DE884004C - Polishing arch - Google Patents
Polishing archInfo
- Publication number
- DE884004C DE884004C DEM7757A DEM0007757A DE884004C DE 884004 C DE884004 C DE 884004C DE M7757 A DEM7757 A DE M7757A DE M0007757 A DEM0007757 A DE M0007757A DE 884004 C DE884004 C DE 884004C
- Authority
- DE
- Germany
- Prior art keywords
- polishing
- layer
- adhesive
- particles
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Polierbogen Die Erfindung bezieht sich auf einen mit einem Überzug versehenen Polierbogen, insbesondere zum Naßpolieren von Glas, der aber auch zu anderen Polierarbeiten Verwendung finden kann und ;der aus einem Polierpulver besteht, das auf elastischen Teilchen aufgebracht ist, die auf einer biegsamen Unterlage befestigt sind, die in ihren Abmessungen möglichst unveränderlich ist.Polishing sheet The invention relates to one having a coating provided polishing sheet, especially for wet polishing of glass, but also to can be used for other polishing work and; which consists of a polishing powder, which is applied to elastic particles, which are on a flexible base are attached, which is as invariable as possible in its dimensions.
Die Kanten von Glastafeln werden bekanntlich mittels Stahlscheiben, Korkscheiben oder Filzscheiben unter Verwendung von losem Schleif- oder Polierstaub geschliffen und poliert, wobei die z. B. als wäßrige Aufschlämmung verwendete Poliermassel stetig aufgebracht wird. Das Vorschleifen erfolgt durch mit Schleifmittel überzogene Riemen, die unter ständiger Benetzung mit Wasser zu arbeiten vermögen und die die losen Schleifstaub verwendenden Systeme ersetzt haben. Früher wurden ,die meisten Poliervorgänge, wenn nicht überhaupt alle Poliervorgänge, mit einer flüssigen Suspension von Juwelierrot oder ähnlichen Polierpulvern durchgeführt, die auf Kork-, Filz- oder auf andere Polierscheiben usw. aufgetragen wurden.As is well known, the edges of glass panels are made using steel disks, Cork discs or felt discs using loose sanding or polishing dust ground and polished, the z. B. used as an aqueous slurry buffing is applied steadily. The pre-grinding is carried out by coated with abrasives Belts that are able to work under constant wetting with water and that the have replaced systems that use loose sanding dust. Before, most of them were Buffing operations, if not all buffing operations, with a liquid suspension carried out by jeweler red or similar polishing powders that are applied to cork, felt or applied to other polishing pads, etc.
Die Erfindung ermöglicht ein schnelleres Polieren mit weniger Schleifgängen, als es .bei den lose Pulver verwendenden Verfahren möglich ist, und vermeidet auch die Unsauberkeit bekannter Polierverfahren.The invention enables faster polishing with fewer grinding steps, than is possible with methods using loose powders, and avoids also the uncleanliness of known polishing processes.
Die verschiedenen Figuren in, -der Zeichnung zeigen in Seitenansicht verschiedene besondere Ausführungsformnen,dier Erfindung.The various figures in, -der drawing show in side view various particular embodiments of the invention.
Die Ausführung gemäß Fig. i besteht aus einer biegsamen Unterlage io, die mit einer Leimschicht i r überzogen ist und eine Lage von elastischen Teilchen 12 trägt, die durch eine erste Klebstoffschicht 13 befestigt sind. Die frei liegende Oberfläche der Teilchen und die zwischen @diesen liegende Klebstoffschicht ist weiterhin mit einer Polierschicht 14 überzogen, die aus Polierpulver besteht, das in einem Klebstoff dispergiert ist, der eine etwas größere Festigkeit und Härte als das Material der ersten Klebstoffschicht 13 hat.The embodiment according to FIG. 1 consists of a flexible base 10 which is coated with a layer of glue ir and carries a layer of elastic particles 12 which are attached by a first layer of adhesive 13. The exposed surface of the particles and the adhesive layer between them is further coated with a polishing layer 14, which consists of polishing powder that is dispersed in an adhesive that has a somewhat greater strength and hardness than the material of the first adhesive layer 13 .
