DE3515574A1 - Coaxial cable and process for producing an insulation surrounding the inner conductor of this cable - Google Patents

Coaxial cable and process for producing an insulation surrounding the inner conductor of this cable

Info

Publication number
DE3515574A1
DE3515574A1 DE19853515574 DE3515574A DE3515574A1 DE 3515574 A1 DE3515574 A1 DE 3515574A1 DE 19853515574 DE19853515574 DE 19853515574 DE 3515574 A DE3515574 A DE 3515574A DE 3515574 A1 DE3515574 A1 DE 3515574A1
Authority
DE
Germany
Prior art keywords
inner conductor
layer
plastic
insulation
insulating layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19853515574
Other languages
German (de)
Inventor
Pertti Oulu Malva
Reijo Espoo Vahteristo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nokia Oyj
Original Assignee
Nokia Oyj
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FI841754A external-priority patent/FI841754A0/en
Priority claimed from FI843308A external-priority patent/FI843308A/en
Application filed by Nokia Oyj filed Critical Nokia Oyj
Publication of DE3515574A1 publication Critical patent/DE3515574A1/en
Withdrawn legal-status Critical Current

Abstract

The invention relates to a coaxial cable and a process for producing an insulation surrounding the inner conductor of this cable. According to the process for producing an insulation surrounding the inner conductor of a coaxial cable, which coaxial cable has an inner conductor, a plastic insulation moulded around the inner conductor, a cylindrical outer conductor, moulded around the insulation, and an outer jacket of plastic, an insulating layer consisting of at least one layer of foam plastic is extruded onto the inner conductor and, after the extrusion, the insulating layer is cooled. According to the invention, the extruding of the insulating layer is carried out in two different stages and the cooling and drying are carried out between the extrusion stages, the thickness of the two extruded part-layers being less than the thickness of the final insulating layer and the cooling being many times quicker. The cable produced according to the invention is characterised in that the insulating layer (10) consists of two extruded layers (8, 9) of foam plastic placed one on top of the other, the thickness of which is approximately half the thickness of the final insulating layer. In an alternative embodiment, the plastic insulation (10) of the inner conductor (7) has a layer (8) of solid plastic adjoining the inner conductor (7) and a layer (9) of foam plastic moulded around this layer. <IMAGE>

Description

Koaxialkabel und Verfahren zur Herstellung einer denCoaxial cable and method of making a den

Innenleiter dieses Kabels umgebenden Isolierung Diese Erfindung bezieht sich auf ein Koaxialkabel, das einen Innenleiter, eine um den Innenleiter ausgeformte Kunststoffisolierung, einen um die Isolierung ausgeformten, zylindrischen Aussenleiter und einen Aussenmantel aus Kunststoff aufweist, und auf ein Verfahren zur Herstellung einer den Innenleiter des Kabels umgebenden Isolierung.Inner conductor of this cable surrounding insulation This invention relates on a coaxial cable that has an inner conductor and one shaped around the inner conductor Plastic insulation, a cylindrical outer conductor molded around the insulation and has an outer jacket made of plastic, and to a method for manufacturing an insulation surrounding the inner conductor of the cable.

Das Allgemeinwerden der Kabelfernsehsysteme und entsprechender Breitbandnetze für Informationsübertragung und der Uebergang von verketteten Gemeinschaftsantennennetzen zu Strahlennetzen vermehren gerade jetzt den quantitativen Bedarf an Koaxialkabeln. Andererseits werden an die Grösse, die elektrischen und mechanischen Eigenschaften von Kabeln dieser Art Anforderungen gestellt, die mittels konventioneller Kabeltypen nicht erfüllt werden können. Ein typisches solches, für Inneninstallationen gebrauchtes Koaxialkabel weist zwishcen den Innen- und Aussenleitern eine Isolierung aus Festkunststoff auf, die einen Durchmesser von 4,8 mm hat und deren Aussenleiter ein aus einem dünnen Kupferleiter ausgeformter Doppelzopf oder eine Kombination eines Zopfes und eines kupfernen Folienbandes ist. Ein solches Kabel ist starr und kann in engen Installationsrohren und -dosen nur mit Mühe installiert werden. The generalization of cable television systems and related broadband networks for information transmission and the transition from concatenated community antenna networks to radiation networks are increasing the quantitative need for coaxial cables right now. On the other hand, the size, the electrical and mechanical properties of cables of this type made demands that by means of conventional cable types cannot be met. A typical one used for indoor installations Coaxial cable has an insulation made of solid plastic between the inner and outer conductors on, which has a diameter of 4.8 mm and whose outer conductor is a thin one Copper wire shaped double braid or a combination of a braid and one copper foil tape is. Such a cable is rigid and can be used in narrow installation conduits and boxes are difficult to install.

