DE8812773U1 - Tile joint profile made of polymer material - Google Patents
Tile joint profile made of polymer materialInfo
- Publication number
- DE8812773U1 DE8812773U1 DE8812773U DE8812773U DE8812773U1 DE 8812773 U1 DE8812773 U1 DE 8812773U1 DE 8812773 U DE8812773 U DE 8812773U DE 8812773 U DE8812773 U DE 8812773U DE 8812773 U1 DE8812773 U1 DE 8812773U1
- Authority
- DE
- Germany
- Prior art keywords
- metallic foil
- tile joint
- profile
- joint profile
- side walls
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
FLIESENFUGENPROFIL AUS POLYMEREN MERKSTOFFENTILE JOINT PROFILE MADE OF POLYMERIC MATERIALS
Die Neuerung betrifft ein Fliesenfugenprofil aus polymeren Werkstoffen mit im Abstand voneinander angeordneten Seitenwänden aus hart eingestelltem Polymermaterial und einer die Seitenwände verbindenden elastischen Polymerkern, wobei der Polymerkern an einer Sichtfläche mit einer metallisierten Folie abgedeckt ist, die ihrerseits durch eine transparente Polymerschicht geschützt ist. Keramische Platten werden bei ihrer Verlegung mit bekannten Verlegeverfahren durch Trennfugen voneinander getrennt, um bei Bewegungen der verlegten Platten selbst bzw. des Untergrundes Absplitterungen von Plattenkanten zu verhindern. Solche Trennfugen werden durch geschäumte Poiymerstreifen geschaffen, die in den Estrich eingebracht werden und aus diesem Bodenaufbau in einer Höhe herausstehen, die in etwa der Höhe der keramischen Platte entspricht.The innovation concerns a tile joint profile made of polymer materials with spaced-apart side walls made of hard polymer material and an elastic polymer core connecting the side walls, with the polymer core being covered on a visible surface with a metallized film, which in turn is protected by a transparent polymer layer. When laying ceramic tiles using known laying methods, they are separated from one another by separating joints in order to prevent the edges of the tiles from splintering when the tiles themselves or the subfloor move. Such separating joints are created by foamed polymer strips that are inserted into the screed and protrude from this floor structure at a height that roughly corresponds to the height of the ceramic tiles.
Trennfugen werden auch schon durch kastenartige Profile aus Polymermaterialien gebildet, die in sich die Ausdehnungen der keramischen Platten aufnehmen. Aus Funktionsgründen ist es bei solchen Profilen erforderlich, daß die Seitenteile aus hart eingestelltem polymeren Werkstoff bestehen, z.B. aus einem Polyvinylchlorid der Shore-Härte A 100. Diese Seitenteile können geradlinig über die Höhe des Profils verlaufen, sie können jedoch auch zur Mitte hin gerichtete längsverlaufende Einschnürungen aufweisen, so daß im Querschnitt ein X-förmiges Profil entsteht. An ihren Außenseiten können diese Profil-Seitenteile längsgerieft sein, um einen besseren Halt im Fugenmörtel zu finden.Separating joints are also formed by box-like profiles made of polymer materials that absorb the expansion of the ceramic tiles. For functional reasons, it is necessary for such profiles that the side parts are made of hard polymer material, e.g. polyvinyl chloride with a Shore hardness of A 100. These side parts can run straight across the height of the profile, but they can also have longitudinal constrictions directed towards the middle, so that an X-shaped profile is created in the cross section. These profile side parts can be longitudinally grooved on their outside to ensure a better grip in the joint mortar.
2 -2 -
Blatt 2page 2
Der Zwischenraum zwischen den hart eingestellten Seitenteilen ist bei den bekannten Profilen dieser Art mit einem elastischen Kern aus polymerem Werkstoff ausgefüllt. Die harten Seitenteile solcher Profile können auch anstelle der gesamten Ausfüllung des Zwischenraums nur über Brücken des elastischen Materials miteinander verbunden sein. Auf diese Weise wird die Elastizität des Endprofiles gesteigert.The space between the hard side parts in the known profiles of this type is filled with an elastic core made of polymer material. The hard side parts of such profiles can also be connected to each other only via bridges made of elastic material instead of filling the entire space. In this way, the elasticity of the final profile is increased.
