DE3633056A1 - Extrudable mixture for halogen-free, highly flame-resistant coverings (sheaths) - Google Patents

Extrudable mixture for halogen-free, highly flame-resistant coverings (sheaths)

Info

Publication number
DE3633056A1
DE3633056A1 DE19863633056 DE3633056A DE3633056A1 DE 3633056 A1 DE3633056 A1 DE 3633056A1 DE 19863633056 DE19863633056 DE 19863633056 DE 3633056 A DE3633056 A DE 3633056A DE 3633056 A1 DE3633056 A1 DE 3633056A1
Authority
DE
Germany
Prior art keywords
mixture according
following
polymer
flame
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE19863633056
Other languages
German (de)
Inventor
Ferdinand Dr Rer Nat Hanisch
Richard Winter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kabelmetal Electro GmbH
Original Assignee
Kabelmetal Electro GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kabelmetal Electro GmbH filed Critical Kabelmetal Electro GmbH
Priority to DE19863633056 priority Critical patent/DE3633056A1/en
Publication of DE3633056A1 publication Critical patent/DE3633056A1/en
Ceased legal-status Critical Current

Abstract

The invention provides an extrudable, halogen-free and highly flame-resistant mixture based on a copolymer of ethylene with a comonomer. To increase the heat resistance, a polymer component is added to the base material in a proportion of from 10 to 50% by weight of the total quantity of polymer.

Description

Die Erfindung betrifft eine extrudierfähige Mischung zur Herstellung einer halogenfreien und schwer entflammbaren Umhüllung von langgestrecktem Gut, wie elektrische Kabel oder Leitungen, Rohrbündelkabel, Rohrleitungen und dergl.The invention relates to an extrudable mixture for producing a halogen-free and flame-retardant wrapping of elongated goods, such as electrical cables or wires, tube bundle cables, pipelines and the like

Schwer entflammbare Mischungen zur Herstellung der unterschiedlichsten Produkte werden auf vielen technischen Gebieten gefordert. So soll bei­ spielsweise die Isolierung elektrischer Kabel und Leitungen aus Polyvinyl­ chlorid unbrennbar sein, wenn solche Kabel oder Leitungen in Bergwerken, auf Schiffen oder in anderen feuergefährlichen oder feuergefährdeten An­ lagen Verwendung finden. Weichmacherfreies Polyvinylchlorid ist zwar un­ brennbar für die Herstellung elektrischer Kabel und Leitungen jedoch nicht geeignet. Zu diesem Zweck ist es daher üblich weichmacherhaltiges Poly­ vinylchlorid zu verwenden, das noch als flammwidrig bezeichnet werden kann. Diese Eigenschaft erhält es durch das bei Erwärmung freiwerdende Chlor­ wasserstoffgas, das bei der Zersetzung der Isolierung aus dem Polyvinyl­ chlorid entsteht und die entstehende Flamme zum Erlöschen bringt. Nachtei­ lig hierbei sind die bekannten Folgeschäden, die sich dadurch ergeben, daß der bei Erwärmung abgespaltene gasförmige Chlorwasserstoff sich mit Wasser oder Wasserdampf zu Salzsäure verbindet, die Metalle, Beton oder sonstige Gegenstände anätzt oder zerstört. Im Bemühen, solche Nachfolgeschäden zu unterbinden, hat man bereits vorgesehen (DE-OS 17 69 343), den polymeren Werkstoffen zur Bindung der unter Wärmeeinwirkung abgespaltenen flüchtigen Säuren sehr feinteiligen, säurebindenden Füllstoff mit einer mittleren Korngröße unter 250 µm zuzugeben. Dieses bekannte Verfahren hat sich in der Praxis nicht durchsetzen können. Flame retardant mixtures for the production of the most varied Products are required in many technical areas. So at for example the insulation of electrical cables and lines made of polyvinyl chloride is non-flammable if such cables or lines are used in mines, on ships or in other flammable or flammable types were used. Unplasticized polyvinyl chloride is un not combustible for the production of electrical cables and wires suitable. For this purpose, it is therefore common to use plasticized poly To use vinyl chloride, which can still be described as flame retardant. It gets this property from the chlorine released when heated hydrogen gas, which decomposes the insulation from the polyvinyl chloride is formed and the flame that is produced goes out. Night egg Lig here are the known consequential damages that result from the fact that the gaseous hydrogen chloride split off when heated up with water or water vapor to form hydrochloric acid that combines metals, concrete or others Etched or destroyed objects. In an effort to cause such consequential damage prevent, has already been provided (DE-OS 17 69 343), the polymer Materials for binding the volatile, split off under the influence of heat Acids very finely divided, acid-binding filler with a medium Add grain size below 250 µm. This known method has become known in cannot enforce in practice.  

