DE7720966U1 - Foam strips - Google Patents

Foam strips

Info

Publication number
DE7720966U1
DE7720966U1 DE7720966U DE7720966U DE7720966U1 DE 7720966 U1 DE7720966 U1 DE 7720966U1 DE 7720966 U DE7720966 U DE 7720966U DE 7720966 U DE7720966 U DE 7720966U DE 7720966 U1 DE7720966 U1 DE 7720966U1
Authority
DE
Germany
Prior art keywords
foam
foam strips
adhesive
viscoelastic material
foam strip
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE7720966U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel Teroson GmbH
Original Assignee
Henkel Teroson GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel Teroson GmbH filed Critical Henkel Teroson GmbH
Priority to DE7720966U priority Critical patent/DE7720966U1/en
Publication of DE7720966U1 publication Critical patent/DE7720966U1/en
Priority to NL7807187A priority patent/NL7807187A/en
Priority to GB7828797A priority patent/GB2011803B/en
Priority to FR7820059A priority patent/FR2396648A1/en
Expired legal-status Critical Current

Description

— '3 — * *- '3 - * *

Es ist häufig aus schwingungstechnischen Gründen notwendig, zwei benachbarte Bleche einer Baugruppe durch eine flexible Zwischenlage dämpfend und/oder dämmend gegeneinander zu isolieren, wozu bisher in großem Umfang plastische oder elastische Klebemassen bzw. Klebekitte eingesetzt wurden, die zu den beiden Flächen Kontakt hatten, so daß sich häufig beim Aushärten des Klebers oder des Kitts infolge Schrumpfung Kontaktverluste im Bereich der Flächen ergaben, was zu verminderten Klebeergebnissen und damit unbefriedigenden Dämmungs- und Dämpfungsergebnissen führte.It is often necessary for reasons of vibration, to isolate two adjacent sheets of an assembly from each other in a damping and / or insulating manner using a flexible intermediate layer, for which purpose plastic or elastic adhesives or adhesive putty have been used to a large extent up to now the two surfaces had contact, so that often when the adhesive or cement hardens as a result of shrinkage Loss of contact in the area of the surfaces resulted in reduced adhesive results and thus unsatisfactory insulation and damping results.

Ferner wurden zu diesem Zweck unvulkanisiarte Gummistreifen verwendet, die wegen ihrer hohen Elastizität nach der Vulkanisation, etwa infolge eines Ofendurchlaufs, einen so geringen Verlustmodul aufweisen, daß selbst bei vollständiger beidseitiger Anlage an den zu dämpfenden Flächen oder Bereichen nur eine verhältnismäßig schlechte Dämpfung zu erzielen war.Furthermore, unvulcanized rubber strips were used for this purpose, which because of their high elasticity after vulcanization, as a result of a furnace run, for example, have such a low loss modulus that even with complete If the surfaces or areas to be damped were placed on both sides, only a relatively poor damping could be achieved.

Es ist daher Aufgabe der Erfindung, einen Schaumstoffstreifen, insbesondere zur Verwendung als dämpfende Zwischenlage im Karosseriebau, zu schaffen, der sich fest an die beiden Flächen anlegt und darüber hinaus einen hohen Verlustmodul, insbesondere im interessierenden Frequenzbereich von 100 Hz bis 1000 Hz hat.It is therefore the object of the invention to provide a foam strip, in particular for use as a damping intermediate layer in bodywork, to create, which is firmly attached to the two surfaces applies and also a high loss modulus, especially in the frequency range of interest from 100 Hz to 1000 Hz.

Zur Lösung dieser Aufgabe dient ein Schaumstoffstreifen, der sich durch eine Tränkung mit viskoelastischem Material aus-A foam strip is used to solve this problem characterized by impregnation with viscoelastic material

7720966 13.10.777720966 10/13/77

zeichnet, durch das der Schaumstoffstreifen in einem komprimierten Zustand gehalten ist.draws, through which the foam strip in a compressed State is maintained.

