DE7204571U - FAST DRYERS FOR EXTRUDED CERAMIC MOLDINGS - Google Patents
FAST DRYERS FOR EXTRUDED CERAMIC MOLDINGSInfo
- Publication number
- DE7204571U DE7204571U DE7204571U DE7204571U DE7204571U DE 7204571 U DE7204571 U DE 7204571U DE 7204571 U DE7204571 U DE 7204571U DE 7204571 U DE7204571 U DE 7204571U DE 7204571 U DE7204571 U DE 7204571U
- Authority
- DE
- Germany
- Prior art keywords
- ceramic
- dryer
- drying
- dryers
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
233-18.298H-HdHp(6) 12. 3. 7β233-18.298H-HdHp ( 6 ) 12.37β
!^ Schnelltrockner für stranggepreßte keramLsche Formlinge ";! ^ Rapid dryer for extruded ceramic bricks ";
Die Neuerung bezieht sich auf einen Schnelltrockner für stranggepreßte keramische Formlinge, insbesondere Ziegel, Dränrohre, Kanalröhre u. dgl. .The innovation relates to a rapid dryer for extruded ceramic moldings, in particular Bricks, drainage pipes, sewer pipes and the like.
In der DT-AS 1 ^59 37^4 ist ein Verfahren beschrieben, nach dem die Verfestigung und Vortrocknung keramischer Formlinge, d. h. aus einer im plastischen Zustand mittels einer Strangpresse verpreßten keramischen Masse erzeugter Halbprodukte durchgeführt werden, indem die Masse durch einen Heizraum geführt wird, um darin elektrisch mit Joule'scher Wärme beim Durchgang elektrischen Stromes durch die keramische Masse auf ^O bis 90 °C erwärmt zu werden. Kurz nach dem Austritt der so erwärmten Masse aus der Strangpresse erfolgt durch Verdampfen eines Teils der Feuchtigkeit ein Verfestigungsprozeß gewöhnlich in der freien Luft, und die stranggepreßte Masse wird in den sogenannten lederhaften Zustand gebracht (sie verliert 2 bis 3 % des Feuchtigkeitsgehalts) und kann ohne Deformation weiter verarbeitet, d. h. ge-In DT-AS 1 ^ 59 37 ^ 4 a process is described according to which the solidification and pre-drying of ceramic moldings, ie semi-products produced from a ceramic mass pressed in the plastic state by means of an extruder, are carried out by passing the mass through a heating room in order to be heated electrically with Joule heat when electric current passes through the ceramic mass to ^ 0 to 90 ° C. Shortly after the thus heated mass emerges from the extruder, a solidification process usually takes place in the open air due to evaporation of part of the moisture, and the extruded mass is brought into what is known as the leathery state (it loses 2 to 3 % of its moisture content) and can without Deformation processed further, i.e.
Λ AIS ΠΑ Λ AIS ΠΑ
schnitten oder spanabhebend bearbeitet werden. Durch die Verfestigung ist jedoch die stranggepreßte keramische Masse noch nicht vollkommen trocken, und das Nachtrocknen der verformten Masse wird gemäß dem bekannten Stand der Technik durch Konvektionstrocknuns in einem gesonderten Warmluftkammertrockner durchgeführt führt. Mit Rücksicht auf die Empfindlichkeit dercuts or machined. Due to the solidification, however, the extruded ceramic The mass is not yet completely dry, and the post-drying of the deformed mass is carried out according to the known State of the art carried out by convection drying in a separate hot air chamber dryer leads. With regard to the sensitivity of the
' Keramik gegen das Trocknungsverfahren muß das Trock'Ceramic against the drying process must be the dry
nen sehr vorsichtig und langsam durchgeführt werden. Wenn das beste Trocknungsverfahren vorgeschlagen werden soll, muß die Theorie der Rißbildung als Folge von Spannungen beim ungleichmäßigen Trocknen in Betracht gezogen werden. Beim Trocknen trocknet und schrumpft die keramische Masse hauptsächlich an der Oberfläche, während sie im Inneren feucht und weniger geschrumpft bleibt. Dadurch entsteht eine übermäßige Oberflächenspannung, die Risse in den keramischen Produkten verursacht. Um dies zu verhüten, müssen die keramischen Formlinge sehr langsam getrocknet werden. Ein solches Trocknungsverfahren ist jedoch sehr langwierig und dauert mehrere Stunden und sogar einige Tage, so daß eine Automatisierung des Produktiontsprozesses und eine Fließbandfertigung völlig ausgeschlossen sind.must be carried out very carefully and slowly. When suggesting the best drying method should take into account the theory of cracking as a result of stresses during uneven drying to be pulled. When drying, the ceramic mass dries and shrinks mainly on the surface, while inside it remains moist and less shrunken. This creates excessive surface tension, which causes cracks in the ceramic products. To prevent this, the ceramic Moldings are dried very slowly. However, such a drying process is very tedious and tedious takes several hours and even several days, so that an automation of the production process and assembly line production are completely excluded.
