the lack
In linseed oil and varnish, people have searched for substances with the help of which one can putty from
can produce better properties.
Wenn an Stelle eines trocknenden Öles nichttrocknende Öle verwendet
werden, beispielsweise Mineralöle oder synthetische Schmieröle, dann erhält man
Massen, die sich zwar in der Konsistenz ähnlich wie Leinölkitte verhalten, beim
praktischen Gebrauch aber die ihnen gegebene Form nicht behalten, sondern aus den
Kittfugen herauslaufen. Wenn der Olanteil verringert wird, dann ergeben sich kurze
und bröckelige Kitte, die jedoch im Falz auch nicht besser erhärten. Auch solche
Kittmassen sind praktisch nicht verwendbar, da ihre Verarbeitung zu viel Zeit erfordert.
Zur Vermeidung dieser Nachteile hat man bereits Kittmassen vorgeschlagen, die neben
mineralischen Ölen teilweise trocknende Öle oder Kunstharzprodukte enthalten.If non-drying oils are used instead of a drying oil
are, for example, mineral oils or synthetic lubricating oils, then one obtains
Masses that behave similarly to linseed oil putty in consistency
practical use, however, does not retain the form given to them, but from the
Putty joints run out. If the proportion of oil is reduced, the result is short ones
and crumbly putty, which, however, does not harden better in the fold. Even those
Putty masses are practically unusable, since their processing takes too much time.
To avoid these disadvantages, putty compounds have already been proposed that, in addition to
mineral oils partly contain drying oils or synthetic resin products.
Es wurde gefunden, daB man Fensterkitte und ähnliche an der Luft erhärtende
Massen mit guten Gebrauchseigenschaften unter ausschließlicher Verwendung von Mineralölen
oder synthetischen Schmierölen mit mineralischen Füllstoffen erhält, z. B. mit Schlämmkreide,
wenn man der Mineralölnüschung
geringe Wassermengen, vorzugsweise
3 bis 4 °/o Wasser, berechnet vom Gewicht der feinstgemahlenen Mineralstoffe, zusetzt.
Der Wasserzusatz stabilisiert die erhaltenen Suspensionen. Auf ioo Teile Mineral
wurde das Optimum des Wasserzusatzes bei 4 Teilen Wasser gefunden. Wählt man Mischungen,
die ohne Wasser bereits bei Zimmertemperatur ablaufen, so liegen deren Ablauftemperaturen
bei 2 Teilen Wasser bei 37
- 3 - - - 62'
- - - 76.
- 5 - - - 420
- 6 - - - 390
Wenn neben dem Wasserzusatz noch ein solcher von geringen Mengen von gebranntem
Kalk, z. B. 2 bis 40/, des Minerals, gegeben wurde, konnte die Ablauftemperatur
weiter gesteigert werden, z. B. bei 4 Teilen gebranntem Kalk auf 8g°. Die Wirkung
des gebrannten Kalkes beruht auf der Neutralisation der durch Alterung in dem (11
entstehenden Fettsäuren. Durch die gebildeten Kalkseifen tritt eine Verfestigung
der Mineralbestandteile ein. An Stelle des gebrannten Kalkes können z. B. auch Magnesia
oder gebrannter Dolomit zugesetzt werden.It has been found that window putties and similar compounds which harden in the air and have good performance properties are obtained using only mineral oils or synthetic lubricating oils with mineral fillers, e.g. B. with whitewashing chalk, if small amounts of water, preferably 3 to 4% water, calculated on the weight of the finely ground minerals, are added to the mineral oil mixture. The addition of water stabilizes the suspensions obtained. For 100 parts of mineral, the optimum water addition was found with 4 parts of water. If you choose mixtures that run off at room temperature without water, then their run-off temperatures lie with 2 parts of water at 37
- 3 - - - 62 '
- - - 76.