Bei der in Fig. 2 dargestellten abweichenden Ausführungsform ist eine biegsame Unterlage 2o unmittelbar mit einer Klebstoffschicht 23 überzogen worden, in die die elastischen Teilchen 22 eingedrückt worden sind. Die Teilchen 22 und die Klebstoffschicht 23 sind dann mit einer Klebstoffschicht 25 und mit einem Entdüberzug aus Polierpulver 26 überzogen worden.In the variant embodiment shown in Fig. 2 is a flexible base 2o has been coated directly with an adhesive layer 23, into which the elastic particles 22 have been pressed. The particles 22 and the adhesive layer 23 are then coated with an adhesive layer 25 and with a dedoating been coated from polishing powder 26.
Fig: 3 zeigt eine Abwandlung, bei der elastische Teilchen 32 zuerst für sich mit einem erhärteten überzug 34 aus einem Gemisch von Polierpulver und Klebstoff eingehüllt worden ist und dann an die biegsame Unterlage 30 mittels einer Klebstoffschicht 33 angeklebt worden ist.3 shows a modification in which elastic particles 32 have first been enveloped for themselves with a hardened coating 34 made from a mixture of polishing powder and adhesive and then adhered to the flexible base 30 by means of an adhesive layer 33.
In Fig: 4 sind die elastischen Teilchen 42 an die biegsame, vorher mit einer Leimschicht 41 bedeckte Unterlage 40 mittels einer Klebstoffschicht 44, die aus einer Dispersion von Polierpulver in einem Klebstoff besteht, angeklebt.In Fig: 4, the elastic particles 42 are attached to the flexible, previously underlay 40 covered with a layer of glue 41 by means of an adhesive layer 44, which consists of a dispersion of polishing powder in an adhesive.
Nachstehend wird nun ein bestimmtes Herstellungsbeispiel eines gemäß Fig. i ausgeführten Polierbogens beschrieben, der mit gutem Erfolg in der Form eines endlosen Riemens beim Naßpolieren von Glas verwendet wurde. Obwohl endlose Riemen bevorzugt werden, kann das Bogenmaterial auch in der Form von Scheiben, Kegeln, flachen- Platten oder Streifen usw. zur Anwendung gelangen.A specific example of the preparation of an according to Fig. I executed polishing sheet described, which with good success in the form of a endless belt was used in wet polishing of glass. Though endless straps are preferred, the sheet material can also be in the form of discs, cones, flat plates or strips etc. are used.
Die biegsame Unterlage wurde aus einem gestreckten Drillichtuch, das zuvor einer Schrumpfungsbehandlung unterworfen worden war, mit einem Gewicht von etwa 3,25 g je 155 cm2 hergestellt. Das Tuch wurde zuerst mit einer 2oo/oigen Lösung von 2o cps (47 bis 5o °/a Äthoxy-) Äthylcellulose imprägniert und enthielt nach dem Trocknen etwa 0,845 bis i,105 g an getrocknetem Rückstand auf je 155 cm2.. Während des Trocknens wurde,die Bahn flachgestreckt gehalten. Die: Äthylcellulose versteifte das Tuch, machte dieses wasserfestig und verbesserte die Verankerung, während das Eindringen des Klebstoffauftrages vermindert wurde.The flexible base was made from a stretched drill cloth that previously subjected to a shrinkage treatment, weighing about 3.25 g per 155 cm2. The cloth was first treated with a 2oo% solution of 20 cps (47 to 50% / a ethoxy) ethyl cellulose impregnated and contained after the drying about 0.845 to i, 105 g of dried residue per 155 cm2 .. During of drying, the web was held stretched flat. The: ethyl cellulose stiffened the cloth, made this waterproof and improved the anchorage, while the Penetration of the adhesive coating was reduced.