e ine Andererseits sind ein Verfahren und,EinrichtungOn the other hand, there is a procedure and, facility
zum Trocknen von insbesondere flachen keramischen Gegenständen, wie Kacheln, Tellern u. dgl. bekannt (DT-AS 686), womit die gepreßten Gegenstände in nochfor drying flat ceramic objects in particular, such as tiles, plates and the like known (DT-AS 686), with which the pressed objects in still
völlig kaltem Zustand einem Heißp-.as-Wärmeschock von etwa JiOO C ausgesetzt werden, Eine solche Behandluni kann man nur bei dünnwandigen Erzeugnissen anwenden.completely cold to a hot gas thermal shock of to be exposed to about 300 C. Such treatment can only be used with thin-walled products.
7204571 oi.07.767204571 oi.07.76
Vi :■■Vi: ■■
da sie bei dickwandigen Formungen, auf deren Trocknung sich die Neuerung bezieht, zu starker Rißbildung führt und daher unbrauchbar ist.because they have to dry out thick-walled moldings the innovation relates, leads to severe cracking and is therefore unusable.
Der Neuerung.liegt die Aufgabe zugrunde, den eingangs genannten Schnelltrockner 30 auszugestalten, daß die Trocknungszeit der keramischen Formlinge wesentlich, nämlich auf einige Stunden oder sogar Minuten, ohne Rißbildung und Verschlechterung ihrer mechanischen oder anderen Eigenschaften verkürzt, der Raumbedarf für die gesamte Trocknung verkleinert und die Automatisierung des gesamten Produktionsprozesses, insbesondere des Sohnelltrockners ermöglicht werden.The innovation. Is based on the task, the initially to design said rapid dryer 30 that the The drying time of the ceramic bricks is essential, namely to a few hours or even minutes without Cracking and deterioration of their mechanical or other properties shortens the space required for the the entire drying process and the automation of the entire production process, especially the Sonell dryers are made possible.
Diese Aufgabe wird neuerungsgemäß gelöst durchThis object is achieved according to the invention by
ein Heißluftzuführrohr und ein HeißluftabfUhrrohr. ■a hot air supply pipe and a hot air discharge pipe. ■
Das Trocknungsgas, z. B. Heißluft wird in den Schnelltrockner zweckmäßig mit einer Temperatur von 60 bis 250 0C eingeführt.The drying gas, e.g. B. hot air is introduced into the flash dryer advantageously with a temperature of 60 to 250 0 C.
Es ist absolut notwendig, daß die den Heizraum der Strangpresse verlassenden stranp,gepreßten Formlinge auf eine Temperatur im Bereich von '40 bis 90 0C, also genügend elektrisch erwärmt werden. Ferner ist es notwendig, daß die stranggepreßte Masse unmittelbar nach dem AustrittIt is absolutely necessary that the heating of the extruder exiting stranp, the pressed moldings are thus sufficiently electrically heated to a temperature in the range from '40 to 90 0 C. It is also necessary that the extruded mass immediately after the exit
7204571 01.07.767204571 07/01/76
aus dem Heizraum der Strangpresse vorzugsweise in einem Zeitabschnitt von einigen zehn Sekunden in einzelne Stücke zerschnitten wird und daß die zerschnittenen Formlingsstucke gleich nach dem Zerschneiden in den Trockner gebracht und dort dem Trocknungsprozeß durch ein heißes Gas, z. B. auf 60 bis 250 °C erwärmte Heißluft und bei manchen Produktionen sogar auf eine höhere Temperatur erhitztes Gas, ausgesetzt werden. Die Temperatur des Trocknungsgases wird in dem oben erwähnten Temperaturbereich nach den Eigenschaften der zu verarbeitenden keramischen Masse, nach der Erzeugnisform und nach der Temperatur der vorhergenenden Erwärmung in dem Heizraum der Strangpresse gewählt. from the heating room of the extruder into individual pieces, preferably in a period of a few tens of seconds is cut and that the cut pieces of briquettes are brought into the dryer immediately after cutting and there the drying process by a hot gas, e.g. B. heated to 60 to 250 ° C hot air and some Productions can even be exposed to gas heated to a higher temperature. The temperature of the drying gas is in the above-mentioned temperature range according to the properties of the ceramic mass to be processed, the shape of the product and the temperature of the previous one Heating in the boiler room of the extruder is selected.
