DE2644089A1 - FILM FOR ELECTROSTATIC REPROGRAPHY - Google Patents
FILM FOR ELECTROSTATIC REPROGRAPHYInfo
- Publication number
- DE2644089A1 DE2644089A1 DE19762644089 DE2644089A DE2644089A1 DE 2644089 A1 DE2644089 A1 DE 2644089A1 DE 19762644089 DE19762644089 DE 19762644089 DE 2644089 A DE2644089 A DE 2644089A DE 2644089 A1 DE2644089 A1 DE 2644089A1
- Authority
- DE
- Germany
- Prior art keywords
- film according
- film
- coating
- transparent
- copies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Folie für die elektrostatische Reprographie.Foil for electrostatic reprography.
Die Erfindung betrifft eine Folie für die elektrostatische Reprographie, insbesondere für die Herstellung von Transparentkopien auf Normalkopiergeräten.The invention relates to a film for electrostatic reprography, especially for the production of transparent copies on normal copiers.
Die bekannten Geräte arbeiten mit Papier, das vorzugsweise beschichtet ist, das jedoch nur geringe oder schlechte Lichtdurchlässigkeit. Sholche Papierträger haben außerdem den Nachteil, daß sie leicht reißen und nur für die Herstellung einer begrenzen Anzahl von Kopien geeignet sind.The known devices work with paper, which is preferably coated is, however, that only low or poor light transmission. Such paper carriers also have the disadvantage that they tear easily and only for the production of one limit number of copies are suitable.
Diese Nachteile werden durch die neue Folie gemäß der Erfindung überwunden.These disadvantages are overcome by the new film according to the invention.
Gegenstand der Erfindung ist eine Folie für elektrostatische Reprographie, insbesondere für die Herstellung von Transparentkopien auf Normalkopiergeräten, die dadurch gekennzeichnet ist, daß sie aus einem antistatischen, transparenten oder matten, gegebenenfalls hitzestabilisierten oder thermofixierten synthetischen Material be- steht und eine hitzebeständige Beschichtung mit einem Erweichungspunkt zwischen 40 und 140 s aus einem quaternären Ammoniumsalz und/oder gesättigten Polyester- oder Acrylharzen oder Polymeren oder Mischpolymeren der Methacrylsäure oder deren Mischungen aufweist und einen Oberflächenwiderstand von 107 bis 1012 Ohm, eine Lichtdurchlässigkeit bis zu 90% und eine mittlere Rauhtiefe von 0,2 bis 6 my hat.The invention relates to a film for electrostatic reprography, especially for the production of transparent copies on normal copiers, which is characterized in that it is made of an antistatic, transparent or matt, optionally heat-stabilized or thermoset synthetic Material loading stands and a heat-resistant coating with a Softening point between 40 and 140 s from a quaternary ammonium salt and / or saturated polyester or acrylic resins or polymers or copolymers of methacrylic acid or mixtures thereof and has a surface resistance of 107 to 1012 Ohm, a light transmission of up to 90% and an average surface roughness of 0.2 to 6 my has.
Die Hauptverwendungsmöglichkeit solcher Folien liegt in der Herstellung von Transparentkopien für die Tageslichtprojektion. Es können aber damit auch Zeichenkopien hergestellt und Zeichnungen, Diagramme, Tabellen und dgl.The main use of such films is in manufacturing of transparencies for daylight projection. But it can also be used to copy characters produced and drawings, diagrams, tables and the like.
in einem Arbeitsgang kopiert und verkleinert werden. Weitere Anwendungsmöglichkeiten bestehen in der Xerographie, der Telekopie, der Mikroverfilmung und Duplizierung, in der Infrarot- und Ultraviolett-Spektroskopie, in der Aufzeichnung chromatischer Trennverfahren. In allen Fällen wird der Vorteil erreicht, daß einfach und wirtschaftlich bis zu 1000mal Transparentkopien erhalten werden können.can be copied and scaled down in one operation. Other possible uses consist of xerography, facsimile, microfilming and duplication, in infrared and ultraviolet spectroscopy, in chromatic recording Separation process. In all cases the advantage is obtained that it is simple and economical up to 1000 times transparencies can be obtained.
Diese Transparentkopien sind im Gegensatz zu Papierträgern reißfest und stabil und bieten die Möglichkeit zur weiteren Durchlichtkopie. Sie lassen sich auch mit geeigneten Zeichenmedien beschriften.In contrast to paper carriers, these transparencies are tear-resistant and stable and offer the possibility of further transparency copies. You let yourself also write on with suitable drawing media.
