DE3743380A1 - METHOD FOR MELTING STEEL IN AN OXYGEN BLOW CONVERTER - Google Patents

Abstract

A steelmaking process in an oxygen-blown converter using ferrous metallic materials in solid form and molten pig iron consists in charging the ferrous metallic materials into the converter, heating them up to a temperature short of the melting point by means of combustion of hydrocarbon and carbonaceous fuels introduced into the converter in a stream of an oxygen-containing gas, where the amount of the hydrocarbon fuel fed from the bottom is confined to a limit of 1.5-6.0 kg of equivalent fuel per tonne of the ferrous metallic materials in solid form subjecting these materials to a homogenizing blast of a neutral gas introduced from the bottom before pouring the molten pig iron into the converter.

Description

Die Erfindung bezieht sich auf das Hüttenwesen und betrifft ein Verfahren zum Erschmelzen von Stahl in einem Sauerstoff-Blaskonverter.The invention relates to metallurgy and relates to a process for melting steel in one Oxygen blow converter.

Die Erfindung kann beim Erschmelzen von Stahl in einem Sauerstoff-Blaskonverter aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen (im folgenden als Metallcharge bezeichnet) verwendet werden. Als feste metallische, eisenhaltige Stoffe (im folgenden als fester metallischer Einsatz bezeichnet) können z. B. Schrott, Alteisen, metallische Abfälle von Walzwerken und Stahlgießereien, Eisenschwamm u. ä. eingesetzt werden.The invention can be used in melting steel in one Oxygen blow converter made of solid metallic, ferrous Substances and liquid pig iron (hereinafter referred to as Metal batch referred to) can be used. As solid metallic, ferrous substances (hereinafter referred to as solid metallic Use designated) can, for. B. scrap, scrap iron, metallic waste from rolling mills and steel foundries, Sponge iron Ä. are used.

Der Anteil des festen metallischen Einsatzes in der Metallcharge ist begrenzt und hängt von der Menge der bei der Oxydation der Begleitstoffe der eisenhaltigen Schmelze freiwerdenden Wärme ab. Um den Anteil des festen metallischen Einsatzes in der Metallcharge zu erhöhen, muß der metallische Einsatz zusätzlich durch Verbrennen eines Brennstoffs im Konverter erhitzt werden. Je stärker erhitzt wird, um so größer ist der Anteil des festen metallischen Einsatzes in der Metallcharge und umgekehrt.The proportion of solid metallic insert in the Metal batch is limited and depends on the amount of items the oxidation of the accompanying substances of the iron-containing melt released heat. To the proportion of solid metallic To increase use in the metal batch, the metallic Use additionally by burning a fuel be heated in the converter. The more you heat, the more the proportion of solid metallic insert is greater in the metal batch and vice versa.

Beim Erhitzen bildet sich in der Regel eine flüssige Phase, die aus flüssiger Schlacke und geschmolzenem Metall besteht. Deshalb ist dieser Prozeß äußerst schwer anwendbar, da auf Grund des erheblichen Unterschieds der Oxydationspotentiale der entstehenden flüssigen Phase und des flüssigen Roheisens es zu Auswürfen der flüssigen Komponenten aus dem Konverter beim Eingießen des flüssigen Roheisens infolge des explosionsartigen Ablaufs der Reaktionen kommen kann.A liquid usually forms when heated Phase consisting of liquid slag and molten metal consists. So this process is extremely difficult to apply because of the considerable difference in the oxidation potential the resulting liquid phase and the liquid Pig iron it to eject the liquid components from the converter when pouring the molten pig iron due to the explosive nature of the reactions can.

Da Roheisen teurer und schwerer zu beschaffen ist als der feste metallische Einsatz besteht gegenwärtig das Problem, ein Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen bereitzustellen, das eine Erhöhung des Anteils des festen metallischen Einsatzes beim Schmelzen im Konverter ermöglicht und den Auswurf von Metall und Schlacke aus dem Konverter während des Eingießens des Roheisens verhindert. Because pig iron is more expensive and harder to obtain than the solid metallic insert currently has the problem a process for melting steel in an oxygen Blow converter made of solid metallic, ferrous Substances and liquid pig iron provide an increase the proportion of the solid metallic insert in the melting in the converter and the ejection of metal and slag from the converter while pouring the pig iron prevented.  

Es ist ein Verfahren zum Erhitzen von festem metallischen Einsatz in einem Konverter bekannt (SU, A, 960270).It is a process for heating solid metallic Use in a converter known (SU, A, 960270).

Zur Durchführung dieses Verfahrens wird der Sauerstoff- Blaskonverter mit Bodenwinddüsen und einer Oberwinddüse ausgerüstet. Durch die Bodenwinddüsen wird ein gasförmiger, aus Kohlenwasserstoffen bestehender Brennstoff und ein sauerstoffhaltiges Gas, und durch die Oberwinddüse ein flüssiger, aus Kohlenwasserstoffen bestehender Brennstoff und ein sauerstoffhaltiges Gas zugeführt.To carry out this process, the oxygen Blowing converter with bottom wind nozzles and a top wind nozzle equipped. A gaseous, fuel consisting of hydrocarbons and one containing oxygen Gas, and through the headwind nozzle a liquid, hydrocarbon fuel and supplied with an oxygen-containing gas.

Das Verfahren besteht in der Durchführung folgender technologischer Hauptarbeitsgänge. In den Konverter gibt man den festen metallischen Einsatz auf, der durch Verbrennen eines gasförmigen, aus Kohlenwasserstoffen bestehenden Brennstoffs erhitzt wird, der in den Konverter von unten zugeführt wird, und eines flüssigen, aus Kohlenwasserstoffen bestehenden Brennstoffs, der in den Konverter in einem sauerstoffhaltigen Gas von oben zugeführt wird, wobei das sauerstoffhaltige Gas, in den Konverter von oben oder unten geblasen wird. Das sauerstoffhaltige Gas wird durch die Oberwindform in einer solchen Menge geblasen, daß dessen Verbrauch 10 bis 30% des theoretisch zum vollkommenen Verbrennen des durch die Oberwinddüse zugeführten flüssigen Brennstoffs notwenigen Verbrauchs des Oxydationsmittels ausmacht. Die übrige Menge des Oxydationsmittels wird durch die Bodenwinddüsen zugeführt. Nach dem Erhitzen des metallischen Einsatzes bis auf die vorgesehene Temperatur wird in den Konverter flüssiges Roheisen eingegossen, der feste metallische Einsatz zum Schmelzen gebracht und die Schmelze nach einem beliebigen, bekannten Verfahren ähnlich wie beim Durchblasen des Roheisens gefrischt.The procedure is to do the following main technological operations. You put in the converter the solid metallic insert that is burned a gaseous fuel consisting of hydrocarbons is heated, which is fed into the converter from below and a liquid one consisting of hydrocarbons Fuel that is in the converter in an oxygen-containing Gas is supplied from above, the oxygen-containing Gas, blown into the converter from above or below becomes. The oxygen-containing gas is created by the headwind shape blown in such an amount that its consumption 10 to 30% of the theoretical for perfect burning of the liquid fuel supplied through the headwind nozzle necessary consumption of the oxidizing agent. The remaining amount of the oxidizing agent is through the floor wind jets fed. After heating the metallic Use up to the intended temperature is in cast in the molten pig iron converter, the solid metallic Use melted and melted by any known method similar to freshly blown when blowing the pig iron.