Nach einem konventionellen Verfahren zur Herstellung von schaumkunststoffisolierten Koaxialkabeln wird auf den Innenleiter in einer Strangpresse Schaumkunststoff gespritzt, der nach dem Pressenende zu seiner endgültigen Dimension schwillt und eine fertige Isolierschicht bildet. Using a conventional method of making foam plastic insulated Coaxial cable is injected onto the inner conductor in a foam plastic extrusion press, which after the end of the press swells to its final dimension and a finished one Forms insulating layer.

Eine Schwierigkeit mit einem Prozess dieser Art ist, den endgültigen Durchmesser des überzogenen Kabels zu kontrollieren, welcher Durchmesser im Rahmen einer Genauigkeit von zehntel Millimetern gehalten werden soll. One difficulty with a process of this type is the final one Diameter of the coated cable to control what diameter in the frame one Accuracy of tenths of a millimeter should be maintained.

Besonders schädliche Herstellungsfehler sind periodische Änderungen im Durchmesser. Ein solcher Fehler geschieht leicht unter der Einwirkung von periodischen Variationen der Geschwindigkeit an einer Produktionsstrasse.Periodic changes are particularly harmful manufacturing defects In diameter. Such an error easily happens under the action of periodic Variations in speed on a production line.

Eine andere Schwierigkeit mit einem konventionellen Ueberzugsverfahren ist die Abkühlung des Kabels. Eine aufgeschäumte, dicke Kunststoffschicht ist gleichzeitig eine gute Wärmeisolierung, was zur Folge hat, dass es lange dauert, bevor die Isolierschicht aus Schaumkunststoff ganz abgekühlt ist. Dadurch wird die Mengenleistung von Kabeln wesentlich herabgesetzt. Another difficulty with a conventional coating process is the cooling of the cable. A foamed, thick layer of plastic is at the same time good thermal insulation, which means that it takes a long time before the insulating layer made of foam plastic has cooled down completely. This increases the volume output of cables substantially reduced.

Dieser Erfindung liegt die Aufgabe zugrunde, ein Verfahren zu schaffen, das die obenerwähnten Nachteile vermeidet und es ermöglicht, eine grössere Mengenleistung und eine bessere Qualität zustandezubringen. This invention is based on the object of creating a method which avoids the disadvantages mentioned above and makes it possible to achieve a greater volume output and bring about better quality.

Diese Aufgabe wird durch ein erfindungsgemässes Verfahren gelöst, wobei zur Herstellung einer den Innenleiter eines Koaxialkabels umgebenden Isolierung, welches Koaxialkabel einen Innenleiter, eine um den Innenleiter ausgeformte Kunststoffisolierung, einen um die Isolierung ausgeformten, zylindrischen Aussenleiter und einen Aussenmantel aus Kunststoll aufweist, nach welchem Verfahren - eine aus mindestens einer Schaumkunststoffschicht bestehende Isolierschicht auf den Innenleiter stranggepresst wird und - die Isolierschicht nach dem Strangpressen abgekühlt wird, und das dadurch gekennzeichnet ist, dass - das Strangpressen der Isolierschicht in zwei verschiedenen Stufen ausgeführt wird, und - das Abkühlen und Trocknen zwischen den Strangpressstufen ausgeführt werden.This object is achieved by a method according to the invention, where for the production of an insulation surrounding the inner conductor of a coaxial cable, which coaxial cable has an inner conductor, a plastic insulation molded around the inner conductor, a cylindrical outer conductor formed around the insulation and an outer jacket from Kunststoll, according to which method - one of at least one foam plastic layer existing insulating layer is extruded onto the inner conductor and - the insulating layer is cooled after extrusion, and which is characterized in that - the extrusion of the insulating layer is carried out in two different stages, and - the cooling and drying are carried out between the extrusion stages.