Der Klebstoff bestand aus 85 Teilen Polyvinylacetat und ii Teilen Diatomeenerde in 148 Teilen Xylol und 148 Teilen Alkohol. Es wurde so viel Lösung aufgetragen,.. daß nach dem Trocknen auf je i55 Cll12 o,65 bis o;78 Festbestandteile zurückblieben. Diese Klebstoffschicht verbesserte weiter die Wasserfestigkeit und Eigenschaft der Bahn und ergab auch eine verbesserte Verankerung für den Klebstoff.The adhesive consisted of 85 parts polyvinyl acetate and ii parts Diatomaceous earth in 148 parts of xylene and 148 parts of alcohol. There was so much solution applied, .. that after drying to 1.55 Cll12 o.65 to o.78 solid components lagged behind. This adhesive layer further improved the water resistance and Property of the sheet and also resulted in improved anchorage for the adhesive.
Ein mit trocknendem Öl modifiziertes Alkydharä wurde als Bindemittel für die elastischen Teilchen verwendet. Als Klebemittel benutzt man die in der Schleifmittelindustrie zum Ankleben von Schleifkörnern. an Stoffunterlagen üblichen, z. B. ein Alkydharzbindemittel, das aus einem mit leinölmodifizierten Phthalglycerid besteht. Durch dessen Verwendung wurden.die elastischen Teilchen fest und elastisch an der geleimten Unterlage gehalten. Auf je 155 cm2 der Unterlage kommen 1,625 bis 1,950 g dieses Bindemittels ohne Anrechnung des Lösungsmittels.An alkyd resin modified with drying oil was used as a binder for the elastic particles. The adhesive is used in the abrasive industry to stick abrasive grains. on material documents usual, z. B. an alkyd resin binder, which consists of a phthalic glyceride modified with linseed oil. By using it, the elastic particles were held firmly and elastically on the glued base. There are 1.625 to 1.950 g of this binding agent for every 155 cm2 of the substrate, not counting the solvent.
Als elastische Teilchen werden in erster Linie Korkteilchen verwendet. Der zerkleinerte Kork wird gesiebt; um übergroße Stücke abzusondern. Die Anteile, die durch ein Maschensieb Nr.24 bis 36 (engl.) hindurchgehen, wurden verwendet, obwohl auch andere Teilchengrößen benutzt werden können. Das Material wurde über den mit Klebstoff bestrichenen Bogen ausgebreitet und mit Walzen niedlerge,drückt. Der überschuß wurde dann abgeschüttelt. Für gewöhnlich wird nur eine einzige Teilchenschicht erhalten, falls das Bindemittelgewicht und die Teilchen die angegebenen Werte haben. Das Gewicht der Schicht aus Korkteilchen betrug annähernd o;585 bis o,65 g je 155 cm2. Der Bogen wurde dann für 24 Stunden in einen Ofen eingebracht, um das Lösungsmittel abzutreiben und den Klebstoff zu härten.Cork particles are primarily used as elastic particles. The crushed cork is sieved; to segregate oversized pieces. The portions which will pass through a # 24-36 mesh screen were used, although other particle sizes could be used. The material was spread over the sheet coated with adhesive and pressed down with rollers. The excess was then shaken off. Usually only a single layer of particles is obtained if the binder weight and the particles are as stated. The weight of the layer of cork particles was approximately 0.585 to 0.65 g per 155 cm2. The sheet was then placed in an oven for 24 hours to drive off the solvent and set the adhesive.