Man ist deshalb inzwischen zu halogenfreien Basismaterialien übergegangen, die man durch flammwidrige halogenfreie Zusätze schwer entflammbar einstellt. Bekannt ist in diesem Zusammenhang eine flammwidrige halogenfreie Polymer­ mischung (DE-OS 28 09 294), die eine definierte Menge an Aluminiumoxidhy­ drat enthält. Als Basismaterialien werden hierbei Kautschuke oder kaut­ schukartige Werkstoffe verwendet, die im Zuge der Verarbeitung zum Endpro­ dukt durch Wärmeeinwirkung chemisch vernetzt werden. Die genannten Werk­ stoffe sind schwer zu verarbeiten, der maschinelle Aufwand ist groß, das Herstellungverfahren damit kostenaufwendig und die Werkstoffe sind nicht in jedem Fall wirklich halogenfrei.One has therefore switched to halogen-free base materials, which is made flame-retardant by flame-retardant halogen-free additives. In this context, a flame-retardant halogen-free polymer is known mixture (DE-OS 28 09 294), which contains a defined amount of alumina drat contains. The base materials used here are rubbers or chewed Schuk-like materials used in the course of processing to Endpro product are chemically cross-linked by the action of heat. The named plant Fabrics are difficult to work with, the mechanical effort is great, that Manufacturing processes are therefore expensive and the materials are not in any case, really halogen-free.

Der Erfindung liegt daher, ausgehend von den bekannten Möglichkeiten, die Aufgabe zugrunde, halogenfreie und schwer entflammbare Mischungen zu finden, die vom Eigenschaftsbild her den gestellten Anforderungen genügen, die darüber hinaus aber wesentlich kostengünstiger zu verarbeiten sind und ver­ besserte Wärmestandfestigkeit aufweisen.The invention is therefore based on the known possibilities that Based on the task of finding halogen-free and flame-retardant mixtures, which meet the requirements in terms of property profile, which in addition, but are much cheaper to process and ver have better heat resistance.

Gelöst wird diese Aufgabe gemäß der Erfindung dadurch, daß die Mischung ein Copolymer des Ethylens mit einem Comonomer-Anteil von 10-30 Gew.% als Basismaterial und eine die Wärmestandfestigkeit erhöhende polymere Komponente enthält, deren Anteil an der Gesamtmenge Polymer 10-50 Gew.% beträgt.This object is achieved according to the invention in that the mixture a copolymer of ethylene with a comonomer content of 10-30% by weight as a base material and a polymer that increases heat resistance Contains component, the proportion of the total amount of polymer 10-50 wt.% is.

Eine solche Mischung ist halogenfrei. Folgeschäden im Brandfall sind nicht zu erwarten. Der Copolymerbasisanteil gewährleistet die gute Aufnahmefähig­ keit von Füllstoffen, die zur Einstellung der geforderten Brandsicherheit notwendig sind. Durch die zusätzliche polymere Komponente erhält eine aus dieser Mischung hergestellte Umhüllung eine den Erfordernissen angepaßte erhöhte Wärmestandfestigkeit, ohne daß ein Vernetzungsschritt nachgeschal­ tet werden müßte. Zudem läßt die dadurch verbesserte Fließfähigkeit der Mischung während der Extrusion zum Endprodukt erhöhte Fertigungsgeschwindig­ keiten bei kostengünstigem maschinellen Aufwand zu. Durch die polymere Zu­ satzkomponente wird neben einer erhöhten mechanischen Formbeständigkeit auch eine für viele Anwendungszwecke gleichzeitig wünschenswerte Ölbe­ ständigkeit erreicht, die bei einer sonst gleichen Mischung ohne Zusatz­ komponente in der Regel nur durch eine zusätzliche Vernetzung des Basis­ materials erzielt werden kann. Such a mixture is halogen-free. Consequential damage in the event of fire is not expected. The copolymer base proportion ensures good absorption of fillers used to adjust the required fire safety are necessary. Due to the additional polymeric component one gets out this mixture produced a casing adapted to the requirements increased heat resistance without the need for a crosslinking step should be done. In addition, the fluidity thereby improved Mixing during extrusion to the final product increased manufacturing speed times with inexpensive machine work. Through the polymeric Zu Set component is in addition to increased mechanical dimensional stability also an oil oil that is desirable for many applications at the same time Stability achieved with an otherwise identical mixture without additives component usually only through additional networking of the base materials can be achieved.  