Das Trägermaterial dieser Folien kann jedes geeignete synthetische Material sein, das die geforderten Bedingungen erfüllt. Vorzugsweise liegt ein Trägermaterial aus Polyäthylentherephthalat, Polycarbonat, Celluloseacetat, Polysulfon, iiystyrol, Polyamid oder Polyimid vor, das insbesondere eine Dicke von 50 bis 250 my hat. Es ist bekannt, daß insbesondere Polyesterfolien eine hohe mechanische und elektrische Festigkeit haben und chemisch und thermisch sehr beständig sind. Ein solches Trägermaterial kann auf einer oder beiden Seiten gleich oder unterschiedlich beschichtet sein, wobei die mittlere Auftragsdichte der Beschichtung vorzugsweise zwischen 0,2 und 6 my beträgt. Polyesterfolien haben vorzugsweise eine Dicke von 100 my, da eine derartige Folie einen optimalen Kompromiß zwischen der für die Anwendung erforderlichen Temperaturbeständigkeit und der Biegsamkeit darstellt.The carrier material for these films can be any suitable synthetic material Be material that meets the required conditions. There is preferably a carrier material made of polyethylene terephthalate, polycarbonate, cellulose acetate, polysulfone, iiystyrene, Polyamide or polyimide, which in particular has a thickness of 50 to 250 my. It it is known that polyester films in particular have a high mechanical and electrical properties Have strength and are very chemically and thermally stable. Such a carrier material can be coated the same or differently on one or both sides, wherein the mean application density of the coating is preferably between 0.2 and 6 my is. Polyester films preferably have a thickness of 100 my, as such a film is an optimal compromise between the for the application represents the required temperature resistance and flexibility.
Vorzugsweise enthält die Beschichtung als quaternäres mmoniumsals ein Derivat einer aliphatischen Carbonsäure mit 4 bis 18 E-Atomen, insbesondere Stearamidopropyldimethtlammoniumnitrat. Die Beschichtung auf der rägerfolie kann farblos oder mit Meta1lkomplexfarbstoffen eingefärbt sein. In der Beschichtung oder auch im Erägermaterial enthaltene Farben tragen bei der Rerstellung von Transparentkopien zur Verdeutlichung von Kurven, Diagrammen und Graphiken bei, da die Kopien getrennt auf verschiedenen Farbfolien hergestellt werden können.Preferably the coating contains as quaternary ammonium a derivative of an aliphatic carboxylic acid with 4 to 18 E atoms, in particular Stearamidopropyl dimethyl ammonium nitrate. The coating on the carrier film can colorless or colored with metal complex dyes. In the coating or Colors contained in the carrier material also play a role in the creation of transparencies to clarify curves, diagrams and graphics, since the copies are separate can be produced on different colored foils.
Die neuen Folien können extrudiert oder gegossen sein.The new foils can be extruded or cast.
Selbstverständlich ist die Isotropie der Beschichtung Voraussetzung für eine gleichmäßig gute Anwendung. Die mittlere Auftragsdicke der Beschichtung liegt vorzugsweise zwischen 0,2 und 6 my.Of course, the isotropy of the coating is a prerequisite for consistently good application. The mean application thickness of the coating is preferably between 0.2 and 6 my.
Die Gleitfähigkeit der Folie ab Stapel und im Transportsystem der Kopiergeräte hängt u.A. von der Härte und Glätte beziehungsweise der Oberflächenrauhigkeit der Beschichtung ab. Um die gewünschte Oberflächenbeschaffenheit der Folie zu erhalten, kann man vorteilhaft anorganische oder organische Körnungsmittel zusetzen, vorzugsweise Siliciumdioxid oder mikrofeine Polymere von äthylen oder Propylen oder deren Mischungen. Die durch Einsatz der Eörnungsmittel regelbare Rauhigkeit der Oberfläche soll vorzugsweise zwischen 0,2 und 6 my liegen. Auch die zugesetzten Pigmente haben vorteilhaft einen entsprechenden Korngrößenbereich.The sliding ability of the film from the stack and in the transport system of the Copier hangs, among other things the hardness and smoothness or the surface roughness the coating. In order to obtain the desired surface quality of the film, one can advantageously add inorganic or organic graining agents, preferably Silicon dioxide or microfine polymers of ethylene or propylene or their mixtures. The roughness of the surface, which can be regulated by using the oiling agent, should preferably be achieved between 0.2 and 6 my. The added pigments also advantageously have one corresponding grain size range.
Bei einer besonders vorteilhaften Ausbildung der erfindungsgemäßen Folie fließt die Hälfte einer auf die Folie aufgebrachten Ladung in weniger als 100 Sekunden ab.In a particularly advantageous embodiment of the invention Foil flows in less than half of a charge placed on the foil 100 seconds off.
