DE4302539A1 - Fluid highly conc. stable calcium and/or magnesium hydroxide slurry - for producing micro-flakes and granules, obtd. by slaking oxide with aq. acid and adding polyanion - Google Patents

Fluid highly conc. stable calcium and/or magnesium hydroxide slurry - for producing micro-flakes and granules, obtd. by slaking oxide with aq. acid and adding polyanion

Info

Publication number
DE4302539A1
DE4302539A1 DE19934302539 DE4302539A DE4302539A1 DE 4302539 A1 DE4302539 A1 DE 4302539A1 DE 19934302539 DE19934302539 DE 19934302539 DE 4302539 A DE4302539 A DE 4302539A DE 4302539 A1 DE4302539 A1 DE 4302539A1
Authority
DE
Germany
Prior art keywords
acid
polyanion
slurry
less
microns
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19934302539
Other languages
German (de)
Other versions
DE4302539C2 (en
Inventor
Henri-Rene Dr Ing Langelin
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lhoist Recherche et Developpement SA
Original Assignee
Lhoist Recherche et Developpement SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from BE9200104A external-priority patent/BE1006655A5/en
Application filed by Lhoist Recherche et Developpement SA filed Critical Lhoist Recherche et Developpement SA
Publication of DE4302539A1 publication Critical patent/DE4302539A1/en
Application granted granted Critical
Publication of DE4302539C2 publication Critical patent/DE4302539C2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Ca(OH)2 and/or Mg(OH)2 slurry (I) contg. over 60% dry substance contains an inorg. acid (poly)anion (II) and a polyanion (III) to give (I) a viscosity less than 1500, pref. 500-1500 cP. Also claimed are: (a) Ca(OH)2 and/or Mg(OH)2 microflakes (IA) with a thickness less than 0.5, pref. less than 0.3 micron and parallel upper and lower sides with an area less than 200, pref. less than 100 micron 2; and (b) Ca(OH)2 and/or Mg(OH)2 granules or granulate (IB) in the form of a mixt. of (IA). (II) is pref. SO3-. SO4(2-) or Cl(-) and (III) is derived from a (co)polymer with anionic gps. of (meth)acrylic, vinylbenzylsulphonic or acrylamino-2-methylpropanesulphonic acid or salt or 2-sulphoethyl methacrylate or salt gps. opt. with (meth)acrylate ester(s) as comonomer. The concs. are 1-50, pref. 6-50, pref. 6-50, esp. 6-30 g/l (II) and 1-50, pref. 5-30 g/l (III). In (I), at least 20%, pref. at least 30% of the Ca(OH)2 particles have a grain size of over 100 microns and over 80% a grain size of over 20 microns. (I) contains less than 5, pref. less than 1% Mg(OH)2 w.r.t. Ca(OH)2+ Mg(OH)2. (IB) has an average grain size of over 20, pref. over 50 microns, with over 80% of the particles larger than 20 microns and esp. a grain size of over 100, partic. over 250 microns. (I) is prepd. by slaking CaO and/or MgO with an aq. soln. contg. (II) and adding (III) before, during or at the end of the slaking reaction. The reaction mixt. is stirred and kept below 30, pref. below 20 deg. C. Its viscosity is regulated, pref. by adding CaO to a viscosity of 300-1200 cP; or by slaking with aq. (II) soln. until the viscosity is 300-1200 cP, adding (III) to reduce the viscosity and then adding CaO and/or MgO to a viscosity of 300-1200 cP. (IA) are produced by sepg. the medium into a solid and liq. phase and opt. drying, milling and opt. drying the solid; and (IB) by sepg. the phases and opt. drying. ADVANTAGE - In spite of its very high solids content, (I) has good stability, i.e. high resistance to sedimentation, which facilitates transport and use.

Description

Die Erfindung betrifft eine Kalk- und/oder Magnesiumhydroxid- Aufschlämmung mit einem Trockensubstanzgehalt von mehr als 60%.The invention relates to a lime and / or magnesium hydroxide Slurry with a dry matter content of more than 60%.

Es ist bekannt, Kalk- und/oder Magnesiumhydroxid-Aufschläm­ mungen durch Reaktion von CaO, MgO, CaO-MgO mit Wasser oder durch Vermischen von Calciumhydroxid und/oder Magnesiumhydroxid in einem wäßrigen Medium herzustellen.It is known lime and / or magnesium hydroxide slurries by reaction of CaO, MgO, CaO-MgO with water or by mixing calcium hydroxide and / or magnesium hydroxide in an aqueous medium.

Bei der Herstellung von Kalkmilch bzw. einer Kalkaufschlämmung durch Reaktion von ungelöschtem bzw. gebranntem Kalk mit Wasser ist die mittlere Teilchengröße der Calciumhydroxidteilchen sehr gering, so daß der Gehalt an Calciumhydroxidteilchen in der Aufschlämmung weniger als 20 bis 30 Gew.-% betragen muß, damit eine ausreichende Fließfähigkeit oder eine ausreichende Pumpfä­ higkeit der Aufschlämmung sichergestellt ist.In the production of lime milk or lime slurry by reaction of quicklime with lime the average particle size of the calcium hydroxide particles is very high low, so that the content of Calciumhydroxidteilchen in the Slurry must be less than 20 to 30 wt .-%, so that sufficient flowability or sufficient Pumpfä the slurry is ensured.

Um diesen Gehalt bis auf 50% zu erhöhen, wird in der EP-A- 03 13 483 die Verwendung eines Polymeren und/oder Copolymeren aus mindestens einem ethylenischen Monocarbonsäuremonomeren empfohlen. In order to increase this content to 50%, EP-A 03 13 483 the use of a polymer and / or copolymers from at least one ethylenic monocarboxylic acid monomer recommended.  

Es ist auch bekannt, daß bei Zunahme der Teilchengröße der Calciumhydroxidteilchen die spezifische Oberfläche dieser Teilchen abnimmt und daß man durch Vergrößern des Durchmessers der Calciumhydroxidteilchen die Viskosität der Kalkaufschläm­ mung verringern oder auch bei einer vorbestimmten Viskosität den Trockensubstanzgehalt der Aufschlämmung erhöhen kann.It is also known that as the particle size increases Calcium hydroxide particles the specific surface of this Particles decreases and that by increasing the diameter the Calciumhydroxidteilchen the viscosity of Kalkaufschläm reduce or even at a predetermined viscosity may increase the dry matter content of the slurry.

Um die Teilchengröße von Ca(OH)2 zu erhöhen und damit die Viskosität der Kalkaufschlämmung zu verringern, wurde bereits in der US-PS 44 64 353 vorgeschlagen, gebrannten Kalk in einem wäßrigen Medium in Gegenwart von 0,5 bis 5 Gew.-% Calciumsul­ fat, bezogen auf das Gewicht des gebrannten Kalks, der gelöscht werden soll, zu löschen. Nach dieser Druckschrift wird der ge­ brannte Kalk gelöscht, bis die Temperatur des Reaktionsmediums etwa 85°C beträgt.In order to increase the particle size of Ca (OH) 2 and thus reduce the viscosity of the lime slurry, it has already been proposed in US Pat. No. 4,464,353 to burn lime in an aqueous medium in the presence of from 0.5 to 5% by weight. Calciumsul fat, based on the weight of the quicklime to be deleted, delete. According to this document, the burned lime is extinguished until the temperature of the reaction medium is about 85 ° C.

Versuche haben gezeigt, daß gemäß einem solchen Verfahren er­ haltene Kalkaufschlämmungen einen Trockensubstanzgehalt in der Größenordnung von maximal 40-45% aufweisen können.Experiments have shown that according to such a method he lime slurries have a dry matter content in the Magnitude of maximum 40-45% may have.

