DE3007712A1 - Stabilisation of propellant powder, charge or munition - contg. nitrocellulose and opt. nitroglycerin by storage in dry atmos. free from oxygen and nitrous gas - Google Patents

Abstract

Improving the storability of propellant powders, propellant charges and combustible munition mouldings contg. nitrocellulose and opt. nitroglycerin involves providing a dry atmos. free from O2 and nitrous gases in the containers and maintaining this during the storage period. Pref. the dry atmos. is produced by placing a suitable desiccant, pref. silica gel (blue gel) in amts. of max. 3 wt.% w.r.t. the propellant powder, in the container. The O2-free atmos. is pref. produced by displacing the air in the container with an O2-free protective gas, pref. a noble gas, esp. Ar, N2 or CO2. The atmos. free from nitrous gases is pref. produced by adding other stabilisers for the propellant powder, pref. diphenylamine, "Centralite" (RTM) or "Akardite" (RTM), in amts. of max. 2 wt.%. The storage life is doubled or trebled without detriment to the propellant.

Description

Verfahren zur Verbesserung der Lagerfähig- Process to improve shelf life

keit von Treibladungspulvern, Treibladungen und verbrennbaren Munitionsformteilen, die Nitrozeltulose oder Nitrozellulose und Sprengöl enthalten Die Erfindting betrifft ein Verfahren nach dem Oberbegriff des Patentanspruchs 1. ability of propellant powder, propellant charges and combustible ammunition molded parts, which contain nitrocellulose or nitrocellulose and explosive oil. The invention relates to a method according to the preamble of claim 1.

Aus der DE-OS 20 33 352 ist eine Verpackung für Munition, Sprcng- und Treibinittel bekannt, die aus einer verschlossenen Dose mit Aufreißöffnung besteht, in der neben der Munition noch Feuchtigkeit absorbierende Chemikalien angeordnct sind. Diese bekannte Verpackung ermöglicht zwar die trockene Lagerung gewisser Munitionsarten, verhindert aber nicht die Zersetzung bestimmter Treibladungskomponenten in Gegenwart von Sacrstoff. Zudem verhindert diese bekannte Verpackung eine regelmäßige Überprüfung des Munitionszustands während der Lagerdauer. Die Ausgestaltung der Verpackung als Aufreißpackung ist zudem für großformatige Treibladungen und verbrennbare Munitionsformteile nicht praktikabel.From DE-OS 20 33 352 a packaging for ammunition, Sprcng- and propellant known, which consists of a sealed can with a tear opening, in which, in addition to the ammunition, there are also moisture-absorbing chemicals are. This known packaging allows certain types of ammunition to be stored in a dry place, but does not prevent the decomposition of certain propellant charge components in the presence of sacrum. In addition, this well-known packaging prevents regular checks the ammunition condition during the storage period. The design of the packaging as The tear-open pack is also suitable for large-format propellant charges and combustible ammunition molded parts not practical.

Der vorliegenden Patentanmeldung liegt die Aufgabe zugrund@ ein Verfahren zur Verbesserung der Lagerfähigkeit von Treibladungspulvern, Treibladungen und verbrennbaren Munitionsfoimteilen anzugeben, das die Lagerfähigkeit wesentlich verbessert, das auch bei großformatigen Treibladungen anwendbar ist und das darüber hinaus eine regelmaßigc Überwachung des Zustands der Treibladungspulver, Treibladungen und verbrennbaren Munitionsformteile während der Lagerdauer ermöglicht.The present patent application is based on the object @ a method to improve the shelf life of propellant powder, propellant and combustible Ammunition moldings indicate that the shelf life is essential improved, which can also be used with large-format propellant charges and, moreover, a Regular monitoring of the condition of the propellant powder, propellant and combustible Ammunition molded parts allows during the storage period.

Diese Aufgabe wird durch die in Patentanspruch 1 angegebene Erfindung gelöst.This object is achieved by the invention specified in claim 1 solved.

Vorteilhafte Ausgestaltungen und Weiterbildungen der Erfindung gehen aus den Unteransprüchen hervor.Advantageous refinements and developments of the invention go from the subclaims.

Nitrozellulosen und/oder Sprengöl( sind die Grundbestandteile konventioneller Treibladungspulver, Treibladungen und verbrennbarer Munitionsformteile für Rohrwaffen.Nitrocelluloses and / or explosive oil (are the basic components of conventional Propellant powder, propellant charges and combustible ammunition molded parts for guns.