Die beschriebene Technologie des Erhitzens des festen metallischen Einsatzes im Konverter ermöglicht es, den Anteil des festen metallischen Einsatzes in der Gesamtmasse der Metallcharge des Konverters durch Erhitzen des in den Konverter eingetragenen festen metallischen Einsatzes beim Verbrennen von Brennstoff zu erhöhen.The described technology of heating the solid metallic use in the converter allows the share the solid metallic insert in the total mass of the metal batch of the converter by heating it in the converter registered solid metallic insert when burning of increasing fuel.

Der durch die Bodenwinddüsen geblasene Sauerstoff oxydiert und schmelzt jedoch die Oberfläche des metallischen Einsatzes in der um die Winddüsen gelegenen Zone, wodurch eine aus Metall und oxydierter Schlacke bestehende flüssige Phase entsteht. Im Ergebnis kann es beim Eingießen des Roheisens zum Auswurf flüssiger Komponenten aus dem Konverter kommen.The oxygen blown through the bottom wind vents oxidizes  and however melts the surface of the metallic Use in the zone around the wind vents, whereby a liquid consisting of metal and oxidized slag Phase arises. As a result, when pouring the Pig iron for ejecting liquid components from the converter come.

Außerdem muß erwähnt werden, daß am äußeren Rand, besonders im unteren Teil des in den Konverter eingetragenen metallischen Einsatzes eine Zone mit niedriger Temperatur (500 bis 700°C) entsteht, wohin die heißen Verbrennungsprodukte des Brennstoffs nur schwer gelangen. Das bedeutet, daß der metallische Einsatz ungleichmäßig durchwärmt wird, weshalb keine wesentliche Erhöhung des Anteils des festen metallischen Einsatzes in der Gesamtmasse der Metallcharge des Konverters erzielt werden kann.It must also be mentioned that on the outer edge, especially in the lower part of the entered in the converter metallic insert a low temperature zone (500 to 700 ° C) arises where the hot combustion products go of fuel is difficult to get. It means that the metallic insert is heated unevenly, which is why no significant increase in the proportion of solid metallic Use in the total mass of the metal batch of Converter can be achieved.

Es ist auch ein weiteres Verfahren zur Erzeugung von Stahl bekannt (DE-A, 28 16 543).Another method of producing steel is also known (DE-A, 28 16 543).

Dieses Verfahren wird in einem Sauerstoff-Blaskonverter durchgeführt, der mit Boden- und Seitenwinddüsen ausgerüstet ist, die eine Konstruktion vom Typ "Rohr im Rohr" darstellen. Durch diese Winddüse leitet man Sauerstoff über den Mittelkanal und einen flüssigen oder gasförmigen, aus Kohlenwasserstoffen bestehenden Brennstoff über den äußeren Kanal. Es ist auch die Verwendung eines festen kohlenstoffhaltigen Brennstoffs vorgesehen.This process is done in an oxygen blow converter carried out, which is equipped with floor and cross wind jets which represent a construction of the type "pipe in pipe". Through this wind nozzle, oxygen is conducted over the Middle channel and a liquid or gaseous, made of hydrocarbons existing fuel through the outer channel. It is also the use of a solid carbonaceous one Fuel provided.

Das Verfahren besteht in der Durchführung folgender technologischer Arbeitsgänge: Aufgeben eines festen metallischen Einsatzes, z. B. Alteisen, und dessen anschließendes Erhitzen bis auf 1100°C durch Verbrennen eines gasförmigen oder flüssigen, aus Kohlenwasserstoffen bestehenden Brennstoffs, der im Laufe des Prozesses in einem Sauerstoffstrom zugeführt wird. Danach gießt man flüssiges Roheisen ein und bringt den festen metallischen Einsatz zum Schmelzen mit anschließendem Frischen der Eisen-Kohlenstoff-Schmelze nach einem beliebigen bekannten Verfahren ähnlich wie beim Durchblasen des Roheisens.The procedure is to do the following technological operations: abandoning a solid metallic Use, e.g. B. scrap iron, and its subsequent Heat up to 1100 ° C by burning a gaseous one or liquid hydrocarbon fuel, which in the course of the process in an oxygen stream is fed. Then pour molten pig iron and brings the solid metallic insert to melt with subsequent refreshing of the iron-carbon melt by any known method similar to that of Blow through the pig iron.

Die heißen Verbrennungsprodukte des Brennstoffs durchdringen die Masse des festen metallischen Einsatzes vor allem in Richtung von unten nach oben und gewährleisten eine ausreichend gute Durchwärmung dieser Masse.Penetrate the hot combustion products of the fuel the mass of the solid metallic insert especially in  Direction from the bottom up and ensure a sufficient good warming of this mass.

Dieses Verfahren ist durch einen erhöhten thermischen Wirkungsgrad und ein schnelles Erhitzen des metallischen Einsatzes gekennzeichnet, was durch einen guten Kontakt zwischen der Oberfläche der Masse des festen metallischen Einsatzes und den heißen Verbrennungsprodukten des Brennstoffs erzielt wird. Den metallischen Einsatz erhitzt man jedoch nur bis auf eine nicht über 1100°C liegende Temperatur, damit keine erheblichen Mengen der flüssigen Phase entstehen.This process is enhanced by a thermal Efficiency and rapid heating of the metallic Use characterized by good contact between the surface of the mass of solid metallic Use and the hot combustion products of the fuel is achieved. However, the metallic insert is heated only up to a temperature not above 1100 ° C, so no significant amounts of the liquid phase arise.

Dieses Verfahren gewährleistet ein schnelles Erhitzen des festen metallischen Einsatzes und ermöglicht die Verarbeitung bis 50% festen metallischen Einsatzes in der Gesamtmenge der Metallcharge beim Schmelzen im Konverter.This process ensures rapid heating solid metallic insert and enables processing up to 50% solid metallic insert in the total amount the metal batch when melting in the converter.

Dieses Verfahren gewährleistet jedoch kein gleichmäßiges Durchwärmen des in den Konverter aufgegebenen festen metallischen Einsatzes. Das Erhitzen des in der Randzone des Metallbades und besonders in deren unterem Teil gelegenen metallischen Einsatzes verläuft schlechter und geht langsamer vonstatten als das Erhitzen des in der Mitte des Metallbades befindlichen metallischen Einsatzes. Das Temperaturgefälle erreicht hierbei erhebliche Werte. So kann z. B. die Temperatur in der Mitte des Metallbades des Konverters Werte erreichen, bei denen der feste metallische Einsatz schmilzt, während am Rand des Bades der metallische Einsatz nur bis auf 500 bis 700°C erwärmt wird.However, this procedure does not guarantee a uniform one Soak the solid fed into the converter metallic insert. Heating the in the peripheral zone of the metal bath and especially in its lower part metallic insert runs worse and is slower than heating the one in the middle the metal insert located in the metal bath. The The temperature gradient reaches considerable values. So can e.g. B. the temperature in the middle of the metal bath of the converter Reach values where the solid metallic Insert melts while at the edge of the bath the metallic Use only heated up to 500 to 700 ° C.