- 5 - - - 420
- 6 - - - 390
If, in addition to the addition of water, such a small amount of quick lime, z. B. 2 to 40 /, the mineral, was given, the drain temperature could be increased further, z. B. with 4 parts burnt lime to 8g °. The action of quick lime is based on the neutralization of the fatty acids formed in the (11) through aging. The lime soaps formed solidify the mineral components. Instead of quick lime, magnesia or burnt dolomite can also be added, for example.
Eine weitere wesentliche Verbesserung tritt ein, wenn man einen Teil
des viskosen Öles durch Schwerbenzin, Dieselöl oder andere flüchtige Kohlenwasserstoffe
ersetzt. Bereits i Teil flüchtige Kohlenwasserstoffe zeigt die Wirkung, daß der
Kitt selbst bei ioo° nicht mehr abläuft. Gegebenenfalls können den Ölen Sikkative
zugesetzt werden.Another major improvement occurs when you look at a part
of the viscous oil through heavy gasoline, diesel oil or other volatile hydrocarbons
replaced. Already i part volatile hydrocarbons shows the effect that the
Putty no longer runs off even at ioo °. If necessary, siccatives can be added to the oils
can be added.
Es wurde weiterhin gefunden, daß der Zusatz von 0,5 bis i Teil Baumharz,
Cumaronharz oder lösliches Kunstharz die Kittmasse zäh und plastisch macht und nach
4 bis 6 Wochen eine oberflächliche Erhärtung durch Bildung von Harz-Kalk-Seifen
mit den Erdalkalioxyden hervorruft. Eine andere Wirkung des Harzzusatzes liegt darin,
daß die Kittmasse auch bei Dauererschütterungen, wie diese sehr oft an Fabrikgebäuden,
in denen Maschinen laufen, die ihr gegebene Form nicht verändert. Auch ein Zusatz
von Tran, z. B. Waltran, gegebenenfalls neben Harzen hat sich als vorteilhaft erwiesen
und erlaubt, geringe Mengen Öl zu verwenden. Bei der Einhaltung der in der Erfindung
gegebenen Vorschriften erhält man Kittmassen, die den aus Leinölfirnis hergestellten
Massen mindestens ebenbürtig, wenn nicht überlegen sind.It was also found that the addition of 0.5 to 1 part tree resin,
Coumarone resin or soluble synthetic resin makes the cement paste tough and plastic and gradually
4 to 6 weeks a superficial hardening through the formation of resin-lime soaps
with the alkaline earth oxides. Another effect of adding resin is to
that the putty compound even with permanent vibrations, as is very often the case in factory buildings,
in which machines run that do not change their given form. Also an addition
from Tran, z. B. Waltran, optionally in addition to resins, has proven advantageous
and allows small amounts of oil to be used. When adhering to in the invention
given regulations one obtains putty masses that are made from linseed oil varnish
Masses are at least equal, if not superior.
Ausführungsbeispiel In einer 8o 1 fassenden Knetmaschine mischt man
ioo kg Kittkreide oder feinstgemahlenes Kalksteinmehl mit 2 kg gemahlenem gebranntem
Kalk und gibt hierzu 3 kg Wasser. Nach dem Durcharbeiten gibt man 16 kg eines hochviskosen
Schmieröles mit einer Jodzahl von 2o, 6o,2 kg einer Auflösung von x Teil Baumharz
in i Teil Schmieröl und 1,5 kg einer über 150' siedenden Kohlenwasserstofffraktion
hinzu, worauf noch 45 Minuten lang geknetet wird. Durch Zugabe von färbenden Bestandteilen
kann die Farbe der Kitte auf den gewünschten Farbton gebracht werden.Exemplary embodiment Mixing is carried out in a kneading machine with a capacity of 8o 1
100 kg of putty chalk or finely ground limestone flour with 2 kg of ground burnt
Lime and add 3 kg of water. After working through you give 16 kg of a highly viscous one
Lubricating oil with an iodine number of 2o, 6o, 2 kg dissolving x part of tree resin
in i part lubricating oil and 1.5 kg of a hydrocarbon fraction boiling over 150 '
added, which is then kneaded for 45 minutes. By adding coloring ingredients
the color of the putty can be brought to the desired shade.