Chemisch gesehen, handelt es sich dabei um Salpetersaure-Ester, die durch Molekülabbau nitrose Gase ahspalten, welche wiederum insbesondere bei Gegenwart von Sauerstoff unter Salpetersäurebildung die Zersetzungsreaktionen so beschleunigen können, daß eine spontane Zersetzung der gelagerten Treibladungspulver, Treibladungen und verbrennbare Munitionsformteile stattfinden kann.From a chemical point of view, these are nitric acid esters, which By breaking down the molecules, nitrous gases are split off, which in turn are especially present in the presence of oxygen with the formation of nitric acid accelerate the decomposition reactions can cause spontaneous decomposition of the stored propellant charge powder, propellant charges and combustible ammunition molded parts can take place.

Dieses nachteilige Verhalten kann erfindungsgerläß auf lange Zeit hinaus dadurch unterbunden werden, daß in Treibladungspulverpackgefäßen, Treibladungen und/oder den die Munition enthaltenden Behältern eine trockene, sauerstoffireie und von nitrosenGasenfreie Atmosphäre geschaffen und auirechterhalten wird.According to the invention, this disadvantageous behavior can last for a long time are also prevented by propellant charges in propellant powder packaging containers and / or the containers containing the ammunition a dry, oxygen-free room and atmosphere is created and maintained by nitrous gases.

Durch an sich bekannte Testbedingungen, die bis an die thermischen Belastbarkeitsgrenzen der Treibladung gehen, kann nach bekannten BezieIungen auf die Zu erwartende Lagerfähigkeit unter Normalbedingungen geschlossen werden.By means of test conditions known per se, which extend to the thermal The capacity limits of the propellant charge can go according to known relationships the expected shelf life under normal conditions must be closed.

Üb erras chenderwei e wurde dabei gefunden, daß bei Anwendung des erfindungsgemäßen Verfahrens eine erhebliche Verbesserung der @agerfähigkeit zu erreichen ist. In der flegel laßt sich bei Anwendung des crf-indungsgemäßen Verfahrens eine Verdopplung oder Verdreifachung der Lagerzeit erreichen, ohne daß die Treibladungsmittel in nachteiliger Weise. beeinflußt werden.Surprisingly, it was found that when using the The method according to the invention leads to a considerable improvement in the ability to wear is to achieve. In the flegel can be when using the crf-ind according to method achieve a doubling or tripling of the storage time without the propellant in a disadvantageous manner. to be influenced.

Die trockene Atmosphäre wird in den Lagerbehältern durch Einbringen eines geeigneten Troclcenmittels erzeugt. Als Trockenmittel eignet sich bevorzugt Silicagel, das in Mengen bis zu etwa 3 Gewichtsprozent des Treibladungspulver gewichts in den Lagerbehälter eingebracht wird.The dry atmosphere is brought into the storage containers a suitable drying agent generated. A suitable desiccant is preferred Silica gel in amounts up to about 3 percent by weight of the propellant powder weight is introduced into the storage container.

Die sauerstofffrele Atmosphäre in den Lagerbehältern wird.The oxygen-rele atmosphere in the storage containers is.

durch Verdrängen der Luft und Einbringen eines Schutzgases, wie insbesondere eines Edelgases, Stickstoff oder'Kohlensäure erzeugt. Ein für diesen Zweck besonders geeignetes Edelgas ist Argon.by displacing the air and introducing a protective gas, such as in particular a noble gas, nitrogen or carbonic acid. One especially for this purpose a suitable noble gas is argon.

Eine von nitrosen Gasen freie Atmosphäre wird in den Lagerbehältern dadurch aufrechterhalten, daß den Treibladungspulvern, Treibladungen und verbrennbaren Munitionsformteilen an sich bekannte, als Nitrosefänger wirksame Treibladungspulverstabilisatoren, insbesondere Diphenylamin, Centralite oder Akardite beigepackt werden.An atmosphere free of nitrous gases is created in the storage containers maintained by the fact that the propellant powder, propellant and combustible Ammunition molded parts known per se and effective as nitrous catchers propellant charge powder stabilizers, in particular Diphenylamine, Centralite or Akardite are included.