Der Bogen ist nun fertig zum Auftragen der Polierschicht, die in diesem Falle aus einem Gemisch von in !der Luft schwebendem Tripoli (einem siliciumartigen Polierpulver) und einem Phenolaldehydfirnis bestand. 75 Gewichtsteile des Tripoli wurden einer ausreichenden Menge flüssigem Firnis zugemischt, so daß in diesem 29 Gewichtsteile der nichtflüchtigen Bestandteile enthalten waren. Das Gewicht eines Überzugs aus diesem Gemisch, auf Trockenbasis bezogen,, betrug 6,76 g je 155 cm2. Weitere Erwärmung des - überzogenen Bogens härtet das Firnisbindemittel, so daß dieses hart und zähe wird.The arch is now ready to apply the polish that is in this Trap made from a mixture of tripoli floating in the air (a silicon-like Polishing powder) and a phenol aldehyde varnish. 75 parts by weight of the Tripoli were mixed with a sufficient amount of liquid varnish, so that in this 29th Parts by weight of the non-volatile components were included. The weight of one Coating from this mixture, on a dry basis, was 6.76 g per 155 cm2. Further heating of the coated sheet hardens the varnish binder so that this becomes hard and tough.
Endlose Riemen wurden in bekannter Weise aus einem überzogenen und gehärteten Bogenmaterial dadurch hergestellt; daß der Bogen auf geeignete Breite geschnitten und dann die Enden abgeschrägt und miteinander verklebt wurden. Der entstehende Riemen behält bei Benutzung seine Form und Festigkeit bei, auch wenn er gleichzeitig der Einwirkung eines ständigen Wasserstroms ausgesetzt wird. Mittels des Riemens würden vorgeschliffene Glaskanten schnell und wirkungsvoll glattpoliert. Beispielsweise wurden Glasplatten, die mit einem mit Schleifkorn Nr. 32o belegten Riemen an den Kanten vorgeschliffen waren, mittels des oben beschriebenen Polierriemens unter einem dauernd fließenden Wasserstrom in weniger als 5 Sekunden auf die gewünschte Hochpolitur geschliffen. Ältere Verfahren zur Oberflächenbearbeitung, bei denen ein Schlamm aus Pulver und Wasser verwendet wird, würden wenigstens mehrere Minuten erfordert haben, um eine gleichgute Kante zu erzeugen.Endless straps were made from a coated and in a known manner hardened sheet material produced thereby; that the arch is at the appropriate width cut and then the ends beveled and glued together. Of the The resulting belt retains its shape and strength when in use, even if it is simultaneously exposed to the action of a constant stream of water. Means of the belt, pre-ground glass edges would be polished smoothly quickly and effectively. For example, glass plates that were coated with an abrasive grain No. 32o Belts were pre-sanded at the edges, using the polishing belt described above under a continuously flowing stream of water in less than 5 seconds to the desired High polish ground. Older methods of surface treatment, at where a powder and water slurry is used, at least several would be Took minutes to create an equally good edge.
Das neue Bogenmaterial erzielt eine hohe Poliergeschwindigkeit und Polierleistung. Ein zusätzlicher und unerwarteter Vorteil beruht auf der langen Verwendungsdauer dieser Polierriemen. Kork ist ziemlich bröcklig, und es sollte erwartet werden, daß der Kork unter den beim Naßschleifen auftretenden hohen Beanspruchungen nach einigen Umläufen über -das Werkstück weg abreißen oder von dem Bindemittel abgzzogen würde. Es wurde jedoch im Gegenteil gefunden, d@aß das Vorhandensein der Korkteilchen sowohl die Verwendungsclauer und die Poliergeschwindigkeit und -leistung als auch die Güte der erzeugten Politur verbessert. Beispielsweise erzeugte ein Riemen, bei dem die gleiche Mischung von Tripoli und Firnis unmittelbar auf das behandelte und geleimte Unterlagetuch ohne Korkteilchen aufgestrichen wurde, Kratzer in der Glaskante und war nach nur wenigen Minuten Benutzungsdauer unwirksam geworden. Im Gegensatz dazu erzielt der eine Lage von Korkteilchen aufweisende und gemäß dem vorstehenden Beispiel hergestellte Riemen eine kratzerfreie Politur und war nach einer Arbeitsdauer von i Stunde noch verwendbar. Ferner war der mit Kork versehene Riemen gemäß der Erfindung leichter zu handhaben; die Lagen aus Kork und Klebstoff machen den Streifen weniger schlaff und wasserfester.The new sheet material achieves a high polishing speed and Polishing performance. An additional and unexpected benefit is based on the long one Duration of use of these polishing belts. Cork is pretty crumbly, and it should be it is expected that the cork will be exposed to the high stresses occurring during wet grinding after a few revolutions over -tear off the workpiece or from the binding agent would be deducted. However, on the contrary, it was found that the presence of the Cork particles both steal the usage and the polishing speed and performance as well as the quality of the polish produced is improved. For example, a generated Belt in which the same mixture of Tripoli and varnish is applied directly to the Treated and glued underlay was spread without cork particles, scratches in the edge of the glass and had become ineffective after only a few minutes of use. In contrast, the one having a layer of cork particles and according to the The belt produced in the previous example had a scratch-free finish and was after can still be used for a working period of 1 hour. Furthermore, the one provided with cork Belts according to the invention easier to handle; the layers of cork and glue make the strip less slack and more waterproof.