Die Erfindung basiert auf dem Gedanken, dass das Strangpressen der den Innenleiter umgebenden Isolierschicht in zwei Stufen mit dazwischen geschehender Abkühlung in einem einheitlichen Produktionsprozess ausgeführt wird. Dadurch werden folgende Vorteile erreicht. Weil die Dicke der abzukühlenden Schicht nur ein Teil der Dicke der endgültigen Isolierschicht ist, findet die Abkühlung der Schicht viele Male schneller statt als die Abkühlung einer direkt zu ihrer endgültigen Dicke stranggepressten Isolierschicht und dadurch kann die Mengenleistung auf 3-5-fältia erhöht werden. Zweitens ist es leichter, den Au#sendurchmesser der endgültigen Isolierschicht zu kontrollieren, wenn das Strangpressen in zwei Stufen stattfindet, weil die von periodischen Geschwindigkeitsänderungen an der Produktionsstrasse veranlassten periodischen Anderungen im Durchmesser in verschiedenen Schichten einander teilweise aufheben und somit eine bessere durchschnittliche Qualität erreicht wird. The invention is based on the idea that the extrusion of the surrounding the inner conductor Insulating layer in two stages with in between cooling that occurs is carried out in a uniform production process. This achieves the following advantages. Because the thickness of the layer to be cooled is only part of the thickness of the final insulating layer, the cooling takes place the layer takes place many times faster than the cooling one straight to its final Thick extruded insulating layer and thereby the volume output can be increased to 3-5 times increase. Second, it is easier to determine the outside diameter of the final insulation layer to control if the extrusion takes place in two stages because that of periodic speed changes on the production line caused periodic ones Changes in diameter in different layers partially cancel each other out and thus a better average quality is achieved.

Die Erfindung bezieht sich ausserdem auf ein Koaxialkabel, das nach dem obenbeschriebenen Verfahren hergestellt ist. Eine Ausführungsform eines solches Kabels ist dadurch gekennzeichnet, dass die Isolierschicht aus zwei auf einander befindlichen stranggepressten Schichten aus Schaumkunststoff besteht, deren Dicke ungefähr die Hälfte der Dicke der endgültigen Isolierschicht ist. The invention also relates to a coaxial cable according to is prepared by the method described above. An embodiment of such a Cable is characterized in that the insulating layer consists of two on top of each other located extruded layers of foam plastic, the thickness of which is approximately half the thickness of the final insulation layer.

Dieser Erfindung liegt auch die Aufgabe zugrunde, ein hauptsächlich zu Inneninstallationen beabsichtigtes Koaxialkabel zustandezubringen, dessen elektrische Eigenschaften alle gestellten Anforderungen erfüllen, dessen Aussendurchmesser aber kleiner als früher ist und dadurch auch zu Installationen besser geeignet ist und dessen Herstellungskosten dazu vorteilhafter sind. This invention is also based on the object of a mainly Coaxial cable intended for indoor installations, its electrical Properties meet all requirements, but its outside diameter is smaller than before and is therefore also better suited for installations and whose manufacturing costs are more advantageous.

Diese Ausführungsform der Erfindung ist dadurch gekennzeichnet, dass die Kunststoffisolierung des Innenleiters eine sich an den Innenleiter anschliessende Schicht aus Festkunststoff und eine um diese Schicht ausgeformte Schicht aus Schaumkunststoff umfasst. Der Querschnitt der Festkunststoffschicht kann rund sein, aber zur Verbesserung der Verankerung des Innenleiters kann die Festkunststoffschicht auch zwei oder mehrere, hinsichtlich des Innenleiters symmetrisch gelegene und davon radial ausgehende, sich im Kabel axial streckende Kämme aufweisen.This embodiment of the invention is characterized in that the plastic insulation of the inner conductor adjoins the inner conductor Layer of solid plastic and one around this layer shaped Includes layer of foam plastic. The cross section of the solid plastic layer can be round, but to improve the anchoring of the inner conductor, the Solid plastic layer also two or more, symmetrical with regard to the inner conductor located and radially extending therefrom, axially extending ridges in the cable.