Derartige Treibladungspulverstabilisatoren werden bevorzugt in Mcngen bis zu etwa 2 Gewichtsprozent des abgepackten Treibladungspulveigewichts in die Lagerbehälter eingebracht Trockenmittel und Treibladungspulverstabilisatoren werden zweckmäßig getrennt voneinander in geeigneten Verpackungseinheiten, z. B. in Beutelforrn abgepackt und den in Lagerbehältern angeordneten Treibladungspulvern, Treibladungen und verbrennbaren Munitionsformteilen beigefügt. Dies ermöglicht bei Bedarf eine leichte Austauschbarkeit der abgepackten Zusatzstoffe.Propellant powder stabilizers of this type are preferred in Mcngen up to about 2 percent by weight of the weight of the packaged propellant powder in the Storage containers are introduced desiccants and propellant powder stabilizers appropriately separated from each other in suitable packaging units, e.g. B. in bag form packaged and the propellant charge powders, propellant charges arranged in storage containers and Combustible ammunition molded parts attached. This allows an easy one if necessary Interchangeability of the packaged additives.

Zweckmäßig werden Trockenmittel und Treibladungspulver stabilisatoren verwendet, die durch eine geeignete Farbreaktion au9 den Feuchtigkeitsgehalt bzw. den Gehalt an nitrosen Gasen der Lageratmosphäre hinweisen. Auf diess Weise kann durch einfache Sichtkontrolle festgestellt werden, ob die mit den Munitionsteilen abgepackten Zusatzstoffe noch in der Lage sind, ihre Schutzfunktion zu erfüllen, oder ob ein Austausch dieser Stoffe angeztigt ist.Desiccants and propellant powder stabilizers are expedient is used, which by means of a suitable color reaction increases the moisture content or indicate the content of nitrous gases in the storage atmosphere. In this way can a simple visual inspection can be used to determine whether the with the ammunition parts packaged additives are still able to fulfill their protective function, or whether an exchange of these substances is indicated.

Um die Überwachung der abgepackten Zusatzstoffe durch Sichtkontrolle zu ermöglichen, werden zweckmäßig Lagerbehälter verwendet, die mindestens ein Sichtfenster aufweisen.To monitor the packaged additives through visual inspection To enable storage containers are expediently used that have at least one viewing window exhibit.

Die Erfindung wird nachfolgend anhand einiger Aus führung s beispiele weiter erläutert.The invention is illustrated below with the aid of a few examples further explained.

Beispiel i Ein einbasiges Treibladungspulver der Zusammensetzung: Nitrozellulqse mit 13,15 % N 97s0i% Äthylcentralit (Stabilisator) 2,99% mit Feuchtigkeit 1,08 erwies sich bei 800C in Luftatmosphäre über 210 Tage stabil.Example i A monobasic propellant powder with the composition: Nitrocellulose with 13.15% N 97% ethyl centralite (stabilizer) 2.99% with moisture 1.08 was found to be stable for 210 days at 800C in an air atmosphere.

Unter sonst gleichen Bedingungen blieb es in Argon- oder Kohlesäureatmosphäre über 600 Ta<r'e stabil. Extrapoliert auf 200C erhöhte sich die Zeitspaiine der chemischen Stabilität in der sauerstofffreien Atmosphäre von 7 auf 21 Jahre Beispiel 2 Ein einbasigos Treibladungspulver der Zusammensetzung: Nitrozellulose mit 13,15 % N 97,4 ß Akardit II (Stabilisator) 2,6 ß mit Feuchtigkeit 1,08% erwies sich bei 80°C in Luftatmosphäre über 480 Tage stabi] Unter sonst gleichen Bedingungen blieb es in Argon- oder Kohlensäureatmosphäre über 1400 Tage stabil. Extrapoliert auf 200C erhöhte sich die Zeitspanne der chemischen Stabilität in diesem Beispiel durch die sauerstofffreie htmosphäre von 26 auf 48 Jahre.All other things being equal, it remained in an argon or carbonic acid atmosphere Stable for over 600 days. Extrapolated to 200C the time span increased chemical stability in the oxygen-free atmosphere from 7 to 21 years example 2 A single-base propellant powder with the composition: nitrocellulose with 13.15 % N 97.4 ß Akardit II (stabilizer) 2.6 ß with moisture 1.08% was found to be 80 ° C in an air atmosphere stable for 480 days] Under otherwise identical conditions it is stable in an argon or carbonic acid atmosphere for 1400 days. Extrapolated to 200C increased the chemical stability time in this example the oxygen-free atmosphere from 26 to 48 years.