Die Erfindung wird durch die nachstehenden Beispiele erläutert: Beispiel 1 Zur Zubereitung einer Beschichtungslösung für die erfindungsgemäße Folie wurde mit folgenden Geräten gearbeitet: Gefäße REhrbehälter aus V4A-Stahl oder Polyäthylen, zylindrisch mit Deckel, vorzugsweise mit Bodenauslaufhahn.The invention is illustrated by the following examples: Example 1 To prepare a coating solution for the film according to the invention, Worked with the following devices: V4A steel or polyethylene containers, cylindrical with lid, preferably with a floor tap.
Misdhwaage Mechanische Waage mit Mischdrehskala und Tariervorrichtung.Misdhwaage Mechanical scales with mixing dial and taring device.
Waagefehler: 0,2 kg Bereich: O - 300 kg Dampfheizung Heizschlange aus V4A, passend zu Rührbehälter. Heizmedium = Dampf bei etwa 4 bar. Zuleitung zu Heizschlange = dampffeste Gummischläuche.Scale error: 0.2 kg Range: O - 300 kg steam heating coil Made of V4A, suitable for the stirred tank. Heating medium = steam at around 4 bar. Supply line to Heating coil = steam-proof rubber hoses.
Rührwerk Wandhub-Ruhrwerk mit Mischpropeller mit Leitring, Drehzahlen stufenlos regelbar von 200 bis 1200 V/min.Agitator wall-lift agitator with mixing propeller with guide ring, speeds continuously adjustable from 200 to 1200 V / min.
Meßzylinder Inhalt 100 - 500 ml Graduierung 1 - 5 ml.Measuring cylinder, content 100 - 500 ml, graduations 1 - 5 ml.
Elektrische Tis chwaage Bereich = 2000 g Teilung = 0,1 g Dispergator V-Xurrax von Janke + Dunkel In den Rührbehälter wurden mit Hilfe der Mischwaage 56,4 Gew. *1,2 - Dichloräthan, 5,0 Gew. % Cyclohexanon und 26,0 Gw. % Tetrahydrofuran als Lösungsmittel vorgelegt. Die Lösungsmittel wurden dann mit der Dampfheizung auf 40 bis 50 T aufgeheizt und 12,5 Gew. * gesättigtes Polyesterharz, MG - 5000, unter kräftigem Rühren in die warmen Lösungsmittel gegeben und gelöst. Danach wurden 0,05 Gew. * Stearamidopropyldimethylammoniumnitrat als Mittel zum Antistatischmachen mit dem Meßzylinder abgemessen und zugegeben. Als Körnungsmittel wurden 0,08 Gew.Electric table scales range = 2000 g division = 0.1 g dispersant V-Xurrax from Janke + Dunkel The mixing scales were used to add 56.4% by weight of 1,2-dichloroethane, 5.0% by weight of cyclohexanone and 26.0% by weight of tetrahydrofuran presented as a solvent. The solvents were then steam heated heated to 40 to 50 T and 12.5 wt. * saturated polyester resin, MG - 5000, added to the warm solvents with vigorous stirring and dissolved. After that were 0.05 Wt. * Stearamidopropyldimethylammonium nitrate as an antistatic agent measured with the measuring cylinder and added. As a grain size 0.08 wt.
Siliciumdioxyd, mittlere Körnung: 6 - 8,5 my, SiO2: > 94 Gew. * auf der Tischwaage abgewogen und zum Schluß zugegeben. Die fertige Lösung wurde nach etwa 15 Minuten bei mittlerer Drehzahl von etwa 500 Umirehungen/Minute gerührt und dann in bekannter Weise auf eine Polyesterfolie beidseitig aufgetragen. Es wurde eine Polyesterfolie der Firma DuPont de Nemours mit folgenden Maßen verwendet: Breite 125 cm, Dicke 0,1 mm, Länge per Rolle 1100 laufende Meter.Silicon dioxide, medium grain size: 6 - 8.5 my, SiO2:> 94 wt. * weighed on the table scales and added at the end. The finished solution was made after about 15 minutes at a medium speed of about 500 revolutions / minute and then applied on both sides of a polyester film in a known manner. It was a polyester film from DuPont de Nemours with the following dimensions is used: width 125 cm, thickness 0.1 mm, length per roll 1100 linear meters.
Die erhaltenen Lösungen sind im allgemeinen niedrig viskos und zeigen ein /Fließverhalten.The solutions obtained are generally of low viscosity and show a / flow behavior.
