DE4308099A1 - Coating composition for walls, ceilings and floors - Google Patents

Coating composition for walls, ceilings and floors

Info

Publication number
DE4308099A1
DE4308099A1 DE19934308099 DE4308099A DE4308099A1 DE 4308099 A1 DE4308099 A1 DE 4308099A1 DE 19934308099 DE19934308099 DE 19934308099 DE 4308099 A DE4308099 A DE 4308099A DE 4308099 A1 DE4308099 A1 DE 4308099A1
Authority
DE
Germany
Prior art keywords
composition
composition according
powder
iron powder
calcium hydroxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19934308099
Other languages
German (de)
Inventor
Udo Frank Dr Windhoevel
Manfred Dr Leder
Thomas Tamcke
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel AG and Co KGaA
Original Assignee
Henkel AG and Co KGaA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel AG and Co KGaA filed Critical Henkel AG and Co KGaA
Priority to DE19934308099 priority Critical patent/DE4308099A1/en
Priority to PCT/EP1994/000714 priority patent/WO1994022151A1/en
Publication of DE4308099A1 publication Critical patent/DE4308099A1/en
Withdrawn legal-status Critical Current

Abstract

A storage-stable non-corroding composition is described for the production of coatings on which coverings can be fastened using magnets. The composition consists of a ferromagnetic compound, especially iron powder, zinc powder, and at least one of the following binders: redispersible vinyl acetate, calcium hydroxide and cement. The composition may also contain a thickener, for example bentonites. When a greater or lesser quantity of water is added, a workable mass is obtained which cures in about 24 hours under normal ambient conditions. Coverings can then be fastened to the cured mass using magnets.

Description

Die Erfindung betrifft eine Zusammensetzung zum Beschichten von Wänden, Decken und Böden, die als magnetisch wirksamen Bestandteil Eisenpulver und ein Bindemittel enthält. Auf dieser Beschichtung können leicht und einfach Beläge mit Magneten befestigt werden.The invention relates to a composition for coating Walls, ceilings and floors that act as a magnetically effective component Contains iron powder and a binder. On this coating can be easily and easily attached with magnets.

Eine derartige Zusammensetzung ist als Spachtelmasse zur Befesti­ gung von Dekorationen durch magnetische Kräfte bekannt. So wird in der DE 26 20 095 ein Verfahren zum Anbringen leicht auswechselbarer Flächendekorationen aus Stein, Keramik, Holz, Metall und derglei­ chen an Wand-, Decken- und/oder Bodenflächen aus gleichen und/oder verschiedenen Werkstoffen beschrieben. Dazu ist es notwendig, auf die eine Fläche eine mit Eisenpulver und auf die andere Fläche eine mit Magnetpulver hochgefüllte Schicht des Bindemittels aufzubringen und diese aushärten zu lassen. Nach einer Magnetisierung kann die Dekoration aufgrund der Magnetwirkung befestigt werden. Es werden Spachtelmassen aus Eisenpulver und anorganischen oder organischen Bindemitteln beschrieben. Als anorganische Bindemittel werden ge­ nannt: Gips, Feinputz und Zement. Als organische Bindemittel werden flüssige Kunststoffmassen, vorzugsweise in nicht-wäßriger Form eingesetzt, z. B. Alkydharze, Epoxidharze, Polyurethane sowie Poly­ mere auf der Basis von Vinyl- und/oder Acrylverbindungen.Such a composition is used as a filler for fastening known decorations by magnetic forces. So in DE 26 20 095 a method for attaching easily replaceable Surface decorations made of stone, ceramic, wood, metal and the like chen on wall, ceiling and / or floor surfaces made of the same and / or different materials described. For this it is necessary to one surface one with iron powder and one on the other surface apply a layer of the binder filled with magnetic powder and let it harden. After magnetization, the Decoration can be attached due to the magnetic effect. It will Leveling compounds made of iron powder and inorganic or organic Binding agents described. As inorganic binders called: plaster, fine plaster and cement. As organic binders liquid plastics, preferably in non-aqueous form used, e.g. B. alkyd resins, epoxy resins, polyurethanes and poly mers based on vinyl and / or acrylic compounds.