Beispiel 3 Ein zweibasiges Treibladungspulver der Zusammensetzung: Nitrozellulose mit 13,15 % N 72,81% Nitroglycerin 23,78% Xthylcentralit (Stabilisator) 3, 41% mit Feuchtigkeit 0,56% erwies sich bei 80°C in Luftatmosphäre 140 Tage stabil.Example 3 A dibasic propellant charge powder with the composition: Nitrocellulose with 13.15% N 72.81% nitroglycerin 23.78% Xthylcentralit (stabilizer) 3.41% with humidity 0.56% was found to be stable for 140 days at 80 ° C in an air atmosphere.

Unter somit gleichen Bedingungen blieb es in Argon- oder Kohlensäureatmosphäre 450 Tage stabil. Extrapoliert auf 200C erhöhte sich die Zeitspanne der chemischen Stabilität in diesem Beispiel durch die sauerstofffrei Atmosphäre von 5 auf 15,5 Jahre.Under the same conditions, it remained in an argon or carbonic acid atmosphere Stable for 450 days. Extrapolated to 200C, the chemical time increased Stability in this example due to the oxygen-free atmosphere from 5 to 15.5 Years.

Beispiel 4 Ein zweibasiges Treiblasungspulver der Zusammensetzung: Nitrozellulose mit 13,15 % N 72,82% Nitroglycerin 24,02% Akardit II (Stabilisator) 3,16% mit Feuchtigkeit 0,58% erwies sich bei 800C in Luftatmosphäre 330 Tage stabil.Example 4 A two-base blowing powder with the composition: Nitrocellulose with 13.15% N 72.82% nitroglycerin 24.02% Akardit II (stabilizer) 3.16% with humidity 0.58% was found to be stable for 330 days at 80 ° C. in an air atmosphere.

Unter sonst gleichen Bedingungen blieb es in Argon-oder Kohlensäureatmosphäre 990 Tage stabil. Extrapoliert auf 200C erhöhte sich in diesen Beispiel die Zeitspanne der chemischen Stabilität von 11 auf 33 Jahrc.All other things being equal, it remained in an argon or carbonic acid atmosphere Stable for 990 days. Extrapolated to 200C, the time span increased in this example chemical stability from 11 to 33 years c.

Die trockene Atmosphäre wurde dadtlrch erzeugt und aufrecht erhalten, daß Beutel mit Silicagel, insbesondere Blaugel in den Gasraum gebracht wurden.The dry atmosphere was created and maintained there, that bags with silica gel, especially blue gel, were brought into the gas space.

Pulverzersetzungen beschleunigen sich bei Auf treten von Stickstoffdioxid bzw. der sich daraus in Anwesenheit von Wasser bildenden Salpetersäure. Sauerstofffreie Atmosphäre verhindert dies weitgehend, da dio Oxidation des Stidcstoffmonoxids durch den Luftsauerstoff entfällt.Powder decomposition accelerates when nitrogen dioxide occurs or the nitric acid which forms therefrom in the presence of water. Oxygen Free The atmosphere prevents this to a large extent, since the oxidation of the nitrogen monoxide occurs through there is no oxygen in the air.

Durch Moleküiabbau von Nitrozellulosen und/oder Sprengölen kann aber unter extremen Belastungen doch noch Stickstoffdioxid gebildet werden. Überraschenderweise wurde nun gefunden, daß abgespaltenes Stickstoffdiexid durch Nitrosegasfänger in der Pulveratmosphäre abgefangen und gebunden werden und so eine zusätzliche Trv3ibladungspulvorstabilisierung bewirkt werden kann.However, by breaking down the molecules of nitrocelluloses and / or explosive oils Nitrogen dioxide can still be formed under extreme loads. Surprisingly it has now been found that nitrogen dioxide split off by nitrous gas scavengers in the powder atmosphere are captured and bound and thus an additional charge powder pre-stabilization can be effected.

