DE696913C - Process for the production of molded bodies from hardenable synthetic resin o. - Google Patents

Description

Verfahren. zum Herstellen von Preßkörpern aus härtbarem Kunstharz o. dgl.Procedure. for the production of compacts from hardenable synthetic resin or the like

Preßkörper aus Kunstharz 0. dgl. stellte man bisher in der Regel zwischen zwei beheizten Preßplatten unter äußerer Einwirkung von Druck und Hitze her. Da Kunstharz ein schlechter Wärmeleiter ist, war es bisher nicht möglich, Preßkörper von größerer Dicke herzustellen, da sonst ein gutes und gleichmäßiges Durchbakelisieren nicht gewährleistet war. Pressed bodies made of synthetic resin 0 between two heated press plates under the external action of pressure and heat here. Since synthetic resin is a poor conductor of heat, it was previously not possible to use molded bodies of greater thickness, otherwise a good and even bakelization was not guaranteed.

Außerdem beanspruchte das Herstellen stärkerer Preßkörper sehr viel Zeit.In addition, making stronger compacts was very demanding Time.

Es ist ferner bekannt, in die Kunstharzmasse elektrisch geheizte Drähte einzubetten. It is also known to be electrically heated in the synthetic resin compound Embed wires.

Bei diesem Verfahren fand eine äußere Hitze-und Druckeinwirkung nicht statt. Man stellte mit diesem Verfahren in der Hauptsache geformte Preßkörper von geringer Wandstärke her, um die teuren Preßformen zu sparen.No external exposure to heat or pressure occurred during this process instead of. This process produced mainly molded compacts from low wall thickness in order to save the expensive molds.

Da die elektrisch beheizten Drähte nur unregelmäßig in der Kunstharzmasse verteilt waren, so war das Durchbakelisieren ebenfalls ungleichmäßig, so daß die Preßkörper kein gleichmäßiges Gefüge hatten. Außerdem bestand die Gefahr von Lunkerbildungen.Because the electrically heated wires only irregularly in the synthetic resin compound were distributed, the bakelishing was also uneven, so that the Pressed bodies did not have a uniform structure. There was also the risk of cavities being formed.

Durch die Erfindung wird es ermöglicht, Preßkörper von jeder beliebigen Stärke innerhalb kurzer Zeit herzustellen, wobei ein gutes und gleichmäßiges Durchbakelisieren des gesamten Preßkörpers gewährleistet ist. Dies wird dadurch erreicht, daß beim Aufbau des Preßkörpers die mit durchgehenden Stromleitern versehenen Gewleb,ebahnen unter Hinzufügen des zu härtenden Bindemittels in der Breite des Preßkörpers übereinandergefaltet und die Stromleiter nach Freilegen ihrer Enden an Stromkreise angeschlossen werden. The invention makes it possible to produce pressed bodies of any desired Produce strength within a short time, with a good and even bakelization of the entire pressed body is guaranteed. This is achieved in that the Structure of the pressed body, the fabric webs provided with continuous current conductors folded over one another in the width of the compact with the addition of the binder to be hardened and the conductors are connected to circuits after exposing their ends.

Die Härtung erfolgt zwischen Preßplatten, die gegebenenfalls beheizt werden. Dadurch, daß die Stromleiter in den Gewebebahnen liegen, die zur Herstellung des Preßkörpers übereinandergefaltet werden, gelingt - es, die Drähte vollkommen gleichmäßig über die ganze Länge 1 und Breite des Preßkörpers zu verteilen, so daß in allen Punkten des Preßkörpers eine gleichmäßige Wärmeentwicklung mit dem Er folg eines gleichmäßigen Durchbalçelisieren949 erzielt wird. So können sowohl die Kettfädü% als auch die Schußfäden der GewebZebahn~ mit Stromleitern versehen sein, so daß selbst bei Ausfall einiger Stromleiter eine gleichmäßige Durchhitzung erreicht wird. Die Drähte selbst erhöhen in dem fertig;gestellten Preßkörper in bekannter Weise seine Festigkeit. Eine gleichmäßige Durchhitzung des Preßkörpers wird in gleicher Weise dadurch gefördert, daß man zwei mit 90° gegeneinander versetzte Gewebebahnen abwlechselnd üb ereinanderfaltet.The hardening takes place between press plates, which are optionally heated will. The fact that the current conductors lie in the webs of fabric that are used for production of the pressed body are folded over, succeeds - the wires completely to distribute evenly over the entire length 1 and width of the pressed body, so that in all points of the compact a uniform heat development with the success even balancing949 is achieved. So both the warp threads as well as the weft threads of the GewebZebahn ~ be provided with conductors so that Even if some conductors fail, even heating is achieved. The wires themselves increase in the finished pressed body in a known manner its firmness. A uniform through-heating of the pressed body is in the same Way promoted by having two webs of fabric offset from one another at 90 ° alternately folded over one another.