Auf der Sichtseite ist das elastische Polymermaterial mit einer metallisierten Folie abgedeckt, die wiederum aus Schutzgründen mit einer dünnen Schicht aus glasklar oder transparent eingestelltem Polymermaterial überspritzt ist. Bei der metallisierten Folie handelt es sich im brannten Profilaufbau um eine metallbedampfte Polyesterfolie, die ein- oder beidseitig einen Haftvermittlerauftrag besitzen kann, üie met?l1isierte Folie wird während des Extrusionsprozesses des Profils auf dessen Oberseite aufgebracht und gleichzeitig mit der Abdeckschicht aus glasklar oder transparent eingestelltem Polymermaterial überspritzt.On the visible side, the elastic polymer material is covered with a metallized film, which in turn is over-molded with a thin layer of crystal-clear or transparent polymer material for protection reasons. The metallized film in the fired profile structure is a metal-coated polyester film that can have an adhesion promoter applied on one or both sides. The metallized film is applied to the top of the profile during the extrusion process and is simultaneously over-molded with the covering layer of crystal-clear or transparent polymer material.
Das extrudierte Profil, das im Koextrusionsverfahren hergestellt wurde, wird noch in der Extrusionsstrecke nach dem Erkalten auf das erforderliche Maß abgelängt und in diesen Abschnitten dem Fliesenleger zur Herstellung von entsprechen Fliesenfugen zur Verfügung gestellt.The extruded profile, which was produced using the co-extrusion process, is cut to the required length in the extrusion line after cooling and is made available in these sections to the tiler for the production of the corresponding tile joints.
Bei der Verarbeitung derartiger Profile hat es sich als nachteilig herausgestellt, daß die metallisierte Folie an den Schnittstellen des Profils durch chemische Angriffe aus dem Fugenmörtel beeinträchtigt wird. Dabei zerstören Chemikalien des zähplastischen Fugenmörtels die aufgedampfte Metallschicht an der Schnittstelle, und diese Zerstörungen werden durch die glasklar oder transparent eingestellte Polymerabdeckung der metallisierten Folie sichtbar.When processing such profiles, it has been found to be disadvantageous that the metallized film at the profile interfaces is damaged by chemical attacks from the joint mortar. Chemicals in the viscoplastic joint mortar destroy the vapor-deposited metal layer at the interface, and this damage becomes visible through the crystal-clear or transparent polymer cover of the metallized film.
Blatt 3Sheet 3
Dadurch wird der optische Effekt solcher Profile erheblich beeinträchtigt.This significantly impairs the optical effect of such profiles.
Obwohl die negative Auswirkung auf die metallisierte Folie nur so lange anhält, bis der zähplastische Fugenmörtel erhärtet ist, reicht diese Zeit aus, um die Metallschicht, angefangen von der Schnittfläche bis unter die glasklare oder transparente r ö &igr; yüiSrä uu6C K UOy &igr;&igr;&idigr;&Pgr;&bgr;&idiagr;&Pgr; ZU ZS"3i.Oren. tylSSSiT) nuCutCIi nCnn" te mit einer aufwendigen Schutzbearbeitung der Schnittstellen abgeholfen werden, jedoch wäre diese Lösung arbeitsintensiv und kostenaufwendig, so daß die Wirtschaftlichkeit eines derart nachbehandelten Profils negativ beeinflußt würde. Although the negative effect on the metallized film only lasts until the viscoplastic joint mortar has hardened, this time is sufficient to remove the metal layer, starting from the cut surface and ending under the crystal-clear or transparent red layer . This can be remedied by means of complex protective processing of the interfaces, but this solution would be labor-intensive and costly, so that the economic efficiency of a profile treated in this way would be negatively affected.