Der durch die Bodenwinddüsen eingeblasene Sauerstoff oxydiert und schmilzt die Oberfläche des metallischen Einsatzes in der um die Winddüsen gelegenen Zone, was zur Entstehung der flüssigen Phase führt. Die Entstehung der flüssigen Phase in den um die Winddüsen gelegenen Zonen des Konverters verursacht Auswürfe von Schlacks und Metall aus dem Konverter beim Eingießen von Roheisen.The oxygen blown in through the floor wind vents oxidizes and melts the surface of the metallic insert in the zone around the wind vents, which led to the emergence leads the liquid phase. The emergence of the liquid Phase in the converter zones around the wind vents causes ejection of slag and metal from the Converter when pouring pig iron.

Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zum Erschmelzen von Stahl in einem Sauerstoff-Blaskonverter aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen bereitzustellen, das durch ein stärkeres und gleichmäßigeres Erhitzen der festen metallischen, eisenhaltigen Stoffe und durch Steuerung dieses Erhitzungsvorgangs eine Erhöhung des Anteils des festen metallischen Einsatzes in der Metallcharge ermöglicht und Auswürfe von Metall und Schlacke aus dem Konverter beim Eingießen von flüssigem Roheisen verhindert.The invention has for its object a method for melting steel in an oxygen blow converter made of solid metallic, ferrous and liquid materials To provide pig iron by a stronger and more uniform Heating the solid metallic, ferrous  Fabrics and by controlling this heating process a Increase in the proportion of solid metallic insert in the metal batch enables and ejection of metal and Slag from the converter when pouring liquid Pig iron prevented.

Diese Aufgabe wird dadurch gelöst, daß in einem Verfahren zum Erschmelzen von Stahl in einem Sauerstoff-Blaskonverter aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen, das im Aufgeben der metallischen, eisenhaltigen Stoffe, deren Erhitzen durch Verbrennen eines aus Kohlenwasserstoffen bestehenden und eines kohlenstoffhaltigen Brennstoffs, die nacheinander im Arbeitsablauf im Strom eines sauerstoffhaltigen Gases zugeführt werden, das in den Konverter von unten nach oben und von oben nach unten eingeführt wird, im anschließenden Eingießen von flüssigem Roheisen und im Ausgaren der entstandenen Schmelze bis zum Erreichen der vorgegebenen chemischen Zusammensetzung besteht, erfindungsgemäß die festen metallischen, eisenhaltigen Stoffe bis auf eine der Schmelztemperatur der eisenhaltigen Stoffe nahe, jedoch darunter liegende Temperatur erhitzt und vor dem Eingießen des flüssigen Roheisens diese Stoffe zum Zweck des Homogenisierens durch Zuführen eines neutralen Gases im von unten nach oben gerichteten Strom des sauerstoffhaltigen Gases, durchblasen werden, wobei die von unten nach oben gerichtet Zufuhr des aus Kohlenwasserstoffen bestehenden Brennstoffs bis auf 1,5 bis 6,0 kg Brennstoff je Tonne der festen metallischen, eisenhaltigen Stoffe gedrosselt wird.This object is achieved in that in one process for melting steel in an oxygen blow converter made of solid metallic, ferrous materials and molten pig iron, which in giving up the metallic, ferrous Substances whose heating by burning one out Existing hydrocarbons and one containing carbon Fuel that flows sequentially in the flow of electricity be supplied with an oxygen-containing gas, which in the Bottom to top and top to bottom converters introduced is, in the subsequent pouring of liquid Pig iron and in the course of curing the resulting melt until The specified chemical composition has been reached, according to the invention the solid metallic, iron-containing Substances up to one of the melting temperature of the iron-containing Close to fabrics, but lower temperature heated and before pouring the molten pig iron these substances for the purpose of homogenization by feeding a neutral gas in the bottom-up direction Stream of the oxygen-containing gas to be blown through, being the bottom-up feed of the Hydrocarbon existing fuel up to 1.5 to 6.0 kg of fuel per ton of solid metallic, iron-containing substances is throttled.

Die Durchführung der Erfindung ermöglicht eine Steuerung der Temperaturführung beim Erhitzen des metallischen Einsatzes. Beim Verbrennen des Brennstoffs im Sauerstoff des sauerstoffhaltigen Gases beträgt die Temperatur der Flamme 1800 bis 2300°C in Abhängigkeit von der Art des Brennstoffs und den Bedingungen, unter denen er brennt. Wenn dem Sauerstoff ein neutrales Gas zugesetzt wird, sinkt die Brenntemperatur der Flamme, wobei die Temperatur der Flamme um so mehr sinkt, je höher der Gehalt des neutralen Gases ist und umgekehrt. Die Temperatur der Flamme kann bei Zufuhr eines neutralen Gases bis auf 1100 bis 1300°C sinken. Deshalb kommt es bei dem zum Zweck des Homogenisierens durchgeführten Durchblasen von unten mit einem neutralen Gas oder dessen Gemisch mit sauerstoffhaltigen Komponenten im Beisein von Erdgas nicht zum Schmelzen des metallischen Einsatzes und zur Entstehung der flüssigen Phase, und die vorher bis zu diesem Zeitpunkt entstandene Schmelze erstarrt zur festen Phase.The implementation of the invention enables control temperature control when heating the metallic insert. When burning the fuel in the oxygen of the oxygen-containing Gases is the temperature of the flame 1800 to 2300 ° C depending on the type of fuel and the conditions under which it burns. If the oxygen If a neutral gas is added, the firing temperature drops of the flame, the temperature of the flame all the more the lower the higher the content of neutral gas, and vice versa. The temperature of the flame can be increased when a  neutral gas drop to 1100 to 1300 ° C. That's why it comes to that carried out for the purpose of homogenization Blow through from below with a neutral gas or its Mixture with oxygen-containing components in the presence of natural gas not for melting the metallic insert and to the formation of the liquid phase, and previously up to at this point, the melt solidifies Phase.