Wie auf Seite 335 von "Chemistry and Technology of Lime and Limestone" angegeben, wird durch Verwendung von Wasser, das SO2 enthält, zum Löschen von gebranntem Kalk die Hydratationsge­ schwindigkeit des Kalks verringert und die Bildung von großen bzw. dicken Teilchen begünstigt, die schnell sedimentieren. Kalkaufschlämmungen, die durch Löschen von gebranntem Kalk in Gegenwart von CaSO4 hergestellt worden sind, weisen aufgrund dieser schnellen Sedimentation nur eine relative Stabilität bzw. Beständigkeit in der Zeit auf.As indicated on page 335 of "Chemistry and Technology of Lime and Limestone", by using water containing SO 2 to quench lime, the rate of hydration of the lime is reduced and the formation of large or thick particles is promoted sediment quickly. Lime slurries made by quenching quick lime in the presence of CaSO 4 , due to this rapid sedimentation, have only a relative stability or stability in time.

Die vorliegende Erfindung hat zum Ziel, diese Nachteile zu be­ heben. Sie betrifft daher eine Kalk- und/oder Magnesiumhy­ droxid-Aufschlämmung mit einem Trockensubstanzgehalt von mehr als 60 Gew.-%, wobei diese Aufschlämmung jedoch zeitstabil ist, d. h. daß mit Hilfe dieser Aufschlämmung das Problem der Sedi­ mentation von Teilchen vermieden bzw. verhindert wird. Die Er­ findung betrifft daher eine Kalk- und/oder Magnesiumhydroxid- Aufschlämmung, die eine Viskosität von weniger als 20 P und einen Trockensubstanzgehalt von mehr als 60 Gew.-% aufweist.The aim of the present invention is to overcome these disadvantages to lift. It therefore relates to a lime and / or Magnesiumhy droxid slurry with a dry matter content of more than 60% by weight, but this slurry is time stable, d. H. that with the help of this slurry the problem of sedi mentation of particles is avoided or prevented. The Er The invention therefore relates to a lime and / or magnesium hydroxide  Slurry having a viscosity of less than 20 P and has a dry matter content of more than 60 wt .-%.

Eine solche Aufschlämmung kann durch Löschen von CaO, MgO, CaO-MgO, vorzugsweise von CaO, mit Wasser in Gegenwart eines Anions einer anorganischen Säure, insbesondere von SO4 = und Cl- und in Gegenwart eines Polyanions erhalten werden.Such a slurry can be obtained by quenching CaO, MgO, CaO-MgO, preferably CaO, with water in the presence of an anion of an inorganic acid, especially SO 4 = and Cl -, and in the presence of a polyanion.

Gemäß einem besonderen Merkmal enthält die erfindungsgemäße Aufschlämmung mindestens ein Anion oder Polyanion einer anor­ ganischen Säure, vor allem einer starken Säure und vorteilhaf­ terweise einer Säure, die aus Schwefelsäure, schwefliger Säure, Chlorwasserstoffsäure ausgewählt worden ist, sowie mindestens ein Polyanion.According to a special feature, the inventive Slurry at least one anion or polyanion of an anor ganic acid, especially a strong acid and beneficial of an acid consisting of sulfuric acid, sulphurous acid, Hydrochloric acid has been selected, as well as at least a polyanion.

Das Anion der anorganischen Säure, das vorteilhafterweise SO3 -, SO4 =, Cl- oder ein Gemisch aus diesen ist, ist in der Kalkaufschlämmung in einer Konzentration vorhanden, die allgemein 1 bis 50 g/l, vorteilhafterweise 6 bis 50 g/l und vorzugsweise 6 bis 30 g/l ausmacht.The inorganic acid anion, which is advantageously SO 3 - , SO 4 = , Cl - or a mixture of these, is present in the lime slurry at a concentration generally 1 to 50 g / l, advantageously 6 to 50 g / l and preferably 6 to 30 g / l.

Vorteilhafterweise stammt dieses Anion aus einem Calcium- oder Magnesiumsalz einer anorganischen Säure, insbesondere aus CaCl2, MgCl2, CaSO4 (vorzugsweise in Form von CaSO4·1/2 H2O), MgSO4 (vorzugsweise in Form von MgSO4·7H2O) und ihren Gemi­ schen.Advantageously, this anion is derived from a calcium or magnesium salt of an inorganic acid, in particular CaCl 2 , MgCl 2 , CaSO 4 (preferably in the form of CaSO 4 .1 / 2H 2 O), MgSO 4 (preferably in the form of MgSO 4) . 7H 2 O) and their mixtures.

Das bei einer besonderen Ausführungsform der erfindungsgemäßen Aufschlämmung in dieser vorhandene Polyanion ist vorteilhafter­ weise ein Polyanion, das andere Anionen als anorganische Säu­ reanionen enthält und insbesondere ein Polymeres oder Copolyme­ res, welches anionische Monomereinheiten enthält, die von Mono­ meren der folgenden Gruppe stammen: Acrylsäure und ihre Salze, Methacrylsäure und ihre Salze, Vinylbenzolsulfonsäure und ihre Salze, 2-Acrylamino-2-methylpropansulfonsäure und ihre Salze, 2-Sulfoethylmethacrylat und seine Salze. Die Konzentration dieses Polyanions in der Aufschlämmung beträgt beispielsweise 1 bis 50 g/l, jedoch vorzugsweise 10 bis 30 g/l. This in a particular embodiment of the invention Slurry in this existing polyanion is more advantageous example, a polyanion, the anions other than inorganic Säu contains reanionen and in particular a polymer or copolymer res containing anionic monomer units derived from mono of the following group: acrylic acid and its salts, Methacrylic acid and its salts, vinylbenzenesulfonic acid and their Salts, 2-acrylamido-2-methylpropanesulfonic acid and its salts, 2-sulfoethyl methacrylate and its salts. The concentration This polyanion in the slurry is, for example, 1 to 50 g / l, but preferably 10 to 30 g / l.  

Bevorzugte Polyanionen sind die Acrylpolymeren oder -copolyme­ ren, insbesondere die Polyacrylate, Polymethacrylate, die Copo­ lymeren aus Acrylsäureester und Methacrylsäureester sowie deren Gemische.Preferred polyanions are the acrylic polymers or copolymers ren, in particular the polyacrylates, polymethacrylates, the copo lymeren of acrylic acid esters and methacrylic acid esters and their Mixtures.

Aufschlämmungen nach der Erfindung können in ihren Ausführungs­ formen eine Viskosität im Bereich von 500 cP (0,5 Pa·s) und 1500 cP (1,5 Pa·s) sowie einen Trockensubstanzgehalt von mehr als 60 Gew.-% aufweisen.Slurries according to the invention may in their execution form a viscosity in the range of 500 cP (0.5 Pa · s) and 1500 cP (1.5 Pa · s) and a dry matter content of more have as 60 wt .-%.

Gemäß einem anderen Merkmal der erfindungsgemäßen Aufschlämmun­ gen enthalten sie einen beträchtlichen Anteil an dicken Teil­ chen wie Teilchen mit einer Korngröße oberhalb 100 µm. So ent­ hält in ihren Ausführungsformen die Aufschlämmung nach der Er­ findung Calciumhydroxid- und/oder Magnesiumhydroxidteilchen von beträchtlicher Korngröße. Die Aufschlämmungen nach der Erfin­ dung zeichnen sich durch gute Stabilität oder hohen Widerstand gegenüber der Sedimentation aus, was ihren Transport und ihren Einsatz bzw. ihre Verwendung erleichtert.According to another feature of Aufschlämmun invention They contain a considerable proportion of thick parts like particles with a particle size above 100 μm. So ent In their embodiments, holds the slurry after the Er Calcium hydroxide and / or Magnesiumhydroxidteilchen of considerable grain size. Slurries on the inventor are characterized by good stability or high resistance towards sedimentation, what their transport and their Use or their use easier.