Auf der Zeichnung ist - die Erfindung dargestellt. In the drawing - the invention is shown.

Abb. I und 2 zeigen in Seitenansicht und Draufsicht ein quaderförmiges Werkstück A. Fig. I and 2 show a cuboid in side view and top view Workpiece A.

Abb. 3 ist ein Querschnitt in vergrößertem Maßstab durch mehrere Schichten, die aus zwei kreuzweise und abwechselnd übereinandergelegten Gewebebahnen gebildet sind. Fig. 3 is a cross-section through several on an enlarged scale Layers consisting of two crosswise and alternately superimposed webs of fabric are formed.

Abb. 4 zeigt einen Querschnitt durch eine dieser beiden Gewebebahnen in vergrößertem Maßstab. Fig. 4 shows a cross section through one of these two fabric webs on a larger scale.

Abb. 5 zeigt in kleinerem Maßstab inDraufsicht das eine Ende einer solchen Gewebebahn. Fig. 5 shows, on a smaller scale, a plan view of one end of a such web of fabric.

Das quaderförmige Werkstück I nach Abb. I und 2 ist dadurch entstanden, daß man zwei Gewebebahnen um go0 gegeneinander versetzt abwechselnd übereinandergefaltet hat. Man kann nun einer jeden Gewebebahn leine solche Länge geben, daß man aus ihr ein Werkstück von der gewünschten Höhe herstellen kann. The cuboid workpiece I according to Fig. I and 2 was created by that one folds two strips of fabric alternately on top of one another, offset from one another by go0 Has. One can now give a length of line to each fabric web so that one can get out of it can produce a workpiece of the desired height.

Will man den Preßkörper nur unmittelbar elektrisch beheizen, ist es in diesem Falle lediglich notwendig, die beiden Enden der GFewebebahnFen aus dem Werkstück etwas berausstehen zu lassen, die Drähte 2 von der Umspinnung freizumachen und an Stromzuführungsschienen 3 oder andere Stromzuführungsvorrichtungen anzuschließen. Man kann nun auf der Höhe eines solchen Preßkörpers mehrere solcher Anschlußstellen 2' vorsehen.If you only want to heat the pressed body directly electrically, it is in this case it is only necessary to remove the two ends of the GFewebebahnFen from the To let the workpiece protrude somewhat, to free the wires 2 from the wrapping and to be connected to power supply rails 3 or other power supply devices. You can now at the level of such a pressed body several such connection points 2 '.

Das empfiehlt sich beispieisweise für den Fall, wo man mit beheizten Freßpiatten ableitet, so daß man die äußeren Abschnitte nicht unmittelbar elektrisch zu beheizen braucht. Diese Anschlüsse 2' kann man dadurch erreichten, daß man bei einer durchgehenden Gewebrebahn die entsprechenden Lagen etwas nach der Seite herauszieht und aufschneidet oder mehrere aufeinanderfeigende Geweblebahnen nimmt, deren Enden man jeweils herausstehen läßt. Die Abb. 2 zeigt, daß zwei um 900 gegeneinander versetzte Geweblebahnen verwendet worden sind, wobei die Enden der Drähte einer jeden Gewebebahn unter sich elektrisch verbunden und bei N an Netzstromkreise angeschlossen sind.This is recommended, for example, in the event that one is heated with Erßpiatten derives, so that the outer sections are not directly electrical needs to be heated. These connections 2 'can be reached by at a continuous web of tissue pulls the corresponding layers out slightly to the side and cuts open or takes several webs of fabric that are slipped onto each other, the ends of which you let each stick out. Fig. 2 shows that two are offset by 900 against each other Fabric panels have been used, with the ends of the wires of each fabric panel are electrically connected to each other and connected to mains circuits at N.