Die FR 2 250 394 betrifft die Verwendung eines verzinnten Teilge­ webes zum magnetischen Verbinden von beliebigen Materialien. So soll z. B. das Sieb auf ein Holzbrett bei seiner Herstellung aufgeklebt werden. Das Holzbrett kann als Zwischenwand dienen, auf die eine dekorative Verkleidung mit aufgeklebten Dauermagneten be­ festigt werden kann. Als Klebstoff wird Kautschuk genannt. Es wird auch ein Muster aus Gips beschrieben, das eine vorgefertigte Zwi­ schenwand darstellt, in die ein Magnet mit Kautschuk eingebunden wurde.FR 2 250 394 relates to the use of a tinned part webes for the magnetic connection of any materials. So should z. B. the sieve on a wooden board during its manufacture  be stuck on. The wooden board can serve as a partition on which be a decorative covering with glued permanent magnets can be consolidated. Rubber is mentioned as the adhesive. It will also described a pattern made of plaster, which a prefabricated Zwi is represented in which a magnet with rubber is integrated has been.

Die DE 40 16 939 betrifft ein Verfahren zur reversiblen Befestigung von Boden- und Wandbelägen durch magnetische Haftung. Auf magne­ tisch nicht-haftenden Untergründen soll einmalig eine magnetische Beschichtung oder eine zu verklebende oder selbstklebende Magnet­ folie aufgebracht werden.DE 40 16 939 relates to a method for reversible fastening of floor and wall coverings through magnetic adhesion. On magne non-adhesive substrates should be a magnetic one-off Coating or a magnet to be glued or self-adhesive foil are applied.

Die bekannten Zusammensetzungen für die Spachtelmassen mit Harzen und insbesondere Epoxidharzen als Bindemittel haben den Nachteil, daß sie aufgrund ihrer großen Zähigkeit schlecht zu verstreichen sind. Ein Zusatz an Lösungsmittel würde dem zwar abhelfen, würde aber andererseits auch Probleme mit der Abluft ergeben.The known compositions for fillers with resins and in particular epoxy resins as binders have the disadvantage that they are difficult to pass due to their great toughness are. Adding solvent would help, though but on the other hand there are also problems with the exhaust air.

Die erfindungsgemäße Aufgabe besteht also darin, eine leicht zu verarbeitende Zusammensetzung zu finden, die nicht nur mit dem Spachtel, sondern auch z. B. mit einer Rolle aufgetragen werden kann und einen dauerhaften Untergrund für magnetisch wirksame Beläge ergibt.The object of the invention is therefore to easily processing composition to find, not only with the Spatula, but also z. B. can be applied with a roller and a permanent base for magnetically effective coverings results.

Die erfindungsgemäße Lösung ist den Patentansprüchen zu entnehmen. Sie besteht im wesentlichen darin, daß die ferromagnetischen Verbindungen, insbesondere das Eisenpulver in Form einer wäßrigen Dispersion aufgetragen werden. Anfängliche Bedenken mit einer wäß­ rigen Dispersion zu arbeiten, da mit ihr leicht eine Entmischung aufgrund des relativ hohen spezifischen Gewichtes von Eisen verbunden ist, und dieses darüber hinaus in wäßrigem Medium beson­ ders leicht rostet, wurden überwunden.The solution according to the invention can be found in the patent claims. It essentially consists in the fact that the ferromagnetic Compounds, especially the iron powder in the form of an aqueous Dispersion can be applied. Initial concerns with an aq Dispersion to work with, as it easily separates due to the relatively high specific weight of iron  is connected, and this in particular in an aqueous medium rusted easily, were overcome.

Die erfindungsgemäße Zusammensetzung enthält neben Eisenpulver auch noch Zinkpulver, und zwar vorzugsweise in einer Menge von 5 bis 20, insbesondere 7 bis 13 Gew.-%, bezogen auf das Eisenpulver.In addition to iron powder, the composition according to the invention also contains still zinc powder, preferably in an amount of 5 to 20, in particular 7 to 13 wt .-%, based on the iron powder.

Als Bindemittel werden redispergierbare Polyvinylacetate, Calciumhydroxid und/oder Zement verwendet, und zwar vorzugsweise in einer Menge von 5 bis 20, vorzugsweise 7 bis 12 Gew.-%, bezogen auf das Eisenpulver. Unter einem redispergierbaren Polyvinylacetat wird ein Polyvinylacetat-Pulver verstanden, das nach Zugabe von Wasser bei Raumtemperatur innerhalb kurzer Zeit durch Rühren in eine wäß­ rige Dispersion überführt werden kann. Das Calciumhydroxid kann - bezogen auf seine rein chemische Formel - mehr oder weniger Wasser enthalten. Der Zement sollte vorzugsweise ein Portland-Zement sein. Die Bindemittel sollten vorzugsweise miteinander kombiniert werden. Dabei ist eine Kombination von Polyvinylacetat mit Calciumhydroxid von besonderer Bedeutung. Ihr Mengenverhältnis sollte im Bereich von 2 : 1 bis 1 : 2 liegen.Redispersible polyvinyl acetates, Calcium hydroxide and / or cement used, preferably in an amount of 5 to 20, preferably 7 to 12 wt .-%, based on the iron powder. Under a redispersible polyvinyl acetate understood a polyvinyl acetate powder that after adding water at room temperature within a short time by stirring in an aq Dispersion can be transferred. The calcium hydroxide can - based on its purely chemical formula - more or less water contain. The cement should preferably be a Portland cement. The binders should preferably be combined with one another. Here is a combination of polyvinyl acetate with calcium hydroxide really important. Your quantitative ratio should be in the range from 2: 1 to 1: 2.