Wenn bei der Herstellung des Profils im Koextrusionsverfahren anstelle der metallisierten eine metallische Folie verwendet wird, entsteht eine Wellenbildung im Bereich der metallischen Folie. Diese Wellenbildung hat ihre Ursache darin, daß bei den unterschiedlichen polymeren Werkstoffen der härteren Seitenteile und des weicher eingestellten Kernes bei der Abkühlung eine Kontraktion im Polymerbereich eintritt, deren Kraft einIf a metallic foil is used instead of the metallized foil when producing the profile in the coextrusion process, waves will form in the area of the metallic foil. This wave formation is caused by the fact that the different polymer materials of the harder side parts and the softer core cause a contraction in the polymer area during cooling, the force of which creates a
nCMI i U \* I · ^ J XJVj UlJ Ul^ &Pgr; UU^I 1 U 1 C 1 VjCII J ^ HU I U CT 11 VJ ^ I C 1 I|\J^UI UVII- nCMI i U \* I · ^ J XJVj UlJ Ul^ &Pgr; UU^I 1 U 1 C 1 VjCII J ^ HU IU CT 11 VJ ^ IC 1 I|\J^UI UVII -
ten metallischen Folie entgegenzusetzen hat. Die Zugkräfte, hervorgerufen durch die Kontraktion der Polymerbereiche, sind somit höher als die Stauchfähigkeit der metallischen Folie. Bei der aus anwendungstechnischen Gründen notwendigen festen Verbindung zwischen der metallischen Folie und den polymeren Werkstoffen des Profils führt di-9 unterschiedliche Kontraktion bei den niedrigeren Shorehärten des elastischen Profiibereiches zur Wellenbildung der Folien einschließlich der Oberfläche des weicheren Profilteiles. Derartige Profile mit welliger Oberfläche sind aber aus optischen Gründen unbrauchbar.The tensile forces caused by the contraction of the polymer areas are therefore higher than the compressibility of the metallic foil. In the case of the solid connection between the metallic foil and the polymer materials of the profile, which is necessary for application-related reasons, the different contraction at the lower Shore hardness of the elastic profile area leads to the formation of waves in the foils, including the surface of the softer profile part. However, such profiles with a wavy surface are unusable for optical reasons.
Hier setzt die Neuerung ein, die sich die Aufgabe gestellt hat, ein Profil aus polymeren Werkstoffen zur Bildung von Fliesenfugen anzugeben, bei dem ohne aufwendige NachbehandlungThis is where the innovation comes in, which has set itself the task of specifying a profile made of polymer materials for the formation of tile joints, without the need for complex post-treatment.
Blatt 4Sheet 4
die metallische Folie an den Schnittstellen ausreichend gegen den Angriff von chemischen Substanzen aus dem zähplastischen Fugenmörtel gesichert ist und bei dem die Wellenbildung der metallischen Folie bei der Herstellung des Profils ausgeschlossen wird.the metallic foil at the interfaces is sufficiently protected against attack by chemical substances from the viscoplastic joint mortar and the formation of waves in the metallic foil during the manufacture of the profile is excluded.
Neuerungsgemäß wird dazu vorgeschlagen, daß der elastische Polymerkern einen Härtegrad besitzt, der maximal 10, vorzugsweise 3-5 Shore-A-Einheiten unter dem Härtegrad der Seitenwände liegt, und daß die metallische Folie eine Metallschicht von wenigstens 10 &mgr; aufweist.According to the innovation, it is proposed that the elastic polymer core has a hardness that is a maximum of 10, preferably 3-5 Shore A units below the hardness of the side walls, and that the metallic foil has a metal layer of at least 10 μ.
Die Neuerung geht von der Tatsache aus, daß die Einwirkungen der metallzersetzenden chemischen Substanzen aus dem Fugenmörtel nur eine relativ kurze Zeitdauer möglich sind, da der Fugenmörtel verhältnismäßig schnell aushärtet. Nach Ablauf des Aushärtungsprozesses sind dann keine chemischen Wechselwirkungen mehr zwischen dem Fugenmörtel und dem Profil- bzw. dem Metallanteil des Profils zu befürchten.The innovation is based on the fact that the effects of the metal-decomposing chemical substances from the joint mortar are only possible for a relatively short period of time, since the joint mortar hardens relatively quickly. After the hardening process has ended, there is no longer any need to fear any chemical interactions between the joint mortar and the profile or the metal part of the profile.
Die angegebenen Schichtdicken setzen dem schädlichen Angriff der chemischen Bestandteile aus dem Fugenmörtel einen solchen Widerstand entgegen, daß nach dem Aushärten des Fugenmörtels wenigstens an der Sichtfläche des Profils durch die glasklar oder transparent eingestellte Polymerabdeckmg keine Beschädigungen des Metalls feststellbar sind. Damit ist der optische Eindruck des Profils im eingebauten Zustand gesichert.The specified layer thicknesses offer such resistance to the damaging attack of the chemical components in the joint mortar that after the joint mortar has hardened, at least on the visible surface of the profile, no damage to the metal can be detected through the crystal-clear or transparent polymer coating. This ensures the optical impression of the profile when installed.