Die Erfindung wird nachstehend anhand der beigefügten Zeichnung näher erläutert, wobei Figur 1 eine auf dem erfindungsgemässen Verfahren basierende Ueberzugsstrasse schematisch darstellt, Figur 2 die Struktur eines erfindungsgemässen Kabels darstellt, Figur 3 einen Querschnitt der Isolierung gemäss der ersten Ausführungsform des erfindungsgemässen Kabels darstellt, Figur 4 einen Querschnitt der Isolierung gemäss der zweiten Ausführungsform des erfindungsgemässen Kabels darstellt, und Figur 5 einen Querschnitt einer Variation der Isolierung gemäss der zweiten Ausführungsform des erfindungsgemässen Kabels darstellt. The invention is explained in more detail below with reference to the accompanying drawing explained, FIG. 1 showing a coating line based on the method according to the invention shows schematically, Figure 2 shows the structure of a cable according to the invention, FIG. 3 shows a cross section of the insulation according to the first embodiment of the invention Cable, Figure 4 shows a cross section of the insulation according to the second embodiment of the cable according to the invention, and FIG. 5 shows a cross section of a variation the insulation according to the second embodiment of the cable according to the invention represents.

An der in Figur 1 der Zeichnung dargestellten Produktionsstrasse sind zwei Strangpressen 1 und 2 in einem Abstand von einander installiert. Nach jeder Strangpresse sind Abkühlungs- und Trocknungsvorrichtungen 3,4 respektive 5,6 installiert. Ein Kabelleiter 7 läuft durch die erste Presse, in der er mit einer Kunststoffschicht 8 überzogen wird, die abgekühlt und getrocknet wird, bevor das vorumhüllte Kabel durch die zweite Presse läuft, wo auf die erste Schicht eine zweite Schicht 9 aus Schaumkunststoff gepresst wird. On the production line shown in Figure 1 of the drawing two extrusion presses 1 and 2 are installed at a distance from each other. To Each extruder has cooling and drying devices 3, 4 and 5, 6, respectively Installed. A cable ladder 7 runs through the first press, in which he is with a Plastic layer 8 is coated, which is cooled and dried before the pre-sheathed cable runs through the second press, where a second layer is applied to the first Layer 9 is pressed from foam plastic.

Diese Schicht wird nach der zweiten Presse abgekühlt und getrocknet, wenn sie durch entsprechende Vorrichtungen läuft. Die erste und zweite Schicht aus Schaumkunststoff bilden die endgültige Isolierschicht 10 auf dem Innenleiter des Kabels.This layer is cooled and dried after the second press, if it runs through appropriate devices. The first and second layers off Foam plastic form the final insulating layer 10 on the Inner conductor of the cable.

Man bemerkt, dass das Ueberziehen des Innenleiters mit einer nötigen Isolierschicht in zwei Stufen I und II geschieht, wobei in beiden Stufen nur die Schicht abgekühlt werden soll, die dünner als die endgültige Isolierschicht ist und die somit wesentlich schneller abgekühlt wird. One notices that the covering of the inner conductor with a necessary Insulating layer happens in two stages I and II, with only the in both stages Layer to be cooled that is thinner than the final insulating layer and which is therefore cooled down much faster.