Bekannte Verfahren sind Angießen, Antauchen und Anspülen; bei schnell-laufenden Beschichtungsmaschinen wird vorzugsweise vordosiert und der ueberschuß über hochglanzpolierte Rakelwalzen abgetragen. Die Maschinengeschwindigkeit lag bei 30 m/Minute bei Temperaturen von 80 s bis 130 s und einer Luftbeaufschlagung von 5 m3/Sekunde/m2.Known methods are pouring on, dipping and rinsing; with fast-running Coating machines are preferably pre-dosed and the excess over highly polished Doctor rollers removed. The machine speed was 30 m / minute at temperatures from 80 s to 130 s and an air admission of 5 m3 / second / m2.
Das erhaltene Produkt besaß folgende Eigenschaften: Aussehen: klar und körnig Oberflächenwiderstand: zwischen 107 - 5 x 1011 Ohm Lichtdurchlässigkeit: 90 * Grabung: 5 * + 2 * multiple feeding: 10 Folien übereinander müssen einzeln eingezogen werden* Planlage der Kopie: Keine kurzen Wellen am Rand des Pormates und keine lokalen Deformationen.The product obtained had the following properties: Appearance: clear and grainy surface resistance: between 107 - 5 x 1011 ohm light transmission: 90 * Dig: 5 * + 2 * multiple feeding: 10 slides on top of each other must be individually be drawn in * Flatness of the copy: No short waves at the edge of the format and no local deformations.
*das multiple feeding wird mit verschiedenen Normalpapierkopiergeräten getestet.* the multiple feeding is possible with different plain paper copiers tested.
Eine solche Folie ist insbesondere für Urockenkopier- geräte geeignet.Such a film is particularly suitable for hard copy devices suitable.
Tonerhaftung: fingernagelfest Schichtdicke: 0,2 - 6 mym Rauhigkeit: 0,2 - 6 mym Beschriftung: wässrige und lösemittelhaltige Filzschreiber waren geeignet Schichthaftung: nach Gitterschnitt einwandkeie Haftung bei Prüfung mit verschiedenen Klebebändern.Toner adhesion: fingernail-proof Layer thickness: 0.2 - 6 μm roughness: 0.2 - 6 μm inscription: aqueous and solvent-based felt-tip pens were suitable Layer adhesion: after cross-cut perfect adhesion when tested with different Adhesive tapes.
Beispiel 2 Es wurde wie im Beispiel 1 gearbeitet, jedoch vor dem Aufbringen auf die Trägerfolie noch mit einem Dispergator etwa 90 Minuten dispergiert. Für die Ansetzung der Lösung wurden folgende Reagenzien verwendet: 80,15 * Methyläthylketon) 8,16 * Dioxan ) Lösungsmittel 12,33 % Polymethylmethacrylat) Harz 0,12 * Siliconöl, 100 c St. ) Dispergierhilfsmittel 1,24 % disperse Kieselsäure ) Oberfläche etwa 200 m2/g ) Körnungsmittel Es wurde eine transparente, hitzestabilisierte Polyesterfolie verwendet. Diese Folie gewahrt nach dem Aufbringen der leicht mattierten Beschichtung eine einwandfreie Annahme von Flüssigkeitstoner. Die Rückseite entsprach der farblosen Beschichtung von Beispiel 1.Example 2 The procedure was as in Example 1, but before application dispersed on the carrier film with a disperser for about 90 minutes. For the preparation of the solution, the following reagents were used: 80.15 * methyl ethyl ketone) 8.16 * dioxane) solvent 12.33% polymethyl methacrylate) resin 0.12 * silicone oil, 100 c St.) dispersing aid 1.24% dispersed silica) surface approx 200 m2 / g) grain size A transparent, heat-stabilized polyester film was used used. This film is preserved after the slightly matt coating has been applied a proper acceptance of liquid toner. The reverse corresponded to the colorless one Coating of Example 1.
Beispiel 3 Es wurde wie in Beispiel 1 gearbeitet und auf eine Trägerfolie wie in Beispiel 1 eine Beschichtung aus den nach- folgend auf geführten Bestaniteilen aufgebracht: 45,65 * Zet Methyläthylketon ) 45,65 % Dioxan ) Lösungsmittel 3,05 % Cyclohexanon ) 5,50 * Polymethacrylat ) Rarz 0,12% handelsäbliches guater- ) Mittel zum Antinahes Ammoniumsalz ) statischmachen 0,03 % Polyäthylen, mikrofein ) Körnungsmittel Die erhaltene Folie besaß die Eigenschaften der Folie des Beispiels 1.Example 3 The procedure was as in Example 1 and applied to a carrier film as in example 1 a coating made of the following following on listed Components applied: 45.65 * Zet methyl ethyl ketone) 45.65% dioxane) solvent 3.05% cyclohexanone) 5.50 * polymethacrylate) Rarz 0.12% commercial grade ) Agent for the anti-near ammonium salt) static make 0.03% polyethylene, microfine ) Grain agent The film obtained had the properties of the film of the example 1.