Um die relativ kurze Zeitdauer des Angriffs auf die Metallbestandteile der Folie zu überstehen schlägt die Neuerung vor, entweder den Metallbestandteil der metallisierten Folie in seiner Dicke gegenüber dem bekannten Stand der Technik extrem zu verstärken, oder eine beidseitig mit Haftvermittler beschichtete Aluminiumfolie zu verwenden.In order to withstand the relatively short period of attack on the metal components of the film, the innovation proposes either to increase the thickness of the metal component of the metallized film considerably compared to the known state of the art, or to use an aluminum foil coated on both sides with an adhesion promoter.
"■SS*-"■SS*-
Blatt 5Sheet 5
Die Metallschicht bei metallbedampfter Polyesterfolien liegt üblicherweise im Angströmbereich. Die Neuerung gibt demgegenüber die Lehre, daß die Metallschicht eine Metalldicke von wenigstens 10 &mgr; betragen soll. Metallschichten mit Dicken von 50, 80, 100 oder 200 &mgr; können im Rahmen der Neuerung ebenso vorteilhaft eingesetzt werden.The metal layer in metal-coated polyester films is usually in the Angstrom range. The innovation teaches, however, that the metal layer should have a metal thickness of at least 10 μm. Metal layers with thicknesses of 50, 80, 100 or 200 μm can also be used advantageously within the scope of the innovation.
einer Shore-Ä-Härte 95a Shore A hardness of 95
Es hat sich gezeigt, daß z.B. bei weicher eingestellten Profilkerns noch eine für den Einsatzzweck ausreichende Elastizität des Fliesenfugenprofi Is gegeben ist, wenn die hart eingestellten Seitenwände eine Shore A-Härte 100 aufweisen. Diese definierten und eng begrenzten Härteunterschiede zwischen den Polymermaterialien einerseits und die neuerungsgemäße Dicke der Metallschicht der metallischen Folie andererseits bewirken, daß die Kontraktion im Polymerbereich bei der Abkühlung des aus der Extrusionsdüse austretenden Fliesenfugenprofi Is eine Größenordnung aufweist, die von Werkstoffeigenschaften der metallischen Folie aufgenommen werden kann. Dadurch wird die aus dem Stand der Technik bekannte Wellenbildung absolut verhindert.It has been shown that, for example, with a softer profile core, the tile joint profile still has sufficient elasticity for the intended purpose if the hard side walls have a Shore A hardness of 100. These defined and narrowly limited differences in hardness between the polymer materials on the one hand and the innovative thickness of the metal layer of the metallic foil on the other hand mean that the contraction in the polymer area when the tile joint profile exits the extrusion nozzle cools is of a magnitude that can be absorbed by the material properties of the metallic foil. This completely prevents the formation of waves known from the state of the art.
Bei einer anderen Ausführungsform des neuerungsgemäßen riiesenfugenprofiIs sind die Seitenwände an ihren der metallischen Folie zugewandten freien Enden durch einen Brückensteg aus dem harten Polymermaterial der Seitenwände miteinander verbunden, Auf diesen Brückensteg ist die metallische Folie aufgebracht und mit dem transparenten Schutzüberzug versehen. Der hinter dem Brückensteg liegende Aufnahmeraum zwischen den Seitenwänden kann jetzt mit einem weicheren Polymermaterial aufgefüllt werden, dessen besondere Kontrektion bei der Abkühlung di> ^ den Brückensteg und die Seitenwände aufgefangen werden, ro i^ß eine schädliche Wellenbildung im Bereich der metalIis^en Folie auch in diesem Fall nicht auftreten kann.In another embodiment of the giant joint profile according to the innovation, the side walls are connected to one another at their free ends facing the metallic foil by a bridge web made of the hard polymer material of the side walls. The metallic foil is applied to this bridge web and provided with the transparent protective coating. The receiving space between the side walls behind the bridge web can now be filled with a softer polymer material, the special contraction of which is absorbed by the bridge web and the side walls when it cools, so that harmful wave formation in the area of the metallic foil cannot occur in this case either.
Blatt 6Sheet 6
Die metallische Folie ist vorteilhaft ein Aluminiumband, welches ein- oder beidseitig mit einem wärmeaktivierbaren Haftvermittler versehen ist.The metallic foil is preferably an aluminum strip which is provided with a heat-activated adhesion promoter on one or both sides.
Auf diese Art und Weise kann die metallische Folie in ihrem Endsitz an der Sichtfläche des Fliesenfugenprofils unverrückbar festgelegt werden.In this way, the metallic foil can be fixed in its final position on the visible surface of the tile joint profile.