Bei der Herstellung von z.B. ganz mit Schaumkunststoff isolierten Stammkabeln für ein Kabelfernsehnetz, siehe den Querschnitt der Isolierung in Figur 3, ist es vorteilhaft, dass in beiden Ueberzugsstufen die Hälfte der endgültigen Dicke der Isolierschicht gepresst wird, wobei eine optimale Erhöhung der Mengenleistung erreicht werden kann. Nach der Abkühlvorrichtung der ersten Presse ist in der Bewegungsbahn des Kabels ein Gerät 11 zum Messen des Aussendurchmessers des Kabels installiert. Dieses Gerät ist mit einer Steuereinheit 12 der zweiten Presse verbunden, welche Steuereinheit die Dicke der in der zweiten Presse zu pressenden Schicht reguliert. Das mittels des Messgeräts erhaltene Messergebnis wird als Korrektionsfaktor in die Steuereinheit gespeist, so dass die Steuereinheit die Dicke der in der zweiten Presse gepressten Schicht korrigiert, und zwar abhängig davon, wie das Nessergebnis von dem Aufgabenwert abweicht. In dieser Weise kann die zweite Presse die eventuellen Massabweichungen der von der ersten Presse gebildeten Kunststoffschicht kompensieren. Infolgedessen ist es möglich, eine bessere durchschnittliche Qualität zu schaffen. In the production of e.g. completely insulated with foam plastic Trunk cables for a cable television network, see the cross section of the insulation in Figure 3, it is advantageous that in both coating stages half of the final Thickness of the insulating layer is pressed, with an optimal increase in the volume output can be reached. After the cooling device of the first press is in the movement path of the cable installed a device 11 for measuring the outer diameter of the cable. This device is connected to a control unit 12 of the second press, which Control unit regulates the thickness of the layer to be pressed in the second press. The measurement result obtained by means of the measuring device is used as a correction factor in the control unit fed so that the control unit the thickness of the in the second Press pressed layer corrected, depending on how the wetting result deviates from the task value. In this way the second press can handle the eventual Compensate for dimensional deviations in the plastic layer formed by the first press. As a result, it is possible to create a better average quality.

Das in Figur 2 der Zeichnung dargstellte Koaxialkabel weist einen Innenleiter 7 und eine darauf angebrachte Kunststoffisolierung 10 auf. Gemäss der in den Figuren 4 und 5 dargestellten zweiten Ausführungsform der Erfindung besteht diese Kunststoffisolierung 10 aus einer den Mittelleiter 7 umgebenden Schicht 8 aus Festkunststoff, beispielsweise aus Hochfrequenzpolyäthylen, und aus einer diese Schicht umgebenden Schicht 9 aus Schaumkunststoff, beispielsweise auch aus Hochfrequenzpolyäthylen. Es soll festgestellt werden, dass obgleich eine ganz aus Schaumkunststoff hergestellte Isolierung zum Erreichen einer kleinen Dielektrizitätskonstante, d.h. eines kleinen &-Werts, gebraucht werden könnte, so ist es bei Inneninstallationskabeln nicht möglich, weil die Axialität eines Innenleiters mit kleinem Durchmesser in einer Schaumkunststoffisolierung unmöglich erhalten bleiben kann. Wesentliche Abweichungen von der Axialität sind wiederum nicht zulässig, weil sie Veränderungen in der Kabelimpedanz und somit unerwünschte Reflexionen und im schlechtesten Fall sogar einen Kurzschluss zwischen dem Innen- und Aussenleiter veranlassen. In der vorliegenden Erfindung wird dieses Problem dadurch gelöst, dass der Innenleiter 1 mit einer Isolierung aus Festkunststoff umgeben wird, die einen in den Figuren 2 und 4 dargestellten runden Querschnitt oder irgendeine andere symmetrische, beispielsweise die in Figur 5 dargestellte, Form aufweist. Diese Festkunststoffschicht 8 verankert den Innenleiter in der Isolierung und garantiert, dass seine Axialität im Kabel erhalten bleibt. Die Schaumkunststoff schicht 9, die die Festkunststoffschicht 8 umgibt, gibt der Isolierung dagegen einen kleineren G -Wert, was eine Verkleinerung der gesamten Isolierdicke und somit eine bessere Biegebeständigkeit und Installierbarkeit des Kabels ermöglicht. In der Beispielskonstruktion der Figur 2 ist die Schaumkunststoffisolierung 9 von einem strahlungsdichten Aussenleiter umgeben, der aus einem Folienband 13 und einem Zopf 14 besteht. Auch andere Aussenleiterkonstruktionen mit bewährter Strahlungsdichtheit sind immerhin möglich. The coaxial cable shown in Figure 2 of the drawing has a Inner conductor 7 and a plastic insulation 10 applied thereon. According to the in Figures 4 and 5 shown second embodiment of the invention this plastic insulation 10 from a central conductor 7 surrounding it layer 8 made of solid plastic, for example made of high frequency polyethylene, and from a this layer surrounding layer 9 made of foam plastic, for example also made of High frequency polyethylene. It should be noted that although a completely off Foam made insulation to achieve a small dielectric constant, i.e. a small & -value, could be needed, so it is with indoor installation cables not possible because the axiality of an inner conductor with a small diameter in foamed plastic insulation cannot possibly be preserved. Significant deviations from the axiality are in turn not allowed because they change the cable impedance and thus unwanted reflections and in the worst case even a short circuit arrange between the inner and outer conductors. In the present invention this problem is solved in that the inner conductor 1 with an insulation is surrounded by solid plastic, the one shown in Figures 2 and 4 round cross-section or any other symmetrical one, for example that in Figure 5 shown, has shape. This solid plastic layer 8 anchors the inner conductor in the insulation and guarantees that its axiality is maintained in the cable. The foam plastic layer 9, which surrounds the solid plastic layer 8, is the Isolation, on the other hand, has a smaller G value, which means a reduction in the overall size Insulation thickness and thus a better bending resistance and installability of the Cable allows. In the example construction of Figure 2 is the foam plastic insulation 9 surrounded by a radiation-proof outer conductor, which consists of a foil strip 13 and a braid 14. Also other outer conductor constructions with tried and tested Radiation tightness is at least possible.