Dies beruht darauf, daß in einer sauerstofffreiell, trockene nen Atmosphäre die Oxidation des Stickstoffmonoxids zum kritischen, die Zersetzung beschleunigenden Stickstoffdioxid mit nachfolgender Bildung von Salpetersäure weitgehend unterbunden wird und Spuren von Stickstoffdioxid, die sich unter extremer Belastung durch Molekül abbau der Nitrozellulosen unModer Sprengöle bilden können, durch chemische Bindung an die zusätzlich beigegebenen Nitrosefänger unwirksam gemacht werden. Stickstoffmonixid beschleunigt die Treibladungspulverzersetzung nicht.This is based on the fact that in an oxygen-free, dry NEN atmosphere the oxidation of nitrogen monoxide to the critical, the decomposition accelerating Nitrogen dioxide with the subsequent formation of nitric acid largely prevented will and traces of nitrogen dioxide, which are under extreme exposure to molecule breakdown of nitrocelluloses or explosive oils through chemical bonding to the additionally added nitrous scavengers are rendered ineffective. Nitric oxide does not accelerate the propellant powder decomposition.

Dies wird anhand weiterer Beispiele crlautert.This is explained using further examples.

Beispiel 5 Ein zweibasiges, stabilisatorfreies Treibladungspulvcr der Zusammensetzung: Nitrozellalose mit 13,15 % N 73,11% Nitroglycerin 23,64% Dibutylphtalat 3,25% mit Feuchtigkeit 0,58% erwies sich im 90°C Gewichtsverlust-Test nur über 30 Std.Example 5 A dibasic, stabilizer-free propellant powder the composition: nitrocellalose with 13.15% N 73.11% nitroglycerin 23.64% dibutyl phthalate 3.25% with moisture 0.58% was only found over 30 in the 90 ° C weight loss test Hours.

chemi.sch stabil. J)urch Bei gabeln von 1 % Centralit 1 stieg die Stabilität aug 17 Tage und die äußerliche Beigabe von 3,5 % auf 34 Tage.chemically stable. With forks of 1% Centralit 1, the Stability for 17 days and the external addition of 3.5% for 34 days.

Ein Vergleichspulver mit 3,5 % homogen eingebautem Centralit 1 und gleichem Gehalt an Nitrozellulose und Sprengöl wie Beispiel 5 erwies sich über 39 Tage im gleichen Test stabil.A comparison powder with 3.5% homogeneously incorporated Centralit 1 and The same nitrocellulose and explosive oil content as Example 5 was found to be over 39 Stable days in the same test.

Beispiel 6 Bei der Herstelluiig von kleinkalibriger Munition wird vor Einfüllen des Treibladungspulvers die Luft aus den Hülsen mittels Kohlensäure, z. B. einer Trockeneistablette, vcrdrängt.Example 6 In the manufacture of small caliber ammunition before filling the propellant powder, the air from the pods by means of carbonic acid, z. B. a dry ice tablet, displaced.

Aus den gasdicht verschließbaren Transport- bzw. Lagerbehältern wird na(:h Einfüllen der Munition die Luft durch Trockeneiszugabe verdrängt. Vor dem Verschließen der Behältcr wird ein Beutel mit Siiicagel, insbesondere Blaugel und Akardit II be. gelegt. Die Beutel sollen eine Farbbeurteilung der Zusatzstoffe ermöglichen und so eingelegt werden, daß ein Austausch leicht möglich ist. Das Trockenmittel sollte 3 % und die Akarditmenge 1 % der Treibladungs pulvermenge (Gewichtsprozent) nicht überschreiten.From the gas-tight lockable transport or storage containers na (: h filling the ammunition, the air is displaced by adding dry ice Closing the container is a bag with Siiicagel, especially blue gel and Akardite II be. placed. The bags should enable the color of the additives to be assessed and inserted in such a way that an exchange is easy. The desiccant should be 3% and the amount of Akardite 1% of the propellant powder amount (percent by weight) do not exceed.

Beispiel 7 Munition unterschiedlicher Ladungen in Stoffbeuteln unc-l/ oder Behältern oder Manschetten aus verb@ennbaren Munitionsformteilen wird in gasdicht verschließbaren Behältern verpackt.Example 7 ammunition of different charges in cloth bags unc-l / or containers or collars made from separable ammunition molded parts becomes gas-tight packed in sealable containers.

Aus den Behältern ist nach Beispiel 6 die Luft durch Kohletlsäure zu verdrängen und gleichermaßen ein lcicht auswechselbarer Beutel mit Silicagel und Akardit II beizulegen.According to Example 6, the air is removed from the containers by carbonic acid to displace and also an easily exchangeable bag with silica gel and Akardit II to be enclosed.