In einer weiteren Ausführung des neuerungsgemäßen Fliesenfugenprofils ist die metallische Folie an dessen beiden Sichtflächen, versehen mit der transparenten Polymerbeschichtung eingebracht. Dieser Profilaufbau hat den Vorteil, daß an einer Sichtfläche beispielsweise eine silberfarbene Metallschicht und an der anderen Sichtfläche eine goldfarbene Metallschicht die optische Wirkung des Fl iesenfugenprofils bestimmt. Ein solcher Profilaufbau bietet eine variable Anwendung und eine reduzierte Lagerhaltung, da für beide optische Eindrücke nur jeweils ein Profil gelagert werden muß. Die sichtbare Oberfläche der metallischen Folie, d.h. die Oberfläche des Aluminiumbandes, kann natürlich auch in anderen Farben gehalten sein. Diese Farben müssen lediglich den Extrusionsprozess bei der Einbringung der metallischen Folie in die Sichtfläche des Fliesenfugenprofils überstehen. Da es eine ganze Anzahl solcher Farben gibt, die die dabei auftretenden Temperaturen aushalten, ist der geschmacklichen Ausgestaltung der neuerungsgemäßen Fliesenfugenprofile kaum eine Grenze gesetzt.In another version of the new tile joint profile, the metallic foil is applied to both of its visible surfaces, provided with a transparent polymer coating. This profile structure has the advantage that, for example, a silver-colored metal layer on one visible surface and a gold-colored metal layer on the other visible surface determine the optical effect of the tile joint profile. Such a profile structure offers variable application and reduced storage, since only one profile needs to be stored for each of the two optical impressions. The visible surface of the metallic foil, i.e. the surface of the aluminum strip, can of course also be in other colors. These colors only have to survive the extrusion process when the metallic foil is applied to the visible surface of the tile joint profile. Since there are a whole number of such colors that can withstand the temperatures that occur, there are hardly any limits to the taste of the new tile joint profiles.
In der Zeichnung ist das neuerungsgemäße Fliesenfugenprofil 1 in isometrischer Darstellung gezeigt. Das Fliesenfugenprof&iacgr;1 1 besitzt die harten Seitenwände 2, 3, zwischen denen der weicher eingestellte Kern 4 eingeschlossen ist. Sowohl die harten Seitenwände 2, 3, als auch der weicher eingestellte Kern 4 sind im KoextruKionsverfahren hergestellt. Am oberen Abschluß des Kerns 4 ist die metallische Folie 5 eingelassen, die ihrerseits durch die {/lasklare oder transparente Polymerabdekkung 6 abgedeckt ist,,The drawing shows the new tile joint profile 1 in an isometric view. The tile joint profile 1 has the hard side walls 2, 3, between which the softer core 4 is enclosed. Both the hard side walls 2, 3 and the softer core 4 are manufactured using the coextrusion process. The metallic foil 5 is embedded at the top of the core 4, which in turn is covered by the clear or transparent polymer cover 6.
Blatt 7Sheet 7
Die Polymerabdeckung 6 ist ebenfalls im Koextrusionsverfahren zusammen mit den harten Seitenwänden 2, 3 und dem weicher eingestellten Kern 4 hergestellt. Die metallische Folie 5 ist -mit ihrer Metallseite zur Sichtfläche nach oben hin - in den Profilaufbau eingelassen. An der sichtbaren harten Seitenwand 3 sind längsverlaufend rippenartige Erhöhungen 31 angedeutet, welche zur Verankerung des Profils im Fugenmörtel dienen. Die gleichen rippenartigen Erhöhungen 31 können auch auf der Aussenseite der harten Seitenwand 2 angeordnet sein. Das Fliesenfugenprofil 1 besitzt eine Höhe, welche der Höhe der eingesetzten Fliesen entspricht. Auf diese Weise schließt das Fliesenfugenprofil 1 im Einsatz bündig mit der Fliesenebene ab.The polymer cover 6 is also manufactured using the coextrusion process together with the hard side walls 2, 3 and the softer core 4. The metallic foil 5 is embedded in the profile structure with its metal side facing upwards towards the visible surface. Rib-like elevations 31 are indicated lengthwise on the visible hard side wall 3, which serve to anchor the profile in the joint mortar. The same rib-like elevations 31 can also be arranged on the outside of the hard side wall 2. The tile joint profile 1 has a height that corresponds to the height of the tiles used. In this way, the tile joint profile 1 is flush with the tile level when in use.
- SchutzansprQche -- Protection claims -
Claims (5)