Für die Zwecke der Erfindung besonders geeignete Copolymere sind solche auf Acetat- oder Acrylat-Basis, beispielsweise Ethylen-Vinylacetate, Ethy­ len-Ethylacrylate oder Ethylen-Butylacrylate.Copolymers which are particularly suitable for the purposes of the invention are those based on acetate or acrylate, for example ethylene vinyl acetate, ethyl len-ethyl acrylates or ethylene-butyl acrylates.

Für die die Wärmestandfestigkeit erhöhende Komponente kommt es wie aus­ geführt, auf hohe Schmelz- oder Erweichungsbereiche dieser Komponente an. Als besonders vorteilhaft für die Zwecke der Erfindung haben sich erwiesen: Hart-Polyethylene mit einer Dichte <0,92 g/cm3, vorzugsweise 0,94 g/cm3, lineare Polyethylene (LLDPE, VLDPE) mit einer Dichte von 0,88-0,95 g/cm3, aber auch Polypropylen mit einem Schmelzbereich bis 165°C, Polyamide und Polyester.For the component that increases the heat resistance, it is important that high melting or softening ranges of this component are important. The following have proven to be particularly advantageous for the purposes of the invention: hard polyethylenes with a density of <0.92 g / cm 3 , preferably 0.94 g / cm 3 , linear polyethylenes (LLDPE, VLDPE) with a density of 0.88 -0.95 g / cm 3 , but also polypropylene with a melting range up to 165 ° C, polyamides and polyester.

Durch den Copolymeranteil der Mischung ist die Aufnahmefähigkeit einer hin­ reichenden Menge an Füllstoffen gewährleistet. Zur Erzielung der geforderten Brandsicherheit können nach der Erfindung deshalb die hierzu geeigneten Füll­ stoffe, etwa Aluminiumoxidhydrate, Magnesiumhydroxide und ähnliche, in aus­ reichender Menge problemlos in die Mischung eingebracht werden. Als für die Zwecke der Erfindung ausreichende Menge an solchen Materialien werden 80 bis 180 Teile, bezogen auf 100 Teile Polymer angesehen. Unberücksichtigt bleibt dabei, daß weitere, nicht aktiv flammwidrig wirkende Füllstoffe, wie Kreide, Talkum usw., hinzukommen können. Durch die entsprechend der Erfindung ge­ wählte Mischungszusammensetzung können die Eigenschaften der hieraus herge­ stellten Endprodukte noch besser den gestellten Anforderungen angepaßt werden.Due to the copolymer content of the mixture, the absorption capacity is a thing of the past sufficient amount of fillers guaranteed. To achieve the required According to the invention, fire safety can therefore be carried out using the appropriate fill substances such as aluminum oxide hydrates, magnesium hydroxides and the like sufficient amount can be easily introduced into the mixture. As for the Sufficient amount of such materials for the purposes of the invention will be 80 to 180 parts, based on 100 parts of polymer. Not taken into account thereby that other fillers which do not have an active flame retardant effect, such as chalk, Talc, etc., can be added. By ge according to the invention Chosen mixture composition can derive the properties of this end products are even better adapted to the requirements.

In Weiterführung des Erfindungsgedankens können in der Mischung zusätzlich ungesättigte, hydrolisierbare Vinylsilane verwendet werden. Diese werden im Zuge der Compoundierung und Verarbeitung auf die Hauptkette wenigstens einer der polymeren Komponenten aufgepfropft, wobei die Mischung durch Feuchtigkeit vernetzbar wird.In continuation of the inventive concept, the mixture can additionally unsaturated, hydrolyzable vinyl silanes can be used. These are in the In the course of compounding and processing on the main chain at least one the polymeric components are grafted on, the mixture being damp becomes networkable.