Die mit dem neuartigen Bogenmaterial erzielten Erfolge lassen sich zum Teil wahrscheinlich in folgender Weise erklären. Das Vorhandensein der elastischen Masse unterhalb des Polierpulvers bewirkt einen nahezu konstanten Druck aller Pulverteilchen gegen die zu polierende Fläche, so daß eine Höchstpolierwirkung erreicht wird; außerdem können etwas gröbere Pulver verwendet werden, als sonst wegen Neigung zum Kratzen angewendet werden dürfen. Die Ungleichmäßigkeit der Polierfläche, die durch das Vorhandensein der Barunterliegenden großen Korkteilchen verursacht wird, erhöht den Flächendruck gegen das Werkstück und ergibt ein schnelles Abschleifen.The successes achieved with the new sheet material can be partly likely to explain in the following way. The presence of the elastic The mass below the polishing powder causes an almost constant pressure of all powder particles against the surface to be polished, so that a maximum polishing effect is achieved; aside from that slightly coarser powders can be used than usual because of the tendency to scratch may be used. The unevenness of the polishing surface caused by the Presence of the underlying large cork particles caused is increased the surface pressure against the workpiece and results in fast sanding.
Das Auftragen des Polierpulvers in unmittelbarer Nähe der elastischen Korkteilchen erhöht die elastischen Eigenschaften der Unterlage und ermöglicht trotzdem die Verwendung eines harten, festen Bindemittels, so daß das Pulver eine höchste Schleifleistung erzielt. Die Korkteilchen selbst tragen zum Polieren bei und verbessern die Politur des Werkstückes.The application of the polishing powder in the immediate vicinity of the elastic Cork particles increase the elastic properties of the underlay and still allow the use of a hard, solid binder, so that the powder is a supreme Grinding performance achieved. The cork particles themselves add to and improve polishing the polishing of the workpiece.