Beispiel 8 In Munition mit Metallkartuschen oder Hülsen aus verbrennbarem Material wird die Luft durch Kohlensäure verdrängt.Example 8 In ammunition with metal cartridges or cases made of combustible Material is displaced from the air by carbon dioxide.

Die Transport- und Lagerbehälter werden nach Beispiel 7 behandelt und ausgestattet.The transport and storage containers are treated according to Example 7 and equipped.

Beispiel 9 In Lager- bzw. Transportbehältern für Treibladungspulver wird nach den Beispielen 7 und 8 die Luft durch Kohlensäure verdrängt. Zusätzlich wird ein Beutel mit Silicagel, insbesondere Blaugel und Akardit II bcigebeben.Example 9 In storage or transport containers for propellant powder according to Examples 7 and 8, the air is displaced by carbonic acid. Additionally a bag with silica gel, especially blue gel and Akardit II will be shaken.

Anstelle des in den Beispielen 6 bis 9 angegebenen Nitrosefängers Akardit kann auch ein anderer geeigneter Stabilisator, wie z. B. Centralit oder Diphenylamin verwendet werden.Instead of the nitrous scavenger specified in Examples 6 to 9 Akardite can also be another suitable stabilizer, such as e.g. B. Centralit or Diphenylamine can be used.

Die Behälter werden zweckmäßig mit mindestens einem Sichtfenster ausgestattet, welches eine Sichtkontrolle der beigepackten Zusatzstoffe ermöglicht.The containers are expediently equipped with at least one viewing window, which enables a visual inspection of the enclosed additives.

Claims (11)