Außerdem vergrößert sich bei der Zuführung von Sauerstoff im Gemisch mit einem neutralen Gas das Volumen der Brennprodukte um ein Mehrfaches infolge des Zusatzes des neutralen Gases, wodurch der Druck der Verbrennungsprodukte in der unteren Zone des in den Konverter eingetragenen metallischen Einsatzes zunimmt. Dabei erwärmt sich das zusammen mit dem Sauerstoff zugeführte neutrale Gas in der um die Winddüsen gelegenen Zone bis auf die Temperatur des umgebenden Mediums. Im Ergebnis sind die aus Brennprodukten des Brennstoffs und aus dem neutralen Gas bestehenden heißen Gase auf ihrem Weg zur Konverteröffnung bestrebt, in alle Hohl- und Zwischenräume zwischen den Stücken des metallischen Einsatzes einzudringen, wodurch der in den Konverter aufgegebene metallische Einsatz schneller und gleichmäßiger sowohl in der Breite, als auch in der Höhe des Konverters erhitzt wird. Das bedeutet, daß das zum Zweck des Homogenisierens durchgeführte Durchblasen ein gleichmäßiges Erhitzen der gesamten Masse des metallischen Einsatzes bis auf die maximal mögliche Temperatur ohne Bildung der flüssigen Phase ermöglicht. Dadurch kann der Anteil des metallischen Einsatzes beim Schmelzen im Konverter bis auf 60 bis 70% erhöht werden.In addition, the supply of oxygen increases mixed with a neutral gas, the volume of the combustion products by a multiple due to the addition of the neutral Gases, which causes the pressure of the combustion products in the lower zone of the metallic in the converter Stake increases. This heats up together with neutral gas supplied to the oxygen around the wind vents located zone up to the temperature of the surrounding medium. As a result, they are made from the fuel's combustion products and hot gases consisting of the neutral gas endeavors to open the converter, in all hollow and Gaps between the pieces of the metallic insert penetrate, causing the input into the converter metallic use faster and more evenly both in the Width, as well as the height of the converter is heated. This means that this is done for the purpose of homogenization Blow through an even heating of the whole Mass of the metallic insert up to the maximum possible temperature without the formation of the liquid phase. As a result, the proportion of metallic insert increased to 60 to 70% when melting in the converter will.

Die optimale Menge des von unten nach oben durch die Bodenwinddüsen während des zum Zweck des Homogenisierens durchgeführten Durchblasens zugeführten Einheitsbrennstoffs beträgt 1,5 bis 6,0 kg je Tonne fester metallischer, eisenhaltiger Stoffe.The optimal amount of the bottom up by the Bottom wind nozzles during homogenizing by blowing supplied fuel is 1.5 to 6.0 kg per ton of solid metallic, iron-containing Fabrics.

Wenn weniger Brennstoff zugeführt wird, ist der Effekt des Homogenisierens nicht hoch; dieser Vorgang übt dann keinen wesentlichen Einfluß auf den Verlauf des Erhitzens des metallischen Einsatzes auf.If less fuel is added, the effect is homogenization not high; then this process does not practice significant influence on the course of the heating of the  metallic insert.

Der Verbrauch von mehr als 6 kg Brennstoff pro Tonne fester metallischer, eisenhaltiger Stoffe während des Durchblasens zum Zweck des Homogenisierens ist unrationell weil dabei ein Temperaturausgleich eintritt, in dessen Ergebnis die durch die Abgase verursachten Wärmeverluste wesentlich zunehmen und der Prozeß sich unwirtschaftlich gestaltet. Außerdem kühlt sich bei diesem Brennstoffverbrauch der metallische Einsatz stark ab, wodurch sich die Wärmebilanz des Schmelzprozesses verschlechtert.The consumption of more than 6 kg of fuel per ton of solid metallic ferrous materials during blowing through for the purpose of homogenization is inefficient because there is a temperature equalization in which Result the heat losses caused by the exhaust gases increase significantly and the process becomes uneconomical designed. This fuel consumption also cools down the metallic insert drops off significantly the heat balance of the melting process deteriorates.

Es ist zweckmäßig, Stickstoff als neutrales Gas zu verwenden, wobei man Stickstoff in Verbindung mit sauerstoffhaltigen Komponenten verwenden kann. Stickstoff ist ein leicht zugängliches und billiges neutrales Gas.It is advisable to use nitrogen as the neutral gas, taking nitrogen in conjunction with oxygen-containing Can use components. Nitrogen is a easily accessible and cheap neutral gas.

Es ist zweckmäßig, daß die Menge der sauerstoffhaltigen Komponenten im Gemisch mit Stickstoff 50 bis 100% der theoretisch für ein vollständiges Verbrennen des von unten nach oben zugeführten Brennstoffs notwenigen Menge ausmacht.It is appropriate that the amount of oxygen-containing Components mixed with nitrogen 50 to 100% of theoretically for a complete burning of the bottom amount required for the fuel supplied above.

Die Zuführung sauerstoffhaltiger Komponenten zusammen mit Stickstoff in einer größeren Menge als die theoretisch für ein vollständiges Verbrennen des Brennstoffs notwenige Menge ist unerwünscht, da die überschüssige Sauerstoffmenge zum Oxydieren des Eisens des metallischen Einsatzes verbraucht wird, was zu verstärkter Bildung von Schlacke und von Eisenoxiden in der Schlacke und zu möglichen Auswürfen von Schlacke und Metall beim Eingießen des Roheisens führt.The supply of oxygen-containing components together with nitrogen in a larger amount than that theoretically for a complete combustion of the fuel Amount is undesirable because the excess amount of oxygen for oxidizing the iron of the metallic insert is consumed, leading to increased formation of slag and of iron oxides in the slag and possible ejection of slag and metal when pouring the pig iron.

Die Zuführung sauerstoffhaltiger Komponenten in einer Menge von weniger als 50% der für das vollkommene Verbrennen des Brennstoffs notwenigen Menge ist unrationell, weil das zum Zweck des Homogenisierens durchgeführte Durchblasen ohne Wirkung bleibt.The supply of oxygen-containing components in one Amount less than 50% for perfect burning amount of fuel necessary is inefficient because blowing through for the purpose of homogenization remains without effect.

Es ist erwünscht, daß gleichzeitig mit dem zum Zweck des Homogenisierens durchgeführten Durchblasen auf die Oberfläche der festen metallischen, eisenhaltigen Stoffe calciumhaltige und kohlenstoffhaltige Stoffe gegeben werden.It is desirable that at the same time with the purpose of the blown through the surface of solid metallic, ferrous substances containing calcium and carbonaceous substances.

Als calciumhaltige und kohlenstoffhaltige Stoffe kann man Kalk und Kohle verwenden.As calcium-containing and carbon-containing substances can to use lime and coal.

Eine wärmeisolierende Schicht von Kalk und Kohle vermeidet größere Wärmeverluste und trägt zu einer gleichmäßigen Verteilung der Verbrennungsprodukte in horizontaler Richtung über die gesamte Masse des metallischen Einsatzes bei. Gleichzeitig passivieren Kalk und Kohle die Abschnitte des oxydierten Einsatzes, da die Eisenoxide in den Kalk eindringen (aufgesaugt werden) oder im Beisein von Kohle reduziert werden. Auf diese Weise begünstigt die Anwendung von Kohle und Kalk ein gleichmäßiges Erhitzen des Alteisens und schwächt den Oxydationsprozeß des metallischen Einsatzes deren Erhitzen ab, wodurch im Ergebnis Auswürfe flüssiger Komponenten aus dem Konverter beim Eingießen von Roheisen vermieden werden.Avoids a heat-insulating layer of lime and coal  greater heat loss and contributes to an even Distribution of the combustion products in the horizontal direction over the entire mass of the metallic insert. At the same time, lime and coal passivate the sections of the oxidized use, since the iron oxides penetrate into the lime (be sucked up) or reduced in the presence of coal will. This favors the use of coal and lime an even heating of the scrap iron and weakens the oxidation process of the metallic insert Heat off, resulting in ejection of liquid components avoided from the converter when pouring pig iron will.