Abgesehen von den für dieVorgänge angeführten Erklärungen steht die Tatsache fest, daß ausgeführte Versuche mit dem neuen Polierbogen, insbesondere in Form von endlosen Riemen auf einer Naßschleifmaschine, ergeben haben, d@aß die Erfindung gegenüber bekannten Verfahren ein schnelleres, leistungsfähigeres, wirtschaftlicheres und im allgemeinen besseres Polieren der Kanten von Glasstreifen oder anderen Flächen auf industrieller Grundlage ermöglicht. Aus den Fiel l#. 2 bis .4 ist erkenntlich, däß mehrere Ausführungsformen verwendet werden können. Fig. -2 zeigt beispielsweise einen Bogen, bei dem die Leimschicht der Fig. i weggelassen ist und bei dem das Polierpulver als ein besonderer Trockenüberzug auf die äußere Klebstoffschicht vor dem Trocknen und Härte n aderselben aufgebracht worden ist. Bei dieser Ausführungsform wird die Unterlage in erhöhtem Maße mit Alkylcellulose oder einem gleichwertigen Imprägnierungsmittel gefüllt, und in den meisten Fällen wird eine etwas größere Menge Klebstoff für die elastischen Teilchen aufgebracht, tun die anliegende Fläche der Unterlage noch weiter zu imprägnieren. Die äußere Klebstoffschicht kann auch etwas dünner sein als bei der in Fig. i dargestellten Ausführung. Die Gesamtmenge an Polierpulver ist demgemäß geringer. Das gesamte Pulver liegt jedoch an oder sehr nahe der Oberfläche des Bogens und mithin in einer Stellung höchster Leistungsfähigkeit.Apart from the explanations given for the processes, the fact is certain that tests carried out with the new polishing sheet, in particular in the form of endless belts on a wet grinding machine, have shown that the invention is faster, more efficient, more economical and in general compared to known methods Enables better polishing of the edges of glass strips or other surfaces on an industrial basis. From the fi el l #. 2 to .4 it can be seen that several embodiments can be used. For example, FIG. 2 shows a sheet in which the glue layer of FIG. 1 is omitted and in which the polishing powder has been applied as a special dry coating to the outer adhesive layer before drying and hardening thereof. In this embodiment, the pad is filled to an increased extent with alkyl cellulose or an equivalent impregnating agent, and in most cases a somewhat larger amount of adhesive is applied for the elastic particles to further impregnate the adjacent surface of the pad. The outer adhesive layer can also be somewhat thinner than in the embodiment shown in FIG. The total amount of polishing powder is accordingly smaller. However, all of the powder lies at or very close to the surface of the sheet and therefore in a position of maximum efficiency.
In Fig. 3 sind die einzelnen Korkteilchen völlig von einer Hülle eines Gemisches aus Polierpulver und Bindemittel umgeben, und die eingehüllten Teilchen sind unmittelbar auf die imprägnierte Unterlage mit einem etwas weicheren Klebmittel angeklebt. Ein derartiger Aufbau erfordert nur einen Klebstoffauftrag auf den Bogen und nur eine Wärmebehandlung.In Fig. 3 the individual cork particles are completely covered by a shell Mixture of polishing powder and binder surrounded, and the encased particles are directly on the impregnated surface with a slightly softer adhesive glued on. Such a structure only requires an application of adhesive to the sheet and only one heat treatment.
Fig..I zeigt eine andere Ausführungsform, für ,die eine einzige Klebstoffschicht genügt. In diesem Falle enthält die einzige Bindemittelmasse sowohl die elastischen Teilchen als auch das Polierpulver.Fig..I shows another embodiment for having a single layer of adhesive enough. In this case the single binder mass contains both the elastic ones Particles as well as the polishing powder.
Es ist aus der Beschreibung ersichtlich, daß viele andere Kombinationen zur Erzielung ähnlicher Vorteile möglich sind. Außerdem sind den Fachleuten viele andere gleichwertige Stoffe und Bestandteile bekannt, die entsprechend den hier gegebenen Lehren verwendet werden können.It will be apparent from the description that many other combinations to achieve similar advantages are possible. In addition, there are many professionals other equivalent substances and ingredients known corresponding to those here given teachings can be used.
Tuchunterlagen können auch vorteilhaft mit Polystyrolharz oder Polyv inylbutyralharz an Stelle von Äthylcellulose imprägniert werden. Papiere oder andere Faserstoffbahnen, die die genügende Festigkeit und Stabilität gegen eine Veränderung der Abmessungen haben, können das Tuch oder den Stoff ersetzen. Vulkanisierte Fasern und verschiedene harzartige Filme aus Kunstharz oder Polymeren können die imprägnierten Faserbahnen als Unterlagen ersetzen.Cloth pads can also be made with polystyrene resin or polyv inylbutyral resin can be impregnated instead of ethyl cellulose. Papers or other Fiber webs that have sufficient strength and stability against change of the dimensions can replace the cloth or fabric. Vulcanized fibers and various resinous films made of synthetic resin or polymer may be impregnated Replace fiber webs as underlays.