Patentansprüche Ö Verfahren zur Verbesserung der Lagerfähigkeit von Treibladungspulvern, Treibladungen und verbrennbaren Munitionsformteilen, die Nitrozellulosen oder Nitrozellulosen und Sprengöl enthalten, d a d u r c h g e k e n n z e i c h n e t, daß in Treibladungspulverpackgefäßens Treibladungon und/oder den die Munition enthaltenden Behältern eine trockene, sauerstofffreie und von nitrosen Gasen freie Atmosphäre geschaffen und während der Lagerdauer aufrechterhalten wird. Claims Ö A method for improving the shelf life of Propellant powder, propellant and combustible ammunition molded parts, the nitrocelluloses or contain nitrocelluloses and explosive oil, d u r g e k e n n z e i c h n e t that in propellant powder packaging vessels propellant charge and / or the ammunition Containers containing a dry, oxygen-free and nitrous gases free Atmosphere is created and maintained during the storage period. 2. Verfangen nach Anspruch 1, d a d u r c h g e -k e n n æ e i c h n e t, daß die trockene Atmosphäre durch Einbringen eines geeigneten Trockenmittels in die Treibladungspulverpackgefäße, Treibladungen und/oder den die Munition enthaltende Behälter erzeugt wird.2. Catching according to claim 1, d a d u r c h g e -k e n n æ e i c h n e t that the dry atmosphere by introducing a suitable desiccant into the propellant powder packaging containers, propellant charges and / or the one containing the ammunition Container is generated. 3. Verfahren nach den Ansprüchen i oder 2, d a d u r c h g e 1c e n n z e i c h n e t, daß als Trockenmittel bevorzugt Silicagel (Blaugel) verwendet wird, in Mengen bis zu 3 Gewi eh Lsp ro zent des Treibladungspulvergewichts.3. The method according to claims i or 2, d a d u r c h g e 1c e It is noted that silica gel (blue gel) is preferably used as the desiccant is, in amounts up to 3 percent by weight of the propellant powder weight. . Verwahren nach einem der Ansprüche 1 bis 3, d a -d u r c h g e k e n n z e i c h n e t, daß die sauerstofffreie Atmosphäre in Treibladungspulverpackgefänen Treibladungen u:id/oder den die Munition enthaltenden Behältern durch Verdrängen der Luft und Einbringung eines sauerstofLfreien Schutzgases erzeugt wird . Storage according to one of claims 1 to 3, d a -d u r c h g e k It is noted that the oxygen-free atmosphere in propellant powder packaging vessels Propellant charges u: id / or the containers containing the ammunition by displacement the air and introduction of an oxygen-free protective gas is generated 5. Verfahren nach einem der Ansprüche 1 bis 4, d a d u r c h g e k e n n z e i c h n e t, daß als Schutzgas ein Edelgas, insbesondere Argon, Stickstoff oder Kohlensäure verwendet wird.5. Procedure according to one of claims 1 to 4, d a d u r c h g e n n n z e i c h n e t that A noble gas, in particular argon, nitrogen or carbonic acid, is used as the protective gas will. 6. Verfahren nach einem der Ansprüche 1 bis 5, d a -d u r c h g c k e n n z e i c h n e t, daß in den Treibladungspulverpackgefäßen, Treibladungen und/oder den die Munition enthaltenden Behältern eine von nitrosen Gasen freie Atmosphäre dadurch erzeugt wird, daß in die Behälter zusätzlich Treibladungspulverstabilisatoren eingebracht wer(len.6. The method according to any one of claims 1 to 5, d a -d u r c h g c It is not stated that in the propellant powder packaging containers, propellant charges and / or the containers containing the ammunition have an atmosphere free of nitrous gases is generated by adding propellant powder stabilizers in the container brought in who (len. 7. Verfahren nach einem der Ansprüche i bis 6, d a -d u r c h g e k e n n z e i c h n e t, daß als Treibladungspulverstabilisatoren Diphenylamin, Gentralite oder Akardite verwendet werden.7. The method according to any one of claims i to 6, d a -d u r c h g e it is not stated that the propellant powder stabilizers used are diphenylamine, Gentralite or Akardite can be used. 8. Verfahren nach einem der Ansprüche 1 bis 7, d a -d u r c h g e k e n n z e i c h n e t, daß dem in Behältern aufbewahrten Treibladungen Treibladungspulver stabilisatoren in Mengen bis zu etwa 2 Gewichtsprozent des Treibladungspulvergewichts beigepackt werden.8. The method according to any one of claims 1 to 7, d a -d u r c h g e it is not stated that the propellant charges stored in containers are propellant powder stabilizers in amounts up to about 2 percent by weight of the propellant powder weight are included. 9. Verfahren nach einem der Ansprüche 1 bis 8, d a -d u r c h g e k e n n z e i c h n e t, daß Trockenmittel und Treibladungspulverstabilisatoren g getrennt voneinander abgepackt und in leicht austauschbaren Verpackungsformen, wie z. B. Beuteln, den Treibladungspulverpackgefäßen, Treibladungen oder Munitionsformteilen beigepackt werden. 9. The method according to any one of claims 1 to 8, d a -d u r c h g e It is not noted that desiccants and propellant powder stabilizers g packed separately from each other and in easily exchangeable packaging forms, such as B. bags, the propellant powder packaging containers, propellant charges or ammunition molded parts are included. 10. Verfahren nach einem der Ansprüche 1 bis 9, da -d u r c h g e k e n n z e i c h n e t, daß Troclconmittel und Trei bladung spulverstttbi 1 i satoren verwendet werden, die den Feuchtigkeitsgehalt bzw. den Gehalt an nitrosen Gasen der die Treibladungspulver, Treibladungen oder verbrennbare Munitionsfonii1;eile umgebenden Atmosphäre durch eine Verfärbung sichtbar maschen.10. The method according to any one of claims 1 to 9, since -d u r c h g e It is not noted that drying agents and tri-loading powder stabilizers are used that determine the moisture content or the content of nitrous gases who hurry the propellant powder, propellant charges or combustible ammunition guns surrounding atmosphere through a discoloration. 11. Verfahren nach einem der Ansprüche i bis 10, d a -du r c h g e k e n n z e i c h n e t, daß für die Lagerung der Treibladungspulver, Treibladungen und verbrennbaren MunitionsSormteile gasdicht verschließbare Behälter verwendet werden, die zumindest ein Sichtfenster aufweisen, welches den Blick auf die in dem Behälter zusätzlich abgepackten Trockenmittel und Treibladungspulverstabilisatoren ermöglicht.11. The method according to any one of claims i to 10, d a -du r c h g e It is not indicated that for the storage of the propellant powder, propellant charges and combustible ammunition parts that can be sealed in a gas-tight manner that have at least one viewing window that allows a view of the in the Containers additionally packaged desiccants and propellant powder stabilizers enables.