Es empfiehlt sich, gleichzeitig mit dem zum Zweck des Homogenisierens durchgeführten Durchblasen den Konverter mit den in ihn eingetragenen festen metallischen, eisenhaltigen Stoffen periodisch bis zur maximal möglichen Neigung zu kippen.It is recommended to use the for the purpose of Blowing performed homogenizing the converter with the solid metallic, ferrous ones entered in it Substances periodically up to the maximum possible inclination tilt.

Bei periodischem Neigen des Konverters verbessert sich der Kontakt zwischen dem festen und dem geschmolzenen flüssigen Teil des Konverterinhalts. Die entstandene Schmelze fließt bei dem Neigen des Konverters von den Stellen, an denen sie sich angesammelt hat, über die Konverterwände und vermischt sich mit den Stücken des metallischen Einsatzes, wobei sie auf die letztere ihre Wärme überträgt. Das führt zum Erstarren der Schmelze, nachdem sie ihre Wärme an den metallischen Einsatz abgegeben hat. Außerdem kommt es zu einem Temperaturausgleich in der gesamten Masse des metallischen Einsatzes. Auf diese Weise ermöglicht diese Empfehlung eine Vergrößerung des Anteils des metallischen Einsatzes beim Schmelzen im Konverter und verhindert Auswürfe von Schlacke und Metall beim Eingießen des Roheisens.Improved for periodic tilting of the converter the contact between the solid and the melted liquid part of the converter content. The resulting melt flows from the points when the converter is tilted which it has accumulated, via the converter walls and mixes with the pieces of the metallic insert, transferring its heat to the latter. Leading to solidify the melt after it has transferred its heat to the has given metallic insert. There is also a Temperature compensation in the entire mass of the metallic Use. In this way, this recommendation enables an increase in the proportion of metallic insert when melting in the converter and prevents ejection of Slag and metal pouring the pig iron.

Es ist zweckmäßig, nach dem zum Zweck des Homogenisierens durchgeführten Durchblasen, aber noch vor dem Eingießen des Roheisens die flüssige Schlacke aus dem Konverter abzuziehen. Dadurch werden Auswürfe von Schlacke und Metall beim Eingießen des Roheisens vermieden.It is expedient, after that for the purpose of homogenization performed blowing, but before pouring of the pig iron to withdraw the liquid slag from the converter. As a result, slag and metal are ejected from the Pouring the pig iron avoided.

Zur Erläuterung der Erfindung werden im folgenden konkrete Durchführungsbeispiele beschrieben. To explain the invention, the following are concrete Implementation examples described.  

Das Verfahren zum Erschmelzen von Stahl wird in einem Sauerstoff-Blaskonverter durchgeführt, der mit Boden- und Seitenwinddüsen vom Typ "Rohr im Rohr" ausgerüstet ist. Durch die Mittelkanäle dieser Winddüsen wird Sauerstoff geleitet und durch die Außenkanäle ein aus Kohlenwasserstoffen bestehender Brennstoff. Die Seitenwinddüsen können sowohl über, als auch unter dem Niveau des Metallbades angebracht werden. Vorgesehen ist die Zuführung von Sauerstoff durch eine wassergekühle Oberwinddüse und auch die Möglichkeit der Zuführung eines beliebigen bekannten Brennstoffes durch diese Winddüse.The process for melting steel is in one Oxygen blowing converter carried out with bottom and Cross wind nozzles of the type "tube in tube" is equipped. By oxygen is conducted through the center channels of these wind vents and a hydrocarbon one through the outer channels Fuel. The side wind nozzles can be as well as below the level of the metal bath. The supply of oxygen is provided by a water-cooled Upper wind nozzle and also the possibility of feeding any known fuel through this Wind nozzle.

Das Verfahren zum Erschmelzen von Stahl aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen geht wie folgt vor sich.The process for melting steel from solid metallic, ferrous materials and liquid pig iron proceeds as follows.

Beim Beschicken werden in den Konverter feste metallische, eisenhaltige Stoffe und flüssiges Roheisen aufgegeben. Als feste metallische, eisenhaltige Stoffe können nach dem erfindungsgemäßen Verfahren Alteisen, Schrott, metallische Abfälle von Walzwerken und Stahlgießereien, Metallpellets, Eisenschwamm u. ä. zu Stahl verarbeitet werden.When loading, solid metallic, iron-containing substances and liquid pig iron abandoned. As solid metallic, iron-containing substances can after Process according to the invention scrap iron, scrap, metallic Waste from rolling mills and steel foundries, metal pellets, Sponge iron Ä. are processed into steel.

Als Brennstoff verwendet man vorrangig gasförmige Kohlenwasserstoffe wie Erdgas, Metahn, Propan, Butan und auch flüssige Kohlenwasserstoffe wie Heizöl, Rohöl, Dieselöl.The main fuel used is gaseous hydrocarbons like natural gas, metahn, propane, butane and also liquid hydrocarbons such as heating oil, crude oil, diesel oil.

Außerdem kann als Brennstoff auch ein fester kohlenstoffhaltiger Brennstoff verwendet werden wie z. B. Koks, Steinkohle, Braunkohle u. ä. sowie Kohlenstaub.In addition, a solid carbon-containing fuel can also be used Fuel can be used such. B. coke, hard coal, Lignite and Ä. and coal dust.

Der Prozeß des Stahlschmelzens aus festen eisenhaltigen Stoffen, z. B. aus Alteisen, und flüssigem Roheisen in einem Sauerstoff-Blaskonverter umfaßt mehrere Perioden, und zwar die Beschickung des Konverters mit Alteisen, das Erhitzen des Alteisens, das Durchblasen zum Zweck des Homogenisierens, das Eingießen des flüssigen Roheisens, das Schmelzen und das anschließende Frischen (d. h. das Ausgaren der entstandenen Schmelze bis zum Erreichen der vorgegebenen chemischen Zusammensetzung).The process of melting steel from solid ferrous Fabrics, e.g. B. from scrap iron and liquid pig iron in one Oxygen blow converter spans several periods loading the converter with scrap iron, heating of scrap iron, blowing through for the purpose of homogenizing, pouring the molten pig iron, melting and the subsequent refreshing (i.e. the cooking of the resulting Melt until the specified chemical is reached Composition).

Das Alteisen wird durch die Wärme erhitzt, die beim Verbrennen des aus Kohlenwasserstoffen bestehenden Brennstoffs entsteht, der durch die Boden- und Seitenwinddüsen und die wassergekühlte Oberwinddüse in einem durch die gleichen Winddüsen zugeleiteten sauerstoffhaltigen Gas zugeführt wird. Im Verlauf des Erhitzens schüttet man in den Konverter auf das Alteisen periodisch einen festen kohlenstoffhaltigen Brennstoff.The scrap iron is heated by the heat generated by the Burn the hydrocarbon fuel arises through the bottom and cross wind jets  and the water-cooled headwind nozzle in one by the same Oxygen-containing gas fed to wind nozzles becomes. In the course of heating, pour into the converter periodically a solid carbon on the scrap iron Fuel.