Bei der bisherigen Beheizung mit beheizten .trSeßPlatten ergab sich der Nachteil, daß die ;.s#itenfiächen des Preßkörpers bis zu einer nicht unerheblichen Tiefe nicht genügend beheizt wurden, so daß diese Teile nicht oder ungenügend durchbakelisierten. Dieses wird durch die Erfindung dadurch vermieden, daß man die an den Seiten des Preßkörpers liegenden Stromkreise stärker beheizt als die in der Mitte liegenden. Zu diesem Zweck faßt man die an den Seitenflächen liegenden Stromleiter unter sich elektrisch zusammen und führt ihnen eine höhere Spannung zu oder bemißt ihren Widerstand geringer.The previous heating with heated .trSeß plates resulted the disadvantage that the; .s # itenfiflächen the pressed body up to a not insignificant Depth were not heated sufficiently, so that these parts were not or insufficiently bakelized. This is avoided by the invention that one on the sides of the Circuits lying in the pressed body are more heated than those in the middle. For this purpose, the current conductors lying on the side surfaces are grasped under them electrically together and supplies them with a higher voltage or measures their resistance less.

3' sind die Stromschienen, die die äußeren Leiter der beiden Gewebebahnen zusammenfassen und an einen besonderen Netzstromkreis N' angeschlossen sind. Die Stromschienen 3 und 3' sind natürlich - gegeneinander isoliert. 3 'are the busbars, which are the outer conductors of the two webs of fabric summarize and are connected to a special network circuit N '. the Busbars 3 and 3 'are of course - insulated from one another.

Zur Beheizung mit Induktionsstrom verbindet man in bekannter Weise die Enden der Drähte einer jeden Gewebebahn mitreinander, wie mit strichpunktierten Linien! angedeutet ist, so daß im Innern des Preßkörpers geschlossene Spulen, Sekundärspuien, gebildet werden. Zur stärkeren Beheizung der Seitenflächen kann man die äußeren Stromkreise ebenfalls für sich zusammenschließen und in diese höhere Induktionsströme induzieren. For heating with induction current, one connects in a known manner the ends of the wires of each web of fabric with each other, as with dash-dotted lines Lines! is indicated, so that closed coils, secondary coils, are formed. For more intense heating of the side surfaces, you can use the outer Circuits also combine for themselves and in this higher induction currents induce.

Die Abb. 3 zeigt in vergrößertem Maßstab die Art der Schichtung. Die Gewebebahn 4 ist abwtechselnd von links nach rechts und umgekehrt geführt, während die weitere Gewebebahn 5 abwechselnd von hinten nach vorn geführt ist. Auf jede Lage der leinen Bahn folgt eine Lage der anderen Bahn. Bei diese Schichtung wird erreicht, daß die Metalldrähte, durch welche die Festigkeit des Werkstückes erhöht wird, gegeneinander versetzt liegen. Die Enden 6 einer jeden Geweebebahn sind seitlich herausgeführt. Die Bespinnung ist an den Enden entfernt, so daß die Drähte 2 der Kettfäden und die Drähte 7 der Schußfäden für den Anschluß in einen Stromkreis zur Beheizung freiliegen. Die Abb. 4 ist ein Querschnitt durch eine der Gewebebahnen 4 oder 5. 8 sind die Kettfäden, die parallel zueinander über die ganze Länge der Geveblebahnen verlaufen. g ist der Schußfaden, der die Kettfäden zu einem Gewebe verbindet. Kettfäden und Schußfäden bestehen aus einem Stromleiter 2 bzw. 7, der mit einer Bespinnung aus Faserstoff versehen ist. Dadurch werden die einzelnen Drähte gleichzeitig gegeneinander isoliert, während der Faserstoff selbst dem Werkstoff eine größere Festigkeit in bekannter Weise gibt. Fig. 3 shows the type of stratification on an enlarged scale. The fabric web 4 is alternately guided from left to right and vice versa, while the further web of fabric 5 is alternately guided from the back to the front. On every One layer of the linen web is followed by one layer of the other web. At this layering will achieved that the metal wires through which the strength of the workpiece increases are offset from each other. The ends 6 of each web of fabric are on the side led out. The spinning is removed at the ends, so that the wires 2 of the Warp threads and the wires 7 of the weft threads for connection in a circuit for Heating exposed. Fig. 4 is a cross-section through one of the fabric panels 4 or 5. 8 are the warp threads that run parallel to each other over the entire length of the Geveblebahnen run. g is the weft thread that turns the warp threads into a fabric connects. Warp threads and weft threads consist of a conductor 2 and 7, respectively is provided with a spinning made of fiber. This will separate the individual wires at the same time isolated from each other, while the fiber itself is the material one gives greater strength in a known manner.