An Stelle von V inylacetatpolymeren können plastizierte Phenolharze als Leimschicht i i bei der Durchführung nach Fig. i verwendet werden. PolyvinyIbuty Talharz wird verwendet, um den Alkydharzklebstoff 13 und den Klebstoff der Polierschicht 1q. zu ersetzen. Bei einer anderen Ausführungsform mit trocknendem Öl wird modifiziertes Phenolaldehydharz als Bindemittel für das Polierpulver mit ausgezeichneten Erfolgen verwendet. Bei einer besonderen Zusammenstellung dieser Art wurde ein Firnis verwendet, der aus einem Teil Paraphenylphenolformaldehydharz und drei Teilen mit Dicyclopentadien modifizierten Leinöls, das in einer Lösung aus Xylol und Naphtha gelöst ist, aufgebracht wird. Ein mit einer kleinen Menge Phenolharz modifiziertes Polyvinylbutyral kann auch verwendet werden. Diese und andere ähnliche filmbildende Klebstoffe zeigten gleichfalls erwünschte Eigenschaften. Weichere Stoffe sind jedoch zu vermeiden, weil ihnen die erforderliche Festigkeit fehlt, und härtere Stoffe, z. B. Kombinationen von Pölyvinylbutyral mit einer übermäßig großen Menge von Phenoläldehydharz, sind umgeeignet, da hierdurch die Glasoberfläche zerkratzt werden kann.Plasticized phenolic resins can be used in place of vinyl acetate polymers can be used as glue layer i i in the implementation according to FIG. PolyvinyIbuty Valley resin is used to make the alkyd resin adhesive 13 and the adhesive of the polishing layer 1q. to replace. Another embodiment with drying oil is modified Phenol aldehyde resin as a binder for the polishing powder with excellent results used. In a special combination of this type a varnish was used that of one part paraphenylphenol formaldehyde resin and three parts with dicyclopentadiene modified linseed oil, which is dissolved in a solution of xylene and naphtha, is applied will. One with a small amount of phenolic resin modified polyvinyl butyral can also be used. These and other similar film-forming adhesives showed also desirable properties. However, softer fabrics are to be avoided, because they lack the required strength, and harder materials, such. B. Combinations of polyvinyl butyral with an excessively large amount of phenolic aldehyde resin unsuitable as this can scratch the glass surface.
Die verschiedenen Kombinationen der obenerwähnten Imprägniermittel, Leime und Klebstoffe zeigen zum Polieren von Glaskanten besonders günstige Ergebnisse in Kombination mit Korkteilchen und Tripoli-Polierpulver. Der verhältnismäßig harte äußere Klebstoff haftet fest an den Korkteilchen und dem umgebenden, etwas weicheren inneren Klebstoff, der seinerseits gut an dem Kork und an der Leimschicht, wo eine solche Leimschicht verwendet wind, oder unmittelbar an der imprägnierten Faserunterlage, wie in Eig. 2 @dargestellt, haftet, so daß man einen gut verfestigten Verbundbogen erhält. Zum Polieren anderer Stoffe können noch andere Kombinationen als geeignet befunden werden. So war ein Bogen"dessenArafibau in Fig. q. dargestellt ist, ausgezeichnet zum Polieren von aus Kunstharz bestehenden Paneelen, wie z. B. einem Polymeren, rd'er Mebhylmethacrylat geeignet. Der Bogen wunde aus einer Tuchunterlage, rdie mit Polyvinylbutyralharz getränkt war, hergestellt. Diese wurde mit durch wärmehärtbares Phenolaldehydharz, das in Wasser, Alkohol und Äthylenglykolmonoäthyläther gelöst war, grundiert, während für die Korkteilchen und das mineralische Polierpulver ein(P'olyvinylbutyralharzklebstoff verwendet wunde. In diesem Fall wurde ein Evsenoxydpolierpulver verwendet.The various combinations of the above-mentioned impregnating agents, Glues and adhesives show particularly favorable results for polishing glass edges in combination