Der erfindungsgemäße Schaumstoffstreifen befindet sich somit normalerweise in einem komprimierten Zustand, und eine Ausdehnung auf sein Ausgangsvolumen wird in üblichen Temperaturbereichen durch die Haftwirkung der Tränkung aus viskoelastischem Material verhindert. Wird ein derartiger Streifen beispielsweise im Karosseriebau eingesetzt und etwa zwischen einen Spriegel und das Karosseriedach gelegt, so wird sich dieser Streifen bei entsprechender Erwärmung, etwa der zum Aushärten des Lackes erfolgenden Erwärmung, ausdehnen, da das viskoelastische Material bei einer Temperatur über 900C seine Viskosität erheblich verringert und somit den Schaumstoff streifen nicht mehr im komprimierten Zustand hält. Der Schaumstoffstreifen kann sich daher ausdehnen und fest an den Spriegel und das Karosseriedach anlegen, d.h. er wird in diesem Bereich eingeklemmt, so daß eine zuverlässige Anlage an beiden Flächen und eine schwingungstechnisch wichtige Vorspannung erreicht wird.The foam strip according to the invention is thus normally in a compressed state, and expansion to its initial volume is prevented in normal temperature ranges by the adhesive effect of the impregnation made of viscoelastic material. If such a strip is used, for example, in the body shop and placed between a bow and the body roof, then this strip will expand with appropriate heating, such as the heating that takes place to cure the paint, since the viscoelastic material is at a temperature above 90 ° C The viscosity is considerably reduced and the foam strip no longer holds it in a compressed state. The foam strip can therefore expand and lay firmly on the bow and the body roof, ie it is clamped in this area, so that a reliable contact on both surfaces and a pre-tensioning which is important in terms of vibration is achieved.

Nach dem Abkühlen kommt das viskoelastische Material wieder in seinen ursprünglichen Viskositätszustand und kann daher die gewünschte Dämpfungswirkung entfalten.After cooling, the viscoelastic material returns to its original viscosity state and can therefore achieve the desired Develop a dampening effect.

Es ist zwar auch bereits bekannt (z.B. DT-OS 25 26 325), in mehrschichtigen, selbsttragenden Verkleidungen für Karosserie-It is already known (e.g. DT-OS 25 26 325), in multi-layer, self-supporting cladding for bodywork

7720966 13.10.777720966 10/13/77

teile eine Schicht aus komprimierten mit viskoelastischem Material getränkten Schaumstoff vorzusehen, um durch die bei Erwärmung erfolgende Ausdehnung dieses Schaumstoffs Fertigungstoleranzen auszugleichen. Diese Verkleidungen unterscheiden sich jedoch wegen ihres mehrschichtigen und selbsttragenden Aufbaus grundsätzlich vom erfindungsgemäßen Schaumstoffstreifen. share a layer of compressed with viscoelastic material Provide impregnated foam in order to compensate for manufacturing tolerances due to the expansion of this foam that takes place when heated. These disguises differ however, because of their multi-layer and self-supporting structure, they basically differ from the foam strips according to the invention.

In diesem Zusammenhang sei darauf hingewiesen, daß die Eigenschaften von sogenannten viskoelastischen Materialien allgemein bekannt sind und daher nicht näher erläutert zu werden brauchen, ι Ganz allgemein kann gesagt werden, daß viskoelastische Materia-In this context it should be noted that the properties are generally known of so-called viscoelastic materials and therefore do not need to be explained in more detail, ι In general, it can be said that viscoelastic materials

lien in einem für sie charakteristischen Temperaturbereich durch einen hohen Verlustmodul eine besonders gute Dämpfungswirkung für einen für sie charakteristischen Frequenzbereich entfalten,They have a particularly good damping effect in a temperature range that is characteristic for them due to a high loss modulus unfold for a frequency range that is characteristic of them,

und daß es ohne weiteres möglich ist, durch entsprechende Mischungen verschiedener viskoelastischer Materialien die gewünschten Temperaturbereiche und die gewünschten Frequenzbereiche sowie durch Variation der Tränkungen die gewünschte Dämpfungshöhe einzustellen.and that it is easily possible through appropriate mixtures different viscoelastic materials the desired temperature ranges and the desired frequency ranges as well as adjusting the desired level of damping by varying the impregnations.

l'i j Zur Tränkung der Schaumstoffstreifen können elastoplastische l'i j To impregnate the foam strips, elastoplastic

f; Kunststoffe, insbesondere Harze, Wachse und/oder Bitumen alf; Plastics, in particular resins, waxes and / or bitumen al

* lein oder in Mischungen verwendet werden.* Can be used alone or in mixtures.

Um bei der Montage ein sicheres Positionieren des Schaumstoffstreifens zu ermöglichen, der vor der Ausdehnung unter Umstän-To ensure safe positioning of the foam strip during assembly to enable, under certain circumstances, the