Zur Viskositätsregulierung kann auch noch ein Verdickungsmittel zugesetzt werden, und zwar in einer Menge von vorzugsweise 0,2 bis 2, insbesondere 0,4 bis 1,0 Gew.-%, bezogen auf das Eisenpulver. Als Verdickungsmittel kommen vor allem anorganische Verdickungs­ mittel in Frage, wie z. B. Bentonite.A thickener can also be used to regulate the viscosity are added, preferably in an amount of 0.2 to 2, in particular 0.4 to 1.0 wt .-%, based on the iron powder. Inorganic thickeners are the main thickeners medium in question, such as B. bentonites.

Darüber hinaus können noch weitere Additive zugesetzt werden, z. B. Farbstoffe. In addition, other additives can be added, e.g. B. Dyes.  

Die obigen Komponenten liegen in Form eines Gemenges vor, d. h. sie sind innig miteinander vermischt. Vorzugsweise ist das Gemenge trocken oder pulverförmig. Es kann aber auch in hochviskoser Form vorliegen, wobei die Viskosität so hoch sein soll, daß praktisch keine Entmischung auftritt.The above components are in the form of a batch, i.e. H. she are intimately mixed. The mixture is preferred dry or powdery. But it can also be in a highly viscous form are present, the viscosity should be so high that practical no segregation occurs.

Vor Gebrauch wird Wasser zugesetzt und unter Rühren geht das Ge­ menge in eine wäßrige Dispersion über. Die Wassermenge richtet sich danach, wie viskos die Dispersion sein soll oder anders gesagt, wie man sie verarbeiten möchte, z. B. mit einer Rolle oder mit einem Spachtel.Water is added before use and the mixture goes under stirring amount in an aqueous dispersion. The amount of water depends depending on how viscous the dispersion should be or in other words how you want to process them, e.g. B. with a role or with a Spatula.

Die dünnflüssige bis pastöse Masse wird auf den zu präparierenden Untergrund aufgetragen, also vor allem auf Wände, Decken und Fuß­ böden oder sonstige Flächen, wie z. B. Platten, auf denen ein Belag magnetisch befestigt werden soll. Dort härtet die Masse aus. Dazu werden je nach den Trockenbedingungen in der Regel mindestens ei­ nige Stunden benötigt. Nach 24 Stunden ist die Beschichtung so hart, daß die Beläge darauf befestigt werden können.The thin to pasty mass is applied to the preparation Applied underground, especially on walls, ceilings and feet floors or other surfaces such as B. plates on which a covering to be attached magnetically. The mass hardens there. To are usually at least egg, depending on the drying conditions needed a few hours. After 24 hours the coating is like this hard that the pads can be attached to it.

Die erfindungsgemäß hergestellte Beschichtung zeichnet sich durch eine gute Haftung auf verschiedenen Untergründen aus, z. B. auf mineralischen Estrichen, Keramik, Holz oder Holzverbundwerkstoffen. Andererseits haften auf ihr alle Arten von Belägen mit magnetischer Wirkung, seien sie aus Keramik, Holz, Textilien, Teppichen, Pappen usw. hergestellt. Es spielt auch keine Rolle, worauf die magnetische Wirkung zurückzuführen ist, sei es auf Folien, auf Siebe oder auf Schüttgut.The coating produced according to the invention is notable for good adhesion to various substrates, e.g. B. on mineral screeds, ceramics, wood or wood composite materials. On the other hand, all types of magnetic surfaces stick to it Effect, be it from ceramics, wood, textiles, carpets, cardboards etc. manufactured. It doesn't matter what the magnetic effect is due, be it on foils, on Sieves or on bulk material.

Die Vorteile der erfindungsgemäßen Zusammensetzung liegen in ihrer Lagerstabilität, einfachen Handhabung, je nach gewünschter Ar­ beitsweise sowie guter Korrosionsbeständigkeit und Wirtschaftlich­ keit. The advantages of the composition according to the invention lie in its Storage stability, easy handling, depending on the desired ar in addition to good corrosion resistance and economical speed.  