with cork particles and Tripoli polishing powder. The relatively hard one outer glue adheres firmly to the cork particles and the surrounding, somewhat softer one inner glue, which in turn works well on the cork and on the glue layer where a such glue layer is used on the wind, or directly on the impregnated fiber base, as in prop. 2 @shown, adheres, so that you get a well-solidified composite sheet receives. For polishing other fabrics, other combinations can be considered suitable be found. Thus, an arch "the structure of which is shown in Fig. Q. Was excellent for polishing panels made of synthetic resin, such as B. a polymer, rd'er methyl methacrylate suitable. The bow wound from a cloth pad, rdie was impregnated with polyvinyl butyral resin. This was made with by thermosetting Phenol aldehyde resin dissolved in water, alcohol and ethylene glycol monoethyl ether was, primed, while for the cork particles and the mineral polishing powder a (polyvinyl butyral resin adhesive used wound. In this case an Evsenoxide polishing powder was used.
In der Luft schwebendes Tripoli ist ein fein zerteiltes Silicatpölierpulver, das eine schnelle Schleifwirkung mit ausgezeichneter Polierwirkung verbindet, sobald es in diesen neuen Polierbögen zum Polieren von Glas verwendet wird, obwohl beim gewöhnlichen Polieren dieses Pulver als zu grob für Feinpolitur angesehen wird. Bimssteinpulver vom Feinheitsgrad 3F oder 4.F ist ebenfalls zufriedenstellend. Poliermittel aus Zinnoxyd, Ceroxyd oder Eisenoxyd wirken zu langsam und sind für die vorliegenden Zwecke, bei denen es sich um das Polieren von Glas handelt, unnötig fein. Diese Stoffe gehören zu den Polierpulversörten, die gewöhnlich beim Polieren von Glas gebraucht werden, um ein Einkratzen der Glasoberfläche zu verhindern.Tripoli floating in the air is a finely divided silicate polishing powder, which combines fast grinding action with excellent polishing action as soon as it is used in these new polishing sheets for polishing glass, although during Ordinary polishing this powder is considered too coarse for fine polishing. 3F or 4F pumice powder is also satisfactory. Polishes made of tin oxide, cerium oxide or iron oxide act too slowly and are for the present Purposes that involve polishing glass unnecessarily fine. These Substances belong to the group of polishing powders that are usually used when polishing glass used to prevent scratching the glass surface.
Als Material für die elastischen Teilchen wird in der Hauptsache Kork verwendet, da; wie erwähnt, dieses Material eine zusätzliche Polierwirkung außer einem besonders vorteilhaften Grad von Zusammendrückbarkeit und Nachgiebigkeithat. Außerdem kleben die bevorzugten Klebstoffmassen gut an den Korkteilchen. Man kann aber auch vorteilhaft vulkanisierten Kautschuk verwenden. Andere zusammendrückbare und elastische Stoffe, natürlichen oder synthetischen Ursprungs, die die Elastizität der bevorzugt verwendeten Korkteilchen haben, können zusammen mit gleichwertigen Stoffen, die gegen Feuchtigkeit und Hitze beständig sind, verwendet werden.The main material used for the elastic particles is cork used because; As mentioned, this material has an additional polishing effect besides has a particularly advantageous degree of compressibility and compliance. In addition, the preferred adhesive compositions adhere well to the cork particles. One can but it is also advantageous to use vulcanized rubber. Others compressible and elastic fabrics, natural or synthetic, that increase elasticity of the preferred cork particles used can be combined with equivalent Materials that are resistant to moisture and heat are used.
Claims (8)