7720966 13.10.777720966 10/13/77

■ I ■■ I ■

ι 1 ■ I . · — » ·ι 1 ■ I. · - »·

— D —- D -

den nicht ausreichend zwischen den beiden Flächen eingeklemmt wird, ist vorzugsweise eine Fläche des SchaumstoffStreifens mit einem Klebstoff beschichtet, etwa einem mit einer schützenden Papierschicht abgedeckten Selbstkleber. Eine weiter verbesserte Haftung an den Flächen rlach dem Ausdehnen des Schaumstoff Streifens läßt sich erreichen, wenn beide entsprechenden Flächen des SchaumstoffStreifens mit einem Klebstoff beschichtet sind. Die erst nach Ausdehnung des SchaumstoffStreifens zur Anlage kommende Fläche kann beispielsweise ebenfalls mit einem Selbstkleber oder mit einem wärmeaktivierbaren Schmelzkleber beschichtet sein.not wedged enough between the two surfaces is preferably one face of the foam strip with coated with an adhesive, such as a self-adhesive covered with a protective paper layer. Another improved one Adhesion to the surfaces after expansion of the foam strip can be achieved if both corresponding surfaces of the foam strip are coated with an adhesive. The surface that comes into contact only after the expansion of the foam strip can, for example, also be coated with a self-adhesive or coated with a heat-activated hot melt adhesive.

In der Figur ist ein Schaumstoffstreifen dargestellt, der mit einem viskoelastischen Material getränkt ist und der sich im komprimierten Zustand befindet. Die Menge an TränkmaterialIn the figure, a foam strip is shown with is soaked in a viscoelastic material and which is in the compressed state. The amount of impregnation material

2 kann je nach Anwendungszweck beispielsweise zwischen 500 g/m2 can be between 500 g / m 2, for example, depending on the application

und 4000 g/m - bezogen auf 10 mm Dicke - liegen.and 4000 g / m - based on a thickness of 10 mm.

Die Materialstärke des komprimierten SchaumstoffStreifens liegt beispielsweise zwischen 1 mm und 5 mm, und diese Materialstärke kann sich beim Ausdehnen beispielsweise um etwa das 6-fache vergrößern, also im ausgedehnten Zustand 6 mm bis 30 mm betragen.The material thickness of the compressed foam strip is for example between 1 mm and 5 mm, and this material thickness can increase by about 6 times when expanding, for example, that is, in the expanded state, be 6 mm to 30 mm.

Es ist ohne weiteres klar, daß der Schaumstoffstreifen im allgemeinen nur in einer Richtung komprimiert wird, doch ist es auch möglich, für bestimmte Anwendungszwecke den Schaumstoffstreifen in zwei quer zur Längserstreckung verlaufenden Richtungen zu komprimieren.It is readily apparent that the foam strip in general is only compressed in one direction, but it is also possible for certain applications to use the foam strips to compress in two directions running transversely to the longitudinal extension.

7720966 13.10.777720966 10/13/77

Claims (4)

S .■? " . ',,' ,äU"EX'K.ÜL!L A StOLbERG PATENTANWÄLTE 2 HAMBURG 52 BESELEPSTRASSE 4 DR, J,-D, FRHR, von UEXKÜLC"» ' DR. ULRICH GRAF STOLBERG DIFL.-ING. JÜRGEN SUCHANTKE Terson GmbH ■ (13807) Hans-Bunte-Straße 4 Heidelberg 1 Hamburg, den 4. Juli 1977 Schaumstoffstreifen SchutzansprücheP. ■? ". ',,', äU" EX'K.ÜL! LA StOLbERG PATENTANWÄLTE 2 HAMBURG 52 BESELEPSTRASSE 4 DR, J, -D, FRHR, from UEXKÜLC "» 'DR. ULRICH GRAF STOLBERG DIFL.-ING. JÜRGEN SUCHANTKE Terson GmbH ■ (13807) Hans-Bunte-Strasse 4 Heidelberg 1 Hamburg, July 4, 1977 Foam strips protection claims 1. Schaumstoffstreifen, insbesondere zur Verwendung als dämpfende Zwischenlage im Karosseriebau, gekennzeichnet durch eine Tränkung mit viskoelastischem Material, durch das der Schaumstoffstreifen in einem komprimierten Zustand gehalten ist.1. Foam strips, especially for use as Damping intermediate layer in the body shop, characterized by an impregnation with viscoelastic material that the foam strip is kept in a compressed state. 2. Schaumstoffstreifen nach Anspruch 1, dadurch gekennzeichnet, daß das viskoelastische Material.aus elastoplastischen Kunststoffen, Harzen, Wachsen und/oder ^-· Bitumen besteht.2. Foam strips according to claim 1, characterized in that that the viscoelastic material. made of elastoplastic plastics, resins, waxes and / or ^ - · Bitumen. 7720966 13.10.777720966 10/13/77 > 1 I ί · f ·> 1 I ί f I I I * ·I I I * IJI I I- ·) _ ·IJI II - ) _ 3. Schaumstoffstreifen nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß mindestens eine Fläche mit einem Klebstoff beschichtet ist.3. Foam strips according to claim 1 or 2, characterized in that at least one surface is coated with an adhesive. 7720966 13.10.777720966 10/13/77
DE7720966U 1977-07-05 1977-07-05 Foam strips Expired DE7720966U1 (en)