Beispiel 4 Es wurde wie in Beispiel 1 gearbeitet und auf eine Trägerfolie gemäß Beispiel 2 eine Beschichtung aus den nachfolgend auf geführten Bestandteilen aufgebracht: 85,5 * Methyläthylketon ) 4,5 % Butylacetat ) Lösungsmittel 4,5 * Cyclohexanon ) 3,75 * Polymethacrylat ) 1,65 % Vinylchlorid-Vinylacetat-) Mischpolymerisat ) Harzmischung MG 8500 - 9500 ) 0,03 * Polyäthylen, mikrofein ) Körnungsmittel Die erhaltene Folie besaß alle Eigenschaften wie das Produkt von Beispiel 1, jedoch betrug der Oberflächenwiderstand etwa 1012 Ohm. Diese Folie ist besonders für Trokkentoner-Duplikatoren geeignet.Example 4 The procedure was as in Example 1 and applied to a carrier film according to Example 2, a coating made from the components listed below applied: 85.5 * methyl ethyl ketone) 4.5% butyl acetate) solvent 4.5 * cyclohexanone ) 3.75 * polymethacrylate) 1.65% vinyl chloride-vinyl acetate) copolymer) Resin mixture MG 8500 - 9500) 0.03 * polyethylene, microfine) graining agent Die The film obtained had all the properties as the product of Example 1, however the surface resistance was about 1012 ohms. This foil is especially for use with dry toner duplicators suitable.
Beispiel 5 Es wurde wie in Beispiel 1 gearbeitet, die Lösungsmittel wurden jedoch nicht erhitzt. Auf eine Folie wie in Beispiel 1 wurde eine Beschichtung aus 37,75 % Methyläthylketon ) 37s75 % Dioxan ) Lösungsmittel 15,9 % Polyesterharz ) 7,9 % Polymethacrylat ) Harze 0,5 % Phosphorsäureester ) Mittel zum Antistatischmachen 0,1 % Polyäthylen, mikrofein ) Körnungsmittel 0,1 * Siliconöl, 100 c St. ) Dispergierhilfsmittel aufgebracht und ein Produkt erhalten, das in seinen Eigenschaften dem Produkt aus Beispiel 1 entsprach.Example 5 The procedure was as in Example 1, the solvents however, were not heated. A coating was applied to a film as in Example 1 from 37.75% methyl ethyl ketone) 37.75% dioxane) solvent 15.9% polyester resin ) 7.9% polymethacrylate) Resins 0.5% phosphoric acid ester) Antistatic agent 0.1% polyethylene, microfine) grain size 0.1 * silicone oil, 100 c St.) dispersing agent applied and obtained a product that distinguishes itself in its properties from the product Example 1 corresponded.
Beispiel 6 Es wurde wie in Beispiel 5 gearbeitet und dabei der Farbstoff im Lösungsmittel 1 vorgelöst.Example 6 The procedure was as in Example 5, except for the dye pre-dissolved in solvent 1.
Auf die Folie wurde eine Beschichtung aus 7,4 % Methanol ) .. . ) Bosungsmittel 1 2,24 * Cyclohexanon ) 0,93 % Kupfer-phtalocynanin- ) blauer organischer sulfamid ) Barbstoff 24,5 % Methyläthylketon ) 53,2 % Dioxan ) Lösungsmittel 2 1,7 * Polyesterharz ) Harz 0,03 * Siliciumdioxyd ) Körnung 6 - 13 my ) Körnungsmittel aufgebracht und ein Produkt erhalten, das in seinen Eigenschaften weitgehend dem Produkt aus Beispiel 1 entsprach.A coating of 7.4% methanol was applied to the film. ) Bosnian agent 1 2.24 * cyclohexanone) 0.93% copper-phtalocynanin-) blue organic sulfamide) dye 24.5% methyl ethyl ketone) 53.2% dioxane) solvent 2 1.7 * Polyester resin) resin 0.03 * silicon dioxide) grain size 6 - 13 my) grain size medium applied and a product obtained, which in its properties largely the Product from Example 1 corresponded.
Durch Austausch des Farbstoffes sind die Farbtöne gelb, grün und rot möglich.By exchanging the dye, the colors are yellow, green and red possible.
Claims (8)