Vorteilhafterweise haben mindestens 20%, vorzugsweise minde­ stens 30% der Calciumhydroxidteilchen eine Korngröße bzw. ei­ nen Durchmesser über 100 µm. Gemäß einem besonderen Merkmal einer solchen Kalkaufschlämmung weisen mehr als 80% der Cal­ ciumhydroxidteilchen eine Korngröße oberhalb 20 µm auf.Advantageously, at least 20%, preferably lower at least 30% of the Calciumhydroxidteilchen a grain size or egg NEN diameter over 100 microns. According to a special feature such lime slurry is more than 80% of cal Ciumhydroxidteilchen a particle size above 20 microns.

Die erfindungsgemäße Aufschlämmung ist in einer Ausführungsform eine Aufschlämmung, die im wesentlichen nur Ca(OH)2 enthält. So enthält entsprechend einer Besonderheit dieser Ausführungsform die Aufschlämmung weniger als 5 Gew. -%, vorzugsweise weniger als 1 Gew.-% und sogar etwa nur 0 Gew.-% Magnesiumhydroxid, be­ zogen auf das Gesamtgewicht an Calciumhydroxid und Magnesiumhy­ droxid.The slurry of the invention in one embodiment is a slurry containing essentially only Ca (OH) 2 . Thus, according to a particularity of this embodiment, the slurry contains less than 5% by weight, preferably less than 1% by weight and even only about 0% by weight of magnesium hydroxide, based on the total weight of calcium hydroxide and magnesium hydroxide.

Die Erfindung betrifft ebenfalls ein Verfahren zur Herstellung einer Kalk- und/oder Magnesiumhydroxid-Aufschlämmung, insbeson­ dere einer Aufschlämmung, die einen Trockensubstanzgehalt von mehr als 50 Gew. -% und eine Viskosität von weniger als 1500 cP (1,5 Pa·s) aufweist, d. h. einer Kalkaufschlämmung nach der Er­ findung.The invention also relates to a process for the preparation a lime and / or magnesium hydroxide slurry, esp a slurry containing a dry matter content of  more than 50% by weight and a viscosity of less than 1500 cP (1.5 Pa · s), i. H. a lime slurry after the Er making.

Entsprechend dem erfindungsgemäßen Verfahren wird Calciumoxid und/oder Magnesiumoxid mit mindestens einer wäßrigen Lösung ge­ löscht, die mindestens ein Anion oder ein Polyanion einer anor­ ganischen Säure enthält, vorteilhafterweise einer starken anor­ ganischen Säure und insbesondere SO3 -, SO4 =, Cl- oder ein Ge­ misch von diesen und/oder ein Polyanion, das SO3 - oder SO4 = oder Cl- oder deren Gemisch enthält; man gibt zu der wäßrigen Lösung ein Polyanion vor, während oder am Ende der Reaktion des Löschens des Calciumoxids und/oder Magnesiumoxids.According to the inventive method, calcium oxide and / or magnesium oxide is erased with at least one aqueous solution containing at least one anion or a polyanion of an anor ganic acid, advantageously a strong anor ganic acid and in particular SO 3 - , SO 4 = , Cl - or a mixture of these and / or a polyanion containing SO 3 - or SO 4 = or Cl - or a mixture thereof; A polyanion is added to the aqueous solution before, during or at the end of the reaction of quenching the calcium oxide and / or magnesium oxide.

Vorteilhafterweise wird im Verlauf oder am Ende der Reaktion ein Polyanion zugesetzt, das andere Anionen als anorganische Säureanionen enthält, insbesondere ein Polymer oder Copolymer, welches anionische Monomereinheiten umfaßt, welche von Monome­ ren stammen, die zu der Gruppe bestehend aus Acrylsäure und ihre Salze, Methacrylsäure und ihre Salze, 2-Acrylamino-2-me­ thylpropansulfonsäure und ihre Salze, 2-Sulfoethylmethacrylat und seine Salze gehören.Advantageously, in the course or at the end of the reaction a polyanion added, the anions other than inorganic Acid anions, in particular a polymer or copolymer, which comprises anionic monomer units derived from monomials come from the group consisting of acrylic acid and their salts, methacrylic acid and its salts, 2-acrylamino-2-me methylpropanesulfonic acid and its salts, 2-sulfoethylmethacrylate and its salts belong.

Die Reaktion des Löschens von CaO, MgO oder einem ihrer Gemi­ sche wird vorteilhafterweise mit Hilfe einer Lösung vorgenom­ men, die 1 bis 50 g/l, vorzugsweise 6 bis 50 g/l und insbeson­ dere 6 bis 30 g/l SO4 = und/oder Cl- enthält.The reaction of quenching CaO, MgO or one of their mixtures is advantageously carried out by means of a solution containing 1 to 50 g / l, preferably 6 to 50 g / l and in particular 6 to 30 g / l of SO 4 = and / or Cl - contains.

Bei dieser Löschreaktion wird das Reaktionsmedium in Bewegung und die Temperatur des Mediums bei unterhalb 30°C, vorzugsweise bei 20°C, gehalten.In this quenching reaction, the reaction medium is in motion and the temperature of the medium below 30 ° C, preferably at 20 ° C, held.

Vorteilhafterweise wird die Reaktion des Löschens durch Messen der Viskosität des Reaktionsmediums kontrolliert bzw. geregelt. Beispielsweise setzt man Calciumoxid und/oder Magnesiumoxid der Lösung zu, bis eine Viskosität im Bereich von 300 bis 1200 cP (0,3 bis 1,2 Pa·s) erreicht ist. Advantageously, the reaction of extinguishment by measuring the viscosity of the reaction medium controlled or regulated. For example, calcium oxide and / or magnesium oxide are used Solution to, until a viscosity in the range of 300 to 1200 cP (0.3 to 1.2 Pa · s) is reached.  

Gemäß einer Ausführungsform des erfindungsgemäßen Verfahrens werden Calciumoxid und/oder Magnesiumoxid mit einer wäßrigen Lösung gelöscht, die mindestens ein Anion einer anorganischen Säure, insbesondere SO4 = und Cl- oder ein Polyanion einer an­ organischen Säure enthält, bis das Reaktionsgemisch eine Visko­ sität im Bereich von 300 bis 1200 cP aufweist; dann wird dem Gemisch ein acrylisches Polymer oder Copolymer zugesetzt, vor­ zugsweise ausgewählt aus einem Polyacrylat oder Polymethacrylat oder einem Copolymeren aus Acrylsäure- und Methacrylsäureestern oder einem Gemisch aus diesen, so daß die genannte Viskosität vermindert wird; dann wird noch Calciumoxid und/oder Magnesium­ oxid zu dem Gemisch zugegeben, um dieses zu löschen, bis man eine Viskosität im Bereich von 300 bis 1200 cP erhält.According to one embodiment of the method calcium oxide and / or magnesium oxide are quenched with an aqueous solution containing at least one anion of an inorganic acid, in particular SO 4 = and Cl - or a polyanion of an organic acid until the reaction mixture has a viscosity in the range from 300 to 1200 cP; then an acrylic polymer or copolymer is added to the mixture, preferably selected from a polyacrylate or polymethacrylate or a copolymer of acrylic acid and methacrylic acid esters or a mixture of these, so that said viscosity is reduced; then calcium oxide and / or magnesium oxide is added to the mixture to quench it until a viscosity in the range of 300 to 1200 cP is obtained.

Gemäß einer besonderen Ausführungsform wird das Calciumoxid mit Hilfe einer wäßrigen Lösung gelöscht, die mindestens ein Anion, vorzugsweise ein Polyanion einer anorganischen Säure sowie ein acrylisches Polymer und/oder Copolymer enthält.According to a particular embodiment, the calcium oxide with Aid of an aqueous solution which contains at least one anion, preferably a polyanion of an inorganic acid and a contains acrylic polymer and / or copolymer.