Nach dem Erhitzen des Alteisens bis auf eine nahe der Schmelztemperatur des Alteisens, aber darunter liegende Temperatur wird das Durchblasen zum Zweck des Homogenisierens vorgenommen. Bei dem zum Zweck des Homogenisierens durchgeführten Durchblasen begrenzt man den Verbrauch des aus Kohlenwasserstoffen bestehenden, von unten nach oben zugeführten Brennstoffs auf 1,5 bis 6,0 kg Brennstoff je Tonne Alteisen.After heating the scrap iron to close to one Melting temperature of the scrap iron, but below that Temperature is blowing for the purpose of homogenization performed. For the purpose of homogenization performed blowing one limits the consumption of the consisting of hydrocarbons, fed from bottom to top Fuel to 1.5 to 6.0 kg of fuel per ton of scrap iron.

Als Oxydationsmittel leitet man von unten nach oben sauerstoffhaltige Komponenten im Gemisch mit Stickstoff in einer Menge von 50 bis 100% des theoretisch für das vollkommene Verbrennen des von unten zugeleiteten gasförmigen Brennstoffs notwenigen Verbrauchs zu.As an oxidizing agent, oxygen-containing substances are passed from bottom to top Components mixed with nitrogen in one Amount from 50 to 100% of the theoretical for the perfect Burning the gaseous fuel supplied from below necessary consumption.

Im Verlauf des zum Zweck des Homogenisierens durchgeführten Durchblasens wird der Konverter periodisch bis zur maximal möglichen Neigung gekippt.During the course of homogenization The converter is blown periodically until tilted to the maximum possible inclination.

Vor dem Beginn des zum Zweck des Homogenisierens durchgeführten Durchblasens gibt man auf die Oberfläche des in den Konverter eingetragenen Alteisens kohlenstoffhaltige und calciumhaltige Stoffe.Before starting for the purpose of homogenization Blow through is given to the surface of the in the converter of old iron containing carbon and calcium-containing substances.

Nach Beendigung des zum Zweck des Homogenisierens durchgeführten Durchblasens wird vor dem Eingießen des Roheisens die flüssige Schlacke aus dem Konverter abgezogen.After completion of the performed for the purpose of homogenization Blow-through is carried out before pouring the pig iron the liquid slag is withdrawn from the converter.

Die Durchführung der Erfindung äußert sich in der Steuerung der Temperaturführung beim Erhitzen des Alteisens.The implementation of the invention manifests itself in the control the temperature control when heating the scrap iron.

Beim Erhitzen des Alteisens bis auf eine nahe seiner Schmelztemperatur, aber darunter liegende Temperatur bildet sich eine flüssige Phase in erheblicher Menge, die aus flüssigem Metall und flüssiger Schlacke besteht.When heating the scrap iron to near its Melting temperature, but lower temperature a liquid phase forms in considerable quantities, which consists of liquid metal and liquid slag.

Die Verwendung der genannten gasförmigen Reaktanten in den genannten Grenzen gewährleistet bei dem zum Zweck des Homogenisierens durchgeführten Durchblasen ein gleichmäßiges Erhitzen des Alteisens in der gesamten Masse und auch die Beseitigung der flüssigen Phase, die sich in der die Bodenwinddüsen umgebenden Zone bildet.The use of the gaseous reactants mentioned in guarantees the limits mentioned for the purpose of Blowing performed homogenizing a uniform Heating the scrap iron in the whole mass and also the  Elimination of the liquid phase in the bottom wind vents surrounding zone forms.

Beim Kontakt mit der flüssigen Phase erfüllen die zugeführten Gase zwei Aufgaben: erstens entziehen sie der Schmelze die Wärme, wodurch die flüssige Phase zur festen Phase erstarrt, und zweitens übertragen die heißen Gase die aufgenommene Wärme an kältere Abschnitte des in den Konverter eingetragenen Alteisens, was zu einem Temperaturausgleich in der gesamten Masse des Alteisens beiträgt.When in contact with the liquid phase, the supplied ones meet Gases perform two tasks: first, they evade the Melt the heat, causing the liquid phase to solid Phase solidifies, and secondly, the hot gases transmit the heat absorbed to colder sections of the converter registered scrap iron, resulting in temperature compensation contributes to the entire mass of scrap iron.

Außerdem gewährleistet das zum Zweck des Homogenisierens durchgeführte Durchblasen ein schnelleres Erhitzen des Alteisens auf Grund der Tatsache, daß bei Verwendung des erfindungsgemäßen Verfahrens eine beliebig hohe, zum Schmelzen des Alteisens notwendige Temperatur verwendet werden kann, ohne die Entstehung von flüssiger Phase zu befürchten, die zu Auswürfen aus dem Konverter führt.This also ensures for the purpose of homogenization by blowing a faster heating of the Alteisens due to the fact that when using the invention Process any height, for melting the temperature of the scrap iron can be used, without fear of the formation of a liquid phase, the leads to ejections from the converter.

Auf diese Weise ermöglicht das erfindungsgemäße Verfahren eine Erhöhung des Anteils des festen metallischen Einsatzes bis auf 60 bis 70% in der Gesamtmenge der Metallcharge und die Beseitigung der Auswürfe flüssiger Schmelzkomponenten beim Eingießen des Roheisens.In this way, the method according to the invention enables an increase in the proportion of solid metallic insert up to 60 to 70% of the total amount of the metal batch and the elimination of the ejection of liquid melt components when pouring the pig iron.

Beispiel 1Example 1

In einen 10-t-Konverter, der mit Boden- und Seitenwinddüsen für Brennstoff und Sauerstoff und einer wassergekühlten Oberwinddüse für Sauerstoff ausgerüstet ist, gibt man 0,70 t Kalk und 6,0 t Alteisen auf. Das Erhitzen des Alteisens geschieht durch Zuführung von 15 bis 20 m³/min Erdgas durch die Bodenwinddüsen. Durch die Seitenwinddüsen bläst man 5 bis 10 m³/min Sauerstoff und 2,5 bis 5,0 m³ Erdgas. Die Zuführung von Sauerstoff durch die Oberwinddüse reguliert man in den Grenzen von 10 bis 15 m³/min. Zwei Minuten nach Beginn des Erhitzens gibt man in den Konverter 0,35 t Kohlenklein aus Steinkohle auf.In a 10 t converter with bottom and side wind jets for fuel and oxygen and a water-cooled Upwind nozzle is equipped for oxygen 0.70 t lime and 6.0 t scrap iron. Heating the scrap iron happens by supplying 15 to 20 m³ / min natural gas through the bottom wind vents. Through the side wind vents one blows 5 to 10 m³ / min oxygen and 2.5 to 5.0 m³ natural gas. The supply of oxygen through the headwind nozzle is regulated one within the limits of 10 to 15 m³ / min. Two minutes after the start of heating, 0.35 t are added to the converter Small coal from hard coal.