Als eine der Komponenten kann auch ein solches Polymer verwendet werden, das hydrolisierbare Silangruppen bereits aufgepfropft oder einpolymerisiert enthält. Auch in dieser Zusammensetzung werden die erfindungsgemäßen Mischungen zusätzlich durch Feuchtigkeit vernetzbar. Such a polymer can also be used as one of the components, the hydrolyzable silane groups are already grafted or polymerized contains. The mixtures according to the invention are also in this composition can also be cross-linked by moisture.  

Die erfindungsgemäße Mischung ist zu einer Umhüllung von langgestrecktem Gut auf den unterschiedlichsten technischen Gebieten geeignet. In be­ sonderem Maße ist an die den äußeren Einflüssen ausgesetzte äußere Um­ hüllung gedacht, das ist z. B. bei elektrischen Kabeln oder Rohrbündel­ kabeln der Kabelmantel und bei Rohrleitungen der Schutzmantel. Ein solcher Schutzmantel ist aber auch ein sog. "Kanalrohrkabel", das als "Rohr" ver­ legt wird und in das nach der Verlegung elektrische Kabel oder Leitungen, insbesondere auch mit Lichtwellenleitern, eingezogen werden.The mixture according to the invention is an encapsulation of elongated Well suited in a wide variety of technical fields. In be is special to the external environment exposed to external influences thought cover, that is z. B. with electrical cables or tube bundles wire the cable sheath and, for pipes, the protective sheath. Such a Protective sheath is also a so-called "sewer pipe cable", which ver as "pipe" is laid and in which after the laying electrical cables or lines, especially with optical fibers.

Für die vorstehenden Anwendungszwecke haben sich z. B. die in den folgenden Beispielen I bis III angeführten Mischungen als besonders geeignet erwiesen.For the above purposes z. B. in the following Mixtures listed in Examples I to III have been found to be particularly suitable.

Beispiel IExample I

Ethylen-Vinylacetat-Copolymer
(EVA) mit einem Acetatanteil von 20% 70 Teile Hartpolyethylen (Dichte 0,96 g/cm³) 30 Teile Aluminiumoxidhydrat130 TeileEthylene vinyl acetate copolymer
(EVA) with an acetate content of 20% 70 parts hard polyethylene (density 0.96 g / cm³) 30 parts alumina hydrate 130 parts

Beispiel IIExample II

Ethylen-Vinylacetat-Copolymer
(wie Beispiel I) 60 Teile Lineares Polyethylen (Dichte 0,92 g/cm³) 40 Teile Magnesiumhydroxid110 TeileEthylene vinyl acetate copolymer
(as Example I) 60 parts linear polyethylene (density 0.92 g / cm³) 40 parts magnesium hydroxide 110 parts

Beispiel IIIExample III

Ethylen-Ethylacrylat-Copolymer 50 Teile Polyethylen (VLDPE) (Dichte 0,9 g/cm³) 50 Teile Aluminiumoxidhydrat140 TeileEthylene-ethyl acrylate copolymer 50 parts Polyethylene (VLDPE) (density 0.9 g / cm³) 50 parts Alumina hydrate 140 parts

Silan (Vinyltrimethoxisilan)  2 Teile Peroxid  0,1 Teil Kondensationskatalysator
(Dibutylzinndilaurat)  0,05 TeileSilane (vinyltrimethoxysilane) 2 parts peroxide 0.1 part condensation catalyst
(Dibutyltin dilaurate) 0.05 parts

Claims (14)