Der Aussenleiter dagegen ist von einem Aussenmantel aus PVC umgeben.The outer conductor, on the other hand, is surrounded by an outer jacket made of PVC.

In Figur 4 wird eine zweite Strukturform der Isolierung 10 dargestellt, deren innere Festkunststoffschicht 8 so ausgeformt ist, dass sie vier hinsichtlich des Innenleiters symmetrische und davon radial ausgehende, sich im Kabel axial streckende Kämme 16 aufweist. Diese Kämme 16 sind dazu geeignet, die Verankerung des Innenleiters 7 mitten im Kabel weiter zu verbessern Oben werden nur zwei Ausführungsformen des erfindungsgemässen Koaxialkabels beschrieben, und es ist verständlich, dass z.B. die Form der Isolierung 8 aus Festkunststoff umfassend variiert werden kann, ohne dass man von dem Schutzumfang der beigefügten Patentansprüche abweicht. In Figure 4, a second structural form of the insulation 10 is shown, whose inner solid plastic layer 8 is shaped so that it has four with respect to of the inner conductor symmetrical and radially outgoing therefrom, axially stretching in the cable Has combs 16. These combs 16 are suitable for anchoring the inner conductor 7 in the middle of the cable to be further improved Above only two embodiments of the described coaxial cable according to the invention, and it will be understood that e.g. the shape of the insulation 8 made of solid plastic can be varied comprehensively without that one deviates from the scope of protection of the attached claims.

- Leerseite -- blank page -

Claims (7)