Die Aufschlämmung von Kalk- und/oder Magnesiumhydroxid, die beispielsweise in der vorstehend beschriebenen Weise herge­ stellt worden ist, kann dann einer Phasentrennung (beispiels­ weise einer Filtration) unterworfen werden, um eine Feststoff­ phase (die die Teilchen enthält) und eine flüssige Phase zu erhalten.The slurry of lime and / or magnesium hydroxide, the For example, in the manner described above can then be a phase separation (for example As a filtration) are subjected to a solid phase (containing the particles) and a liquid phase receive.

Die Feststoffphase, die vorteilhafterweise getrocknet wird, wird dann vermahlen, um Mikroblättchen, insbesondere von Cal­ ciumhydroxid, zu bilden. Diese Mikroblättchen können dann, wenn erforderliche, getrocknet werden.The solid phase, which is advantageously dried, is then ground to microspheres, especially Cal ciumhydroxid to form. These micro-leaves can then, if required to be dried.

Nach dem erneuten Vermischen dieser Mikroblättchen mit Wasser kann eine Aufschlämmung von Kalk- und/oder Magnesiumhydroxid erhalten werden, die insgesamt Mikroblättchen von Calciumhy­ droxid und/oder Magnesiumhydroxid enthält.After mixing these microplates with water again may be a slurry of lime and / or magnesium hydroxide obtained, the total microsheets of Calciumhy contains droxid and / or magnesium hydroxide.

Die Erfindung betrifft daher auch eine Aufschlämmung, welche Mikroblättchen von Calcium- und/oder Magnesiumhydroxid enthält. The invention therefore also relates to a slurry which Microspheres of calcium and / or magnesium hydroxide.  

Solche Mikroblättchen weisen vorteilhafterweise eine Dicke bzw. Stärke von weniger als 0,5 µm, vorzugsweise von weniger als 0,3 µm auf und können bei Ausführungsformen zueinander paralle­ le Unter- und Oberseiten aufweisen, wobei die Oberfläche dieser (beiden) Seiten weniger als 200 µm2, vorzugsweise weniger als 100 µm2 beträgt.Such micro-platelets advantageously have a thickness of less than 0.5 .mu.m, preferably less than 0.3 .mu.m, and in embodiments may have parallel undersides and upper sides, the surface area of these (two) sides being less than 200 μm 2 , preferably less than 100 μm 2 .

Die Erfindung betrifft ebenfalls Mikroblättchen von Calcium- und/oder Magnesiumhydroxid, die vorteilhafterweise eine Dicke von weniger als 0,5 µm (vorzugsweise weniger als 0,3 µm) auf­ weisen sowie eine untere Außenseite und eine obere Außenseite, die zueinander parallel liegen, wobei die Oberfläche dieser Seiten bzw. Flächen weniger als 200 µm2, vorzugsweise weniger als 100 µm2 beträgt.The invention also relates to micro-leaves of calcium and / or magnesium hydroxide, which advantageously have a thickness of less than 0.5 microns (preferably less than 0.3 microns) and a lower outer side and an upper outer side, which are parallel to each other the surface area of these sides or areas is less than 200 μm 2 , preferably less than 100 μm 2 .

Wenn man das Reaktionsgemisch nur einer Phasentrennung, bei­ spielsweise einer Filtration, und gegebenenfalls einer Trock­ nung unterwirft, erhält man Körner oder Teilchen von Ca(OH)2 in Form von Mikroblättchen in einer Dicke von weniger als 0,5 µm, vorzugsweise von weniger als 0,3 µm. Diese Mikroblättchen wei­ sen vorzugsweise eine untere Außenseite und eine obere Außen­ seite auf, die zueinander parallel verlaufen, wobei die Fläche dieser Seiten weniger als 200 µm2, vorzugsweise weniger als 100 µm2 beträgt.If the reaction mixture subjected only to a phase separation, for example, a filtration, and optionally a Trock statement, granules or particles of Ca (OH) 2 in the form of micro-leaves in a thickness of less than 0.5 .mu.m, preferably less than 0.3 μm. These micro-plates preferably have a lower outer side and an upper outer side which run parallel to one another, the area of these sides being less than 200 μm 2 , preferably less than 100 μm 2 .

Gemäß einer Ausführungsform weisen solche Körner bzw. weist ein solches Granulat eine mittlere Korngröße von mehr als 20 µm, vorzugsweise von mehr als 50 µm auf. Vorzugsweise liegt die Korngröße von mehr als 80% der Teilchen oder Körner oberhalb 20 µm.According to one embodiment, such grains have or comprises such granules have an average particle size of more than 20 μm, preferably greater than 50 microns. Preferably, the Grain size of more than 80% of the particles or grains above 20 μm.

Besonders vorteilhafte Körner oder Granulate sind diejenigen mit einer Korngröße von mehr als 100 µm, vorzugsweise von mehr als 250 µm.Particularly advantageous granules or granules are those with a grain size of more than 100 microns, preferably more as 250 μm.

Diese Körner bzw. Granulate nach der Erfindung besitzen große Poren (beispielsweise von 30 bis 35 µm), so daß sie vorteilhaf­ terweise zum Einfangen von dicken Teilchen verwendet werden. These grains or granules according to the invention have large Pores (for example, from 30 to 35 microns), so that they vorteilhaf be used for capturing thick particles.  

Weitere Einzelheiten und Merkmale der Erfindung gehen aus der folgenden Beschreibung hervor, in der auf die Herstellungsbei­ spiele sowie auf die beigefügten Zeichnungen Bezug genommen wird.Further details and features of the invention will be apparent from the following description, in which the Herstellungsbei and to the attached drawings becomes.

In den Zeichnungen zeigtIn the drawings shows

Fig. 1 eine schematische Ansicht einer Anlage, die zur Herstellung einer Aufschlämmung nach der Erfin­ dung verwendet werden kann; und Fig. 1 is a schematic view of a plant which can be used to prepare a slurry according to the inven tion; and

Fig. 2 und 3 Ansichten bzw. Aufnahmen eines Calciumhy­ droxidkorns nach der Erfindung. Figs. 2 and 3 are views and recordings of a Calciumhy droxidkorns according to the invention.

Die zur Herstellung der Aufschlämmung nach der Erfindung ge­ nützte Anlage umfaßt einen Bottich 1, versehen mit einem Kühl­ mantel 11 und einem Rührwerk 12 (vorzugsweise vom Typ Ankerrüh­ rer). Das Calcium- und/oder Magnesiumoxid oder das Calcium- und/oder Magnesiumhydroxid wird in einen Trichter 2 gefüllt und dem Bottich 1 über eine Endlosschnecke 3 zugeführt. Die Ge­ schwindigkeit des Rührwerks beträgt beispielsweise 200 bis 600 UpM.The ge used to prepare the slurry according to the invention used system comprises a tub 1 , provided with a cooling jacket 11 and a stirrer 12 (preferably of the type Ankerrüh rer). The calcium and / or magnesium oxide or the calcium and / or magnesium hydroxide is filled into a funnel 2 and fed to the tub 1 via an endless screw 3 . The speed of the agitator is, for example, 200 to 600 rpm.

Wasser, das Anion einer anorganischen Säure und das Polyanion werden jeweils dem Bottich 1 über die Leitungen 41 bzw. 42 bzw. 43 zugeführt.Water, the anion of an inorganic acid and the polyanion are respectively supplied to the tub 1 via the lines 41, 42 and 43, respectively.

Der Bottich 1 weist an seinem Boden eine Austragsleitung 5 für die entstandene Kalk- und/oder Magnesiumhydroxid-Aufschlämmung auf.The tub 1 has at its bottom a discharge line 5 for the resulting lime and / or magnesium hydroxide slurry.