Wenn die erwärmten Bedingungen erfüllt werden, haben die fertigen Keramikerzeugnisse sogar bessere mechanische Eigenschaften, besonders eine bessere mechanische Festigkeit als diejenigen Produkte, die langsam in freier Luft getrocknet oder in einem gewöhnlichen Trocknungsprozeß behandelt werden, was im Vergleich mit den bisherigen Er- Γ~\ kenntnissen als sehr überraschend anzusehen ist. AußerdemWhen the heated conditions are met to have the final ceramic products even better mechanical properties, especially a better mechanical strength than those products which are treated slowly in the open air dried or in a conventional drying process, which, in comparison with the previous ER Γ ~ \ knowledge is to be regarded as very surprising. aside from that
ermöglicht die Neuerung eine wesentliche Verkürzung der Nachtrocknungszeit, verkleinert die Ausschußquote und ermöglicht eine volle Automatisierung und einen Fließbandbetrieb des ganzen Produktionsprozesses.The innovation enables a significant reduction in the post-drying time, reduces the reject rate and enables full automation and assembly line operation of the entire production process.
Der neuerungsgemäße Schnelltrockner findet Anwendung bei der Herstellung stranggspreßter Produkte, welche nur von einem zusammenhängenden Massestrang abgeschnitten werden, eine Endform bereits besitzen und weiter nicht mehr geformt zu werden brauchen, wie z. B. Ziegel, Dränrohre, Kanalrühre usw.The rapid dryer according to the innovation is used at the manufacture of extruded products, which only from be cut from a coherent mass strand, already have a final shape and no longer formed need to become such. B. bricks, drainage pipes, sewer pipes, etc.
Die Neuerung soll nun anhand eines in der Zeichnung dargestellten Ausführungsbeispiels n'iher erläutert werden.The innovation will now be explained in more detail using an exemplary embodiment shown in the drawing.
7204571 01.07.767204571 07/01/76
Die einzige Figur zeigt eine Einrichtung mit dem neuerungsgemäßen Schnalltrockner für keramische Formlinge,The only figure shows a device with the buckle dryer according to the innovation for ceramic briquettes,
Die Einrichtung besteht aus einer bekannten Strangpresse 1 mit einem Heizraum 2, der eine elektrische Erwärmung der stranggepreßten keramischen Masse ermöglicht. Beim Verlassen des Mundstücks 4 der Strangpresse 1 wird die stranggepreßte keramische Masse 3 durch einen Abschneider 6, der in der Figur nur durch ein Messer dargestellt ist, in einzelne Formlingsstücke 5 zerschnitten. Die stranggepreßte Masse 3 wird beim Zerschneiden durch einen Hilfstisch 7 unterstützt. Die zerschnittenen Formlingsstücke 5 werden durch einen Bandförderer 8 in einen Schnelltrockner 9 transportiert, welcher ein Zuführrohr 10 und ein Abführrohr 11 erwärmten Trocknungsgases aufweist. Die getrockneten Formlinge 12 verlassen nachher den Schnelltrockner und werden auf einen Austrittstisch 13 gebracht, von wo sie direkt auf Ofenwagen verladen werden, um zum Brand in einem Brennofen gebracht zu werden.The device consists of a known extrusion press 1 with a heating room 2, which provides electrical heating the extruded ceramic mass allows. When leaving the mouthpiece 4 of the extruder 1, the extruded ceramic mass 3 by a cutter 6, which is shown in the figure only by a knife, in individual molded pieces 5 cut up. The extruded mass 3 is cut by an auxiliary table 7 supports. The cut pieces of molding 5 are conveyed to a high-speed dryer 9 by a belt conveyor 8 transported, which has a supply pipe 10 and a discharge pipe 11 heated drying gas. The dried ones Moldings 12 then leave the high-speed dryer and are brought onto an exit table 13, from where they are loaded directly onto kiln cars to be burned in a kiln.
Zusätzlich kann ein Infrarottrockner vorgesehen sein.In addition, an infrared dryer can be provided.
Die Konstruktion des Schnelltrockners ist nicht sehr wichtig. Es ist vorteilhaft, Schnell- oder Kammertrockner mit Gleich-, Gegen-, gemischter Strömung oder mit einer anderen Art von Strömung zu verwenden. Es ist jedoch wichtig, daß die zerschnittenen Formlinge auf eine Temperatur vonThe construction of the flash dryer is not very important. It is advantageous to use a rapid or chamber dryer Same, counter, mixed flow or with another Kind of flow to use. However, it is important that the cut moldings to a temperature of
o Schnell
mindestens 35 C in den trockner gebracht werden, weshalb der
Schnelltrockner direkt mit der übrigen Einrichtung versehen
und direkt anschließend an den Abschneider an^eordnet
sein muß. o Fast
at least 35 C must be brought into the dryer, which is why the rapid dryer must be provided directly with the rest of the equipment and placed directly next to the cutter.
7204571 01.07.767204571 07/01/76
Claims (1)