Patentansprüche: 1. Verfahren zur Herstellung einer den Innenleiter eines Koaxialkabels umgebenden Isolierung, welches Koaxialkabel einen Innenleiter, eine um den Innenleiter ausgeformte Kunststoffisolierung, einen um die Isolierung ausgeformten, zylindrischen Aussenleiter und einen Aussenmantel aus Kunststoff aufweist, nach welchem Verfahren - eine aus mindestens einer Schaumkunststoffschicht bestehende Isolierschicht auf den Innenleiter stranggepresst wird und - die Isolierschicht nach dem Strangpressen abgekühlt wird, d a d u r c h a e k e n n z e i c h n e t, dass - das Strangpressen der Isolierschicht in zwei verschiedenen Stufen ausgeführt wird, und - das Abkühlen und Trocknen zwischen den Strangpressstufen ausgeführt werden. Claims: 1. A method for producing an inner conductor insulation surrounding a coaxial cable, which coaxial cable has an inner conductor, one plastic insulation molded around the inner conductor and one around the insulation has a shaped, cylindrical outer conductor and an outer sheath made of plastic, according to which method - one consisting of at least one foam plastic layer The insulating layer is extruded onto the inner conductor and - the insulating layer after extrusion it is cooled down, that - the extrusion of the insulating layer is carried out in two different stages and - the cooling and drying are carried out between the extrusion stages will. 2. Verfahren nach Patentanspruch 1, d a -d u r c h g e k e n n z e i c h n e t, dass die Hälfte der Dicke der endgültigen Isolierschicht in jeder Strangpressstufe gepresst wird. 2. The method according to claim 1, d a -d u r c h g e k e n n z e i n e t that half the thickness of the final insulating layer in each Extrusion stage is pressed. 3. Verfahren nach Patentanspruch 1 oder 2, d a d u r c h g e k e n n z e i c h n e t, dass in der ersten Pressstufe der Aussendurchmesser der stranggepressten Schicht nach der Abkühlung der Schicht gemessen wird und dass in der zweiten Pressstufe der Aussendurchmesser der strangzupressenden Schicht gemäss dem erwähnten gemessenen Aussendurchmesser gesteuert wird, damit ein genauer Aussendurchmesser für die endgültige Isolierschicht bewirkt wird. 3. The method according to claim 1 or 2, d a d u r c h g e k e It is not noted that in the first pressing stage the outer diameter of the extruded Layer after cooling the layer is measured and that in the second pressing stage the outside diameter of the layer to be extruded according to the measured value mentioned Outside diameter is controlled so that an accurate outside diameter for the final Insulating layer is effected. 4. Koaxialkabel, das einen Innenleiter (7), eine um den Innenleiter ausgeformte Kunststoffisolierung (10), einen um die Isolierung (10) ausqeformten, zylindrischen Aussenleiter (13, 14) und einen Aussenmantel (15) aus Kunststoff aufweist, d a d u r c h g e k e n n -z e i c h n e t, dass die Isolierschicht (10) aus zwei auf einander gelegenen, stranggepressten Schichten (8, 9) aus Schaumkunststoff besteht, deren Dicke ungefähr die Hälfte der Dicke der endgültigen Isolierschicht ist. 4. Coaxial cable, one inner conductor (7), one around the inner conductor molded plastic insulation (10), one molded around the insulation (10), has a cylindrical outer conductor (13, 14) and an outer jacket (15) made of plastic, d a d u r c h e k e n n -z e i n e t that the insulating layer (10) of two extruded layers (8, 9) of foam plastic lying on top of one another whose thickness is approximately half the thickness of the final insulating layer is. 5. Koaxialkabel, das einen Innenleiter (7), eine um den Innenleiter ausgeformte Kunststoffisolierung (10), einen um die Isolierung (10) ausgeformten, zylindrischen Aussenleiter (13, 14) und einen Aussenmantel (15) aus Kunststoff aufweist, d a d u r c h g e k e n n z e i c h n e t, dass die Kunststoffisolierung (10) eine sich an den Innenleiter (7) anschliessende Schicht (8) aus Festkunststoff und eine um diese Schicht ausgeformte Schicht (9) aus Schaumkunststoff aufweist. 5. Coaxial cable, one inner conductor (7), one around the inner conductor molded plastic insulation (10), one molded around the insulation (10), has a cylindrical outer conductor (13, 14) and an outer jacket (15) made of plastic, d u r c h e k e n n n z e i c h n e t that the plastic insulation (10) is a the inner conductor (7) adjoining layer (8) made of solid plastic and a has formed around this layer layer (9) made of foam plastic. 6. Koaxialkabel nach Patentanspruch 5, d a -d u r c h g e k e n n z e i c h n e t. dass der Querschnitt der Festkunststoffschicht (8) rund ist. 6. Coaxial cable according to claim 5, d a -d u r c h g e k e n n d e i n e t. that the cross-section of the solid plastic layer (8) is round. 7. Koaxialkabel nach Patentanspruch 5, d a -d u r c h g e k e n n z e i c h n e t, dass die Festkunststoffschicht (8) zwei oder mehrere hinsichtlich des Innenleiters (7) symmetrisch gelegene und davon radial ausgehende, sich im Kabel axial streckende Kämme (16) aufweist. 7. Coaxial cable according to claim 5, d a -d u r c h g e k e n n it is noted that the solid plastic layer (8) has two or more terms of the inner conductor (7) symmetrically located and radially extending therefrom, are in the cable has axially stretching combs (16).
DE19853515574 1984-05-03 1985-04-30 Coaxial cable and process for producing an insulation surrounding the inner conductor of this cable Withdrawn DE3515574A1 (en)