Vorteilhafterweise ist der Bottich 1 auch mit einer Vorrichtung 6 zum Messen der Viskosität ausgestattet, die an ein Regelungs­ system 7 angeschlossen ist, welches auf den Motor 8 einwirkt, der die Endlosschnecke 3 antreibt. Dieses System 7 ermöglicht dann, die Zugabegeschwindigkeit von Cao, MgO, Ca(OH)2 und/oder Mg(OH)2 zu steuern, um das vorgegebene Viskositätsniveau zu er­ halten, d. h. um am Ende des Arbeitsganges ein Produkt mit einer vorbestimmten Viskosität zu erhalten.Advantageously, the tub 1 is also equipped with a device 6 for measuring the viscosity, which is connected to a control system 7 , which acts on the motor 8 , which drives the endless screw 3 . This system 7 then makes it possible to control the rate of addition of Cao, MgO, Ca (OH) 2 and / or Mg (OH) 2 in order to maintain the predetermined level of viscosity, ie at the end of the operation to obtain a product of a predetermined viscosity receive.

Ein Temperaturfühler 9 ist an ein Steuersystem 10 eines Einlaß­ ventils 21 für eine Kühlflüssigkeit in den Mantel 11 des Bot­ tichs 1 angeschlossen. Auf diese Weise kann sichergestellt wer­ den, daß die Temperatur des im Bottich enthaltenen Gemisches eine vorbestimmte Temperatur, beispielsweise 40°C, vorzugsweise 30°C, nicht übersteigt.A temperature sensor 9 is connected to a control system 10 of an inlet valve 21 for a cooling liquid in the shell 11 of the bot tichs 1 . In this way, who can ensure that the temperature of the mixture contained in the tub does not exceed a predetermined temperature, for example 40 ° C, preferably 30 ° C.

HerstellungsbeispielePreparation Examples Beispiel 1example 1

Zu einer wäßrigen Lösung, die 10 g/l CaSO4 · H2O enthielt, wurde Calciumoxid gegeben. Während der exothermen Hydratationsreak­ tion wurde die Temperatur des Mediums bei etwa 30°C gehalten. Diese Hydratationsreaktion wurde unter Rühren (Umdrehungsge­ schwindigkeit 400 UpM) durchgeführt.To an aqueous solution containing 10 g / l of CaSO 4 .H 2 O was added calcium oxide. During the exothermic hydration reaction, the temperature of the medium was maintained at about 30 ° C. This hydration reaction was carried out with stirring (revolution speed 400 rpm).

Das in der Lösung vorhandene Calciumsulfat hemmte die Hydrata­ tionsreaktion, d. h. verringerte die Hydratationsgeschwindigkeit und ermöglichte somit ein besseres Abführen der bei der Reak­ tion freigesetzten Wärme.The calcium sulfate present in the solution inhibited the hydrata tion reaction, d. H. reduced the rate of hydration and thus enabled a better removal of the at the Reak heat released.

Sobald die Viskosität des Reaktionsgemisches 800 cP betrug, wurde Natriumpolyacrylat in einer Menge entsprechend 1% des angestrebten Gewichtes von Calciumhydroxid in der Kalkauf­ schlämmung zugesetzt. Nach diesem Zusatz wies das gerührte Gemisch eine Viskosität von 300 cP (0,3 Pa·s) auf. Dann wurde weiter Calciumoxid zu dem Gemisch gegeben, bis die Viskosität etwa 800 cP betrug. Während der Hydratationsreaktion des Cal­ ciumoxids wurde die Temperatur des Reaktionsmediums bei etwa 30°C gehalten.As soon as the viscosity of the reaction mixture was 800 cP, was sodium polyacrylate in an amount corresponding to 1% of targeted weight of calcium hydroxide in the lime sludge added. After this addition, the stirred Mixture has a viscosity of 300 cP (0.3 Pa · s). Then it became Continue adding calcium oxide to the mixture until the viscosity about 800 cP. During the hydration reaction of Cal Ciumoxids was the temperature of the reaction medium at about Kept at 30 ° C.

Die auf diese Weise hergestellte Aufschlämmung wies eine Kon­ zentration an Ca(OH)2 von etwa 65% auf. The slurry prepared in this way had a concentration of Ca (OH) 2 of about 65%.

Beispiel 2Example 2

Beispiel 1 wurde wiederholt mit der Abwandlung, daß zunächst eine Lösung enthaltend 10 g/l CaSO4·1/2 H2O und 6 g/l Natrium­ polyacrylat hergestellt und dann der ungelöschte Kalk mit Hilfe dieser Lösung gelöscht wurde, bis man eine Viskosität von 800 cP erhielt. Die auf diese Weise erhaltene Aufschlämmung wies eine Konzentration an Ca(OH)2 von etwa 65-70 Gew.-% auf.Example 1 was repeated with the modification that first a solution containing 10 g / l CaSO 4 · 1/2 H 2 O and 6 g / l sodium polyacrylate prepared and then the quicklime was quenched using this solution until a viscosity received from 800 cP. The slurry thus obtained had a Ca (OH) 2 concentration of about 65-70% by weight.

Durch Filtrieren wurden aus dieser Aufschlämmung Ca(OH)2-Teil­ chen gewonnen, wie sie in den Fig. 2 und 3 gezeigt sind. Diese Teilchen zeigten sich in Form eines Ganzen oder eines Gemisches von Mikroblättchen. Die Dicke dieser Mikroblättchen lag in der Größenordnung von 0,1 bis 0,2 µm. Diese Mikroblättchen wiesen eine untere Außenseite und eine obere Außenseite auf, die zu­ einander parallel verliefen. Die Oberfläche dieser Seiten be­ trug etwa 25 bis 50 µm2.By filtration, Ca (OH) 2 particles as shown in Figs. 2 and 3 were recovered from this slurry. These particles appeared in the form of a whole or a mixture of microspheres. The thickness of these microplates was of the order of 0.1 to 0.2 μm. These microplates had a lower outside and an upper outside, which ran parallel to each other. The surface of these pages was about 25 to 50 microns 2 .

In der folgenden Tabelle sind die Korngrößenverteilungen der in diesem Beispiel hergestellten Kalkaufschlämmung und einer Aufschlämmung vom klassischen Typ, d. h. nach dem Stand der Tech­ nik, aufgeführt. In the following table, the particle size distributions of in prepared in this example lime slurry and a Classic type slurry, d. H. according to the state of the art nik, listed.  

Tabelle table

Wie die Tabelle zeigt, ist die erfindungsgemäße Aufschlämmung dieses Beispiels durch die Anwesenheit von Teilchen oder Kör­ nern mit einer mittleren Korngröße von weit über 20 µm (um etwa 50 µm mehr) gekennzeichnet. Tatsächlich weisen mehr als 80 Gew.-% der Teilchen eine Korngröße von über 20 µm auf. Eine be­ trächtliche Anzahl der Teilchen weist eine Korngröße von mehr als 250 µm auf.As the table shows, the slurry of the invention is this example by the presence of particles or Kör ners with a mean grain size of well over 20 μm (approx 50 μm more). In fact, more than 80 Wt .-% of the particles have a particle size of about 20 microns. One be Considerable number of particles has a grain size of more than 250 microns.

Beispiel 3Example 3

Beispiel 1 wurde wiederholt mit der Abwandlung, daß eine Lö­ sung, die 20 g/l MgSO4 · 7 H2O anstelle einer Lösung, die 10 g/l CaSO4 · 1/2 H2O enthielt, eingesetzt wurde. Auf diese Weise konnte eine Kalkaufschlämmung hergestellt werden, die etwa 65 Gew.-% Ca(OH)2 enthielt.Example 1 was repeated except that a solution containing 20 g / l MgSO 4 .7H 2 O was used in place of a solution containing 10 g / l CaSO 4. 1/2 H 2 O. In this way, a lime slurry containing about 65% by weight Ca (OH) 2 could be prepared.