10 Minuten nach Beginn des Erhitzens wird ein Durchblasen zum Zweck des Homogenisierens vorgenommen. Von unten leitet man durch die Bodenwinddüsen: 2,34 m³/min Erdgas, 1,63 m³/min Sauerstoff und 6,28 m³/min Stickstoff.A blow will blow 10 minutes after the start of heating made for the purpose of homogenization. From underneath one passes through the bottom wind vents: 2.34 m³ / min natural gas, 1.63 m³ / min oxygen and 6.28 m³ / min nitrogen.

Der Verbrauch des von oben zugeführten Sauerstoffs ändert sich nicht.The consumption of the oxygen supplied from above  does not change.

Das zum Zweck des Homogenisierens durchgeführte Durchblasen dauert zwei Minuten, danach wird 4,1 t flüssiges Roheisen eingegossen.The blow-through performed for the purpose of homogenization takes two minutes, after which 4.1 t of molten pig iron is used poured.

Während des Schmelzens des Alteisens und des Frischens der Schmelze leitet man durch die Bodenwindformen 15 bis 20 m³/min Sauerstoff und 2,5 bis 3,0 m³/min Erdgas; durch die Seitenwinddüsen - 5 m³/min Sauerstoff und 2 m³/min Erdgas und durch die Oberwinddüse - 10 bis 15 m³ Sauerstoff. Das Schmelzen des Alteisens und das Frischen der Schmelze dauert 30,5 min. Die Gesamtzeit des Durchblasens beträgt 42,5 min. Nach Beendigung des Durchblasens hat das Metall eine Temperatur von 1630°C. Der fertige Stahl hat folgende Zusammensetzung: 0,07% C; 0,05% Mn; 0,009% P; 0,035% S; der Rest ist Eisen.During the melting of the scrap iron and the freshening the melt is passed through the bottom wind forms 15 to 20 m³ / min oxygen and 2.5 to 3.0 m³ / min natural gas; by the side wind nozzles - 5 m³ / min oxygen and 2 m³ / min natural gas and through the headwind nozzle - 10 to 15 m³ of oxygen. Melting the old iron and freshening the melt takes 30.5 min. The total blowing time is 42.5 min. After the blowing has finished the metal a temperature of 1630 ° C. The finished steel has the following Composition: 0.07% C; 0.05% Mn; 0.009% P; 0.035% S; the The rest is iron.

Es wurde 8,6 t flüssigen Stahls gewonnen.8.6 tons of liquid steel were obtained.

Beispiel 2Example 2

In einen 10-t-Konverter gibt man 0,7 t Kalk und 6,1 t Alteisen auf. Die Windführung während des Erhitzens, die Schmelzführung und der Gang des Frischens der Schmelze verläuft ähnlich wie im Beispiel 1. Während des Erhitzens wurde in den Konverter 350 kg Kohlenklein aus Steinkohle gegeben.0.7 t lime and 6.1 t are placed in a 10 t converter Scrap iron on. The wind direction during heating, the Melt guidance and the course of the melting of the melt runs Similar to example 1. During heating placed in the converter 350 kg of small coal from hard coal.

Während des zum Zweck des Homogenisierens durchgeführten Durchblasens wird zugeführt: von unten durch die Bodenwinddüsen 2,38 m³/min Erdgas, 1,66 m³/min Sauerstoff und 6,24 m³/min Sauerstoff. Das Durchblasen dauert drei Minuten.During the run for the purpose of homogenization Blow through is supplied: from below through the Floor wind nozzles 2.38 m³ / min natural gas, 1.66 m³ / min oxygen and 6.24 m³ / min oxygen. The blowing takes three Minutes.

Nach dem zum Zweck des Homogenisierens durchgeführten Durchblasen wird 3,9 t flüssiges Roheisen zugegossen. Das Schmelzen des metallischen Einsatzes und das Frischen der Schmelze dauert 28,5 min. Die Gesamtdauer des Durchblasens beträgt 41,5 min. Nach Beendigung des Durchblasens hat das Metall eine Temperatur von 1625°C. Der fertige Stahl hat folgende Zusammensetzung: 0,10% C; 0,09% Mn; 0,010% P; 0,033% S; der Rest ist Eisen.After that carried out for the purpose of homogenization 3.9 t of molten pig iron are poured in by blowing. The Melting the metallic insert and freshening up the The melt lasts 28.5 min. The total duration of the blow through is 41.5 min. After blowing has finished, that has Metal a temperature of 1625 ° C. The finished steel has the following Composition: 0.10% C; 0.09% Mn; 0.010% P; 0.033% S; the rest is iron.

Es wurde 8,6 t flüssigen Stahls gewonnen. 8.6 tons of liquid steel were obtained.  

Beispiel 3Example 3

In einen 10-t-Konverter gibt man 0,7 t Kalt und 5,9 t Alteisen auf. Während des Erhitzens gibt man in den Konverter 350 kg Kohlenklein aus Steinkohle. Während des zum Zweck des Homogenisierens durchgeführten Durchblasens wird von unten 6,1 m³/min Erdgas, 4,27 m³/min Sauerstoff und 16,1 m³/min Stickstoff zugeführt. Dann gießt man 4,1 t flüssiges Roheisen in den Konverter.0.7 t cold and 5.9 t are placed in a 10 t converter Scrap iron on. While heating, put in the converter 350 kg small coal from hard coal. During the Purge is carried out for the purpose of homogenization from below 6.1 m³ / min natural gas, 4.27 m³ / min oxygen and 16.1 m³ / min nitrogen supplied. Then pour 4.1 t of liquid Pig iron in the converter.

Das Schmelzen des metallischen Einsatzes und das Frischen der Schmelze dauert 27 min. Die Gesamtzeit des Durchblasens beträgt 40,0 min. Nach Beendigung des Durchblasens hat das Metall eine Temperatur von 1640°C. Der fertige Stahl hat folgende Zusammensetzung: 0,09% C; 0,08% Mn; 0,009% P; 0,030 S; der Rest ist Eisen. Es wurde 8,7 t flüssigen Stahls gewonnen.Melting the metallic insert and freshening it up the melt lasts 27 min. The total blowing time is 40.0 min. After blowing through the metal has a temperature of 1640 ° C. The finished one Steel has the following composition: 0.09% C; 0.08% Mn; 0.009% P; 0.030 S; the rest is iron. It became 8.7 t liquid Steel won.

Tabelle 1 enthält Angaben zu den Beispielen eins, zwei, drei und anderen, die das erfindungsgemäße Verfahren innerhalb und außerhalb der Grenzen der notwendigen Kennwerte kennzeichnen.Table 1 contains information on examples one, two, three and others that the process of the invention within and outside the limits of the necessary parameters mark.

Tabelle 2 enthält zum Vergleich Angaben über den Verarbeitungsprozeß von festem Alteisen und flüssigem Roheisen in einem 10-t-Konverter beim Betrieb nach der herkömmlichen Technologie.For comparison, Table 2 contains information about the processing process of solid scrap iron and liquid pig iron in a 10 t converter when operating according to the conventional Technology.