Die Erfindung wird durch folgende Zusammensetzung im einzelnen er­ läutert:The invention is detailed by the following composition purifies:

500 g Eisenpulver,
50 g Zinkpulver,
20 g Polyvinylacetat-Redispersionspulver,
25 g Calciumhydroxid und
2,5 g Bentone LT.500 g iron powder,
50 g zinc powder,
20 g polyvinyl acetate redispersion powder,
25 g calcium hydroxide and
2.5 g Bentone LT.

Diese Zusammensetzung wird mit 180 ml Wasser in 2 min bei Raumtemperatur durch Rühren mit einem maschinellen Rührer zu einer breiigen Masse verarbeitet. Diese läßt sich mit einem Spachtel sehr gut sowohl auf Holz als auch auf Estrichen auftragen. Nach 24 Stunden unter Umgebungsbedingungen ist die Masse hart. Sie haftet gut auf beiden Untergründen. Rostbildung ist unter üblicher Raumluftfeuchtigkeit nicht zu bemerken.This composition is mixed with 180 ml of water in 2 min Room temperature by stirring with a mechanical stirrer pulpy mass processed. This can be done very well with a spatula apply well to both wood and screed. After 24 The mass is hard for hours under ambient conditions. It is liable good on both surfaces. Rust formation is more common Not noticing room humidity.

Der Ableitwiderstand, gemessen nach DIN 53276, beträgt etwa 106 bis 107 Ohm.The leakage resistance, measured according to DIN 53276, is approximately 10 6 to 10 7 ohms.

Claims (6)

1. Zusammensetzung zur Beschichtung von Wänden, Decken und Böden, enthaltend
  • A) als magnetisch wirksamen Bestandteil ferromagnetische Ver­ bindungen,
  • B) als Rostschutzmittel Zinkpulver und
  • C) als Bindemittel redispergierbares Polyvinylacetat, Calciumhydroxid und/oder Zement.
1. Composition for coating walls, ceilings and floors containing
  • A) ferromagnetic compounds as a magnetically active component,
  • B) as a rust preventive, zinc powder and
  • C) as a binder redispersible polyvinyl acetate, calcium hydroxide and / or cement.
2. Zusammensetzung nach Anspruch 1, gekennzeichnet durch Eisen­ pulver als ferromagnetische Verbindung.2. Composition according to claim 1, characterized by iron powder as a ferromagnetic compound. 3. Zusammensetzung nach Anspruch 1 oder 2, gekennzeichnet durch 5 bis 20, insbesondere 8 bis 13 Gew.-% an Zinkpulver und 5 bis 20, insbesondere 7 bis 12 Gew.-% an Bindemittel, bezogen auf das Eisenpulver.3. Composition according to claim 1 or 2, characterized by 5 to 20, in particular 8 to 13 wt .-% of zinc powder and 5 to 20, in particular 7 to 12 wt .-% of binder, based on the iron powder. 4. Zusammensetzung nach Anspruch 1, 2 oder 3, gekennzeichnet durch die Verwendung von Polyvinylacetat und Calciumhydroxid im Ge­ wichtsverhältnis von 2 : 1 bis 1 : 2 als Bindemittel.4. Composition according to claim 1, 2 or 3, characterized by the use of polyvinyl acetate and calcium hydroxide in Ge weight ratio of 2: 1 to 1: 2 as a binder. 5. Zusammensetzung nach mindestens einem der Ansprüche 1 bis 4, gekennzeichnet durch die zusätzliche Verwendung eines Verdickungs­ mittels, insbesondere eines Bentonits in einer Menge von 0,2 bis 2, vorzugsweise 0,5 bis 1 Gew.-%, bezogen auf das Ei­ senpulver.5. Composition according to at least one of claims 1 to 4, characterized by the additional use of a thickener means, in particular a bentonite in an amount of 0.2 to 2, preferably 0.5 to 1 wt .-%, based on the egg must powder. 6. Zusammensetzung nach mindestens einem der Ansprüche 1 bis 5, gekennzeichnet durch die zusätzliche Verwendung von Wasser und sonstigen Additiven zur Herstellung von Beschichtungsmassen in flüssigem, breiigem oder pastenförmigem Zustand.6. The composition according to at least one of claims 1 to 5, characterized by the additional use of water and other additives for the production of coating compositions in liquid, mushy or pasty state.
DE19934308099 1993-03-15 1993-03-15 Coating composition for walls, ceilings and floors Withdrawn DE4308099A1 (en)