Trotz der Anwesenheit einer beträchtlichen Menge von Körnern mit einer Korngröße über 200 µm wurde festgestellt, daß eine solche Kalkaufschlämmung eine ausgezeichnete Stabilität von mehr als 24 Stunden ohne Rühren sowie von mehr als 15 Tagen bei leichtem Rühren (100 UpM) aufwies.Despite the presence of a considerable amount of grains with a grain size over 200 microns was found that a such lime slurry has excellent stability of more than 24 hours without stirring and more than 15 days gentle stirring (100 rpm).

In der folgenden Tabelle sind die Werte für die Viskosität der Kalkaufschlämmung in einem Bottich und unter leichtem Rühren aufgeführt.In the following table the values for the viscosity of the Lime slurry in a tub and with gentle stirring listed.

Verweilzeit (Tage)Dwell time (days) Viskosität (cP)Viscosity (cP) 11 315315 22 310310 33 320320 44 315315 55 307307 66 315315

Eine solche Kalkaufschlämmung kann Dank ihrer Stabilität leicht in Tankwagen transportiert und aus diesem abgegeben werden.Such lime slurry can be light thanks to its stability be transported in tankers and delivered from this.

Beispiel 4Example 4

Beispiel 2 wurde wiederholt mit der Abwandlung, daß die Temperatur des Mediums bzw. Gemisches nicht bei einer Temperatur un­ terhalb 40°C gehalten wurde.Example 2 was repeated with the modification that the temperature of the medium or mixture not at a temperature un was kept below 40 ° C.

In der folgenden Tabelle sind die Temperaturen des Mediums nach Zugabe von 150 g CaO in 600 ml einer wäßrigen Lösung, die gege­ benenfalls CaSO4 sowie Natriumpolycarbonat enthielt, aufge­ führt.In the following table, the temperatures of the medium after addition of 150 g of CaO in 600 ml of an aqueous solution, where appropriate, CaSO 4 and sodium polycarbonate contained, leads up.

Dieses Beispiel zeigt, daß es zwar nicht möglich ist, ein Ca(OH)2 Granulat gemäß der Erfindung in Abwesenheit eines Poly­ anions (Natriumpolycarbonat) herzustellen, das CaSO4 aber er­ möglicht, die Hydratationsgeschwindigkeit des (ungelöschten) Kalks und damit die Geschwindigkeit der Freisetzung von Wärme bei dieser Reaktion herabzusetzen.This example shows that although it is not possible to produce a Ca (OH) 2 granules according to the invention in the absence of a poly anion (sodium polycarbonate), the CaSO 4 but it allows, the rate of hydration (uncalcined) lime and thus the speed of Release heat to decrease in this reaction.

Weitere Beispiele für das erfindungsgemäße Verfahren wurden durchgeführt. In diesen Beispielen wurden eingesetzt:Further examples of the method according to the invention were carried out. In these examples were used:

CaCl2, MgCl2 als Substanzen, die ein Anion einer anorganischen Säure freisetzen,
Natrium- und/oder Ammoniumsalze einer Polycarbonsäure sowie ge­ mischte Salze von polymerer Acrylsäure als Substanzen, die ein Polyanion freisetzen und MgO sowie CaO · MgO als Ausgangsstoffe, die gelöscht werden sollten, für die Herstellung der Aufschläm­ mung.CaCl 2 , MgCl 2 as substances which release an anion of an inorganic acid,
Sodium and / or ammonium salts of a polycarboxylic acid and ge mixed salts of polymeric acrylic acid as substances that release a polyanion and MgO and CaO · MgO as starting materials that should be deleted for the production of Aufschläm determination.

Diese Beispiele haben gezeigt, daß es bei Verwendung dieser Stoffe möglich war, Aufschlämmungen mit hoher Konzentration an Trockensubstanz (60 bis 70%) und mit einer Viskosität von we­ niger als 1000 cP (1 Pa·s) zu erhalten.These examples have shown that when using this Substances was possible, slurries with high concentration  Dry substance (60 to 70%) and with a viscosity of we niger than 1000 cP (1 Pa · s).

Die erfindungsgemäße Kalkaufschlämmung wird vor allem Dank der Form und der Größe ihrer Teilchen (Mikroblättchen, Makroporen, beträchtliche Korngröße, geringer Gehalt an Wasser (25 bis 30%)) mit Vorteil für die Behandlung von Industrieabfällen ein­ gesetzt, beispielsweise von Industrie-Abfällen (flüssig oder gasförmig), von Abfällen, die Schwermetalle enthalten usw.The lime slurry of the invention is mainly thanks to the Shape and size of their particles (micro-leaflets, macropores, considerable grain size, low water content (25 to 30%)) beneficial for the treatment of industrial waste set, for example, by industrial waste (liquid or gaseous), waste containing heavy metals, etc.

Die erfindungsgemäßen Granulate, insbesondere der Teil davon mit einer Korngröße über 200 µm werden/wird vorteilhafterweise verwendet, um Filterbetten herzustellen. Solche Körner oder Granulate weisen eine geringe spezifische Oberfläche (9 m2/g gegenüber 20 bis 25 m2 /g für Ca(OH)2 einer bekannten Aufschläm­ mung) auf, aber Makroporen oder Käfige von 20 bis 50 µm.The granules according to the invention, in particular the part thereof with a particle size of more than 200 μm, are / is advantageously used to produce filter beds. Such grains or granules have a low specific surface area (9 m 2 / g compared to 20 to 25 m 2 / g for Ca (OH) 2 of a known Aufschläm tion), but macropores or cages of 20 to 50 microns.

Schließlich wurde durch Vermahlen des Granulats einer Kalkauf­ schlämmung, erhalten durch Filtrieren und Trocknen, ein Gemisch von Mikroblättchen aus Ca(OH)2 erhalten. Solche Mikroblättchen werden aufgrund ihrer geringen Dicke (0,2 bis 0,3 µm und wegen ihrer Oberfläche (25 bis 30 µm2) vorteilhafterweise bei der Herstellung von Filmen und Folien aus Kunststoffmaterialien, cellulosischen Materialien (Papier . . .) usw. verwendet. Solche Mikroblättchen wirken als Flammverzögerer.Finally, by grinding the granules of a lime slurry obtained by filtration and drying, a mixture of microspheres of Ca (OH) 2 was obtained. Such micro-platelets are advantageously used in the manufacture of films and sheets of plastic materials, cellulosic materials (paper, etc.), etc. due to their small thickness (0.2 to 0.3 μm and surface area (25 to 30 μm 2 ). Such micro-leaves act as flame retardants.

Die in der Beschreibung angegebenen Viskositätswerte sind Werte nach Brookfield, bestimmt mit der Nadel Nr. 3 und bei einer Um­ drehungsgeschwindigkeit von 60 UpM.The viscosity values given in the description are values to Brookfield, determined with the needle No. 3 and at a Um rotation speed of 60 rpm.