Tabelle 1 Table 1

Abhängigkeit der Hauptkennwerte des Schmelzens von Verlauf des Durchblasens zum Zweck des Homogenisierens Dependence of the main parameters of melting on the course of blowing through for the purpose of homogenization

Fortsetzung der Tabelle 1 Continuation of table 1

Fortsetzung der Tabelle 1 Continuation of table 1

Fortsetzung der Tabelle 1 Continuation of table 1

Fortsetzung der Tabelle 1 Continuation of table 1

Vergleichbare Schmelze ohne Durchblasen zum Zweck des Homogenisierens Comparable melt without blowing through for the purpose of homogenization

Aus den angeführten Beispielen und Tabellen ist ersichtlich, daß die Anwendung des erfindungsgemäßen Verfahrens zum Erschmelzen von Stahl in einem Sauerstoff-Blaskonverter eine Erhöhung des Anteils des festen metallischen Einsatzes beim Schmelzen im Konverter bis auf 60 bis 70% der Gesamtmetallcharge ermöglicht und die Auswürfe von Metall und Schlacke aus dem Konverter während des Eingießens von Roheisen beseitigt.It can be seen from the examples and tables given that that the application of the inventive method for Melt steel in an oxygen blow converter Increase in the proportion of solid metallic insert in Melting in the converter up to 60 to 70% of the total metal batch allows and the ejection of metal and slag removed from the converter during the casting of pig iron.

Die Erhöhung des Anteils der festen metallischen, eisenhaltigen Stoffe beim Schmelzen im Konverter führt zur Senkung der Selbstkosten des erzeugten Stahls.Increasing the proportion of solid metallic, ferrous Substances when melting in the converter lead to lowering the cost price of the steel produced.

Claims (8)

1. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter aus festen metallischen, eisenhaltigen Stoffen und flüssigem Roheisen, das im Aufgeben der festen metallischen, eisenhaltigen Stoffe, deren Erhitzen durch Verbrennen eines aus Kohlenwasserstoffen bestehenden und eines kohlenstoffhaltigen Brennstoffs, die nacheinander im Arbeitsablauf im Strom eines sauerstoffhaltigen Gases zugeführt werden, das in den Konverter von unten nach oben und von oben nach unten eingeführt wird, im anschließenden Eingießen von flüssigem Roheisen und im Ausgaren der entstandenen Schmelze bis zum Erreichen der vorgegebenen chemischen Zusammensetzung besteht, dadurch gekennzeichnet, daß die festen metallischen, eisenhaltigen Stoffe bis auf eine nahe der Schmelztemperatur der festen metallischen, eisenhaltigen Stoffe, aber darunter liegende Temperatur erhitzt und vor dem Eingießen des flüssigen Roheisens diese Stoffe zum Zweck des Homogenisierens durch Zuführen eines neutralen Gases im von unten nach oben gerichteten Strom des sauerstoffhaltigen Gases, durchblasen werden, wobei die Zufuhr des von unten nach oben zugeführten, aus Kohlenwasserstoffen bestehenden Brennstoffs bis auf 1,5 bis 6,0 kg Brennstoff je Tonne der festen metallischen, eisenhaltigen Stoffe gedrosselt wird.1.Method for melting steel in an oxygen blow converter made of solid metallic, ferrous substances and liquid pig iron, which in the abandonment of solid metallic, ferrous substances, their heating by burning a hydrocarbon and a carbonaceous fuel, which are successively in the workflow in Stream of an oxygen-containing gas are supplied, which is introduced into the converter from bottom to top and from top to bottom, in the subsequent pouring of molten pig iron and in the resulting melt until the predetermined chemical composition is reached, characterized in that the solid metallic, iron-containing substances to a temperature close to the melting temperature of the solid metallic, iron-containing substances, but below this temperature and before pouring the molten pig iron these substances for the purpose of homogenization by supplying a neutral gas in the u nten upward stream of the oxygen-containing gas, are blown, the supply of the bottom-up fuel consisting of hydrocarbons is throttled to 1.5 to 6.0 kg of fuel per ton of solid metallic, iron-containing substances. 2. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach Anspruch 1, dadurch gekennzeichnet, daß Stickstoff als neutrales Gas verwendet wird.2. Process for melting steel in an oxygen Blow converter according to claim 1, characterized in that nitrogen is used as a neutral gas becomes. 3. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach Anspruch 2, dadurch gekennzeichnet, daß Stickstoff im Gemisch mit sauerstoffhaltigen Komponenten verwendet wird.3. Process for melting steel in an oxygen Blow converter according to claim 2, characterized in that nitrogen mixed with oxygen Components is used. 4. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach Anspruch 3, dadurch gekennzeichnet, daß die Menge der sauerstoffhaltigen Komponenten im Gemisch mit Stickstoff 50 bis 100% der theoretisch für vollständiges Verbrennen des von unten nach oben zugeführten Brennstoffs notwendigen Menge ausmacht.4. Process for melting steel in an oxygen Blow converter according to claim 3, characterized in that the amount of oxygenated components in a mixture with nitrogen 50 to 100% of theoretical for completely burning the bottom up fuel supplied makes up the necessary amount. 5. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß gleichzeitig mit dem Durchblasen zum Zweck des Homogenisierens auf die Oberfläche der festen, metallischen, eisenhaltigen Stoffe calciumhaltige und kohlenstoffhaltige Stoffe gegeben werden.5. Process for melting steel in an oxygen Blow converter according to one of claims 1 to 4, characterized in that at the same time with blowing for the purpose of homogenizing the surface of solid, metallic, ferrous materials Calcium-containing and carbon-containing substances are given. 6. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach Anspruch 5, dadurch gekennzeichnet, daß Kalk und Kohle als calciumhaltige und kohlenstoffhaltige Stoffe verwendet werden.6. Process for melting steel in an oxygen Blow converter according to claim 5, characterized in that lime and coal as calcium and carbonaceous substances are used. 7. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach Anspruch 1 oder 5, dadurch gekennzeichnet, daß gleichzeitig mit dem zum Zweck des Homogeniserens durchgeführten Durchblasen der Konverter mit den in ihn aufgegebenen festen metallischen, eisenhaltigen Stoffen periodisch bis zur maximal möglichen Neigung gekippt wird.7. Process for melting steel in an oxygen Blow converter according to claim 1 or 5, characterized in that that at the same time with that for the purpose the converter is blown through the homogeniser with the solid metallic, ferruginous metals added to it Fabrics periodically up to the maximum possible inclination is tilted. 8. Verfahren zum Erschmelzen von Stahl in einem Sauerstoff- Blaskonverter nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß nach dem zum Zweck des Homogenisierens durchgeführten Durchblasen, aber vor dem Eingießen des flüssigen Roheisens die entstandene flüssige Schlacke abgezogen wird.8. Process for melting steel in an oxygen Blow converter according to one of claims 1  to 4, characterized in that according to the blowing through for the purpose of homogenization, but before pouring the molten pig iron, the resulting one liquid slag is withdrawn.