1. Extrudierfähige Mischung zur Herstellung einer halogenfreien und schwer entflammbaren Umhüllung von langgestrecktem Gut, wie elek­ trische Kabel oder Leitungen, Rohrbündelkabel, Rohrleitungen und dergl., gekennzeichnet durch ein Copolymer des Ethylens mit einem Comonomer-Anteil von 10-30 Gew.% als Basismaterial und einer die Wärmestandfestigkeit erhöhenden polymeren Komponente, deren Anteil an der Gesamtmenge Polymer 10-50 Gew.% beträgt.1. Extrudable mixture for the production of a halogen-free and flame-retardant covering of elongated goods, such as electrical cables or lines, bundled cables, pipes and the like, characterized by a copolymer of ethylene with a comonomer content of 10-30% by weight as the base material and a polymer component which increases the heat resistance, the proportion of which in the total amount of polymer is 10-50% by weight. 2. Mischung nach Anspruch 1, dadurch gekennzeichnet, daß das Comono­ mere ein Acetat ist.2. Mixture according to claim 1, characterized in that the comono mere is an acetate. 3. Mischung nach Anspruch 1, dadurch gekennzeichnet, daß das Comono­ mere ein Acrylat ist.3. Mixture according to claim 1, characterized in that the comono mere is an acrylate. 4. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die die Wärmestandfestigkeit erhöhende polymere Kom­ ponente ein Hart-Polyethylen mit einer Dichte <0,92 g/cm3, vorzugs­ weise 0,94 g/cm3, ist.4. Mixture according to claim 1 or one of the following, characterized in that the thermal stability-increasing polymer component is a hard polyethylene with a density <0.92 g / cm 3 , preferably 0.94 g / cm 3 . 5. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die die Wärmestandfestigkeit erhöhende polymere Kom­ ponente ein lineares Polyethylen (LLDPE, VLDPE) mit einer Dichte von 0,88-0,95 g/cm3 ist.5. Mixture according to claim 1 or one of the following, characterized in that the heat-resistant polymer component Kom is a linear polyethylene (LLDPE, VLDPE) with a density of 0.88-0.95 g / cm 3 . 6. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die die Wärmestandfestigkeit erhöhende hochpolymere Komponente Polypropylen ist. 6. Mixture according to claim 1 or one of the following, characterized is characterized in that the high polymer increases the heat resistance Component is polypropylene.   7. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die die Wärmestandfestigkeit erhöhende hochpolymere Kom­ ponente Polyester ist.7. Mixture according to claim 1 or one of the following, characterized is characterized in that the high polymer com component is polyester. 8. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die die Wärmestandfestigkeit erhöhende hochpolymere Kom­ ponente -Polyamid ist.8. Mixture according to claim 1 or one of the following, characterized is characterized in that the high polymer com component is polyamide. 9. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß als flammwidriger Zusatz ein Aluminiumoxidhydrat dient.9. Mixture according to claim 1 or one of the following, characterized records that an aluminum oxide hydrate serves as a flame-retardant additive. 10. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß als flammwidriger Zusatz ein Magnesiumhydroxid dient.10. Mixture according to claim 1 or one of the following, characterized records that a magnesium hydroxide serves as a flame retardant additive. 11. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß die genannten flammwidrigen Zusätze als Kombination oder auch mit anderen, nicht aktiv flammwidrig wirkenden Füllstoffzusätzen, wie Kreide, Talkum usw., verwendet werden.11. Mixture according to claim 1 or one of the following, characterized records that the flame retardant additives mentioned as a combination or also with other fillers that are not actively flame retardant, such as chalk, talc, etc. can be used. 12. Mischung nach Anspruch 9, 10 oder 11, dadurch gekennzeichnet, daß die flammwidrigen Zusätze 80 bis 180 Teile bezogen auf 100 Teile Basis­ material betragen.12. Mixture according to claim 9, 10 or 11, characterized in that the flame retardant additives 80 to 180 parts based on 100 parts basis material. 13. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß als weiterer Zusatz ungesättigte, hydrolisierbare Silane verwendet sind, die im Zuge der Compoundierung oder Verarbeitung auf die Polymerkette mindestens eines der genannten Polymere aufgepfropft werden.13. Mixture according to claim 1 or one of the following, characterized records that as a further additive unsaturated, hydrolyzable silanes are used in the course of compounding or processing the polymer chain is grafted onto at least one of the polymers mentioned will. 14. Mischung nach Anspruch 1 oder einem der folgenden, dadurch gekenn­ zeichnet, daß mindestens eine der polymeren Komponenten hydrolisier­ bare Silane bereits in aufgepfropfter Form oder in die Hauptkette des Polymers bereits einpolymerisiert enthält.14. Mixture according to claim 1 or one of the following, characterized records that at least one of the polymeric components hydrolyzed bare silanes already in grafted form or in the main chain of the Polymer already contains copolymerized.
DE19863633056 1986-09-29 1986-09-29 Extrudable mixture for halogen-free, highly flame-resistant coverings (sheaths) Ceased DE3633056A1 (en)