Dadurch, daß gleichzeitig Kettfäden und Schußfäden einen Stromleiter zur Beheizung enthalten, ist es unwesentlich, wenn der eine oder andere Draht der Kette als Stromleiter ausfällt, weil gleichzeitig noch der Schußfaden zur Beheizung dient, der über die ganze Breite der Gewebebahn verläuft. Man kann selbstverständlich auch entweder nur die Kette oder nur den Schuß zur Stromleitung benutzen. Der Draht besteht vorzugsweise aus Weicheisen, weil er dadurch dem Werkstück die besten Festigkeitseigenschaften verleiht.The fact that warp threads and weft threads create a current conductor at the same time included for heating, it is immaterial if one or the other wire of the The chain as a conductor fails because at the same time the weft thread for heating serves, which runs over the entire width of the fabric web. Of course you can also use either only the chain or only the weft to the power line. The wire is preferably made of soft iron, because it gives the workpiece the best strength properties confers.

Durch Bemessung des Widerstandes der Leiter und der Stromquelle kann man die gewünschte Temperatur mit Leichtigkeit einsteilen. Die Abb. 5 zeigt in Draufsicht die Zueinanderordnung der Kett- und Schußfäden. Für die Beheizung mit Induktionsstrom ist es zweckmäßig, die Drähte der verschiedenen Gewleblebahnen nicht rechtwinklig, sondern spitzwinldig, vorzugsweise unter einem Winkel von 450, zueinander verlaufen zu lassen. In diesem Falle braucht man nur eine oder höchstens zwei Primärspulen.By measuring the resistance of the conductors and the power source, you can set the desired temperature with ease. Fig. 5 shows in plan view the relationship between the warp and weft threads. For heating with induction current it is advisable not to have the wires of the various woven webs at right angles, but rather acute-angled, preferably at an angle of 450 to each other allow. In this case you only need one or at most two primary coils.

Runde Werkstücke kann man dadurch herstellen, daß man- die Gewebebahnen in bekannter Weise rund aufwickelt. Dadurch erreicht man in gleicher Weise, daß alle übereinanderliegenden Schichten in gleichmäßigem Abstand die Stromleiter enthalten. Round workpieces can be produced by the fabric webs winds around in a known manner. This achieves in the same way that all layers lying on top of one another contain the current conductors at an even distance.

Es ist selbstverständlich nicht notwendig, daß man zur Herstellung quaderförmiger Werkstücke zwei gegeneinander vlersetzte, abwechselnd geschichtete Gewebebahnen nimmt, sondern es würde eine ziehharmonikaartig gefaltete Gewebebahn mit dem gleichen Erfolg verwendet werden können. Die kreuzweise Übereinanderschichtung zweier Gleweblebahnen hat lediglich den Zweck, zu erreichen, daß die Metalldrähte der einzelnen Schichten gegeneinander versetzt liegen, so daß das Werkstück eine größere Festigkeit erhält. It is of course not necessary to be able to manufacture cuboid workpieces two mutually stacked, alternately layered Instead it would be an accordion-like folded fabric sheet can be used with equal success. The criss-cross layering The only purpose of the two Glewebbenbahn is to achieve that the metal wires of the individual layers are offset from one another, so that the workpiece a receives greater strength.

Claims (3)

PATENTANSPRÜCHE: I. Verfahren zum Herstellen von Preß-\ körpern aus härtblarem Kunstharz o. dgl., bei dem das Härten durch ei.ektrisches Beheizen leingebtettet,er Drahteinlagen unter Druck zwischen gegebenenfalls geheizten Preßplatten erfolgt, dadurch gekennzeichnet, daß beim Aufbau des Preßkörpers die mit durchgehenden Stromleitern versehenen Gew,eblebahnen unter Hinzufügen des zu härtenden Bindemittels in der Breite des Preßkörpers üblereinandergefaltet und die Stromleiter nach Freilegen ihrer Enden am Stromkreis angeschlossen werden. PATENT CLAIMS: I. Process for producing pressed bodies from Hardenable synthetic resin or the like, in which hardening is embedded by electrical heating, he Wire inserts are made under pressure between possibly heated press plates, characterized in that during the construction of the pressed body with continuous current conductors provided Gew, eblebahnen with the addition of the binder to be hardened in the Width of the pressed body folded over and the conductors after exposure their ends are connected to the circuit. 2. Verfahren nach Anspruch I, dadurch gekennzeichnet, daß zwei um gpO gegeneinander versetzte Gewebebahnen abwechselnd übereinandergefaltet werden. 2. The method according to claim I, characterized in that two to gpO mutually offset fabric webs are alternately folded over one another. 3. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die an den Seitenflächen des Preßkörpers liegenden Stromkreise stärker beheizt werden. 3. The method according to claim 1 and 2, characterized in that the Circuits lying on the side surfaces of the pressed body are heated more intensely.