Claims (30)

1. Kalk- und/oder Magnesiumhydroxid-Aufschlämmung mit einem Trockensubstanzgehalt von mehr als 60%, dadurch gekennzeichnet, daß sie ein Anion oder ein Polyanion einer anorganischen Säure und ein Polyanion enthält, um in der Aufschlämmung eine Viskosität von weniger als 1500 cP, vorzugsweise im Bereich von 500 bis 1500 cP sicherzustellen.Lime and / or magnesium hydroxide slurry having a dry matter content of more than 60%, characterized in that it contains an anion or a polyanion of an inorganic acid and a polyanion to give in the slurry a viscosity of less than 1500 cP, preferably in the range of 500 to 1500 cps. 2. Aufschlämmung nach Anspruch 1, dadurch gekennzeichnet, daß das Anion oder Anion des Polyanions einer anorganischen Säure ausgewählt wird aus SO3 -, SO4 = und Cl-.2. A slurry according to claim 1, characterized in that the anion or anion of the polyanion of an inorganic acid is selected from SO 3 - , SO 4 = and Cl - . 3. Aufschlämmung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß sie 1 bis 50 g/l des Anions oder des Anions des Polyanions einer anorganischen Säure enthält.3. A slurry according to claim 1 or 2, characterized in that it is 1 to 50 g / l of the anion or anion of the polyanion of an inorganic Contains acid. 4. Aufschlämmung nach Anspruch 3, dadurch gekennzeichnet, daß sie 6 bis 50 g/l, vorzugsweise 6 bis 30 g/l des Anions oder Anions des Polyanions der anorganischen Säure enthält. 4. A slurry according to claim 3, characterized in that it is 6 to 50 g / l, preferably 6 to 30 g / l of the anion or anion of the polyanion containing the inorganic acid.   5. Aufschlämmung nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß das Polyanion ein Polymer oder Copolymer ist, welches anionische Monomereneinhei­ ten enthält, die von Monomeren aus der Gruppe umfassend Acryl­ säure und ihre Salze, Methacrylsäure und ihre Salze, Vinylben­ zylsulfonsäure und ihre Salze, Acrylamino-2-methylpropansulfon­ säure und ihre Salze, 2-Sulfoethylmethacrylat und seine Salze stammen.5. A slurry according to any one of claims 1 to 4, characterized in that the polyanion a Polymer or copolymer which is anionic monomer containing monomers selected from the group comprising acrylic acid and its salts, methacrylic acid and its salts, vinylbenzene cylsulfonic acid and its salts, acrylamino-2-methylpropanesulfone acid and its salts, 2-sulfoethyl methacrylate and its salts come. 6. Aufschlämmung nach Anspruch 5, dadurch gekennzeichnet, daß sie 1 bis 50 g/l, vorzugsweise 5 bis 30 g/l Polyanion enthält.6. A slurry according to claim 5, characterized in that it is 1 to 50 g / l, preferably 5 to 30 g / l polyanion. 7. Aufschlämmung nach Anspruch 6, dadurch gekennzeichnet, daß sie ein Anion oder Polyanion einer anorganischen Säure und ein Polyanion aus­ gewählt aus den acrylischen Polymeren und Copolymeren enthält.7. A slurry according to claim 6, characterized in that it is an anion or polyanion of an inorganic acid and a polyanion selected from the acrylic polymers and copolymers. 8. Aufschlämmung nach Anspruch 7, dadurch gekennzeichnet, daß die acrylischen Polymeren und Copolymeren ausgewählt sind aus den Polyacryla­ ten, Polymethacrylaten, Copolymeren von Acrylsäure- und Meth­ acrylsäureestern und deren Gemischen.8. A slurry according to claim 7, characterized in that the acrylic Polymers and copolymers are selected from the polyacryla th, polymethacrylates, copolymers of acrylic acid and meth acrylic acid esters and mixtures thereof. 9. Aufschlämmung nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß mindestens 20%, vorzugsweise mindestens 30% der Calciumhydroxidteilchen eine Korngröße von mehr als 100 µm aufweisen.9. A slurry according to any one of the preceding claims, characterized in that at least 20%, preferably at least 30% of the calcium hydroxide particles Grain size of more than 100 microns have. 10. Aufschlämmung nach Anspruch 9, dadurch gekennzeichnet, daß mehr als 80% der Calciumhydroxidteilchen eine Korngröße von mehr als 20 µm auf­ weisen.10. A slurry according to claim 9, characterized in that more than 80% of Calciumhydroxidteilchen a grain size of more than 20 microns point. 11. Aufschlämmung nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß sie Mikroblätt­ chen aus Calciumhydroxid enthält. 11. A slurry according to any one of claims 1 to 8, characterized in that it microblätt contains calcium hydroxide.   12. Aufschlämmung nach Anspruch 11, dadurch gekennzeichnet, daß die Mikroblätt­ chen eine Dicke von weniger als 0,5 µm, vorzugsweise von weni­ ger als 0,3 µm aufweisen.12. A slurry according to claim 11, characterized in that the micro-leaf chen a thickness of less than 0.5 microns, preferably von weni ger than 0.3 microns. 13. Aufschlämmung nach Anspruch 12, dadurch gekennzeichnet, daß die Mikroblätt­ chen eine untere Außenseite und eine obere Außenseite aufwei­ sen, die zueinander parallel verlaufen und daß die Oberfläche dieser Seiten weniger als 200 µm2, vorzugsweise weniger als 100 µm2, beträgt.13. A slurry according to claim 12, characterized in that the Mikroblätt Chen a lower outer side and an upper outer side aufwei sen, which are parallel to each other and that the surface of these sides less than 200 microns 2 , preferably less than 100 microns 2 , is. 14. Aufschlämmung nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß sie weniger als 5 Gew.-%, vorzugsweise weniger als 1 Gew.-% Magnesiumhydroxid, bezogen auf das Gesamtgewicht von Calciumhydroxid und Magne­ siumhydroxid, enthält.14. A slurry according to any one of the preceding claims, characterized in that they are less than 5% by weight, preferably less than 1% by weight, of magnesium hydroxide, based on the total weight of calcium hydroxide and magne sodium hydroxide. 15. Verfahren zur Herstellung einer Kalkaufschlämmung nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, daß man Calciumoxid und/oder Magnesiumoxid mit Hilfe einer wäßrigen Lösung löscht, die mindestens ein Anion oder ein Polyanion einer anorganischen Säure enthält und daß man der wäßrigen Lösung vor, während oder am Ende der Reaktion des Löschens ein Polyanion zusetzt.15. A method for producing a lime slurry after one of claims 1 to 10, characterized in that one calcium oxide and / or magnesium oxide is quenched by means of an aqueous solution, the at least one anion or a polyanion of an inorganic Contains acid and that the aqueous solution before, during or add a polyanion at the end of the quench reaction. 16. Verfahren nach Anspruch 15, dadurch gekennzeichnet, daß man das Calcium­ oxid und/oder Magnesiumoxid mit einer Lösung löscht, die min­ destens ein Anion, ausgewählt aus SO3 -, SO4 = und Cl- und/oder ein Polyanion, enthaltend SO3 -, SO4 = und Cl-, enthält und daß man im Verlauf der Reaktion oder am Ende der Reaktion ein Poly­ mer oder Copolymer zusetzt, das anionische Monomereneinheiten enthält, die aus Monomeren hervorgegangen sind, welche der Gruppe, umfassend Acrylsäure und ihre Salze, Methacrylsäure und ihre Salze, Vinylbenzylsulfonsäure und ihre Salze, Acrylamino- 2-methylpropansulfonsäure und ihre Salze und 2-Sulfoethylmeth­ acrylat und seine Salze, angehören.16. The method according to claim 15, characterized in that the calcium oxide and / or magnesium oxide is quenched with a solution containing at least one anion selected from SO 3 - , SO 4 = and Cl - and / or a polyanion containing SO 3 - , SO 4 = and Cl - , and in the course of the reaction or at the end of the reaction adding a polymer or copolymer containing anionic monomer units derived from monomers belonging to the group comprising acrylic acid and its salts , Methacrylic acid and its salts, vinylbenzylsulfonic acid and its salts, acrylamino-2-methylpropanesulfonic acid and its salts, and 2-sulfoethylmethacrylate and its salts. 17. Verfahren nach Anspruch 15 oder 16, dadurch gekennzeichnet, daß man das Calcium­ oxid mit einer Lösung löscht, die 1 bis 50 g/l, vorzugsweise 6 bis 30 g/l, SO4 = und/oder Cl- enthält.17. The method according to claim 15 or 16, characterized in that the calcium oxide is quenched with a solution containing 1 to 50 g / l, preferably 6 to 30 g / l, SO 4 = and / or Cl - . 18. Verfahren nach Anspruch 16 oder 17, dadurch gekennzeichnet, daß man im Verlauf oder am Ende der Reaktion ein Polyanion, ausgewählt aus einem Polyacrylat oder Polymethacrylat oder einem Copolymeren von Acrylsäure- und Methacrylsäureestern oder einem Gemisch aus diesen so zusetzt, daß die Konzentration an Polyanion, ausge­ wählt aus einem Polyacrylat oder Polymethacrylat oder einem Co­ polymeren von Acrylsäure- und Methacrylsäureestern oder einem Gemisch aus diesen im Bereich von 1 bis 50 g/l, vorzugsweise im Bereich von 5 bis 30 g/l, liegt.18. The method according to claim 16 or 17, characterized in that one in the course or at the end of the reaction, a polyanion selected from a Polyacrylate or polymethacrylate or a copolymer of Acrylic acid and methacrylic acid esters or a mixture of this added so that the concentration of polyanion, out selected from a polyacrylate or polymethacrylate or a co polymers of acrylic acid and methacrylic acid esters or a Mixture of these in the range of 1 to 50 g / l, preferably in Range of 5 to 30 g / l. 19. Verfahren nach einem der Ansprüche 15 bis 18, dadurch gekennzeichnet, daß man das Reaktions­ gemisch rührt und die Temperatur des Reaktionsgemisches unter­ halb 30°C, vorzugsweise unterhalb 20°C, hält.19. The method according to any one of claims 15 to 18, characterized in that the reaction stirred mixture and the temperature of the reaction mixture below half 30 ° C, preferably below 20 ° C, holds. 20. Verfahren nach einem der Ansprüche 15 bis 19, dadurch gekennzeichnet, daß man die Viskosi­ tät des Reaktionsmediums regelt.20. The method according to any one of claims 15 to 19, characterized in that the Viskosi regulates the activity of the reaction medium. 21. Verfahren nach Anspruch 20, dadurch gekennzeichnet, daß man der Lösung Calciumoxid zusetzt, bis zu einer Viskosität im Bereich von 300 bis 1200 cP.21. The method according to claim 20, characterized in that the solution Calcium oxide added, up to a viscosity in the range of 300 to 1200 cp. 22. Verfahren nach Anspruch 20, dadurch gekennzeichnet, daß man Calciumoxid und/oder Magnesiumoxid mit einer wäßrigen Lösung, die min­ destens ein Anion einer anorganischen Säure, insbesondere SO4 = und Cl- oder ein Polyanion einer anorganischen Säure, enthält, löscht, bis das Reaktionsgemisch eine Viskosität im Bereich von 300 bis 1200 cP aufweist und daß man dann dem Gemisch ein Acrylpolymer oder -copolymer, vorzugsweise ausgewählt aus einem Polyacrylat oder Polymethacrylat oder ein Copolymer aus Acryl­ säure- und Methacrylsäureester oder einem Gemisch aus diesen zusetzt, um die Viskosität zu vermindern und daß man dann dem Gemisch noch Calciumoxid und/oder Magnesiumoxid zusetzt, bis man eine Viskosität im Bereich von 300 bis 1200 cP erhält.22. The method according to claim 20, characterized in that one contains calcium oxide and / or magnesium oxide with an aqueous solution containing at least one anion of an inorganic acid, in particular SO 4 = and Cl - or a polyanion of an inorganic acid, until the reaction mixture has a viscosity in the range of 300 to 1200 cP and then adding to the mixture an acrylic polymer or copolymer, preferably selected from a polyacrylate or polymethacrylate or a copolymer of acrylic acid and methacrylic acid ester or a mixture of these, the viscosity and then adding calcium oxide and / or magnesium oxide to the mixture until a viscosity in the range of 300 to 1200 cP is obtained. 23. Verfahren nach einem der Ansprüche 15 bis 22, dadurch gekennzeichnet, daß man Calciumoxid mit einer Lösung löscht, die mindestens ein Anion einer anorga­ nischen Säure, vorzugsweise ein Polyanion einer anorganischen Säure und ein Acrylpolymer und/oder -copolymer enthält.23. The method according to any one of claims 15 to 22, characterized in that one calcium oxide with a solution that deletes at least one anion of anorga nical acid, preferably a polyanion of an inorganic Acid and an acrylic polymer and / or copolymer. 24. Mikroblättchen von Calciumhydroxid und/oder Magnesiumhy­ droxid mit einer Dicke von weniger als 0,5 µm, vorzugsweise von weniger als 0,3 µm, die eine untere und eine obere Seite auf­ weisen, die zueinander parallel verlaufen, wobei die Fläche dieser Seiten weniger als 200 µm2, vorzugsweise weniger als 100 µm2, beträgt.24. microplates of calcium hydroxide and / or Magnesiumhy hydroxide having a thickness of less than 0.5 .mu.m, preferably less than 0.3 .mu.m, having a lower and an upper side, which extend parallel to each other, wherein the surface of these pages less than 200 μm 2 , preferably less than 100 μm 2 . 25. Verfahren, das zur Herstellung von Mikroblättchen nach Anspruch 24 angewandt werden kann, bei dem man eine Aufschläm­ mung nach einem der Ansprüche 1 bis 10 herstellt, dadurch gekennzeichnet, daß man das Medium einer Phasentrennung unterwirft, bei der man eine Feststoff­ phase und eine flüssige Phase erhält, daß man gegebenenfalls die Feststoffphase trocknet, daß man die Feststoffphase ver­ mahlt und daß man gegebenenfalls die vermahlene Feststoffphase trocknet.25. Method for the preparation of micro-leaves after Claim 24 can be applied, in which a Aufschläm mung according to one of claims 1 to 10 produces, characterized in that the medium subjected to a phase separation, in which a solid phase and a liquid phase, that optionally the solid phase is dried, that the solid phase ver grinding and that optionally the ground solid phase dries. 26. Korn oder Granulat von Calciumhydroxid und/oder Magnesium­ hydroxid in Form eines Gemisches von Mikroblättchen nach An­ spruch 24. 26. Grain or granules of calcium hydroxide and / or magnesium hydroxide in the form of a mixture of microspheres according to An award 24.   27. Korn oder Granulat nach Anspruch 26, dadurch gekennzeichnet, daß es eine mittlere Korngröße von mehr als 20 µm, vorzugsweise von mehr als 50 µm, aufweist.27. Grain or granules according to claim 26, characterized in that it has a mean Grain size of more than 20 μm, preferably more than 50 μm, having. 28. Korn oder Granulat nach Anspruch 27, dadurch gekennzeichnet, daß mehr als 80% der Teilchen eine Korngröße von mehr als 20 µm aufweisen.28. Grain or granules according to claim 27, characterized in that more than 80% of Particles have a particle size of more than 20 microns. 29. Korn oder Granulat nach Anspruch 27, dadurch gekennzeichnet, daß es eine Korngröße von mehr als 100, vorzugsweise von mehr als 250 µm, aufweist.29. Grain or granules according to claim 27, characterized in that it has a grain size of more than 100, preferably more than 250 microns. 30. Verfahren zur Herstellung von Körnern oder Granulat nach einem der Ansprüche 26 bis 29, dadurch gekennzeichnet, daß man eine Auf­ schlämmung nach einem der Ansprüche 1 bis 10 herstellt und das Medium einer Phasentrennung und gegebenenfalls einer Trocknung unterwirft.30. Process for the preparation of grains or granules after one of claims 26 to 29, characterized in that an up Sludge according to any one of claims 1 to 10 produces and the Medium of a phase separation and optionally a drying subjects.
DE19934302539 1992-01-31 1993-01-29 Lime and / or magnesium hydroxide slurry and its manufacture Expired - Fee Related DE4302539C2 (en)